U.S. patent application number 12/041769 was filed with the patent office on 2008-06-26 for modified support materials for catalysts.
This patent application is currently assigned to CELANESE INTERNATIONAL CORP.. Invention is credited to Barbara Kimmich, Roelandus Hendrikus Wilhelmus Moonen, Andre Harmen Sijpkes, Leslie E. Wade, Tao Wang.
Application Number | 20080153692 12/041769 |
Document ID | / |
Family ID | 36061714 |
Filed Date | 2008-06-26 |
United States Patent
Application |
20080153692 |
Kind Code |
A1 |
Kimmich; Barbara ; et
al. |
June 26, 2008 |
MODIFIED SUPPORT MATERIALS FOR CATALYSTS
Abstract
The present invention relates to a method of producing a
catalyst or pre-catalyst suitable for assisting in the production
of alkenyl alkanoates. The method includes contacting a modifier
precursor to a support material to form a modified support
material. One or more catalytic component precursors (palladium or
gold) may be contacted to the modified support material. The atomic
ratio of gold to palladium is preferably in the range of about 0.3
to about 0.90. The support materials with the catalytic component
may then be reduced using a reducing environment. A composition for
catalyzing the production of an alkenyl alkanoates including a
modified support material with palladium and gold is also included
within the invention. Catalysts of the present invention may be
used to produce alkenyl alkanoates in general and vinyl acetate in
particular and are useful to produce low EA/VA ratios while
maintaining or improving CO.sub.2 selectivity.
Inventors: |
Kimmich; Barbara; (League
City, TX) ; Wade; Leslie E.; (Pearland, TX) ;
Wang; Tao; (Houston, TX) ; Sijpkes; Andre Harmen;
(Almere, NL) ; Moonen; Roelandus Hendrikus Wilhelmus;
(Alkmaar, NL) |
Correspondence
Address: |
SIMMONS PERRINE PLC
THIRD FLOOR TOWER PLACE, 22 SOUTH LINN STREET
IOWA CITY
IA
52240
US
|
Assignee: |
CELANESE INTERNATIONAL
CORP.
Dallas
TX
|
Family ID: |
36061714 |
Appl. No.: |
12/041769 |
Filed: |
March 4, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11285436 |
Nov 21, 2005 |
|
|
|
12041769 |
|
|
|
|
60637529 |
Dec 20, 2004 |
|
|
|
Current U.S.
Class: |
502/242 ;
502/304; 502/317; 502/321; 502/339; 502/340; 502/344; 502/349;
502/350; 502/353; 502/355 |
Current CPC
Class: |
B01J 23/52 20130101;
B01J 21/08 20130101; B01J 37/0207 20130101; B01J 37/16 20130101;
C07C 69/15 20130101; C40B 40/18 20130101; C07C 69/24 20130101; B01J
23/63 20130101; C07C 69/01 20130101; C07C 67/055 20130101; B01J
21/066 20130101; B01J 23/44 20130101; C07C 67/055 20130101; B01J
21/063 20130101; C40B 30/08 20130101; B01J 23/682 20130101; C07C
67/055 20130101; C07C 67/055 20130101; B01J 23/58 20130101; B01J
23/648 20130101; B01J 2219/00747 20130101; B01J 2219/00745
20130101 |
Class at
Publication: |
502/242 ;
502/340; 502/344; 502/304; 502/353; 502/350; 502/355; 502/349;
502/321; 502/317; 502/339 |
International
Class: |
B01J 21/06 20060101
B01J021/06; B01J 23/02 20060101 B01J023/02; B01J 23/10 20060101
B01J023/10; B01J 23/44 20060101 B01J023/44; B01J 21/00 20060101
B01J021/00; B01J 23/48 20060101 B01J023/48; B01J 23/28 20060101
B01J023/28; B01J 23/20 20060101 B01J023/20 |
Claims
1. A method of producing a catalyst or pre-catalyst suitable for
assisting in the production of alkenyl alkanoates, comprising:
contacting a modifier precursor to a support material; contacting
at least one catalytic component precursor to the modified support
material; and reducing the catalytic component precursor by
contacting a reducing environment to the support material.
2. The method of claim 1 further comprising calcining the modified
support material in a non-reducing atmosphere prior to contacting
the at least one catalytic component precursor to the modified
support material.
3. The method of claim 2 wherein the modifier precursor comprises
barium, magnesium, cerium, potassium, calcium, niobium, tantalum,
titanium, yttrium, strontium, zirconium, lanthanum, praseodymium,
vanadium, molybdenum, rubidium, or binary combinations thereof.
4. The method of claim 3 wherein the modifier precursor comprises
niobium, titanium, magnesium, zirconium or combinations
thereof.
5. The method of claim 4 wherein the modifier precursor comprises
niobium, titanium, magnesium or combinations thereof.
6. The method of claim 2 wherein the modifier precursor comprises a
chloride, a nitrate, an oxalate, a lactate or combinations
thereof.
7. The method of claim 2 wherein the support material comprises
zirconia.
8. The method of claim 20 wherein the support material comprises
titano-silicate or zircono silicate.
9. The method of claim 2 wherein the support material is a layered
support material.
10. The method of claim 1 wherein the first contacting step
comprises impregnating the support material with an aqueous
modifier precursor solution.
11. The method of claim 10 wherein the first contacting step
comprises contacting the support material with between about 0.1 wt
% and about 4.0 wt % of modifier based on the weight of support
material.
12. The method of claim 1 wherein the second contacting step
comprises impregnating the support material with an aqueous
catalytic component precursor solution.
13. The method of claim 3 wherein the modifier calcining step
comprises calcining at a temperature between about 300.degree. C.
and about 700.degree. C.
14. The method of claim 1 further comprising calcining after
contacting the support material with the catalytic component
precursor.
15. The method of claim 1 wherein the catalytic component precursor
comprises gold, palladium, or a combination thereof.
16. The method of claim 15 wherein the atomic ratio of gold to
palladium is between about 0.1 and about 1.25.
17. The method of claim 16 wherein atomic ratio of gold to
palladium is between about 0.3 and about 0.90.
18. The method of claim 1 further comprising contacting the
catalyst or pre-catalyst with an activating agent.
19. The method of claim 18 further comprising contacting alkali
metal acetate to the support material in an amount of between about
10 and 70 grams per liter of catalyst.
20. The method of claim 15 wherein the catalytic component
contacting step comprises contacting between about 1 to about 10
grams of palladium per liter of catalyst, and about 0.5 to about 10
grams of gold per liter of catalyst, with the amount of gold being
from about 10 to about 125 wt % based on the weight of
palladium.
21. A composition for catalyzing the production of an alkenyl
alkanoates, comprising: a modified support material with at least
palladium and gold contacted thereon to form a catalyst or
pre-catalyst, wherein the modified support material is formed from
one or more modifier precursors.
Description
CLAIM OF PRIORITY
[0001] The application is a divisional of U.S. patent application
Ser. No. 11/285,436, filed on Nov. 21, 2005, which in turn claims
the benefit of U.S. application Ser. No. 60/637,529, filed on Dec.
20, 2004, which is hereby incorporated by reference.
FIELD OF THE INVENTION
[0002] The present invention relates to catalysts, methods of
making the catalysts, and methods of making alkenyl alkanoates.
More particularly, the invention relates to catalysts, methods of
making the catalysts, and methods of making vinyl acetate.
BACKGROUND OF THE INVENTION
[0003] Certain alkenyl alkanoates, such as vinyl acetate (VA), are
commodity chemicals in high demand in their monomer form. For
example, VA is used to make polyvinyl acetate (PVAc), which is used
commonly for adhesives, and accounts for a large portion of VA use.
Other uses for VA included polyvinyl alcohol (PVOH), ethylene vinyl
acetate (EVA), vinyl acetate ethylene (VAE), polyvinyl butyral
(PVB), ethylene vinyl alcohol (EVOH), polyvinyl formal (PVF), and
vinyl chloride-vinyl acetate copolymer. PVOH is typically used for
textiles, films, adhesives, and photosensitive coatings. Films and
wire and cable insulation often employ EVA in some proportion.
Major applications for vinyl chloride-vinyl acetate copolymer
include coatings, paints, and adhesives often employ VAE having VA
in some proportion. VAE, which contains more than 50 percent VA, is
primarily used as cement additives, paints, and adhesives. PVB is
mainly used for under layer in laminated screens, coatings, and
inks. EVOH is used for barrier films and engineering polymers. PVF
is used for wire enamel and magnetic tape.
