U.S. patent application number 11/253930 was filed with the patent office on 2006-03-09 for microfiber articles from multi-layer substrates.
This patent application is currently assigned to 3M Innovative Properties Company. Invention is credited to Terry R. Hobbs, Kimberley D. Klepzig, Robert S. Kody, Timothy J. Lindquist, John W. Longabach, Matthew J. Michel, Mario A. Perez, John M. Sebastian, Ravi K. Sura.
Application Number | 20060049386 11/253930 |
Document ID | / |
Family ID | 34136428 |
Filed Date | 2006-03-09 |
United States Patent
Application |
20060049386 |
Kind Code |
A1 |
Kody; Robert S. ; et
al. |
March 9, 2006 |
Microfiber articles from multi-layer substrates
Abstract
Described are microfiber articles and methods and intermediates
for their production, the microfiber articles being preferably
produced from co-extruded multi-layer films, and the articles
having a multi-layer construction that allows selection of the
different layers to have different properties such that the article
can have a desired combination of properties.
Inventors: |
Kody; Robert S.;
(Minneapolis, MN) ; Perez; Mario A.; (Burnsville,
MN) ; Longabach; John W.; (White Bear Lake, MN)
; Klepzig; Kimberley D.; (Saint Paul, MN) ;
Sebastian; John M.; (Maplewood, MN) ; Hobbs; Terry
R.; (Saint Paul, MN) ; Michel; Matthew J.;
(Saint Paul, MN) ; Lindquist; Timothy J.; (Saint
Paul, MN) ; Sura; Ravi K.; (Woodbury, MN) |
Correspondence
Address: |
3M INNOVATIVE PROPERTIES COMPANY
PO BOX 33427
ST. PAUL
MN
55133-3427
US
|
Assignee: |
3M Innovative Properties
Company
|
Family ID: |
34136428 |
Appl. No.: |
11/253930 |
Filed: |
October 19, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10641730 |
Aug 15, 2003 |
|
|
|
11253930 |
Oct 19, 2005 |
|
|
|
09974040 |
Oct 9, 2001 |
6977113 |
|
|
10641730 |
Aug 15, 2003 |
|
|
|
Current U.S.
Class: |
252/500 |
Current CPC
Class: |
B32B 2262/0253 20130101;
H01L 51/0058 20130101; B32B 2307/728 20130101; B01D 39/1623
20130101; B32B 27/12 20130101; B01D 2239/0663 20130101; H01L
51/0508 20130101; B82Y 30/00 20130101; B32B 27/08 20130101; B32B
37/153 20130101; B32B 2307/51 20130101; H01L 51/0068 20130101; B32B
2307/724 20130101; D04H 13/02 20130101; C07D 333/06 20130101; B32B
2307/306 20130101; B32B 2307/73 20130101; H01L 51/0052 20130101;
H01L 51/0054 20130101; B32B 5/02 20130101; B32B 2307/3065 20130101;
B82Y 10/00 20130101; C08G 61/126 20130101 |
Class at
Publication: |
252/500 |
International
Class: |
H01B 1/12 20060101
H01B001/12 |
Claims
1. A multi-layer microfiber article comprising at least one
microfiber layer comprising microfibers having an average effective
diameter of less than 20 microns and a transverse aspect ratio of
from 1.5:1 to 20:1, and a non-microfiber layer comprising a
material selected from the group consisting of a polypropylene, a
polyethylene, a styrene-ethylenelbutylene-styrene block copolymer,
a styrene-isoprene-styrene block copolymer, a polyurethane, a
fluoropolymer, poly(butylene), poly(isoprene), a nylon, and an
adhesive.
2. The article of claim 1 wherein the non-microfiber layer is
elastomeric.
3. The article of claim 1 wherein the non-microfiber layer exhibits
a property selected from the group consisting of: elasticity, high
or low modulus, puncture resistance, breathability, flame
retardancy, temperature resistance, and combinations thereof.
4. The article of claim 1 wherein the microfiber layer comprises
polypropylene.
5. The film of claim 1 comprising a non-microfiber-forming layer
sandwiched between two microfiber-forming layers.
6. The film of claim 1 wherein the non-microfiber layer comprises
an elastomeric polymer.
7. The film of claim 1 wherein the film comprises a non-microfiber
layer comprising a material selected from the group consisting of a
polypropylene, a polyethylene, a styrene-ethylene/butylene-styrene
block copolymer, a styrene-isoprene-styrene block copolymer, a
polyurethane, a fluoropolymer, poly(butylene), poly(isoprene), a
nylon, and an adhesive.
8. The article of claim 1 wherein the article is co-extruded.
9. The article of claim 1 comprising from 2 to 5 layers.
10. The article of claim 1 wherein the microfibers have an average
effective diameter of less than 5 microns.
11. The film of claim 1 wherein the microfibers have an average
cross-sectional area of 0.7.sup.2 to 2.1.mu..sup.2.
12. A method of producing a microfiber article of claim 1 the
method comprising: providing a multi-layer film comprising at least
one microfiber-forming layer, and microfibrillating the
microfiber-forming layer to form microfibers.
13. The method of claim 12 wherein the film is uniaxially-oriented.
Description
[0001] This application is a divisional of U.S. Ser. No. 09/974040,
filed Oct. 9, 2001, now allowed, the disclosure of which is herein
incorporated by reference.
FIELD OF THE INVENTION
[0002] The invention relates to multi-layer films that bear a
microfiber surface, films and methods used to prepare them, and
articles made from them.
BACKGROUND
[0003] Polymeric materials that can be processed to form microfiber
surfaces and microfiber articles have been identified, including
mono-axially oriented films such as polypropylene. See U.S. Pat.
No. 6,110,588. Such polymeric materials can be selected and
processed using various techniques, to produce oriented films
capable of being microfibrillated to a microfiber surface.
[0004] Multi-layer films are generally known, and include a huge
variety of different combinations of layer composition, sizes, and
methods of preparing the different layers into a multi-layer film,
e.g., lamination, co-extrusion, the use of adhesives, etc.
[0005] Until now, there has been little if any recognition of the
potential benefits and synergies that can be achieved using
multi-layer films, particularly co-extruded multi-layer films, to
form microfibers, microfiber surfaces, and microfiber articles.
SUMMARY OF THE INVENTION
[0006] The invention identifies multi-layer films that bear very
fine fibers, e.g., microfibers, and methods of preparing them from
multi-layer film precursors, preferably co-extruded multi-layer
film precursors.
[0007] Advantageously, the different layers of the multi-layer film
can be selected based on the independent properties of the
different layers to produce a multi-layer microfiber article having
a combination of desired properties. For example, different layers
of a multi-layer film can be independently selected to provide one
or more layers that are hydrophobic; hydrophilic; oleophobic;
oleophilic; dielectric; to exhibit certain physical properties such
as rigidity, flexibility, high or low elasticity, high or low
strength, tear or puncture resistance, stain resistance,
breathability, and being waterproof; to give a desired frictional
property such as a high or low coefficient of friction; to provide
a desired color or color combination; to provide a desired size of
fibers, fibrils, or microfibers, or a desired surface area of a
fiber or microfiber surface; to provide high or low temperature
resistance or flame retardance; or a combination thereof.
[0008] As a particular example, one layer can be selected to give a
hydrophilic surface, while another layer has an oleophilic surface.
Using a multi-layer film to produce a microfiber film or
fibrillated article, for example, can allow the production of
various multi-surface articles such as pads, drapes, cloth-like
wipes, microfiber mats, and a large variety of others, which
contain layers of two or more different types of materials. This
could be useful to make a wipe that is both water and oil
absorbing, by starting from a film with layers of polypropylene and
a hydrophilic polymer.
[0009] In a different embodiment, layers can be selected to include
one or more microfiber-forming layers and one or more layers that
are not microfiber-forming layers, preferably to give a combination
of properties from the different layers. The non-microfiber-forming
layer can be selected to give a certain physical or chemical
property such as hydrophobicity, hydrophilicity, etc.; stain or
water resistance; or a mechanical property such as rigidity,
flexibility, tear or puncture resistance, breathability, strength,
and elasticity. As an example, a multi-layer film can have a
non-microfiber-forming inner layer of a plastic, a fluoropolymer, a
hard yet flexible rubber or soft rubber, or an elastomer, and
surface layers of a microfiber-forming polymer such as
polypropylene. The microfiber article may exhibit a combination of
properties including properties of a waterproof elastomer and a
microfiber surface, to give a microfiber article having combined
properties of a flexible or stretchable microfiber-surface-bearing
cloth.
[0010] In certain embodiments, the invention takes advantage of the
understanding that films having multiple different layers with
independently selected properties can be efficiently co-extruded to
form a multi-layer film, which can then be microfibrillated to
produce a microfiber article having a desired combination of
properties based on the composition and properties of the different
layers of the co-extruded film. The preparation of a multi-layer
film by co-extruding can realize processing advantages because
co-extruding different layers into a single film can be more
efficient and economical than other possible (and still useful)
methods of producing a multi-layer film, such as by separate
production of individual layers and lamination or adhesion of those
layers to one another.
[0011] According to preferred embodiments of the invention,
oriented, multi-layer polymeric films can be transformed into
microfiber mats, wipes, or other types of cloth-like materials
using standard methods of microfibrillation, including
hydroentanglement techniques using a hydroentangling machine. One
or more layers of a multi-layer film, and different amounts or
thicknesses of the one or more layers, may be microfibrillated to
form microfibers.
[0012] An aspect of the invention relates to a multi-layer film
comprising microfibers. The preferred films can be oriented to
facilitate formation of microfibers. Preferred films can also
include layers of different materials selected to provide a desired
combination of properties in the film.
[0013] Another aspect of the invention relates to a microfiber
article including one or more microfiber layers and a
non-microfiber layer comprising a material selected from the group
consisting of a polypropylene, a polyethylene, a
styrene-ethylene/butylene-styrene block copolymer, a
styrene-isoprene-styrene block copolymer, a polyurethane, and a
fluoropolymer.
[0014] Another aspect of the invention relates to a co-extruded,
oriented multi-layer film comprising one or more microfiber-forming
layers.
[0015] Another aspect of the invention relates to a two-layer
co-extruded film comprising one or two microfiber-forming
layers.
[0016] Another aspect of the invention relates to a three-layer
co-extruded film comprising two microfiber-forming layers
sandwiching a non-microfiber core layer.
