U.S. patent application number 11/332430 was filed with the patent office on 2006-06-01 for production of lithium compounds directly from lithium containing brines.
Invention is credited to Daniel Alfred Boryta, Teresita Frianeza Kullberg, Anthony Michael Thurston.
Application Number | 20060115407 11/332430 |
Document ID | / |
Family ID | 29716254 |
Filed Date | 2006-06-01 |
United States Patent
Application |
20060115407 |
Kind Code |
A1 |
Boryta; Daniel Alfred ; et
al. |
June 1, 2006 |
Production of lithium compounds directly from lithium containing
brines
Abstract
Methods and apparatus for the production of low sodium lithium
carbonate and lithium chloride from a brine concentrated to about
6.0 wt % lithium are disclosed. Methods and apparatus for direct
recovery of technical grade lithium chloride from the concentrated
brine are also disclosed.
Inventors: |
Boryta; Daniel Alfred;
(Cherryville, NC) ; Kullberg; Teresita Frianeza;
(Gastonia, NC) ; Thurston; Anthony Michael;
(Edmond, OK) |
Correspondence
Address: |
FULBRIGHT & JAWORSKI, LLP
666 FIFTH AVE
NEW YORK
NY
10103-3198
US
|
Family ID: |
29716254 |
Appl. No.: |
11/332430 |
Filed: |
January 13, 2006 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10395984 |
Mar 25, 2003 |
|
|
|
11332430 |
Jan 13, 2006 |
|
|
|
09707427 |
Nov 7, 2000 |
6936229 |
|
|
10395984 |
Mar 25, 2003 |
|
|
|
09353185 |
Jul 14, 1999 |
6207126 |
|
|
09707427 |
Nov 7, 2000 |
|
|
|
60100340 |
Sep 14, 1998 |
|
|
|
60093024 |
Jul 16, 1998 |
|
|
|
Current U.S.
Class: |
423/421 ;
423/179.5 |
Current CPC
Class: |
B01J 8/00 20130101; C01D
15/04 20130101; C22B 3/44 20130101; C01F 11/18 20130101; C01D 15/08
20130101; C01P 2006/80 20130101; C22B 26/12 20130101; C01F 11/462
20130101; C01F 5/22 20130101; Y02P 10/20 20151101; Y02P 10/234
20151101 |
Class at
Publication: |
423/421 ;
423/179.5 |
International
Class: |
C01D 15/00 20060101
C01D015/00 |
Claims
1-13. (canceled)
14. A continuous process for preparing high purity lithium chloride
comprising: reacting the lithium carbonate having a sodium content
of less than 0.0002 wt % with hydrochloric acid having less than I
ppm sodium to produce high purity lithium chloride having sodium
content of less than 0.001 wt %.
15. High purity lithium chloride containing less than 20 ppm
sodium.
16. The high purity lithium chloride of claim 15 containing less
than 8 ppm sodium.
17-20. (canceled)
Description
[0001] This application is a continuation-in-part of U.S. Ser. No.
09/707,427 filed Nov. 7, 2000, which is a divisional application of
U.S. Ser. No. 09/353,185, now U.S. Pat. No. 6,207,126.
[0002] This application claims priority under 35 U.S.C.
.sctn.119(e) from U.S. Provisional Application Nos. 60/100,340
filed Sep. 14, 1998 and 60/093,024 filed Jul. 16, 1998.
BACKGROUND AND SUMMARY OF THE INVENTION
[0003] The present invention relates to an integral process that
uses a minimum number of process steps for producing chemical and
high purity grades of lithium carbonate and lithium chloride
directly from the same natural brine source. More generally, the
method also relates to a method of producing purified metal
carbonate salts that are generally insoluble in water but which
have corresponding bicarbonate salts that are more then 75% soluble
in water by reaction with carbon dioxide.
[0004] It is desirable, from a commercial standpoint, to provide a
source of lithium low in sodium content because sodium becomes
reactive and potentially explosive in certain chemical processes,
particularly those in production of lithium metal from lithium
salts. A substantial portion of presently available lithium is
recovered from brines, which also contain high levels of sodium,
making the production of low sodium lithium salts difficult and
expensive. At the present time, there does not exist a viable low
cost integral processes for producing low sodium lithium carbonate
and chemical and high purity grades of lithium chloride directly
from natural brines containing lithium.
[0005] Natural brines that contain lithium also contain many
constituents as illustrated in the following Table: TABLE-US-00001
TABLE 1 NATURAL BRINE COMPOSITION Dead Great Salt Bonneville Salton
Sea Silver Peak Salar de Atacama Ocean Sea Israel Lake Utah Brine
Utah Brine Calif Brine Nevada Brines Chile Na 1.05 3.0 7.0 9.4 5.71
6.2 7.17 5.70 K 0.038 0.6 0.4 0.6 1.42 0.8 1.85 1.71 Mg 0.123 4.0
0.8 0.4 0.028 0.02 0.96 1.37 Li 0.0001 0.002 0.006 0.007 0.022 0.02
0.15 0.193 Ca 0.04 0.05 1.5 0.5 0.0 0.71 1.46 0.043 Cl 1.9 16.0
14.0 16.0 15.06 10.06 16.04 17.07 Br 0.0065 0.4 0.0 0.0 0.0 0.002
0.005 0.005 B 0.0004 0.003 0.007 0.007 0.039 0.005 0.04 0.04 Li/Mg
0.0008 0.0005 0.0075 0.0175 0.786 1.0 0.156 0.141 Li/K 0.0026
0.0033 0.015 0.0049 0.0155 0.016 0.081 0.113 Li/Ca 0.0025 0.0064
0.2 0.0583 0.0008 1.0 4.84 0.244 Li/B 0.25 0.6666 0.857 1.0 0.051
4.0 3.75 4.83 (All values in weight percent)
[0006] Production of lithium carbonate and lithium chloride with
acceptable qualities from such brines requires employing techniques
to remove specific cations and anions that accompany the lithium in
solution, and then concentrating the lithium for extraction.
[0007] Individual applications require that these ion impurities be
reduced to specific maximum levels and a number of processes have
been described for removing these impurities. For example, U.S.
Pat. No. 5,219,550 to Brown and Boryta describes a method for
producing chemical grade lithium carbonate from natural lithium
containing brine by first removing most of the components from the
brine by concentrating utilizing solar evaporation techniques.
Concentrating the brine with respect to lithium by solar
evaporation causes most of the unwanted components to precipitate
from the brine, i.e., salt out. Boron, which concentrates with the
lithium, is subsequently removed using an extraction process. The
remaining magnesium is removed by adding a base to precipitate
magnesium carbonate and/or magnesium hydroxide, and the lithium is
finally precipitated from the purified brine as lithium carbonate
by the addition of soda ash. Other processes related to the above
process are disclosed in U.S. Pat. Nos. 4,036,718; 4,243,392; and
4,261,960.
[0008] Other techniques for producing purified lithium salts are
known. For example, German Patent DE 19,541,558 to Wusson et al
describes a process to reduce sodium from lithium chloride
solutions by cooling. U.S. Pat. No. 4,859,343 to Kullberg et al
describes an ion exchange method for removing sodium from brines.
U.S. Pat. No. 5,599,516 and Russian Patent No. 9,419,280 describe
absorption/ion exchange processes for recovering lithium from
brine.
[0009] U.S. Pat. No. 4,980,136 discloses a procedure for preparing
chemical grade and low sodium lithium chloride (battery grade, less
than 20 ppm sodium and less than 5 ppm magnesium) from concentrated
natural brine by crystallizing lithium chloride from a
magnesium/lithium chloride brine to produce a chemical grade of
lithium chloride crystal. This is followed by alcoholic extraction
of the soluble lithium chloride from the crystal leaving sodium
chloride as the insoluble phase. The alcohol solution containing
the lithium chloride is then filtered and evaporated to form a high
purity grade of lithium chloride crystal.
