U.S. patent application number 11/987986 was filed with the patent office on 2008-07-10 for process for producing carbamoyloxy (meth) acrylates and new carbamoyloxy (meth) acrylates.
Invention is credited to Vincent Stone, Hugues Van Den Bergen, Jurgen Van Holen.
Application Number | 20080167489 11/987986 |
Document ID | / |
Family ID | 32479723 |
Filed Date | 2008-07-10 |
United States Patent
Application |
20080167489 |
Kind Code |
A1 |
Stone; Vincent ; et
al. |
July 10, 2008 |
Process for producing carbamoyloxy (meth) acrylates and new
carbamoyloxy (meth) acrylates
Abstract
The invention relates to a process for producing
carbamoyloxy(meth)acrylates which comprises transesterification of
hydroxyalkyl carbamates with an (meth)acrylate of formula
CH.sub.2.dbd.CR.sup.29--COOR.sup.30 wherein R.sup.29 is hydrogen or
methyl and R.sup.30 represents an alkyl group comprising from 1 to
8 carbon atoms, in the presence of an organotitanate, an
organozirconate catalyst or an organotin catalyst, the
carbamoyloxy(meth)acrylates thereby obtained and their use in
radiation curable compositions.
Inventors: |
Stone; Vincent; (Brussels,
BE) ; Van Holen; Jurgen; (Gent, BE) ; Van Den
Bergen; Hugues; (Drogenbos, BE) |
Correspondence
Address: |
WENDEROTH, LIND & PONACK, L.L.P.
2033 K STREET N. W., SUITE 800
WASHINGTON
DC
20006-1021
US
|
Family ID: |
32479723 |
Appl. No.: |
11/987986 |
Filed: |
December 6, 2007 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10536017 |
May 20, 2005 |
7329773 |
|
|
PCT/EP2003/012887 |
Nov 18, 2003 |
|
|
|
11987986 |
|
|
|
|
Current U.S.
Class: |
560/158 ;
560/160 |
Current CPC
Class: |
C07C 269/06 20130101;
C07C 271/16 20130101 |
Class at
Publication: |
560/158 ;
560/160 |
International
Class: |
C07C 271/10 20060101
C07C271/10 |
Foreign Application Data
Date |
Code |
Application Number |
Dec 12, 2002 |
EP |
02027835.4 |
Claims
1-27. (canceled)
28. Carbamoyloxy(meth)acrylates obtainable by a process which
comprises the transesterification of an hydroxyalkyl carbamate of
formula (I), (II), (III), (IV), (V), (VI) or (VII) ##STR00023##
##STR00024## wherein k.gtoreq.2 n=0 to 2 m=0 to 2 n+m.gtoreq.1 p=n
or m, q=n or m, r=n or m, s=n or m, v=n or m, w=n or m
(p+q)=(r+s)=(v+w)=(n+m) each R.sup.1, each R.sup.2, each R.sup.20
is, independently, chosen from the group of hydrogen, halogen,
hydroxy, alkyl, optionally substituted by hydroxy; halogen; aryl
and/or aryl substituted by hydroxy, halogen or alkyl; and
optionally containing from 1 to 8 ether bridges, alkenyl,
optionally substituted by hydroxy; halogen; aryl and/or aryl
substituted by hydroxy, halogen or alkyl; and optionally containing
from 1 to 8 ether bridges, aryl, optionally substituted by hydroxy;
halogen; alkyl; alkyl substituted by hydroxy, halogen and/or aryl;
and/or alkyl containing from 1 to 8 ether bridges, R.sup.3 is an
alkyl, optionally substituted by hydroxy, tertiary amine and/or
aryl, and optionally containing from 1 to 20 ether bridges and/or
from 1 to 3 tertiary amine bridges, R.sup.4, R.sup.5, R.sup.6,
R.sup.12, R.sup.13, R.sup.14, R.sup.15 and R.sup.16 are,
independently, chosen from the group of hydrogen, and alkyl,
optionally substituted by hydroxy, tertiary amine and/or aryl, and
optionally containing from 1 to 8 ether bridges and/or from 1 to 3
tertiary amine bridges, with the proviso that, respectively,
R.sup.3 and R.sup.4, R.sup.5 and R.sup.6, R.sup.12 and/or R.sup.13
and/or R.sup.14, R.sup.15 and R.sup.16 may be linked together in
order to form a ring, R.sup.7, R.sup.8, R.sup.9, R.sup.10, R.sup.17
and R.sup.18 are, independently, chosen from alkylene, alkenylene,
arylene and aralkylene chains which may contain from 1 to 8 ether
bridges and/or from 1 to 3 tertiary amine bridges, R.sup.11 is
hydrogen or alkyl; R.sup.19, R.sup.21, R.sup.22, R.sup.23,
R.sup.25, R.sup.26, R.sup.27 and R.sup.28, are, independently,
chosen from alkylene, alkenylene, arylene and aralkylene chains
which may contain from 1 to 20 ether bridges, from 1 to 4 tertiary
amine bridges, from 1 to 4 --CO-- bridges and/or from 1 to 4
--O--CO-- bridges; A is ##STR00025## wherein R.sup.24 is hydrogen
or alkyl; with an (meth)acrylate of formula (VIII)
CH.sub.2.dbd.CR.sup.29--COOR.sup.30 (VIII) wherein R.sup.29 is
hydrogen or methyl, and R.sup.30 represents an alkyl group
comprising from 1 to 8 carbon atoms; in an equivalent ratio of
(meth)acrylate to hydroxyalkyl carbamate higher than 3.5 and in the
presence of an organotitanate, an organozirconate or an organotin
catalyst.
29. Carbamoyloxy(meth)acrylates of formula (XVII), (XVIII), (XIX),
(XX), (XXI), (XXII), (XXIII), (XXIV), (XXV) and (XXVI) ##STR00026##
##STR00027## ##STR00028## ##STR00029## wherein k, n, m, p, q, r, S,
V, w, A, R.sup.7, R.sup.8, R.sup.9, R.sup.10, R.sup.17, R.sup.18,
R.sup.11, R.sup.19, R.sup.21, R.sup.22, R.sup.23, R.sup.24,
R.sup.25, R.sup.26, R.sup.27, R.sup.28 and R.sup.29 are as defined
in claim 1, t.gtoreq.3 R.sup.37 is an alkyl substituted by a
tertiary amine, and optionally containing from 1 to 20 ether
bridges and/or from 1 to 3 tertiary amine bridges; or an alkyl
containing from 1 to 20 ether bridges and/or from 1 to 3 tertiary
amine bridges, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2, tertiary amine and/or aryl; each
R.sup.38, each R.sup.40 is, independently, such as defined for
R.sup.31 with the proviso that at least one R.sup.38 and at least
one R.sup.40 is chosen from the group of halogen,
--O--CO--CR.sup.29.dbd.CH.sub.2, alkyl substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2; halogen; aryl and/or aryl
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen or alkyl;
and optionally containing from 1 to 8 ether bridges, alkyl
containing from 1 to 8 ether bridges, alkenyl, optionally
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen; aryl
and/or aryl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen
or alkyl; and optionally containing from 1 to 8 ether bridges,
aryl, optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2;
halogen; alkyl; alkyl substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2, halogen and/or aryl; and/or alkyl
containing from 1 to 8 ether bridges, R.sup.39 is
2-methyl-1,5-pentamethylene; or R.sup.39 is chosen from alkylene
containing from 1 to 8 ether bridges and/or from 1 to 3 tertiary
amine bridges; alkenylene, arylene and aralkylene chains each of
which may contain from 1 to 8 ether bridges and/or from 1 to 3
tertiary amine bridges, or R.sup.39 is chosen from alkylene when at
least one of R.sup.35 and R.sup.36 is different from hydrogen, each
R.sup.31, each R.sup.32, each R.sup.50 is, independently, chosen
from the group of hydrogen, halogen
--O--CO--CR.sup.29.dbd.CH.sub.2, alkyl, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2; halogen; aryl and/or aryl
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen or alkyl;
and optionally containing from 1 to 8 ether bridges alkenyl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen;
aryl and/or aryl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
halogen or alkyl; and optionally containing from 1 to 8 ether
bridges aryl, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2; halogen; alkyl; alkyl substituted
by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen and/or aryl; and/or
alkyl containing from 1 to 8 ether bridges R.sup.33 is an alkyl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, tertiary
amine and/or aryl, and optionally containing from 1 to 20 ether
bridges and/or from 1 to 3 tertiary amine bridges, R.sup.34,
R.sup.35, R.sup.36, R.sup.42, R.sup.43, R.sup.44, R.sup.45 and
R.sup.46 are, independently, chosen from the group of hydrogen, and
alkyl, optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
tertiary amine and/or aryl, and optionally containing from 1 to 8
ether bridges and/or from 1 to 3 tertiary amine bridges, with the
proviso that, respectively, R.sup.33 and R.sup.34, R.sup.35 and
R.sup.36, R.sup.42 and/or R.sup.43 and/or R.sup.44, R.sup.45 and
R.sup.46 may be linked together in order to form a ring.
30. Carbamoyloxy(meth)acrylates of formula (XVIII) according to
claim 29, wherein R.sup.34 is hydrogen and R.sup.37 is alkyl
comprising at least 3 carbon atoms, containing one or two ether
bridges and substituted by --O--CO--CR.sup.29.dbd.CH.sub.2
31. Carbamoyloxy(meth)acrylates of formula (XX) according to claim
29, wherein R.sup.39 is 2-methyl-1,5-pentamethylene.
32. Carbamoyloxy(meth)acrylates of formula (XXIV), (XXV) and (XXVI)
according to claim 29, wherein n+m, p+q, r+s and v+w are equal to
1.
33. Carbamoyl(meth)acrylates according to claim 29 wherein each
R.sup.31, each R.sup.32 and each R.sup.50 is hydrogen.
34. Carbamoyl(meth)acrylates according to claim 29 wherein
R.sup.34, at least one of R.sup.35 and R.sup.36, at least one of
R.sup.42, R.sup.43 and R.sup.44, at least one of R.sup.45 and
R.sup.46 is different from hydrogen.
35. A radiation curable composition comprising a
carbamoyloxy(meth)acrylate according to claim 28.
Description
[0001] The present invention relates to a process for producing
carbamoyloxy(meth)acrylates and to new carbamoyloxy(meth)acrylates
thereby obtained. The invention also relates to the uses of such
compounds, especially in radiation curable compositions.
[0002] Radiation curable compositions have found a wide range of
applications in numerous fields, for example as coatings, varnishes
and paints for protecting and decorating the most diverse
substrates such as glass, metals, plastics, paper, as printing
varnishes and inks or as adhesives for laminates, and the like.
Because of the high viscosity of radiation curable oligomers or
prepolymers used in radiation curable compositions, diluents are
generally added in these compositions. In order to retain the
advantage of radiation curing, so-called "reactive diluents" are
used, permitting to eliminate the presence of solvents. These
reactive diluents are generally low molecular weight compounds
bearing one or more reactive carbon-carbon double bond, permitting
them to be incorporated in the final polymer coating. These
reactive diluents should have the following properties: low
toxicity and irritancy, low volatility and odour, low viscosity,
high reactivity. Moreover, they should be colorless and they should
be able to preserve the performance integrity of the oligomers and
prepolymers.
[0003] Current commercial available reactive diluents never
completely fulfil all these prerequisites at the same time. Low
molecular weight (meth)acrylates bearing carbamate groups are known
as reactive diluents presenting one of the best compromises of the
above-required properties. However, their properties and more
specific properties such as adhesion on difficult substrates,
pencil hardness and abrasion resistance, could still be improved.
One of the best carbamoyloxy(meth)acrylates used in the art is
n-butyl acryloyloxy ethyl carbamate.
[0004] Different processes have been disclosed for the synthesis of
carbamoyloxy(meth)acrylates able to be used as reactive diluents in
radiation curable compositions. U.S. Pat. No. 3,674,838 describes
their synthesis by the so-called chloroformate method using
phosgene as raw material and by the so-called urea method which
need to be conducted at high temperatures, leading to an
uncontrolled radical polymerization of the (meth)acrylates. U.S.
Pat. No. 3,674,838 further mentions that
carbamoyloxy(meth)acrylates could be synthesized via a
transesterification reaction under conditions well known in the
art. However, U.S. Pat. No. 4,126,747 teaches that methods using
typical transesterification catalysts produces commercially
unacceptable yields of desired carbamoyloxy(meth)acrylates and that
these products are highly colored. U.S. Pat. No. 4,126,747 further
describes a direct esterification process using (meth)acrylic acid.
B. M. Culbertson, H. J. Langer, L. K. Post, Org. Coat. Plast. Chem.
(1979), 40, 903-8, describes the so-called isocyanate method to
make monofunctional(meth)acrylic monomers containing carbamate
functionality by treating hydroxyalkyl(meth)acrylates with
equimolar amounts of various isocyanates. Currently used industrial
process for making n-butyl acryloyloxy ethyl carbamates based on
the isocyanate method.
