U.S. patent application number 11/731494 was filed with the patent office on 2009-02-26 for concrete reinforcement structure.
This patent application is currently assigned to Polymer Group, Inc.. Invention is credited to David Anderson, Gene Lamb, Paul Schmidt.
Application Number | 20090049779 11/731494 |
Document ID | / |
Family ID | 33551519 |
Filed Date | 2009-02-26 |
United States Patent
Application |
20090049779 |
Kind Code |
A1 |
Schmidt; Paul ; et
al. |
February 26, 2009 |
Concrete reinforcement structure
Abstract
This invention relates to a reinforcement structure which is
used in providing cementitious mixtures supplemental support and
strength upon setting, and more particularly, to a reinforcement
structure which comprises a plurality of oriented reinforcing
fibrous and/or filamentary components having a finite cut length,
and fastening the reinforcing fibrous and/or filamentary components
by one or more circumferential retaining elements.
Inventors: |
Schmidt; Paul; (Pretty
Prairie, KS) ; Lamb; Gene; (Kingman, KS) ;
Anderson; David; (Kingman, KS) |
Correspondence
Address: |
WOOD, PHILLIPS, KATZ, CLARK & MORTIMER
500 W. MADISON STREET, SUITE 3800
CHICAGO
IL
60661
US
|
Assignee: |
Polymer Group, Inc.
|
Family ID: |
33551519 |
Appl. No.: |
11/731494 |
Filed: |
March 30, 2007 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10858315 |
Jun 1, 2004 |
7219478 |
|
|
11731494 |
|
|
|
|
60475038 |
Jun 2, 2003 |
|
|
|
Current U.S.
Class: |
52/309.17 |
Current CPC
Class: |
C04B 28/02 20130101;
C04B 28/02 20130101; C04B 2103/0077 20130101; C04B 28/02 20130101;
E04C 5/07 20130101; C04B 20/0048 20130101; C04B 16/0608
20130101 |
Class at
Publication: |
52/309.17 |
International
Class: |
E04B 1/00 20060101
E04B001/00; E04G 21/00 20060101 E04G021/00; E04C 2/28 20060101
E04C002/28 |
Claims
1-6. (canceled)
7. A reinforcement structure comprising two or more reinforcing
components, said two or more reinforcing components comprising at
least one of fibrous components or at least one of filamentary
components and each of said reinforcing components being of finite
staple lengths, wherein said reinforcing components are combined in
an essentially parallel orientation and circumscribed with one or
more circumferential retaining elements about the circumference of
said reinforcing components.
8. A reinforcement structure as in claim 7, wherein said one or
more circumferential retaining elements comprises no more than 80%
of the total surface area of said reinforcement structure.
9. A reinforcement structure as in claim 8, wherein said one or
more circumferential retaining elements comprises no more than 50%
of the total surface area of said reinforcement structure.
10. A reinforcement structure as in claim 9, wherein said one or
more circumferential retaining elements comprises no more than 30%
of the total surface area of said reinforcement structure.
11. A reinforcement structure as in claim 7, wherein said
reinforcing components comprise polymer compositions.
12. A reinforcement structure as in claim 7, wherein at least one
of said reinforcing components and circumferential retaining
elements of said reinforcement structure have at least one of a
textured surface or raised surface asperities.
13. A reinforcement structure as in claim 7, wherein said
circumferential retaining elements comprise a binder that exhibits
sufficient durability to maintain the orientation of said
reinforcing components.
14. A reinforcement structure comprising two or more reinforcing
components, said two or more reinforcing components comprising at
least one of fibrous components and at least one of filamentary
components and each of said reinforcing components being of
infinite lengths, wherein said reinforcing components are combined
in an essentially parallel orientation and circumscribed with one
or more circumferential retaining elements about the circumference
of said reinforcing components.
15. A reinforcement structure as in claim 14, wherein said
reinforcing components comprise polymer compositions.
16. A reinforcement structure as in claim 14, wherein at least one
of said reinforcing components and circumferential retaining
elements of said reinforcement structure have at least one of a
textured surface or raised surface asperities.
