U.S. patent application number 11/321399 was filed with the patent office on 2006-05-25 for composition and method for preparing novel cationic thickeners.
Invention is credited to Olivier Braun, Paul Mallo, Herve Rolland.
Application Number | 20060111509 11/321399 |
Document ID | / |
Family ID | 32731995 |
Filed Date | 2006-05-25 |
United States Patent
Application |
20060111509 |
Kind Code |
A1 |
Braun; Olivier ; et
al. |
May 25, 2006 |
Composition and method for preparing novel cationic thickeners
Abstract
A composition and method for a linear or crosslinked cationic
polyelectrolyte, involving copolymerization of at least one
cationic monomer with at least one neutral monomer and at least
one-nonionic surfactant monomer.
Inventors: |
Braun; Olivier; (Naves,
FR) ; Mallo; Paul; (Croissy-Sur-Seine, FR) ;
Rolland; Herve; (Castres, FR) |
Correspondence
Address: |
Linda K. Russell
Suite 1800
2700 Post Oak Blvd.
Houston
TX
77056
US
|
Family ID: |
32731995 |
Appl. No.: |
11/321399 |
Filed: |
December 29, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10777848 |
Feb 12, 2004 |
7015279 |
|
|
11321399 |
Dec 29, 2005 |
|
|
|
Current U.S.
Class: |
524/815 ;
514/939; 514/941; 523/337; 524/827; 524/829; 524/831; 524/832 |
Current CPC
Class: |
C11D 3/3776 20130101;
A61K 8/72 20130101; A61Q 5/00 20130101; A61Q 17/005 20130101; D06P
1/5257 20130101; C08F 220/60 20130101; A61K 2800/5422 20130101;
A61Q 5/06 20130101; A61K 2800/5426 20130101; C08F 2/32 20130101;
Y10S 514/939 20130101; D06P 1/5242 20130101; A61Q 19/10 20130101;
Y10S 514/941 20130101; C09K 3/00 20130101; C11D 3/3769 20130101;
C08F 220/58 20130101; D06P 1/525 20130101; A61K 8/88 20130101 |
Class at
Publication: |
524/815 ;
524/827; 524/829; 524/831; 524/832; 523/337; 514/939; 514/941 |
International
Class: |
B41M 5/00 20060101
B41M005/00; C08F 2/20 20060101 C08F002/20 |
Foreign Application Data
Date |
Code |
Application Number |
Feb 13, 2003 |
FR |
0301723 |
Claims
1. (canceled)
2-15. (canceled)
16. A linear or crosslinked cationic polyelectrolyte composition,
wherein said composition comprises copolymerization of at least one
cationic monomer with at least one neutral monomer and at least one
nonionic surfactant monomer.
17. The composition according to claim 16, wherein said neutral
monomer comprises at least one component selected from the group
consisting of: a) acrylamide, b) methacrylamide, c)
vinylpyrrolidone, d) diacetone-acrylamide, e) dimethylacrylamide,
f) (2-hydroxyethyl) acrylate, g) (2,3-dihydroxypropyl) acrylate, h)
(2-hydroxyethyl) methacrylate, and i) (2,3-dihydroxypropyl)
methacrylate.
18. The composition according to claim 17, wherein said composition
further comprises an ethoxylated derivative of said component and
the molecular weight of said derivative is in the range of from
about 400 to about 1000.
19. The composition according to claim 16, wherein said cationic
monomer comprises at least one component selected from the group
consisting of: a)
2,N,N,N-tetramethyl-2-[(1-oxo-2-propenyl)amino]propanammonium
chloride (AMPTAC), b)
2,N,N-trimethyl-2-[(1-oxo-2-propenyl)amino]propanammonium chloride,
c) N,N,N-trimethyl-3-[(1-oxo-2-propenyl)amino]propanammonium
chloride (APTAC), d) "diallyldimethylammonium chloride (DADMAC), e)
N,N, N-trimethyl-2-[(1-oxo-2-propenyl)]ethanammonium chloride, f)
N,N,N-trimethyl-2-[(1-oxo-2-methyl-2-propenyl)]ethanammonium
chloride, g) N-[2-(dimethylamino)-1,1-dimethyl]acrylamide,
N-[2-(methylamino)-1,1-dimethyl]acrylamide, 2-(dimethylamino)ethyl
acrylate, h) 2-(dimethylamino)ethyl methacrylate, and i)
N-[3-(dimethylamino)propyl]acrylamide.
20. The composition according to claim 16, wherein said nonionic
surfactant monomers are represented by at least one formula
selected from the group consisting of: a)
A-C(.dbd.C)--O--[(CH.sub.2--CH(R.sub.1)--O].sub.n--R (I) b)
R'--[O--CH(R.sub.1')--CH.sub.2].sub.n--O--(O.dbd.)C-A'-C(.dbd.O)--O--[(CH-
.sub.2--CH(R.sub.1)--O].sub.nR (I') wherein said n and said n' each
are in the range of from about 1 to about 50; wherein said A is an
unsaturated aliphatic monovalent radical comprising from about 2 to
about 6 carbon atoms; wherein said A' is an unsaturated aliphatic
divalent radical comprising from about 2 to about 6 carbon atoms;
wherein said R.sub.1 and said R'.sub.1 each comprise at least one
at least one component selected from the group consisting of a
hydrogen atom, a methyl radical, and an ethyl radical; wherein said
R and said R' each comprise an aliphatic hydrocarbon radical which
is saturated, unsaturated, linear, or branched; and wherein said
aliphatic hydrocarbon radicals of said R and said R' each further
comprise from about a to about 30 carbon atoms.
