U.S. patent application number 11/338785 was filed with the patent office on 2006-08-03 for photothermographic material.
This patent application is currently assigned to FUJI PHOTO FILM CO., LTD.. Invention is credited to Kouta Fukui.
Application Number | 20060172234 11/338785 |
Document ID | / |
Family ID | 36756978 |
Filed Date | 2006-08-03 |
United States Patent
Application |
20060172234 |
Kind Code |
A1 |
Fukui; Kouta |
August 3, 2006 |
Photothermographic material
Abstract
A photothermographic material having, on at least one side of a
support, an image forming layer including at least a photosensitive
silver halide, a non-photosensitive organic silver salt, a reducing
agent, and a binder, wherein 1) the binder includes a polymer latex
having a monomer component represented by formula (M):
CH.sub.2.dbd.CR.sup.01--CR.sup.02.dbd.CH.sub.2 Formula (M) 2) the
photothermographic material includes a compound represented by
formula (SA): ##STR1## and 3) the photothermographic material
further includes a metal phthalocyanine dye represented by formula
(PC-1): ##STR2## wherein at least one of R.sup.1, R.sup.4, R.sup.5,
R.sup.8, R.sup.9, R.sup.12, R.sup.13, and R.sup.16 is an
electron-attracting group. The invention provides a
photothermographic material which produces an image free from
unevenness in color tone, having high image quality, and is
excellent in image storability.
Inventors: |
Fukui; Kouta; (Kanagawa,
JP) |
Correspondence
Address: |
TAIYO CORPORATION
401 HOLLAND LANE
#407
ALEXANDRIA
VA
22314
US
|
Assignee: |
FUJI PHOTO FILM CO., LTD.
|
Family ID: |
36756978 |
Appl. No.: |
11/338785 |
Filed: |
January 25, 2006 |
Current U.S.
Class: |
430/619 |
Current CPC
Class: |
G03C 2200/36 20130101;
G03C 1/49863 20130101; G03C 1/49845 20130101; G03C 1/49854
20130101 |
Class at
Publication: |
430/619 |
International
Class: |
G03C 1/00 20060101
G03C001/00 |
Foreign Application Data
Date |
Code |
Application Number |
Jan 28, 2005 |
JP |
2005-22108 |
Claims
1. A photothermographic material comprising, on at least one side
of a support, an image forming layer comprising at least a
photosensitive silver halide, a non-photosensitive organic silver
salt, a reducing agent, and a binder, wherein (1) the binder
comprises a polymer latex having a monomer component represented by
the following formula (M):
CH.sub.2.dbd.CR.sup.01--CR.sup.02.dbd.CH.sub.2 Formula (M) wherein
R.sup.01 and R.sup.02 each independently represent one selected
from a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, a
halogen atom, or a cyano group; and R.sup.01 and R.sup.02 are not
simultaneously a hydrogen atom; (2) the photothermographic material
comprises a compound represented by the following formula (SA):
##STR80## wherein M represents a hydrogen atom or a cation having a
valency of k; R represents a substituent; n represents an integer
of from 1 to 4; when n is 2 or more, a plurality of R may be the
same or different from one another; k represents an integer of 1 or
more; and when M is a hydrogen atom, k is 1; and (3) the
photothermographic material further comprises a metal
phthalocyanine dye represented by formula (PC-1): ##STR81##
wherein, M represents a metal atom; R.sup.1, R.sup.4, R.sup.5,
R.sup.8, R.sup.9, R.sup.12, R.sup.13, and R.sup.16 each
independently represent a hydrogen atom or a substituent; at least
one of R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9, R.sup.12,
R.sup.13, and R.sup.16 is an electron-attracting group; and
R.sup.2, R.sup.3, R.sup.6, R.sup.7, R.sup.10, R.sup.11, R.sup.14,
and R.sup.15 each independently represent a hydrogen atom or a
substituent.
2. The photothermographic material according to claim 1, wherein,
in formula (SA), M represents a metallic ion selected from the
group consisting of zinc, iron, manganese, cadmium, chromium,
cobalt, ruthenium, rhodium, and silver.
3. The photothermographic material according to claim 1, wherein,
in formula (SA), the substituent represented by R is one selected
from the group consisting of an alkyl group, an alkenyl group, an
alkynyl group, an aralkyl group, an aryl group, an amino group, an
alkoxy group, an acyl group, an alkoxycarbonyl group, an acyloxy
group, an acylamino group, alkoxycarbonylamino group, a
sulfonylamino group, a sulfamoyl group, a carbamoyl group, a ureido
group, an alkylthio group, a sulfonyl group, a hydroxy group, a
mercapto group, a halogen atom, a cyano group, a sulfo group, a
carboxy group, a nitro group, and a heterocyclic group.
4. The photothermographic material according to claim 3, wherein,
in formula (SA), the substituent represented by R is one selected
from the group consisting of an alkyl group, an alkenyl group, an
aralkyl group, an amino group, an alkoxy group, an alkylthio group,
a hydroxy group, a mercapto group, a halogen atom, a sulfo group,
and a carboxy group.
5. The photothermographic material according to claim 1, wherein,
in formula (SA), R represents an alkyl group which substitutes at
at least one of an ortho-position and a para-position of the OH
group of formula (SA).
6. The photothermographic material according to claim 1, wherein,
in formula (M), R.sup.01 represents a hydrogen atom, and R.sup.02
represents a methyl group.
7. The photothermographic material according to claim 1, wherein
the polymer latex is a polymer latex which contains a monomer
having an acid group in a range of from 1% by weight to 20% by
weight as a copolymer component.
8. The photothermographic material according to claim 1, wherein,
in formula (PC-1), at least one of R.sup.1, R.sup.4, R.sup.5,
R.sup.8, R.sup.9, R.sup.12, R.sup.13, and R.sup.16 is a group
represented by the following formula (II): -L.sup.1-R.sup.17
Formula (II) wherein L.sup.1 represents a group selected from
**--SO.sub.2--*, **--SO.sub.3--*, **--SO.sub.2NR.sub.N--*,
**--SO--*, **--CO--*, **--CONR.sub.N--*, **--COO--*, **--COCO--*,
**--COCO.sub.2--*, and **--COCONR.sub.N--*; ** denotes a bond with
a phthalocyanine skeleton at this position, and * denotes a bond
with R.sup.17 at this position; R.sub.N represents one selected
from a hydrogen atom, an alkyl group, an aryl group, a heterocyclic
group, an acyl group, an alkoxycarbonyl group, a carbamoyl group, a
sulfonyl group, or a sulfamoyl group; and R.sup.17 represents one
selected from a hydrogen atom, an alkyl group, an aryl group, or a
heterocyclic group.
9. The photothermographic material according to claim 8, wherein
four or more from among R.sup.1, R.sup.4, R.sup.5, R.sup.8,
R.sup.9, R.sup.12, R.sup.13, and R.sup.16 in formula (PC-1) are a
group represented by formula (II).
10. The photothermographic material according to claim 9, wherein
the metal phthalocyanine dye is water soluble.
11. The photothermographic material according to claim 8, wherein,
in formula (PC-1), R.sup.2, R.sup.3, R.sup.6, R.sup.7, R.sup.10,
R.sup.11, R.sup.14, and R.sup.15 are each a hydrogen atom; and at
least one of R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9, R.sup.12,
R.sup.13, and R.sup.16 is a group represented by formula (II).
12. The photothermographic material according to claim 11, wherein
four or more from among R.sup.1, R.sup.4, R.sup.5, R.sup.8,
R.sup.9, R.sup.12, R.sup.13, and R.sup.16 in formula (PC-1) are a
group represented by formula (II).
13. The photothermographic material according to claim 12, wherein
the metal phthalocyanine dye is water soluble.
Description
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application claims priority under 35 USC 119 from
Japanese Patent Application No. 2005-022108, the disclosure of
which is incorporated by reference herein.
BACKGROUND OF THE INVENTION
[0002] 1. Field of the Invention
[0003] The present invention relates to a photothermographic
material preferably used in the field of films for medical
diagnosis, the field of films for graphic arts, or the like.
[0004] 2. Description of the Related Art
[0005] In recent years, in the medical field and the graphic arts
field, there has been a strong desire for providing a dry
photographic process from the viewpoints of protecting the
environment and economy of space. Further, the development of
digitization in these fields has resulted in the rapid development
of systems in which image information is captured and stored in a
computer, and then when necessary processed and output by
transmitting it to a desired location. Here the image information
is output onto a photosensitive material using a laser image setter
or a laser imager, and developed to form an image at the location.
It is necessary for the photosensitive material to be able to
record an image with high-intensity laser exposure and that a clear
black-tone image with a high resolution and sharpness can be
formed. While various kinds of hard copy systems using pigments or
dyes, such as ink-jet printers or electrophotographic systems, have
been distributed as general image forming systems using such
digital imaging recording materials, images on the digital imaging
recording materials obtained by such general image forming systems
are insufficient in terms of the image quality (sharpness,
granularity, gradation, and tone) needed for medical images used in
making diagnoses, and high recording speeds (sensitivity). These
kinds of digital imaging recording materials have not reached a
level at which they can replace medical silver halide film
processed with conventional wet development.
[0006] Photothermographic materials utilizing organic silver salts
are already known. Photothermographic materials have an image
forming layer in which a reducible silver salt (for example, an
organic silver salt), a photosensitive silver halide, and if
necessary, a toner for controlling the color tone of developed
silver images are dispersed in a binder.
[0007] Photothermographic materials form black silver images by
being heated to a high temperature (for example, 80.degree. C. or
higher) after imagewise exposure to cause an oxidation-reduction
reaction between a silver halide or a reducible silver salt
(functioning as an oxidizing agent) and a reducing agent. The
oxidation-reduction reaction is accelerated by the catalytic action
of a latent image on the silver halide generated by exposure. As a
result, a black silver image is formed in the exposed region.
Photothermographic materials have been described in many documents,
and the Fuji Medical Dry Imager FM-DPL is an example of a practical
medical image forming system using a photothermographic material
that has been marketed.
[0008] These photothermographic materials utilizing an organic
silver salt have a great characteristic of containing all
components necessary for image formation in the film in advance and
being capable of forming images only by heating. However, on the
other hand, there are many problems to be solved.
[0009] Photothermographic materials do not require the processing
solutions used in conventional wet processing in the case of silver
halide photosensitive materials, and have an advantage in that
processing can be carried out easily and rapidly. However, there
are still problems to be solved with respect to photothermographic
materials, which do not occur in conventional wet processing in the
case of silver halide photosensitive materials. One of them is the
problem of decolorization of dyes. Silver halide photosensitive
materials commonly incorporate dyes in order to provide a light
filter and prevent halation or irradiation therein. The added dyes
function during imagewise exposure. In the case where the dyes have
a spectral light absorption in the visible region, if the dyes
remain in a photosensitive material after performing their
function, the formed images may be colored by the dyes, and image
quality may be damaged. Therefore the residual dyes are preferably
removed from the photosensitive materials during the developing
process. In a wet developing process, the residual dyes can be
removed easily from the photosensitive materials by a processing
solution. On the other hand, in the case of the photothermographic
material, it is a significant task to remove the residual dyes.
[0010] More specifically, in order to attain images with a good
degree of sharpness, the incorporation of dyes is very important
for photothermographic materials exposed by a laser beam to provide
sufficient antihalation and anti-irradiation effects at the
wavelength used for the imagewise exposure. As for the wavelength
of a laser beam used for the exposure, a wide range of wavelength
regions such as the near infrared region, the infrared region, or
the visible region from red to blue can be applied.
[0011] For photothermographic materials exposed with either a near
infrared or an infrared laser beam, Japanese Patent Application
Laid-Open (JP-A) Nos. 9-146220 and 11-228698 disclose
photothermographic materials which practically require no color
bleaching mechanism therein due to use of a dye which has an
absorption maximum within the near infrared regions outside of
visual sensitivity, a narrow half band width, and little light
absorption within the visual region. All patents, patent
publications, and non-patent literature cited in this specification
are hereby expressly incorporated by reference herein.
[0012] For photothermographic materials which are subjected to
imagewise exposure with a laser beam having a wavelength within the
visible region of blue to red, it is preferable to incorporate some
kind of decoloring reaction mechanism.
[0013] A method for decoloring dyes by way of heating during a
thermal developing process has been proposed. For example, U.S.
Pat. No. 5,135,842 discloses a method for decoloring polymethine
dyes of a specific structure by heating. Moreover, U.S. Pat. Nos.
5,314,795, 5,324,627, and 5,384,237 disclose methods in which
polymethine dyes are decolorized by heating using a carbanion
generating agent.
[0014] However, the decoloring mechanisms described above often
bring about problems such as incomplete decoloring of dyes or dye
decolorization during storage of photothermographic materials due
to the insufficient stability of dye occurring after bleaching
ability has been enhanced. Especially, in photothermographic
materials used in medical diagnosis, high sharpness and preferable
image tone are required. Furthermore, demand has increased for
image forming methods used for processing photothermographic
materials rapidly at a higher speed within a short time.
Particularly in uses for medical treatment, there is a strong
desire for rapid diagnosis.
SUMMARY OF THE INVENTION
[0015] An aspect of the invention is to provide a
photothermographic material comprising, on at least one side of a
support, an image forming layer comprising at least a
photosensitive silver halide, a non-photosensitive organic silver
salt, a reducing agent, and a binder, wherein
[0016] (1) the binder comprises a polymer latex having a monomer
component represented by the following formula (M):
CH.sub.2.dbd.CR.sup.01--CR.sup.02.dbd.CH.sub.2 Formula (M)
[0017] wherein R.sup.01 and R.sup.02 each independently represent
one selected from a hydrogen atom, an alkyl group having 1 to 6
carbon atoms, a halogen atom, or a cyano group; and R.sup.01 and
R.sup.02 are not simultaneously a hydrogen atom;
[0018] (2) the photothermographic material comprises a compound
represented by the following formula (SA): ##STR3##
[0019] wherein M represents a hydrogen atom or a cation having a
valency of k; R represents a substituent; n represents an integer
of from 1 to 4; when n is 2 or more, a plurality of R may be the
same or different from one another; k represents an integer of 1 or
more; and when M is a hydrogen atom, k is 1; and
[0020] (3) the photothermographic material further comprises a
metal phthalocyanine dye represented by formula (PC-1):
##STR4##
[0021] wherein, M represents a metal atom; R.sup.1, R.sup.4,
R.sup.5, R.sup.8, R.sup.9, R.sup.12, R.sup.13, and R.sup.16 each
independently represent a hydrogen atom or a substituent; at least
one of R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9, R.sup.12,
R.sup.13, and R.sup.16 is an electron-attracting group; and
R.sup.2, R.sup.2, R.sup.3, R.sup.6, R.sup.7, R.sup.10, R.sup.11,
and R.sup.15 each independently represent a hydrogen atom or a
substituent.
DETAILED DESCRIPTION OF THE INVENTION
[0022] An object of the present invention is to provide a
photothermographic material which exhibits high sharpness,
preferable image tone, and excellent image storability.
[0023] The inventors aimed to realize a photothermographic material
that produces images with a high degree of sharpness and preferable
image tone and searched for a solution and means of improvement for
the causes of worsening of uneven image quality, and especially
uneven image tone. As a result, the inventors found that the
selection of a polymer binder having a specific structure, the use
of salicylic acid derivatives having a specific structure, and the
use of a metal phthalocyanine compound having a specific structure
is effective in improving image color tone, uneven image density,
and image stability with respect to light, whereby they arrived at
the present invention disclosed in claim 1. Further search for more
preferred constituent conditions led to the invention disclosed in
claim 2 to claim 8.
[0024] The present invention is especially effective for forming an
image by rapid thermal development processing in uses for the
medical field.
[0025] The present invention is explained below in detail.
[0026] The photothermographic material of the present invention
has, on at least one side of a support, an image forming layer
containing at least a photosensitive silver halide, a
non-photosensitive organic silver salt, a reducing agent, and a
binder. The photothermographic material may further have a
non-photosensitive layer such as a surface protective layer or an
intermediate layer between the image forming layer and the surface
protective layer, when necessary. The surface protective layer may
be a single layer or plural layers. Further, the photothermographic
material may have a back layer or a back surface protective layer
on the opposite side of the support from the image forming
layer.
[0027] (Binder for Image Forming Layer)
[0028] In the present invention, the binder of the image forming
layer contains a polymer latex having a monomer component
represented by the following formula (M).
CH.sub.2.dbd.CR.sup.01--CR.sup.02.dbd.CH.sub.2 Formula (M)
[0029] In the formula, R.sup.01 and R.sup.02 each independently
represent one selected from a hydrogen atom, an alkyl group having
1 to 6 carbon atoms, a halogen atom, or a cyano group. However,
R.sup.01 and R.sup.02 are not simultaneously a hydrogen atom.
[0030] As an alkyl group for R.sup.01 or R.sup.02, an alkyl group
having one to four carbon atoms is preferred, and more preferred is
an alkyl group having one or two carbon atoms. As a halogen atom
for R.sup.01 or R.sup.02, a fluorine atom, a chlorine atom, and a
bromine atom are preferred, and more preferred is a chlorine
atom.
[0031] Particularly preferably, one of R.sup.01 or R.sup.02 is a
hydrogen atom and the other is a methyl group or a chlorine atom.
More preferably, one of R.sup.01 or R.sup.02 is a hydrogen atom and
the other is a methyl group.
[0032] Specific examples of the monomer represented by formula (M)
of the present invention include 2-ethyl-1,3-butadiene,
2-n-propyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene,
2-methyl-1,3-butadiene, 2-chloro-1,3-butadiene,
1-bromo-1,3-butadiene, 2-fluoro-1,3-butadiene,
2,3-dichloro-1,3-butadiene, and 2-cyano-1,3-butadiene.
[0033] The binder of the present invention is a polymer obtained by
copolymerizing the monomer represented by formula (M), where the
copolymerization ratio of the monomer represented by formula (M)
for the polymer is in a range of from 10% by weight to 70% by
weight, preferably from 15% by weight to 65% by weight, and more
preferably from 20% by weight to 60% by weight. When the
copolymerization ratio of the monomer represented by formula (M) is
lower than 10% by weight, bonding component of the binder is
decreased and manufacturing-related brittleness is deteriorated.
When the copolymerization ratio of the monomer represented by
formula (M) exceeds 70% by weight, bonding component of the binder
is increased and mobility of the binder is increased, and as a
result, image storability is deteriorated.
[0034] In the invention, the other monomers, which are capable to
copolymerize with the monomer represented by formula (M), are not
particularly restricted, and any monomers may be preferably used
provided that they can polymerize by usual radical polymerization
or ion polymerization. As the monomer which can be used preferably,
it is capable to select the combination independently and freely
from the monomer groups (a) to (j) described below.
Monomer Groups (a) to (j)
[0035] (a) conjugated dienes: 1,3-butadiene, 1,3-pentadiene,
1-phenyl-1,3-butadiene, 1-.alpha.-naphthyl-1,3-butadiene,
1-.beta.-naphthyl-1,3-butadiene, 1'-bromo-1,3-butadiene,
1-chloro-1,3-butadiene, 1,1,2-trichloro-1,3-butadiene,
cyclopentadiene, and the like;
[0036] (b) olefins: ethylene, propylene, vinyl chloride, vinylidene
chloride, 6-hydroxy-1-hexene, 4-pentenoic acid, methyl 8-nonenate,
vinylsulfonic acid, trimethylvinylsilane, trimethoxyvinylsilane,
1,4-divinylcyclohexane, 1,2,5-trivinylcyclohexane, and the
like;
[0037] (c) .alpha.,.beta.-unsaturated carboxylic acid and salts
thereof: acrylic acid, methacrylic acid, itaconic acid, maleic
acid, sodium acrylate, ammonium methacrylate, potassium itaconate,
and the like;
[0038] (d) .alpha.,.beta.-unsaturated carboxylate esters: alkyl
acrylate (for example, methyl acrylate, ethyl acrylate, butyl
acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, dodecyl
acrylate, and the like), substituted alkyl acrylate (for example,
2-chloroethyl acrylate, benzyl acrylate, 2-cyanoethyl acrylate, and
the like), alkyl methacrylate (for example, methyl methacrylate,
butyl methacrylate, 2-ethylhexyl methacrylate, dodecyl
methacrylate, and the like), substituted alkyl methacrylate (for
example, 2-hydroxyethyl methacrylate, glycidyl methacrylate,
glycerine monomethacrylate, 2-acetoxyethyl methacrylate,
tetrahydrofurfulyl methacrylate, 2-methoxyethyl methacrylate,
polypropyleneglycol monomethacrylate (addition mole number of
polyoxypropylene=2 to 100), 3-N,N-dimethylaminopropyl methacrylate,
chloro-3-N,N,N-trimethylammoniopropyl methacrylate, 2-carboxyethyl
methacrylate, 3-sulfopropyl methacrylate, 4-oxysulfobutyl
methacrylate, 3-trimethoxysilylpropyl methacrylate, allyl
methacrylate, 2-isocyanatoethyl methacrylate, and the like),
derivatives of unsaturated dicarboxylic acid (for example,
monobutyl maleate, dimethyl maleate, monomethyl itaconate, dibutyl
itaconate, and the like), and polyfunctional esters (for example,
ethyleneglycol diacrylate, ethyleneglycol dimethacrylate,
1,4-cyclohexane diacrylate, pentaerythritol tetramethacrylate,
pentaerythritol triacrylate, trimethylolpropane triacrylate,
trimethylolethane triacrylate, dipentaerythritol pentamethacrylate,
pentaerythritol hexaacrylate, 1,2,4-cyclohexane tetramethacrylate,
and the like);
[0039] (e) amides of .beta.-unsaturated carboxylic acid: for
example, acrylamide, methacrylamide, N-methylacrylamide,
N,N-dimethylacrylamide, N-methyl-N-hydroxyethyl methacrylamide,
N-tert-butyl acrylamide, N-tert-octyl methacrylamide, N-cyclohexyl
acrylamide, N-phenyl acrylamide, N-(2-acetoacetoxyethyl)
acrylamide, N-acryloyl morpholine, diacetone acrylamide, diamide
itaconate, N-methyl maleimide, 2-acrylamide-methylpropanesulfonic
acid, methylenebis acrylamide, dimethacryloyl piperazine, and the
like;
[0040] (f) unsaturated nitriles: acrylonitrile, methacrylonitrile,
and the like;
[0041] (g) styrene and derivatives thereof: styrene, vinyltoluene,
p-tert-butylstyrene, vinylbenzoic acid, methyl vinylbenzoate,
.alpha.-methylstyrene, p-chloromethylstyrene, vinylnaphthalene,
p-hydroxymethylstyrene, sodium p-styrenesulfonate, potassium
p-styrenesulfinate, p-aminomethylstyrene, 1,4-divinylbenzene, and
the like;
[0042] (h) vinylethers: methylvinyl ether, butylvinyl ether,
methoxyethylvinyl ether, and the like;
[0043] (i) vinyl esters: vinyl acetate, vinyl propionate, vinyl
benzoate, vinyl salicylate, vinyl chloroacetate, and the like;
and
[0044] (j) other polymerizable monomers: N-vinylimidazole,
4-vinylpyridine, N-vinylpyrrolidone, 2-vinyloxazoline,
2-isopropenylozazoline, divinylsulfone, and the like.
[0045] Preferred examples of a polymer copolymerized with the
monomer represented by formula (M) of the present invention include
copolymers with styrene (for example, random copolymer, block
polymer, or the like), copolymers with styrene and butadiene (for
example, random copolymer, butadiene-isoprene-styrene block
copolymer, styrene-butadiene-isoprene-styrene block copolymer, or
the like), copolymers with ethylene and propylene, copolymers with
acrylonitrile, copolymers with isobutyrene, copolymers with acrylic
esters (for example, as acrylic ester, ethyl acrylate, butyl
acrylate, or the like can be used), and copolymers with acrylic
ester and acrylonitrile (the same acrylic esters as mentioned above
can be used). Among these, most preferred is a copolymer with
styrene.
[0046] In addition to the above components, the polymer of the
present invention is preferably further copolymerized with a
monomer having an acid group. As the acid group, preferred are a
carboxylic acid, a sulfonic acid, and a phosphoric acid. The
copolymerization ratio of a monomer having the acid group is
preferably from 1% by weight to 20% by weight, and more preferably
from 1% by weight to 10% by weight.
[0047] Examples of a monomer having the acid group include acrylic
acid, methacrylic acid, itaconic acid, p-styrene sulfonic acid
sodium salt, isopyrene sulfonic acid, phoshoryl ethyl methacrylate,
and the like.
[0048] Any kind of polymer may be used in combination with the
polymer obtained by copolymerizing the monomer represented by
formula (M) as the binder of the invention. Suitable as the
polymer, which can be used in combination, are those that are
transparent or translucent, and that are generally colorless, such
as natural resin or polymer and their copolymers; synthetic resin
or polymer and their copolymer; or media forming a film; for
example, included are gelatins, rubbers, poly(vinyl alcohols),
hydroxyethyl celluloses, cellulose acetates, cellulose acetate
butyrates, poly(vinyl pyrrolidones), casein, starch, poly(acrylic
acids), poly(methyl methacrylates), poly(vinyl chlorides),
poly(methacrylic acids), styrene-maleic anhydride copolymers,
styrene-acrylonitrile copolymers, styrene-butadiene copolymers,
poly(vinyl acetals) (e.g., poly(vinyl formal) or poly(vinyl
butyral)), polyesters, polyurethanes, phenoxy resin,
poly(vinylidene chlorides), polyepoxides, polycarbonates,
poly(vinyl acetates), polyolefins, cellulose esters, and
polyamides. A binder may be used with water, an organic solvent or
emulsion to form a coating solution.
[0049] The binder of the present invention preferably has a grass
transition temperature (Tg) in a range of from -30.degree. C. to
70.degree. C., more preferably, in a range of from -10.degree. C.
to 50.degree. C., and even more preferably in a range of from
0.degree. C. to 40.degree. C., considering manufacturing-related
brittleness and image storability. Two or more polymers can be
blended for the binder, and in this case, the blended polymer has a
weighed averaged Tg which preferably falls within the range above,
considering composition components. When the polymers exhibit phase
separation or has a core-shell structure, a weighed averaged Tg
preferably falls within the range above.
[0050] In the specification, Tg is calculated according to the
following equation. 1/Tg=.SIGMA.(Xi/Tgi)
[0051] Where, the polymer is obtained by copolymerization of n
monomer compounds (from i=1 to i=n); Xi represents the mass
fraction of the ith monomer (.SIGMA.Xi=1), and Tgi is the glass
transition temperature (absolute temperature) of the homopolymer
obtained with the ith monomer. The symbol .SIGMA. stands for the
summation from i=1 to i=n. Values for the glass transition
temperature (Tgi) of the homopolymers derived from each of the
monomers were obtained from J. Brandrup and E. H. Immergut, Polymer
Handbook (3rd Edition) (Wiley-Interscience, 1989).
[0052] The polymer used for the binder of the invention can be
readily obtained by a solution polymerizing method, a suspension
polymerizing method, an emulsion polymerizing method, a dispersion
polymerizing method, an anionic polymerizing method, a cationic
polymerizing method, or the like, however most preferable is an
emulsion polymerizing method by which polymer can be obtained as a
latex. For example, the polymer latex is obtained by emulsion
polymerization at about 30.degree. C. to 100.degree. C., preferably
at 60.degree. C. to 90.degree. C., for 3 hours to 24 hours with
stirring using water or a mixed solvent of water and a
water-miscible organic solvent (for example, methanol, ethanol,
acetone, or the like) as a dispersion medium, and using a monomer
mixture in an amount of 5% by weight to 150% by weight with respect
to the dispersion solvent, an emulsifying agent in an amount of
0.1% by weight to 20% by weight with respect to a total amount of
monomers, and a polymerization initiator. Conditions such as the
dispersion medium, monomer concentration, the amount of the
initiator, the amount of the emulsifying agent, the amount of the
dispersing agent, the reaction temperature, and the adding method
of the monomer may be appropriately determined considering the kind
of the monomer used. The dispersing agent is preferably used, if
necessary.
[0053] Emulsion polymerization is usually carried out according to
the following documents: "Gosei Jushi Emulsion (Synthetic Resin
Emulsion)" ed. by Taira Okuda and Hiroshi Inagaki, Polymer
Publishing Association (1978); "Gosei Latex no Oyo (Application of
Synthetic Latex)" ed. by Taka-aki Sugimura, Yasuo Kataoka, Soichi
Suzuki and Keiji Kasahara, Polymer Publishing Association (1993);
and "Gosei Latex no Kagaku (Chemistry of Synthetic Latex)" by
Soichi Muroi, Polymer Publishing Association (1970).
[0054] Emulsion polymerizing method for synthesizing the polymer
latex of the invention may be selected from an overall polymerizing
method, a monomer addition (continuous or divided) method, an
emulsion adding method and a seed polymerizing method. The overall
polymerizing method, monomer adding (continuous or divided) method,
and emulsion adding method are preferable in view of productivity
of the latex.
[0055] The polymerization initiator described above has radical
generation ability, and examples of them available include
inorganic peroxides such as persulfate salts and hydrogen peroxide,
peroxides described in the catalogue of organic peroxides by Nippon
Oil and Fat Co., and azo compounds described in azo polymerization
initiator catalogue by Wako Pure Chemical Industries, Ltd. Among
them, water-soluble peroxides such as persulfate, and water-soluble
azo compounds described in azo polymerization initiator catalogue
by Wako Pure Chemical Industries, Ltd., are preferable. Ammonium
persulfate, sodium persulfate, potassium persulfate,
azobis(2-methylpropionamidine)hydrochloride,
azobis(2-methyl-N-(2-hydroxyethyl)propionamide and
azobiscyanovaleric acid are more preferable, and particularly,
peroxides such as ammonium persulfate, sodium persulfate and
potassium persulfate are preferable from the viewpoint of image
storability, solubility, and cost.
[0056] The addition amount of the polymerization initiator
described above is preferably in a range of from 0.3% by weight to
2.0% by weight, more preferably from 0.4% by weight to 1.75% by
weight, and particularly preferably from 0.5% by weight to 1.5% by
weight, based on a total amount of monomers. Image storability
decreases when the amount of the polymerization initiator is less
than 0.3% by weight, while the latex tends to be aggregated to
deteriorate coating ability when the amount of the polymerization
initiator exceeds 2.0% by weight.
[0057] As the polymerization emulsifying agent mentioned above, any
surfactants such as an anionic surfactant, a nonionic surfactant, a
cationic surfactant, or an amphoteric surfactant can be employed.
An anionic surfactant is preferably employed from the viewpoint of
dispersibility and image storability, and more preferred is a
sulfonic acid-type anionic surfactant which maintains the
polymerization stability even in a small amount and has a
hydrolysis resistance. Preferred is a long chain alkyl
diphenylether disulfonate such as "PELEX SS-H" (trade name,
available from Kao Co., Ltd.), and particularly preferred is a low
electrolyte-type surfactant such as "PIONIN A-43-S" (trade name,
available from Takemoto Oil & Fat Co., Ltd.).
