U.S. patent application number 11/114249 was filed with the patent office on 2005-11-17 for method and apparatus for microcellular polymer extrusion.
This patent application is currently assigned to Trexel, Inc.. Invention is credited to Anderson, Jere R., Burnham, Theodore A., Cha, Sung Woon, Kim, Roland Y., Pallaver, Matthew, Stevenson, James F., Suh, Nam P., Walat, Robert H..
Application Number | 20050256215 11/114249 |
Document ID | / |
Family ID | 27362362 |
Filed Date | 2005-11-17 |
United States Patent
Application |
20050256215 |
Kind Code |
A1 |
Burnham, Theodore A. ; et
al. |
November 17, 2005 |
Method and apparatus for microcellular polymer extrusion
Abstract
Continuous polymeric extrusion nucleation systems and methods
useful for making polymeric microcellular foamed materials,
including crystalline and semi-crystalline polymeric microcellular
materials, are provided. Pressure drop rate is an important feature
in some embodiments, and the invention provides systems for
controlling these and other parameters. One aspect involves a
multiple-pathway nucleator that is separated from a shaping die by
a residence chamber. Another aspect involves a die for making
advantageously thick articles, including a multiple-pathway
nucleation section. Microcellular material can be continuously
extruded onto wire, resulting in a very thin, essentially
closed-cell microcellular insulating coating secured to a wire.
Other very thin microcellular products can be fabricated as
well.
Inventors: |
Burnham, Theodore A.;
(Winchester, MA) ; Cha, Sung Woon; (Juyup-Dong,
KR) ; Walat, Robert H.; (Boston, MA) ; Kim,
Roland Y.; (Somerville, MA) ; Anderson, Jere R.;
(Newburyport, MA) ; Stevenson, James F.;
(Morristown, NJ) ; Suh, Nam P.; (Sudbury, MA)
; Pallaver, Matthew; (Lexington, MA) |
Correspondence
Address: |
WOLF GREENFIELD & SACKS, PC
FEDERAL RESERVE PLAZA
600 ATLANTIC AVENUE
BOSTON
MA
02210-2211
US
|
Assignee: |
Trexel, Inc.
Woburn
MA
|
Family ID: |
27362362 |
Appl. No.: |
11/114249 |
Filed: |
April 25, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11114249 |
Apr 25, 2005 |
|
|
|
09626808 |
Jul 27, 2000 |
|
|
|
6884377 |
|
|
|
|
09626808 |
Jul 27, 2000 |
|
|
|
09258625 |
Feb 26, 1999 |
|
|
|
6284810 |
|
|
|
|
09258625 |
Feb 26, 1999 |
|
|
|
PCT/US97/15088 |
Aug 26, 1997 |
|
|
|
09258625 |
Feb 26, 1999 |
|
|
|
08777709 |
Dec 20, 1996 |
|
|
|
60024623 |
Aug 27, 1996 |
|
|
|
60026889 |
Sep 23, 1996 |
|
|
|
Current U.S.
Class: |
521/79 |
Current CPC
Class: |
B29K 2105/16 20130101;
B29C 48/29 20190201; B29C 44/3473 20130101; B29C 48/2886 20190201;
B29K 2105/0005 20130101; B29C 44/348 20130101; B29C 44/3446
20130101; B29C 48/06 20190201; B29C 44/322 20130101; B29C 44/461
20130101; B29C 44/468 20130101; B29C 48/07 20190201 |
Class at
Publication: |
521/079 |
International
Class: |
C08J 009/00 |
Claims
What is claimed is:
1. A system comprising: an extruder designed to convey a first
stream of a fluid, polymeric material in a downstream direction and
having a blowing agent port constructed and arranged to inject a
blowing agent into the stream, the extruder adapted to admix the
stream with the blowing agent to form a single-phase solution of
polymeric material and blowing agent; a nucleator constructed and
arranged to divide the single-phase solution of polymeric material
into separate portions and to continuously nucleate each of the
separate portions at a rate sufficient to form a microcellular
polymeric material.
2. A method comprising: establishing a stream of polymeric material
flowing at a rate of at least about 5 lbs per hour within a polymer
processing space between a rotating screw and an extruder barrel;
introducing, into the stream of polymeric material, a blowing agent
through a plurality of orifices of the extruder barrel while
passing the orifices with a flight of the rotating screw; and
admixing the polymeric material and the blowing agent to form a
single-phase solution of polymeric material and blowing agent.
3-10. (canceled)
11. A method comprising continuously extruding microcellular
polymeric material having cells of essentially uniform size of less
than about 50 microns average size from a single-phase solution of
polymeric material and blowing agent contained in extrusion
apparatus including a nucleating pathway, the blowing agent present
in the solution in an amount less than about 80 percent saturation
concentration as determined at the lowest pressure in the system
after the point of blowing agent injection prior to the nucleating
pathway.
12-13. (canceled)
Description
RELATED APPLICATIONS
[0001] This application commonly-owned, co-pending is a
continuation of U.S. application Ser. No. 09/626,808, filed Jul.
27, 2000, which is a divisional of U.S. application Ser. No.
09/258,625, filed Feb. 26, 1999, which is a continuation of Int'l
patent application serial no. PCT/US97/15088, filed Aug. 26, 1997,
which claims priority to commonly-owned, co-pending U.S.
provisional patent application Ser. No. 60/024,623 entitled "Method
and Apparatus for Microcellular Extrusion", filed Aug. 27, 1996 by
Burnham, et al., to commonly-owned, co-pending U.S. provisional
patent application Ser. No. 60/026,889, entitled "Method and
Apparatus for Microcellular Extrusion", filed Sep. 23, 1996 by Kim,
et al, and to commonly-owned, co-pending U.S. patent application
Ser. No. 08/777,709, entitled "Method and Apparatus for
Microcellular Extrusion", filed Dec. 20, 1996 by Kim, et al, each
of which is incorporated herein by reference.
FIELD OF THE INVENTION
[0002] The present invention relates generally to polymeric foam
processing, and more particularly to a continuous microcellular
polymer extrusion system and method that allows control of the
material density, cell density, thickness, and shape of
microcellular and supermicrocellular material.
BACKGROUND OF THE INVENTION
[0003] Foamed polymeric materials are well known, and typically are
produced by introducing a physical blowing agent into a molten
polymeric stream, mixing the blowing agent with the polymer, and
extruding the mixture into the atmosphere while shaping the
mixture. Exposure to atmospheric conditions causes the blowing
agent to gasify, thereby forming cells in the polymer. Under some
conditions the cells can be made to remain isolated, and a
closed-cell foamed material results. Under other, typically more
violent foaming conditions, the cells rupture or become
interconnected and an open-cell material results. As an alternative
to a physical blowing agent, a chemical blowing agent can be used
which undergoes chemical decomposition in the polymer material
causing formation of a gas.
[0004] U.S. Pat. No. 3,796,779 (Greenberg; Mar. 12, 1976) describes
injection of a gas into a flowing stream of molten plastic, and
expansion to produce a foam. The described technique typically
produces voids or cells within the plastic that are relatively
large, for example on the order of 100 microns or greater. The
number of voids or cells per unit volume of material typically is
relatively low according to that technique and often the material
exhibits a non-uniform distribution of cells throughout the
material. Therefore, thin sheets and sheets having very smooth
finishes typically cannot be made by the technique, and materials
produced typically have relatively low mechanical strengths and
toughness.
[0005] U.S. Pat. No. 4,548,775 (Hayashi, et al.) describes a
technique involving extruding an expandable resin through a
plurality of holes bored in a die and then fusing together material
extruded from the holes. The technique is designed to form a
high-density skin layer on the foamed material since, according to
Hayashi, et al., with single-hole dies the extrudate is deformed by
foaming after the material leaves the die and it is not possible to
form a skin layer uniformly.
[0006] U.S. Pat. No. 3,624,192 (McCoy, et al.) disclose extrusion
of thermoplastic polyaromatic resin, admixed with a nucleating
agent, through a network of slits to form a foam board.
[0007] U.S. Pat. No. 3,720,572 (Soda, et al.) disclose production
of "synthetic wood" defined by an elongated microporous article
formed of a plurality of coalesced, foamed resin strands. Borders
between the strands mimic wood grain, which is the object of the
invention.
[0008] U.S. Pat. No. 4,473,665 (Martini-Vvedensky, et al.; Sep. 25,
1984) describes a process for making foamed polymer having cells
less than about 100 microns in diameter. In the technique of
Martini-Vvedensky, et al., a material precursor is saturated with a
blowing agent, the material is placed under high pressure, and the
pressure is rapidly dropped to nucleate the blowing agent and to
allow the formation of cells. The material then is frozen rapidly
to maintain a desired distribution of microcells.
