U.S. patent application number 11/197581 was filed with the patent office on 2005-12-08 for polymer and epoxy resin compositions.
This patent application is currently assigned to Kaneka Corporation. Invention is credited to Fujita, Masayuki, Kitano, Kenichi, Nakagawa, Yoshiki.
Application Number | 20050272882 11/197581 |
Document ID | / |
Family ID | 27332138 |
Filed Date | 2005-12-08 |
United States Patent
Application |
20050272882 |
Kind Code |
A1 |
Kitano, Kenichi ; et
al. |
December 8, 2005 |
Polymer and epoxy resin compositions
Abstract
The present invention provides a vinyl polymer with an epoxy
group terminally introduced therein and an epoxy resin composition
comprising (A) an epoxy resin and (B) a vinyl polymer which has a
main chain produced by living radical polymerization and has a
reactive functional group at a main chain terminus. A flexible
epoxy resin composition can be obtained using these compounds. The
invention further provides an epoxy resin composition having an
epoxy group at a main chain terminus thereof.
Inventors: |
Kitano, Kenichi; (Kobe-shi,
JP) ; Nakagawa, Yoshiki; (Kobe-shi, JP) ;
Fujita, Masayuki; (Kobe-shi, JP) |
Correspondence
Address: |
CONNOLLY BOVE LODGE & HUTZ LLP
SUITE 800
1990 M STREET NW
WASHINGTON
DC
20036-3425
US
|
Assignee: |
Kaneka Corporation
Osaka-shi
JP
|
Family ID: |
27332138 |
Appl. No.: |
11/197581 |
Filed: |
August 5, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11197581 |
Aug 5, 2005 |
|
|
|
10370727 |
Feb 24, 2003 |
|
|
|
6943219 |
|
|
|
|
10370727 |
Feb 24, 2003 |
|
|
|
09763150 |
Apr 20, 2001 |
|
|
|
6555622 |
|
|
|
|
09763150 |
Apr 20, 2001 |
|
|
|
PCT/JP99/04471 |
Aug 20, 1999 |
|
|
|
Current U.S.
Class: |
525/523 ;
528/421 |
Current CPC
Class: |
C08F 8/26 20130101; C08L
63/00 20130101; C08G 8/38 20130101; C08F 8/02 20130101; C08L 61/06
20130101; C08L 33/18 20130101; C08G 8/10 20130101; C08L 63/00
20130101; C08F 8/02 20130101; C08F 8/00 20130101; C08L 61/06
20130101; C08L 63/00 20130101; C08F 8/26 20130101; C08L 2666/04
20130101; C08F 120/18 20130101; C08F 120/18 20130101; C08F 8/26
20130101; C08L 33/00 20130101; C08F 120/18 20130101; C08F 8/00
20130101; C08L 61/04 20130101; C08F 8/00 20130101; C08F 2810/40
20130101; C08G 59/50 20130101; C08G 59/027 20130101; C08F 8/26
20130101; C08L 63/00 20130101; C08L 61/06 20130101; C08G 59/02
20130101 |
Class at
Publication: |
525/523 ;
528/421 |
International
Class: |
C08L 063/00 |
Foreign Application Data
Date |
Code |
Application Number |
Aug 20, 1998 |
JP |
10/234430 |
Aug 20, 1998 |
JP |
10/234431 |
Sep 14, 1998 |
JP |
10/260195 |
Claims
1-37. (canceled)
38. An epoxy resin composition which comprises a vinyl polymer
having a group represented by the following general formula (1) at
a main chain terminus thereof: 5wherein, R.sup.1, R.sup.2 and
R.sup.3 are the same or different and each represents a hydrogen
atom, a monovalent hydrocarbon group containing 1 to 10 carbon
atoms or a monovalent group containing 1 to 10 carbon atoms as
derived from two hydrocarbon groups by being bound together via an
ether bond or ester bond, and R.sup.1 and R.sup.2 or R.sup.2 and
R.sup.3 may be combined together at respective other termini to
form a cyclic structure; wherein the vinyl polymer having a group
represented by the general formula (1) at a main chain terminus
thereof is obtained by reacting a reactive functional group of a
vinyl polymer having the reactive functional group at a main chain
terminus thereof with a compound represented by the following
general formula (2): 6wherein, R.sup.1, R.sup.2 and R.sup.3 are
defined as above, R.sup.4 and R.sup.5 are the same or different and
each represents a hydrogen atom, a monovalent hydrocarbon group
containing 1 to 10 carbon atoms or a monovalent group containing 1
to 10 carbon atoms as derived from two hydrocarbon groups by being
bound together via an ether bond or ester bond and X represents a
chlorine, bromine or iodine atom; wherein the vinyl polymer having
the reactive functional group at a main chain terminus thereof is
obtained by (1) carrying out polymerization of a vinyl monomer by
the living radical polymerization technique and (2) reacting, at
the end point of the polymerization, the resulting polymer with a
compound having both a reactive functional group and an
ethylenically unsaturated group.
39. A vinyl polymer having a group represented by the following
general formula (1) at a main chain terminus thereof: 7wherein,
R.sup.1, R.sup.2 and R.sup.3 are the same or different and each
represents a hydrogen atom, a monovalent hydrocarbon group
containing 1 to 10 carbon atoms or a monovalent group containing 1
to 10 carbon atoms as derived from two hydrocarbon groups by being
bound together via an ether bond or ester bond, and R.sup.1 and
R.sup.2 or R.sup.2 and R.sup.3 may be combined together at
respective other termini to form a cyclic structure. which polymer
is obtained by reacting a reactive functional group of a vinyl
polymer having the reactive functional group at a main chain
terminus thereof with a compound represented by the following
general formula (2): 8wherein, R.sup.1, R.sup.2 and R.sup.3 are
defined as above, R.sup.4 and R.sup.5 are the same or different and
each represents a hydrogen atom, a monovalent hydrocarbon group
containing 1 to 10 carbon atoms or a monovalent group containing 1
to 10 carbon atoms as derived from two hydrocarbon groups by being
bound together via an ether bond or ester bond and X represents a
chlorine, bromine or iodine atom; wherein the vinyl polymer having
the reactive functional group at a main chain terminus thereof is
obtained by (1) carrying out polymerization of a vinyl monomer by
the living radical polymerization technique and (2) reacting, at
the end point of the polymerization, the resulting polymer with a
compound having both a reactive functional group and an
ethylenically unsaturated group.
Description
TECHNICAL FIELD
[0001] The present invention relates to an epoxy resin composition.
More particularly, it relates to an epoxy-terminated vinyl polymer,
a composition comprising the polymer and a flexible composition
comprising an epoxy resin and a reactive functional
group-containing vinyl polymer.
BACKGROUND ART
[0002] When combined with a curing agent, epoxy resins give cured
products having a three-dimensionally crosslinked structure and
thus exhibiting various desirable characteristics. Crosslinked
epoxy groups are exploited in a wide range of applications, such as
paints, electrics/electronics, civil engineering/building,
adhesives, and composite materials, owing to excellence in the
balance between heat resistance and mechanical/physical properties
and in electrical characteristics, adhesive characteristics and
corrosion resistance, among others, and to the ease of molding.
[0003] On the other hand, epoxy resins are generally hard and
brittle by nature and may form cracks upon exposure to stress
strain or thermal shock on the occasion of curing or in use, hence
epoxy resins are required to be rendered tenacious and flexible. In
the field of IC sealing, for instance, where packages are becoming
smaller and thinner, improvement in crack resistance is needed.
[0004] As a means for providing epoxy resins with flexibility,
there may be mentioned the combined use of a flexible epoxy resin.
The flexible epoxy resin includes, among others, diglycidyl esters
of long-chain fatty acids such as linoleic acid dimer; polyglycidyl
ethers of polyhydric alcohols such as glycerol, pentaerythritol and
trimethylolpropane; diglycidyl ethers of polyalkylene glycols such
as polyethylene glycol; and the like. However, long-chain fatty
acid glycidyl esters are short of alkali resistance and gasoline
resistance, although they are excellent in flexibility.
Polyalkylene glycol glycidyl ethers also have problems, for example
they are inferior in weathering resistance.
[0005] It is known that crosslinking functional group-terminated
liquid oligbmers, when used alone or combined with an appropriate
curing agent, give cured products excellent in rubber elasticity.
Thus, it is expected that an epoxy-terminated vinyl polymer, if
successfully obtained in a simple and easy manner, might serve as a
novel flexible epoxy resin excellent in flexibility. Further, vinyl
polymers show various characteristics depending on the main chain
skeleton thereof and, therefore, are amenable to molecular design
according to the use/purpose thereof.
