U.S. patent application number 12/168349 was filed with the patent office on 2008-10-30 for pipe/connector weld joint, and methods of welding same.
This patent application is currently assigned to Grant Prideco, L.P.. Invention is credited to Richard Lyell Holdren.
Application Number | 20080264909 12/168349 |
Document ID | / |
Family ID | 34102805 |
Filed Date | 2008-10-30 |
United States Patent
Application |
20080264909 |
Kind Code |
A1 |
Holdren; Richard Lyell |
October 30, 2008 |
Pipe/Connector Weld Joint, and Methods of Welding Same
Abstract
The present invention is directed to a method for welding a pipe
section and a connector, wherein each of the pipe and connector
have inner and outer beveled surfaces and the joint is comprised of
an angular alignment land. In one embodiment, an outer beveled
surface on the pipe and an inner beveled surface on the connector
cooperate to define the angular alignment land. In yet another
illustrative embodiment, the inner beveled surface of the connector
and the outer beveled surface of the pipe have a bevel angle of
approximately 30 degrees, while the outer beveled surface of the
connector and the inner beveled surface of the pipe have a beveled
angle of approximately 45 degrees.
Inventors: |
Holdren; Richard Lyell;
(Lancaster, OH) |
Correspondence
Address: |
JEFFREY E. DALY;GRANT PRIDECO, L.P.
400 N. SAM HOUSTON PARKWAY EAST, SUITE 900
HOUSTON
TX
77060
US
|
Assignee: |
Grant Prideco, L.P.
|
Family ID: |
34102805 |
Appl. No.: |
12/168349 |
Filed: |
July 7, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10546348 |
Apr 11, 2006 |
|
|
|
PCT/US04/23329 |
Jul 20, 2004 |
|
|
|
12168349 |
|
|
|
|
60488931 |
Jul 21, 2003 |
|
|
|
Current U.S.
Class: |
219/61 |
Current CPC
Class: |
B23K 9/0286 20130101;
B23K 9/16 20130101; B23K 9/0284 20130101; B23K 2101/06 20180801;
B23K 33/006 20130101; B23K 9/18 20130101; F16L 13/02 20130101 |
Class at
Publication: |
219/61 |
International
Class: |
B23K 31/02 20060101
B23K031/02 |
Claims
1. A method, comprising: positioning a connector adjacent an end of
a pipe, said connector and said pipe adapted to be welded together
in a gas metal arc welding process at a weld joint, wherein said
weld joint has only a single inner beveled surface, only a single
outer beveled surface, and an angular alignment land; and
performing a single interior welding pass to fill the weld joint at
the inner beveled surface, and; performing a single interior
exterior welding pass to fill the weld joint at the outer beveled
surface, to weld said connector to said pipe at said weld
joint.
2. The method of claim 1, wherein said connector is comprised of an
internally threaded box.
3. The method of claim 1, wherein said connector is comprised of an
externally threaded pin.
4. The method of claim 1, wherein said angular alignment land has a
radial thickness ranging from 0.25-0.375 inches.
5. The method of claim 1, wherein said angular self-alignment land
begins at a point that is radially offset 0.125-0.25 inches from an
internal cylindrical surface of said pipe.
6. The method of claim 1, wherein said angular alignment land
begins at a point that is radially offset 0.125-0.25 inches from an
external cylindrical surface of said pipe.
7. The method of claim 1, wherein said angular alignment land is
formed at an angle ranging from 25 to 50 degrees on either side of
a line normal to a longitudinal centerline of said pipe.
8. The method of claim 1, wherein said angular alignment land is
defined by an engagement between said outer beveled surface of said
pipe and said inner beveled surface of said connector.
9. The method of claim 1, wherein said angular alignment land is
defined by an engagement between said outer beveled surface of said
connector and said inner beveled surface of said pipe.
10. The method of claim 1, further comprising performing the
submerged arc welding process on the interior portion of said weld
joint at an amperage ranging from approximately 480-510 amps and at
a voltage ranging from approximately 36-38 volts; and, performing
the submerged arc welding process welding pass on an exterior
portion of said weld joint, at an amperage ranging from
approximately 675-700 amps and at a voltage ranging from
approximately 36-38 volts.
11. The method of claim 10, wherein said connector is comprised of
an internally threaded box.
