U.S. patent application number 11/215451 was filed with the patent office on 2006-01-05 for systems and apparatus for atomic-layer deposition.
This patent application is currently assigned to Micron Technology, Inc.. Invention is credited to Kie Y. Ahn, Leonard Forbes.
Application Number | 20060000412 11/215451 |
Document ID | / |
Family ID | 29269052 |
Filed Date | 2006-01-05 |
United States Patent
Application |
20060000412 |
Kind Code |
A1 |
Ahn; Kie Y. ; et
al. |
January 5, 2006 |
Systems and apparatus for atomic-layer deposition
Abstract
The present inventors devised unique atomic-layer deposition
systems, methods, and apparatus suitable for aluminum-oxide
deposition. One exemplary method entails providing an outer chamber
enclosing a substrate, forming an inner chamber within the outer
chamber, and introducing an oxidant into the inner chamber, and
introducing an aluminum precursor into the inner chamber. The inner
chamber has a smaller volume than the outer chamber, which
ultimately requires less time to fill and purge and thus promises
to reduce cycle times for deposition of materials, such as aluminum
oxide.
Inventors: |
Ahn; Kie Y.; (Chappaqua,
NY) ; Forbes; Leonard; (Corvallis, OR) |
Correspondence
Address: |
SCHWEGMAN, LUNDBERG, WOESSNER & KLUTH
1600 TCF TOWER
121 SOUTH EIGHT STREET
MINNEAPOLIS
MN
55402
US
|
Assignee: |
Micron Technology, Inc.
|
Family ID: |
29269052 |
Appl. No.: |
11/215451 |
Filed: |
August 29, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10137168 |
May 2, 2002 |
|
|
|
11215451 |
Aug 29, 2005 |
|
|
|
Current U.S.
Class: |
118/715 |
Current CPC
Class: |
C23C 16/45544 20130101;
C23C 16/45574 20130101; C23C 16/45565 20130101; C23C 16/4412
20130101 |
Class at
Publication: |
118/715 |
International
Class: |
C23C 16/00 20060101
C23C016/00 |
Claims
1. An atomic-layer deposition system comprising: a chamber; and a
gas-distribution fixture in the chamber, the fixture including a
gas-distribution surface having a first plurality of holes and a
second plurality of holes and a gas-confinement member extending
from the gas-distribution surface around the first and second
plurality of holes, wherein the first and second pluralities of
holes are isolated from each other such that gases that flow into
the first and second pluralities of holes do not mix inside the
gas-distribution fixture.
2. The atomic-layer deposition system of claim 1, wherein the
gas-confinement member surrounds all the holes.
3. The atomic-layer deposition system of claim 1, wherein the
gas-confinement member consists essentially of a material different
from that of the gas-distribution surface.
4. The atomic-layer deposition system of claim 1, wherein the
gas-distribution surface is substantially planar and includes
silicon and silicon oxide.
5. The atomic-layer deposition system of claim 1, wherein the
atomic-layer deposition system includes an RF source coupled to
wafer holder.
6. The atomic-layer deposition system of claim 1, wherein the
atomic-layer deposition system includes: a wafer holder having a
wafer-support surface confronting the gas-distribution surface; a
first source to couple a precursor to the first plurality of holes
in the gas-distribution fixture; and a second source to couple an
oxidant to the second plurality of holes in the gas-distribution
fixture.
7. The atomic-layer deposition system of claim 6, wherein the
gas-confinement member extends perpendicularly from the
gas-distribution surface toward the wafer-support surface.
8. The atomic-layer deposition system of claim 6, wherein the
wafer-support surface is substantially parallel to the
gas-distribution surface.
9. The atomic-layer deposition system of claim 6, wherein the first
source includes trimethylaluminum as the precursor and the second
source includes water as the oxidant.