[0058] As the polymerization emulsifying agent mentioned above, a
sulfonic acid-type surfactant is preferably used in a range of from
0.1% by weight to 10.0% by weight, based on a total amount of
monomers, more preferably from 0.2% by weight to 7.5% by weight,
and particularly preferably from 0.3% by weight to 5.0% by weight.
Stability in the emulsion polymerization process can not secure
when the addition amount of the polymerization emulsifying agent is
less than 0.1% by weight, while image storability decreases when
the addition amount exceeds 10.0% by weight.
[0059] Chelating agents are preferably used for the synthesis of
the polymer latex used in the invention. The chelating agent is a
compound capable of coordinating multi-valent metal ions such as
iron ion, and alkali earth metal ions such as calcium ion, and
examples thereof include the compounds described in Japanese Patent
Application Publication (JP-B) No. 6-8956; U.S. Pat. No. 5,053,322;
and JP-A Nos. 4-73645, 4-127145, 4-247073, 4-305572, 6-11805,
5-173312, 5-66527, 5-158195, 6-118580, 6-110168, 6-161054,
6-175299, 6-214352, 7-114161, 7-114154, 7-120894, 7-199433,
7-306504, 9-43792, 8-314090, 10-182571, 10-182570, and
11-190892.
[0060] The chelating agent used in the invention is preferably an
inorganic chelating compound (sodium tripolyphosphate, sodium
hexametaphosphate, sodium tetrapolyphosphate, or the like), an
aminopolycarboxylic acid chelating compound (nitrilotriacetic acid,
ethylenediamine tetraacetic acid, or the like), an organic
phosphonic acid chelating agent (compounds described in Research
Disclosure No. 18170, JP-A Nos. 52-102726; 53-42730, 56-97347,
54-121127, 55-4024, 55-4025, 55-29883, 55-126241, 55-65955,
55-65956, 57-179843, and 54-61125; and West Germany Patent (WGP)
No. 1045373), a polyphenol chelating agent, or a polyamine
chelating agent. An aminopolycarboxylic acid derivative is
particularly preferable.
[0061] Preferable examples of the aminopolycarboxylic acid
derivative are described in the supplement table of "EDTA
(-Chemistry of Complexane-)", Nankodo 1977. A part of the carboxyl
group of these compounds may be substituted by a salt of alkali
metal such as sodium or potassium, or an ammonium salt.
Particularly preferable aminocarboxylic acid derivatives include
iminodiacetic acid, N-methyliminodiacetic acid,
N-(2-aminoethyl)iminodiacetic acid, N-(carbamoylethyl)iminodiacetic
acid, nitrilotriacetic acid, ehylenediamine-N,N'-diacetic acid,
ehylenediamine-N,N'-di-.alpha.-propionic acid,
ethylenediamine-N,N'-di-.beta.-propionic acid,
N,N'-ethylene-bis(.alpha.-o-hydroxyphenyl)glycine,
N,N'-di(2-hydroxybenzyl)ethylenediamine-N,N'-diacetic acid,
ethylenediamine-N,N'-diacetic acid-N,N'-diacetohydroxamic acid,
N-hydroxyethylethylenediamine-N,N',N'-triacetic acid,
ethylenediamine-N,N,N',N'-tetraacetic acid,
1,2-propylenediamine-N,N,N',N'-tetraacetic acid,
d,1-2,3-diaminobutane-N,N,N',N'-tetraacetic acid,
meso-2,3-diaminobutane-N,N,N',N'-tetraacetic acid,
1-phenylethylenediamine-N,N,N',N'-tetraacetic acid,
d,1-1,2-diphenylethylenediamine-N,N,N',N'-tetraacetic acid,
1,4-diaminobutane-N,N,N',N'-tetraacetic acid,
trans-cyclobutane-1,2-diamine-N,N,N',N'-tetraacetic acid,
trans-cyclopentane-1,2-diamine-N,N,N',N'-tetraacetic acid,
trans-cyclohexane-1,2-diamine-N,N,N',N'-tetraacetic acid,
cic-cyclohexane-1,2-diamine-N,N,N',N'-tetraacetic acid,
cyclohexane-1,3-diamine-N,N,N',N'-tetraacetic acid,
cyclohexane-1,4-diamine-N,N,N',N'-tetraacetic acid,
o-phenylenediamine-N,N,N', N'-tetraacetic acid,
trans-1,4-diaminobutene-N,N',N',N'-tetraacetic acid,
trans-1,4-diaminobutene-N,N,N',N'-tetraacetic acid,
.alpha.,.alpha.'-diamino-o-xylene-N,N,N',N'-tetraacetic acid,
2-hydroxy-1,3-propanediamine-N,N,N',N'-tetraacetic acid,
2,2-oxy-bis(ethyliminodiacetic acid),
2,2'-ethylenedioxy-bis(ethyliminodiacetic acid),
ethylenediamine-N,N'-diacetic acid-N,N'-di-.beta.-propionic acid,
ethylenediamine-N,N'-diacetic acid-N,N'-di-.beta.-propionic acid,
ethylenediamine-N,N,N',N'-tetrapropionic acid,
diethylenetriamine-N,N,N',N'',N''-pentaacetic acid,
triethylenetetramine-N,N,N',N'',N''',N'''-hexaacetic acid, and
1,2,3-triaminopropane-N,N,N',N'',N''',N'''-hexaacetic acid. A part
of the carboxylic group of these compounds may be substituted by a
salt of alkali metal such as sodium or potassium, or an ammonium
salt.
[0062] The addition amount of the chelating agent described above
is preferable from 0.01% by weight to 0.4% by weight, more
preferably from 0.02% by weight to 0.3% by weight, and particularly
preferably from 0.03% by weight to 0.15% by weight, based on a
total amount of monomers. When the amount of the chelating agent is
less than 0.01% by weight, metal ions contaminated in the
production process of the polymer latex are insufficiently trapped
to decrease stability of the latex against aggregation to
deteriorate coating ability. When the amount exceeds 0.4% by
weight, the viscosity of the latex increases to deteriorate coating
ability.
[0063] The chain transfer agent is preferably used in the synthesis
of the polymer latex used in the invention. A gelling ratio can be
controlled by the addition of the chain transfer agent. The
compounds described in Polymer Handbook Third Edition
(Wiley-Interscience, 1989) are preferable as the chain transfer
agents. Sulfur compounds are preferable since they have high chain
transfer ability to make the amount of use of the reagent small.
Particularly preferable chain reaction agents are hydrophobic
mercaptan chain transfer agents such as tert-dodecylmercaptan,
n-dodecylmercaptan, and the like.
[0064] The amount of the chain transfer agent described above is
preferably from 0.2% by weight to 2.0% by weight, more preferably
from 0.3% by weight to 1.8% by weight, and particularly preferably
from 0.4% by weight to 1.6% by weight, based on a total amount of
monomers. Manufacturing-related brittleness is decreased when the
amount of the chain transfer agent is less than 0.2% by weight,
while image storability is deteriorated when the amount exceeds
2.0% by weight.
[0065] In the emulsion polymerization, additives such as an
electrolyte, a stabilizer, a viscosity increasing agent, an
antifoaming agent, an antioxidant, a vulcanizing agent, an
antifreeze agent, a gelling agent, vulcanization accelerator, or
the like described in Synthetic Rubber Handbook and the like may be
used in addition to the compounds above.
[0066] <Specific Examples of Polymer>
[0067] Specific examples of the polymer used in the present
invention are listed below (compound Nos. P-1 to P-29), however the
invention is not restricted to these. x, y, z, and z' in chemical
formula show the mass ratios in the polymer composition, and the
sum of x, y, z, and z' is equal to 100%. Tg represents the glass
transition temperature of a dry film obtained from the polymer.
##STR5## ##STR6## ##STR7## ##STR8## ##STR9## ##STR10##
[0068] While examples of synthesis of the polymers used in the
invention are shown below, the invention is not restricted to the
synthetic methods shown below. Similar synthetic method may be used
for other compounds in the examples.
[0069] <Synthetic Example 1: Synthesis of Illustrated Compound
No. P-1>
[0070] Into the polymerization vessel of gas monomer reaction
apparatus (type TAS-2J, manufactured by Taiatsu Techno Corp.), 1500
g of distilled water were poured and heated for 3 hours at
90.degree. C. to make passive film over the stainless-steel vessel
surface and stainless-steel stirring device. Into the
polymerization vessel after this treatment were added 584.86 g of
distilled water which was bubbled with nitrogen gas for 1 hour,
9.45 g of a surfactant (PIONIN A-43-S produced by Takemoto Oil and
Fats Cp.), 20.25 g of 1 mol/L sodium hydroxide, 0.216 g of
ethylenediamine tetraacetic acid tetrasodium salt, 332.1 g of
styrene, 191.7 g of isoprene, 16.2 g of acrylic acid, and 4.32 g of
tert-dodecyl mercaptan. And then the reaction vessel was sealed the
mixture was stirred at 225 rpm, followed by elevating the inner
temperature to 60.degree. C. To the aforementioned mixture was
added a solution prepared through dissolving 2.7 g of ammonium
persulfate in 50 mL of water, and kept for 7 hours with stirring.
Furthermore, the mixture was heated to 90.degree. C. with stirring
for 3 hours. After the reaction was completed, the inner
temperature of the reaction vessel was cooled to room temperature.
The polymer obtained was filtered through a filter cloth (mesh:
225), then 1145 g of the example compound No. P-1 (solid content of
45% by weight, mean particle diameter of 112 nm) was obtained.
[0071] <Synthetic Example 2: Synthesis of Compound No.
P-2>
[0072] Into the reaction vessel of gas monomer reaction apparatus
(type TAS-2J manufactured by Tiatsu Garasu Kogyo Ltd.) pretreated
to make passive film similar to the above-described Synthetic
Example 1, 350.92 g of distilled water which was bubbled with
nitrogen gas for 1 hour, 3.78 g of the surfactant (PIONIN A-43-S
produced by Takemoto Oil and Fats Cp.), 20.25 g of 1 mol/L sodium
hydroxide, 0.216 g of ethylenediamine tetraacetic acid tetrasodium
salt, 34.02 g of styrene, 18.36 g of isoprene, 1.62 g of acrylic
acid, and 2.16 g of tert-dodecyl mercaptan were added. Thereafter,
the reaction vessel was sealed and the mixture was stirred at 225
rpm, followed by elevating the inner temperature to 65.degree. C.
To this mixture was added a solution prepared through dissolving
1.35 g of ammonium persulfate in 50 mL of water and kept for 2
hours with stirring. An emulsion was separately prepared by adding,
with stirring, 233.94 g of distilled water, 5.67 g of the
surfactant (PIONIN A-43-S produced by Takemoto Oil and Fats Cp.),
306.18 g of styrene, 165.24 g of isoprene, 14.58 g of acrylic acid,
2.16 g of tert-dodecyl mercaptan, and 1.35 g of ammonium
persulfate. The emulsion was poured dropwise over 8 hours into the
reaction vessel described above. The reaction solution was further
stirred for 2 hours after completing the addition. Thereafter the
resulting mixture was further stirred for 3 hours by elevating the
temperature at 90.degree. C. After the reaction was completed, the
inner temperature of the reaction vessel was cooled to room
temperature. The polymers obtained was filtered through a filter
cloth (mesh: 225), then 1147 g of the example compound No. P-2
(solid content of 45% by weight, mean particle diameter of 121 nm)
was obtained.
[0073] <Synthetic Example 3: Synthesis of Compound No.
P-4>
[0074] Into the reaction vessel of gas monomer reaction apparatus
(type TAS-2J manufactured by Tiatsu Garasu Kogyo Ltd.) pretreated
to make passive film similar to the above-described Synthetic
example 1, 578.11 g of distilled water which was bubbled with
nitrogen gas for one hour, 16.2 g of the surfactant (PELEX SS-H
produced by Kao Co., Ltd.), 20.25 g of 1 mol/L sodium hydroxide,
0.216 g of ethylenediamine tetraacetic acid tetrasodium salt, 321.3
g of styrene, 202.5 g of isoprene, 1.62 g of acrylic acid, and 4.32
g of tert-dodecyl mercaptan were added. Thereafter the reaction
vessel was sealed and the mixture was stirred at the stirring rate
of 225 rpm, followed by elevating the inner temperature to
60.degree. C. To the mixture was added a solution prepared through
dissolving 2.7 g of ammonium persulfate in 25 mL of water, and kept
for 5 hours with stirring. Furthermore a solution obtained
dissolving 1.35 g of ammonium persulfate dissolved in 25 mL of
water was added to the mixture. Then the mixture was heated to
90.degree. C. and stirred for 3 hours. After the reaction was
completed, the inner temperature of the vessel was cooled to room
temperature. The polymers obtained was filtered through filter
cloth (mesh: 225), then 1139 g of the example compound No. P-4
(solid content of 45% by weight, mean particle diameter of 105 nm)
was obtained.
[0075] In the present invention, for the solvent of a coating
solution for the polymer latex, aqueous solvent can be used and any
of water-miscible organic solvents may be used in combination.
[0076] As water-miscible organic solvents, there can be used, for
example, alcohols such as methyl alcohol, ethyl alcohol, propyl
alcohol, or the like; cellosolves such as methyl cellosolve, ethyl
cellosolve, butyl cellosolve, and the like; ethyl acetate,
dimethylformamide, or the like.
[0077] The addition amount of the organic solvent is preferably 50%
by weight or less, and more preferably 30% by weight or less, with
respect to the solvent.
[0078] Concerning the polymer latex of the present invention, the
concentration of the polymer is preferably from 10% by weight to
70% by weight, more preferably from 20% by weight to 60% by weight,
and particularly preferably from 30% by weight to 55% by weight,
with respect to the latex liquid in each case.
[0079] Concerning the binder polymer of the present invention, the
equilibrium water content under 25.degree. C. and 60% RH is
preferably 2% by weight or lower, more preferably, in a range of
from 0.01% by weight to 1.5% by weight, and even more preferably,
from 0.02% by weight to 1.0% by weight.
[0080] The term "equilibrium water content under 25.degree. C. and
60% RH" as referred herein can be expressed as follows: Equilibrium
water content under 25.degree. C. and 60% RH=[(W1-W0)/W0].times.100
(% by weight)
[0081] wherein W1 is the weight of the polymer in
moisture-controlled equilibrium under the atmosphere of 25.degree.
C. and 60% RH, and W0 is the absolutely dried weight at 25.degree.
C. of the polymer.
[0082] For the definition and the method of measurement for water
content, reference can be made to Polymer Engineering Series 14,
"Testing methods for polymeric materials" (The Society of Polymer
Science, Japan, published by Chijin Shokan).
[0083] In the present invention, polymers capable of being
dispersed in an aqueous solvent are particularly preferable.
Examples of dispersed states may include a latex, in which
water-insoluble fine particles of hydrophobic polymer are
dispersed, or such in which polymer molecules are dispersed in
molecular states or by forming micelles, but preferred are
latex-dispersed particles. A mean particle diameter of the
latex-dispersed particles is in a range from 1 nm to 50000 nm,
preferably from 5 nm to 1000 nm, more preferably from 10 nm to 500
nm, and even more preferably from 50 nm to 200 nm. There is no
particular limitation concerning particle diameter distribution of
the dispersed particles, and they may be widely distributed or may
exhibit a monodisperse particle diameter distribution. From the
viewpoint of controlling physical properties of the coating
solution, preferred mode of usage includes mixing two or more types
of particles each having monodisperse particle diameter
distribution.
[0084] In the image forming layer of the present invention, if
necessary, there can be added hydrophilic polymers such as gelatin,
poly(vinyl alcohol), methyl cellulose, hydroxypropyl cellulose,
carboxymethyl cellulose, or the like. The hydrophilic polymers
above are added in an amount of 30% by weight or less, preferably
20% by weight or less, with respect to the total weight of the
binder incorporated in the image forming layer.
[0085] The image forming layer of the present invention is
preferably formed by using the polymer latex of the present
invention. Concerning the amount of the binder for the image
forming layer, the mass ratio of total binder relative to organic
silver salt (total binder/organic silver salt) is preferably in a
range of from 1/10 to 10/1, more preferably from 1/3 to 5/1, and
even more preferably from 1/1 to 3/1.
[0086] A mass ratio of total binder relative to photosensitive
silver halide (total binder/photosensitive silver halide) is
preferably in a range of from 5 to 400, and more preferably from 10
to 200.
[0087] The total amount of binder in the image forming layer of the
invention is preferably in a range of from 0.2 g/m.sup.2 to 30
g/m.sup.2, more preferably from 1 g/m.sup.2 to 15 g/m.sup.2, and
even more preferably from 2 g/m.sup.2 to 10 g/m.sup.2. Concerning
the image forming layer of the invention, there may be added a
crosslinking agent for crosslinking, a surfactant to improve
coating ability, or the like.
[0088] (Compound Represented by Formula (SA))
[0089] The compound represented by formula (SA), which is used in
the present invention, is explained in detail. ##STR11##
[0090] In formula (SA), M represents a hydrogen atom or an anion
having a valency of k (for example, a metal ion such as sodium ion,
potassium ion, calcium ion, barium ion, or zinc ion; an ammonium
ion such as tetramethyl ammonium ion or tetrabutyl ammonium ion; or
the like). k is an integer of one or more, like as the illustrated
ion shows, and it is usually one or two. When M is a hydrogen atom,
k is one. M is preferably a heavy metal ion and specifically zinc,
iron, manganese, cadmium, chromium, cobalt, rhutenium, rhodium,
silver, or the like.
[0091] In formula (SA), R represents a substituent, for example,
linear, branched, or heterocyclic alkyl group (preferably, having 1
to 20 carbon atoms, more preferably, having 1 to 12 carbon atoms,
and particularly preferably, having 1 to 8 carbon atoms; for
example, methyl, ethyl, iso-propyl, t-butyl, n-octyl,
1,1,3,3-tetramethylbutyl, t-amyl, cyclohexyl, and the like are
described), an alkenyl group (preferably, having 2 to 20 carbon
atoms, more preferably, having 2 to 12 carbon atoms, and
particularly preferably, having 2 to 8 carbon atoms; for example,
vinyl, allyl, 2-butenyl, 3-pentenyl, and the like are described),
an alkynyl group (preferably, having 2 to 20 carbon atoms, more
preferably, having 2 to 12 carbon atoms, and particularly
preferably, having 2 to 8 carbon atoms; for example, propargyl,
3-pentynyl, and the like are described), an aralkyl group
(preferably, having 7 to 30 carbon atoms, more preferably, having 7
to 20 carbon atoms, and particularly preferably, having 7 to 16
carbon atoms; for example, benzyl, .alpha.-methylbenzyl,
.alpha.-ethylbenzyl, diphenylmethyl, naphthylmethyl,
naphthylphenylmethyl, and the like are described), an aryl group
(preferably, having 6 to 30 carbon atoms, more preferably, having 6
to 20 carbon atoms, particularly preferably, having 6 to 12 carbon
atoms; for example, phenyl, p-methylphenyl, naphthyl, and the like
are described), an amino group (preferably, having 0 to 20 carbon
atoms, more preferably, having 0 to 10 carbon atoms, even more
preferably, having 0 to 6 carbon atoms; for example, amino,
methylamino, dimethylamino, diethylamino, dibenzylamino, and the
like are described), an alkoxy group (preferably, having 1 to 20
carbon atoms, more preferably, having 1 to 12 carbon atoms,
particularly preferably, having 1 to 8 carbon atoms; for example,
methoxy, ethoxy, butoxy, and the like are described), an aryloxy
group (preferably, having 6 to 20 carbon atoms, more preferably,
having 6 to 16 carbon atoms, and particularly preferably, having 6
to 12 carbon atoms; for example, phenyloxy, 2-naphthyloxy, and the
like are described), an acyl group (preferably, having 1 to 20
carbon atoms, more preferably, having 1 to 16 carbon atoms, and
particularly preferably, having 1 to 12 carbon atoms; for example,
acetyl, benzoyl, formyl, pivaloyl, and the like are described), an
alkoxycarbonyl group (preferably, having 2 to 20 carbon atoms, more
preferably, having 2 to 16 carbon atoms, and particularly
preferably, having 2 to 12 carbon atoms; for example,
methoxycarbonyl, ethoxycarbonyl, and the like are described), an
aryloxycarbonyl group (preferably, having 7 to 20 carbon atoms,
more preferably, having 7 to 16 carbon atoms, and particularly
preferably, having 7 to 10 carbon atoms; for example,
phenoxycarbonyl and the like are described), an acyloxy group
(preferably, having 1 to 20 carbon atoms, more preferably, having 2
to 16 carbon atoms, and particularly preferably, having 2 to 10
carbon atoms; for example, acetoxy, benzoyloxy, and the like are
described), an acylamino group (preferably, having 1 to 20 carbon
atoms, more preferably, having 2 to 16 carbon atoms, and
particularly preferably, having 2 to 10 carbon atoms; for example,
acetylamino, benzoylamino, and the like are described), an
alkoxycarbonylamino group (preferably, having 2 to 20 carbon atoms,
more preferably, having 2 to 16 carbon atoms, and particularly
preferably, having 2 to 12 carbon atoms; for example,
methoxycarbonylamino and the like are described), an
aryloxycarbonylamino group (preferably, having 7 to 20 carbon
atoms, more preferably, having 7 to 16 carbon atoms, and
particularly preferably, having 7 to 12 carbon atoms; for example,
phenyloxycarbonylamino and the like are described), a sulfonylamino
group (preferably, having 1 to 20 carbon atoms, more preferably,
having 1 to 16 carbon atoms, and particularly preferably, having 1
to 12 carbon atoms; for example, methanesulfonylamino,
benzenesulfonylamino, and the like are described), a sulfamoyl
group (preferably, having 0 to 20 carbon atoms, more preferably,
having 0 to 16 carbon atoms, and particularly preferably, having 0
to 12 carbon atoms; for example, sulfamoyl, methylsulfamoyl,
dimethylsulfamoyl, phenylsulfamoyl, and the like are described), a
carbamoyl group (preferably, having 0 to 20 carbon atoms, more
preferably, having 0 to 16 carbon atoms, and particularly
preferably, having 0 to 12 carbon atoms; for example, carbamoyl,
diethylcarbamoyl, phenylcarbamoyl, and the like are described), a
ureido group (preferably, having 1 to 20 carbon atoms, more
preferably, having 1 to 16 carbon atoms, and particularly
preferably, having 1 to 12 carbon atoms; for example, ureido,
methylureido, phenylureido, and the like are described), an
alkylthio group (preferably, having 1 to 20 carbon atoms, more
preferably, having 1 to 16 carbon atoms, and particularly
preferably, having 1 to 12 carbon atoms; for example, methylthio,
ethylthio, and the like are described), an arylthio group
(preferably, having 6 to 20 carbon atoms, more preferably, having 6
to 16 carbon atoms, and particularly preferably, having 6 to 12
carbon atoms; for example, phenylthio and the like are described),
a sulfony group (preferably, having 1 to 20 carbon atoms, more
preferably, having 1 to 16 carbon atoms, and particularly
preferably, having 1 to 12 carbon atoms; for example, mesyl, tosyl,
and the like are described), a sulfinyl group (preferably, having 1
to 20 carbon atoms, more preferably, having 1 to 16 carbon atoms,
and particularly preferably, having 1 to 12 carbon atoms; for
example, methanesulfinyl, benzenesulfinyl, and the like are
described), amide phosphate group (preferably, having 1 to 20
carbon atoms, more preferably, having 1 to 16 carbon atoms, and
particularly preferably, having 1 to 12 carbon atoms; for example,
diethyl amide phosphate, phenyl amide phosphate, and the like are
described), a hydroxy group, a mercapto group, a halogen atom (for
example, a fluorine atom, a chlorine atom, a bromine atom, or an
iodine atom), a cyano group, a sulfo group, a carboxy group, a
nitro group, a hydroxamic group, a sulfino group, a hydrazino
group, a sulfonylthio group, a thiosulfonyl group, a heterocyclic
group (for example, imidazolyl, pyridyl, furyl, piperidyl,
morpholyl, and the like are described), a disulfide group, and the
like are described.
[0092] These substituents may be further substituted and may form
salts when these groups are possible to form salts. n represents a
integer from 1 to 4, however when there are two or more
substituents, namely n is 2 or more, these may be the same or
different. n is preferably 1, 2, or 3, and most preferably, 2.
[0093] Further, these substituents may bond to each other to form a
5- to 7-membered aromatic or non-aromatic carbon ring (for example,
a benzene ring). Furthermore, this ring may be substituted by
another substituent (for example, a halogen atom or a carboxy
group).
[0094] The substituent represented by R is preferably an alkyl
group, an alkenyl group, an alkynyl group, an aralkyl group, an
aryl group, an amino group, an alkoxy group, an acyl group, an
alkoxycarbonyl group, an acyloxy group, an acylamino group, an
alkoxycarbonylamino group, a sulfonylamino group, a sulfamoyl
group, a carbamoyl group, a ureido group, an alkylthio group, a
sulfonyl group, a hydroxy group, a mercapto group, a halogen atom,
a cyano group, a sulfo group, a carboxy group, a nitro group, a
heterocyclic group, and more preferably an alkyl group, an alkenyl
group, an aralkyl group, an amino group, an alkoxy group, an
alkylthio group, a hydroxy group, a mercapto group, a halogen atom,
a sulfo group, or a carboxy group.
[0095] Furthermore, in formula (SA), it is particularly preferable
that an alkyl group (including an aralkyl group) substitutes at an
ortho-position and/or a para-position of the hydroxy group.
[0096] Further preferably, the compound of formula (SA) has a
bisphenol structure which is bonded through one carbon atom.
[0097] Next, specific examples of the compound represented by
formula (SA) of the present invention are shown below, however the
present invention is not limited in these. ##STR12## ##STR13##
##STR14## ##STR15## ##STR16## ##STR17## ##STR18## ##STR19##
##STR20##
[0098] As the compound represented by formula (SA) of the present
invention, commercially avaivable compound may be used. The
compound represented by formula (SA) of the present invention can
be easily synthesized, for example, by the method described in JP-A
No. 251838, by an acid-catalyzed condensation reaction with
salicylic acid and carbonyl compound described in J. Med. Chem.,
vol. 34, page 342 (1991) and the like.
[0099] The compound of formula (SA) in the present invention can be
used by dissolving it in water or a suitable organic solvent, for
example, alcohols (methanol, ethanol, propanol, or fluoroalcohol),
ketones (acetone or methylethyl ketone), dimethylformamide,
dimethylsufoxide, methylcellusolve, or the like.
[0100] Further, the compound can be used in the form of an
emulsified dispersion or a solid fine particle dispersion. As well
known emulsified dispersing method, there can be mentioned a method
comprising dissolving the compound in an oil such as
dibutylphthalate, tricresylphosphate, glyceryl triacetate,
diethylphthalate, or the like, and an auxiliary solvent such as
ethyl acetate, cyclohexanone, or the like; from which an emulsified
dispersion is mechanically produced. As well-known solid dispersing
method, there can be mentioned a method comprising dispersing the
powder of the compound in water by means of a ball mill, a colloid
mill, a sand grinder mill, a manton-gorlin mill, a micro fluidizer,
or an ultrasonics, thereby obtaining solid dispersion.
[0101] The compound of formula (SA) of the present invention may be
added to any layer which is disposed on the same side of the
support as image forming layer, namely the image forming layer or
any other layer of this layer side, but it is preferable to add the
compound to the image forming layer or the layer adjacent to the
image forming layer.
[0102] The addition amount of the compound represented by formula
(SA), which is showed by molar quantity per 1 mol of coated silver
(mol/mol Ag), is preferably from 1.times.10.sup.-5 mol/mol Ag to
5.times.10.sup.-1 mol/mol Ag, more preferably from
5.times.10.sup.-5 mol/mol Ag to 1.times.10.sup.-1 mol/mol Ag, and
even more preferably from 1.times.10.sup.-4 mol/mol Ag to 5.times.1
0-2 mol/mol Ag. The compound may be used alone or two or more of
them may be used in combination.
[0103] (Non-Photosensitive Organic Silver Salt)
[0104] 1) Composition
[0105] The organic silver salt which can be used in the present
invention is relatively stable to light but serves as to supply
silver ions and forms silver images when heated to 80.degree. C. or
higher in the presence of an exposed photosensitive silver halide
and a reducing agent. The organic silver salt may be any material
containing a source supplying silver ions that are reducible by a
reducing agent. Such a non-photosensitive organic silver salt is
disclosed, for example, in JP-A No. 10--62899 (paragraph Nos. 0048
to 0049), European Patent (EP) No. 0803764A1 (page 18, line 24 to
page 19, line 37), EP No. 0962812A1, JP-A Nos. 11-349591,
2000-7683, and 2000-72711, and the like. A silver salt of an
organic acid, particularly, a silver salt of a long chained
aliphatic carboxylic acid (having 10 to 30 carbon atoms, and
preferably having 15 to 28 carbon atoms) is preferable. Preferred
examples of the silver salt of a fatty acid can include, for
example, silver lignocerate, silver behenate, silver arachidinate,
silver stearate, silver oleate, silver laurate, silver capronate,
silver myristate, silver palmitate, silver erucate, and mixtures
thereof. In the invention, among these silver salts of a fatty
acid, it is preferred to use a silver salt of a fatty acid with a
silver behenate content of 50 mol % or higher, more preferably, 85
mol % or higher, and even more preferably, 95 mol % or higher.
Further, it is preferred to use a silver salt of a fatty acid with
a silver erucate content of 2 mol % or lower, more preferably, 1
mol % or lower, and even more preferably, 0.1 mol % or lower.
[0106] It is preferred that the content of silver stearate is 1 mol
% or lower. When the content of silver stearate is 1 mol % or
lower, a silver salt of an organic acid having low fog, high
sensitivity and excellent image storability can be obtained. The
above-mentioned content of silver stearate is preferably 0.5 mol %
or lower, and particularly preferably, silver stearate is not
substantially contained.
[0107] Further, in the case where the silver salt of an organic
acid includes silver arachidinate, it is preferred that the content
of silver arachidinate is 6 mol % or lower in order to obtain a
silver salt of an organic acid having low fog and excellent image
storability. The content of silver arachidinate is more preferably
3 mol % or lower.
[0108] 2) Shape
[0109] There is no particular restriction on the shape of the
organic silver salt usable in the invention and it may be
needle-like, bar-like, tabular, or flake shaped.
[0110] In the invention, a flake shaped organic silver salt is
preferred. Short needle-like, rectangular, cuboidal, or potato-like
indefinite shaped particles with the major axis to minor axis ratio
being lower than 5 are also used preferably. Such organic silver
salt particles suffer less from fogging during thermal development
compared with long needle-like particles with the major axis to
minor axis length ratio of 5 or higher. Particularly, a particle
with the major axis to minor axis ratio of 3 or lower is preferred
since it can improve the mechanical stability of the coating film.