[0005] These known processes, and especially the chloroformate and
isocyanate methods, for making known carbamoyloxy acrylates or
methacrylates use highly toxic and dangerous raw materials, such as
low molecular weight isocyanates and phosgene. Storing, handling
and processing these toxic raw materials at large scale can only
occur with highly expensive secured industrial equipments and
safety procedures in an adapted industrial environment. Moreover,
the reactions involved in these methods being highly exothermic,
risk for runaway reactions leading to polymerization in the reactor
and atmospheric pollution with toxic materials is important at
large scale. Another major drawback of the known processes, and
especially of the isocyanate method, is that it may lead to
products containing significant amounts of toxic impurities, for
example aliphatic isocyanates, such as butyl isocyanate, and/or low
molecular weight hydroxyalkyl acrylates, such as hydroxyethyl
acrylate. The legislation on toxic impurities calls for the need of
processes that are able to lead to products free of such impurities
or containing these impurities in very low concentrations,
typically below 1000 ppm. Moreover, these processes generally lead
to relative low yields so that highly expensive purification
processes are needed. They also lead to highly colored products
that precludes their use in some applications such as overprint
varnishes. The direct esterification method described in U.S. Pat.
No. 4,126,747 presents the disadvantage to produce a relative low
yield so that a large amount of non-(meth)acrylated
hydroxycarbamate is still present in the final product which may
have a detrimental effect on the diluting power of the product due
to its relative high viscosity and which may lead to migration
problems in the cured coatings. Another problem with this direct
esterification method is that high concentrations of acidic
catalyst is needed, which in general triggers side reactions
leading directly or indirectly to the formation of toxic
by-products (such as hydroxyethyl acrylate) and which also causes
problems with corrosion and for elimination of catalyst residues.
Another drawback of this direct esterification method is that high
excess in (meth)acrylic acid is needed which requires efficient
recycling procedures.
[0006] Higher molecular weight carbamoyloxy(meth)acrylates are also
the subject of this invention. Being of higher viscosity, the
latter structures can be used as an oligomer in radiation curable
formulations. The two approaches applied to make the current
commercially available oligomers bearing carbamate groups (often
referred to as "urethane(meth)acrylates") make use of aliphatic or
aromatic multifunctional (mostly difunctional) isocyanates. The
first approach makes use of the above mentioned isocyanate
method:multifunctional isocyanates are reacted with
hydroxyfunctional(meth)acrylate monomers like
hydroxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate or
pentaerythritol tri(meth)acrylate. In a second approach, this
isocyanate method is modified to enlarge the range of accessible
structures. A portion of the hydroxyfunctional(meth)acrylate
monomers is replaced by other structures having OH groups such as
polyols (such as ethylene glycol, glycerol or hexanediol),
polyester polyols (such as hexanediol/adipic acid OH-terminated
polyester) or polyether polyols (such as polyethyleneglycol,
polypropyleneglycol). Both approaches being based on the above
isocyanate method, both present the same above process-related
drawbacks. Moreover, for a given molecular weight and
(meth)acrylate functionality, urethane(meth)acrylates obtained by
these methods are known to show a high viscosity as compared to the
other oligomers used in radiation curable formulations, one of the
main reasons being the strong hydrogen bonding involving the
protons of the carbamate groups. In the second approach, every
supplemental (meth)acrylate group in the molecule implies the
presence of two supplemental urethane groups if a diisocyanate is
used. In other words, viscosity will increase very much with
(meth)acrylate functionality. This leads to the facts that the
urethane(meth)acrylates obtained by this approach will have to be
of limited (meth)acrylate functionality (typically .ltoreq.3)
and/or will often have to be diluted with an (meth)acrylate monomer
at the end of their synthesis to remain tractable when they will
have to be formulated. Furthermore, radiation-curable formulations
will always have to contain a limited amount of
urethane(meth)acrylate(s) and high amounts of reactive diluents in
order to have a viscosity compatible with industrial application
equipments. Due to these limitations, specific coating properties
that can only be achieved by use of urethane(meth)acrylates, can
thus often not be maximized. The need for high amounts of irritant
and sensitizing reactive diluents precludes the use of
urethane(meth)acrylates in certain applications where the viscosity
of the formulation should be very low (e.g. spray coatings).
[0007] The present invention aims to find an improved process that
overcomes these problems.
[0008] The present invention provides a process for producing
carbamoyloxy(meth)acrylates which comprises the transesterification
of an hydroxyalkyl carbamate of formula (I), (II), (III), (IV),
(V), (VI) or (VII)
##STR00001## ##STR00002##
wherein k.gtoreq.2 n=0 to 2 m=0 to 2 n+m.gtoreq.1 p=n or m, q=n or
m, r=n or m, s=n or m, v=n or m, w=n or m (p+q)=(r+s)=(v+w)=(n+m)
each R.sup.1, each R.sup.2, each R.sup.20 is, independently, chosen
from the group of [0009] hydrogen, [0010] halogen, [0011] hydroxy,
[0012] alkyl, optionally substituted by hydroxy; halogen; aryl
and/or aryl substituted by hydroxy, halogen or alkyl; and
optionally containing from 1 to 8 ether bridges, [0013] alkenyl,
optionally substituted by hydroxy; halogen; aryl and/or aryl
substituted by hydroxy, halogen or alkyl; and optionally containing
from 1 to 8 ether bridges, [0014] aryl, optionally substituted by
hydroxy; halogen; alkyl; alkyl substituted by hydroxy, halogen
and/or aryl; and/or alkyl containing from 1 to 8 ether bridges,
[0015] R.sup.3 is an alkyl, optionally substituted by hydroxy,
tertiary amine and/or aryl, and optionally containing from 1 to 20
ether bridges and/or from 1 to 3 tertiary amine bridges, [0016]
R.sup.4, R.sup.5, R.sup.6, R.sup.12, R.sup.13, R.sup.14, R.sup.15
and R.sup.16 are, independently, chosen from the group of [0017]
hydrogen, and [0018] alkyl, optionally substituted by hydroxy,
tertiary amine and/or aryl, and optionally containing from 1 to 8
ether bridges and/or from 1 to 3 tertiary amine bridges, [0019]
with the proviso that, respectively, R.sup.3 and R.sup.4, R.sup.5
and R.sup.6, R.sup.12 and/or R.sup.13 and/or R.sup.14, R.sup.15 and
R.sup.16 may be linked together in order to form a ring, [0020]
R.sup.7, R.sup.8, R.sup.9, R.sup.10, R.sup.17 and R.sup.18 are,
independently, chosen from alkylene, alkenylene, arylene and
aralkylene chains which may contain from 1 to 8 ether bridges
and/or from 1 to 3 tertiary amine bridges, [0021] R.sup.11 is
hydrogen or alkyl; [0022] R.sup.19, R.sup.21, R.sup.22, R.sup.23,
R.sup.25, R.sup.26, R.sup.27 and R.sup.28, are, independently,
chosen from alkylene, alkenylene, arylene and aralkylene chains
which may contain from 1 to 20 ether bridges, from 1 to 4 tertiary
amine bridges, from 1 to 4 --CO-- bridges and/or from 1 to 4
--O--CO-- bridges; [0023] A is
[0023] ##STR00003## [0024] wherein R.sup.24 is hydrogen or alkyl;
[0025] with a (meth)acrylate of formula (VIII)
[0025] CH.sub.2.dbd.CR.sup.29--COOR.sup.30 (VIII) [0026] wherein
R.sup.29 is hydrogen or methyl, and R.sup.30 represents an alkyl
group comprising from 1 to 8 carbon atoms; in an equivalent ratio
of (meth)acrylate to hydroxylalkyl carbamate higher than 3.5 and in
the presence of an organotitanate, an organozirconate or an
organotin catalyst.
[0027] The term "alkyl", as used herein, is defined as including
saturated, monovalent hydrocarbon radicals having straight,
branched or cyclic moieties or combinations thereof and containing
1 to 50 carbon atoms.
[0028] The term "alkenyl" as used herein, is defined as including
straight and cyclic, branched and unbranched, unsaturated
hydrocarbon radicals having at least one double bond and containing
from 2 to 50 carbon atoms; such as ethenyl (=vinyl),
1-methyl-1-ethenyl, 2-methyl-1-propenyl, 1-propenyl, 2-propenyl
(=allyl), 1-butenyl, 2-butenyl, 3-butenyl, 4-pentenyl,
1-methyl-4-pentenyl, 3-methyl-1-pentenyl, 1-hexenyl, 2-hexenyl, and
the like.
[0029] The term "aryl" as used herein, is defined as including an
organic radical derived from an aromatic hydrocarbon comprising 1
or more rings by removal of one hydrogen, and containing from 5 to
30 carbon atoms, such as phenyl and naphthyl.
[0030] The term "alkoxy", as used herein, is defined as --O-alkyl
groups wherein "alkyl" is as defined above.
[0031] The term "alkylene" as used herein, is defined as including
saturated, divalent hydrocarbon radicals having straight, branched
or cyclic moieties or combinations thereof and containing 1 to 50
carbon atoms.
[0032] The term "alkenylene" as used herein, is defined as
including unsaturated, divalent hydrocarbon radicals having
straight, branched or cyclic moieties or combinations thereof,
containing at least one carbon-carbon double bond and containing 1
to 50 carbon atoms.
[0033] The term "arylene" as used herein, is defined as including
divalent radicals derived from an aromatic hydrocarbon comprising
one or more rings by removal of two hydrogen atoms and containing
from 5 to 30 carbon atoms.
[0034] The term "aralkylene" as used herein, represents a divalent
radical comprising a combination of alkylene and arylene
moieties.
[0035] By alkyl, alkenyl, alkylene, alkenylene, arylene and
aralkylene containing an ether bridge is meant an alkyl, alkenyl,
alkylene, alkenylene, arylene or aralkylene radical wherein a
carbon atom is replaced by an oxygen atom, forming a group such as
--O--C--.
[0036] By alkyl, alkylene, alkenylene, arylene and aralkylene chain
containing tertiary amine bridge is meant such radical wherein a
tertiary amine group is present between 2 carbon atoms, forming a
group of formula --C--NR--C--, wherein R represents an alkyl or
aryl group. In that case, R is preferably an alkyl group containing
from 1 to 15 carbon atoms.
[0037] By alkylene, alkenylene, arylene and aralkylene containing a
--CO--O-- bridge is meant an alkylene, alkenylene, arylene or
aralkylene radical wherein a
##STR00004##
group is present between 2 carbon atoms, forming a group of
formula
##STR00005##
[0038] By alkylene, alkenylene, arylene and aralkylene containing a
--CO-- bridge is meant an alkylene, alkenylene, arylene or
aralkylene radical wherein a
##STR00006##
group is present between 2 carbon atoms.
[0039] The transesterification reaction in the process according to
the invention is preferably effectuated at temperatures of at least
40.degree. C., more preferably of at least 50.degree. C., and most
preferably of at least 60.degree. C. The transesterification
reaction is generally effectuated at a temperature of at most
110.degree. C., more preferably of at most 105.degree. C. When
hydroxyalkyl carbamates bearing only primary hydroxy group(s) such
as those wherein R.sup.1 and R.sup.2 on the same carbon atom as the
--OH are hydrogen, and alkyltitanate catalysts, are used, the
temperature at which the transesterification reaction is conducted
is more preferably of at most 75.degree. C., and most preferably of
at most 70.degree. C.
[0040] The maintenance of the temperature during the
transesterification reaction can be done by any means known
therefore. The maintenance of the temperature is preferably
achieved by distilling off, in general under reduced pressure, the
azeotrope formed by the (meth)acrylate of formula (VIII) with its
corresponding alcohol which is formed during the reaction.
[0041] The catalyst used in the transesterification reaction can be
an organotin catalyst. The organotin catalyst is preferably chosen
from dibutyltin oxide, monobutyltin oxide,
monobutyltindihydroxychloride, n-butyl tin tris(2-ethylhexanoate),
dibutyltindilaurate, dioctyltindilaurate, dibutyltinmaleate,
dibutyltindiacetate, dibutyltindiisooctoate, dibutyltincarboxylate,
dimethyltindichloride, and their mixtures; it is most preferably
dibutyltindilaurate and/or dioctyltindilaurate.
[0042] The catalyst used in the transesterification reaction is
preferably an organotitanate catalyst. The organotitanate catalyst
is preferably chosen from alkyltitanates, more particularly from
tetraalkyltitanates, wherein each alkyl, independently, comprises
from 2 to 8 carbon atoms. More preferred are isopropyltitanate,
n-butyltitanate, ethyltitanate, n-propyltitanate,
2-ethylhexyltitanate and their mixtures. Particularly preferred are
isopropyltitanate, n-butyltitanate and their mixtures.
[0043] The catalyst used in the transesterification reaction is
most preferably an organozirconate catalyst. The latter is
preferably chosen from zirconium acetate, zirconium
acetylacetonate, zirconium hexafluoroacetylacetonate, zirconium
trifluoroacetylacetonate, zirconium propionate, zirconium
2-ethylhexanoate, zirconium t-butoxide, zirconium n-butoxide,
zirconium ethoxide, zirconium n-propoxide, zirconium isopropoxide,
zirconium chloride, zirconium bromide, zirconium fluoride,
zirconium iodide, zirconium oxychloride, zirconium hydrochloride,
zirconium methacrylate and their mixtures; it is most preferably
zirconium acetylacetonate and/or zirconium n-butoxide.
[0044] The organozirconate catalyst is preferably chosen from
alkylzirconates, more particularly from tetraalkylzirconates,
wherein each alkyl, independently, comprises from 2 to 8 carbon
atoms and from zirconium 1,3-diketone chelates, and their
mixtures.