[0006] As for the production of epoxy-terminated vinyl polymers,
U.S. Pat. No. 4,429,099, for instance, discloses a method which
comprises reacting the termini of polyisobutylene with a phenol in
the manner of Friedel-Crafts reaction and further utilizing the
reactivity of the phenol group to synthesize an epoxy-terminated
polyisobutylene. However, low-polarity polymers such as
polyisobutylene are poor in compatibility with epoxy resins and, if
well dispersed, give a high viscosity.
[0007] In view of the above state of the art, it is an object of
the present invention to provide a vinyl polymer with an epoxy
group terminally introduced therein and an epoxy resin composition
in which such polymer is used.
[0008] A further object of the invention is to provide an epoxy
resin composition having flexibility by adding a vinyl polymer
having a terminal reactive functional group to an epoxy resin.
SUMMARY OF THE INVENTION
[0009] Thus, according to a first aspect thereof, the invention
provides an epoxy resin composition
[0010] which comprises a vinyl polymer having a group represented
by the following general formula (1) at a main chain terminus
[0011] as well as a vinyl polymer having a group represented by the
following general formula (1) at a main chain terminus. 1
[0012] In the above formula, R.sup.1, R.sup.2 and R.sup.3 are the
same or different and each represents a hydrogen atom, a monovalent
hydrocarbon group containing 1 to 10 carbon atoms or a monovalent
group containing 1 to 10 carbon atoms as derived from two
hydrocarbon groups by being bound together via an ether bond or
ester bond, and R.sup.1 and R.sup.2 or R.sup.2 and R.sup.3 may be
combined together at respective other termini to form a cyclic
structure.
[0013] In accordance with a second aspect, the invention provides
an epoxy resin composition which comprises (A) an epoxy resin and
(B) a vinyl polymer having a main chain produced by living radical
polymerization and a reactive functional group at a main chain
terminus.
[0014] In the following, the present invention is described in
detail.
DETAILED DISCLOSURE OF THE INVENTION
[0015] The first aspect of the invention lies in an epoxy resin
composition comprising a vinyl polymer terminally having a group
represented by the general formula (1) shown above, namely an
epoxy-terminated vinyl polymer.
[0016] In the general formula (1), R.sup.1, R.sup.2 and R.sup.3 are
the same or different and each represents a hydrogen atom, a
monovalent hydrocarbon group containing 1 to 10 carbon atoms or a
monovalent group containing 1 to 10 carbon atoms as derived from
two hydrocarbon groups by being bound together via an ether bond or
ester bond, and R.sup.1 and R.sup.2 or R.sup.2 and R.sup.3 may be
combined together at respective other termini to form a cyclic
structure.
[0017] The monomer constituting the main chain of the above vinyl
polymer is not particularly restricted but may be any of various
monomers. As examples, there may be mentioned (meth) acrylic
monomers such as (meth)acrylic acid, methyl (meth)acrylate, ethyl
(meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate,
n-butyl (meth)acrylate, isobutyl (meth)acrylate, tert-butyl
(meth)acrylate, n-pentyl (meth)acrylate, n-hexyl (meth)acrylate,
cyclohexyl (meth)acrylate, n-heptyl (meth)acrylate, n-octyl
(meth)acrylate, 2-ethylhexyl (meth)acrylate, nonyl (meth)acrylate,
decyl (meth)acrylate, dodecyl (meth)acrylate, phenyl
(meth)acrylate, toluyl (meth)acrylate, benzyl (meth)acrylate,
2-methoxyethyl (meth)acrylate, 3-methoxybutyl (meth)acrylate,
2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate,
stearyl (meth)acrylate, glycidyl (meth)acrylate, 2-aminoethyl
(meth)acrylate, .gamma.-(methacryloyloxypropyl)trimethoxysil- ane,
(meth)acrylic acid-ethylene oxide adducts, trifluoromethylmethyl
(meth)acrylate, 2-trifluoromethylethyl (meth)acrylate,
2-perfluoroethylethyl (meth)acrylate,
2-perfluoroethyl-2-perfluorobutylet- hyl (meth)acrylate,
2-perfluoroethyl (meth)acrylate, perfluoromethyl (meth)acrylate,
diperfluoromethylmethyl (meth)acrylate,
2-perfluoromethyl-2-perfluoroethylmethyl (meth)acrylate,
2-perfluorohexyletiyl (meth)acrylate, 2-perfluorodecylethyl
(meth)acrylate and 2-perfluorohexadecylethyl (meth)acrylate;
styrenic monomers such as styrene, vinyltoluene,
.alpha.-methylstyrene, chlorostyrene, and styrenesulfonic acid and
salts thereof; fluorine-containing vinyl monomers such as
perfluoroethylene, perfluoropropylene and vinylidene fluoride;
silicon-containing vinyl monomers such as vinyltrimethoxysilane and
vinyltriethoxysilane; maleic anhydride, maleic acid and monoalkyl
esters and dialkyl esters of maleic acid; fumaric acid and
monoalkyl esters and dialkyl esters of fumaric acid; maleimide
monomers such as maleimide, methylmaleimide, ethylmaleimide,
propylmaleimide, butylmaleimide, hexylmaleimide, octylmaleimide,
dodecylmaleimide, stearylmaleimide, phenylmaleimide and
cyclohexylmaleimide; nitrile-containing vinyl monomers such as
acrylonitrile and methacrylonitrile; amido-containing vinyl
monomers such as acrylamide and methacrylamide; vinyl esters such
as vinyl acetate, vinyl propionate, vinyl pivalate, vinyl benzoate
and vinyl cinnamate; alkenes such as ethylene and propylene;
conjugated dienes such as butadiene and isoprene; vinyl chloride,
vinylidene chloride, allyl chloride, allyl alcohol and so forth.
These may be used singly or a plurality of them may be
copolymerized. Preferred among them from the viewpoint of physical
properties of products, among others, are styrenic monomers and
(meth)acrylic monomers, more preferably (meth)acrylic ester
monomers, still more preferably acrylic ester monomers, and butyl
acrylate is most preferred. In the practice of the invention, these
preferred monomers may be copolymerized with another monomer or
other monomers and, on that occasion, the content of these
preferred monomers is preferably 40% by weight.
[0018] The molecular weight distribution of the above vinyl polymer
is not particularly restricted but the ratio (Mw/Mn) of weight
average molecular weight (Mw) to number average molecular weight
(Mn) as determined by gel permeation chromatography is generally
less than 1.8, preferably not more than 1.7, more preferably not
more than 1.6, still more preferably not more than 1.5, especially
preferably not more than 1.4, most preferably not more than 1.3. In
GPC measurements in the practice of the invention, the measurements
are generally carried out using polystyrene gel columns with
chloroform as the mobile phase. The number average molecular weight
and so on can be determined on the polystyrene equivalent
basis.
[0019] The number average molecular weight of the above vinyl
polymer is not particularly restricted but preferably is within the
range of 500 to 1,000,000, more preferably 1,000 to 100,000.
[0020] The vinyl polymer having a terminal structure represented by
the general formula (1) can be obtained by reacting the reactive
functional group of a reactive functional group-terminated vinyl
polymer with a compound represented by the general formula (2)
given below. The reactive functional group is not particularly
restricted but preferably is an alcoholic hydroxyl group, a
phenolic hydroxyl group, an amino groupior a carboxyl group. 2
[0021] In the general formula (2), R.sup.1, R.sup.2 and R.sup.3 are
as defined above. R.sup.4 and R.sup.5 are the same or different and
each represents a hydrogen atom, a monovalent hydrocarbon group
containing 1 to 10 carbon atoms or a monovalent group containing 1
to 10 carbon atoms as derived from two hydrocarbon groups by being
bound together via an ether bond or ester bond. X represents a
chlorine, bromine or iodine atom.
[0022] In the first aspect of the invention, the reactive
functional group-terminated vinyl polymer is produced by the
following steps:
[0023] (1) Polymerizing a vinyl monomer(s) by the technique of
living radical polymerization and
[0024] (2) Reacting, at the end point of the polymerization, the
polymer with a compound having both a reactive function group and
an ethylenically unsaturated group.
[0025] Thus, radical polymerization of a vinyl monomer(s) is
carried out in the manner of living radical polymerization,
typically atom transfer radical polymerization, followed by causing
the species active in polymerization, namely the polymer radical,
to add to the ethylenically active group of the compound having
both ethylenically unsaturated group and a reactive functional
group as well, whereupon a reactive functional group-terminated
vinyl polymer can be obtained.
[0026] While "living polymerization", in its narrow sense, means
the polymerization in which molecular chains grow while the
terminal activity thereof is always maintained, it generally
includes pseudo-living polymerization in which molecular chains
grow while terminally inactivated species and terminally active
species are in equilibrium. It is the latter definition that
applies in the present invention. In recent years, "living radical
polymerization" has been actively studied by a number of groups. As
examples, there may be mentioned, among others, the technique using
such a radical capping agent as a cobalt-porphyrin complex (J. Am.
