U.S. patent application number 10/882203 was filed with the patent office on 2005-12-15 for semiconductor device and method of manufacturing the same.
This patent application is currently assigned to KABUSHHIKI KAISHA TOSHIBA. Invention is credited to Bruchhaus, Rainer, Itokawa, Hiroshi, Yamakawa, Koji.
Application Number | 20050274999 10/882203 |
Document ID | / |
Family ID | 35459611 |
Filed Date | 2005-12-15 |
United States Patent
Application |
20050274999 |
Kind Code |
A1 |
Itokawa, Hiroshi ; et
al. |
December 15, 2005 |
Semiconductor device and method of manufacturing the same
Abstract
A semiconductor device according to the present invention
comprises a semiconductor substrate, a capacitor including a lower
electrode disposed above the semiconductor substrate, a dielectric
film disposed above the lower electrode, and an upper electrode
disposed above the dielectric film, the upper electrode including
metal oxide formed of ABO.sub.3 perovskite oxide and containing at
least an Ru element as a B site element, and a metal film
containing a Ti element being disposed between the dielectric film
and the upper electrode.
Inventors: |
Itokawa, Hiroshi;
(Yokohama-shi, JP) ; Yamakawa, Koji; (Tokyo,
JP) ; Bruchhaus, Rainer; (Munich, DE) |
Correspondence
Address: |
Finnegan, Henderson, Farabow,
Garrett & Dunner, L.L.P.
1300 I Street, N.W.
Washington
DC
20005-3315
US
|
Assignee: |
KABUSHHIKI KAISHA TOSHIBA
Tokyo
JP
INFINEON TECHNOLOGIES AG
Munich
DE
|
Family ID: |
35459611 |
Appl. No.: |
10/882203 |
Filed: |
July 2, 2004 |
Current U.S.
Class: |
257/295 ;
257/306; 257/310; 257/E21.009; 257/E21.021; 257/E21.648;
257/E21.664; 257/E27.086; 257/E27.104; 438/244; 438/3 |
Current CPC
Class: |
H01L 27/11502 20130101;
H01L 27/11507 20130101; H01L 28/65 20130101; H01L 28/55 20130101;
H01L 27/10852 20130101; H01L 27/10808 20130101; H01L 28/75
20130101 |
Class at
Publication: |
257/295 ;
438/003; 257/306; 438/244; 257/310 |
International
Class: |
H01L 021/8242; H01L
031/062 |
Foreign Application Data
Date |
Code |
Application Number |
Jun 10, 2004 |
JP |
2004-172696 |
Claims
What is claimed is:
1. A semiconductor device comprising: a semiconductor substrate; a
capacitor including a lower electrode disposed above the
semiconductor substrate, a dielectric film disposed above the lower
electrode, and an upper electrode disposed above the dielectric
film; the upper electrode including metal oxide formed of ABO.sub.3
perovskite oxide and containing at least an Ru element as a B site
element; and a metal film containing a Ti element being disposed
between the dielectric film and the upper electrode.
2. A semiconductor device comprising: a semiconductor substrate;
and a capacitor including a lower electrode disposed above the
semiconductor substrate, a dielectric film disposed above the lower
electrode, and an upper electrode disposed above the dielectric
film; the upper electrode including metal oxide formed of ABO.sub.3
perovskite oxide and containing at least an Ru element and a Ti
element as B site elements.
3. The semiconductor device according to claim 1, wherein the
dielectric film contains at least Pb.
4. The semiconductor device according to claim 2, wherein the
dielectric film contains at least Pb.
5. The semiconductor device according to claim 1, wherein metal
oxide is at least one of SrRuO.sub.3 and BaRuO.sub.3.
6. The semiconductor device according to claim 2, wherein metal
oxide is at least one of Sr(Ru, Ti)O.sub.3 and Ba(Ru,
Ti)O.sub.3.
7. The semiconductor device according to claim 1, wherein the
capacitor includes a ferroelectric substance and has a nonvolatile
memory function.
8. The semiconductor device according to claim 2, wherein the
capacitor includes a ferroelectric substance and has a nonvolatile
memory function.
9. A method of manufacturing a semiconductor device, comprising:
disposing a lower electrode disposed above a semiconductor
substrate; disposing a dielectric film above the lower electrode;
disposing a metal film containing a Ti element above the dielectric
film; and disposing an upper electrode including metal oxide formed
of ABO.sub.3 perovskite oxide and containing at least an Ru element
as a B site element above the metal film to form a capacitor.
10. A method of manufacturing a semiconductor device, comprising:
disposing a lower electrode above a semiconductor substrate;
disposing a dielectric film above the lower electrode; and
disposing an upper electrode including metal oxide formed of
ABO.sub.3 perovskite oxide and containing at least an Ru element
and a Ti element as B site elements above the dielectric film to
form a capacitor.
11. The method according to claim 9, wherein the dielectric film
contains at least Pb.
12. The method according to claim 10, wherein the dielectric film
contains at least Pb.