17. A reinforcement structure as in claim 14, wherein said
circumferential retaining elements comprise a binder that exhibits
sufficient durability to maintain the orientation of said
reinforcing components.
18. A reinforcement structure as in claim 14, wherein said
reinforcement structure comprises a series of segmented weakened
points along said reinforcing components effective that a selected
portion is separable from the remainder thereof.
Description
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application is a division of U.S. patent application
Ser. No. 10/858,315, which was filed Jun. 1, 2004.
TECHNICAL BACKGROUND
[0002] This invention relates to a reinforcement structure which is
used in providing cementitious mixtures supplemental support and
strength upon setting, and more particularly, to a reinforcement
structure which comprises a plurality of oriented reinforcing
fibrous and/or filamentary components having a finite cut length,
said reinforcing fibrous and/or filamentary components fastened by
one or more circumferential retaining elements.
BACKGROUND OF THE INVENTION
[0003] The use of metal rods or "rebar" is a common and economical
way to reinforce concrete. These rods, usually of steel, are
available in a number of different sizes and lengths. The rods are
typically cut and bent to fit the concrete structure, and the
concrete is then placed around and over the rods. The reinforcing
rods are completely embedded in the concrete matrix. As the mixture
hardens, the concrete bonds strongly to the surface of the rods
which, in turn, impart flexural strength to the concrete mass. Of
course, rods do not come in the exact lengths for all concrete
forms. Typically, the rods must be cut and spliced to fit a
particular job. Because the final strength of the cured concrete
depends on the strength of the reinforcing rods, splices must not
weaken the rod.
[0004] The strength of the hardened concrete depends, to a great
extent, on the strength of the reinforcing rods. Therefore,
corrosion of the rods becomes a serious problem. Hardened concrete
is somewhat porous so that air and moisture can penetrate and
contact the reinforcing rods and promote oxidation (rust).
Furthermore, the wet concrete itself is alkaline, which can further
promote the corrosion of the metal. When rods rust, they not only
lose their strength, but they also swell, causing the concrete to
split.
[0005] An unmet need exists for a reinforcing structure that
provides cementitious mixtures with the necessary strength and
support that steel reinforcement currently provides, but is
insusceptible to corrosion, bends more easily, lightweight, cuts
easily, and able to be thermally bonded to itself more easily in
cross-overs.
SUMMARY OF THE INVENTION
[0006] This invention relates to a reinforcement structure which is
used in providing cementitious mixtures supplemental support and
strength upon setting, and more particularly, to a reinforcement
structure which comprises a plurality of oriented reinforcing
fibrous and/or filamentary components having a finite cut length,
and fastening the reinforcing fibrous and/or filamentary components
by one or more circumferential retaining elements.
[0007] In a first embodiment, the reinforcement structure of the
present invention is formed from two or more reinforcing fibrous
and/or filamentary components of finite staple length and
essentially parallel orientation. In a second embodiment, the
reinforcement structure of the present invention is formed from two
or more reinforcing fibrous and/or filamentary components of
infinite length and essentially parallel orientation. The
reinforcement structure may comprise both fibers and filaments,
wherein the fibers and filaments may be of similar or dissimilar
materials and further provide similar or dissimilar functions
within the cementitious mixture. Further, the orientation of the
fibrous and/or filamentary components may be other than that of a
parallel orientation, other orientations may include a twisted
orientation or an interwoven orientation, wherein the components
are intertwined with one another.
[0008] The compositions of the reinforcing components is selected
from the group consisting of synthetic polymers, natural polymers,
and the combinations thereof, and are not necessarily of the same
polymeric composition, denier, finite staple length, or
functionality. Once the cementitious mixture is deposited over and
around the reinforcement structure, the mixture is able to
penetrate the parallel orientation of the reinforcing fibrous
and/or filamentary components of the reinforcement structure.
Further, the reinforcing fibrous and/or filamentary components
provide more surface area for the cementitious mixture to hold onto
upon drying.
