U.S. patent application number 10/984122 was filed with the patent office on 2006-05-11 for roofing cover board, roofing panel composite, and method.
Invention is credited to Brad C. Burdic, Christopher J. Griffin, Joel Evan Hazy, Raymond C. Swann.
Application Number | 20060096205 10/984122 |
Document ID | / |
Family ID | 36314876 |
Filed Date | 2006-05-11 |
United States Patent
Application |
20060096205 |
Kind Code |
A1 |
Griffin; Christopher J. ; et
al. |
May 11, 2006 |
Roofing cover board, roofing panel composite, and method
Abstract
A prefabricated cover board has a high-density polymer or
predominantly polymer material core layer having a density between
6 lbs/ft.sup.3 and 25 lbs/ft.sup.3. A prefabricated roofing panel
composite includes the cover board and an insulation board that has
a low-density polymer or predominantly polymer material foam core
layer having a density less than 6 lbs/ft.sup.3. The cover board
may have a waterproofing membrane forming the top major surface of
the cover board. When making the roofing panel composite, the
low-density foam core layer of the insulation board may be formed
with the high-density core layer of the cover board being currently
or subsequently formed over and bonded to a top major surface of
the low-density foam core layer in the same operation or preformed
insulation boards may be fed into a production line with the
high-density core layer of the cover board being formed over and
bonded to top major surfaces of the low-density foam core layers of
the insulation boards.
Inventors: |
Griffin; Christopher J.;
(Aurora, CO) ; Swann; Raymond C.; (Kansas City,
MO) ; Hazy; Joel Evan; (Brighton, CO) ;
Burdic; Brad C.; (Littleton, CO) |
Correspondence
Address: |
JOHNS MANVILLE INTERNATIONAL, INC.
717 SEVENTEENTH STREET
DENVER
CO
80202
US
|
Family ID: |
36314876 |
Appl. No.: |
10/984122 |
Filed: |
November 9, 2004 |
Current U.S.
Class: |
52/309.4 |
Current CPC
Class: |
B29C 44/24 20130101;
E04C 2/296 20130101; B32B 27/42 20130101; B32B 5/18 20130101; B29K
2075/00 20130101; B29D 99/001 20130101; E04C 2/284 20130101; E04C
2/205 20130101; Y10T 428/24967 20150115; B32B 27/32 20130101; B32B
2262/101 20130101; E04D 3/352 20130101; E04D 3/18 20130101; Y10T
156/10 20150115; Y10T 428/249953 20150401; Y10T 428/24998 20150401;
E04D 12/00 20130101; B32B 7/02 20130101; B32B 2038/0084 20130101;
Y10T 428/24331 20150115; Y10T 428/24992 20150115; B32B 27/40
20130101; B32B 5/022 20130101; Y10T 428/249987 20150401; E04D 3/354
20130101; B29C 44/326 20130101; Y10T 428/249989 20150401; E04D
3/351 20130101; B32B 2307/72 20130101; B32B 2419/06 20130101; B32B
5/24 20130101 |
Class at
Publication: |
052/309.4 |
International
Class: |
E04C 1/00 20060101
E04C001/00 |
Claims
1. A cover board for overlying low-density insulation of a roofing
system, comprising: a high-density predominantly polymer material
core layer with a density between 6 lbs/ft.sup.3 and 25
lbs/ft.sup.3; the high-density predominantly polymer material core
layer having a length, a width, and a thickness; the high density
predominantly polymer material core layer having a top major
surface and a bottom major surface that are each defined by the
length and the width of the high density predominantly polymer
material core layer.
2. The cover board for overlying low-density insulation of a
roofing system according to claim 1, wherein: the thickness of the
high-density predominantly polymer material core layer is between
about 0.08 inches and about 0.75 inches; and the high-density
predominantly polymer material core layer is a high-density
predominantly polyisocyanurate polymer material core layer.
3. The cover board for overlying low-density insulation of a
roofing system according to claim 1, wherein: the thickness of the
high-density predominantly polymer material core layer is between
about 0.08 inches and about 0.75 inches; and the high-density
predominantly polymer material core layer is a high-density
predominantly polyisocyanurate polymer material foam core
layer.
4. The cover board for overlying low-density insulation of a
roofing system according to claim 1, wherein: a waterproofing
membrane overlies and is bonded to the top major surface of the
high-density predominantly polymer material core layer and the
high-density predominantly polymer material core layer is a
high-density predominantly polyisocyanurate material core
layer.
5. The cover board for overlying low-density insulation of a
roofing system according to claim 1, wherein: a waterproofing
membrane overlies and is bonded to the top major surface of the
high-density predominantly polymer material core layer; the bottom
major surface of the high-density predominantly polymer material
core layer forms a bottom major surface of the cover board; and the
high-density predominantly polymer material core layer is a
high-density predominantly polyisocyanurate material foam core
layer.
6. A prefabricated roofing system panel comprising: a cover board;
the cover board comprising a high-density predominantly polymer
material core layer; the high-density core layer of the cover board
having a density between 6 lbs/ft.sup.3 and 25 lbs/ft.sup.3; the
high-density core layer of the cover board having a length, a
width, and a thickness; the high density core layer of the cover
board having a top major surface and a bottom major surface that
are each defined by the length and the width of the high density
core layer; an insulation board, the insulation board comprising a
low-density predominantly polymer material foam core layer; the
low-density foam core layer of the insulation board having a
density less than 6 lbs/ft.sup.3; the low-density foam core layer
of the insulation board having a length, a width, and a thickness;
the low-density foam core layer of the insulation board having a
top major surface and a bottom major surface that are each defined
by the length and the width of the low-density foam core layer; and
the bottom major surface of the high-density core layer of the
cover board being bonded to the top major surface of the
low-density foam core layer of the insulation board; and the bottom
major surface of the high-density core layer of the cover board and
the top major surface of the low-density foam core layer of the
insulation board being substantially coextensive.
7. The prefabricated roofing system panel according to claim 6,
wherein: the thickness of the high-density core layer of the cover
board is about 0.08 inches or greater; the thickness of the low
density foam core layer of the insulation board is about 0.50
inches or greater; and the lengths and widths of the high-density
core layer of the cover board and the low-density foam core layer
of the insulation board are each about 4 feet or greater.
8. The prefabricated roofing system panel according to claim 6,
wherein: the thickness of the high-density core layer of the cover
board is between about 0.08 inches and about 0.75 inches; the
thickness of the low-density foam core layer of the insulation
board is between about 0.50 inches and about 6 inches; the lengths
of the high-density core layer of the cover board and the
low-density foam core layer of the insulation board are each about
8 feet or greater; and the widths of the high-density core layer of
the cover board and the low-density foam core layer of the
insulation board are each about 4 feet or greater.
9. The prefabricated roofing system panel according to claim 6,
wherein: the polymer material of the high-density core layer of the
cover board and the low-density foam core layer of the insulation
board is polyisocyanurate.
10. The prefabricated roofing system panel according to claim 6,
wherein: the high-density core layer of the cover board is a
high-density predominantly polymer material foam core layer.
11. The prefabricated roofing system panel according to claim 6,
wherein: the cover board includes a top facer that overlies and is
bonded to the top major surface of the high-density core layer of
the cover board; the insulation board includes a bottom facer that
overlies and is bonded to the bottom major surface of the
low-density foam core layer of the insulation board; and the cover
board and the insulation board have a common facer that overlies
and is bonded to the bottom major surface of the high-density core
layer of the cover board and the top major surface of the
low-density foam core layer of the insulation board.
12. The prefabricated roofing system panel according to claim 11,
wherein: the top facer of the cover board is a waterproofing
membrane.
13. The prefabricated roofing system panel according to claim 6,
including: a baseboard comprising a high-density predominantly
polymer material core layer; the high-density core layer of the
baseboard having a density between 6 lbs/ft.sup.3 and 25
lbs/ft.sup.3; the high-density core layer of the baseboard having a
length, a width, and a thickness; the high-density core layer of
the baseboard having a top major surface and a bottom major surface
that are defined by the length and the width of the high-density
core layer of the baseboard; and the bottom major surface of the
low-density foam core layer of the insulation board being bonded to
the top major surface of the high-density core layer of the
baseboard; and the bottom major surface of the low-density foam
core layer of the insulation board and the top major surface of the
high-density core layer of the baseboard being substantially
coextensive.
14. The prefabricated roofing system panel according to claim 13,
wherein: the cover board includes a top facer that overlies and is
bonded to the top major surface of the high-density core layer of
the cover board; the baseboard includes a bottom facer that
overlies and is bonded to the bottom major surface of the
high-density core layer of the baseboard; the cover board and the
insulation board have a common facer that overlies and is bonded to
the bottom major surface of the high-density core layer of the
cover board and the top major surface of the low-density foam core
layer of the insulation board; and the baseboard and the insulation
board have a common facer that overlies and is bonded to the top
major surface of the high-density core layer of the baseboard and
the bottom major surface of the low-density foam core layer of the
insulation board.