[0045] As described in FR2747675 (Elf Atochem SA), any of these
zirconium catalysts can be doped with .beta.-diketones (e.g.
acetylacetone), esters of ketonic acid (e.g. ethylacetoacetate) or
.beta.-hydroxydiketones (e.g. hydroxybenzophenone).
[0046] The organozirconium catalyst is most preferably chosen from
alkylzirconates, especially zirconium n-butoxide, in combination
with zirconium acetylacetonate and/or a .beta.-diketone, especially
acetylacetone.
[0047] The amount of catalyst used in the transesterification
reaction according to the invention, is preferably such that the
weight ratio of catalyst to the generated
carbamoyloxy(meth)acrylate is at least 0.003, preferably at least
0.005. The weight ratio does preferably not exceed 0.1, most
preferably not 0.09. A too low concentration in catalyst could lead
to unacceptable yields of the desired carbamoyloxy(meth)acrylate;
higher concentrations could lead to the formation of undesirable
side products and/or could influence the properties of the final
product, necessitating or complicating its removal.
[0048] Although not absolutely required, residual catalyst may be
removed from the reaction mixture obtained after the
transesterification reaction. Organotin catalysts may be removed by
one of the methods known in the art. Methods to get rid of tin
catalysts from organic media relies either on adding a reagent that
makes them insoluble in the matrix or washing methods by hydrolytic
treatments. Organotitanate and organozirconate catalysts can be
easily removed by adding any substance (polyol, water, . . . ) able
to react with this catalyst and forming an insoluble precipitate
that can be removed from the reaction mixture.
[0049] In a preferred embodiment of the process according to the
invention, the reaction mixture obtained after the
transesterification reaction is treated with water. The quantity of
water used is preferably in the range of 0.1 to 5 g, most
preferably from 0.5 to 3 g, per g of catalyst present in the
reaction mixture. The treatment with water is preferably done under
agitation, during 10 to 120 minutes, most preferably during 30 to
90 minutes. This treatment is preferably done at a temperature of
60 to 80.degree. C. Titanium hydrolyzates being generally totally
insoluble in the reaction mixture, they can easily be filtrated out
by through standard filtration procedures. Zirconium hydrolyzates
being generally soluble in the water phase, they can be extracted
by water treatment.
[0050] In another preferred embodiment of the process according to
the invention, the reaction mixture obtained after the
transesterification reaction is treated with a polyol that, after
reaction with the catalyst, can form a precipitate. For convenience
of use, the polyol is preferably liquid in standard conditions.
Useful polyols are ethylene glycol, alkoxylated pentaerythritols,
alkoxylated trimethylolpropane, alkoxylated neopentyl glycol,
glycerol. Most preferred polyol is glycerol. The quantity of polyol
used is preferably such that the equivalent ratio of polyol to
organotitanate is higher than 1 and lower than 1.3. By equivalent
ratio of polyol to organotitanate is understood the number of
equivalents of OH present in the polyol to the number of equivalent
of alkyl groups present in the organotitanate catalyst. The
treatment with polyol is preferably done under agitation, during 10
to 120 minutes, most preferably during 30 to 90 minutes. This
treatment is preferably done at a temperature of 60 to 80.degree.
C. When reaction products are of high viscosity (typically >1000
mPas), it has been found that the titanium precipitate obtained by
this way can be sometimes more easily filtrated than by using
water.
[0051] When left in the reaction mixture, the catalyst is
preferably immobilized on a polymer or reacted with a radically
polymerizable compound. This precludes leaching phenomena in the
end application.
[0052] While it is generally preferred not to use any solvent for
the transesterification reaction, the latter may be used, for
example, in order to improve the compatibility of a reagent or a
catalyst so that the reaction mixture is homogeneous throughout the
reaction.
[0053] The amount of (meth)acrylate of formula (VIII) used in the
transesterification reaction according to the invention, is such
that the equivalent ratio of (meth)acrylate to hydroxyalkyl
carbamate is higher than 3.5. By equivalent ratio of (meth)acrylate
to hydroxyalkyl carbamate is understood the number of equivalents
of (meth)acrylate to the number of equivalents of hydroxy groups
present in the hydroxyalkyl carbamate. The equivalent ratio is
preferably at least 4, more preferably at least 4.5. The equivalent
ratio does preferably not exceed 10, most preferably not 8. A too
low amount in (meth)acrylate leads to unacceptable yields of
desired carbamoyloxy(meth)acrylate.
[0054] A part of the excess (meth)acrylate is preferably
continuously distilled as an azeotrope with the corresponding
alcohol formed during the transesterification reaction. The
remaining part of the excess may be removed at the end of the
transesterification reaction by concentration/stripping under
vacuum, preferably under injection of air in order to prevent
polymerization. This remaining part of the excess is preferably
removed after removal of the residual catalyst.
[0055] The transesterification reaction is usually conducted in the
presence of at least one polymerization inhibitor. By
polymerization inhibitor is understood an additive which slows or
inhibits the polymerization of the reactives and/or the formed
products.
[0056] The transesterification reaction is preferably done in the
presence of at least one polymerization inhibitor chosen from
sterically hindered phenol derivatives. By sterically hindered
phenol derivative is meant to designate a molecule containing a
phenyl ring bearing at least one hydroxy group (--OH) and wherein
at least one substituent other than hydrogen is present in ortho
position of the --OH group on the phenyl ring. Preferred are
sterically hindered phenol derivatives wherein a substituent other
than hydrogen is present in each ortho positions of the --OH group,
i.e. o,o'-disubstituted phenols. In this case, both substituents
may be the same or different. The substituent present in ortho of
the --OH group is preferably an alkyl group, most preferably
containing from 1 to 20 carbon atoms. The sterically hindered
phenol derivative may contain different phenol moieties. Preferred
sterically hindered phenol derivatives are chosen from the group of
2,6-di-tert-butyl-4-methylphenol (BHT), 2,6-dimethylphenol,
2,2'-methylenebis(4-methyl-6-(1-methyl-cyclohexyl)phenol),
2,2'-methylenebis(4-methyl-6-tert-butylphenol),
2,2'-methylenebis(4-ethyl-6-tert-butylphenol),
2,4-dimethyl-6-(1-methylpentadecyl)-phenol, alpha-tocopherol
(vitamin E) and their mixtures.
[0057] The amount of sterically hindered phenol derivative present
during the transesterification reaction is in general at least 100
ppm w/w, preferably at least 300 ppm w/w based on the quantity of
carbamoyloxy(meth)acrylate formed. The amount of sterically
hindered phenol derivative preferably does not exceed 5000 ppm w/w,
most preferably not 3000 ppm w/w based on the quantity of final
product formed.
[0058] Instead of, or in addition to, the sterically hindered
phenol derivatives, other phenolic inhibitors may be added during
the transesterification reaction. In a preferred embodiment of the
process according to the invention, less than 1000 ppm, preferably
less than 100 ppm, w/w based on the quantity of
carbamoyloxy(meth)acrylate formed phenolic polymerization inhibitor
other than the sterically hindered phenol derivatives, i.e.
phenolic derivatives wherein the positions in ortho of the --OH
group are hydrogen, are added to the reaction mixture.
[0059] Instead of, or in addition to, the sterically hindered
phenol derivatives, other non-phenolic polymerization inhibitors
may be added during the transesterification reaction. In this case,
the amount of these non-phenolic polymerization inhibitors is
preferably at least 100 ppm w/w based on the quantity of
carbamoyloxy(meth)acrylate formed. In general, this amount does not
exceed 900 ppm, preferably not 500 ppm w/w based on the quantity of
final product formed. Preferred other polymerization inhibitors are
chosen from phenothiazine, triphenylstibine, triphenylphosphine,
quinones (such as para-benzoquinone), nitrones, nitro- and nitroso
compounds (such as nitrobenzene), stable radicals (such as
2,2,6,6-tetramethyl-1-piperidinyloxy and diphenylpicrylhydrazil).
Most preferred non-phenolic inhibitor is phenothiazine.
[0060] In the (meth)acrylates of formula (VIII) used in the process
according to the invention, R.sup.30 is preferably an alkyl
comprising from 1 to 4 carbon atoms, most preferably, methyl, ethyl
or n-butyl.
[0061] The hydroxyalkyl carbamates of formula (I), (II), (III),
(IV), (V), (VI) and (VII) used in the process according to the
invention may be obtained by any method suitable therefore.
[0062] Hydroxyalkyl carbamates of formula (I), (II), (III) and (IV)
are preferably obtained by reacting amines of, respectively,
formula (IX), (X), (XI) and (XII)
##STR00007##
wherein R.sup.3, R.sup.4, R.sup.5, R.sup.6, R.sup.7, R.sup.8,
R.sup.9, R.sup.10, R.sup.11, R.sup.12, R.sup.13, R.sup.14,
R.sup.15, R.sup.16, R.sup.17 and R.sup.18, are defined as here
above, with a cyclic carbonate of formula (XIII)
##STR00008## [0063] wherein R.sup.1, R.sup.2 and k are defined as
here above.
[0064] Hydroxyalkyl carbamates of formula (V), (VI) and (VII) are
preferably obtained by reacting an amine of formula (IX)
##STR00009##
wherein R.sup.3 and R.sup.4 are defined as here above, with,
respectively, a cyclic carbonate of formula (XIV), (XV) and
(XVI)
##STR00010## [0065] wherein R.sup.1, R.sup.2, R.sup.19, R.sup.20,
R.sup.21, R.sup.22, R.sup.23, R.sup.24, R.sup.25, R.sup.26,
R.sup.27, R.sup.28, A, n and m are defined as here above.
[0066] The preparation of the hydroxyalkyl carbamates by the above
mentioned processes is exothermic. Therefore, the reaction
temperature is preferably controlled in order to avoid side
reactions which could give toxic by-products or which could lead to
products which form toxic by-products further in the process
according to the invention. During the preparation processes, the
temperature is in general maintained below 100.degree. C.,
preferably between 40 and 90.degree. C. and most preferably between
50 and 80.degree. C. When a primary amine is used, the reaction may
be so exothermic that it is difficult to maintain the reaction
mixture within the above temperature range. It is then preferred to
add the cyclic carbonate to the amine in order to have a better
control of the reaction temperature.
[0067] During the preparation of the hydroxyalkyl carbamates, the
reaction mixture is preferably sparged with nitrogen. This sparging
with nitrogen helps to avoid moisture that can lead to hydrolysis
of the cyclic carbonate catalyzed by the amine. Sparging with
nitrogen can also help in reducing the color of the hydroxyalkyl
carbamate, especially when readily oxidized amines are used such as
secondary amines or amines with ether groups. Alternatively or in
addition to the sparging with nitrogen, an antioxidant may be used
during the preparation of the hydroxyalkyl carbamates. Preferred
antioxidants are aromatic phosphites, most preferred are
triphenylphosphite or trisnonylphenylphosphite. The amount of these
antioxidants is preferably at least 300 ppm w/w based on the
quantity of hydroxyalkyl carbamate formed. In general, this amount
does not exceed 5000 ppm, preferably not 2000 ppm w/w based on the
quantity of hydroxyalkyl carbamate formed.
[0068] During the preparation of the hydroxyalkyl carbamates, the
equivalent ratio amine to cyclic carbonate is preferably of 1.01 to
1.1 and most preferably, of 1 to 1.05. The equivalent ratio amine
to cyclic carbonate is meant to designate the number of primary and
secondary amine groups of the amine of formula (IX), (X), (XI) or
(XII) per number of cyclic carbonate groups present in the cyclic
carbonates of formula (XIII), (XIV), (XV) or (XVI) used. Especially
when the boiling point of the amine is lower than 100.degree. C. so
that it can be stripped off the reactor under vacuum below this
temperature, it is preferred working with an amine excess to so as
speeding up the reaction. This is especially true for secondary
amines with which reaction times are typically longer due to steric
hindrance around the opening proton.
[0069] During the preparation of the hydroxyalkyl carbamates, a
catalyst can be used. Secondary, higher molecular weight primary or
hindered primary amines may lead to very slow ring opening
reactions, especially when substituent(s) lie on the cyclic
carbonate rings. When these amines are used, it is preferred to use
one or a combination of the known catalysts for this opening
reaction, such as strongly basic amines (such as
diazabicyclooctane, tetramethylguanidine), strongly basic
quaternary ammonium compounds (such as
alkyl(C16-C22)benzyltrimethyl ammonium hydroxide or carbonate and
tetrabutylammonium hydroxide or carbonate), supranucleophilic
catalysts (such as 4-pyrrolidinepyridine,
poly(N,N-dialkylaminopyridine, dimethylaminopyridine), base anions
whose conjugate acid has a pKa of about 11 or more (such as
tert-butoxide).
[0070] While it is preferred not to use any solvent for the
preparation reaction of the hydroxyalkyl carbamates, the latter may
be used, for example, in order to improve the compatibility of a
reagent or a catalyst such as the reaction mixture is homogeneous
throughout the reaction.
[0071] In the hydroxyalkyl carbamates of formula (I), (II), (III),
(IV) and in the cyclic carbonates of formula (XIII) used in the
process according to the invention k is preferably at most 3, most
preferably k is 2.
[0072] In the hydroxyalkyl carbamates of formula (V), (VI) and
(VII) and in the cyclic carbonates of formula (XIV), (XV) and (XVI)
used in the process according to the invention n, m, p, q, r, s, v
and w are, independently, preferably 0 or 1.