[0017] Another aspect of the invention relates to a multi-layer
microfiber article that includes a first microfiber layer at a
surface of the article, and second microfiber layer adjacent to the
first microfiber-layer. Areas of the article surface are
microfibrillated to form microfibers of only the first layer, and
areas of the surface are microfibrillated through the first layer
to form microfibers of the second layer.
[0018] Another aspect of the invention relates to a method of
producing a microfiber-forming multi-layer film. The method
includes providing an oriented polymeric film, casting a polymeric
film onto the oriented film to produce a multi-layer film, and
orienting the multi-layer film to produce a multi-layer film having
one or more layers that can be microfibrillated to produce
microfibers.
[0019] Another aspect of the invention relates to a method of
producing a microfiber article. The method comprises providing a
multi-layer film comprising at least one microfiber-forming layer,
and microfibrillating the microfiber-forming layer to form
microfibers.
[0020] Still another aspect of the invention relates to a method of
producing a microfibrillated article. The method comprises
co-extruding a multi-layer film having at least two layers,
orienting the film to produce a microfiber-forming layer that can
be microfibrillated to produce microfibers, and microfibrillating
the microfiber-forming layer to form microfibers from the
layer.
[0021] Yet another aspect of the invention relates to a method of
producing a microfibrillated article. The method includes providing
an oriented film, casting a polymeric film onto the oriented film
to produce a multi-layer film, orienting the multi-layer film to
produce a multi-layer film having one or more layers that can be
microfibrillated to produce microfibers, and fibrillating the layer
to form microfibers.
BRIEF DESCRIPTION OF THE DRAWINGS
[0022] FIG. 1 illustrates a cross-section of an embodiment of a
multi-layer film of the invention having two layers.
[0023] FIG. 1a illustrates a cross-section of an embodiment of a
microfiber article of the invention.
[0024] FIG. 1b illustrates a cross-section of an embodiment of a
microfiber article of the invention.
[0025] FIG. 2 illustrates a cross-section of an embodiment of a
multi-layer film of the invention.
[0026] FIG. 2a illustrates a cross-section of an embodiment of a
microfiber article of the invention having a non-microfiber surface
and a microfiber surface.
[0027] FIG. 3 illustrates a cross-section of an embodiment of a
multi-layer film of the invention 15 having a core layer and two
surface layers.
[0028] FIG. 3a illustrates a cross-section of an embodiment of a
microfiber article of the invention having a non-microfiber-forming
core layer and two microfiber surfaces.
[0029] All drawings are not drawn to scale.
DETAILED DESCRIPTION
[0030] The invention relates to multi-layer films that include at
least one layer that can be microfibrillated to form microfibers on
a microfiber surface, i.e., a "microfiber-forming layer." The
multi-layer film will also include one or more additional layers,
any of which can be a microfiber-forming layer or a
non-microfiber-forming layer, or another fiber-forming layer, etc.
The terms "non-microfiber layer" and "non-microfiber-forming layer"
refer to a layer that is not capable of being microfibrillated to
produce microfibers, and that does not contain microfibers. The
term "microfiber layer" refers to a layer that comprises
microfibers, e.g., due to the layer being a microfibrillated
microfiber-forming layer. The multi-layer films can be processed by
microfibrillating at least one microfiber-forming layer to produce
a "microfiber article," which as used herein is a multi-layer
article having at least one microfiber layer. (Generally herein,
the terms "microfiber-forming layer" and "microfiber layer" refer
to the same layer of a multi-layer film, the only difference being
that the microfiber layer is a microfiber-forming layer that has
been microfibrillated. Thus, other than this difference, those two
terms can normally be interchangeable.)
[0031] The use of multi-layer films to prepare microfiber articles
allows preparation of microfiber articles that exhibit a
combination of two or more desired properties (e.g., chemical,
mechanical, physical, or aesthetic properties, etc.) in a single
article, based on the properties of the chosen layers. Almost any
variety of different chemical, mechanical, physical, or aesthetic
properties can be independently provided in a multi-layer film,
depending on the choice of materials for the different layers.
Examples of different properties include: attractive or repulsive
properties with respect to different chemical materials such water
and oil, e.g., by using materials or layers that are hydrophobic,
hydrophilic, oleophobic, oleophilic, etc., including the properties
of being "water-resistant" or "water-proof"; electrically
conductive or insulative properties such as a dielectric layer or
an electrically conductive layer, or a layer that can retain an
electric or electrostatic charge; breathability; inertness or stain
resistance such as by inclusion of a fluoropolymer layer; desired
mechanical properties such as a frictional property (high or low
coefficient of friction, especially a low coefficient of friction
for wiping), high or low elasticity, high or low modulus, high or
low strength, tear resistance, puncture resistance; high or low
temperature resistance; flame retardance; desired aesthetic
properties such as color; a property of enabling a particular size
of fiber, fibril, or microfiber, or a desired surface area of a
fiber, fibril, or microfiber surface; electrostatic properties such
as the ability to hold an electrostatic charge and attract dust or
other relatively small particles; anti-microbial properties; or a
combination thereof. These separate properties can be associated
with one or more different layers of a multi-layer film to provide
a desired combination of properties based on the combined
properties of the different layers.
[0032] The term "multi-layer film" refers to films that include at
least two layers, with (according to the invention) one or more
layers being a microfiber-forming layer, and optionally one or more
non-microfiber layers. Different properties, such as those
discussed elsewhere within the present description, can be
associated with either a microfiber-forming layer or a
non-microfiber-forming layer. More specifically, "multi-layer"
refers to films that include two or more layers of materials that
may be the same, different, or similar, and which, according to the
invention, may be used to prepare a microfiber article, for example
a microfiber article including two or more layers of materials, at
least one of which is a microfiber layer, and which different
layers preferably independently provide useful or desirable
properties to the microfiber article.
[0033] In general, the thickness of layers of a multi-layer film
can be any useful thickness based on factors such as the
composition of a layer and its desired function within a microfiber
article. The total thickness of a multi-layer film useful according
to the invention may also be based on factors such as the
composition of the intended microfiber article, the composition of
layers of the microfiber article, and the intended utility of the
microfiber article. The term "multi-layer" films does not include
films referred to as "microlayer films," as described in Assignee's
copending U.S. patent application Ser. No. 09/858,253, entitled
"Fibrous Films and Articles from Microlayer Substrates," filed May
15, 2001 and incorporated herein by reference. Multi-layer films
may, however, include such microlayer films as one or more layers
within a multi-layer film.
[0034] The thickness of a layer of multi-layer film can be chosen
based on overall product construction, which can relate to the
total number of layers of a film and their purposes, as well as the
composition and function of a layer. For example, a non-microfiber
layer such as an elastomeric layer may be of a thickness that gives
a desired mechanical property such as elasticity. The thickness
required for a desired elasticity will depend on the material used
for that layer of film. In an oriented film construction, prior to
fibrillation, useful non-microfiber layers generally can each be,
e.g., of a thickness in the range from about 13 to about 10,160
micrometers, preferably from about 50 to about 2,540 micrometers.
Certain useful elastomeric layers may each, for example, be in the
range from about 25 to about 1,200 micrometers, preferably from
about 50 to about 250 micrometers in thickness.
[0035] The microfiber-forming layers can be of a thickness to allow
microfibrillation. Also, thickness of a microfiber-forming layer
may be selected based on the degree of microfibrillation intended
to occur in that layer, and whether that layer is adjacent to
another microfiber-forming layer, which, perhaps, is intended to be
microfibrillated through the first microfiber-forming layer. In
some embodiments of the invention, a microfiber-forming layer may
be of a thickness to allow microfibrillation fully through the
microfiber-forming layer, e.g., to expose an adjacent layer of the
film which may be a microfiber-forming layer that may also be
fibrillated, or to expose a non-microfiber layer. The thickness of
any particular microfiber-forming layer may also be influenced by
the overall product construction and composition of the multi-layer
film and its different layers. Typically, the thickness of a
microfiber-forming layer of an oriented multi-layer film may be in
the range from about 5 to about 2,540 micrometers, with thicknesses
in the range from about 10 to about 508 micrometers sometimes being
preferred.
[0036] Overall, multi-layer films useful according to the invention
can have a number of layers each of a useful size (thickness) and
composition to allow for the production of a useful microfiber
article. Multi-layer films may include, for example, 2, 3, 4 to 8
to 10 layers, with the lower range, e.g., below 5 layers, being
typical. The total thickness of a multi-layer film prior to
fibrillation can be any thickness that will be useful in preparing
a microfiber article as described herein, with exemplary
thicknesses being in the range from about 25 to about 10,160
micrometers, e.g., in the range from about 50 to about 254
micrometers.
[0037] The composition of different layers of a multi-layer film
can be chosen to provide different properties to a multi-layer film
and a microfiber article prepared from the film. The composition of
a layer may be any desired material, and often includes a polymeric
material, sometimes a polymeric material that can be extruded as a
single layer of material or that can be co-extruded as a layer of a
co-extruded multi-layer film, and can also, according to the
invention, be chosen either as a material that can produce
microfibers or one that cannot produce microfibers but that can
preferably provide a microfiber article with a different desired
property.
[0038] Typical or preferred properties of different layers of a
multi-layer film used according to the invention are described
generally above. Of these different properties, any can be
associated with either of a microfiber-forming layer, a microfiber
layer, or a non-microfiber layer. Examples of certain properties
that can be associated with a microfiber-forming layer or a
microfiber layer include properties of attracting or repelling
water or oil; electrostatic or insulative properties; aesthetic
properties such as colors; and properties of being capable of
forming a particular size of microfiber or microfiber surface area.
Examples of certain properties that can be associated with a
non-microfiber layer can include electrically conductive or
insulative properties; inertness or chemical resistance; mechanical
properties such as strength, modulus, elasticity, or puncture or
tear resistance; the ability to form fibrils or flakes that are not
of the small size of microfibers; and aesthetic properties. Of
course, these descriptions of exemplary properties of different
types of film layers do not exclude any property from being
associated with any type of layer of a multi-layer film, and the
invention generally allows for any of these or other desired or
useful properties to be associated with any layer of a multi-layer
film.