[0009] U.S. Pat. No. 5,158,986 (Cha, et al.; Oct. 27, 1992)
describes formation of microcellular polymeric material using a
supercritical fluid as a blowing agent. In a batch process of Cha,
et al., a plastic article is submerged at pressure in supercritical
fluid for a period of time, and then quickly returned to ambient
conditions creating a solubility change and nucleation. In a
continuous process, a polymeric sheet is extruded, then run through
rollers in a container of supercritical fluid at high pressure, and
then exposed quickly to ambient conditions. In another continuous
process, a supercritical fluid-saturated molten polymeric stream is
established. The stream is rapidly heated, and the resulting
thermodynamic instability (solubility change) creates sites of
nucleation, while the system is maintained under pressure
preventing significant growth of cells. The material then is
injected into a mold cavity where pressure is reduced and cells are
allowed to grow.
[0010] In continuous extrusion processes in general, typical goals
involve high production rates (flow rates), production of material
having a desired shape, size, material density and cell density,
especially materials having relatively thin or thick portions, and
production of materials with a highly smooth surface. In all cases,
of course, it is a goal to produce material at the lowest possible
cost. While conventional foam processing can operate at very high
output rates, typical known continuous microcellular extrusion
production rates do not approach the rates achievable with
conventional processes. In conventional foam polymer processing, a
desired shape, size and density of a product generally can be
achieved using a conventional shaping die. However, extruding very
thin material or very thick microcellular material can be
difficult. With respect to thick sheets, it has been difficult or
impossible to create the necessary solubility change uniformly
throughout a thick product produced by extrusion to produce a thick
microcellular article continuously. With respect to thin sheets,
where the cell size is large relative to the thickness of the
sheet, small holes in the sheet can develop where a particular cell
is of a dimension larger than the thickness of a sheet. Additional
control problems exist in many known thin foam sheet extrusion
techniques. Accordingly, it has been a challenge to extrude thin
coatings of conventional foam cellular material onto substrates
such as wire. In particular, where a substrate such as wire must be
isolated from moisture, if a foam material is to be used to coat
the substrate then the foam should be essentially completely
closed-cell material. Therefore, it has been difficult or
impossible to extrude thin, closed-cell polymeric material onto
wire to form a coating having acceptable electrical insulation
properties under various conditions.
[0011] Traditionally, chlorofluorocarbons (CFC's),
hydrochlorofluorocarbon- s, (HCFC's), and alkanes (butane, pentane,
isopentane) have been used as blowing agents to produce foam
products. These agents reportedly provided superior foaming
control, as they reportedly are partially soluble in polymers,
acting as plasticizers to lower the glass transition temperature
(Tg) of the material, thereby reducing melt viscosity and
permitting process cooling of the extruder melt as necessary to
obtain foam physical characteristics such as mechanical strength,
smooth foam, and unruptured cells. In part due to environmental
problems associated with these agents, however, effort has been
directed towards the use of low environmental impact atmospheric
gases such as carbon dioxide, nitrogen, and air as blowing agents,
and success has been met in some cases (see, e.g., U.S. Pat. No.
5,158,986 (Cha), above). But successful control during foaming with
atmospheric gases has been more difficult to achieve than with
conventional agents. Some references report that the solubility of
atmospheric gases in polymers is inherently lower than conventional
blowing agents, therefore Tg and melt viscosity are not reduced to
the same degree, necessitating relatively higher processing
temperatures when using atmospheric gases in order to maintain
necessary melt flow. Higher processing and melt temperatures can
produce reduced polymer melt strength as compared to similar
conditions using conventional blowing agents, resulting, in many
cases, in explosive cell expansion upon release of the melt to
atmosphere.
[0012] In some instances, control in atmospheric gas blowing agent
processes has been addressed with high temperature melt processing
during the incorporation of the blowing agent, followed by melt
cooling prior to extrusion and foaming to increase melt strength.
In particular, several patents and publications focusing on foaming
of amorphous polymers using solely carbon dioxide as blowing agent
have stressed criticality of melt and/or die temperature do not
exceed a particular temperature.
[0013] For example, U.S. Pat. No. 4,436,679 issued to Winstead on
Mar. 13, 1984, and U.S. Pat. Nos. 5,266,605 and 5,250,577 issued to
Welsh on Nov. 30, 1993 and Oct. 5, 1993, respectively, disclose
cooling prior to the extrusion of amorphous polymer foams formed
using solely carbon dioxide blowing agent. European Patent
Application EP 0 707 935 A2 published Apr. 24, 1996 by Baumgart et
al. (Assignee BASF) describes extrusion of amorphous polymeric
material with a large temperature drop to control extrusion.
[0014] Due to the process and material limitations described above,
and in particular temperature limitations, those of ordinary skill
in the art would not expect to achieve highly-controlled, high
volume microcellular processing of crystalline and semi-crystalline
polymers, especially when using atmospheric gases. Crystalline and
semi-crystalline polymers differ from amorphous materials in that
they have a distinct crystalline melting temperature (Tm) that is
much higher than their glass transition temperature. If cooled to
Tm, these materials will abruptly solidify, making further
processing impossible. Prior to this abrupt solidification, the
melt strength of the polymer will not increase appreciably with
increased cooling, as in the case of amorphous polymers, because
the temperature of the polymer is necessarily so much higher than
Tg. That is, crystalline and semi-crystalline polymers must be
processed at temperatures well above (relative to Tg) ceiling
temperature for amorphous polymers, driving cell expansion and
making it extremely difficult to maintain small cell sizes.
[0015] Therefore, the production of microcellular material using
atmospheric gases has focused primarily on amorphous polymers,
which become viscous and flow easily at temperatures above Tg.
[0016] While the above and other reports represent several
techniques associated with the manufacture of microcellular
material, there is a need in the industry for a viable continuous
method of producing crystalline and semi-crystalline microcellular
material.
[0017] It is, therefore, an object of the invention to provide a
high-throughput, continuous, microcellular or supermicrocellular
polymer extrusion system effective in producing microcellular
material of high quality and in any of a variety of desired
thicknesses, in producing microcellular material as a coating for
wire, and in producing high-quality crystalline and
semi-crystalline microcellular material.
SUMMARY OF THE INVENTION
[0018] The present invention provides methods and systems for
producing microcellular material, and microcellular articles. In
one aspect, the invention provides a method that involves
establishing a first stream of a fluid, single-phase solution of a
precursor of foamed polymeric material and a blowing agent, and
continuously nucleating the blowing agent mixed with the precursor
by dividing the stream into separate portions and separately
nucleating each of the separate portions. The separate portions can
be nucleated simultaneously by, in one embodiment, diverging the
first stream into at least two divided solution streams and
separately nucleating each of the divided streams. The divided
streams can be recombined into a single stream of nucleated, fluid
polymeric material. Nucleation can be effected by subjecting each
of the separate portions to conditions of solubility change, or
thermodynamic instability, sufficient to create sites of nucleation
in the solution in the absence of an auxiliary nucleating agent.
The method can further involve shaping the recombined stream into a
desired shape while lowering pressure applied to the recombined
stream to a pressure allowing final foaming of the material.
[0019] In another aspect, the invention provides a method for
rapidly mixing a fluid polymeric material and a fluid that is a gas
under ambient conditions and that can serve as a blowing agent. The
method involves introducing, into fluid polymeric material flowing
at a rate of at least about 10 lbs/hr, a fluid that is a gas under
ambient conditions. In a period of less than about 1 minute, a
single-phase solution of the fluid and the polymer are created. The
fluid is present in the solution in an amount of at least about 2%
by weight based on the weight of the solution. In one embodiment,
the method is carried out by injecting the fluid that is a gas
under ambient conditions through at least one orifice of an
extruder barrel. The method can involve injecting the fluid through
at least about 100 orifices into the barrel in another embodiment,
and through more orifices according to other embodiments. This
aspect of the invention can find use in a variety of mixing
arrangements, and finds particularly advantageous use in connection
with other methods of the present invention.