[0073] In the hydroxyalkyl carbamates of formula (V), (VI) and
(VII) and in the cyclic carbonates of formula (XIV), (XV) and (XVI)
used in the process according to the invention n+m, p+q, r+s, v+W,
are preferably 1.
[0074] In the hydroxyalkyl carbamates of formula (I), (II), (III),
(IV), (V), (VI) and (VII) and in the cyclic carbonates of formula
(XIII), (XIV), (XV) and (XVI) used in the process according to the
invention each R.sup.1 and each R.sup.2 is, independently,
preferably chosen from the group of hydrogen; alkyl comprising from
1 to 6 carbon atoms, optionally substituted by hydroxy or halogen;
and alkenyl comprising from 1 to 6 carbon atoms; both optionally
containing from 1 to 3 ether bridges.
[0075] In the hydroxyalkyl carbamates of formula (I), (II), (III),
(IV), (V), (VI) and (VII) and in the cyclic carbonates of formula
(XIII), (XIV), (XV) and (XVI) used in the process according to the
invention, preferably, all but one of the R.sup.1 substituents are
hydrogen.
[0076] In these preferred hydroxyalkyl carbamates, all but one of
the R.sup.2 substituents are preferably hydrogen. Most preferably,
in these hydroxyalkyl carbamates, all R.sup.2 substituents are
hydrogen.
[0077] Particularly preferred hydroxyalkyl carbamates of formula
(I), (II), (III) and (IV) and particularly preferred cyclic
carbonates of formula (XIII) are those wherein one of the R.sup.1
substituents is chosen from the group of hydrogen, methyl, ethyl,
hydroxymethyl, chloromethyl, allyloxymethyl, and wherein the
R.sup.2 substituent present on the same carbon atom as this R.sup.1
substituent is chosen from hydrogen and methyl, all other R.sup.1
and all other R.sup.2 substituents being hydrogen.
[0078] Particularly preferred hydroxyalkyl carbamates of formula
(V), (VI) and (VII) and particularly preferred cyclic carbonates of
formula (XIV), (XV) and (XVI) are those wherein each R.sup.1 and
each R.sup.2 is hydrogen.
[0079] In the hydroxyalkyl carbamates of formula (V), (VI) and
(VII) and in the cyclic carbonates of formula (XIV), (XV) and (XVI)
used in the process according to the invention each R.sup.20 is
preferably hydrogen.
[0080] In the hydroxyalkyl carbamates of formula (I), (V), (VI) and
(VII) and in the amines of formula (IX) used in the process
according to the invention R.sup.3 is preferably an alkyl,
optionally substituted by hydroxy, tertiary amine and/or aryl, and
optionally containing from 1 to 20 ether bridges. Most preferably,
R.sup.3 is chosen from the group of alkyl comprising up to 10
carbon atoms, optionally substituted by one hydroxy or tertiary
amine and/or optionally containing one or two ether bridges.
Non-limiting examples are R.sup.3 substituents chosen from the
group of n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl,
tert-butyl, n-hexyl, n-octyl, 2-ethylhexyl, isononyl, cyclopentyl,
cyclohexyl, 2-methylcyclohexyl, N,N-(di-tert-butyl)ethyl, benzyl,
2-(2-hydroxyethoxy)ethyl, 5-hydroxypentyl, 2-hydroxyethyl,
2-hydroxypropyl, 3-hydroxypropyl, 3-(diethylamino)propyl,
2-(diethylamino)ethyl, 1-methyl-4-(diethylamino)butyl,
2-((di-tert-butyl)amino)ethyl, 3-(dimethylamino)propyl,
2-methoxyethyl, 2-ethoxyethyl, 3-methoxypropyl, 2-methoxyisopropyl,
3-ethoxypropyl, 3-isopropoxypropyl, 3-(2-methoxyethoxy)propyl,
3-(2-ethylhexyloxy)propyl,
CH.sub.3--O--(CH.sub.2CH.sub.2O).sub.6--(CH.sub.2CHR--O).sub.10--CH.sub.2-
--CH(CH.sub.3)-- wherein R is H or CH.sub.3 in a proportion of 1:9,
ethyl, methyl, 1,2-dimethylpropyl.
[0081] In the hydroxyalkyl carbamates of formula (I), (V), (VI) and
(VII) and in the amines of formula (IX) used in the process
according to the invention R.sup.4 is preferably chosen from the
group of hydrogen and alkyl, optionally substituted by hydroxy,
tertiary amine or aryl, and optionally containing from 1 to 8 ether
bridges. Most preferably, R.sup.4 is chosen from the group of
hydrogen and alkyl comprising up to 10 carbon atoms, optionally
substituted by one hydroxy or tertiary amine and/or optionally
containing one or two ether bridges. Non-limiting examples are
R.sup.4 substituents chosen from the group of hydrogen, ethyl,
n-propyl, isopropyl, n-hexyl, methyl, tert-butyl, n-butyl,
isobutyl, n-octyl, 2-ethylhexyl, 1,2-dimethylpropyl, cyclohexyl,
2-hydroxyethyl, 2-hydroxyisopropyl, 3-hydroxypropyl,
2-methoxyethyl, 3-(dimethylamino)propyl.
[0082] In the hydroxyalkyl carbamates of formula (I), (V), (VI) and
(VII) and in the amines of formula (IX) used in the process
according to the invention R.sup.4 is more preferably hydrogen and
R.sup.3 is as defined here above, more specifically R.sup.3 is an
alkyl comprising at least 3 carbon atoms and substituted by at
least one hydroxy and optionally containing one or two ether
bridges. Particularly preferred R.sup.4 is hydrogen and R.sup.3 is
2-(2-hydroxyethoxy)ethyl.
[0083] In the hydroxyalkyl carbamates of formula (II), (III), (IV)
and in the amines of formula (X), (XI) and (XII) used in the
process according to the invention R.sup.5, R.sup.6, R.sup.12,
R.sup.13, R.sup.14, R.sup.15 and R.sup.16 are preferably,
independently, chosen from the group of hydrogen and alkyl
comprising up to 10 carbon atoms, most preferably up to 6 carbon
atoms.
[0084] In the hydroxyalkyl carbamates of formula (I), (II), (III),
(IV), (V), (VI) and (VII) and in the amines of formula (IX), (X),
(XI) and (XII) used in the process according to the invention
R.sup.3 and R.sup.4, R.sup.5 and R.sup.6, R.sup.12 and/or R.sup.13
and/or R.sup.14, R.sup.15 and R.sup.16, respectively, may be linked
together in order to form a ring. In this case, these substituents
are preferably linked so that they form an alkylene chain
comprising from 2 to 7 carbon atoms, and optionally containing 1 or
2 ether bridges. In case of R.sup.3 and R.sup.4, this alkylene
chain is preferably such that a 5 to 7-membered ring is formed, for
example a pyrrolidine ring, a piperidine ring or a morpholine ring,
which may further be substituted by alkyl groups. In case of
R.sup.5 and R.sup.6, this alkylene chain is preferably such that a
5 to 7-membered ring is formed, for example piperazine, which may
further be substituted by alkyl groups.
[0085] In the hydroxyalkyl carbamates of formula (II) and in the
amines of formula (X) used in the process according to the
invention R.sup.7 is preferably chosen from the group of alkylene
and aralkylene chains, containing up to 20 carbon atoms and which
may contain from 1 to 8 ether bridges and/or from 1 to 3 tertiary
amine bridges. Most preferably, R.sup.7 is chosen from the group of
ethylene, 1,2-propylene, trimethylene, hexamethylene,
2,2-dimethylpropylene, 1-methyltrimethylene,
1,2,3-trimethyltetramethylene, 2-methyl-pentamethylene, 2,2,4-(or
2,4,4-)trimethylhexamethylene, metaxylylene,
3,5,5-trimethylcyclohexyl-1-ene-3-methylene,
bis(cyclohexyl-4-ene)methane, bis(4-methylcyclohexyl-3-ene)methane,
cyclohexyl-1,3-ene, cyclohexyl-1,4-ene,
1,4-bis(propoxy)-3-ene)butane, N,N-bis(trimethylene)methylamine,
3,6-dioxaoctylene, 3,8-dioxadodecylene, 4,7,10-trioxamidecylene,
poly(oxytetramethylene), poly(oxypropylene) with 2 to 15
1,2-propylene oxide units, poly(oxypropylene-co-oxyethylene) with 2
to 15 propylene oxide and 2 to 15 ethylene oxide units,
2,2-dimethylpropylene.
[0086] In the hydroxyalkyl carbamates of formula (III) and in the
amines of formula (XI) used in the process according to the
invention R.sup.8, R.sup.9, R.sup.10 are preferably, independently,
chosen from the group of alkylene, optionally containing from 1 to
8 ether bridges.
[0087] Most preferably R.sup.8, R.sup.9, R.sup.10 are chosen from
alkylene comprising up to 15 carbon atoms and containing up to 5
ether bridges.
[0088] In the hydroxyalkyl carbamates of formula (IV) and in the
amines of formula (XII) used in the process according to the
invention R.sup.17 and R.sup.18 are preferably, independently,
chosen from the group of alkylene. Most preferably R.sup.17 and
R.sup.18 are chosen from alkylene comprising up to 6 carbon
atoms.
[0089] In the hydroxyalkyl carbamates of formula (III) and in the
amines of formula (XI) used in the process according to the
invention R.sup.11 is preferably hydrogen or an alkyl containing
from 1 to 4 carbon atoms.
[0090] In the hydroxyalkyl carbamates of formula (V) and in the
cyclic carbonates of formula (XIV) used in the process according to
the invention R.sup.19 is preferably chosen from alkylene and
aralkylene chains which may contain from 1 to 20 ether bridges.
Preferred are alkylene and aralkylene chains comprising at least 2
ether bridges.
[0091] In the hydroxyalkyl carbamates of formula (VI) and (VII) and
in the cyclic carbonates of formula (XV) and (XVI) used in the
process according to the invention R.sup.21, R.sup.22, R.sup.23,
R.sup.25, R.sup.26, R.sup.27 and R.sup.28, are preferably,
independently, chosen from alkylene and aralkylene chains which may
contain from 1 to 3 ether bridges.
[0092] In the hydroxyalkyl carbamates of formula (VI) and in the
cyclic carbonates of formula (XV) used in the process according to
the invention R.sup.24 is preferably hydrogen or alkyl comprising
form 1 to 4 carbon atoms.
[0093] Cyclic carbonates such as used in the process according to
the invention are known in the art or can easily be prepared by
known methods. Cyclic carbonates of formula (XIII) wherein k=2 and
cyclic carbonates of formulas (XIV), (XV) and (XVI) wherein n+m,
p+q, r+s or v+w are equal to 1 can easily be prepared by the
reaction of the corresponding epoxides with carbon dioxide. Typical
reaction conditions are described in Kihara, N., Hara, N., Endo,
T., J. Org. Chem., 1993, 58, 6198., J. Org. Chem., 1993, 58,
6198-6202. Some of the catalysts described hereabove for the
preparation of the hydroxyalkyl carbamates by opening of the cyclic
carbonate with the amine, are also known as catalysts for the
reaction between carbon dioxide and an epoxide group. Cyclic
carbonates of formula (XIII) wherein k=2 and cyclic carbonates of
formulas (XIV), (XV) and (XVI) wherein n+m, p+q, r+s or v+w are
equal to 1 can easily be prepared by the reaction of the
corresponding epoxides with carbon dioxide. In this case, it is
preferred to choose a catalyst active for both the formation of the
cyclic carbonate group(s) and their opening by the amine.
[0094] Cyclic carbonates of formula (XIII) wherein k=3 can be
prepared by transesterification of propane-1,3-diols with dialkyl
carbonates such as described for example in Hu, B., Zhuo, R. X.,
Fan, C. L., Polym. Adv. Technol., 1998, 9, 145. Cyclic carbonates
of formulas (XIV), (XV) and (XVI) wherein n+m, p+q, r+s or v+w are
equal to 2 can be prepared by transesterification of polyols
containing several propane-1,3-diols groups such as
ditrimethylolpropane with dialkyl carbonates. They can also be
obtained by reacting 6-membered cyclic carbonates containing one
functional group such as OH group in
5-ethyl-5-hydroxymethyl-1,3-dioxan-2-one with coupling agents such
as multifunctional chloroformates.
[0095] Cyclic carbonates of formula (XIII) wherein k>3 and
cyclic carbonates of formulas (XIV), (XV) and (XVI) wherein n+m,
p+q, r+s or v+w are >2 can be prepared according to the same
transesterification reaction pathways as that leading to the
lower-membered rings (Matsuo, J. et al., J. Polym. Sci. A: Polym.
Chem., 1997, 35, 1375).
[0096] Cyclic carbonates of formula (XIII) which are particularly
useful in the process according to the invention are
1,3-dioxolan-2-one (ethylene carbonate),
4-methyl-1,3-dioxolan-2-one(propylene carbonate),
4-ethyl-1,3-dioxolan-2-one(butylene carbonate),
4-hydroxymethyl-1,3-dioxolan-2-one (glycerine carbonate),
4-chloromethyl-1,3-dioxolan-2-one,
4-allyloxymethyl-1,3-dioxolan-2-one, 5,5-dimethyl-1,3-dioxan-2-one,
(neopentylglycol carbonate).
