U.S. patent application number 11/334745 was filed with the patent office on 2006-08-03 for light emitting device and method of making the same.
This patent application is currently assigned to TOYODA GOSEI CO., LTD.. Invention is credited to Yoshinobu Suehiro, Seiji Yamaguchi.
Application Number | 20060171152 11/334745 |
Document ID | / |
Family ID | 36756325 |
Filed Date | 2006-08-03 |
United States Patent
Application |
20060171152 |
Kind Code |
A1 |
Suehiro; Yoshinobu ; et
al. |
August 3, 2006 |
Light emitting device and method of making the same
Abstract
A light emitting device having: a flip-mounting type light
emitting element; a substrate on which the light emitting element
is mounted, the substrate being of an inorganic material; a sealing
portion to seal the light emitting element, the sealing portion
being of an inorganic sealing material; an optical-shaped portion
formed nearly semispherical, the optical-shaped portion being of
the inorganic sealing material; and a phosphor portion formed
covering the optical-shaped portion.
Inventors: |
Suehiro; Yoshinobu;
(Aichi-ken, JP) ; Yamaguchi; Seiji; (Aichi-ken,
JP) |
Correspondence
Address: |
MCGINN INTELLECTUAL PROPERTY LAW GROUP, PLLC
8321 OLD COURTHOUSE ROAD
SUITE 200
VIENNA
VA
22182-3817
US
|
Assignee: |
TOYODA GOSEI CO., LTD.
Aichi-ken
JP
|
Family ID: |
36756325 |
Appl. No.: |
11/334745 |
Filed: |
January 19, 2006 |
Current U.S.
Class: |
362/363 ;
257/E33.059 |
Current CPC
Class: |
H01L 2924/12041
20130101; H01L 2924/00014 20130101; H01L 2224/48465 20130101; H01L
33/44 20130101; H01L 2924/00011 20130101; H01L 2924/00014 20130101;
H01L 2224/48091 20130101; H01L 2224/48465 20130101; H01L 2224/16225
20130101; H01L 33/486 20130101; H01L 2924/1815 20130101; H01L
2224/0401 20130101; H01L 2924/00 20130101; H01L 2924/00 20130101;
H01L 2924/00 20130101; H01L 2224/0401 20130101; H01L 2224/48091
20130101; H01L 2224/48227 20130101; H01L 2924/00014 20130101; H01L
2224/48465 20130101; H01L 2224/48227 20130101; H01L 2924/12041
20130101; H01L 24/97 20130101; H01L 2924/00011 20130101; H01L
2224/48091 20130101; H01L 33/56 20130101; H01L 33/507 20130101;
F21K 9/00 20130101 |
Class at
Publication: |
362/363 |
International
Class: |
F21S 13/10 20060101
F21S013/10 |
Foreign Application Data
Date |
Code |
Application Number |
Jan 20, 2005 |
JP |
2005-012810 |
Feb 3, 2005 |
JP |
2005-027484 |
Claims
1. A light emitting device, comprising: a flip-mounting type light
emitting element; a substrate on which the light emitting element
is mounted, the substrate comprising an inorganic material; a
sealing portion to seal the light emitting element, the sealing
portion comprising an inorganic sealing material; an optical-shaped
portion formed nearly semispherical, the optical-shaped portion
comprising the inorganic sealing material; and a phosphor portion
formed covering the optical-shaped portion.
2. A light emitting device, comprising: a flip-mounting type light
emitting element; a substrate on which the light emitting element
is mounted, the substrate comprising an inorganic material; a
sealing portion to seal the light emitting element, the sealing
portion comprising an inorganic sealing material; an optical-shaped
portion formed nearly semispherical, the optical-shaped portion
comprising the inorganic sealing material; and a phosphor portion
formed covering the optical-shaped portion, wherein the inorganic
material comprises a thermal expansion coefficient equivalent to
that of the light emitting element, and the inorganic sealing
material comprises a thermal expansion coefficient equivalent to
that of the substrate and the light emitting element.
3. The light emitting device according to claim 1, wherein: the
inorganic sealing material comprises a glass material.
4. The light emitting device according to claim 1, wherein: the
phosphor portion comprises an inorganic material and a
phosphor.
5. The light emitting device according to claim 4, wherein: the
phosphor portion comprises a thermal expansion coefficient greater
than the sealing portion.
6. The light emitting device according to claim 1, wherein: the
phosphor portion comprises a dichroic mirror that a plurality of
materials with different refractive indexes are alternately
laminated, and a phosphor layer formed on the dichroic mirror.
7. The light emitting device according to claim 1, wherein: the
phosphor portion comprises a low-melting fluoride glass.
8. The light emitting device according to claim 1, wherein: the
optical-shaped portion comprises a dimension to define a ratio to a
width of the light emitting element of 2.sup.1/2 or more and 10 or
less.
9. A light emitting device, comprising: a light emitting element; a
substrate on which the light emitting element is mounted, the
substrate comprising an inorganic material; a sealing portion to
seal the light emitting element, the sealing portion comprising an
inorganic sealing material; and a coating portion formed covering
the sealing portion, wherein the sealing portion comprises a
cutting face at which an interface of the inorganic sealing
material and the substrate is exposed and by which the light
emitting element is surrounded, and the sealing portion is covered
with the coating portion on an entire surface thereof.
10. A light emitting device, comprising: a light emitting element;
a substrate on which the light emitting element is mounted, the
substrate comprising an inorganic material; a sealing portion to
seal the light emitting element, the sealing portion comprising an
inorganic sealing material; and a coating portion formed covering
the sealing portion, wherein the sealing portion comprises a
cutting face by which the light emitting element is surrounded, and
the sealing portion is covered with the coating portion on an
entire surface thereof that light emitted from the light emitting
element reaches directly.
11. The light emitting device according to claim 9, wherein: the
light emitting element comprises a flip-mounting type light
emitting element, and the substrate comprises the inorganic
material that comprises a thermal expansion coefficient equivalent
to that of the sealing portion.
12. The light emitting device according to claim 9, wherein: the
coating portion comprises a light-transmitting inorganic
material.
13. The light emitting device according to claim 9, wherein: the
coating portion comprises a phosphor-containing material.
14. The light emitting device according to claim 13, wherein: the
coating portion comprises a dichroic mirror.
15. A method of making a light emitting device, comprising: a first
step that a substrate comprising an inorganic material is provided;
a second stet that a plurality of light emitting elements are
mounted on the substrate; a third step that the substrate with the
plurality of light emitting elements mounted thereon is sealed with
a sealing material; a fourth step that a cutting portion is
provided in the sealing material; a fifth step that a coating is
formed on a surface of the sealing material including an exposed
portion formed by providing the cutting portion; and a sixth step
that the substrate with the sealing material is separated along the
cutting potion.
16. The method according to claim 15, wherein: the coating in the
fifth step is formed by sputtering.
17. The method according to claim 15, wherein: the coating in the
fifth step is formed by electrostatic coating.
Description
[0001] The present application is based on Japanese patent
application Nos. 2005-012810 and 2005-027484, the entire contents
of which are incorporated herein by reference.
BACKGROUND OF THE INVENTION
[0002] 1. Field of the Invention
[0003] This invention relates to a wavelength-conversion type light
emitting device to wavelength-convert a light emitted from a light
emitting element and, in particular, to a wavelength-conversion
type light emitting device that is excellent in reliability, stable
in brightness over a long term, and excellent in unevenness of
emission color.
