United States Patent
Application |
20070200272 |
Kind Code |
A1 |
Horst; David E. ; et
al. |
August 30, 2007 |
Viscosity breaking process for olefin polymers
Abstract
Disclosed is a method for viscosity breaking of a polypropylene
polymer, a polypropylene copolymer or a polypropylene polymer
blend, which process comprises adding a chain transfer agent and an
initiator to a polypropylene polymer, polypropylene copolymer or
polypropylene polymer blend and heating the resultant composition.
The chain transfer agent has a Cs value of greater than or equal to
about 0.04 as measured in ethylene polymerization at 130.degree. C.
The initiator is for example an organic or inorganic peroxide, a
carbon based radical generator, a bis azo compound, a stable
nitroxyl compound, a sterically hindered NO-acyl compound or a
sterically hindered alkoxyamine compound.
Inventors: |
Horst; David E.; (Danbury,
CT) ; Roth; Michael; (Lautertal, DE) ;
Nesvadba; Peter; (Marly, CH) |
Correspondence
Address: |
CIBA SPECIALTY CHEMICALS CORPORATION;PATENT DEPARTMENT
540 WHITE PLAINS RD
P O BOX 2005
TARRYTOWN
NY
10591-9005
US
|
Family ID: |
37963757 |
Appl. No.: |
11/708943 |
Filed: |
February 20, 2007 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
60776572 |
Feb 24, 2006 |
|
|
|
Current U.S.
Class: |
264/211.24 ;
264/349; 525/333.7; 525/375; 525/376; 525/387 |
Current CPC
Class: |
C08F 2810/10 20130101;
C08F 2500/12 20130101; C08F 110/06 20130101; B29K 2023/0641
20130101; B29C 48/00 20190201; C08L 23/10 20130101; C08F 8/50
20130101; C08F 110/06 20130101; C08F 8/50 20130101; C08F 110/06
20130101; B29K 2023/12 20130101; B29C 48/03 20190201; C08L 2023/42
20130101; C08F 2500/02 20130101; C08F 8/06 20130101 |
Class at
Publication: |
264/211.24 ;
264/349; 525/375; 525/376; 525/387; 525/333.7 |
International
Class: |
B29C 47/78 20060101
B29C047/78 |
Claims
1. A method for viscosity breaking of a polypropylene polymer, a
propylene copolymer or a polypropylene polymer blend, which method
comprises adding a chain transfer agent and an initiator to the
polypropylene polymer, propylene copolymer or polypropylene polymer
blend and heating the resultant composition, wherein the chain
transfer agent has a Cs value of greater than or equal to about
0.04 as measured in ethylene polymerization at 130.degree. C.
2. A method according to claim 1 wherein the chain transfer agent
is selected from the group consisting of thiols, disulfides,
phosphorus acid ester, phosphines, organic iodides, organic
chlorides, propionic acid esters, adehydes or tertiary amines.
3. A method according to claim 1 where the chain transfer agent is
a thiol, a disulfide or a tertiary amine.
4. A method according to claim 1 where the chain transfer agent is
a thiol or a disulfide of the formulae R--S-A or R--S--S--R where R
is an mono, di, tri or tetravalent hydrocarbyl group attached to
the sulfur atom with a carbon atom and A is hydrogen or
--SO.sub.3.sup.-B.sup.+ where B.sup.+ is an organic or inorganic
cation.
5. A method according to claim 1 where the chain transfer agent is
a thiol or a disulfide of the formulae R--S-A or R--S--S--R where R
is C.sub.8-C.sub.22alkyl, hydroxy-C.sub.2-C.sub.8alkyl,
mercapto-C.sub.2-C.sub.8alkyl, mercapto-C.sub.8-C.sub.20alkyl
interrupted by one or more --NH-- groups,
mercapto-C.sub.8-C.sub.20alkyl interrupted by one or more --OCO--
groups, mercapto-C.sub.8-C.sub.18alkyl substituted by one or more
hydroxyl groups, C.sub.6-C.sub.10aryl or is C.sub.6-C.sub.10aryl
substituted by one or more substituents selected from the group
consisting of C.sub.1-C.sub.4alkyl, 4-thiophenyl,
3-methyl-4-thiophenyl and
C.sub.6-C.sub.10aryl-C.sub.1-C.sub.4alkyl.
6. A method according to claim 1 where the initiator is an organic
or inorganic peroxide, a carbon based radical generator, a bis azo
compound, a stable nitroxyl compound, a sterically hindered NO-acyl
compound or is a sterically hindered alkoxyamine compound.