Chem. Soc., 1994, 116, 7943) or a nitroxide compound
(Macromolecules, 1994, 27, 7228) and the atom transfer radical
polymerization (ATRP) technique using an organic halide or the like
as an initiator and a transition metal complex as a catalyst. In
spite of the fact that it belongs to the class of radical
polymerization in which the rate of polymerization is high and a
termination reaction such as mutual coupling of radicals readily
occurs and which is said to be difficult to control, living radical
polymerization is hardly subject to such termination reaction and
can give a polymer with a narrow molecular weight distribution
(Mw/Mn=1.1 to 1.8) and renders it possible to control the molecular
weight arbitrarily by selecting the monomer/initiator charge
ratio.
[0027] Further, "living radical polymerization" is characterized by
nature in that the structures of the polymer termini are distinct
and terminal functional group introduction is easy and, therefore,
it is preferred as the method of producing a vinyl polymer
terminally having a specific functional group. Among living radical
polymerization techniques, the atom transfer radical polymerization
technique is most preferred because of the ease of molecular weight
and molecular weight distribution control.
[0028] Atom transfer radical polymerization is characterized in
that a vinyl monomer(s) is (are) polymerized using an organic
halide (e.g. a compound having a halogen atom at the a position, or
a compound having a halogen atom at the benzyl position) or a
halogenated sulfonyl compound as the initiator and a transition
metal complex as the catalyst.
[0029] The above organic halide or halogenated sulfonyl compound
contains a carbon atom bound to a halogen atom and further bound to
a carbonyl, phenyl or sulfonyl group, so that the carbon-halogen
bond can be readily activated and can function as an initiator.
Among typical examples of such compound, there are the following:
C.sub.6H.sub.5--CH.sub.2X, C.sub.6H.sub.5--C(H) (X)CH.sub.3,
C.sub.6H.sub.5--C(X) (CH.sub.3).sub.2 (where C.sub.6H.sub.5
represents a phenyl group and X represents a chlorine, bromine or
iodine atom); R.sup.8--C(H) (X)--CO.sub.2R.sup.9,
R.sup.8--C(CH.sub.3) (X)--CO.sub.2R.sup.9, R.sup.8--C(H)
(X)--C(O)R.sup.9, R.sup.8--C(CH.sub.3) (X)--C(O)R.sup.9 (where
R.sup.8 and R.sup.9 are the same or different and each represents a
hydrogen atom, an alkyl group containing 1 to 20 carbon atoms, an
aryl group containing 6 to 20 carbon atoms or an aralkyl group
containing 7 to 20 carbon atoms and X represents a chlorine,
bromine or iodine atom); R.sup.8--C.sub.6H.sub.4--SO.sub.2X (where
R.sup.8 represents a hydrogen atom, an alkyl group containing 1 to
20 carbon atoms, an aryl group containing 6 to 20 carbon atoms or
an aralkyl group containing 7 to 20 carbon atoms and X represents a
chlorine, bromine or iodine atom); and the like. By converting the
terminal halogen of a polymer obtained by using this initiator by
the method mentioned later herein, a vinyl polymer having a group
represented by the general formula (1) at one terminus is
produced.
[0030] An organic halide or halogenated sulfonyl compound having a
functional group other than the functional group serving to
initiate the polymerization may also be used. In that case, a
polymer is produced which has the functional group bound to the
initiator at one terminus of the main chain and the halogen group
at the other terminus. As the functional group, there may be
mentioned alkenyl, crosslinking silyl, hydroxyl, epoxy, amino,
amido and carboxyl groups, among others. When the terminal halogen
atom of the polymer is converted to a substituent having a group of
the general formula (1), a vinyl polymer having, at both termini,
functional groups which are the same or different. By coupling the
terminal halogens together, it is possible to produce a vinyl
polymer which has functional groups at both termini.
[0031] The polymerization may also be carried out by using an
organic halide or halogenated sulfonyl compound having two or more
initiation sites as the initiator. In such case, a vinyl polymer
having two or more halogen groups in each molecule is produced.
When the termini of this polymer are converted by the method
mentioned later herein, a vinyl polymer having two or more groups
represented by the general formula (1) per molecule is obtained. By
carrying out the polymerization using an initiator having two
initiation sites and converting the both termini of the polymer by
the method mentioned later herein, a vinyl polymer having a group
of the general formula (1) at both termini is produced.
[0032] Specific examples of the initiator having two initiation
sites are as follows: 3
[0033] (In the above formulas, C.sub.6H.sub.4 represents a
phenylene group, X represents a chlorine, bromine or iodine atom, R
represents an alkyl group containing 1 to 20 carbon atoms, an aryl
group containing 6 to 20 carbon atoms or an aralkyl group
containing 7 to 20 carbon atoms and n represents an integer of 0 to
20); 4
[0034] (In the above formulas, X represents a chlorine, bromine or
iodine atom, n represents an integer of 0 to 20 and C.sub.6H.sub.4
represents a phenylene group); and the like.
[0035] Living radical polymerization can be carried out in the
absence of or in any of various organic solvents. As the solvents,
there may be mentioned hydrocarbon solvents such as benzene and
toluene; ether solvents such as diethyl ether, tetrahydrofuran,
diphenyl ether, anisole and dimethoxybenzene; halogenated
hydrocarbon solvents such as methylene chloride, chloroform and
chlorobenzene; ketone solvents such as acetone, methyl ethyl ketone
and methyl isobutyl ketone; alcohol solvents such as methanol,
ethanol, propanol, isopropanol, n-butyl alcohol and tert-butyl
alcohol; nitrile solvents such as acetonitrile, propionitrile and
benzonitrile; ester solvents such as ethyl acetate and butyl
acetate; carbonate solvents such as ethylene carbonate and
propylene carbonate; and so on. These may be used singly or two or
more of them may be used in admixture. It is also possible to carry
out the polymerization in an emulsion system or in a system in
which the supercritical fluid CO.sub.2 is used as a medium. The
above polymerization can be effected within the temperature range
of 0 to 200.degree. C., preferably within the range of room
temperature to 150.degree. C.
[0036] The transition metal complex to be used as the catalyst is
not particularly restricted but includes, as preferred species,
complexes of zero-valence copper, univalent copper, bivalent
ruthenium, bivalent iron or bivalent nickel. Among them, copper
complexes are preferred. As specific examples of the univalent
copper compound, there may be mentioned cuprous chloride, cuprous
bromide, cuprous iodide, cuprous cyanide, cuprous oxide and cuprous
perchlorate. When a copper compound is used, a ligand, for example
2,2'-bipyridyl or a derivative thereof, 1,10-phenanthroline or a
derivative thereof, or a polyamine such as
tetramethylethylenediamine, pentamethyl-diethylenetriamine or
hexamethyltris(2-aminoethyl)amine, is added for increasing the
catalytic activity. The tristriphenylphosphine complex of bivalent
ruthenium chloride (RuCl.sub.2(PPh.sub.3).sub.3) is also suited for
use as a catalyst. When a ruthenium compound is used as a catalyst,
an aluminum alkoxide is added as an activator. Further, the
bistriphenylphosphine complex of bivalent iron
(FeCl.sub.2(PPh.sub.3).sub.2), the bistriphenylphosphine complex of
bivalent nickel (NiCl.sub.2 (PPh.sub.3).sub.2) and the
bistributylphosphine complex of bivalent nickel
(NiBr.sub.2(PBu.sub.3).sub.2) are also suited as catalysts.
[0037] The compound having both an ethylenically unsaturated group
and a reactive functional group is not particularly restricted but
includes, among others, hydroxy-containing vinyl monomers such as
2-hydroxyethyl (meth)acrylate and 2-hydroxypropyl (meth)acrylate;
amido-containing vinyl monomers such as (meth) acrylamide;
amino-containing vinyl monomers such as 2-aminoethyl
(meth)acrylate; carboxyl-containing vinyl monomers such as (meth)
acrylic acid, maleic acid, maleic acid monoalkyl esters, fumaric
acid and fumaric acid monoalkyl esters, and the like.
[0038] Further, maleic anhydride; maleimide monomers such as
maleimide, methylmaleimide, ethylmaleimide, propylmaleimide,
butylmaleimide, hexylmaleimide, octylmaleimide, dodecylmaleimide,
stearylmaleimide, phenylmaleimide and cyclohexylmaleimide;
tert-butoxystyrene; acetoxystyrene; and the like may also be
used.
[0039] Further, phenols having an ethylenically unsaturated group,
such as o-, m- and p-allylphenol and o-, m- and p-allyloxyphenol;
alcohols having an ethylenically unsaturated group, such as allyl
alcohol, butenyl alcohol, pentenyl alcohol and hexenyl alcohol;
amines having an ethylenically unsaturated group, such as
allylamine, butenylamine, pentenylamine and hexenylamine;
carboxylic acid compounds having an ethylenically unsaturated
group, such as vinyl acetate, pentenoic acid, heptenoic acid and
undecenoic acid; and the like may also be used.