[0004] Because VA is the basis for so many commercially significant
materials and products, the demand for VA is large, and VA
production is frequently done on a relatively large scale, e.g.
50,000 metric tons or more per year. This large scale production
means that significant economies of scale are possible and
relatively subtle changes in the process, process conditions or
catalyst characteristics can have a significant economic impact on
the cost of the production of VA.
[0005] Many techniques have been reported for the production of
alkenyl alkanoates. For example, in making VA, a widely used
technique includes a catalyzed gas phase reaction of ethylene with
acetic acid and oxygen, as seen in the following reaction:
C.sub.2H.sub.4+CH.sub.3COOH+0.5O.sub.2.fwdarw.CH.sub.3COOCH.dbd.CH.sub.2-
+HO
Several side reactions may take place, including, such as, the
formation of CO.sub.2. The results of this reaction are discussed
in terms of the space-time yield (STY) of the reaction system,
where the STY is the grams of VA produced per liter of catalyst per
hour of reaction time (g/l*h).
[0006] The composition of the starting material feed can be varied
within wide limits. Typically, the starting material feed includes
30-70% ethylene, 10-30% acetic acid and 4-16% oxygen. The feed may
also include inert materials such as CO.sub.2, nitrogen, methane,
ethane, propane, argon and/or helium. The primary restriction on
feed composition is the oxygen level in the effluent stream exiting
the reactor must be sufficiently low such that the stream is
outside the flammability zone. The oxygen level in the effluent is
affected by the oxygen level in the starting material stream,
O.sub.2 conversion rate of the reaction and the amount of any inert
material in the effluent.
[0007] The gas phase reaction has been carried out where a feed of
the starting materials is passed over or through fixed bed
reactors. Successful results have been obtained through the use of
reaction temperatures in the range of 125.degree. C. to 200.degree.
C., while reaction pressures of 1-15 atmospheres are typical.
[0008] While these systems have provided adequate yields, there
continues to be a need for reduced production of by-products,
higher rates of VA output, and lower energy use during production.
One approach is to improve catalyst characteristics, particularly
as to CO.sub.2 selectivity and/or activity of the catalyst. Another
approach is to modify reaction conditions, such as the ratio of
starting materials to each other, the O.sub.2 conversion of the
reaction, the space velocity (SV) of the starting material feed,
and operating temperatures and pressures.
[0009] The formation of CO.sub.2 is one aspect which may be reduced
through the use of improved catalysts. The CO.sub.2 selectivity is
the percentage of the ethylene converted that goes to CO.sub.2.
Decreasing the CO.sub.2 selectivity permits a larger amount of VA
per unit volume and unit time in existing plants, even retaining
all other reaction conditions.
[0010] The formation of ethyl acetate (EA) is another aspect which
may be reduced through the use of improved catalysts. The EA
selectivity is usually expressed in ppm as the ratio EA/VA wt/wt.
Decreasing the EA selectivity permits reducing or eliminating
post-production purification of VA. By reducing the EA selectivity
of a catalyst, the processing steps associated with EA removal
could be eliminated, thus providing cost savings. It would be
desirable to achieve an EA/VA ratio less than the typical ratio of
about 700 ppm, preferably less than about 200 ppm without
sacrificing the catalysts' CO.sub.2 selectivity or its
activity.
[0011] Attempts to reduce EA output have included increasing the
gold to palladium ratio on the catalyst, such as shown in U.S. Pat.
No. 5,185,308. While this patent indicates that the EA/VA ratio
eventually goes to zero with a high enough gold to palladium ratio,
experimental testing has been unable to reproduce this result.
Furthermore, CO.sub.2 selectivity is sacrificed through the use of
an increased gold to palladium ratio. Consequently, another
approach is needed.
[0012] VA output of a particular reaction system is affected by
several other factors including the activity of the catalyst, the
ratio of starting materials to each other, the O.sub.2 conversion
of the reaction, the space velocity (SV) of the starting material
feed, and operating temperatures and pressures. All these factors
cooperate to determine the space-time yield (STY) of the reaction
system, where the STY is discussed in terms of grams of VA produced
per liter of catalyst per hour of reaction time or g/l*h.
[0013] Generally, activity is a significant factor in determining
the STY, but other factors may still have a significant impact on
the STY. Typically, the higher the activity of a catalyst, the
higher the STY the catalyst is able to produce.
[0014] The O.sub.2 conversion is a measure of how much oxygen
reacts in the presence of the catalyst. The O.sub.2 conversion rate
is temperature dependent such that the conversion rate generally
climbs with the reaction temperature. However, the CO.sub.2
selectivity also increases along with the increase in temperature.
Thus, the O.sub.2 conversion rate is selected to give the desired
VA output balanced against the amount of CO.sub.2 produced. A
catalyst with a higher activity means that the overall reaction
temperature can be lowered while maintaining the same O.sub.2
conversion. Alternatively, a catalyst with a higher activity will
give a higher O.sub.2 conversion rate at a given temperature and
space velocity.
[0015] It is common that catalysts employ one or more catalytic
components carried on a relatively inert support material. In the
case of VA catalysts, the catalytic components are typically a
mixture of metals that may be distributed uniformly throughout the
support material ("all through-out catalysts"), just on the surface
of the support material ("shell catalysts"), just below a shell of
support material ("egg white catalysts") or in the core of the
support material ("egg yolk catalysts"). Preferred type of metal
distribution is dependent a number of factors including the reactor
system and catalyst size/shape.
[0016] Numerous different types of support materials have been
suggested for use in VA catalyst including silica, cerium doped
silica, alumina, titania, zirconia and oxide mixtures. But very
little investigation of the differences between the support
materials has been done. For the most part, only silica and alumina
have actually been commercialized as support materials.
[0017] One useful combination of metals for VA catalysis is
palladium and gold. Pd/Au catalysts provide adequate CO.sub.2
selectivity and activity, but there continues to be a need for
improved catalysts given the economies of scale that are possible
in the production of VA.
[0018] One process for making Pd/Au catalysts typically includes
the steps of impregnating the support with aqueous solutions of
water-soluble salts of palladium and gold; reacting the impregnated
water-soluble salts with an appropriate alkaline compound e.g.,
sodium hydroxide, to precipitate (often called fixing) the metallic
elements as water-insoluble compounds, e.g. the hydroxides; washing
the fixed support material to remove un-fixed compounds and to
otherwise cleanse the catalyst of any potential poisons, e.g.
chloride; reducing the water insoluble compounds with a typical
reductant such as hydrogen, ethylene or hydrazine, and adding an
alkali metal compound such as potassium or sodium acetate.
[0019] Various modifications to this basic process have been
suggested. For example, in U.S. Pat. No. 5,990,344, it is suggested
that sintering of the palladium be undertaken after the reduction
to its free metal form. In U.S. Pat. No. 6,022,823, it suggested
that calcining the support in a non-reducing atmosphere after
impregnation with both palladium and gold salts might be
advantageous. In WO94/21374, it is suggested that after reduction
and activation, but before its first use, the catalyst may be
pretreated by successive heating in oxidizing, inert, and reducing
atmospheres.
[0020] In U.S. Pat. No. 5,466,652, it is suggested that salts of
palladium and gold that are hydroxyl-, halide- and barium-free and
soluble in acetic acid may be useful to impregnate the support
material. A similar suggestion is made in U.S. Pat. No. 4,902,823,
i.e. use of halide- and sulfur-free salts and complexes of
palladium soluble in unsubstituted carboxylic acids having two to
ten carbons.
[0021] In U.S. Pat. No. 6,486,370, it suggested that a layered
catalyst may be used in a dehydrogenation process where the inner
layer support material differs from the outer layer support
material. Similarly, U.S. Pat. No. 5,935,889 suggests that a
layered catalyst may useful as acid catalysts. But neither suggests
the use of layered catalysts in the production of alkenyl
alkanoates. In U.S. Patent Publication 2005/0181940, layered
catalysts for vinyl acetate are shown, but modified support
materials are not.
[0022] In U.S. Pat. No. 5,808,136 it suggested that a titanium or
zirconium may be used to pre-treat a silica or alumina support
material to improved activity and/or CO.sub.2 selectivity of the
catalyst.
[0023] Taken together, the inventors have recognized and addressed
the need for continued improvements in the field of VA catalysts to
provide improved VA production at lower costs.