13. The method according to claim 9, wherein metal oxide is at
least one of SrRuO.sub.3 and BaRuO.sub.3.
14. The method according to claim 10, wherein metal oxide is at
least one of Sr(Ru, Ti)O.sub.3 and Ba(Ru, Ti)O.sub.3.
15. The method according to claim 9, further comprising: forming
metal oxide by one of a sputtering process, a CVD process, and a
sol-gel process.
16. The method according to claim 10, further comprising: forming
metal oxide by one of a sputtering process, a CVD process, and a
sol-gel process.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to a semiconductor device and
a method of manufacturing the device, more specifically, to a
semiconductor device including a capacitor using a dielectric film,
and a method of manufacturing the device.
[0003] 2. Description of the Related Art
[0004] In recent years, development of a ferroelectric random
access memory (FeRAM), which is a nonvolatile memory using a
ferroelectric thin film, has been advanced.
[0005] For the FeRAM, ferroelectric materials such as
PZT(Pb(Zr.sub.XTi.sub.1-X)O.sub.3), BIT(Bi.sub.4Ti.sub.3O.sub.12),
and SBT(SrBi.sub.2Ta.sub.2O.sub.9) are used in a capacitor. All of
these materials have a crystalline structure on the basis of a
perovskite structure, whose basic structure is an oxygen
octahedron. Different from a conventional Si oxide film, these
materials do not have characteristic ferroelectricity in an
amorphous state, and cannot therefore be used in amorphous.
Therefore, processes for crystallization, such as a crystallizing
heat treatment at a high temperature, and an in-situ
crystallization process at the high temperature are required. In
general, the temperature required for the crystallization is in a
range of at least 400 to 700.degree. C., depending on the material.
Examples of a film forming method include an MOCVD process, a
sputtering process, and a chemical solution deposition (CSD)
process.
[0006] Moreover, a method of manufacturing a semi-conductor device
using such ferroelectric thin film has been disclosed in Jpn. Pat.
Appln. KOKAI Publication No. 2000-260954.
[0007] The FeRAM using PZT which is a Pb compound as a typical
ferroelectric material as described above essentially contains
wear-out factors, and is therefore requested to include a
conductive oxide material as an electrode. As the conductive oxide
material, conductive perovskite oxide films such as an SrRuO.sub.3
film are used which have a satisfactory interface matching property
with the perovskite oxide materials such as PZT.
[0008] However, when SrRuO.sub.3 containing an Ru element is
employed to an electrode film, excess Pb reacts with Ru at a film
interface between PZT and SrRuO.sub.3 and at a PZT grain boundary
to form a conductive material (Pb.sub.2Ru.sub.2O.sub.7-X, and the
like), which act as a leak path, and an increase of a leak current
caused by the path leads to a characteristics deterioration
problem.
BRIEF SUMMARY OF THE INVENTION
[0009] According to an aspect of the invention, there is provided a
semiconductor device comprising: a semiconductor substrate; a
capacitor including a lower electrode disposed above the
semiconductor substrate, a dielectric film disposed above the lower
electrode, and an upper electrode disposed above the dielectric
film; the upper electrode including metal oxide formed of ABO.sub.3
perovskite oxide and containing at least an Ru element as a B site
element; and a metal film containing a Ti element being disposed
between the dielectric film and the upper electrode.
[0010] According to another aspect of the invention, there is
provided a semiconductor device comprising: a semiconductor
substrate; and a capacitor including a lower electrode disposed
above the semiconductor substrate, a dielectric film disposed above
the lower electrode, and an upper electrode disposed above the
dielectric film; the upper electrode including metal oxide formed
of ABO.sub.3 perovskite oxide and containing at least an Ru element
and a Ti element as B site elements.
[0011] According to another aspect of the invention, there is
provided a method of manufacturing a semiconductor device,
comprising: disposing a lower electrode disposed above a
semiconductor substrate; disposing a dielectric film above the
lower electrode; disposing a metal film containing a Ti element
above the dielectric film; and disposing an upper electrode
including metal oxide formed of ABO.sub.3 perovskite oxide and
containing at least an Ru element as a B site element above the
metal film to form a capacitor.
[0012] According to another aspect of the invention, there is
provided a method of manufacturing a semiconductor device,
comprising: disposing a lower electrode above a semiconductor
substrate; disposing a dielectric film above the lower electrode;
and disposing an upper electrode including metal oxide formed of
ABO.sub.3 perovskite oxide and containing at least an Ru element
and a Ti element as B site elements above the dielectric film to
form a capacitor.
BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING
[0013] FIG. 1A is a sectional view showing a process of
manufacturing an FeRAM according to a first embodiment;
[0014] FIG. 1B is a sectional view showing the process of
manufacturing the FeRAM according to the first embodiment;
[0015] FIG. 1C is a sectional view showing the process of
manufacturing the FeRAM according to the first embodiment;
[0016] FIG. 2A is a sectional view showing the process of
manufacturing the FeRAM according to a second embodiment;
[0017] FIG. 2B is a sectional view showing the process of
manufacturing the FeRAM according to the second embodiment;
[0018] FIG. 2C is a sectional view showing the process of
manufacturing the FeRAM according to the second embodiment;
[0019] FIG. 3A is a sectional view showing the process of
manufacturing the FeRAM according to a third embodiment;
[0020] FIG. 3B is a sectional view showing the process of
manufacturing the FeRAM according to the third embodiment;
[0021] FIG. 3C is a sectional view showing the process of
manufacturing the FeRAM according to the third embodiment;
[0022] FIG. 4A is a sectional view showing the process of
manufacturing the FeRAM according to a fourth embodiment;
[0023] FIG. 4B is a sectional view showing the process of
manufacturing the FeRAM according to the fourth embodiment;
[0024] FIG. 4C is a sectional view showing the process of
manufacturing the FeRAM according to the fourth embodiment; and
[0025] FIG. 5 is a diagram showing leak current characteristics of
PZT capacitors formed by a manufacturing process of the embodiment
and a conventional manufacturing process.
DETAILED DESCRIPTION OF THE INVENTION
[0026] Embodiments will hereinafter be described with reference to
the drawings.
[0027] FIGS. 1A, 1B, and 1C are sectional views showing a process
of manufacturing an FeRAM according to a first embodiment. In the
first embodiment, in a capacitor, a metal film containing titanium
(Ti) having a film thickness of 2.5 nm is disposed between a
ferroelectric film, which is a PZT (Pb(Zr.sub.XTi.sub.1-X)O.sub.3)
film, and a metal oxide film constituting an upper electrode, which
is an SrRuO.sub.3 film. An example of application of this capacitor
to an offset type FeRAM cell will hereinafter be described.
[0028] First, as shown in FIG. 1A, a trench for isolating devices
is formed in a region other than a transistor active region of a
surface of a P type Si substrate S, then an SiO.sub.2 is buried in
the trench to form an isolation 101 (shallow trench isolation).
Subsequently, a transistor for operating switches is formed.
[0029] First, an oxide film 102 having a thickness of about 6 nm is
formed on the entire surface of the Si substrate S by thermal
oxidation, subsequently, an n+ type polycrystalline silicon film
103 doped with arsenic is formed on the entire surface of the oxide
film 102, further a WSi.sub.x film 104 is formed on the
polycrystalline silicon film 103, and a nitride film 105 is formed
on the WSi.sub.x film 104. Thereafter, the polycrystalline silicon
film 103, WSi.sub.x film 104, and nitride film 105 are processed by
conventional photolithography and RIE processes to form a gate
electrode 100.
[0030] Furthermore, a nitride film 106 is deposited, and a spacer
is formed on a side wall of the gate electrode 100 leaving the side
wall spacer by anisotropic RIE. Moreover, although details of the
process are omitted from the description, sources/drains 107 are
formed by ion implantations and heat treatments.
[0031] Next, as shown in FIG. 1B, a CVD oxide film 108 is deposited
on the entire surface. Thereafter, the surface is once planarized
by CMP, and a contact hole 109 connecting with one of the
source/drain 107 of a transistor is formed. Thereafter, a thin
titanium film is deposited by sputtering or CVD, and a heat
treatment is performed in a forming gas to form a TiN film 110.
Subsequently, a CVD tungsten 111 is deposited on the entire
surface, the tungsten 111 is removed from a region other than the
contact hole 109 by CMP process, so that the tungsten is buried in
the contact hole 109.
[0032] Thereafter, a CVD nitride film 112 is deposited on the
entire surface, a contact hole 113 connecting with the other
source/drain 107 of the transistor is formed, another TiN film 114
is similarly formed, and a tungsten 115 is buried in the contact
hole 113 to form a plug connecting with a capacitor.
[0033] Thereafter, as shown in FIG. 1C, a titanium film 116 having
a thickness of 10 nm is deposited on the entire surface of the CVD
nitride film 112 by sputtering, and subsequently a platinum film
117 having a thickness of about 100 nm is deposited on the entire
surface of the titanium film 116 by sputtering. Thereafter, a first
SrRuO.sub.3 film 118 serving as a lower electrode 200 of the
capacitor and having a thickness of 10 nm is deposited on the
entire surface of the platinum film 117 by sputtering, and the
first SrRuO.sub.3 film 118 is once crystallized by rapid thermal
anneal (RTA) in oxygen. In this case, when the first SrRuO.sub.3
film 118 is deposited, for example, at a temperature of 550.degree.
C., it is possible to easily form a crystalline SrRuO.sub.3 film
having a satisfactory quality.
[0034] Furthermore, a PZT film 119 serving as a capacitor
dielectric film 300 is formed on the first SrRuO.sub.3 film 118 by
sputtering, and the PZT film 119 is once crystallized by rapid
thermal anneal (RTA) in oxygen. Thereafter, a titanium film 120
having a thickness of 2.5 nm is deposited on the PZT film 119 by
sputtering, and a second SrRuO.sub.3 film (ABO.sub.3 perovskite
oxide film) 121 serving as an upper electrode 400 of the capacitor
and having a thickness of 10 nm is deposited on the titanium film
120, and the second SrRuO.sub.3 film 121 is once crystallized in
oxygen by rapid thermal anneal (RTA). In this case, when the second
SrRuO.sub.3 film 121 is deposited, for example, at a temperature of
550.degree. C., it is possible to easily form the SrRuO.sub.3 film
having a satisfactory quality. Thereafter, a platinum film 122 is
formed on the second SrRuO.sub.3 film 121 by sputtering.
