U.S. patent application number 11/226542 was filed with the patent office on 2006-01-12 for embossed multi-ply fibrous structure product and process for making same.
Invention is credited to Christopher Scott Kraus, Kevin Benson McNeil, Michael Gomer JR. Stelljes, George Vincent Wegele.
Application Number | 20060005916 11/226542 |
Document ID | / |
Family ID | 34376658 |
Filed Date | 2006-01-12 |
United States Patent
Application |
20060005916 |
Kind Code |
A1 |
Stelljes; Michael Gomer JR. ;
et al. |
January 12, 2006 |
Embossed multi-ply fibrous structure product and process for making
same
Abstract
Multi-ply fibrous structure products, more specifically embossed
multi-ply fibrous structure products and methods for making same
are provided.
Inventors: |
Stelljes; Michael Gomer JR.;
(Mason, OH) ; Kraus; Christopher Scott; (Sunman,
IN) ; Wegele; George Vincent; (Fairfield, OH)
; McNeil; Kevin Benson; (Loveland, OH) |
Correspondence
Address: |
THE PROCTER & GAMBLE COMPANY;INTELLECTUAL PROPERTY DIVISION
WINTON HILL TECHNICAL CENTER - BOX 161
6110 CENTER HILL AVENUE
CINCINNATI
OH
45224
US
|
Family ID: |
34376658 |
Appl. No.: |
11/226542 |
Filed: |
September 14, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10673659 |
Sep 29, 2003 |
|
|
|
11226542 |
Sep 14, 2005 |
|
|
|
Current U.S.
Class: |
156/209 |
Current CPC
Class: |
Y10T 428/24562 20150115;
B31F 2201/0764 20130101; Y10T 156/1023 20150115; B31F 2201/0787
20130101; Y10T 428/24612 20150115; B31F 1/07 20130101; B31F
2201/0774 20130101; B32B 7/10 20130101; Y10T 428/24463 20150115;
B32B 5/26 20130101; B32B 37/12 20130101; B32B 38/06 20130101; Y10T
428/24628 20150115; Y10T 428/24479 20150115; B31F 2201/0738
20130101; B32B 7/12 20130101; B32B 3/28 20130101; Y10T 428/24992
20150115; B32B 5/24 20130101; B31F 2201/0743 20130101 |
Class at
Publication: |
156/209 |
International
Class: |
B32B 31/00 20060101
B32B031/00 |
Claims
1. A method for making an embossed multi-ply fibrous structure
product comprising the steps of: a) adhesively binding two or more
plies of fibrous structure together to form a multi-ply fibrous
structure by applying an adhesive to at least one surface of the
two or more plies, wherein the adhesive is applied to less than
about 30% of at least one of the two or more plies surfaces; b)
embossing the multi-ply fibrous structure such that the multi-ply
fibrous structure exhibits an embossment height of at least about
1000 .mu.m to form the embossed multi-ply fibrous structure
product.
2. The method according to claim 1 wherein the adhesive is applied
in an amount sufficient to provide a plybond strength of at least 4
g/in in the embossed multi-ply fibrous structure product.
3. The method according to claim 1 wherein at least one of the two
or more plies of fibrous structure comprises a fibrous structure
selected from the group consisting of: through-air-dried fibrous
structure plies, differential density fibrous structure plies, wet
laid fibrous structure plies, air laid fibrous structure plies,
conventional fibrous structure plies and mixtures thereof
4. The method according to claim 1 wherein the multi-ply embossed
fibrous structure product exhibits a wet burst of at least about
305 g.
5. The method according to claim 1 wherein the adhesive is applied
to the adjacent surfaces in the form of separate, discrete dots
and/or separate, discrete stripes.
6. A method for making an embossed multi-ply fibrous structure
product comprising the steps of: a) providing a first ply of
fibrous structure; b) providing a second ply of fibrous structure;
c) applying an adhesive to a surface of the first ply of fibrous
structure such that the adhesive contacts from about 0.1% to about
30% of the surface area of the first ply of fibrous structure; d)
combining and marrying the first and second plies of fibrous
structure along adjacent surfaces of the first and second plies of
fibrous structure such that the adhesive bonds the two plies
together to form a multi-ply fibrous structure exhibiting a plybond
strength of at least about 4 g/in; and e) embossing the multi-ply
fibrous structure such that an embossed multi-ply fibrous structure
product exhibiting an embossment height of at least 1000 .mu.m is
formed.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a divisional application of U.S.
application Ser. No. 10/673,659, filed Sep. 29, 2003.
FIELD OF THE INVENTION
[0002] The present invention relates to multi-ply fibrous structure
products, more specifically embossed multi-ply fibrous structure
products and methods for making same.
BACKGROUND OF THE INVENTION
[0003] Conventional embossed multi-ply fibrous structure products
having embossment heights of 1000 .mu.m or greater are known in the
art. However, such conventional embossed multi-ply fibrous
structure products contained bonded, densified embossment sites.
Such conventional embossed multi-ply fibrous structure products
exhibited product property deficiencies, especially with respect to
the wet burst strength. Such conventional embossed multi-ply
fibrous structure products exhibited a wet burst strength of 303 g
or less. In addition, such conventional embossed multi-ply fibrous
structure products suffered from problems associated with the
adhesive between the plies moving when embossed prior to achieving
acceptable plybond strength. Tensile strengths in such products
were also typically lower than acceptable.