[0039] Useful materials for a non-microfiber layer can include any
material that can be used to produce a non-microfiber layer of a
useful microfiber article. A non-microfiber layer can be included
to provide a desired property, as described. As an example, a
non-microfiber layer can provide mechanical support for a
microfiber layer in a microfiber article. For example, a polymeric
material such as high modulus poly(ethylene terephthalate) (PET)
may function as a relatively stiff, high-strength support layer for
a microfiber-forming layer.
[0040] Other non-microfiber layers can be prepared from materials
chosen to provide a support property, but also to provide a
property that is more than just the structural support of a
microfiber layer, and therefore, many preferred materials for
non-microfiber layers can be different from high modulus PET. For
example, in addition to pure support, a non-microfiber layer can
preferably, in some embodiments, have desired properties of
puncture or tear resistance; elasticity; stain resistance;
attraction or repulsion to water or oil; breathability; etc.
[0041] The term "elastomeric" refers to materials that are
well-known in the film and polymeric material arts to exhibit
elastomeric properties, for example that can be stretched easily to
high extensions, e.g., 3 to 10 times their original dimensions, and
rapidly recover their original dimensions when the applied stress
is released. Exemplary materials considered to be elastomeric
include butyl rubber, poly(isoprene), polyurethanes, and
elastomeric polyolefins such as certain polypropylenes and
polyethylenes. One specific useful elastomer includes the type of
copolymers known generally as styrenic thermoplastic elastomeric
block copolymers. Examples of specific block copolymers within this
class include polystyrene-polyisoprene-polystyrene,
polystyrene-polybutadiene-polystyrene, and polystyrene-poly
(ethylene-butylene)-polystyrene based triblock copolymers. Such
copolymers are commercially available from a variety of sources,
for example under the brand-name Kraton.TM., from Shell, and from
DEXCO, under the brand-name Vector.TM..
[0042] "High elastic modulus" materials include materials that are
either glassy or at least partially crystalline. Examples of such
materials can include, but are not limited to, nylons,
fluoropolymers, polyesters, polystyrene, polycarbonate,
polypropylene and polyethylene, particularly when highly oriented
and crystalline.
[0043] A layer can be water resistant or waterproof, meaning in
general that liquid water does not diffuse through the film layer.
Water-resistant and water-proof materials include almost all
non-porous, non-water-soluble polymers, but particularly include
polypropylene, polyethylene, polystyrene, poly(ethylene
terephthalate), fluoropolymers, polyurethane, tri-block copolymers
with polystyrene end blocks and a rubbery poly(ethylene-butylene)
or poly(isoprene) mid block, butyl rubber, and poly(isoprene).
[0044] A layer can be puncture resistant or tear resistant. The
term "puncture resistant" refers to materials that require a
significant amount of energy to puncture with a pointed or sharp
object. Examples of materials considered to be puncture resistant
include materials having a high friction or adhesive surface, such
as tri-block copolymers with polystyrene end blocks and a rubbery
poly(ethylene-butylene) mid block, butyl rubber, and polyethylene
elastomers. The term "tear resistant" refers to materials that
require a significant amount of energy to initiate and propagate a
tear or crack. Examples of materials considered to be tear
resistant include thermoplastics, especially modified
thermoplastics and thermosets. Such materials include
polypropylene, polyethylene, impact modified polystyrene, rubber
modified epoxies, and elastomers, such poly(butylenes),
poly(isoprene), and tri-block copolymers with polystyrene end
blocks and a rubbery poly(ethylene-butylene) or poly(isoprene) mid
block.
[0045] A layer can be associated with the property of
breathability. The term "breathability" or "breathable" refers to
materials that allow gasses, specifically water vapor, to pass
though them, especially where liquids such as liquid water cannot.
Examples of materials considered to be breathable include
polyurethanes, and porous polymer films. Examples of porous polymer
films include polypropylene, polyethylene, and fluoropolymers that
have been blended with particulate fillers or solvent fillers and
then oriented in a manner to create voids or pores in the film.
[0046] A layer can be associated with a property of high or low
temperature resistance. This property refers to the ability to
withstand extreme temperatures, for example in excess of
150.degree. C. or below -23.degree. C. Examples of materials
considered to be high temperature resistant include materials such
as fluoropolymers, nylons, and polyolefins such as highly
crystalline polyester or propylene. Examples of materials
considered to be low temperature resistant include materials such
as polyethylenes, silicone rubbers, and highly crystalline
polypropylenes that do not exhibit a significant glass
transition.
[0047] A layer can be associated with a property of being flame
retardant. Examples of materials considered to be flame retardant
include materials such as halogenated polymers, such as poly(vinyl
chloride), and also a variety of polymers containing flame
retardant additives. Examples of flame retardant blends include
polypropylene and polyethylene that contain: inorganic additives
such as aluminum trihydrate, antimony trioxide, magnesium
hydroxide, aluminum hydroxide; phosphorus compounds such as
ammonium polyphosphate, polyphazenes, and aluminum phosphates;
nitrogen additives such as melamine cyanurate and melamine
phosphate; silicone polymer additives; halogenated additives like
chlorinated compounds, brominated compounds, fluorinated compounds
such as potassium perfluorobutanesulfonate; and other additives
such as nano-clay particles, expandable graphite, silica gel, and
potassium carbonate.
[0048] The multi-layer films according to the invention include at
least one microfiber-forming layer. Microfiber-forming materials,
e.g., microfiber layers, microfiber-forming films, or
microfiber-forming film layers, useful according to the invention
can include any materials that can be processed to form
microfibers. Several classes of such materials exist and are known
in the film and polymer arts. Examples of some of these materials,
their methods of preparation, and methods of processing these
materials to microfiber materials, are described in U.S. Pat. No.
6,110,588; Assignee's copending U.S. patent application Ser. No.
09/307,577, filed May 7, 1999, entitled "Films Having a Fibrillated
Surface and Method of Making"; U.S. patent application Ser. No.
09/602,978, filed Jun. 23, 2000, entitled "Fibrillated Article and
Method of Making"; and U.S. patent application Ser. No. 09/746,355,
filed Dec. 12, 2000, entitled "Microfibers, Microfibrillated
Articles and Use Thereof," the entirety of each of these
disclosures being incorporated herein by reference.
[0049] Useful materials for a microfiber-forming layer can include
any material that can be used to produce a microfiber-forming layer
or microfiber layer of a microfiber article. Different properties
can be associated with a microfiber layer. A microfiber-forming
layer or microfiber layer can provide a microfiber surface having
particular properties based on the size and composition of the
microfibers. Additionally, a microfiber-forming layer or microfiber
layer can provide properties that are independent of the presence
or dimensions of the microfibers themselves, but relate to a
property of the material that makes up the film or microfiber, for
example properties that are mechanical, chemical, or aesthetic in
nature, or otherwise are not based on the presence or dimensions of
microfibers.
[0050] In addition to providing a microfiber surface, a
microfiber-forming layer or microfiber layer can in some
embodiments have desired mechanical properties such as high or low
modulus; puncture and tear resistance; elasticity; stain
resistance; attraction or repulsion to water or oil; breathability;
etc., e.g., as discussed above.
[0051] A microfiber layer can exhibit attractive or repulsive
forces with respect to certain chemical materials such as water or
oil. Materials that exhibit such properties are often referred to
as hydrophobic, hydrophilic, oleophobic, oleophilic, etc. These
properties are well-known in the film and polymeric material arts.
Exemplary materials considered to be hydrophobic, hydrophilic,
oleophobic, oleophilic, etc., include the following, as well as
others. Exemplary hydrophobic materials can include any one or more
of a fluoropolymer or polyolefin such as polyethylene,
polypropylene, or blends thereof, optionally containing other
materials such as fillers or other hydrophobic polymers, such as
fluoropolymers or thermoplastics.
[0052] Microfiber-forming layers and microfiber layers can also be:
water resistant or waterproof, associated with a property of
breathability, associated with a property of high or low
temperature resistance, or associated with a property of flame
retardance.
[0053] Of course, as will be understood by one of skill in the arts
relating to polymeric materials and multi-layer materials, the
multi-layer film can include other components such as layers that
form fibers or fibrils that are not "microfibers"; or layers that
serve the purpose of a tie-layer, to adhere two other layers
together.
[0054] A layer of a multi-layer film may also have a coating or
adhesive placed on a surface of the film, e.g., may include
materials such as adhesives, primers, or protective coatings, etc.,
as desired. These "coatings" are not considered to be "layers" of a
"multi-layer" film.
[0055] In accordance with the above description of properties
related to a multi-layer film and layers thereof, multi-layer films
that contain one or more microfiber-forming layers can be prepared
from materials known in the polymeric material arts and other known
methods.
[0056] In general, a "microfiber-forming material" is any material,
especially a film or a layer of a multi-layer film, which is
capable of being processed to form microfibers. Microfiber-forming
materials are typically made of polymeric materials that can have a
structure or morphology that includes features, which upon
mechanical contact, will cause a microfiber to be formed from the
polymeric film. Properties of a film that facilitate formation of
microfibers, e.g., breaking or splitting of the film to form
microfibers, can include structural features such as microvoids,
spherulites, or other additives or disturbances in the polymer,
e.g., calcium carbonate; orientation of the film, e.g., bi-axially,
but especially mono-axially (uni-axial orientation); multiple
layers, especially where an interface at surfaces of different
layers weakens the internal structure of a multi-layer film; and
morphology, such as crystallinity. These features can be present
alone in a film to allow microfibrillation. Alternatively, two or
more of the different features can be present in combination. When
combinations of different properties are present, the amount or
severity of one or both properties may be reduced relative to the
amount or severity of that property that would be necessary to
allow microfibrillation if only that single property were
present.
[0057] Properties that may facilitate microfibrillation can be
created in a film during manufacturing of the film to cause the
film to be a microfiber-forming film. In general, the described
properties and combinations of the properties can be produced in a
polymeric film by selecting one or more of the composition of the
film, processing conditions, e.g., processing conditions during
extrusion or co-extrusion of a film or multi-layer film, and
processing conditions after extrusion or co-extrusion, possibly
including individual steps or combinations of steps such as
casting, quenching, annealing, calendering, orienting, solid-state
drawing, roll-trusion, and the like.