[0035] Subsequently, once a CVD oxide film is deposited as a
processing mask material, the CVD oxide film is patterned by
photolithography and RIE processes. After a photo resist is
removed, the platinum film 122, second SrRuO.sub.3 film 121,
titanium film 120, and PZT film 119 are etched by RIE (processes).
Furthermore, the first SrRuO.sub.3 film 118, platinum film 117, and
titanium film 116 are patterned in order by a combination of the
photolithography and RIE (processes) to complete the forming of a
capacitor 10. The capacitor 10 has a nonvolatile memory function.
Thereafter, a CVD oxide film 123 is deposited all over the surface
of the capacitor 10 to cover the capacitor 10, and a heat treatment
is performed in oxygen at about 650.degree. C. in order to recover
damage in the PZT film 119 generated during the processing.
[0036] Thereafter, although the details are omitted, a drive line
and a bit line are formed, further, a wiring 50 is formed to
connect a contact connecting with the other source/drain 107 of the
transistor and the platinum film 122, then an upper-layer metal
wiring is formed. Through this process, the FeRAM is completed.
[0037] It is to be noted that a BaRuO.sub.3 film may also be used
instead of the second SrRuO.sub.3 film 121. Moreover, the titanium
film 120 may also be formed by a CVD process or a sol-gel process
instead of the sputtering process.
[0038] As described above, in the capacitor of FeRAM of the first
embodiment, a metal film containing Ti is disposed between the
upper electrode including metal oxide containing Ru and the PZT
film. This prevents reaction of excess Pb with Ru at a film
interface between the PZT film and the upper electrode and at a PZT
grain boundary, so that leak current is reduced.
[0039] FIGS. 2A, 2B, and 2C are sectional views showing a process
of manufacturing an FeRAM according to a second embodiment. In the
second embodiment, in a capacitor, an SrRuO.sub.3 film as a metal
oxide constituting an upper electrode is doped with titanium to
form an Sr(Ru, Ti)O.sub.3 film having a thickness of 10 nm. Another
example of the application of this capacitor to the offset type
FeRAM cell will hereinafter be described. It is to be noted that
remaining structure is similar to that of the first embodiment.
[0040] First, as shown in FIG. 2A, a trench for isolating the
devices is formed in a region other than a transistor active region
of a surface of a P type Si substrate S, then an SiO.sub.2 is
buried in the trench to form an isolation 201 (shallow trench
isolation). Subsequently, a transistor for operating switches is
formed.
[0041] First, an oxide film 202 having a thickness of about 6 nm is
formed on the entire surface of the Si substrate S by thermal
oxidation, subsequently, an n+ type polycrystalline silicon film
203 doped with arsenic is formed on the entire surface of the oxide
film 202, further a WSi.sub.x film 204 is formed on the
polycrystalline silicon film 203, and a nitride film 205 is formed
on the WSi.sub.x film 204. Thereafter, the polycrystalline silicon
film 203, WSi.sub.x film 204, and nitride film 205 are processed by
conventional photolithography and RIE processes to form a gate
electrode 100.
[0042] Furthermore, a nitride film 206 is deposited, and a spacer
is formed on the side wall of the gate electrode 100 leaving the
side wall spacer by anisotropic RIE. Moreover, although the details
of the process are omitted from the description, sources/drains 207
are formed by ion implantations and heat treatments.
[0043] Next, as shown in FIG. 2B, a CVD oxide film 208 is deposited
on the entire surface. Thereafter, the surface is once planarized
by CMP, and a contact hole 209 connecting with one of the
source/drain 207 of a transistor is formed. Thereafter, a thin
titanium film is deposited by sputtering or CVD, and a heat
treatment is performed in a forming gas to form a TiN film 210.
Subsequently, a CVD tungsten 211 is deposited on the entire
surface, the tungsten 211 is removed from the region other than the
contact hole 209 by CMP, so that the tungsten is buried in the
contact hole 209.
[0044] Thereafter, a CVD nitride film 212 is deposited on the
entire surface, a contact hole 213 connecting with the other
source/drain 207 of the transistor is formed, another TiN film 214
is similarly formed, and a tungsten 215 is buried in the contact
hole 213 to form a plug connecting with a capacitor.