[0097] Cyclic carbonates of formulas (XIV), (XV) and (XVI) which
are particularly useful in the process according to the invention
are those obtained from the reaction of carbon dioxide with
polyepoxide compounds, such as the polyglycidyl ethers of aliphatic
or aromatic polyols, such as, for example, 1,4-butanediol,
neopentylglycol, cyclohexanedimethanol, diethyleneglycol,
polyethyleneglycol, dipropyleneglycol, polypropyleneglycol,
2,2,4-trimethyl-1,3-pentanediol, 1,6-hexanediol,
trimethylolpropane, trimethylolethane, glycerol,
4,4'-isopropylidenediphenol, 1,1,1-tris(4-hydroxyphenyl)ethane,
hydroquinone, 4,4'-bisphenol, 2,2'-bisphenol,
4,4'-dihydroxybenzophenone, 1,5-dihydroxynaphthalene, resorcinol.
Preferred are the polyglycidyl ethers of aliphatic polyols, and
most preferred the diglycidyl ether of polypropyleneglycol
containing from 2 to 15 1,2-propylene oxide units.
[0098] Amines of formula (IX), (X), (XI) and (XII) are known in the
art. Amines of formula (IX) which are particularly useful in the
process according to the invention are n-propylamine,
isopropylamine, n-butylamine, isobutylamine, sec-butylamine,
tert-butylamine, 3-methylbutylamine, n-hexylamine, n-octylamine,
2-ethylhexylamine, isononylamine, cyclopentylamine,
cyclohexylamine, 2-methylcyclohexylamine,
N,N-(di-tert-butyl)ethyleneamine, benzylamine,
2-(2-aminoethoxy)ethanol, 5-aminopentanol, ethanolamine,
1-aminopropan-2-ol, 3-amino-1-propanol,
3-(diethylamino)propylamine, 2-(diethylamino)ethylamine,
1-methyl-4-(diethylamino)butylamine,
2,2-(di-tert-butylamino)ethylamine, 3-(dimethylamino)propylamine,
2-methoxyethylamine, 2-ethoxyethylamine, 3-methoxypropylamine,
1-methoxyisopropylamine, 3-ethoxypropylamine,
3-isopropoxypropylamine, 3-(2-methoxyethoxy)propylamine,
3-(2-ethylhexyloxy)propylamine,
.alpha.-oxymethyl-.omega.-(2-propylamino)-poly(oxypropylene-co-oxyethylen-
e) with an average number of 1,2-propylene oxide units of 9 and an
average number of ethylene oxide units of 7, also known as
Jeffamine.RTM. M-600 (manufactured by Hunstman), diethylamine,
di-n-propylamine, diisopropylamine, di-n-hexylamine,
N-methylbutylamine, N-ethylbutylamine, di-n-butylamine,
diisobutylamine, di-n-octylamine, bis(2-ethylhexyl)amine,
N-ethyl-1,2-dimethylpropylamine, dicyclohexylamine,
cyclohexylmethylamine, cyclohexylethylamine, N-methylbenzylamine,
2-methylaminoethanol, 2-ethylaminoethanol, 2-butylaminoethanol,
diethanolamine, diisopropanolamine,
3-(2-hydroxyethyl)aminopropanol, bis(2-methoxyethyl)amine,
bis(3-dimethylaminopropyl)amine, pyrrolidine, piperidine,
morpholine, 2,6-dimethylmorpholine.
[0099] Amines of formula (X) which are particularly useful in the
process according to the invention are ethylenediamine,
1,2-propylenediamine, trimethylenediamine, hexamethylenediamine,
2,2-dimethylpropane-1,3-diamine, 1-methyl-1,3-propanediamine,
1,2,3-trimethyl-1,4-butanediamine, 2-methyl-1,5 diaminopentane,
2,2,4-(or 2,4,4-)trimethylhexamethylene diamine,
metaxylylenediamine, 1-amino-3-aminomethyl-3,5,5
trimethylcyclohexane (isophorone diamine),
bis-(4-aminocyclohexyl)-methane,
bis-(4-amino-3-methyl-cyclohexyl)-methane, 1,3-cyclohexanediamine,
1,4-cyclohexanediamine, 1,4-Bis(3-aminopropoxy)butane diamine,
N,N-bis(3-aminopropyl)methylamine, triethyleneglycol diamine,
3,3'-(butane-1,4-diylbis(oxy))bispropaneamine,
4,7,10-trioxamidecan-1,13-diamine,
.alpha.-amino-.omega.-(4-butylamino)-poly(oxytetramethylene),
.alpha.-amino-.omega.-(2-propylamino)-poly(oxypropylene) with an
average number of 1,2-propylene oxide units of 2.6, also known as
Jeffamine.RTM. D-230 (manufactured by Hunstman),
.alpha.-amino-.omega.-(2-propylamino)-poly(oxypropylene) with an
average number of 1,2-propylene oxide units of 5.6, also known as
Jeffamine.RTM. D-400 (manufactured by Hunstman),
.alpha.-amino-.omega.-(2-propylamino)-poly(oxypropylene-co-oxyethylene)
with an average number of 1,2 propylene oxide units of 2.5 and
ethylene oxide units of 8.5, also known as Jeffamine.RTM. ED-600
(manufactured by Hunstman), N,N'-dimethyl-1,3-propanediamine,
N,N'-di-tert-butyl-ethanediamine, N,N'-dimethylhexyl-1,6-diamine,
piperazine, 2,5-dimethylpiperazine.
[0100] Amines of formula (XI) that are particularly useful in the
process according to the invention is propoxylated
trimethylopropane triamine with an average number of number of
1,2-propylene oxide units of 5.3, also known as Jeffamine.RTM.
T-403 (manufactured by Hunstman).
[0101] Amines of formula (XII) that are particularly useful in the
process according to the invention are
N,N-dimethyldipropylenetriamine, bis(hexamethylene)triamine.
[0102] The process according to the invention permits to produce
low color carbamoyloxy(meth)acrylates, having a color index of
below 2 Gardner, as measured according to ASTM D 1544-68.
[0103] The process according to the invention permits to obtain
carbamoyloxy(meth)acrylates of high purity, containing no or less
toxic side products than the processes disclosed in the prior art,
even without the use of extra purification procedures. The process
according to the invention permits to obtain products containing no
residual isocyanates and no hydroxyethyl(meth)acrylate. The process
according to the invention also presents the advantage that cheap
and safe raw materials can be used. The process involving nor toxic
raw materials nor highly exothermic reactions leading to
atmospheric pollution with toxic materials, standard industrial
equipments and safety procedures can be used at larger scale.
[0104] The process according to the invention permits to obtain new
carbamoyloxy(meth)acrylates not known in the prior art, most of
which are not obtainable by the current commercial processes such
as the isocyanate process.
[0105] The present invention also relates to new
carbamoyloxy(meth)acrylates that can be obtained with the process
according to the present invention. The invention also relates to
carbamoyloxy acrylates of formula (XVII), (XVIII), (XIX), (XX),
(XXI), (XXII), (XXIII), (XXIV), (XXV) and (XXVI)
##STR00011## ##STR00012## ##STR00013## ##STR00014## [0106] wherein
[0107] k, n, m, p, q, r, s, v, w, A, R.sup.7, R.sup.8, R.sup.9,
R.sup.10, R.sup.17, R.sup.18, R.sup.11, R.sup.19, R.sup.21,
R.sup.22, R.sup.23, R.sup.24, R.sup.25, R.sup.26, R.sup.27,
R.sup.28 and R.sup.29 are as defined here above, [0108] t.gtoreq.3
[0109] R.sup.37 is an alkyl substituted by a tertiary amine, and
optionally containing from 1 to 20 ether bridges and/or from 1 to 3
tertiary amine bridges; or an alkyl containing from 1 to 20 ether
bridges and/or from 1 to 3 tertiary amine bridges, optionally
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, tertiary amine
and/or aryl; [0110] each R.sup.38, each R.sup.40 is, independently,
such as defined for R.sup.31 with the proviso that at least one
R.sup.38 and at least one R.sup.40 is chosen from the group of
[0111] halogen [0112] --O--CO--CR.sup.29.dbd.CH.sub.2, [0113] alkyl
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen; aryl
and/or aryl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen
or alkyl; and optionally containing from 1 to 8 ether bridges,
[0114] alkyl containing from 1 to 8 ether bridges, [0115] alkenyl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen;
aryl and/or aryl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
halogen or alkyl; and optionally containing from 1 to 8 ether
bridges, [0116] aryl, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2; halogen; alkyl; alkyl substituted
by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen and/or aryl; and/or
alkyl containing from 1 to 8 ether bridges [0117] R.sup.39 is
2-methyl-1,5-pentamethylene, or R.sup.39 is chosen from alkylene
containing from 1 to 8 ether bridges and/or from 1 to 3 tertiary
amine bridges; alkenylene, arylene and aralkylene chains each of
which may contain from 1 to 8 ether bridges and/or from 1 to 3
tertiary amine bridges, or R.sup.39 is chosen from alkylene when at
least one of R.sup.35 and R.sup.36 is different from hydrogen,
[0118] each R.sup.31, each R.sup.32, each R.sup.50 is,
independently, chosen from the group of [0119] hydrogen, [0120]
halogen [0121] --O--CO--CR.sup.29.dbd.CH.sub.2, [0122] alkyl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen;
aryl and/or aryl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
halogen or alkyl; and optionally containing from 1 to 8 ether
bridges [0123] alkenyl, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2; halogen; aryl and/or aryl
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, halogen or alkyl;
and optionally containing from 1 to 8 ether bridges [0124] aryl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2; halogen;
alkyl; alkyl substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
halogen and/or aryl; and/or alkyl containing from 1 to 8 ether
bridges [0125] R.sup.33 is an alkyl, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2, tertiary amine and/or aryl, and
optionally containing from 1 to 20 ether bridges and/or from 1 to 3
tertiary amine bridges, [0126] R.sup.34, R.sup.35, R.sup.36,
R.sup.42, R.sup.43, R.sup.44, R.sup.45 and R.sup.46 are,
independently, chosen from the group of [0127] hydrogen, and [0128]
alkyl, optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2,
tertiary amine and/or aryl, and optionally containing from 1 to 8
ether bridges and/or from 1 to 3 tertiary amine bridges, [0129]
with the proviso that, respectively, R.sup.33 and R.sup.34,
R.sup.35 and R.sup.36, R.sup.42 and/or R.sup.43 and/or R.sup.44,
R.sup.45 and R.sup.46 may be linked together in order to form a
ring.
[0130] In the carbamoyloxy(meth)acrylates of formula (XVII), t is
preferably 3.
[0131] In the carbamoyloxy(meth)acrylates of formula (XVIII),
R.sup.37 is preferably chosen from the group of alkyl comprising up
to 10 carbon atoms substituted by alkoxy comprising less than 6
carbon atoms or tertiary amine and/or optionally containing one or
two ether bridges; and alkyl comprising up to 10 carbon atoms,
containing one or two ether bridges and substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2. Non-limiting examples are R.sup.37
substituents chosen from the group of N,N-(di-tert-butyl)ethyl,
3-(diethylamino)propyl, 2-(diethylamino)ethyl,
2-methyl-4-(diethylamino)butyl, 2,2-(di-tert-butylamino)ethyl,
3-(dimethylamino)propyl, 2-methoxyethyl, 2-ethoxyethyl,
3-methoxypropyl, 1-methoxyisopropyl, 3-ethoxypropyl,
3-isopropoxypropyl, 3-(2-methoxyethoxy)propyl,
3-(2-ethylhexyloxy)propyl,
CH.sub.3--O--(CH.sub.2CH.sub.2O).sub.6--(CH.sub.2CHR--O).sub.10--CH.sub.2-
--CH(CH.sub.3)-- wherein R is H or CH.sub.3 in a proportion of 1:9,
--CH.sub.2--CH.sub.2--O--CH.sub.2--CH.sub.2--O--CO--CR.sup.29.dbd.CH.sub.-
2.
[0132] In the carbamoyloxy(meth)acrylates of formula (XVIII),
R.sup.34 is preferably hydrogen and R.sup.37 is as described here
above, more specifically R.sup.37 is alkyl comprising at least 3
carbon atoms, containing one or two ether bridges and substituted
by --O--CO--CR.sup.29.dbd.CH.sub.2
[0133] In the carbamoyloxy(meth)acrylates of formula (XIX) and
(XXI), each R.sup.38, each R.sup.40 is, preferably, independently,
such as defined for R.sup.31 with the proviso that at least one
R.sup.38 and at least one R.sup.40 is chosen from the group of
[0134] alkyl comprising from 1 to 6 carbon atoms and substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2 or halogen; and optionally
containing from 1 to 3 ether bridges [0135] alkenyl comprising from
1 to 6 carbon atoms, and optionally containing from 1 to 3 ether
bridges.
[0136] Most preferably, only one of R.sup.38 and only one of
R.sup.40 is chosen from the group of alkyl comprising from 1 to 6
carbon atoms and substituted by --O--CO--CR.sup.29.dbd.CH.sub.2 or
halogen; and optionally containing from 1 to 3 ether bridges; and
alkenyl comprising from 1 to 6 carbon atoms, and optionally
containing from 1 to 3 ether bridges; all other R.sup.38 and
R.sup.40 groups being hydrogen. Particularly preferred
carbamoyloxy(meth)acrylates of formula (XIX) are those wherein one
of the R.sup.38 substituents is chosen from the group of methyl
substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, chloromethyl and
allyloxymethyl, all other R.sup.38 and all R.sup.32 being
hydrogen.
