U.S. patent application number 12/074804 was filed with the patent office on 2008-10-30 for production of nanostructure by curie point induction heating.
This patent application is currently assigned to Board of Trustees of the University of Arkansas. Invention is credited to Alexandru Radu Biris, Alexandru Sorin Biris, Dan Alexander Buzatu, Jerry A. Darsey, Dan Lupu, Dwight Wayne Miller, Jon Gardner Wilkes.
Application Number | 20080264330 12/074804 |
Document ID | / |
Family ID | 46325155 |
Filed Date | 2008-10-30 |
United States Patent
Application |
20080264330 |
Kind Code |
A1 |
Wilkes; Jon Gardner ; et
al. |
October 30, 2008 |
Production of nanostructure by curie point induction heating
Abstract
An apparatus for synthesizing nanostructures. In one embodiment,
the apparatus includes a heating device that defines a reaction
zone therein and a susceptor made of a ferromagnetic material with
a Curie temperature and placed in the reaction zone, where the
Curie temperature substantially corresponds to a temperature at
which the growth of desired nanostructures occurs and the heating
device is capable of heating the susceptor substantially at the
Curie temperature.
Inventors: |
Wilkes; Jon Gardner; (Little
Rock, AR) ; Buzatu; Dan Alexander; (Little Rock,
AR) ; Miller; Dwight Wayne; (Whitehall, AR) ;
Biris; Alexandru Sorin; (Little Rock, AR) ; Biris;
Alexandru Radu; (Cluj Napoca, RO) ; Lupu; Dan;
(Cluj Napoca, RO) ; Darsey; Jerry A.; (Little
rock, AR) |
Correspondence
Address: |
MORRIS MANNING MARTIN LLP
3343 PEACHTREE ROAD, NE, 1600 ATLANTA FINANCIAL CENTER
ATLANTA
GA
30326
US
|
Assignee: |
Board of Trustees of the University
of Arkansas
Little Rock
AR
|
Family ID: |
46325155 |
Appl. No.: |
12/074804 |
Filed: |
March 6, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11302986 |
Dec 14, 2005 |
7365289 |
|
|
12074804 |
|
|
|
|
11228023 |
Sep 15, 2005 |
|
|
|
11302986 |
|
|
|
|
11131912 |
May 18, 2005 |
|
|
|
11228023 |
|
|
|
|
60638243 |
Dec 21, 2004 |
|
|
|
60611018 |
Sep 17, 2004 |
|
|
|
60571999 |
May 18, 2004 |
|
|
|
60611018 |
Sep 17, 2004 |
|
|
|
60571999 |
May 18, 2004 |
|
|
|
60638243 |
Dec 21, 2004 |
|
|
|
Current U.S.
Class: |
117/3 ; 117/200;
219/634 |
Current CPC
Class: |
B82Y 30/00 20130101;
B01J 8/0015 20130101; B01J 8/087 20130101; B82Y 40/00 20130101;
H05B 6/108 20130101; B01J 12/007 20130101; Y10S 977/844 20130101;
B01J 8/0285 20130101; B01J 23/88 20130101; B01J 23/755 20130101;
B01J 23/44 20130101; C01B 32/162 20170801; B01J 8/1836 20130101;
C23C 16/46 20130101; B01J 2208/00469 20130101; B01J 2208/0084
20130101; B01J 8/1845 20130101; H05B 2206/023 20130101; B01J 8/12
20130101; Y10T 117/10 20150115; B01J 8/40 20130101; B01J 2208/00557
20130101; Y10S 977/90 20130101 |
Class at
Publication: |
117/3 ; 117/200;
219/634 |
International
Class: |
C30B 11/00 20060101
C30B011/00; H05B 6/10 20060101 H05B006/10 |
Claims
1. An apparatus for synthesizing nanostructures, comprising: a. a
heating device defines a reaction zone therein; and b. a susceptor
made of a ferromagnetic material having a characteristic
temperature and placed in the reaction zone, wherein the heating
device is capable of heating the susceptor substantially at the
characteristic temperature.
2. The apparatus of claim 1, wherein the characteristic temperature
corresponds to a temperature at which the growth of desired
nanostructures occurs.
3. The apparatus of claim 2, wherein the characteristic temperature
is substantially equal to a Curie temperature of the ferromagnetic
material.
4. The apparatus of claim 1, wherein the heating device comprises
an inductively heating device.
5. The apparatus of claim 4, wherein the inductively heating device
comprises an inductor coil.
6. The apparatus of claim 5, wherein the inductor coil is
electrically coupled to an alternating current (AC) power
supply.
7. The apparatus of claim 6, wherein the inductor coil is
configured such that, in operation, it allows an alternating
current to pass through to generate an electromagnetic field with a
radio frequency (RF) in the reaction zone to heat the susceptor
substantially at the characteristic temperature.
8. The apparatus of claim 1, wherein the susceptor comprises a foil
or plate of the ferromagnetic material, and wherein the foil or
plate has a surface for nanostructures to grow on the surface.
9. The apparatus of claim 8, wherein the foil or plate of the
ferromagnetic material is coated with a non-magnetic conductive
material.
10. The apparatus of claim 9, wherein the non-magnetic conductive
material comprises gold or chromium.
11. The apparatus of claim 8, wherein the susceptor is mounted on
an ultra-low heat conductivity/capacity insulator.
12. The apparatus of claim 11, wherein the ultra-low heat
conductivity/capacity insulator is made of silicate.