21. The composition according to claim 20, wherein said A comprises
at least one component selected from the group consisting of: a)
vinyl radical, and b) 2-propenyl radical.
22. The composition according to claim 20, wherein said A'
comprises at least one component selected from the group consisting
of: a) 1,2-ethenediyl radical, and b) 2-propene-1,2-diyl
radical.
23. The composition according to claim 20, wherein said aliphatic
hydrocarbon radicals of said R and said R' each comprise from about
8 to about 18 carbon atoms.
24. The composition according to claim 20, wherein said R and said
R' each comprise at least one linear primary alcohol selected from
the group consisting of: a) octyl, b) pelargonic, c) decyl, d)
undecyl, e) undecenyl, f) lauryl, g) tridecyl, h) myristyl, i)
pentadecyl, i) cetyl, k) heptadecyl, l) stearyl, m) oleyl, n)
linoleyl, o) nonadecyl, p) arachidyl, q) behenyl, and r)
erucyl.
25. The composition according to claim 20, wherein said R and said
R' each comprise at least one 1-triacontenoic alcohol selected from
the group consisting of: a) octyl, b) nonyl, c) decyl, d) undecyl,
e) 10-undecenyl, f) dodecyl, g) tridecyl, h) tetradecyl, i)
pentadecyl, j) hexadecyl, k) heptadecyl, i) octadecyl, m)
octadecenyl, n) 10,12-octadecadienyl, o) 13-docosenyl, and p)
triacontanyl radicals.
26. The composition according to claim 20, wherein said R.sub.1 and
R'.sub.1 each further comprise a hydrogen atom.
27. The composition according to claim 20, wherein said n and n'
each comprise a range of from about 1 to about 10.
28. The composition according to claim 16, wherein said composition
comprises: a) from about 5% to about 35% of said cationic monomer;
b) from about 55% to about 95% of said neutral monomer; and c) from
about 0.1% to about 5% of said nonionic surfactant monomer, wherein
said percentages of each monomer are expressed in terms of
monomeric units.
29. The composition according to claim 28, wherein said composition
further comprises a non-zero proportion of
N-[2-hydroxy-1,1-bis(hydroxymethyl)ethyl]propenamide monomer.
30. The composition according to claim 29, wherein said composition
comprises: a) from about 5% to about 35% of a cationic monomer; b)
from about 35% to about 91% of a neutral monomer; c) from about
0.1% to about 5% of a nonionic surfactant monomer; and d) from
about 3% to about 20% of a
N-[2-hydroxy-1,1-bis(hydroxymethyl)ethyl]propenamide monomer,
wherein said percentages of each monomer are expressed in terms of
monomeric units.
31. The composition according to claim 30, wherein said composition
is not crosslinked.
32. The composition according to claim 30, wherein said composition
is crosslinked.
33. The composition according to claim 32, wherein said crosslinked
agent is selected from the group consisting of: a) diethylene, b)
polyethylenic compounds, c) diallyloxyacetic acid, d) sodium salt,
e) triallylamine, f) trimethylol propanetriacrylate, g) ethylene
glycol dimethacrylate, h) diethylene glycol diacrylate i)
diallylurea, and j) methylene bis(acrylamide).
34. The composition according to claim 33, wherein the molar
proportion of said crosslinked agent is in the range of from about
0.005% to about 1% of the total composition.
35. The composition according to claim 34, wherein said proportion
is in the range of from about 0.01% to about 0.2%.
36. The composition according to claim 35, wherein said proportion
is in the range of from about 0.01% to about 0.1%.
37. The composition according to claim 18, wherein said composition
may be utilized for at least one function selected from the group
consisting of: a) a thickener or an emulsifier for cosmetic or
pharmaceutical formulations; b) a thickener or an emulsifier for
printing pastes for the textile industry; c) a thickener or ran
emulsifier for industrial or household detergents; d) an additive
for the petroleum industry; and e) a rheology modifier for drilling
mud.
38. The composition according to claim 16, wherein said formulation
comprise hair care products.
39. A method for preparing a linear or crosslinked cationic
polyelectrolyte composition comprising copolymerizing at least one
cationic monomer with at least one neutral monomer and at least one
nonionic surfactant monomer.
40. A method for preparing a self-reversible invert latex
comprising the steps of: a) emulsifying monomers in an aqueous
solution in the presence of at least one water-in-oil type
emulsifying agent and a nonionic surfactant monomer; b) initiating
a polymerization reaction by introducing an emulsion formed in step
i) and a free radical initiator; and c) introducing at least one
oil-in-water type emulsifying agent when the polymerization
reaction is complete.
41. The method according to claim 40, wherein said method further
comprises emulsifying additives.
42. The method according to claim 40, wherein said method further
comprises adding a coinitiator.
43. The method according to claim 40, wherein the step of
introducing at least one oil-in-water type emulsifying agent occurs
at a temperature of less than about 50.degree. C.
44. The method according to claim 40, wherein step (ii) further
comprises distillation before introducing at least one oil-in-water
type emulsifying agent.
45. The method according to claim 40, wherein said polymerization
reaction is initiated by an oxidation-reduction pair generating
hydrogen sulphite ions (HSO.sub.3.sup.-).
46. The method according to claim 45, wherein said hydrogen
sulphite ions (HSO.sub.3.sup.-) comprises at least one component
selected from the group consisting of: a) cumene
hydroperoxide-sodium metabisulphite (Na.sub.2S.sub.2O.sub.5) pair;
and b) cumene hydroperoxide-thionyl-chloride (SOCl.sub.2) pair.