7. A method according to claim 1 where the initiator is an organic
or an inorganic peroxide which is
2,5-dimethyl-2,5-di(t-butylperoxy)hexane,
2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3,3,6,6,9,9-pentamethyl-3-(ethyl
acetate)-1,2,4,5-tetraoxy cyclononane, t-butyl hydroperoxide,
hydrogen peroxide, dicumyl peroxide, t-butyl peroxy isopropyl
carbonate, di-t-butyl peroxide, p-chlorobenzoyl peroxide, dibenzoyl
diperoxide, t-butyl cumyl peroxide; t-butyl hydroxyethyl peroxide,
di-t-amyl peroxide and 2,5-dimethylhexene-2,5-diperisononanoate,
acetylcyclohexanesulphonyl peroxide, diisopropyl peroxydicarbonate,
tert-amyl perneodecanoate, tert-butyl-perneodecanoate,
tert-butylperpivalate, tert-amylperpivalate,
bis(2,4-dichlorobenzoyl)peroxide, diisononanoyl peroxide,
didecanoyl peroxide, dioctanoyl peroxide, dilauroyl peroxide,
bis(2-methylbenzoyl)peroxide, disuccinoyl peroxide, diacetyl
peroxide, dibenzoyl peroxide, tert-butyl per-2-ethylhexanoate,
bis(4-chlorobenzoyl)peroxide, tert-butyl perisobutyrate, tert-butyl
permaleate, 1,1-bis(tert-butylperoxy)-3,5,5-trimethylcyclohexane,
1,1-bis(tert-butylperoxy)cyclohexane, tert-butyl peroxyisopropyl
carbonate, tert-butyl perisononaoate, 2,5-dimethylhexane
2,5-dibenzoate, tert-butyl peracetate, tert-amyl perbenzoate,
tert-butyl perbenzoate, 2,2-bis(tert-butylperoxy)butane,
2,2-bis(tert-butylperoxy)propane, dicumyl peroxide,
2,5-dimethylhexane 2,5-di-tert-butylperoxid,
3-tert-butylperoxy-3-phenyl phthalide, di-tert-amyl peroxide,
.alpha.,.alpha.'-bis(tert-butylperoxyisopropyl)benzene,
3,5-bis(tert-butylperoxy)-3,5-dimethyl-1,2-dioxolane, di-tert-butyl
peroxide, 2,5-dimethylhexyne 2,5-di-tert-butyl peroxide,
3,3,6,6,9,9-hexamethyl-1,2,4,5-tetraoxacyclononane, p-menthane
hydroperoxide, pinane hydroperoxide, diisopropylbenzene
mono-.alpha.-hydroperoxide, cumene hydroperoxide or tert-butyl
hydroperoxide.
8. A method according to claim 1 where the initiator is an azo
compound which is 2,2'-azobisisobutyronitrile,
2,2'-azobis(2-methylbutyronitrile),
2,2'-azobis(2,4-dimethylvaleronitrile),
2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile),
1,1'-azobis(1-cyclohexanecarbonitrile),
2,2'-azobis(isobutyramide)dihydrate,
2-phenylazo-2,4-dimethyl-4-methoxyvaleronitrile, dimethyl
2,2'-azobisisobutyrate, 2-(carbamoylazo)isobutyronitrile,
2,2'-azobis(2,4,4-trimethylpentane), 2,2'-azobis(2-methylpropane),
2,2'-azobis(N,N'-dimethyleneisobutyramidine) as free base or
hydrochloride, 2,2'-azobis(2-amidinopropane) as free base or
hydrochloride,
2,2'-azobis{2-methyl-N-[1,1-bis(hydroxymethyl)ethyl]propionamide}
or
2,2'-azobis{2-methyl-N-[1,1-bis(hydroxymethyl)-2-hydroxyethyl]propionamid-
e}.
9. A method according to claim 1 where the initiator is a stable
nitroxyl compound which is of the formula ##STR14## or which
contains one or more groups of the formula ##STR15## where each R
is methyl or ethyl and T is a group required to complete a 5- or
6-membered ring.
10. A method according to claim 1 where the initiator is a stable
nitroxyl compound which is
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate,
4-hydroxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-ethoxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-propoxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-acetamido-1-oxyl-2,2,6,6-tetramethylpiperidine,
1-oxyl-2,2,6,6-tetramethylpiperidine,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-one,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl acetate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 2-ethylhexanoate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl stearate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl benzoate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 4-t-butyl-benzoate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)succinate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)n-butylmalonate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)phthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)isophthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)terephthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)hexahydroterephthalate,
N,N'-bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipamide,
N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)caprolactam,
N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)dodecylsuccinimide,
2,4,6-tris-[N-butyl-N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)]-s-triaz-
ine, 4,4'-ethylenebis(1-oxyl-2,2,6,6-tetramethylpiperazin-3-one),
2-oxyl-1,1,3,3-tetramethyl-2-isobenzazole,
1-oxyl-2,2,5,5-tetramethylpyrrolidine or
N,N-bis-(1,1,3,3-tetramethylbutyl)nitroxide.
11. A method according to claim 1 where the initiator is a
sterically hindered NO-acyl compound that contains one or more of
the moieties of the formula ##STR16##
12. A method according to claim 1 where the initiator is a
sterically hindered alkoxyamine compound contains one or more
moieties of the formula ##STR17## where R is C.sub.1-C.sub.20alkyl,
OH-substituted C.sub.1-C.sub.20alkyl or
C.sub.5-C.sub.12cycloalkyl.
13. A method according to claim 1 where the chain transfer agent
and the initiator are present from about 10 ppm to about 2000 ppm
by weight, based on the weight of the polypropylene polymer,
propylene copolymer or polypropylene polymer blend.
14. A method according to claim 1 where the weight:weight ratio of
initiator to chain transfer agent is between about 1:10 to about
10:1.
15. A method according to claim 1 where the heating takes place in
an extruder.
16. A method according to claim 1 where the heating takes place
between about 160.degree. C. and about 280.degree. C.
17. A polymer composition comprising a polypropylene polymer, a
polypropylene copolymer or a polypropylene blend, a chain transfer
agent and an initiator, wherein the chain transfer agent has a Cs
value of greater than or equal to about 0.04 as measured in
ethylene polymerization at 130.degree. C.
Description
[0001] This application claims benefit of U.S. provisional
application No. 60/776,572, filed Feb. 24, 2006, the contents of
which are hereby incorporated by reference.
[0002] Disclosed are polypropylene, propylene copolymer or
polypropylene blend compositions and a process for viscosity
breaking (vis-breaking) of polypropylene, propylene copolymers or
polypropylene blends.