10. An atomic-layer deposition system comprising: a chamber; a
gas-distribution fixture in the chamber, the fixture including: a
gas-distribution member including: a plurality of first channels
and a plurality of second channels; and a gas-distribution surface
having a plurality of first holes and a plurality of second holes,
with each of the first holes in fluid communication with at least
one of the first channels and each of the second holes in fluid
communication with at least one the second channels, the plurality
of first holes isolated from the plurality of second holes such
that gases that flow into the plurality of first holes and the
plurality of second holes do not mix inside the gas-distribution
fixture; and a gas-confinement member within the first chamber and
extending around the plurality of first holes and the plurality of
second holes; a wafer holder having a wafer-support surface
confronting the first and second holes; a first source to couple a
precursor to the plurality of first channels; and a second source
to couple an oxidant to the plurality of second holes.
11. The atomic-layer deposition system of claim 10, wherein the
gas-confinement member extends perpendicularly relative to the
gas-distribution surface.
12. The atomic-layer deposition system of claim 10, wherein the
gas-confinement member surrounds all the holes.
13. The atomic-layer deposition system of claim 10, wherein the
gas-confinement member consists essentially of a material different
from that of the gas-distribution surface.
14. The atomic-layer deposition system of claim 10, wherein the
gas-distribution surface is substantially planar and includes
silicon.
15. The atomic-layer deposition system of claim 10, wherein the
first source includes trimethylaluminum as the precursor and the
second source includes water as the oxidant.
16. An atomic-layer deposition system comprising: a first chamber
for confining gases; a second chamber within the first chamber for
at least partially containing a substrate during deposition; and a
gas-distribution fixture in the second chamber, the fixture
including a gas-distribution surface having a first plurality of
holes and a second plurality of holes and a gas-confinement member
extending from the gas-distribution surface around the first and
second plurality of holes, wherein the first and second pluralities
of holes are isolated from each other such that gases that flow
into the first and second pluralities of holes do not mix inside
the gas-distribution fixture.
17. The atomic-layer deposition system of claim 16, wherein the
first chamber is a right cylindrical chamber.
18. The atomic-layer deposition system of claim 16, wherein the
second chamber includes a surface of a substrate-support
structure.
19. The atomic-layer deposition system of claim 16, wherein
atomic-layer deposition system includes a supply essentially of
trimethylaluminum coupled to the second chamber and a supply
essentially of water coupled to the second chamber.
20. An atomic-layer deposition system comprising: a first chamber
having an interior sidewall; and a second chamber within the first
chamber, the second chamber including: a gas-distribution fixture
in the second chamber including a gas-distribution member having a
first plurality of holes and a second plurality of holes that
define a gas-distribution surface, wherein the first and second
pluralities of holes are isolated from each other such that gases
that flow into the first and second pluralities of holes do not mix
inside the gas-distribution fixture; a gas-confinement surface at
least partly encircling the plurality of holes, the gas-confinement
surface spaced from the interior sidewall of the first chamber and
nonparallel to the gas-distribution surface; and a wafer-support
surface confronting the gas-distribution surface.
21. The atomic-layer deposition system of claim 20, wherein the
gas-confinement surface is substantially perpendicular to the
gas-distribution surface.
22. The atomic-layer deposition system of claim 20, wherein the
wafer support surface is substantially parallel to the
gas-distribution surface.
23. The atomic-layer deposition system of claim 20, wherein the
gas-confinement surface consists essentially of a material
different from that of the gas-distribution surface.
24. The atomic-layer deposition system of claim 20, wherein the
gas-distribution surface is substantially planar and includes
silicon.
25. The atomic-layer deposition system of claim 20, wherein the
atomic-layer deposition system includes: a first source to couple
an aluminum precursor to the second chamber; and a second source to
couple an oxidant to the second chamber.