[0004] Further, this invention relates to a light emitting device
that the light emitting element is sealed with a glass sealing
material and, in particular, to a light emitting device that is
excellent in mass productivity, in sealing property and
deterioration resistance under a high-temperature and high-humidity
environment, and in evenness of emission color.
[0005] Further, this invention relates to a method of making the
above light emitting device.
[0006] 2. Description of the Related Art
[0007] A light emitting device is conventionally known that uses an
LED (light emitting diode) element as a light source. In recent
years, such a light emitting device is in wide use for an
automobile lighting apparatus, a backlight light source in LCD
devices, a lamp in small electronic device etc., and the other uses
are also promising.
[0008] A semiconductor light emitting device is proposed that white
light is radiated by wavelength-converting a light emitted from the
LED element by a phosphor (e.g., JP-A-2004-221619, [0009], [0014]
and FIG. 1 thereof)
[0009] The semiconductor light emitting device in JP-A-2004-221619
comprises an LED with a lens-shaped resin sealing portion, and a
transparent phosphor cover which is disposed around the resin
sealing portion. The LED is a GaN-based semiconductor light
emitting element which has an emission peak in 430 to 480 nm. The
phosphor cover comprises a thin-film resin which has an elasticity
to be in close contact with the resin sealing portion, and a
phosphor which radiates a fluorescent light by being excited by
light emitted from the semiconductor light emitting element.
[0010] The semiconductor light emitting device in JP-A-2004-221619
is advantageous in that a desired emission color with high
brightness can be obtained by mixing a light emitted from the
semiconductor light emitting element with a light
wavelength-converted by the phosphor since the phosphor cover is
disposed around the resin sealing portion.
[0011] However, the semiconductor light emitting device in
JP-A-2004-221619 has the following problems.
[0012] (1) It is difficult to secure its long-term reliability
since the resin sealing portion and the phosphor cover deteriorate
due to the light emitted from the GaN-based semiconductor light
emitting element. Further, the brightness of the light emitting
device lowers due to the deterioration.
[0013] (2) The profile accuracy of the phosphor cover and the
uniformity of phosphor dispersed must be enhanced in consideration
of the unevenness in emission color and the light distribution
property since the light radiation characteristics of the
semiconductor light emitting device are dependent on the shaping
property of the resin sealing portion and the phosphor cover.
Therefore, the manufacturing process will be complicated and the
manufacturing cost will increase.
[0014] On the other hand, a resin-sealed type LED is conventionally
known that an LED element is sealed with a transparent resin
material such as an epoxy resin.
[0015] It is known that the resin-sealed type LED is subjected to a
deterioration such as yellowing when the transparent resin material
is reacted with intense light while it is excellent in sealing
workability due to using the transparent resin material. Especially
in using a group III nitride-based compound semiconductor light
emitting element to emit short-wavelength light, the transparent
resin material near the element can be yellowed due to high-energy
light emitted from the element and heat generated from the element.
Therefore, the light extraction efficiency may lower
significantly.
[0016] To prevent the deterioration of the sealing material, a
light emitting device is proposed that uses a low-melting glass as
the sealing material (e.g., JP-A-11-177129, [0007] and FIG. 1
thereof).
[0017] FIG. 15 is a cross sectional view showing the light emitting
device disclosed in JP-A-11-177129. The light emitting device 50
comprises an LED element 51, a printed-circuit board 52, a wiring
pattern 53 formed on the surface of the printed-circuit board 52, a
wire 54 which electrically connects between the LED element 51 and
the wiring pattern 53, and the low-melting glass 55 which seals the
LED element 51 and the wire 54, and has a refractive index of about
2 which is near 2.3 or so, the refractive index of a GaN-based LED
element.
[0018] The light emitting device in JP-A-11-177129 is advantageous
in that a light returned to the inside of the LED element 51 due to
total reflection on the surface thereof can be reduced by sealing
the LED element 51 with the low-melting glass 55 which has a
refractive index close to that of the GaN-based LED element. Thus,
the amount of light entering into the low-melting glass 55 after
being emitted from the LED element 51 can be increased. As a
result, the light extraction efficiency can be enhanced as compared
to the conventional device with the LED element sealed with the
epoxy resin.
[0019] However, the light emitting device in JP-A-11-177129 has
problems in practical manufacturing and mass productivity since the
low-melting glass cannot be easy processed like the epoxy
resin.
[0020] For example, when the LED element is sealed with the glass
in high-viscosity state so as to prevent the heat damage of the LED
element, the wire may be deformed by the high-viscosity glass so
that the electrical short-circuiting or the disconnection of wire
may occur. Even when using the glass in low-viscosity state, the
molding as shown in FIG. 15 is difficult to conduct. On the other
hand, a resin printed-circuit board cannot endure the processing
temperature, and an inorganic printed-circuit board may be broken
when being pressed by a mold. Further, since the glass-sealed LED
element requires an individual processing, not a batch processing
due to the high-temperature processing, it cannot be applied to the
mass production.
[0021] As described above, a phosphor white LED with a good
long-term reliability is never proposed, and a glass-sealed LED
with a good mass productivity is never proposed.
SUMMARY OF THE INVENTION
[0022] It is an object of the invention to provide a light emitting
device that is excellent in long-term reliability so that the
brightness can be stabilized over a long term, and excellent in
evenness of emission color.
[0023] It is a further object of the invention to provide a light
emitting device that is excellent in mass productivity, in sealing
property and deterioration resistance under a high-temperature and
high-humidity environment, and in evenness of emission color.
[0024] It is a further object of the invention to provide a method
of making the light emitting device.
[0025] (1) According to one aspect of the invention, a light
emitting device comprises:
[0026] a flip-mounting type light emitting element;
[0027] a substrate on which the light emitting element is mounted,
the substrate comprising an inorganic material;
[0028] a sealing portion to seal the light emitting element, the
sealing portion comprising an inorganic sealing material;
[0029] an optical-shaped portion formed nearly semispherical, the
optical-shaped portion comprising the inorganic sealing material;
and
[0030] a phosphor portion formed covering the optical-shaped
portion.
[0031] (2) According to another aspect of the invention, a light
emitting device comprises:
[0032] a flip-mounting type light emitting element;
[0033] a substrate on which the light emitting element is mounted,
the substrate comprising an inorganic material;
[0034] a sealing portion to seal the light emitting element, the
sealing portion comprising an inorganic sealing material;
[0035] an optical-shaped portion formed nearly semispherical, the
optical-shaped portion comprising the inorganic sealing material;
and
[0036] a phosphor portion formed covering the optical-shaped
portion,
[0037] wherein the inorganic material comprises a thermal expansion
coefficient equivalent to that of the light emitting element,
and
[0038] the inorganic sealing material comprises a thermal expansion
coefficient equivalent to that of the substrate and the light
emitting element.
[0039] In the above invention (1) or (2), the following
modifications and changes can be made.
[0040] (i) The inorganic sealing material comprises a glass
material.
[0041] (ii) The phosphor portion comprises an inorganic material
and a phosphor.
[0042] (iii) The phosphor portion comprises a thermal expansion
coefficient greater than the sealing portion.
[0043] (iv) The phosphor portion comprises a dichroic mirror that a
plurality of materials with different refractive indexes are
alternately laminated, and a phosphor layer formed on the dichroic
mirror.
[0044] (v) The the phosphor portion comprises a low-melting
fluoride glass.