[0004] Prior art attempts to overcome the prior art's product
property deficiencies included applying excess adhesive to the
plies of the fibrous structure prior to embossing and then marrying
the plies to form a multi-ply fibrous structure product. The
adhesive covered greater than 40% of the surface area of the plies.
The relatively large amount of adhesive was required to get
acceptable plybond strength in the product.
[0005] Accordingly, there is a need for an embossed multi-ply
fibrous structure product wherein the plies of the multi-ply
fibrous structure product were bonded together by an adhesive over
less than 40% of the surface area of the plies. Further, there is a
need for an embossed multi-ply fibrous structure product that
comprises embossments having an embossment height of greater than
1000 .mu.m and a wet burst strength of at least 305 g and/or a
plybond strength of at least 4 g/in.
SUMMARY OF THE INVENTION
[0006] The present invention fulfills the need described above by
providing an embossed multi-ply fibrous structure product.
[0007] In one aspect of the present invention, an embossed
multi-ply fibrous structure product comprising two or more plies of
fibrous structure bonded together along adjacent surfaces of the
two or more plies by an adhesive to form a bond area, wherein the
bond area is less than about 30% of the bonded adjacent surfaces,
wherein the product comprises two faces, wherein one face comprises
non-adhesively bonded embossed sites and the other face comprises
adhesively bonded non-embossed sites, and wherein the fibrous
structure product exhibits an embossment height of at least about
1000 .mu.m, is provided.
[0008] In another aspect of the present invention, an embossed
multi-ply fibrous structure product comprising two or more plies of
fibrous structure bonded together at a plybond strength of at least
about 4 g/in along adjacent surfaces of the two or more plies by an
adhesive to form a bond area, wherein the bond area is less than
about 30% of the bonded adjacent surfaces, wherein the product
exhibits an embossment height of at least about 1000 .mu.m, and a
wet burst of at least about 305 g, is provided.
[0009] In still another aspect of the present invention, an
embossed multi-ply fibrous structure product comprising a first
face and a second face, wherein the first face comprises
non-adhesively bonded embossed sites and the second face comprises
adhesively bonded non-embossed sites, is provided.
[0010] In even another aspect of the present invention, an embossed
multi-ply fibrous structure product comprising a first face and a
second face, wherein the first face comprises non-densified
embossed sites and the second face comprises densified non-embossed
sites, is provided.
[0011] In yet another aspect of the present invention, a method for
making an embossed multi-ply fibrous structure product comprising
the steps of: [0012] a) adhesively binding two or more plies of
fibrous structure together to form a multi-ply fibrous structure by
applying an adhesive to at least one surface of the two or more
plies, wherein the adhesive is applied to less than about 30% of at
least one of the two or more plies surfaces; [0013] b) embossing
the multi-ply fibrous structure such that the multi-ply fibrous
structure exhibits an embossment height of at least about 1000
.mu.m to form the embossed multi-ply fibrous structure product, is
provided.
[0014] In still yet another aspect of the present invention, a
method for making an embossed multi-ply fibrous structure product
comprising the steps of: [0015] a) providing a first ply of fibrous
structure; [0016] b) providing a second ply of fibrous structure;
[0017] c) applying an adhesive to a surface of the first ply of
fibrous structure such that the adhesive contacts less than about
30% of the surface area of the first ply of fibrous structure;
[0018] d) combining and marrying the first and second plies of
fibrous structure along adjacent surfaces of the first and second
plies of fibrous structure such that the adhesive bonds the two
plies together to form a multi-ply fibrous structure exhibiting a
plybond strength of at least about 4 g/in; and [0019] e) embossing
the multi-ply fibrous structure such that an embossed multi-ply
fibrous structure product exhibiting an embossment height of at
least 1000 .mu.m is formed, is provided.
[0020] Accordingly, the present invention provides an embossed
multi-ply fibrous structure product and methods for making embossed
multi-ply fibrous structure products.
BRIEF DESCRIPTION OF THE DRAWINGS
[0021] FIG. 1A is a fragmentary side sectional view of one
embodiment of an embossed multi-ply fibrous structure product
according to the present invention.
[0022] FIG. 1B is a fragmentary side sectional view of another
embodiment of an embossed multi-ply fibrous structure product
according to the present invention.
[0023] FIG. 1C is a fragmentary side sectional view of another
embodiment of an embossed multi-ply fibrous structure product
according to the present invention.
[0024] FIG. 2 is a schematic side elevational view of one
embodiment of an apparatus used for making an embossed multi-ply
fibrous structure product according to the present invention.
[0025] FIG. 3 is an enlarged fragmentary side elevational view of
the apparatus shown in FIG. 2.
[0026] FIG. 4 is a top plan view of a fibrous structure comprising
an adhesive in pattern form.