[0040] When the above compound having both an ethylenically
unsaturated group and a reactive functional group is reacted with
the polymer terminus, the compound as such may be subjected to
reaction. In some cases, however, the reactive functional group may
affect the polymer terminus and, in such cases, it may be used in
the form having a protective group. As the protective group, there
may be mentioned acetyl, silyl groups and alkoxy groups, among
others. Suited for use as the compound having a protective
functional group are all the compounds mentioned above whose
functional group is protected.
[0041] The above compound having both a reactive functional group
and an ethylenically unsaturated group may be subjected to reaction
with the polymer isolated after completion of the vinyl monomer
polymerization by adding to that polymer together with a catalyst
or may be added and subjected to reaction in the course of
polymerization (in situ). In the latter case, the monomer
conversion of the first polymerization should be as high as
possible, preferably not less than 80%. If the conversion is not
more than 80%, the crosslinking silyl group is distributed on side
chains, not at molecular termini, whereby the mechanical
characteristics of cured products will be impaired. In principle,
the addition of such compound having a polymerizable alkenyl group
and a crosslinking silyl group in an equivalent amount relative to
the whole number of termini results in introduction of the
functional group at all termini. For securing the introduction of
the functional group at all termini, however, it is recommendable
to use the compound in excess, specifically in an amount of 1 to 5
times excess relative to the number of termini. When it is used in
an amount not less than 5 times, the functional group is introduced
terminally into the polymer at an excessively high density and this
is unfavorable from the cured product physical properties
viewpoint.
[0042] In the first aspect of the invention, the vinyl polymer
having a reactive functional group is also produced by the
following steps:
[0043] (1) Producing a vinyl polymer having a terminal structure
represented by the following general formula 3 (a vinyl polymer
having a halogen atom at a main chain terminus) by subjecting vinyl
monomers to atom transfer radical polymerization, namely radical
polymerization using an organic halide or halogenated sulfonyl
compound as an initiator and a transition metal complex as a
catalyst:
--C(R.sup.6)(R.sup.7)(X) (3)
[0044] wherein R.sup.6 and R.sup.7 each represents a group bound to
the ethylenically unsaturated group and X represents a chlorine,
bromine or iodine atom) and
[0045] (2) Converting the halogen atom in general formula (3) to a
substituent having a reactive functional group.
[0046] The initiators, catalysts, solvents, polymerization
conditions and so forth as already mentioned hereinabove
specifically for atom transfer radical polymerization all can
adequately be used.
[0047] As the method of converting the halogen at a polymer
terminus, there may be mentioned, for example, the nucleophilic
substitution reaction using a nucleophilic reagent having a
reactive functional group. As such nucleophilic reagent, there may
be mentioned, among others, alcohol compounds, phenol compounds,
carboxylic compounds, amine compounds and amide compounds each
having a reactive functional group, and alkali metal salts or
ammonium salts thereof. Carbanions having a reactive functional
group and stabilized by an electron-attracting substituent are also
suited for use. Specific examples of the nucleophilic reagent are
shown below.
[0048] As the alcohols having a reactive function group, there may
be mentioned, among others, aliphaticdiols such as ethylene glycol;
alicyclic diols such as 1,2-cyclopentanediol, 1,3-cyclopentanediol,
1,2-cyclohexanediol, 1,3-cyclohexanediol and 1,4-cyclohexanediol;
amino-containing alcohols such as ethanolamine; and the like.
[0049] As the phenols having a reactive function group, there may
be mentioned, among others, compounds having two phenolic hydroxyl
groups in each molecule, such as hydroquinone, catechol,
resorcinol, bisphenol A and biphenol; and the like.
[0050] As the carboxylic acids having a reactive function group,
there may be mentioned, among others, hydroxyl-containing
carboxylic acid compounds such as HO--(CH.sub.2)--CO.sub.2H (n
being an integer of 0 to 10); carboxylic acid compounds having a
phenolic hydroxyl group, such as hydroxybenzoic acid and
4'-hydroxy-4-biphenylcarboxylic acid; amino acid compounds; dibasic
carboxylic acids such as oxalic acid, malonic acid, succinic acid,
glutaric acid, adipic acid, HO.sub.2C--(CH.sub.2).sub.n--C-
O.sub.2H (n being an integer of 5 to 20),
1,2-cyclopentanedicarboxylic acid, 1,2-cyclohexanedicarboxylic
acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic
acid, maleic acid, fumaric acid, malic acid, tartaric acid,
phthalic acid, isophthalic acid, terephthalic acid and
naphthalenedicarboxylic acids; halides of the dibasic carboxylic
acids mentioned above; cyclic acid anhydrides such as succinic
anhydride, maleic anhydride and phthalic anhydride; and the
like.
[0051] As the amines having a reactive function group, there may be
mentioned, among others, hydroxyl-containing amines such as
ethanolamine; diamine compounds such as ethylenediamine,
1,3-diaminopropane, 1,2-diaminopropane, 1,4-diaminobutane,
1,2-diamino-2-methylpropane, 1,5-diaminopentane,
2,2-dimethyl-1,3-propanediamine, 1,6-hexanediamine,
1,7-heptanediamine, 1,8-octanediamine, 1,9-nonanediamine,
1,10-decanediamine, 1,12-dodecanediamine,
4,4'-methylenebis(cyclohexylami- ne), 1,2-diaminocyclohexane,
1,3-diaminocyclohexane, 1,4-diaminocyclohexane,
1,2-phenylenediamine, 1,3-phenylenediamine, 1,4-phenylenediamine
and .alpha.,.alpha.'-diamino-p-xylene; and the like.
[0052] Alkali metal salts and ammonium salts of the above-mentioned
various nucleophilic reagents may also be used as nucleophilic
reagents. The alkali metal salts and ammonium salts are obtained by
reacting the above nucleophilic reagents with a basic compound. The
basic compound is not particularly restricted but, for preparing
alkali metal salts, for instance, use is made of alkali metals such
as potassium, sodium and lithium; metal alkoxides such as sodium
methoxide, potassium methoxide, lithium methoxide, sodium ethoxide,
potassium ethoxide, lithium ethoxide, sodium tert-butoxide and
potassium tert-butoxide; carbonates such as sodium carbonate,
potassium carbonate, lithium carbonate and sodium hydrogen
carbonate; hydroxides such as sodium hydroxide and potassium
hydroxide; hydrides such as sodium hydride and potassium hydride;
organolithium compounds such as methyllithium, ethyllithium,
n-butyllithium, tert-butyllithium, lithium diisopropylamide and
lithium hexamethyldisilazide; and like bases. In preparing ammonium
salts, use is made of, for example, ammonium, amines such as
trimethylamine, triethylamine, tributylamine,
tetramethylethylenediamine and pentamethyl-diethylenetriamine;
pyridine compounds such as pyridine and picoline; and like nitrogen
bases.
[0053] Quaternary ammonium salts may also be used as the
nucleophilic reagent. The quaternary ammonium salts can be prepared
by reacting the alkali metal salts mentioned above with a
quaternary ammonium halide. The quaternary ammonium halide is not
particularly restricted but includes, among others,
tetramethylammonium halides, tetraethylammonium halides,
trimethylbenzylammonium halides, trimethyldodecylammonium halides
and tetrabutylammonium halides.
[0054] As the solvent to be used in the nucleophilic substitution
reaction, there may be mentioned, among others, hydrocarbon
solvents such as benzene, toluene and xylene; halogenated
hydrocarbon solvents such as methylene chloride, chloroform and
chlorobenzene; ether solvents such as diethyl ether, dioxane,
tetrahydrofuran, diphenyl ether, anisole and dimethoxybenzene;
ester solvents such as ethyl acetate and butyl acetate; ketone
solvents such as acetone, methyl ethyl ketone and methyl isobutyl
ketone; alcohol solvents such as methanol, ethanol, propanol,
isopropanol, n-butyl alcohol and tert-butyl alcohol; nitrile
solvents such as acetonitrile, propionitrile and benzonitrile;
amide solvents such as dimethylformamide, dimethylacetamide and
hexamethylphosphoric triamide; sulfoxide solvents such as dimethyl
sulfoxide; carbonate solvents such as ethylene carbonate and
propylene carbonate; water and so on. These may be used singly or
two or more of them may be used in admixture. The substitution
reaction can be carried out at 0 to 150.degree. C.
[0055] For promoting the substitution reaction, a basic compound
may be added to the reaction system. All the bases already
specifically mentioned hereinabove may adequately be used as the
base.
[0056] A phase transfer catalyst such as a quaternary ammonium
halide and crown ether may also be added to the reaction system for
promoting the substitution reaction. Those already specifically
mentioned hereinabove may be used as the quaternary ammonium
halide.