[0003] The controlled preparation of polyolefin grades (polymer
types having different molar masses, melt viscosities, densities,
molar mass distributions, etc.) by customary compounding methods,
for example by extrusion or injection molding, is a routine process
employed by polymer manufacturers and polymer processors/
compounders.
[0004] The setting of the desired parameters, for example the melt
viscosity, by means of this polymer process step is critically
dependent on the controlled reactivity and mode of action of the
additives employed.
[0005] The use of free radical initiators for modifying the melt
viscosity (rheology) of polyolefins is a generally known method.
Whether it results in a lowering of the molecular weight
(degradation) or an increase in the molecular weight (crosslinking)
depends primarily on the chemical structure of the polyolefin.
[0006] The reaction of a polymer of the polypropylene type with a
free radical initiator during a polymer processing step generally
results in the degradation of the polymer, whereas polymers of the
polyethylene type tend to crosslink.
[0007] In the case of copolymers and terpolymers or copolymer
blends, high proportions of propylene produce polypropylene like
behavior, while high proportions of ethylene result in polyethylene
like behavior. If the above mentioned copolymers and terpolymers or
copolymer blends comprise proportions of multiply unsaturated
olefins, the probability of crosslinking decreases with decreasing
concentration of free double bonds.
[0008] The controlled degradation of polypropylene (PP) to give a
product having a lower molecular weight and a narrower molecular
weight distribution is a commercially important process for
producing `controlled rheology` polypropylene (CR-PP). See for
example Plastic Additives Handbook, 5.sup.th ed., H. Zweifel, Ed.,
2001, Hanser publishers, pp. 791-796. While specific PP grades
("reactor grades") are obtainable by optimization of the synthesis
process or the catalyst systems (metallocene catalyst, Ziegler
catalyst), standard PP grades are frequently modified in process
technology by means of a processing step following the
synthesis.
[0009] Known degradation processes proceed either thermally, in
particular at temperatures above 280.degree. C., or in the presence
of free radical initiators. In process technology, the free radical
induced process is carried out in extruders or injection molding
machines at temperatures above for example 180.degree. C. Suitable
free radical initiators are organic peroxides which are added
during the processing step in diluted form (PP Mastermix, diluted
in oil, stabilized on inorganic supports) or directly as a liquid.
Under the given processing conditions, the peroxide disintegrates
into free radicals, which initiate the chain cleavage reactions and
form polymers having the desired rheological properties (desired
melt viscosities). The degradation of a PP to form a product having
a lower molecular weight (higher melt flow rate (MFR)) is generally
referred to as a viscosity-breaking or a vis-breaking process. The
process is also referred to as a controlled rheology process.
[0010] CR-PP grades are mainly used for fiber applications and
injection molding applications in which low melt viscosities are a
prerequisite for economical processing. A wide range of melt
viscosities or molecular weights is nowadays required in process
technology.
[0011] A further parameter that influences the processing behavior
of the polymer, in addition to the molecular weight, is the
molecular weight distribution (MWD). While polymer grades having
broad MWDs display improved orientation behavior of the polymer
chains at low pull-off speeds in a fiber spinning process, the
reverse is the case for high pull off speeds and broad MWDs. For
this reason, narrow MWDs are essential at high pull-off speeds in
order to achieve improved continuity in the spinning process.
[0012] The use of peroxides has a drawback, since only a restricted
"processing temperature window" is available because of their
decomposition temperatures, which are generally below the customary
temperatures of polymer processing. In addition, strict safety
regulations have to be adhered to during storage, handling and
processing of peroxides. A further disadvantage of peroxides is the
impossibility of decomposition-free melt compounding with
polymers.
[0013] Apart from peroxides, other sources of free radicals are
also known, e.g. C-radical generators based on cumyl systems, but
these can be used only at temperatures above 280.degree. C.
[0014] U.S. Pat. No. 6,133,414 describes a process for reducing the
molecular weight of polymers at temperatures above 280.degree. C.
using so-called NOR-HALS (HALS: Hindered Amino Light Stabilizers),
compounds containing the group: ##STR1##
[0015] wherein G is hydrogen or methyl and G.sub.1 and G.sub.2 are
each hydrogen, methyl or are together oxo. These known NOR-HALS
compounds produce appreciable polymer degradation only at
temperatures above 280.degree. C.
[0016] Published U.S. app. No. 2003/216494 discloses a process for
reducing the molecular weight of polypropylene, propylene
copolymers or polypropylene blends, wherein a hydroxylamine ester
of the formula: ##STR2##
[0017] wherein among others R.sub.a' is a monoacyl radical and
R.sub.1-R.sub.4 are alkyl-substituents; is added to the
polypropylene polymers to be degraded, and the mixture is heated to
temperatures below 280.degree. C.
[0018] U.S. Pat. No. 6,599,985 teaches the preparation of high melt
flow rate propylene polymers with the aid of cracking-resistant
polymers.
[0019] One issue that is common to the process of visbreaking is
the formation of volatile components. The condensable portion of
volatiles produced during visbreaking or compounding is called
"smoke". U.S. Pat. No. 5,834,541 discusses a way to reduce smoke
formation by using a stabilization system containing among other
ingredients,
2,2',2''-nitrilo[triethyl-tris(3,3'5,5'-tetra-tert-butylphenyl)phosphate.
[0020] The Polymer Handbook (4.sup.th Ed., John Wiley & Sons,
Ed. Brandrup, Innergut, and Grulke) discusses the use of chain
transfer agents for reducing the molecular weight in free radical
polymerization. A chain transfer agent works during free radical
polymerization by reacting with a growing polymer radical to form
dead polymer and a new radical. The dimensionless transfer
constant, C.sub.s is defined as the ratio of the rate constant for
transfer of a radical to the chain transfer agent to the rate
constant for propagation of the polymer chain by reaction with
monomer. Experimental values for C.sub.s obtained during free
radical polymerization of various monomers are compiled in the
Polymer Handbook.