In the present specification, the flake shaped organic silver salt
is defined as described below. When an organic silver salt is
observed under an electron microscope, calculation is made while
approximating the shape of an organic silver salt particle to a
rectangular body and assuming each side of the rectangular body as
a, b, c from the shorter side (c may be identical with b) and
determining x based on numerical values a, b for the shorter side
as below. x=b/a
[0111] As described above, x is determined for the particles by the
number of about 200 and those capable of satisfying the relation: x
(average).gtoreq.=1.5 as an average value x is defined as a flake
shape. The relation is preferably: 30.gtoreq.x (average).gtoreq.1.5
and, more preferably, 15.gtoreq.x (average).gtoreq.1.5. By the way,
needle-like is expressed as 1.ltoreq.x (average)<1.5.
[0112] In the flake shaped particle, a can be regarded as a
thickness of a tabular particle having a major plane with b and c
being as the sides. a in average is preferably from 0.01 .mu.m to
0.3 .mu.m and, more preferably, from 0.1 .mu.m to 0.23 .mu.m. c/b
in average is preferably from 1 to 9, more preferably from 1 to 6,
even more preferably from 1 to 4 and, most preferably from 1 to
3.
[0113] By controlling the equivalent spherical diameter being from
0.05 .mu.m to 1 .mu.m, it causes less agglomeration in the
photothermographic material and image storability is improved. The
equivalent spherical diameter is preferably from 0.1 .mu.m to 1
.mu.m. In the invention, an equivalent spherical diameter can be
measured by a method of photographing a sample directly by using an
electron microscope and then image processing the negative
images.
[0114] In the flake shaped particle, the equivalent spherical
diameter of the particle/a is defined as an aspect ratio. The
aspect ratio of the flake particle is preferably from 1.1 to 30
and, more preferably, from 1.1 to 15 with a viewpoint of causing
less agglomeration in the photothermographic material and improving
image storability.
[0115] As the particle size distribution of the organic silver
salt, monodispersion is preferred. In the monodispersion, the
percentage for the value obtained by dividing the standard
deviation for the length of minor axis and major axis by the minor
axis and the major axis respectively is, preferably, 100% or less,
more preferably, 80% or less and, even more preferably, 50% or
less. The shape of the organic silver salt can be measured by
analyzing a dispersion of an organic silver salt as transmission
type electron microscopic images. Another method of measuring the
monodispersion is a method of determining of the standard deviation
of the volume weighted mean diameter of the organic silver salt in
which the percentage for the value defined by the volume weight
mean diameter (variation coefficient), is preferably, 100% or less,
more preferably, 80% or less and, even more preferably, 50% or
less. The monodispersion can be determined from particle size
(volume weighted mean diameter) obtained, for example, by a
measuring method of irradiating a laser beam to organic silver
salts dispersed in a liquid, and determining a self correlation
function of the fluctuation of scattered light to the change of
time.
[0116] 3) Preparation
[0117] Methods known in the art can be applied to the method for
producing the organic silver salt used in the invention and to the
dispersing method thereof. For example, reference can be made to
JP-A No. 10-62899, EP Nos. 0803763A1 and 0962812A1, JP-A Nos.
11-349591, 2000-7683, 2000-72711, 2001-163889, 2001-163890,
2001-163827, 2001-33907, 2001-188313, 2001-83652, 2002-6442,
2002-49117, 2002-31870, and 2002-107868, and the like.
[0118] When a photosensitive silver salt is present together during
dispersion of the organic silver salt, fog increases and
sensitivity becomes remarkably lower, so that it is more preferred
that the photosensitive silver salt is not substantially contained
during dispersion. In the invention, the amount of the
photosensitive silver salt to be dispersed in the aqueous
dispersion is preferably 1 mol % or less, more preferably 0.1 mol %
or less, per 1 mol of the organic silver salt in the solution and,
even more preferably, positive addition of the photosensitive
silver salt is not conducted.
[0119] In the invention, the photothermographic material can be
prepared by mixing an aqueous dispersion of the organic silver salt
and an aqueous dispersion of a photosensitive silver salt and the
mixing ratio between the organic silver salt and the photosensitive
silver salt can be selected depending on the purpose. The ratio of
the photosensitive silver salt relative to the organic silver salt
is preferably in a range of from 1 mol % to 30 mol %, more
preferably, from 2 mol % to 20 mol % and, particularly preferably,
3 mol % to 15 mol %. A method of mixing two or more aqueous
dispersions of organic silver salts and two or more aqueous
dispersions of photosensitive silver salts upon mixing is used
preferably for controlling photographic properties.
[0120] 4) Addition Amount
[0121] While the organic silver salt according to the invention can
be used in a desired amount, a total amount of coated silver
including silver halide is preferably in a range of from 0.1
g/m.sup.2 to 5.0 g/m.sup.2, more preferably from 0.3 g/m.sup.2 to
3.0 g/m.sup.2, and even more preferably from 0.5 g/m.sup.2 to 2.0
g/m.sup.2. In particular, in order to improve image storability,
the total amount of coated silver is preferably 1.8 mg/m.sup.2 or
less, and more preferably 1.6 mg/m.sup.2 or less. When a preferable
reducing agent in the invention is used, it is possible to obtain a
sufficient image density by even such a low amount of silver.
[0122] (Metal Phthalocyanine Dye Represented by Formula (PC-1))
[0123] The metal phthalocyanine dye represented by formula (PC-1)
according to the present invention is explained.
[0124] The metal phthalocyanine dye represented by formula (PC-1)
used for the present invention preferably has a half band width of
100 nm or less at the maximum absorbance, more preferably, a half
band width of 80 nm or less, and even more preferably, a half band
width of 50 nm or less.
[0125] The wavelength region having the maximum absorbance is
preferably in a range of from 600 nm to 750 nm, more preferably
from 600 nm to 720 nm, and even more preferably from 620 nm to 700
nm. ##STR21##
[0126] In formula (PC-1), M represents a metal atom. The metal atom
may be any metal which forms a stable complex, and a metal selected
from the group consisting of Li, Na, K, Be, Mg, Ca, Ba, Al, Si, Cd,
Hg, Cr, Fe, Co, Ni, Cu, Zn, Ge, Pd, Sn, Pt, Pb, Sr, or Mn can be
used. Mg, Ca, Co, Zn, Pd, or Cu is preferably used, more
preferably, Co, Pd, Zn, or Cu is used, and particularly preferably,
Cu is used.
[0127] <Substituents and the Like>
[0128] In formula (PC-1), R.sup.1, R.sup.4, R.sup.5, R.sup.8,
R.sup.9, R.sup.12, R.sup.13, and R.sup.16 each independently
represent a hydrogen atom, a substituent, or an electron-attracting
group, and at least one of R.sup.1, R.sup.4, R.sup.5, R.sup.8,
R.sup.9, R.sup.12, R.sup.13, and R.sup.16 is an electron-attracting
group.
[0129] The electron-attracting group herein is selected from groups
represented by a halogen atom, a cyano group, a nitro group,
--C(.dbd.O)--R, --C(.dbd.O)--C(.dbd.O)--R, --S(.dbd.O)--R,
--S(.dbd.O).sub.2--R, --C(.dbd.N--R')--R, --S(.dbd.NR')--R,
--S(.dbd.NR').sub.2--R, --P(.dbd.O)R.sub.2, --O--R'', --S--R'',
--N(--R')--C(.dbd.O)--R, --N(--R')--S(.dbd.O)--R,
--N(--R')--S(.dbd.O).sub.2--R, --N(--R')--C(.dbd.N--R')--R,
--N(--R')--S(.dbd.NR').sub.2--R, and --N(--R')--P(.dbd.O)R.sub.2.
Herein R represents one selected from a hydrogen atom, an alkyl
group, an aryl group, a heterocyclic group, an amino group, an
alkyloxy group, an aryloxy group, a heterocyclic oxy group, a
hydroxy group, an alkylthio group, an arylthio group, a
heterocyclic thio group, or an SH group. R' represents one selected
from a hydrogen atom, an alkyl group, an aryl group, a heterocyclic
group, an acyl group, a sulfonyl group, a sulfinyl group, or a
phosphoryl group. R'' represents one selected from a perfluoro
alkyl group, a cyano group, an acyl group, a sulfonyl group, or a
sulfinyl group.
[0130] The groups represented by R, R', and R'' may be substituted
by a substituent. Specific examples of the substituent include a
halogen atom (a fluorine atom, a chlorine atom, a bromine atom, or
an iodine atom), an alkyl group (including an aralkyl group, a
cycloalkyl group, an active methine group, and the like), an
alkenyl group, an alkynyl group, an aryl group, a heterocyclic
group (at any substitution position), a heterocyclic group
containing a quaternary nitrogen atom (for example, a pyridinio
group, an imidazolio group, a quinolinio group, or an isoquinolinio
group), an acyl group, an alkoxycarbonyl group, an aryloxycarbonyl
group, a carbamoyl group, a carboxy group or a salt thereof, a
sulfonylcarbamoyl group, an acylcarbamoyl group, a
sulfamoylcarbamoyl group, a carbazoyl group, an oxalyl group, an
oxamoyl group, a cyano group, a thiocarbamoyl group, a hydroxy
group, an alkoxy group (including a group in which ethylene oxy
group units or propylene oxy group units are repeated), an aryloxy
group, a heterocyclic oxy group, an acyloxy group, an alkoxy
carbonyloxy group, an aryloxy carbonyloxy group, a carbamoyloxy
group, a sulfonyloxy group, an amino group, an alkylamino group, an
arylamino group, a heterocyclic amino group, an acylamino group, a
sulfonamide group, an ureido group, a thioureido group, an imide
group, an alkoxycarbonylamino group, an aryloxycarbonylamino group,
a sulfamoylamino group, a semicarbazide group, a thiosemicarbazide
group, a hydrazino group, an ammonio group, an oxamoylamino group,
an alkylsulfonylureido group, an arylsulfonylureido group, an
acylureido group, an acylsulfamoylamino group, a nitro group, a
mercapto group, an alkylthio group, an arylthio group, a
heterocyclic thio group, an alkylsulfonyl group, an arylsulfonyl
group, an alkylsulfinyl group, an arylsulfinyl group, a sulfo group
or a salt thereof, a sulfamoyl group, an acylsulfamoyl group, a
sulfonylsulfamoyl group or a salt thereof, a group containing a
phosphoric amide structure or a phosphate ester structure), a
silyloxy group (for example, trimethylsilyloxy, or
t-butyldimethylsilyloxy), a silyl group (for example,
trimethylsilyl, t-butyldimethylsilyl, or phenyldimethylsilyl), and
the like. These substituents may be further substituted by these
substituents.
[0131] In formula (PC-1), a group represented by formula (II) is
preferably used as an electron-attracting group. -L.sup.1-R.sup.17
Formula (II)
[0132] L.sup.1 represents a group selected from **--SO.sub.2--*,
**SO.sub.3*, **--SO.sub.2NR.sub.N--*, **--SO--*, **--CO--*,
**--CONR.sub.N--*, **--COO--*, **--COCO--*, **--COCO.sub.2--*, and
COCONR.sub.N--*. ** denotes a bond with a phthalocyanine skeleton
at this position. * denotes a bond with R.sup.17 at this position.
RN represents one selected from a hydrogen atom, an alkyl group, an
aryl group, a heterocyclic group, an acyl group, an alkoxycarbonyl
group, a carbamoyl group, a sulfonyl group, or a sulfamoyl group.
RN may further be substituted by a substituent which R.sub.1,
R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8
in formula (PC-1) may have. L.sup.1 is preferably **--SO.sub.2--*,
**--SO.sub.2NR.sub.N--*, **--CO--*, **--CONR.sub.N--*, or
**--COO--*, more preferably, **--SO.sub.2--*,
**--SO.sub.2NR.sub.N--*, or **--CONR.sub.N--*, and particularly
preferably, **--SO.sub.2--* or **--SO.sub.2NR.sub.N--*.
[0133] R.sub.N is preferably a hydrogen atom, an alkyl group, an
aryl group, or a heterocyclic group, preferably a hydrogen atom, an
alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to
20 carbon atoms, or a heterocyclic group having 1 to 20 carbon
atoms, more preferably a hydrogen atom, an alkyl group having 1 to
10 carbon atoms, an aryl group having 6 to 10 carbon atoms, or a
heterocyclic group having 1 to 10 carbon atoms, and particularly
preferably a hydrogen atom or an alkyl group having 1 to 6 carbon
atoms.
[0134] R.sup.17 represents one selected from a hydrogen atom, an
alkyl group, an aryl group, or a heterocyclic group. In the case
where R.sup.17 represents an alkyl group, an aryl group or a
heterocyclic group, these groups may be further substituted by
substituents which R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9,
R.sup.12, R.sup.13, or R.sup.16 in formula (PC-1) can have.
R.sup.17 is preferably an alkyl group or an aryl group, and
particularly preferably an alkyl group. R.sup.17 has 1 to 30 carbon
atoms, preferably 1 to 20 carbon atoms, and more preferably 1 to 10
carbon atoms.
[0135] R.sup.17 is preferably substituted by a hydrophilic group.
Herein, a hydrophilic group indicates a carboxy group, a sulfo
group, a phosphate group, a group having a structure of quaternary
salt of nitrogen, a group having a structure of quaternary salt of
phosphorus, or a group in which ethylene oxy group units are
repeated. In the case where the hydrophilic group is a carboxy
group, a sulfo group, or a phosphate group, the hydrophilic group
may have a counter cation, when necessary. As the counter cation, a
metal cation, an ammonium ion, a group having a structure of
quaternary salt of nitrogen, or a group having a structure of a
quaternary salt of phosphorus is used.
[0136] In the case where W is a group having a structure of
quaternary salt of nitrogen, or a group having a structure of
quaternary salt of phosphorus, W may have a counter anion, when
necessary. As examples of the counter anion, a halogen ion, a
sulfate ion, a nitrate ion, a phosphate ion, an oxalate ion, an
alkanesulfonate ion, an arylsulfonate ion, an alkanecarboxylate
ion, an arylcarboxylate ion, and the like can be described. The
hydrophilic group is preferably a carboxy group, a sulfo group, or
a phosphate group, and more preferably, a carboxy group or a sulfo
group. In this case, as a counter cation, Li.sup.+, Na.sup.+,
K.sup.+, Mg.sup.2+, Ca.sup.2+ or NH.sub.4.sup.+ is preferably used,
more preferably, Li.sup.+, Na.sup.+, K.sup.+ or NH.sub.4.sup.+ is
used, and particularly preferably, Li.sup.+ or Na.sup.+ is
used.
[0137] In formula (PC-1), when R.sup.1, R.sup.4, R.sup.5, R.sup.8,
R.sup.9, R.sup.12, R.sup.13, or R.sup.16 is a substituent, the
substituent can be a substituent selected from the same group as R,
R', or R'' in formula (PC-1). These substitutents may be further
substituted by these substituents.
[0138] The substituents are preferably a halogen atom, an alkyl
group, an alkenyl group, an alkynyl group, an aryl group, a
heterocyclic group (at any substitution position), a heterocyclic
group containing a quaternary nitrogen atom (for example, a
pyridinio group, an imidazolio group, a quinolinio group, or an
isoquinolinio group), an acyl group, an alkoxycarbonyl group, an
aryloxycarbonyl group, a carbamoyl group, a carboxy group or a salt
thereof, a sulfonylcarbamoyl group, an acylcarbamoyl group, a
sulfamoylcarbamoyl group, a carbazoyl group, an oxalyl group, an
oxamoyl group, a cyano group, a thiocarbamoyl group, a sulfonyloxy
group, an imide group, a sulfamoylamino group, a semicarbazide
group, a thiosemicarbazide group, a nitro group, an alkylsulfonyl
group, an arylsulfonyl group, an alkylsulfinyl group, an
arylsulfinyl group, a sulfo group or a salt thereof, a sulfamoyl
group, an acylsulfamoyl group, a sulfonylsulfamoyl group or a salt
thereof, or a group containing a phosphoric amide structure or a
phosphate ester structure. More preferably, an alkyl group, an aryl
group, a heterocyclic group, an acyl group, an alkoxycarbonyl
group, a carbamoyl group, a carboxy group or a salt thereof, an
oxalyl group, an oxamoyl group, a cyano group, an imide group, a
sulfamoylamino group, an alkylsulfonyl group, an arylsulfonyl
group, an alkylsulfinyl group, an arylsulfinyl group, a sulfo group
or a salt thereof, a sulfamoyl group, an acylsulfamoyl group, or a
sulfonylsulfamoyl group or a salt thereof is used.
[0139] Even more preferably, an aryl group, a heterocyclic group,
an acyl group, an alkoxycarbonyl group, a carbamoyl group, a
carboxy group or a salt thereof, an alkylsulfonyl group, an
arylsulfonyl group, an alkylsulfinyl group, an arylsulfinyl group,
a sulfo group or a salt thereof, or a sulfamoyl group is used.
[0140] In the compound represented by formula (PC-1), four or more
from among R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9, R.sup.12,
R.sup.13, and R.sup.16 are preferably a group represented by
formula (II), and more preferably, the compound represented by
formula (PC-1) is water soluble. Further preferably, at least one
of R in each combination of R.sup.1 and R.sup.4, R.sup.5 and
R.sup.8, R.sup.9 and R.sup.12, and R.sup.13 and R.sup.16 is a group
represented by formula (II). Particularly preferably, one of R in
each combination of R.sup.1 and R.sup.4, R.sup.5 and R.sup.8,
R.sup.9 and R.sup.12, and R.sup.13 and R.sup.16 is a group
represented by formula (II), and the other is a hydrogen atom. When
a plural number of groups represented by formula (II) are present
in a same molecule, these may be identical or different from one
another.
[0141] In formula (PC-1), R.sup.2, R.sup.3, R.sup.6, R.sup.7,
R.sup.10, R.sup.11, R.sup.14, and R.sup.15 each independently
represent a hydrogen atom or a substituent. Herein, the substituent
is selected from the same range as R.sup.1, R.sup.4, R.sup.5,
R.sup.8, R.sup.9, R.sup.12, R.sup.13, and R.sup.16 in formula
(PC-1).
[0142] R.sup.2, R.sup.3, R.sup.6, R.sup.7, R.sup.10, R.sup.14, and
R.sup.15 are preferably a hydrogen atom, a halogen atom, a carboxy
group, an alkoxycarbonyl group, an acyl group, a sulfo group, a
sulfamoyl group, a sulfonyl group, an alkyl group, an aryl group,
or a heterocyclic group. More preferable are a hydrogen atom, a
halogen atom, a sulfo group, a sulfamoyl group, and a sulfonyl
group, and particularly preferable are a hydrogen atom, a sulfo
group, and a halogen atom.
[0143] Particularly preferably, in formula (PC-1), R.sup.2,
R.sup.3, R.sup.6, R.sup.7, R.sup.10, R.sup.11, R.sup.14, and
R.sup.15 each represent a hydrogen atom and at least one of
R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9R.sup.12, R.sup.13 and
R.sup.16 represents a group represented by formula (II). More
preferably, R.sup.2, R.sup.3, R.sup.6, R.sup.7, R.sup.10, R.sup.11,
R.sup.14, and R.sup.15 each represent a hydrogen atom and four or
more from among R.sup.1, R.sup.4, R.sup.5, R.sup.8, R.sup.9,
R.sup.12, R.sup.13 and R.sup.16 represent a group represented by
formula (II). Even more preferably, R.sup.2, R.sup.2R.sup.6,
R.sup.7, R.sup.10, R.sup.11, R.sup.14, and R.sup.15 each represent
a hydrogen atom, and four or more from among R.sup.1, R.sup.4,
R.sup.5, R.sup.8, R.sup.9, R.sup.12, R.sup.13 and R.sup.16
represent a group represented by formula (II) and are a
water-soluble group.
[0144] In general, compounds having a plural number of substituents
may have a regioisomer, in which the substituents have different
bonding positions.
[0145] The compounds represented by formula (PC-1) in the invention
are not exceptional. In some cases several kinds of regioisomers
may be present. In the invention, the phthalocyanine compound may
be used as a single compound but it may be used as a mixture of
regioisomers. In the case where a mixture of regioisomers is used,
any number of regioisomers, any substitution position in the
isomer, and any ratio of isomers may be employed.
[0146] <Specific Examples>
[0147] Examples of the compound represented by formula (PC-1) used
in the present invention are shown below. However, the present
invention is not limited by these examples. In the following
examples of the compound, mixtures of regioisomers are described as
a single compound. TABLE-US-00001 ##STR22## ##STR23## ##STR24##
##STR25## ##STR26## ##STR27## ##STR28## ##STR29## ##STR30##
##STR31## ##STR32## ##STR33## ##STR34## ##STR35## ##STR36##
##STR37## ##STR38## ##STR39## ##STR40## ##STR41## ##STR42##
##STR43## ##STR44## ##STR45## ##STR46## ##STR47## ##STR48##
##STR49##
[0148] <Synthesis of Illustrated Compound No. 2>
##STR50##
[0149] CuCl.sub.2 (134 mg, 1 mmol) was added to a synthetic
intermediate A (1.26 g, 4 mmol) in an ethylene glycol solution (10
mL), and this was heated to 100.degree. C. DBU (1.52 g, 10 mmol)
was added to the reaction mixture, and stirring was carried out for
10 hours at 100.degree. C. The reaction mixture was acidified with
hydrochloric acid, and LiCl was added thereto to separate a crude
phthalocyanine. The obtained crude product was purified through
column chromatography using Sephadex G-15 as a carrier. 67 mg of a
mixture of illustrated compound No. 2 was obtained (yield of
5%).
[0150] <Adding Method of Dye>
[0151] The dye of the invention is preferably water-soluble and is
preferably used for the manufacturing of photothermographic
material as an aqueous solution prepared in advance by water as a
medium. In the said solution, the water-soluble phthalocyanine
compound of the present invention is contained in an amount of from
0.1% by weight to 30% by weight, preferably from 0.5% by weight to
20% by weight, and more preferably from 1% by weight to 8% by
weight. The said solution further may contain a water-soluble
organic solvent or an auxiliary additive. A content of
water-soluble organic solvent is from 0% by weight to 30% by
weight, and preferably from 5% by weight to 30% by weight. A
content of auxiliary additive is from 0% by weight to 5% by weight,
and preferably from 0% by weight to 2% by weight.
[0152] At the preparation of an aqueous solution of water-soluble
phthalocyanine compound according to the present invention, as
specific examples of the usable water-soluble organic solvent,
alkanol having 1 to 4 carbon atoms such as methanol, ethanol,
propanol, isopropanol, butanol, isobutanol, sec-butanol,
tert-butanol, or the like; amide carboxylate such as
N,N-dimethlyformamide, N,N-dimethylacetamide, or the like; lactams
such as .epsilon.-caprolactam, N-methylpirrolidine-2-one, or the
like; urea; a cyclic urea such as 1,3-dimethylimidazolidine-2-one,
1,3-dimethylhexahydropyrimide-2-one, or the like; ketone or
ketoalcohol such as acetone, methyl ethyl ketone,
2-methyl-2-hydroxypentane-4-one, or the like; ether such as
tertahydrofuran, dioxan, or the like; mono-, oligo-, and
polyalkylene glycol or thioglycol having an alkylene unit with 2 to
6 carbon atoms such as ethylene glycol, 1,2- or 1,3-propylene
glycol, 1,2- or 1,4-butylene glycol, 1,6-hexylene glycol,
diethylene glycol, triethylene glycol, dipropylene glycol,
thiodiglycol, polyethylene glycol, polypropylene glycol, or the
like; polyol (triol) such as glycerine, hexane-1,2,6-triol, or the
like; alkylether with 1 to 4 carbon atoms of poly-alcohol such as
ethylene glycol monomethylether, ethylene glycol monoethylether,
diethylene glycol monomethylether, diethylene glycol
monoethylether, triethylene glycol monomethylether, triethylene
glycol monoethylether, or the like; .gamma.-butylolactone,
dimethylsulfoxide, and the like can be described. Two or more of
these water-soluble organic solvents can be used in
combination.
[0153] Among the water-soluble organic solvents described above,
urea, N-methylpyrrolidine-2-one, mono, di, or trialkylene glycol
having an alkylene unit with 2 to 6 carbon atoms are preferable,
and mono, di, or triethylene glycol, dipropylene glycol,
dimethylsulfoxide, and the like are more preferable. Particularly,
N-methlpyrrolidine-2-one, diethylene glycol, dimethysulfoxide, or
urea is preferably used, and urea is most preferable. As the
water-soluble phthalocyanine compound of the invention is diluted
by mixing the said aqueous solution with various chemicals at the
making of photothermographic material, the method of containing an
water-soluble organic solvent, besides the said aqueous solution,
in an amount of from 1 mol to 500 mol per 1 mol of the
water-soluble dye is also preferably applied.
[0154] Examples of the auxiliary additives include an antiseptic, a
pH control agent, a chelating agent, a rust-preventing agent, a
water-soluble ultraviolet ray absorbing agent, a water-soluble
polymer, a dye solvent, a surfactant, and the like, and they are
added if necessary.
[0155] Examples of the antiseptic include sodium dihydroacetate,
sodium sorbinate, sodium 2-pyridinethiol-1-oxide, sodium benzoate,
sodium pentachloro phenol, benzisothiazolinone and a salt thereof,
p-hydroxybenzoic acid esters, and the like.
[0156] As the pH control agent, any compounds can be applied as far
as it can control the pH of the prepared solution in a range of
from 4 to 11 without any bad effect. Examples of the pH control
agent include alkanolamine such as diethanolamine or triethanol
amine; alkali metal salts of hydroxide such as lithium hydroxide,
sodium hydroxide, or potassium hydroxide; ammonium hydroxide; and
alkali metal salts of carbonic acid such as lithium carbonate,
sodium carbonate, or potassium carbonate.
[0157] Examples of the chelating agent include a sodium salt of
ethylenediaminetetraacetic acid, a sodium salt of nitrilotriacetic
acid, a sodium salt of hydroxyethyl ethylenediaminetriacetic acid,
a sodium salt of diethylene triaminepentaacetic acid, a sodium salt
of uracil diacetic acid, and the like. Examples of the
rust-preventing agent include hyposulfites, sodium thiosulfate,
thioglycolic acid ammonium salt, diisopropyl ammonium nitrite,
pentaerythrithol tetranitrate, dicyclohexylammonium nitrite, and
the like. Examples of the water-soluble polymer include poly(vinyl
alcohol), a cellulose derivative, polyamine, polyimine, and the
like. Examples of the water-soluble ultraviolet ray absorbing agent
include a sulfonated benzophenone, a sulfonated benztriazole, and
the like. Examples of the dye solvent include
.epsilon.-caprolactam, ethylene carbonate, urea, and the like.
Examples of the surfactant include well-known surfactants of
anionic, cationic, and nonionic surfactants, and a surfactant of
acetyleneglycol type or the like is also preferably used.
[0158] <Layer to be Added>
[0159] The dye of the present invention can be incorporated in at
least one layer on the side of the support where an image forming
layer is provided, or in at least one layer provided on the
opposite side of the support from the side where an image forming
layer is provided. The dye can be incorporated on both sides of the
support.
[0160] <Range of Addition Amount>
[0161] To adjust the image tone after thermal developing process in
a preferable level, the addition amount of dye is determined by the
combination with a color tone of developed silver image or a color
tone obtained by other additives. Generally, the dye is used at an
amount as such that the optical density does not exceed 1.5 when
measured at the desired wavelength. The optical density is from
0.01 to 1.2, preferably from 0.05 to 1.0, and more preferably from
0.1 to 0.8. To obtain the above optical density, the addition
amount of dye is generally from 0.5 mg/m.sup.2 to 200 mg/m.sup.2,
preferably from 1 mg/m.sup.2 to 160 mg/m 2, and more preferably
from 5 mg/m.sup.2 to 120 mg/m.sup.2.
[0162] (Reducing Agent)
[0163] The photothermographic material of the present invention
preferably contains a reducing agent for organic silver salts as a
thermal developing agent. The reducing agent for organic silver
salts can be any substance (preferably, organic substance) capable
of reducing silver ions into metallic silver. Examples of the
reducing agent are described in JP-A No. 11-65021 (column Nos. 0043
to 0045) and EP No. 0803764 (p. 7, line 34 to p. 18, line 12).
[0164] The reducing agent according to the invention is preferably
a so-called hindered phenolic reducing agent or a bisphenol agent
having a substituent at the ortho-position to the phenolic hydroxy
group. It is more preferably a reducing agent represented by the
following formula (R). ##STR51##
[0165] In formula (R), R.sup.11 and R.sup.11' each independently
represent an alkyl group having 1 to 20 carbon atoms. R.sup.12 and
R.sup.12' each independently represent a hydrogen atom or a group
capable of substituting for a hydrogen atom on a benzene ring. L
represents an --S-- group or a --CHR.sup.13-- group. R.sup.13
represents a hydrogen atom or an alkyl group having 1 to 20 carbon
atoms. X.sup.1 and X.sup.1' each independently represent a hydrogen
atom or a group capable of substituting for a hydrogen atom on a
benzene ring.
[0166] Formula (R) is to be described in detail.
[0167] In the following description, when referred to as an alkyl
group, it means that the alkyl group contains a cycloalkyl group,
as far as it is not mentioned specifically.
[0168] 1) R.sup.11 and R.sup.11'
[0169] R.sup.11 and R.sup.11' each independently represent a
substituted or unsubstituted alkyl group having 1 to 20 carbon
atoms. The substituent for the alkyl group has no particular
restriction and can include, preferably, an aryl group, a hydroxy
group, an alkoxy group, an aryloxy group, an alkylthio group, an
arylthio group, an acylamino group, a sulfonamide group, a sulfonyl
group, a phosphoryl group, an acyl group, a carbamoyl group, an
ester group, a ureido group, a urethane group, a halogen atom, and
the like.
[0170] 2) R.sup.12 and R.sup.12', X.sup.1 and X.sup.1'
[0171] R.sup.12 and R.sup.12' each independently represent a
hydrogen atom or a group capable of substituting for a hydrogen
atom on a benzene ring. X.sup.1 and X.sup.1 each independently
represent a hydrogen atom or a group capable of substituting for a
hydrogen atom on a benzene ring. As each of the groups capable of
substituting for a hydrogen atom on the benzene ring, an alkyl
group, an aryl group, a halogen atom, an alkoxy group, and an
acylamino group are described preferably.
[0172] 3) L
[0173] L represents an --S-- group or a --CHR.sup.13-- group.
R.sup.13 represents a hydrogen atom or an alkyl group having 1 to
20 carbon atoms in which the alkyl group may have a substituent.
Specific examples of the unsubstituted alkyl group for R.sup.13 can
include, for example, a methyl group, an ethyl group, a propyl
group, a butyl group, a heptyl group, an undecyl group, an
isopropyl group, a 1-ethylpentyl group, a 2,4,4-trimethylpentyl
group, cyclohexyl group, 2,4-dimethyl-3-cyclohexenyl group,
3,5-dimethyl-3-cyclohexenyl group, and the like. Examples of the
substituent for the alkyl group can include, similar to the
substituent of R.sup.11, a halogen atom, an alkoxy group, an
alkylthio group, an aryloxy group, an arylthio group, an acylamino
group, a sulfonamide group, a sulfonyl group, a phosphoryl group,
an oxycarbonyl group, a carbamoyl group, a sulfamoyl group, and the
like.