[0010] East German Patent DD 257,245 describes a method for
recovering lithium chloride from concentrated brine containing both
calcium chloride and magnesium chloride and selectively extracting
lithium chloride with alcohol. Other patents related to such
processes include U.S. Pat. Nos. 4,271,131 and 4,274,834.
[0011] U.S. Pat. No. 4,207,297 describes production of a low sodium
lithium carbonate (sodium less than 10 ppm in lithium carbonate)
from technical lithium carbonate. This is accomplished by reacting
lithium carbonate with lime followed by filtration to produce a
lithium hydroxide solution. The solution is subsequently purified
with just enough carbon dioxide to remove the residual calcium and
filtered. More carbon dioxide gas is added to the purified lithium
hydroxide solution to re-precipitate lithium carbonate crystal as a
high purity product.
[0012] Except for the methods described in DE 19,541,558, U.S. Pat.
No. 4,243,392 and U.S. Pat. No. 5,219,550, the methods of the prior
art are not practiced today because they are either technically or
economically not viable.
[0013] Another process for producing lithium chloride is set forth
in Chilean Patent Application No. 550-95, which describes a
procedure whereby a purified brine containing essentially lithium
chloride is directly produced from natural brines that have been
concentrated by solar evaporation and treated by an extraction
process to remove boron. However, the sodium, calcium, and sulfate
levels in the resultant brine are too high to be an acceptable
brine source of lithium chloride for producing a technical grade
lithium metal, primarily because the two major remaining
impurities, sodium and magnesium, have to be further reduced to
acceptable levels to produce chemical grade lithium chloride
crystal. Specifically, magnesium must be reduced to less than 0.005
wt % Mg, and sodium to less than 0.16wt % Na in the anhydrous
lithium chloride salt. Salting out anhydrous lithium chloride
directly from brine above 110.degree. C. in a vacuum crystallizer
as described in U.S. Pat. No. 4,980,136 yields a lithium chloride
containing at best 0.07 wt % Mg and 0.17 wt % Na.
[0014] It is accepted, although not proven, that lithium chloride
crystal containing 0.07 wt % Mg may be too high in magnesium to be
used for producing lithium metal and for subsequent use in the
production of lithium organometallic compounds. Thus, the industry
demands that organolithium catalysts in polymerization reactions be
low in magnesium. Lithium chloride high in magnesium can also
adversely affect the operation of the lithium electrolysis cell
when producing the lithium metal.
[0015] As noted above, the sodium impurity in the lithium chloride
crystal reports directly to the metal when producing lithium metal.
Thus, low sodium lithium salts are desirable. Sodium in lithium
chloride crystal above 0.6 wt % produces metal containing 1 wt %
sodium or higher. Sodium concentrations of about 1 wt % in lithium
metal or above render the lithium metal more reactive to natural
components of air. This makes the metal more difficult and more
dangerous to handle. Table 2 sets forth data concerning sodium
limits and tolerances in different lithium sources: TABLE-US-00002
TABLE 2 SODIUM CONTENT OF LITHIUM CHLORIDE Brown & Maximum
limits Na in LiCl chloride Becherman for chemical required for
battery chemical grade grade metal grade metal % Lithium 99.2 99.2
99.8 chloride % Na** 0.17 0.04 0.0006 **wt % in Lithium
chloride
[0016] Commercial methods employed to produce low sodium lithium
carbonate and lithium chloride on a commercial scale include
extraction of lithium compounds from mineral deposits such as
spodumene bearing ore and natural brines. A number of processes
have been described and some have been commercialized for producing
lithium carbonate from these sources.
[0017] One such commercial method involves extraction of lithium
from a lithium containing ore or brine to make a pure lithium
sulfate solution such as described in U.S. Pat. No. 2,516,109, or a
lithium chloride solution such as described in U.S. Pat. No.
5,219,550. After purifying the solutions, sodium carbonate is added
as either a solid or a solution to precipitate lithium carbonate
crystals. The lithium carbonate is subsequently filtered from the
spent liquor. (mother liquor), and the lithium carbonate is washed,
dried, and packaged.
[0018] Lithium carbonate is often used as a feed material for
producing other lithium compounds such as lithium chloride, lithium
hydroxide monohydrate, lithium bromide, lithium nitrate, lithium
sulfate, lithium niobate, etc. Lithium carbonate itself is used as
an additive in the electrolytic production of aluminum to improve
cell efficiency and as a source of lithium oxide in the making of
glass, enamels, and ceramics. High purity lithium carbonate is used
in medical applications.
[0019] For example, a presently used commercial procedure for
producing chemical grade lithium chloride is to react a lithium
base such as lithium carbonate or lithium hydroxide monohydrate
with concentrated hydrochloric acid to produce a pure lithium
chloride brine. The resultant lithium chloride brine is evaporated
in a vacuum crystallizer at or above 110.degree. C. to produce an
anhydrous lithium chloride crystal product. This procedure yields a
product that meets most commercial specifications for chemical
grade lithium chloride, but not low sodium grades of lithium
chloride. Chemical grade lithium chloride is suitable for air
drying applications, fluxes, an intermediate in manufacture of
mixed ion-exchange zeolites, and as a feed to an electrolysis cell
for producing chemical grade lithium metal. Chemical grade lithium
metal is used, inter alia, to produce lithium organometallic
compounds. These compounds are used as a catalyst in the
polymerization and pharmaceutical industry.
[0020] Chemical grade anhydrous lithium chloride should contain
less than 0.16% sodium in order to produce metal containing less
than 1% sodium. The importance of minimizing the sodium content in
the metal and the costs associated therewith are the principle
reasons for using lithium hydroxide monohydrate or lithium
carbonate as the raw material for producing lithium chloride and,
subsequently, lithium metal. In consideration, low sodium lithium
chloride, typically contains less than 0.0008 wt % sodium, and is
commercially produced to manufacture low sodium lithium metal
suitable for battery applications and for producing alloys.
[0021] Commercially, low sodium lithium chloride is produced
indirectly from chemical grade lithium carbonate. Chemical grade
lithium carbonate is produced from Silver Peak Nevada brine, Salar
de Atacama brines in Chile, Hombre Muerto brines in Argentina, and
from spodumene ore (mined in North Carolina). The lithium carbonate
is converted to lithium hydroxide monohydrate by reaction with
slaked lime. The resultant slurry contains precipitated calcium
carbonate and a 2-4 wt % lithium hydroxide solution, which are
separated by filtration.
[0022] The lithium hydroxide solution is concentrated in a vacuum
evaporation crystallizer in which the lithium hydroxide monohydrate
is crystallized, leaving the soluble sodium in the mother liquor
solution. The crystal lithium hydroxide monohydrate is separated
from the mother liquor and dried. This salt normally contains
between 0.02 and 0.04% sodium. To further reduce the sodium levels,
the lithium hydroxide monohydrate must be dissolved in pure water
and recrystallized, and subsequently reacted with pure hydrochloric
acid to form a concentrated lithium chloride brine containing less
than 10 ppm sodium. The resultant lithium chloride solution is then
evaporated to dryness to yield anhydrous lithium chloride suitable
for producing battery grade lithium metal containing less than 100
ppm sodium. The above process requires seven major processing steps
described as follows:
[0023] 1) Extraction and purification of a low boron aqueous
solution containing 0.66 to 6 wt % Li from lithium containing ore
or natural brine;
[0024] 2) Purification of the brine with respect to magnesium and
calcium and filtered;
[0025] 3) Precipitation of lithium carbonate from the purified
brine by addition of Na.sub.2CO.sub.3, and filtering and drying the
lithium carbonate;
[0026] 4) Reacting slaked lime and lithium carbonate to produce a
LiOH solution and filtering;
[0027] 5) Crystallizing LiOH.H.sub.2O in a vacuum crystallizer;
[0028] 6) Dissolving the LiOH.H.sub.2O crystals and
re-crystallizing LiOH H.sub.2O from solution; and
[0029] 7) Reacting high purity HCl with re-crystallized
LiOH.H.sub.2O to produce a high purity lithium chloride brine from
which low sodium lithium chloride is crystallized and drying the
lithium chloride.