[0058] Polymeric films typically comprise long molecular chains
having a backbone of carbon atoms. The facility with which the
surface of a polymer film can be microfibrillated is often not
realized due to random orientation and entanglement of the polymer
chains. As one method of facilitating microfibrillation, polymer
chains can be oriented to be relatively more parallel to one
another and partially disentangled. The degree of molecular
orientation is generally defined as the draw ratio, which is the
ratio of the final length to the original length. This orientation
may be effected by a combination of techniques, including the steps
of calendering and length orienting.
[0059] Microfibrillation of certain polymeric layers can be
facilitated by orientation, especially with some films, uni-axial
orientation. Uni-axial orientation means that the film is
lengthened or stretched in one direction relatively more than it is
stretched in another, e.g., perpendicular, direction. By exemplary
methods, a film can be stretched in a machine direction while its
width is not held, and the film gets longer in length, thinner, and
narrower in width. In another exemplary method, the width may be
held constant while the length is stretched. In other words,
sufficient orientation may be achieved for microfibrillation by
inducing a relatively greater amount of orientation in one
direction, the machine direction, compared to a lesser degree of
orientation in another direction, especially a perpendicular
direction, such as the cross direction.
[0060] Bi-axial orientation of a film can also be used to provide
microfibers. For example, a film can be oriented, e.g., stretched
or lengthened, in two directions, with stretching or lengthening in
one direction being sufficient to produce microfibers. (If not
sufficiently oriented, a bi-axially oriented film may alternatively
be fibrillated to produce flakes or other fibrils that are not
microfibers.) Preferably, to produce microfibers, a bi-axially
oriented film can be oriented to a draw ratio of at least 4:1 or
5:1, in one direction.
[0061] Crystallinity also affects the ability of a film to form
microfibers. A variety of semi-crystalline, crystalline, and
highly-crystalline materials can be processed to form microfibers.
Examples of polymeric materials for forming microfiber-forming
films can include semicrystalline melt processed films having a
maximized crystallinity induced in the polymeric film layer by an
optimal combination of casting and subsequent processing such as
calendering, annealing, stretching and recrystallizing. For
polypropylene, as an example, preferred crystallinity can be above
60%, preferably above 70%, most preferably above 75%. The
crystallinity may be measured by differential scanning calorimetry
(DSC) and comparison with extrapolated values for 100% crystalline
polymers. See, e.g., B. Wunderlich, Thermal Analysis, Academic
Press, Boston, Mass., 1990.
[0062] Microfiber-forming materials and films also may contain
spherulites and microvoids to facilitate microfibrillation. See,
e.g., U.S. Pat. No. 6,110,588.
[0063] Any suitable combination of polymer film composition and
processing steps and conditions may be used to impart sufficient
microscopic structure, e.g., crystallinity, microvoids,
spherulites, multiple layers, orientation, etc., to produce a layer
of a multi-layer film that will form microfibers upon
microfibrillation. These conditions may include combinations of
casting, quenching, annealing, calendering, orienting, solid-state
drawing, roll-trusion, and the like.
[0064] Some specific examples of materials that can be used to
prepare a microfiber-forming film layer are discussed, e.g., in
U.S. Pat. No. 6,110,588. Exemplary semicrystalline polymers include
high and low density polyethylene, polypropylene, polyoxymethylene,
poly(vinylidine fluoride), poly(methyl pentene),
poly(ethylene-chlorotrifluoroethylene), poly(vinyl fluoride),
poly(ethylene oxide), poly(ethylene terephthalate), poly(butylene
terephthalate), poly(lactic acid), nylon 6, nylon 66, polybutene,
and thermotropic liquid crystal polymers. Examples of suitable
thermotropic liquid crystal polymers include aromatic polyesters
that exhibit liquid crystal properties when melted and that can be
synthesized from aromatic diols, aromatic carboxylic acids,
hydroxycarboxylic acids, and other similar monomers. Typical
examples include a first type consisting of parahydroxybenzoic acid
(PHB), terephthalic acid, and biphenol; a second type consisting of
PHB and 2,6-hydroxynaphthoic acid; and a third type consisting of
PHB, terephthalic acid, and ethylene glycol. Preferred polymers
include polyolefins such as polypropylene and polyethylene which
are readily available at low cost and can provide highly desirable
properties in microfibrillated articles such as high modulus and
high tensile strength.
[0065] Preferred semicrystalline polymers can include high density
polyethylene, low density polyethylene, polypropylene,
polyoxymethylene, poly(vinylidine fluoride), poly(methyl pentene),
poly(ethylene-chlorotrifluoroethylene), poly(vinyl fluoride),
poly(ethylene oxide), poly(ethylene terephthalate), poly(ethylene
naphthalate), poly(butylene terephthalate), poly(lactic acid),
nylon 612, nylon 6, nylon 66, polybutene, a thermotropic liquid
crystal polymer, a blend of one or more of these polymers with
another of these or another polymer, or a copolymer made from any
of the listed monomers, and any other listed monomer or a different
monomer.
[0066] The molecular weight of the polymer can be chosen so that
the polymer is melt processable (i.e., extrudable or co-extrudable)
under the processing conditions used in extrusion and co-extrusion.
For polypropylene and polyethylene, for example, the molecular
weight may be from about 5,000 to 499,000 and is preferably from
about 100,000 to 300,000.
[0067] Referring again to the '588 patent, it describes that any
suitable combination of processing conditions may be used to impart
crystallinity and orientation to a melt-processed film. Starting
with a melt-processed, cast film, for example, the film may be
calendered, stretched, oriented, cast, quenched, annealed, drawn,
roll-truded, etc. Such processing generally serves to increase the
degree of crystallinity of the polymer film as well as the size and
number of spherulites.
[0068] The '588 patent describes additional details and recites
examples of preferred embodiments of materials and techniques, and
optional processing steps, that may be used to prepare useful
microfiber-forming films. That description, along with the balance
of the present disclosure and knowledge available to a skilled
artisan will enable the preparation of multi-layer films as well as
microfiber articles derived from the multi-layer films, as
described herein.
[0069] Another class of microfiber-forming materials that can be
included as a microfiber-forming layer of a multi-layer film as
described herein, includes microfiber-forming materials described
in Assignee's copending patent application U.S. Ser. No.
09/602,978, "Fibrillated Article and Method of Making," filed on
Jun. 23, 2000, the entirety of which is incorporated herein by
reference. This patent application describes high melt strength
polypropylene foams prepared by extruding a foamable mixture
comprising a high melt-strength polypropylene and a blowing agent,
and orienting in at least one direction.
[0070] The high melt strength polypropylene includes homo- and
copolymers containing 50 weight percent or more propylene monomer
units, preferably at least 70 weight percent, and has a melt
strength in the range of 25 to 60 cN at 190.degree. C. Melt
strength may be measured using an extensional rheometer by
extruding the polymer through a 2.1 mm diameter capillary having a
length of 41.9 mm at 190.degree. C. and at a rate of 0.030 cc/sec;
the strand is stretched at a constant rate while measuring the
force. Preferably the melt strength of the polypropylene is in the
range of 30 to 55 cN, as described in WO 99/61520, the entirety of
that disclosure being incorporated by reference.
[0071] The foamable polypropylene may consist of propylene
homopolymers or may comprise a copolymer having 50 weight percent
or more propylene monomer content. Further, the foamable
polypropylene may comprise a mixture or blend of propylene
homopolymers or copolymers with a homo- or copolymer other than
propylene homo- or copolymers.
[0072] A variety of blowing agents may be used, including physical
blowing agents and chemical blowing agents. The amount of blowing
agent incorporated into a foamable polymer mixture can be chosen to
yield a foam having a void content in excess of 10%, and even in
excess of 20%, as measured by density reduction; i.e., 1-(the ratio
of the density of the foam to that of the neat polymer).times.100.
Generally, these greater foam void contents can enhance
microfibrillation and can I 0 produce a greater yield of a
microfibrillated surface.
[0073] To facilitate microfiber-formation from a multi-layer film
as described, the film (i.e., its polymer chains) may be oriented
along at least one major axis. Suitable stretching conditions can
be used to increase the crystallinity of the polymer and the void
volume of the foam.
[0074] Other components, e.g., non-polymeric materials, may be
mixed into a polymeric material of a multi-layer film to facilitate
microfiber formation, such as void-initiating components, calcium
carbonate, or others, e.g., as described in Assignee's copending
patent application U.S. Ser. No. 09/307,577, "Films Having
Fibrillated Surface and Method of Making," filed on May 7, 1999,
the entire disclosure of which is incorporated herein by
reference.
[0075] Methods for producing multi-layer films are well known in
the arts of polymeric materials and film processing, and materials
such as those described herein can be used with those methods to
produce multi-layer films that contain at least one
microfiber-forming layer, from those materials. Examples of useful
techniques include casting, extrusion, co-extrusion, lamination,
and other known methods of producing films that are well known and
understood in the polymer film arts. Useful equipment for producing
the films will also be apparent to those of ordinary skill and will
include extruders, multi-cavity dies, multilayer feedblocks,
laminators, as well as various other types of equipment known in
the arts of films and film processing, some of them being mentioned
herein. Also well known in the art of polymeric films are
subsequent processing techniques for films such as casting,
quenching, annealing, calendering, orienting, solid-state drawing,
roll-trusion and the like. Using these techniques, suitable
equipment, and the present disclosure, a skilled artisan will be
able to prepare multi-layer microfiber-forming films and microfiber
articles according to the invention.
[0076] The different steps of extrusion, casting, orienting,
calendering, etc., can be done in any order that is useful for
preparing a film as described herein. More than one of any step
(e.g., two lengthening steps) may be used.
[0077] One example of a method of producing a multi-layer film of
the invention is to co-extrude a multi-layer (e.g., 2 or 3 layer)
film, then orient by calendering and/or lengthening, to produce at
least one microfiber-forming layer.
[0078] Another exemplary method is to first extrude and orient a
single layer of film. Onto that oriented film, one or more
additional film layers can be cast. The multi-layer film can then
be oriented to produce a multi-layer film having at least one
microfiber-forming layer. As one specific example, a first layer
can be extruded and oriented in a first direction. A second layer
can then be cast onto the oriented film. The two-layer film can be
oriented again in a second direction, e.g., perpendicular to the
first orientation, to produce a two-layer film comprising one layer
that is uni-axially oriented and one layer that is bi-axially
oriented. At least one of the layers can be microfibrillated to
produce microfibers. Calendering and other steps can optionally be
included where appropriate or desired.