[0137] In the carbamoyloxy(meth)acrylates of formula (XX), R.sup.39
is preferably chosen from 2-methyl-1,5-pentamethylene, from
alkylene containing up to 20 carbon atoms and containing from 1 to
8 ether bridges and/or from 1 to 3 tertiary amine bridges and from
aralkylene chains containing up to 20 carbon atoms and which may
contain from 1 to 8 ether bridges and/or from 1 to 3 tertiary amine
bridges. Most preferred are poly(oxypropylene) with 2 to 15
1,2-propylene oxide units and poly(oxypropylene-co-oxyethylene)
with 2 to 15 propylene oxide and 2 to 15 ethylene oxide units.
[0138] In the carbamoyloxy(meth)acrylates of formula (XVII),
(XVIII), (XIX), (XX), (XXI), (XXII), (XXIII), (XXIV), (XXV) and
(XXVI), each R.sup.31 and each R.sup.32 is, independently,
preferably chosen from the group of hydrogen; alkyl comprising from
1 to 6 carbon atoms, optionally substituted by
--O--CO--CR.sup.29.dbd.CH.sub.2 or halogen; and alkenyl comprising
from 1 to 6 carbon atoms; both optionally containing from 1 to 3
ether bridges.
[0139] In the carbamoyloxy(meth)acrylates of formula (XVII),
(XVIII), (XX), (XXI), (XXII), (XXIII), (XXIV), (XXV) and (XXVI),
preferably, all but one of the R.sup.31 substituents are hydrogen.
In these preferred carbamoyloxy(meth)acrylates, all but one of the
R.sup.32 substituents are preferably hydrogen. Most preferably, in
these carbamoyloxy(meth)acrylates, all R.sup.32 substituents are
hydrogen.
[0140] Particularly preferred carbamoyloxy(meth)acrylates of
formula (XVII), (XVIII), (XX), (XXI), (XXII) and (XXIII) are those
wherein one of the R.sup.31 substituents is chosen from the group
of hydrogen, methyl, ethyl,
--CH.sub.2--O--CO--CR.sup.29.dbd.CH.sub.2, chloromethyl,
allyloxymethyl, and wherein the R.sup.32 substituent present on the
same carbon atom as this R.sup.31 substituent is chosen from
hydrogen and methyl, all other R.sup.31 and all other R.sup.32
substituents being hydrogen.
[0141] Particularly preferred carbamoyloxy(meth)acrylates of
formula (XVIII) are those wherein all R.sup.31 and all R.sup.32
substituents are hydrogen.
[0142] Particularly preferred carbamoyloxy(meth)acrylates of
formula (XXIV), (XXV) and (XXVI) are those wherein n+m, p+q, r+s
and v+w are equal to 1, and more particularly those wherein each
R.sup.31, each R.sup.32 and each R.sup.50 is hydrogen.
[0143] In the carbamoyloxy(meth)acrylates of formula (XVII), (XIX),
(XXIV), (XXV) and (XXVI), R.sup.33 is preferably an alkyl,
optionally substituted by --O--CO--CR.sup.29.dbd.CH.sub.2, tertiary
amine and/or aryl, and optionally containing from 1 to 20 ether
bridges. Most preferably, R.sup.33 is chosen from the group of
alkyl comprising up to 10 carbon atoms, optionally substituted by
one --O--CO--CR.sup.29.dbd.CH.sub.2 group or tertiary amine and/or
optionally containing one or two ether bridges. Non-limiting
examples are R.sup.33 substituents chosen from the group of
n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl,
n-hexyl, n-octyl, 2-ethylhexyl, isononyl, cyclopentyl, cyclohexyl,
2-methylcyclohexyl, N,N-(di-tert-butyl)ethyl, benzyl,
--CH.sub.2--CH.sub.2--O--CH.sub.2--CH.sub.2--O--CO--CR.sup.29.dbd.CH.sub.-
2, --(CH.sub.2).sub.5--O--CO--CR.sup.29.dbd.CH.sub.2,
--(CH.sub.2).sub.2--O--CO--CR.sup.29.dbd.CH.sub.2,
--CH.sub.2--CH(CH.sub.3)--O--CO--CR.sup.29.dbd.CH.sub.2,
--(CH.sub.2).sub.3--O--CO--CR.sup.29.dbd.CH.sub.2,
3-(diethylamino)propyl, 2-(diethylamino)ethyl,
4-(diethylamino)pentyl 2-methyl-4-(diethylamino)butyl,
3-(tert-butylamino)ethyl 2,2-di(tert-butyl)ethyl,
3-(dimethylamino)propyl, 2-methoxyethyl, 2-ethoxyethyl,
3-methoxypropyl, 1-methoxyisopropyl, 3-ethoxypropyl,
3-isopropoxypropyl, 3-(2-methylethoxypropyl
3-(2-methoxyethoxypropyl, 3-(2-ethylhexyloxy)propyl,
CH.sub.3--O--(CH.sub.2CH.sub.2O).sub.6--(CH.sub.2CHR--O).sub.10--CH.sub.2-
--CH(CH.sub.3)-- wherein R is H or CH.sub.3 in a proportion of 1:9,
ethyl, methyl, 1,2-dimethylpropylamine.
[0144] In the carbamoyloxy(meth)acrylates of formula (XVII),
(XVIII), (XIX), (XXIV), (XXV) and (XXVI), R.sup.34 is preferably
chosen from the group of hydrogen and alkyl, optionally substituted
by --O--CO--CR.sup.29.dbd.CH.sub.2, tertiary amine and/or aryl, and
optionally containing from 1 to 8 ether bridges. Most preferably,
R.sup.34 is chosen from the group of hydrogen and alkyl comprising
up to 10 carbon atoms, optionally substituted by one
--O--CO--CR.sup.29.dbd.CH.sub.2 group or tertiary amine and/or
optionally containing one or two ether bridges. Non-limiting
examples are R.sup.34 substituents chosen from the group of
hydrogen, ethyl, n-propyl, isopropyl, n-hexyl, methyl, tert-butyl,
n-butyl, isobutyl, n-octyl, 2-ethylhexyl, 1,2-dimethylpropyl,
cyclohexylamine, --(CH.sub.2).sub.2--O--CO--CR.sup.29.dbd.CH.sub.2,
--CH.sub.2--CH(CH.sub.3)--O--CO--CR.sup.29.dbd.CH.sub.2,
--(CH.sub.2).sub.3--O--CO--CR.sup.29.dbd.CH.sub.2, 2-methoxyethyl,
3-(dimethylamino)propyl.
[0145] In the carbamoyloxy(meth)acrylates of formula (XX), (XXI),
(XXII) and (XXIII), R.sup.35, R.sup.36, R.sup.42, R.sup.43,
R.sup.44, R.sup.45 and R.sup.46 are preferably, independently,
chosen from the group of hydrogen and alkyl comprising up to 10
carbon atoms, most preferably up to 6 carbon atoms.
[0146] In the carbamoyloxy(meth)acrylates of formula (XVII),
(XVIII), (XIX), (XX), (XXI), (XXII), (XXIII), (XXIV), (XXV) and
(XXVI), R.sup.33 and R.sup.34, R.sup.35 and R.sup.36, R.sup.42
and/or R.sup.43 and/or R.sup.44, R.sup.45 and R.sup.46,
respectively, may be linked together in order to form a ring. In
this case, these substituents are preferably linked so that they
form an alkylene chain comprising from 2 to 7 carbon atoms, and
optionally containing 1 or 2 ether bridges. In case of R.sup.33 and
R.sup.34, this alkylene chain is preferably such that a 5 to
7-membered ring is formed, for example a pyrrolidine ring, a
piperidine ring or a morpholine ring, which may further be
substituted by alkyl groups. In case of R.sup.35 and R.sup.36, this
alkylene chain is preferably such that a 5 to 7-membered ring is
formed, for example piperazine, which may further be substituted by
alkyl groups.
[0147] Carbamoyl(meth)acrylates of formula (XVII), (XVIII), (XIX),
(XX), (XXI), (XXII), (XXIII), (XXIV), (XXV) and (XXVI) wherein
R.sup.34, at least one of R.sup.35 and R.sup.36, at least one of
R.sup.42, R.sup.43 and R.sup.44 and at least one of R.sup.45 and
R.sup.46 are different from hydrogen are another aspect of the
invention.
[0148] The carbamoyloxy(meth)acrylates according to the invention
are useful in the manufacture of radiation curable compositions.
The carbamoyloxy(meth)acrylates according to the invention can be
used in any known radiation-curable coating compositions (e.g. for
wood, glass fibers, etc.), printing inks, photoresists, adhesives,
decoration for paper, glass and packages, gravure images and other
applications containing (meth)acrylates with carbamate
residues.
[0149] The carbamoyloxy(meth)acrylates according to the invention
having a molecular weight lower than 400 are very useful as
reactive diluents in radiation curable compositions. The
carbamoyloxy(meth)acrylates according to the invention having a
molecular weight of at least 400, preferably higher than 400 and
most preferably not exceeding 3000, can be used as oligomers in
radiation curable compositions.
[0150] The carbamoyloxy(meth)acrylates of formula (XXIV), (XXV) and
(XVI) have in general a much lower viscosity as compared to
existing carbamoyloxy(meth)acrylates having similar molecular
weights and same acrylate functionality.
[0151] The new low viscous carbamoyloxy(meth)acrylates allow
reducing significantly the amount of reactive diluents needed to
make the radiation-curable formulations. This allows maximizing
properties specifically brought by (meth)acrylates with carbamate
residues (adhesion, abrasion resistance . . . ) and makes possible
the use of carbamoyloxy(meth)acrylates to applications where the
viscosity of the formulation should be very low, such as spray
coatings. Besides lowering the overall irritancy and smell of the
formulation, reducing the amount of reactive diluents also allows
reducing the well-known detrimental effect(s) the latter may have
on specific coatings and inks properties. For example, reducing the
amount of reactive diluents in UV parquet topcoats formulations is
indeed well-known to improve significantly their abrasion
resistance. In radiation-curable flexographic inks and varnishes
used in food packaging, reducing the amount of reactive diluents
are known to reduce significantly migration and off-odor
problems.
EXAMPLES
Example 1
Preparation of N-Butyl Acryloyloxy Ethyl Carbamate
##STR00015##
[0152] 1/Preparation of 2-Hydroxyethyl Butyl Carbamate from Butyl
Amine and Ethylene Carbonate
[0153] 253.4 g (3.47 moles) of butylamine was charged in a
double-wall glass reactor with a capacity of 2 l sparged with
nitrogen. The reactor was fitted with an agitator, a thermometer, a
gas inlet tube, a double-wall glass addition funnel, a connection
to vacuum and an vacuum-jacketed distillation column. A liquid
semi-automatic splitter using a solenoid-activated PTFE valve and
timer was used to control the reflux and takeoff from the
distillation column into a cooled double-walled receiving flask.
The splitter and a double-walled condenser connected to a cooling
unit (-5.degree. C.) were fitted on top of the distillation
column.
[0154] 277.4 g (3.15 moles, equivalent ratio amine to cyclic
carbonate=1.1) of pre-melted ethylene carbonate (EC, sold by
Hunstman) was slowly added from the funnel at a temperature of
45.degree. C. Addition rate was chosen such as that the temperature
in the reactor did not exceed 60.degree. C.
[0155] Titration of the amine indicated that the reaction was
complete at the end of the alimentation. The amine excess was
stripped at 60.degree. C. for 2 hours. A GC characterization of the
hydroxycarbamate indicated that a >98% w/w pure product is
obtained. 300 ppm free ethylene glycol was detected, but may be
accounted entirely for the ethylene glycol coming from the starting
ethylene carbonate (600 ppm).
[0156] 2/Acrylation of 2-Hydroxyethyl Butyl Carbamate by
Transesterification
[0157] Transesterification of 2-hydroxyethyl butyl carbamate was
carried out adding 1220 g (14.2 moles, equivalent ratio alkyl
acrylate to hydroxyalkyl carbamate=4.5) methyl acrylate, 300 ppm on
end product of 2,6-di-tert-butyl-4-methylphenol (BHT) and 300 ppm
on end product phenothiazine (PTZ). At this stage, air was injected
throughout the reaction mixture.
[0158] Before adding the catalyst, about 10% of extra methyl
acrylate (120 g) was added in the reactor and this extra amount was
distilled over at 73.degree. C. in order to dry the reaction
mixture (b.p. water/methylacrylate azeotrope=72.degree. C.). At
this stage, the water content dropped below 100 ppm as measured by
coulometry.
[0159] After addition of a mixture containing 80/20 w/w isopropyl
titanate/n-butyl titanate (Tyzor TPT-20B manufactured by Dupont)
(24 g, weight ratio of catalyst to the generated
carbamoyloxy(meth)acrylate=0.035)), the reaction mixture was
maintained at 65.degree. C. by applying a slight vacuum (600 mmHg)
and the methanol generated was taken off overhead as a
methanol/methyl acrylate azeotrope, such a removal being followed
by a temperature sensor located at the column's head. The azeotrope
was removed as soon as the temperature at the top of the column
dropped down to 50.degree. C. Refractive index measurements of the
distillate showed that at this temperature the azeotrope
composition is near to theoretical (54% w/w methanol). The reaction
was continued until a measure of the refractive index indicated
that no more methanol was present in the distillate. Reaction time
was 10.5 hours.