Description
[0001] The subject of the invention is novel polymers, their method
of preparation and their use as thickening and/or emulsifying
agent.
[0002] The thickening of aqueous phases is generally carried out by
incorporating therein hydrophilic polymers of all sorts, whether
they are synthetic or of natural origin.
[0003] Among the polymers of natural origin, xanthan or guar gums
are fairly widely used. They however have the conventional
disadvantages of natural products, namely a fluctuating quality and
price.
[0004] Among the hydrophilic synthetic thickeners most widely used
are polymers in the form of self-reversible invert latexes or
powders. They are used in a wide pH range and are often well
tolerated by humans. Such compositions are described for example in
French patents and patent applications published under the numbers
2721511, 2773805, 2774688, 2774996, 2782086, 2785801, 2786493,
2787457, 2789395, 2794034, 2794124, 2808446, 2808447 and
2810883.
[0005] These polymers are anionic and are essentially intended to
thicken and/or emulsify cosmetic, dermo-pharmaceutical or
pharmaceutical topical formulations which contain numerous
constituents such as oils, nonionic or anionic surfactants,
inorganic salts and/or weak acids.
[0006] Some formulations, in particular those intended for hair
care, also contain cationic surfactants and/or cationic
conditioning polymers. In this particular case, thickeners
consisting of anionic polymers are not recommended because of
electrostatic interactions between the positive and negative
charges which cause precipitation of the polymer, and cationic
thickening polymers such as those described in American patents
published under the numbers U.S. Pat. No. 4,806,345 and U.S. Pat.
No. 5,100,660 are preferably used.
[0007] Although the latter behave satisfactorily in an acidic
medium and are compatible with cationic surfactants, they
nevertheless lose their thickening power in formulations high in
electrolytes.
[0008] Accordingly, the applicant focussed on developing novel
thickeners of a cationic nature, which are compatible with cationic
surfactants while preserving their thickening power in media high
in electrolytes.
[0009] According to a first aspect, the subject of the invention is
a linear or crosslinked cationic polyelectrolyte, characterized in
that it is obtained by copolymerization of at least one cationic
monomer with at least one neutral monomer and at least one nonionic
surfactant monomer.
[0010] The expression crosslinked polyelectrolyte denotes a
nonlinear polyelectrolyte which exists in the form of a
three-dimensional network which is insoluble in water, but which is
capable of swelling in water and therefore leading to the
production of a chemical gel.
[0011] The expression copolymerization means, in the context of the
present invention, that the polymerization reaction uses at least
three different monomers. It can however involve more than three
different monomers.
[0012] The expression neutral monomer denotes monomers not
containing any strong or weak acid functional group or any
positively charged group. They are more particularly chosen from
acrylamide, methacrylamide, vinylpyrrolidone, diacetoneacrylamide,
dimethylacrylamide, (2-hydroxyethyl) acrylate,
(2,3-dihydroxypropyl) acrylate, (2-hydroxyethyl) methacrylate,
(2,3-dihydroxypropyl) methacrylate or an ethoxylated derivative
having a molecular weight of between 400 and 1000, of each of these
esters.
[0013] The expression cationic monomers denotes more particularly
monomers containing a quaternary ammonium functional group. They
are more particularly chosen from
2,N,N,N-tetramethyl-2-[(1-oxo-2-propenyl)amino]propanammonium
chloride (AMPTAC),
2,N,N-trimethyl-2-[(1-oxo-2-propenyl)amino]propanammonium chloride,
N,N,N-trimethyl-3-[(1-oxo-2-propenyl)amino]propanammonium chloride
(APTAC), diallyldimethylammonium chloride (DADMAC),
N,N,N-trimethyl-2-[(1-oxo-2-propenyl)]ethanammonium chloride,
N,N,N-trimethyl-2-[(1-oxo-2-methyl-2-propenyl)]-ethanammonium
chloride, N-[2-(dimethylamino)-1,1-dimethyl]acrylamide,
N-[2-(methylamino)-1,1-dimethyl]acrylamide, 2-(dimethylamino)ethyl
acrylate, 2-(dimethylamino)ethyl methacrylate or
N-[3-(dimethylamino)propyl]-acrylamide.
[0014] The expression nonionic surfactant monomer denotes more
particularly the polyalkoxylated derivatives of esters of monomers
containing a weak acid functional group with fatty alcohols. Such
compounds are represented either by general formula (I):
A-C(.dbd.O)--O--[(CH.sub.2--CH(R.sub.1)--O].sub.n--R (I) or
alternatively by general formula (I'):
R'--[O--CH(R'.sub.1)--CH.sub.2].sub.n--O--(O.dbd.)C-A'-C(.dbd.O)--O--[(CH-
.sub.2--CH(R.sub.1)--O].sub.n--R (I') in which formulae (I) and
(I'):
[0015] n and n' represent, independently of each other, a number
between 1 and 50;
[0016] A represents an unsaturated aliphatic monovalent radical
comprising from 2 to 6 carbon atoms,
[0017] A' represents an unsaturated aliphatic divalent radical
comprising from 2 to 6 carbon atoms,
[0018] R.sub.1 and R'.sub.1 represent, independently of each other,
a hydrogen atom, a methyl radical or an ethyl radical; and
[0019] R and R' represent, independently of each other, a saturated
or unsaturated, linear or branched, aliphatic hydrocarbon radical
comprising from 8 to 30 carbon atoms.