12. The method of claim 10, wherein said connector is comprised of
an externally threaded pin.
13. The method of claim 10, wherein said angular alignment land has
a radial thickness ranging from 0.25-0.375 inches.
14. The method of claim 10, wherein said angular self-alignment
land begins at a point that is radially offset 0.125-0.25 inches
from an internal cylindrical surface of said pipe.
15. The method of claim 10, wherein said angular alignment land
begins at a point that is radially offset 0.125-0.25 inches from an
external cylindrical surface of said pipe.
16. The method of claim 10, wherein said angular alignment land is
formed at an angle ranging from 25 to 50 degrees on either side of
a line normal to a longitudinal centerline of said pipe.
17. The method of claim 10, wherein said angular alignment land is
defined by an engagement between said outer beveled surface of said
pipe and said inner beveled surface of said connector.
18. The method of claim 10, wherein said angular alignment land is
defined by an engagement between said outer beveled surface of said
connector and said inner beveled surface of said pipe.
Description
[0001] This application is a divisional application of U.S. Ser.
No. 10/546,348, filed on Apr. 11, 2006, presently pending, and
incorporated by reference herein for all it discloses.
BACKGROUND OF THE INVENTION
[0002] 1. Field of the Invention
[0003] The present invention is generally directed to the field of
tubular structures, and, more particularly, to a novel joint design
between a tubular component and a connector and a method of welding
same.
[0004] 2. Description of the Related Art
[0005] In the oilfield industry, many separate lengths of pipe are
coupled together to create, in some cases, very long conduit
structures. Such structures may be used for a variety of purposes,
e.g., transportation of oil and gas, lining of wells, etc.
Typically, each section of pipe is provided with a threaded pin
connector (male connector) on one end and a threaded box connector
(female connector) on the other end. Pipe sections are coupled to
one another by threadingly engaging the pin connector on one
tubular with a box connector on another tubular. This process is
continued until the desired length of the structure is
completed.
[0006] In some cases, a section of pipe is provided and the pin and
box connectors are welded onto the opposite ends of the pipe. The
diameter of the pipe may vary depending on the particular
application, e.g., 20'', 26'', 30'', etc. The wall thickness of the
pipe may also vary depending upon the particular application, i.e.,
the wall thickness may vary between approximately 0.438-2.0
inches.
[0007] As indicated in FIG. 1, in some cases, the joint 10 between
the pipe 12 and the connector 14 was a single bevel joint in which
the standard pipe joint bevel of approximately 30 degrees was
provided on both components. The longitudinal centerline 13 of the
pipe 12 is schematically depicted in FIG. 1 as are exterior
surfaces 18 and interior surfaces 20 of the pipe 12 and connector
14. Also depicted in FIG. 1 is a vertical land 15 formed on both
the pipe 12 and the connector 14. Typically, the joint 10 was
filled by performing one or more welding passes from the outside of
the joint 10.
[0008] Joining the pipe 12 and connector 14 using the joint 10
configuration depicted in FIG. 1 presented several problems. For
example, especially with large diameter piping, obtaining axial
alignment between the pipe 12 and the connector 14 was a very
difficult and time-consuming process due to a variety of reasons,
e.g., the pipe and/or connector being out-of-round, the weight and
stiffness of the pipe 12 and connector 14, waviness in the pipe 12,
etc. Typically, prior art techniques for axially aligning the pipe
12 and connector 14 might involve welding on various clips and
manipulating the pipe 12 and/or connector 14 until such time as the
proper axial alignment was achieved. Such manipulation of the
components was very difficult due to, among other things, the
physical size and weight of the pipe 12 and the connector 14.
Thereafter, prior art welding processes often involved tack welding
the joint 10 at several locations around the perimeter of the joint
10, followed by performing a MIG welding process to lay down a
relatively small weld bead in the joint 10 at the root 19.
Thereafter, the joint 10 was completed by performing any of a
variety of known welding processes to completely fill the joint 10.
Due to the volume of the joint 10, it typically took several
passes, i.e., multiple weld beads, to completely fill the joint
10.
[0009] The present invention is directed to a device and various
methods that may solve, or at least reduce, some or all of the
aforementioned problems.