13. The apparatus of claim 1, wherein the susceptor comprises a bed
of powders made from the ferromagnetic material.
14. The apparatus of claim 13, wherein each of the powders is
coated with a catalyst and support materials.
15. The apparatus of claim 1, further comprising a chamber having a
first end, an opposite, second end, and a body portion defined
therebetween.
16. The apparatus of claim 15, wherein the heating device is formed
on the exterior surface of the body portion of the chamber such
that the reaction zone is defined inside the chamber.
17. An apparatus for synthesizing nanostructures, comprising a
susceptor made of a ferromagnetic material having a characteristic
temperature.
18. The apparatus of claim 17, further comprising a heating device
for heating the susceptor substantially at the characteristic
temperature.
19. The apparatus of claim 17, wherein the characteristic
temperature corresponds to a temperature at which the growth of
desired nanostructures occurs.
20. The apparatus of claim 19, wherein the characteristic
temperature is substantially equal to a Curie temperature of the
ferromagnetic material.
21-39. (canceled)
Description
CROSS-REFERENCE TO RELATED PATENT APPLICATION
[0001] This application is a continuation-in-part of U.S. patent
application Ser. No. 11/228,023, filed Sep. 15, 2005, entitled
"APPARATUS AND METHODS FOR SYNTHESIS OF LARGE SIZE BATCHES OF
CARBON NANOSTRUCTURES," by Alexandru Sorin Biris, Alexandru Radu
Biris, Dan Lupu, Jon Gardner Wilkes, Dan Alexander Buzatu, Dwight
Wayne Miller, and Jerry A. Darsey (hereinafter the "'023
application"), the disclosure of which is hereby incorporated
herein by reference in its entirety. The status of the '023
application is pending and itself claims the benefit, pursuant to
35 U.S.C. .sctn.119(e), of U.S. provisional patent application Ser.
No. 60/611,018, filed Sep. 17, 2004, entitled "APPARATUS AND
METHODS FOR SYNTHESIS OF LARGE SIZE BATCHES OF CARBON
NANOSTRUCTURES," by Alexandru Sorin Biris, Dan Alexander Buzatu,
Alexandru Radu Biris, Jon Gardner Wilkes, Dwight Wayne Miller,
Jerry A. Darsey, and Dan Lupu. The '023 application also is a
continuation-in-part of U.S. patent application Ser. No.
11/131,912, filed May 18, 2005, entitled "APPARATUS AND METHODS OF
MAKING NANOSTRUCTURES BY INDUCTIVE HEATING," by Alexandru Radu
Biris, Dan Lupu, Alexandru Sorin Biris, Jon Gardner Wilkes, Dan
Alexander Buzatu, Dwight Wayne Miller, and Jerry A. Darsey
(hereinafter the "'912 application"). The status of the '912
application is pending and itself claims the benefit, pursuant to
35 U.S.C. .sctn. 119(e), of U.S. provisional patent application
Ser. No. 60/571,999, filed May 18, 2004, entitled "APPARATUS AND
METHODS OF HIGH THROUGHPUT GENERATION OF NANOSTRUCTURES BY
INDUCTIVE HEATING AND IMPROVEMENTS INCREASING PRODUCTIVITY WHILE
MAINTAINING QUALITY AND PURITY," by Alexandru Radu Biris, Dan Lupu,
Alexandru Sorin Biris, Jon Gardner Wilkes, Dan Alexander Buzatu,
Dwight Wayne Miller, and Jerry A. Darsey.
[0002] This application also claims the benefit, pursuant to 35
U.S.C. .sctn.119(e), of U.S. provisional patent application Ser.
No. 60/638,243, filed Dec. 21, 2004, entitled "PRODUCTION OF
NANOSTRUCTURES BY CURIE POINT INDUCTION HEATING," by Jon Gardner
Wilkes, Dan Alexander Buzatu, Dwight Wayne Miller, Alexandru Sorin
Biris, Alexandru Radu Biris, Dan M. Lupu, and Jerry A. Darsey,
which is incorporated herein by reference in its entirety.
[0003] Some references, if any, which may include patents, patent
applications and various publications, are cited and discussed in
the description of this invention. The citation and/or discussion
of such references is provided merely to clarify the description of
the present invention and is not an admission that any such
reference is "prior art" to the invention described herein. All
references, if any, cited and discussed in this specification are
incorporated herein by reference in their entireties and to the
same extent as if each reference individually incorporated by
reference.
FIELD OF THE INVENTION
[0004] The present invention is generally related to the field of
production of nanostructures, and, more particularly, is related to
apparatus and methods for synthesizing nanostructures by
inductively heating a susceptor made of a ferromagnetic material
substantially at a Curie temperature associated with the
ferromagnetic material.
BACKGROUND OF THE INVENTION
[0005] The production of high purity carbon nanostructures such as
single wall and multi wall nanotubes and nanofibers as well as
nanomaterials from other elements has been achieved by several
methods, including arc discharge, pulsed laser vaporization
(hereinafter "PLV"), and chemical catalytic vapor deposition
(hereinafter "CCVD"). To date one promising technology for
producing nanostructures is CCVD. A CCVD nanostructure reactor
enables the control of most of the physical and chemical parameters
that influence both the nucleation and the growth of highly pure
carbon nanostructures. The important parameters for producing
nanostructures include the nature and support of a catalyst, a
hydrocarbon source and concentration, a flow rate and type of
carrier gas, a reaction time, a reaction temperature and thermal
stability in a reaction zone of a nanostructure reactor.