[0174] 4) Preferred Substituents
[0175] R.sup.11 and R.sup.11' are preferably a primary, secondary,
or tertiary alkyl group having 1 to 15 carbon atoms and can
include, specifically, a methyl group, an isopropyl group, a
t-butyl group, a t-amyl group, a t-octyl group, a cyclohexyl group,
a cyclopentyl group, a 1-methylcyclohexyl group, a
1-methylcyclopropyl group, and the like. R.sup.11 and R.sup.11'
each represent, more preferably, an alkyl group having 1 to 8
carbon atoms and, among them, a methyl group, a t-butyl group, a
t-amyl group, and a 1-methylcyclohexyl group are further preferred
and, a methyl group and a t-butyl group being most preferred.
[0176] R.sup.12 and R.sup.12' are preferably an alkyl group having
1 to 20 carbon atoms and can include, specifically, a methyl group,
an ethyl group, a propyl group, a butyl group, an isopropyl group,
a t-butyl group, a t-amyl group, a cyclohexyl group, a
1-methylcyclohexyl group, a benzyl group, a methoxymethyl group, a
methoxyethyl group, and the like. More preferred are a methyl
group, an ethyl group, a propyl group, an isopropyl group, and a
t-butyl group, and particularly preferred are a methyl group and an
ethyl group.
[0177] X.sup.1 and X.sup.1' are preferably a hydrogen atom, a
halogen atom, or an alkyl group, and more preferably a hydrogen
atom.
[0178] L is preferably a --CHR.sup.13-- group.
[0179] R.sup.13 is preferably a hydrogen atom or an alkyl group
having 1 to 15 carbon atoms. The alkyl group is preferably a chain
or a cyclic alkyl group. And, a group which has a C.dbd.C bond in
these alkyl group is also preferably used. Preferable examples of
the alkyl group can include a methyl group, an ethyl group, a
propyl group, an isopropyl group, a 2,4,4-trimethylpentyl group, a
cyclohexyl group, a 2,4-dimethyl-3-cyclohexenyl group, a
3,5-dimetyl-3-cyclohexenyl group and the like. Particularly
preferable R.sup.13 is a hydrogen atom, a methyl group, an ethyl
group, a propyl group, an isopropyl group, or a
2,4-dimethyl-3-cyclohexenyl group.
[0180] In the case where R.sup.11 and R.sup.11' are a tertiary
alkyl group and R.sup.12 and R.sup.12' are a methyl group, R.sup.13
preferably is a primary or secondary alkyl group having 1 to 8
carbon atoms (a methyl group, an ethyl group, a propyl group, an
isopropyl group, a 2,4-dimethyl-3-cyclohexenyl group, or the
like).
[0181] In the case where R.sup.11 and R.sup.11' are a tertiary
alkyl group and R.sup.12 and R.sup.12' are an alkyl group other
than a methyl group, R.sup.13 preferably is a hydrogen atom.
[0182] In the case where R.sup.11 and R.sup.11' are not a tertiary
alkyl group, R.sup.13 preferably is a hydrogen atom or a secondary
alkyl group, and particularly preferably a secondary alkyl group.
As the secondary alkyl group for R.sup.13, an isopropyl group and a
2,4-dimethyl-3-cyclohexenyl group are preferred.
[0183] The reducing agent described above shows different thermal
developing performances, color tones of developed silver images, or
the like depending on the combination of R.sup.11, R.sup.11',
R.sup.12, R.sup.12', and R.sup.13. Since these performances can be
controlled by using two or more reducing agents in combination, it
is preferred to use two or more reducing agents in combination
depending on the purpose.
[0184] Specific examples of the reducing agents of the invention
including the compounds represented by formula (R) according to the
invention are shown below, but the invention is not restricted to
these. ##STR52## ##STR53## ##STR54##
[0185] As preferred reducing agents of the invention other than
those above, there can be mentioned compounds disclosed in JP-A
Nos. 2001-188314, 2001-209145, 2001-350235, and 2002-156727, and EP
No. 1278101A2.
[0186] The addition amount of the reducing agent is preferably from
0.1 g/m.sup.2 to 3.0 g/m.sup.2, more preferably from 0.2 g/m.sup.2
to 2.0 g/m.sup.2 and, even more preferably from 0.3 g/m.sup.2 to
1.0 g/m.sup.2. It is preferably contained in a range of from 5 mol
% to 50 mol %, more preferably from 8 mol % to 30 mol % and, even
more preferably from 10 mol % to 20 mol %, per 1 mol of silver in
the image forming layer. The reducing agent is preferably contained
in the image forming layer.
[0187] In the invention, the reducing agent may be incorporated
into a photothermographic material by being added into the coating
solution, such as in the form of a solution, an emulsified
dispersion, a solid fine particle dispersion, or the like.
[0188] As well known emulsified dispersing method, there can be
mentioned a method comprising dissolving the reducing agent in an
oil such as dibutylphthalate, tricresylphosphate, dioctylsebacate,
tri(2-ethylhexyl)phosphate, or the like, and an auxiliary solvent
such as ethyl acetate, cyclohexanone, or the like, and then adding
a surfactant such as sodium dodecylbenzenesulfonate, sodium
oleoil-N-methyltaurinate, sodium di(2-ethylhexyl)sulfosuccinate or
the like; from which an emulsified dispersion is mechanically
produced. During the process, for the purpose of controlling
viscosity of oil droplet and refractive index, the addition of
polymer such as .alpha.-methylstyrene oligomer,
poly(t-butylacrylamide), or the like is preferable.
[0189] As a solid particle dispersing method, there can be
mentioned a method comprising dispersing the powder of the reducing
agent in a proper solvent such as water or the like, by means of
ball mill, colloid mill, vibrating ball mill, sand mill, jet mill,
roller mill, or ultrasonics, thereby obtaining solid dispersion. In
this case, there may be used a protective colloid (such as
poly(vinyl alcohol)), or a surfactant (for instance, an anionic
surfactant such as sodium triisopropylnaphthalenesulfonate (a
mixture of compounds having the three isopropyl groups in different
substitution sites)). In the mills enumerated above, generally used
as the dispersion media are beads made of zirconia or the like, and
Zr or the like eluting from the beads may be incorporated in the
dispersion. Although depending on the dispersing conditions, the
amount of Zr or the like incorporated in the dispersion is
generally in a range of from 1 ppm to 1000 ppm. It is practically
acceptable so long as Zr is incorporated in an amount of 0.5 mg or
less per 1 g of silver.
[0190] Preferably, an antiseptic (for instance, benzisothiazolinone
sodium salt) is added in an aqueous dispersion.
[0191] The reducing agent is particularly preferably used as solid
particle dispersion, and is added in the form of fine particles
having average particle size of from 0.01 .mu.m to 10 .mu.m,
preferably from 0.05 .mu.m to 5 .mu.m and, more preferably from 0.1
.mu.m to 2 .mu.m. In the invention, other solid dispersions are
preferably used with this particle size range.
[0192] (Development Accelerator)
[0193] In the photothermographic material of the invention, as a
development accelerator, sulfonamide phenolic compounds described
in the specification of JP-A No. 2000-267222, and represented by
formula (A) described in the specification of JP-A No. 2000-330234;
hindered phenolic compounds represented by formula (II) described
in JP-A No. 2001-92075; hydrazine compounds described in the
specification of JP-A No. 10-62895, represented by formula (I)
described in the specification of JP-A No. 11-15116, represented by
formula (D) described in the specification of JP-A No. 2002-156727,
and represented by formula (1) described in the specification of
JP-A No. 2002-278017; and phenolic or naphtholic compounds
represented by formula (2) described in the specification of JP-A
No. 2001-264929 are used preferably. The development accelerator
described above is used in a range of from 0.1 mol % to 20 mol %,
preferably, in a range of from 0.5 mol % to 10 mol % and, more
preferably in a range of from 1 mol % to 5 mol %, with respect to
the reducing agent. The introducing methods to the
photothermographic material can include similar methods as those
for the reducing agent and, it is particularly preferred to add as
a solid dispersion or an emulsified dispersion. In the case of
adding as an emulsified dispersion, it is preferred to add as an
emulsified dispersion dispersed by using a high boiling solvent
which is solid at a normal temperature and an auxiliary solvent
having a low boiling point, or to add as a so-called oilless
emulsified dispersion not using the high boiling solvent.
[0194] In the present invention, among the development accelerators
described above, hydrazine compounds represented by formula (D)
described in the specification of JP-A No. 2002-156727, and
phenolic or naphtholic compounds represented by formula (2)
described in the specification of JP-A No. 2001-264929 are more
preferred.
[0195] Particularly preferred development accelerators of the
invention are compounds represented by the following formulae (A-1)
or (A-2). Q.sub.1-NHNH-Q.sub.2 Formula (A-1)
[0196] In the formula, Q.sub.1 represents an aromatic group or a
heterocyclic group which bonds to --NHNH-Q.sub.2 at a carbon atom,
and Q.sub.2 represents one selected from a carbamoyl group, an acyl
group, an alkoxycarbonyl group, an aryloxycarbonyl group, a
sulfonyl group, or a sulfamoyl group.
[0197] In formula (A-1), the aromatic group or the heterocyclic
group represented by Q.sub.1 is preferably a 5- to 7-membered
unsaturated ring. Preferred examples include a benzene ring, a
pyridine ring, a pyrazine ring, a pyrimidine ring, a pyridazine
ring, a 1,2,4-triazine ring, a 1,3,5-triazine ring, a pyrrole ring,
an imidazole ring, a pyrazole ring, a 1,2,3-triazole ring, a
1,2,4-triazole ring, a tetrazole ring, a 1,3,4-thiadiazole ring, a
1,2,4-thiadiazole ring, a 1,2,5-thiadiazole ring, a
1,3,4-oxadiazole ring, a 1,2,4-oxadiazole ring, a 1,2,5-oxadiazole
ring, a thiazole ring, an oxazole ring, an isothiazole ring, an
isooxazole ring, a thiophene ring, and the like. Condensed rings in
which the rings described above are condensed to each other are
also preferred.
[0198] The rings described above may have substituents and in a
case where they have two or more substituents, the substituents may
be identical or different from one another. Examples of the
substituents can include a halogen atom, an alkyl group, an aryl
group, a carbonamide group, an alkylsulfonamide group, an
arylsulfonamide group, an alkoxy group, an aryloxy group, an
alkylthio group, an arylthio group, a carbamoyl group, a sulfamoyl
group, a cyano group, an alkylsulfonyl group, an arylsulfonyl
group, an alkoxycarbonyl group, an aryloxycarbonyl group, and an
acyl group. In the case where the substituents are groups capable
of substitution, they may have further substituents and examples of
preferred substituents can include a halogen atom, an alkyl group,
an aryl group, a carbonamide group, an alkylsulfonamide group, an
arylsulfonamide group, an alkoxy group, an aryloxy group, an
alkylthio group, an arylthio group, an acyl group, an
alkoxycarbonyl group, an aryloxycarbonyl group, a carbamoyl group,
a cyano group, a sulfamoyl group, an alkylsulfonyl group, an
arylsulfonyl group, and an acyloxy group.
[0199] The carbamoyl group represented by Q.sub.2 is a carbamoyl
group preferably having 1 to 50 carbon atoms and, more preferably
having 6 to 40 carbon atoms, and examples can include unsubstituted
carbamoyl, methyl carbamoyl, N-ethylcarbamoyl, N-propylcarbamoyl,
N-sec-butylcarbamoyl, N-octylcarbamoyl, N-cyclohexylcarbamoyl,
N-tert-butylcarbamoyl, N-dodecylcarbamoyl,
N-(3-dodecyloxypropyl)carbamoyl, N-octadecylcarbamoyl,
N-{3-(2,4-tert-pentylphenoxy)propyl}carbamoyl,
N-(2-hexyldecyl)carbamoyl, N-phenylcarbamoyl,
N-(4-dodecyloxyphenyl)carbamoyl,
N-(2-chloro-5-dodecyloxycarbonylphenyl)carbamoyl,
N-naphthylcarbamoyl, N-3-pyridylcarbamoyl, and
N-benzylcarbamoyl.
[0200] The acyl group represented by Q.sub.2 is an acyl group,
preferably having 1 to 50 carbon atoms and, more preferably having
6 to 40 carbon atoms, and can include, for example, formyl, acetyl,
2-methylpropanoyl, cyclohexylcarbonyl, octanoyl, 2-hexyldecanoyl,
dodecanoyl, chloroacetyl, trifluoroacetyl, benzoyl,
4-dodecyloxybenzoyl, and 2-hydroxymethylbenzoyl. The alkoxycarbonyl
group represented by Q.sub.2 is an alkoxycarbonyl group, preferably
having 2 to 50 carbon atoms and, more preferably having 6 to 40
carbon atoms, and can include, for example, methoxycarbonyl,
ethoxycarbonyl, isobutyloxycarbonyl, cyclohexyloxycarbonyl,
dodecyloxycarbonyl, and benzyloxycarbonyl.
[0201] The aryloxy carbonyl group represented by Q.sub.2 is an
aryloxycarbonyl group, preferably having 7 to 50 carbon atoms and,
more preferably having 7 to 40 carbon atoms, and can include, for
example, phenoxycarbonyl, 4-octyloxyphenoxycarbonyl,
2-hydroxymethylphenoxycarbonyl, and 4-dodecyloxyphenoxycarbonyl.
The sulfonyl group represented by Q.sub.2 is a sulfonyl group,
preferably having 1 to 50 carbon atoms and, more preferably, having
6 to 40 carbon atoms and can include, for example, methylsulfonyl,
butylsulfonyl, octylsulfonyl, 2-hexadecylsulfonyl,
3-dodecyloxypropylsulfonyl, 2-octyloxy-5-tert-octylphenyl sulfonyl,
and 4-dodecyloxyphenyl sulfonyl.
[0202] The sulfamoyl group represented by Q.sub.2 is a sulfamoyl
group, preferably having 0 to 50 carbon atoms, more preferably
having 6 to 40 carbon atoms, and can include, for example,
unsubstituted sulfamoyl, N-ethylsulfamoyl group,
N-(2-ethylhexyl)sulfamoyl, N-decylsulfamoyl, N-hexadecylsulfamoyl,
N-{3-(2-ethylhexyloxy)propyl}sulfamoyl,
N-(2-chloro-5-dodecyloxycarbonylphenyl)sulfamoyl, and
N-(2-tetradecyloxyphenyl)sulfamoyl. The group represented by
Q.sub.2 may further have a group mentioned as the example of the
substituent of 5- to 7-membered unsaturated ring represented by
Q.sub.1 at the position capable of substitution. In a case where
the group has two or more substituents, such substituents may be
identical or different from one another.
[0203] Next, preferred, range for the compound represented by
formula (A-1) is to be described. A 5- or 6-membered unsaturated
ring is preferred for Q.sub.1, and a benzene ring, a pyrimidine
ring, a 1,2,3-triazole ring, a 1,2,4-triazole ring, a tetrazole
ring, a 1,3,4-thiadiazole ring, a 1,2,4-thiadiazole ring, a
1,3,4-oxadiazole ring, a 1,2,4-oxadiazole ring, a thioazole ring,
an oxazole ring, an isothiazole ring, an isooxazole ring, and a
ring in which the ring described above is condensed with a benzene
ring or unsaturated hetero ring are more preferred. Further,
Q.sub.2 is preferably a carbamoyl group and, particularly, a
carbamoyl group having a hydrogen atom on the nitrogen atom is
particularly preferred. ##STR55##
[0204] In formula (A-2), R.sub.1 represents one selected from an
alkyl group, an acyl group, an acylamino group, a sulfonamide
group, an alkoxycarbonyl group, or a carbamoyl group. R.sub.2
represents one selected from a hydrogen atom, a halogen atom, an
alkyl group, an alkoxy group, an aryloxy group, an alkylthio group,
an arylthio group, an acyloxy group, or a carbonate ester group.
R.sub.3 and R.sub.4 each independently represent a group capable of
substituting for a hydrogen atom on a benzene ring which is
mentioned as the example of the substituent for formula (A-1).
R.sub.3 and R.sub.4 may link together to form a condensed ring.
[0205] R.sub.1 is preferably an alkyl group having 1 to 20 carbon
atoms (for example, a methyl group, an ethyl group, an isopropyl
group, a butyl group, a tert-octyl group, a cyclohexyl group, or
the like), an acylamino group (for example, an acetylamino group, a
benzoylamino group, a methylureido group, a 4-cyanophenylureido
group, or the like), or a carbamoyl group (for example, a
n-butylcarbamoyl group, an N,N-diethylcarbamoyl group, a
phenylcarbamoyl group, a 2-chlorophenylcarbamoyl group, a
2,4-dichlorophenylcarbamoyl group, or the like). An acylamino group
(including a ureido group and a urethane group) is more preferred.
R.sub.2 is preferably a halogen atom (more preferably, a chlorine
atom or a bromine atom), an alkoxy group (for example, a methoxy
group, a butoxy group, an n-hexyloxy group, an n-decyloxy group, a
cyclohexyloxy group, a benzyloxy group, or the like), or an aryloxy
group (for example, a phenoxy group, a naphthoxy group, or the
like).
[0206] R.sub.3 is preferably a hydrogen atom, a halogen atom, or an
alkyl group having 1 to 20 carbon atoms, and most preferably a
halogen atom. R.sub.4 is preferably a hydrogen atom, an alkyl
group, or an acylamino group, and more preferably an alkyl group or
an acylamino group. Examples of the preferred substituent thereof
are similar to those for R.sub.1. In the case where R.sub.4 is an
acylamino group, R.sub.4 may preferably link with R.sub.3 to form a
carbostyryl ring.
[0207] In the case where R.sub.3 and R.sub.4 in formula (A-2) link
together to form a condensed ring, a naphthalene ring is
particularly preferred as the condensed ring. The same substituent
as the example of the substituent referred to for formula (A-1) may
bond to the naphthalene ring. In the case where formula (A-2) is a
naphtholic compound, R.sub.1 is preferably a carbamoyl group. Among
them, a benzoyl group is particularly preferred. R.sub.2 is
preferably an alkoxy group or an aryloxy group and, particularly
preferably an alkoxy group.
[0208] Preferred specific examples for the development accelerator
of the invention are to be described below. The invention is not
restricted to them. ##STR56## ##STR57##
[0209] (Hydrogen Bonding Compound)
[0210] In the invention, in the case where the reducing agent has
an aromatic hydroxy group (--OH) or an amino group (--NHR, R
represents a hydrogen atom or an alkyl group), particularly in the
case where the reducing agent is a bisphenol described above, it is
preferred to use in combination, a non-reducing compound having a
group reacting with these groups of the reducing agent, and also
forming a hydrogen bond therewith.
[0211] As a group forming a hydrogen bond with a hydroxy group or
an amino group, there can be mentioned a phosphoryl group, a
sulfoxide group, a sulfonyl group, a carbonyl group, an amide
group, an ester group, a urethane group, a ureido group, a tertiary
amino group, a nitrogen-containing aromatic group, and the like.
Particularly preferred among them is a phosphoryl group, a
sulfoxide group, an amide group (not having --N(H)-- moiety but
being blocked in the form of --N(Ra)-- (where, Ra represents a
substituent other than H)), a urethane group (not having --N(H)--
moiety but being blocked in the form of --N(Ra)-- (where, Ra
represents a substituent other than H)), and a ureido group (not
having --N(H)-- moiety but being blocked in the form of --N(Ra)--
(where, Ra represents a substituent other than H)).
[0212] In the invention, particularly preferable as the hydrogen
bonding compound is the compound expressed by formula (D) shown
below. ##STR58##
[0213] In formula (D), R.sup.21 to R.sup.23 each independently
represent one selected from an alkyl group, an aryl group, an
alkoxy group, an aryloxy group, an amino group, or a heterocyclic
group, which may be substituted or unsubstituted.
[0214] In the case where R.sup.21 to R.sup.23 contain a
substituent, examples of the substituent include a halogen atom, an
alkyl group, an aryl group, an alkoxy group, an amino group, an
acyl group, an acylamino group, an alkylthio group, an arylthio
group, a sulfonamide group, an acyloxy group, an oxycarbonyl group,
a carbamoyl group, a sulfamoyl group, a sulfonyl group, a
phosphoryl group, and the like, in which preferred as the
substituents are an alkyl group or an aryl group, e.g., a methyl
group, an ethyl group, an isopropyl group, a t-butyl group, a
t-octyl group, a phenyl group, a 4-alkoxyphenyl group, a
4-acyloxyphenyl group, and the like.
[0215] Specific examples of an alkyl group expressed by R.sup.21 to
R.sup.23 include a methyl group, an ethyl group, a butyl group, an
octyl group, a dodecyl group, an isopropyl group, a t-butyl group,
a t-amyl group, a t-octyl group, a cyclohexyl group, a
1-methylcyclohexyl group, a benzyl group, a phenetyl group, a
2-phenoxypropyl group, and the like.
[0216] As an aryl group, there can be mentioned a phenyl group, a
cresyl group, a xylyl group, a naphthyl group, a 4-t-butylphenyl
group, a 4-t-octylphenyl group, a 4-anisidyl group, a
3,5-dichlorophenyl group, and the like.
[0217] As an alkoxyl group, there can be mentioned a methoxy group,
an ethoxy group, a butoxy group, an octyloxy group, a
2-ethylhexyloxy group, a 3,5,5-trimethylhexyloxy group, a
dodecyloxy group, a cyclohexyloxy group, a 4-methylcyclohexyloxy
group, a benzyloxy group, and the like.
[0218] As an aryloxy group, there can be mentioned a phenoxy group,
a cresyloxy group, an isopropylphenoxy group, a 4-t-butylphenoxy
group, a naphthoxy group, a biphenyloxy group, and the like.
[0219] As an amino group, there can be mentioned a dimethylamino
group, a diethylamino group, a dibutylamino group, a dioctylamino
group, an N-methyl-N-hexylamino group, a dicyclohexylamino group, a
diphenylamino group, an N-methyl-N-phenylamino group, and the
like.
[0220] Preferred as R.sup.21 to R.sup.23 is an alkyl group, an aryl
group, an alkoxy group, or an aryloxy group. Concerning the effect
of the invention, it is preferred that at least one of R.sup.21 to
R.sup.23 is an alkyl group or an aryl group, and more preferably,
two or more of them are an alkyl group or an aryl group. From the
viewpoint of low cost availability, it is preferred that R.sup.21
to R.sup.23 are of the same group.
[0221] Specific examples of the hydrogen bonding compound
represented by formula (D) of the invention and others are shown
below, but the invention is not limited thereto. ##STR59##
##STR60##
[0222] Specific examples of hydrogen bonding compounds other than
those enumerated above can be found in those described in EP No.
1,096,310 and in JP-A Nos. 2002-156727 and 2002-318431.
[0223] The compound expressed by formula (D) used in the invention
can be used in the photothermographic material by being
incorporated into the coating solution in the form of solution,
emulsified dispersion, or solid fine particle dispersion, similar
to the case of reducing agent. However, it is preferably used in
the form of solid dispersion. In the solution, the compound
expressed by formula (D) forms a hydrogen-bonded complex with a
compound having a phenolic hydroxy group or an amino group, and can
be isolated as a complex in crystalline state depending on the
combination of the reducing agent and the compound expressed by
formula (D).
[0224] It is particularly preferred to use the crystal powder thus
isolated in the form of solid fine particle dispersion, because it
provides stable performance. Further, it is also preferred to use a
method of leading to form complex during dispersion by mixing the
reducing agent and the compound expressed by formula (D) in the
form of powders and dispersing them with a proper dispersion agent
using sand grinder mill or the like.
[0225] The compound expressed by formula (D) is preferably used in
a range from 1 mol % to 200 mol %, more preferably from 10 mol % to
150 mol %, and even more preferably, from 20 mol % to 100 mol %,
with respect to the reducing agent.
[0226] (Photosensitive Silver Halide)
[0227] 1) Halogen Composition For the photosensitive silver halide
used in the invention, there is no particular restriction on the
halogen composition and silver chloride, silver bromochloride,
silver bromide, silver iodobromide, silver iodochlorobromide, and
silver iodide can be used. Among them, silver bromide, silver
iodobromide, and silver iodide are preferred. The distribution of
the halogen composition in a grain may be uniform or the halogen
composition may be changed stepwise, or it may be changed
continuously. Further, a silver halide grain having a core/shell
structure can be used preferably. Preferred structure is a twofold
to fivefold structure and, more preferably, a core/shell grain
having a twofold to fourfold structure can be used. Further, a
technique of localizing silver bromide or silver iodide to the
surface of a silver chloride, silver bromide or silver
chlorobromide grains can also be used preferably.
2) Method of Grain Formation
[0228] The method of forming photosensitive silver halide is
well-known in the relevant art and, for example, methods described
in Research Disclosure No. 10729, June 1978 and U.S. Pat. No.
3,700,458 can be used. Specifically, a method of preparing a
photosensitive silver halide by adding a silver-supplying compound
and a halogen-supplying compound in a gelatin or other polymer
solution and then mixing them with an organic silver salt is used.
Further, a method described in JP-A No. 11-119374 (paragraph Nos.
0217 to 0224) and methods described in JP-A Nos. 11-352627 and
2000-347335 are also preferred.
[0229] 3) Grain Size
[0230] The grain size of the photosensitive silver halide is
preferably small with an aim of suppressing clouding after image
formation and, specifically, it is 0.20 .mu.m or less, more
preferably, in a range of from 0.01 .mu.m to 0.15 .mu.m and, even
more preferably, from 0.02 .mu.m to 0.12 .mu.m. The grain size as
used herein means an average diameter of a circle converted such
that it has a same area as a projected area of the silver halide
grain (projected area of a major plane in a case of a tabular
grain).
[0231] 4) Grain Shape
[0232] The shape of the silver halide grain can include, for
example, cubic, octahedral, tabular, spherical, rod-like, or
potato-like shape. The cubic grain is particularly preferred in the
invention. A silver halide grain rounded at corners can also be
used preferably. The surface indices (Miller indices) of the outer
surface of a photosensitive silver halide grain is not particularly
restricted, and it is preferable that the ratio occupied by the
{100} face is large, because of showing high spectral sensitization
efficiency when a spectral sensitizing dye is adsorbed. The ratio
is preferably 50% or higher, more preferably, 65% or higher and,
even more preferably, 80% or higher. The ratio of the {100} face,
Miller indices, can be determined by a method described in T. Tani;
J. Imaging Sci., vol. 29, page 165, (1985) utilizing adsorption
dependency of the {111} face and {100} face in adsorption of a
sensitizing dye.
[0233] 5) Heavy Metal
[0234] The photosensitive silver halide grain of the invention can
contain metals or complexes of metals belonging to groups 6 to 13
of the periodic table (showing groups 1 to 18). Preferred are
metals or complexes of metals belonging to groups 6 to 10. The
metal or the center metal of the metal complex from groups 6 to 10
of the periodic table is preferably rhodium, ruthenium, iridium, or
ferrum. The metal complex may be used alone, or two or more
complexes comprising identical or different species of metals may
be used together. A preferred content is in a range from
1.times.10.sup.-9 mol to 1.times.10.sup.-3 mol per 1 mol of silver.
The heavy metals, metal complexes and the adding method thereof are
described in JP-A No. 7-225449, in paragraph Nos. 0018 to 0024 of
JP-A No. 11-65021 and in paragraph Nos. 0227 to 0240 of JP-A No.
1-119374.
[0235] In the present invention, a silver halide grain having a
hexacyano metal complex present on the outermost surface of the
grain is preferred. The hexacyano metal complex includes, for
example, [Fe(CN).sub.6].sup.4-, [Fe(CN).sub.6].sup.3-,
[Ru(CN).sub.6].sup.4-, [Os(CN).sub.6].sup.4--[Co(CN).sub.6].sup.3-,
[Rh(CN).sub.6].sup.3-, [Ir(CN).sub.6].sup.3-,
[Cr(CN).sub.6].sup.3-, and [Re(CN).sub.6].sup.3-. In the invention,
hexacyano Fe complex is preferred.
[0236] Since the hexacyano complex exists in ionic form in an
aqueous solution, paired cation is not important and alkali metal
ion such as sodium ion, potassium ion, rubidium ion, cesium ion and
lithium ion, ammonium ion, alkyl ammonium ion (for example,
tetramethyl ammonium ion, tetraethyl ammonium ion, tetrapropyl
ammonium ion, and tetra(n-butyl)ammonium ion), which are easily
miscible with water and suitable to precipitation operation of a
silver halide emulsion are preferably used.
[0237] The hexacyano metal complex can be added while being mixed
with water, as well as a mixed solvent of water and an appropriate
organic solvent miscible with water (for example, alcohols, ethers,
glycols, ketones, esters, amides, or the like) or gelatin.
[0238] The addition amount of the hexacyano metal complex is
preferably from 1.times.10.sup.-5 mol to 1.times.10.sup.-2 mol and,
more preferably, from 1.times.10.sup.-4 mol to 1.times.10.sup.-3
mol, per 1 mol of silver in each case.
[0239] In order to allow the hexacyano metal complex to be present
on the outermost surface of a silver halide grain, the hexacyano
metal complex is directly added in any stage of: after completion
of addition of an aqueous solution of silver nitrate used for grain
formation, before completion of an emulsion formation step prior to
a chemical sensitization step, of conducting chalcogen
sensitization such as sulfur sensitization, selenium sensitization
and tellurium sensitization or noble metal sensitization such as
gold sensitization, during a washing step, during a dispersion step
and before a chemical sensitization step. In order not to grow fine
silver halide grains, the hexacyano metal complex is rapidly added
preferably after the grain is formed, and it is preferably added
before completion of the emulsion formation step.
[0240] Addition of the hexacyano complex may be started after
addition of 96% by weight of an entire amount of silver nitrate to
be added for grain formation, more preferably started after
addition of 98% by weight and, particularly preferably, started
after addition of 99% by weight.
[0241] When any of the hexacyano metal complex is added after
addition of an aqueous silver nitrate just before completion of
grain formation, it can be adsorbed to the outermost surface of the
silver halide grain and most of them form an insoluble salt with
silver ions on the surface of the grain. Since the hexacyano iron
(II) silver salt is a less soluble salt than AgI, re-dissolution
with fine grains can be prevented and fine silver halide grains
with smaller grain size can be prepared.
[0242] Metal atoms that can be contained in the silver halide grain
used in the invention (for example, [Fe(CN).sub.6].sup.4-),
desalting method of a silver halide emulsion and chemical
sensitizing method are described in paragraph Nos. 0046 to 0050 of
JP-A No. 11-84574, in paragraph Nos. 0025 to 0031 of JP-A No.
11-65021, and paragraph Nos. 0242 to 0250 of JP-A No.
11-119374.
[0243] 6) Gelatin
[0244] As the gelatin contained in the photosensitive silver halide
emulsion used in the invention, various kinds of gelatins can be
used. It is necessary to maintain an excellent dispersion state of
a photosensitive silver halide emulsion in an organic silver salt
containing coating solution, and gelatin having a molecular weight
of 10,000 to 1,000,000 is preferably used. Phthalated gelatin is
also preferably used. These gelatins may be used at grain formation
step or at the time of dispersion after desalting treatment and it
is preferably used at grain formation step.