[0021] The present invention relates to the problem of improving
the cited art with a more efficient method of vis-breaking
polypropyelene. The present process further minimizes smoke
(volatiles) generation during vis-breaking of polypropylene
polymers. Likewise, the present invention will minimize smoke
generation during any high temperature melt processing of PP. In
addition, the required amount of initiator to achieve a desired
amount of vis-breaking is reduced.
SUMMARY
[0022] Disclosed is a method for viscosity breaking of a
polypropylene polymer, a propylene copolymer or a polypropylene
polymer blend,
[0023] which method comprises
[0024] adding a chain transfer agent and an initiator to the
polypropylene polymer, propylene copolymer or polypropylene polymer
blend and heating the resultant composition,
[0025] wherein the chain transfer agent has a Cs value of greater
than or equal to about 0.04 as measured in ethylene polymerization
at 130.degree. C.
[0026] Also disclosed is a polymer composition comprising
[0027] a polypropylene polymer, a polypropylene copolymer or a
polypropylene blend,
[0028] a chain transfer agent and
[0029] an initiator,
[0030] wherein the chain transfer agent has a Cs value of greater
than or equal to about 0.04 as measured in ethylene polymerization
at 130.degree. C.
DETAILED DISCLOSURE
Polypropylene Polymer, Propylene Copolymer or Polypropylene Polymer
Blend
[0031] The present polypropylene type polymers to be degraded may
encompass propylene homopolymers, propylene copolymers and
polypropylene blends. Propylene copolymers may contain various
proportions, for example up to about 90%, or up to about 50%, of
comonomers. Examples of comonomers such are: olefins such as
1-olefins, e.g. ethylene, 1-butene, 1-pentene, 1-hexene, 1-heptene
or 1-octene, isobutylene; cycloolefins, e.g. cyclopentene,
cyclohexene, norbornene or ethylidenenorborne; dienes such as
butadiene, isoprene, 1,4-hexadiene, cyclopentadiene,
dicyclopentadiene or norbornadiene; and also acrylic acid
derivatives and unsaturated carboxylic anhydrides such as maleic
anhydride.
[0032] Polypropylene blends which can be employed are for instance
mixtures of polypropylene with polyolefins. Examples are blends of
polypropylene with polyethylene selected from the group consisting
of high density polyethylene (HDPE), high molecular weight high
density polyethylene (HMW HDPE), ultra high molecular weight high
density polyethylene (UHMW HDPE), medium density polyethylene
(MDPE), low density polyethylene (LDPE), linear low density
polyethylene (LLDPE), branched low density polyethylene (BLDPE) and
ethylene-propylene-diene terpolymers (EPDM) containing small
proportions of diene.
Chain Transfer Agent
[0033] The present chain transfer agent has a Cs value of greater
than or equal to about 0.04 as measured in ethylene polymerization
at 130.degree. C.
[0034] The chain transfer agent may be of the class of thiols,
disulfides, phosphorus acid esters, phosphines, organic iodides,
organic chlorides, propionic (or higher) acid esters, aldehydes or
tertiary amines.
[0035] The table below shows some values of C.sub.s: TABLE-US-00001
*C.sub.S value for ethylene Compound polymerization at 130.degree.
C. decane 0.012 heptane 0.008 2-methyl propane 0.005, 0.0072 2,2,4
trimethyl pentane 0.0064 tributyl amine 0.082 trimethyl amine
0.018, 0.033 1,1-bis(dimethylamino) ethane 0.107 propionaldehyde
0.23, 0.33 heptaldehyde 0.26, 0.39 1-butanethiol 5.8 2-methyl
2-propanethiol 15 *values obtained from tables 4 or 5 of the
Polymer Handbook, 4.sup.th Ed., John Wiley & Sons, Ed.
Brandrup, Innergut, and Grulke
[0036] For instance, the Cs value for the present chain transfer
agents, as measured in ethylene polymerization at 130.degree. C. is
greater than or equal to about 0.05, greater than or equal to about
0.07, greater than or equal to about 0.08, greater than or equal to
about 0.1, greater than or equal to about 0.15, greater than or
equal to about 0.20, greater than or equal to about 0.50, greater
than or equal to about 1.0, or greater than or equal to about 2.0,
3.0, 4.0 or 5.0.
[0037] For example, the present thiols and disulfides are of the
formulae R--S-A or R--S--S--R
[0038] where
[0039] R is an mono, di, tri or tetravalent hydrocarbyl group
attached to the sulfur atom with a carbon atom and
[0040] A is hydrogen or --SO.sub.3.sup.-B.sup.+ where B.sup.+ is an
organic or inorganic cation.
[0041] Also included are thiouram sulfides, dithiocarbamates,
mercaptobenzthiazoles and sulfenamides.
[0042] R, as hydrocarbyl which is attached to the sulfur atom with
a carbon atom, is, for example, C.sub.8-C.sub.22alkyl,
hydroxy-C.sub.2-C.sub.8alkyl, mercapto-C.sub.2-C.sub.8alkyl,
mercapto-C.sub.8-C.sub.20alkyl interrupted by one or more --NH--
groups, mercapto-C.sub.8-C.sub.20alkyl interrupted by one or more
--OCO-- groups, mercapto-C.sub.8-C.sub.18alkyl substituted by one
or more hydroxyl groups, C.sub.6-C.sub.10aryl or is
C.sub.6-C.sub.10aryl substituted by one or more substituents
selected from the group consisting of C.sub.1-C.sub.4alkyl,
4-thiophenyl, 3-methyl-4-thiophenyl and
C.sub.6-C.sub.10aryl-C.sub.1-C.sub.4alkyl.