SUMMARY OF THE INVENTION
[0024] The present invention relates to a method of producing a
catalyst or pre-catalyst suitable for assisting in the production
of alkenyl alkanoates. The method includes contacting a modifier
precursor to a support material to form a modified support
material. One or more catalytic component precursors (palladium
and/or gold) may be contacted to the modified support material. The
atomic ratio of gold to palladium is preferably in the range of
about 0.3 to about 0.90. The support materials with the catalytic
component may then be reduced using a reducing environment and/or
activated using with an activating agent such as KOAc. A
composition for catalyzing the production of an alkenyl alkanoates
including a modified support material with palladium and gold is
also included within the invention. Catalysts of the present
invention may be used to produce alkenyl alkanoates in general and
vinyl acetate in particular.
DETAILED DESCRIPTION
[0025] Catalysts
[0026] For present purposes, a catalyst is any support material
that contains at least one catalytic component and that is capable
of catalyzing a reaction, whereas a pre-catalyst is any material
that results from any of the catalyst preparation steps discussed
herein.
[0027] Catalysts and pre-catalysts of the present invention may
include those having a modified support material. Effective use of
the catalyst accordingly should help improve EA selectivity while
maintaining or improving CO.sub.2 selectivity, activity or both,
particularly as pertaining to VA production. Moreover, the
combination of improving EA selectively while maintaining or
improving CO.sub.2 selectivity may be desirable even if activity is
adversely affected.
[0028] It should be appreciated that the present invention is
described in the context of certain illustrative embodiments, but
may be varied in any of a number of aspects depending on the needs
of a particular application. By way of example, without limitation,
the catalysts may have the catalytic components uniformly
distributed throughout the support material or they may be shell
catalysts where the catalytic components are found in a relatively
thin shell around a support material core. Egg white catalysts may
also be suitable, where the catalytic components reside
substantially away from the center of support material. Egg yolk
catalysts may also be suitable. Preferred type of metal
distribution is dependent on a number of factors including the
reactor system and catalyst size/shape and include shell catalysts
and layered catalysts.
[0029] Catalytic Components
[0030] In general, the catalysts and pre-catalysts of the present
invention include metals and particularly include a combination of
at least two metals. In particular, the combination of metals
includes at least one from Group VIIIB and at least one from Group
IB. It will be appreciated that "catalytic component" is used to
signify the metal that ultimately provides catalytic functionally
to the catalyst, but also includes the metal in a variety of
states, such as salt, solution, sol-gel, suspensions, colloidal
suspensions, free metal, alloy, or combinations thereof. Preferred
catalysts include palladium and gold as the catalytic
components.
[0031] Another preferred embodiment of the catalyst includes
between about 1 to about 10 grams of palladium and preferably
between about 1 and 10 grams of palladium per liter.
[0032] In one embodiment for catalysts, Au to Pd atomic ratios
between about 0.1 and about 1.25 may be preferred for catalysts.
Most preferred Au:Pd atomic ratios are from 0.3-0.9. The atomic
ratio can be adjusted to balance the EA/VA selectivity and CO.sub.2
selectivity. Employment of higher Au/Pd weight or atomic ratios
tends to favor relatively lower EA/VA ratios but higher CO.sub.2
selectivity.
[0033] One embodiment is the use of ground or powder catalysts for
screening of catalyst compositions. A ground catalyst may be one
where the catalytic components are contacted to the support
material followed by a reduction in the particle size (e.g. by
grinding or ball milling) or one where the catalytic components are
contacted to the support material after the support material has
been reduced in size. In one embodiment, a ground or powder
catalyst is used to simulate a shell catalyst. In simulated shell
catalyst, an aliquot of support material with a relatively high
concentration of modifiers and/or catalytic components is diluted
with a support material that is substantially free of modifiers
and/or catalytic component, but has been activated with an
activation agent (e.g. potassium acetate), as discussed below. The
diluted support material then has the preferred amounts of
modifiers and/or catalytic components in the catalyst.
[0034] For shell catalysts, the thickness of the shell of catalytic
components on the support material ranges from about 5 .mu.m to
about 500 .mu.m. More preferred ranges include from about 5 .mu.m
to about 300 .mu.m.
[0035] Support Materials
[0036] In one aspect of the invention, the catalytic components of
the present invention generally will be carried by a support
material. Suitable support materials typically include materials
that are substantially uniform in identity or a mixture of
materials. Overall, the support materials are typically inert in
the reaction being performed. Support materials may be composed of
any suitable substance preferably selected so that the support
materials have a relatively high surface area per unit mass or
volume, such as a porous structure, a molecular sieve structure, a
honeycomb structure, or other suitable structure. For example, the
support material may contain silica, alumina, silica-alumina,
titania, titano-silicate, zirconia, zircono-silicate, niobia,
silicates, alumino-silicates, titanates, spinel, silicon carbide,
silicon nitride, carbon, cordierite, steatite, bentonite, clays,
metals, glasses, quartz, pumice, zeolites, non-zeolitic molecular
sieves combinations thereof and the like. Any of the different
crystalline form of the materials may also be suitable, e.g. alpha
or gamma alumina. Zirconia, zircono-silicates and titano-silicates
containing support materials are the most preferred. In addition,
multilayer support materials are also suitable for use in the
present invention.
[0037] The support material in the catalyst of this invention may
be composed of particles having any of various regular or irregular
shapes, such as spheres, tablets, cylinders, discs, rings, stars,
or other shapes. The support material may have dimensions such as
diameter, length or width of about 1 to about 10 mm, preferably
about 3 to about 9 mm. In particular having a regular shape (e.g.
spherical) will have as its preferred largest dimension of about 4
mm to about 8 mm. In addition, a ground or powder support material
may be suitable such that the support material has a regular or
irregular shape with a diameter of between about 10 microns and
about 1000 micron, with preferred sizes being between about 10 and
about 700 microns, with most preferred sizes being between about
180 microns and about 450 microns. Larger or smaller sizes may be
employed, as well as polydisperse collections of particles sizes.
For example, for a fluid bed catalyst a preferred size range would
include 10 to 150 microns. For precursors used in layered
catalysts, a size range of 10 to 250 microns is preferred.
[0038] Surface areas available for supporting catalytic components,
as measured by the BET (Brunauer, Emmett, and Teller) method, may
generally be between about 1 m.sup.2/g and about 500 m.sup.2/g,
preferably about 20 m.sup.2/g to about 200 m.sup.2/g. For example,
for a porous support, the pore volume of the support material may
generally be about 0.1 to about 2 ml/g, and preferably about 0.4 to
about 1.2 ml/g. An average pore size in the range, for example, of
about 50 to about 2000 angstroms is desirable, but not
required.
[0039] Examples of suitable silica containing support materials
include KA160 from Sud Chemie, Aerolyst350 from Degussa and other
pyrogenic or microporous-free silicas with a particle size of about
1 mm to about 10 mm.
[0040] Examples of suitable zirconia containing support materials
include those from NorPro, Zirconia Sales (America), Inc., Daichi
Kigenso Kagaku Kogyo, Engelhard and Magnesium Elektron Inc (MEI).
Suitable zirconia support materials have a wide range of surface
areas from less than about 5 m.sup.2/g to more than 300 m.sup.2/g.
Preferred zirconia support materials have surface areas from about
20 m.sup.2/g to about 150 m.sup.2/g, with a range of between about
30 m.sup.2/g and about 100 m.sup.2/g more preferred. Support
materials may have their surfaces treated through a calcining step
in which the virgin support material is heated. The heating reduces
the surface area of the support material (e.g. calcining). This
provides a method of creating support materials with specific
surface areas that may not otherwise be readily available from
suppliers.
[0041] Examples of other suitable support materials include
titano-silicates from Grace such as SP18-9534 (silica with 0.61%
TiO.sub.2) or zircono-silicates from Grace such as SP189043 (silica
with 1.69% ZrO.sub.2). More generally, suitable support materials
may include up to about 50% TiO.sub.2; more preferably between
about 0.01% and about 25% TiO.sub.2; and most preferably between
about 0.1 and about 5% TiO.sub.2. Also, suitable support materials
may include up to about 50% ZrO.sub.2; more preferably between
about 0.01% and about 25% ZrO.sub.2; and most preferably between
about 0.1 and about 5% ZrO.sub.2.