[0045] Thereafter, as shown in FIG. 2C, a titanium film 216 having
a thickness of 10 nm is deposited on the entire surface of the CVD
nitride film 212 by sputtering, and subsequently a platinum film
217 having a thickness of about 100 nm is deposited on the entire
surface of the titanium film 216 by sputtering. Thereafter, an
SrRuO.sub.3 film 218 serving as a lower electrode 200 of the
capacitor and having a thickness of 10 nm is deposited on the
entire surface of the platinum film 217 by sputtering, and the
SrRuO.sub.3 film 218 is once crystallized by rapid thermal anneal
(RTA) in oxygen. In this case, when the SrRuO.sub.3 film 218 is
deposited, for example, at a temperature of 550.degree. C., it is
possible to easily form the crystalline SrRuO.sub.3 film having the
satisfactory quality.
[0046] Furthermore, a PZT film 219 serving as a capacitor
dielectric film 300 is formed on the SrRuO.sub.3 film 218 by
sputtering, and the PZT film 219 is once crystallized by rapid
thermal anneal (RTA) in oxygen. Thereafter, an Sr(Ru, Ti)O.sub.3
film (ABO.sub.3 perovskite oxide film) 220 serving as an upper
electrode 400 of the capacitor and having a thickness of 10 nm is
deposited on the PZT film 219 by sputtering, and the Sr(Ru,
Ti)O.sub.3 film 220 is once crystallized in oxygen by rapid thermal
anneal (RTA). It is to be noted that the Sr(Ru, Ti)O.sub.3 film 220
is a film obtained by doping the SrRuO.sub.3 film with titanium,
and the content of Ti in Sr(Ru, Ti)O.sub.3 is less than 50%. In
this case, when the Sr(Ru, Ti)O.sub.3 film 220 is deposited, for
example, at a temperature of 550.degree. C., it is possible to
easily form the Sr(Ru, Ti)O.sub.3 film having a satisfactory
quality. Thereafter, a platinum film 221 is formed on the Sr(Ru,
Ti)O.sub.3 film 220 by sputtering.
[0047] Subsequently, once a CVD oxide film is deposited as a
processing mask material, the CVD oxide film is patterned by the
photolithography and RIE processes. After a photo resist is
removed, the platinum film 221, Sr(Ru, Ti)O.sub.3 film 220, and PZT
film 219 are etched by RIE (processes). Furthermore, the
SrRuO.sub.3 film 218, platinum film 217, and titanium film 216 are
patterned in order by the combination of the photolithography and
RIE (processes) to complete the forming of a capacitor 20. The
capacitor 20 has the nonvolatile memory function. Thereafter, a CVD
oxide film 222 is deposited on the entire surface of the capacitor
20 to cover the capacitor 20, then a heat treatment is performed in
oxygen at about 650.degree. C. in order to recover the damage in
the PZT film 219 generated during the processing.
[0048] Thereafter, although the details are omitted, a drive line
and bit line are formed, further, the wiring 50 is formed to
connect the contact connecting with the other source/drain 207 of
the transistor and the platinum film 221, then an upper-layer metal
wiring is formed. Through this process, the FeRAM is completed.
[0049] It is to be noted that the Sr(Ru, Ti)O.sub.3 film 220 formed
by doping SrRuO.sub.3 with titanium is formed as the upper
electrode of the capacitor, but the material is not limited to
this, and a Ba(Ru, Ti)O.sub.3 film, and the like may also be
used.
[0050] As described above, in the capacitor of FeRAM of the second
embodiment the upper electrode using metal oxide containing Ru and
Ti is applied. This prevents a reaction of excess Pb with Ru at the
film interface between the PZT film and the upper electrode and at
the PZT grain boundary, and the leak current can be reduced.
[0051] FIGS. 3A, 3B, and 3C are sectional views showing the process
of manufacturing an FeRAM according to a third embodiment. In the
third embodiment, a tungsten is used in a plug material positioned
under a capacitor, and a metal film containing titanium (Ti) having
a film thickness of 2.5 nm is disposed between a PZT film which is
a ferroelectric film and an SrRuO.sub.3 film which is metal oxide
constituting an upper electrode of the capacitor. An example of the
application to a COP type FeRAM cell will hereinafter be
described.
[0052] First, as shown in FIG. 3A, a trench for isolating the
devices is formed in a region other than a transistor active region
of the surface of a P type Si substrate S, then an SiO.sub.2 is
buried in the trench to form an isolation 301 (shallow trench
isolation). Subsequently, a transistor for operating switches is
formed.
[0053] First, an oxide film 302 having a thickness of about 6 nm is
formed on the entire surface of the Si substrate S by thermal
oxidation, subsequently, an n+ type polycrystalline silicon film
303 doped with arsenic is formed on the entire surface of the oxide
film 102, further a WSi.sub.x film 304 is formed on the
polycrystalline silicon film 303, and a nitride film 305 is formed
on the WSi.sub.x film 304. Thereafter, the polycrystalline silicon
film 303, WSi.sub.x film 304, and nitride film 305 are processed by
conventional photolithography and RIE processes to form a gate
electrode 100.
[0054] Furthermore, a nitride film 306 is deposited, and a spacer
is formed on a side wall of the gate electrode 100 leaving the side
wall spacer by anisotropic RIE. Moreover, although the details of
the process are omitted from the description, sources/drains 307
are formed by ion implantations and heat treatments.