[0030] Low sodium lithium carbonate can be prepared from
re-crystallized LiOH.H.sub.2O using the first part of the process
described above. The recrystallized LiOH.H.sub.2O is then mixed
with water and reacted with CO.sub.2 to precipitate the lithium
carbonate. The processing steps are set forth below:
[0031] 1) Extraction and purification of a low boron aqueous
solution containing 0.66 to 6 wt % Li from lithium containing ore
or natural brine;
[0032] 2) Purifying the brine is then purified with respect to
magnesium and calcium and filtered.
[0033] 3) Precipitate Li.sub.2CO.sub.3 from the purified brine with
the addition of Na.sub.2CO.sub.3, filtered and dried.
[0034] 4) React slaked lime and Li.sub.2CO.sub.3 to produce a LiOH
solution and filter.
[0035] 5) LiOH.H.sub.2O is crystallized in a vacuum
crystallizer.
[0036] 6) Dissolve again and re-crystallize LiOH.H.sub.2O from
solution.
[0037] 7) React CO.sub.2 gas with a slurry containing
re-crystallized LiOH H.sub.2O to Crystallize low sodium high purity
lithium carbonate crystal, filter and dry.
[0038] Production of lithium chloride direct from concentrated
brine has also been described in U.S. Pat. No. 4,274,834.
[0039] The present invention provides an integral and novel process
which reduces the number of major processing steps for producing
chemical (technical) grade and low sodium lithium carbonate and
lithium chloride directly from natural lithium containing brines
concentrated to about 6.0 wt % Li without the lithium hydroxide
monohydrate single and double recrystallization steps present in
the processes of the prior art.
[0040] The present invention also relates to a method for preparing
chemical grade lithium chloride direct from the same concentrated
starting brine as that used to prepare the lithium carbonate.
[0041] The present invention incorporates the process described in
U.S. Pat. No. 5,219,550 to produce a chemical grade lithium
carbonate to specifically utilize the mother liquor by-product
stream from that process to recover lithium from the magnesium
containing purification muds that are formed when producing lithium
chloride directly from brine, eliminating the steps of first
precipitating lithium carbonate or lithium hydroxide and then
transforming these salts to lithium chloride. Additionally, the
process of the invention yields a high purity lithium carbonate
having less than about 0.002 wt % sodium using a carbon
dioxide/bicarbonate cycle, and a process of preparing a high purity
lithium chloride by reacting the high purity lithium carbonate with
a high purity hydrochloric acid.
[0042] A preferred method is directed to a continuous process for
directly preparing high purity lithium carbonate from lithium
containing brines by preparing a brine containing about 6.0 wt %
lithium and further containing other ions such as sodium,
magnesium, calcium, and sulfates naturally occurring in brines;
adding mother liquor containing carbonate from a prior
precipitation step to precipitate magnesium as magnesium carbonate;
adding a solution of CaO and sodium carbonate to remove calcium and
residual magnesium; precipitating lithium carbonate from the
purified brine by adding soda ash solution; filtering the resultant
solution to obtain solid lithium carbonate; preparing an aqueous
slurry of the lithium carbonate in a reactor equipped with an inlet
for introducing carbon dioxide gas into said aqueous slurry to form
an aqueous lithium bicarbonate solution, the reactor being at a
temperature from at least minus 10 to +40.degree. C.; passing said
aqueous lithium bicarbonate solution through a filter to clarify
the solution and optionally an ion exchange column for further
calcium and magnesium removal; introducing said filtered lithium
bicarbonate solution into a second reactor and adjusting of the
solution to from 60-100 .degree. C. to precipitate ultra-pure
lithium carbonate with sodium less than 0.0002 wt %, calcium less
than 0.00007 wt % and magnesium less than 0.00001 wt %.
[0043] Another preferred embodiment relates to a continuous process
for directly preparing high purity lithium carbonate from lithium
containing brines by preparing a brine containing about 6.0 wt %
lithium and further containing other ions such as sodium,
magnesium, calcium, and sulfates naturally occurring in brines;
adding CaO to remove magnesium; adding mother liquor containing
carbonate from a prior precipitation step and soda ash solution to
precipitate calcium carbonate; filtering to remove calcium
carbonate and to yield a purified lithium containing brine; adding
soda ash to said purified brine to precipitate lithium carbonate;
filtering the solution to recover the precipitated lithium
carbonate, preparing an aqueous lithium carbonate slurry in a
reactor where such reactor is equipped with an inlet for
introducing carbon dioxide gas into the lithium carbonate slurry to
produce an aqueous lithium bicarbonate solution, wherein the
reactor is at a temperature from at least minus 10 to +40.degree.
C.; passing the aqueous lithium bicarbonate solution through a
clarifying filter and optionally an ion exchange column for further
calcium and magnesium removal; introducing the filtered solution
into a second reactor and adjusting the temperature of the solution
to from 60-100.degree. C. to precipitate the ultra-pure lithium
carbonate with sodium less than 0.0002 wt %, calcium less than,
0.00007 wt % and magnesium less than 0.00001 wt %.
[0044] In preferred embodiment, the lithium bicarbonate is only
passed through a filter and proceeding to the second reactor at
60-100.degree. C. to precipitate low sodium lithium carbonate with
a sodium content of less than 0.0002 wt %.
[0045] In other preferred embodiments the lithium bicarbonate is
only passed through a filter and proceeding to the second reactor
at 60-100.degree. C. to precipitate low sodium lithium carbonate
with a sodium content of less than 0.0002 wt %.
[0046] In other embodiments, the carbon dioxide absorption reactor
is from minus 10.degree. C. but not more than 40.degree. C, and
preferably from 0-35.degree. C., and the temperature of the reactor
for precipitating high purity lithium carbonate is from
60-100.degree. C., preferably 70-95.degree. C.
[0047] A preferred ion exchange column contains Amberlite IRC-718
as a cation exchange resin.
[0048] The methods are conducted at less than or equal to
atmospheric pressure.
[0049] The high purity lithium carbonate preferably contains less
than 20 ppm sodium as an impurity, preferably less than 2 ppm
sodium.
[0050] In a preferred embodiment, the purified lithium carbonate
contains TABLE-US-00003 Wt % High Purity Low Sodium
Li.sub.2CO.sub.3 Li2CO3 >99.4 Mg <0.0007 Na <0.0010 K
<0.00025 Ca <0.0120 B <0.0001 Al <0.0002 As <0.0001
Fe <0.0001 Si <0.0010 Zn <0.00005 SO4 <0.037 Cl
<0.005
[0051] In another preferred embodiment, the purified lithium
carbonate has the following composition: TABLE-US-00004 Wt %
Ultra-High Purity Li2CO3 Li2CO3 >99.995 Mg <0.00001 Na
<0.0002 K <0.00015 Ca <0.00007 B <0.0001 Al <0.0002
As <0.0001 Fe <0.0001 Si <0.00011 Zn <0.000014 SO4
<0.0030 Cl <0.005
[0052] The invention also relates to high purity lithium chloride
containing less than 20 ppm sodium, and preferably less than 8 ppm
sodium.
[0053] Such high purity lithium chloride is prepared by a process
which is also a part of the present invention, the process
including the steps of reacting lithium carbonate having a sodium
content of less than 0.0002 wt % with hydrochloric acid having less
than 1 ppm sodium to produce high purity lithium chloride having
sodium content of less than 0.001 wt %. The lithium carbonate may
be prepared according to processes described above and elsewhere
herein.