BRIEF SUMMARY OF THE INVENTION
[0010] In one illustrative embodiment, the present invention is
directed to a pipe section and a connector that are adapted to be
welded together, wherein each of the pipe and connector have inner
and outer beveled surfaces and the joint is comprised of an angular
alignment land. In one embodiment, an outer beveled surface on the
pipe and an inner beveled surface on the connector cooperate to
define the angular alignment land. In yet another illustrative
embodiment, the inner beveled surface of the connector and the
outer beveled surface of the pipe have a bevel angle of
approximately 30 degrees, while the outer beveled surface of the
connector and the inner beveled surface of the pipe have a beveled
angle of approximately 45 degrees.
[0011] In another illustrative embodiment, the present invention is
directed to a method of welding a pipe and a connector together,
wherein the joint may be completely welded by performing a single
weld pass on the interior of the weld joint and by performing a
single weld pass on the exterior of the joint. In some cases, e.g.,
for pipe having a wall thickness in excess of one inch, the outer
portion of the weld joint may be filled by performing multiple
welding passes. In another illustrative embodiment, the present
invention is directed to a product that is formed by performing the
welding method described above to join a pipe end to a
connector.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] The invention may be understood by reference to the
following description taken in conjunction with the accompanying
drawings, in which like reference numerals identify like elements,
and in which:
[0013] FIG. 1 is a cross-sectional depiction of an illustrative
prior art weld joint between a pipe and a connector.
[0014] FIG. 2 is a schematic view of an illustrative tubular
component having connectors attached thereto in accordance with one
illustrative embodiment of the present invention.
[0015] FIGS. 3A-3B are cross-sectional views depicting various
details of a weld joint between a pipe and a connector in
accordance with one illustrative embodiment of the present
invention.
[0016] FIGS. 4A-4C depict illustrative embodiments of a welding
process that may be employed in accordance with the present
invention to fill various illustrative weld joints.
[0017] FIGS. 5A-5B depict one illustrative technique for forming
the inner beveled surface of the pipe in accordance with one aspect
of the present invention.
[0018] While the invention is susceptible to various modifications
and alternative forms, specific embodiments thereof have been shown
by way of example in the drawings and are herein described in
detail. It should be understood, however, that the description
herein of specific embodiments is not intended to limit the
invention to the particular forms disclosed, but on the contrary,
the intention is to cover all modifications, equivalents, and
alternatives falling within the spirit and scope of the invention
as defined by the appended claims.
DETAILED DESCRIPTION OF THE INVENTION AND THE PREFERRED
EMBODIMENT
[0019] Illustrative embodiments of the invention are described
below. In the interest of clarity, not all features of an actual
implementation are described in this specification. It will, of
course, be appreciated that in the development of any such actual
embodiment, numerous implementation-specific decisions must be made
to achieve the developers' specific goals, such as compliance with
system-related and business-related constraints, which will vary
from one implementation to another. Moreover, it will be
appreciated that such a development effort might be complex and
time-consuming, but would nevertheless be a routine undertaking for
those of ordinary skill in the art having the benefit of this
disclosure.
[0020] The present invention will now be described with reference
to the attached drawings which are included to describe and explain
illustrative examples of the present invention. The words and
phrases used herein should be understood and interpreted to have a
meaning consistent with the understanding of those words and
phrases by those skilled in the relevant art. No special definition
of a term or phrase, i.e., a definition that is different from the
ordinary and customary meaning as understood by those skilled in
the art, is intended to be implied by consistent usage of the term
or phrase herein. To the extent that a term or phrase is intended
to have a special meaning, i.e., a meaning other than that
understood by skilled artisans, such a special definition will be
expressly set forth in the specification in a definitional manner
that directly and unequivocally provides the special definition for
the term or phrase.
[0021] As indicated in the background section of the application,
tubular components 22 are provided with connectors, such that they
may be coupled to other tubular components. FIG. 2 depicts an
illustrative pipe section 20 comprised of a length of pipe 22, a
female connector 24 having an internally threaded box connection 25
and a male connector having an externally threaded pin connection
27. The connectors 24 and 27 are coupled to the pipe 22 using weld
joints 30 in accordance with the present invention. Pipe sections
20 may be coupled to one another via engagement of the threaded
connections on adjacent pipe sections 20.