[0043] R defined as C.sub.8-C.sub.22alkyl is straight-chain or
branched C.sub.8-C.sub.18alkyl e.g. n-octyl, isooctyl types, e.g.
3,4-, 3,5- or 4,5-dimethyl-1-hexyl or 3- or 5-methyl-1-heptyl,
other branched octyl types, such as 1,1,3,3-tetramethylbutyl or
2-ethylhexyl, n-nonyl, 1,1,3-trimethylhexyl, n-decyl, n-undecyl,
1-methylundecyl, 2-n-butyl-n-octyl, isotridecyl, 2-n-hexyl-n-decyl,
2-n-octyl-n-dodecyl or straight-chain C.sub.12-C.sub.19alkyl, e.g.
lauryl (C12), myristyl (C14), cetyl (C16) or n-octadecyl (C18).
[0044] R defined as hydroxy-C.sub.2-C.sub.8alkyl is, for example,
2-hydroxyethyl, 2- or 3-hydroxypropyl, 4-hydroxy-2-hexyl or
4-hydroxy-3-hexyl.
[0045] R defined as mercapto-C.sub.2-C.sub.8alkyl is, for example,
C.sub.2-C.sub.8alkyl substituted at the terminal carbon atom by a
thiol (mercapto) group, e.g. 6-mercapto-n-hexyl or
5-mercapto-n-pentyl.
[0046] R defined as mercapto-C.sub.8-C.sub.20alkyl interrupted by
one or more --NH-- groups is exemplified by the substituted
diamino-C.sub.2-C.sub.4alkylene groups: ##STR3## where * represents
the bond to the S-A group.
[0047] R defined as mercapto-C.sub.8-C.sub.18alkyl substituted by
one or more hydroxy groups is exemplified by the mercaptoethylene
glycol group ##STR4##
[0048] R as mercapto-C.sub.8-C.sub.20alkyl interrupted by one or
more --OCO-- groups is for example ##STR5##
[0049] R defined as C.sub.6-C.sub.10aryl is for example phenyl.
[0050] R defined as C.sub.6-C.sub.10aryl substituted by one or more
groups selected from the group consisting of C.sub.1-C.sub.4alkyl,
4-thiophenyl and 3-methyl-4-thiophenyl is exemplified by the
following partial formula: ##STR6## wherein R.sub.a and R.sub.b
independently of one another represent hydrogen or methyl.
[0051] R defined as C.sub.6-C.sub.10aryl-C.sub.1-C.sub.4alkyl is,
for example, benzyl, phen-1-ethyl or phenyl-2-ethyl.
[0052] A cation or a cationic group B.sup.+ is for example, an
alkali metal cation, e.g. sodium or potassium ion, ammonium ion,
tri-C.sub.1-C.sub.4alkylammonium ion, e.g. the tetramethyl- or
tetraethylammonium ion, or the cholinyl cation.
[0053] Suitable sulfur compounds, wherein R represents the above
defined hydrocarbyl group, which is attached to the sulfur atom
with a carbon atom and A represents hydrogen or the group ##STR7##
wherein B.sup.+ represents the above defined cation or a cationic
group, are for example represented by the following structural
formulae: ##STR8## wherein R.sub.a and R.sub.b independently of one
another represent hydrogen or methyl.
[0054] The sulfur compounds are known or can be obtained by known
methods.
Initiator
[0055] The present initiators are for example organic or inorganic
peroxides. Typical examples of suitable peroxides include
2,5-dimethyl-2,5-di(t-butylperoxy)hexane,
2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3,3,6,6,9,9-pentamethyl-3-(ethyl
acetate)-1,2,4,5-tetraoxy cyclononane, t-butyl hydroperoxide,
hydrogen peroxide, dicumyl peroxide, t-butyl peroxy isopropyl
carbonate, di-t-butyl peroxide, p-chlorobenzoyl peroxide, dibenzoyl
diperoxide, t-butyl cumyl peroxide; t-butyl hydroxyethyl peroxide,
di-t-amyl peroxide and 2,5-dimethylhexene-2,5-diperisononanoate,
acetylcyclohexanesulphonyl peroxide, diisopropyl peroxydicarbonate,
tert-amyl perneodecanoate, tert-butyl-perneodecanoate,
tert-butylperpivalate, tert-amylperpivalate,
bis(2,4-dichlorobenzoyl)peroxide, diisononanoyl peroxide,
didecanoyl peroxide, dioctanoyl peroxide, dilauroyl peroxide,
bis(2-methylbenzoyl)peroxide, disuccinoyl peroxide, diacetyl
peroxide, dibenzoyl peroxide, tert-butyl per-2-ethylhexanoate,
bis(4-chlorobenzoyl)peroxide, tert-butyl perisobutyrate, tert-butyl
permaleate, 1,1-bis(tert-butylperoxy)-3,5,5-trimethylcyclohexane,
1,1-bis(tert-butylperoxy)cyclohexane, tert-butyl peroxyisopropyl
carbonate, tert-butyl perisononaoate, 2,5-dimethylhexane
2,5-dibenzoate, tert-butyl peracetate, tert-amyl perbenzoate,
tert-butyl perbenzoate, 2,2-bis(tert-butylperoxy)butane, 2,2-bis
(tert-butylperoxy)propane, dicumyl peroxide, 2,5-dimethylhexane
2,5-di-tert-butylperoxid, 3-tert-butylperoxy-3-phenyl phthalide,
di-tert-amyl peroxide,
.alpha.,.alpha.'-bis(tert-butylperoxyisopropyl)benzene,
3,5-bis(tert-butylperoxy)-3,5-dimethyl-1,2-dioxolane, di-tert-butyl
peroxide, 2,5-dimethylhexyne 2,5-di-tert-butyl peroxide,
3,3,6,6,9,9-hexamethyl-1,2,4,5-tetraoxacyclononane, p-menthane
hydroperoxide, pinane hydroperoxide, diisopropylbenzene
mono-.alpha.-hydroperoxide, cumene hydroperoxide or tert-butyl
hydroperoxide.