15. The prefabricated roofing system panel according to claim 14,
wherein: the top facer of the cover board is a waterproofing
membrane.
16. A method of making prefabricated roofing system panels,
comprising: forming an insulation board comprising a low-density
predominantly polymer material foam core layer having a density of
less than 6 lbs/ft.sup.3 in a continuous process wherein the
low-density foam core layer of the insulation board formed has a
width, a thickness, a continuous length, and a top major surface
and a bottom major surface that are each defined by the length and
the width of the low-density foam core layer of the insulation
board; forming a cover board comprising a high-density
predominantly polymer material core layer having a density between
6 lbs/ft.sup.3 and 25 lbs/ft.sup.3 in a continuous process wherein
the high-density core layer of the cover board formed has a width,
a thickness, a continuous length, and a top major surface and a
bottom major surface that are each defined by the length and the
width of the high-density core layer of the cover board; and
forming the widths of the low-density foam core layer of the
insulation board and the high-density core layer of the cover board
to be substantially the same with the core layer of one of the
boards being formed over and bonded to one of the major surfaces of
the core layer of the other board to form a composite.
17. The method of making prefabricated roofing system panels
according to claim 16, wherein: the core layers of the insulation
board and the cover board are formed concurrently.
18. The method of making prefabricated roofing system panels
according to claim 15, wherein: the thickness of the high-density
core layer of the cover board is about 0.08 inches or greater; the
thickness of low-density foam core layer of the insulation board is
about 0.50 inches or greater; the widths of the high-density foam
core layer of the cover board and the low-density foam core layer
of the insulation board are each about 4 feet or greater; and the
composite formed by the high-density foam core layer of the cover
board and the low-density foam core layer of the insulation board
is periodically cut to form roofing systems panels that are each
about 4 feet or greater in length.
19. The method of making prefabricated roofing system panels
according to claim 16, wherein: the thickness of high-density core
layer of the cover board is between about 0.08 inches and about
0.75 inches; the thickness of the low-density foam core layer of
the insulation board is between about 0.50 inches and about 6
inches; the widths of the high-density foam core layer of the cover
board and the low-density foam core layer of the insulation board
are each about 4 feet or greater; and the composite formed by the
high-density core layer of the cover board and the low-density foam
core layer of the insulation board is periodically cut to form
roofing system panels that are each about 8 feet or greater in
length.
20. The method of making prefabricated roofing system panels
according to claim 16, wherein: the polymer material of the
high-density core layer of the cover board and the low-density foam
core layer of the insulation board is polyisocyanurate.
21. The method of making prefabricated roofing system panels
according to claim 16, wherein: the high-density core layer of the
cover board is formed over and bonded to the top major surface of
the low-density foam core layer of the insulation board.
22. The method of making prefabricated roofing system panels
according to claim 16, including: applying a top facer to the
low-density foam core layer of the insulation board during the
formation of the low-density foam core layer of the insulation
board that overlies and is bonded to the top major surface of the
low-density foam core layer of the insulation board and applying a
bottom facer to the low-density foam core layer of the insulation
board during the formation of the low-density foam core layer of
the insulation board that overlies and is bonded to the bottom
major surface of the low-density foam core layer of the insulation
board; applying a top facer to the high-density core layer of the
cover board during the formation of the high-density core layer of
the cover board that overlies and is bonded to the top major
surface of the high-density core layer of the cover board; and
forming the high-density core layer of the cover board on the top
facer of the low-density foam core layer of the insulation board
whereby the top facer of the low-density foam core layer of the
insulation board becomes a common facer for the high-density foam
core layer of the cover board and the low-density foam core layer
of the insulation board.
23. The method of making prefabricated roofing system panels
according to claim 22, wherein: the top facer applied to the top
major surface of the high-density core layer of the cover board is
a waterproofing membrane.
24. A method of making prefabricated roofing system panels,
comprising: feeding a series of insulation boards that each
comprise a low-density predominantly polymer material foam core
layer having a density of less than 6 lbs/ft.sup.3 into a
production line in a continuous process; the low-density foam core
layer of each of the insulation boards having a width, a thickness,
a length, and a top major surface and a bottom major surface that
are each defined by the length and the width of the low-density
foam core layer of the insulation board; forming a cover board
comprising a high-density predominantly polymer material core layer
having a density between 6 lbs/ft.sup.3 and 25 lbs/ft.sup.3 and a
width substantially equal to the widths of the low-density foam
core layers of the insulation boards; the high-density core layer
of the cover board being formed in a continuous process over and
bonded to the top major surfaces of the low-density foam core
layers of the insulation boards fed into the production line to
form a composite; and the composite being cut to the lengths of the
low-density foam core layers of the insulation boards fed into the
production line.
25. The method of making prefabricated roofing system panels
according to claim 24, wherein: the thickness of the high-density
core layer of the cover board is about 0.08 inches or greater; the
thickness of low-density foam core layer of each of the insulation
boards is about 0.50 inches or greater; the widths of the
high-density core layer of the cover board and the low-density foam
core layers of each of the insulation boards are each about 4 feet
or greater; and the composite formed by the high-density core layer
of the cover board and the low-density foam core layers of each of
the insulation boards is periodically cut to form roofing systems
panels that are each about 4 feet or greater in length.
26. The method of making prefabricated roofing system panels
according to claim 24, wherein: the thickness of high-density core
layer of the cover board is between about 0.08 inches and about
0.75 inches; the thickness of the low-density foam core layer of
each of the insulation boards is between about 0.50 inches and
about 6 inches; the widths of the high-density core layer of the
cover board and the low-density foam core layers of each of the
insulation boards are each about 4 feet or greater; and the
composite formed by the high-density core layer of the cover board
and the low-density foam core layers of each of the insulation
boards is periodically cut to form roofing system panels that are
each about 8 feet or greater in length.
27. The method of making prefabricated roofing system panels
according to claim 24, wherein: the polymer material of the
high-density core layer of the cover board and the low-density foam
core layers of each of the insulation boards is
polyisocyanurate.
28. The method of making prefabricated roofing system panels
according to claim 24, wherein: the low-density foam core layers of
each of the insulation boards have top and bottom facers that
overlie and are bonded to the top and bottom major surfaces of the
low-density foam core layers of each of the insulation boards; and
a top facer is applied to the high-density core layer of the cover
board during the formation of the high-density core layer of the
cover board that overlies and is bonded to a top major surface of
the high-density core layer of the cover board and the top facers
of the low-density foam core layers of the insulation boards become
a bottom facer for the high-density core layer of the cover
board.
29. The method of making prefabricated roofing system panels
according to claim 28, wherein: the top facer applied to the top
major surface of the high-density core layer of the cover board is
a waterproofing membrane.
Description
BACKGROUND OF THE INVENTION
[0001] The subject invention relates to low-slope roofs that are
typically found on commercial and industrial buildings and in
particular to a prefabricated high-density polymer or predominantly
polymer material cover board and a prefabricated roofing panel
composite, which includes the high-density polymer or predominantly
polymer material cover board and a low-density polymer or
predominantly polymer material foam insulation board, for use on
such low-slope roofs and to a method of making the cover board and
the roofing panel composite
[0002] Commercial and industrial buildings typically have roofs
with low-slope roof decks. The roofing systems for these roofs with
low-slope roof decks typically include one or more layers of a
low-density roofing insulation, a layer of roofing cover boards
that overlie the low-density roofing insulation layer(s), and a
waterproofing membrane that overlies the layer of cover boards. The
layer(s) of low-density insulation, such as a low-density
polymer-based foam insulation, if not protected, can be partially
crushed or otherwise damaged from worker traffic over the
insulation, the placement of heaving objects on the insulation, the
weather, and other causes commonly encountered in roofing
construction. The layer of roofing cover boards that overlies the
one or more layers of low-density insulation, protects the more
fragile low density insulation from damage, acts as a fire barrier,
provides a suitable substrate for the attachment of the overlying
waterproofing membrane, and augments the insulating function of the
low-density insulation. The uppermost waterproofing membrane layer
overlying the cover board layer protects the underlying cover board
and insulation layers from moisture and other adverse climatic
conditions. Normally, these three components (the low-density
insulation boards, the roofing cover boards, and the waterproofing
membrane) of the roofing system are separately manufactured and
separately and successively applied to the low-slope roof deck.