26. An atomic-layer deposition system comprising: a first chamber
having an interior sidewall; a second chamber within the first
chamber, the second chamber including: a gas-distribution fixture
in the second chamber including a gas-distribution member having a
first plurality of holes and a second plurality of holes that
define a gas-distribution surface, wherein the first and second
pluralities of holes are isolated from each other such that gases
that flow into the first and second pluralities of holes do not mix
inside the gas-distribution fixture; a gas-confinement wall at
least partly encircling the plurality of holes, the gas-confinement
wall spaced from the interior sidewall of the first chamber and
nonparallel to the gas-distribution surface; and a wafer-support
surface confronting the gas-distribution surface; a first source to
couple a precursor to the second chamber; and a second source to
couple an oxidant to the second chamber.
27. The atomic-layer deposition system of claim 26, wherein the
wafer-support surface contacts the gas-confinement wall.
28. The atomic-layer deposition system of claim 26, wherein the
gas-confinement wall is substantially perpendicular to the
gas-distribution surface and the wafer-support surface.
29. The atomic-layer deposition system of claim 26, wherein the
wall has a uniform height measured from the gas-distribution
surface.
30. The atomic-layer deposition system of claim 26, wherein the
wall consists essentially of a stainless steel.
31. The atomic-layer deposition system of claim 26, wherein the
atomic-layer deposition system includes a first plurality of
channels in fluid communication with a first subset of the holes
and second plurality of channels in fluid communication with a
second subset of the holes.
32. The atomic-layer deposition system of claim 26, wherein the
first source includes trimethylaluminum as the precursor and the
second source includes water as the oxidant.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application is a divisional of U.S. application
Ser. No. 10/137,168, filed May 2, 2002, which is incorporated
herein by reference in its entirety.
TECHNICAL FIELD
[0002] This invention concerns methods of making integrated
circuits, particularly layer formation techniques, such as
chemical-vapor deposition and atomic-layer deposition.
BACKGROUND OF INVENTION
[0003] Integrated circuits, the key components in thousands of
electronic and computer products, are interconnected networks of
electrical components fabricated on a common foundation, or
substrate. Fabricators generally build these circuits layer by
layer, using techniques, such as deposition, doping, masking, and
etching, to form and interconnect thousands and even millions of
microscopic transistors, resistors, and other electrical components
on a silicon substrate, known as a wafer.
[0004] One common technique for forming layers in an integrated
circuit is called chemical vapor deposition. Chemical vapor
deposition generally entails placing a substrate in a reaction
chamber, heating the substrate to prescribed temperatures, and
introducing one or more gases, known as precursor gases, into the
chamber to begin a deposition cycle. The precursor gases enter the
chamber through a gas-distribution fixture, such as a gas ring or a
showerhead, one or more centimeters above the substrate, and
descend toward the heated substrate. The gases react with each
other and/or the heated substrate, blanketing its surface with a
layer of material. An exhaust system then pumps gaseous by-products
or leftovers from the reaction out of the chamber through a
separate outlet to complete the deposition cycle.
[0005] Conventional chemical-vapor-deposition (CVD) systems suffer
from at least two problems. First, conventional CVD systems
generally form non-uniformly thick layers that include microscopic
hills and valleys, and thus generally require use of
post-deposition planarization or other compensation techniques.
Second, it is difficult, if not impossible, for CVD to provide
uniform coverage of trench sidewalls or complete filling of holes
and trenches.
[0006] To address these shortcomings, fabricators have developed
atomic-layer deposition (ALD), a special form of CVD that allows
highly uniform formation of ultra-thin layers having thicknesses of
one molecule or several atoms of the deposited material. Though
similar to CVD in terms of equipment and process flow, ALD relies
on adsorption of some of the reactants into exposed surfaces, and
thus provides coverage and fill of structural features that are
difficult, if not impossible, using CVD.
[0007] In recent years, researchers and engineers have made strides
toward making ALD commercially viable for some applications. For
example, one team of researchers reportedly optimized an ALD
process for depositing an aluminum oxide (AlO.sub.x) film in
thin-film heads--devices used to read and write magnetic data. See,
Paranjpe et al., Atomic Layer Deposition of AlO.sub.x for Thin Film
Head Gap Applications, Journal of Electrochemical Society, 148 (9),
pp. G465-G471 (2001), which is incorporated herein by
reference.