Additionally, in order to efficiently mass-produce highly pure
nanostructures at low cost, energy consumption during the heating
process need to be minimized.
[0006] One of the major limitations of a conventional CCVD
nanostructure reactor for nanostructure synthesis is the size of a
susceptor that can be used. Large size susceptors, desirable for
producing large quantities of carbon nanostructures, introduce
difficulties in controlling the hydrocarbon gas flow over the
catalyst powder bed and attaining tight control of a reaction
temperature. Furthermore, the use of conventional ovens results in
temperature gradient along the length of the oven. This temperature
gradient results in varying temperature conditions that have a
significant negative impact on the quality, characteristics, and
purity of carbon nanostructures grown therein. Additionally,
conventional ovens consume large amounts of energy and heat
inefficiently.
[0007] An alternative technology for heating a reaction zone of a
nanostructure reactor is inductive heating (hereinafter "IH"). IH
can be easily controlled, can be focused on catalyst particles
alone, and presents a uniform temperature within the reaction zone.
IH also consumes significantly lower energy compared to classical
heating because it mostly heats the reactants and their physical
support such as a susceptor. Another advantage of IH is the time
required for the catalyst particles and "susceptor" to reach the
temperature of reaction is about 2 to 3 minutes, which is much
shorter, compared to the about 30 minutes required for classical
heating. Altogether, the time required to produce a batch of
nanostructures by IH is approximately one third of the time
required by using a classical oven to produce a similar batch of
nanostructures.
[0008] In an IH nanostructure reactor, high purity graphite is
typically formed into the shape of a boat and used as the
susceptor. The susceptor boat lies within the radio frequency
(hereinafter "RF") field, absorbs its energy, and heats the
catalyst and other reactants. If the RF field intensity is
increased, the susceptor temperature rises. Therefore, the amount
of RF energy has to be carefully controlled, particularly if there
are variations in power or ambient temperature. Additionally, there
is the aforementioned 2 to 3 minutes of susceptor warm-up time to
achieve temperature equilibrium. The length of this warm up time
period and the corresponding cool down time period upon reaction
completion is a function of the thermal mass of the susceptor.
Susceptor mass becomes an increasingly important synthesis
bottleneck as one attempts to scale up for large scale
production.
[0009] Therefore, a heretofore unaddressed need exists in the art
to address the aforementioned deficiencies and inadequacies.
SUMMARY OF THE INVENTION
[0010] In one aspect, the present invention relates to an apparatus
for synthesizing nanostructures. In one embodiment, the apparatus
includes a heating device that defines a reaction zone therein, and
a susceptor made of a ferromagnetic material having a
characteristic temperature and placed in the reaction zone, where
the characteristic temperature substantially corresponds to a
temperature at which the growth of desired nanostructures occurs
and the heating device is capable of heating the susceptor
substantially at the characteristic temperature. In one embodiment,
the characteristic temperature is substantially equal to a Curie
temperature of the ferromagnetic material.
[0011] In one embodiment, the heating device comprises an
inductively heating device. The inductively heating device includes
an inductor coil. The inductor coil is electrically coupled to an
alternating current (hereinafter "AC") power supply, and is
configured such that, in operation, it allows an alternating
current to pass through to generate an electromagnetic field with a
radio frequency in the reaction zone to heat the susceptor
substantially at the characteristic temperature.
[0012] The susceptor, in one embodiment, includes a foil or plate
of the ferromagnetic material, where the foil or plate has a
surface for nanostructures to grow on the surface. The foil or
plate of the ferromagnetic material may be coated with a
non-magnetic conductive material. In one embodiment, the
non-magnetic conductive material comprises gold or chromium. The
susceptor, in one embodiment, is mounted on an ultra-low heat
conductivity/capacity insulator. The ultra-low heat
conductivity/capacity insulator is made of silicate. In another
embodiment, the susceptor includes a bed of powders made from the
ferromagnetic material, where each of the powders is coated with a
catalyst and support materials.
[0013] The apparatus may further comprise a chamber having a first
end, an opposite, second end, and a body portion defined
therebetween, where the heating device is formed on the exterior
surface of the body portion of the chamber such that the reaction
zone is defined inside the chamber.
[0014] In another aspect, the present invention relates to an
apparatus for synthesizing nanostructures. In one embodiment the
apparatus has a susceptor made of a ferromagnetic material having a
characteristic temperature. The characteristic temperature
corresponds to a temperature at which the growth of desired
nanostructures occurs and is substantially equal to a Curie
temperature of the ferromagnetic material. The apparatus further
has a heating device for heating the susceptor substantially at the
characteristic temperature.
[0015] In yet another aspect, the present invention relates to a
method for synthesizing nanostructures. In one embodiment, the
method includes the step of providing a nanostructure reactor
having a reaction zone and a susceptor placed in the reaction zone,
where the susceptor is made of a ferromagnetic material having a
Curie temperature and contains a catalyst. In one embodiment, the
susceptor comprises a foil or plate of the ferromagnetic material,
and wherein the foil or plate has a surface for nanostructures to
grow on the surface. The foil or plate of the ferromagnetic
material may be coated with a non-magnetic conductive material. In
another embodiment, the susceptor comprises a bed of powders made
from the ferromagnetic material. Each of the powders is coated with
a catalyst and support materials.