[0054] The present invention also provides an apparatus for
continuously purifying lithium carbonate having a dissolver which
is a baffled reactor to dissolve lithium carbonate that includes a
mixer/disperser, a carbon dioxide gas dispersion tube, a wash water
filtrate/mother liquor filtrate recycle line, a cooler, a stilling
well to separate gas and undissolved lithium carbonate solids from
the resultant lithium bicarbonate solution, and a continuous
chemical grade lithium carbonate crystal feeder; an inline filter
to remove insoluble impurities from the lithium bicarbonate
solution coming from the stilling well; a heat exchanger to recover
heat from the hot mother liquor that is recycled to the dissolver;
a heated gas sealed crystallizer with mixer to decompose the
lithium bicarbonate solution to form low sodium lithium carbonate
crystals, carbon dioxide gas, and mother liquor; a slurry valve to
remove the low sodium lithium carbonate crystals and mother liquor
from the gas sealed crystallizer; a gas line to continuously return
the carbon dioxide produced in the crystallizer to the dissolver; a
separator such as a continuous belt filter to separate the low
sodium lithium carbonate from the mother liquor and a wash water
section to wash the lithium carbonate crystals; a pump and line to
return the mother liquor and wash filtrate to the dissolver; a
mother liquor bleed to control the sodium level and to maintain a
constant liquid volume; and a carbon dioxide source. Preferably,
the apparatus has a reactor using absorption columns, such as a
sieve tray or a Scheibel column, to facilitate absorption of carbon
dioxide in the aqueous slurries.
[0055] The invention also relates to a method for purifying metal
carbonates that are insoluble in water but have corresponding metal
bicarbonate salts that are more than 75% by wt. soluble in water by
preparing an aqueous slurry of said metal carbonate; introducing
carbon dioxide gas into said aqueous slurry to form a corresponding
metal bicarbonate solution; and heating the metal bicarbonate
solution to form a purified metal carbonate, wherein the heating is
such that the temperature of the solution is raised to a
temperature at which the metal carbonate is insoluble to
precipitate the purified metal carbonate. Lithium is a preferred
metal.
[0056] The pressures used to make any of these salts according to
the processes may be, e.g., less than or equal to atmospheric
pressure.
[0057] A preferred cation exchange resin is Amberlite IRC-718
commercially available from Rohm and Haas.
[0058] The purified salts prepared according to the methods of the
invention also preferably, have a potassium content of less than 20
ppm, a calcium content of not greater than 140 ppm Ca, a magnesium
content of from 3-7 ppm, and not greater than 400 ppm sulfate
(SO.sub.4.sup.-), or any combination of these.
[0059] Any patents and references cited herein are incorporated by
reference in their entireties.
BRIEF DESCRIPTION OF THE FIGURES
[0060] FIG. 1 is a flow diagram showing the production of technical
grade lithium carbonate according to the present invention;
[0061] FIG. 2 is a flow diagram showing the production of low
sodium lithium carbonate according to the present invention;
[0062] FIG. 3 is a flow diagram of the process of direct lithium
chloride recovery from brine according to the present invention of
a preferred embodiment of the invention;
[0063] FIG. 4 is a laboratory apparatus for producing low sodium
lithium carbonate according to the present invention;
[0064] FIG. 5 is an apparatus with an absorption column for
preparing the low sodium lithium carbonate according to the present
invention wherein carbon dioxide from the process reaction is
recycled into the absorption column;
[0065] FIG. 6 shows a preferred apparatus having a sieve column for
preparing the low sodium lithium carbonate of the present
invention; and
[0066] FIG. 7 shows an alternative apparatus having a Scheibel
column for preparing the low sodium lithium carbonate of the
present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0067] The following describes in detail the process for making low
sodium lithium carbonate from chemical grade lithium carbonate
without the need for using the double crystallization process for
making high purity lithium hydroxide monohydrate.
[0068] There are different chemical compositions of brine that
exists in nature that contain lithium (see Table 1, supra). For
example, there exist in the Salar de Atacama basin two different
types of lithium containing brine. These are described as high
sulfate brine and high calcium brine. Sulfate may be removed from
the brine by adding either lime or a calcium chloride by-product
from another source, or mixing with a brine containing calcium to
precipitate the calcium and sulfate as gypsum (CaSO.sub.4.2H.sub.2O
). This produces a low calcium low sulfate brine that can be solar
concentrated and have a higher lithium yield than concentrating a
brine containing sulfate or calcium. Reducing the sulfate in the
brine also allows for better recoveries of potash from brines that
naturally contain potassium.
[0069] The natural brine is concentrated to a lithium content of
about 6.0%, e.g. 6.0-6.5% by solar evaporation. During the solar
evaporation process, gypsum continues to co-precipitate with sodium
chloride when sulfate and calcium are stoichiometrically balanced.
With continued evaporation, potassium chloride and sodium chloride
precipitate until the lithium and magnesium concentrations
increases to about 0.76 wt % Li and 5.2 wt % Mg. Concentrating the
brine from 0.76 wt % Li to 1.4 wt % Li will precipitate the
carnallite salt (KCl.MgCl.sub.2.6H.sub.2O). This reduces the Mg:Li
ratio in solution from about 6.8:1 to 5.1: 1, and removes most of
the sodium and potassium from solution. Continued evaporation and
concentration of the brine from 1.4 wt % Li to 4.2 wt % Li
precipitates the bischofite salt (MgCl.sub.2.6H.sub.2O). This
further reduces the Mg:Li ratio to 0.93:1.
[0070] Further concentration of the brine from about 4.2 wt % Li to
about 6.2 wt % Li precipitates the lithium carnallite salt
(LiCl.MgCl.sub.2.7H.sub.2O ). This further reduces the Mg:Li ratio
to about 0.24:1.
[0071] To improve the lithium yield when concentrating the brine to
about 6 wt % lithium, the lithium precipitated from brine as
lithium carnallite is converted to the bischofite salt and lithium
chloride brine by mixing the lithium carnallite salt with brine
containing between 1.4 to 3 wt % Li. In order to convert 100% of
lithium carnallite to bischofite, the resultant recovered brine
contained in the bischofite salt ponds must not exceed a lithium
concentration of 4.2 wt % Li.
[0072] Magnesium polyborates precipitate slowly from the
concentrated brines. This usually causes the boron salts to super
saturate when the brine resident time in the ponds is short. As a
result, the boron content of the brines can range between 0.5 to
1.2 wt % boron.
[0073] At ambient conditions, the concentrated brine will contain
on the average: TABLE-US-00005 6.0 .+-. 0.3 % Li 1.65 .+-. 0.4 % Mg
0.08 % Na 0.02 % K 0.033 % Ca 0.019 % SO.sub.4 0.8 .+-. 0.2 % B 35
.+-. 0.5 % Cl
[0074] Natural brines containing lithium, magnesium, potassium,
sodium, boron, wherein calcium and sulfate are stoichiometrically
balanced, will have this general composition when evaporated and
concentrated under ambient conditions by solar evaporation to 6 wt
% lithium. Brine containing 6.5 wt % Li cannot be further
concentrated because, at ambient conditions, this concentration
defines the "end point" or the drying up point of the
Li--Mg--Cl--H.sub.2O system. Further evaporation will not change
composition of the brine or the Mg:Li ratio of the brine, and will
serve only to precipitate a mixture of lithium carnallite and
lithium chloride monohydrate (LiCl.H.sub.2O) as the brine
evaporates. The resultant salt mixture will have the same Mg:Li
ratio as the end point brine.
[0075] The boron and magnesium remaining in brine concentrated to
about 6 wt % Li must be removed in order to make a suitable lithium
carbonate product. It is preferred that boron is removed by an
alcohol extraction such as described in U.S. Pat. No. 5,219,550,
hereby incorporated by reference in its entirety. This extraction
process reduces the boron in the concentrated brine to less than
about 0.0005 wt % B.