[0079] Still other combinations of these processing steps can be
used in any variety to prepare multi-layer films as described
herein.
[0080] Once a multi-layer film is prepared, a multi-layer film can
be microfibrillated to produce a microfiber surface by any of a
variety of methods known to be useful for microfibrillating.
[0081] The term "microfibrillation," as used herein, refers to
methods of imparting energy to liberate microfibers from a
polymeric film. Such methods are known in the art of processing
polymeric materials, and include methods of imparting a gaseous
fluid using, for example, ultrasound techniques, and methods of
imparting liquid fluids such as water, for example using
high-pressure water jets. Optionally, prior to microfibrillation, a
film may be subjected to a conventional, mechanical, fibrillation
step to produce macroscopic fibers from the multi-layer film, such
as by the use of a rotating drum or roller having cutting elements
such as needles or teeth in contact with the moving film, or by
twisting, brushing (as with a porcupine roller), rubbing, for
example with leather pads, and flexing.
[0082] A microfibrillated surface is a surface that includes
microfibers from one or more layers of a multi-layer film. The
microfibers are portions of one or more multi-layer film layer or
layers that have been mechanically separated or fragmented from the
continuous film, and are therefore typically relatively flat, thin,
or elongate, e.g., "ribbon-shaped," with a typically rectangular
cross section. The microfibers preferably remain attached to the
film at one end, but may also become completely detached from the
base film.
[0083] Microfibers typically have a rectangular cross section with
a cross sectional aspect ratio (transverse width to thickness)
ranging from about 1.5:1 to about 20:1, preferably from 3:1 to 9:1.
Preferred microfibers can also have one or more of the following
features or dimensions: an average effective diameter of from 0.01
to 10 microns, preferably of less than 5 microns; an average
cross-sectional area of 0.5.mu..sup.2to 3.0.mu..sup.2, preferably
from about 0.7.sup.2 to 2.1.mu..sup.2 Further, the sides of the
rectangular shaped microfibers are not normally smooth, but may
have a scalloped appearance in cross section. Certain preferred
microfiber surfaces may exhibit a relatively high surface area, up
to or exceeding 0.25 square meters per gram, as measured using an
Quantachrome AUTOSORB 1-KR gas sorption instrument (available from
Quantachrome Corp., Boyhton Beach, Fla.) with krypton
adsorbate.
[0084] One method of microfibrillating a film surface is with fluid
jets. In this process, one or more jets of a fine fluid stream
impact the surface of a multi-layer film which may be supported by
a screen or moving belt, thereby releasing microfibers from a
film's polymer matrix. The degree of microfibrillation is dependent
on the exposure time of the film to the fluid jet, the pressure of
the fluid jet, the cross-sectional area of the fluid jet, the fluid
contact angle, the polymer properties and, to a lesser extent, the
fluid temperature.
[0085] Any type of liquid or gaseous fluid may be used. Liquid
fluids may include water or organic solvents such as ethanol or
methanol. Suitable gases such as nitrogen, air, or carbon dioxide
may be used, as well as mixtures of liquids and gases. Any such
fluid is preferably non-swelling (i.e., is not absorbed by the
film), which would reduce the orientation and degree of
crystallinity of the microfibers. The fluid can preferably be
water.
[0086] The fluid temperature may be elevated, although suitable
results may be obtained using ambient temperature fluids. The
pressure of the fluid should be sufficient to impart some degree of
microfibrillation to at least a portion of the film, and suitable
conditions can vary widely depending on the fluid, the nature of
the polymeric material, including the composition and morphology,
configuration of the fluid jet, angle of impact and temperature.
Typically, the fluid can be water at room temperature and at
pressures of at least 3400 kPa (500 psi), although lower pressure
and longer exposure times may be used. Such fluid will generally
impart a minimum of 5 watts/cm.sup.2 or 10 W/cm.sup.2 based on
calculations assuming incompressibility of the fluid, a smooth
surface, and no losses due to friction.
[0087] The jets may be configured such that all or part of the film
surface is microfibrillated. Alternatively, the jets may be
configured so that only selected areas of the film are
microfibrillated. Certain areas of the film may be masked, using
conventional masking agents, screens or films, to leave selected
areas free from microfibrillation. Likewise, microfibrillation may
be conducted so that the microfibrillated surface penetrates only
partially, or fully through the thickness of a microfiber-forming
layer of a multi-layer, or fully or partially through one or more
adjacent microfiber-forming layers. When combined with masking
different areas of a microfiber-forming film, penetrating different
thicknesses of a multi-layer film can advantageously produce a
microfiber article having different microfibers on different areas
of a surface. If it is desired that the microfibrillation extend
through the entire thickness of the multi-layer film, conditions
may be selected so that the integrity of the article is maintained
and the film is not severed into individual yarns or fibers, for
example by microfibrillating the multi-layer film only in selected
regions.
[0088] A hydroentangling machine, for example, can be used to
microfibrillate a surface by exposing the film to its fluid jets.
Alternatively, a pressure waterjet, with a swirling or oscillating
head, may be used, which allows manual control of the impingement
of the fluid jet. Such machines are commercially available.
[0089] Microfibrillation may be accomplished by other methods as
well, as will be understood by the skilled artisan, e.g., by
immersing a microfiber-forming material in a high energy cavitating
medium, e.g., and achieving cavitation by applying ultrasonic waves
to the fluid.
[0090] The multi-layer film, upon microfibrillation to produce at
least one microfiber surface, becomes a multi-layer microfiber
article. One example of a microfiber article of the invention is a
microfiber article containing two layers that are both microfiber
layers. Another example is a microfiber article that contains two
layers, where one layer is a microfiber layer and one is a
non-microfiber layer.
[0091] Microfiber articles of the invention may also contain three
or more layers. In a three-layer microfiber article, one or more
layer may be a microfiber layer at a surface of the article. A
non-microfiber fiber layer may be included as a support layer
and/or to exhibit a property other than support of a microfiber
layer. A second microfiber layer may be present on the second
surface of a microfiber article such that one or more
non-microfiber layer is sandwiched between microfiber layers
present at both surfaces of the microfiber article.
[0092] According to any of these or other embodiments of
multi-layer microfiber articles, different materials used for
different layers of a multi-layer film may be chosen to provide any
desired combination of properties. Examples of desired combinations
of materials used in different layers of a multi-layer film or
microfiber article of the invention may include a hydrophilic
surface layer opposite of an oleophilic surface layer; an
elastomeric, soft-rubbery, or flexible non-microfiber (e.g., inner
layer) and one or two microfiber-forming surface layers that are
any of hydrophobic, hydrophilic, oleophobic, oleophilic; one
surface with microfibers for picking up dust and an opposite
surface with larger flakes, fibers, or fibrils, for picking up
larger particles, etc. A non-microfiber layer may still be capable
of being fibrillated to form fibrils that are not microfibers. Such
a layer could be used in combination with microfiber-forming layers
or non-microfiber-forming layers to produce various product
constructions such as a cloth with a microfiber surface on one
side, e.g., for picking up dust, and a (non-microfiber) fibrous
surface on the other side, e.g., for picking up other larger
particles such as sand or sawdust; or, larger fibrils could be used
to scrub and small microfibers could be used to polish.
[0093] Other examples of microfiber articles include cloths or
cloth-like materials, e.g., for cleaning; tape backings; filter
materials; fibrous mats; thermal and acoustical insulation; wipes;
adhesive bandages; as well as others. Also, the multi-layer films,
as well as microfiber articles made from the films, can be
processed with other materials, including other microfiber-forming
materials and other materials that are not microfiber-forming
materials. See, e.g., Assignee's copending U.S. patent application
Ser. No. 09/858273, entitled "Microfiber-Entangled Products and
Related Methods," filed May 15, 2001, and incorporated herein by
reference.
[0094] One embodiment of a microfiber article of the invention is a
two-layer microfiber article, wherein one layer is a microfiber
layer and the other layer is either a microfiber layer or a
non-microfiber layer.
[0095] FIG. 1 shows two-layer co-extruded film 6 having layers 2
and 4, where each layer can be chosen to provide a property such
that a microfiber article prepared from the film exhibits a desired
combination of properties. Layer 2 is a microfiber-forming layer.
Layer 4 can be a microfiber-forming layer or a
non-microfiber-forming layer. In either case, layer 4 can be
selected to provide a desired property in combination with
properties of microfiber-forming layer 2. If layer 4 is chosen to
be a microfiber-forming layer, it can be chosen to provide a
property that is the same as or different from properties of
microfiber-forming layer 2. If layer 4 is a non-microfiber layer,
it can be chosen to provide a property that is or is not merely for
support of microfiber-forming layer 2, e.g., non-microfiber layer 4
can be chosen to exhibit one or more desired properties in addition
to performing the function of a support layer. For example, such a
layer can be an elastomeric material or can exhibit any one or more
of the properties of a non-microfiber layer discussed elsewhere in
this description.
[0096] Exemplary combinations of materials of a two-layer film
wherein both layers are microfiber layers include the following: a
hydrophobic layer and a hydrophobic layer; a hydrophilic layer and
an oleophilic layer.
[0097] In a specific embodiment of FIG. 1, a microfiber article can
include exactly two layers, one of which comprises a microfiber
surface and one of which is a non-microfiber layer. A
non-microfiber layer may be a soft rubbery material, e.g., an
elastomeric material. Exemplary materials for an elastomeric
non-microfiber layer include butyl rubber, poly(isoprene),
polyurethanes, and elastomeric polyolefins such as certain
polypropylenes and polyethylenes. One specific useful elastomer
includes the type of copolymers known generally as styrenic
thermoplastic elastomeric block copolymers. Examples of specific
block copolymers within this class include
polystyrene-polyisoprene-polystyrene,
polystyrene-polybutadiene-polystyrene, and polystyrene-poly
(ethylene-butylene)-polystyrene based triblock copolymers. Such
copolymers are commercially available from a variety of sources,
for example under the brand-name Kraton, from Shell, and from
DEXCO, under the brand-name Vector.
[0098] Exemplary combinations of materials of a two-layer film
wherein one layer is a microfiber layer and the second layer is a
non-microfiber layer, include the following: an elastomeric
non-microfiber layer in combination with a microfiber layer that is
chosen from a hydrophilic, hydrophobic, oleophilic, or oleophobic
layer; an elastomeric layer with a microfiber layer that attracts
dust or particles; a microfiber layer with a non-microfiber layer
that is flame retardant, puncture resistant, or tear resistant. As
a more specific example, a two-layer film could include a
microfibrillated polypropylene surface on one side, and a blend
containing polypropylene, sorbitan monolaurate and glycerol
monolaurate on the other side to wipe up water.