[0008] However, the present inventors have recognized that the
equipment and processes reported as optimal for thin-film head
applications suffer from some limitations relative to use in
fabricating integrated circuits. For example, the reported process
deposits material at the slow rate of less than one Angstrom per
cycle, suggesting that more than 50 cycles would be necessary to
form a 50-Angstrom-thick layer. Moreover, the reported equipment
uses a larger than desirable reaction chamber, which takes longer
to fill up or pump out, and thus prolongs the duration of each
deposition cycle.
[0009] Accordingly, there is a need for better systems and methods
of atomic-layer deposition of aluminum oxides as well as other
material compositions.
SUMMARY OF SELECTED EMBODIMENT(S)
[0010] To address these and/or other problems, the present inventor
devised new systems, methods, and apparatuses for atomic layer
deposition. One exemplary atomic-layer deposition system, well
suited for aluminum-oxide depositions in integrated-circuit
fabrication, includes an outer chamber, a substrate holder, and a
unique gas-distribution fixture. The fixture includes a
gas-distribution surface having two sets of holes and a
gas-confinement member that forms a wall around the holes. In
operation, one set of holes dispenses an aluminum-carrying
precursor and the other dispenses an oxidizing agent gas, after the
gas-confinement member engages, or otherwise cooperates with the
substrate holder to form an inner chamber within the outer
chamber.
[0011] The inner chamber has a smaller volume than the outer
chamber and thus consumes less gas during the deposition process
than would the outer chamber used alone. Also, the smaller chamber
volume allows the exhaust system to pump the chamber more quickly,
thus allowing shorter ALD cycles and potentially increasing rates
of production.
[0012] These and other embodiments, aspects, advantages, and
features of the present invention are set forth in part in the
description and claims which follow, and in part will become
apparent to those skilled in the art by reference to the following
description of the invention and referenced drawings or by practice
of the invention. The aspects, advantages, and features of the
invention are realized and attained by means of the
instrumentalities, procedures, and combinations particularly
pointed out in the appended claims.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] FIG. 1 is a side view of an exemplary deposition reactor
according to the invention;
[0014] FIG. 2 is a plan view of an exemplary gas-distribution
fixture according to the invention; and
[0015] FIG. 3 is a flowchart showing an exemplary method according
to the invention.
DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS
[0016] The following detailed description, which references and
incorporates the above-identified figures, describes and
illustrates one or more specific embodiments of the invention.
These embodiments, offered not to limit but only to exemplify and
teach the invention, are shown and described in sufficient detail
to enable those skilled in the art to make and use the invention.
Thus, where appropriate to avoid obscuring the invention, the
description may omit certain information known to those of skill in
the art.
[0017] FIG. 1 shows an exemplary atomic-layer-deposition system 100
which incorporates teachings of the present invention. In
particular, system 100 includes a chamber 110, a wafer holder 120,
a gas-distribution fixture (or showerhead) 130, a gas-supply system
140, and exhaust pumps 150 and 160.
[0018] More particularly, chamber 110 includes respective top and
bottom plates 112 and 114 and a sidewall 116. In the exemplary
embodiment, chamber 110 is a cylindrical structure formed of
stainless steel or glass. However, other embodiments use different
structures and materials. Bottom plate 114 includes an opening
114A. Extending through opening 114A is a stem portion 122 of wafer
holder 120.
[0019] Wafer holder 120 also includes a support platform 124, one
or more heating elements 126, one or more temperature sensors 128,
and an RF source 129. Holder 120 (also called a chuck) raises and
rotates manually or automatically via lift and rotation devices,
and is coupled to a power supply and temperature control circuitry
(all of which are not shown). Support platform 124 supports one or
more substrates, wafers, or integrated-circuit assemblies 200.
Substrate 200 has an exemplary width or diameter of about 30
centimeters and an exemplary thickness in the range of 850-1000
microns. (The term "substrate," as used herein, encompasses a
semiconductor wafer as well as structures having one or more
insulative, conductive, or semiconductive layers and materials.