[0016] The method also includes the steps of supplying a feedstock
reagent to the reaction zone, heating the susceptor to increase the
temperature of the susceptor to the Curie temperature, and keeping
the susceptor substantially at the Curie temperature for a period
of time for the growth of desired nanostructures from the catalyst
and the feedstock reagent. In one embodiment, the heating step
includes the step of inductively heating the susceptor with an
electromagnetic field with an RF.
[0017] The method may further include the step of optimizing the
characteristic temperature for the growth of the desired
nanostructures. The optimizing step comprises the step of selecting
the ferromagnetic material with a Curie temperature that
substantially corresponds to a temperature at which the growth of
the desired nanostructures occurs. The method may also include the
step of maintaining a sufficient amount of the feedstock reagent in
the reaction zone.
[0018] In a further aspect, the present invention relates to a
method for synthesizing nanostructures. In one embodiment, the
method includes the steps of providing a susceptor containing a
catalyst, where the susceptor is made of a ferromagnetic material
having a characteristic temperature, and heating the susceptor
substantially at the characteristic temperature for the growth of
desired nanostructures from the catalyst. The heating step
comprises the steps of inductively heating the susceptor to
increase temperature of the susceptor to the characteristic
temperature, and keeping the susceptor substantially at the
characteristic temperature for a period of time for the growth of
the desired nanostructures. In one embodiment, the inductively
heating step is performed with an electromagnetic field with an RF.
In one embodiment, the method further includes the step of
supplying a feedstock reagent. The method may also include the step
of optimizing the characteristic temperature for the growth of the
desired nanostructures, where the optimizing step includes the step
of selecting the ferromagnetic material with a Curie temperature
that substantially corresponds to a temperature at which the growth
of the desired nanostructures occurs.
[0019] In yet a further aspect, the present invention relates to a
method for synthesizing nanostructures. In one embodiment, the
method includes the step of heating a susceptor containing a
catalyst substantially at a characteristic temperature at which the
growth of desired nanostructures occurs, where the susceptor is
made of a ferromagnetic material with a Curie temperature that is
substantially equal to the characteristic temperature. The heating
step comprises the steps of inductively heating the susceptor to
increase temperature of the susceptor to the characteristic
temperature, and keeping the susceptor substantially at the
characteristic temperature for a period of time for the growth of
the desired nanostructures. In one embodiment, the inductively
heating step is performed with an electromagnetic field with an RF.
The method further includes the step of supplying a feedstock
reagent to the susceptor.
[0020] These and other aspects of the present invention will become
apparent from the following description of the preferred embodiment
taken in conjunction with the following drawings, although
variations and modifications therein may be affected without
departing from the spirit and scope of the novel concepts of the
disclosure.
BRIEF DESCRIPTION OF THE DRAWINGS
[0021] The accompanying drawings illustrate one or more embodiments
of the invention and, together with the written description, serve
to explain the principles of the invention. Wherever possible, the
same reference numbers are used throughout the drawings to refer to
the same or like elements of an embodiment, and wherein:
[0022] FIG. 1 shows schematically a perspective view of an
apparatus for synthesizing nanostructures according to one
embodiment of the present invention.
[0023] FIG. 2 shows schematically a perspective view of a susceptor
according to one embodiment of the present invention.
[0024] FIG. 3 shows temperature profiles of different types of
heating devices for synthesizing nanostructures.
[0025] FIG. 4 shows schematically a cross-sectional view of an
apparatus for synthesizing nanostructures according to another
embodiment of the present invention.
[0026] FIG. 5 shows synthesized carbon nanotubes according to one
embodiment of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0027] The present invention is more particularly described in the
following examples that are intended as illustrative only since
numerous modifications and variations therein will be apparent to
those skilled in the art. Various embodiments of the invention are
now described in detail. Referring to the drawings FIGS. 1-5, like
numbers indicate like components throughout the views. As used in
the description herein and throughout the claims that follow, the
meaning of "a", "an", and "the" includes plural reference unless
the context clearly dictates otherwise. Also, as used in the
description herein and throughout the claims that follow, the
meaning of "in" includes "in" and "on" unless the context clearly
dictates otherwise. Moreover, titles or subtitles may be used in
the specification for the convenience of a reader, which shall have
no influence on the scope of the present invention. Additionally,
some terms used in this specification are more specifically defined
below.
DEFINITIONS
[0028] The terms used in this specification generally have their
ordinary meanings in the art, within the context of the invention,
and in the specific context where each term is used.
[0029] Certain terms that are used to describe the invention are
discussed below, or elsewhere in the specification, to provide
additional guidance to the practitioner in describing the apparatus
and methods of the invention and how to make and use them. For
convenience, certain terms may be highlighted, for example using
italics and/or quotation marks. The use of highlighting has no
influence on the scope and meaning of a term; the scope and meaning
of a term is the same, in the same context, whether or not it is
highlighted. It will be appreciated that the same thing can be said
in more than one way. Consequently, alternative language and
synonyms may be used for any one or more of the terms discussed
herein, nor is any special significance to be placed upon whether
or not a term is elaborated or discussed herein. Synonyms for
certain terms are provided. A recital of one or more synonyms does
not exclude the use of other synonyms. The use of examples anywhere
in this specification, including examples of any terms discussed
herein, is illustrative only, and in no way limits the scope and
meaning of the invention or of any exemplified term. Likewise, the
invention is not limited to various embodiments given in this
specification. Furthermore, subtitles may be used to help a reader
of the specification to read through the specification, which the
usage of subtitles, however, has no influence on the scope of the
invention.