DETAILED DESCRIPTION OF THE INVENTION
[0027] "Fiber" as used herein means an elongate particulate having
an apparent length greatly exceeding its apparent width, i.e. a
length to diameter ratio of at least about 10. More specifically,
as used herein, "fiber" refers to papermaking fibers. The present
invention contemplates the use of a variety of papermaking fibers,
such as, for example, natural fibers or synthetic fibers, or any
other suitable fibers, and any combination thereof. Papermaking
fibers useful in the present invention include cellulosic fibers
commonly known as wood pulp fibers. Applicable wood pulps include
chemical pulps, such as Kraft, sulfite, and sulfate pulps, as well
as mechanical pulps including, for example, groundwood,
thermomechanical pulp and chemically modified thermomechanical
pulp. Chemical pulps, however, may be preferred since they impart a
superior tactile sense of softness to tissue sheets made therefrom.
Pulps derived from both deciduous trees (hereinafter, also referred
to as "hardwood") and coniferous trees (hereinafter, also referred
to as "softwood") may be utilized. The hardwood and softwood fibers
can be blended, or alternatively, can be deposited in layers to
provide a stratified web. U.S. Pat. No. 4,300,981 and U.S. Pat. No.
3,994,771 are incorporated herein by reference for the purpose of
disclosing layering of hardwood and softwood fibers. Also
applicable to the present invention are fibers derived from
recycled paper, which may contain any or all of the above
categories as well as other non-fibrous materials such as fillers
and adhesives used to facilitate the original papermaking. In
addition to the above, fibers and/or filaments made from polymers,
specifically hydroxyl polymers may be used in the present
invention. Nonlimiting examples of suitable hydroxyl polymers
include polyvinyl alcohol, starch, starch derivatives, chitosan,
chitosan derivatives, cellulose derivatives, gums, arabinans,
galactans and mixtures thereof.
[0028] "Wet Burst Strength" as used herein is a measure of the
ability of a fibrous structure and/or a fibrous structure product
incorporating a fibrous structure to absorb energy, when wet and
subjected to deformation normal to the plane of the fibrous
structure and/or fibrous structure product.
[0029] "Basis Weight" as used herein is the weight per unit area of
a sample reported in lbs/3000 ft.sup.2 or g/m.sup.2. Basis weight
is measured by preparing one or more samples of a certain area
(m.sup.2) and weighing the sample(s) of a fibrous structure
according to the present invention and/or a fibrous structure
product comprising such fibrous structure on a top loading balance
with a minimum resolution of 0.01 g. The balance is protected from
air drafts and other disturbances using a draft shield. Weights are
recorded when the readings on the balance become constant. The
average weight (g) is calculated and the average area of the
samples (m.sup.2). The basis weight (g/m.sup.2) is calculated by
dividing the average weight (g) by the average area of the samples
(m.sup.2).
[0030] "Machine Direction" or "MD" as used herein means the
direction parallel to the flow of the fibrous structure through the
papermaking machine and/or product manufacturing equipment.
[0031] "Cross Machine Direction" or "CD" as used herein means the
direction perpendicular to the machine direction in the same plane
of the fibrous structure and/or fibrous structure product
comprising the fibrous structure.
[0032] "Sheet Caliper" or "Caliper" as used herein means the
macroscopic thickness of a sample.
[0033] "Densified" as used herein means a portion of a fibrous
structure product that exhibits a greater density than another
portion of the fibrous structure product. For example, a densified
area of the embossed multi-ply fibrous structure product according
to the present invention is typically 0.19 g/cc or greater. In one
embodiment of the present invention, the embossed multi-ply fibrous
structure product comprises a densified area that is at least 2
times the density of another portion of the embossed multi-ply
fibrous structure product.
[0034] "Non-densified" as used herein means a portion of a fibrous
structure product that exhibits a lesser density than another
portion of the fibrous structure product. For example, a
non-densified area of the embossed multi-ply fibrous structure
product according to the present invention is typically less than
about 0.19 g/cc. In one embodiment of the present invention, the
embossed multi-ply fibrous structure product comprises a
non-densified area that is less than 2 times the density of another
portion of the embossed multi-ply fibrous structure product.
[0035] "Stretch" as used herein is determined by measuring a
fibrous structure's Dry Tensile Strength in MD and/or CD.
[0036] "Apparent Density" or "Density" as used herein means the
basis weight of a sample divided by the caliper with appropriate
conversions incorporated therein. Apparent density used herein has
the units g/cm.sup.3 (alternatively g/cc).
[0037] "Bulk Density" as used herein means the apparent density of
an entire fibrous structure product rather than a discrete area
thereof.
[0038] "Ply" or "Plies" as used herein means an individual fibrous
structure optionally to be disposed in a substantially contiguous,
face-to-face relationship with other plies, forming a multi-ply
fibrous structure. It is also contemplated that a single fibrous
structure can effectively form two "plies" or multiple "plies", for
example, by being folded on itself.
Embossed Multi-ply Fibrous Structure Product
[0039] The embossed multi-ply fibrous structure product according
to the present invention comprises two or more plies of fibrous
structure that are bonded together along their adjacent surfaces by
an adhesive. The adhesive may cover less than about 30% and/or from
about 0.1% to about 30% and/or from about 3% to about 30% and/or
from about 5% to about 25% and/or from about 5% to about 20% of the
bonded adjacent surfaces. The adhesive may be applied to one or
more of the plies of fibrous structure in a continuous and/or
discontinuous network pattern, such as separate, discrete dots
and/or separate, discrete stripes.