[0020] In formulae (I) and (I'), as defined above, the divalent
radicals: --[(CH.sub.2--CH(R.sub.1)--O].sub.n-- and
--[O--CH(R'.sub.1)--CH.sub.2].sub.n-- represent, independently of
each other:
[0021] either chains composed solely of ethoxyl groups (R.sub.1=H;
n>0),
[0022] or chains composed solely of propoxyl groups
(R.sub.1=CH.sub.3; n>0),
[0023] or chains composed solely of butoxyl groups
(R.sub.1=C.sub.2H.sub.5; n>0),
[0024] or chains composed of at least two different groups chosen
from ethoxyl, propoxyl and/or butoxyl groups.
[0025] When these chains are composed of different groups, they are
distributed right along this chain, in a block or randomly.
[0026] The expression unsaturated aliphatic monovalent radical
comprising from 2 to 6 carbon atoms denotes more particularly for
A, the vinyl radical (CH.sub.2.dbd.CH--) or the 2-propenyl radical
[CH.sub.2.dbd.C(CH.sub.3)--].
[0027] The expression unsaturated aliphatic divalent radical
comprising from 2 to 6 carbon atoms denotes more particularly for
A', the 1,2-ethenediyl radical (--CH.dbd.CH--) or the
2-propene-1,2-diyl radical [--CH.sub.2--C(.dbd.CH.sub.2)--].
[0028] The expression saturated or unsaturated, linear aliphatic
hydrocarbon radical comprising from 8 to 30 carbon atoms denotes
more particularly for R and R', the radicals derived from linear
primary alcohols such as for example those derived from octyl,
pelargonic, decyl, undecyl, undecenyl, lauryl, tridecyl, myristyl,
pentadecyl, cetyl, heptadecyl, stearyl, oleyl, linoleyl, nonadecyl,
arachidyl, behenyl, erucyl or 1-triacontanoic alcohols. They are in
this case octyl, nonyl, decyl, undecyl, 10-undecenyl, dodecyl,
tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl,
9-octadecenyl, 10,12-octadecadienyl, 13-docosenyl or triacontanyl
radicals.
[0029] The expression saturated or unsaturated, branched aliphatic
hydrocarbon radical comprising from 8 to 30 carbon atoms denotes
more particularly for R and R',
[0030] either the radicals derived from Guerbet alcohols, which are
branched 1-alkanols corresponding to general formula:
CH.sub.3--(CH.sub.2).sub.pCH[CH.sub.3--(CH.sub.2).sub.p-2]--CH.sub.2OH,
in which p represents an integer between 2 and 14, such as for
example the 2-ethylhexyl, 2-propylheptyl, 2-butyloctyl,
2-pentylnonyl, 2-hexyldecyl or 2-octyldodecyl radicals;
[0031] or the radicals derived from isoalkanols corresponding to
general formula:
CH.sub.3--CH(CH.sub.3)--(CH.sub.2).sub.m--CH.sub.2OH, in which m
represents an integer between 2 and 26, such as for example the
4-methylpentyl, 5-methylhexyl, 6-methylheptyl, 15-methylpentadecyl
or 16-methylheptadecyl radicals;
[0032] or the 2-hexyloctyl, 2-octyldecyl or 2-hexyldodecyl
radicals.
[0033] The subject of the invention is more particularly a cationic
polyelectrolyte as defined above, characterized in that the
nonionic surfactant monomer is chosen from the compounds of formula
(I) or the compounds of formula (I') as defined above, in
which:
[0034] R and R' represent, independently of each other, a saturated
or unsaturated, linear or branched, aliphatic hydrocarbon radical
comprising from 8 to 18 carbon atoms,
[0035] R.sub.1 and R'.sub.1 each represent a hydrogen atom, and
[0036] n and n' represent, independently of each other, a number
between 1 and 10.
[0037] The subject of the invention is more particularly a cationic
polyelectrolyte as defined above, characterized in that:
[0038] from 5% to 35% of the monomeric units which it comprises is
a cationic monomer,
[0039] from 55% to 95% of the monomeric units which it comprises is
a neutral monomer, and
[0040] from 0.1% to 5% of the monomeric units which it comprises is
a surfactant monomer.
[0041] According to another particular aspect of the present
invention, its subject is a cationic polyelectrolyte as defined
above, characterized in that it is obtained by copolymerization of
at least one cationic monomer with at least one neutral monomer, at
least one nonionic surfactant monomer and a non-zero proportion of
N-[2-hydroxy-1,1-bis(hydroxymethyl)ethyl)propenamide.
[0042] N-[2-Hydroxy-1,1-bis(hydroxymethyl)ethyl]propenamide, also
called tris(hydroxymethyl)acrylamidomethane or THAM: ##STR1## is
described in European patent application published under the number
EP 0 900 786.
[0043] When the polyelectrolyte which is the subject of the present
invention contains a non-zero proportion of THAM monomer,
[0044] from 5% to 35% of the monomeric units which it comprises is
a cationic monomer,
[0045] from 35% to 91% of the monomeric units which it comprises is
a neutral monomer,
[0046] from 0.1% to 5% of the monomeric units which it comprises is
a nonionic surfactant monomer, and
[0047] from 3% to 20% of the monomeric units which it comprises is
the THAM monomer.
[0048] According to another particular aspect of the present
invention, the polyelectrolyte as defined above is not
crosslinked.