[0057] As already mentioned hereinabove, a vinyl polymer having a
functional group at both termini can be produced also by
polymerizing vinyl monomers using an initiator having a reactive
functional group, followed by coupling of a polymer terminus with
another. As the method of coupling, there may be mentioned, for
example, a method which comprises coupling terminal halogens with
each other using a compound having a total of two or more
functional groups which may be the same or different and each can
substitute the terminal halogen in the general formula 3.
[0058] The compound having a total of two or more functional groups
each capable of substituting the terminal halogen atom is not
particularly restricted but preferably is a polyol, polyamine,
polycarboxylic acid or polythiol, or a salt thereof, an alkali
metal sulfide or the like. Specific examples of these compounds are
as follows:
[0059] Polyols such as ethylene glycol, 1,2-propanediol,
1,3-propanediol, 2-methyl-1,3-propanediol,
2,2-dimethyl-1,3-propanediol, 1,4-butanediol, 1,3-butanediol,
1,2-butanediol, 2,3-butanediol, pinacol, 1,5-pentanediol,
1,4-pentanediol, 2,4-pentanediol, 1,6-hexanediol, 1,7-heptanediol,
1,8-octanediol, 1,9-nonanediol, 1,10-decanediol, 1,12-dodecanediol,
1,2-cyclopentanediol, 1,3-cyclopentanediol, 1,2-cyclohexanediol,
1,3-cyclohexanediol, 1,4-cyclohexanediol, glycerol,
1,2,4-butanetriol, catechol, resorcinol, hydroquinone,
1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene,
1,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 2,2'-biphenol,
4,4'-biphenol, bis(4-hydroxyphenyl)methane,
4,4'-isopropylidenephenol, 3,3'-(ethylenedioxy)diphenol,
.alpha.,.alpha.'-dihydroxy-p-xylene,
1,1,1-tris(4-hydroxyphenyl)ethane, pyrogallol and
1,2,4-benzenetriol; and alkali metal salts of the above polyol
compounds;
[0060] Polyamines such as ethylenediamine, 1,3-diaminopropane,
1,2-diaminopropane, 1,4-diaminobutane, 1,2-diamino-2-methylpropane,
1,5-diaminopentane, 2,2-dimethyl-1,3-propanediamine,
1,6-hexanediamine, 1,7-heptanediamine, 1,8-octanediamine,
1,9-diaminononane, 1,10-diaminodecane, 1,12-diaminododecane,
4,4'-methylenebis(cyclohexylami- ne), 1,2-diaminocyclohexane,
1,3-diaminocyclohexane, 1,4-diaminocyclohexane,
1,2-phenylenediamine, 1,3-phenylenediamine, 1,4-phenylenediamine
and .alpha.,.alpha.'-diamino-p-xylene; and alkali metal salts of
the above polyamines;
[0061] Polycarboxylic acids such as oxalic acid, malonic acid,
methylmalonic acid, dimethylmalonic acid, succinic acid,
methylsuccinic acid, glutaric acid, adipic acid,
1,7-heptanedicarboxylic acid, 1,8-octanedicarboxylic acid,
1,9-nonanedicarboxylic acid, 1,10-decanedicarboxylic acid,
1,11-undecanedicarboxylic acid, 1,12-dodecanedicarboxylic acid,
1,2-cyclopentanedicarboxylic acid, 1,2-cyclohexane-dicarboxylic
acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic
acid, 1,3,5-cyclohexanetricarboxylic acid, phthalic acid,
isophthalic acid, terephthalic acid, 1,2,3-benzenetricarboxylic
acid and 1,2,4,5-benzene-tetracarboxylic acid; and alkali metal
salts of the above polycarboxylic acids;
[0062] Polythiols such as 1,2-ethanedithiol, 1,3-propanedithiol,
1,4-butanedithiol, 2,3-butanedithiol, 1,5-pentanedithiol,
1,6-hexanedithiol, 1,7-heptanedithiol, 1,8-octanedithiol,
1,9-nonanedithiol, 2-mercaptoethyl ether,
p-xylene-.alpha.,.alpha.'-dithi- ol, 1,2-benzenedithiol,
1,3-benzenedithiol and 1,4-benzenedithiol; and alkali metal salts
of the above polythiol compounds;
[0063] Lithium sulfide, sodium sulfide and potassium sulfide; and
so forth.
[0064] For promoting the substitution reaction, a basic compound or
a quaternary ammonium salt may also be added. As specific examples
thereof, those already specifically mentioned hereinabove may be
mentioned.
[0065] The vinyl polymer having a reactive functional group at a
main chain terminus according to the first aspect of the invention
can also be produced by radical polymerization of a vinyl
monomer(s) using a chain transfer agent having a reactive function
group(s).
[0066] The reactive functional group-terminated vinyl polymer
obtained in the above manner, when reacted with a compound
represented by the general formula (2), gives a vinyl polymer
terminally having a group represented by the general formula (1).
The reactive functional group-terminated vinyl polymer is produced
by the method already mentioned.
[0067] The compound represented by the general formula (2) is not
particularly restricted but epichlorohydrin and epibromohydrin are
preferred because of ready availability.
[0068] As the solvent to be used in carrying out the reaction,
there may be mentioned, among others, hydrocarbon solvents such as
benzene, toluene and xylene; halogenated hydrocarbon solvents such
as methylene chloride, chloroform and chlorobenzene; ether solvents
such as diethyl ether, dioxane, tetrahydrofuran, diphenyl ether,
anisole and dimethoxybenzene; ester solvents such as ethyl acetate
and butyl acetate; ketone solvents such as acetone, methyl ethyl
ketone and methyl isobutyl ketone; alcohol solvents such as
methanol, ethanol, propanol, isopropanol, n-butyl alcohol and
tert-butyl alcohol; nitrile solvents such as acetonitrile,
propionitrile and benzonitrile; amide solvents such as
dimethylformamide, dimethylacetamide and hexamethylphosphoric
triamide; sulfoxide solvents such as dimethyl sulfoxide; carbonate
solvents such as ethylene carbonate and propylene carbonate; water
and so on. These may be used singly or two or more of them may be
used in admixture.
[0069] The reaction is desirably carried out in the presence of a
basic compound. As such basic compound, all specifically mentioned
hereinabove can adequately be used. For accelerating the reaction,
any of the phase transfer catalysts known in the art may be added
to the reaction system. As examples of the phase transfer catalyst,
there may be mentioned quaternary ammonium salts and crown ethers,
among others.
[0070] The vinyl polymer having a group represented by the general
formula (1) as produced according to the invention can be made into
an epoxy resin composition and this constitutes one aspect of the
invention.
[0071] This composition generally comprises the following two
components: the vinyl polymer having a group represented by the
general formula (1) at a main chain terminus and an epoxy resin
curing agent.
[0072] The vinyl polymer may comprise a single species or a mixture
of two or more species.
[0073] The epoxy resin curing agent is not particularly restricted
but use may be made of such photo- or ultraviolet-curing agents as
aliphatic amines, alicyclic amines, aromatic amines; acid
anhydrides; polyamides; imidazoles; amineimides; urea; melamine and
derivatives thereof; polyamine salts; phenol resins;
polymercaptans, polysulfides; aromaticdiazoniumsalts;
diallyliodoniumsalts, triallylsulfonium salts, triallylselenium
salts and the like.
[0074] Further, an epoxy resin known in the art may be used in
combination with the vinyl polymer of the invention. Such epoxy
resin is not particularly restricted but includes, but is not
limited to, glycidyl ether type epoxy resins derived from bisphenol
A, bisphenol F or tetrabromobisphenol A, novolak type epoxy resins,
hydrogenated bisphenol A-based epoxy resins, glycidyl ether type
epoxy resins derived from bisphenol A-propylene oxide adducts,
p-hydroxybenzoic acid glycidyl ether ester type epoxy resins,
m-aminophenol-based epoxy resins, diaminodiphenylmethane-based
epoxy resins, urethane-modified epoxy resins, various alicyclic
epoxy resins, N,N-diglycidylaniline, N,N-diglycidyl-o-toluidine,
triglycidyl isocyanurate, polyalkylene glycol diglycidyl ethers,
glycidyl ethers of polyhydric alcohols such as glycerol, hydantoin
type epoxy resins, epoxidization products from unsaturatedpolymers
such as petroleum resins and the like. These epoxy resins may be
used singly or two or more of them may be used in admixture.