[0022] As will be understood by those skilled in the art after a
complete reading of the present application, the present invention
is not limited to use with any particular type of tubular
components or with any particular type of connector 24, 26. For
example, the present invention may be employed using API line pipe
governed by API Specification 5L (Forty-second edition, January
2000) which is hereby incorporated by reference in its entirety.
The connectors 24, 26 may employ any type or size of threads. Thus,
the illustrative examples depicted herein should not be considered
a limitation of the present invention unless such limitations are
expressly recited in the appended claims.
[0023] Details and associated geometry of the weld joints 30 in
accordance with illustrative embodiments of the present invention
will now be described with reference to FIGS. 3A-3B wherein an
illustrative pipe 22 is adapted to be welded to a generic connector
40, which may be threaded or not. In FIGS. 3A-3B, a longitudinal
axis or centerline 75 of the pipe 22 is depicted. In the lower
portions of FIGS. 3A-3B, the pipe 22 and the connector 40 are
depicted in an axially spaced-apart relationship, whereas in the
upper portions of FIGS. 3A-3B, the pipe 22 and the connector 40 are
depicted in an illustrative engaged position. As set forth above,
the pipe 22 should be understood to be any type of pipe and the
connector 40 should be understood to be any type of connector. In
general, the details of the weld joint 30, i.e., geometry and
dimensions, may vary depending upon the wall thickness 32 of the
pipe 22. The pipe 22 has an inner surface 22I and an outer surface
22O. Similarly, the connector 40 has an inner surface 40I and an
outer surface 40O. In the illustrative embodiment, the pipe 22 has
an outer beveled surface 31 and an inner beveled surface 33. The
connector 40 has an outer beveled surface 41 and an inner beveled
surface 43. In joints 30 wherein the wall thickness 32 is greater
than 1.375 inches, the connector 40 may have a secondary outer
beveled surface 45 (see FIG. 3D).
[0024] In the illustrative embodiments depicted in FIGS. 3A-3B, the
pipe outer beveled surface 31 and connector inner beveled surface
43 are beveled at an angle 42 of approximately 30 degrees.+-.5
degrees with respect to a line 50 normal to the longitudinal
centerline 75 of the pipe 22. However, the included angular
misalignment of the mating surfaces 31, 43 should generally be
small enough after mating to prevent blowthrough, typically less
than approximately 2 degrees. Therefore, in a preferred embodiment,
the angle 42 is approximately 30 degrees.+-.1 degree. The pipe
inner beveled surface 33 and connector outer beveled surface 41 are
beveled at an angle 44 of approximately 45 degrees.+-.5 degrees
with respect to the line 50. In the depicted embodiment, the
surfaces 31 and 43 have the same bevel angle and the surfaces 33
and 41 have the same bevel angle although that is not required in
all embodiments of the present invention. For the embodiments where
the wall thickness 32 is greater than 1.375 inches, the secondary
outer beveled surface 45 is beveled at an angle 46 of approximately
15 degrees.+-.5 degrees with respect to a normal line 50. The
secondary outer beveled surface 45 is provided to, among other
things; reduce the volume of the weld joint 30. As such, the
secondary outer beveled surface 45 may not be required in all
embodiments of the present invention.
[0025] In the illustrative embodiments depicted in FIGS. 3A-3B, the
pipe inner beveled surface 33 has a radial dimension 51
approximately 0.25 inches, and the connector inner beveled surface
43 has a radial dimension 53 of approximately 0.50 inches. If
employed, the secondary outer beveled surface 45 may begin at a
radial dimension 55 of approximately 1.25 inches from the inner
surface 401 of the connector 40. Of course, these dimensions may
vary depending upon the particular application.
[0026] As depicted in FIGS. 3A-3B, in one illustrative embodiment,
the weld joint 30 of the present invention has an angular alignment
land 60 with an illustrative radial thickness 61 of approximately
0.25 inches. The radial thickness 61 of the angular alignment
surface 60 may vary from approximately 0.25-0.375 inches depending
upon the particular application. That is, the angular alignment
land 60 is positioned at an angle, relative to the line 50, that
may vary from, for example, approximately 25-50 degrees on either
side of the line 50. In general, as the angle 42 gets larger
(relative to the line 50) the self-alignment capabilities of the
joint 30 tend to increase, but at some point the ability to achieve
complete weld penetration of the joint 30 becomes more difficult
also. Thus, these competing concerns must be addressed for each
particular application.