[0042] In another embodiment, it is contemplated to employ at least
a plural combination of support materials, each with a different
characteristic. For example, at least two support materials (e.g.
zirconia and silica) with different characteristics may exhibit
different activities and CO.sub.2 selectivities, thus permitting
preparation of catalysts with a desired set of characteristics,
i.e. activity of a catalyst may be balanced against the CO.sub.2
selectivity of the catalyst.
[0043] Layered Support Materials
[0044] In one embodiment, plural different supports are employed in
a layered configuration as discussed in U.S. Patent Publication
2005/0181940, which is hereby incorporated by reference. Layering
may be achieved in any of a number of different approaches, such as
a plurality of lamella that are generally flat, undulated or a
combination thereof. One particular approach is to utilize
successively enveloping layers relative to an initial core layer.
In general, herein, layered support materials typically include at
least an inner layer and an outer layer at least partially
surrounding the inner layer. All the layers of a layered catalyst
may be modified as discussed below, with at least the outer layer
preferably being modified. The outer layer also preferably contains
substantially more of catalytic components than the inner layer. In
one embodiment, the inner and outer layers are made of different
materials; but the materials may be the same. While the inner layer
may be non-porous, other embodiments include an inner layer that is
porous.
[0045] The layered support material preferably results in a form of
a shell catalyst. But the layered support material offers a well
defined boundary between the areas of the support material that
have catalytic components and the areas that do not. Also, the
outer layer can be constructed consistently with a desired
thickness. Together the boundary and the uniform thickness of the
outer layer result in a shell catalyst that is a shell of catalytic
components that is of a uniform and known thickness.
[0046] Several techniques are known for creating layered support
materials includes those described in U.S. Pat. Nos. 6,486,370;
5,935,889; and 5,200,382, each of which is incorporated by
reference. In one embodiment, the materials of the inner layer are
also not substantially penetrated by liquids, e.g., metals
including but not limited to aluminum, titanium and zirconium.
Examples of other materials for the inner layer include, but are
not limited to, silica, alumina, silica-alumina, titania,
titano-silicate, zirconia, zircono-silicate, niobia, silicates,
alumino-silicates, titanates, spinel, silicon carbide, silicon
nitride, carbon, cordierite, steatite, bentonite, clays, metals,
glasses, quartz, pumice, zeolites, non-zeolitic molecular sieves
combinations thereof and the like. A preferred inner layer is
silica and KA160, in particular.
[0047] These materials which make up the inner layer may be in a
variety of forms such as regularly shaped particulates, irregularly
shaped particulates, pellets, discs, rings, stars, wagon wheels,
honeycombs or other shaped bodies. A spherical particulate inner
layer is preferred. The inner layer, whether spherical or not, has
an effective diameter of about 0.02 mm to about 10.0 mm and
preferably from about 0.04 mm to about 8.0 mm.
[0048] The outermost layer of any multilayer structure is one which
is porous, has a surface area in the range of about 5 m.sup.2/g to
about 300 m.sup.2/g. The material of the outer layer is a metal,
ceramic, or a combination thereof, and in one embodiment it is
selected from alumina, silica, silica-alumina, titania, zirconia,
niobia, silicates, aluminosilicates, titanates, spinel, silicon
carbide, silicon nitride, carbon, cordierite, steatite, bentonite,
clays, metals, glasses, quartz, pumice, zeolites, non-zeolitic
molecular sieves and combinations thereof and preferably include
alumina, silica, silica/alumina, zeolites, non-zeolite molecular
sieves (NZMS), titania, zirconia and mixtures thereof. Specific
examples include zirconia, silica and alumina or combinations
thereof.
[0049] While the outer layer typically surrounds substantially the
entire inner layer, this is not necessarily the case and a
selective coating on the inner layer by the outer layer may be
employed.
[0050] The outer layer may be coated on to the underlying layer in
a suitable manner. In one embodiment, a slurry of the outer layer
material is employed. Coating of the inner layer with the slurry
may be accomplished by methods such as rolling, dipping, spraying,
wash coating, other slurry coating techniques, combinations thereof
or the like. One preferred technique involves using a fixed or
fluidized bed of inner layer particles and spraying the slurry into
the bed to coat the particles evenly. The slurry may be applied
repeatedly in small amounts, with intervening drying, to provide an
outer layer that is highly uniform in thickness.
[0051] The slurry utilized to coat the inner layer may also include
any of a number of additives such as a surfactant, an organic or
inorganic bonding agent that aids in the adhesion of the outer
layer to an underlying layer, or combinations thereof. Examples of
this organic bonding agent include but are not limited to PVA,
hydroxypropylcellulose, methyl cellulose, and
carboxymethylcellulose. The amount of organic bonding agent which
is added to the slurry may vary, such as from about 1 wt % to about
15 wt % of the combination of outer layer and the bonding agent.
Examples of inorganic bonding agents are selected from an alumina
bonding agent (e.g. Bohmite), a silica bonding agent (e.g. Ludox,
Teos), zirconia bonding agent (e.g. zirconia acetate or colloidal
zirconia) or combinations thereof. Examples of silica bonding
agents include silica sol and silica gel, while examples of alumina
bonding agents include alumina sol, bentonite, Bohmite, and
aluminum nitrate. The amount of inorganic bonding agent may range
from about 2 wt % to about 15 wt % of the combination of the outer
layer and the bonding agent. The thickness of the outer layer may
range from about 5 microns to about 500 microns and preferably
between about 20 microns and about 250 microns.
[0052] Once the inner layer is coated with the outer layer, the
resultant layered support will be dried, such as by heating at a
temperature of about 100.degree. C. to about 320.degree. C. (e.g.
for a time of about 1 to about 24 hours) and then may optionally be
calcined at a temperature of about 300.degree. C. to about
900.degree. C. (e.g. for a time of about 0.5 to about 10 hours) to
enhance bonding the outer layer to it underlying layer over a least
a portion of its surface and provide a layered catalyst support.
The drying and calcining steps can be combined into one step. The
resultant layered support material may be contacted with catalytic
components just as any other support material in the production of
catalysts, as described below. Alternately, the outer layer support
material is contacted to catalytic components before it is coated
onto the underlying layer.
[0053] In another embodiment of the layered support, a second outer
layer is added to surround the initial outer layer to form at least
three layers. The material for the second outer layer may be the
same or different than the first outer layer. Suitable materials
include those discussed with respect to the first outer layer. The
method for applying the second outer layer may be the same or
different than the method used to apply the middle layer and
suitable methods include those discussed with respect to the first
outer layer. Organic or inorganic bonding agents as described may
suitably used in the formation of the second outer layer.
[0054] The initial outer layer may or may not contain catalytic
components. Similarly, the second outer layer may or may not
contain catalytic components. If both outer layers contain
catalytic component, then preferably different catalytic components
are used in each layer, although this is not necessarily the case.
In one preferred embodiment, the initial outer layer does not
contain a catalytic component. Contacting catalytic component to
the outer layers may be accomplished by impregnation or spray
coating, as described below.
[0055] In embodiments where the initial outer layer contains
catalytic component, one method of achieving this is to contact the
catalytic component to the material of the initial outer layer
before the material is applied to the inner layer. The second outer
layer may be applied to the initial outer layer neat or containing
catalytic component.
[0056] Other suitable techniques may be used to achieve a three
layered support material in which one or more of the outer layers
contain catalytic components. Indeed, the layered support material
is not limited to three layers, but may include four, five or more
layers, some or all of which may contain catalytic components.
[0057] In addition, the number and type of catalytic components
that vary between the layers of the layered support material, other
characteristics (e.g. porosity, particle size, surface area, pore
volume, or the like) of the support material may vary between the
layers.
[0058] Modified Support Materials
[0059] In another embodiment, the support material may be a
modified support material. A modified support material is one that
includes a modifier. The modifier is preferably a metal selected
from alkali metals, alkaline earth metals, transition metals, and
lanthanides. More preferably the modifier is selected from group 1
to 6 elements. Of these elements, barium, magnesium, cerium,
potassium, calcium, niobium, tantalum, titanium, yttrium,
strontium, zirconium, lanthanum, praseodymium, vanadium,
molybdenum, and rubidium are more preferred. Niobium, titanium,
magnesium, and zirconium represent the preferred modifiers, with
zirconium being slightly less preferred. Combinations of these
elements are also suitable with binary combinations the preferred
type of combination. For example, suitable binary combinations
include Ti--Zr, Mg--Nb, Nb--Zr, Mg--Ti, Nb--Ti, Mg--Zr or the like.