While these roofing systems function very well, there has remained
a need to provide an improved roofing cover board and to provide
prefabricated roofing panel composites that combine at least an
insulation board and the improved roofing cover board layer, and
that, preferably, combine an insulation board, the improved roofing
cover board layer and a waterproofing membrane. With the use of
such an improved roofing cover board and prefabricated roofing
panel composites, roofing systems for low-slope roof decks can be
improved and/or the time, labor and costs associated with the
installation of roofing systems on low-slope roof decks can be
reduced. The subject invention provides an improved roofing cover
board, an improved prefabricated roofing cover board and
waterproofing membrane composite, an improved prefabricated roofing
panel cover board and insulation board composite, and an improved
prefabricated roofing panel cover board, insulation board, and
waterproofing membrane composite. The subject invention also
provides a method for making the improved roofing cover board and
the prefabricated roofing panel composites including the improved
roofing cover board that is highly productive, relatively
economical, and efficient.
SUMMARY OF THE INVENTION
[0003] The high-density polymer or predominantly polymer material
cover board of the subject invention is or includes a high-density
polymer or predominantly polymer material core layer with a density
between 6 lbs/ft.sup.3 and 25 lbs/ft.sup.3. Preferably, a
waterproofing membrane overlies and is bonded to the top major
surface of the high-density core layer of the cover board to form a
cover board and waterproofing membrane composite. When the cover
board and waterproofing membrane composite is laid down and the
waterproofing membrane is bonded and sealed to the waterproofing
membranes of other cover board and waterproofing membrane
composites, the waterproofing membrane protects the high-density
core layer of the composite and underlying layers of the roofing
system from moisture and other climatic conditions. A separate
waterproofing membrane does not have to be applied over the cover
board and waterproofing membrane composite at the job site to
protect the high-density core layer of the cover board and
underlying roofing system layers from moisture, UV radiation, and
other climatic conditions. The density and thickness of the
high-density polymer or predominantly polymer material core layer
of the cover board are selected to provide the cover board with the
compressive strength to resist deformation so that the cover board
protects low-density insulation layers overlaid by the cover board
from damage and so that the cover board has surface characteristics
that promote the bonding of a top facer, e.g. waterproofing
membrane, to the high-density core layer of the cover board. The
prefabricated high-density polymer or predominantly polymer
material cover board of the subject invention is relatively
lightweight and easily cut. This makes the cover board easier to
install and increases the productivity of workers installing the
cover boards. In addition, the high-density polymer or
predominantly polymer material cover board of the subject invention
does not support mold growth, there are no glass fiber shards to
cause skin and eye irritation for installers, and the cover board
is not negatively impacted by the application of solvents, hot
asphalt, or adhesives.
[0004] The prefabricated roofing panel composites of the subject
invention include the cover board with its high density polymer or
predominantly polymer material core layer that has a density
between 6 lbs/ft.sup.3 and 25 lbs/ft.sup.3 and a low-density
insulation board with its low-density polymer or predominantly
polymer material foam core layer that has a density less than 6
lbs/ft.sup.3. The bottom major surface of the high-density cover
board overlies and is bonded to the top major surface of the
low-density foam insulation board and, in a preferred embodiment,
the high-density cover board includes a waterproofing membrane
facer that overlies and is bonded to the top major surface of the
high-density polymer or predominantly polymer material core of the
cover board. The cover board and the roofing panel composite may be
secured in a roofing system mechanically with screws, nails or
other mechanical fasteners and/or adhesively with asphalt or other
adhesives.
[0005] When making the high-density polymer or predominantly
polymer material cover board in accordance with the method of the
subject invention, the high-density polymer or predominantly
polymer material core layer of the cover board may be made without
facers, with only a top waterproofing membrane facer, or with both
a top waterproofing membrane facer and a bottom facer. When making
the prefabricated roofing panel composites in accordance with the
method of the subject invention, the low-density polymer or
predominantly polymer material foam core layer of the low-density
foam insulation board may be formed with the high-density core
layer of the high-density cover board being concurrently or
subsequently formed over and bonded to a top major surface of the
low-density foam insulation board in the same operation. In an
alternate version of the method of the subject invention for making
the prefabricated roofing panel composite, preformed low-density
foam insulation boards may be fed into a production line with the
high-density polymer or predominantly polymer material core layer
of the cover board being formed over and bonded to the top major
surfaces of the preformed low-density foam insulation boards. In
the method of the subject invention for making the prefabricated
roofing panel composite, no facer or a common facer may be used
intermediate the high-density core layer of the cover board and the
low-density foam core layer of the foam insulation board. In
addition, a waterproofing membrane facer may be applied and bonded
to the top major surface of the high-density polymer or
predominantly polymer material core layer of the cover board.
BRIEF DESCRIPTION OF THE DRAWINGS
[0006] FIG. 1 is a schematic perspective view of a prefabricated
high-density polymer or predominantly polymer material cover board
of the subject invention.
[0007] FIG. 2 is a schematic perspective view of a composite of the
subject invention that includes a prefabricated high-density
polymer or predominantly polymer material cover board and a top
facer.
[0008] FIG. 3 is a schematic perspective view of a prefabricated
roofing panel composite of the subject invention that includes a
high-density polymer or predominantly polymer material cover board
and a low-density polymer or predominantly polymer material foam
insulation board.
[0009] FIG. 4 is a schematic perspective view of a prefabricated
roofing panel composite of the subject invention that includes a
high-density polymer or predominantly polymer material cover board,
a low-density polymer or predominantly polymer material foam
insulation board, and a top facer.
[0010] FIG. 5 is a schematic perspective view of a prefabricated
roofing panel composite of the subject invention that includes a
high-density polymer or predominantly polymer material cover board,
a low-density polymer or predominantly polymer material foam
insulation board, and a high-density polymer or predominantly
polymer material baseboard.
[0011] FIG. 6 is a schematic perspective view of a prefabricated
roofing panel composite of the subject invention that includes a
high-density polymer or predominantly polymer material cover board,
a low-density polymer or predominantly polymer material foam
insulation board, a high-density polymer or predominantly polymer
material baseboard, and a top facer.
[0012] FIG. 7 is a schematic side view of a first production line
that can be used with the method of the subject invention to make a
prefabricated roofing panel composite of the subject invention that
includes a high-density polymer or predominantly polymer material
cover board and a low-density polymer or predominantly polymer
material foam insulation board.
[0013] FIG. 8 is a schematic side view of a second production line
that can be used with the method of the subject invention to make a
prefabricated roofing panel composite of the subject invention that
includes a high-density polymer or predominantly polymer material
cover board and a low-density polymer or predominantly polymer
material foam insulation board.
[0014] FIG. 9 is a schematic side view of a production line that
can be used with the method of the subject invention to make a
prefabricated roofing panel composite of the subject invention that
includes a high-density polymer or predominantly polymer material
cover board, a low-density polymer or predominantly polymer
material foam insulation board, and a high-density polymer or
predominantly polymer material baseboard.
[0015] FIG. 10 is a schematic side view of a third production line
that can be used with the method of the subject invention to make a
prefabricated roofing panel composite of the subject invention that
includes a high-density polymer or predominantly polymer material
cover board and a low-density polymer or predominantly polymer
material foam insulation board.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0016] FIG. 1 is a schematic perspective view of the cover board 10
of the subject invention, which has a high-density polymer or
predominantly polymer material core layer 12. The high-density
polymer or predominantly polymer material core layer 12 of the
cover board 10 has a density between 6 lbs/ft.sup.3 and 25
lbs/ft.sup.3 and preferably a density of at least 8 lbs/ft.sup.3.
The high-density polymer or predominantly polymer material core
layer 12 of the cover board 10 has a thickness of about 0.08 inches
or greater and, preferably, a thickness between about 0.08 inches
and about 0.75 inches. The density and thickness of the
high-density polymer or predominantly polymer material core layer
12 of the cover board 10 are selected to provide the cover board
with the compressive strength to resist deformation and protect
low-density insulation layers overlaid by the cover board from
damage, and to provide surface characteristics that promote the
bonding of a top facer, e.g. a waterproofing membrane, to the
high-density core layer of the cover board.
[0017] The high-density polymer or predominantly polymer material
core layer 12 has a top major surface 14 and a bottom major surface
16 that are each defined by the length and the width of the
high-density polymer or predominantly polymer material core layer.
The high-density polymer or predominantly polymer material core
layer 12 typically has a width of about four feet or greater and a
length of about four feet or greater, preferably, about eight feet
or greater and could have lengths that are limited only by the
ability to store, transport, and handle the high-density polymer or
predominantly polymer material cover board 10 prior to
installation.
[0018] The cover board 10 may have top and/or bottom facers that
are not shown in FIG. 1. When used, the top and/or bottom facers
typically overlie the entire or substantially the entire major
surface 14 and/or 16 of the high-density polymer or predominantly
polymer material core layer 12 to which the facers are bonded. The
top and bottom facers of the high-density polymer or predominantly
polymer material cover board 10 may be any sheet material that
provides suitable top and bottom major surfaces for the cover
board, such as but not limited to paper, foil, woven or nonwoven
mats made of fiberglass or other fibers or filaments, scrims,
etc.