[0056] Other known initiators are carbon based radical generators,
for example cumyl based systems.
[0057] Suitable bis azo compounds may also be employed as a source
of free radicals. Such azo compounds are for example
2,2'-azobisisobutyronitrile, 2,2'-azobis(2-methylbutyronitrile),
2,2'-azobis(2,4-dimethylvaleronitrile),
2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile),
1,1'-azobis(1-cyclohexanecarbonitrile),
2,2'-azobis(isobutyramide)dihydrate,
2-phenylazo-2,4-dimethyl-4-methoxyvaleronitrile, dimethyl
2,2'-azobisisobutyrate, 2-(carbamoylazo)isobutyronitrile,
2,2'-azobis(2,4,4-trimethylpentane), 2,2'-azobis(2-methyl-propane),
2,2'-azobis(N,N'-dimethyleneisobutyramidine) as free base or
hydrochloride, 2,2'-azobis(2-amidinopropane) as free base or
hydrochloride,
2,2'-azobis{2-methyl-N-[1,1-bis(hydroxymethyl)ethyl]propionamide}
or
2,2'-azobis{2-methyl-N-[1,1-bis(hydroxymethyl)-2-hydroxyethyl]propionamid-
e}.
[0058] Free radical initiators may also be selected from known
stable nitroxyl compounds. The nitroxyl initiators are for example
of the generic structure ##STR9##
[0059] or are compounds that contain one or more groups of the
formula ##STR10##
[0060] where each R is alkyl and T is a group required to complete
a 5- or 6-membered ring.
[0061] Two or more nitroxyl groups may be present in the same
molecule by being linked through the T moiety as exemplified below
where E is a linking group. ##STR11##
[0062] Typical nitroxyls include
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate,
4-hydroxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-ethoxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-propoxy-1-oxyl-2,2,6,6-tetramethylpiperidine,
4-acetamido-1-oxyl-2,2,6,6-tetramethylpiperidine,
1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-
2,2,6,6-tetramethylpiperidin-4-one,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl acetate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 2-ethylhexanoate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl stearate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl benzoate,
1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 4-t-butyl-benzoate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)succinate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)n-butylmalonate,
bis(1-oxyl-2, 2,6,6-tetramethylpiperidin-4-yl)phthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)isophthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)terephthalate,
bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)hexahydroterephthalate,
N,N'-bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipamide,
N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)caprolactam,
N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)dodecylsuccinimide,
2,4,6-tris-[N-butyl-N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)]-s-triaz-
ine, 4,4'-ethylenebis(1-oxyl-2,2,6,6-tetramethylpiperazin-3-one),
2-oxyl-1,1,3,3-tetramethyl-2-isobenzazole,
1-oxyl-2,2,5,5-tetramethylpyrrolidine, and
N,N-bis-(1,1,3,3-tetramethylbutyl)nitroxide.
[0063] Another suitable free radical initiator may be selected from
the group consisting of the NO-acyl hindered amine (sterically
hindered NO-acyl) compounds. These compounds are disclosed in
published U.S. app. No. 2003/0216494, the contents of which are
hereby incorporated by reference.
[0064] In particular, suitable NO-acyl compounds contain one or
more moieties of the formula ##STR12##
[0065] Further, initiators may also be selected from the group
consisting hindered N-alkoxy hindered amine compounds, for example
as disclosed in U.S. Pat. No. 6,133,414, the contents of which are
hereby incorporated by reference.
[0066] For instance, the suitable hindered N-alkoxy (NOR hindered
amine or sterically hindered alkoxyamine compound) contain one or
more moieties of the formula ##STR13##
[0067] where R is for instance C.sub.1-C.sub.20alkyl,
OH-substituted C.sub.1-C.sub.20alkyl or
C.sub.5-C.sub.12cycloalkyl.
[0068] The above mentioned free radical initiators employed for
controlled degradation are advantageously added to the
polypropylene polymers in amounts smaller than those customary when
they are used alone in the processes of the prior art.
[0069] In a further preferred embodiment of the present invention,
at least 2 different free radical initiators having different
decomposition temperatures are employed, so that the degradation of
the polymers may occur in 2 stages. This process is also referred
to as sequential degradation.
[0070] Suitable compositions comprise, for example, a combination
of the abovementioned peroxides and NOR-compounds or NO-acyl
compounds.
[0071] It is essential that the two decomposition temperatures are
sufficiently apart for effecting a 2-stage process. For example, a
peroxide having a decomposition temperature in the range of about
180 to about 220.degree. C. can be combined with an NO-acyl
compound having decomposition temperatures in the range of about
240 to about 280.degree. C. and/or with an NOR-compound having a
decomposition temperature above 300.degree. C.
[0072] It is of course possible to use mixtures of free radical
generators having different decomposition temperatures in the
process.
[0073] The addition to the polypropylene, propylene copolymers or
polypropylene blend can be carried out in all customary mixing
machines in which the polymer is melted and mixed with the
additives. Suitable machines are known to those skilled in the art.
They are predominantly mixers, kneaders and extruders.