[0076] Procedures known in the art for directly removing magnesium
from concentrated brine as magnesium hydroxide are costly because
valuable lithium will be retained by the magnesium hydroxide which
forms as a voluminous precipitate which is difficult to filter. To
achieve maximum lithium yields and facilitate filtration, the
magnesium may be removed in two steps. As much as 97% of the
magnesium may be removed as magnesium carbonate (MgCO.sub.3) by
mixing the concentrated brine with recycled mother liquor from the
lithium carbonate precipitation step. This utilizes the carbonate
present in the lithium carbonate crystallizer mother liquor and
recovers most of the lithium that remains soluble in the mother
liquor.
[0077] When recycling mother liquor, it is important to carefully
control the CO.sub.3/Mg ratio to prevent lithium carbonate from
precipitating with the magnesium carbonate. This is because the
lithium concentration at this point in the process may be high (0.5
to 1.2 wt % Li), but this becomes less problematic at lower lithium
concentrations, e.g., at about 1.0%. After the magnesium carbonate
is precipitated and filtered, the magnesium carbonate solids are
given a displacement wash using lithium carbonate mother liquor to
recover some of the concentrated brine retained with the magnesium
carbonate solids. Using mother liquor as the wash instead of water
reduces the water input to the process that must be subsequently
removed as a process bleed stream. The mother liquor constitutes
the process bleed whereby all the water (from brine and wash water)
and sodium chloride are continuously removed from the process (from
soda ash reaction with lithium and magnesium chloride) and which
contains about 5% of the total lithium in the concentrated feed
brine. The washed muds contain between 5 and 12% of the total
lithium input and constitutes a major lithium loss for the process
in addition to the lithium lost with the proceed bleed.
[0078] The magnesium remaining in the brine (generally from 0.06 to
0.02 wt % Mg) is finally removed by treating the brine with a
lime/soda ash (CaO/Na.sub.2CO.sub.3) slurry to form insoluble
magnesium hydroxide (Mg(OH).sub.2) and insoluble calcium carbonate
(CaCO.sub.3). The coprecipitated CaCO.sub.3 acts as a filter aid in
filtering the Mg(OH).sub.2 muds. Additional filter aid may be added
to further improve filtration. The lime/soda ash ratio is adjusted
to control the level of soluble calcium remaining in the purified
brine.
[0079] Because magnesium hydroxide usually precipitates as a gel,
it is preferred to maintain the pH between 8.45 and 9.10 (measured
directly with a slurry pH electrode) in order to achieve maximum
filtration rates. After separation of the solids from the purified
brine, the brine contains between 0.5% Li and 1.2% Li, less than
0.0001 wt % magnesium, less than 0.0015 wt % calcium, and less than
0.0005 wt % boron.
[0080] The magnesium-calcium-boron free brine is subsequently
treated with a soda ash solution to precipitate lithium carbonate
and the mother liquor is recycled as described above. The sodium
added to the process as Na.sub.2CO.sub.3 is removed with the mother
liquor bleed. stream as dissolved sodium chloride (NaCl). Hot
de-ionized water is used to wash the lithium carbonate mother
liquor from the filtered lithium carbonate crystal to remove sodium
and chloride. The lithium in the wash filtrate is recovered by
using the wash filtrate to produce the soda ash solution.
[0081] The lithium carbonate product produced by the foregoing
process is characterized as technical grade, and a typical
technical grade lithium carbonate contains about 0.04 wt %
sodium.
[0082] This product is a suitable source of lithium for producing
chemical grade lithium carbonate having less then 0.04% Na, and
subsequently, low sodium lithium chloride, without need for
preparation of lithium hydroxide and the recrystallization steps of
prior art processes. However, the chemical grade lithium carbonate
first needs to be processed to reduce these impurities to a level
suitable for producing a low sodium battery grade lithium chloride.
The sodium content in low sodium lithium carbonate is reduced to
below about 0.0002 wt % Na.
[0083] Purification of the lithium carbonate to produce low sodium
lithium carbonate may be conducted in a continuous
reactor/crystallizer apparatus as shown in FIG. 4. The apparatus is
designed to continuously dissolve lithium carbonate as lithium
bicarbonate (LiHCO.sub.3) by reacting a slurry (3-5% solids) of the
technical grade lithium carbonate prepared as described above and
water with CO.sub.2 gas at room temperature (minus 10 to 40.degree.
C.) in a dissolver shown as 3 in FIG. 2. The resultant LiHCO.sub.3
solution (7.0-8.5 wt % LiHCO.sub.3) is transferred on a continuous
basis to a crystallizer shown as 5 in FIG. 2 which is maintained at
70.degree. C.-95.degree. C. to precipitate high purity lithium
carbonate crystals and evolve carbon dioxide gas, which may be
recycled into the process. Lower temperatures may be used in the
dissolver shown as 3 in FIG. 2 to increase the lithium bicarbonate
concentration per cycle for purification, thereby, increasing
equipment throughput.
[0084] In the crystallizer shown as 5 in FIG. 2, high purity
lithium carbonate crystals precipitate from the lithium bicarbonate
solution at the higher temperature and CO.sub.2 gas is evolved. The
slurry is continuously removed and the lithium carbonate crystals
are filtered hot and washed with sodium free de-ionized water. The
lithium carbonate mother liquor contains valuable soluble lithium
and is recycled to the dissolver shown as 3 in FIG. 2 to minimize
lithium loss. The source of CO.sub.2 may be from the gas evolved in
the crystallizer, from CO.sub.2 generated when reacting lithium
carbonate with hydrochloric acid, or from a commercial CO.sub.2
source. Use of a commercial CO.sub.2 source yields a simplified
process, and does not require special added equipment to recover
the CO.sub.2. Furthermore, no chemical reagents are required except
for sodium free deionized water. The temperature differential
between the dissolver shown as 3 in FIG. 2 and the crystallizer
shown as 5 in FIG. 2 defines the throughput.
[0085] The apparatus in FIG. 4 is now described in more detail. The
dissolver/settler is preferably a cooled baffled reactor with a
high height to diameter aspect ratio containing a gas
disperse/mixer designed to completely absorb CO.sub.2 gas. The
reactor preferably has a minimum active height of 8 feet. A
settler/decanter is incorporated to eliminate undissolved solids
from contaminating the clear LiHCO.sub.3 solution being
continuously removed from the dissolver. A baffle is preferably
placed below the decanter to prevent carbon dioxide gas from
entering and incapacitating the settler/decanter. The cool
LiHCO.sub.3 solution is polish filtered to remove insoluble
impurities, then preheated with the recycled mother liquor in a
heat exchanger. A cartridge filter may be incorporated prior to the
heat exchanger to remove insolubles. The preheated LiHCO.sub.3
solution is then pumped via a pump to a heated crystallizer where
it is decomposed at between 70 and 95.degree. C. to form low sodium
lithium carbonate crystals, CO.sub.2 gas, and mother liquor. The
mother liquor contains dissolved lithium carbonate and a small
amount of LiHCO.sub.3. The mother liquor and CO.sub.2 are recycled
back to the dissolver/settler reactor. Sodium is removed from the
process using a mother liquor process bleed so that the mother
liquor contains less than 500 ppm sodium. The lithium contained in
the mother liquor bleed stream is recovered by using the bleed
stream as part of the wash water used on the filtration equipment
for producing technical grade lithium carbonate. The number of
times the mother liquor is recycled is defined by the sodium
content and the degree of purification needed.
[0086] As an alternative to using a dissolver/settler for the
conversion of chemical grade lithium carbonate to a LiHCO.sub.3
solution is to employ, for example, a carbon dioxide absorption
column such as shown in FIG. 5, a sieve tray column as shown in
FIG. 6 or a Scheibel column commercially available from Glitch
Technology Corporation) such as shown in FIG. 7.
[0087] Ultra high purity lithium can be produced by passing the
LiHCO.sub.3 solution through an ion exchange column prior to
decomposing and recrystallizing the Li.sub.2CO.sub.3, to reduce
total impurity content, preferably to less than 10 ppm. Of course,
the brine may be passed through at any point during the process
after the magnesium and calcium precipitation steps to remove other
impurities. In a preferred embodiment, Amberlite IRC-718 resin
commercially available from Rohm and Haas is used in the column.