[0049] According to another particular aspect of the present
invention, the polyelectrolyte as defined above is crosslinked. In
the latter case, the crosslinking agent is chosen in particular
from diethylenic or polyethylenic compounds, and most particularly
from diallyloxyacetic acid or one of the salts and in particular
its sodium salt, triallylamine, trimethylol propanetriacrylate,
ethylene glycol dimethacrylate, diethylene glycol diacrylate,
diallylurea or methylene bis(acrylamide).
[0050] The crosslinking agent is then generally used in the molar
proportion, expressed relative to the monomers used, of 0.005% to
1%, in particular 0.01% to 0.2%, and more particularly 0.01% to
0.1%.
[0051] According to a second aspect of the present invention, its
subject is a composition comprising an oily phase, an aqueous
phase, at least one water-in-oil (W/O) type emulsifying agent, at
least one oil-in-water (O/W) type emulsifying agent, in the form of
a self-reversible invert latex comprising from 20% to 70% by
weight, preferably from 25% to 40% by weight, of a cationic
polyelectrolyte as defined above.
[0052] The self-reversible invert latex according to the invention
generally contains from 2.5% to 15% by weight, and preferably from
4% to 9% by weight, of emulsifying agents, of which from 20% to
50%, in particular from 25% to 40% of the total weight of the
emulsifying agents present are of the water-in-oil (W/O) type and
in which from 80% to 50%, in particular from 75% to 60%, of the
total weight of the emulsifying agents are of the oil-in-water
(O/W) type.
[0053] In the self-reversible invert latex as defined above, the
oily phase generally represents from 15% to 50%, preferably from
20% to 25%, of its total weight.
[0054] The self-reversible invert latex also contains between 5%
and 60% by weight of water and more particularly between 20% and
50% by weight of water.
[0055] The self-reversible invert latex according to the invention
may also contain various additives such as complexing agents or
chain-regulating agents.
[0056] The expression "water-in-oil type emulsifying agent" denotes
emulsifying agents possessing a sufficiently low HLB value to form
water-in-oil emulsions, such as the surfactant polymers marketed
under the name HYPERMER.TM. such as HYPERMER.TM. B246, HYPERMER.TM.
B41 or HYPERMER.TM. 2296 or such as sorbitan esters, such as the
sorbitan monooleate marketed by the company SEPPIC under the name
MONTANE.TM. 80, the sorbitan isostearate marketed by SEPPIC under
the name MONTANE.TM. 70 or the sorbitan sesquioleate marketed by
SEPPIC under the name MONTANE.TM. 83. In the case of a mixture of
water-in-oil type emulsifying agents, the HLB value to be taken
into consideration is that of the said mixture.
[0057] The expression "oil-in-water type emulsifying agent" denotes
emulsifying agents possessing a sufficiently high HLB value to give
oil-in-water emulsions such as for example the ethoxylated sorbitan
esters such as the ethoxylated sorbitan oleate containing 20 moles
of ethylene oxide, ethoxylated castor oil containing 40 moles of
ethylene oxide, ethoxylated sorbitan laurate containing 20-moles of
ethylene oxide which are marketed by the company SEPPIC under the
names MONTANOX.TM. 80, SIMULSOL.TM. OL 50 and MONTANOX.TM. 20,
respectively, the ethoxylated lauryl alcohol containing 7 moles of
ethylene oxide marketed by the company SEPPIC under the name
SIMULSOL.TM. P7, the decaethoxylated oleocetyl alcohol of ethylene
marketed by the company SEPPIC under the name SIMULSOL.TM. OC 710
or the polyethoxylated sorbitan hexaoleates marketed by the company
ATLAS Chemical Industries under the names G-1086 and G-1096,
ethoxylated nonylphenols.
[0058] The oily phase of the self-reversible invert latex described
above consists:
[0059] either of a commercially available mineral oil containing
saturated hydrocarbons of the paraffin, isoparaffin and
cycloparaffin type, having at room temperature a density between
0.7 and 0.9 and a boiling point greater than 180.degree. C., such
as for example ISOPAR.TM. M or ISOPAR.TM. L, EXXOL.TM. D 100 S
marketed by EXXON or the white mineral oils in conformity with the
FDA regulations 21 CFR 172,878 and FR 178,3620(a), such as
MARCOL.TM. 52 or MARCOL.TM. 82, also marketed by EXXON;
[0060] or of the hydrogenated polyisobutene marketed in France by
the company Ets B. Rossow and Co under the name
PARLEAM--POLYSYNLANE.TM. and cited in Michel and Irene Ash;
Thesaurus of Chemical products, Chemise Publicite Cos, Ince. 1986
Volume 1, page 211 (ISBN 0 7131 3603 0);
[0061] or of the isohexadecane identified in Chemical Abstracts by
the number RN=93685-80-4 and which is a mixture of C.sub.12,
C.sub.16 and C.sub.20 isoparaffins containing at least 97% of
C.sub.16 isoparaffins, of which the principal constituent is
2,2,4,4,6,8,8-heptamethylnonane (RN=4390-04-9), marketed in France
by the company Bayer;
[0062] or of the isododecane marketed in France by the company
Bayer;
[0063] or of the squalane which is identified in Chemical Abstracts
by the number RN=111-01-3 and which is a mixture of hydrocarbons
containing more than 80% by weight of
2,6,10,15,19,23-hexamethyltetracosane. It is marketed in France by
the company SOPHIM, under the name PHYTOSQUALANE.TM.;