[0099] FIG. 1a illustrates an embodiment of a two-layer film,
showing microfiber article 24 having non-microfiber layer 34, which
can be, for example, an elastomeric layer, and microfiber layer 26
with microfiber surface 28. The materials of each of layers 34 and
26 can be chosen to provide a desired combination of
properties.
[0100] Another embodiment of a two layer microfiber article
includes two microfiber layers and two microfiber surfaces. The
microfiber layers can be chosen to exhibit a useful combination of
properties. An example of such an article is illustrated in FIG.
1b, which shows microfiber article 30 having microfiber layers 32
and 36 and microfiber surfaces 38 and 40, respectively.
[0101] While not shown in FIG. 1b, microfiber article 30 could be
microfibrillated to cause microfiber formation down to any desired
depth of either of layers 32 or 36, such as microfibrillation of
only the two surfaces; or microfibrillation of a surface of one of
either layer, and microfibrillation fully through the other layer,
optionally to cause microfibrillation of the internal surface of
the first layer in contact with the second layer; or
microfibrillation fully through both layers.
[0102] More generally, microfibrillation of any multi-layer film,
e.g., a two-layer film like that of FIG. 1b, having two
microfiber-forming layers, may be controlled to cause
microfibrillation through a full layer and to a second
microfiber-forming layer, to produce microfibers at the interface
between the two layers and into the second layer, so that one or
both types of microfibers can be present at a single microfiber
surface. The other surface may or may not be microfibrillated. This
can produce an article with only one microfiber surface, with that
microfiber surface having microfibers from both layers.
[0103] A different embodiment of a multi-layer film can have three
or more layers, at least one of which is a microfiber-forming
layer. For example, two layers may be microfiber-forming layers and
a third layer (or more layers) may be a non-microfiber-forming
layer.
[0104] FIG. 2 shows an embodiment of a three-layer film wherein one
surface includes a microfiber-forming layer and one surface
includes a non-microfiber-forming layer. Film 8 includes layers 10,
12, and 14. In exemplary film 8, layer 10 can be a
non-microfiber-forming layer, and layer 12 can be a
microfiber-forming layer. Layer 14 can be either a
microfiber-forming layer or a non-microfiber layer.
[0105] In a version of the invention illustrated in FIG. 2a,
microfiber-forming layers may be adjacent to one another and a
non-microfiber layer may be adjacent to only one microfiber-forming
layer. FIG. 2a shows microfiber article 42 having non-microfiber
layer 44 adjacent to microfiber-forming layer 46, which is adjacent
to microfiber-forming layer 48. Microfiber article 42 has
non-microfiber surface 56, and microfiber surface 54.
Microfiber-forming layer 48 has been microfibrillated to produce
microfibers 50, and has been microfibrillated (at least at a
portion of its area) fully through the microfiber forming layer 48.
Over at least those portions of the area, microfiber-forming layer
46 has also been microfibrillated (through layer 48) to produce
microfibers 52, so that both of microfibers 50 and 52 make up the
microfiber surface 54. While FIG. 2a illustrates microfiber article
42 with two adjacent microfiber layers 46 and 48, one of which can
be fibrillated fully through and one of which can be fibrillated
partially through, more than two microfiber layers may be used,
with two or more being fibrillated fully through and one
(typically) being fibrillated at least partially through.
Similarly, this could be done on two surfaces of a microfiber
article, as well as one (as illustrated).
[0106] Exemplary combinations of materials of a three-layer film
according to FIG. 2 wherein the middle layer 14 is a microfiber
layer, include a construction according to FIG. 2a, where layer 48
can be a microfibrillated polypropylene layer, layer 46 can be a
microfibrillated blend containing polypropylene, sorbitan
monolaurate and glycerol monolaurate, and layer 44 can be an
elastomeric non-microfibrillated layer. This construction would be
useful in applications where it is desired for water to be repelled
from the top surface, but absorbed in the middle layer. An example
of such an application could be a dry-to-touch floor mat.
[0107] FIG. 3 shows film 16 having a non-microfiber-forming core
layer 18, such as an elastomeric polymer, and surface layers 20 and
22, which can be microfiber-forming layers, and can be the same or
different. The combined properties of the three layers can be
chosen as desired to provide a useful microfiber article. For
example, the properties of the three layers can combine to produce
a flexible hard rubber or elastomeric cloth-like article with
microfiber surfaces that might independently be hydrophobic,
hydrophilic, oleophobic, oleophilic, etc. Or, the different layers
may be chosen to have different microfiber surface properties, or
preferred mechanical properties.
[0108] Exemplary combinations of materials of a three-layer film
according to FIG. 23, wherein the middle layer 14 is a
non-microfiber layer, include the following: an elastomeric
non-microfiber core layer with two microfiber skin layers, the
microfiber layers being independently any of hydrophobic,
hydrophilic, oleophobic, or oleophilic; a mechanically stiff
non-microfiber core layer with two microfiber skin layers; or a
water-proof and/or breathable non-microfiber core layer with two
microfiber skin layers. Another advantage of using a multi-layer
film in which the two surface layers are fibrillated is the utility
of having the core layer contain a tie layer, which can hold two
microfiber layers together.
[0109] Other examples of three-layer films could include a
fluoropolymer or elastomeric core, or a core of a more rigid solid
plastic, and two microfibrillated surfaces, which may be useful as
a water-proof cloth, a rigid polishing or scrubbing pad, or
possibly a surgical drape.
[0110] Another example of a multi-layer film of the invention
incorporates the use of a multi-layer film that can be
microfibrillated through one layer to a lower level, to produce
microfibers from two or more layers of the film on a single surface
of the film, with fibrillation of the surface in a pattern where
different areas of the pattern are fibrillated to different depths
to produce exposed microfibers from different layers of the
multi-layer film.
[0111] Specifically, microfiber articles of the invention can be
produced to include microfibers from different layers of a
multi-layer film at a single surface of the microfiber article.
FIG. 2a shows multi-layer film 42 with microfibers 50 and 52
present at surface 54 of the film, originating from two different
layers 46 and 48 of the multi-layer film. Thus, according to the
invention, the surface 54 can include microfibers of different
layers, and each the microfibers from each layer can be selected to
have a different property, including any of the properties
mentioned herein, or otherwise.
[0112] According to a specific embodiment of the invention, the
surface of such a multi-layer article can be fibrillated in a
pattern, to different degrees (or depths) to produce exposed
microfibers from the different layers, and to cause the surface to
have selected microfibers from the different layers over different
areas of the article. For instance, referring to FIG. 2a, portions
of surface 54 may be microfibrillated into only layer 48 such that
those portions of the surface 54 include microfibers 50 from layer
48. These portions may be produced in any pattern, such as a strip,
circle, rectangle, triangle, curves, or otherwise. Other areas of
surface 54 can be fibrillated to produce microfibers from layer 46.
By selective microfibrillation of different areas of surface 54 on
multi-layer film 41, in some areas into only the outermost layer 48
and in some areas into a deeper layer 46, a microfiber article can
include an area having microfibers 50 from only layer 48, and can
have a second area having microfibers 52 of layer 46. In this
embodiment, any microfibers 48 produced in the second area of
microfibers 52 may preferably become unattached, leaving only
microfibers 52 from layer 46 on that area.
[0113] The different layers 46 and 48 can be chosen to provide the
first and second microfiber areas on the same surface, having a
desired combination of first and second properties on surface 59 of
the microfiber article. The surface can be of any pattern, as
discussed, and can have different areas, in combination, chosen
from microfibers that are hydrophilic, hydrophobic, oleophilic,
oleophobic, stain resistant, temperature resistant, etc. A
preferred article, for instance, may have different microfiber
areas in the combination of an area of hydrophilic microfibers and
an area of oleophilic or hydrophobic microfibers.
Exemplary Microfibrillated Multi-Layer Film Preparation
Processes
Process I--Casting of Multi-Layer Films
[0114] Multi-layer films were prepared by coextrusion of polymer
melt streams through a 25.4 cm wide Cleoron 3-Layer coextrusion
die, resulting in an A-B or A-B-C multi-layer film construction.
The die was maintained at 243.degree. C. The polymer melt stream
for the A-layer of the multi-layer film was extruded into the
3-layer die using a 51 mm single screw extruder. The extruder
temperature settings increased from 204.degree. C. to 260.degree.
C. from the first heated section of the extruder to the die. The
melt stream for the B-layer of the multi-layer film was extruded
into the 3-layer die using a 25 mm twin-screw extruder. The
extruder temperature settings increased from 204.degree. C. to
243.degree. from the first heated section to the output of the
extruder. The melt stream for the C-layer of the multi-layer film
was extruded into the 3-layer die using a 38 mm single screw
extruder. The extruder temperature settings increased from
204.degree. C. to 260.degree. from the first heated section to the
output of the extruder.
[0115] The output of the coextrusion die traveled over a single
stainless-steel cast roll that was water heated to 99.degree. C.,
with the A-layer of the resulting multi-layer cast film contacting
and electrostatically pinned to the cast roll to help improve the
quality of the film surface. The density of the resulting
multi-layer cast film was determined as described in Test Procedure
II below.
Process II--Calendering and Length Orienting of Multi-Layer Cast
Films
[0116] Multi-layer cast films were calendered and length oriented
on a series of rolls, including a calender. In this process, the
cast film was fed from an unwind station through a series of idler
rolls and into the compressive nip of a calender (rolls 1 and 2).
The film exiting rolls 1 and 2 was further oriented as it passed
over heated rolls 3 and 4 and cooled by traveling over an unheated
roll 5. The resulting oriented film was wound onto a core under
tension. For each of the films, the speed of roll 4 was set at a
speed just below the speed at which the film would break. Test
Procedure I described below was used to determine the draw ratio of
the resulting film. Test Procedure II described below was used to
determine the density and void content of the resulting film.