[0045] (vi) The optical-shaped portion comprises a dimension to
define a ratio to a width of the light emitting element of
2.sup.1/2 or more and 10 or less.
[0046] (3) According to another aspect of the invention, a light
emitting device comprises:
[0047] a light emitting element;
[0048] a substrate on which the light emitting element is mounted,
the substrate comprising an inorganic material;
[0049] a sealing portion to seal the light emitting element, the
sealing portion comprising an inorganic sealing material; and
[0050] a coating portion formed covering the sealing portion,
[0051] wherein the sealing portion comprises a cutting face at
which an interface of the inorganic sealing material and the
substrate is exposed and by which the light emitting element is
surrounded, and
[0052] the sealing portion is covered with the coating portion on
an entire surface thereof.
[0053] (4) According to another aspect of the invention, a light
emitting device comprises:
[0054] a light emitting element;
[0055] a substrate on which the light emitting element is mounted,
the substrate comprising an inorganic material;
[0056] a sealing portion to seal the light emitting element, the
sealing portion comprising an inorganic sealing material; and
[0057] a coating portion formed covering the sealing portion,
[0058] wherein the sealing portion comprises a cutting face by
which the light emitting element is surrounded, and
[0059] the sealing portion is covered with the coating portion on
an entire surface thereof that light emitted from the light
emitting element reaches directly.
[0060] In the above invention (3) or (4), the following
modifications and changes can be made.
[0061] (vii) The light emitting element comprises a flip-mounting
type light emitting element, and
[0062] the substrate comprises the inorganic material that
comprises a thermal expansion coefficient equivalent to that of the
sealing portion.
[0063] (viii) The coating portion comprises a light-transmitting
inorganic material.
[0064] (ix) The coating portion comprises a phosphor-containing
material.
[0065] (x) The coating portion comprises a dichroic mirror.
[0066] (5) According to another aspect of the invention, a method
of making a light emitting device comprises:
[0067] a first step that a substrate comprising an inorganic
material is provided;
[0068] a second stet that a plurality of light emitting elements
are mounted on the substrate;
[0069] a third step that the substrate with the plurality of light
emitting elements mounted thereon is sealed with a sealing
material;
[0070] a fourth step that a cutting portion is provided in the
sealing material;
[0071] a fifth step that a coating is formed on a surface of the
sealing material including an exposed portion formed by providing
the cutting portion; and
[0072] a sixth step that the substrate with the sealing material is
separated along the cutting potion.
[0073] In the above invention (5), the following modifications and
changes can be made.
[0074] (xi) The coating in the fifth step is formed by
sputtering.
[0075] (xii) The coating in the fifth step is formed by
electrostatic coating.
ADVANTAGES OF THE INVENTION
[0076] According to the invention, since the light emitting element
and the substrate both made of the inorganic material are sealed
with the inorganic sealing material, the sealing property and
reliability can be enhanced. Further, deterioration caused by light
emitted from the light emitting element can be suppressed, and a
stable brightness can be kept without unevenness in emission color
over a long term.
[0077] Furthermore, since the sealing portion and the substrate are
covered with the light-transmitting inorganic coating portion, the
water resistance of the sealing portion can be enhanced and a good
adhesion between the substrate and the sealing portion can be
secured. Further, even in high humidity environment, it can have a
good sealing property and deterioration resistance.
BRIEF DESCRIPTION OF THE DRAWINGS
[0078] The preferred embodiments according to the invention will be
explained below referring to the drawings, wherein:
[0079] FIG. 1A is a cross sectional view showing a light emitting
device (herein also called LED) in a first preferred embodiment
according to the invention;
[0080] FIG. 1B is a schematic diagram illustrating light radiation
on the surface of a glass sealing portion;
[0081] FIGS. 2A to 2E are cross sectional views showing a method of
making the LED in the first embodiment;
[0082] FIG. 3 is a cross sectional view showing a light emitting
device in a second preferred embodiment according to the
invention;
[0083] FIG. 4 is a cross sectional view showing a light emitting
device in a third preferred embodiment according to the
invention;
[0084] FIG. 5A is a plain view showing an LED in a fifth preferred
embodiment according to the invention;
[0085] FIG. 5B is a cross sectional view cut along a line B-B in
FIG. 5A;
[0086] FIG. 6A is a cross sectional view showing an LED lamp in a
sixth preferred embodiment according to the invention;
[0087] FIG. 6B is a cross sectional view showing: a light-emitting
portion mounted on the LED lamp in FIG. 6A;
[0088] FIG. 7 is a cross sectional view showing a light emitting
device in a seventh preferred embodiment according to the
invention;
[0089] FIG. 8A to 8C are cross sectional views showing a wiring
formation step to a glass preparation step in a method of making
the LED in FIG. 7;
[0090] FIG. 9A to 9D are cross sectional views showing a glass
sealing step to an LED separation step in the method of making the
LED in FIG. 7;
[0091] FIG. 10 is a cross sectional view showing a light emitting
device in an eighth preferred embodiment according to the
invention;
[0092] FIG. 11 is a cross sectional view showing a light emitting
device (LED) in a ninth preferred embodiment according to the
invention;
[0093] FIG. 12A to 12C are cross sectional views showing a wiring
formation step to a glass preparation step in a method of making
the LED in FIG. 11;
[0094] FIG. 13A to 13C are cross sectional views showing a glass
sealing step to an LED separation step in the method of making the
LED in FIG. 11;
[0095] FIG. 14A to 14D are cross sectional views showing a glass
sealing step to an LED separation step in a method of making a
concave groove in an LED in a tenth preferred embodiment according
to the invention; and
[0096] FIG. 15 is a cross sectional view showing the conventional
light emitting device in JP-A-11-177129.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
First Embodiment
[0097] FIG. 1A is a cross sectional view showing a light emitting
device in the first preferred embodiment according to the
invention. FIG. 1B is a schematic diagram illustrating light
radiation on the surface of a glass sealing portion.
Components of the Device
[0098] As shown in FIG. 1A, the LED 1 comprises: a flip-chip type
LED element 2; an Al.sub.2O.sub.3 substrate 3, as an inorganic
material substrate, provided with circuit patterns 4A, 4B, and via
holes 3A; an Au bump 5 to electrically connect between the circuit
pattern 4B and an electrode of the LED element 2; and a glass
sealing portion 6 that is made of an inorganic sealing material to
seal the Al.sub.2O.sub.3 substrate 3 and the LED element 2 and is
provided with an optical-shaped portion 6A formed
semispherical.
(Details of the Components)
[0099] The LED element 2 comprises, sequentially grown on an
underlying sapphire substrate, an AlN buffer layer and a GaN-based
semiconductor layer including an n-GaN layer, a light-emitting
layer, and a p-GaN layer. It has a horizontal type electrode
structure that a part of the n-GaN layer is exposed as an
n-electrode formation region by etching the p-GaN layer through the
n-GaN layer. It is flip-chip mounted on the circuit pattern 4B
through the Au bump 5. The LED element 2 has a central emission
wavelength of about 470 nm and a thermal expansion coefficient of
7.times.10.sup.-6/.degree. C. The ratio of the width of the
optical-shaped portion 6A of the LED 1 and the width (i.e., the
maximum width, the length of a diagonal line in case of a square)
of the LED element 2 is determined to be 2.sup.1/2 or more and 10
or less.