[0030] As used herein, "around", "about" or "approximately" shall
generally mean within 20 percent, preferably within 10 percent, and
more preferably within 5 percent of a given value or range.
Numerical quantities given herein are approximate, meaning that the
term "around", "about" or "approximately" can be inferred if not
expressly stated.
[0031] As used herein, "catalytic chemical vapor deposition method"
or "CCVD" refers to a method in the art to synthesize fullerenes
and carbon nanotubes by using acetylene gas, methane gas, or the
like that contains carbon as a raw material, and generating carbon
nanotubes in chemical decomposition reaction of the raw material
gas. Among other things, the chemical vapor deposition depends on
chemical reaction occurring in the thermal decomposition process of
the methane gas and the like serving as the raw material, thereby
enabling the manufacture of carbon nanotubes having high
purity.
[0032] As used herein, "carbon nanostructures" refer to carbon
fibers or carbon nanotubes that have a diameter of 1 .mu.m or
smaller which is finer than that of carbon fibers. However, there
is no particularly definite boundary between carbon fibers and
carbon nanotubes. By a narrow definition, the material whose carbon
faces with hexagon meshes are almost parallel to the axis of the
corresponding carbon tube is called a carbon nanotube, and even a
variant of the carbon nanotube, around which amorphous carbon
exists, is included in the carbon nanotube.
[0033] As used herein, "single wall nanotube" and its acronym
"SWNT" refer to a carbon nanotube having a structure with a single
hexagon mesh tube (graphene sheet).
[0034] As used herein, "multi-wall nanotube" and its acronym "MWNT"
refer to a carbon nanotube made of multilayer graphene sheets.
[0035] As used herein, "carbon nanotubes" refers to several of
SWNTs, MWNTs, or a combination of them.
[0036] As used herein, "Curie temperature" or "Curie point" refers
to a characteristic property of a ferromagnetic material. The Curie
temperature of a ferromagnetic material is the temperature above
which it loses its characteristic ferromagnetic ability to possess
a net (spontaneous) magnetization in the absence of an external
magnetic field. At temperatures below the Curie temperature, the
magnetic moments are partially aligned within magnetic domains in
ferromagnetic materials. As the temperature is increased from below
the Curie temperature, thermal fluctuations increasingly destroy
this alignment, until the net magnetization becomes zero at and
above the Curie temperature. Above the Curie temperature, the
material is purely paramagnetic.
[0037] As used herein, "reaction zone" refers to a
three-dimensional zone inside a nanostructure reactor where
hydrocarbon molecules are heated to produce carbon molecules.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0038] Nanostructure reactors that implement CCVD methods to
produce carbon nanostructures require that hydrocarbon molecules be
deposited on a heated catalyst material. The catalyst is typically
used to disassociate the hydrocarbon molecules. Using hydrocarbons
as a carbon source, the hydrocarbons flow into a reaction zone of a
nanostructure reactor, where the hydrocarbons are heated at a high
temperature. The dissociation of the hydrocarbon breaks the
hydrogen bond, thus producing pure carbon molecules. The important
parameters that influence the growth of carbon nanostructures are,
among other things, the nature and support of the catalyst, the
hydrocarbon source and concentration, the flow rate and type of
carrier gas, the time of reaction, the temperature of reaction and
the thermal stability in the reaction zone.
[0039] The present invention relates to apparatus and methods for
synthesizing high quality and purity nanostructures with large
quantities by, among other things, inductively heating a susceptor
made of a ferromagnetic material to a Curie temperature of the
ferromagnetic material and keeping the susceptor substantially at
the Curie temperature for a period of time. The Curie temperature
substantially corresponds to a temperature at which the growth of
desired nanostructures occurs.
[0040] Without intent to limit the scope of the invention, various
embodiments of the present invention are described below.
[0041] The present invention, in one aspect, relates to a method
for synthesizing nanostructures. The method in one embodiment
includes the following steps: at first, a nanostructure reactor
having a reaction zone and a susceptor placed in the reaction zone
is provided, where the susceptor is made of a ferromagnetic
material with a Curie temperature and contains a catalyst. A
feedstock reagent and/or carrier gas is supplied to the reaction
zone. Then, the susceptor is heated to increase its temperature to
the Curie temperature and kept substantially at the Curie
temperature for a period of time for the growth of desired
nanostructures from the catalyst and the feedstock reagent.
[0042] The nanostructure reactor may or may not include a chamber.
The susceptor can be formed in the form of a foil or plate of the
ferromagnetic material. The foil or plate of the ferromagnetic
material may be coated with a non-magnetic conductive material. The
susceptor can also be formed in the form of powders that are made
of the ferromagnetic material. Each of the powders is coated with a
catalyst and support materials. The susceptor can also be formed in
other forms. The susceptor is heated by an inductive heating device
such as an inductive coil for generating an RF field in the
reaction zone in which the susceptor is placed.
[0043] The method may further include the step of selecting the
ferromagnetic material with a Curie temperature that substantially
corresponds to a temperature at which the growth of desired
nanostructures occurs so as to optimize the temperature for the
growth of the desired nanostructures. The method may also include
the step of maintaining a sufficient amount of the feedstock
reagent and/or carrier gas in the reaction zone.