[0064] or of the fatty acid esters of formula (II):
R.sub.1--(C.dbd.O)--O--[[CH.sub.2--CH[O--[C(.dbd.O)].sub.m--R.sub.2]--CH.-
sub.2--O].sub.n--[C(.dbd.O)].sub.p].sub.q--R.sub.3 (II) in which
R.sub.1 represents a linear or branched, saturated or unsaturated
hydrocarbon chain containing from 7 to 30 carbon atoms, R.sub.2
represents, independently of R.sub.1, a hydrogen atom, a linear or
branched, saturated or unsaturated hydrocarbon chain containing
from 7 to 30 carbon atoms, R.sub.3 represents, independently of
R.sub.1 or of R.sub.2, a hydrogen atom or a linear or branched,
saturated or unsaturated hydrocarbon chain containing from 1 to 30
carbon atoms, m, n, p and q are, independently of each other, equal
to 0 or 1, it being understood that when R.sub.3 represents a
hydrogen atom, q is different from 0. As compounds of formula (II),
there are more particularly the compounds of formula (IIa):
R.sub.1--(C.dbd.O)--O--CH.sub.2--CH[O--[C(.dbd.O)].sub.m--R.sub.2]--CH.su-
b.2--O--[C(.dbd.O)].sub.p--R.sub.3 (IIa) corresponding to formula
(II) as defined above, in which q and n are equal to 1, or a
mixture of compounds of formulae (IIa); in this case, they are,
preferably, either a compound of formula (IIa.sub.1):
R.sub.1--(C.dbd.O)--O--CH.sub.2--CH(OH)--CH.sub.2--OH (IIa.sub.1)
corresponding to formula (IIa) as defined above, in which m and p
are equal to 0 and R.sub.2 and R.sub.3 represent a hydrogen atom,
or a compound of formula (IIa.sub.2):
R.sub.1--(C.dbd.O)--O--CH.sub.2--CH(OH)--CH.sub.2--O--C(.dbd.O)--R.sub.3
(IIa.sub.2) corresponding to formula (IIa) as defined above in
which p is equal to 1, m is equal to 0 and R.sub.2 represents a
hydrogen atom, or a compound of formula (IIa.sub.3)
R.sub.1--(C.dbd.O)--O--CH.sub.2--CH[O--C(.dbd.O)--R.sub.2]--CH.sub.2--O---
C(.dbd.O)--R.sub.3 (IIa.sub.3) corresponding to formula (IIa) as
defined above in which m and p are equal to 1, or a mixture of
compounds of formulae (IIa.sub.1), (IIa.sub.2) and/or
(IIa.sub.3).
[0065] As examples of compounds of formulae (IIa.sub.1),
(IIa.sub.2) or (IIa.sub.3), there are for example triglycerides of
fatty acids or of mixtures of fatty acids such as the mixture of
fatty acid triglycerides containing from 6 to 10 carbon atoms,
marketed under the name SOFTENOL.TM. 3819, the mixture of fatty
acid triglycerides containing from 8 to 10 carbon atoms, marketed
under the name SOFTENOL.TM. 3108, the mixture of fatty acid
triglycerides containing from 8 to 18 carbon atoms, marketed under
the name SOFTENOL.TM. 3178, the mixture of fatty acid triglycerides
containing from 12 to 18 carbon atoms, marketed under the name
SOFTENOL.TM. 3100, the mixture of fatty acid triglycerides
containing 7 carbon atoms, marketed under the name SOFTENOL.TM.
3107, the mixture of fatty acid triglycerides containing 14 carbon
atoms, marketed under the name SOFTENOL.TM. 3114 or the mixture of
fatty acid triglycerides containing 18 carbon atoms, marketed under
the name SOFTENOL.TM. 3118, glyceryl dilaurate, glyceryl dioleate,
glyceryl isostearate, glyceryl distearate, glyceryl monolaurate,
glyceryl monooleate, glyceryl monoisostearate, glyceryl
monostearate or a mixture of these compounds.
[0066] According to a third aspect of the present invention, its
subject is also a method for preparing a self-reversible invert
latex as defined above, characterized in that:
[0067] a) an aqueous solution containing the monomers and the
optional additives is emulsified in an oily phase in the presence
of one or more water-in-oil type emulsifying agents and nonionic
surfactant monomer,
[0068] b) the polymerization reaction is initiated by introducing
into the emulsion formed in a) a free radical initiator and
optionally a coinitiator and then it is allowed to progress,
[0069] c) when the polymerization reaction is complete, one or more
oil-in-water type emulsifying agents are introduced at a
temperature of less than 50.degree. C.
[0070] According to one variant of this method the reaction medium
derived from step b) is concentrated by distillation, before
carrying out step c).
[0071] According to a preferred embodiment of the method as defined
above, the polymerization reaction is initiated by an
oxidation-reduction pair generating hydrogen sulphite ions
(HSO.sub.3.sup.-), such as the cumene hydroperoxide-sodium
metabisulphite (Na.sub.2S.sub.2O.sub.5) pair or the cumene
hydroperoxide-thionyl chloride (SOCl.sub.2) pair at a temperature
of less than or equal to 10.degree. C., if desired accompanied by a
polymerization coinitiator such as for example
azobis(isobutyronitrile), dilauryl peroxide or sodium persulphate
and then carried out either almost adiabatically until a
temperature greater than or equal to 50.degree. C. is obtained, or
by controlling the temperature.
[0072] The polyelectrolyte as defined above may be isolated from
the preceding self-reversible invert latex by various methods known
to persons skilled in the art, such as the precipitation technique
which consists in pouring the latex into a large excess of a
solvent such as acetone, isopropanol or ethanol, or such as the
spray-drying technique which is described in the international
publication WO 00/01757 or by azeotropic dehydration.