[0055] Next, as shown in FIG. 3B, after depositing a CVD oxide film
308 on the entire surface, the surface is once planarized by CMP,
and a contact hole 309 connecting with one of the source/drain 307
of the transistor is formed. Thereafter, a thin titanium film is
deposited by sputtering or CVD, and a heat treatment is performed
in a forming gas to form a TiN film 310. Subsequently, a CVD
tungsten 311 is deposited on the entire surface, the tungsten 311
is removed from the region other than the contact hole 309 by CMP,
and the tungsten is buried in the contact hole 309.
[0056] Thereafter, a CVD nitride film 312 is deposited on the
entire surface, a contact hole 313 connecting with the other
source/drain 307 of the transistor is formed, another TiN film 314
is similarly formed, and a tungsten 315 is buried in the contact
hole 313 to form a plug connecting with a capacitor.
[0057] Thereafter, as shown in FIG. 3C, a titanium film 316 having
a thickness of 10 nm is deposited on the entire surface of the CVD
nitride film 312 by sputtering, and subsequently an iridium film
317 having a thickness of about 100 nm is deposited on the entire
surface of the titanium film 316 by sputtering. Thereafter, a
platinum film 318 having a thickness of about 50 nm is deposited on
the entire surface of the iridium film 317 by sputtering.
Thereafter, a first SrRuO.sub.3 film 319 forming a lower electrode
200 of the capacitor and having a thickness of 10 nm is deposited
on the entire surface of the platinum film 318 by sputtering, and
the first SrRuO.sub.3 film 319 is once crystallized by rapid
thermal anneal (RTA) in oxygen. In this case, when the first
SrRuO.sub.3 film 319 is deposited, for example, at a temperature of
550.degree. C., it is possible to easily form the crystalline
SrRuO.sub.3 film having a satisfactory quality.
[0058] Furthermore, a PZT film 320 serving as a capacitor
dielectric film 300 is formed on the first SrRuO.sub.3 film 319 by
sputtering, and the PZT film 320 is once crystallized by rapid
thermal anneal (RTA) in oxygen Thereafter, a titanium film 321
having a thickness of 2.5 nm is deposited on the PZT film 320 by
sputtering. Furthermore, a second SrRuO.sub.3 film (ABO.sub.3
perovskite oxide film) 322 serving as an upper electrode 400 of the
capacitor and having a thickness of 10 nm is deposited on the
titanium film 321 by sputtering, and the second SrRuO.sub.3 film
322 is once crystallized in oxygen by rapid thermal anneal (RTA).
In this case, when the second SrRuO.sub.3 film 322 is deposited,
for example, at a temperature of 550.degree. C., it is possible to
easily form the Sr(Ru, Ti)O.sub.3 film having a satisfactory
quality. Thereafter, a platinum film 323 is formed on the second
SrRuO.sub.3 film 322 by sputtering.
[0059] Subsequently, once a CVD oxide film is deposited as a
processing mask material, the CVD oxide film is patterned by the
photolithography and RIE processes. After a photo resist is
removed, the platinum film 323, second SrRuO.sub.3 film 322,
titanium film 321, and PZT film 320 are etched by RIE. Furthermore,
the first SrRuO.sub.3 film 319, platinum film 318, iridium film
317, and titanium film 316 are patterned in order by the
combination of the photolithography and RIE (processes) to complete
the forming of a capacitor 30. The capacitor 30 has the nonvolatile
memory function. Thereafter, a CVD oxide film 324 is deposited on
the entire surface of the capacitor 30 to cover the capacitor 30,
and a heat treatment is performed in oxygen at about 650.degree. C.
in order to recover the damage in the PZT film 320 generated during
the processing. In this case, oxygen also penetrates to the
capacitor 30 to contribute to recovery from the damage. On the
other hand, a part of oxygen also reaches the lower electrode 200,
but the iridium film 317 has an oxygen diffusion preventing effect,
and therefore underlying tungsten 315 is not oxidized.
[0060] Thereafter, although the details are omitted, a drive line
and bit line are formed, then an upper-layer metal wiring is
formed. Through this process, the FeRAM is completed.
[0061] It is to be noted that in the third embodiment, the iridium
film 317 is formed, but noble metal materials such as ruthenium and
its oxide may also be used instead of iridium. Moreover,
BaRuO.sub.3, and the like may also be used instead of SrRuO.sub.3
for the films 319, 322 having a film thickness of 10 nm. The
titanium film 321 may also be formed by a CVD process or a sol-gel
process instead of the sputtering process.
[0062] As described above, in the capacitor of FeRAM of the third
embodiment, the metal film containing Ti is disposed between the
upper electrode using metal oxide containing Ru and the PZT film.
This prevents the reaction of excess Pb with Ru at the film
interface between the PZT film and the upper electrode and at the
PZT grain boundary, so that the leak current can be reduced.