[0019] The high-density polymer or predominantly polymer material
core layer 12 of the cover board 10 may be made of various
high-density polymer or predominantly polymer materials [e.g. a
high-density polyisocyanurate, polyurethane, polystyrene, or
phenolic material or a high-density material made of a blend of
these materials; a high-density polyisocyanurate, polyurethane,
polystyrene, or phenolic foam material or a high-density foam
material made of a blend of these materials; a high-density
predominantly polyisocyanurate, polyurethane, polystyrene, or
phenolic material with inorganic filler(s) or a high-density
material made of a blend of these materials with filler(s); a
high-density predominantly polyisocyanurate, polyurethane,
polystyrene, or phenolic foam material with inorganic filler(s) or
a high-density foam material made of a blend of these materials
with filler(s), a high-density material made of other thermoset
matrix polymers; etc.]. However, a preferred material for the
high-density core layer 12 is a high-density polyisocyanurate or
predominantly polyisocyanurate material or foam material. The
predominantly polymer materials of the high-density core layer 12
may contain various powdered and liquid fillers, fiber
reinforcements, fungi growth-inhibiting agents, and fire-retardants
to reduce the cost of and/or modify the properties of the
high-density core layer 12, such as but not limited to the
compressive strength, the toughness, the flexibility, the
friability, and the fire resistance of the core layer. Examples of
fillers that may be used in the high-density predominantly polymer
material core layer 12 are fillers such as limestone (CaCO.sub.3),
fiberglass, recycled polyisocyanurate dust, and
extenders/plasticizers.
[0020] FIG. 2 is a schematic perspective view of a prefabricated
cover board and facer composite 20 of the subject invention. The
composite 20 includes the cover board 10 and a facer 22, e.g. a
waterproofing membrane. Other than the inclusion of a top facer 22,
the prefabricated cover board and facer composite 20 is the same as
the cover board 10 of FIG. 1.
[0021] The top facer 22 of the composite 20 may be any sheet
material that provides a suitable top major surface for the cover
board and facer composite, such as but not limited to paper, foil,
woven or nonwoven mats made of fiberglass or other fibers or
filaments, scrims, etc. However, a preferred sheet material for the
top facer 22 is a sheet material that serves the dual function of
providing a facing during the manufacturing process and a
waterproofing membrane on the finished product such as but not
limited to a bituminous or modified bituminous membrane, or a
single ply membrane (e.g. a EPDM, PVC, or TPO membrane). Where the
top facer 22 is a waterproofing membrane, the facer may extend
beyond the high-density polymer or predominantly polymer material
core layer of the cover board 10 on one or more of the four sides
of the core layer (e.g. beyond a side edge and an end edge of the
top major surface of the core layer) to form membrane overlaps for
sealing to the membranes of other composites 20. While not shown,
the composite may also include a bottom facer that is bonded to the
bottom major surface of the high-density polymer or predominantly
polymer material core layer of the cover board. When used, the
bottom facer of the composite 20 may be any sheet material that
provides a suitable bottom major surface for the cover board and
facer composite for bonding to an underlying layer of the roofing
system, such as but not limited to paper, woven or nonwoven mats
made of fiberglass or other fibers or filaments, scrims, etc.
[0022] FIG. 3 is a schematic perspective view of a first
prefabricated roofing panel composite 30 of the subject invention.
The prefabricated roofing panel composite 30 includes a
high-density polymer or predominantly polymer material cover board
32 and an insulation board 34 that, as shown, are bonded directly
together. The prefabricated roofing panel composite 30 has a top
major surface 36 and a bottom major surface 38 that are each
defined by the length and the width of the roofing panel composite.
The prefabricated roofing panel composite 30 typically has a width
of about four feet or greater and a length of about four feet or
greater, preferably, about eight feet or greater and could have
lengths that are limited only by the ability to store, transport
and handle the roofing panel composites prior to installation.
[0023] In the prefabricated roofing panel composite 30, the cover
board 32 has a high-density polymer or predominantly polymer
material core layer 40. The high-density polymer or predominantly
polymer material core layer 40 of the cover board 32 in the
prefabricated roofing panel composite 30 has a density between 6
lbs/ft.sup.3 and 25 lbs/ft.sup.3 and preferably a density of at
least 8 lbs/ft.sup.3. The high-density polymer or predominantly
polymer material core layer 40 of the cover board 32 in the
prefabricated roofing panel composite has a thickness of about 0.08
inches or greater and, preferably, a thickness between about 0.08
inches and about 0.75 inches. The density and thickness of the
high-density polymer or predominantly polymer material core layer
40 of the cover board 32 are selected to provide the cover board
with the compressive strength to resist deformation and protect the
low-density insulation board 34 that is overlaid by the cover board
from damage, and to provide surface characteristics that promote
the bonding of a top facer, e.g. a waterproofing membrane, to the
high-density core layer 40 of the cover board.
[0024] The insulation board 34 in the prefabricated roofing panel
composite 30 includes a low-density polymer or predominantly
polymer material foam core layer 42. The low-density polymer or
predominantly polymer material foam core layer 42 of the insulation
board 34 has a density less than 6 lbs/ft.sup.3, preferably less
than 4 lbs/ft.sup.3, and typically a density between about 1
lbs/ft.sup.3 and about 3 lbs/ft.sup.3. The low-density polymer or
predominantly polymer material foam core layer 42 has a thickness
of about 0.50 inches or greater and, preferably, a thickness
between about 0.50 inches and about 6 inches. The density and
thickness of the low-density polymer or predominantly polymer
material foam core layer 42 of the insulation board 34 are selected
to provide the prefabricated roofing panel composite 30 with the
desired insulating properties for the roofing system
application.
[0025] The high-density polymer or predominantly polymer material
core layer 40 of the cover board 32 may be made of various
high-density polymer or predominantly polymer materials [e.g. a
high-density polyisocyanurate, polyurethane, polystyrene, or
phenolic material or a high-density material made of a blend of
these materials; a high-density polyisocyanurate, polyurethane,
polystyrene, or phenolic foam material or a high-density foam
material made of a blend of these materials; a high-density
predominantly polyisocyanurate, polyurethane, polystyrene, or
phenolic material with inorganic filler(s) or a high-density
material made of a blend of these materials with filler(s); a
high-density predominantly polyisocyanurate, polyurethane,
polystyrene, or phenolic foam material with inorganic filler(s) or
a high-density foam material made of a blend of these materials
with filler(s), a high-density material made of other thermoset
matrix polymers; etc.]. However, a preferred material for the
high-density core layer 40 is a high-density polyisocyanurate or
predominantly polyisocyanurate material or foam material.
[0026] The low-density polymer or predominantly polymer material
foam core layer 42 of the insulation board 34 may be made of
various low-density polymer or predominantly polymer foam materials
[e.g. a low-density polyisocyanurate, polyurethane, polystyrene, or
phenolic foam material or a low-density foam material made of a
blend of these materials; a low-density predominantly
polyisocyanurate, polyurethane, polystyrene, or phenolic foam
material with inorganic filler(s) or a low-density foam material
made of a blend of these materials with filler(s), a low-density
foam material made of other thermoset matrix polymers; etc.].
However, a preferred material for the low-density core layer 42 is
a low-density polyisocyanurate or predominantly polyisocyanurate
foam material.
[0027] When the high-density core layer 40 is made of a
predominantly polymer material, the high-density predominantly
polymer material of the core layer 40 may contain various powdered
and liquid fillers, fiber reinforcements, fire-retardants, fungi
growth-inhibiting agents, etc. to reduce the cost and/or modify the
properties of the high-density core layer 40 (such as but not
limited to the compressive strength, the flexibility, the
friability, the fire resistance of the core layer). When the
low-density core layer 42 is made of a predominantly polymer
material foam, the low-density predominantly polymer material foam
core layer 42 may contain various powdered and liquid fillers fiber
reinforcements, fire-retardants, fungi growth-inhibiting agents,
etc. to reduce the cost and/or modify the properties of the
low-density predominantly polymer material foam core layer.
Examples of fillers that may be used in the high-density core layer
40 of the cover board 32 and the low-density core layer 42 of the
insulation board 34 are fillers such as limestone (CaCO.sub.3),
fiberglass, recycled polyisocyanurate dust, and
extenders/plasticizers.