[0040] In one embodiment of the present invention, the embossed
multi-ply fibrous structure exhibits a plybond strength of at least
about 4 g/in and/or at least about 5 g/in and/or at least about 6
g/in as measured by the Plybond Strength Test Method described
herein.
[0041] In another embodiment of the present invention, the embossed
multi-ply fibrous structure product comprises a first face and a
second face, wherein the first face comprises non-adhesively bonded
embossed sites and the second face comprises adhesively bonded
non-embossed sites.
[0042] In still another embodiment of the present invention, the
embossed multi-ply fibrous structure product comprises a first face
and a second face, wherein the first face comprises non-densified
embossed sites and the second face comprises densified non-embossed
sites.
[0043] In even another embodiment of the present invention, the
embossed multi-ply fibrous structure product exhibits a wet burst
strength of at least 305 g and/or at least about 315 g and/or at
least about 325 g and/or at least about 400 g as measured by the
Wet Burst Strength Test Method as described herein.
[0044] In yet another embodiment of the present invention, the
embossed multi-ply fibrous structure product comprises embossed
sites of at least 1000 .mu.m and/or from about 1000 .mu.m to about
5000 .mu.m and/or from about 1100 .mu.m to about 3000 .mu.m and/or
from about 1100 .mu.m to about 2000 .mu.m as measured by the
Embossment Height Test Method described herein.
[0045] In even another embodiment of the present invention, the
embossed multi-ply fibrous structure product comprises densified
and non-densified regions wherein the densified regions exhibit a
caliper of 10 mils or less and/or from about 0.1 to about 6 mils
and/or from about 1 to about 5 mils.
[0046] In still yet another embodiment of the present invention,
the embossed multi-ply fibrous structure product wherein the
product exhibits a sheet caliper of at least about 30 mils and/or
at least about 40 mils and/or at least about 50 mils as measured by
the Sheet Caliper Test Method.
[0047] In even yet another embodiment of the present invention, the
embossed multi-ply fibrous structure product exhibits a sheet
caliper to effective caliper ratio of greater than 1.1 and/or
greater than 1.2 and/or greater than 1.3.
[0048] In even still another embodiment of the present invention,
the embossed multi-ply fibrous structure product exhibits a cross
machine direction stretch at peak load of greater than about 8%
and/or greater than about 10% and/or greater than about 12% as
measured by the Stretch Test Method described herein.
[0049] The embossed multi-ply fibrous structure product may be in
roll form. When in roll form, the embossed multi-ply fibrous
structure product may be convolutely wound about a core or may be
convolutely wound without a core.
[0050] The embossed multi-ply fibrous structure product may have a
basis weight of between about 10 g/m.sup.2 and about 120 g/m.sup.2,
and bulk density of about 0.10 g/cc or less. Preferably, the basis
weight will be below about 60 g/m.sup.2; and the bulk density will
be about 0.07 g/cc or less. Most preferably, the bulk density will
be between about 0.02 g/cc and about 0.07 g/cc as measured by the
Basis Weight Method described herein.
[0051] The embossed multi-ply fibrous structure product may
comprise coloring agents, such as print elements.
[0052] A nonlimiting example of an embossed multi-ply fibrous
structure product in accordance with the present invention is shown
in FIG. 1A. As shown in FIG. 1A, the embossed multi-ply fibrous
structure product 10 comprises a first ply of fibrous structure 12
and a second ply of fibrous structure 14 that are adhesively bonded
together by an adhesive along their adjacent surfaces 16 and 18,
respectively at bond sites 20. The embossed multi-ply fibrous
structure product 10 further comprises embossment sites 22. The
embossment sites 22 exhibit an embossment height a of at least 1000
.mu.m. The embossment sites 22 extend in the y-direction from the
x-plane of the embossed multi-ply fibrous structure product 10. The
embossment sites are not adhesively bonded together and are not
densified. The bond sites 20 are adhesively bonded together by
adhesive 24 and are densified.
[0053] Further, the embossed multi-ply fibrous structure product 10
as shown in FIG. 1A comprises a first face 52 and a second face
54.
[0054] Another embodiment of an embossed multi-ply fibrous
structure product in accordance with the present invention is shown
in FIG. 1B. As shown in FIG. 1B, the embossed multi-ply fibrous
structure product 10 comprises a first ply of fibrous structure 12
and a second ply of fibrous structure 14 that are adhesively bonded
together by an adhesive along their adjacent surfaces 16 and 18,
respectively at bond sites 20. The embossed multi-ply fibrous
structure product 10 further comprises embossment sites 22. The
embossment sites 22 exhibit an embossment height a of at least 1000
.mu.m. The embossment sites 22 extend in the y-direction from the
x-plane of the embossed multi-ply fibrous structure product 10. The
embossment sites are not adhesively bonded together and are not
densified. The bond sites 20 are adhesively bonded together by
adhesive 24 and are densified and plybond strength is
maintained.
[0055] Further, the embossed multi-ply fibrous structure product 10
as shown in FIG. 1B comprises a first face 52 and a second face
54.