[0245] 7) Sensitizing Dye
[0246] As the sensitizing dye applicable in the invention, those
capable of spectrally sensitizing silver halide grains in a desired
wavelength region upon adsorption to silver halide grains having
spectral sensitivity suitable to the spectral characteristic of an
exposure light source can be advantageously selected. The
sensitizing dyes and the adding method are disclosed, for example,
JP-A No. 11-65021 (paragraph Nos. 0103 to 0109), as a compound
represented by the formula (II) in JP-A No. 10-186572, dyes
represented by the formula (I) in JP-A No. 11-119374 (paragraph No.
0106), dyes described in U.S. Pat. Nos. 5,510,236 and 3,871,887
(Example 5), dyes disclosed in JP-A Nos. 2-96131 and 59-48753, as
well as in page 19, line 38 to page 20, line 35 of EP No.
0803764A1, and in JP-A Nos. 2001-272747, 2001-290238 and
2002-23306. The sensitizing dyes described above may be used alone
or two or more of them may be used in combination. In the
invention, sensitizing dye can be added preferably after a
desalting step and before coating, and more preferably after a
desalting step and before the completion of chemical ripening.
[0247] In the invention, the sensitizing dye may be added at any
amount according to the property of sensitivity and fogging, but it
is preferably added in an amount of from 10.sup.-6 mol to 1 mol,
and more preferably from 10.sup.-4 mol to 10.sup.-1 mol, per 1 mol
of silver halide in the image forming layer.
[0248] The photothermographic material of the invention can contain
super sensitizers in order to improve the spectral sensitizing
effect. The super sensitizers usable in the invention can include
those compounds described in EP-A No. 587338, U.S. Pat. Nos.
3,877,943 and 4,873,184, JP-A Nos. 5-341432, 11-109547, and
10.sup.-111543, and the like.
[0249] 8) Chemical Sensitization
[0250] The photosensitive silver halide grain in the invention is
preferably chemically sensitized by sulfur sensitizing method,
selenium sensitizing method or tellurium sensitizing method. As the
compound used preferably for sulfur sensitizing method, selenium
sensitizing method and tellurium sensitizing method, known
compounds, for example, compounds described in JP-A No. 7-128768
can be used. Particularly, tellurium sensitization is preferred in
the invention and compounds described in the literature cited in
paragraph No. 0030 in JP-A No. 11-65021 and compounds shown by
formulae (II), (III), and (IV) in JP-A No. 5-313284 are
preferred.
[0251] The photosensitive silver halide grain in the invention is
preferably chemically sensitized by gold sensitizing method alone
or in combination with the chalcogen sensitization described above.
As the gold sensitizer, those having an oxidation number of gold of
either +1 or +3 are preferred and those gold compounds used usually
as the gold sensitizer are preferred. As typical examples,
chloroauric acid, bromoauric acid, potassium chloroaurate,
potassium bromoaurate, auric trichloride, potassium auric
thiocyanate, potassium iodoaurate, tetracyanoauric acid, ammonium
aurothiocyanate and pyridyl trichloro gold are preferred. Further,
gold sensitizers described in U.S. Pat. No. 5,858,637 and JP-A No.
2002-278016 are also used preferably.
[0252] In the invention, chemical sensitization can be applied at
any time so long as it is after grain formation and before coating
and it can be applied, after desalting, (1) before spectral
sensitization, (2) simultaneously with spectral sensitization, (3)
after spectral sensitization, (4) just before coating, or the
like.
[0253] The amount of sulfur, selenium, or tellurium sensitizer used
in the invention may vary depending on the silver halide grain
used, the chemical ripening condition and the like and it is used
by about 10.sup.-8 mol to 10.sup.-2 mol, preferably, 10.sup.-7 mol
to 10.sup.-3 mol, per 1 mol of silver halide.
[0254] The addition amount of the gold sensitizer may vary
depending on various conditions and it is generally from 10.sup.-7
mol to 10.sup.-3 mol and, preferably from 10.sup.-6 mol to
5.times.10.sup.-4 mol, per 1 mol of silver halide.
[0255] There is no particular restriction on the condition for the
chemical sensitization in the invention and, appropriately, the pH
is from 5 to 8, the pAg is from 6 to 11, and the temperature is
from 40.degree. C. to 95.degree. C.
[0256] In the silver halide emulsion used in the invention, a
thiosulfonic acid compound may be added by the method shown in EP-A
No. 293,917.
[0257] A reductive compound is preferably used for the
photosensitive silver halide grain in the invention. As the
specific compound for the reduction sensitization, ascorbic acid or
thiourea dioxide is preferred, as well as use of stannous chloride,
aminoimino methane sulfonic acid, hydrazine derivatives, borane
compounds, silane compounds and polyamine compounds are preferred.
The reduction sensitizer may be added at any stage in the
photosensitive emulsion producing process from crystal growth to
the preparation step just before coating. Further, it is preferred
to apply reduction sensitization by ripening while keeping the pH
to 7 or higher or the pAg to 8.3 or lower for the emulsion, and it
is also preferred to apply reduction sensitization by introducing a
single addition portion of silver ions during grain formation.
[0258] 9) Compound that is One-Electron-Oxidized to Provide a
One-Electron Oxidation Product which Releases One or More
Electrons
[0259] The photothermographic material of the invention preferably
contains a compound that is one-electron-oxidized to provide a
one-electron oxidation product which releases one or more
electrons. The said compound can be used alone or in combination
with various chemical sensitizers described above to increase the
sensitivity of silver halide.
[0260] As the compound that is one-electron-oxidized to provide a
one-electron oxidation product which releases one or more electrons
is preferably a compound selected from the following Groups 1 or
2.
[0261] (Group 1) a compound that is one-electron-oxidized to
provide a one-electron oxidation product which further releases one
or more electrons, due to being subjected to a subsequent bond
cleavage reaction;
[0262] (Group 2) a compound that is one-electron-oxidized to
provide a one-electron oxidation product, which further releases
one or more electrons after being subjected to a subsequent bond
formation reaction.
[0263] The compound of Group 1 will be explained below.
[0264] In the compound of Group 1, as a compound is be
one-electron-oxidized to provide a one-electron oxidation product
which further releases one electron, due to being subjected to a
subsequent bond cleavage reaction, specific examples include
examples of compound referred to as "one photon two electrons
sensitizer" or "deprotonating electron-donating sensitizer"
described in JP-A No. 9-211769 (Compound PMT-1 to S-37 in Tables E
and F, pages 28 to 32); JP-A No. 9-211774; JP-A No. 11-95355
(Compound INV 1 to 36); JP-W No. 2001-500996 (Compound 1 to 74, 80
to 87, and 92 to 122); U.S. Pat. Nos. 5,747,235 and 5,747,236; EP
No. 786692A1 (Compound INV 1 to 35); EP No. 893732A1; U.S. Pat.
Nos. 6,054,260 and 5,994,051; etc. Preferred ranges of these
compounds are the same as the preferred ranges described in the
quoted specifications.
[0265] In the compound of Group 1, as a compound that is
one-electron-oxidized to provide a one-electron oxidation product
which further releases one or more electrons, due to being
subjected to a subsequent bond cleavage reaction, specific examples
include the compounds represented by formula (1) (same as formula
(1) described in JP-A No. 2003-114487), formula (2) (same as
formula (2) described in JP-A No. 2003-114487), formula (3) (same
as formula (1) described in JP-A No. 2003-114488), formula (4)
(same as formula (2) described in JP-A No. 2003-114488), formula
(5) (same as formula (3) described in JP-A No. 2003-114488),
formula (6) (same as formula (1) described in JP-A No. 2003-75950),
formula (7) (same as formula (2) described in JP-A No. 2003-75950),
and formula (8) (same as formula (1) described in JP-A No.
2004-239943), and the compound represented by formula (9) (same as
formula (3) described in JP-A No. 2004-245929) among the compounds
which can undergo the chemical reaction represented by chemical
reaction formula (1) (same as chemical reaction formula (1)
described in JP-A No. 2004-245929). And the preferable ranges of
these compounds are the same as the preferable ranges described in
the quoted specifications. ##STR61##
[0266] In formulae (1) and (2), RED.sub.1 and RED.sub.2 each
independently represent a reducing group. R.sub.1 represents a
nonmetallic atomic group forming a cyclic structure equivalent to a
tetrahydro derivative or an octahydro derivative of a 5- or
6-membered aromatic ring (including a hetero aromatic ring) with a
carbon atom (C) and RED.sub.1. R.sub.2, R.sub.3, and R.sub.4 each
independently represent a hydrogen atom or a substituent. Lv.sub.1
and Lv.sub.2 each independently represent a leaving group. ED
represents an electron-donating group. ##STR62##
[0267] In formulae (3), (4), and (5), Z, represents an atomic group
capable to form a 6-membered ring with a nitrogen atom and two
carbon atoms of a benzene ring. R.sub.5, R.sub.6, R.sub.7, R.sub.9,
R.sub.10, R.sub.11, R.sub.13, R.sub.14, R.sub.15, R.sub.16,
R.sub.17, R.sub.18, and R.sub.19 each independently represent a
hydrogen atom or a substituent. R.sub.20 represents a hydrogen atom
or a substituent, however, in the case where R.sub.20 represents a
group other than an aryl group, R.sub.16 and R.sub.17 bond to each
other to form an aromatic ring or a hetero aromatic ring. R.sub.8
and R.sub.12 represent a substituent capable of substituting for a
hydrogen atom on a benzene ring. m.sub.1 represents an integer of 0
to 3, and m2 represents an integer of 0 to 4. Lv.sub.3, Lv.sub.4,
and Lv.sub.5 each independently represent a leaving group.
##STR63##
[0268] In formulae (6) and (7), RED.sub.3 and RED.sub.4 each
independently represent a reducing group. R.sub.21 to R.sub.30 each
independently represent a hydrogen atom or a substituent. Z.sub.2
represents one selected from --CR.sub.111R.sub.112--,
--NR.sub.113--, or --O--. R.sub.111 and R.sub.112 each
independently represent a hydrogen atom or a substituent. R.sub.113
represents one selected from a hydrogen atom, an alkyl group, an
aryl group, or a heterocyclic group. ##STR64##
[0269] In formula (8), RED.sub.5 is a reducing group and represents
an arylamino group or a heterocyclic amino group. R.sub.31
represents a hydrogen atom or a substituent. X represents one
selected from an alkoxy group, an aryloxy group, a heterocyclic oxy
group, an alkylthio group, an arylthio group, a heterocyclic thio
group, an alkylamino group, an arylamino group, or a heterocyclic
amino group. Lv.sub.6 is a leaving group and represents a carboxy
group or a salt thereof, or a hydrogen atom. ##STR65##
[0270] The compound represented by formula (9) is a compound that
undergoes a bonding reaction represented by reaction formula (I)
after undergoing two-electrons-oxidation accompanied by
decarbonization and further oxidized. In reaction formula (1),
R.sub.32 and R.sub.33 represent a hydrogen atom or a substituent.
Z.sub.3 represents a group to form a 5- or 6-membered heterocycle
with C.dbd.C. Z.sub.4 represents a group to form a 5- or 6-membered
aryl group or heterocyclic group with C.dbd.C. M represents one
selected from a radical, a radical cation, and a cation. In formula
(9), R.sub.32, R.sub.33, and Z.sub.3 are the same as those in
reaction formula (1). Z.sub.5 represents a group to form a 5- or
6-membered cyclic aliphatic hydrocarbon group or heterocyclic group
with C--C.
[0271] Next, the compound of Group 2 is explained.
[0272] In the compound of Group 2, as a compound that is
one-electron-oxidized to provide a one-electron oxidation product
which further releases one or more electrons, after being subjected
to a subsequent bond cleavage reaction, specific examples can
include the compound represented by formula (10) (same as formula
(1) described in JP-A No. 2003-140287), and the compound
represented by formula (11) (same as formula (2) described in JP-A
No. 2004-245929) which can undergo the chemical reaction
represented by reaction formula (1) (same as chemical reaction
formula (1) described in JP-A No. 2004-245929). The preferable
ranges of these compounds are the same as the preferable ranges
described in the quoted specifications. RED.sub.6-Q-Y Formula
(10)
[0273] In formula (10), RED.sub.6 represents a reducing group which
can be one-electron-oxidized. Y represents a reactive group
containing a carbon-carbon double bond part, a carbon-carbon triple
bond part, an aromatic group part, or benzo-condensed nonaromatic
heterocyclic part which can react with one-electron-oxidized
product formed by one-electron-oxidation of RED.sub.6 to form a new
bond. Q represents a linking group to link RED.sub.6 and Y.
##STR66##
[0274] The compound represented by formula (11) is a compound that
undergoes a bonding reaction represented by reaction formula (1) by
being oxidized. In reaction formula (1), R.sub.32 and R.sub.33 each
independently represent a hydrogen atom or a substituent. Z.sub.3
represents a group to form a 5- or 6-membered heterocycle with
C.dbd.C. Z.sub.4 represents a group to form a 5- or 6-membered aryl
group or heterocyclic group with C.dbd.C. Z.sub.5 represents a
group to form a 5- or 6-membered cyclic aliphatic hydrocarbon group
or heterocyclic group with C--C. M represents one selected from a
radical, a radical cation, and a cation. In formula (II), R.sub.32,
R.sub.33, Z.sub.3, and Z.sub.4 are the same as those in reaction
formula (1).
[0275] The compounds of Groups 1 or 2 preferably are "the compound
having an adsorptive group to silver halide in a molecule" or "the
compound having a partial structure of a spectral sensitizing dye
in a molecule". The representative adsorptive group to silver
halide is the group described in JP-A No. 2003-156823, page 16
right, line 1 to page 17 right, line 12. A partial structure of a
spectral sensitizing dye is the structure described in JP-A No.
2003-156823, page 17 right, line 34 to page 18 right, line 6.
[0276] As the compound of Groups 1 or 2, "the compound having at
least one adsorptive group to silver halide in a molecule" is more
preferred, and "the compound having two or more adsorptive groups
to silver halide in a molecule" is further preferred. In the case
where two or more adsorptive groups exist in a single molecule,
those adsorptive groups may be identical or different from one
another.
[0277] As preferable adsorptive group, a mercapto-substituted
nitrogen-containing heterocyclic group (e.g., a 2-mercaptothiazole
group, a 3-mercapto-1,2,4-triazole group, a 5-mercaptotetrazole
group, a 2-mercapto-1,3,4-oxadiazole group, a 2-mercaptobenzoxazole
group, a 2-mercaptobenzothiazole group, a
1,5-dimethyl-1,2,4-triazolium-3-thiolate group, or the like) or a
nitrogen-containing heterocyclic group having --NH-group as a
partial structure of heterocycle capable to form a silver imidate
(--N(Ag)--) (e.g., a benzotriazole group, a benzimidazole group, an
indazole group, or the like) are described. A 5-mercaptotetrazole
group, a 3-mercapto-1,2,4-triazole group and a benzotriazole group
are particularly preferable, and a 3-mercapto-1,2,4-triazole group
and a 5-mercaptotetrazole group are most preferable.
[0278] As an adsorptive group, the group which has two or more
mercapto groups as a partial structure in a molecule is also
particularly preferable. Herein, a mercapto group (--SH) may become
a thione group in the case where it can tautomerize. Preferred
examples of an adsorptive group having two or more mercapto groups
as a partial structure (dimercapto-substituted nitrogen-containing
heterocyclic group and the like) are a 2,4-dimercaptopyrimidine
group, a 2,4-dimercaptotriazine group, and a
3,5-dimercapto-1,2,4-triazole group.
[0279] Further, a quaternary salt structure of nitrogen or
phosphorus is also preferably used as an adsorptive group. As
typical quaternary salt structure of nitrogen, an ammonio group (a
trialkylammonio group, a dialkylarylammonio group, a
dialkylheteroarylammonio group, an alkyldiarylammonio group, an
alkyldiheteroarylammonio group, or the like) and a
nitrogen-containing heterocyclic group containing quaternary
nitrogen atom can be used. As a quaternary salt structure of
phosphorus, a phosphonio group (a trialkylphosphonio group, a
dialkylarylphosphonio group, a dialkylheteroarylphosphonio group,
an alkyldiarylphosphonio group, an alkyldiheteroarylphosphonio
group, a triarylphosphonio group, a triheteroarylphosphonio group,
or the like) is described. A quaternary salt structure of nitrogen
is more preferably used and a 5- or 6-membered aromatic
heterocyclic group containing a quaternary nitrogen atom is further
preferably used. Particularly preferably, a pyrydinio group, a
quinolinio group and an isoquinolinio group are used. These
nitrogen-containing heterocyclic groups containing a quaternary
nitrogen atom may have any substituent.
[0280] Examples of counter anions of quaternary salt are a halogen
ion, carboxylate ion, sulfonate ion, sulfate ion, perchlorate ion,
carbonate ion, nitrate ion, BF.sub.4.sup.-, PF.sub.6.sup.-,
Ph.sub.4B.sup.-, and the like. In the case where the group having
negative charge at carboxylate group and the like exists in a
molecule, an inner salt may be formed with it. As a counter ion
outside of a molecule, chloro ion, bromo ion, and methanesulfonate
ion are particularly preferable.
[0281] The preferred structure of the compound represented by
Groups 1 or 2 having a quaternary salt of nitrogen or phosphorus as
an adsorptive group is represented by formula (X).
(P-Q.sub.1-).sub.i--R(-Q.sub.2-S).sub.j Formula (X)
[0282] In formula (X), P and R each independently represent a
quaternary salt structure of nitrogen or phosphorus, which is not a
partial structure of a spectral sensitizing dye. Q.sub.1 and
Q.sub.2 each independently represent a linking group and typically
represent a single bond, an alkylene group, an arylene group, a
heterocyclic group, --O--, --S--, --NR.sub.N, --C(.dbd.O)--,
--SO.sub.2--, --SO--, --P(.dbd.O)-- or combinations of these
groups. Herein, R.sub.N represents one selected from a hydrogen
atom, an alkyl group, an aryl group, or a heterocyclic group. S
represents a residue which is obtained by removing one atom from
the compound represented by Group 1 or 2. i and j are an integer of
one or more and are selected in a range of i+j=2 to 6. The case
where i is 1 to 3 and j is 1 to 2 is preferable, the case where i
is 1 or 2 and j is 1 is more preferable, and the case where i is 1
and j is 1 is particularly preferable. The compound represented by
formula (X) preferably has 10 to 100 carbon atoms in total, more
preferably 10 to 70 carbon atoms, further preferably 11 to 60
carbon atoms, and particularly preferably 12 to 50 carbon atoms in
total.
[0283] The compounds of Groups 1 or 2 may be used at any time
during preparation of the photosensitive silver halide emulsion and
production of the photothermographic material. For example, the
compound may be used in a photosensitive silver halide grain
formation step, in a desalting step, in a chemical sensitization
step, before coating, or the like. The compound may be added in
several times during these steps. The compound is preferably added
after the photosensitive silver halide grain formation step and
before the desalting step; at the chemical sensitization step (just
before the chemical sensitization to immediately after the chemical
sensitization); or before coating. The compound is more preferably
added from at the chemical sensitization step to before being mixed
with non-photosensitive organic silver salt.
[0284] It is preferred that the compound of Groups 1 or 2 according
to the invention is dissolved in water, a water-soluble solvent
such as methanol or ethanol, or a mixed solvent thereof. In the
case where the compound is dissolved in water and solubility of the
compound is increased by increasing or decreasing a pH value of the
solvent, the pH value may be increased or decreased to dissolve and
add the compound.
[0285] The compound of Groups 1 or 2 according to the invention is
preferably used in the image forming layer which contains the
photosensitive silver halide and the non-photosensitive organic
silver salt. The compound may be added to a surface protective
layer, or an intermediate layer, as well as the image forming layer
containing the photosensitive silver halide and the
non-photosensitive organic silver salt, to be diffused to the image
forming layer in the coating step. The compound may be added before
or after addition of a sensitizing dye. Each compound is contained
in the image forming layer preferably in an amount of from
1.times.10.sup.-9 mol to 5.times.10.sup.-1 mol, more preferably
from 1.times.10.sup.-8 mol to 5.times.10.sup.-2 mol, per 1 mol of
silver halide.
[0286] 10) Compound Having Adsorptive Group and Reducing Group
[0287] The photothermographic material of the present invention
preferably comprises a compound having an adsorptive group to
silver halide and a reducing group in a molecule. It is preferred
that the compound is represented by the following formula (I).
A-(W)n-B Formula (I)
[0288] In formula (I), A represents a group capable of adsorption
to a silver halide (hereafter, it is called an adsorptive group); W
represents a divalent linking group; n represents 0 or 1; and B
represents a reducing group.
[0289] In formula (I), the adsorptive group represented by A is a
group to adsorb directly to a silver halide or a group to promote
adsorption to a silver halide. As typical examples, a mercapto
group (or a salt thereof), a thione group (--C(.dbd.S)--), a
nitrogen atom, a heterocyclic group containing at least one atom
selected from a nitrogen atom, a sulfur atom, a selenium atom, or a
tellurium atom, a sulfide group, a disulfide group, a cationic
group, an ethynyl group, and the like are described.
[0290] The mercapto group (or the salt thereof) as an adsorptive
group means a mercapto group (or a salt thereof) itself and
simultaneously more preferably represents a heterocyclic group or
an aryl group or an alkyl group substituted by at least one
mercapto group (or a salt thereof). Herein, as the heterocyclic
group, a monocyclic or a condensed aromatic or nonaromatic
heterocyclic group having at least a 5- to 7-membered ring, for
example, an imidazole ring group, a thiazole ring group, an oxazole
ring group, a benzimidazole ring group, a benzothiazole ring group,
a benzoxazole ring group, a triazole ring group, a thiadiazole ring
group, an oxadiazole ring group, a tetrazole ring group, a purine
ring group, a pyridine ring group, a quinoline ring group, an
isoquinoline ring group, a pyrimidine ring group, a triazine ring
group, and the like are described. A heterocyclic group having a
quaternary nitrogen atom may also be adopted, wherein a mercapto
group as a substituent may dissociate to form a mesoion. When the
mercapto group forms a salt, a counter ion of the salt may be a
cation of an alkaline metal, an alkaline earth metal, a heavy
metal, or the like, such as Li.sup.+, Na.sup.+, K.sup.+, Mg.sup.2+,
Ag.sup.+ and Zn.sup.2+; an ammonium ion; a heterocyclic group
containing a quaternary nitrogen atom; a phosphonium ion; or the
like.
[0291] Further, the mercapto group as an adsorptive group may
become a thione group by a tautomerization.
[0292] The thione group used as the adsorptive group also includes
a linear or cyclic thioamide group, thioureido group, thiourethane
group, and dithiocarbamate ester group.
[0293] The heterocyclic group, as an adsorptive group, which
contains at least one atom selected from a nitrogen atom, a sulfur
atom, a selenium atom, or a tellurium atom represents a
nitrogen-containing heterocyclic group having --NH-- group, as a
partial structure of a heterocycle, capable to form a silver
iminate (--N(Ag)--) or a heterocyclic group, having an --S-- group,
a --Se-- group, a --Te-- group or a .dbd.N-- group as a partial
structure of a heterocycle, and capable to coordinate to a silver
ion by a chelate bonding. As the former examples, a benzotriazole
group, a triazole group, an indazole group, a pyrazole group, a
tetrazole group, a benzimidazole group, an imidazole group, a
purine group, and the like are described. As the latter examples, a
thiophene group, a thiazole group, an oxazole group, a
benzothiophene group, a benzothiazole group, a benzoxazole group, a
thiadiazole group, an oxadiazole group, a triazine group, a
selenoazole group, a benzoselenoazole group, a tellurazole group, a
benzotellurazole group, and the like are described.
[0294] The sulfide group or disulfide group as an adsorptive group
contains all groups having "--S--" or "--S--S--" as a partial
structure.
[0295] The cationic group as an adsorptive group means the group
containing a quaternary nitrogen atom, such as an ammonio group or
a nitrogen-containing heterocyclic group including a quaternary
nitrogen atom. As examples of the heterocyclic group containing a
quaternary nitrogen atom, a pyridinio group, a quinolinio group, an
isoquinolinio group, an imidazolio group, and the like are
described.
[0296] The ethynyl group as an adsorptive group means --C.ident.CH
group and the said hydrogen atom may be substituted.
[0297] The adsorptive group described above may have any
substituent.
[0298] Further, as typical examples of an adsorptive group, the
compounds described in pages 4 to 7 in the specification of JP-A
No. 11-95355 are described.
[0299] As an adsorptive group represented by A in formula (1), a
heterocyclic group substituted by a mercapto group (e.g., a
2-mercaptothiadiazole group, a 2-mercapto-5-aminothiadiazole group,
a 3-mercapto-1,2,4-triazole group, a 5-mercaptotetrazole group, a
2-mercapto-1,3,4-oxadiazole group, a 2-mercaptobenzimidazole group,
a 1,5-dimethyl-1,2,4-triazorium-3-thiolate group, a
2,4-dimercaptopyrimidine group, a 2,4-dimercaptotriazine group, a
3,5-dimercapto-1,2,4-triazole group, a 2,5-dimercapto-1,3-thiazole
group, or the like) and a nitrogen atom containing heterocyclic
group having an --NH-- group capable to form an imino-silver
(--N(Ag)--) as a partial structure of heterocycle (e.g., a
benzotriazole group, a benzimidazole group, an indazole group, or
the like) are preferable, and more preferable as an adsorptive
group are a 2-mercaptobenzimidazole group and a
3,5-dimercapto-1,2,4-triazole group.
[0300] In formula (I), W represents a divalent linking group. The
said linking group may be any divalent linking group, as far as it
does not give a bad effect toward photographic properties. For
example, a divalent linking group which includes a carbon atom, a
hydrogen atom, an oxygen atom, a nitrogen atom, or a sulfur atom,
can be used. As typical examples, an alkylene group having 1 to 20
carbon atoms (e.g., a methylene group, an ethylene group, a
trimethylene group, a tetramethylene group, a hexamethylene group,
or the like), an alkenylene group having 2 to 20 carbon atoms, an
alkynylene group having 2 to 20 carbon atoms, an arylene group
having 6 to 20 carbon atoms (e.g., a phenylene group, a naphthylene
group, or the like), --CO--, --SO.sub.2--, --O--, --S--,
--NR.sub.1--, and the combinations of these linking groups are
described. Herein, R.sub.1 represents a hydrogen atom, an alkyl
group, a heterocyclic group, or an aryl group.
[0301] The linking group represented by W may have any
substituent.
[0302] In formula (I), a reducing group represented by B represents
the group capable to reduce a silver ion. As the examples, a formyl
group, an amino group, a triple bond group such as an acetylene
group, a propargyl group and the like, a mercapto group, and
residues which are obtained by removing one hydrogen atom from
hydroxyamines, hydroxamic acids, hydroxyureas, hydroxyurethanes,
hydroxysemicarbazides, reductones (reductone derivatives are
contained), anilines, phenols (chroman-6-ols,
2,3-dihydrobenzofuran-5-ols, aminophenols, sulfonamidophenols, and
polyphenols such as hydroquinones, catechols, resorcinols,
benzenetriols, bisphenols are included), acylhydrazines,
carbamoylhydrazines, 3-pyrazolidones, and the like can be
described. They may have any substituent.
[0303] The oxidation potential of a reducing group represented by B
in formula (I), can be measured by using the measuring method
described in Akira Fujishima, "DENKIKAGAKU SOKUTEIHO", pages 150 to
208, GIHODO SHUPPAN and The Chemical Society of Japan, "ZIKKEN
KAGAKUKOZA", 4th ed., vol. 9, pages 282 to 344, MARUZEN. For
example, the method of rotating disc voltammetry can be used;
namely the sample is dissolved in the solution (methanol:pH 6.5
Britton-Robinson buffer=10%:90% (% by volume)) and after bubbling
with nitrogen gas during 10 minutes the voltamograph can be
measured under the conditions of 1000 rotations/minute, the sweep
rate 20 mV/second, at 25.degree. C. by using a rotating disc
electrode (RDE) made by glassy carbon as a working electrode, a
platinum electrode as a counter electrode and a saturated calomel
electrode as a reference electrode. The half wave potential (E1/2)
can be calculated by that obtained voltamograph.
[0304] When a reducing group represented by B in the present
invention is measured by the method described above, an oxidation
potential is preferably in a range of from about -0.3 V to about
1.0 V, more preferably from about -0.1 V to about 0.8 V, and
particularly preferably from about 0 V to about 0.7 V.
[0305] In formula (I), a reducing group represented by B is
preferably a residue which is obtained by removing one hydrogen
atom from hydroxyamines, hydroxamic acids, hydroxyureas,
hydroxysemicarbazides, reductones, phenols, acylhydrazines,
carbamoylhydrazines, or 3-pyrazolidones.
[0306] The compound of formula (I) according to the present
invention may have the ballasted group or polymer chain in it
generally used in the non-moving photographic additives as a
coupler. And as a polymer, for example, the polymer described in
JP-A No. 1-100530 can be selected.
[0307] The compound of formula (I) according to the present
invention may be bis or tris type of compound. The molecular weight
of the compound represented by formula (I) according to the present
invention is preferably from 100 to 10000, more preferably from 120
to 1000, and particularly preferably from 150 to 500.
[0308] The examples of the compound represented by formula (I)
according to the present invention are shown below, but the present
invention is not limited in these. ##STR67## ##STR68##
##STR69##
[0309] Further, example compounds 1 to 30 and 1''-1 to 1''-77 shown
in EP No. 1308776A2, pages 73 to 87 are also described as
preferable examples of the compound having an adsorptive group and
a reducing group according to the invention.
[0310] These compounds can be easily synthesized by any known
method. The compound of formula (I) according to the present
invention can be used alone, but it is preferred to use two or more
of the compounds in combination. When two or more of the compounds
are used in combination, those may be added to the same layer or
the different layers, whereby adding methods may be different from
one another.
[0311] The compound represented by formula (I) according to the
present invention is preferably added to an image forming layer and
more preferably is to be added at an emulsion preparing process. In
the case, where these compounds are added at an emulsion preparing
process, these compounds may be added at any step in the process.
For example, the compounds may be added during the silver halide
grain formation step, the step before starting of desalting step,
the desalting step, the step before starting of chemical ripening,
the chemical ripening step, the step before preparing a final
emulsion, or the like. The compound can be added in several times
during these steps. It is preferred to be added in the image
forming layer. But the compound may be added to a surface
protective layer or an intermediate layer, in combination with its
addition to the image forming layer, to be diffused to the image
forming layer in the coating step.
[0312] The preferred addition amount is largely dependent on the
adding method described above or the kind of the compound, but
generally from 1.times.10.sup.-6 mol to 1 mol, preferably from
1.times.10.sup.-5 mol to 5.times.10.sup.-1 mol, and more preferably
from 1.times.10.sup.-4 mol to 1.times.10.sup.-1 mol, per 1 mol of
photosensitive silver halide in each case.
[0313] The compound represented by formula (I) according to the
present invention can be added by dissolving in water or
water-soluble solvent such as methanol, ethanol and the like or a
mixed solution thereof. At this time, the pH may be arranged
suitably by an acid or an alkaline and a surfactant can coexist.