[0028] While, as shown in FIG. 3, the prefabricated roofing panel
composite 30 has no facers, the prefabricated roofing panel
composite 30 could have a common facer intermediate and bonded to
both the bottom major surface of the cover board core layer 40 and
the top major surface of the insulation board core layer 42, a top
facer bonded to the top major surface of the cover board core layer
40, and/or a bottom facer bonded to the bottom major surface of the
insulation board core layer 42. When used, the common facer of the
prefabricated roofing panel composite 30 may be any sheet material
with good bonding surfaces that facilitates a good bond between the
cover board 32 and insulation board 34, such as but not limited to
woven or nonwoven mats made of glass fibers, other fibers or
filaments, scrims, etc. When used, the top facer of the
prefabricated roofing panel composite 30 overlies the entire or
substantially the entire top major surface of the high-density core
layer 40 of the cover board 32. The top facer of the prefabricated
roofing panel composite 30 may be any sheet material that provides
a suitable top major surface for the prefabricated roofing panel
composite 30, such as but not limited to paper, foil, woven or
nonwoven mats made of fiberglass or other fibers or filaments,
scrims, etc. When used, the bottom facer of the prefabricated
roofing panel composite 30 overlies the entire or substantially the
entire bottom surface of the low-density foam core layer 42 of the
insulation board 34. The bottom facer of the prefabricated roofing
panel composite 30 may be any sheet material that provides a
suitable bottom major surface for the roofing panel composite 30,
such as but not limited to paper, foil, woven or nonwoven mats made
of fiberglass or other fibers or filaments, scrims, etc.
[0029] FIG. 4 is a schematic perspective view of a prefabricated
roofing panel composite 50 of the subject invention. The
prefabricated roofing panel composite 50 includes the high-density
polymer or predominantly polymer material cover board 32 and the
low-density polymer or predominantly polymer material foam
insulation board 34 that, as shown in FIG. 4, are bonded directly
together, and a top facer 52. Other than the inclusion of the top
facer 52, the prefabricated roofing panel composite 50 is the same
as the prefabricated roofing panel composite 30 of FIG. 3.
[0030] The top facer 52 of the prefabricated roofing panel
composite 50 is bonded to and overlies the entire or substantially
the entire top surface of the high-density polymer or predominantly
polymer material core layer of the cover board 32. The top facer 52
of the prefabricated roofing panel composite 50 may be any sheet
material that provides a suitable top major surface for the cover
board and facer composite, such as but not limited to paper, foil,
woven or nonwoven mats made of fiberglass or other fibers or
filaments, scrims, etc. However, a preferred sheet material for the
top facer 52 is a sheet material that serves the dual function of
providing a facing during the manufacturing process and a
waterproofing membrane on the finished product such as but not
limited to a bituminous or modified bituminous membrane, or a
single ply membrane (e.g. a EPDM, PVC, or TPO membrane). Where the
top facer 52 is a waterproofing membrane, the facer may extend
beyond the high-density core layer of the cover board 32 on one or
more of the four sides of the core layer, e.g. beyond a side edge
and an end edge of the top major surface of the core layer to
provide overlaps for sealing with the membranes of adjacent
panels.
[0031] While, as shown in FIG. 4, the prefabricated roofing panel
composite 50 only has a top facer 52, the prefabricated roofing
panel composite 50 could have a common facer intermediate and
bonded to both the bottom major surface of the cover board 32 core
layer 40 and the top major surface of the insulation board 34 core
layer 42, and/or a bottom facer bonded to the bottom major surface
of the insulation board 34 core layer 42. When used, the common
facer of the prefabricated roofing panel composite 50 may be any
sheet material with good bonding surfaces that facilitates a good
bond between the cover board 32 and insulation board 34, such as
but not limited to woven or nonwoven mats made of glass fibers,
other fibers or filaments, scrims, etc. When used, the bottom facer
of the prefabricated roofing panel composite 50 overlies the entire
or substantially the entire bottom surface of the low-density foam
core layer of the insulation board 34. The bottom facer of the
prefabricated roofing panel composite 50 may be any sheet material
that provides a suitable bottom major surface for the roofing panel
composite 50, such as but not limited to paper, foil, woven or
nonwoven mats made of fiberglass or other fibers or filaments,
scrims, etc.
[0032] FIG. 5 is a schematic perspective view of a prefabricated
roofing panel composite 60 of the subject invention that includes:
a high-density polymer or predominantly polymer material cover
board 62, a low-density polymer or predominantly polymer material
foam insulation board 64, and a high-density polymer or
predominantly polymer material baseboard 66. The high-density
polymer or predominantly polymer material cover board 62 and
baseboard 66 may have the same density or different densities. As
shown in FIG. 5, the cover board 62, the insulation board 64, and
the baseboard 66 are bonded directly together. The prefabricated
roofing panel composite 60 has a top major surface 68 and a bottom
major surface 70 that are each defined by the length and the width
of the prefabricated roofing panel composite. The prefabricated
roofing panel composite 60 typically has a width of about four feet
or greater and a length of about four feet or greater, preferably,
about eight feet or greater and could have lengths that are limited
only by the ability to store, transport and handle the roofing
panel composites prior to installation.
[0033] In the prefabricated roofing panel composite 60, the cover
board 62 has a high-density polymer or predominantly polymer
material core layer 72 and the baseboard 66 has a high-density
polymer or predominantly polymer material core layer 74. The
high-density polymer or predominantly polymer material core layers
72 and 74 each have a density between 6 lbs/ft.sup.3 and 25
lbs/ft.sup.3 and preferably a density of at least 8 lbs/ft.sup.3.
The high-density polymer or predominantly polymer material core
layer 72 of the cover board 62 and the high-density polymer or
predominantly polymer material core layer 74 of the baseboard 66
each have a thickness of about 0.08 inches or greater and,
preferably, a thickness between about 0.08 inches and about 0.75
inches. The density and thickness of the high-density polymer or
predominantly polymer material core layer 72 of the cover board 62
are selected to provide the cover board with the compressive
strength to resist deformation and protect the low-density
insulation board 64 that is overlaid by the cover board from
damage, and to provide surface characteristics that promote the
bonding of a top facer, e.g. a waterproofing membrane, to the core
layer 72 of the cover board.
[0034] The insulation board 64 in the prefabricated roofing panel
composite 60 includes a low-density polymer or predominantly
polymer foam core layer 76. The low-density polymer or
predominantly polymer material foam core layer 76 of the insulation
board 64 has a density less than 6 lbs/ft.sup.3, preferably less
than 4 lbs/ft.sup.3, and typically a density between about 1
lbs/ft.sup.3 and about 3 lbs/ft.sup.3. The low-density polymer or
predominantly polymer material foam core layer 76 has a thickness
of about 0.50 inches or greater and, preferably, a thickness
between about 0.50 inches and about 6 inches. The density and
thickness of the low-density polymer or predominantly polymer
material foam core layer 76 of the insulation board 64 are selected
to provide the prefabricated roofing panel composite 60 with the
desired insulating properties for the roofing system
application.
[0035] The high-density polymer or predominantly polymer material
core layers 72 and 74 of the cover board 62 and the baseboard 66
may be made of various high-density polymer or predominantly
polymer materials [e.g. a high-density polyisocyanurate,
polyurethane, polystyrene, or phenolic material or a high-density
material made of a blend of these materials; a high-density
polyisocyanurate, polyurethane, polystyrene, or phenolic foam
material or a high-density foam material made of a blend of these
materials; a high-density predominantly polyisocyanurate,
polyurethane, polystyrene, or phenolic material with inorganic
filler(s) or a high-density material made of a blend of these
materials with filler(s); a high-density predominantly
polyisocyanurate, polyurethane, polystyrene, or phenolic foam
material with inorganic filler(s) or a high-density foam material
made of a blend of these materials with filler(s), a high-density
material made of other thermoset matrix polymers; etc.]. However, a
preferred material for the high-density core layers 72 and 74 is a
high-density polyisocyanurate or predominantly polyisocyanurate
material or foam material.
[0036] The low-density polymer or predominantly polymer material
foam core layer 76 of the insulation board 64 may be made of
various low-density polymer or predominantly polymer foam materials
[e.g. a low-density polyisocyanurate, polyurethane, polystyrene, or
phenolic foam material or a low-density foam material made of a
blend of these materials; a low-density predominantly
polyisocyanurate, polyurethane, polystyrene, or phenolic foam
material with inorganic filler(s) or a low-density foam material
made of a blend of these materials with filler(s), a low-density
material made of other thermoset matrix polymers; etc.]. However, a
preferred material for the low-density core layer 76 is a
low-density polyisocyanurate or predominantly polyisocyanurate foam
material.
[0037] When the high-density core layers 72 and 74 are made of a
predominantly polymer material, the high-density predominantly
polymer material of the core layers 72 and 74 may contain various
powdered and liquid fillers, fiber reinforcements, fire-retardants,
fungi growth-inhibiting agents, etc. to reduce the cost and/or
modify the properties of the high-density core layers 72 and 74
(such as but not limited to the compressive strength, the
flexibility, the friability, the fire resistance of the core
layer). When the low-density core layer 76 is made of a
predominantly polymer material foam, the low-density predominantly
polymer material foam core layer 76 may contain various powdered
and liquid fillers fiber reinforcements, fire-retardants, fungi
growth-inhibiting agents, etc. to reduce the cost and/or modify the
properties of the low-density foam core layer. Examples of fillers
that may be used in the high-density core layers 72 of the cover
board 62 and the baseboard 66 and the low-density core layer 76 of
the insulation board 64 are fillers such as limestone (CaCO.sub.3),
fiberglass, recycled polyisocyanurate dust, and
extenders/plasticizers.