[0044] In another aspect, the present invention relates to an
apparatus for synthesizing nanostructures. Referring now to FIGS. 1
and 2, an apparatus 100 for synthesizing nanostructures according
to one embodiment of the present invention is shown. The apparatus
100 has a cylindrical process chamber 10 having a body portion 12
defining a bore 14 with an axis 16 therein, an inductively heating
device 20 in the form of inductor coils 28 formed on the exterior
surface of the chamber 10, thereby defining a reaction zone inside
the bore 14, and a susceptor 30 placed in the reaction zone.
[0045] The cylindrical process chamber 10 further has a first end
18a and an opposite, second end 18b. The body portion 12 of the
cylindrical process chamber 10 is located between the first end 18a
and the second end 18b. The first end 18a and the second end 18b
may be sealed by a first seal 3a and a second seal 3b,
respectively. An inlet tube 1a can be used for interconnecting
through the first seal 3a to establish a fluid communication with
the bore 14 of the cylindrical process chamber 10, and an outlet
tube 1b can be used for interconnecting through the second seal 3b
to establish a fluid communication with the bore 14 of the
cylindrical process chamber 10, respectively. Inlet tube 1a and
outlet 1b are used to transport carbon feedstock and/or carrier
gases in to and out from the bore 14 of the cylindrical process
chamber 10, among other things. Inlet tube 1a and outlet 1b may
also be connected to other control device(s) (not shown) that are
adapted for maintaining a sufficient amount of the carbon feedstock
and/or carrier gases in the reaction zone in the bore 14 of the
cylindrical process chamber 10. Additional inlet(s) and/or
outlet(s) may also be utilized.
[0046] As shown in FIG. 1, the cylindrical process chamber 10 is
held by holders 5a and 5b at the first end 18a and the second end
18b, respectively. Other types of holding means such as one or more
hangers may also be used.
[0047] The process chamber 10 can also be formed in other geometric
shapes. For example, the process chamber 10 can be spherical. The
cylindrical process chamber 10 can be made of a substantially
non-conductive material such glass. In one embodiment, the
cylindrical process chamber 10 is substantially made of quartz. The
cylindrical process chamber 10 may be made of other types of
materials including non-magnetic conductive materials.
[0048] The inductively heating device 20, as shown in FIG. 1, is in
the form of an inductive coil 28 that is substantially uniformly
surrounding the exterior surface of the body portion 12 of the
cylindrical process chamber 10 and defines a reaction zone inside
the bore 14 of the cylindrical process chamber 10 with a
longitudinal length L.sub.I. The inductive coil 28 is positioned in
relation to the body portion 12 of the cylindrical process chamber
10 such that there is a distance between the inductive coil 28 and
the exterior surface of the body portion 12 of the cylindrical
process chamber 10, and the distance can be any value in the range
of 0 to 10 cm.
[0049] The inductive coil 28 can be made from at least one of
metals, alloys, and conducting polymeric materials. In one
embodiment, the inductive coil 28 is substantially made from
copper. The inductive coil 28 is electrically coupled to an AC
power supply 7 through a first end 22, and a second end 24,
respectively. For example, a high or RF frequency generator can be
used as an AC power supply 7. The inductive coil 28 is configured
such that, in operation, it allows an alternating current to pass
through to generate an electromagnetic field with an RF in the
reaction zone to heat the susceptor 30 substantially at the
characteristic temperature.
[0050] Other types of inductive heating devices can also be
utilized to practice the current invention.
[0051] As shown in FIG. 2, the susceptor 30 has a first end portion
32 and an opposite, second end portion 34 defining a body portion
36 with a longitudinal length L.sub.s therebetween. The body
portion 36 defines a recess 46 with a supporting surface 38 for
supporting a catalyst 60. The supporting surface 38 can be flat,
sloped, or curved. The body portion 36 of the susceptor 30 is
formed with a bottom surface 40, a first side surface 42, and a
second, opposite side surface 44. Alternatively, the body portion
36 can be formed such that the supporting surface 38 is the tope
surface of the body portion 36.
[0052] The body portion 36 of the susceptor 30 is formed such that
when the susceptor 30 is positioned in the reaction zone in the
bore 14 of the cylindrical process chamber 10, there is at least
one space formed between the supporting surface 38 and the inner
surface of the body portion 12 for facilitating fluid communication
inside the bore 14 of the cylindrical process chamber 10 and
allowing nanostructures to grow on the supporting surface 38.
[0053] The longitudinal length L.sub.I of the reaction zone and the
longitudinal length L.sub.s of the susceptor 30 satisfy the
following relationship:
L.sub.s<L.sub.I,
which allows the susceptor 30 to be uniformly heated during an
operation. However, the present invention can be practiced with the
relationship L.sub.s.gtoreq.L.sub.I.
[0054] The susceptor 30 is made of a ferromagnetic material having
a Curie temperature (Curie point), T.sub.c, which substantially
corresponds to a temperature at which the growth of desired
nanostructures occurs. The Curie temperature T.sub.c is a
temperature above which the ferromagnetic material loses its
ferromagnetic character and becomes transparent to an RF field.
When the susceptor 30 lies within an RF field, it interacts with
the RF field. Such an interaction causes the susceptor 30 to absorb
the energy of the RF field and therefore causes the temperature of
the susceptor 30 to rise. When the temperature of the susceptor 30
rises to the Curie temperature T.sub.c, the susceptor 30 becomes
transparent to the RF field and then its temperature remains at the
Curie temperature T.sub.c as long as the RF filed is being
applied.