Ratios of metals in the binary combinations range from about 4:1 to
about 1:4.
[0060] Support materials are typically modified before catalytic
components are added to the support material. In one preferred
embodiment, a support material is impregnated with one or more
aqueous solution of the modifiers (referred to as modifier
precursor solutions). The physical state of the support material
during the contacting step may be a dry solid, a slurry, a sol-gel,
a colloidal suspension or the like.
[0061] In one embodiment, the modifiers contained in the precursor
solution are water soluble salts made of the modifiers, including
but not limited to, chlorides, other halides, nitrates, nitrites,
hydroxides, oxides, oxalates, lactates, acetates (OAc), ammoniums
and amines, with chloride free salts being preferred, with
lactates, oxalates and nitrates being most preferred. Examples of
modifier salts suitable for use in modifier precursor solutions
include Ba(NO.sub.3).sub.2, Mg(NO.sub.3).sub.2.6H.sub.2O,
Ce(NO.sub.3).sub.3.6H.sub.2O, KNO.sub.3,
Ca(NO.sub.3).sub.2.4H.sub.2O,
(NH.sub.4).sub.1.35Nb(C.sub.2O.sub.4).sub.2.73,
Ta(C.sub.2O.sub.4).sub.2.5,
Ti(CH.sub.3CH(O--)CO.sub.2NH.sub.4).sub.2(OH).sub.2,
Y(NO.sub.3).sub.3.6H.sub.2O, ZrO(NO.sub.3).sub.2.xH.sub.2O.
[0062] Furthermore, more than one salt may be used in a given
modifier precursor solution. Precursor solutions typically may be
made by dissolving the selected salt or salts in water, with or
without solubility modifiers such as acids, bases or other
solvents. Other non-aqueous solvents may also be suitable.
[0063] The modifier precursor solutions may be impregnated onto the
support material in a single impregnation, although support
materials maybe impregnated multiple times with modifiers having
low atomic weight (e.g. Mg) or limited solubility in water (e.g. Nb
or Ba). If multiple modifiers are utilized, the impregnation may be
simultaneous (e.g. co-impregnation) or sequential and support
material may be impregnated through the use of one or multiple
precursor solutions. Suitably, the amount of modifier impregnated
on to the support material is between about 0.01 wt % and about 5.0
wt % of the support material, and preferably between about 0.1 wt %
and about 4.0 wt %.
[0064] For the impregnating step, the volume of precursor solution
may be selected so that it corresponds to up to about 110% of the
pore volume of the support material. Volumes between about 95% and
about 100% of the pore volume of the support material are
preferred
[0065] Typically, the modifier precursor solution is added to the
support material and the support material is allowed absorb the
precursor solution. This may be done drop wise until incipient
wetness of the support material is substantially achieved.
Alternatively, the support material may be placed by aliquots or
batch wise into the precursor solution. A roto-immersion or other
assistive apparatus may be used to achieve thorough contact between
the support material and the precursor solution. Further, a spray
device may be used such that the precursor solution is sprayed
through a nozzle onto the support material, where it absorbed. A
fixing step is typically not used to fix the modifier on to the
support material, although this is not necessarily the case.
[0066] The modifier may be distributed all throughout the support
material, distributed as a shell, and as an egg white or as an
egg-yolk. Other contacting techniques may be used. For example,
modifiers may be contacted to a support material through a chemical
vapor deposition process, such as described in US2001/0048970,
which is incorporated by reference. Also, spray coating or
otherwise layering a uniformly pre-impregnated support material, as
an outer layer, on to an inner layer may be suitable.
[0067] After the modifier precursor solution has been contacted to
the support material, decanting, heat or reduced pressure may be
used to remove any excess liquid not absorbed by the support
material or to dry the support material.
[0068] After at least one modifier has been contacted to the
support material, a calcining step may also be employed. The
calcining step typically is before the catalytic components are
contacted to the modified support material. The calcining step
includes heating the support material in a non-reducing atmosphere
(i.e. oxidizing or inert). During calcination, the modifiers on the
support material are at least partially decomposed from their salts
to a mixture of their oxide and free metal form.
[0069] For example, the calcining step is carried out at a
temperature in the range of about 100.degree. C. to about
900.degree. C., preferably between about 300.degree. C. and about
700.degree. C. Non-reducing gases used for the calcination may
included one or more inert or oxidizing gases such as helium,
nitrogen, argon, neon, nitrogen oxides, oxygen, air, carbon
dioxide, combinations thereof or the like. In one embodiment, the
calcining step is carried out in an atmosphere of substantially
pure nitrogen, oxygen, air or combinations thereof. Calcination
times may vary but preferably are between about 1 and 5 hours. The
degree of decomposition of the modifier salts depends on the
temperature used and length of time the modified support material
is calcined and can be followed by monitoring volatile
decomposition products.
[0070] Methods of Making Catalysts
[0071] In general the method includes contacting modified support
material with catalytic components and reducing the catalytic
components. Preferred methods of the present invention include
impregnating the catalytic components into the support material,
calcining the catalytic component containing support material,
reducing the catalytic components and activating the reduced
catalytic components on the support material. Additional steps such
as fixing the catalytic components on the support material and
washing the fixed catalytic components may also be included in the
method of making the catalyst or pre-catalyst. Some of the steps
listed above are optional and others may be eliminated (e.g. the
washing and/fixing steps). In addition, some steps may be repeated
(e.g. multiple impregnation or fix steps) and the order of the
steps may be different from that listed above (e.g. the reducing
step precedes the calcining step). To a certain extent, the
contacting step will determine what later steps are needed for the
formation of the catalyst.
[0072] Contacting Step
[0073] One particular approach to contacting is one pursuant to
which an egg yolk catalyst or pre-catalyst is formed, an egg white
catalyst or pre-catalyst is formed, an all throughout catalyst or
pre-catalyst is formed or a shell catalyst or pre-catalyst is
formed, or a combination thereof. In one embodiment, techniques
that form shell catalysts are preferred.
[0074] The contacting step may be carried out using any of the
modified support materials described above, with niobium, titanium
and magnesium modifiers on support materials containing zirconia
being the most favored. The contacting step is preferably carried
out at ambient temperature and pressure conditions; however,
reduced or elevated temperatures or pressures may be employed.
[0075] In one preferred contacting step, a modified support
material is impregnated with one or more aqueous solutions of the
catalytic components (referred to as catalytic precursor
solutions). The physical state of the support material during the
contacting step may be a dry solid, a slurry, a sol-gel, a
colloidal suspension or the like.
[0076] In one embodiment, the catalytic components contained in the
precursor solution are water soluble salts made of the catalytic
components, including but not limited to, chlorides, other halides,
nitrates, nitrites, hydroxides, oxides, oxalates, acetates (OAc),
and amines, with halide free salts being preferred and chloride
free salts being more preferred. Examples of palladium salts
suitable for use in precursor solutions include PdCl.sub.2,
Na.sub.2PdCl.sub.4, Pd(NH.sub.3).sub.2(NO.sub.2).sub.2,
Pd(NH.sub.3).sub.4(OH).sub.2, Pd(NH.sub.3).sub.4(NO.sub.3).sub.2,
Pd(NO.sub.3).sub.2, Pd(NH.sub.3).sub.4(OAc).sub.2,
Pd(NH.sub.3).sub.2(OAc).sub.2, Pd(OAc).sub.2 in KOH and/or
NMe.sub.4OH and/or NaOH, Pd(NH.sub.3).sub.4(HCO.sub.3).sub.2 and
palladium oxalate. Of the chloride-containing palladium precursors,
Na.sub.2PdCl.sub.4 is most preferred. Of the chloride free
palladium precursor salts, the following four are the most
preferred: Pd(NH.sub.3).sub.4(NO.sub.3).sub.2, Pd(NO.sub.3).sub.2,
Pd(NH.sub.3).sub.2(NO.sub.2).sub.2, Pd(NH.sub.3).sub.4(OH).sub.2.
Examples of gold salts suitable for use in precursor solution
include AuCl.sub.3, HAuCl.sub.4, NaAuCl.sub.4, KAuO.sub.2,
NaAuO.sub.2, NMe.sub.4AuO.sub.2, Au(OAc).sub.3 in KOH and/or
NMe.sub.4OH as well as HAu(NO.sub.3).sub.4 in nitric acid, with
KAuO.sub.2 being the most preferred of the chloride free gold
precursors.