[0056] Another embodiment of an embossed multi-ply fibrous
structure product in accordance with the present invention is shown
in FIG. 1C. As shown in FIG. 1C, the embossed multi-ply fibrous
structure product 10 comprises a first ply of fibrous structure 12
and a second ply of fibrous structure 14 that are adhesively bonded
together by an adhesive along their adjacent surfaces 16 and 18,
respectively at bond sites 20. The embossed multi-ply fibrous
structure product 10 further comprises embossment sites 22. The
embossment sites 22 exhibit an embossment height a of at least 1000
.mu.m. The embossment sites 22 extend in the y-direction from the
x-plane of the embossed multi-ply fibrous structure product 10. The
embossment sites are not adhesively bonded together and are not
densified. The bond sites 20 are adhesively bonded together by
adhesive 24 and are densified and plybond strength is
maintained.
[0057] Further, the embossed multi-ply fibrous structure product 10
as shown in FIG. 1C comprises a first face 52 and a second face
54.
[0058] The embossed multi-ply fibrous structure product 10 as shown
in FIGS. 1B and 1C may have been designed to look identical to the
embossed multi-ply fibrous structure product 10 as shown in FIG.
1A. However, during the embossing step of the method of making the
product, the bond sites 20 of the multi-ply fibrous structure from
which the product 10 derives may shift relative to the embossment
sites 22.
Fibrous Structure
[0059] The embossed multi-ply fibrous structure product in
accordance with the present invention may comprise a ply of fibrous
structure selected from the group consisting of: through-air-dried
fibrous structure plies, differential density fibrous structure
plies, wet laid fibrous structure plies, air laid fibrous structure
plies, conventional fibrous structure plies and mixtures thereof.
The embossed multi-ply fibrous structure product may comprise
identical types of plies or mixtures of different types of
plies.
[0060] The fibrous structure may be foreshortened by creping and/or
by wet microcontraction and/or by rush transferring. Alternatively,
the fibrous structure may not be foreshortened.
[0061] The fibrous structure may be pattern densified. A pattern
densified fibrous structure is characterized by having a relatively
high-bulk field of relatively low fiber density and an array of
densified zones of relatively high fiber density. The high-bulk
field is alternatively characterized as a field of pillow regions.
The densified zones are alternatively referred to as knuckle
regions. The densified zones may be discretely spaced within the
high-bulk field or may be interconnected, either fully or
partially, within the high-bulk field. A preferred method of making
a pattern densified fibrous structure and devices used therein are
described in U.S. Pat. Nos. 4,529,480 and 4,528,239.
[0062] The fibrous structure may be uncompacted, non
pattern-densified.
[0063] The fibrous structure may be of a homogenous or multilayered
construction.
[0064] The fibrous structure may be made with a fibrous furnish
that produces a single layer embryonic fibrous web or a fibrous
furnish that produces a multi-layer embryonic fibrous web.
Ingredients
[0065] The fibrous structures and/or embossed multi-ply fibrous
structure product made therefrom may comprise one or more
ingredients, such as softening agents, absorbency agents such as
surfactants, wet strength agents, lotions, antibacterial agents,
coloring agents, perfumes.
Methods for Making Embossed Multi-ply Fibrous Structure Product
[0066] The embossed multi-ply fibrous structure product of the
present invention may be made by the following nonlimiting
example.
[0067] As shown in FIGS. 2 and 3, a first ply of fibrous structure
12 contacts knob surfaces 42 of a first embossing roll 26, such as
an engraved steel embossing roll. An applicator roll 28 for
applying an adhesive 24 applies the adhesive 24 to the first ply of
fibrous structure 12 where the fibrous structure ply 12 is
supported by the knob surfaces 42. The adhesive 24 may be applied
to the fibrous structure ply 12 in a pattern of discrete dots 50 to
produce an adhesive-containing fibrous structure 12' as shown in
FIG. 4. The adhesive 24 may be applied to the applicator roll 28 by
a gravure system, preferably an offset gravure system comprising a
gravure roll 30. The gravure system can meter a specified amount of
adhesive 24 from an adhesive pan (not shown) onto the applicator
roll 28. Other suitable means of applying the adhesive 24 are known
to those of ordinary skill in the art. The adhesive 24 may be any
suitable adhesive known in the art. Preferably, the adhesive 24
comprises polyvinyl alcohol.
[0068] The first ply of fibrous structure 12 may be under tension
suitable for controlling the first ply at some point during its
contact with the first embossing roll 26.
[0069] A second ply of fibrous structure 14 is brought into contact
with the adhesive 24 present on the first ply of fibrous structure
12' at a nip between the first embossing roll 26 and a marrying
roll 32. The first ply and second ply are bonded together (i.e.,
combined) into a multi-ply fibrous structure 48. The marrying roll
32 may be a solid marrying roll, i.e., smooth surface marrying
roll.
[0070] The marrying roll 32 applies pressure to the multi-ply
fibrous structure 48 and the adhesive 24 is pressed between the two
plies of fibrous structure at the bond sites 20 where the first ply
of fibrous structure 12' is supported by knob surfaces 42. This
action bonds the two plies together and produces a plybond strength
of at least about 4 g/in. At this point, the multi-ply fibrous
structure 48 has not yet been embossed.