[0055] The susceptor 30 can also be formed in other forms. For
example, the susceptor can be formed in a thin Curie point foil
mounted on an ultra-low heat conductivity/capacity insulator made
of silicate or materials used for space shuttle tiles. The foil may
be coated with a non-magnetic shield or higher temperature
non-paramagnetic/non-reactive materials to prevent the foil alloy
from reacting with the carbon source or feedstock reagents. The
non-magnetic shield or higher temperature
non-paramagnetic/non-reactive materials includes gold, chromium or
the likes. The same design can be employed if the Curie point foil
alloy exhibits any independent catalytic activity toward the carbon
or feedstock materials. The low thermal mass of the Curie point
foil material allows for rapid turnaround between batches in a
serial production of nanostructures.
[0056] Alternatively, the susceptor 30 may be formed in the form of
fine powders of Curie point (ferromagnetic) material coated with a
catalyst and support materials as a susceptor. The coated powders
are exposed to the feedstock/reactant gases via a fluidized bed or
spill/screw assembly. In this embodiment, the reaction container
(chamber) and/or screw is made preferably from fused silica or
other RF transparent materials. In this embodiment, a foil or
deposited coating having the same Curie temperature Tc as the
powders would line the container and the screw to eliminate contact
cooling.
[0057] In operation, the susceptor 30 containing the catalyst 60 is
positioned in the reaction zone in the bore 14 of the cylindrical
process chamber 10. A carbon feedstock and/or carrier gas is
transported into in the reaction zone. The inductive coil 28 is
electrically powered with an AC power supply 7 to generate an RF
field in the reaction zone. The interaction of the RF field with
the susceptor 30 results in an increase of the temperature of the
susceptor 30 to the Curie temperature T.sub.c at which desired
nanostructures start to grow from the catalyst 60 and the feedstock
reagent on the supporting surface 38 of the susceptor 30. By
continuously supplying the RF field in the reaction zone, the
temperature of the susceptor 30 remains substantially at the Curie
temperature T.sub.c, thereby allowing the growth of the desired
nanostructure to continue at a substantially constant thermal
environment.
[0058] Referring to FIG. 3, an apparatus 300 for synthesizing
nanostructures is shown according to another embodiment of the
present invention. In the exemplary embodiment, the apparatus 300
includes a heating device 320 that defines a reaction zone 380
therein, and a susceptor 330 made of a ferromagnetic material
having a characteristic temperature and placed in the reaction zone
380, where the characteristic temperature substantially corresponds
to a temperature at which the growth of desired nanostructures
occurs and is substantially equal to a Curie temperature of the
ferromagnetic material. As shown in FIG. 3, the susceptor 330 is
formed in the form of a plate defining a recess 346 with a
supporting surface 338 for supporting a catalyst 360. The susceptor
330 is supported by an ultra-low heat conductivity/capacity
insulator 340. The ultra-low heat conductivity/capacity insulator
340 may comprise a material used for space shuttle tiles, or
silicate, for examples. The susceptor 330 can be formed in any
forms, for example, a thin foil or a boat-like structure. The
heating device 320 is adapted for heating the susceptor 330
substantially at the Curie temperature. As shown in FIG. 3, the
heating device 320 is in the form of an inductive coil 328. The
inductive coil 328 is electrically coupled to an AC power supply
(not shown) for generating an electromagnetic field with an RF in
the reaction zone 380 to heat the susceptor 330 substantially at
the Curie temperature.
[0059] Additionally, according to the embodiments of the present
invention as disclosed in the specification, the apparatus may
includes means for supplying a feedstock reagent and/or carrier gas
to the reaction zone, and means for keeping a sufficient amount of
the feedstock reagent and/or carrier gas in the reaction zone. The
apparatus may also include means for consecutively introducing
batches of a catalyst to the susceptor in the reaction zone, where
each batch of the catalyst is positioned in the reaction zone for a
period of time for the growth of desired nanostructures.
[0060] The use of an inductively heating device to heat a susceptor
of a ferromagnetic material (alloy) according to the present
invention has great advantages over conventional heating processes.
For example, for inductively heating a susceptor of a thin foil of
ferromagnetic alloy by an RF field, the time for which the
temperature of the susceptor rises from an ambient temperature to
the Curie temperature T.sub.c is as few as 0.2 seconds. The
susceptor is also cooled down almost instantly once the RF field is
turned off. However, inductively heating a conventional susceptor
made of a non-ferromagnetic material from an ambient temperature to
a temperature of reaction may take about 2 to 3 minutes. And
classically heating a ferromagnetic susceptor or conventional
susceptor from an ambient temperature to a temperature of reaction
may take up to about 30 minutes. Therefore, the time required to
produce a batch of nanostructures by inductively heating a
ferromagnetic susceptor is much less than the time required to
produce a similar batch of nanostructures by conventional
processes. The use of a ferromagnetic susceptor allows for very low
energy consumption during synthesis of desired nanostructures.
[0061] Furthermore, when a ferromagnetic susceptor is inductively
heated by an RF field, the temperature of the ferromagnetic
susceptor is uniformly distributed over the reaction zone, which
is, for example, indicated by the temperature distribution 430 in
FIG. 4. As a comparison, FIG. 4 also shows the temperature
distributions 410 and 420 of a conventional susceptor heated by a
classical oven and an inductive heating device, respectively. These
distributions indicate the thermal stability in the reaction zone.