Prior to use, it is preferred to remove sodium from the Amberlite
resin, e.g. by passing HCl through the column. A lithium hydroxide
solution is then run through the column to convert the resin to the
lithium form. The lithium bicarbonate solution (7.5-8% LiHCO.sub.3)
is then passed through the column, and the purified solution is
heated to 95.degree. C. to precipitate the lithium carbonate which
is washed with 95.degree. C. deionized water. The solid is then
dried to yield high purity lithium carbonate.
[0088] Table 3 shows the typical content of the lithium carbonates
prepared by the processes of the invention: TABLE-US-00006 TABLE 3
CHEMICAL COMPOSITION OF CHEMICAL, LOW SODIUM, AND HIGH PURITY LOW
SODIUM LITHIUM CARBONATE Chemical Grade Low Sodium High Purity %
Li.sub.2CO.sub.3 99.38 .+-. 0.026 99.4 99.995 % Mg 0.004 .+-.
0.0006 0.0005 .+-. 0.0002 0.00001 % Na 0.069 .+-. 0.005 0.0002 .+-.
0.001* 0.0002 % K 0.0003 .+-. 0.00002 0.00015 .+-. 0.0001 0.00015 %
Ca 0.014 .+-. 0.001 0.012 .+-. 0.0014 0.00007 % SO.sub.4 0.037 .+-.
0.003 0.003 to 0.037* 0.003 % B 0.0003 .+-. 0.00001 <0.0001
<0.0001 % Cl 0.01 .+-. 0.006 <0.005 <0.005 % Al 0.0007
0.0002 % As 0.0002 0.0001 % Fe 0.0005 0.0001 % Si 0.0076 0.001
0.00011 % Zn 0.0001 0.00005 0.000014 *function of ion concentration
in mother liquor recycle
[0089] High purity lithium chloride can then be produced from the
low sodium lithium carbonate by conventional reaction in solution
with hydrochloric acid such as used in the prior art, except that
the hydrochloric acid must have a low sodium content, e.g. 0.02 wt
% sodium or less such that additional sodium is not entered into
the system as a contaminant.
[0090] The lithium carbonate processes are described in more detail
with respect to FIGS. 1 and 2.
[0091] Lithium Carbonate Process Flow Diagram A
[0092] FIG. 1 shows that (1) solid soda ash is mixed with wash
water filtrate (17) to make soda ash solution, SAS (2). In the
first stage reactor raffinate 3 containing 6% lithium is mixed with
SAS (2), mud from the direct chloride process (4) and mother liquor
(5). This recovers the lithium entrained in the direct chloride
muds, removes the magnesium and dilutes the lithium concentration
to around 1%.
[0093] (7) The MgCO.sub.3 mud (8) is separated from the brine and
washed with mother liquor. The wash filtrate and the filtered brine
are combined and sent to the second stage reactor (12).
[0094] (12) In the second stage reactor, reagent (11) which is a
combination of lime (9) and SAS (2) is added to precipitate
Mg(OH).sub.2 and CaCO.sub.3 (14) which are removed by filtration
(13).
[0095] (15) In the lithium carbonate reactor SAS (2) is added to
precipitate lithium carbonate. The solid is separated from the
mother liquor by filtration (18). The mother liquor is recycled and
excess is removed through (19). The lithium carbonate is washed
with water (16) which is recycled through (17) and used in the
production of SAS (2)
[0096] (20) A portion of the wet lithium carbonate from the filter
is sent to (B1) to be used in the production of low sodium lithium
carbonate and the majority is sent to the dryer (21) and packaged
as technical lithium carbonate (22).
[0097] FIG. 2
[0098] Low Sodium Lithium Carbonate Process Flow Diagram B
[0099] (1) Wet lithium carbonate from (A20) is used as feed
material.
[0100] (2) Lithium carbonate is mixed with the
bicarbonate/carbonate mother liquor recycle and fed into the
lithium bicarbonate sparger reactor (3).
[0101] (3) Carbon dioxide gas is bubbled into the reactor where it
reacts with the lithium carbonate forming lithium bicarbonate.
Reaction #1: H.sub.2O+CO.sub.2+LiCO.sub.3.fwdarw.2LiHCO.sub.3
[0102] (4) Lithium bicarbonate solution is filtered to remove
insoluble and un-reacted small particles that are not removed by
the settler.
[0103] (5) Lithium bicarbonate solution is heated to 90' C. to
reverse Reaction #1 and precipitate purified lithium carbonate.
Reaction #2: 2LiHCO.sub.3.fwdarw.LiCO.sub.3+CO.sub.2+H.sub.2O
[0104] (6) Lithium carbonate is separated from mother liquor and
washed with 90.degree. C. deionized water from (7) on filter
(6).
[0105] (8) Lithium carbonate is packaged in maxi sacks and stored
until processing in the direct lithium chloride plant at (C18) or
dried to provide low sodium lithium carbonate.
[0106] (9) Mother liquor from the bicarbonate/carbonate
crystallizer and wash water are recycled and a bleed (10) equal to
the input wash is removed and used in the lithium carbonate plant
product as wash water (A 16).
[0107] (11) Carbon dioxide gas used in the generation of lithium
bicarbonate solution is recycled from the bicarbonate/carbonate
crystallizer and a make up source (12) is used to compensate for
system leaks and to keep a constant pressure to the lithium
bicarbonate sparger reactor (3)
[0108] (13) A heat exchanger is used to preheat the bicarbonate
solution prior to the precipitation tank and conserve system
heat.
[0109] To increase the rate of conversion of lithium carbonate to
lithium bicarbonate, it is preferred to employ baffles and dual
pusher propellers to maximize the time that a bubble of carbon
dioxide remains in solution. Increasing the height of the vessel
also increases the residence time of the carbon dioxide. It was
also discovered that using lithium carbonate with an average
particle size of from about 75 to about 425 microns, and preferably
less than 250 microns, most preferably about 425 microns, also
increases conversion rates of lithium carbonate to lithium
bicarbonate.
[0110] It was also discovered that technical grade lithium chloride
can be directly precipitated from the same starting brine (about
6.0 wt % Li) used to prepare the low sodium lithium carbonate as
described above. Thus, the process of the present invention
produces a technical grade of lithium chloride product that is made
directly from concentrated natural brine containing essentially 6
wt % lithium from which boron has been removed by the described
extraction process of Brown and Boryta (U.S. Pat. No. 5,219,550).
The lithium chloride produced by this process is essentially higher
in purity with respect to sodium and calcium content. Using quick
lime (CaO) instead of slaked lime (Ca(OH).sub.2) to precipitate
magnesium as a double salt gives better filtration properties and
improved lithium yield as concentrated brine than what can be
achieved using the Chilean Patent application 550-95. Brine
concentrated to lower lithium concentrations may also be treated by
this method. However, the magnesium to lithium ratio is minimized
when the concentration of lithium can be increased to approach the
endpoint concentration of the system, i.e., 6 wt % Li, 1.7 wt % Mg,
thereby minimizing the amount of magnesium that has to be
removed.
[0111] The process involves removing the magnesium from the brine
as a double salt using excess quick lime (CaO), separating the
magnesium and calcium muds by filtration, cooling the filtered
brine to reduce the sodium by precipitating sodium chloride,
separating the sodium chloride solids by filtration, diluting the
filtered brine slightly (to 29% LiCl) and treating the filtered
brine with oxalate.(oxalic acid) and barium (barium chloride) to
remove precipitated calcium oxalate and barium sulfate, and
subsequently crystallizing lithium chloride directly from the
purified brine, e.g. in a vacuum crystallizer. The process may
utilize the mother liquor produced in the process for preparing
lithium carbonate as shown in FIG. 1 to recover the lithium lost to
the magnesium removal step as described above. The use of lithium
carbonate mother liquor improves the overall recovery of lithium as
commercial products.