[0038] While, as shown in FIG. 5, the prefabricated roofing panel
composite 60 has no facers, the prefabricated roofing panel
composite 60 could have a common facer intermediate and bonded to
both the bottom major surface of the cover board core layer 72 and
the top major surface of the insulation board core layer 76, a
common facer intermediate and bonded to both the bottom major
surface of the insulation board core layer 76 and the top major
surface of the baseboard core layer 74, a top facer bonded to the
top major surface of the cover board core layer 72, and/or a bottom
facer bonded to the bottom major surface of the baseboard core
layer 74. When used, the common facers of the prefabricated roofing
panel composite 60 may be any sheet material with good bonding
surfaces that facilitates a good bond between the cover board 62,
the insulation board 64, and the baseboard 66, such as but not
limited to woven or nonwoven mats made of glass fibers, other
fibers or filaments, scrims, etc. When used, the top facer of the
prefabricated roofing panel composite 60 overlies the entire or
substantially the entire top major surface of the high-density core
layer 72 of the cover board 62. The top facer of the prefabricated
roofing panel composite 60 may be any sheet material that provides
a suitable top major surface for the prefabricated roofing panel
composite 60, such as but not limited to paper, foil, woven or
nonwoven mats made of fiberglass or other fibers or filaments,
scrims, etc. When used, the bottom facer of the prefabricated
roofing panel composite 60 overlies the entire or substantially the
entire bottom surface of the high-density core layer 74 of the
baseboard 66. The bottom facer of the prefabricated roofing panel
composite 60 may be any sheet material that provides a suitable
bottom major surface for the roofing panel composite 60, such as
but not limited to paper, foil, woven or nonwoven mats made of
fiberglass or other fibers or filaments, scrims, etc.
[0039] FIG. 6 is a schematic perspective view of a prefabricated
roofing panel composite 80 of the subject invention. The
prefabricated roofing panel composite 80 includes the high-density
polymer or predominantly polymer material cover board 62, the
low-density polymer or predominantly polymer material foam
insulation board 64, and the high-density polymer or predominantly
polymer material baseboard 66, that, as shown in FIG. 6, are bonded
directly together, and a top facer 82. Other than the inclusion of
a top facer 82, the prefabricated roofing panel composite 80 of
FIG. 6 is the same as the prefabricated roofing panel composite 60
of FIG. 5.
[0040] The top facer 82 of the prefabricated roofing panel
composite 80 is bonded to and overlies the entire or substantially
the entire top surface of the high-density polymer or predominantly
polymer material core layer of the cover board 62. The top facer 82
of the prefabricated roofing panel composite 80 may be any sheet
material that provides a suitable top major surface for the cover
board and facer composite, such as but not limited to paper, foil,
woven or nonwoven mats made of fiberglass or other fibers or
filaments, scrims, etc. However, a preferred sheet material for the
top facer 82 is a sheet material that serves the dual function of
providing a facing during the manufacturing process and a
waterproofing membrane on the finished product such as but not
limited to a bituminous or modified bituminous membrane, or a
single ply membrane (e.g. a EPDM, PVC, or TPO membrane). Where the
top facer 82 is a waterproofing membrane, the facer may extend
beyond the high-density polymer or predominantly polymer material
core layer of the cover board 62 on one or more of the four sides
of the core layer, e.g. beyond a side edge and an end edge of the
top major surface of the core layer to provide membrane overlaps
for sealing with the membranes of adjacent panels.
[0041] While, as shown in FIG. 6, the prefabricated roofing panel
composite 80 only has a top facer 82, the prefabricated roofing
panel composite 80 could have a common facer intermediate and
bonded to both the bottom major surface of the cover board core
layer and the top major surface of the insulation board core layer,
a common facer intermediate and-bonded to both the bottom major
surface of the insulation board core layer and the top major
surface of the baseboard core layer, and/or a bottom facer bonded
to the bottom major surface of the baseboard core layer. When used,
the common facers of the prefabricated roofing panel composite 80
may be any sheet material with good bonding surfaces that
facilitates a good bond between the cover board and insulation
board and the insulation board and the baseboard, such as but not
limited to woven or nonwoven mats made of glass fibers, other
fibers or filaments, scrims, etc. When used, the bottom facer of
the prefabricated roofing panel composite 80 overlies the entire or
substantially the entire bottom surface of the high-density core
layer of the baseboard 66. The bottom facer of the prefabricated
roofing panel composite 80 may be any sheet material that provides
a suitable bottom major surface for the prefabricated roofing panel
composite 80, such as but not limited to paper, foil, woven or
nonwoven mats made of fiberglass or other fibers or filaments,
scrims, etc.
[0042] FIG. 7 is a schematic side view of a first production line
100 that can be used with the method of the subject invention to
continuously make prefabricated roofing panel composites of the
subject invention in line, such as the prefabricated roofing panel
composites 30 of FIG. 3 and 50 of FIG. 4. The prefabricated roofing
panel composites 30 and 50 each include a high-density polymer or
predominantly polymer material cover board 32 and a low-density
polymer or predominantly polymer material foam insulation board 34.
The production line 100 includes: a first forming station 102 for
forming the low-density polymer or predominantly polymer material
foam insulation board 34 of the prefabricated roofing panel
composites 30 and 50; a second forming station 104 for forming the
high-density polymer or predominantly polymer material cover board
32 of the prefabricated roofing panel composites 30 and 50; and a
cutting station 106 for cutting the prefabricated roofing panel
composites 30 and 50 to length.
[0043] The first forming station 102 for forming the low-density
foam insulation board 34 includes a conventional dispenser 108 for
dispensing a low-density polymer or predominantly polymer material
foam precursor 110 (e.g. a low-density polyisocyanurate or
predominantly polyisocyanurate foam precursor) onto a facer, when
used, overlying a conveyor 112 of two spaced-apart opposed forming
conveyers 112 and 114 or directly onto the conveyor 112. As the
foam precursor 110 passes between the forming conveyors 112 and
114, foams and at least partially sets, the forming conveyors 112
and 114 cooperate to set the thickness of the low-density polymer
or predominantly polymer material foam core layer 42 of the
low-density polymer or predominantly polymer foam insulation board
34 formed from the precursor 110. The first forming station 102
also includes supplies (e.g. rolls) of facer materials 116 and 118
that can be fed over and/or beneath the low-density polymer or
predominantly polymer material foam precursor 110 to form a common
facer of the prefabricated roofing panel composites 30 and 50 and a
bottom facer of the prefabricated roofing panel composites 30 and
50.
[0044] The second forming station 104 of the production line 100
for forming the high-density polymer or predominantly polymer
material cover board 32 of the prefabricated roofing panel
composites 30 and 50 includes a conventional dispenser 120 for
dispensing a high-density polymer or predominantly polymer material
or foam precursor 122 (e.g. a high-density polyisocyanurate or
predominantly polyisocyanurate foam precursor) onto the low-density
polymer or predominantly polymer material foam core layer 42 or,
when used, a common facer overlying the low-density polymer or
predominantly polymer material foam core layer 42. With the
high-density polymer or predominantly polymer material precursor
122 overlying the low-density foam core layer 42 or, when used, the
common facer, the high-density polymer or predominantly polymer
material precursor 122 and the low-density foam core layer 42 pass
between two spaced-apart opposed forming conveyers 112 and 124
where the high-density polymer or predominantly polymer material
core layer 38 is formed and bonded directly to the low-density foam
core layer 42 or to the common facer overlying the low-density foam
core layer 42. The spaced-apart opposed forming conveyors 112 and
124 cooperate to set the thickness of both the high-density polymer
or predominantly polymer material core layer 40 and the
prefabricated roofing panel composite 30 or 50. The second forming
station 104 also includes supplies (e.g. rolls) of a facer material
126 that is fed over the high-density polymer or predominantly
polymer material precursor 122 to form the top facer 52 of both the
high-density cover board 32 and the prefabricated roofing panel
composite 50.
[0045] With the high-density core layer 40 and the low-density foam
core layer 42 of the prefabricated roofing panel composite 30 or 50
bonded together in the second forming station 104 to form a
continuous length of the prefabricated roofing panel composite 30
or 50, the prefabricated roofing panel composite 30 or 50 is then
cut to length to complete the formation of the prefabricated
roofing panel composite 30 or 50. In the cutting station 106 a
cutter, such as but not limited to a reciprocating cutter 128, cuts
the prefabricated roofing panel composite 30 or 50 coming from the
second forming station 104 to length.