3/Work-Up
[0160] After complete reaction, the catalyst was hydrolyzed by
adding water (3 g per g catalyst). Stirring vigorously the mixture
at 70.degree. C. for 1.5 hour was found sufficient for complete
hydrolysis of the catalyst, as evidenced by the disappearance of
the yellowish color of the organic phase.
[0161] Diatomaceous earth was added to the reaction mixture to aid
the filtration of the white precipitate thus obtained. Vacuum
filtration occurred utilizing a side-arm filtering flask and a
3-liter filter funnel wherein an diatomaceous earth bed had been
deposited on a paper filter. Less than 30 minutes was needed to
obtain a clear mixture.
[0162] The methyl acrylate excess was removed by
concentration/stripping under vacuum (100 mmHg) at 75.degree. C.
for 2 hours. Air was injected during concentration/stripping to
prevent polymerization. The final product was almost colorless and
contained 6 ppm residual titanium as measured by atomic absorption
spectrometry.
Comparative Example 2R
Preparation of n-Butyl Acryloyloxy Ethyl Carbamate by the Direct
Esterification Method
[0163] 1/Acrylation of 2-Hydroxyethyl Butyl Carbamate by Direct
Esterification
[0164] Direct esterification of 2-hydroxyethyl butyl carbamate
prepared such as described in Example 1 (1/) was carried out adding
to a double-wall glass reactor (1.5 l) fitted with an agitator, a
thermometer, a gas inlet tube, a connection to vacuum and an
azeotropic distillation column having a Dean-Stark separator at its
overhead, 332 g (2 moles) 2-hydroxyethyl butyl carbamate, 202 g
(2.8 moles) acrylic acid, 350 g toluene (37% by weight of the
reacting mixture), 500 ppm on end product methyl ether hydroquinone
(MeHQ), and 0.1% on end product H.sub.3PO.sub.2. PTSA
(p-toluenesulfonic acid, 70 g) was added to reach an end
concentration of 18% mol on starting hydroxyalkyl carbamate. An air
sparge was injected to prevent gelation.
[0165] Pressure was reduced in the reaction vessel to about 350
mmHg in order to allow reflux of a toluene/water azeotrope. The
mixture was heated to 70.degree. C. and stirred until no more water
was distilled over. After 6 hours, 33 g (77% of the theoretical
value) of esterification water was collected in the Dean Stark.
2/Work-Up
[0166] When no more water was distilled over, the mixture was
cooled to 60.degree. C. and neutralized by the addition of 140 g of
a 50% solution of NaOH in water. This mixture was washed three
times with 20% by weight of the reacting mixture with water
containing 20% NaCl, dried via azeotropic distillation with air
sparging to remove all the water and finally filtered. The toluene
was distilled and stripped under vacuum (30 mmHg) to remove all
traces of toluene. Air was sparged to prevent
polymerization/gelation.
Comparative Example 3R
Preparation of n-Butyl Acryloyloxy Ethyl Carbamate by
Transesterification Using a Lower Amount of Methylacrylate
[0167] Example 1 was repeated, except that the transesterification
of 2-hydroxyethyl butyl carbamate was carried out by adding 809.3 g
(9.4 moles, equivalent ratio alkylacrylate to hydroxyalkyl
carbamate=3) methyl acrylate.
[0168] The reaction was continued until a measure of the refractive
indicated that no more methanol was present in the distillate.
Reaction time was 14.5 hours.
[0169] The table here below gives the results (GC compositions)
obtained in the different examples, together with the analysis of
Genomer 1122 (commercial product supplied by Rahn, as which was
prepared by the isocyanate method).
TABLE-US-00001 Purity BuNCO* HEA.sup.x MA.sup.+ Color Product (%
w/w) (% w/w) (% w/w) (% w/w) (Apha) Example 1 96.5 n.d. n.d. n.d.
36 Comparative 75 n.d. 0.8 n.d. 25 Example 2R Genomer .RTM. 94.4
0.25 0.2 n.d. 15 1122 Comparative 77.2 n.d. 0.12 n.d. 41 example 3R
*butyl isocyanate. .sup.xhydroxyethyl acrylate. .sup.+methyl
acrylate.
[0170] These results clearly show that the process according to the
invention gives, at the same time, very good purity, no or very low
amount of toxic by-products and very low coloration.
Example 4
Preparation of n-Butyl Acryloyloxy Ethyl Carbamate Using an
Organotin Catalyst
[0171] Example 1 was repeated, except that the organotitanate
catalyst Tyzor TPT-20B was replaced by n-butyl tin
tris(2-ethylhexanoate). The catalyst concentration was chosen such
as Sn content was the same as Ti content in Example 1.
[0172] The same results as in Example 1 were obtained except that
the transesterification reaction was complete only after 16 h,
hence compared to the organotitanate catalyst, the reaction rate
was lower.
Example 5
Preparation of 2-Propenoic Acid,
3,8-dioxo-7-oxa-6-azaethane-1,10-diyl Ester
##STR00016##
[0174] The starting hydroxyalkyl carbamate was obtained by adding
139.2 g (1.58 moles) EC on 166.1 g (1.58 moles)
2-(2-aminoethoxyethanol) (equivalent ratio amine to cyclic
carbonate=1) in same conditions as in Example 1, except that an
aromatic phosphite was also added (trisnonylphenylphosphite, 2000
ppm based on the quantity of hydroxyalkyl carbamate formed) in
order to avoid oxidation of the amine. Titration of the amine
indicated that the reaction was completed after maintaining the
reaction mixture 3 hours at 60.degree. C. after at the end of the
alimentation. A GC characterization of the hydroxyalkyl carbamate
indicated that a >97% w/w pure product was obtained.
[0175] The hydroxyalkyl carbamate was then acrylated using the same
conditions as in Example 1 using 1220 g (14.2 moles, equivalent
ratio alkyl acrylate to hydroxyalkyl carbamate=4.5) methyl
acrylate, 300 ppm on end product of BHT, 300 ppm on end product of
PTZ and 17.1 g of Tyzor TPT-20B (weight ratio of catalyst to the
generated carbamoyloxy(meth)acrylate=0.036). After a same work-up
procedure as in Example 1, a low colored product (1.5 Gardner) with
a GC purity of 95.3% w/w and a Hoppler viscosity at 25.degree. C.
of 89 mPas was obtained.
[0176] This product was very suitable as diluent in radiation
curable compositions.
Example 6
Preparation of 2-Propenoic Acid, 7,7,9 (or
7,9,9)-trimethyl-4,13-dioxo-3,14-dioxa-5,12-diazahexadecane-1,16-diyl
Ester
##STR00017##
[0178] The starting hydroxyalkyl carbamate was obtained by slowly
adding 228.8 g (2.6 moles) EC on 205.8 g (1.3 moles) 2,2,4-(or
2,4,4-)trimethylhexamethylene diamine (equivalent ratio amine to
cyclic carbonate=1) such as the maximum temperature was 70.degree.
C. Titration of the amine showed that the reaction was done after
an additional 4 hours at 70.degree. C. .sup.1H NMR indicated a
conversion rate in expected product of 98% mol.
[0179] The hydroxyalkyl carbamate was then acrylated using the same
conditions as in Example 1 using 1005 g (11.7 moles, equivalent
ratio alkyl acrylate to hydroxyalkyl carbamate=4.5) methyl
acrylate, 300 ppm on end product BHT, 300 ppm on end product of PTZ
and 33.5 g of Tyzor TPT-20B (weight ratio of catalyst to the
generated carbamoyloxy(meth)acrylate=0.042). Reaction time was 11.5
hours. After a same work-up procedure as in Example 1, a low
colored product (1.2 Gardner) with 96% of the OH groups from the
starting hydroxyalkylcarbamate being acrylated according .sup.1H
NMR, was obtained.
Example 7
Preparation of 2-Propenoic Acid, 1,7,14 (or 1,7,15 or
2,7,14)-trimethyl-4,12-dioxo-3,13-dioxa-5,11-diazapentadecane-1,15-diyl
Ester
##STR00018##
[0181] The starting hydroxyalkyl carbamate, obtained by reacting 2
moles of propylene carbonate with 1 mole of 2-methyl-1,5
diaminopentane, is commercially-available from King Industries Ltd.
(K-flex UD-320-100).
[0182] Acrylation of K-flex UD-320-100 by transesterification was
performed using same equipment as in Example 1. The reaction
mixture containing 288.6 g K-flex UD-320-100 (0.85 moles), 1301 g
(13 moles, equivalent ratio alkyl acrylate to hydroxyalkyl
carbamate=7.6) ethyl acrylate, 1000 ppm on end product of BHT and
300 ppm on end product of PTZ was first dried by azeotropic
distillation, as in Example 1. After adding 25.5 g Tyzor TPT-20B
(weight ratio of catalyst to the generated
carbamoyloxy(meth)acrylate=0.07), the reaction mixture was
maintained at 102-103.degree. C. and the ethanol generated was
taken off overhead as a ethanol/ethyl acrylate azeotrope. The
reaction was continued until a measure of the refractive index
indicated that no more ethanol was present in the distillate.
Reaction time was 10 hours. After a same work-up procedure as in
Example 1, a low colored product (1.9 Gardner) with 92% of the OH
groups from the starting hydroxyalkylcarbamate being acrylated
according .sup.1H NMR, was obtained.
[0183] In another experiment, glycerol was used instead of water to
precipitate the catalyst.
[0184] In that case, filtration time was decreased by a factor
5.
Example 8
Preparation of 2-Propenoic Acid,
2-[[3-[(1-oxo-2-propenyl)oxy]-2-[[(butylamino)carbonyl]oxy]propoxy]butoxy-
]1-[[[[(butylamino)carbonyl]oxy]methyl]ethyl Ester and Isomers
##STR00019##
[0185] 1/Preparation of 1,3-Dioxolan-2-one,
4,4'-[1,4-butanediylbis(oxymethylene)]bis)-
[0186] The latter was prepared from Oxirane,
2,2'-[1,4-butanediylbis(oxymethylene)]bis)-, commercially-available
from EMS-Chemie as Grilonit RV 1806, and CO.sub.2 with the
procedure described in Kihara, N., Hara, N., Endo, T., J. Org.
Chem., 1993, 58, 6198. .sup.1H NMR indicated complete
transformation of the oxirane into cyclic carbonate groups.
Potentiometric titration of the cyclocarbonate groups of the final
product lead to a cyclic carbonate equivalent weight of 163.5 g/eq
(theory: 145 g/eq).
2/Preparation of
[2-[[3-hydroxy-2-[[(butylamino)carbonyl]oxy]propoxy]butoxy]-1-[[[(butylam-
ino)carbonyl]oxy]methyl]ethyl]hydroxy and isomers
[0187] 282.9 g 1,3-Dioxolan-2-one,
4,4'-[1,4-butanediylbis(oxymethylene)]bis) prepared in 1/and 138.5
g (1.9 moles, equivalent ratio amine to cyclic carbonate=1.1)
butylamine was charged in the same reactor as described in Example
1. The mixture was slowly heated to 70.degree. C. Titration of the
amine indicated that the reaction was complete after 3 h at
70.degree. C. The amine excess was stripped at 70.degree. C. for
4.5 hours.
A FTIR spectrum of the stripped product indicated the almost
complete disappearance of the absorption band at 1797 cm.sup.-1,
characteristic of the carbonyl functions of the cyclic carbonate
groups. .sup.1H NMR indicated that the expected reaction occurred
quantitatively (97% mol) to give a statistical mixture of the
expected isomers.
3/Acrylation of
[2-[[3-hydroxy-2-[[(butylamino)carbonyl]oxy]propoxy]butoxy]-1-[[[(butylam-
ino)carbonyl]oxy]methyl]ethyl]hydroxy and Isomers by
Transesterification
[0188] Acrylation was then performed adding to the hydroxyalkyl
carbamate prepared in 2/, 1251.3 g (12.5 moles, equivalent ratio
alkyl acrylate to hydroxyalkyl carbamate=7.2) ethyl acrylate, 1000
ppm on end product of BHT and 300 ppm on end product of PTZ was
first dried by azeotropic distillation, as in Example 1. After
adding 23.6 g Tyzor TPT-20B (weight ratio of catalyst to the
generated carbamoyloxy(meth)acrylate=0.05), the reaction mixture
was maintained at 102-103.degree. C. by injecting air and the
ethanol generated was taken off overhead as a ethanol/ethyl
acrylate azeotrope. The reaction was continued until a measure of
the refractive index indicated that no more ethanol was present in
the distillate. Reaction time was 12 hours. After a same work-up
procedure as in Example 1, a low colored product (1.7 Gardner) with
95% of the OH groups from the starting hydroxyalkylcarbamate being
acrylated according .sup.1H NMR, was obtained.