[0075] For improving the mechanical/physical properties or cured
products, various fillers may be incorporated. Usable as the
fillers are reinforcing fillers such as fumed silica, precipitated
silica, silicic anhydride, hydrous silicic acid and carbon black;
such fillers as calcium carbonate, magnesium carbonate,
diatomaceous earth, calcined clay, clay, talc, titanium oxide,
bentonite, organic bentonite, ferric oxide, zinc oxide, activated
zinc white and sirasu balloons; and fibrous fillers such as
asbestos, and glass fibers and filaments. For obtaining cured
products having high strength using these fillers, a filler
selected mainly from among-fumed silica, precipitated silica,
silicic anhydride, hydrous silicic acid, carbon black,
surface-treated, finely divided calcium carbonate, calcined clay,
clay, activated zinc white and the like is used in an amount within
the range of 1 to 100 parts by weight per 100 parts by weight of
the (meth) acrylic polymer, whereupon favorable results can be
obtained. For obtaining cured products low in strength but high in
elongation, a filler selected mainly from among titanium oxide,
calcium carbonate, talc, ferric oxide, zinc oxide and sirasu
balloons is used in an amount within the range of 5 to 200 parts by
weight per 100 parts of the (meth)acrylic polymer to give favorable
results. These fillers may be used singly or two or more of them
may be used in admixture.
[0076] It is also possible to use various plasticizers, coupling
agents, mold release agents and so forth.
[0077] Now, the second aspect of the invention is explained.
[0078] The second aspect of the invention lies in an epoxy resin
composition comprising two components, namely (A) an epoxy resin
and (B) a vinyl polymer having a main chain produced by living
radical polymerization and a reactive functional group at a main
chain terminus.
[0079] The component (A) epoxy resin according to the second aspect
of the invention is not particularly restricted but includes
various ones. Examples include, but are not limited to glycidyl
ether type epoxy resins derived from bisphenol A, bisphenol F,
tetrabromobisphenol A or the like, novolak type epoxy resins,
hydrogenated bisphenol A-based epoxy resins, glycidyl ether type
epoxy resins derived from bisphenol A-propylene oxide adducts,
p-hydroxybenzoic acid glycidyl ether ester type epoxy resins,
m-aminophenol-based epoxy resins, diaminodiphenylmethane-based
epoxy resins, urethane-modified epoxy resins, various alicyclic
epoxy resins, N,N-diglycidylaniline, N,N-diglycidyl-o-toluidine,
triglycidyl isocyanurate, polyalkylene glycol diglycidyl ethers,
glycidyl ethers of polyhydric alcohols such as glycerol, hydantoin
type epoxy resins, epoxidation products derived from unsaturated
polymers such as petroleum resins, and the like. These epoxy resins
may be used singly or two or more of them may be used in
admixture.
[0080] The reactive functional group according to the second aspect
of the invention is not particularly restricted but may be any
functional group capable of reacting with the epoxy group of the
epoxy resin to thereby effect crosslinking. As examples, there may
be mentioned an alcoholic hydroxyl group, a phenolic hydroxyl
group, an amino group, an amide group and a carboxyl group.
[0081] The vinyl type monomer constituting the main chain of the
vinyl polymer in the second aspect of the invention is not
particularly restricted but may be any of those mentioned
hereinabove referring to the first aspect of the invention.
[0082] The molecular weight distribution of the above vinyl polymer
is not particularly restricted but, generally, the ratio (Mw/Mn) of
weight average molecular weight (Mw) to number average molecular
weight (Mn) as determined by gel permeation chromatography is less
than 1.8, preferably not more than 1.7, more preferably not more
than 1.6, still more preferably not more than 1.5, especially
preferably not more than 1.4, most preferably not more than 1.3. In
the practice of the invention, GPC measurements are generally
carried out using polystyrene gel columns with chloroform as the
mobile phase and the number average molecular weight and so on can
be determined on the polystyrene equivalent basis.
[0083] The number average molecular weight of the vinyl polymer in
the practice of the second aspect of the invention is not
particularly restricted but preferably is within the range of 500
to 1,000,000, more preferably 1,000 to 100,000.
[0084] The vinyl polymer having a reactive functional group which
is to be used in the practice of the second aspect of the invention
may be any polymer terminally having a reactive functional group.
In view of the ease of control of the molecular weight, molecular
weight distribution andof terminal functional group introduction,
however, the above-mentioned living radical polymerization method
is preferably employed as the method of producing the main chain of
the vinyl polymer.
[0085] For producing the vinyl polymer having a reactive functional
group by using the living radical polymerization, a process
comprising the following steps, for instance, may be mentioned:
[0086] (1) Forming a vinyl polymer bypolymerizing a vinyl
monomer(s) bythe living radical polymerization technique and
[0087] (2) Reacting, at the end point of the polymerization, the
polymer with a compound having both a reactive functional group and
an ethylenically unsaturated group.
[0088] The compound having both an ethylenically unsaturated group
and a reactive functional group is not particularly restricted but
includes, among others, hydroxy-containing vinyl monomers such as
2-hydroxyethyl (meth)acrylate and 2-hydroxypropyl (meth) acrylate;
amido-containing vinyl monomers such as (meth) acrylamide;
amino-containing vinyl monomers such as 2-aminoethyl
(meth)acrylate; carboxyl-containing vinyl monomers such as (meth)
acrylic acid, maleic acid, maleic acid monoalkyl esters, fumaric
acid and fumaric acid monoalkyl esters, and the like.
[0089] Further, maleic anhydride; maleimide monomers such as
maleimide, methylmaleimide, ethylmaleimide, propylmaleimide,
butylmaleimide, hexylmaleimide, octylmaleimide, dodecylmaleimide,
stearylmaleimide, phenylmaleimide and cyclohexylmaleimide;
tert-butoxystyrene; acetoxystyrene; and the like may also be
used.
[0090] Further, phenols having an ethylenically unsaturated group,
such as o-, m- and p-allylphenol and o-, m- and p-allyloxyphenol;
alcohols having an ethylenically unsaturated group, such as allyl
alcohol, butenyl alcohol, pentenyl alcohol and hexenyl alcohol;
amines having an ethylenically unsaturated group, such as
allylamine, butenylamine, pentenylamine and hexenylamine;
carboxylic acid compounds having an ethylenically unsaturated
group, such as vinyl acetate, pentenoic acid, heptenoic acid and
undecenoic acid; and the like may also be used.
[0091] When the compound having both an ethylenically unsaturated
group and a reactive functional group is reacted with the polymer
terminus, the compound as such may be subjected to reaction. In
some cases, however, the reactive functional group may affect the
polymer terminus and, in such cases, it may be used in the form
having a protective group. As the protective group, there may be
mentioned acetyl, silyl groups and alkoxy groups, among others.
Suited for use as the compound having a protective group are all
the compounds mentioned above whose functional group is
protected.
[0092] The compound having both a reactive functional group and an
ethylenically unsaturated group may be subjected to reaction with
the polymer isolated after completion of the vinyl monomer
polymerization by newly adding that compound to that polymer
together with a catalyst or may be added and subjected to reaction
in the course of polymerization (in situ). In the latter case, the
monomer conversion of the first polymerization should be as high as
possible, preferably not less than 80%. If the conversion is not
more than 80%, the reactive functional group is distributed on side
chains, not at molecular termini, whereby the mechanical
characteristics of cured products will be impaired. In principle,
the addition of such compound having a reactive functional group
and an ethylenically unsaturated group in an equivalent amount
relative to the whole number of termini results in introduction of
the functional group at all termini. For securing the introduction
of the functional group at all termini, however, it is
recommendable to use the compound in excess, specifically in an
amount of 1 to 5 times excess relative to the number of termini.
When it is used in an amount not less than 5 times, the functional
group is introduced terminally into the polymer at an excessively
high density and this is unfavorable from the cured product
physical properties viewpoint.
[0093] The vinyl polymer having a reactive functional group
according to the invention may also be produced by the following
steps:
[0094] (1) Producing a vinyl polymer terminally having a halogen,
and
[0095] (2) Converting the halogen at the polymer terminus to a
substituent having a reactive functional group.
[0096] A chlorine, bromine or iodine atom is preferred as the
halogen. As the method of producing the halogen-terminated vinyl
polymer, there may be mentioned the radical polymerization method
using a halide compound as a chain transfer agent and the
above-mentioned atom transfer radical polymerization. In view of
the ease of control of the molecular weight and molecular weight
distribution, the latter is preferred. The initiators, catalysts,
solvents, polymerization conditions and so forth as already
mentioned hereinabove specifically for atom transfer radical
polymerization all can adequately be used.
[0097] As the method of converting the halogen at a polymer
terminus, there may be mentioned, for example, the nucleophilic
substitution reaction using a nucleophilic reagent having a
reactive functional group. As such nucleophilic reagent, there may
be mentioned, among others, alcohols, phenols, carboxylic acids and
amines each having a reactive functional group, and alkali metal
salts or ammonium salts thereof. Carbanions having a reactive
functional group and stabilized by an electron-attracting
substituent are also suited for use. Specific examples of the
nucleophilic reagent are shown below.
[0098] As the alcohols having a reactive function group, there may
be mentioned, among others, aliphatic diols such as ethylene
glycol; alicyclic diols such as 1,2-cyclopentanediol,
1,3-cyclopentanediol, 1,2-cyclohexanediol, 1,3-cyclohexanediol and
1,4-cyclohexanediol; amino-containing alcohols such as
ethanolamine; and the like.