[0077] Furthermore, more than one salt may be used in a given
precursor solution. For example, a palladium salt may be combined
with a gold salt or two different palladium salts may be combined
together in a single precursor solution. Precursor solutions
typically may be made by dissolving the selected salt or salts in
water, with or without solubility modifiers such as acids, bases or
other solvents. Other non-aqueous solvents may also be
suitable.
[0078] The precursor solutions may be impregnated onto the support
material simultaneously (e.g. co-impregnation) or sequentially and
may be impregnated through the use of one or multiple precursor
solutions. In addition, a catalytic component may be impregnated on
to support material in multiple steps, such that a portion of the
catalytic component is contacted each time. For example, one
suitable protocol may include impregnating with Pd, followed by
impregnating with Au, followed by impregnating again with Au. In
another protocol, Pd and Au are preferably co-impregnated.
[0079] The order of impregnating the modified support material with
the catalytic precursor solutions is not critical; although there
may be some advantages to certain orders, as discussed below, with
respect to the calcining step. Preferably, the palladium catalytic
component is impregnated onto the support material first, with gold
being impregnated after palladium, or last. Also, the support
material may be impregnated multiple times with the same catalytic
component. For example, a portion of the overall gold contained in
the catalyst may be first contacted, followed by contacting of a
second portion of the gold. One more other steps may intervene
between the steps in which gold is contacted to the support
material, e.g. calcining, reducing, and/or fixing.
[0080] The acid-base profile of the precursor solutions may
influence whether a co-impregnation or a sequential impregnation is
utilized. Thus, only precursor solutions with similar acid-base
profile should be used together in a co-impregnating step; this
eliminates any acid-base reactions that may foul the precursor
solutions
[0081] For the impregnating step, the volume of precursor solution
is selected so that it corresponds to between about 85% and about
110% of the pore volume of the support material. Volumes between
about 95% and about 100% of the pore volume of the support material
are preferred. Further, for one step fixing and modifying discussed
below, the modifier precursor solution may make up a lower
percentage of pore volume. For example, less than 50% of the pore
volume, less than 25% of the pore volume or less than 10% of the
pore volume.
[0082] Typically, the precursor solution is added to the support
material and the support material is allowed absorb the precursor
solution. This may be done drop wise until incipient wetness of the
support material is substantially achieved. Alternatively, the
support material may be placed by aliquots or batch wise into the
precursor solution. A roto-immersion or other assistive apparatus
may be used to achieve thorough contact between the support
material and the precursor solution. Further, a spray device may be
used such that the precursor solution is sprayed through a nozzle
onto the support material, where it absorbed. Optionally,
decanting, heat or reduced pressure may be used to remove any
excess liquid not absorbed by the support material or to dry the
support material after impregnation.
[0083] Other contacting techniques may be used to avoid a fixing
step while still achieving a shell catalyst. For example, catalytic
components may be contacted to a support material through a
chemical vapor deposition process, such as described in
US2001/0048970, which is incorporated by reference. Also, spray
coating or otherwise layering a uniformly pre-impregnated support
material, as an outer layer, on to an inner layer effectively forms
shell catalyst that may also be described as a layered support
material. In another technique, organometallic precursors of
catalytic components, particularly with respect to gold, may be
used to form shell catalysts, as described in U.S. Pat. No.
5,700,753, which is incorporated by reference.
[0084] A physical shell formation technique may also be suitable
for the production of shell catalysts. Here, the precursor solution
may be sprayed onto a heated modified support material or a layered
modified support material, where the solvent of the precursor
solution evaporates upon contact with the heated support material,
thus depositing the catalytic components in a shell on the support
material. Preferably, temperatures between about 40 and 140.degree.
C. may be used. Selecting the temperature of the support material
and the flow rate of the solution through the spray nozzle may be
used control the thickness of the shell. For example, with
temperatures above about 100.degree. C., a relatively thin shell is
formed. This embodiment may be particularly useful when chloride
free precursors are utilized to help enhance the shell formation on
the support material. See for example U.S. Patent Publication
20050181940.
[0085] One skilled in the art will understand that a combination of
the contacting steps may be an appropriate method of forming a
contacted support material.
[0086] Fixing Step
[0087] It may be desirable to transform at least a portion of the
catalytic components on the contacted and modified support material
from a water-soluble form to a water-insoluble form. Such a step
may be referred to as a fixing step. This may be accomplished by
applying a fixing agent (e.g. dispersion in a liquid, such as a
solution) to the impregnated support material which causes at least
a portion of the catalytic components to precipitate. This fixing
step helps to form a shell catalyst, but is not required to form
shell catalysts.
[0088] Any suitable fixing agent may be used, with hydroxides (e.g.
alkali metal hydroxides), silicates, borates, carbonates and
bicarbonates in aqueous solutions being preferred. The preferred
fixing agent is NaOH. Fixing may be accomplished by adding the
fixing agent to the support material before, during or after the
precursor solutions are impregnated on the support material.
Typically, the fixing agent is used subsequent to the contacting
step such that the contacted support material is allowed to soak in
the fixing agent solution for about 1 to about 24 hours. The
specific time depends upon the combination of the precursor
solution and the fixing agent. Like the impregnating step, an
assistive device, such as a roto immersion apparatus as described
in U.S. Pat. No. 5,332,710, which is incorporated herein by
reference, may advantageously be used in the fixing step.
[0089] The fixing step may be accomplished in one or multiple
steps, referred as a co-fix or a separate fix. In a co-fix, one or
more volumes of a fixing agent solution is applied to the contacted
support material after all the relevant precursor solutions have
been contacted to the support material, whether the contact was
accomplished through the use of one or multiple precursor
solutions. For example, fixing after sequential impregnation with a
palladium precursor solution and a gold precursor solution would be
a co-fix. An example of co-fixing may be found in U.S. Pat. No.
5,314,888, which is incorporated by reference.
[0090] A separate fix, on the other hand, would include applying a
fixing agent solution during or after each impregnation with a
precursor solution. For example, the following protocols would be a
separate fix: a) impregnating palladium followed by fixing followed
by impregnating with gold followed by fixing; or b) co-impregnating
with palladium followed by fixing followed by impregnating with
gold followed by fixing. Between a fix and subsequent impregnation,
any excess liquid may be removed and the support material dried,
although this is not necessarily the case. An example of separate
fixing may be found in U.S. Pat. No. 6,034,030, which is
incorporated by reference.
[0091] In another embodiment, the fixing step and the contacting
step are conducted simultaneously, one example of which is
described in U.S. Pat. No. 4,048,096, which is incorporated by
reference. For example, a simultaneous fix might be: impregnating
with palladium followed by fixing followed by impregnating with
gold and fixing agent. In a variation on this embodiment, the fix
may be conducted twice for a catalytic component. A catalytic
component may be partially fixed when it is contacted to the
support material (called a "pre-fix"), followed an additional,
final fix. For example: impregnating with palladium followed by
impregnating with gold and a pre-fixing agent followed by fixing
with a final fixing agent. This technique may be used to help
insure the formation of shell type catalyst as opposed to an all
throughout catalyst.
[0092] In another embodiment of the simultaneous fixing and
contacting step, the fixing solution is impregnated into the
modified support material such that between about 25 and about 95%
of the pore volume is filled. Preferably, between about 70 and
about 90% of the pore volume is filled by the fixing solution. The
remainder of the pore volume is then filled with the catalytic
precursor solution. Step-wise or co-impregnation of the catalytic
precursor may be used. This simultaneous fix and contacting step
avoids the need for a drying step, thus simplifying the process.
Examples of fixing solutions include those comprising alkali metal
hydroxides, alkali metal carbonates, alkali metal bicarbonates or
mixtures thereof. The fixing solutions may also be buffered to help
maintain the pH of the solution.
[0093] In another embodiment, particularly suitable for use with
chloride free precursors, the modified support material is
pre-treated with a fixing agent to adjust the properties of the
support material. In this embodiment, the support material is first
impregnated with either an acid or base solution, typically free of
metals. After drying, the support material is impregnated with a
precursor solution that has the opposite acidity/alkalinity as the
dried support material. The ensuing acid-base reaction forms a
shell of catalytic components on the support material. For example,
nitric acid may be used to pre-treat a support material that in
turn is impregnated with a basic precursor solution such as
Pd(OH).sub.2 or Au(OH).sub.3. This formation technique may be
considered as using a fixing step followed by a contacting
step.