Example 9
Preparation of
.alpha.-[3-[(1-oxo-2-propenyl)oxy]-2-[[(butylamino)carbonyl]oxy]propoxy]--
.omega.-[3-[[(butylamino)carbonyl]oxy]-2-[(1-oxo-2-propenyl)oxy]propyl]-po-
ly[oxy(methyl-1,2-ethanediyl)] and Isomers with an Average Number
of oxy(methyl-1,2-ethanediyl) Units Between 9 and 10
##STR00020##
[0189] 1/Preparation of
.alpha.-[(2-oxo-1,3-dioxolan-4-yl)methoxy]-.omega.-[(2-oxo-1,3-dioxolan-4-
-yl)methyl]-poly[oxy(methyl-1,2-ethanediyl)] with an Average Number
of oxy(methyl-1,2-ethanediyl) Units Between 9 and 10
[0190] The latter was prepared from
.alpha.-[oxiranylmethoxy]-.omega.-[oxiranylmethyl]-poly[oxy(methyl-1,2-et-
hanediyl)] with an average number of oxy(methyl-1,2-ethanediyl)
units between 9 and 10 (epoxide equivalent weight: 320 g/eq),
commercially-available from Dow as D.E.R. 732P, and CO.sub.2 with
the procedure described in Kihara, N., Hara, N., Endo, T., J. Org.
Chem., 1993, 58, 6198. .sup.1H NMR indicated complete
transformation of the oxirane into cyclic carbonate groups.
Potentiometric titration of the cyclocarbonate groups of the final
product lead to a cyclic carbonate equivalent weight of 382 g/eq
(theory: 365 g/eq).
2/Preparation of
.alpha.-[3-hydroxy-2-[[(butylamino)carbonyl]oxy]propoxy]-.omega.-[3-[[(bu-
tylamino)carbonyl]oxy]-2-[hydroxypropyl]-poly[oxy(methyl-1,2-ethanediyl)]
and Isomers with an Average Number of oxy(methyl-1,2-ethanediyl)
Units Between 9 and 10
[0191] 500 g of the
.alpha.-[(2-oxo-1,3-dioxolan-4-yl)methoxy]-.omega.-[(2-oxo-1,3-dioxolan-4-
-yl)methyl]-poly[oxy(methyl-1,2-ethanediyl)] prepared in 1/and
105.3 g (1.44 moles, equivalent ratio amine to cyclic
carbonate=1.1) of butylamine was charged in the same reactor as
described in Example 1. The mixture was slowly heated to 70.degree.
C. Titration of the amine indicated that the reaction was complete
after 3 h at 70.degree. C. The amine excess was stripped at
70.degree. C. for 3 hours.
[0192] A FTIR spectrum of the stripped product indicated the
complete disappearance of the absorption band at 1797 cm.sup.-1,
characteristic of the carbonyl functions of the cyclic carbonate
groups. .sup.1H NMR indicated that the expected reaction occurred
quantitatively to give a statistical mixture of the expected
isomers (98% mol).
3/Acrylation of
.alpha.-[3-hydroxy-2-[[(butylamino)carbonyl]oxy]propoxy]-.omega.-[3-[[(bu-
tylamino)carbonyl]oxy]-2-[hydroxypropyl]-poly[oxy(methyl-1,2-ethanediyl)]
and Isomers by Transesterification
[0193] Acrylation was then performed adding to the hydroxyalkyl
carbamate prepared in 2/, 917.9 g (9.17 moles, equivalent ratio
alkyl acrylate to hydroxyalkyl carbamate=7) ethyl acrylate, 2410
ppm on end product of BHT and 965 ppm on end product of PTZ. The
reaction mixture was first dried by azeotropic distillation, as in
Example 1. After adding 14.37 g zirconium n-butoxide (80% in
butanol; Tyzor TNBZ manufactured by DuPont) and 13.28 g zirconium
acetylacetonate (manufactured by Sachem; weight ratio of catalyst
to the generated carbamoyloxy(meth)acrylate=0.04), the reaction
mixture was maintained at 102-105.degree. C. under air sparge and
the ethanol generated was taken off overhead as a ethanol/ethyl
acrylate azeotrope. The reaction was continued until a measure of
the refractive index indicated that no more ethanol was present in
the distillate. Reaction time was 11 hours.
[0194] After complete reaction, the catalyst was hydrolyzed by
adding water (4.4 g per g catalyst) and stirring vigorously the
mixture at 75.degree. C. for 2 hour. After vacuum filtration on a
diatomaceous earth bed and concentration/stripping (100 mmHg,
75.degree. C., 3.5 hours), a product with 95% of the OH groups from
the starting hydroxyalkylcarbamate being acrylated (according
.sup.1H NMR), and containing 1.5 ppm residual zirconium (according
to atomic absorption spectrometry) was obtained.
Example 10
Preparation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-[(1-oxo-2-propenyl)oxy]-2-[[(N-methylbutylamino)carbonyl]oxy]p-
ropoxy]-.omega.-[3-[[(N-methylbutylamino)carbonyl]oxy]-2-[(1-oxo-2-propeny-
l)oxy]propyl] and Isomers with an Average Number of
oxy(methyl-1,2-ethanediyl) Units Between 9 and 10
##STR00021##
[0195] 1/Preparation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-hydroxy-2-[[(N-methylbutylamino)carbonyl]oxy]propoxy]-.omega.--
[3-[[(N-methylbutylamino)carbonyl]oxy]-2-[hydroxypropyl] and
Isomers with an Average Number of oxy(methyl-1,2-ethanediyl) Units
Between 9 and 10
[0196]
.alpha.-[3-[(1-oxo-2-propenyl)oxy]-2-[[(butylamino)carbonyl]oxy]pro-
poxy]-.omega.-[3-[[(butylamino)carbonyl]oxy]-2-[(1-oxo-2-propenyl)oxy]prop-
yl]-poly[oxy(methyl-1,2-ethanediyl)] from Example 9 was reacted
using the same procedures and same stoichiometry as in Example 9,
replacing butylamine by N-methylbutylamine.
2/Acrylation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-hydroxy-2-[[(N-methylbutylamino)carbonyl]oxy]propoxy]-.omega.--
[3-[[(N-methylbutylamino)carbonyl]oxy]-2-[hydroxypropyl] and
Isomers by Transesterification
[0197] Same procedure with same stoichiometry was used as in
Example 9.
Example 11
Preparation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-[(1-oxo-2-propenyl)oxy]-2-[[[[[(1-oxo-2-propenyl)oxy]ethoxy]et-
hylamino]carbonyl]oxy]propoxy]-.omega.-[3-[[[[[(1-oxo-2-propenyl)oxy]ethox-
y]ethylamino]carbonyl]oxy]-2-[(1-oxo-2-propenyl)oxy]propyl] and
Isomers with an Average Number of oxy(methyl-1,2-ethanediyl) Units
Between 9 and 10
##STR00022##
[0198] 1/Preparation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-hydroxy-2-[[[[[(1-oxo-2-propenyl)oxy]ethoxy]ethylamino]carbony-
l]oxy]propoxy]-.omega.-[3-[[(N-methylbutylamino)carbonyl]oxy]-2-[hydroxypr-
opyl] and Isomers with an Average Number of
oxy(methyl-1,2-ethanediyl) Units Between 9 and 10
[0199] 312.4 g of the
.alpha.-[(2-oxo-1,3-dioxolan-4-yl)methoxy]-.omega.-[(2-oxo-1,3-dioxolan-4-
-yl)methyl]-poly[oxy(methyl-1,2-ethanediyl)] from Example 9 and
97.1 g (0.92 moles, equivalent ratio amine to cyclic
carbonate=1.12) of 2-(2-aminoethoxyethanol) was charged in the same
reactor as described in Example 1. The mixture was slowly heated to
80.degree. C. Titration of the amine indicated that the reaction
was complete after 5 h at 80.degree. C.
[0200] Measurement of the hydroxyl content by titration (250 mg
KOH/g) indicated that the expected reaction occurred quantitatively
(theory: 239 mgKOH/g). Measurement of the ratio primary to
secondary OH groups by .sup.31P NMR after derivatization of the OH
groups with chlorophospholane (0.67:0.33), indicated a
near-to-statistical mixture of the expected isomers (theory:
0.705:0.295).
2/Acrylation of poly[oxy(methyl-1,2-ethanediyl)],
.alpha.-[3-hydroxy-2-[[[[[(1-oxo-2-propenyl)oxy]ethoxy]ethylamino]carbony-
l]oxy]propoxy]-.omega.-[3-[[(N-methylbutylamino)carbonyl]oxy]-2-[hydroxypr-
opyl] and Isomers by Transesterification
[0201] Acrylation was then performed adding to the hydroxyalkyl
carbamate prepared in 1/, 1202 g (12.0 moles, equivalent ratio
alkyl acrylate to hydroxyalkyl carbamate=6) ethyl acrylate, 3600
ppm on end product of BHT and 1810 ppm on end product of PTZ. The
reaction mixture was first dried by azeotropic distillation, as in
Example 1. After adding 5.3 g zirconium n-butoxide (80% in butanol)
and 4.9 g zirconium acetylacetonate (weight ratio of catalyst to
the generated carbamoyloxy(meth)acrylate=0.02), the reaction
mixture was maintained at 100-103.degree. C. under air sparge and
the ethanol generated was taken off overhead as a ethanol/ethyl
acrylate azeotrope. The reaction was continued until a measure of
the refractive index indicated that no more ethanol was present in
the distillate. Reaction time was 7.5 hours.
[0202] After complete reaction, the catalyst was hydrolyzed by
adding water (4 g per g catalyst) and stirring vigorously the
mixture at 75.degree. C. for 3 hours. After vacuum filtration on a
diatomaceous earth bed and concentration/stripping (100 mmHg,
85.degree. C., 2.5 hours), a product with 92% of the OH groups from
the starting hydroxyalkylcarbamate being acrylated (according
.sup.1H NMR), and containing 2 ppm residual zirconium (according to
atomic absorption spectrometry) was obtained.
[0203] The table here below gives the molecular weights (calculated
from molecular formulae) and acrylate functionality as well as the
measured viscosities of the undiluted products obtained from
examples 6 to 11. Also given is the viscosity of CB 32 (commercial
product supplied by Ackros), same product as Example 6 but obtained
according to the isocyanate method by reacting 1 mole of trimethyl
hexamethylene diisocyanate with 2 mole of HEA.
TABLE-US-00002 Theoretical Molecular Acrylate Hoppler viscosity
Product weight (Dalton) Functionality (25.degree. C., mPa s)
Example 6 442 2 7100 CB 32 442 2 7010 Example 7 429 2 11530 Example
8 545 2 2150 Example 9 984 2 1160 Example 10 1016 2 495 Example 11
1156 4 3370
[0204] The performances of coatings obtained from various
formulations containing Example 6 and CB 32 have also been
compared.
Formulations
TABLE-US-00003 [0205] F1 F2 F3 F4 F5 F6 (parts) (parts) (parts)
(parts) (parts) (parts) Example 6 70 70 70 0 0 0 CB32 0 0 0 70 70
70 HDDA 30 0 0 30 0 0 Ebecryl .RTM. 160 (UCB 0 30 0 0 30 0 Surface
Specialties) Genomer .RTM. 1122 0 0 30 0 0 30 Irgacure .RTM. 500 4
4 4 4 4 4 (CibaGeigy) Brookfield viscosity 285 1251 810 270 1206
804 (25.degree. C., mPa s)
Performances: 10 .mu.m on Chamtenero 60 paper 80 W/cm, H bulb non
focalised
TABLE-US-00004 F1 F2 F3 F4 F5 F6 (parts) (parts) (parts) (parts)
(parts) (parts) Reactivity: Touch Dry (m/min) 10 15 10 5 10 10 Talc
Dry (m/min) 10 15 10 5 10 5 Acetone Double 45 >80 45 35 >80
35 Rubs (ADR) > 50 (m/min) Cross-hatch Tape + + + + + + (TESA
4104) Adhesion (curing at 2 .times. 50 ADR) Chemical Resistance:
Distilled water OK OK OK OK OK OK Ethanol (48% in OK OK OK OK OK OK
water) Ammonia (10%) OK OK OK OK OK OK Oil (Paraffinum OK OK OK OK
OK OK liquidum) Scratch Resistance 5.times. 5.times. 9.times.
5.times. 6.times. 8.times. (steel wool)
[0206] These results clearly show that the process according to the
invention can lead to already-described urethane acrylates (Example
6) giving same or even slightly better coating properties as
commercially-available products (CB 32) obtained using toxic raw
materials.
[0207] They also clearly show that, when starting from
multifunctional cyclic carbonates (Examples 8, 9 and 10), the
process according to the invention leads to new urethane acrylates
showing surprisingly much lower viscosity while having a similar
(or even higher) molecular weight and a same functionality than
already described products (CB 32). Using a secondary amine instead
of a primary one for making the hydroxyalkyl carbamate can further
lower the viscosity of the acrylate (Example 10 vs. Example 9).
[0208] Example 11 shows that the process according to the invention
can lead to tetrafunctional urethane acrylate with an unprecedented
low viscosity.
Example 12
[0209] Example 1 was repeated, except that a mixture of zirconium
catalysts (11 grams of zirconium n-butoxide and acetylacetone (4
grams, manufactured by Wacker)) was used. The reaction was run at
ambient pressure and after 4 hours the reaction mixture was cooled
down and washed twice with water (12% w/w, 15% w/w Na.sub.2CO.sub.3
solution). After concentration under reduced pressure a clear, low
colored (47 Apha), low viscous product (31 mPas) was obtained.
Analysis showed the purity of the product was at least 95% w/w,
containing less than 10 ppm Zr.
* * * * *