[0020] In another aspect, the invention provides a method that
involves maintaining in extrusion apparatus a relatively constant
pressure profile in a mixture of fluid polymeric material and fluid
that is a gas under ambient conditions and that can serve as a
blowing agent. Specifically, the method involves providing an
extruder having an inlet at an inlet end thereof designed to
receive a precursor of foamed material and an outlet at an outlet
end thereof designed to release foamed material from the extruder
and an enclosed passageway connecting the inlet with the outlet
constructed and arranged to advance a fluid polymeric stream within
the passageway in a downstream direction from the inlet end toward
the outlet end. The method involves establishing a stream of fluid
polymeric material flowing in the extruder in a downstream
direction and introducing a fluid that is a gas under ambient
conditions into the stream at an injection location of the
extruder. The stream is maintained, downstream of the injection
location and upstream of a foaming region, under pressure varying
by no more than about 1,500 psi. The extruder can include a
nucleation region at which a single-phase solution of fluid
polymeric material and blowing agent flowing therethrough is
nucleated, and the relatively constant pressure can be maintained
downstream of the injection location and upstream of the nucleation
region. The fluid that is gas under ambient conditions, and that
can serve as blowing agent, can be introduced into the extruder
through one or more orifices, for example 4, 25, 50 or 100 or more
orifices, and can be introduced therethrough simultaneously.
Introduction of the gas can be carried out in an extruder barrel
with a screw including flights passing each of the orifices at a
rate of at least about 0.5 passes per second, or more.
[0021] In another aspect, the invention provides a method of
creating very high pressure drop rates in material to be foamed.
One method involves establishing a stream of a material to be
foamed including a blowing agent, and continuously decreasing the
pressure within successive, continuous portions of a flowing stream
of the material to be foamed, the pressure continuously decreased
at a rate that increases. This can involve establishing a fluid,
single-phase solution of a precursor of foamed polymeric material
and a blowing agent, and continuously nucleating the solution by
continuously decreasing the pressure within successive, continuous
portions of the flowing, single-phase stream at a rate which
increases.
[0022] In another aspect, the invention involves a method involving
continuously extruding microcellular material onto a wire
substrate. This method can involve incorporation of all others of
the methods described in accordance with the invention.
[0023] The invention also provides, according to another aspect, a
method involving continuously extruding microcellular polymeric
material having cells of essentially uniform size of less than
about 50 microns average size from a single-phase solution of
polymeric material and blowing agent. The blowing agent is present
in the solution, according to the method, in an amount less than
about 80% saturation concentration. The saturation concentration is
determined at the lowest pressure in the system after the point of
blowing agent injection but prior to the nucleating pathway of
extrusion apparatus in which the method is carried out.
[0024] In another aspect, the invention provides a method including
continuously extruding essentially closed-cell microcellular
polymeric material having cells of essentially uniform size of less
than about 50 microns average size. The polymeric material has a
minimum cross-sectional dimension of less than about 0.5 mm, and is
extruded from a single-phase solution of polymeric material and
blowing agent.
[0025] In another aspect, the invention involves a method including
continuously extruding foamed polyethylene terephthalate (PET) of
I.V. less than one. Another aspect involves continuous extrusion of
foamed crystalline or semicrystalline polymeric material of density
less than about 8 lbs./ft.sup.3. In another aspect, the method
involves extruding foamed crystalline or semicrystalline polymeric
material essentially free of foam-controllability modifiers.
[0026] The invention also provides a method of producing foamed
material. A continuous stream of crystalline or semi-crystalline
polymeric material is established, and the stream is a continuous
homogeneous single-phase solution of the polymeric material and the
blowing agent is formed. The homogeneous single-phase solution is
subjected to a rapid pressure drop to form nucleated polymeric
material, and the material is continuously extruded into a work
area as microcellular polymeric material.
[0027] Also provided is a method involving establishing a
continuously-flowing stream of a fluid, single-phase solution of
polymeric material and blowing agent, continuously nucleating the
solution and extruding and foaming the solution through a shaping
die. In the method a microcellular foamed polymeric material is
produced at a die temperature at least 100.degree. F. (37.8.degree.
C.) greater than Tg of the polymeric material.
[0028] The invention provides a series of systems and forming dies,
as well. In one aspect the invention provides a polymer forming die
mountable on polymer extrusion apparatus. The die includes a
polymer receiving end constructed and arranged to receive a fluid,
non-nucleated, single-phase solution of polymeric material and
blowing agent, a polymer foam extrusion end constructed and
arranged to release foamed material to ambient conditions, and a
fluid pathway connecting the polymer receiving end to the foam
extrusion end. The pathway has length and cross-sectional
dimensions that are defined as follows. When fluid polymer admixed
homogeneously with about 6 wt % CO.sub.2 is passed through the
pathway at a rate of about 40 lbs. fluid per hour, a pressure drop
rate in the fluid polymer of at least about 0.3 GPa/sec is created.
The fluid pathway that creates this pressure drop can include a
single channel, or at least two separate fluid channels that can,
in turn, communicate with a shaping channel to shape polymeric
microcellular foam material.
[0029] The invention also provides a system including a polymeric
material nucleator constructed and arranged for use in combination
with polymer extrusion apparatus. The nucleator includes a polymer
receiving end constructed and arranged to receive a fluid,
non-nucleated, single-phase solution of a polymeric material and a
blowing agent, a nucleated polymer releasing end constructed and
arranged to release nucleated polymeric material, and a fluid
pathway connecting the receiving end to the releasing end. The
pathway has length and cross-sectional dimensions that are defined
as above, that is, as follows. When fluid polymer admixed
homogeneously with about 6 wt % CO.sub.2 is passed through the
pathway at a rate of about 40 lbs. fluid per hour, a pressure drop
in the fluid polymer of at least about 0.3 GPa/sec is created. The
system includes, as well, a chamber for controlling the density of
microcellular material released by the nucleator. The chamber has
an inlet communicating with the nucleator releasing end and an
outlet, and has a diameter of at least about 0.25 inch and a length
to diameter ratio of at least one. The chamber is constructed and
arranged to maintain polymeric material within the chamber at a
pressure of at least about 150 psi. This inhibits the formation and
growth of cells within the chamber.
[0030] The invention also provides polymer extrusion apparatus
including a polymer nucleator having a polymer receiving end
constructed and arranged to receive a fluid, non-nucleated,
single-phase solution of a polymeric material and a blowing agent,
a nucleated fluid releasing end, and a fluid pathway connecting the
polymer receiving end to the releasing end. The pathway decreases
in cross-sectional dimension in a downstream direction, and the
apparatus is constructed and arranged to feed a fluid,
non-nucleated, single-phase solution of a polymeric material and a
blowing agent to the nucleator receiving end.
[0031] In another embodiment, the invention provides a system for
producing microcellular material. The system includes an extruder
having an inlet end for receiving a precursor of microcellular
material, an outlet designed to release microcellular material from
the extruder, and an enclosed passageway connecting the inlet with
the outlet. The passageway is constructed and arranged to receive a
blowing agent and to contain a homogeneous, single-phase solution
of the blowing agent with the precursor in a fluid state at an
elevated pressure within the passageway and to advance the solution
as a fluid stream within the passageway in a downstream direction
from the inlet toward the outlet. The enclosed passageway includes
a nucleating pathway in which a single-phase solution of blowing
agent and microcellular material precursor passing therethrough can
be nucleated. The extruder is adapted to receive wire and to
position the wire in communication with the passageway. Another
system, or this system can include a wire take-up device positioned
to receive microcellular polymeric material-coated wire ejected
from the system.
[0032] All of the above-described methods can, in certain
embodiments, be used in conjunction with any others, and any can be
used individually or in combination with any others with any of the
above-described systems, or any combination of the systems.
Similarly, any of the systems can be used alone, or in combination,
and can be used with one or more, singly or in combination, of the
above-described methods. The systems and methods are described in
more detail in the detailed description of the invention below, and
any of the features that can optionally be added to any of the
arrangements can also be added to any others of the
arrangements.
[0033] The invention also provides a series of articles. In one
aspect, the invention provides a foamed material obtained by
continuously introducing a blowing agent into a material comprising
a crystalline or semi-crystalline polymeric material, and causing
the material to take the form of the foamed material. The foamed
material is in the shape of a continuous extrusion, and is
microcellular. In another aspect, the invention provides an article
including wire, and a coating of microcellular material around the
wire, which can be of thickness as described herein with regard to
very thin microcellular material. The coating is well-secured to
the wire, and provides good electrical insulation. The
microcellular material has a maximum thickness of less than about
0.5 mm. The material can be microcellular polyolefin and can have
an average cell size of less than about 30 microns. In one
embodiment, the material has a maximum cell size of about 50
microns. The material can be essentially closed-cell, and can have
a moisture absorption of less than about 0.1% by weight based on
the weight of the coating after immersion in water for 24
hours.