[0099] As the phenols having a reactive function group, there may
be mentioned, among others, compounds having two phenolic hydroxyl
groups in each molecule, such as hydroquinone, catechol,
resorcinol, bisphenol A and biphenol; and the like.
[0100] As the carboxylic acids having a reactive function group,
there may be mentioned, among others, hydroxyl-containing
carboxylic acid compounds such as HO--(CH.sub.2).sub.n--CO.sub.2H
(n being an integer of 0 to 10); carboxylic acid compounds having a
phenolic hydroxyl group, such as hydroxybenzoic acid and
4'-hydroxy-4-biphenylcarboxylic acid; amino acid compounds; dibasic
carboxylic acids such as oxalic acid, malonic acid, succinic acid,
glutaric acid, adipic acid, HO.sub.2C--(CH.sub.2).sub.n--C-
O.sub.2H (n being an integer of 5 to 20),
1,2-cyclopentanedicarboxylic acid, 1,2-cyclohexanedicarboxylic
acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic
acid, maleic acid, fumaric acid, malic acid, tartaric acid,
phthalic acid, isophthalic acid, terephthalic acid and
naphthalenedicarboxylic acids; halides of the dibasic carboxylic
acids mentioned above; cyclic acid anhydrides such as succinic
anhydride, maleic anhydride and phthalic anhydride; and the
like.
[0101] As the amines having a reactive function group, there may be
mentioned, among others, aliphatic amines, alicyclic amines and
aromatic amines each having a reactive functional group.
[0102] Alkali metal salts and ammonium salts of the above-mentioned
various nucleophilic reagents may also be used as nucleophilic
reagents. The alkali metal salts and ammonium salts are obtained by
reacting the above nucleophilic reagents with a basic compound. The
basic compound is not particularly restricted but includes, among
others, alkali metals such as potassium, sodium and lithium; metal
alkoxides such as sodium methoxide, potassium methoxide, lithium
methoxide, sodium ethoxide, potassium ethoxide, lithium ethoxide,
sodium tert-butoxide and potassium tert-butoxide; carbonates such
as sodium carbonate, potassium carbonate, lithium carbonate and
sodium hydrogen carbonate; hydroxides such as sodium hydroxide and
potassium hydroxide; hydrides such as sodium hydride and potassium
hydride; organolithium compounds such as methyllithium,
ethyllithium, n-butyllithium, tert-butyllithium, lithium
diisopropylamide and lithium hexamethyldisilazide; ammonium, amines
such as trimethylamine, triethylamine, tributylamine,
tetramethylethylenediamine and pentamethyldiethylenetriamine;
pyridine compounds such as pyridine and picoline; and the like.
[0103] Quaternary ammonium salts may also be used as the
nucleophilic reagent. The quaternary ammonium salts can be prepared
by reacting the alkali metal salts mentioned above with a
quaternary ammonium halide. The quaternary ammonium halide is not
particularly restricted but includes, among others,
tetramethylammonium halides, tetraethylammonium halides,
trimethylbenzylammonium halides, trimethyldodecylammonium halides
and tetrabutylammonium halides.
[0104] As the solvent to be used in the nucleophilic substitution
reaction, there may be mentioned, among others, hydrocarbon
solvents such as benzene, toluene and xylene; halogenated
hydrocarbon solvents such as methylene chloride, chloroform and
chlorobenzene; ether solvents such as diethyl ether, dioxane,
tetrahydrofuran, diphenyl ether, anisole and dimethoxybenzene;
ester solvents such as ethyl acetate and butyl acetate; ketone
solvents such as acetone, methyl ethyl ketone and methyl isobutyl
ketone; alcohol solvents such as methanol, ethanol, propanol,
isopropanol, n-butyl alcohol and tert-butyl alcohol; nitrile
solvents such as acetonitrile, propionitrile and benzonitrile;
amide solvents such as dimethylformamide, dimethylacetamide and
hexamethylphosphoric triamide; sulfoxide solvents such as dimethyl
sulfoxide; carbonate solvents such as ethylene carbonate and
propylene carbonate; water and so on. These may be used singly or
two or more of them may be used in admixture. The substitution
reaction can be carried out at 0 to 150.degree. C.
[0105] For promoting the substitution reaction, a basic compound
may be added to the reaction system. All the bases already
specifically mentioned hereinabove may adequately be used as the
base.
[0106] A phase transfer catalyst such as a quaternary ammonium
halide and crown ether may also be added to the reaction system for
promoting the substitution reaction.
[0107] As already mentioned hereinabove, a vinyl polymer having a
functional group at both termini can be produced also by
polymerizing vinyl monomers using an initiator having a reactive
functional group, followed by coupling of a polymer terminus with
another. As the method of coupling, there may be mentioned, for
example, a method which comprises coupling terminal halogens with
each other using a compound having a total of two or more
functional groups which may be the same or different and each can
substitute the polymer terminal halogen.
[0108] The compound having a total of two or more functional groups
which may be the same or different and each can substitute the
polymer terminal halogen is not particularly restricted but
preferably is a polyol, polyamine, polycarboxylic acid or
polythiol, or a salt thereof, an alkali metal sulfide or the like.
Specific examples of these compounds are as follows:
[0109] Polyols such as ethylene glycol, 1,2-propanediol,
1,3-propanediol, 2-methyl-1,3-propanediol,
2,2-dimethyl-1,3-propanediol, 1,4-butanediol, 1,3-butanediol,
1,2-butanediol, 2,3-butanediol, pinacol, 1,5-pentanediol,
1,4-pentanediol, 2,4-pentanediol, 1,6-hexanediol, 1,7-heptanediol,
1,8-octanediol, 1,9-nonanediol, 1,10-decanediol, 1,12-dodecanediol,
1,2-cyclopentanediol, 1,3-cyclopentanediol, 1,2-cyclohexanediol,
1,3-cyclohexanediol, 1,4-cyclohexanediol, glycerol,
1,2,4-butanetriol, catechol, resorcinol, hydroquinone,
1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene,
1,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 2,2'-biphenol,
4,4'-biphenol, bis(4-hydroxyphenyl)methane,
4,4'-isopropylidenephenol, 3,3'-(ethylenedioxy)diphenol,
.alpha.,.alpha.'-dihydroxy-p-xylene,
1,1,1-tris(4-hydroxyphenyl)ethane, pyrogallol and
1,2,4-benzenetriol; and alkali metal salts of the above polyol
compounds;
[0110] Polyamines such as ethylenediamine, 1,3-diaminopropane,
1,2-diaminopropane, 1,4-diaminobutane, 1,2-diamino-2-methylpropane,
1,5-diaminopentane, 2,2-dimethyl-1,3-propanediamine,
1,6-hexanediamine, 1,7-heptanediamine, 1,8-octanediamine,
1,9-diaminononane, 1,10-diaminodecane, 1,12-diaminododecane,
4,4'-methylenebis(cyclohexylami- ne), 1,2-diaminocyclohexane,
1,3-diaminocyclohexane, 1,4-diaminocyclohexane,
1,2-phenylenediamine, 1,3-phenylenediamine, 1,4-phenylenediamine
and .alpha.,.alpha.'-diamino-p-xylene; and alkali metal salts of
the above polyamines;
[0111] Polycarboxylic acids such as oxalic acid, malonic acid,
methylmalonic acid, dimethylmalonic acid, succinic acid,
methylsuccinic acid, glutaric acid, adipic acid,
1,7-heptanedicarboxylic acid, 1,8-octanedicarboxylic acid,
1,9-nonanedicarboxylic acid, 1,10-decanedicarboxylic acid,
1,11-undecanedicarboxylic acid, 1,12-dodecanedicarboxylic acid,
1,2-cyclopentanedicarboxylic acid, 1,2-cyclohexane-dicarboxylic
acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic
acid, 1,3,5-cyclohexanetricarboxylic acid, phthalic acid,
isophthalic acid, terephthalic acid, 1,2,3-benzenetricarboxylic
acid and 1,2,4,5-benzenetetracarboxylic acid; and alkali metal
salts of the above polycarboxilic acids;
[0112] Polythiols such as 1,2-ethanedithiol, 1,3-propanedithiol,
1,4-butanedithiol, 2,3-butanedithiol, 1,5-pentanedithiol,
1,6-hexanedithiol, 1,7-heptanedithiol, 1,8-octanedithiol,
1,9-nonanedithiol, 2-mercaptoethyl ether,
p-xylene-.alpha.,.alpha.'-dithi- ol, 1,2-benzenedithiol,
1,3-benzenedithiol and 1,4-benzenedithiol; and alkali metal salts
of the above polythiol compounds;
[0113] Lithium sulfide, sodium sulfide and potassium sulfide; and
so forth.