[0063] FIGS. 4A, 4B, and 4C are sectional views showing the process
of manufacturing an FeRAM according to a fourth embodiment. In the
fourth embodiment, a tungsten is used in a plug material positioned
under a capacitor, and an SrRuO.sub.3 film serving as an upper
electrode of the capacitor and formed of metal oxide is doped with
titanium to form an Sr(Ru, Ti)O.sub.3 film having a film thickness
of 10 nm. Another example of the application to the COP type FeRAM
cell will hereinafter be described. It is to be noted that the
remaining structure is similar to that of the third embodiment.
[0064] First, as shown in FIG. 4A, a trench for isolating devices
is formed in a region other than a transistor active region of the
surface of a P type Si substrate S, and an SiO.sub.2 is buried in
the trench to form an isolation 401 (shallow trench isolation).
Subsequently, a transistor for operating switches is formed.
[0065] First, an oxide film 402 having a thickness of about 6 nm is
formed on the entire surface of the Si substrate S by a thermal
oxidation, subsequently, an n+ type polycrystalline silicon film
403 doped with arsenic is formed on the entire surface of the oxide
film 402, further a WSi.sub.x film 404 is formed on the
polycrystalline silicon film 403, and a nitride film 405 is formed
on the WSi.sub.x film 404. Thereafter, the polycrystalline silicon
film 403, WSi.sub.x film 404, and nitride film 405 are processed by
conventional photolithography and RIE processes to form a gate
electrode 100.
[0066] Furthermore, a nitride film 406 is deposited, and a spacer
is formed on a side wall of the gate electrode 100 leaving the side
wall spacer by anisotropic RIE. Moreover, although the details of
the process are omitted from the description, sources/drains 407
are formed by ion implantations and heat treatments.
[0067] Next, as shown in FIG. 4B, after depositing a CVD oxide film
408 on the entire surface, the surface is once planarized by CMP,
and a contact hole 409 connecting with one of the source/drain 407
of the transistor is formed. Thereafter, a thin titanium film is
deposited by sputtering or CVD, and a heat treatment is performed
in a forming gas to form a TiN film 410. Subsequently, a CVD
tungsten 411 is deposited on the entire surface, the tungsten 411
is removed from the region outside the contact hole 409 by CMP, and
the tungsten is buried in the contact hole 409.
[0068] Thereafter, a CVD nitride film 412 is deposited on the
entire surface, a contact hole 413 connecting with the other
source/drain 407 of the transistor is formed, a TiN film 414 is
similarly formed, and a tungsten 415 is buried in the contact hole
413 to form a plug connecting with the capacitor.
[0069] Thereafter, as shown in FIG. 4C, a titanium film 416 having
a thickness of 10 nm is deposited on the entire surface of the CVD
nitride film 412 by sputtering, and subsequently, an iridium film
417 having a thickness of about 100 nm is deposited on the entire
surface of the titanium film 416 by sputtering. Thereafter, a
platinum film 418 having a thickness of about 50 nm is deposited on
the entire surface of the iridium film 417 by sputtering.
Thereafter, an SrRuO.sub.3 film 419 serving as a lower electrode
200 of the capacitor and having a thickness of 10 nm is deposited
on the entire surface of the platinum film 418 by sputtering, and
the SrRuO.sub.3 film 419 is once crystallized by rapid thermal
anneal (RTA) in oxygen. In this case, when the SrRuO.sub.3 film 419
is deposited, for example, at a temperature of 550.degree. C., it
is possible to easily form the crystalline SrRuO.sub.3 film having
a satisfactory quality.
[0070] Furthermore, a PZT film 420 serving as a capacitor
dielectric film 300 is formed on the SrRuO.sub.3 film 419 by
sputtering, and the PZT film 420 is once crystallized by rapid
thermal anneal (RTA) in oxygen. Thereafter, an Sr(Ru, Ti)O.sub.3
film (ABO.sub.3 perovskite oxide film) 421 serving as an upper
electrode 400 of the capacitor and having a thickness of 10 nm is
deposited on the PZT film 420 by sputtering, and the Sr(Ru,
Ti)O.sub.3 film 421 is once crystallized in oxygen by rapid thermal
anneal (RTA). It is to be noted that the Sr(Ru, Ti)O.sub.3 film 421
is a film obtained by doping the SrRuO.sub.3 film with titanium,
and the content of Ti in Sr(Ru, Ti)O.sub.3 is less than 50%. In
this case, when the Sr(Ru, Ti)O.sub.3 film 421 is deposited, for
example, at a temperature of 550.degree. C., it is possible to
easily form the Sr(Ru, Ti)O.sub.3 film having a satisfactory
quality. Thereafter, a platinum film 422 is formed on the Sr(Ru,
Ti)O.sub.3 film 421 by sputtering.
[0071] Subsequently, once a CVD oxide film is deposited as a
processing mask material, the CVD oxide film is patterned by
photolithography and RIE processes. After a photo resist is
removed, the platinum film 422, Sr(Ru, Ti)O.sub.3 film 421, and PZT
film 420 are etched by RIE (processes). Furthermore, the
SrRuO.sub.3 film 419, platinum film 418, iridium film 417, and
titanium film 416 are patterned in order by a combination of
photolithography and RIE (processes) to complete the forming of a
capacitor 40. The capacitor 40 has the nonvolatile memory function.