[0034] In another aspect, the invention provides an article
comprising foamed PET of I.V. less than one. Another aspect
involves foamed crystalline or semicrystalline polymeric material
of density of less than 8 lbs./ft.sup.3. Another aspect involves
foamed crystalline or semicrystalline polymeric material
essentially free of foam-controllability modifiers.
BRIEF DESCRIPTION OF THE DRAWINGS
[0035] FIG. 1 illustrates an extrusion system of the invention
including a multi-hole nucleator, residence chamber downstream
thereof, and shaping die downstream of the residence chamber;
[0036] FIG. 2 illustrates a multi-hole blowing agent feed orifice
arrangement and extrusion screw;
[0037] FIG. 3 illustrates an extrusion system of the invention
including a multi-passage nucleating and shaping die;
[0038] FIG. 4 is a cross-section through line 4-4 of FIG. 1;
[0039] FIG. 5 illustrates a multi-passage nucleating and shaping
die in accordance with the invention;
[0040] FIG. 6 is a cross-sectional view through line 6-6 of FIG.
5;
[0041] FIG. 7 is a cross-sectional view through line 6-6 of FIG. 5
according to an alternate embodiment of the invention;
[0042] FIG. 8 is a cross-sectional view through line 6-6 of FIG. 5
according to yet another alternate embodiment of the invention;
[0043] FIG. 9 illustrates a multiple concentric plate nucleator of
a forming die of the type illustrated in FIG. 5;
[0044] FIG. 10 is a multiple concentric plate nucleator of a
forming die of the type illustrated in FIG. 5 according to another
embodiment;
[0045] FIG. 11 illustrates a multi-hole nucleator or shaping die of
the invention including separate, slanted nucleating pathways;
[0046] FIGS. 12a-12h illustrate multi-hole nucleators or nucleating
portions of shaping dies having a variety of passageway
arrangements and cross-sections;
[0047] FIG. 13 is a plot of a typical pressure drop through a
parallel-landed (straight) nucleating pathway typical of a standard
extrusion die configuration, a plot of an ideal pressure drop
through a parallel-landed pathway, and a plot of a pressure profile
through a nucleating pathway of the invention which decreases in
cross-sectional area in a downstream direction;
[0048] FIG. 14 illustrates a wire extrusion system of the invention
including a tapered nucleating pathway;
[0049] FIG. 15 is a photocopy of a scanning electron micrograph
(SEM) image of a cross-section of microcellular polymeric material
extrusion coated onto wire, following removal of the wire;
[0050] FIG. 16 is a photocopy of an SEM image of the coating of
FIG. 15, at higher magnification;
[0051] FIG. 17 is a photocopy of an (SEM) image of a cross-section
of microcellular polymeric material extrusion coated onto wire,
following removal of the wire;
[0052] FIG. 18 is a photocopy of an SEM image of the coating of
FIG. 17, at higher magnification;
[0053] FIG. 19 is a photocopy of an SEM image of a cross-section of
another example of microcellular wire coating;
[0054] FIG. 20 is a photocopy of an SEM image of the microcellular
wire coating of FIG. 19 at higher magnification;
[0055] FIG. 21 is a photocopy of an SEM image of a cross-section of
another example of microcellular wire coating;
[0056] FIG. 22 is a photocopy of an SEM image of the microcellular
wire coating of FIG. 21 at higher magnification;
[0057] FIG. 23 is a photocopy of an optical micrograph of the wire
coating sample of FIGS. 21 and 22, without wire removed, mounted in
epoxy;
[0058] FIG. 24 is a photocopy of an optical micrograph of the wire
coating sample of FIGS. 21 and 22, without wire removed, mounted in
epoxy;
[0059] FIG. 25 is a photocopy of an SEM image of cross-section of
polyethylene terephthalate (PET) extrudate that is
non-microcellular;
[0060] FIG. 26 is a photocopy of an SEM image of a cross-section of
microcellular extrudate;
[0061] FIG. 27 is a photocopy of an SEM image of a cross-section of
non-uniform flame retardant polyethylene (FRP) extrudate;
[0062] FIG. 28 is a photocopy of an SEM image of a cross-section of
microcellular FRPE extrudate;
[0063] FIG. 29 is a photocopy of an SEM image of a cross-section of
non-microcellular, filled, plasticized polyvinyl chloride (PVC)
extrudate;
[0064] FIG. 30 is a photocopy of an SEM image of a cross-section of
microcellular filled, plasticized PVC extrudate;
[0065] FIG. 31 is a photocopy of an SEM image of a cross-section of
non-microcellular polypropylene extrudate;
[0066] FIG. 32 is a photocopy of an SEM image of a cross-section of
microcellular polypropylene extrudate;
[0067] FIG. 33 is a photocopy of an SEM image of a cross-section of
relatively open-celled microcellular FRPE extrudate;
[0068] FIG. 34 is a photocopy of an SEM image of a cross-section of
relatively closed-cell microcellular FRPE;
[0069] FIG. 35 is a graph of a pressure profile between
stabilization after blowing each into injection and nucleation of
molten PET containing 6.5% CO.sub.2 blowing agent;
[0070] FIG. 36 is a photocopy of an SEM image of a cross-section of
microcellular PET extrudate;
[0071] FIG. 37 illustrates a multi-nucleating pathway die in
accordance with one embodiment of the invention; and
[0072] FIG. 38 is a photocopy of an SEM image of the cross section
of microcellular PET extrudate;
[0073] FIG. 39 is a photocopy of an SEM of a cross section of thin
microcellular polypropylene;
[0074] FIG. 40 is a photocopy of an SEM of the material of FIG. 39,
at higher magnification;
[0075] FIG. 41 is a photocopy of an SEM of a cross section of thin
microcellular polypropylene of another example; and
[0076] FIG. 42 is a photocopy of an SEM of the material of FIG. 41,
at higher magnification.
DETAILED DESCRIPTION OF THE INVENTION
[0077] Commonly owned, co-pending U.S. provisional patent
application Ser. No. 60/024,623, entitled "Method and Apparatus for
Microcellular Extrusion", filed Aug. 27, 1996 by Burnham, et al.,
(pending), commonly-owned, co-pending U.S. provisional patent
application Ser. No. 60/026,889 entitled "Method and Apparatus for
Microcellular Extrusion", filed Sep. 23, 1996 by Kim, et al.,
(pending), and commonly-owned, co-pending U.S. patent application
Ser. No. 08/777,709 entitled "Method and Apparatus for
Microcellular Polymer Extrusion", filed Dec. 20, 1996 all are
incorporated herein by reference.
[0078] The various embodiments and aspects of the invention will be
better understood from the following definitions. As used herein,
"nucleation" defines a process by which a homogeneous, single-phase
solution of polymeric material, in which is dissolved molecules of
a species that is a gas under ambient conditions, undergoes
formations of clusters of molecules of the species that define
"nucleation sites", from which cells will grow. That is,
"nucleation" means a change from a homogeneous, single-phase
solution to a multi-phase mixture in which, throughout the
polymeric material, sites of aggregation of at least several
molecules of blowing agent are formed. A "nucleating agent" is a
dispersed agent, such as talc or other filler particles, added to a
polymer and able to promote formation of nucleation sites from a
single-phase, homogeneous solution. Thus "nucleation sites" do not
define locations, within a polymer, at which nucleating agent
particles reside. "Nucleated" refers to a state of a fluid
polymeric material that had contained a single-phase, homogeneous
solution including a dissolved species that is a gas under ambient
conditions, following an event (typically thermodynamic
instability) leading to the formation of nucleation sites.
"Non-nucleated" refers to a state defined by a homogeneous,
single-phase solution of polymeric material and dissolved species
that is a gas under ambient conditions, absent nucleation sites. A
"non-nucleated" material can include nucleating agent such as
talc.
[0079] The present invention provides a system for extruding
microcellular or supermicrocellular polymeric material. The
material can be extruded onto a substrate such as wire. For
purposes of the present invention, microcellular material is
defined as foamed material containing cells of size less than about
100 microns in diameter, or material of cell density of generally
greater than at least about 10.sup.6 cells per cubic centimeter, or
preferably both. In some embodiments, microcellular material of the
invention contains cells of size less than about 50 microns in
diameter, more preferably less than about 30 microns in diameter.
The void fraction of microcellular material generally varies from
5% to 98%. Supermicrocellular material is defined for purposes of
the invention by cell sizes smaller than 1 .mu.m and cell densities
greater than 10.sup.12 cells per cubic centimeter.