[0027] In one illustrative embodiment, for pipes 22 having a wall
thickness 32 of 0.75 inches or greater, the joint 30 is configured
such that the angular alignment land 60 begins at a radial location
65 that is approximately 0.25 inches from the inner surface 221 of
the pipe 22. However, depending on the particular application, the
radial location 65 may vary. For example, for pipes 22 having a
wall thickness 32 of approximately 0.50 inches, the radial location
65 may be approximately 0.125 inches from the inner surface 221 of
the pipe 22.
[0028] For pipes 22 having a wall thickness 32 less than one inch,
the angular alignment land 60 is also provided, and it may also
have a radial thickness 61 of approximately 0.25 inches. For such
relatively thin-walled pipe 22, the angular alignment surface 60
may be positioned at approximately mid-thickness of the pipe 22.
For example, for a pipe thickness 32 of 0.500 inches, the radial
dimension 51 (see FIG. 3A) of the pipe inner beveled surface 33 may
be 0.125 inches, thereby leaving an additional 0.25 inches of
thickness beyond the height 61 of the angular alignment land 60.
(0.125'' internal bevel height+0.25 inches angular alignment land
thickness+0.125'' outer bevel height=0.50'' total pipe well
thickness). The precise values would, of course, vary depending
upon the particular application. However, it is envisioned that in
at least some embodiments the angular alignment land 60 would
usually have a radial thickness 61 ranging from approximately
0.25-0.375 inches. It should also be understood that in relatively
thin-walled pipes 22, the position of the angular alignment land 60
within the wall of the pipe may vary, i.e., it need not be
positioned at the mid-thickness of the pipe 22 in all
situations.
[0029] The angular alignment land 60 provides many benefits with
respect to the alignment of the pipe 22 and the connector 40. For
example, in the depicted embodiment, due to the interaction of the
pipe outer beveled surface 31 and the connector inner beveled
surface 43 of the connector 40, the pipe 22 and connector 40 tend
to self-align themselves (in an axial direction) when they are
axially urged together with sufficient force. Such force may be
applied by a variety of techniques.
[0030] Once the weld joint 30 is properly aligned, both axially and
circumferentially, the joint 30 may be welded using a variety of
known techniques, such as, for example, submerged arc welding
(SAW), gas metal arc welding (GMAW) or SAW in combination with GMAW
techniques. The joint 30 may be welded using the practices and
procedures described in API's specification entitled "Welding
Connectors to Pipe" (API Recommended Practice 5C6, First Edition,
December 1996), which is hereby incorporated by reference in its
entirety.
[0031] For pipes 22 having a wall thickness 32 less than or equal
to one inch, the design of the joint 30 is such that it may be
welded together using a welding process wherein a single pass is
made on the inside of the joint 30 and, thereafter, a single pass
is made from the outside of the joint 30. That is, such joints 30
may, in some embodiments of the present invention, be completed by
performing only two welding passes, one from the inside, one from
the outside. For pipes 22 having a wall thickness 32 greater than
one inch, the inner portion of the joint 30 may be filled with a
single weld pass, like that described above. However, the outer
portion of the weld joint 30 may require multiple welding passes to
completely fill the outer portion of the joint 30 due to its
increased volume.
[0032] One illustrative welding process that may be employed to
weld the joint 30 will be described with more detail with reference
to FIGS. 4A and 4B. FIG. 4A depicts an illustrative joint 30
wherein the thickness 32 of the pipe 22 is less than or equal to
one inch. The intersection between the outer beveled surface 41 of
the connector 40 and the outer beveled surface 31 of the pipe 22
defines an outer root 65 of the joint 30. The intersection of the
inner beveled surface 33 of the pipe 22 and the inner beveled
surface 43 of the connector 40 defines an inner root 67 of the
joint 30.