[0009] The reinforcement structure comprises one or more
circumferential retaining elements that maintain the integrity of
the reinforcement structure. Suitable circumferential retaining
elements include chemical and/or mechanical means, including a
binder that exhibits sufficient durability to maintain the
orientation of the reinforcing fibrous and/or filamentary
components. Additional circumferential retaining elements include,
but are not limited to clips, wires, ties, adhesives, and other
various retaining means comprised of synthetic polymers and/or
natural polymers. Optionally, the reinforcing fibrous and/or
filamentary components may comprise an chemical and/or mechanical
internal interlocking system that maintains the orientation of the
components.
[0010] Preferably, the one or more circumferential retaining
elements comprises no more than 80% of the total surface area of
the reinforcement structure; more preferably comprises no more than
50% of the total surface area of the reinforcement structure; and
most preferably comprises no more than 30% of the total surface
area of the reinforcement structure, wherein the total surface area
is defined as the overall length and circumference of the
reinforcement structure. Limiting the circumferential retaining
elements serves to expose the significant and useful proportion of
the oriented reinforcing fibrous and/or filamentary components to
the external environment.
[0011] It should be noted that the reinforcing fibrous and/or
filamentary components, as well as the resulting reinforcement
structure, can be further treated with performance modifying
additives, such as represented by the topical application of a
material flow-enhancing lubricant. Further, additional temporary
binding agents, including water-soluble chemistries such as
polyvinyl alcohol, can be used in conjunction with a primary
interlocking means.
[0012] Upon final formation of the reinforcement structure, the
structure can be more easily handled than steel reinforcement
structures. The reinforcement structure of the present invention
may prolong the life span of cementitious construction due to its
durability and resistance to corrosion, which tends to result in
cracks, having an overall deleterious affect on cementitious
construction. Further, the reinforcement structure of the present
invention is lightweight and easily bent to fit small spaces.
Further still, the reinforcement structure more readily thermally
bonds to itself compared to steel.
[0013] Other features and advantages of the present invention will
become readily apparent from the following detailed description,
the accompanying drawings, and the appended claims.
DETAILED DESCRIPTION
[0014] While the present invention is susceptible of embodiment in
various forms, hereinafter is described a presently preferred
embodiment of the invention, with the understanding that the
present disclosure is to be considered as an exemplification of the
invention, and is not intended to limit the invention to the
specific embodiment illustrated.
[0015] Steel reinforcement bars are routinely used in cementitious
mixtures so as to render a corresponding cured cementitious
construct more resistant to structural defect and failure. Due to
difficulties encountered in the actual handling of the steel
reinforcement bars and the poor performance experienced in the
cured cementitious construct, the present invention is directed to
a means for providing the necessary strength and support to
acementitious construct without deleterious affecting the
cementitious construct.
[0016] In accordance with the present invention, the reinforcement
structure comprises a plurality of reinforcing fibrous and/or
filamentary components, wherein the fibrous and/or filamentary
components have an essentially parallel orientation. Optionally,
the reinforcing fibrous and/or filamentary components of the
reinforcement structure may be twisted or interwoven with one
another.
[0017] In a first embodiment, the reinforcement structure of the
present invention is formed from two or more reinforcing fibrous
and/or filamentary components of finite staple length and
essentially parallel orientation. In a second embodiment, the
reinforcement structure of the present invention is formed from two
or more reinforcing fibrous and/or filamentary components of
infinite length and essentially parallel orientation. The
reinforcement structure may comprise both fibers and filaments,
wherein the fibers and filaments may be of similar or dissimilar
materials and further provide similar or dissimilar functions
within the cementitious mixture.
[0018] The composition of such reinforcing fibrous and/or
filamentary components is selected from the group consisting of
synthetic polymers, natural polymers, and the combinations thereof.
Preferably, the composition of the reinforcing fibrous and/or
filamentary components is selected from the synthetic polymers
including, without limitation, thermoplastic and thermoset
polymers. A particularly preferred embodiment of the present
invention is directed to reinforcing staple fibers comprising
polyolefin thermoplastic resins. It is within the purview of the
present invention that the individual reinforcing fibrous and/or
filamentary components as incorporated in the reinforcement
structure need not necessarily be of the same polymeric
composition, denier, finite staple length, or functionality.