Further, these compounds can be added as an emulsified dispersion
by dissolving them in an organic solvent having a high boiling
point and also can be added as a solid dispersion.
[0314] 11) Combined Use of a Plurality of Silver Halides
[0315] The photosensitive silver halide emulsion in the
photothermographic material used in the invention may be used
alone, or two or more of them (for example, those of different
average particle sizes, different halogen compositions, of
different crystal habits and of different conditions for chemical
sensitization) may be used together. Gradation can be controlled by
using plural photosensitive silver halides of different
sensitivity. The relevant techniques can include those described,
for example, in JP-A Nos. 57-119341, 53-106125, 47-3929, 48-55730,
46-5187, 50-73627, and 57-150841. It is preferred to provide a
sensitivity difference of 0.2 or more in terms of log E between
each of the emulsions.
[0316] 12) Coating Amount
[0317] The addition amount of the photosensitive silver halide,
when expressed by the amount of coated silver per 1 m.sup.2 of the
photothermographic material, is preferably from 0.03 g/m.sup.2 to
0.6 g/m.sup.2, more preferably, from 0.05 g/m.sup.2 to 0.4
g/m.sup.2 and, most preferably, from 0.07 g/m.sup.2 to 0.3
g/m.sup.2. The photosensitive silver halide is used in a range of
from 0.01 mol to 0.5 mol, preferably, from 0.02 mol to 0.3 mol, and
even more preferably from 0.03 mol to 0.2 mol, per 1 mol of the
organic silver salt.
[0318] 13) Mixing Photosensitive Silver Halide and Organic Silver
Salt
[0319] The method of mixing separately prepared the photosensitive
silver halide and the organic silver salt can include a method of
mixing prepared photosensitive silver halide grains and organic
silver salt by a high speed stirrer, ball mill, sand mill, colloid
mill, vibration mill, or homogenizer, or a method of mixing a
photosensitive silver halide completed for preparation at any
timing in the preparation of an organic silver salt and preparing
the organic silver salt. The effect of the invention can be
obtained preferably by any of the methods described above. Further,
a method of mixing two or more aqueous dispersions of organic
silver salts and two or more aqueous dispersions of photosensitive
silver salts upon mixing is used preferably for controlling the
photographic properties.
[0320] 14) Mixing Silver Halide into Coating Solution
[0321] In the invention, the time of adding silver halide to the
coating solution for the image forming layer is preferably in a
range of from 180 minutes before to just prior to the coating, more
preferably, 60 minutes before to 10 seconds before coating. But
there is no restriction for mixing method and mixing condition as
long as the effect of the invention is sufficient. As an embodiment
of a mixing method, there is a method of mixing in a tank and
controlling an average residence time. The average residence time
herein is calculated from addition flux and the amount of solution
transferred to the coater. And another embodiment of mixing method
is a method using a static mixer, which is described in 8th edition
of "Ekitai Kongo Gijutu" by N. Harnby and M. F. Edwards, translated
by Koji Takahashi (Nikkan Kogyo Shinbunsha, 1989).
[0322] (Antifoggant)
[0323] As an antifoggant, stabilizer and stabilizer precursor
usable in the invention, there can be mentioned those disclosed as
patents in paragraph number 0070 of JP-A No. 10--62899 and in line
57 of page 20 to line 7 of page 21 of EP-A No. 0803764A1, the
compounds described in JP-A Nos. 9-281637 and 9-329864, in U.S.
Pat. No. 6,083,681, and in EP-A No. 1048975. Furthermore, the
antifoggant preferably used in the invention is an organic halogen
compound, and those disclosed in paragraph Nos. 0111 to 0112 of
JP-A No. 11-65021 can be enumerated as examples thereof. In
particular, the organic halogen compound expressed by formula (P)
in JP-A No. 2000-284399, the organic polyhalogen compound expressed
by formula (II) in JP-A No. 10--339934, and organic polyhalogen
compounds described in JP-A Nos. 2001-31644 and 2001-33911 are
preferred.
[0324] 1) Organic Polyhalogen Compound
[0325] Preferable organic polyhalogen compound that is used in the
invention is explained specifically below. In the invention,
preferred organic polyhalogen compound is the compound expressed by
the following formula (H). Q-(Y)n-C(Z.sub.1)(Z.sub.2)X Formula
(H)
[0326] In formula (H), Q represents one selected from an alkyl
group, an aryl group, or a heterocyclic group; Y represents a
divalent linking group; n represents 0 or 1; Z.sub.1 and Z.sub.2
each represent a halogen atom; and X represents a hydrogen atom or
an electron-attracting group.
[0327] In formula (H), Q is preferably an aryl group, or a
heterocyclic group.
[0328] In formula (H), in the case where Q is a heterocyclic group,
Q is preferably a nitrogen-containing heterocyclic group having 1
or 2 nitrogen atoms, and particularly preferably a 2-pyridyl group
or a 2-quinolyl group.
[0329] In formula (H), in the case where Q is an aryl group, Q
preferably is a phenyl group substituted by an electron-attracting
group whose Hammett substituent coefficient .sigma. p yields a
positive value. For the details of Hammett substituent coefficient,
reference can be made to Journal of Medicinal Chemistry, vol. 16,
No. 11 (1973), pp. 1207 to 1216, and the like. As such
electron-attracting group, examples include, halogen atoms
(fluorine atom (.sigma. p value: 0.06), chlorine atom (.sigma. p
value: 0.23), bromine atom (a p value: 0.23), iodine atom (.sigma.
p value: 0.18)), trihalomethyl groups (tribromomethyl (.sigma. p
value: 0.29), trichloromethyl (.sigma. p value: 0.33),
trifluoromethyl (.sigma. p value: 0.54)), a cyano group (.sigma. p
value: 0.66), a nitro group (.sigma. p value: 0.78), an aliphatic
aryl sulfonyl group or a heterocyclic sulfonyl group (for example,
methanesulfonyl (.sigma. p value: 0.72)), an aliphatic aryl acyl
group or a heterocyclic acyl group (for example, acetyl (.sigma. p
value: 0.50) and benzoyl (.sigma. p value: 0.43)), an alkynyl
(e.g., C.ident.CH (.sigma. p value: 0.23)), an aliphatic aryl
oxycarbonyl group or a heterocyclic oxycarbonyl group (for example,
methoxycarbonyl (.sigma. p value: 0.45) and phenoxycarbonyl
(.sigma. p value: 0.44)), a carbamoyl group (.sigma. p value:
0.36), a sulfamoyl group (.sigma. p value: 0.57), a sulfoxido
group, a heterocyclic a group, a phosphoryl group, and the like.
Preferred range of the a p value is from 0.2 to 2.0, and more
preferably, from 0.4 to 1.0. Particularly preferred as the
electron-attracting groups are a carbamoyl group, an alkoxycarbonyl
group, an alkylsulfonyl group, and an alkylphosphoryl group, and
most preferred among them is a carbamoyl group.
[0330] X is preferably an electron-attracting group, and more
preferably, a halogen atom, an aliphatic aryl sulfonyl group, a
heterocyclic sulfonyl group, an aliphatic aryl acyl group, a
heterocyclic acyl group, an aliphatic aryl oxycarbonyl group, a
heterocyclic oxycarbonyl group, a carbamoyl group, or a sulfamoyl
group; particularly preferred among them is a halogen atom. Among
halogen atoms, preferred are chlorine atom, bromine atom, and
iodine atom; more preferred are chlorine atom and bromine atom; and
particularly preferred is bromine atom.
[0331] Y preferably represents --C(.dbd.O)--, --SO--, or
--SO.sub.2--; more preferably, --C(.dbd.O)-- or --SO.sub.2--; and
particularly preferred is --SO.sub.2--. n represents 0 or 1, and
preferably represents 1.
[0332] Specific examples of the compounds expressed by formula (H)
of the invention are shown below. ##STR70## ##STR71##
[0333] As preferred organic polyhalogen compounds of the invention
other than those above, there can be mentioned compounds disclosed
in JP-A Nos. 2001-31644, 2001-56526, and 2001-209145.
[0334] The coating amount of the organic polyhalogen compound is
preferably in a range of from 0.01 g/m.sup.2 to 0.5 g/m.sup.2, more
preferably from 0.01 g/m.sup.2 to 0.4 g/m.sup.2, and even more
preferably from 0.01 g/m.sup.2 to 0.3 g/m.sup.2. When the coating
amount exceeds 0.5 g/m.sup.2 or more, sensitivity decreases
significantly and it is not preferred.
[0335] The compounds expressed by formula (H) of the invention are
preferably used in an amount of from 10.sup.-4 mol to 1 mol, more
preferably from 10.sup.-3 mol to 0.5 mol, and even more preferably
from 1.times.10.sup.-2 mol to 0.2 mol, per 1 mol of
non-photosensitive silver salt incorporated in the image forming
layer.
[0336] In the invention, usable methods for incorporating the
antifoggant into the photosensitive material are those described
above in the method for incorporating the reducing agent.
Furthermore, the organic polyhalogen compound is also preferably
used in the form of solid fine particle dispersion.
[0337] 2) Other Antifoggants
[0338] As other antifoggants, there can be mentioned a mercury (II)
salt described in paragraph number 0113 of JP-A No. 11-65021,
benzoic acids described in paragraph number 0114 of the same
literature, a salicylic acid derivative described in JP-A No.
2000-206642, a formalin scavenger compound expressed by formula (S)
in JP-A No. 2000-221634, a triazine compound related to Claim 9 of
JP-A No. 11-352624, a compound expressed by formula (III),
4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene and the like, described
in JP-A No. 6-11791.
[0339] The photothermographic material of the invention may further
contain an azolium salt in order to prevent fogging. Azolium salts
useful in the present invention include a compound expressed by
formula (XI) described in JP-A No. 59-193447, a compound described
in JP-B No. 55-12581, and a compound expressed by formula (II) in
JP-A No. 60-153039. The azolium salt may be added to any part of
the photothermographic material, but as an additional layer, it is
preferred to select a layer on the side having thereon the image
forming layer, and more preferred is to select the image forming
layer itself. The azolium salt may be added at any time of the
process of preparing the coating solution; in the case where the
azolium salt is added into the image forming layer, any time of the
process may be selected, from the preparation of the organic silver
salt to the preparation of the coating solution, but preferred is
to add the salt after preparing the organic silver salt and just
before coating. As the method for adding the azolium salt, any
method using a powder, a solution, a fine-particle dispersion, and
the like, may be used. Further, it may be added as a solution
having mixed therein other additives such as sensitizing agents,
reducing agents, toners, and the like. In the invention, the
azolium salt may be added at any amount, but preferably, it is
added in a range of from 1.times.10.sup.-6 mol to 2 mol, and more
preferably, from 1.times.10.sup.-3 mol to 0.5 mol, per 1 mol of
silver.
[0340] (Other Additives)
[0341] 1) Mercapto Compounds, Disulfides and Thiones
[0342] In the invention, mercapto compounds, disulfide compounds,
and thione compounds can be added in order to control the
development by suppressing or enhancing development, to improve
spectral sensitization efficiency, and to improve storage
properties before and after development. Descriptions can be found
in paragraph numbers 0067 to 0069 of JP-A No. 10--62899, a compound
expressed by formula (1) of JP-A No. 10--186572 and specific
examples thereof shown in paragraph numbers 0033 to 0052, in lines
36 to 56 in page 20 of EP No. 0803764A1. Among them,
mercapto-substituted heterocyclic aromatic compounds described in
JP-A Nos. 9-297367, 9-304875, 2001-100358, 2002-303954, and
2002-303951, and the like are preferred.
[0343] 2) Toner
[0344] In the photothermographic material of the present invention,
the addition of a toner is preferred. Description on the toner can
be found in JP-A No. 10-62899 (paragraph numbers 0054 to 0055), EP
No. 0803764A1 (page 21, lines 23 to 48), JP-A Nos. 2000-356317 and
2000-187298. Preferred are phthalazinones (phthalazinone,
phthalazinone derivatives and metal salts thereof, (e.g.,
4-(1-naphthyl)phthalazinone, 6-chlorophthalazinone,
5,7-dimethoxyphthalazinone, and 2,3-dihydro-1,4-phthalazinedione);
combinations of phthalazinones and phthalic acids (e.g., phthalic
acid, 4-methylphthalic acid, 4-nitrophthalic acid, diammonium
phthalate, sodium phthalate, potassium phthalate, and
tetrachlorophthalic anhydride); phthalazines (phthalazine,
phthalazine derivatives and metal salts thereof, (e.g.,
4-(1-naphthyl)phthalazine, 6-isopropylphthalazine,
6-tert-butylphthalazine, 6-chlorophthalazine,
5,7-dimethoxyphthalazine, and 2,3-dihydrophthalazine); combinations
of phthalazines and phthalic acids. Particularly preferred is a
combination of phthalazines and phthalic acids. Among them,
particularly preferable are the combination of
6-isopropylphthalazine and phthalic acid, and the combination of
6-isopropylphthalazine and 4-methylphthalic acid.
[0345] 3) Plasticizer and Lubricant
[0346] Plasticizers and lubricants usable in the image forming
layer of the invention are described in paragraph No. 0117 of JP-A
No. 11-65021. Lubricants are described in paragraph Nos. 0061 to
0064 of JP-A No. 11-84573.
[0347] 4) Nucleator
[0348] Concerning the photothermographic material of the invention,
it is preferred to add a nucleator into the image forming layer.
Details on the nucleators, method for their addition and addition
amount can be found in paragraph No. 0118 of JP-A No. 11-65021,
paragraph Nos. 0136 to 0193 of JP-A No. 11-223898, as compounds
expressed by formulae (H), (1) to (3), (A), and (B) in JP-A No.
2000-284399; as for a nucleation accelerator, description can be
found in paragraph No. 0102 of JP-A No. 11-65021, and in paragraph
Nos. 0194 to 0195 of JP-A No. 11-223898.
[0349] In the case of using formic acid or formates as a strong
fogging agent, it is preferably incorporated into the side having
thereon the image forming layer containing photosensitive silver
halide in an amount of 5 mmol or less, and more preferably 1 mmol
or less, per 1 mol of silver.
[0350] In the case of using a nucleator in the photothermographic
material of the invention, it is preferred to use an acid resulting
from hydration of diphosphorus pentaoxide, or a salt thereof in
combination. Acids resulting from the hydration of diphosphorus
pentaoxide or salts thereof include metaphosphoric acid (salt),
pyrophosphoric acid (salt), orthophosphoric acid (salt),
triphosphoric acid (salt), tetraphosphoric acid (salt),
hexametaphosphoric acid (salt), and the like. Particularly
preferred acids obtainable by the hydration of diphosphorus
pentaoxide or salts thereof include orthophosphoric acid (salt) and
hexametaphosphoric acid (salt). Specifically mentioned as the salts
are sodium orthophosphate, sodium dihydrogen orthophosphate, sodium
hexametaphosphate, ammonium hexametaphosphate, and the like.
[0351] The addition amount of the acid obtained by hydration of
diphoshorus pentaoxide or the salt thereof (i.e., the coating
amount per 1 m.sup.2 of the photothermographic material) may be set
as desired depending on sensitivity and fogging, but preferred is
an amount of from 0.1 mg/m.sup.2 to 500 mg/m.sup.2, and more
preferably, from 0.5 mg/m.sup.2 to 100 mg/m.sup.2.
[0352] (Preparation of Coating Solution and Coating)
[0353] The temperature for preparing the coating solution for the
image forming layer of the invention is preferably from 30.degree.
C. to 65.degree. C., more preferably, 35.degree. C. or more and
less than 60.degree. C., and further preferably, from 35.degree. C.
to 55.degree. C. Furthermore, the temperature of the coating
solution for the image forming layer immediately after adding the
polymer latex is preferably maintained in the temperature range
from 30.degree. C. to 65.degree. C.
[0354] (Layer Constitution and Constituent Components)
[0355] The non-photosensitive layers of the photothermographic
material according to the invention can be classified depending on
the layer arrangement into (a) a surface protective layer provided
on the image forming layer (on the side farther from the support),
(b) an intermediate layer provided among plural image forming
layers or between the image forming layer and the protective layer,
(c) an undercoat layer provided between the image forming layer and
the support, and (d) a back layer which is provided on the side
opposite to the image forming layer.
[0356] Furthermore, a layer that functions as an optical filter may
be provided as (a) or (b) above. An antihalation layer may be
provided as (c) or (d) to the photothermographic material. Dyes to
prevent irradiation are preferably contained in the
non-photosensitive layer on the side having thereon the image
forming layer as well as in the image forming layer.
[0357] 1) Surface Protective Layer
[0358] The photothermographic material of the invention may further
comprise a surface protective layer with an object to prevent
adhesion of the image forming layer. The surface protective layer
may be a single layer, or plural layers.
[0359] Description on the surface protective layer may be found in
paragraph Nos. 0119 to 0120 of JP-A No. 11-65021 and in JP-A No.
2000-171936.
[0360] Preferred as the binder of the surface protective layer of
the invention is gelatin, but poly(vinyl alcohol) (PVA) may be used
preferably instead, or in combination. As gelatin, there can be
used an inert gelatin (e.g., Nitta gelatin 750), a phthalated
gelatin (e.g., Nitta gelatin 801), and the like. Usable as PVA are
those described in paragraph Nos. 0009 to 0020 of JP-A No.
2000-171936, and preferred are the completely saponified product
PVA-105, the partially saponified PVA-205, and PVA-335, as well as
modified poly(vinyl alcohol) MP-203 (all trade name of products
from Kuraray Ltd.). The amount of coated poly(vinyl alcohol) (per 1
m.sup.2 of support) in the surface protective layer (per one layer)
is preferably in a range of from 0.3 g/m.sup.2 to 4.0 g/m.sup.2,
and more preferably, from 0.3 g/m to 2.0 g/m.sup.2.
[0361] The total amount of the coated binder (including
water-soluble polymer and latex polymer) (per 1 m.sup.2 of support)
in the surface protective layer (per one layer) is preferably in a
range of from 0.3 g/m.sup.2 to 5.0 g/m.sup.2, and more preferably,
from 0.3 g/m.sup.2 to 2.0 g/m.sup.2.
[0362] 2) Back Layer
[0363] The photothermographic material of the invention is
preferably a so-called one-side photosensitive material, which
comprises at least one layer of a image forming layer containing
silver halide emulsion on one side of the support, and a back layer
on the other side.
[0364] Back layers usable in the invention are described in
paragraph Nos. 0128 to 0130 of JP-A No. 11-65021.
[0365] The back layer can include an antihalation dye. Dyes which
have a light absorption characteristic corresponding to the
wavelength region of the imagewise exposure can be selectively used
as the antihalation dye. In the case where the light source for
exposing is within the visible region of from green to red, the
metal phthalocyanine compound represented by formula (PC-1)
described above is preferably employed.
[0366] In the invention, coloring matters having maximum absorption
in the wavelength range from 300 nm to 450 nm can be added in order
to improve color tone of developed silver images and a
deterioration of the images during aging. Such coloring matters are
described in, for example, JP-A Nos. 62-210458, 63-104046,
63-103235, 63-208846, 63-306436, 63-314535, 01-61745, 2001-100363,
and the like.
[0367] Such coloring matters are generally added in a range of from
0.1 mg/m.sup.2 to 1 g/m.sup.2, preferably to the back layer which
is provided to the opposite side of the support from the image
forming layer.
[0368] Further, in order to control the basic color tone, it is
preferred to use a dye having an absorption peak in a wavelength
range from 580 nm to 680 nm. As a dye satisfying this purpose,
preferred are oil-soluble azomethine dyes described in JP-A Nos.
4-359967 and 4-359968, or water-soluble phthalocyanine dyes
described in JP-A No. 2003-295388, which have low absorption
intensity on the short wavelength side. The dyes for this purpose
may be added to any of the layers, but more preferred is to add
them in the non-photosensitive layer on the image forming side, or
in the back side.
[0369] 3) Matting Agent
[0370] A matting agent is preferably added to the
photothermographic material of the invention in order to improve
transportability. Description on the matting agent can be found in
paragraphs Nos. 0126 to 0127 of JP-A No. 11-65021. The addition
amount of the matting agent is preferably in a range from 1
mg/m.sup.2 to 400 mg/m.sup.2, and more preferably, from 5
mg/m.sup.2 to 300 mg/m.sup.2, with respect to the coating amount
per 1 ml of the photothermographic material.
[0371] The shape of the matting agent usable in the invention may
fixed form or non-fixed form. Preferred is to use those having
fixed form and globular shape. The mean particle diameter is
preferably in a range of from 0.5 .mu.m to 10 .mu.m, more
preferably, from 1.0 .mu.m to 8.0 .mu.m, and further preferably,
from 2.0 .mu.m to 6.0 .mu.m. Furthermore, the particle size
distribution of the matting agent is preferably set as such that
the variation coefficient may become 50% or lower, more preferably,
40% or lower, and further preferably, 30% or lower. The variation
coefficient, herein, is defined by (the standard deviation of
particle diameter)/(mean diameter of the particle).times.100.
Furthermore, it is preferred to use two types of matting agents
having low variation coefficient and the ratio of their mean
particle diameters being higher than 3, in combination.
[0372] The level of matting on the image forming layer surface is
not restricted as far as star-dust trouble occurs, but the level of
matting of from 30 seconds to 2000 seconds is preferred,
particularly preferred, from 40 seconds to 1500 seconds as Beck's
smoothness. Beck's smoothness can be calculated easily, using Japan
Industrial Standard (JIS) P8119 "The method of testing Beck's
smoothness for papers and sheets using Beck's test apparatus", or
TAPPI standard method T479.
[0373] The level of matting of the back layer in the invention is
preferably in a range of 1200 seconds or less and 10 seconds or
more; more preferably, 800 seconds or less and 20 seconds or more;
and even more preferably, 500 seconds or less and 40 seconds or
more, when expressed by Beck's smoothness.
[0374] In the present invention, a matting agent is preferably
contained in an outermost layer, in a layer which can function as
an outermost layer, or in a layer nearer to outer surface, and also
preferably is contained in a layer which can function as a
so-called protective layer.
[0375] 4) Polymer Latex
[0376] The change in size of the photothermographic material can be
reduced by adding a polymer latex in the surface protective layer
or the back layer of the photothermographic material. As such
polymer latex, descriptions can be found in "Gosei Jushi Emulsion
(Synthetic resin emulsion)" (Taira Okuda and Hiroshi Inagaki, Eds.,
published by Kobunshi Kankokai (1978)), "Gosei Latex no Oyo
(Application of synthetic latex)" (Takaaki Sugimura, Yasuo Kataoka,
Soichi Suzuki, and Keiji Kasahara, Eds., published by Kobunshi
Kankokai (1993)), and "Gosei Latex no Kagaku (Chemistry of
synthetic latex)" (Soichi Muroi, published by Kobunshi Kankokai
(1970)). More specifically, there can be mentioned a latex of
methyl methacrylate (33.5% by weight)/ethyl acrylate (50% by
weight)/methacrylic acid (16.5% by weight) copolymer, a latex of
methyl methacrylate (47.5% by weight)/butadiene (47.5% by
weight)/itaconic acid (5% by weight) copolymer, a latex of ethyl
acrylate/methacrylic acid copolymer, a latex of methyl methacrylate
(58.9% by weight)/2-ethylhexyl acrylate (25.4% by weight)/styrene
(8.6% by weight)/2-hydroethyl methacrylate (5.1% by weight)/acrylic
acid (2.0% by weight) copolymer, a latex of methyl methacrylate
(64.0% by weight)/styrene (9.0% by weight)/butyl acrylate (20.0% by
weight)/2-hydroxyethyl methacrylate (5.0% by weight)/acrylic acid
(2.0% by weight) copolymer, and the like. Furthermore, as the
binder for the surface protective layer, there can be applied the
technology described in paragraph Nos. 0021 to 0025 of the
specification of JP-A No. 2000-267226, and the technology described
in paragraph Nos. 0023 to 0041 of the specification of JP-A No.
2000-19678. The polymer latex in the surface protective layer is
preferably contained in an amount of from 10% by weight to 90% by
weight, particularly preferably from 20% by weight to 80% by
weight, based on a total weight of binder.
[0377] 5) Surface pH
[0378] The surface pH of the photothermographic material according
to the invention preferably yields a pH of 7.0 or lower, and more
preferably 6.6 or lower, before thermal developing process.
Although there is no particular restriction concerning the lower
limit, the lower limit of pH value is about 3. The most preferred
surface pH range is from 4 to 6.2. From the viewpoint of reducing
the surface pH, it is preferred to use an organic acid such as
phthalic acid derivative or a non-volatile acid such as sulfuric
acid, or a volatile base such as ammonia for the adjustment of the
surface pH. In particular, ammonia can be used favorably for the
achievement of low surface pH, because it can easily vaporize to
remove it before the coating step or before applying thermal
development.
[0379] It is also preferred to use a non-volatile base such as
sodium hydroxide, potassium hydroxide, lithium hydroxide, and the
like, in combination with ammonia. The method of measuring surface
pH value is described in paragraph No. 0123 of the specification of
JP-A No. 2000-284399.
[0380] 6) Hardener
[0381] A hardener may be used in each of image forming layer,
protective layer, back layer, and the like of the invention. As
examples of the hardener, descriptions of various methods can be
found in pages 77 to 87 of T. H. James, "THE THEORY OF THE
PHOTOGRAPHIC PROCESS, FOURTH EDITION" (Macmillan Publishing Co.,
Inc., 1977). Preferably used are, in addition to chromium alum,
sodium salt of 2,4-dichloro-6-hydroxy-s-triazine, N,N-ethylene
bis(vinylsulfonacetamide), and N,N-propylene
bis(vinylsulfonacetamide), polyvalent metal ions described in page
78 of the above literature and the like, polyisocyanates described
in U.S. Pat. No. 4,281,060, JP-A No. 6-208193, and the like, epoxy
compounds of U.S. Pat. No. 4,791,042 and the like, and vinylsulfone
compounds of JP-A No. 62-89048.
[0382] The hardener is added as a solution, and the solution is
added to a coating solution 180 minutes before coating to just
before coating, preferably 60 minutes before to 10 seconds before
coating. However, so long as the effect of the invention is
sufficiently exhibited, there is no particular restriction
concerning the mixing method and the conditions of mixing. As
specific mixing methods, there can be mentioned a method of mixing
in the tank, in which the average stay time calculated from the
flow rate of addition and the feed rate to the coater is controlled
to yield a desired time, or a method using static mixer as
described in Chapter 8 of N. Harnby, M. F. Edwards, A. W. Nienow
(translated by Koji Takahashi) "Ekitai Kongo Gijutu (Liquid Mixing
Technology)" (Nikkan Kogyo Shinbunsha, 1989), and the like.
[0383] 7) Surfactant
[0384] Concerning the surfactant, the solvent, the support, the
antistatic agent, and the electrically conductive layer, and the
method for obtaining color images applicable in the invention,
there can be used those disclosed in paragraph numbers 0132, 0133,
0134, 0135, and 0136, respectively, of JP-A No. 11-65021.
Concerning lubricants, there can be used those disclosed in
paragraph numbers 0061 to 0064 of JP-A No. 11-84573 and in
paragraph numbers 0049 to 0062 of JP-A No. 2001-83679.
[0385] In the invention, it is preferred to use a fluorocarbon
surfactant. Specific examples of fluorocarbon surfactants can be
found in those described in JP-A Nos. 10-197985, 2000-19680, and
2000-214554. Polymer fluorocarbon surfactants described in JP-A No.
9-281636 can be also used preferably. For the photothermographic
material in the invention, the fluorocarbon surfactants described
in JP-A Nos. 2002-82411, 2003-57780, and 2001-264110 are preferably
used. Especially, the usage of the fluorocarbon surfactants
described in JP-A Nos. 2003-57780 and 2001-264110 in an aqueous
coating solution is preferred viewed from the standpoint of
capacity in static control, stability of the coated surface state
and sliding facility. The fluorocarbon surfactant described in JP-A
No. 2001-264110 is most preferred because of high capacity in
static control and that it needs small amount to use.
[0386] According to the invention, the fluorocarbon surfactant can
be used on either side of both sides of the support, but is
preferred to use on the both sides. Further, it is particularly
preferred to use in combination with electrically conductive layer
including metal oxides described below. In this case the amount of
the fluorocarbon surfactant on the side of the electrically
conductive layer can be reduced or removed.
[0387] The addition amount of the fluorocarbon surfactant is
preferably in a range of from 0.1 mg/m.sup.2 to 100 mg/m.sup.2,
more preferably from 0.3 mg/m to 30 mg/m.sup.2, and even more
preferably from 1 mg/m.sup.2 to 10 mg/m.sup.2. Especially, the
fluorocarbon surfactant described in JP-A No. 2001-264110 is
effective, and used preferably in a range of from 0.01 mg/m.sup.2
to 10 mg/m.sup.2, and more preferably, in a range of from 0.1
mg/m.sup.2 to 5 mg/m.sup.2.
[0388] 8) Antistatic Agent
[0389] The photothermographic material of the invention preferably
contains an electrically conductive layer including metal oxides or
electrically conductive polymers. The antistatic layer may serve as
an undercoat layer, a back surface protective layer, or the like,
but can also be placed specially. As an electrically conductive
material of the antistatic layer, metal oxides having enhanced
electric conductivity by the method of introducing oxygen defects
or different types of metallic atoms into the metal oxides are
preferable for use. Examples of metal oxides are preferably
selected from ZnO, TiO.sub.2, or SnO.sub.2. As the combination of
different types of atoms, preferred are ZnO combined with Al, or
In; SnO.sub.2 with Sb, Nb, P, halogen atoms, or the like; TiO.sub.2
with Nb, Ta, or the like.
[0390] Particularly preferred for use is SnO.sub.2 combined with
Sb. The addition amount of different types of atoms is preferably
in a range of from 0.01 mol % to 30 mol %, and more preferably, in
a range of from 0.1 mol % to 10 mol %. The shape of the metal
oxides can include, for example, spherical, needle-like, or
tabular. The needle-like particles, with the rate of (the major
axis)/(the minor axis) is 2.0 or more, and more preferably in a
range of from 3.0 to 50, is preferred viewed from the standpoint of
the electric conductivity effect. The metal oxides is preferably
used in a range of from 1 mg/m.sup.2 to 1000 mg/m.sup.2, more
preferably from 10 mg/m.sup.2 to 500 mg/m.sup.2, and even more
preferably from 20 mg/m.sup.2 to 200 mg/m.sup.2. The antistatic
layer can be laid on either side of the image forming layer side or
the backside, it is preferred to set between the support and the
back layer. Specific examples of the antistatic layer in the
invention include described in paragraph Nos. 0135 of JP-A No.
11-65021, in JP-A Nos. 56-143430, 56-143431, 58-62646, and
56-120519, and in paragraph Nos. 0040 to 0051 of JP-A No. 11-84573,
in U.S. Pat. No. 5,575,957, and in paragraph Nos. 0078 to 0084 of
JP-A No. 11-223898.