[0080] In preferred embodiments, microcellular material of the
invention is produced having average cell size of less than about
50 microns. In some embodiments particularly small cell size is
desired, and in these embodiments material of the invention has
average cell size of less than about 20 microns, more preferably
less than about 10 microns, and more preferably still less than
about 5 microns. The microcellular material preferably has a
maximum cell size of about 100 microns. In embodiments where
particularly small cell size is desired, the material can have
maximum cell size of about 50 microns, more preferably about 25
microns, and more preferably still about 15 microns. A set of
embodiments includes all combinations of these noted average cell
sizes and maximum cell sizes. For example, one embodiment in this
set of embodiments includes microcellular material having an
average cell size of less than about 30 microns with a maximum cell
size of about 50 microns, and as another example an average cell
size of less than about 30 microns with a maximum cell size of
about 35 microns, etc. That is, microcellular material designed for
a variety of purposes can be produced having a particular
combination of average cell size and a maximum cell size preferable
for that purpose. Control of cell size is described in greater
detail below. In one set of preferred embodiments the void fraction
of the microcellular material of the invention is as described
below with reference to FIG. 14.
[0081] In one embodiment, essentially closed-cell microcellular
material is produced. As used herein, "essentially closed-cell" is
meant to define material that, at a thickness of about 100 microns,
contains no connected cell pathway through the material.
[0082] Although not necessary for all embodiments, one set of
embodiments of the invention relies upon separate nucleation of
separate portions of a stream of a single-phase solution of a fluid
polymeric material admixed with blowing agent. The separate
portions then are recombined to form a single stream or article. In
a preferred embodiment the separate portions are separately
nucleated simultaneously. By dividing a stream into separate
portions, separately nucleating the separate portions
simultaneously, and recombining the separate portions to form a
single, nucleated stream or microcellular article, much higher
throughput can be achieved and thicker parts can be made because of
the simultaneous nucleation and because separate nucleation of
smaller quantities and recombination of the smaller quantities to
form a larger quantity results in better uniformity of high-quality
cells throughout a cross-section of polymer.
[0083] Separate nucleation of separate portions of a fluid stream
and recombination of the stream can occur at a multiple-pathway
nucleator that is positioned upstream of the shaping die of the
apparatus. In this way, nucleation and shaping are separated, with
separate nucleation resulting in a relatively large cross-sectional
stream of a high density of nucleation, with very good uniformity,
and this stream is fed to a shaping die which can make use of the
large-cross-section, high-cell-density stream to shape a variety of
parts. By separating nucleation from shaping, nucleation occurs in
a manner free of the limitation of the shape of the final product.
The multiple-pathway nucleator can be separated from the shaping
die, in this set of embodiments, by a chamber that controls the
pressure and temperature of a fluid polymeric mixture within the
chamber. Thus, the density of the material, and cell density, can
be controlled. To facilitate recombination of the separate
portions, a mixer, such as a static mixer, can be positioned
downstream of the nucleator, optionally in chamber 70, described
below.
[0084] Separation of nucleation from shaping can be carried out
with single-hole nucleators or other nucleators that do not include
multiple pathways, while realizing advantages of the technique.
[0085] In another set of embodiments, nucleation and shaping occur
in the same general area, namely, at a nucleating shaping die, and
the nucleating shaping die can include a plurality of separate
nucleating pathways, that is, can define a multiple-pathway
nucleating die, which can allow higher throughput and thicker parts
than are achievable typically in prior art techniques.
[0086] Referring to FIG. 1, an extrusion system 30 according to one
embodiment of the invention is illustrated schematically. Extrusion
system 30 includes a barrel 32 having a first, upstream end 34 and
a second, downstream end 36. Mounted for rotation within barrel 32
is an extrusion screw 38 operably connected, at its upstream end,
to a drive motor 40. Although not shown in detail, extrusion screw
38 includes feed, transition, gas injection, mixing, and metering
sections.
[0087] Positioned along extrusion barrel 32, optionally, are
temperature control units 42. Control units 42 can be electrical
heaters, can include passageways for temperature control fluid, or
the like. Units 42 can be used to heat a stream of pelletized or
fluid polymeric material within the extrusion barrel to facilitate
melting, and/or to cool the stream to control viscosity, skin
formation and, in some cases, blowing agent solubility. The
temperature control units can operate differently at different
locations along the barrel, that is, to heat at one or more
locations, and to cool at one or more different locations. Any
number of temperature control units can be provided.
[0088] Extrusion barrel 32 is constructed and arranged to receive a
precursor of a fluid polymeric material. Amorphous,
semicrystalline, and crystalline material including styrenic
polymers, polyolefins such as polyethylene and polypropylene,
fluoropolymers, crosslinkable polyolefins, polyamides,
polyaromatics such as polystyrene and polyvinyl chloride can be
used. Typically, this involves a standard hopper 44 for containing
pelletized polymeric material to be fed into the extruder barrel
through orifice 46, although a precursor can be a fluid
prepolymeric material injected through an orifice and polymerized
within the barrel via, for example, auxiliary polymerization
agents. When chemical blowing agents are used, they typically are
compounded in polymer pellets introduced into hopper 44.
[0089] Immediately downstream of the downstream end 48 of screw 38
in FIG. 1 is a region 50 which can be a temperature adjustment and
control region, auxiliary mixing region, auxiliary pumping region,
or the like. For example, region 50 can include temperature control
units to adjust the temperature of a fluid polymeric stream prior
to nucleation, as described below. Region 50 can include instead,
or in addition, standard mixing units (not shown), or a
flow-control unit such as a gear pump (not shown). In another
embodiment, region 50 is replaced by a second screw of a tandem
extrusion apparatus, the second screw optionally including a
cooling region.
[0090] When a physical blowing agent is used, along barrel 32 of
system 30 is a port 54 in fluid communication with a source 56 of a
physical blowing agent. (This apparatus is not required when a
chemical blowing agent alone is used). Any of a wide variety of
blowing agents known to those of ordinary skill in the art such as
hydrocarbons, chlorofluorocarbons, nitrogen, carbon dioxide, and
the like can be used in connection with this embodiment of the
invention and, according to a preferred embodiment, source 56
provides carbon dioxide as a blowing agent. A pressure and metering
device 58 typically is provided between blowing agent source 56 and
port 54. Supercritical fluid blowing agents are especially
preferred, in particular supercritical carbon dioxide.
[0091] Any of a wide variety of blowing agents can be used in
connection with the present invention, for example, physical
blowing agents and chemical blowing agents. Suitable chemical
blowing agents include those typically relatively low molecular
weight organic compounds that decompose at a critical temperature
or another condition achievable in extrusion and release a gas or
gases such as nitrogen, carbon dioxide, or carbon monoxide.
Examples include azo compounds such as azo dicarbonamide. Where a
chemical blowing agent is used, the blowing agents can be
introduced into systems of a invention by being compounded within
polymer pellets feed into the system, or other techniques available
to those of ordinary skill in the art.
[0092] Device 58 can be used to meter the blowing agent so as to
control the amount of the blowing agent in the polymeric stream
within the extruder to maintain a level of blowing agent at a
level, according to one set of embodiments, between about 1% and
15% by weight, preferably between about 3% and 12% by weight, more
preferably between about 5% and 10% by weight, more preferably
still between about 7% and 9% by weight, based on the weight of the
polymeric stream and blowing agent. In another set of embodiments,
described below, it is preferred that lower levels of blowing agent
be used. As will become apparent to the reader, different levels of
blowing agent are desirable under different conditions and/or for
different purposes which can be selected in accordance with the
invention.
[0093] The pressure and metering device can be connected to a
controller (not shown) that also is connected to drive motor 40
and/or a drive mechanism of a gear pump (not shown) to control
metering of blowing agent in relationship to flow of polymeric
material to very precisely control the weight percent blowing agent
in the fluid polymeric mixture.
[0094] Although port 54 can be located at any of a variety of
locations along the extruder barrel, according to a preferred
embodiment it is located just upstream from a mixing section 60 of
the extrusion screw and at a location 62 of the screw where the
screw includes unbroken flights.
[0095] Referring now to FIG. 2, a preferred embodiment of the
blowing agent port is illustrated in greater detail and, in
addition, two ports on opposing top and bottom sides of the barrel
are shown. In this preferred embodiment, port 54 is located at a
region upstream from mixing section 60 of screw 38 (including
highly-broken flights) at a distance upstream of the mixing section
of no more than about 4 full flights, preferably no more than about
2 full flights, or no more than 1 full flight. Positioned as such,
injected blowing agent is very rapidly and evenly mixed into a
fluid polymeric stream to quickly produce a single-phase solution
of the foamed material precursor and the blowing agent.