[0074] According to a preferred embodiment of the invention the
additives are added to blends of polypropylene with polyethylene
selected from the group consisting of high density polyethylene
(HDPE), high molecular weight high density polyethylene (HMW HDPE),
ultra high molecular weight high density polyethylene (UHMW HDPE),
medium density polyethylene (MDPE), low density polyethylene
(LDPE), linear low density polyethylene (LLDPE), branched low
density polyethylene (BLDPE) and ethylene-propylene-diene
terpolymers (EPDM) containing small proportions of diene.
[0075] The process is preferably carried out in an extruder by
introducing the additives during processing.
[0076] Particularly preferred processing machines are single-screw
extruders, contra-rotating and co-rotating twin-screw extruders,
planetary-gear extruders, ring extruders or co-kneaders. It is also
possible to use processing machines provided with at least one gas
removal compartment to which a vacuum can be applied.
[0077] Suitable extruders and kneaders are described, for example,
in Handbuch der Kunststoffextrusion, Vol. 1 Grundlagen, Editors F.
Hensen, W Knappe, H. Potente, 1989, pp. 3-7, ISBN:3-446-14339-4
(Vol. 2 Extrusionsanlagen 1986, ISBN 3-446-14329-7). For example,
the screw length is 1-60 screw diameters, preferably 35-48 screw
diameters. The rotational speed of the screw is preferably 10-600
rotations per minute (rpm), very particularly preferably 25-300
rpm.
[0078] The maximum throughput is dependent on the screw diameter,
the rotational speed and the driving force. The process of the
present invention can also be carried out at a level lower than
maximum throughput by varying the parameters mentioned or employing
weighing machines delivering dosage amounts.
[0079] If a plurality of components are added, these can be
premixed or added individually. The polymers may need to be
subjected to an elevated temperature for a sufficient period of
time, so that the desired degradation occurs. The temperature is
generally above the softening point of the polymers.
[0080] In a preferred embodiment of the process of the present
invention, a temperature range lower than 280.degree. C.,
particularly from about 160.degree. C. to about 280.degree. C. is
employed. In a particularly preferred process variant, the
temperature range from about 200.degree. C. to about 270.degree. C.
is employed. The period of time necessary for degradation can vary
as a function of the temperature, the amount of material to be
degraded and the type of, for example, extruder used. It is usually
from about 10 seconds to 20 minutes, in particular from 20 seconds
to 10 minutes.
[0081] In the process for reducing the molecular weight
(degradation process) of the polypropylene polymers, the chain
transfer agent is added for example at a level of from about 10 to
about 2000 ppm by weight, based on the weight of the polymer. For
example, the chain transfer agent is present from about 50 to about
1500 ppm, or from about 100 to about 1000 ppm, based on the weight
of the polypropylene polymer.
[0082] The initiator is added in amounts within the same ranges as
the chain transfer agents. The weight:weight ratio of the initiator
to the chain transfer agent is between about 1:10 to about 10:1,
for example between about 1:9 to about 9:1, between about 1:8 to
about 8:1, between about 1:7 to about 7:1, between about 1:6 to
about 6:1, between about 1:5 to about 5:1, between about 1:4 to
about 4:1, between about 1:3 to about 3:1, between about 1:2 to
about 2:1, or between about 1:1.5 to about 1.5:1.
[0083] While the sometimes volatile decomposition products (smoke)
of peroxides (initiators) can lead to discoloration or odor in the
degraded polymers, very little discoloration and odor occurs in the
present process as the amount of peroxides is reduced and the
temperature may be reduced.
[0084] Incorporation into the polymers can be carried out, for
example, by mixing the above described additives and, if desired,
further additives into the polymers using the methods customary in
process technology.
[0085] Incorporation can, alternatively, also be carried out at
temperatures, which do not yet cause decomposition of the polymers
(latent compound). The polymers prepared in this way can
subsequently be heated a second time and subjected to an elevated
temperature for a sufficient period of time so that the desired
polymer degradation occurs.
[0086] The present additives can also be added to the polymers to
be degraded in the form of a masterbatch, in which these compounds
are present, for example, in a concentration of from about 1.0 to
about 25.0% by weight. The masterbatch (concentrate) can be
produced at temperatures, which do not yet cause decomposition of
the compounds of the present invention.
[0087] This provides a product, which is defined by specific dosage
amounts and may be compounded with other additives. The masterbatch
can then be compounded with the polymer to be degraded.
[0088] The present invention therefore further provides a
concentrate in which the chain transfer compounds are present in a
concentration of about 1.0 about 25.0% by weight and which can be
added to the polymer to be degraded. The desired product is thus
obtainable in an advantageous two-stage process.
[0089] In a specific embodiment, suitable further additives, such
as metal salts, e.g. of Ca, Fe, Zn or Cu, are added to the polymers
to be degraded. Particular preference is given to the presence of a
metal salt selected from the group consisting of CaO, CaCO.sub.3,
ZnO, ZnCO.sub.3, MgO, MgCO.sub.3 and Mg(OH).sub.2.
[0090] Apart from the additives discussed herein, further additives
may also be present in the polymer. For example, additives selected
from the group consisting of the dialkylhydroxylamine, sterically
hindered amine, phenolic antioxidant, benzofuranone, organic
phosporus compounds and hydroxyphenylbenzotriazole,
hydroxyphenyl-s-triazine or benzophenone ultraviolet light
absorbers.