[0073] According to a variant of the methods of preparation as
defined above, the polyelectrolyte which is the subject of the
present invention is isolated from the self-reversible invert
latex.
[0074] The polyelectrolyte or the self-reversible invert latex
which are the subject of the present invention may be used for
example as a thickener for cosmetic or pharmaceutical compositions,
as a thickener for printing pastes for the textile industry, as
thickeners for industrial or household detergents, as additives for
the petroleum industry, as a rheology modifier for drilling
mud.
[0075] By virtue of its cationic character, the polyelectrolyte
which is the subject of the present invention, and the
self-reversible invert latexes containing it, are advantageously
used as thickeners and/or as emulsifiers in cosmetic or
pharmaceutical compositions intended for hair care and/or
conditioning.
[0076] Such compositions are usually provided in the form of
emulsion or microemulsion shampoos and in particular in the case of
vaporizable emulsion conditioners.
[0077] Accordingly, according to a final aspect, the subject of the
invention is a cosmetic or pharmaceutical composition,
characterized in that it contains, as emulsifying and/or thickening
agent, an effective quantity either of the cationic polyelectrolyte
as defined above, or of the self-reversible invert latex containing
it.
[0078] The cationic polyelectrolytes or the self-reversible invert
latexes may be formulated in cosmetic, dermopharmaceutical or
pharmaceutical formulas such as mousses, gels, lotions, sprays,
shampoos, conditioners, lotions for the hands and the body,
sunscreens, and more generally in care products.
[0079] The following examples illustrate the present invention
without however limiting it.
A--EXAMPLES OF PREPARATION OF A SELF-REVERSIBLE INVERT LATEX
CONTAINING POLYELECTROLYTES ACCORDING TO THE INVENTION
Example 1
Self-Reversible Invert Latex of the Copolymer
AM/APTAC/LA(4EO) (84.7/14.9/0.4) crosslinked with MBA
[0080] The following are loaded into a beaker, with stirring:
[0081] 164.4 g of deionized water, [0082] 362.1 g of a commercial
solution containing 50% of acrylamide (AM), [0083] 123.9 g of a
commercial solution containing 75% of
acrylamidopropyltrimethylammonium chloride (APTAC) [0084] 0.070 g
of methylene bisacrylamide (MBA), [0085] 0.45 g of a commercial
aqueous solution containing 40% of the sodium salt of
diethylenetriaminepentaacetic acid.
[0086] An oily phase is prepared by successively mixing: [0087] 259
g of isohexadecane, [0088] 20 g of sorbitan isostearate
(MONTANE.TM. 70), [0089] 5 g of HYPERMER.TM. 2296 (Uniquema),
[0090] 5 g of tetraethoxylated lauryl acrylate [LA(4EO)], [0091]
0.1 g of azobis(isobutyronitrile) (AIBN).
[0092] The aqueous phase is gradually incorporated into the organic
phase and then subjected to vigorous mechanical stirring by means
of an ULTRA-TURRAX.TM. type turbine mixer in order to form an
invert emulsion (water/oil).
[0093] The emulsion is then cooled to about 10.degree. C. and
placed under nitrogen bubbling for about 60 minutes in order to
remove oxygen therefrom. The polymerization is then initiated by
incorporating therein 10 cm.sup.3 of a solution of cumene
hydroperoxide at 0.68% by weight in isohexadecane. After
homogenization of the medium, 25 g of an aqueous sodium
metabisulphite solution at 0.1% by weight are added while allowing
the temperature of the mixture to rise to the final polymerization
temperature and then leaving the mixture for 90 minutes. The whole
is then cooled to about 35.degree. C., and then 40 g of ethoxylated
lauryl alcohol at 7 moles (SIMULSOL.TM. P7) are added. The desired
self-reversible invert latex is obtained.
[0094] Analysis
Polyelectrolyte content: about 27.5% by weight
[0095] Measurement of Viscosity
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex (Brookfield RVT, No. 6 rotor; speed: 5
revolutions per minute); .eta.=45 000 mPas
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex and containing 1% o of sodium
chloride
(Brookfield RVT, No. 3 rotor; speed: 5 revolutions per minute);
.eta.=1 280 mPas.
Example 2
Self-Reversible Invert Latex of the Copolymer
Noncrosslinked AM/APTAC/THAM/LA(4EO) (77.7/14.9/7.0/0.4)
[0096] The following are loaded into a beaker, with stirring:
[0097] 157.6 g of deionized water, [0098] 332.3 g of a commercial
solution containing 50% of acrylamide (AM), [0099] 123.9 g of a
commercial solution containing 75% of
acrylamidopropyltrimethylammonium chloride (APTAC) [0100] 36.8 g of
tris(hydroxymethyl)acrylamidomethane (THAM), [0101] 0.45 g of a
commercial aqueous solution containing 40% of the sodium salt of
diethylenetriaminepentaacetic acid.
[0102] An oily phase is prepared by successively mixing: [0103] 259
g of isohexadecane, [0104] 20 g of sorbitan isostearate
(MONTANE.TM. 70), [0105] 5 g of HYPERMER.TM. 2296 (Uniquema),
[0106] 5 g of tetraethoxylated lauryl acrylate [LA(4EO)], [0107]
0.1 g of azobis(isobutyronitrile) (AIBN).
[0108] The procedure is then carried out according to a procedure
identical to that of Example 1 and the desired self-reversible
invert latex is obtained.