[0391] 9) Support
[0392] As the transparent support, preferably used is polyester,
particularly, polyethylene terephthalate, which is subjected to
heat treatment in the temperature range of from 130.degree. C. to
185.degree. C. in order to relax the internal strain caused by
biaxial stretching and remaining inside the film, and to remove
strain ascribed to heat shrinkage generated during thermal
development. In the case of a photothermographic material for
medical use, the transparent support may be colored with a blue dye
(for instance, dye-1 described in the Example of JP-A No.
8-240877), or may be uncolored. As to the support, it is preferred
to apply undercoating technology, such as water-soluble polyester
described in JP-A No. 11-84574, a styrene-butadiene copolymer
described in JP-A No. 10-186565, a vinylidene chloride copolymer
described in JP-A No. 2000-39684, and the like. The moisture
content of the support is preferably 0.5% by weight or lower when
coating for an image forming layer or a back layer is conducted on
the support.
[0393] 10) Other Additives
[0394] Furthermore, an antioxidant, stabilizing agent, plasticizer,
UV absorbent, or film-forming promoting agent may be added to the
photothermographic material. Each of the additives is added to
either of the image forming layer or the non-photosensitive layer.
Reference can be made to WO No. 98/36322, EP No. 803764A1, JP-A
Nos. 10.sup.-186567 and 10.sup.-18568, and the like.
[0395] 11) Coating Method
[0396] The photothermographic material of the invention may be
coated by any method. Specifically, various types of coating
operations including extrusion coating, slide coating, curtain
coating, immersion coating, knife coating, flow coating, or an
extrusion coating using the type of hopper described in U.S. Pat.
No. 2,681,294 are used. Preferably used is extrusion coating or
slide coating described in pages 399 to 536 of Stephen F. Kistler
and Petert M. Shweizer, "LIQUID FILM COATING" (Chapman & Hall,
1997), and particularly preferably used is slide coating. Example
of the shape of the slide coater for use in slide coating is shown
in FIG. 11b.1, page 427, of the same literature. If desired, two or
more layers can be coated simultaneously by the method described in
pages 399 to 536 of the same literature, or by the method described
in U.S. Pat. No. 2,761,791 and British Patent No. 837,095.
Particularly preferred in the invention is the method described in
JP-A Nos. 2001-194748, 2002-153808, 2002-153803, and
2002-182333.
[0397] The coating solution for the image forming layer in the
invention is preferably a so-called thixotropic fluid. For the
details of this technology, reference can be made to JP-A No.
11-52509. Viscosity of the coating solution for the image forming
layer in the invention at a shear velocity of 0.1 S.sup.-1 is
preferably from 400 mPas to 100,000 mPas, and more preferably, from
500 mPas to 20,000 mPas. At a shear velocity of 1000 S.sup.-1, the
viscosity is preferably from 1 mPas to 200 mPas, and more
preferably, from 5 mPas to 80 mPas.
[0398] In the case of mixing two types of liquids on preparing the
coating solution of the invention, known in-line mixer and in-plant
mixer can be used favorably. Preferred in-line mixer of the
invention is described in JP-A No. 2002-85948, and the in-plant
mixer is described in JP-A No. 2002-90940.
[0399] The coating solution of the invention is preferably
subjected to antifoaming treatment to maintain the coated surface
in a fine state. Preferred method for antifoaming treatment in the
invention is described in JP-A No. 2002-66431.
[0400] In the case of applying the coating solution of the
invention to the support, it is preferred to perform
diselectrification in order to prevent the adhesion of dust,
particulates, and the like due to charge up. Preferred example of
the method of diselectrification for use in the invention is
described in JP-A No. 2002-143747.
[0401] Since a non-setting coating solution is used for the image
forming layer in the invention, it is important to precisely
control the drying wind and the drying temperature. Preferred
drying method for use in the invention is described in detail in
JP-A Nos. 2001-194749 and 2002-139814.
[0402] In order to improve the film-forming properties in the
photothermographic material of the invention, it is preferred to
apply a heat treatment immediately after coating and drying. The
temperature of the heat treatment is preferably in a range of from
60.degree. C. to 100.degree. C. at the film surface, and time
period for heating is preferably in a range of from 1 second to 60
seconds. More preferably, heating is performed in a temperature
range of from 70.degree. C. to 90.degree. C. at the film surface,
and the time period for heating is from 2 seconds to 10 seconds. A
preferred method of heat treatment for the invention is described
in JP-A No. 2002-107872.
[0403] Furthermore, the producing methods described in JP-A Nos.
2002-156728 and 2002-182333 are favorably used in the invention in
order to stably and successively produce the photothermographic
material of the invention.
[0404] The photothermographic material is preferably of mono-sheet
type (i.e., a type which can form image on the photothermographic
material without using other sheets such as an image-receiving
material).
[0405] 12) Wrapping Material
[0406] In order to suppress fluctuation from occurring on
photographic property during a preservation of the
photothermographic material of the invention before thermal
development, or in order to improve curling or winding tendencies
when the photothermographic material is manufactured in a roll
state, it is preferred that a wrapping material having low oxygen
transmittance and/or vapor transmittance is used. Preferably,
oxygen transmittance is 50 mLatm.sup.-1 m.sup.-2 day- or lower at
25.degree. C., more preferably, 10 mLatm.sup.-1 m.sup.-2 day.sup.-1
or lower, and even more preferably, 1.0 mLatm.sup.-1 m.sup.-2
day.sup.-1 or lower. Preferably, vapor transmittance is 10
gatm.sup.-1 m.sup.-2 day.sup.-1 or lower, more preferably, 5
gatm.sup.-1 m.sup.-2 day.sup.-1 or lower, and even more preferably,
1 gatm.sup.-1 m.sup.-2 day.sup.-1 or lower.
[0407] As specific examples of a wrapping material having low
oxygen transmittance and/or vapor transmittance, reference can be
made to, for instance, the wrapping material described in JP-A Nos.
8-254793 and 2000-206653.
[0408] 13) Other Applicable Techniques
[0409] Techniques which can be used for the photothermographic
material of the invention also include those in EP No. 803764A1, EP
No. 883022A1, WO No. 98/36322, JP-A Nos. 56-62648, 58-62644, JP-A
Nos. 9-43766, 9-281637, 9-297367, 9-304869, 9-311405, 9-329865,
10-10669, 10-62899, 10-69023, 10-186568, 10-90823, 10-171063,
10-186565, 10-186567, 10-186569 to 10-186572, 10-197974, 10-197982,
10-197983, 10-197985 to 10-197987, 10-207001, 10-207004, 10-221807,
10-282601, 10-288823, 10-288824, 10-307365, 10-312038, 10-339934,
11-7100, 11-15105, 11-24200, 11-24201, 11-30832, 11-84574,
11-65021, 11-109547, 11-125880, 11-129629, 11-133536 to 11-133539,
11-133542, 11-133543, 11-223898, 11-352627, 11-305377, 11-305378,
11-305384, 11-305380, 11-316435, 11-327076, 11-338096, 11-338098,
11-338099, 11-343420, JP-A Nos. 2000-187298, 2000-10229,
2000-47345, 2000-206642, 2000-98530, 2000-98531, 2000-112059,
2000-112060, 2000-112104, 2000-112064, and 2000-171936.
[0410] (Image Forming Method)
[0411] 1) Exposure
[0412] The photothermographic material of the invention may be
subjected to imagewise exposure by various light sources. The
photothermographic material of the present invention is preferably
subjected to scanning exposure using a laser beam source. As the
laser beam source, He--Ne laser of red through infrared emission,
red laser diode, or Ar.sup.+, He--Ne, He--Cd laser of blue through
green emission, or blue laser diode can be used. Preferred is red
to infrared laser diode and the peak wavelength of laser beam is
600 nm to 900 nm, and preferably 620 nm to 850 nm. In recent years,
development has been made particularly on a light source module
with an SHG (a second harmonic generator) and a laser diode
integrated into a single piece whereby a laser output apparatus in
a short wavelength region has become popular. A blue laser diode
enables high definition image recording and makes it possible to
obtain an increase in recording density and a stable output over a
long lifetime, which results in expectation of an expanded demand
in the future. The peak wavelength of blue laser beam is preferably
from 300 nm to 500 nm, and particularly preferably from 400 nm to
500 nm.
[0413] Laser beam which oscillates in a longitudinal multiple
modulation by a method such as high frequency superposition is also
preferably employed.
[0414] 2) Thermal Development
[0415] Although any method may be used for developing the
photothermographic material of the present invention, development
is usually performed by elevating the temperature of the
photothermographic material exposed imagewise. The temperature of
development is preferably from 80.degree. C. to 250.degree. C.,
more preferably from 100.degree. C. to 140.degree. C., and even
more preferably from 110.degree. C. to 130.degree. C. Time period
for development is preferably from 1 second to 60 seconds, more
preferably from 3 second to 30 seconds, even more preferably from 5
seconds to 25 seconds, and particularly preferably from 7 seconds
to 15 seconds.
[0416] In the process of thermal development, either a drum type
heater or a plate type heater may be used, although a plate type
heater is preferred. A preferable process of thermal development by
a plate type heater is a process described in JP-A No. 11-133572,
which discloses a thermal developing apparatus in which a visible
image is obtained by bringing a photothermographic material with a
formed latent image into contact with a heating means at a thermal
developing section, wherein the heating means comprises a plate
heater, and a plurality of pressing rollers are oppositely provided
along one surface of the plate heater, the thermal developing
apparatus is characterized in that thermal development is performed
by passing the photothermographic material between the pressing
rollers and the plate heater. It is preferred that the plate heater
is divided into 2 to 6 steps, with the leading end having a lower
temperature by 1.degree. C. to 10.degree. C. For example, 4 sets of
plate heaters which can be independently subjected to the
temperature control are used, and are controlled so that they
respectively become 112.degree. C., 119.degree. C., 121.degree. C.,
and 120.degree. C.
[0417] Such a process is also described in JP-A No. 54-30032, which
allows for passage of moisture and organic solvents included in the
photothermographic material out of the system, and also allows for
suppressing the change of shapes of the support of the
photothermographic material upon rapid heating of the
photothermographic material.
[0418] For downsizing the thermal developing apparatus and for
reducing the time period for thermal development, it is preferred
that the heater is more stably controlled, and a top part of one
sheet of the photothermographic material is exposed and thermal
development of the exposed part is started before exposure of the
end part of the sheet has completed. Preferable imagers which
enable a rapid process according to the invention are described in,
for example, JP-A Nos. 2002-289804 and 2002-287668. Using such
imagers, thermal development within 14 seconds is possible with a
plate type heater having three heating plates which are controlled,
for example, at 107.degree. C., 121.degree. C. and 121.degree. C.,
respectively. Thus, the output time period for the first sheet can
be reduced to about 60 seconds. For such a rapid developing
process, it is preferred to use the photothermographic materials of
the present invention, which exhibit high sensitivity and are
hardly influenced by environmental temperature, in combination with
the process.
[0419] 3) System
[0420] Examples of a medical laser imager equipped with an exposing
portion and a thermal developing portion include Fuji Medical Dry
Laser Imager FM-DPL and DRYPIX 7000. In connection with FM-DPL,
description is found in Fuji Medical Review No. 8, pages 39 to 55.
The described techniques may be applied as the laser imager for the
photothermographic material of the invention. In addition, the
present photothermographic material can be also applied as a
photothermographic material for the laser imager used in "AD
network" which was proposed by Fuji Film Medical Co., Ltd. as a
network system accommodated to DICOM standard.
[0421] (Application of the Invention)
[0422] The photothermographic material of the invention is
preferably used for photothermographic materials for use in medical
diagnosis, photothermographic materials for use in industrial
photographs, photothermographic materials for use in graphic arts,
as well as for COM, through forming black and white images by
silver imaging.
EXAMPLES
[0423] The present invention is specifically explained by way of
Examples below, which should not be construed as limiting the
invention thereto.
Example 1
[0424] (Preparation of PET Support)
[0425] 1) Film Manufacturing
[0426] PET having IV (intrinsic viscosity) of 0.66 (measured in
phenol/tetrachloroethane=6/4 (mass ratio) at 25.degree. C.) was
obtained according to a conventional manner using terephthalic acid
and ethylene glycol. The product was pelletized, dried at
130.degree. C. for 4 hours, and melted at 300.degree. C.
Thereafter, the mixture was extruded from a T-die and rapidly
cooled to form a non-tentered film.
[0427] The film was stretched along the longitudinal direction by
3.3 times using rollers of different peripheral speeds, and then
stretched along the transverse direction by 4.5 times using a
tenter machine. The temperatures used for these operations were
110.degree. C. and 130.degree. C., respectively. Then, the film was
subjected to thermal fixation at 240.degree. C. for 20 seconds, and
relaxed by 4% along the transverse direction at the same
temperature. Thereafter, the chucking part was slit off, and both
edges of the film were knurled. Then the film was rolled up at the
tension of 4 kg/cm.sup.2 to obtain a roll having the thickness of
175 .mu.m.
[0428] 2) Surface Corona Discharge Treatment
[0429] Both surfaces of the support were treated at room
temperature at 20 m/minute using Solid State Corona Discharge
Treatment Machine Model 6 KVA manufactured by Piller GmbH. It was
proven that treatment of 0.375 kVAminute/m.sup.2 was executed,
judging from the readings of current and voltage on that occasion.
The frequency upon this treatment was 9.6 kHz, and the gap
clearance between the electrode and dielectric roll was 1.6 mm.
[0430] 3) Undercoating TABLE-US-00002 <Preparations of coating
solution for undercoat layer> Formula (1) (for undercoat layer
on the image forming layer side) Pesresin A-520 manufactured by
Takamatsu Oil & 46.8 g Fat Co., Ltd. (30% by weight solution)
BAIRONAARU MD-1200 manufactured by Toyo Boseki 10.4 g Co., Ltd.
Polyethyleneglycol monononylphenylether 11.0 g (average ethylene
oxide number = 8.5) 1% by weight solution MP-1000 manufactured by
Soken Chemical & Engineering 0.91 g Co., Ltd. (PMMA polymer
fine particle, mean particle diameter of 0.4 .mu.m) Distilled water
931 mL Formula (2) (for first layer on the backside)
Styrene-butadiene copolymer latex 130.8 g (solid content of 40% by
weight, styrene/butadiene mass ratio = 68/32) Sodium salt of
2,4-dichloro-6-hydroxy-S-triazine 5.2 g (8% by weight aqueous
solution) 1% by weight aqueous solution of sodium 10 mL
laurylbenzenesulfonate Polystyrene particle dispersion 0.5 g (mean
particle diameter of 2 .mu.m, 20% by weight) Distilled water 854 mL
Formula (3) (for second layer on the backside) SnO.sub.2/SbO (9/1
by mass ratio, mean particle diameter 84 g of 0.5 .mu.m, 17% by
weight dispersion) Gelatin 7.9 g METOLOSE TC-5 manufactured by
Shin-Etsu Chemical 10 g Co., Ltd. (2% by weight aqueous solution)
1% by weight aqueous solution of sodium 10 mL
dodecylbenzenesulfonate NaOH (1% by weight) 7 g Proxel
(manufactured by Imperial Chemical 0.5 g Industries PLC) Distilled
water 881 mL
[0431] <Undercoating>
[0432] Both surfaces of the biaxially tentered polyethylene
terephthalate support having the thickness of 175 .mu.m were
subjected to the corona discharge treatment as described above,
respectively. Thereafter, the aforementioned formula (1) of the
coating solution for the undercoat was coated on one side (image
forming layer side) with a wire bar so that the amount of wet
coating became 6.6 mL/m.sup.2 (per one side), and dried at
180.degree. C. for 5 minutes. Then, the aforementioned formula (2)
of the coating solution for the undercoat was coated on the reverse
side (backside) with a wire bar so that the amount of wet coating
became 5.7 mL/m.sup.2, and dried at 180.degree. C. for 5 minutes.
Furthermore, the aforementioned formula (3) of the coating solution
for the undercoat was coated on the reverse side (backside) with a
wire bar so that the amount of wet coating became 8.4 mL/m.sup.2,
and dried at 180.degree. C. for 6 minutes. Thus, an undercoated
support was produced.
[0433] (Back Layer)
[0434] 1) Preparation of Coating Solution for Antihalation
Layer
[0435] <Preparation of Dispersion of Solid Fine Particles (a) of
Base Precursor>
[0436] 2.5 kg of base precursor-1, 300 g of a surfactant (trade
name: DEMOL N, manufactured by Kao Corporation), 800 g of
diphenylsulfone, and 1.0 g of benzoisothiazolinone sodium salt were
mixed with distilled water to give the total amount of 8.0 kg. This
mixed liquid was subjected to beads dispersion using a horizontal
sand mill (UVM-2: manufactured by AIMEX Co., Ltd.). Process of
dispersion includes feeding the mixed liquid to UVM-2 packed with
zirconia beads having a mean particle diameter of 0.5 mm with a
diaphragm pump, followed by the dispersion at the inner pressure of
50 hPa or higher until desired mean particle diameter could be
achieved.
[0437] Dispersion was continued until the ratio of the optical
density at 450 nm to the optical density at 650 nm for the spectral
absorption of the dispersion (D.sub.450/D.sub.650) became 3.0 upon
spectral absorption measurement. The resulting dispersion was
diluted with distilled water so that the concentration of the base
precursor became 25% by weight, and filtrated (with a polypropylene
filter having a mean fine pore diameter of 3 .mu.m) for eliminating
dust to put into practical use.
[0438] <Preparation of Solid Fine Particle Dispersion of
Dye>
[0439] Cyanine dye-1 in an amount of 6.0 kg, 3.0 kg of sodium
p-dodecylbenzenesulfonate, 0.6 kg of DEMOL SNB (a surfactant
manufactured by Kao Corporation), and 0.15 kg of an antifoaming
agent (trade name: SURFYNOL 104E, manufactured by Nissin Chemical
Industry Co., Ltd.) were mixed with distilled water to give the
total amount of 60 kg. The mixed liquid was subjected to dispersion
with 0.5 mm zirconia beads using a horizontal sand mill (UVM-2:
manufactured by AIMEX Co., Ltd.).
[0440] Dispersion was continued until the ratio of the optical
density at 650 nm to the optical density at 750 nm for the spectral
absorption of the dispersion (D.sub.650/D.sub.750) became 5.0 or
higher upon spectral absorption measurement. The resulting
dispersion was diluted with distilled water so that the
concentration of the cyanine dye became 6% by weight, and filtrated
with a filter (mean fine pore diameter: 1 .mu.m) for eliminating
dust to put into practical use.
[0441] <Preparation of Coating Solution for Antihalation
Layer>
[0442] A vessel was kept at 40.degree. C., and thereto were added
37 g of gelatin having an isoelectric point of 6.6 (ABA gelatin,
manufactured by Nippi Co., Ltd.), 0.1 g of benzoisothiazolinone,
and water to allow gelatin to be dissolved. Additionally, 36 g of
the above-mentioned dispersion of the solid fine particles of the
dye, 73 g of the above-mentioned dispersion of the solid fine
particles (a) of the base precursor, 43 mL of a 3% by weight
aqueous solution of sodium polystyrenesulfonate, and 82 g of a 10%
by weight liquid of SBR latex (styrene/butadiene/acrylic acid
copolymer; mass ratio of the copolymerization of 68.3/28.7/3.0)
were admixed to give a coating solution for the antihalation layer
in an amount of 773 mL. The pH of the resulting coating solution
was 6.3.
[0443] 2) Preparation of Coating Solution for Back Surface
Protective Layer
[0444] A vessel was kept at 40.degree. C., and thereto were added
43 g of gelatin having an isoelectric point of 4.8 (PZ gelatin,
manufactured by Miyagi Chemical Industry Co., Ltd.), 0.21 g of
benzoisothiazolinone, and water to allow gelatin to be dissolved.
Additionally, 8.1 mL of a 1 mol/L sodium acetate aqueous solution,
0.93 g of monodispersed fine particles of poly(ethylene glycol
dimethacrylate-co-methylmethacrylate) (a mean particle diameter of
7.7 .mu.m, and a standard deviation of particle diameter of 0.3), 5
g of a 10% by weight emulsion of liquid paraffin, 10 g of a 10% by
weight emulsion of dipentaerythritol hexaisostearate, 10 mL of a 5%
by weight aqueous solution of sodium
di(2-ethylhexyl)sulfosuccinate, 17 mL of a 3% by weight aqueous
solution of sodium polystyrenesulfonate, 2.4 mL of a 2% by weight
solution of a fluorocarbon surfactant (F-1), 2.4 mL of a 2% by
weight solution of another fluorocarbon surfactant (F-2), and 30 mL
of a 20% by weight liquid of ethyl acrylate/acrylic acid copolymer
(mass ratio of the copolymerization of 96.4/3.6) latex were
admixed. Just prior to the coating, 50 mL of a 4% by weight aqueous
solution of N,N-ethylenebis(vinylsulfone acetamide) was admixed to
give a coating solution for the back surface protective layer in an
amount of 855 mL. The pH of the resulting coating solution was
6.2.
[0445] 3) Coating of Back Layer
[0446] The backside of the undercoated support described above was
subjected to simultaneous double coating so that the coating
solution for the antihalation layer gave the coating amount of
gelatin of 0.54 g/m.sup.2, and so that the coating solution for the
back surface protective layer gave the coating amount of gelatin of
1.85 g/m.sup.2, followed by drying to produce a back layer.
[0447] (Image Forming Layer, Intermediate Layer, and Surface
Protective Layer)
1. Preparations of Coating Material
[0448] 1) Preparation of Silver Halide Emulsion
[0449] <<Preparation of Silver Halide Emulsion 1>>
[0450] A liquid was prepared by adding 3.1 mL of a 1% by weight
potassium bromide solution, and then 3.5 mL of 0.5 mol/L sulfuric
acid and 31.7 g of phthalated gelatin to 1421 mL of distilled
water. The liquid was kept at 30.degree. C. while stirring in a
stainless steel reaction vessel, and thereto were added a total
amount of: solution A prepared through diluting 22.22 g of silver
nitrate by adding distilled water to give the volume of 95.4 mL;
and solution B prepared through diluting 15.3 g of potassium
bromide and 0.8 g of potassium iodide with distilled water to give
the volume of 97.4 mL, over 45 seconds at a constant flow rate.
[0451] Thereafter, 10 mL of a 3.5% by weight aqueous solution of
hydrogen peroxide was added thereto, and 10.8 mL of a 10% by weight
aqueous solution of benzimidazole was further added. Moreover, a
solution C prepared through diluting 51.86 g of silver nitrate by
adding distilled water to give the volume of 317.5 mL and a
solution D prepared through diluting 44.2 g of potassium bromide
and 2.2 g of potassium iodide with distilled water to give the
volume of 400 mL were added. A controlled double jet method was
executed through adding the total amount of the solution C at a
constant flow rate over 20 minutes, accompanied by adding the
solution D while maintaining the pAg at 8.1. Potassium
hexachloroiridate (III) was added in its entirely to give
1.times.10.sup.-4 mol per 1 mol of silver, at 10 minutes post
initiation of the addition of the solution C and the solution D.
Moreover, at 5 seconds after completing the addition of the
solution C, a potassium hexacyanoferrate (II) in an aqueous
solution was added in its entirety to give 3.times.10.sup.-4 mol
per 1 mol of silver. The mixture was adjusted to the pH of 3.8 with
0.5 mol/L sulfuric acid. After stopping stirring, the mixture was
subjected to precipitation/desalting/water washing steps. The
mixture was adjusted to the pH of 5.9 with 1 mol/L sodium hydroxide
to produce a silver halide dispersion having the pAg of 8.0.
[0452] The above-described silver halide dispersion was kept at
38.degree. C. with stirring, and thereto was added 5 mL of a 0.34%
by weight methanol solution of 1,2-benzisothiazoline-3-one,
followed by elevating the temperature to 47.degree. C. at 40
minutes thereafter. At 20 minutes after elevating the temperature,
sodium benzene thiosulfonate in a methanol solution was added at
7.6.times.10.sup.-5 mol per 1 mol of silver. At additional 5
minutes later, a tellurium sensitizer C in a methanol solution was
added at 2.9.times.10.sup.-4 mol per 1 mol of silver and subjected
to ripening for 91 minutes. Thereafter, a methanol solution of a
spectral sensitizing dye A and a spectral sensitizing dye B with a
molar ratio of 3:1 was added thereto at 1.2.times.10.sup.-3 mol in
total of the spectral sensitizing dye A and B per 1 mol of silver.
At 1 minute later, 1.3 mL of a 0.8% by weight methanol solution of
N,N'-dihydroxy-N'',N''-diethylmelamine was added thereto, and at
additional 4 minutes thereafter, 5-methyl-2-mercaptobenzimidazole
in a methanol solution at 4.8.times.10.sup.-3 mol per 1 mol of
silver, 1-phenyl-2-heptyl-5-mercapto-1,3,4-triazole in a methanol
solution at 5.4.times.10.sup.-3 mol per 1 mol of silver, and
1-(3-methylureidophenyl)-5-mercaptotetrazole in an aqueous solution
at 8.5.times.10.sup.-3 mol per 1 mol of silver were added to
produce a silver halide emulsion 1.
[0453] Grains in thus prepared silver halide emulsion were silver
iodobromide grains having a mean equivalent spherical diameter of
0.042 .mu.m, a variation coefficient of an equivalent spherical
diameter distribution of 20%, which uniformly include iodine at 3.5
mol %. Grain size and the like were determined from the average of
1000 grains using an electron microscope. The {100} face ratio of
these grains was found to be 80% using a Kubelka-Munk method.
[0454] <<Preparation of Silver Halide Emulsion 2>>
[0455] Preparation of silver halide dispersion 2 was conducted in a
similar manner to the process in the preparation of the silver
halide emulsion 1 except that: the temperature of the liquid upon
the grain forming process was altered from 30.degree. C. to
47.degree. C.; the solution B was changed to that prepared through
diluting 15.9 g of potassium bromide with distilled water to give
the volume of 97.4 mL; the solution D was changed to that prepared
through diluting 45.8 g of potassium bromide with distilled water
to give the volume of 400 mL; time period for adding the solution C
was changed to 30 minutes; and potassium hexacyanoferrate (II) was
deleted; further the precipitation/desalting/water
washing/dispersion were carried out similar to the silver halide
emulsion 1. Furthermore, the spectral sensitization, chemical
sensitization, and addition of 5-methyl-2-mercaptobenzimidazole and
1-phenyl-2-heptyl-5-mercapto-1,3,4-triazole were executed to the
silver halide dispersion 2 similar to the silver halide emulsion 1
except that: the amount of the tellurium sensitizer C to be added
was changed to 1.1.times.10.sup.-4 mol per 1 mol of silver; the
amount of the methanol solution of the spectral sensitizing dye A
and a spectral sensitizing dye B with a molar ratio of 3:1 to be
added was changed to 7.0.times.10.sup.-4 mol in total of the
spectral sensitizing dye A and the spectral sensitizing dye B per 1
mol of silver; the addition of
1-phenyl-2-heptyl-5-mercapto-1,3,4-triazole was changed to give
3.3.times.10.sup.-3 mol per 1 mol of silver; and the addition of
1-(3-methylureidophenyl)-5-mercaptotetrazole was changed to give
4.7.times.10.sup.-3 mol per 1 mol of silver, to produce silver
halide emulsion 2. Grains in the silver halide emulsion 2 were
cubic pure silver bromide grains having a mean equivalent spherical
diameter of 0.080 .mu.m and a variation coefficient of an
equivalent spherical diameter distribution of 20%.
[0456] <<Preparation of Silver Halide Emulsion 3>>
[0457] Preparation of silver halide dispersion 3 was conducted in a
similar manner to the process in the preparation of the silver
halide emulsion 1 except that the temperature of the liquid upon
the grain forming process was altered from 30.degree. C. to
27.degree. C., and in addition, the precipitation/desalting/water
washing/dispersion were carried out similarly to the silver halide
emulsion 1. Silver halide emulsion 3 was obtained similarly to the
silver halide emulsion 1 except that: to the silver halide
dispersion 3, the addition of the methanol solution of the spectral
sensitizing dye A and the spectral sensitizing dye B was changed to
the solid dispersion (aqueous gelatin solution) at a molar ratio of
1:1 with the amount to be added being 6.times.10.sup.-3 mol in
total of the spectral sensitizing dye A and spectral sensitizing
dye B per 1 mol of silver; the addition amount of tellurium
sensitizer C was changed to 5.2.times.10.sup.-4 mol per 1 mol of
silver; and bromoauric acid at 5.times.10.sup.-4 mol per 1 mol of
silver and potassium thiocyanate at 2.times.10.sup.-3 mol per 1 mol
of silver were added at 3 minutes following the addition of the
tellurium sensitizer. Grains in the silver halide emulsion 3 were
silver iodobromide grains having a mean equivalent spherical
diameter of 0.034 .mu.m and a variation coefficient of an
equivalent spherical diameter distribution of 20%, which uniformly
include iodine at 3.5 mol %.
[0458] <<Preparation of Mixed Emulsion A for Coating
Solution>>
[0459] The silver halide emulsion 1 at 70% by weight, the silver
halide emulsion 2 at 15% by weight, and the silver halide emulsion
3 at 15% by weight were dissolved, and thereto was added
benzothiazolium iodide in a 1% by weight aqueous solution to give
7.times.10.sup.-3 mol per 1 mol of silver.
[0460] Further, as "a compound that is one-electron-oxidized to
provide a one-electron oxidation product, which releases one or
more electrons", the compounds Nos. 1, 2, and 3 were added
respectively in an amount of 2.times.10.sup.-3 mol per 1 mol of
silver in silver halide.
[0461] Thereafter, as "a compound having an adsorptive group and a
reducing group", the compound Nos. 1 and 2 were added respectively
in an amount of 5.times.10.sup.-3 mol per 1 mol of silver
halide.
[0462] Further, water was added thereto to give the content of
silver of 38.2 g per 1 kg of the mixed emulsion for a coating
solution, and 1-(3-methylureidophenyl)-5-mercaptotetrazole was
added to give 0.34 g per 1 kg of the mixed emulsion for a coating
solution.
[0463] 2) Preparation of Dispersion of Silver Salt of Fatty
Acid
[0464] 88 kg of the recrystallized behenic acid, 422 L of distilled
water, 49.2 L of 5 mol/L sodium hydroxide aqueous solution, and 120
L of t-butyl alcohol were admixed, and subjected to reaction with
stirring at 75.degree. C. for one hour to give a solution of sodium
behenate. Separately, 206.2 L of an aqueous solution of 40.4 kg of
silver nitrate (pH 4.0) was provided, and kept at a temperature of
10.degree. C. A reaction vessel charged with 635 L of distilled
water and 30 L of t-butyl alcohol was kept at 30.degree. C., and
thereto were added the total amount of the solution of sodium
behenate and the total amount of the aqueous silver nitrate
solution with sufficient stirring at a constant flow rate over 93
minutes and 15 seconds, and 90 minutes, respectively. Upon this
operation, during first 11 minutes following the initiation of
adding the aqueous silver nitrate solution, the added material was
restricted to the aqueous silver nitrate solution alone. The
addition of the solution of sodium behenate was thereafter started,
and during 14 minutes and 15 seconds following the completion of
adding the aqueous silver nitrate solution, the added material was
restricted to the solution of sodium behenate alone. The
temperature inside of the reaction vessel was then set to
30.degree. C., and the temperature outside was controlled so that
the liquid temperature could be kept constant. In addition, the
temperature of a pipeline for the addition system of the solution
of sodium behenate was kept constant by circulation of warm water
outside of a double wall pipe, so that the temperature of the
liquid at an outlet in the leading edge of the nozzle for addition
was adjusted to be 75.degree. C. Further, the temperature of a
pipeline for the addition system of the aqueous silver nitrate
solution was kept constant by circulation of cool water outside of
a double wall pipe. Position at which the solution of sodium
behenate was added and the position, at which the aqueous silver
nitrate solution was added, was arranged symmetrically with a shaft
for stirring located at a center. Moreover, both of the positions
were adjusted to avoid contact with the reaction liquid.