[0100] The Al.sub.2O.sub.3 substrate 3 has a thermal expansion
coefficient of 7.times.10.sup.-6/.degree. C., which is nearly
equivalent to that of the LED element 2. It is provided with the
circuit patterns 4A, 4B and the via pattern 4C which are made of
tungsten (W)--nickel (Ni)--gold (Au).
[0101] The glass sealing portion 6 is made of low-melting glass
which can be processed by hot pressing at a low melting point of
600.degree. C. or less, and it has a thermal expansion coefficient
(7.times.10.sup.-6/.degree. C.) nearly equivalent to that of the
LED element 2 and the Al.sub.2O.sub.3 substrate 3. It is, on its
surface, provided with the optical-shaped portion 6A which is
formed semispherical, and a phosphor film 6B which is formed, as a
phosphor portion, on the surface of the optical-shaped portion
6A.
[0102] The phosphor film 6B is formed by coating an acrylic coating
material containing Ce:YAG (yttrium aluminum garnet) phosphor on
the surface of the optical-shaped portion 6A and then drying it. As
shown in FIG. 1B, light Lb reaching the phosphor film 6B while
transmitting the glass sealing portion 6 is irradiated to the
phosphor and, thereby, yellow lights Lb1 to Lb3 are radiated from
the phosphor.
(Method of Making the LED 1)
[0103] A method of making the LED 1 of the first embodiment will be
described below.
[0104] FIGS. 2A to 2E are cross sectional views showing the method
of making the LED 1 in the first embodiment. Hereinafter, the
Al.sub.2O.sub.3 substrate 3 is used which is previously provided
with a V groove 3G for separation and a via hole.
[0105] (Wiring Formation Step)
[0106] As shown in FIG. 2A, a W paste is screen-printed on the
Al.sub.2O.sub.3 substrate 3 according to the circuit pattern. Then,
the Al.sub.2O.sub.3 substrate 3 with the W paste printed thereon is
heated at 1500.degree. C. to burn the W onto the Al.sub.2O.sub.3
substrate 3. Then, Ni plating and Au plating are provided on the W
to form the circuit patterns 4A, 4B and the via pattern 4C.
[0107] (LED Element Mounting Step)
[0108] Then, as shown in FIG. 2B, the LED element 2 is flip-mounted
through the Au bump 5 on the circuit pattern 4B of the
Al.sub.2O.sub.3 substrate 3.
[0109] (Low-Melting Glass Preparation Step)
[0110] Then, as shown in FIG. 2C, a plate-like
P.sub.2O.sub.5--ZnO--Li.sub.2O-based low-melting glass 60 is
parallel placed over the Al.sub.2O.sub.3 substrate 3.
[0111] (Glass Sealing Step)
[0112] Then, as shown in FIG. 2D, the low-melting glass 60 is
hot-pressed at 550 to 500.degree. C. in a nitrogen atmosphere. The
low-melting glass 60 is bonded to the surface of the substrate
through oxides contained in the Al.sub.2O.sub.3 substrate 3 and the
glass, and the glass sealing portion 6 is molded to have the
semispherical optical-shaped portion 6A according to the form of a
pressing mold.
[0113] (Phosphor Film Formation Step)
[0114] Then, as shown in FIG. 2E, with the plural LED's 1 formed in
an array, the phosphor-containing acrylic coating material is
coated on the surface of the glass sealing portion 6 and then dried
to form the phosphor film 6B on the surface of the glass sealing
portion 6.
[0115] Then, the LED 1 is separated by cutting the Al.sub.2O.sub.3
substrate 3 along the V groove 3G.
(Operation of the LED 1)
[0116] The operation of the first embodiment will be described
below.
[0117] When current is fed through the circuit pattern 4A from a
power supply (not shown), the light-emitting layer is current-fed
through the electrode of the LED element 2. Thereupon, the
light-emitting layer emits blue light. The blue light is inputted
from the GaN-based semiconductor layer through the sapphire
substrate to the glass sealing portion 6, reaching the
optical-shaped portion 6A. The blue light reaching the
optical-shaped portion 6A is then inputted to the phosphor film 6B.
Thereupon, the phosphor contained in the phosphor film 6B radiates
yellow light while being excited by the inputted blue light.
Thereupon, white light is generated by mixing the yellow light with
the blue light, and externally radiated from the phosphor film
6B.
Effects of the First Embodiment
[0118] The effects of the first embodiment are as follows.
[0119] (1) Since the LED element 2 is sealed with the glass sealing
portion 6 with the semispherical optical-shaped portion 6A,
deterioration in the sealing material due to the self-heating or
self-irradiating of the LED element 2 does not occur so that the
LED 1 can have an excellent sealing property of the LED element 2
and a stable brightness over a long term. Further, the bonding
strength between the glass sealing portion 6 and the
Al.sub.2O.sub.3 substrate 3 can be enhanced since they have an
equivalent thermal expansion coefficient each other, different from
the case of using the resin sealing material. Thus, the small LED 1
can be obtained with a high reliability.
[0120] (2) The phosphor film 6B is disposed at a suitable distance
from the light extracting surface (i.e., bottom of the sapphire
substrate) of the LED element 2, and the phosphor film 6B is
provided with a uniform thickness. Thereby, even in case of the
downsized LED 1, unevenness in emission color can be prevented as
compared to the case of a phosphor-dispersed type which is likely
to have unevenness in emission color caused by a difference in
optical path length inside the phosphor layer. For example, in the
phosphor-dispersed type, light with a long optical path length is
shifted to yellow since it has a long distance to transmit the
phosphor layer, and light with a short optical path length is
likely to be blue since it has a short distance to transmit the
phosphor layer. Thus, in this embodiment, the difference in optical
path length can be substantially removed by forming the uniform
thin-film phosphor layer on the surface of the optical-shaped
portion 6A.
[0121] The optical-shaped portion 6A is formed nearly semispherical
so as to allow the suitable distance from the LED element 2 to the
phosphor film 6B so that lights emitted from the LED element 2 in
any directions have a substantially even incident angle, around the
perpendicular incident angle, to the optical-shaped portion 6A. By
configuring thus, interface reflection loss at the optical-shaped
portion 6A can be minimized such that light reflected on the
surface of the optical-shaped portion 6A or on the phosphor film 6B
is absorbed again by the LED element 2. Further, since the incident
angle to the phosphor film 6B can be substantially uniformed,
unevenness in emission color can be prevented. Further, since
unevenness in emission color or reduction in light extraction
efficiency can be prevented even in case of the downsized LED 1,
the amount of phosphor used can be reduced and, thereby, the
manufacturing cost can be reduced.
[0122] (3) The phosphor film 6B can be formed by coating the
phosphor-containing acrylic coating material on the plural LED's 1
disposed on the substrate. Thus, the good phosphor film 6B can be
formed together on the plural LED's 1 to enhance the productivity.
Further, since the acrylic resin is excellent in light resistance,
deterioration in the phosphor film 6B can be prevented.
[0123] Although in the first embodiment the LED 1 is separated
through the V groove 3G formed on the Al.sub.2O.sub.3 substrate 3,
the LED LED 1 may be diced by using a dicer.
[0124] The LED element 2 mounted on the Al.sub.2O.sub.3 substrate 3
may be a GaP-based or GaAs-based LED element other than the
GaN-based LED element.
[0125] The phosphor can be chosen from phosphors to be excited by
the emission wavelength of an LED element used.
[0126] The optical-shaped portion 6A is intended not to focusing of
light but to external light radiation with high efficiency and good
evenness in emission color. If the focusing characteristic is
required, a focusing optical system can be provided such that the
LED 1 is further resin-molded.