[0109] Analysis
Polyelectrolyte content: about 29.7% by weight
[0110] Measurement of Viscosity
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex (Brookfield RVT, No. 6 rotor; speed: 5
revolutions per minute); .eta.=48 200 mPas
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex and containing 1% o of sodium
chloride
(Brookfield RVT, No. 3 rotor; speed: 5 revolutions per minute); 1=1
760 mPas.
Example 3
Self-Reversible Invert Latex of the Copolymer
Noncrosslinked AM/APTAC/THAM/LA(4EO) (72.7/19.9/7.0/0.4)
[0111] The following are loaded into a beaker, with stirring:
[0112] 137.5 g of deionized water, [0113] 311 g of a commercial
solution containing 50% of acrylamide (AM), [0114] 165.2 g of a
commercial solution containing 75% by weight of
acrylamidopropyltrimethylammonium chloride (APTAC) [0115] 36.8 g of
tris(hydroxymethyl)acrylamidomethane (THAM), [0116] 0.45 g of a
commercial aqueous solution containing 40% of the sodium salt of
diethylenetriaminepentaacetic acid.
[0117] An oily phase is prepared by successively mixing: [0118] 259
g of isohexadecane, [0119] 20 g of sorbitan isostearate
(MONTANE.TM. 70), [0120] 5 g of HYPERMER.TM. 2296 (Uniquema),
[0121] 5 g of tetraethoxylated lauryl acrylate [LA(4EO)I, [0122]
0.1 g of azobis(isobutyronitrile) (AIBN).
[0123] The procedure is then carried out according to a procedure
identical to that of Example 1 and the desired self-reversible
invert latex is obtained.
[0124] Measurement of Viscosity
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex (Brookfield RVT, No. 6 rotor; speed: 5
revolutions per minute); .eta.=84 000 mPas
Viscosity of an aqueous solution containing 3% by weight of the
self-reversible invert latex and containing 1% o of sodium
chloride
(Brookfield RVT, No. 3 rotor; speed: 5 revolutions per minute);
.eta.=3 560 mPas.
Examples of Formulations
Example 4
Antistress Hair Care
[0125] TABLE-US-00001 Formula Phase A Water qs 100% Xanthan gum
0.50% Phase B SEPICAP .TM. MP 3.00% Phase C Composition of Example
1 4.00% Phase D Butylene glycol 5.00% LANOL .TM. 99 5.00% SEPICIDE
.TM. HB 0.30% SEPICIDE .TM. CI 0.20% Perfume 0.20%
Procedure
[0126] Disperse the xanthan gum in water with a deflocculating
device. Then add SEPICAP.TM. MP, then the composition of Example 1;
disperse it and then add the ingredients of Phase D.
Example 5
Restructuring Cream Mask for Stressed and Embrittled Hair
[0127] TABLE-US-00002 Formula Phase A MONTANOV .TM. 82 3.00% LANOL
.TM. P 6.00% AMONYL .TM. DM 1.00% Isostearyl isononanoate 5.00%
Composition of Example 2 2.50% Phase B Water qs 100% Phase C
SEPICAP .TM. MP 3.00% SEPICIDE .TM. HB 0.30% SEPICIDE .TM. CI
0.20%
Procedure
[0128] Melt Phase A at 75.degree. C. Heat Phase B to 75.degree. C.
Emulsify A in B. At around 40.degree. C., introduce the
constituents of Phase C.
Example 6
Purifying Gel for the Face
[0129] TABLE-US-00003 Formula Phase A MONTALINE .TM. C 40 7.00%
Pearlescent base 2078 5.00% Composition of Example 3 2.00% Phase B
Water qs 100%
Example 7
Colouring Shampoo
[0130] TABLE-US-00004 Formula Phase A MONTALINE .TM. C 40 15.00%
Disodium cocamphoacetate 5.00% Cetrimonium chloride 1.00% SEPIPERL
.TM. N 3.00% Composition of Example 2 3.00% Phase B Colour qs Water
qs 100%
Example 8
Antimicrobial Soap for the Hands
[0131] TABLE-US-00005 Formula Phase A MONTALINE .TM. C 40 20.00%
Glycerin 5.00% Composition of Example 2 1.00% Phase B Water qs
100%
Example 9
Antiseptic Liquid Soap
[0132] TABLE-US-00006 Formula Phase A MONTALINE .TM. C 40 30.00%
ORAMIX .TM. NS 10 15.00% Chlorhexidine digluconate (at 20%) 5.00%
Composition of Example 1 2.00% Phase B Water qs 100%
[0133] The definitions of the commercial products used in the
examples are the following:
SEPICIDE.TM. HB is a preserving mixture comprising phenoxyethanol,
methylparaben, ethylparaben, propylparaben and butylparaben,
marketed by the company SEPPIC.
SEPICIDE.TM. CI is imidazolidinylurea, marketed by the company
SEPPIC.
ORAMIX.TM. NS 10: decyl glucoside marketed by SEPPIC.
MONTALINE.TM. C 40: (cocoammoniumcarbamoyl chloride) marketed by
SEPPIC.
SEPIPERL.TM. N: (cocoyl glucoside/cocoyl alcohol) marketed by
SEPPIC.
MONTANOV.TM. 82: (cocoyl glucoside/cetearyl alcohol) marketed by
SEPPIC.
AMONYL.TM. DM: (quaternium 82) marketed by SEPPIC.
SEPICAP.TM. MP: (sodium cocoyl amino acids/potassium dimethicone
copolyol panthenyl phosphate) marketed by SEPPIC.
LANOL.TM. P: (glycol palmitate) marketed by SEPPIC.
LANOL.TM. 99: (isononyl isononanoate) marketed by SEPPIC.
* * * * *