Thus, for example, the term embraces silicon-on-insulator,
silicon-on-sapphire, and other advanced structures.)
[0020] Heating elements 126 and temperature sensors 128 are used
for heating substrates 200 to a desired temperature. Radio
Frequency (RF) source 129, for example, a
1.25-kilowatt-13.56-megahertz RF generator, is used to generate and
sustain a capacitively coupled plasma between the wafer holder and
gas-distribution fixture 130. (Some embodiments use generators with
smaller or larger capacities.)
[0021] Fixture 130, positioned above wafer holder 120 and substrate
200, includes a gas-distribution member 132, a surface-projection
(or gas-confinement) member 134, and gas inlets 136 and 137. In the
exemplary embodiment, fixture 130 has three operating positions
138A, 138B, and 138C relative support platform 124. Fixture 130
takes operating position 138A, before and after depositions and
operating position 138B during depositions. Position 138C is taken
during a plasma anneal to ensure stability of the plasma.
[0022] Gas-distribution member 132 includes main gas inputs 132A
and 132B, gas-distribution channels 132D and 132F, and
gas-distribution holes 132E and 132G. Main gas inputs 132A and 132B
feed respective gas-distribution channels 132D and 132F, which in
turn feed respective gas-distribution holes 132E and 132G. (Holes
132E and 132G are actually interleaved in the exemplary embodiment,
though shown simply in the figure as spatially segregated groups.)
Holes 132D and 132F define a gas-distribution surface 132C.
[0023] In the exemplary embodiment, holes 132D and 132F are
substantially circular with a common diameter in the range of 15-20
microns; gas-distribution channels 132D and 132F have a common
width in the range of 20-45 microns; and surface 132C is
substantially planar and parallel to platform 124 of wafer holder
120. However, other embodiments use other surface forms as well as
shapes and sizes of holes and channels.
[0024] Extending from gas-distribution surface 132C is
surface-projection member (or collar) 134. Member 134 projects or
extends from surface 132C toward support platform 124, defining a
fixture cavity 134A. The exemplary embodiment forms
surface-projection member 134 from stainless steel as a uniform
annular or circular wall or collar that projects perpendicularly
from surface 132C to define a right-cylindrical cavity.
[0025] However, other embodiments form member 134 to project at
other angles relative surface 132C. For example, some form the
projection at an acute or obtuse angle, such as 45 or 135 degrees,
and others form the projection to peripherally define an oval,
ellipse, triangle, square, or any desirable regular or irregular
polygon. Thus, the present invention encompasses a wide variety of
projection shapes and configurations, indeed any projection shape
that facilitates definition of an effective cavity or
gas-confinement volume in cooperation with wafer holder 120 and/or
substrate 200.
[0026] FIG. 2, a plan view, shows further details of the exemplary
embodiment of gas-distribution fixture 130. In particular, the plan
view shows not only exemplary circular peripheries of
gas-distribution member 132 and surface-projection member 134, but
also an exemplary interleaved distribution pattern for holes 132E
and 132G, and an exemplary orthogonal arrangement of
gas-distribution channels 132D and 132F. (Holes 132E are shown
darkly shaded to distinguish them from holes 132G, which are
cross-hatched.)
[0027] Other embodiments use other hole distribution patterns and
channel arrangements. For example, some embodiments include random
or concentric hole patterns and various channel geometries,
including concentric circles, rectangles, or other regular or
irregular concentric polygons. Some embodiments may also dedicate
various subsets of channels and corresponding holes to different
gases. For example, one embodiment provides one set of holes and
channels for approximately uniform distribution of a gas or vapor,
such as TMA precursor and argon carrier gas mixture, and another
set of holes and channels for approximately uniform distribution of
a gas or vapor, such as a water-argon mixture.
[0028] Gas-distribution member 132 can be made in a number of ways.