[0046] While the production line 100, as shown, is capable of
applying three facer materials 116, 118, and 126 to the insulation
board 34 and the cover board 32 to form the prefabricated roofing
panel composites 30 and 50. The application of any one, any two, or
all of the facing materials 116, 118 and 126 to the insulation
board and cover board can be omitted to form the prefabricated
roofing panel composite 30 and all but the top facing material can
be omitted to form the prefabricated roofing panel composite 50
with the desired number of facers. The facers 116, 118 and 126
normally prevent the polymer or predominantly polymer layers from
sticking to the conveyors. However, with a shift in the chemistry
of the precursors 110 and 122 to affect the tackiness of the layers
produced so that they do not stick to the surfaces of the conveyors
or by applying release films or coatings to the surfaces of the
conveyers that will not allow the layers produced to stick to the
surfaces of the conveyors, when desired, any one or all of the
facing materials are not needed for and could be eliminated from
the manufacturing process.
[0047] FIG. 8 is a schematic side view of a second production line
200 that can be used with the method of the subject invention to
continuously make prefabricated roofing panel composites of the
subject invention, such as the prefabricated roofing panel
composites 30 of FIG. 3 and 50 of FIG. 4. The prefabricated roofing
panel composites 30 and 50 each include a high-density polymer or
predominantly polymer material cover board and a low-density
polymer or predominantly polymer material foam insulation board.
The production line 200 includes: an in-feed conveyor 202 for
continuously feeding a series of low-density polymer or
predominantly polymer material foam insulation boards 34 of the
prefabricated roofing panel composite into a forming station 204;
the forming station 204 for forming the high-density polymer or
predominantly polymer material cover board 32 of the prefabricated
roofing panel composites 30 and 50; and a cutting station 206 for
cutting the prefabricated roofing panel composites 30 and 50 to
length.
[0048] The low-density polymer or predominantly polymer material
foam insulation boards 34 may include a top facer that, when used,
forms a common facer of the prefabricated roofing panel composites
30 and 50 and may include a bottom facer that, when used, forms a
bottom facer of the prefabricated roofing panel composites.
Preferably, the low-density polymer or predominantly polymer
material foam insulation boards 34 are fed into the forming station
204 lengthwise with the ends of successive insulation boards 34 in
the continuous series of insulation boards abutting each other.
[0049] The forming station 204 of the production line 200 for
forming the high-density polymer or predominantly polymer material
cover board 32 of the prefabricated roofing panel composite 30
includes a conventional dispenser 208 for dispensing the
high-density polymer or predominantly polymer material precursor
210 (e.g. a high-density polyisocyanurate or predominantly
polyisocyanurate precursor) directly onto the low-density foam core
layers 42 of the insulation boards 34 or, when used the common
facers overlying the low-density foam core layers of the
low-density foam insulation boards. With the high-density polymer
or predominantly polymer material precursor 210 directly overlying
the low-density foam core layers 42 of the insulation boards or the
common facers 36 carried by the low-density foam insulation boards
34, the high-density polymer or predominantly polymer material
precursor 210 and the low-density foam insulation boards 34 pass
between two spaced-apart opposed forming conveyers 212 and 214
where the high-density polymer or predominantly polymer material
core layers 38 of the cover boards 32 are formed and bonded
directly to the low-density foam core layers 42 of the insulation
boards 34 or to the common facers overlying the low-density foam
insulation board 34. The spaced-apart opposed forming conveyors 212
and 214 cooperate to set the thickness of both the high-density
polymer or predominantly polymer material core layer 40 and the
prefabricated roofing panel composite 30 or 50. The forming station
204 also includes supplies (e.g. rolls) of a facer material 216
that is fed over the high-density polymer or predominantly polymer
material precursor 210 to form the top facer 52 of both the
high-density polymer or predominantly polymer material cover board
32 and the prefabricated roofing panel composite 50.
[0050] With the high-density core layer 40 and the low-density foam
core layer 42 of the prefabricated roofing panel composite 30 or 50
bonded together in the forming station 204 to form a continuous
length of the prefabricated roofing panel composite 30 or 50, the
prefabricated roofing panel composite 30 or 50 is then cut to
length to complete the formation of the prefabricated roofing panel
composite 30 or 50. In the cutting station 206 a cutter, such as
but not limited to a reciprocating cutter 218, cuts the
prefabricated roofing panel composite 30 coming from the forming
station 204 to length.
[0051] The production line 200, as shown, is capable of making the
prefabricated roofing panel composite 30 by feeding preformed
low-density polymer or predominantly polymer material foam
insulation boards 34 into the forming station 204 and omitting the
application of the facer material 216 to the cover board 32 and is
capable of making the prefabricated roofing panel composite 50 by
feeding preformed low-density polymer or predominantly polymer
material foam insulation boards 34 into the forming station 204 and
applying of the facer material 216 to the cover board 32. The facer
216 normally prevents the high-density polymer or predominantly
polymer material layer from sticking to the conveyor 212. However,
with a shift in the chemistry of the precursor 210 to affect the
tackiness of the layer produced so that the layer does not stick to
the surface of the conveyor 212 or by applying a release film or
coating to the surface of the conveyer 212 that will not allow the
layer produced to stick to the surface of the conveyor, when
desired, the facing materials 216 is not needed for and could be
eliminated from the manufacturing process.
[0052] FIG. 9 is a schematic side view of a production line 300
that can be used with the method of the subject invention to
continuously make a prefabricated roofing panel composite of the
subject invention, such as the prefabricated roofing panel
composites 60 of FIG. 5 and 80 of FIG. 6. These prefabricated
roofing panel composites each include: a high-density polymer or
predominantly polymer material cover board 62, a low-density
polymer or predominantly polymer material foam insulation board 64,
and a high-density polymer or predominantly polymer material
baseboard 66. The production line 300 includes: a first forming
station 302 for forming the high-density polymer or predominantly
polymer material baseboard 66 of the prefabricated roofing panel
composites 60 and 80; a second forming station 304 for forming the
low-density polymer or predominantly polymer material foam
insulation board 64 of the prefabricated roofing panel composites
60 and 80; a third forming station 306 for forming the high-density
polymer or predominantly polymer material cover board 62 of the
prefabricated roofing panel composites 60 and 80; and a cutting
station 308 for cutting the prefabricated roofing panel composites
60 and 80 to length.
[0053] The first forming station 302 for forming the high-density
polymer or predominantly polymer material baseboard 56 includes a
conventional dispenser 310 for dispensing a high-density polymer or
predominantly polymer material precursor 312 (e.g. a high-density
polyisocyanurate or predominantly polyisocyanurate precursor) onto
a facer, when used, overlying a conveyor 314 of two spaced-apart
opposed forming conveyers 314 and 316 or directly onto the conveyor
314. As the precursor 310 passes between the forming conveyors 314
and 316, forms and at least partially sets, the forming conveyors
314 and 316 cooperate to set the thickness of the high-density
polymer or predominantly polymer material core layer 74 of the
high-density baseboard 66 formed from the precursor 310. The first
forming station 302 also includes supplies (e.g. rolls) of facer
materials 318 and 320 that may be fed over and/or beneath the
high-density polymer or predominantly polymer material precursor
310 to form, when used, a common facer of the prefabricated roofing
panel composites 60 and 80 and a bottom facer of the prefabricated
roofing panel composites 60 and 80.
[0054] The second forming station 304 of the production line 300
for forming the low-density polymer or predominantly polymer
material foam insulation board 64 of the prefabricated roofing
panel composites 60 and 80 includes a conventional dispenser 322
for dispensing a low-density polymer or predominantly polymer
material foam precursor 324 (e.g. a low-density polyisocyanurate or
predominantly polyisocyanurate foam precursor) directly onto the
high-density core layer 74 or, when used, onto a common facer
overlying the high-density core layer 74 of the baseboard 66. With
the low-density polymer or predominantly polymer material foam
precursor 324 directly overlying high-density core layer 74 or the
common facer overlying the high-density core layer 74 of the
baseboard 66, the low-density polymer or predominantly polymer
material foam precursor 324 and the high-density core layer 74 pass
between two spaced-apart opposed forming conveyers 314 and 326
where the low-density polymer or predominantly polymer material
foam core layer 76 of the insulation board 64 is formed and bonded
to the high-density core layer 74 or the common facer overlying the
high-density core layer 74 of the baseboard 66. The spaced-apart
opposed forming conveyors 314 and 326 cooperate to set the
thickness of the low-density polymer or predominantly polymer
material foam core layer 76 of the insulation board 64. The second
forming station 304 also includes supplies (e.g. rolls) of a facer
material 328 that can be fed over the low-density polymer or
predominantly polymer material foam precursor 324 to form a common
facer of the prefabricated roofing panel composites 60 and 80.