The present invention allows a substantially uniform temperature
distribution 430 longitudinally across the reaction zone. That is,
no temperature hysteresis exists in the reaction zone, which
indicates thermal stability and temperature accuracy is independent
of operational parameters in the reaction zone. However, a
classical heating process results in a non-uniform gradient
temperature distribution 410 across the reaction zone. The lack of
uniformity in a classical heating process is directly responsible
for a lack of purity in reaction products.
[0062] Inductive heating can be used for a plurality of metallic
catalysts on metal oxide supports and carrier/hydrocarbon or
carrier/heteroatom source gas combinations. The specific types of
nanostructures that are produced are a function of a chosen
catalyst and a carrier gas (e.g., argon, nitrogen, hydrogen,
helium, or mixtures of these gases in various ratios). For carbon
nanostructures, hydrocarbon feedstock can be gaseous (e.g.,
methane, ethylene, acetylene, or the likes), liquid (e.g., xylene,
benzene, n-hexane, alcohol, or the like), or solid (e.g.,
anthracene, naphthalene, or the likes). The above-mentioned reasons
make inductive heating suitable for large-scale carbon
nanostructure production. Additionally, embodiments of the present
invention can also be practiced with modifications for the assembly
of non-carbon based nanomaterials.
[0063] FIG. 5 shows an image of multi wall carbon nanotubes
(MW-CNTs) 550 grown in a stainless steel laboratory scoopula
(susceptor) 530 by inductively heating the scoopula substantially
at its Curie temperature according to the present invention.
[0064] The scoopula 530 was made of a Curie Poking alloy having a
Curie temperature Tc=640.degree. C., a temperature at which the
growth of MW-CNTs occurs. The scoopula 530 was placed in an RF
field generated by an inductive coil and heated instantly to the
Curie temperature Tc=640.degree. C. with the RF field. Without
adding a catalyst or support, carbon source gases were introduced,
and no reaction between carbon source gases and the scoopula 530
was found. Repeating the process with the catalyst and support
presented in the scoopula 530, the MW-CNTs were formed on the
catalyst. It should be noted that SW-CNTs, MW-CNTs, carbon
nanofibers (CNFs), Boron-nitride nanotubes, Boron-carbon nanotubes,
and other nanoparticles may be optimally synthesized at
temperatures different from 640.degree. C. so that susceptor foils
or particles with corresponding Curie temperatures Tc would be
required for each application. It is important to have special
purpose alloys for various nanostructures. These alloys can be
fabricated as foil, wire, rod, or plate. The Curie temperature Tc
of a ferromagnetic alloy can be adjusted by incremental adjustment
of the alloy composition or annealing process.
[0065] A significant aspect of practicing the present invention is
that RF energy is used to inductively heat a ferromagnetic
susceptor containing a catalyst to a Curie temperature of the
susceptor directly, which is coincident with the reaction
temperature of the catalyst. An apparatus having a ferromagnetic
susceptor with inductive heating enables the control of most of the
physical and chemical parameters that influence the nucleation and
the growth of highly pure carbon nanostructures.
[0066] Thus, according to the present invention, inductive heating
directly heats a susceptor made of a ferromagnetic material,
therefore making methods that utilize inductive heating
exceptionally efficient. Another advantage of inductive heating is
that the time required for increasing the temperature of the
susceptor from an ambient temperature to the Curie temperature of
the ferromagnetic material, which corresponds to the temperature of
reaction of catalyst particles, is much shorter in comparison to
conventional heating methods. In a further comparison with
conventional heating methods, the inductive heating presents a
uniform temperature distribution in the reaction zone. Therefore,
the invented apparatus and methods for synthesizing nanostructures
assure temperature reproducibility, stability, and accuracy for the
growth of desired nanostructures.
[0067] Among others things, the current invention can be applied
for synthesis processes involving (i) chemical vapor deposition of
non-carbon-based nanostructures such as those using boron and
nitrogen; (ii) elemental substitution of already formed nanotube or
nanofiber structures, such as those involving boron substitution
for carbon atoms to form boron-carbon nanostructures; (iii)
post-formation layering or other treatment of nanostructures. In
the elemental substitution, layering, or treatment processes, heat
from the Curie point foil or particle is not located precisely at
the point of catalytic activity as in the CCVD-based primary
formation of carbon or other nanostructures. Therefore precise
temperature control may not be achieved. In these instances, a
major benefit of exploiting the Curie point principle would be the
drastically reduced energy costs needed to achieve a useful
synthesis temperature.
[0068] Any of the above-mentioned embodiments alone or in
combination will permit the continuous production of
nanostructures. Further, any other methods that achieve the same
result by controlling the above-mentioned pertinent factors are
encompassed within the scope of this invention.
[0069] The foregoing description of the exemplary embodiments of
the invention has been presented only for the purposes of
illustration and description and is not intended to be exhaustive
or to limit the invention to the precise forms disclosed. Many
modifications and variations are possible in light of the above
teaching.
[0070] The embodiments were chosen and described in order to
explain the principles of the invention and their practical
application so as to enable others skilled in the art to utilize
the invention and various embodiments and with various
modifications as are suited to the particular use contemplated.
Alternative embodiments will become apparent to those skilled in
the art to which the present invention pertains without departing
from its spirit and scope. Accordingly, the scope of the present
invention is defined by the appended claims rather than the
foregoing description and the exemplary embodiments described
therein.
* * * * *