[0096] Port 54, in the preferred embodiment illustrated, is a
multi-hole port including a plurality of orifices 64 connecting the
blowing agent source with the extruder barrel. As shown, in
preferred embodiments a plurality of ports 54 are provided about
the extruder barrel at various positions radially and can be in
alignment longitudinally with each other. For example, a plurality
of ports 54 can be placed at the 12 o'clock, 3 o'clock, 6 o'clock,
and 9 o'clock positions about the extruder barrel, each including
multiple orifices 64. In this manner, where each orifice 64 is
considered a blowing agent orifice, the invention includes
extrusion apparatus having at least about 10, preferably at least
about 40, more preferably at least about 100, more preferably at
least about 300, more preferably at least about 500, and more
preferably still at least about 700 blowing agent orifices in fluid
communication with the extruder barrel, fluidly connecting the
barrel with a source of blowing agent.
[0097] Also in preferred embodiments is an arrangement (as shown in
FIG. 2) in which the blowing agent orifice or orifices are
positioned along the extruder barrel at a location where, when a
preferred screw is mounted in the barrel, the orifice or orifices
are adjacent full, unbroken flights 65. In this manner, as the
screw rotates, each flight, passes, or "wipes" each orifice
periodically. This wiping increases rapid mixing of blowing agent
and fluid foamed material precursor by, in one embodiment,
essentially rapidly opening and closing each orifice by
periodically blocking each orifice, when the flight is large enough
relative to the orifice to completely block the orifice when in
alignment therewith. The result is a distribution of relatively
finely-divided, isolated regions of blowing agent in the fluid
polymeric material immediately upon injection and prior to any
mixing. In this arrangement, at a standard screw revolution speed
of about 30 rpm, each orifice is passed by a flight at a rate of at
least about 0.5 passes per second, more preferably at least about 1
pass per second, more preferably at least about 1.5 passes per
second, and more preferably still at least about 2 passes per
second. In preferred embodiments, orifices 54 are positioned at a
distance of from about 15 to about 30 barrel diameters from the
beginning of the screw (at upstream end 34).
[0098] The described arrangement facilitates a method of the
invention that is practiced according to one set of embodiments.
The method involves introducing, into fluid polymeric material
flowing at a rate of at least about 40 lbs/hr., a blowing agent
that is a gas under ambient conditions and, in a period of less
than about 1 minute, creating a single-phase solution of the
blowing agent fluid in the polymer. The blowing agent fluid is
present in the solution in an amount of at least about 2.5% by
weight based on the weight of the solution in this arrangement. In
preferred embodiments, the rate of flow of the fluid polymeric
material is at least about 60 lbs/hr., more preferably at least
about 80 lbs/hr., and in a particularly preferred embodiment
greater than at least about 100 lbs/hr., and the blowing agent
fluid is added and a single-phase solution formed within one minute
with blowing agent present in the solution in an amount of at least
about 3% by weight, more preferably at least about 5% by weight,
more preferably at least about 7%, and more preferably still at
least about 10% (although, as mentioned, in a another set of
preferred embodiments lower levels of blowing agent are used). In
these arrangements, at least about 2.4 lbs per hour blowing agent,
preferably CO.sub.2, is introduced into the fluid stream and
admixed therein to form a single-phase solution. The rate of
introduction of blowing agent is matched with the rate of flow of
polymer to achieve the optimum blowing agent concentration.
[0099] Returning again to the embodiment illustrated in FIG. 1, a
system is provided that can produce microcellular or
supermicrocellular product having very small cell size, high cell
density, and controlled cell density, in articles having very small
cross-sectional dimension or very large cross-sectional dimensions
by separating nucleation from shaping. This involves, according to
the embodiment of FIG. 1, a nucleator 66 located far enough
downstream of blowing agent injection port 54 that it will receive
a fluid, single-phase solution of the polymeric precursor of the
microcellular material and the blowing agent, and a shaping die 68
located downstream of nucleator 66. In the preferred embodiment
illustrated, nucleator 66 is a multiple-pathway nucleator including
a plurality of separate nucleating pathways 67, each fluidly
connecting the region of the extrusion barrel upstream of the
nucleator with the region of the extruder downstream thereof.
[0100] As used herein, "nucleating pathway" is meant to define a
pathway that forms part of microcellular polymer foam extrusion
apparatus and in which, under conditions in which the apparatus is
designed to operate (typically at pressures of from about 1500 to
about 5000 psi upstream of the nucleator and at flow rates of
greater than about 10 lbs polymeric material per hour), the
pressure of a single-phase solution of polymeric material admixed
with blowing agent in the system drops below the saturation
pressure for the particular blowing agent concentration at a rate
or rates facilitating nucleation. A nucleating pathway defines,
optionally with other nucleating pathways, a nucleation or
nucleating region of an extruder. While a multiple-pathway
nucleator is preferred in some embodiments, one aspect of the
invention involves in its broadest sense the separation of
nucleation and shaping, and in this aspect any arrangement can
serve as a nucleator that subjects a flowing stream of a
single-phase solution of foamed material precursor and blowing
agent to a solubility change sufficient to nucleate the blowing
agent. This solubility change can involve a rapid temperature
change, a rapid pressure change, or a combination, and those of
ordinary skill in the art will recognize a variety of arrangements
for achieving nucleation in this manner.
[0101] Where a rapid temperature change is selected to achieve
nucleation, temperature control units can be provided about
nucleator 66. Nucleation by temperature control is described in
U.S. Pat. No. 5,158,986 (Cha., et al.). Temperature control units
can be used alone or in combination with a fluid pathway of
nucleator 66 creating a high pressure drop rate in fluid polymeric
material flowing therethrough.
[0102] As discussed above, separation of nucleation from shaping
allows a large fluid stream of highly-nucleated, highly-uniform
polymeric material to be fed to a die. Separation of nucleation
from shaping also is advantageous in that shaping need not involve
nucleation. Prevalent in the prior art is the assumption that
control in foaming material via pressure drop is a challenge due to
the fact that release of a fluid mixture of blowing agent and
polymeric material from pressure in which the blowing agent is
fluid into ambient conditions (typical of foam processing) can
result in violent expansion of the blowing agent and the creation
of open-cell material. While creation of open-cell material is
desirable for a variety of products, it is often a goal to create
closed-cell material and closed-cell, microcellular material is
preferred in the present invention. Difficulty in control can be
exacerbated by the fact that maintaining a fluid mixture of blowing
agent and polymeric material prior to foaming often is accomplished
by maintaining the mixture at a temperature above the melt
temperature of the polymer, and at very high pressures. Rapid
transferral from high-pressure, high-temperature conditions to
ambient conditions is difficult to accomplish controllably. Even if
a rapid pressure drop is accomplished, if the transfer to ambient
temperature does not take place quickly, cells may continue to
expand undesirably.
[0103] Therefore, the shaping die 68 and nucleator 66 of the
invention can be separated from each other by a distance sufficient
to allow conditions to be controlled such that shaping can be
accomplished controllably. That is, the pressure and temperature
conditions downstream of the nucleator need not be as severe as
those upstream, where it is necessary to maintain a single-phase
solution, so that high density nucleation can be achieved. A
residence chamber 70 is positioned between nucleator 66 and shaping
die 68 to control conditions of temperature and, where desired,
pressure. Of course, if no pressure-control devices are provided
within the chamber, pressure will drop naturally to some extent via
flow through the chamber. Preferably, the residence chamber has an
outer wall addressed by one or more temperature control units 42.
Although not illustrated, temperature control units 42 can include
fluid pathways through which a temperature control fluid, such as a
cooling fluid, can be passed. Chamber 70 can be of any
cross-sectional shape, and can be annular.
[0104] Chamber 70 has several functions, including recombining
streams of nucleated material as they emerge from a
multiple-pathway nucleator, and controlling the cell growth of the
nucleated material by varying the length of time that it remains in
the chamber ("residence time") and by varying the external pressure
and temperature within the chamber. The chamber may contain mixing
elements, such as a static mixer, to combine nucleated streams and
provide a more uniform temperature or blowing agent concentration.
The cooling function of the chamber can be used to form a skin on
the exterior of the polymer. The degree of cell growth is a
function of residence time, external pressure and temperature of
polymer melt. Preferred chambers of the invention are designed with
varying lengths to allow residence times of up to about 1.5
minutes, although residence times of at least about 10 seconds, 20
seconds, 40 seconds, 1 minute, or 1.25 minutes can be used.