[0071] Next, the multi-ply fibrous structure 48 enters the
interface between the first embossing roll 26 with its depressions
44 and a second embossing roll 34 with its protuberances 46. The
second embossing roll 34 may be a steel embossing roll. The
protuberances 46 of the second embossing roll 34 and the
depressions 44 of the first embossing roll 26 are aligned such that
the protuberances 46 nest within the depressions 44. The
protuberances 46 are engaged into the depressions 44 at a length of
at least about 50 mils such that an embossed height of at least
1000 .mu.m is formed in the multi-ply fibrous structure 48. The
embossed multi-ply fibrous structure 10 product exits the nip
between the first embossing roll 26 and the second embossing roll
34.
[0072] The bond sites 20 are densified at the nip between the first
embossing roll 26 and the marrying roll 32 and/or at the interface
between the first embossing roll 26 and the second embossing roll
34.
[0073] The embossment sites 16 which result from the protuberances
46 of the second embossing roll 34 engaging the depressions 44 of
the first embossing roll 26 are non-densified.
[0074] Web handling rolls 36, 38 and 40 may be used to control
and/or advance the fibrous structures 12 and 14 and/or multi-ply
fibrous structure product 10.
[0075] Preferred rotational direction of the rolls used in this
method are represented by arrows associated with the rolls.
[0076] It is desirable that rolls 26, 28, 32 and 34 run at the same
speed. Web handling rolls 36, 38 and 40 do not have to run at the
same speed as rolls 26, 28, 32 and 34.
[0077] Preferred machine direction of the fibrous structures 12 and
14 and/or multi-ply fibrous structure product 10 are represented by
arrows associated with the fibrous structures 12 and 14 and/or
multi-ply fibrous structure product 10.
Test Methods:
Effective Caliper Test
[0078] Effective caliper of a fibrous structure in roll form is
determined by the following equation:
EC=(RD.sup.2-CD.sup.2)/(0.00127.times.SC.times.SL) wherein EC is
effective caliper in mils of a single sheet in a wound roll of
fibrous structure; RD is roll diameter in inches; CD is core
diameter in inches; SC is sheet count; and SL is sheet length in
inches. Plybond Strength Test Method
[0079] Plybond strength is measured according to the following test
method.
[0080] From a single multi-ply fibrous structure comprising an
adhesive that bonds two or more of the plies together cut four (4)
3''.times.8.2'' (76.2 mm.times.208.3 mm) continuous (i.e.,
non-perforated) fibrous structure sample strips conditioned with
all wrapping and/or packaging materials removed, if necessary, at a
temperature of 73.degree. F..+-.2.degree. F. (about 23.degree.
C..+-.1.degree. C.) and a relative humidity of 50%.+-.2% for two
(2) hours. This test method measures the plybond strength between
two adjacent plies of the fibrous structure.
[0081] The fibrous structure sample strips are prepared by using a
cutting die [3''.times.11''(76.2 mm.times.279.4 mm)] on a plywood
base, commercially available from Acme Steel Rule Corp., 5 Stevens
St., Waterbury, Conn. 06714. The cutting die must be modified with
a soft foam rubber insert material. A JDC Cutter 3'' (76.2 mm),
Model #JDC-3-12 Precision Sample Cutter, Thwing-Albert Instrument
Company, 10960 Dutton Road, Philadelphia, Pa. 19154, having a side
capacity to cut 3''.times.8.2'' (76.2 mm.times.208.3 mm) fibrous
structure sample strips is used to cut the fibrous structure
samples. The 3'' (76.2 mm) wide strip are cut from the center of
the fibrous structure. The strips are cut in the MD direction of
the fibrous structure. If the fibrous structure is in roll form,
cut the samples from greater than 40'' (1016 mm) from the ends of
the roll.
[0082] Individually take each sample strip and gently manually
initiate ply separation along the MD direction and continuing for
2'' (50 mm).
[0083] Do not use samples that contain obvious defects, such as
wrinkles, creases, tears, holes, etc.
[0084] The measuring of the samples and the preparation of the
samples should all occur in a conditioned environment at a
temperature of 73.degree. F..+-.2.degree. F. (about 23.degree.
C..+-.1.degree. C.) and a relative humidity of 50%.+-.2%.
[0085] A Thwing-Albert EJA or Intelect-II-STD, Cat. No. 1451-24PG;
Thwing-Albert Instrument Company tensile tester is used to measure
the plybond strength of the samples. The tensile tester has general
purpose air-operated grips (Cat. No. 734K) with 1''.times.3'' (25.4
mm.times.76.2 mm) inserts. The load cell of the tensile tester is
5000 g. The Sample Size Setting (Load Divider) is set to 3. The
tensile tester is operated as follows: [0086] 1. Place one of the
separated plies of the prepared sample strip in the top grid of the
tensile tester. The other ply is placed in the bottom grid. The
sample strip needs to be centered in the grips and straight. [0087]
2. Activate the tensile tester. When the test is complete, record
the value for the load mean. Remove the sample strip from the grips
and discard. Check the load cell for a zero reading. [0088] 3.
Repeat steps 1 and 2 for each sample strip.
[0089] The tensile tester will display a value for load mean in
g/in (g/25.4 mm). Take the average of four (4) sample strips to
obtain the plybond strength of the fibrous structure.
Bond Area Test Method
[0090] Bond area is a measurement that a manufacturer of a fibrous
structure knows before the fibrous structure is produced. It
represents the surface area of adjacent surfaces of two or more
plies of fibrous structure that are bonded together by an adhesive.