[0094] In another embodiment, the modified support may be
pre-treated before impregnation of the Pd and or Au in order to
neutralize potentially chemically reactive sites on the support
material which may cause poor shell formation. For example, a basic
support (e.g. zirconia) may be pre-treated with HCl to neutralize
selected sites, followed by with Pd and Au impregnation and by
fixing with base.
[0095] The concentration of fixing agent in the solution is
typically a molar excess of the amount of catalytic components
impregnated on the support material. The amount of fixing agent
should be between about 1.0 to about 3.0, preferably about 1.1 to
about 2.0 times the amount necessary to react with the
catalytically active cations present in the water-soluble salt.
[0096] The volume of fixing agent solution supplied generally
should be an amount sufficient to cover the available free surfaces
of the impregnated support material This may be accomplished by
introducing, for example, a volume that is greater than the pore
volume of the contacted support material.
[0097] The combination of impregnating and fixing steps can form a
shell type catalyst. But, the use of halide free precursor
solutions also permits the formation of a shell catalyst while
optionally eliminating the fixing step. In the absence of a
chloride precursor, a washing step, as discussed below, may be
obviated. Further, the process can be free of a step of fixing
catalytic components that would otherwise be needed to survive the
washing step. Because no washing step is needed, the catalytic
components need not be fixed to survive the washing step.
Subsequent steps in the method making the catalyst do not require
the catalytic components be fixed and thus the remainder of the
step maybe carried out without additional preparatory steps.
Overall, the use of chloride free precursors permits a catalyst or
pre-catalyst production method that is free of a step of washing,
thus reducing the number of steps needed to produce the catalyst
and eliminating the need to dispose of chloride containing
waste.
[0098] Washing Step
[0099] Particularly, when halide containing precursor solutions are
utilized and in other applications as desired, after the fixing
step, the fixed support material may be washed to remove any halide
residue on the support or otherwise treated to eliminate the
potential negative effect of a contaminant on the support material.
The washing step included rinsing the fixed support material in
water, preferably deionized water. Washing may be done in a batch
or a continuous mode. Washing at room temperature should continue
until the effluent wash water has a halide ion content of less than
about 1000 ppm, and more preferably until the final effluent gives
a negative result to a silver nitrate test. The washing step may be
carried out after or simultaneously with the reducing step,
discussed below, but preferably is carried out before. As discussed
above, the use of halide free precursor solutions permits the
elimination of the washing step.
[0100] Calcining Step of Catalytic Components
[0101] After at least one catalytic component has been contacted to
the support material, one or more a calcining steps may be
employed, although this is not necessarily the case and in some
instances is not preferred. The calcining step typically is before
the reducing step and after the fixing step (if such a step is
used) but may take place elsewhere in the process. In another
embodiment, the calcining step is carried out after the reducing
step. The calcining step includes heating the support material in a
non-reducing atmosphere (i.e. oxidizing or inert). During
calcination, the catalytic components on the modified support
material are at least partially decomposed from their salts to a
mixture of their oxide and free metal form.
[0102] For example, the calcining step is carried out at a
temperature in the range of about 100.degree. C. to about
700.degree. C., preferably between about 200.degree. C. and about
500.degree. C. Non-reducing gases used for the calcination may
included one or more inert or oxidizing gases such as helium,
nitrogen, argon, neon, nitrogen oxides, oxygen, air, carbon
dioxide, combinations thereof or the like. In one embodiment, the
calcining step is carried out in an atmosphere of substantially
pure nitrogen, oxygen, air or combinations thereof. Calcination
times may vary but preferably are between about 1 and 5 hours. The
degree of decomposition of the catalytic component salts depends on
the temperature used and length of time the impregnated catalyst is
calcined and can be followed by monitoring volatile decomposition
products. Optionally, on zirconia support materials, only the Pd is
calcined.
[0103] Reducing Step
[0104] Another step employed generally herein to at least partially
transform any remaining catalytic components from a salt or oxide
form to a catalytically active state, such as by a reducing step.
Typically this is done by exposure of salts or oxides to a reducing
agent, examples of which include ammonia, carbon monoxide,
hydrogen, hydrocarbons, olefins, aldehydes, alcohols, hydrazine,
primary amines, carboxylic acids, carboxylic acid salts, carboxylic
acid esters and combinations thereof. Hydrogen, ethylene,
propylene, alkaline hydrazine and alkaline formaldehyde and
combinations thereof are preferred reducing agents with ethylene
and hydrogen blended with inert gases particularly preferred.
Although reduction employing a gaseous environment is preferred, a
reducing step carried with a liquid environment may also be used
(e.g. employing a reducing solution). The temperature selected for
the reduction can range from ambient up to about 550.degree. C.
Reduction times will typically vary from about 1 to about 10 hours,
with 5 hours preferred.
[0105] Since the process used to reduce the catalytic components
may influences the characteristics of the final catalyst,
conditions employed for the reduction may be varied depending on
whether high activity, high selectivity or some balance of these
properties is desired.
[0106] In one embodiment, palladium is contacted to the support
material, fixed and reduced before gold is contacted and reduced,
as described in U.S. Pat. Nos. 6,486,093, 6,015,769 and related
patents, all of which are incorporated by reference.
[0107] Exemplary protocols including a reducing step include: a)
impregnating with palladium followed by optionally calcining
followed by impregnating with gold followed by reducing; b)
co-impregnating with palladium and gold followed by optionally
calcining followed by reducing; or c) impregnating with palladium
followed by optionally calcining followed by reducing followed by
impregnating with gold.
[0108] Activating Step
[0109] Usually after the reducing step and before the catalyst is
used, an activating step is desirable. While the catalyst may be
used without the activating step, the step has several beneficial
results, including lengthening the operational life time of the
catalyst. The activating step may be accomplished in accordance
with conventional practice. Namely, the reduced support material is
contacted with an activating agent, such as an alkali metal salt
(e.g. carboxylate and/or alkali metal hydroxide), prior to use.
Conventional alkali metal carboxylates such as the sodium,
potassium, lithium and cesium salts of C.sub.2-4 aliphatic
carboxylic acids are employed for this purpose. A preferred
activating agent in the production of VA is an alkali acetate, with
potassium acetate (KOAc) being the most preferred.
[0110] The support material may optionally be impregnated with a
solution of the activating agent. After drying, the catalyst may
contain, for example, about 10 to about 70 grams, preferably about
20 to about 60 grams of activating agent per liter of catalyst.
[0111] Methods of Making Alkenyl Alkanoates
[0112] The present invention may be utilized to produce alkenyl
alkanoates from an alkene, alkanoic acid and an oxygen containing
gas in the presence of a catalyst. Preferred alkene starting
materials contain from two to four carbon atoms (e.g. ethylene,
propylene and n-butene). Preferred alkanoic acid starting materials
used in the process of this invention for producing alkenyl
alkanoates contain from two to four carbon atoms (e.g., acetic,
propionic and butyric acid). Preferred products of the process are
VA, vinyl propionate, vinyl butyrate, and allyl acetate. The most
preferred starting materials are ethylene and acetic acid with the
VA being the most preferred product. Thus, the present invention is
useful in the production of olefinically unsaturated carboxylic
esters from an olefinically unsaturated compound, a carboxylic acid
and oxygen in the presence of a catalyst. Although the rest of the
specification discusses VA exclusively, it should be understood
that the catalysts, method of making the catalysts and production
methods are equally applicable to other alkenyl alkanoates, and the
description is not intended as limiting the application of the
invention to VA.
[0113] When VA is produced using the catalyst of the present
invention, a stream of gas, which contains ethylene, oxygen or air,
and acetic acid is passed over the catalyst. The composition of the
gas stream can be varied within wide limits, taking in account the
zone of flammability of the effluent. For example, the molar ratio
of ethylene to oxygen can be about 80:20 to about 98:2, the molar
ratio of acetic acid to ethylene can be about 100:1 to about 1:100,
preferably about 10:1 to 1:10, and most preferably about 1:1 to
about 1:8. The gas stream may also contain gaseous alkali metal
acetate and/or inert gases, such as nitrogen, carbon dioxide and/or
saturated hydrocarbons. Reaction temperatures which can be used are
elevated temperatures, preferably those in the range of about
125-220.degree. C. The pressure employed can be a somewhat reduced
pressure, normal pressure or elevated pressure, preferably a
pressure of up to about 20 atmospheres gauge.