Thereafter, a CVD oxide film 423 is deposited on the entire surface
of the capacitor 40 to cover the capacitor 40, and a thermal
treatment is performed in oxygen at about 650.degree. C. in order
to recover a damage in the PZT film 420 generated during the
processing. In this case, oxygen also penetrates to the capacitor
40 to contribute to the recovery from the damages. On the other
hand, a part of oxygen also reaches the lower electrode 200, but
the iridium film 417 then has an oxygen diffusion preventing
effect, and therefore underlying tungsten 415 is not oxidized.
[0072] Thereafter, although the details are omitted, a drive line
and bit line are formed, and an upper-layer metal wiring is formed.
Through this process, the FeRAM is completed.
[0073] It is to be noted that in the fourth embodiment, the iridium
film 417 is formed, but the noble metal materials such as ruthenium
and its oxide may also be used instead of iridium. Moreover, Ba(Ru,
Ti)O.sub.3, and the like may also be used instead of Sr(Ru,
Ti)O.sub.3 for the film 421 having a film thickness of 10 nm.
[0074] As described above, in the capacitor of FeRAM of the fourth
embodiment, the upper electrode including metal oxide containing Ru
and Ti is applied. This prevents the reaction of excess Pb with Ru
at the film interface between the PZT film and the upper electrode
and at the PZT grain boundary, so that the leak current can be
reduced.
[0075] FIG. 5 is a diagram showing leak current characteristics of
PZT capacitors formed by the manufacturing processes of the present
embodiment and a conventional technique. In FIG. 5, the leak
current characteristics offered by the present embodiments are
shown by open circles, and those of the conventional technique are
shown by solid circles.
[0076] For the PZT capacitor produced by the manufacturing process
of the present embodiment, after forming a titanium film having a
thickness of 10 nm on an SiO.sub.2 film formed on an Si substrate,
a 100 nm thick platinum film is formed, and further a 10 nm thick
SrRuO.sub.3 film is formed. Subsequently, a 140 nm thick PZT film,
2.5 nm to 5 nm (e.g., 2.5 nm) thick titanium film, 10 nm thick
SrRuO.sub.3 film, and 50 nm thick platinum film are successively
deposited.
[0077] For the PZT capacitor produced by the manufacturing process
of the related art, after forming a titanium film having a
thickness of 10 nm on an SiO.sub.2 film formed on an Si substrate,
a 100 nm thick platinum film is formed, and further a 10 nm thick
SrRuO.sub.3 film is formed. Subsequently, a 140 nm thick PZT film,
10 nm thick SrRuO.sub.3 film, and 50 nm thick platinum film are
successively deposited.
[0078] In both the present embodiment and the conventional
technique, for the SrRuO.sub.3 film and the PZT film formation,
amorphous films are formed by sputtering, and the films are
annealed and accordingly crystallized in an oxygen atmosphere. As
shown in FIG. 5, when the titanium film is applied at the interface
between the PZT film and the upper SrRuO.sub.3 film as in the
present embodiment, the leak current can be reduced as compared
with that in the conventional technique.
[0079] As described above, the capacitor of FeRAM produced by the
present embodiment applies the metal film containing Ti, which is
disposed between the upper electrode including the metal oxide
containing Ru and the PZT film, or the upper electrode including
the metal oxide containing Ru and Ti is applied. In this structure
containing Ti, excess Pb is prevented from reacting with Ru at the
film interface between the PZT film and the upper electrode and at
the PZT grain boundary, thus the leak current can be reduced.
Therefore, it is possible to realize the FeRAM having superior
characteristics, and it is also possible to provide a semiconductor
device high in reliability.
[0080] It is to be noted that in the capacitor of the present
embodiment, not only PZT but also ferroelectric materials such as
BIT(Bi.sub.4Ti.sub.3O.sub.12) and SBT(SrBi.sub.2Ta.sub.2O.sub.9)
may be used. Moreover, the capacitor using the ferroelectric film
of the present embodiment may be applied not only to the FeRAM but
also to a DRAM, and the DRAM having fine and highly integrated
superior characteristics. Therefore, it is possible to provide a
highly reliable FeRAM and fine DRAM.
[0081] According to the embodiments of the present invention, there
can be provided a semiconductor device in which a leak current in a
capacitor using a dielectric film is reduced, and a method of
manufacturing the device. That is, according to the present
invention, it is possible to form a stable capacitor superior in
characteristics, and it is possible to provide semiconductor
devices such as an FeRAM and DRAM which are high in reliability,
fine, and high in density and integration.
[0082] Additional advantages and modifications will readily occur
to those skilled in the art. Therefore, the invention in its
broader aspects is not limited to the specific details and
representative embodiments shown and described herein. Accordingly,
various modifications may be made without departing from the spirit
or scope of the general inventive concept as defined by the
appended claims and their equivalents.
* * * * *