Most typically, the adhesive is applied only to the tips of the
embossing knobs of an embossing roll. This area is known from the
manufacturer of the embossing rolls, from which the manufacturer of
the fibrous structure can obtain such bond area measurement.
[0091] Additionally, the bond area can be measured by taking a
sample of fibrous structure that comprises an adhesive comprising
polyvinyl alcohol as the only adhesive, rather than a non-polyvinyl
alcohol-containing adhesive. Accordingly, if a fibrous structure
typically is made with a non-polyvinyl alcohol-containing adhesive,
the maker of such a fibrous structure will need to replace its
non-polyvinyl alcohol-containing adhesive with an adhesive
comprising polyvinyl alcohol. The maker will then produce its
fibrous structure in the identical manner as it does when making
its non-polyvinyl alcohol-containing fibrous structure.
[0092] Next, the sample of fibrous structure comprising the
adhesive comprising polyvinyl alcohol is subjected to an 8:1 ratio
by volume of boric acid solution to iodine solution mixture. The
boric acid solution is a 4% boric acid solution in deionized water.
The iodine solution is a 0.1 N iodine solution in deionized water.
The mixture is sprayed onto the sample. The polyvinyl alcohol in
the adhesive will turn bluish green. The resulting image can be
analyzed for % bond area (i.e., adhesive area coverage) using
standard image analysis techniques.
[0093] Also, the bond area of a sample of fibrous structure that
comprises a non-polyvinyl alcohol-containing adhesive as the only
adhesive can be measured by subjecting such a sample to a method
that identifies the area of the fibrous structure sample that
comprises the non-polyvinyl alcohol-containing adhesive. For
example, by subjecting the fibrous structure sample to a condition,
such as a chemical agent, that colorizes the non-polyvinyl
alcohol-containing adhesive making it readily visible for image
analysis techniques. Another example includes subjecting the
fibrous structure sample to a condition, such as a chemical agent,
that colorizes everything but the non-polyvinyl alcohol-containing
adhesive making the adhesive readily visible for image analysis
techniques.
[0094] If any one of these techniques identifies a fibrous
structure sample as comprising a bond area of from about 0.1% to
about 30% of the surface area of the adjacent surfaces of the two
or more plies, then the fibrous structure satisfies the bond area
aspect of the present invention.
Embossment Height Test Method
[0095] Embossment height is measured using a GFM Primos Optical
Profiler instrument commercially available from GFMesstechnik GmbH,
Warthestra.beta.e 21, D14513 Teltow/Berlin, Germany. The GFM Primos
Optical Profiler instrument includes a compact optical measuring
sensor based on the digital micro mirror projection, consisting of
the following main components: a) DMD projector with 1024.times.768
direct digital controlled micro mirrors, b) CCD camera with high
resolution (1300.times.1000 pixels), c) projection optics adapted
to a measuring area of at least 27.times.22 mm, and d) recording
optics adapted to a measuring area of at least 27.times.22 mm; a
table tripod based on a small hard stone plate; a cold light
source; a measuring, control, and evaluation computer; measuring,
control, and evaluation software ODSCAD 4.0, English version; and
adjusting probes for lateral (x-y) and vertical (z)
calibration.
[0096] The GFM Primos Optical Profiler system measures the surface
height of a sample using the digital micro-mirror pattern
projection technique. The result of the analysis is a map of
surface height (z) vs. xy displacement. The system has a field of
view of 27.times.22 mm with a resolution of 21 microns. The height
resolution should be set to between 0.10 and 1.00 micron. The
height range is 64,000 times the resolution.
[0097] To measure a fibrous structure sample do the following:
[0098] 1. Turn on the cold light source. The settings on the cold
light source should be 4 and C, which should give a reading of
3000K on the display; [0099] 2. Turn on the computer, monitor and
printer and open the ODSCAD 4.0 Primos Software. [0100] 3. Select
"Start Measurement" icon from the Primos taskbar and then click the
"Live Pic" button. [0101] 4. Place a 30 mm by 30 mm sample of
fibrous structure product conditioned at a temperature of
73.degree. F..+-.2.degree. F. (about 23.degree. C..+-.1.degree. C.)
and a relative humidity of 50%.+-.2% under the projection head and
adjust the distance for best focus. [0102] 5. Click the "Pattern"
button repeatedly to project one of several focusing patterns to
aid in achieving the best focus (the software cross hair should
align with the projected cross hair when optimal focus is
achieved). Position the projection head to be normal to the sample
surface. [0103] 6. Adjust image brightness by changing the aperture
on the lens through the hole in the side of the projector head
and/or altering the camera "gain" setting on the screen. Do not set
the gain higher than 7 to control the amount of electronic noise.