[0114] For promoting the reaction, a basic compound may also be
added to the reaction system. As the base to be used, those already
specifically mentioned hereinabove all are suited for use.
[0115] For promoting the reaction, a phase transfer catalyst such
as a quaternary ammonium halide and crown ether may also be added
to the reaction system.
[0116] The epoxy resin composition according to the second aspect
of the invention comprises, as essential components, the epoxy
resin, namely the above-mentioned (A) component, and the vinyl
polymer terminally having a reactive functional group, namely the
above-mentioned (B) component. The mixing ratio between the both
components is generally such that the vinyl polymer accounts for
0.1 to 1,000 parts by weight, preferably 1 to 500 parts by weight,
more preferably 1 to 200 parts by weight, per 100 parts by weight
of the epoxy resin. At an addition amount below 0.1 part by weight,
the effects of incorporation are not fully produced. At an amount
above 1,000 parts by weight, the rate of curing unfavorably
falls.
[0117] The invention also includes the combined use of an epoxy
resin curing agent known in the art. As examples of such curing
agent, there may be mentioned:
[0118] Primary amines such as diethylenetriamine,
triethylenetetramine, tetraethylenepentamine, hexamethylenediamine,
diethylaminopropylamine, N-aminoethylpiperazine, BASF's Lamilon
C-260, CIBA's Araldite HY-964, Rohm and Haas' Menthenediamine,
isophoronediamine, diaminodicyclohexylmethane, m-xylylenediamine,
m-phenylenediamine, diaminodiphenylmethane and diaminodiphenyl
sulfone, straight-chain diamines represented by
(CH.sub.3).sub.2N(CH.sub.2) N(CH.sub.3).sub.2 (n being an integer
of 1 to 10), straight-chain tertiary amines represented by
(CH.sub.3).sub.2N(CH.sub.2) CH.sub.3 (n being an integer of 0 to
10), tetramethylguanidine, alkyl-tertiary monoamines represented by
N[(CH.sub.2).sub.nCH.sub.3] .sub.3 (n being an integer of 1 to 10),
triethanolamine, piperidine, N,N'-dimethylpiperazine,
triethylenediamine, pyridine, picoline, diazabicycloundecene,
benzyldimethylamine, 2-(dimethylaminomethyl)phenol,
2,4,6-tris(dimethyl-aminomethyl)phenol and like secondary or
tertiary amines, acid anhydrides such as phthalic anhydride,
trimellitic anhydride and benzophenonetetracarboxylic anhydride,
various polyamide resins, dicyandiamide and derivatives thereof,
various imidazoles, and the like.
[0119] For improving the mechanical/physical properties of cured
products, various fillers may be incorporated. Usable as the
fillers are reinforcing fillers such as fumed silica, precipitated
silica, silicic anhydride, hydrous silicic acid and carbon black;
such fillers as calcium carbonate, magnesium carbonate,
diatomaceous earth, calcined clay, clay, talc, titanium oxide,
bentonite, organic bentonite, ferric oxide, zinc oxide, activated
zinc white and sirasu balloons; and fibrous fillers such as
asbestos, and glass fibers and filaments. For obtaining cured
products having high strength using these fillers, a filler
selected mainly from among fumed silica, precipitated silica,
silicic anhydride, hydrous silicic acid, carbon black,
surface-treated, finely divided calcium carbonate, calcined clay,
clay, activated zinc white and the like is used in an amount within
the range of 1 to 100 parts by weight per 100 parts by weight of
the (meth) acrylic polymer, whereupon favorable results can be
obtained. For obtaining cured products low in strength but high in
elongation, a filler selected mainly from among titanium oxide,
calcium carbonate, talc, ferric oxide, zinc oxide and sirasu
balloons is usediin an amount within the range of 5 to 200 parts by
weight per 100 parts of the (meth)acrylic polymer to give favorable
results. These fillers may be used singly or two or more of them
may be used in admixture.
[0120] It is also possible to use various plasticizers, coupling
agents, mold release agents and so forth.
[0121] As specific uses of the composition of the present
invention, there may be mentioned, among others, sealing materials,
adhesives, pressure sensitive adhesives, elastic adhesives, coating
compositions, powder coating compositions, foamed or expanded
articles, potting agents for electric and electronic use, films,
molding materials and artificial marble.
BEST MODES FOR CARRYING OUT THE INVENTION
[0122] In the following, some specific examples of the present
invention are described together with a comparative example. They
are, however, by no means limitative of the scope of the invention.
In the examples, the "number average molecular weight" and
"molecular weight distribution (ratio between weight average
molecular weight and number average molecular weight)" were
determined by the standard polystyrene equivalent method using gel
permeation chromatography (GPC). Columns packed with crosslinked
polystyrene gels were used as GPC columns and chloroform was used
as the GPC solvent.
PRODUCTION EXAMPLE 1
Synthesis of Br-Terminated poly(butyl acrylate)
[0123] A 10-liter separable flask equipped with a reflux condenser
and a stirrer was charged with CuBr (28.0 g, 0.20 mol) and the
reactor inside was purged with nitrogen. Acetonitrile (559 mL) was
added, and the contents were stirred on an oil bath at 70.degree.
C. for 40 minutes. Thereto were added butyl acrylate (1.00 kg),
diethyl 2,5-dibromoadipate (117 g, 0.325 mol) and
pentamethyldiethylenetriamine (hereinafter, "triamine"; 1.7 mL, 1.4
g, 8.1 mmol) to thereby start the reaction. While heating at
70.degree. C. with stirring, butyl acrylate (4.00 kg) was added
dropwise continuously. During dropping of butyl acrylate, the
triamine (8.5 mL, 7.06 g, 0.041 mol) was further added.
[0124] The reaction mixture was diluted with toluene and passed
through an activated alumina column, and the volatile matter was
then distilled off under reduced pressure to give a Br-terminated
polymer (polymer [1]). The polymer [1] had a number average
molecular weight of 19,500 and a molecular weight distribution of
1.17.
EXAMPLE 1
Synthesis of a phenol Group-Terminated poly(butyl acrylate)
[0125] A 100-ml reaction vessel was charged with the polymer [1]
(50 g) obtained in Production Example 1, potassium
p-hydroxybenzoate (1.96 g, 11.1 mmol) and dimethylacetamide (50
mL). The contents were heated at 70.degree. C. with stirring for 3
hours under a stream of nitrogen. The reaction mixture was diluted
with toluene and passed through an activated alumina column, and
the volatile matter was then distilled off under reduced pressure.
The polymer obtained was dissolved in toluene and the solution was
again passed through an activated alumina column, and the toluene
was distilled off under reduced pressure to give phenol-terminated
poly(butyl acrylate) (polymer [2]). The average number of phenol
groups introduced per molecule of the polymer was determined to be
2.3 by .sup.1H NMR spectrometry.
EXAMPLE 2
Synthesis of an epoxy-terminated poly(butyl acrylate)
[0126] A 50-mL two-necked flask equipped with a reflux condenser
was charged with the polymer [2] (5.0 g) obtained in Production
Example 2, tert-butoxypotassium (0.070 mg) and dimethylacetamide
(10 mL), and the contents were heated at 70.degree. C. with
stirring. Epichlorohydrin (2.5 mL) was added, and the mixture was
heated at 70.degree. C. with stirring for 1 hour. The reaction
mixture was diluted with toluene and passed through an activated
alumina column, and the volatile matter was then
distilledoffunderreducedpressure. The polymerobtained was dissolved
in toluene and the solution was again passed through an activated
alumina column, and the toluene was distilled off under reduced
pressure to give a polymer [3].
[0127] Upon analysis of the polymer [3] by .sup.1H NMR
spectrometry, an epoxy group-due peak was observed at around 2.9
ppm, indicating that the epoxy group introduction into the polymer
had been accomplished.
EXAMPLE 3
Modification of an Epoxy Resin
[0128] A bisphenol A-based liquid epoxy resin (2.0 g; Epikote 825,
product of Yuka Shell Epoxy Kabushiki Kaisha), the polymer [2] (2.0
g) obtained in Example 1 and a tertiary amine (0.080 g; Epicure
3010, product of Yuka Shell Epoxy Kabushiki Kaisha) were thoroughly
mixed up and the mixture was heated at 150.degree. C. for 1 hour to
give a cured product. The cured product had flexibility. The
uncured fraction of the cured product was extracted with toluene
and the gel fraction of the cured product was determined based on
the weight ratio between the weight of the cured product before
extraction and that after extraction and found to be 91%.
INDUSTRIAL APPLICABILITY
[0129] The terminally reactive vinyl polymer and epoxy resin
composition of the invention can improve the hard and brittle
characteristics of epoxy resins and provide them flexibility,
without impairing the favorable characteristics of the epoxy
resins, such as the bond properties.
* * * * *