[0465] After completing the addition of the solution of sodium
behenate, the mixture was left to stand at the temperature as it
was for 20 minutes. The temperature of the mixture was then
elevated to 35.degree. C. over 30 minutes followed by ripening for
210 minutes. Immediately after completing the ripening, solid
matters were filtered out with centrifugal filtration. The solid
matters were washed with water until the electric conductivity of
the filtrated water became 30 .mu.S/cm. A silver salt of a fatty
acid was thus obtained. The resulting solid matters were stored as
a wet cake without drying.
[0466] When the shape of the resulting particles of the silver
behenate was evaluated by an electron micrography, a crystal was
revealed having a=0.21 .mu.m, b=0.4 .mu.m and c=0.4 .mu.m on the
average value, with a mean aspect ratio of 2.1, and a variation
coefficient of an equivalent spherical diameter distribution of 11%
(a, b and c are as defined aforementioned.).
[0467] To the wet cake corresponding to 260 kg of a dry solid
matter content, were added 19.3 kg of poly(vinyl alcohol) (trade
name: PVA-217) and water to give the total amount of 1000 kg. Then,
slurry was obtained from the mixture using a dissolver blade.
Additionally, the slurry was subjected to preliminary dispersion
with a pipeline mixer (manufactured by MIZUHO Industrial Co., Ltd.:
PM-10 type).
[0468] Next, a stock liquid after the preliminary dispersion was
treated three times using a dispersing machine (trade name:
Microfluidizer M-610, manufactured by Microfluidex International
Corporation, using Z type Interaction Chamber) with the pressure
controlled to be 1150 kg/cm.sup.2 to give a dispersion of silver
behenate. For the cooling manipulation, coiled heat exchangers were
equipped in front of and behind the interaction chamber
respectively, and accordingly, the temperature for the dispersion
was set to be 18.degree. C. by regulating the temperature of the
cooling medium.
[0469] 3) Preparations of Reducing Agent Dispersion
[0470] <<Preparation of Reducing Agent-1
Dispersion>>
[0471] To 10 kg of reducing agent-1
(2,2'-methylenebis-(4-ethyl-6-tert-butylphenol)) and 16 kg of a 10%
by weight aqueous solution of modified poly(vinyl alcohol)
(manufactured by Kuraray Co., Ltd., Poval MP203) was added 10 kg of
water, and thoroughly mixed to give slurry.
[0472] This slurry was fed with a diaphragm pump, and was subjected
to dispersion with a horizontal sand mill (UVM-2: manufactured by
AIMEX Co., Ltd.) packed with zirconia beads having a mean particle
diameter of 0.5 mm for 3 hours. Thereafter, 0.2 g of a
benzisothiazolinone sodium salt and water were added thereto,
thereby adjusting the concentration of the reducing agent to be 25%
by weight. This dispersion was subjected to heat treatment at
60.degree. C. for 5 hours to obtain reducing agent-1 dispersion.
Particles of the reducing agent included in the resulting reducing
agent dispersion had a median diameter of 0.40 .mu.m, and a maximum
particle diameter of 1.4 .mu.m or less. The resultant reducing
agent dispersion was subjected to filtration with a polypropylene
filter having a pore size of 3.0 .mu.m to remove foreign substances
such as dust, and stored.
[0473] <<Preparation of Reducing Agent-2
Dispersion>>
[0474] To 10 kg of reducing agent-2
(6,6'-di-t-butyl-4,4'-dimethyl-2,2'-butylidenediphenol)) and 16 kg
of a 10% by weight aqueous solution of modified poly(vinyl alcohol)
(manufactured by Kuraray Co., Ltd., Poval MP-203) was added 10 kg
of water, and thoroughly mixed to give slurry. This slurry was fed
with a diaphragm pump, and was subjected to dispersion with a
horizontal sand mill (UVM-2: manufactured by AIMEX Co., Ltd.)
packed with zirconia beads having a mean particle diameter of 0.5
mm for 3 hours and 30 minutes. Thereafter, 0.2 g of a
benzoisothiazolinone sodium salt and water were added thereto,
thereby adjusting the concentration of the reducing agent to be 25%
by weight. This dispersion was warmed at 40.degree. C. for one
hour, followed by a subsequent heat treatment at 80.degree. C. for
one hour to obtain reducing agent-2 dispersion. Particles of the
reducing agent included in the resulting reducing agent dispersion
had a median diameter of 0.50 .mu.m, and a maximum particle
diameter of 1.6 .mu.m or less.
[0475] The resultant reducing agent dispersion was subjected to
filtration with a polypropylene filter having a pore size of 3.0
.mu.m to remove foreign substances such as dust, and stored.
[0476] 4) Preparation of Hydrogen Bonding Compound-1 Dispersion
[0477] To 10 kg of hydrogen bonding compound-1
(tri(4-t-butylphenyl)phosphineoxide) and 16 kg of a 10% by weight
aqueous solution of modified poly(vinyl alcohol) (manufactured by
Kuraray Co., Ltd., Poval MP203) was added 10 kg of water, and
thoroughly mixed to give slurry. This slurry was fed with a
diaphragm pump, and was subjected to dispersion with a horizontal
sand mill (UVM-2: manufactured by AIMEX Co., Ltd.) packed with
zirconia beads having a mean particle diameter of 0.5 mm for 4
hours. Thereafter, 0.2 g of a benzisothiazolinone sodium salt and
water were added thereto, thereby adjusting the concentration of
the hydrogen bonding compound to be 25% by weight. This dispersion
was warmed at 40.degree. C. for one hour, followed by a subsequent
heat treatment at 80.degree. C. for one hour to obtain hydrogen
bonding compound-1 dispersion. Particles of the hydrogen bonding
compound included in the resulting hydrogen bonding compound
dispersion had a median diameter of 0.45 .mu.m, and a maximum
particle diameter of 1.3 .mu.m or less. The resultant hydrogen
bonding compound dispersion was subjected to filtration with a
polypropylene filter having a pore size of 3.0 .mu.m to remove
foreign substances such as dust, and stored.
[0478] 5) Preparation of Development Accelerator-1 Dispersion
[0479] To 10 kg of development accelerator-1 and 20 kg of a 10% by
weight aqueous solution of modified poly(vinyl alcohol)
(manufactured by Kuraray Co., Ltd., Poval MP203) was added 10 kg of
water, and thoroughly mixed to give slurry. This slurry was fed
with a diaphragm pump, and was subjected to dispersion with a
horizontal sand mill (UVM-2: manufactured by AIMEX Co., Ltd.)
packed with zirconia beads having a mean particle diameter of 0.5
mm for 3 hours and 30 minutes. Thereafter, 0.2 g of a
benzisothiazolinone sodium salt and water were added thereto,
thereby adjusting the concentration of the development accelerator
to be 20% by weight. Accordingly, development accelerator-1
dispersion was obtained. Particles of the development accelerator
included in the resultant development accelerator dispersion had a
median diameter of 0.48 .mu.m, and a maximum particle diameter of
1.4 .mu.m or less. The resultant development accelerator dispersion
was subjected to filtration with a polypropylene filter having a
pore size of 3.0 .mu.m to remove foreign substances such as dust,
and stored.
[0480] 6) Preparations of Solid Dispersions of Development
Accelerator-2 and Color-tone-adjusting Agent-1
[0481] Also concerning solid dispersions of development
accelerator-2 and color-tone-adjusting agent-1, dispersion was
executed similar to the development accelerator-1, and thus
dispersions of 20% by weight and 15% by weight were respectively
obtained.
[0482] 7) Preparations of Organic Polyhalogen Compound
Dispersion
[0483] <<Preparation of Organic Polyhalogen Compound-1
Dispersion>>
[0484] 10 kg of organic polyhalogen compound-1 (tribromomethane
sulfonylbenzene), 10 kg of a 20% by weight aqueous solution of
modified poly(vinyl alcohol) (manufactured by Kuraray Co., Ltd.,
Poval MP203), 0.4 kg of a 20% by weight aqueous solution of sodium
triisopropylnaphthalenesulfonate and 14 kg of water were thoroughly
admixed to give slurry. This slurry was fed with a diaphragm pump,
and was subjected to dispersion with a horizontal sand mill (UVM-2:
manufactured by AIMEX Co., Ltd.) packed with zirconia beads having
a mean particle diameter of 0.5 mm for 5 hours. Thereafter, 0.2 g
of a benzisothiazolinone sodium salt and water were added thereto,
thereby adjusting the concentration of the organic polyhalogen
compound to be 26% by weight. Accordingly, organic polyhalogen
compound-1 dispersion was obtained. Particles of the organic
polyhalogen compound included in the resulting organic polyhalogen
compound dispersion had a median diameter of 0.41 .mu.m, and a
maximum particle diameter of 2.0 .mu.m or less. The resultant
organic polyhalogen compound dispersion was subjected to filtration
with a polypropylene filter having a pore size of 10.0 .mu.m to
remove foreign substances such as dust, and stored.
[0485] <<Preparation of Organic Polyhalogen Compound-2
Dispersion>>
[0486] 10 kg of organic polyhalogen compound-2
(N-butyl-3-tribromomethane sulfonylbenzamide), 20 kg of a 10% by
weight aqueous solution of modified poly(vinyl alcohol)
(manufactured by Kuraray Co., Ltd., Poval MP203) and 0.4 kg of a
20% by weight aqueous solution of sodium
triisopropylnaphthalenesulfonate were thoroughly admixed to give
slurry. This slurry was fed with a diaphragm pump, and was
subjected to dispersion with a horizontal sand mill (UVM-2:
manufactured by AIMEX Co., Ltd.) packed with zirconia beads having
a mean particle diameter of 0.5 mm for 5 hours. Thereafter, 0.2 g
of a benzisothiazolinone sodium salt and water were added thereto,
thereby adjusting the concentration of the organic polyhalogen
compound to be 30% by weight. This dispersion was heated at
40.degree. C. for 5 hours to obtain organic polyhalogen compound-2
dispersion. Particles of the organic polyhalogen compound included
in the resulting organic polyhalogen compound dispersion had a
median diameter of 0.40 .mu.m, and a maximum particle diameter of
1.3 .mu.m or less. The resultant organic polyhalogen compound
dispersion was subjected to filtration with a polypropylene filter
having a pore size of 3.0 .mu.m to remove foreign substances such
as dust, and stored.
[0487] 8) Preparation of Dispersion of Compound Represented by
Formula (SA)
[0488] The compound represented by formula (SA) shown in Table 1 in
an amount of 60 g and 150 g of a 10% by weight aqueous solution of
modified poly(vinyl alcohol) (manufactured by Kuraray Co., Ltd.,
Poval MP-203) were added to 90 g of water and thoroughly mixed to
give slurry. Zirconia beads having the mean particle diameter of
0.5 mm were provided in an amount of 720 g, and charged in a vessel
with the slurry. Dispersion was performed with a dispersing machine
(1/4G sand grinder mill: manufactured by AIMEX Co., Ltd.) for 15
hours. Thereto was added water to obtain a 20% by weight
dispersion. Particles included in the resulting dispersion had a
mean particle diameter of from 0.38 .mu.m to 0.45 .mu.m.
[0489] 9) Preparation of Phthalazine Compound-1 Solution
[0490] Modified poly(vinyl alcohol) MP-203 in an amount of 8 kg was
dissolved in 174.57 kg of water, and then thereto were added 3.15
kg of a 20% by weight aqueous solution of sodium
triisopropylnaphthalenesulfonate and 14.28 kg of a 70% by weight
aqueous solution of phthalazine compound-1 (6-isopropyl
phthalazine) to prepare a 5% by weight solution of phthalazine
compound-1.
[0491] 10) Preparations of Aqueous Solution of Mercapto
Compound
[0492] <<Preparation of Aqueous Solution of Mercapto
Compound-1>>
[0493] Mercapto compound-1 (1-(3-sulfophenyl)-5-mercaptotetrazole
sodium salt) in an amount of 7 g was dissolved in 993 g of water to
give a 0.7% by weight aqueous solution.
[0494] <<Preparation of Aqueous Solution of Mercapto
Compound-2>>
[0495] Mercapto compound-2
(1-(3-methylureidophenyl)-5-mercaptotetrazole) in an amount of 20 g
was dissolved in 980 g of water to give a 2.0% by weight aqueous
solution.
[0496] 11) Preparations of Pigment Dispersion and Aqueous Solution
of Dye
[0497] <<Preparation of Comparative Pigment-1
Dispersion>>
[0498] C.I. Pigment Blue 60 in an amount of 64 g and 6.4 g of DEMOL
N manufactured by Kao Corporation were added to 250 g of water and
thoroughly mixed to give slurry. Zirconia beads having the mean
particle diameter of 0.5 mm were provided in an amount of 800 g,
and charged in a vessel with the slurry. Dispersion was performed
with a dispersing machine (1/4G sand grinder mill: manufactured by
AIMEX Co., Ltd.) for 25 hours. Thereto was added water to adjust so
that the concentration of the pigment became 5% by weight to obtain
pigment-1 dispersion. Particles of the pigment included in the
resulting pigment dispersion had a mean particle diameter of 0.21
.mu.m.
[0499] <<Preparation of Aqueous Solution of Metal
Phthalocyanine Dye of the Invention>>
[0500] A 5% by weight aqueous solution of metal phthalocyanine dye
No. 11 was prepared.
[0501] 12) Preparation of Polymer Latex Liquid
[0502] <<Syntheses of Polymer Latex Having a Monomer
Component Represented by Formula (M)>>
[0503] Polymer latex Nos. P-1, P-2, and P-4, which are explained in
the aforementioned synthetic example-1 to -3, were used.
[0504] <<Preparation of SBR Latex Liquid>>
[0505] To a polymerization vessel of a gas monomer reaction
apparatus (manufactured by Taiatsu Techno Corporation, TAS-2J type)
were charged 287 g of distilled water, 7.73 g of a surfactant
(Pionin A-43-S (manufactured by TAKEMOTO OIL & FAT CO., LTD.):
solid matter content of 48.5% by weight), 14.06 mL of 1 mol/L
sodium hydroxide, 0.15 g of ethylenediamine tetraacetate
tetrasodium salt, 255 g of styrene, 11.25 g of acrylic acid, and
3.0 g of tert-dodecyl mercaptan, followed by sealing of the
reaction vessel and stirring at a stirring rate of 200 rpm.
Degassing was conducted with a vacuum pump, followed by repeating
nitrogen gas replacement several times. Thereto was injected 108.75
g of 1,3-butadiene, and the inner temperature was elevated to
60.degree. C. Thereto was added a solution of 1.875 g of ammonium
persulfate dissolved in 50 mL of water, and the mixture was stirred
for 5 hours as it stands. The temperature was further elevated to
90.degree. C., followed by stirring for 3 hours. After completing
the reaction, the inner temperature was lowered to reach to the
room temperature, and thereafter the mixture was treated by adding
1 mol/L sodium hydroxide and ammonium hydroxide to give the molar
ratio of Na.sup.+ ion:NH.sub.4.sup.+ ion=1:5.3, and thus, the pH of
the mixture was adjusted to 8.4. Thereafter, filtration with a
polypropylene filter having the pore size of 1.0 .mu.m was
conducted to remove foreign substances such as dust followed by
storage. Accordingly, SBR latex was obtained in an amount of 774.7
g. Upon the measurement of halogen ion by ion chromatography,
concentration of chloride ion was revealed to be 3 ppm. As a result
of the measurement of the concentration of the chelating agent by
high performance liquid chromatography, it was revealed to be 145
ppm.
[0506] The aforementioned latex had a mean particle diameter of 90
nm, Tg of 17.degree. C., a solid matter concentration of 44% by
weight, an equilibrium moisture content at 25.degree. C. and 60% RH
of 0.6% by weight, and an ionic conductance of 4.80 mS/cm
(measurement of the ionic conductance was performed using a
conductivity meter CM-30S manufactured by Toa Electronics Ltd. for
the latex stock solution (44% by weight) at 25.degree. C.).
2. Preparations of Coating Solution
[0507] 1) Preparation of Coating Solution for Image Forming
Layer
[0508] To the dispersion of the silver salt of fatty acid obtained
as described above in an amount of 1000 g were serially added
water, the dye or the pigment (shown in Table 1), the organic
polyhalogen compound-1 dispersion, the organic polyhalogen
compound-2 dispersion, the phthalazine compound-1 solution, the
polymer latex liquid (shown in Table 1), the reducing agent-1
dispersion, the reducing agent-2 dispersion, the hydrogen bonding
compound-1 dispersion, the development accelerator-1 dispersion,
the development accelerator-2 dispersion, the color-tone-adjusting
agent dispersion, the dispersion of the compound represented by
formula (SA), the mercapto compound-1 aqueous solution, the
mercapto compound-2 aqueous solution. Just prior to the coating,
the mixed emulsion A for coating solution in an amount of 140 g was
added thereto, followed by thorough mixing just prior to the
coating, which was fed directly to a coating die.
[0509] 2) Preparations of Coating Solution for Intermediate Layer
A
[0510] <<Coating Solution A-1 for Intermediate
Layer>>
[0511] The coating solution A-1 for the intermediate layer
contained poly(vinyl alcohol) (PVA) and acrylate latex in a mixing
ratio (mass ratio of solid content) of 56/44, as a binder.
[0512] To 1000 g of poly(vinyl alcohol) PVA-205 (manufactured by
Kuraray Co., Ltd.), 27 mL of a 5% by weight aqueous solution of
sodium di(2-ethylhexyl)sulfosuccinate, 4200 mL of a 19% by weight
liquid of methyl methacrylate/styrene/butyl acrylate/hydroxyethyl
methacrylate/acrylic acid copolymer (mass ratio of the
copolymerization of 57/8/28/5/2) latex, 27 mL of a 5% by weight
aqueous solution of aerosol OT (manufactured by American Cyanamid
Co.), and 135 mL of a 20% by weight aqueous solution of diammonium
phthalate was added water to give a total amount of 10000 g. The
mixture was adjusted with sodium hydroxide to give the pH of 7.5.
Accordingly, the coating solution for the intermediate layer was
prepared, and was fed to a coating die to provide 8.9 mL/m
[0513] <<Coating Solution A-2 for Intermediate
Layer>>
[0514] Preparation of coating solution A-2 for intermediate layer
was conducted in a similar manner to the process in the preparation
of coating solution A-1 for intermediate layer except that the
poly(vinyl alcohol) (PVA) and the acrylic latex were not added, but
instead, the polymer latex P-4 containing a monomer component
represented by formula (M) of the present invention was added to
make the same total coating amount thereof.
[0515] 3) Preparation of Coating Solution for Intermediate Layer
B
[0516] In 840 mL of water were dissolved 100 g of inert gelatin and
10 mg of benzoisothiazolinone, and thereto were added 180 g of a
19% by weight liquid of methyl methacrylate/styrene/butyl
acrylate/hydroxyethyl methacrylate/acrylic acid copolymer (mass
ratio of the copolymerization of 57/8/28/5/2) latex, 46 mL of a 15%
by weight methanol solution of phthalic acid, and 5.4 mL of a 5% by
weight aqueous solution of sodium di(2-ethylhexyl)sulfosuccinate,
and were mixed. Immediately before coating, 40 mL of a 4% by weight
chrome alum which had been mixed with a static mixer was fed to a
coating die so that the amount of the coating solution became 26.1
mL/m.sup.2.
[0517] Viscosity of the coating solution was 20 [mPas] which was
measured with a B type viscometer at 40.degree. C. (No. 1 rotor, 60
rpm).
[0518] 4) Preparation of Coating Solution for Outermost Layer
[0519] In 800 mL of water were dissolved 100 g of inert gelatin and
10 mg of benzoisothiazolinone, and thereto were added 40 g of a 10%
by weight liquid paraffin emulsion, 40 g of a 10% by weight
emulsion of dipentaerythritol hexa-isostearate, 180 g of a 19% by
weight liquid of methyl methacrylate/styrene/butyl
acrylate/hydroxyethyl methacrylate/acrylic acid copolymer (mass
ratio of the copolymerization of 57/8/28/5/2) latex, 40 mL of a 15%
by weight methanol solution of phthalic acid, 5.5 mL of a 1% by
weight solution of a fluorocarbon surfactant (F-1), 5.5 mL of a 1%
by weight aqueous solution of another fluorocarbon surfactant
(F-2), 28 mL of a 5% by weight aqueous solution of sodium
di(2-ethylhexyl)sulfosuccinate, 4 g of poly(methyl methacrylate)
fine particles (mean particle diameter of 0.7 .mu.m, volume
weighted mean distribution of 30%), and 21 g of poly(methyl
methacrylate) fine particles (mean particle diameter of 3.6 .mu.m,
volume weighted mean distribution of 60%), and the obtained mixture
was mixed, which was fed to a coating die so that 8.3 mL/m.sup.2
could be provided.
[0520] Viscosity of the coating solution was 19 [mPas] which was
measured with a B type viscometer at 40.degree. C. (No. 1 rotor, 60
rpm).
3. Preparations of Photothermographic Material-1 to -11
[0521] Reverse surface of the back surface was subjected to
simultaneous overlaying coating by a slide bead coating method in
order of coating solution for the image forming layer, the coating
solution for intermediate layer A, the coating solution for
intermediate layer B, and the coating solution for the outermost
layer, and thus sample of photothermographic material was produced.
The combination of the coating solution for the image forming layer
and the coating solution for the intermediate layer A is shown in
Table 1. In this method, the temperature of the coating solution
was adjusted to 31.degree. C. for the image forming layer and
intermediate layer A, to 36.degree. C. for intermediate layer B,
and to 37.degree. C. for the outermost layer. TABLE-US-00003 TABLE
1 Image Forming Layer Compound of Formula (SA) Dye Addition
Addition Sample Amount Amount Intermediate No. Binder No.
(g/m.sup.2) No. (g/m.sup.2) Layer A Note 1 Comparative -- --
Pigment-1 0.045 A-1 Comparative A (SBR) 2 Comparative SA-26 0.025
Pigment-1 0.045 A-1 Comparative A (SBR) 3 P-4 -- -- Pigment-1 0.045
A-1 Comparative 4 P-4 SA-26 0.025 No. 11 0.025 A-1 Invention 5 P-1
SA-26 0.025 No. 11 0.025 A-1 Invention 6 P-2 SA-26 0.025 No. 11
0.025 A-1 Invention 7 P-4 SA-27 0.070 No. 11 0.025 A-1 Invention 8
P-4 SA-40 0.070 No. 11 0.025 A-1 Invention 9 P-1 SA-26 0.025 No. 11
0.025 A-2 Invention 10 P-2 SA-26 0.025 No. 11 0.025 A-2 Invention
11 P-4 SA-26 0.025 No. 11 0.025 A-2 Invention
[0522] The coating amount of each compound (g/m.sup.2) for the
image forming is as follows. TABLE-US-00004 Organic silver salt
4.88 Dye or pigment (see Table 1) Organic polyhalogen compound-1
0.108 Organic polyhalogen compound-2 0.225 Phthalazine compound-1
0.161 Binder (see Table 1) Reducing agent-1 0.36 Reducing agent-2
0.36 Hydrogen bonding compound-1 0.522 Development accelerator-1
0.010 Development accelerator-2 0.007 Color-tone-adjusting agent-1
0.006 Compound represented by formula (SA) (see Table 1) Mercapto
compound-1 0.0018 Mercapto compound-2 0.0108 Silver halide (on the
basis of Ag content) 0.09
[0523] Conditions for coating and drying are as follows.
[0524] Coating was performed at the speed of 160 m/min. The
clearance between the leading end of the coating die and the
support was from 0.10 mm to 0.30 mm. The pressure in the vacuum
chamber was set to be lower than atmospheric pressure by 196 Pa to
882 Pa. The support was decharged by ionic wind.
[0525] In the subsequent cooling zone, the coating solution was
cooled by wind having the dry-bulb temperature of from 10.degree.
C. to 20.degree. C. Transportation with no contact was carried out,
and the coated support was dried with an air of the dry-bulb of
from 23.degree. C. to 45.degree. C. and the wet-bulb of from
15.degree. C. to 21.degree. C. in a helical type contactless drying
apparatus.
[0526] After drying, moisture conditioning was performed at
25.degree. C. in the humidity of from 40% RH to 60% RH. Then, the
film surface was heated to be from 70.degree. C. to 90.degree. C.,
and after heating, the film surface was cooled to 25.degree. C.
[0527] Thus prepared photothermographic material had a level of
matting of 550 seconds on the image forming layer side, and 130
seconds on the back surface as Beck's smoothness. In addition,
measurement of pH of the film surface on the image forming layer
side gave the result of 6.0.
[0528] Chemical structures of the compounds used in Examples of the
invention are shown below. ##STR72## Compound 1 that is
one-electron-oxidized to provide a one-electron oxidation product
which releases one or more electrons ##STR73## Compound 2 that is
one-electron-oxidized to provide a one-electron oxidation product
which releases one or more electrons ##STR74## Compound 3 that is
one-electron-oxidized to provide a one-electron oxidation product
which releases one or more electrons ##STR75## Compound 1 having
adsorptive group and reducing group ##STR76## Compound 2 having
adsorptive group and reducing group ##STR77## ##STR78## ##STR79##
4. Evaluation of Photographic Properties 4-1. Preparation
[0529] The obtained sample was cut into a half-cut size (43 cm in
length.times.35 cm in width), and was wrapped with the following
packaging material under an environment of 25.degree. C. and 50%
RH, and stored for 2 weeks at an ambient temperature.
[0530] <<Packaging Material>>
[0531] A film laminated with PET 10 .mu.m/PE 12 .mu.m/aluminum foil
9 .mu.m/Ny 15 .mu.m/polyethylene 50 .mu.m containing carbon at 3%
by weight:
[0532] oxygen permeability at 25.degree. C.: 0.02 mLatm.sup.-1
m.sup.-2 day.sup.-1;
[0533] vapor permeability at 25.degree. C.: 0.10
gatm.sup.-.mu.m.sup.-2 day.sup.-1.
4-2. Exposure and Thermal Development
[0534] To each sample, exposure and thermal development (24 seconds
in total with 4 panel heaters set to 112.degree. C.-119.degree.
C.-121.degree. C.-121.degree. C.) with Fuji Medical Dry Laser
Imager FM-DPL (equipped with 660 nm laser diode having a maximum
output of 60 mW (IIIB)) were performed. Evaluation on the obtained
image was performed with a densitometer.
4-3. Terms for Evaluation
[0535] 1) Image Tone
[0536] The unexposed portion after thermal development was
evaluated sensory by ten persons by the following rankings. The
most selected ranking among ten persons was taken as the ranking
for the specimen.
[0537] A: Low density and highly clear, and favor for transparent
photographic materials;
[0538] B: Slightly colored, but allowable level for transparent
photographic materials;
[0539] C: Strongly colored, and not allowable level for transparent
photographic materials.
[0540] 2) Sharpness
[0541] The sample was subjected to similar exposure described
above, but with a rectangular pattern, and thermal development. The
value obtained by dividing the density difference in the
rectangular pattern at a spatial frequency of 5 lines/mm by the
density difference at 0.01 lines/mm was taken as A. The value A of
other samples was represented by the relative value (%) based on
the value A obtained for sample No. 1 as the standard, which was
regard as the sharpness. The higher is the value, the better is the
sharpness.
[0542] 3) Image Storability
[0543] <Rubbing Test by Fingers>
[0544] After thermal development, the unexposed portion of the
sample was touched by a finger wearing a cotton glove followed by
rubbing the surface back and forth thereby for 20 times over 20 cm
width. Thereafter, the stain attached on the cotton glove was
sensory evaluated.
[0545] The higher is the point, the better is the performance.
[0546] 3 points: No transferred stain is seen;
[0547] 2 points: Slightly blue tine stain is seen;
[0548] 1 point: Clearly remarkable blue tine stain is seen.
[0549] <Water Dropping Test>
[0550] After thermal development, 100 .mu.L of water was dropped on
the unexposed portion and wiped out after 10 seconds. The trace
wiped out was observed and sensory evaluated. It is preferred that
the color tint of the wiped portion is not different from the
neighboring portion.
[0551] 3 points: No color difference between the wiped portion and
the neighboring portion is seen;
[0552] 2 points: The wiped portion is slightly decolored compared
with the neighboring portion;
[0553] 1 point: The wiped portion is decolored, and thereby clear
trace is seen.
[0554] <Image Storability to Light>
[0555] As an evaluation of the image storability with respect to
light, the print-out performances were evaluated for samples stored
in an accelerated condition.
[0556] Thermally developed samples were left for 5 days on a
transmission-type lighting viewer (an illumination condition of
7,000 lux) at 25.degree. C. and 60 RH %. Thereafter, changes in
image tone before and after the above accelerated test were sensory
evaluated over the portion having an image density of 1.0.
[0557] .circleincircle.: Changes in image tone are not
observed;
[0558] .largecircle.: Changes in image tone are slightly observed,
but practical level for image reading;
[0559] .DELTA.: Apparent changes in image tone are seen and
laborious levels for image reading;
[0560] x: Changes in image tone are big, and difficult for image
reading.
[0561] 4) Results of Evaluation
[0562] The obtained results are shown in Table 2.
[0563] The samples of the present invention exhibit excellent color
tone and high sharpness. Furthermore, even in various accelerated
conditions, the samples of the present invention show excellent
image storability.
[0564] Particularly, sample Nos. 9 to 11 show more excellent
performances. TABLE-US-00005 TABLE 2 Water Rubbing Image Sample
Dropping Test by Storability No. Sharpness Image Tone Test Fingers
to Light Note 1 97 A 3 3 .DELTA. Comparative 2 97 C 3 3 .DELTA.
Comparative 3 97 C 3 3 .DELTA. Comparative 4 99 A 2 2
.circleincircle. Invention 5 99 A 2 2 .circleincircle. Invention 6
99 A 2 2 .circleincircle. Invention 7 99 A 2 2 .circleincircle.
Invention 8 99 A 2 2 .circleincircle. Invention 9 99 A 3 3
.circleincircle. Invention 10 99 A 3 3 .circleincircle. Invention
11 99 A 3 3 .circleincircle. Invention
Example 2
[0565] Samples were prepared similar to Example 1 except that the
dye No. 11 of formula (PC-1) was changed to Nos. 32, 2, and 31,
respectively. The prepared samples were evaluated similar to
Example 1. As a result, the samples of the present invention
exhibit excellent performances similar to Example 1.
* * * * *