[0112] The process eliminates the need for using hydrochloric acid
to produce lithium chloride from lithium carbonate and/or the
LiOH.H.sub.2O as in the processes of the prior art. The resultant
chemical grade lithium chloride process of the invention
application has essentially 5 major steps described as follows:
[0113] 1) Preparation of a low boron aqueous solution from natural
brine and concentrating to a lithium content of about 6 wt %;
[0114] 2) Removing magnesium and calcium by precipitation and
filtration.
[0115] 3) Cooling the brine to reduce the sodium content;
[0116] 4) Adding oxalate and barium to remove calcium and sulfate;
and
[0117] 5) Direct crystallization of lithium chloride.
[0118] The 6 wt % lithium brine is prepared as described above,
e.g. by solar evaporation. The purification of the boron free
concentrated brine containing essentially 6 wt % lithium is
described in more detail as follows:
[0119] Magnesium is removed from the brine by adding enough quick
lime to form magnesium and a calcium insoluble double salts. The
use of quick lime instead of slaked lime improves the filterability
of the magnesium/calcium containing muds and improves the overall
brine yield containing lithium according to the follow reaction
which occurs in lithium concentrated brine at Ca(OH).sub.2/Mg mole
ratio from 2 - 3: 18 Ca(OH).sub.2 solid+10 MgCl.sub.2
solid+0.5H2O.sub.liquid.fwdarw.
Mg.sub.10(OH).sub.18Cl.sub.2.0.5H.sub.2O.sub.solid+18
CaClOH.sub.solid
[0120] The filtration properties and lithium yield as brine
improves substantially using quick lime (CaO) compared to slaked
lime (Ca(OH).sub.2). In order to maintain the calcium insoluble,
the Ca to Mg mole ratio for quick lime addition is preferably
between 3 and 4 and the reaction is set forth below: 18
CaO.sub.solid+10 MgCl.sub.2 solution+9.5
H.sub.2O.sub.liquid.fwdarw. 18
CaClOH.sub.solid+Mg.sub.10(OH).sub.18Cl.sub.2.0.5H.sub.2O.sub.solid
[0121] Regardless of whether quick lime or slaked lime is used, the
process is typically conducted at temperatures ranging from about
25.degree. C. to about 120.degree. C. If filtration becomes a
production rate controlling variable, then the temperature may be
increased to precipitate both magnesium and calcium.
[0122] The final pH of the brine after completion of the reaction
generally ranges from about 9.5 to about 12.0 measured at
1:10dilution with water.
[0123] Excess slaked lime or additional reaction time may be used
as a process control.
[0124] In a preferred embodiment, lithium lost to the lithium
chloride magnesium purification solids may be recovered by
re-slurrying these muds in the reactor for precipitating magnesium
carbonate in the lithium carbonate process.
[0125] Compared to the magnesium removal steps described above for
preparation of lithium carbonate (FIG. 1. (6)), an overall increase
in lithium yield may be obtained for this purification step by
adding magnesium and calcium double salt purification muds (FIG. 1
(4)) from the direct lithium chloride process.
[0126] Sodium may be removed to acceptable levels by either cooling
before or after magnesium removal. However, cooling before
magnesium removal also salts out LiCl.H.sub.2O because the brine is
saturated with respect to lithium chloride and magnesium chloride.
To overcome the loss of lithium, an extra filtration step may be
used to recover the lithium precipitated followed by recycling the
LiCl.H.sub.2O salt.
[0127] In a preferred embodiment, magnesium is removed first by
addition of lime followed by cooling the brine containing 6% Li to
from minus 30 to +10.degree. C., preferably below 0.degree. C., and
more preferably -15.degree. C. to -20.degree. C., preferably from
-30 to below -20.degree. C., to reduce the sodium concentration to
less than 0.05 wt % sodium in the brine. This level of sodium is
low enough for producing a chemical grade of lithium chloride
crystal that can be used as feed salt to produce lithium metal
containing less than 1% Na. Removal of magnesium prior to cooling
in essence produces a dilute brine with respect to lithium
chloride, thereby substantially eliminating a lithium loss at this
point in the process. A substantial portion of the calcium
concentration in the brine when magnesium is removed is initially
controlled by the quick lime addition in excess of a Ca/Mg mole
ratio of 3, or by adjusting the pH above 11 by adding quick
lime.
[0128] Removing the remaining calcium as insoluble calcium oxalate
and sulfate as barium sulfate by the addition of oxalic acid and
barium chloride, respectively, may be done in the same reactor with
a single filtration step. Lithium oxalate and barium chloride are
preferred salts for the precipitation step, although others may be
used. Removal of calcium and sulfate may be done either before or
after the sodium removal step. The brine is preferably diluted to
between 29 and 33 wt % lithium chloride for this step. Therefore,
it is preferred to conduct this purification step after the sodium
removal.
[0129] In preferred embodiments, the calcium/sulfate removal is
conducted by first lowering pH to about 10.0 by addition of
concentrated HCl, and then adjusting the calcium concentration to
500 ppm by the addition of calcium chloride. The pH of the brine is
then adjusted to a pH of between 7.0 and 4.0.
[0130] In a particularly preferred embodiment, a solution of
lithium oxalate is added to the brine at a ratio of 1.5 moles
lithium oxalate to 1.0 mole calcium. Barium chloride is added at a
1:1 molar ratio to precipitate the sulfate. The brine is mixed and
allowed to react for between 4 to 24 hours. Preferably, the lithium
oxalate is added first, the reaction allowed to continue for about
4 hours. Then the pH is adjusted to about 7.0, and the barium
chloride is then added to precipitate the sulfate as barium
sulfate. The filtered lithium chloride solution will then be ready
for the crystallizer.
[0131] The final brine is evaporated to dryness to recover the
lithium chloride. Alternatively, the brine can be used as a
crystallizer feed brine to precipitate anhydrous lithium
chloride.
[0132] To produce anhydrous lithium chloride from solution, it is
preferred to conduct the crystallization in an evaporation
crystallizer operating at a temperature above 110.degree. C. If
impurities reach unacceptable concentrations, the crystallizer
solution may be returned to the purification steps for
adjustment.
[0133] An example of the lithium chloride purity produced by the
above process is as follows: TABLE-US-00007 LiCl 99.0 wt % Na
0.09-0.11 wt % Ca 0.0015-0.003 wt % Mg <0.0003 wt % Ba 0.007 wt
% SO.sub.4 0.007 wt % Si 0.004 wt %
[0134] The direct lithium chloride process is now described in more
detail below with respect to FIG. 3. (1) CaO and low boron
raffinate feed containing 6% lithium (2) are fed into the liming
tank (3) where they are mixed at a weight ratio of 15 % lime to
brine, they are mixed until a pH greater than 11.0 as measured on a
filtered sample diluted 1:10 with water.
[0135] (4) The slurry produced in the liming tank is filtered to
separate the magnesium free brine from the Ca/Mg mud. The brine is
sent to the filtrate tank (6) and the mud is sent to the muds tank
(5) where it can be slurried and pumped to the lithium carbonate
plant (A4 in FIG. 1) for recovering the entrained lithium in the
first stage of the lithium carbonate plant (shown in FIG. 1 as
6).
[0136] (7) The magnesium free brine is fed into the cooling reactor
to precipitate sodium chloride to acceptable levels and is filtered
at temperature in (8). The solids (9) are sent to waste or for
lithium recovery in the carbonate plant. The low sodium brine is
sent to the purification tank (10).
[0137] (10) In the purification tank water is added to dilute the
magnesium free low sodium brine to 33% lithium chloride, HCI is
added to adjust the pH to 4.0 and barium chloride is added to
precipitate barium sulfate from the brine. The pH is raised to 10.0
with lithium hydroxide monohydrate and lithium oxalate is added to
precipitate calcium oxalate.