One exemplary method entails laminating several material layers,
with each layer including holes and/or channels to effect
distribution of the gases to the separate holes. If the layers are
made of silicon, the material layers can be patterned and etched,
for example, using conventional photolithographic or
micro-electro-mechanical systems (MEMS) technology, to form holes
and channels. Dry-etching techniques produce small openings and
channels, while wet etching produces larger openings and channels.
For further details, see, for example, M. Engelhardt, "Modern
Application of Plasma Etching and Patterning in Silicon Process
Technology," Contrib. Plasma Physics, vol. 39, no. 5, pp. 473-478
(1999). Also see co-pending and co-assigned U.S. patent application
Ser. No. 09/797,324 (docket 303.717US1 and 00-0264), which was
filed on Mar. 1, 2001 and which is incorporated herein by
reference.
[0029] The processed layers can then be bonded together with the
holes and channels in appropriate alignment using known
wafer-bonding techniques. See, for example, G. Krauter et al.,
"Room Temperature Silicon Wafer Bonding with Ultra-Thin Polymer
Films," Advanced Materials, vol. 9, no. 5, pp. 417-420 (1997); C.
E. Hunt et al., "Direct Bonding of Micromachined Silicon Wafers for
Laser Diode Heat Exchanger Applications," Journal of Micromechan.
Microeng, vol. 1, pp. 152-156 (1991); Zucker, O. et al.,
"Applications of oxygen plasma processing to silicon direct
bonding," Sensors and Actuators, A. Physical, vol. 36, no. 3, pp.
227-231 (1993), which are all incorporated herein by reference. See
also, co-pending and co-assigned U.S. patent application Ser. No.
09/189,276 (dockets 303.534US1 and 97-1468) entitled "Low
Temperature Silicon Wafer Bond Process with Bulk Material Bond
Strength," which was filed Nov. 10, 1998 and which is also
incorporated herein by reference. The resulting bonded structure is
then passivated using thermal oxidation for example.
[0030] For an alternative fixture structure and manufacturing
method that can be combined with those of the exemplary embodiment,
see U.S. Pat. No. 5,595,606, entitled "Shower Head and Film Forming
Apparatus Using Same, which is incorporated herein by reference. In
particular, one embodiment based on this patent adds a projection
or gas-confinement member to the reported showerhead structure.
[0031] FIG. 1 also shows that gas inlets 136 and 137, which feed
respective holes 132E and 132G, are coupled to gas-supply system
140. Specifically, gas-supply system 140 includes gas lines 142 and
143, gas sources 144, 145, and 146, and manual or automated
mass-flow controllers 147, 148, and 149. Gas line or conduit 142,
which includes one or more flexible portions (not specifically
shown), passes through an opening 116A in chamber sidewall 116 to
connect with gas inlet 136. Gas sources 144 and 145 are coupled
respectively via mass-flow controllers 147 and 148 to gas line 142.
Gas line 143, which also includes one or more flexible portions
(not specifically shown), passes through an opening 116B in chamber
sidewall 116 is coupled via mass-flow controller 149 to source
146.
[0032] In the exemplary embodiment, which is tailored for aluminum
oxide deposition, source 144 provides a vapor-drawn aluminum
precursor, such as trimethylaluminum (TMA) with a vapor pressure of
11 Torr at room temperature; source 145 provides a carrier gas,
such as argon; and source 146 provides an oxidant, such as a
water-argon mixture. The water-argon mixture can be implemented by
bubbling an argon carrier through a water reservoir. Other
embodiments use other aluminum precursors, such as
trisobutylaluminum (TIBA), dimethylaluminum hydride (DMAH),
AlC.sub.3, and other halogenated precursors and organometallic
precursors. Other types of oxidants include H.sub.2O.sub.2,
O.sub.2, O.sub.3, N.sub.2O. Thus, the present invention is not
limited to specific aluminum precursors or oxidants.