When the illumination is optimum, the red circle at bottom of the
screen labeled "I.O." will turn green. [0104] 7. Select Technical
Surface/Rough measurement type. [0105] 8. Click on the "Measure"
button. This will freeze on the live image on the screen and,
simultaneously, the image will be captured and digitized. It is
important to keep the sample still during this time to avoid
blurring of the captured image. The image will be captured in
approximately 20 seconds. [0106] 9. If the image is satisfactory,
save the image to a computer file with ".omc" extension. This will
also save the camera image file ".kam". [0107] 10. To move the date
into the analysis portion of the software, click on the
clipboard/man icon. [0108] 11. Now, click on the icon "Draw Cutting
Lines". Make sure active line is set to line 1. Move the cross
hairs to the lowest point on the left side of the computer screen
image and click the mouse. Then move the cross hairs to the lowest
point on the right side of the computer screen image on the current
line and click the mouse. Now click on "Align" by marked points
icon. Now click the mouse on the lowest point on this line, and
then click the mouse on the highest point on this line. Click the
"Vertical" distance icon. Record the distance measurement. Now
increase the active line to the next line, and repeat the previous
steps, do this until all lines have been measured (six (6) lines in
total. Take the average of all recorded numbers, and if the units
is not micrometers, convert it to micrometers (.mu.m). This number
is the embossment height. Repeat this procedure for another image
in the fibrous structure product sample and take the average of the
embossment heights. Wet Burst Strength Test Method
[0109] Wet burst strength may be measured using a Thwing-Albert
Burst Tester Cat. No. 177 equipped with a 2000 g load cell
commercially available from Thwing-Albert Instrument Company,
Philadelphia, Pa.
[0110] Wet burst strength is measured by taking two (2) multi-ply
fibrous structure product samples. Using scissors, cut the samples
in half in the MD so that they are approximately 228 mm in the
machine direction and approximately 114 mm in the cross machine
direction, each two (2) plies thick (you now have 4 samples).
First, condition the samples for two (2) hours at a temperature of
73.degree. F..+-.2.degree. F. (about 23.degree. C..+-.1.degree. C.)
and a relative humidity of 50%.+-.2%. Next age the samples by
stacking the samples together with a small paper clip and "fan" the
other end of the stack of samples by a clamp in a 105.degree. C.
(.+-.1.degree. C.) forced draft oven for 5 minutes (.+-.10
seconds). After the heating period, remove the sample stack from
the oven and cool for a minimum of three (3) minutes before
testing. Take one sample strip, holding the sample by the narrow
cross machine direction edges, dipping the center of the sample
into a pan filled with about 25 mm of distilled water. Leave the
sample in the water four (4) (.+-.0.5) seconds. Remove and drain
for three (3) (.+-.0.5) seconds holding the sample so the water
runs off in the cross machine direction. Proceed with the test
immediately after the drain step. Place the wet sample on the lower
ring of a sample holding device of the Burst Tester with the outer
surface of the sample facing up so that the wet part of the sample
completely covers the open surface of the sample holding ring. If
wrinkles are present, discard the samples and repeat with a new
sample. After the sample is properly in place on the lower sample
holding ring, turn the switch that lowers the upper ring on the
Burst Tester. The sample to be tested is now securely gripped in
the sample holding unit. Start the burst test immediately at this
point by pressing the start button on the Burst Tester. A plunger
will begin to rise toward the wet surface of the sample. At the
point when the sample tears or ruptures, report the maximum
reading. The plunger will automatically reverse and return to its
original starting position. Repeat this procedure on three (3) more
samples for a total of four (4) tests, i.e., four (4) replicates.
Report the results as an average of the four (4) replicates, to the
nearest g.
Sheet Caliper Test Method
[0111] Sheet Caliper or Caliper of a sample of fibrous structure
product is determined by cutting a sample of the fibrous structure
product such that it is larger in size than a load foot loading
surface where the load foot loading surface has a circular surface
area of about 3.14 in.sup.2. The sample is confined between a
horizontal flat surface and the load foot loading surface. The load
foot loading surface applies a confining pressure to the sample of
14.7 g/cm.sup.2 (about 0.21 psi). The caliper is the resulting gap
between the flat surface and the load foot loading surface. Such
measurements can be obtained on a VIR Electronic Thickness Tester
Model II available from Thwing-Albert Instrument Company,
Philadelphia, Pa. The caliper measurement is repeated and recorded
at least five (5) times so that an average caliper can be
calculated. The result is reported in mils.
Stretch Test Method
[0112] Stretch is measured by providing one (1) inch by five (5)
inch (2.5 cm.times.12.7 cm) strips of fibrous structure. Each strip
is placed on an electronic tensile tester Model 1122 commercially
available from Instron Corp., Canton, Mass. in a conditioned room
at a temperature of 73.degree. F..+-.2.degree. F. (about 23.degree.
C..+-.1.degree. C.) and a relative humidity of 50%.+-.2%. The
crosshead speed of the tensile tester is 2.0 inches per minute
(about 5.1 cm/minute) and the gauge length is 4.0 inches (about
10.2 cm). The Stretch at Peak Load is measured.
[0113] All documents cited in the Detailed Description of the
Invention are, in relevant part, incorporated by reference herein;
the citation of any document is not to be construed as an admission
that it is prior art with respect to the present invention. To the
extent that any meaning or definition of the term in this written
document conflicts with any meaning or definition of the term in a
document incorporated by reference, the meaning or definition
assigned to the term in this written document shall govern.
[0114] While particular embodiments of the present invention have
been illustrated and described, it would be obvious to those
skilled in the art that various other changes and modifications can
be made without departing from the spirit and scope of the
invention. It is therefore intended to cover in the appended claims
all such changes and modifications that are within the scope of
this invention.
* * * * *