[0114] In addition to fixed bed reactors, the methods of producing
alkenyl alkanoates and the catalyst of the present invention may
also be suitably employed in other types of reaction, for example,
fluidized bed reactors.
[0115] The methods of VA production preferably achieve an EA/VA
ratio of less than about 800 ppm, more preferably less than about
400 ppm, more preferably less than about 250 ppm and most
preferably less than about 200 ppm. The methods also preferably
achieve a CO.sub.2 selectivity of less than about 10%, and more
preferably less than about 9% and most preferably less than 8% when
the O.sub.2 conversion is 45%. Most preferably, the catalyst will
have both the EA/VA ratio and CO.sub.2 selectivity discussed
above.
[0116] Moreover, the present methods of VA production preferably
result in maintained or improved CO.sub.2 selectivities as compared
to a standard catalyst utilized in similar processing conditions. A
standard catalyst is any catalyst that may be used as a control,
and preferably does not include a modified support material. To
make the comparison, the standard catalyst is used as a control in
the same or similar processing conditions as processing conditions
for the modified support material catalyst. The catalyst on the
modified support material need only match (or improve upon) the
CO.sub.2 selectivity of the standard catalyst at a given O.sub.2
conversion. One example of a catalyst that may be used as a
standard catalyst is shown in U.S. Pat. No. 5,332,710, hereby
incorporated by reference.
[0117] Examples of Catalysts on Modified Support Materials
[0118] Combinatorial/High Throughput chemistry and analysis
techniques were utilized to screen catalysts with modified support
materials. The compositional space for the screened catalysts
included those with gold and palladium as catalytic components
where the atomic ratio of gold to palladium is between 0.3 to 1.2.
Support materials included: KA-160 (silica-alumina), Norpro XZ
16052 (zirconia), Aerolyst 350 (silica), Grace SP-9600 (silica),
Grace SP-9601 (silica), Grace SP-9599 (silica), Grace SP-9602
(silica), Grace SP189043.USA3 (zircono-silica), Grace SP18-9534
(titano-silicate), Norpro XZ 16075 (zirconia) and Norpro XZ 16052
(zirconia). The above support materials were modified with Ba, Mg,
Ce, K, Ca, Nb, Ta, Ti, Y, Sr, Z, La, Pr, V, Mo, Rb, and selected
bimetallic combinations discussed above. Unmodified support
materials were also tested as controls.
[0119] Modified support materials other than zirconia were prepared
by impregnating 0.5 g samples of support (dried at 120.degree. C.
for at least 2 h) to incipient wetness with modifier precursor
solutions to achieve one of three levels: 1.0, 2.0 and 4.0 wt %.
This was followed by drying at 105.degree. C. for at least 2 h and
calcination at 500.degree. C., with 2.degree. C./min heating rate.
A robot from Hamilton was used to do all liquid dispensing
[0120] The modified support materials were impregnated to incipient
wetness with a solution of Pd(NH.sub.3).sub.4(OH).sub.2 to a Pd
loading of 42.6 g Pd/L catalyst. During and after impregnation, the
support materials were homogenized for at least 1 h. After
impregnation, the support materials were dried in air at
105.degree. C. for at least 2 h, and then calcined in air at
350.degree. C. for 2 h, with a heating rate of 2.degree.
C./min.
[0121] Next, the modified support materials were impregnated to
incipient wetness with freshly prepared 1 M [KOH+Au(OH).sub.3]
solution to achieve Au:Pd ratios of 0.45, 0.6, 0.9, and 1.2. During
and after impregnation, the impregnated support materials were
homogenized for at least 1 h, followed by drying in air at
105.degree. C. for at least 2 h.
[0122] The modified support materials with the catalytic components
were reduced in 7% hydrogen in nitrogen. The samples were placed in
small crucibles in which the catalyst bed was about 1 to 3 mm deep.
A flow of 100 mL was maintained throughout the reduction, with a
2.degree. C./min heating rate, 5 h at 350.degree. C. After
reduction, the samples were activated by impregnation with a KOAc
solution to 40 g KOAc/L catalyst and dried at 105.degree. C. for at
least 2 h.
[0123] Modified zirconia support materials were made using
essentially that same procedure as discussed above, except that no
calcination took place after Pd impregnation and the reduction
utilized 5% ethylene in nitrogen at 150.degree. C.
[0124] Catalysts prepared according to this protocol were
heterogeneously diluted with support material containing 40 g/l
KOAc to give an overall Pd loading of 7 g/l. The simulated shell
catalysts were tested using a standard line-in protocol to test the
catalysts' CO.sub.2 selectivity and EA/VA ratios using a parallel
reactor system. The standard protocol included testing the
catalysts for 8 hours under normal feeds at 145.degree. C. (13.8%
HOAc, 40% C.sub.2H.sub.4, 7.9% O.sub.2 and 38% N.sub.2, P=10 atm,
SV=138 cc/min/cc catalyst). A temperature ramp of 155.degree. C.,
165.degree. C., 175.degree. C. and 145.degree. C. was then used to
obtain information on each catalyst. Catalysts that showed CO.sub.2
selectivity less than about 9.0% at 45% O.sub.2 conversion and an
EA/VA ratio of less than 800 ppm were deemed acceptable.
[0125] Catalysts on modified support materials that showed
acceptable CO.sub.2 selectivity and EA/VA ratios are shown in the
table below:
TABLE-US-00001 Support material Name Ta Nb Ti Y Zr Mg Pr La
silica-alumina KA-160 x x x x x x zircono-silicate Grace
SP189043.USA3 x x x silica Aerolyst 350 x x titano-silicate Grace
SP18-9534 x x x x silica Grace SP-9601 x x x zirconia Norpro XZ
16075 x x x x x x zirconia Norpro XZ 16052 x x x
[0126] Based on the results above, other levels of modifier (e.g.
0.1 wt % and 0.4 wt %) and/or other Au:Pd ratios were tested to
optimize the CO.sub.2 selectivity and the EA/VA ratio. Furthermore,
variations in catalyst preparation conditions were also tested
(e.g. different calcination temperatures, impregnation methods
and/or different reduction conditions).
[0127] To differentiate between the acceptable catalysts, a high
temperature deactivation test was used. Normal feeds (13.8% HOAc,
40% C.sub.2H.sub.4, 7.9% O.sub.2 and 38% N.sub.2, P=10 atm, SV=138
cc/min/cc catalyst) were used for 8 hours at 180.degree. C. as a
line-in protocol. The line-in was followed by a temperature ramp of
165.degree. C., 175.degree. C., 185.degree. C., 195.degree. C. and
165.degree. C. Catalysts that showed acceptable properties under a
more stringent set of guidelines (e.g. an EA/VA ratio of less than
about 250 ppm with acceptable CO.sub.2 selectivity at 45% O.sub.2
conversion) would be the most preferred of the catalysts on the
modified support materials. Under this protocol, the most preferred
modified supports include niobium, titanium and magnesium on
zirconia support materials. Also preferred were titanium and
zirconium modifiers on the titano-silicate.
[0128] Comparison of catalysts with and without modified support
materials may be carried out using any VA synthetic procedure so
long as the same procedure is used to test both types of catalysts.
It will be further appreciated that functions or structures of a
plurality of components or steps may be combined into a single
component or step, or the functions or structures of one-step or
component may be split among plural steps or components. The
present invention contemplates all of these combinations. Unless
stated otherwise, dimensions and geometries of the various
structures depicted herein are not intended to be restrictive of
the invention, and other dimensions or geometries are possible.
Plural structural components or steps can be provided by a single
integrated structure or step. Alternatively, a single integrated
structure or step might be divided into separate plural components
or steps. In addition, while a feature of the present invention may
have been described in the context of only one of the illustrated
embodiments, such feature may be combined with one or more other
features of other embodiments, for any given application. It will
also be appreciated from the above that the fabrication of the
unique structures herein and the operation thereof also constitute
methods in accordance with the present invention.
[0129] The explanations and illustrations presented herein are
intended to acquaint others skilled in the art with the invention,
its principles, and its practical application. Those skilled in the
art may adapt and apply the invention in its numerous forms, as may
be best suited to the requirements of a particular use.
Accordingly, the specific embodiments of the present invention as
set forth are not intended as being exhaustive or limiting of the
invention. The scope of the invention should, therefore, be
determined not with reference to the above description, but should
instead be determined with reference to the appended claims, along
with the full scope of equivalents to which such claims are
entitled. The disclosures of all articles and references, including