[0127] The ratio of the width of the optical-shaped portion 6A and
the width of the LED element 2 is preferably 5 or less although it
depends on the sealing material, the bonding strength to the
substrate and the damage under processing conditions etc.
Second Embodiment
[0128] FIG. 3 is a cross sectional view showing a light emitting
device in the second preferred embodiment according to the
invention. Hereinafter, like components are indicated by the same
numerals used in the first embodiment.
(Components of the Device)
[0129] The LED 1 of the second embodiment is different from that of
the first embodiment in that a phosphor-containing glass layer 6C
is used in place of the phosphor film 6B of the first
embodiment.
(Details of the Components)
[0130] The phosphor-containing glass layer 6C is made of a mixture
material (with a melting point of about 300.degree. C.) that a
phosphor particle with an average outside diameter of 10 .mu.m is
mixed with a fluoride low-melting glass particle with an average
outside diameter of 10 .mu.m. The phosphor-containing glass layer
6C is formed integrally on the surface of the glass sealing portion
6 with the optical-shaped portion 6A by conducting the
electrostatic coating of the mixture material while heating the
glass sealing portion 6 at 300.degree. C. and applying a voltage
thereto and then heating it at 350.degree. C.
Effects of the Second Embodiment
[0131] In the second embodiment, since it is glass-sealed, the
electrostatic coating can be conducted by applying the voltage
thereto while heating it. Further, since the mixture material of
the phosphor particle and the fluoride low-melting glass particle
is electrostatically adhered to the surface of the glass sealing
portion 6, an effect other than the effects of the first embodiment
can be obtained that the mixture material can be, with a uniform
film thickness, adhered to the uneven surface of the glass sealing
portion 6 and the phosphor-containing glass layer 6C with a uniform
thickness can be easy formed by fusion bonding. Further, since the
fluoride coating of fluoride low-melting glass is formed on the
surface of the glass sealing portion 6, the humidity resistance of
the LED 1 can be further enhanced.
[0132] Glass materials are likely to be cracked due to difference
of thermal expansion coefficient. However, since the fluorine
low-melting glass with a thermal expansion coefficient greater than
the glass sealing portion 6 is adhered onto the semispherical glass
sealing portion 6, stress in a direction likely to cause the
cracking can be suppressed when it is cooled to room temperature
from the melted state free of stress. Namely, it is composed such
that only compressive stress is generated except tensile stress and
shear stress. In this regard, the fluorine low-melting glass with
the phosphor particle contained therein needs to have a thermal
expansion coefficient greater than the glass sealing portion 6.
Third Embodiment
[0133] FIG. 4 is a cross sectional view showing a light emitting
device in the third preferred embodiment according to the
invention.
(Components of the Device)
[0134] The LED 1 of the third embodiment is different from that of
the first embodiment in that a dichroic mirror 6D is formed between
the glass sealing portion 6 and the phosphor film 6B such that it
prevents the re-entering of light radiated from the phosphor to the
glass sealing portion 6.
(Details of the Components)
[0135] The dichroic mirror 6D is formed by laminating alternately
TiO.sub.2 film and SiO.sub.2 film and severs to transmit light of
less than 500 nm and to reflect light of more than 500 nm. Thus,
the dichroic mirror 6D can transmit blue light of 470 nm emitted
from the LED element 2 and reflect yellow light radiated from the
phosphor of the phosphor film 6B to prevent the re-entering thereof
to the glass sealing portion 6.
Effects of the Third Embodiment
[0136] In the third embodiment, the brightness can be enhanced in
addition to the effects of the first embodiment since the dichroic
mirror 6D is provided between the glass sealing portion 6 and the
phosphor film 6B. Namely, it can be prevented that the yellow light
radiated from the phosphor film 6B is re-entered to the glass
sealing portion 6 and absorbed in the LED element 2 to reduce the
light extraction efficiency of the LED 1.
[0137] Further, since the TiO.sub.2 film and SiO.sub.2 film also
are a humidity-resistant coating material, the humidity resistance
of the device can be further enhanced.
Fourth Embodiment
[0138] The fourth embodiment is constructed such that the phosphor
film 6B is formed by sputtering on the optical-shaped portion 6A of
the LED 1 as described in the third embodiment.
Effects of the Fourth Embodiment
[0139] In the fourth embodiment, by forming the phosphor film 6B by
sputtering, the phosphor film 6B can have a high phosphor
concentration with high accuracy and, therefore, can have the same
effects as the third embodiment. As compared to the third
embodiment, yellow light generated from the phosphor film 6B is
more likely to be radiated to the direction of the glass sealing
portion 6 due to the high phosphor concentration. However, since
the dichroic mirror 6D can reflect the yellow light being radiated
to the direction of the glass sealing portion 6, the mixing of the
yellow light and blue light can be promoted to obtain white light
without unevenness in emission color.
Fifth Embodiment
[0140] FIG. 5A is a plain view showing an LED in the fifth
preferred embodiment according to the invention. FIG. 5B is a cross
sectional view cut along a line B-B in FIG. 5A.
(Components of the Device)
[0141] The fifth embodiment is different from the third embodiment
in that the LED 1 is provided with plural light-emitting portions
10 of 9=3.times.3 which have as a light source a ultraviolet LED
element 2 with a central emission wavelength of 370 nm formed on
the Al.sub.2O.sub.3 substrate 3, the dichroic mirror 6D is formed
covering the surface of the plural light-emitting portions 10, and
the phosphor film 6B is further formed on the surface.
(Details of the Components)
[0142] The Al.sub.2O.sub.3 substrate 3 is provided with a
heat-radiating pattern 4D that is made of copper foil and allows
heat generated from the plural LED elements 2 to be radiated
outside of the substrate.
[0143] The phosphor film 6B contains R, G and B phosphors at a
predetermined ratio to be excited by ultraviolet light emitted from
the LED element 2, and it radiates white light based on the mixing
of R, G and B visible lights generated by being excited.
[0144] The dichroic mirror 6D is formed by laminating alternately
Ta.sub.2O.sub.5 film and SiO.sub.2 film and severs to transmit
ultraviolet light emitted from the LED element 2 and to reflect the
R, G and B visible lights radiated from the phosphor film 6B to
prevent the re-entering thereof to the glass sealing portion 6.
Effects of the Fifth Embodiment
[0145] In the fifth embodiment, the plural light-emitting portions
10 are formed on the Al.sub.2O.sub.3 substrate 3 with the
ultraviolet LED element 2 having high emission efficiency and the
phosphor film 6B containing the R, G and B phosphors. Therefore,
the LED 1 can radiate white light with a color rendering property
at high brightness, in addition to the effects of the third
embodiment.
[0146] Further, even when the ultraviolet LED element 2 is used,
the sealing material does not deteriorate since the LED 1 is sealed
with the glass sealing portion 6. Thus, the LED 1 can have a high
reliability over a long term while using the ultraviolet LED
element 2 with the high emission efficiency as a light source.
[0147] Although the LED 1 of the fifth embodiment has the nine
light-emitting portions 10 formed on the Al.sub.2O.sub.3 substrate
3, the number of the light-emitting portions 10 may be changed.
Sixth Embodiment
[0148] FIG. 6A is a cross sectional view showing an LED lamp in the
sixth preferred embodiment according to the invention. FIG. 6B is a
cross sectional view showing a light-emitting portion mounted on
the LED lamp in FIG. 6A.