[0105] By cooling a nucleated fluid mixture of polymeric material
and blowing agent within chamber 70, shaping can occur with less
simultaneous expansion. That is, expansion of cells can occur
within the residence chamber in a controlled manner and then, with
the fluid mixture of polymeric material and very small cells at a
temperature high enough to allow shaping, the mixture can be passed
through shaping die 68 and formed into a final product.
[0106] Also illustrated in FIG. 1 is an optional shaping element 69
downstream of shaping die 68. Shaping element 69 can provide
further control over the thickness or shape of an extruded product
by restricting expansion, further cooling the extrudate (via, for
example, fluid cooling channels or other temperature control units
in element 69, not shown), or a combination. Without element 69,
extrudate is extruded into ambient conditions upon emergence from
shaping die 68 (restricted only by polymeric extrudate downstream
of the exit of the shaping die). With element 69, the extrudate
generally emerges from shaping die into conditions of pressure
slightly above ambient.
[0107] With reference to FIG. 1, several arrangements of the
invention are described. In one, polymeric extrudate emerges from
nucleating pathways into ambient conditions and is recombined
there. This would involved elimination of components downstream of
nucleator 66, and is described below with reference to FIGS. 3 and
5 with the exception that the arrangements of FIGS. 3 and 5 include
regions downstream of the nucleator that provide enclosure and
shaping for the extrudate. In another arrangement, only forming
element 69 exists downstream of the nucleator (analogous to the
embodiments of FIGS. 3 and 5). In another, the system includes
nucleator 66, an enclosure downstream thereof (chamber 70) and a
constriction at the end of the chamber (forming die 68). In still
another, the system includes nucleator 66, chamber 70, forming die
68, and forming element 69, as illustrated in the complete system
of FIG. 1. Described another way, the invention includes one or
more constrictions constructed and arranged to define nucleating
pathway(s) and one or more constrictions upstream and/or downstream
of the nucleating pathway(s) that each optionally include
temperature control and/or shaping capability.
[0108] Very thin product, such as sheet, can be made by controlling
cell growth such that very small cells result and the cells are
well-contained within the sheet (the cells do not create holes
across the sheet), and very thick material can be produced
(especially with a multi-hole nucleator) because controlled-growth
cells are evenly distributed within residence chamber 70 just
upstream of shaping die 68. In contrast, where in typical prior art
microcellular processes the entire microcellular foaming process
occurs at the shaping die, it has been difficult to produce thick
material since rapid nucleation and cell growth in a single step
typically cannot be made to occur uniformly throughout a large
cross-section of material, and pressure drop rates sufficient to
cause nucleation are difficult to achieve through nucleators of
large cross sectional dimension.
[0109] In a preferred embodiment, nucleator 66 has a polymer
receiving end in fluid communication with the extrusion barrel,
constructed and arranged to receive a fluid, non-nucleated,
single-phase solution of polymeric material and blowing agent
supplied by the barrel. The nucleator includes a nucleated polymer
releasing end in communication with residence chamber 70
constructed and arranged to contain nucleated polymeric material
under conditions controlling cell growth, and a fluid pathway
connecting the receiving end to the releasing end. The fluid
pathway of the nucleator has length and cross-sectional dimensions
creating a desired pressure drop rate through the pathway. In one
set of embodiments, the pressure drop rate is relatively high, and
a wide range of pressure drop rates are achievable. A pressure drop
rate can be created, through the pathway, of at least about 0.1
GPa/sec in molten polymeric material admixed homogeneously with
about 6 wt % CO.sub.2 passing through the pathway of a rate of
about 40 pounds fluid per hour. Preferably, the dimensions create a
pressure drop rate through the pathway of at least about 0.3
GPa/sec under these conditions, more preferably at least about 1
GPa/sec, more preferably at least about 3 GPa/sec, more preferably
at least about 5 GPa/sec, and more preferably still at least about
7, 10, or 15 Gpa/sec.
[0110] The nucleator is particularly suitable for producing
material at high throughput. Residence chamber 70 has a smallest
cross-sectional dimension (i.e. diameter with a circular cross
section, or cross section of an annular pathway, etc.) about 0.25
inch in one set of embodiments, about 0.4 inch in another set of
embodiments, about 0.6 inch in another set of embodiments, about
0.8 inch in another set of embodiments, and about 1.0 inch in
another set of embodiments. Chamber 70 has a length to diameter
ratio of at least about 1, preferably at least about 2, and more
preferably at least about 3. Preferably, the length to diameter
ratio is at least 10, preferably 20, more preferably 40. Chamber 70
is constructed and arranged to maintain polymeric material within
the chamber at a pressure of at least about 150 psi, preferably at
least about 500 psi. Thus, the residence chamber should include a
combination of one or more of temperature control, outlet orifice
size, cross-sectional diameter, and length to control pressure
accordingly.
[0111] Referring now to FIG. 3, an extruder system 80 is
illustrated which is similar to extruder system 30 with the
exception that it does not include a nucleator 66 separate from a
shaping die, but includes a unique shaping die 82 of the invention
which allows rapid nucleation and controlled cell growth to produce
high-quality microcellular or supermicrocellular material. System
80 includes, generally, components similar to those of system 30,
but shaping die 82 of the invention is a multiple-pathway die that
includes separate nucleating pathways 83 into which a single-phase
solution of polymeric material and blowing agent is introduced.
Each nucleating pathway is arranged to provide a pressure drop rate
in the material sufficient to cause nucleation, and nucleated
product emerging from the nucleating pathways is recombined to form
a microcellular or supermicrocellular product having dimensions
unachievable, or difficult to achieve, without compromising cell
size, density, or other aspects, in the prior art.
[0112] Thus, in the preferred embodiment of system 30 in which
nucleator 66 is a multi-hole nucleator, and in the embodiment of
system 80, including shaping die 82, each of the nucleator 66 and
nucleating shaping die 82 includes at least two separate nucleating
pathways each constructed and arranged to receive a fluid,
single-phase solution of a polymeric material and non-nucleated
blowing agent, each pathway constructed and arranged to create a
pressure drop rate of at least about 0.1, 1, 3, 5, 7, 10, or 15
GPa/sec in molten polymeric material, or other higher pressure drop
rates described above, when the molten polymeric material is
admixed homogeneously with about 6 wt % CO.sub.2 passing through
the pathway at a rate of about 40 pounds fluid per hour. These
conditions of percent CO.sub.2 and flow rate are definitive of the
construction of the nucleating pathways, and are not intended to be
limiting with respect to particular flow rates and/or blowing agent
concentrations to be used in accordance with the invention. The
nucleating pathways are constructed, according to a variety of
embodiments, to provide the above-noted pressure drop rates in
solutions of fluid polymer and blowing agent according to other
flow rates and/or blowing agent concentrations described
herein.
[0113] A more detailed description of these fluid passageways is
provided below, and any description applied to either of nucleator
66 or die 82 can be applied to the other. Thus, each of nucleator
66 according to the preferred embodiment and die 82 continuously
nucleates blowing agent admixed with material to be foamed by
dividing a fluid stream containing the material and blowing agent
into separate portions and separately nucleating each of the
separate portions. Die 82 is constructed and arranged to release
foamed material to a channel exposed, without further constriction,
to ambient conditions in the embodiment illustrated.
[0114] The nucleator and/or nucleating capacity of the die of the
invention facilitates one aspect of the invention which involves
extrusion apparatus constructed and arranged to nucleate a fluid,
single-phase solution of a polymeric material and a blowing agent
without the necessity of an auxiliary nucleating agent such as
talc. In conventional foaming techniques, a nucleating agent such
as talc can be used to create sites of nucleation. In such
techniques, the limited number of nucleating agent particles and
resulting low cell density and cell size are unacceptable in many
applications, such as wire applications, involving very thin
coatings. Auxiliary nucleating agents can also, for example,
attenuate a signal in a wire via introduction of impurities. This
is not to say that impurities, and additives commonly added in
polymeric extrusion such as flame retardants, which can instigate
nucleation, are excluded from mixtures to be extruded in the
invention. Indeed, auxiliary nucleating agents can be added to
formulations of the invention according to some embodiments. But in
many embodiments nucleation can be made to occur without auxiliary
nucleating agents.
[0115] The nucleator 66 and die 82 are designed to restrict a
stream of blowing agent-containing polymeric material in order to
create a high pressure drop rate required for cell nucleation, and
can be made by forming a plurality of apertures in the face of a
disc or, alternatively, from a porous material comprising a
plurality of apertures. The dimensions and quantity of the
plurality of apertures can be varied to achieve varying magnitudes
of pressure drop, pressure drop rates, and polymer melt shear
rates. The magnitude of the pressure drop can be varied by changing
the aperture length. The rate at which the pressure drops can be
varied by changing the number of apertures. The shear rate of the
polymer melt can be varied by changing the cross-sectional
dimension of the apertures. Since the magnitude of the solubility
change required varies with the polymer type, temperature, and flow
rate, different nucleators can be designed for different process
applications.