Process III--Microfibrillation of Oriented Multi-Layer Films
[0117] Calendered and length-oriented multi-layer films were
microfibrillated on one or both major surfaces in a hydroentangler
(70 cm wide, manufactured by Honeycomb Systems Inc., Biddeford,
Me.) using approximately 13.8 MPa water pressure, with multiple
passes at a belt speed of 3.05 m/min, and a water jet strip having
15.75 holes/cm, with each hole having a diameter of 1.0 micron.
Test Procedures
Test Procedure I--Draw Ratio Measurement
[0118] The draw ratio of calendered and length oriented films were
calculated by dividing the roll 4 (described above) output speed by
the input speed of the cast web into rolls 1 and 2 (described
above).
Test Procedure II--Density Measurement and Void Content
Determination
[0119] Densities of cast films and films after calendering and
orienting were measured at 23.degree. C. in deionized water
according to the method of ASTM D792-86. Each film sample was
weighed on a Mettler AG245 high precision balance (Mettler-Toledo,
Inc., Highstown, N.J.) and placed underwater. The mass of the water
displaced was measured using the density measurement fixture. The
volume of water displaced by the sample was thereby determined and,
in combination with the sample weight, used to calculate the sample
density. The void content was then calculated as follows:
[0120] Calculated Void content={1-(final density/initial
density)}.times.100 where the initial density is the density of the
cast film before orientation, and the final density is the density
of the oriented film.
EXAMPLES
Example 1
[0121] An "A-B-C" 3-layer cast film was prepared according to
Process I using polypropylene homopolymer (Fina 3271, available
from Atofina Inc., Houston, Tex.) for the A-layer melt stream, a
tri-block copolymer with polystyrene end blocks and a rubbery
poly(ethylene-butylene) mid block (Kraton G1657, available from
Kraton Polymers, Houston Tex.) for the B-layer melt stream, and a
polypropylene homopolymer (Fina 3271, available from Atofina Inc.,
Houston, Tex.) for the C-layer melt stream. The resulting 3-layer
cast film had a thickness of 940 micrometer, a width of 241 mm, and
a density of 0.9 gram/cm.sup.3.
[0122] The resulting cast film was calendered and length oriented
according to Process II. The cast film was fed from an unwind
station into the compressive nip of rolls 1 and 2 at a rate of 0.23
m/min. Rolls 1 and 2 each had surface speed of 0.91 m/min, a
temperature of 120.degree. C., and a gap between the rolls of 0.18
mm. Roll 3 had a surface speed of 2.97 m/min and a temperature of
120.degree. C. Roll 4 had a surface speed of 3.27 m/min and a
temperature of 145.degree. C. The film was oriented to a draw ratio
of 14.5:1 as determined by Test Procedure 1. The resulting oriented
film had a thickness of 100 micrometers, a width of 169.9 mm, and a
density of 0.93 gram/cm.sup.3. Although the film appeared white and
hence voided; the film was calculated to contain 0% voids.
[0123] Finally the oriented film was microfibrillated on both sides
as described in Process III, by passing the film through the
hydroentangler 6 times on each side. This resulted in a film with
an elastomeric core layer and two microfibrillated surfaces. The
properties of this film made it useful as a waterproof cloth-like
film.
Example 2
[0124] An "A-B-C" 3-layer cast film was prepared according to
Process I using polypropylene homopolymer (Fina 3271, available
from Atofina Inc., Houston, Tex.) for the A-layer melt stream, a
blend of 80% polypropylene homopolymer (Fina 3271, available from
ATOFINA Inc., Houston, Tex.) and 20% of an ethylene vinyl acetate
copolymer (Elvax 670, available from DuPont Chemical Co.,
Wilmington, Del.) for the B-layer melt stream, and a polypropylene
homopolymer (Fina 3271, available from Atofina Inc., Houston, Tex.)
for the C-layer melt stream. The resulting cast film had a
thickness of 880 micrometer, a width of 240 mm, and a density of
0.91 grams/cm.sup.3.
[0125] The resulting 3-layer cast film was calendered and length
oriented according to Process II. The cast film was fed from an
unwind station into the compressive nip of rolls 1 and 2 at a rate
of 0.32 m/min. Rolls 1 and 2 each had surface speed of 0.91 m/min,
a temperature of 100.degree. C., and a gap between the rolls of
0.18 mm. Roll 3 had a surface speed of 4.11 m/min and a temperature
of 145.degree. C. Roll 4 had a surface speed of 6.79 m/min and a
temperature of 145.degree. C. The film was oriented to a draw ratio
of 21.4:1. The oriented film had a thickness of 121 micrometers, a
width of 127 mm, and a density of 0.82 gram/cm.sup.3. The film was
calculated to contain 10% voids.
[0126] The oriented film was microfibrillated on both sides as
described in Process III, by passing the film through the
hydroentangler 4 times on each side. The preparation of the
resulting microfibrillated 3-layer film showed that the use of
polypropylene protective A and C layers assisted in the orienting
process and resulted in a film that was oriented to an extension
ratio of 21.4:1, contained 10% by volume of voids, and was able to
be fibrillated completely through the oriented film, without
leaving an inner layer of film.
Example 3
[0127] An "A-B-C" 3-layer cast film was prepared according to
Process I using a blend of 80% polypropylene homopolymer (Fina
3271, available from Atofina Inc., Houston, Tex.) and 20% of an
ethylene vinyl acetate copolymer (Elvax 670, available from DuPont
Chemical Co., Wilmington, Del.) for the A-layer melt stream,
polypropylene homopolymer (Fina 3271, available from Atofina Inc.,
Houston, Tex.) for the B-layer melt stream, and a blend of 80%
polypropylene homopolymer (Fina 3271, available from Atofina Inc.,
Houston, Tex.) and 20% of an ethylene vinyl acetate copolymer
(Elvax 670, available from DuPont Chemical Co., Wilmington, Del.)
for the C-layer melt stream. The resulting 3-layer cast film had a
thickness of 920 micrometer, a width of 243 mm, and a density of
0.91 grams/cm.sup.3.
[0128] The resulting 3-layer cast film was calendered and length
oriented according to Process II. The cast film was fed from an
unwind station into the compressive nip of rolls 1 and 2 at a rate
of 0.31 m/min. Rolls 1 and 2 each had a surface speed of 0.91
m/min, a temperature of 100.degree. C., and a gap between the rolls
of 0.18 mm. Roll 3 had a surface speed of 4.11 m/min and a
temperature of 145.degree. C. Roll 4 had a surface speed of 4.94
m/min and a temperature of 145.degree. C. The film was oriented to
a draw ratio of 15.9:1. The oriented film had a thickness of 98
micrometers, a width of 165 mm, and a density of 0.87
gram/cm.sup.3. The film was calculated to contain 4% voids.
[0129] The oriented film was microfibrillated on both sides as
described in Process III by passing the film through the
hydroentangler 4 times on each side. The resulting 3-layer film,
although microfibrillated on both surfaces, still contained a core
layer of film. The film was oriented to an extension ratio of
15.9:1, contained 4% by volume of voids, and was not fibrillated
completely through the film, leaving an inner layer of intact film.
This shows that the use of polypropylene protective layers A and C
in Example 2 assisted in increasing the extent of orientation,
resulting in a film that was easier to microfibrillate than this
3-layer film of Example 3.
Example 4
[0130] An "A-B" 2-layer cast film was prepared according to Process
I using a blend of 80% polypropylene homopolymer (Fina 3271,
available from Atofina Inc., Houston, Tex.) and 20% of an ethylene
vinyl acetate copolymer (Elvax 670, available from DuPont Chemical
Co., Wilmington, Del.) for both the A- and B-layer melt streams.
The cast film had a thickness of 924 micrometer, a width of 241 mm,
and a density of 0.91 grams/cm.sup.3.
[0131] The resulting cast film was calendered and length oriented
according to Process II. The cast film was fed from an unwind
station into the compressive nip of rolls 1 and 2 at a rate of 0.27
m/min. Rolls 1 and 2 each had surface speed of 0.91 m/min, a
temperature of 100.degree. C., and a gap between the rolls of 0.18
mm. Roll 3 had a surface speed of 3.66 m/min and a temperature of
145.degree. C. Roll 4 had a surface speed of 5.49 m/min and a
temperature of 145.degree. C. The film was oriented to a draw ratio
of 20.1:1. The oriented film had a thickness of 77 micrometers, a
width of 152 mm, and a density of 0.91 gram/cm.sup.3. The resulting
oriented 2-layer film was clear and was calculated to contain 0%
voids.
[0132] The oriented 2-layer film was subjected to conditions for
microfibrillation on both sides as described in Process III, by
passing the film through the hydroentangler 4 times on each side.
The resulting film, although microfibrillated on both surfaces,
still contained internal portions of intact film. In comparison
with the microfibrillated 3-layer film of Example 2, Example 4
resulted in a film that was oriented to an extension ratio of
20.1:1, contained 0% by volume of voids, and was not
microfibrillated completely through, leaving an inner portion of
intact film. This further shows that the use of polypropylene
protective layers in Example 2 assisted in increasing the extent of
orientation, resulting in a more voided film and hence a more
thoroughly microfibrillated film than this 2-layer film of Example
4.
Example 5
[0133] An "A-B-C" 3-layer cast film was prepared according to
Process I using a blend of 80% by weight polypropylene homopolymer
(Fina 3271, available from ATOFina Inc., Houston, Tex.) and 20% by
weight of an ethylene vinyl acetate copolymer (Elvax 670, available
from DuPont Chemical Co., Wilmington, Del.) for the A-layer melt
stream, a low density polyethylene (Eastman LDPE 1550P, available
from Eastman Chemical Co., Kingsport, Tenn.) for the B-layer melt
stream, and a blend of 80% by weight polypropylene homopolymer
(Fina 3271, available from ATOFina Inc., Houston, Tex.) and 20% by
weight of an ethylene vinyl acetate copolymer (Elvax 670, available
from DuPont Chemical Co., Wilmington, Del.) for the C-layer melt
stream. The resulting 3-layer cast film had a thickness of 926
micrometers, a width of 241 mm, and a density of 0.92
grams/cm.sup.3.
[0134] The resulting cast film was calendered and length oriented
according to Process II. The cast film was fed from an unwind
station into the compressive nip of rolls 1 and 2 at a rate of 0.31
m/min. Rolls 1 and 2 each had a surface speed of 0.91 m/min, a
temperature of 100.degree. C., and a gap between the rolls of 0.18
mm. Roll 3 had a surface speed of 4.11 m/min and a temperature of
145.degree. C. Roll 4 had a surface speed of 5.35 m/min and a
temperature of 145.degree. C. The film was oriented to a draw ratio
of 17.2:1. The resulting oriented 3-layer film had a thickness of
144 micrometers, a width of 162 mm, and a density of 0.84
gram/cm.sup.3. The film was calculated to contain 8.7% voids.