[0055] The third forming station 306 of the production line 300 for
forming the high-density polymer or predominantly polymer material
cover board 62 of the prefabricated roofing panel composites 60 and
80 includes a conventional dispenser 330 for dispensing a
high-density polymer or predominantly polymer material precursor
332 (e.g. a high-density polyisocyanurate or predominantly
polyisocyanurate precursor) directly onto the low-density foam core
layer 76 or the common facer overlying the low-density foam core
layer 76 of the insulation board 64. With the high-density polymer
or predominantly polymer material precursor 332 overlying the
low-density foam core layer 76 or the common facer overlying the
low-density foam core layer 76, the high-density polymer or
predominantly polymer material precursor 332, the low-density foam
insulation board 64, and the high-density baseboard 66 pass between
two spaced-apart opposed forming conveyers 314 and 334 where the
high-density polymer or predominantly polymer material core layer
72 of the cover board 62 is formed and bonded to the low-density
foam core layer 76 or the common facer overlying the low-density
foam core layer 76 of the insulation board 64. The spaced-apart
opposed forming conveyors 314 and 334 cooperate to set the
thickness of both the high-density polymer or predominantly polymer
material core layer 72 and the prefabricated roofing panel
composite 60 or 80. The third forming station 306 also includes
supplies (e.g. rolls) of a facer material 336 that is fed over the
high-density polymer or predominantly polymer material precursor
332 to form the top facer 82 of both the high-density cover board
62 and the prefabricated roofing panel composite 80.
[0056] With the high-density polymer or predominantly polymer
material cover board 62, the low-density polymer or predominantly
polymer material foam insulation board 64, and the high-density
polymer or predominantly polymer material baseboard 66 of the
prefabricated roofing panel composites 60 or 80 bonded together in
the third forming station 306 to form a continuous length of the
prefabricated roofing panel composite 60 or 80, the prefabricated
roofing panel composite 60 or 80 is then cut to length to complete
the formation of the prefabricated roofing panel composite 60 or
80. In the cutting station 308 a cutter, such as but not limited to
a reciprocating cutter 338, cuts the continuous prefabricated
roofing panel composite 60 or 80 coming from the third forming
station 306 to length.
[0057] While the production line 300, as shown, is capable of
applying four facer materials 318, 320, 328, and 336 to the
baseboard 66, the insulation board 64 and the cover board 62 to
form the prefabricated roofing panel composites 60 and 80. The
application of any one, any two, any three or all of the facing
materials 318, 320, 328, and 336 to the baseboard, the insulation
board and the cover board can be omitted to form the prefabricated
roofing panel composite 60 and all but the top facing material can
be omitted to form the prefabricated roofing panel composite 80
with the desired number of facers. The facers 318, 320, 328, and
336 normally prevent the composite layers from sticking to the
conveyors. However, with a shift in the chemistry of the precursors
312,324, and 332 to affect the tackiness of the layers produced so
that they do not stick to the surfaces of the conveyors or by
applying release films or coatings to the surfaces of the conveyers
that will not allow the layers produced to stick to the surfaces of
the conveyors, when desired, any one or all of the facing materials
are not needed for and could be eliminated from the manufacturing
process.
[0058] FIG. 10 is a schematic side view of another production line
400 that can be used with the method of the subject invention to
continuously make prefabricated roofing panel composites of the
subject invention in line, such as the prefabricated roofing panel
composites 30 of FIG. 3 and 50 of FIG. 4. The prefabricated roofing
panel composites 30 and 50 each include a high-density polymer or
predominantly polymer material cover board 32 and a low-density
polymer or predominantly polymer material foam insulation board 34.
The production line 400 includes: a forming station 402 for forming
the low-density polymer or predominantly polymer material foam
insulation board 34 and the high-density polymer or predominantly
polymer material cover board 32 of the prefabricated roofing panel
composites 30 and 50; and a cutting station 404 for cutting the
prefabricated roofing panel composites 30 and 50 to length.
[0059] The forming station 402 for forming the low-density foam
insulation board 34 and the high-density cover board includes a
conventional dispenser 406 for dispensing a low-density polymer or
predominantly polymer material foam precursor 408 (e.g. a
low-density polyisocyanurate or predominantly polyisocyanurate foam
precursor) onto a facer, when used, overlying a conveyor 410 of two
spaced-apart opposed forming conveyers 410 and 412 or directly onto
the conveyor 410. The forming station 402 also includes a
conventional dispenser 414 for dispensing a high-density polymer or
predominantly polymer material precursor 416 (e.g. a high-density
polyisocyanurate or predominantly polyisocyanurate material
precursor) onto the low-density polymer or predominantly polymer
material foam precursor of the core layer 42 or, when used, a
common facer overlying the low-density polymer or predominantly
polymer material foam precursor of the core layer 42. As the layers
of precursor 408 and 416 pass between the forming conveyors 410 and
412, the precursors form and at least partially set, the forming
conveyors 410 and 412 cooperate to set the thickness of the
low-density polymer or predominantly polymer material foam core
layer 42 of insulation board 34 formed from the precursor 408, the
thickness of the high-density polymer or predominantly polymer
material core layer 40 of cover board 32 formed from the precursor
416, and the thickness of the prefabricated roofing panel composite
30 or 50. The forming station 402 also includes supplies (e.g.
rolls) of facer materials 418, 420, and 422 that can be fed over
and/or beneath the low-density polymer or predominantly polymer
material foam precursor 408 to form a common facer of the
prefabricated roofing panel composites 30 and 50 and a bottom facer
of the prefabricated roofing panel composites 30 and 50 and that
can be fed over the high-density polymer or predominantly polymer
material precursor 416 to form a top facer of the prefabricated
roofing panel composites 30 and 50.
[0060] With the high-density core layer 40 and the low-density foam
core layer 42 of the prefabricated roofing panel composite 30 or 50
bonded together to form a continuous length of the prefabricated
roofing panel composite 30 or 50, the prefabricated roofing panel
composite 30 or 50 is then cut to length to complete the formation
of the prefabricated roofing panel composite 30 or 50. In the
cutting station 404 a cutter, such as but not limited to a
reciprocating cutter 424, cuts the prefabricated roofing panel
composite 30 or 50 coming from the forming station 402 to
length.
[0061] While the production line 400, as shown, is capable of
applying three facer materials 418, 420 and 422 to the insulation
board 34 and the cover board 32 to form the prefabricated roofing
panel composites 30 and 50. The application of any one, any two, or
all of the facing materials 418, 420, and 422 to the insulation
board and cover board can be omitted to form the prefabricated
roofing panel composite 30 and all but the top facing material can
be omitted to form the prefabricated roofing panel composite 50
with the desired number of facers. The facers 418, 420, and 422
normally prevent the layers of the composite from sticking to the
conveyors. However, with a shift in the chemistry of the precursors
408 and 416 to affect the tackiness of the layers produced so that
they do not stick to the surfaces of the conveyors or by applying
release films or coatings to the surfaces of the conveyers that
will not allow the layers produced to stick to the surfaces of the
conveyors, when desired, any one or all of the facing materials are
not needed for and could be eliminated from the manufacturing
process.
[0062] Preferably, the low-density polymer or predominantly polymer
material foam precursors 110, 324, and 408 are low-density
polyisocyanurate or predominantly polymer foam precursors.
Preferably, the high-density polymer or predominantly polymer
material precursors 122, 210, 312, 332, and 416 are high-density
polyisocyanurate or predominantly polyisocyanurate material
precursors. The high-density polymer or predominantly polymer
material precursors 122, 210, 312, 332, and 416 can be formulated
to produce high-density materials or foams by significantly
reducing or eliminating the blowing agent(s) from the precursors
122, 210, 312, 332, and 416. Pentane (HFC), micro-spheres, CO.sub.2
and water (as well as other materials) will act as blowing agents
for the precursors. The relatively high-density layers produced
using these types of precursors have improved strength
characteristics over the low-density foams normally produced for
insulation products. As the amount of blowing agent is reduced in
the precursors 122, 210, 312, 332, and 416, the density and the
compressive strength of the high-density layers produced increase.
These types of high-density core layers are much more resistant to
deformation than the typical low-density foam core layers.
[0063] In describing the invention, certain embodiments have been
used to illustrate the invention and the practices thereof.
However, the invention is not limited to these specific embodiments
as other embodiments and modifications within the spirit of the
invention will readily occur to those skilled in the art on reading
this specification. For example, the prefabricated roofing panel
composites could be in an upside down orientation to that shown and
described in connection with FIGS. 7 to 9. Thus, the invention is
not intended to be limited to the specific embodiments disclosed,
but is to be limited only by the claims appended hereto.
* * * * *