[0033] System 100 also includes vacuum pumps 150 and 160. Vacuum
pump 150 is coupled to gas-distribution fixture 130 via a mass-flow
controller 152 and gas line 142. And, vacuum pump 160 is coupled to
the interior of chamber 110 via a line 162 and an opening 114B in
chamber bottom plate 114.
[0034] In general operation, system 100 functions, via manual or
automatic control, to move gas-distribution fixture 130 from
operating position 138A to position 138B, to introduce reactant
gases from sources 145, 146, and 147 through holes 132E and 132G in
gas-distribution fixture 130 onto substrate 200, and to deposit
desired matter, such as an aluminum oxide, onto a substrate.
[0035] More particularly, FIG. 3 shows a flowchart 300 which
illustrates an exemplary method of operating system 100. Flowchart
300 includes process blocks 302-320.
[0036] The exemplary method begins at block 302 with insertion of
substrate 200 onto wafer holder 120. Execution then proceeds to
block 304.
[0037] In block 304, the system forms or closes an inner chamber
around substrate 200, or at least a portion of substrate 200
targeted for deposition. In the exemplary embodiment, this entails
using a lever or other actuation mechanism (not shown) to move
gas-distribution fixture 130 from position 138A to position 138B or
to move wafer holder 120 from position 138B to 138A. In either
case, this movement places gas-distribution surface 132C 10-20
millimeters from an upper most surface of substrate 200. In this
exemplary position, a lower-most surface of surface-projection
member 134 contacts the upper surface of support platform 124, with
the inner chamber bounded by gas-distribution surface 132C,
surface-projection member 134, and the upper surface of support
platform 124.
[0038] Other embodiments define the inner chamber in other ways.
For example, some embodiments include a surface-projection member
on support platform 124 of wafer holder 120 to define a cavity
analogous in structure and/or function to cavity 134A. In these
embodiments, the surface-projection member takes the form of a
vertical or slanted or curved wall, that extends from support
platform 124 and completely around substrate 200, and the
gas-distribution fixture omits a surface-projection member.
However, some embodiments include one or more surface-projection
members on the gas-distribution fixture and the on the support
platform, with the projection members on the fixture mating,
engaging, or otherwise cooperating with those on the support
platform to define a substantially or effectively closed chamber.
In other words, the inner chamber need not be completely closed,
but only sufficiently closed to facilitate a desired
deposition.
[0039] In block 306, after forming the inner chamber, the exemplary
method continues by establishing desired ambient conditions for the
desired deposition. This entails setting temperature and pressure
conditions within chamber 110, including cavity 134A. To this end,
the exemplary embodiment operates heating element 126 to heat
substrate 200 to a desired temperature, such as 150-200.degree. C.,
and operating vacuum pump 150 and/or pump 160 to establish a
desired ambient pressure, such as 3.0 Torr. Gas-distribution
fixture 130 is held at a temperature 30-50.degree. C. warmer than
its surroundings. (However, other embodiments can maintain the
fixture at other relative operating temperatures.) After
establishing the desired ambient conditions, execution continues at
block 308.
[0040] Block 308 entails hydroxylating the surface of substrate 200
by introducing an oxidant into the separate chamber. To this end,
the exemplary embodiment shuts mass-flow controllers 147 and 148
and operates mass-flow controller 149 to transfer an oxidant, such
as a water in an argon carrier, from source 146 through gas line
143 and holes 132G into cavity 134A for a period, such as two
seconds.
[0041] Notably, the inner chamber is smaller in volume than chamber
100 and thus requires less gas and less fill time to achieve
desired chemical concentrations (assuming all other factors equal.)
More precisely, the exemplary embodiment provides an inner chamber
with an empty volume in the range of 70 to 350 cubic centimeters,
based on a 1-to-5 millimeter inner-chamber height and a fixture
with a 30-centimeter diameter. Additionally, the number and
arrangement of holes in the fixture as well as the placement of the
holes close to the substrate, for example within five millimeters
of the substrate, promote normal gas incidence and uniform
distribution of gases over the targeted portion of substrate
200.