(Components of the Device)
[0149] The LED lamp 100 comprises a case 20 made of nylon resin, a
light-emitting portion 10 mounted on an element mounting surface 21
formed at the bottom of a concave portion of the case 20, a
phosphor film 22A which covers an opening of the case 20 and
contains R, G and B phosphors, and a dichroic mirror 23 which is
laminated on the phosphor film 22A. The dichroic mirror 23 serves
to transmit visible light and to reflect ultraviolet light. The
light-emitting portion 10 comprises the ultraviolet LED element 2
as a light source, and the dichroic mirror 6D formed on the
optical-shaped portion 6A to transmit visible light and to reflect
ultraviolet light.
[0150] The case 20 comprises a reflection surface 22 formed curved
from the element mounting surface 21 to the opening of the case 20,
a circuit pattern 24A formed on the bottom of the case 20 for
external circuit connection, a circuit pattern 24B formed on the
element mounting surface 21 for the mounting of the light-emitting
portion 10, and an internal wiring pattern 24C to connect between
the circuit pattern 24A and the circuit pattern 24B.
(Operation of the LED Lamp 100)
[0151] The operation of the sixth embodiment will be described
below.
[0152] When current is fed through the circuit pattern 24A from a
power supply (not shown), the light-emitting layer is current-fed
through the electrode of the LED element 2. Thereupon, the
light-emitting layer emits blue light. The blue light is inputted
from the GaN-based semiconductor layer through the sapphire
substrate to the glass sealing portion 6, reaching the
optical-shaped portion 6A. The blue light reaching the
optical-shaped portion 6A is then transmitted through the dichroic
mirror 6D, radiated outside of the light-emitting portion 10.
[0153] Light radiated laterally from the light-emitting portion 10
is inputted to the phosphor film 22A formed on the reflection
surface 22, exciting the R, G and B phosphors therein and then
reflected in directions according to the curved face of the
reflection surface 22. The reflected light is mixed with
ultraviolet light transmitted through the dichroic mirror 6D of the
light-emitting portion 10 to generate visible light. The visible
light is transmitted through the dichroic mirror 23 and radiated
outside of the case 20.
[0154] On the other hand, light radiated upward from the optical
fiber main body 10 is inputted to the phosphor film 22A covering
the case 20, exciting the R, G and B phosphors therein. Excited
light radiated from the R, G and B phosphors is mixed with
ultraviolet light transmitted through the dichroic mirror 6D of the
light-emitting portion 10 to generate visible light. The visible
light is transmitted through the dichroic mirror 23 and radiated
outside of the case 20.
Effects of the Sixth Embodiment
[0155] In the sixth embodiment, although the phosphor film 22A is
formed on the side of the case 20 while being separated from the
light-emitting portion 10, the LED lamp 100 can have high
brightness and reliability without unevenness in emission
color.
[0156] The ultraviolet LED element 2 may be replaced by the blue
LED element 2 and the R, G and B phosphors contained in the
phosphor film 22A may be replaced by a yellow phosphor such as YAG.
Thereby, white light can be radiated outside of the LED lamp
100.
Seventh Embodiment
[0157] FIG. 7 is a cross sectional view showing a light emitting
device in the seventh preferred embodiment according to the
invention.
(Components of the Device)
[0158] As shown in FIG. 7, the LED 1 comprises: a flip-chip type
LED element 2; an Al.sub.2O.sub.3 substrate 3, as an inorganic
material substrate, provided with circuit patterns 4A, 4B, and via
holes 3A; an Au bump 5 to electrically connect between the circuit
pattern 4B and an electrode of the LED element 2; and a glass
sealing portion 6 that is made of an inorganic sealing material to
seal the Al.sub.2O.sub.3 substrate 3 and the LED element 2.
(Details of the Components)
[0159] The LED element 2 comprises, sequentially grown on an
underlying sapphire substrate, an AlN buffer layer and a GaN-based
semiconductor layer including an n-GaN layer, a light-emitting
layer, and a p-GaN layer. It has a horizontal type electrode
structure that a part of the n-GaN layer is exposed as an
n-electrode formation region by etching the p-GaN layer through the
n-GaN layer. It is flip-chip mounted on the circuit pattern 4B
through the Au bump 5. The LED element 2 has a central emission
wavelength of about 470 nm and a thermal expansion coefficient of
7.times.10.sup.-6/.degree. C. The ratio of the width of the LED 1
and the width of the LED element 2 is determined to be 1 or more
and 5 or less.
[0160] The Al.sub.2O.sub.3 substrate 3 has a thermal expansion
coefficient of 7.times.10.sup.-6/.degree. C., which is nearly
equivalent to that of the LED element 2. It is provided with the
circuit patterns 4A, 4B and the via pattern 4C which are made of
tungsten (W)--nickel (Ni)--gold (Au) on its element mounting
surface, via hole 3A and bottom surface. Further, it is provided
with a step portion 3B at a portion corresponding to an outer edge
of the LED 1.
[0161] The glass sealing portion 6 is made of low-melting glass
which can be processed by hot pressing at a low melting point of
600.degree. C. or less, and it has a thermal expansion coefficient
(7.times.10.sup.-6/.degree. C.) nearly equivalent to that of the
LED element 2 and the Al.sub.2O.sub.3 substrate 3. It is, on its
surface, provided with the optical-shaped portion 6A which is
formed semispherical, and an Al.sub.2O.sub.3 coating film 6F which
is formed on the surface of the optical-shaped portion 6A.
[0162] The Al.sub.2O.sub.3 coating film 6F is formed by sputtering
Al.sub.2O.sub.3 on the surface of the optical-shaped portion 6A and
then drying it. The Al.sub.2O.sub.3 coating film 6F is provided
with an end-face protecting portion 6E which covers the end face of
the glass sealing portion 6 and the step portion 3B.
(Method of Making the LED 1)
[0163] A method of making the LED 1 of the seventh embodiment will
be described below.
[0164] FIG. 8A to 8C are cross sectional views showing a wiring
formation step to a glass preparation step in the method of making
the LED in FIG. 7. FIG. 9A to 9D are cross sectional views showing
a glass sealing step to an LED separation step in the method of
making the LED in FIG. 7.
[0165] (Wiring Formation Step)
[0166] As shown in FIG. 8A, a W paste is screen-printed on the
Al.sub.2O.sub.3 substrate 3 according to the circuit pattern. Then,
the Al.sub.2O.sub.3 substrate 3 with the W paste printed thereon is
heated at 1500.degree. C. to burn the W-onto the Al.sub.2O.sub.3
substrate 3. Then, Ni plating and Au plating are provided on the W
to form the circuit patterns 4A, 4B and the via pattern 4C.
[0167] (LED Element Mounting Step)
[0168] Then, as shown in FIG. 8B, the LED element 2 is flip-mounted
through the Au bump 5 on the circuit pattern 4B of the
Al.sub.2O.sub.3 substrate 3.
[0169] (Low-Melting Glass Preparation Step)
[0170] Then, as shown in FIG. 8C, a plate-like
P.sub.2O.sub.5--ZnO--Li.sub.2O-based low-melting glass 60 is
parallel placed over the Al.sub.2O.sub.3 substrate 3.