[0019] The reinforcing filamentary components of the present
invention may be manufactured by directly extruding a polymeric
sheet into a bath comprised of water so as to instantly quench the
extruded film, slitting the film into ribbons, and chopping the
film filaments into preselected widths. Optionally, the film
filaments may be fibrillated, micro-fibrillated, or imparted with
some texture to enhance adhesion of the cementitous mixtures to the
filamentary components. Further, the filamentary components may be
manufactured in accordance with U.S. published patent application
US20030044592A1, to Perez, et al., hereby incorporated by
reference, wherein the filaments may be prepared by extruding a
cast film of melt processible polymer, length orienting said cast
film, slitting said oriented film into ribbons of preselected
widths, and chopping said fibers to preselected lengths. If
desired, the fibers may be shaped, or a pattern imparted to one or
more surfaces.
[0020] The reinforcement structure comprises one or more
circumferential retaining elements that maintain the integrity of
the reinforcement structure. Suitable circumferential retaining
elements include chemical and/or mechanical means, including a
binder that exhibits sufficient durability to maintain the
orientation of the reinforcing fibrous and/or filamentary
components. Additional circumferential retaining elements include,
but are not limited to clips, wires, ties, adhesives, and other
various retaining means comprised of synthetic polymers and/or
natural polymers. Optionally, the reinforcing fibrous and/or
filamentary components may comprise a chemical and/or mechanical
internal interlocking system that maintains the orientation of the
reinforcing fibrous and/or filamentary components.
[0021] Preferably, the one or more circumferential retaining
elements comprises no more than 80% of the total surface area of
the reinforcement structure; more preferably comprises no more than
50% of the total surface area of the reinforcement structure; and
most preferably comprises no more than 30% of the total surface
area of the reinforcement structure, wherein the total surface area
is defined as the overall length and circumference of the
reinforcement structure. Limiting the circumferential retaining
elements serves to expose the significant and useful proportion of
the oriented reinforcing fibrous and/or filamentary components to
the external environment. In addition, the exposure of the
reinforcing fibrous and/or filamentary components allows for
optimal penetration of the cementitous mixture into the
reinforcement structure and an increase in surface area for the
cementitous mixture to hold on to upon drying. In order to further
increase the amount of surface area available to the cementitous
mixture, the reinforcing fibrous or filamentary components and/or
the circumferential retaining elements of the reinforcement
structure may have a textured surface or raised surface asperities,
such as nubs.
[0022] In accordance with the present invention, the reinforcing
fibrous and/or filamentary components may also be of infinite
length, whereby one or more circumferential retaining elements
circumscribe about the overall circumference of the continuous
reinforcing fibrous and/or filamentary components. Upon final
formation of the reinforcement structure, the continuous structure
can be readily packaged through an automatic packaging system or
containerized in bulk. A continuous formation of the reinforcement
structure allows the reinforcement structure to be available in a
continuous roll form or packaged in a continuous lap or coil
formation to be cut to desired lengths. Further, the reinforcement
structure may comprise a series of segmented weakened points along
the continuous formation so that the desired portion may be
selected and detracted from the remainder of the roll form.
[0023] It should be noted that the reinforcing fibrous and/or
filamentary components, as well as the resulting reinforcement
structure, can be further treated with performance modifying
additives, such as represented by the topical application of a
material flow-enhancing lubricant and additional temporary binding
agents, such as supplimental water-soluble chemistries and
pro-degradants.
[0024] From the foregoing, it will be observed that numerous
modifications and variations can be affected without departing from
the true spirit and scope of the novel concept of the present
invention. It is to be understood that no limitation with respect
to the specific embodiments illustrated herein is intended or
should be inferred. The disclosure is intended to cover, by the
appended claims, all such modifications as fall within the scope of
the claims.
* * * * *