[0042] Block 310 entails purging or evacuating the inner chamber to
reduce water concentration in the gas-distribution fixture and
inner chamber to trace levels. To this end, the exemplary method
initially drives a high flow of argon gas from source 145 through
fixture 130 into the inner chamber and then draws the gas out of
the inner chamber through the fixture via vacuum pump 150, defining
a purge cycle of less than five seconds, for example three-four
seconds. The present invention, however, is not believed to be
limited to any particular purge-cycle duration.
[0043] Next, as block 312 shows, the exemplary method introduces an
aluminum precursor into the inner chamber through gas-distribution
fixture 130. This entail operating mass-flow controllers 147 and
148 to respectively allow the flow of TMA and an argon carrier into
fixture 130 via line 142 for a period of time such as 0.5-2.0
seconds. During this period, the argon carries the TMA to the
hydroxylated surface of the substrate, causing formation of an
approximately 0.8 Angstrom (.ANG.) monolayer of aluminum oxide
(AlO.sub.x).
[0044] Block 314 entails purging or evacuating the inner chamber to
reduce precursor concentration in the gas-distribution fixture and
inner chamber to trace levels. To this end, the exemplary method
initially drives a flow of argon gas from source 145 through
fixture 130 into the inner chamber and then draws the gas out of
the inner chamber through the fixture via vacuum pump 150. Again,
this purge cycle is expected to consume less than five seconds.
[0045] At this point, as represented by a return path 315 back to
block 304, blocks 304-314 can be repeated as many times as desired
to achieve an aluminum-oxide layer within roughly one Angstrom of
virtually any desired thickness from 5-10 Angstroms upwards. For
semiconductor applications, such as forming gate dielectrics,
thicknesses in the range of 50-80 Angstroms could be used.
[0046] Block 316 entails annealing the substrate and deposited
aluminum-oxide layer to enhance the dielectric breakdown voltage of
the layer. In the exemplary embodiment, this entails moving fixture
130 to operating position 138C (which establishes a
substrate-to-fixture separation in the range of 30-50 millimeters)
and using RF source 129 to generate a 250 Watt capacitively coupled
plasma at 0.12 Torr in an argon-oxygen atmosphere (10 atom percent
O.sub.2) between the wafer holder. Some embodiments anneal after
every monolayer to maximize dielectric breakdown strength, and some
anneal after each 25-50 Angstroms of deposited material thickness.
Though various anneal times are feasible, the exemplary embodiment
anneals for 10-15 seconds in high-temperature environment. A return
path 317 back to block 304 indicates that blocks 304-316 can be
repeated as many times as desired.
[0047] In block 318, the system opens the separate chamber. In the
exemplary embodiment, this entails automatically or manually moving
gas-distribution fixture 130 to position 138A. Other embodiments,
however, move the wafer holder or both the fixture and the wafer
holder. Still other embodiments may use multipart collar or
gas-confinement members which are moved laterally relative the
wafer holder or gas-distribution fixture to open and close an inner
chamber.
[0048] In block 320, substrate 200 is unloaded from chamber 110.
Some embodiments remove the substrate manually, and others remove
it using an automated wafer transport system.
CONCLUSION
[0049] In furtherance of the art, the inventors have presented new
systems, methods, and apparatuses for atomic-layer deposition. One
exemplary system includes an outer chamber, a substrate holder, and
a unique gas-distribution fixture. The fixture engages, or
otherwise cooperates with the substrate holder to form an inner
chamber within the outer chamber. Notably, the inner chamber not
only consumes less gas during deposition to reduce deposition waste
and cost, but also facilitates rapid filling and purging to reduce
deposition cycle times (with all other factors being equal.)
[0050] The embodiments described above are intended only to
illustrate and teach one or more ways of practicing or implementing
the present invention, not to restrict its breadth or scope. The
actual scope of the invention, which embraces all ways of
practicing or implementing the invention, is defined only by the
following claims and their equivalents.
* * * * *