[0171] (Glass Sealing Step)
[0172] Then, as shown in FIG. 9A, the low-melting glass 60 is
hot-pressed at 550 to 500.degree. C. in a nitrogen atmosphere. The
low-melting glass 60 is bonded to the surface of the substrate
through oxides contained in the Al.sub.2O.sub.3 substrate 3 and the
glass, and the glass sealing portion 6 is molded to have the
semispherical optical-shaped portion 6A according to the form of a
pressing mold.
[0173] (Groove Formation Step)
[0174] Then, as shown in FIG. 9B, a groove 30 is formed by
half-cutting a thin portion of the glass sealing portion 6 by using
a dicing saw. The groove 30 has such a depth that can prevent the
separation of the Al.sub.2O.sub.3 substrate 3. In this state, the
interface of the glass sealing portion 6 and the Al.sub.2O.sub.3
substrate 3 is exposed, and a part corresponding to the LED 1 is,
in plain view thereof, surrounded by the groove 30 as a cutting
face.
[0175] (Coating Film Formation Step)
[0176] Then as shown in FIG. 9C, the Al.sub.2O.sub.3 coating film
6F is formed by sputtering to cover the surface of the glass
sealing portion 6. In this state, the entire surface of the part
corresponding to the LED 1 surrounded by the groove 30 is covered
with the Al.sub.2O.sub.3 coating film 6F.
[0177] (LED Separation Step)
[0178] Then, as shown in FIG. 9D, the LED 1 is separated by cutting
the Al.sub.2O.sub.3 substrate 3 along the groove 30. The LED 1
separated has the end face of the glass sealing portion 6 covered
with the Al.sub.2O.sub.3 coating film.
(Operation of the LED 1)
[0179] The operation of the seventh embodiment will be described
below.
[0180] When current is fed through the circuit pattern 4A from a
power supply (not shown), the light-emitting layer is current-fed
through the electrode of the LED element 2. Thereupon, the
light-emitting layer emits blue light. The blue light is inputted
from the GaN-based semiconductor layer through the sapphire
substrate to the glass sealing portion 6, reaching the
optical-shaped portion 6A. The blue light reaching the
optical-shaped portion 6A is externally radiated through the
Al.sub.2O.sub.3 coating film 6F.
Effects of the Seventh Embodiment
[0181] The effects of the seventh embodiment are as follows.
[0182] (1) After the LED element 2 is seal with glass, the grove 30
is formed penetrating through the glass sealing portion 6 into the
Al.sub.2O.sub.3 substrate 3, and the Al.sub.2O.sub.3 coating film
6F is formed on the surface of the glass as well as the groove 30
to protect the surface of the glass. Therefore, even when the LED 1
is separated, the end face of the glass sealing portion 6 can be
thereby protected without being exposed. Thus, even when the glass
sealing portion 6 has a relatively low humidity resistance due to
its restrictions such as reduction in glass melting point,
adjustment in thermal expansion coefficient or refractive index
etc., the glass sealing portion 6 can be stably used over a long
term without deteriorating under high temperature and humidity
environment.
[0183] Further, since the Al.sub.2O.sub.3 coating film 6F is formed
by sputtering, it can be easy formed in the groove 30.
[0184] (2) Since moisture does not penetrate through between the
glass sealing portion 6 and the A.sub.2O.sub.3 substrate 3 due to
the Al.sub.2O.sub.3 coating film 6F, reduction in bonding strength
between the glass sealing portion 6 and the Al.sub.2O.sub.3
substrate 3 can be prevented.
[0185] (3) Since the groove 30 is formed by the half-cutting with
the dicing saw after the formation of the glass sealing portion 6,
the LED 1 can be easy separated after the formation of the
Al.sub.2O.sub.3 coating film 6F. Thus, the productivity can be
enhanced.
[0186] Although in the seventh embodiment the Al.sub.2O.sub.3
coating film 6F is formed on the surface of the glass sealing
portion 6, the coating film 6F may be made of SiO.sub.2, SiN,
MgF.sub.2 etc. other than Al.sub.2O.sub.3.
[0187] Although in the seventh embodiment the groove 30 is formed
by using the dicing saw, the groove 30 may be formed by laser
light. The laser processing allows reduction in process time and
enhancement in productivity. Especially short-time pulse
irradiation such as femtosecond laser pulse allows the formation of
a smooth-faced groove.
[0188] It is confirmed by experiments that glass can be well bonded
to the Al.sub.2O.sub.3 when it has a thermal expansion coefficient
of 6.9.times.10.sup.-6/.degree. C. to 7.7.times.10.sup.-6/.degree.
C. Although the bonding strength depends on the size, melting
characteristic and stress direction of glass, it does not always
need to have a difference in thermal expansion coefficient within a
few %. Thus, even when the difference is about 15%, it only has to
have a sufficient bonding strength.
Eighth Embodiment
[0189] FIG. 10 is a cross sectional view showing a light emitting
device in the eighth preferred embodiment according to the
invention. Like components are indicated by the same numerals used
in the seventh embodiment.
(Components of the Device)
[0190] The LED 1 of the eighth embodiment is different from that of
the seventh embodiment in that a dichroic mirror 6D and a
phosphor-containing glass layer 6C are used place of the
Al.sub.2O.sub.3 coating film 6F.
(Details of the Components)
[0191] The dichroic mirror 6D is formed by laminating alternately
TiO2 film and SiO.sub.2 film and severs to transmit light of less
than 500 nm and to reflect light of more than 500 nm. Thus, the
dichroic mirror 6D can transmit blue light of 470 nm emitted from
the LED element 2 and reflect yellow light radiated-from the
phosphor of the phosphor-containing glass layer 6C to prevent the
re-entering thereof to the glass sealing portion 6.
[0192] The phosphor-containing glass layer 6C is made of a mixture
material (with a melting point of about 300.degree. C.) that a
phosphor particle with an average outside diameter of 10 .mu.m is
mixed with a fluoride low-melting glass particle with an average
outside diameter of 10 .mu.m. The phosphor-containing glass layer
6C is formed integrally on the surface of the glass sealing portion
6C is formed integrally on the surface of the glass sealing
electrostatic coating of the mixture material while heating glass
sealing portion 6 at 300.degree. C. and applying a voltage thereto
and then heating it at 350.degree. C. In this case, the phosphor
used is to be excited by blue light emitted from the LED element 2.
For example, the phosphor can be Ce:YAG (yttrium aluminum garnet)
phosphor.
Effects of the Eighth Embodiment
[0193] In the eighth embodiment, since the dichroic mirror 6D and
the phosphor-containing glass layer 6C are formed on the entire
surface of the glass sealing portion 6, unevenness in emission
color can be suppressed.
[0194] Further, since it is glass-sealed, the electrostatic coating
can be conducted by applying the voltage thereto while heating it.
Further, since the mixture material of the phosphor particle and
the fluoride low-melting glass particle is electrostatically
adhered to the surface of the glass sealing portion 6, an effect
other than the effects of the seventh embodiment can be obtained
that the mixture material can be, with a uniform film thickness,
adhered to the uneven surface of the glass sealing portion 6 and
the phosphor-containing glass layer 6C with a uniform thickness can
be easy formed by fusion bonding.
[0195] Further, since the fluoride coating of fluoride low-melting
glass is formed on the surface of the glass sealing portion 6, the
humidity resistance of the LED 1 can be further enhanced.
Ninth Embodiment
[0196] FIG. 11 is a cross sectional view showing a light emitting
device (LED) in the ninth preferred embodiment according to the
invention.