[0091] For instance, further additives are stabilizers selected
from the group consisting of pentaerythrityl
tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate),
octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate),
3,3',3',5,5',5'-hexa-tert-butyl-.alpha.,.alpha.',.alpha.'-(mesitylene-2,4-
,6-triyl)tri-p-cresol, calcium diethyl
bis(((3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl)methyl)phosphonate),
1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-1,3,5-triazine-2,4,6(1H
,3H,5H)trione, tris(2,4-di-tert-butylphenyl)phosphite,
tris(nonylphenyl)phosphite,
tetrakis(2,4-di-tert-butylphenyl)[1,1-biphenyl]-4,4'-diylbisphosphonite,
didodecyl 3,3'-thiodipropionate, dioctadecyl 3,3'-thiodipropionate,
5,7-di-tert-butyl-3-(3,4-dimethylphenyl)-3H-benzofuran-2-one and
di-hydrogenated-tallowalkylhydroxylamine.
[0092] Further additives are antacids, such as calcium stearate or
zinc stearate, hydrotalcites or calcium lactate or calcium
lactylate.
[0093] The invention is illustrated by the following Examples.
Levels are in weight percent based on polyolefin unless otherwise
indicated.
EXAMPLE 1
[0094] Polypropylene homopolymer manufactured by the Spheripol
process, nominal melt index 4.6 dg/min (2.36 kg/230.degree. C.),
commercially available as Profax.RTM. 6501 from Basell Polyolefins,
is visbroken to a target melt index of 38 by compounding the
polymer with 2,5-dimethyl-2,5-di-tertbutylperoxy-hexane (DTBPH).
The amount of DTBPH is adjusted as necessary in order to obtain the
target melt flow. Base stabilization is 1000 ppm of
tris(2,4-di-tert-butylphenyl)phosphite, 500 ppm of a
di-hydrogenated-tallowalkylhydroxylamine processing stabilizer and
500 ppm of calcium lactate. The formulation of the present
invention is additionally compounded with 200 ppm of
pentaerythritol tetrakis(3-mercaptopropionate) (PTOP; CASRN
7575-23-7; available from Aldrich chemical company) or with 356 ppm
tri-dodecylamine as chain transfer agents. The formulations are
visbroken on an MPM single screw extruder. The extruder is fitted
with a polyolefin screw with a Maddock mixing head operated at 90
RPM. The four zone temperatures are set at 475,500,525, and
525.degree. F. The extruder has a length to diameter ratio of 24:1.
The results are the average of 2 experiments. Results are below.
TABLE-US-00002 Formulation Chain Transfer Agent Amount of DTBPH
Required control none 642 ppm 1 200 ppm PTOP 241 ppm 2 356 ppm
tri-dodecylamine 540 ppm
[0095] It is seen that the additional compounding with the present
chain transfer agents results in a significant reduction of the
amount of initiator required.
EXAMPLE 2
[0096] Example 1 is repeated, with base stabilization of 1000 ppm
tris(2,4-di-tert-butylphenyl)phosphite, 500 ppm
di-hydrogenated-tallowalkylhydroxylamine and 250 ppm calcium
lactate. In this experiment, the amount of the peroxide DTBPH is
varied. Melt flow with and without 200 ppm PTOP is shown in the
following table. TABLE-US-00003 Melt Flow peroxide ppm control
control + 200 ppm PTOP 0 3.7 3.9 100 6.1 7.8 200 9.5 22.7 300 12.8
41.0 450 18.2 74.2 600 28.3 136.8
[0097] It is seen that far greater melt flow rates are achieved
with formulations of the present invention that include both a
peroxide and a certain chain transfer agent.
EXAMPLE 3
[0098] Example 1 is repeated, with base stabilization of 1000 ppm
phosphate process stabilizer, 500 ppm
di-hydrogenated-tallowalkylhydroxylamine and 250 ppm calcium
lactate. Again, PP homopolymer is visbroken to a target melt flow
of 38 dg/min with the initiator as in Example 1. With no chain
transfer agent, 642 ppm of DTBPH are required, with 200 ppm PTOP,
241 ppm of DTBPH are required. The following procedure is used to
estimate the relative proportions of low molecular weight fragments
that are produced during the visbreaking process. The polymer
pellets from the extruder are contacted with methylene chloride at
room temperature for a duration of 2 days shaking occasionally each
of the samples. The ratio of polymer to methylene chloride is 40 g
to 100 g.
[0099] The extracts are shot on a GC with a constant injection
volume of 1 micro liter. The peaks between 3 minutes and 20.5
minutes are integrated and summed and considered as volatiles
(extractables). The GC is performed under the following conditions:
30 m ZB-5 capillary column (equivalent to DB-5), temperature
program is 40.degree. C. held for 1 minute then programmed at
15.degree. C. per minute to 300.degree. C. and held. The integrated
counts for the various formulations are shown below. TABLE-US-00004
chain transfer agent counts none 9635 none 10497 none 9879 none*
10305 200 ppm PTOP 5203 *contains 1000 ppm of pentaerythrityl
tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate in place
of the hydroxylamine stabilizer.
[0100] The presence of the chain transfer agent PTOP during the
visbreaking results in a significant reduction in the amount of low
molecular weight extractable material produced during the
visbreaking process.
EXAMPLE 4
[0101] Polypropylene homopolymer (Moplen.RTM. FLF20 from Basell) is
visbroken with 500 ppm of DTBPH and varying amounts of octadecane
thiol (C18-SH). All of the formulations contained base
stabilization of 500 ppm of pentaerythrityl
tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, 500 ppm
of tris(2,4-di-tert-butylphenyl)phosphite, and 500 ppm of calcium
stearate. The extrusion temperature is 250.degree. C. The melt flow
rate is determined at 230.degree. C. using a 2.16 kg weight with a
die diameter of 0.75 mm. The results are shown below.
TABLE-US-00005 amount of C18-SH MFR none 4.0 62 ppm 7.7 125 ppm
11.9 250 ppm 14.2
* * * * *