[0135] The oriented 3-layer film was microfibrillated on both sides
as described in Procedure III by passing the film through the
hydroentangler 12 times on each side. This resulted in a film with
a solid waterproof core layer and two microfibrillated
surfaces.
Example 6
[0136] An "A-B-C" 3-layer cast film was prepared according to
Process I using a polypropylene homopolymer (Fina 3271, available
from Atofina Inc., Houston, Tex.) for the A-layer melt stream, a
tri-block copolymer with polystyrene end blocks and a rubbery
poly(ethylene-butylene) mid block (Kraton G 1657, available from
Kraton Polymers, Houston Tex.) for the B-layer melt stream, and a
polyethylene elastomer (Affinity 1845, available from Dow Plastics,
Midland, Mich.) for the C-layer melt stream. The resulting 3-layer
cast film had a thickness of 880 micrometer, a width of 241 mm, and
a density of 0.88 gram/cm.sup.3.
[0137] The resulting cast film was calendered and length oriented
according to Process II. The cast film was fed from an unwind
station into the compressive nip of rolls 1 and 2 at a rate of 0.34
m/min. Rolls 1 and 2 each had surface speed of 0.61 m/min, a
temperature of 80.degree. C., and a gap between the rolls of 0.18
mm. Roll 3 had a surface speed of 2.44 m/min and a temperature of
145.degree. C. Roll 4 had a surface speed of 3.55 m/min and a
temperature of 145.degree. C. The film was oriented to a draw ratio
of 10.3:1. The resulting oriented 3-layer film had a thickness of
151 micrometers, a width of 160 mm, and a density of 0.9
gram/cm.sup.3. This film was clear and was calculated to contain 0%
voids.
[0138] Only the "A" side of the oriented 3-layer film was subjected
to conditions for microfibrillation as described in Process III by
passing the film through the hydroentangler 12 times. This resulted
in a 3-layer puncture resistant film with one microfibrillated
surface.
Example 7
[0139] An "A-B" 2-layer cast film was prepared according to Process
I using a polypropylene homopolymer (Fina 3271, available from
Atofina Inc., Houston, Tex.) for the A-layer melt stream, and a
blend containing polypropylene homopolymers (22.5 weight % Fina
3445 with a melt flow index of 35 and 73.5 weight % Fina 3181 with
a melt flow index of 0.75, both available from Atofina Inc.,
Houston Tex.), 1.3 weight % sorbitan monolaurate (SPAN 20 available
from Uniqema, New Castle, Del.), and 2.7 weight % glycerol
monolaurate (Lauricidin available from Med-Chem Labs, Inc., Galena,
Ill.) for the B-layer melt stream. The resulting two-layer cast
film had a thickness of 876 micrometer, a width of 237 mm, and a
density of 0.91 gram/cm.sup.3.
[0140] The resulting 2-layer cast film was calendered and length
oriented according to Process II. The cast film was fed from an
unwind station into the compressive nip of rolls 1 and 2 at a rate
of 0.3 m/min. Roll 1 had surface speed of 0.91 m/min, a temperature
of 120.degree. C. Roll 2 had surface speed of 1.6 m/min and a
temperature of 120.degree. C. The gap between rolls 1 and 2 was set
to 0.2 mm. Rolls 3 and 4 each had a surface speed of 4.8 m/min and
a temperature of 145.degree. C. The film was oriented to a draw
ratio of 15.8:1. The resulting oriented 2-layer film had a
thickness of 93 micrometers, a width of 249 mm, and a density of
0.90 g/cm.sup.3. Although the film appeared white and hence voided;
the film was calculated to contain only 0.2% voids.
[0141] The oriented 2-layer film was microfibrillated on both sides
as described in Process III by passing the film through the
hydroentangler 6 times on each side. The resulting 3-layer film,
although microfibrillated on both surfaces, was not fibrillated
completely through the film, leaving an inner portion of intact
film in the core. This resulted in a microfibrillated film or
non-woven cloth that was hydrophilic on one side and hydrophobic
and oleophilic on the other side.
Example 8
[0142] An "A-B-C" 3-layer cast film was prepared according to
Process I using a polypropylene homopolymer (Fina 3271, available
from Atofina Inc., Houston, Tex.) for the A-layer melt stream, a
blend containing polypropylene homopolymers (22.5 weight % Fina
3445 with a melt flow index of 35 and 73.5 weight % Fina 3181 with
a melt flow index of 0.75, available from Atofina Inc., Houston,
Tex.), 1.3 weight % sorbitan monolaurate (SPAN 20 available from
Uniqema, New Castle Del.), and 2.7 weight % glycerol monolaurate
(Lauricidin available from Med-Chem Labs, Inc., Galena, Ill.) for
the B-layer melt stream, and a polypropylene homopolymer (Fina
3271, available from Atofina Inc., Houston, Tex.) for the C-layer
melt stream. The resulting 3-layer cast film had a thickness of 878
micrometers, a width of 238 mm, and a density of 0.9
gram/cm.sup.3.
[0143] The resulting cast film was calendered and length oriented
according to Process II. The cast film was fed from an unwind
station into the compressive nip of rolls 1 and 2 at a rate of 0.33
m/min. Rolls 1 and 2 each had a surface speed of 0.91 m/min and a
temperature of 120.degree. C. The gap between rolls 1 and 2 was set
to 0.18 mm. Roll 3 had a surface speed of 4.57 m/min and a
temperature of 145.degree. C. Roll 4 had a surface speed of 6.17
mn/min and a temperature of 145.degree. C. The film was oriented to
a draw ratio of 18.5:1. The oriented film had a thickness of 100
micrometers, a width of 152 mm, and a density of 0.80
gram/cm.sup.3. The film was calculated to contain 11% voids.
[0144] The oriented film was microfibrillated on both sides as
described in Process III by passing the film through the
hydroentangler 6 times on each side. The preparation of the
resulting microfibrillated 3-layer film showed that the use of
polypropylene protective A and C layers assisted in the orienting
process and resulted in a film that was oriented to an extension
ratio of 18.5:1, contained 11% by volume of voids, and was able to
be microfibrillated completely through the oriented film, without
leaving an inner portion of un-fibrillated film. Compared with the
microfibrillated film of Example 7, this microfibrillated 3-layer
film of Example 8 had an increased extent of orientation, an
increased void volume per cent, and was more thoroughly
microfibrillated. Similar to microfibrillated film of Example 7,
this construction was also a non-woven cloth-like film with both
hydrophilic and oleophilic surface properties.
Example 9
[0145] An "A-B-C" 3-layer cast film was prepared according to
Process I using a polypropylene homopolymer (Fina 3271, available
from Atofina Inc., Houston, Tex.) for the A-layer melt stream, a
fluoropolymer (THV 220, available from Dyneon LLC, Oakdale, Minn.)
for the B-layer melt stream, and a polypropylene homopolymer (Fina
3271, available from Atofina Inc., Houston, Tex.) for the C-layer
melt stream. The resulting cast film had a thickness of 831
micrometer, a width of 222 mm, and a density of 1.1
grams/cm.sup.3.
[0146] The resulting 3-layer cast film was calendered and length
oriented according to Process II. The cast film was fed from an
unwind station into the compressive nip of rolls 1 and 2 at a rate
of 0.48 m/min. Rolls 1 and 2 each had a surface speed of 0.91
m/min, a temperature of 80.degree. C., and a gap between the rolls
of 0.18 mm. Roll 3 had a surface speed of 4.57 m/min and a
temperature of 120.degree. C. Roll 4 had a surface speed of 4.65
m/min and a temperature of 145.degree. C. The film was oriented to
a draw ratio of 10.8:1. The resulting oriented 3-layer film had a
thickness of 186 micrometers, a width of 143 mm, and a density of
0.86 gram/cm.sup.3. The film appeared white and hence voided;
although there was some delamination between the layers.
[0147] The oriented 3-layer film was microfibrillated on both sides
as described in Process III by passing the film through the
hydroentangler 6 times on each side. This resulted in a film with a
fluoropolymer core layer and two microfibrillated surfaces.
Example 10
[0148] An "A-B-C" 3-layer film was cast and oriented as in Example
8. A poly(vinylchloride) tape was applied to the top "A" layer to
mask the film, leaving only one square region of the surface
exposed. The masked film was microfibrillated on the masked "A"
side through the "A" layer and into the underlying "B" layer as
described in Process III, by passing the film through the
hydroentangler 4 times, exposing only the unmasked portion of the
"A" layer to the water jets. The masking tape was then removed from
the "A" top layer. The result was a selectively microfibrillated,
chemically differentiated sheet having a square region which
contained microfibers of both the "A" and "B" layers surrounded by
the unfibrillated region (masked area) of the top "A" layer. The
microfibrillated region possessed a hydrophilic quality due to the
presence of the fibers which originated from the underlying "B"
layer, while the surrounding region was hydrophobic, because it was
composed solely of the unfibrillated "A" top layer of
polypropylene. These results show that a multilayer film, having a
selected microfibrous area of one property adjacent an
unfibrillated area of another property.
Example 11
[0149] An "A-B-C" 3-layer film was cast and oriented as in Example
8. The oriented film was microfibrillated only partially through
the top "A" layer as described in Process III, by passing the film
through the hydroentangler one time, exposing only the "A" layer of
the 3-layer film to the water jets. Then an aluminum plate having
several circular holes was placed over the resulting top "A" layer
to mask the film, leaving several circular regions of the film
surface exposed. The masked film was then microfibrillated on the
masked side as described in Process 111, by passing the film
through the hydroentangler three more times, exposing only the
unmasked circular regions of the film to the water jets. The
resulting construction had a chemically differentiated, selectively
patterned fibrous surface having circular regions containing fibers
of both the "A" layer and the "B" layer. These regions possessed a
hydrophilic character and were surrounded by regions containing
only fibers of the "A" layer which were hydrophobic in nature.
These results show that a multilayer film, having selected
microfibrous areas of one property adjacent a microfibrillated area
of another property, was formed.
* * * * *