(Components of the Device)
[0197] The LED 1 of the ninth embodiment is different from that of
the seventh or eighth embodiment in that it is provided with the
Al.sub.2O.sub.3 substrate 3 having a concave portion 3C with a
height different from the element mounting surface, the glass
sealing portion 6 is formed covering the concave portion 3C as well
as the Al.sub.2O.sub.3 substrate 3 and the LED element 2, and that
it is provided with only the phosphor-containing glass layer 6C
instead of the Al.sub.2O.sub.3 coating film 6F and the dichroic
mirror 6D.
(Details of the Components)
[0198] The glass sealing portion 6 is formed by hot pressing to
cover the concave portion 3C as well as having the optical-shaped
portion 6A. The phosphor-containing glass layer 6C as described in
the eighth embodiment is formed on the surface of the glass sealing
portion 6.
(Method of Making the LED 1)
[0199] A method of making the LED 1 of the ninth embodiment will be
described below.
[0200] FIG. 12A to 12C are cross sectional views showing a wiring
formation step to a glass preparation step in the method of making
the LED in FIG. 11. FIG. 13A to 13C are cross sectional views
showing a glass sealing step to an LED separation step in the
method of making the LED in FIG. 11.
[0201] (Wiring Formation Step)
[0202] As shown in FIG. 12A, a W paste is, according to the circuit
pattern, screen-printed on the Al.sub.2O.sub.3 substrate 3. Then,
the Al.sub.2O.sub.3 substrate 3 with the W paste printed thereon is
heated at 1500.degree. C. to burn the W onto the Al.sub.2O.sub.3
substrate 3. Then, Ni plating and Au plating are provided on the W
to form the circuit patterns 4A, 4B and the via pattern 4C. The
concave portion 3C is formed by cutting or sand-blasting after the
formation of the circuit patterns 4A, 4B and the via pattern 4C.
Alternatively, it may be formed before the formation.
[0203] (LED Element Mounting Step)
[0204] Then, as shown in FIG. 12B, the LED element 2 is
flip-mounted through the Au bump 5 on the circuit pattern 4B of the
Al.sub.2O.sub.3 substrate 3.
[0205] (Low-Melting Glass Preparation Step) Then, as shown in FIG.
12C, a plate-like P.sub.2O.sub.5--ZnO--Li.sub.2O-based low-melting
glass 60 is parallel placed over the Al.sub.2O.sub.3 substrate
3.
[0206] (Glass Sealing Step)
[0207] Then, as shown in FIG. 13A, the low-melting glass 60 is
hot-pressed at 550 to 500.degree. C. in a nitrogen atmosphere. The
low-melting glass 60 is bonded to the surface of the substrate
through oxides contained in the Al.sub.2O.sub.3 substrate 3 and the
glass, and the glass sealing portion 6 is molded to have the
semispherical optical-shaped portion 6A according to the form of a
pressing mold. In this stage, the glass sealing portion 6 is
provided with a concave groove 6G which is a thin portion
corresponding to the concave portion 3C.
[0208] (Coating Film Formation Step)
[0209] Then, as shown in FIG. 13B, the phosphor-containing glass
layer 6C is formed.
[0210] (LED Separation Step)
[0211] Then, as shown in FIG. 13C, the LED 1 is separated by
cutting the substrate along the concave groove 6G by using a
dicer.
Effects of the Ninth Embodiment
[0212] In the ninth embodiment, the Al.sub.2O.sub.3 substrate 3
with the concave portion 3C formed thereon is sealed with the
low-melting glass 60, the low-melting glass 60 is concave-convex
sealed in close contact with the side face of the concave portion
3C based on internal stress to be generated by heat contraction of
the low-melting glass 60. Thus, since the glass sealing portion 6
is in close contact with the glass sealing portion 6 at the edge of
the LED 1, the separation of glass or the penetration of moisture
can be very effectively prevented.
[0213] Although in the ninth embodiment the glass sealing portion 6
is slightly exposed at the end-face protecting portion 6E, the
optical influence thereof is negligible such that unevenness in
emission color does not occur since light emitted from the LED
element 2 does not reach directly this portion. Meanwhile, in this
case, the glass sealing portion 6 is desirably of a material with
high humidity resistance.
[0214] Optionally, the Al.sub.2O.sub.3 coating film may be formed
in addition to the phosphor-containing glass layer 6C. Glass may be
clouded at its surface in a high temperature and humidity
environment. However, when the Al.sub.2O.sub.3 coating film is
formed on the glass surface that light emitted from the LED element
2 reaches directly, the optical characteristics do not change.
Tenth Embodiment
[0215] FIG. 14A to 14D are cross sectional views showing a glass
sealing step to an LED separation step in a method of making a
concave groove in an LED in the tenth preferred embodiment
according to the invention.
(Components of the Device)
[0216] The tenth embodiment is constructed such the glass sealing
portion 6 is prevented from being exposed at the concave portion 3C
as described in the ninth embodiment.
(Method of Making the Device)
[0217] The method of making the concave groove in the LED will be
described below.
[0218] (Glass Sealing Step)
[0219] As shown in FIG. 14A, the glass sealing step is conducted
such that the concave groove 6G corresponding to the concave
portion 3C has a groove width not to disturb the groove shaping
process as described later. The other process is the same as
described in the glass sealing step in FIG. 13A.
[0220] (Groove Formation Step)
[0221] As shown in FIG. 14B, the groove formation step is conducted
such that the groove 30 is formed by irradiating laser light to the
concave groove 6G of the glass sealing portion 6 to allow the
Al.sub.2O.sub.3 substrate 3 to be exposed. Instead of the
irradiation of the laser light, the dicing with a dicer may be
conducted to form the groove 30 with a depth reaching the
Al.sub.2O.sub.3 substrate 3.
[0222] (Coating Film Formation Step)
[0223] As shown in FIG. 14C, the coating film formation step is
conducted such that the Al.sub.2O.sub.3 coating film 6F is formed
covering the Al.sub.2O.sub.3 substrate 3 exposed in the groove
formation step so as to coat the concave groove 6G exposed by the
irradiation of the laser light.
[0224] (LED Separation Step)
[0225] As shown in FIG. 14D, the LED separation step is conducted
such that LED 1 is individually separated by cutting the substrate
at the groove 30 by a dicer after the coating film formation step.
The end-face of the separated LED 1 is concave-convex sealed with
the glass sealing portion 6 at the concave portion 3C of the
Al.sub.2O.sub.3 substrate 3, and the interface of the glass sealing
portion 6 and the Al.sub.2O.sub.3 substrate 3 is sealed with the
Al.sub.2O.sub.3 coating film 6F.
Effects of the Tenth Embodiment
[0226] In the tenth embodiment, the Al.sub.2O.sub.3 substrate 3
with the concave portion 3C is glass-sealed with the low-melting
glass 60, and the groove 30 formed at the glass-sealed concave
portion 3C is coated with the Al.sub.2O.sub.3 coating film 6F.
Therefore, a high bonding strength can be obtained between the
Al.sub.2O.sub.3 substrate 3 and the glass sealing portion 6 based
on the heat contraction of the low-melting glass. Further, a high
humidity resistance and deterioration resistance can be obtained by
thus protecting the entire surface of the glass sealing portion
6.
[0227] Although the invention has been described with respect to
the specific embodiments for complete and clear disclosure, the
appended claims are not to be thus limited but are to be construed
as embodying all modifications and alternative constructions that
may occur to one skilled in the art which fairly fall within the
basic teaching herein set forth.
* * * * *