[0138] (12) The solution is filtered to remove the barium sulfate,
calcium oxalate, and magnesium hydroxide solids and is sent to the
adjustment tank (13) for a final pH adjustment to 7.0 for feed to
the crystallizer (14) and dryer (15) to produce anhydrous technical
lithium chloride (17)
[0139] (16) An optional pure lithium chloride wash solution can be
employed to reduce potassium levels for technical lithium
chloride
[0140] (18) Low sodium lithium carbonate from (FIG. 2 B8) is
reacted with hydrochloric acid to produce a high purity lithium
chloride solution, which is fed into the purification tank (10) and
treated for sulfate and calcium as before to produce battery grade
anhydrous lithium chloride.
[0141] The invention also relates to a method for purifying metal
carbonates that are insoluble in water but have corresponding metal
bicarbonate salts that are more 75% by wt. soluble in water by
prepare an aqueous slurry of said metal carbonate; introducing
carbon dioxide gas into said aqueous slurry to form a corresponding
metal bicarbonate solution; and heating the metal bicarbonate
solution to form a purified metal carbonate, wherein the heating is
such that the temperature of the solution is raised to a
temperature at which the metal carbonate is insoluble to
precipitate the purified metal carbonate. Lithium is a preferred
metal, but any metal having a carbonate that is insoluble in water,
preferably at a temperature of 70-95.degree. C., but wherein the
bicarbonate is at least 75% soluble (by weight), may be used in
accordance with the present invention. Thus, a general method of
providing purified metal carbonates is also a part of the
invention.
EXAMPLE 1
Preparing Low Sodium Lithium Carbonate
[0142] To a concentrated brine containing 6.19% Li, 1.51% Mg,
0.179% Na, 0.026% K, 0.056% Ca, 0.002% SO.sub.4, 0.0003% B, and 36%
Cl, recycled mother liquor containing 0.14% Li, 8.26% Na, 0.18%
SO.sub.4, 12.37% Cl, and 0.58% CO.sub.3 was added at a temperature
of 70.degree. C. Enough mother liquor was added to form a solution
containing 1 % Li. This also precipitated most of the magnesium as
magnesium carbonate and basic magnesium carbonate. The solution was
filtered to remove the precipitated magnesium. The magnesium
remaining in solution was removed by adding a limed soda ash
reagent which also reduced calcium as an insoluble calcium
carbonate solid. The resultant purified brine was filtered and
contained 1%Li, 0.0002% Mg, 0.0024% Ca, 6.9% Na, 15.5% Cl. A soda
ash solution was prepared using lithium carbonate wash water
filtrate and added to the purified brine. The lithium carbonate
crystals were filtered and subsequently washed with hot de-ionized
or distilled water and subsequently used as the feed to the
bicarbonate reactor. The lithium carbonate filtrate, which is the
mother liquor, was recycled to the process, and the wash filtrate
was recycled to prepare the soda ash solution. A portion of the
mother liquor was discharged from the process to remove the excess
water and sodium chloride accumulated in the aqueous phase.
[0143] The filtered lithium carbonate crystals, a cooled mixture of
recycled low sodium lithium carbonate mother liquor filtrate and
wash water filtrate, and carbon dioxide gas from the low sodium
lithium carbonate crystallizer were fed continuously to form a
slurry in a baffled bicarbonate reactor. The carbon dioxide gas was
dispersed using a high-speed mixer. The carbon dioxide gas and the
mother liquor/wash filtrate solution were fed to the bottom of the
reactor. This formed a bicarbonate solution that was filtered and
sent to the lithium carbonate crystallizer. In this example the
reactor temperature to form the bicarbonate solution was controlled
between. 0.degree. C. and 35.degree. C. The lithium carbonate feed
rate was controlled to maintain as much suspended solids as
possible. The liquid volume of the entire system was maintained
constant and the excess liquid volume generated by the addition of
the wash filtrate was used as the process bleed.
[0144] Prior to feeding the cool bicarbonate solution to the
crystallizer, it was filtered to remove insoluble impurities and
heated in a heat exchanger to recover the heat contained in the
recycled mother liquor and wash filtrate. The preheated bicarbonate
solution was then continuously added to the heated bicarbonate
decomposer/lithium carbonate crystallizer maintained at 70.degree.
C. to 90.degree. C. The lithium carbonate solids and the liquid
were continuously removed and filtered hot. The filtered low sodium
lithium carbonate crystals were continuously washed with hot
distilled water then dried. The mother liquor and the wash filtrate
were recycled to the bicarbonate reactor via a heat exchanger.
[0145] Table 4 gives an example of the production rate for the
continuous purification apparatus described according to the
conditions in Example 1. Table 5 gives the analysis of products
produced. TABLE-US-00008 TABLE 4 RELATION OF PRODUCTION RATE AND
TEMPERATURE IN AN APPARATUS FOR CONTINUOUSLY PRODUCING LOW SODIUM
LITHIUM CARBONATE REACTOR TEMPERATURE, .degree. C. Li2CO3
CRYSTALLIZATION LiHCO.sub.3 Li.sub.2CO.sub.3 RATE, grams/hour 35 70
45.4 35 90 89.2 10 70 108.9 0 70 113.4 10 90 133.5 0 90 195.2
[0146] TABLE-US-00009 TABLE 5 CHEMICAL ANALYSIS (DRY BASIS) Low
Sodium Li2CO3, ppm Li2CO3 Feed, ppm (average from Example 1) Na 800
4.0 .+-. 0.7 Mg 28 6.3 .+-. 1 Ca 81 34 .+-. 14 S 120 16 .+-. 16 B
1.2 0.5 .+-. 0.04 Si 82 4.5 .+-. 1.5 Fe 3.3 1.2 .+-. 0.3
EXAMPLE 2
[0147] Preparing Ultra High Purity Lithium Carbonate
[0148] Ultra high purity lithium carbonate was prepared as
described above in the same equipment to which was added an ion
exchanger between the filter and the heat exchanger. The ion
exchange column contains Rohm and Haas, Amberlite IRC-718. The
purity of this product is listed in Table 6. TABLE-US-00010 TABLE 6
ULTRA HIGH PURITY LITHIUM CARBONATE (EXAMPLE 2) Wt % Li2CO3
>99.995 Mg <0.00001 Na <0.0004 K <0.00015 Ca
<0.00007 SO4 <0.003 B <0.0001 Cl <0.005 Si <0.0001
Zn <0.00001 Cr <0.00001 Cu <0.0001 Fe <0.0001 Ni
<0.0001 P <0.006
EXAMPLE 3
[0149] Preparing Low Sodium Lithium Chloride
[0150] Hydrochloric acid (35% conc.) containing less than 0.00015%
sodium was reacted with lithium carbonate prepared in Example 1.
The resulting solution was evaporated to crystallize lithium
chloride. The lithium chloride was filtered from the evaporated
solution and dried.
EXAMPLE 4
[0151] Preparing Ultra High Purity Lithium Chloride
[0152] As in Example 2, ultra-high purity lithium chloride was
prepared by passing the lithium chloride solution described in
Example 3 through an ion-exchange column to further reduce divalent
and trivalent impurities. The solution was crystallized to make
ultra-high purity lithium chloride.
EXAMPLE 5
[0153] Low Sodium Lithium Carbonate Using an Absorption Column
[0154] The diagram in FIG. 5 was the laboratory set-up used from
which the larger scale tests were done using a sieve tray column
(FIG. 6) and Scheibel column (FIG. 7).
[0155] The method followed that already described in Example 1. The
purified product had the same composition as in Example 1. This
demonstrated that absorption of carbon dioxide can be accomplished
in a typical reactor with a bubbler or an absorption column.
[0156] Other facets of the invention will be clear to the skilled
artisan, and need not be set out here. The terms and expression
which have been employed are used as terms of description and not
of limitation, and there is no intention in the use of such terms
and expression of excluding any equivalents of the features shown
and described or portions thereof, it being recognized that various
modifications are possible within the scope of the invention.
* * * * *