[0033] As indicated previously, in one illustrative embodiment of
the present invention, a single inner weld bead 70 may be used to
fill the inner portion of the joint 30 using a SAW process. The
longitudinal axis of the pipe 22 is indicated by the line 75. The
bead 70 may be formed by welding approximately 370 degrees around
the interior of the joint 30. The additional 10 degrees of
circumferential weld is provided to stitch or overlap the start
point of the weld bead 70. The amperage employed to produce the
weld bead 70 may be reduced in the area of overlap so as not to
result in a localized spot of excessive reinforcement. The initial
weld bead 70 should be formed using a process that provides
sufficient energy such that the penetration of the weld bead 70, as
indicated by dashed line 71, approaches, but does not burn through,
the outer root 65 of the joint 30 to the point where the resulting
weld joint 30 is defective. In some cases, the weld bead 70 will be
formed such that the penetration of the weld bead 70 approaches 50%
of the wall thickness 32 of the pipe 22.
[0034] The next process of this illustrative embodiment of the
present invention involves forming an outer weld bead 72 in the
outer portion of the joint 30 as depicted in FIG. 4B. The weld bead
72 may be formed using a welding process, for example, a SAW
process, in a single pass that is performed approximately 370
degrees around the exterior circumference of the joint 30. The
penetration of the illustrative weld bead 72 is schematically
depicted by the dashed line 73. Due to the presence of the weld
bead 70, the process used to form the weld bead 72 may be performed
at a relatively high energy level to insure full penetration of the
completed joint 30.
[0035] In one illustrative embodiment, the joint 30 may be
completed using the following illustrative SAW welding procedures.
The illustrative welding procedures are described for a joint 30
between a pipe 22 (API 5L X56) having a diameter of 20 inches and a
wall thickness of 0.812 inches, and a connector 40 (ASTM A694 F70).
The joint 30 is provided with an angular alignment land 60 with a
radial thickness 61 of approximately 0.25 inches and the beveled
angles 42, 44 (see FIGS. 3A-3B) are approximately 30 and 45
degrees, respectively. In this particularly illustrative example,
the joint 30 may be completed by performing a single SAW weld pass
on the interior of the joint 30 and by performing a single SAW weld
pass on the exterior of the joint 30. The SAW process performed to
fill the interior of the joint 30 may be performed at approximately
480-510 amps, approximately 36-38 volts and at a travel speed of
approximately 14-15 inches per minute. In one very particular
embodiment, the first pass may be performed on the interior of the
joint 30 at approximate 480 amps, approximately 37 volts and at a
travel speed of approximately 14 inches per minute. The SAW process
performed to fill the exterior portion of the joint 30 may be
performed at approximately 675-700 amps, approximately 36-39 volts,
and at a travel speed ranging from approximately 16.5-17.5 inches
per minute. In one very particular embodiment, the SAW process to
fill the exterior portion of the joint 30 may be performed at
approximately 675 amps, approximately 37 volts and at a travel
speed of approximately 16.5 inches per minute. The welding is
performed in the flat (horizontal) position while the work pieces
are rotated. No preheat or post weld heat treatment was performed
in this particular application, although such heat treating process
may be required in other applications. The weld interpass
temperature is approximately 450 F. In one particular embodiment,
the joint 30 may be welded using 3/32 inch diameter Lincoln L-56
wire with 880M flux wherein the typical electrode stick out is
approximately 1.125 inches. In performing the SAW process to fill
the exterior portion of the joint 30, the electrode may be offset
from the centerline of the joint 30 by approximately 1 inch.
However, it should be understood that the above details regarding
the SAW welding procedures are illustrative in nature. Thus, the
present invention should not be limited to such details unless they
are specifically set forth in the appended claims.
[0036] Although a process has been disclosed wherein the joint 30
depicted in FIG. 4A may be completed by performing single weld
passes from both the inside and outside of the joint 30, the
present invention is not limited to such a process. That is, the
novel configuration of the joint 30, as defined by the detailed
geometry of the pipe surfaces 31, 33 and connector surfaces 41, 43,
may be welded together using other welding processes and
techniques. For example, the inner portion of the joint 30 may be
filled with two or more weld beads instead of the single weld bead
70 depicted in FIG. 4A.
[0037] FIG. 4C depicts an illustrative joint 30 wherein the
thickness 32 of the pipe 22 is greater than one inch. In one
illustrative embodiment, the inner portion of the joint 30 depicted
in FIG. 4C may be filled with a single weld bead 70 using a welding
process as described above with reference to FIG. 4A. Due to its
relatively large volume, the outer portion of the joint 30 in FIG.
4C may be filled with multiple weld beads by performing multiple
welding passes or using multiple welding tools. For example, the
outer portion of the joint 30 may be filled using four weld beads
81, 82, 83 and 84 that are sequentially deposited using any of a
variety of welding techniques. During the formation of the first
weld bead 81, the energy of the welding process may be increased to
insure complete penetration of the joint 30. In fact, the first
weld bead 81 may be applied at a relatively high energy due to the
presence of the previously formed weld bead 70 on the inner portion
of the joint 30.
[0038] The various beveled surfaces 31, 33, 41, 43 on pipe 22 and
connector 40 may be formed by a variety of techniques, e.g.,
machining, cutting, grinding, arc gouging, torch cutting, etc. The
surface finish on the various beveled surfaces, e.g., 31, 33, 41,
43 may be approximately 250 RMS. In one particular embodiment, as
indicated in FIG. 5A, the pipe 22 may be purchased with an industry
standard 30.quadrature. bevel and vertical land 87. Thereafter, the
inner beveled surface 33 (indicated in dashed lines 88 in FIG. 5A)
may be formed by removing the vertical land 87 and the adjacent
material 89 as indicated in FIGS. 5A-5B. That is, an internal
chamfer may be formed on standard API pipe to define the inner
beveled surface 33. As set forth above, any technique may be
employed to remove the land 87 and the adjacent material 89 to
thereby define the inner beveled surface 33. Moreover, it will be
understood by those skilled in the art after reading the present
application that the beveled surfaces formed on the pipe 22 and
connector 40 could, if desired, be reversed. That is, the beveled
surfaces 41, 43 formed on the connector 40 could be formed on the
pipe 22, and the beveled surfaces 31, 33 formed on the pipe 22
could be formed on the connector 40. Moreover, the present
invention may also be employed in situations when the joint 30 is
inverted, i.e., the beginning radial location of the angular
alignment land 60 may be positioned approximately 0.25-0.375 inches
from the outer surface 220 of the pipe 22. Thus, the present
invention should not be considered as limited to the illustrative
embodiments and configurations depicted herein unless such
limitations are expressly recited in the pending claims.
[0039] The present invention is generally directed to a novel weld
joint that may be used to join tubular components, such as, for
example, a connector and a pipe and to various novel methods of
welding such components together. In one illustrative embodiment,
the present invention is directed to a device comprised of a pipe
and a connector adapted to be welded to the pipe at a weld joint,
wherein the pipe and the connector each have an inner beveled
surface and an outer beveled surface, and wherein the weld joint
has an angular alignment land. In another illustrative embodiment,
the present invention is directed to a method comprised of
positioning a connector adjacent an end of a pipe to which it is
adapted to be welded at a weld joint, wherein the pipe and the
connector each have an inner beveled surface and an outer beveled
surface, and wherein the weld joint has an angular alignment land,
and performing at least one welding process to weld the connector
to the pipe at the weld joint. In another illustrative embodiment,
the present invention is directed to a method wherein the weld
joint is completed by performing at least one welding pass to fill
an interior portion of the weld joint, and performing at least one
welding pass to fill an exterior portion of the weld joint. In yet
another illustrative embodiment, the present invention is directed
to a method wherein the welding is accomplished by performing a
first single welding pass to fill an interior portion of the weld
joint, and performing a second single welding pass to fill an
exterior portion of the weld joint. In yet a further embodiment,
the present invention is directed to a method comprised of
performing a first single welding pass to fill an interior portion
of the weld joint, and performing a plurality of welding passes to
fill an exterior portion of the weld joint.
[0040] The particular embodiments disclosed above are illustrative
only, as the invention may be modified and practiced in different
but equivalent manners apparent to those skilled in the art having
the benefit of the teachings herein. For example, the process steps
set forth above may be performed in a different order. Furthermore,
no limitations are intended to the details of construction or
design herein shown, other than as described in the claims below.
It is therefore evident that the particular embodiments disclosed
above may be altered or modified and all such variations are
considered within the scope and spirit of the invention.
Accordingly, the protection sought herein is as set forth in the
claims below.
[0041] Whereas the present invention has been described in
particular relation to the drawings attached hereto, it should be
understood that other and further modifications apart from those
shown or suggested herein, may be made within the scope and spirit
of the present invention.
* * * * *