[0116] FIG. 4 is a cross-section through lines 4-4 of FIG. 1,
illustrating a multi-hole nucleator in one embodiment of the
invention. The multi-hole nucleator includes a plurality of
nucleating pathways 67, as illustrated. Arrangements for multi-hole
nucleator 66 and die 82 of the invention can be very similar in at
least the portion of each component designed to nucleate.
[0117] FIG. 5 is a cross-section of an annular die 90 that can
serve as a die of the invention without separate nucleator 66. The
die is designed to achieve a degree of solubility change by causing
nucleation through a plurality of channels and shaping in a
controlled manner, allowing formation of microcellular material.
The die includes an annular fluid inlet 92 (the inlet can be
non-annular, such as circular), an annular fluid outlet 94, and an
annular section 96 connecting the inlet with the outlet that
increases in radius as a function of distance from the inlet to the
outlet so as to enable the manufacture of a large diameter tubular
section. Alternatively, the annular section can decrease in radius
to produce small diameter tubes. Annular section 96, as
illustrated, also increases in cross-sectional area in a downstream
direction to control pressure drop rates, but can be of constant
cross-sectional area or can decrease in cross-sectional area.
Sections that increase or decrease in cross-sectional area are
included in the invention. Also located between inlet 92 and outlet
94 is a multiple-pathway nucleating section 98 of the die including
a plurality of nucleating pathways 100, each constructed and
arranged to provide a pressure drop rate thereacross allowing
nucleation. In another embodiment, the die includes a single
nucleating pathway rather than multiple nucleating pathways
100.
[0118] Die 90, as illustrated, includes a shaping section 104 in
which nucleated material emerging from nucleating pathways 100 is
recombined, and thereafter extruded to form a final part. Cooling
channels 106 or other means of cooling the die can be provided
upstream and/or downstream of the nucleating section 98 to control
viscosity, pressure within cells, and to control the formability of
the extrudate at exposure to ambient conditions. The ability to
control the temperature of the polymer melt as it flows through the
die allows improved control of cell size by minimizing growth of
very large cells that can create imperfections in the surface of
the extrudate. It also allows for formation of a smooth skin on the
surface of the extrudate.
[0119] In FIG. 5, nucleating section 98 can be provided at other
locations, such as in portion 96. Moreover, the annulus cross
section and radius can be changed. For example, a die can be
arranged in which flow would be as if 94 were an inlet and 92 an
outlet.
[0120] FIG. 6 is a cross-section through line 6-6 of FIG. 5,
showing a plurality of nucleating pathways 100 of circular cross
section within nucleating section 98.
[0121] FIGS. 7 and 8 illustrate alternate embodiments of the die 90
of FIG. 5, each taken in cross-section through line 6-6 of each
alternative die. In FIG. 7, nucleating pathways 108 are curved
slits that each pass from the outer limit of the nucleation section
to the inner limit thereof. FIG. 8 includes nucleating slits 110,
each of which is arranged to extend circumferentially in the
nucleating section.
[0122] FIG. 9, taken along line 6-6 of FIG. 5 in another embodiment
and showing the nucleation section only, includes a plurality of
concentric annuli 114, each including a plurality of semicircular
indentations 116 (or indentations of another geometry) arranged
such that the semicircular indentations align with each other to
provide a plurality of nucleating pathways. The uppermost and
lowermost annuli 114 include indentations 116 only at one face of
the annulus. Annuli 114 of FIG. 9 can be arranged with one or more
of annuli 114 offset circumferentially such that the semicircular
indentations 116 are not aligned, but communicate with each other,
to provide a series of concentric, undulating annuli defining
nucleating pathways. FIG. 10 illustrates an arrangement similar to
that of FIG. 9 in which each of three top plates 117 include
semicircular indentations in one face only, and bottom plate 119
includes no indentations, the arrangement defining a plurality of
separate nucleating pathways of semicircular cross-section.
[0123] FIGS. 5-10 demonstrate that the annular die 90 of the
invention can include nucleating pathways defined by slits or
passages of any of a variety of geometries so long as the desired
pressure drop and pressure drop rate across the passages is
achieved, and fluid flowing through the passages can be recombined
to form a final product. Other contemplated geometries include
combinations of slits and holes, for example a series of holes,
some or all of which are interconnected by slits to define
dumbbell-shaped cross-sectional nucleating pathways. In these
arrangements, the thickness, or cross-sectional dimension, of an
extruded article can be controlled by providing additional layers
of fluid passageways. Essentially any combination of shapes, sizes,
and changes in shape, size, and cross section can be provided in
the die and/or nucleator of the invention. For example, a die or
nucleator can have any combination of different passages, so long
as a desired pressure drop and pressure drop rate is achieved.
[0124] FIGS. 5-10 also demonstrate the ability of the dies of the
present invention to extrude thick microcellular material, that is,
material having a large cross-sectional dimension. Referring to any
of FIGS. 5-10, it can be seen that increasing the width of the
annulus of nucleation can be achieved while each separate
nucleating pathway remains of a fixed cross-sectional dimension.
Thus, pressure drop rate can remain constant while highly uniform,
thick material is produced. A cylinder of microcellular material
extruded from a die such as that shown in FIG. 5 can be sliced
longitudinally following extrusion to produce an essentially
non-corrugated sheet of any of a variety of widths and thicknesses,
the thickness being controlled as described above and the width
being controlled by adjusting the radius of the annular fluid
outlet 94.
[0125] FIG. 11 illustrates a multiple-pathway die or nucleator 118
in accordance with the invention in which a plurality of nucleating
pathways 120 communicate at their upstream ends with a section 121
of the extruder providing a single-phase solution of polymeric
material and blowing agent, and at their downstream ends with a
section 124 which can be the residence chamber 70 or a shaping
section of a die. Nucleating pathways 120 are not aligned axially
with the extruder, but are slanted relative to the extruder axis. A
plurality of nucleating pathways 122, also communicating fluidly
with sections 121 and 124, are arranged along axes that also are
not in alignment with the axis of the extruder, and are not aligned
with the axes of passages 120. That is, the pathways 120 and
pathways 122 are not parallel, but slanted relative to each other.
Each of the pathways 120 and 122 can provide flow into section 124
that is separate, for example as in passages 100 of FIG. 5, and
then is recombined, or can provide flow that recombines at the
exits of the pathways. That is, one or more of the pathways can
converge and intersect each other at or prior to the end of each
passageway. Additionally, as described above, the pathways can be
of any cross-sectional shape such as circular, triangular, square,
rectangular, slits, or the like, and can increase or decrease in
cross-section in a downstream direction. This design, in which
nucleating pathways are non-parallel, reduce molecular orientation
and weak weld lines in the extrudate. For purposes of clarity, in
FIG. 11 a plate 123 within which passages 120 and 122 are bored is
not shown to contain pathways at all locations. Pathways can be
provided throughout plate 123 from top to bottom, or at selected
locations. For example, a series of clusters of pathways 120 and
122 can be provided, each cluster converging in an outlet, a
plurality of resulting outlets providing nucleated material that is
recombined in section 124.
[0126] Pathways that decrease or increase in cross-section allow
control over the local pressure drop rate of polymeric material
flowing though them. Passages with non-circular cross-sections and
variable spacing between them control the distribution of nucleated
material.
[0127] Referring now to FIGS. 12a-12h, a variety of geometries of
separate nucleating pathways is illustrated. The various
arrangements can be provided in the multi-hole nucleator of the
invention or in a multi-hole nucleation section of a die. FIG. 12a
illustrates an article (nucleator or nucleating pathway of die) 126
including pathways 128 of essentially circular cross-section. The
pathways do not converge or change in cross-section along their
length, but are slanted relative to the axis of the extruder and
relative to each other. FIG. 12b illustrates an article 130
including a passageway 132 that decreases in cross-sectional area
along its length and a passageway 134 that increases in
cross-sectional dimension lengthwise. FIG. 12c illustrates an
article 136 having two parallel pathways 138, each of triangular
cross section, neither changing in cross-sectional dimension along
its length. FIG. 12d illustrates an article 140 including a
plurality of passages 142, each of essentially rectangular cross
section, and none of which change in cross-sectional dimension
along its length. The passages are arranged axially with the
extruder, and each rectangle is arranged with its larger dimension
aligned radially. FIG. 12e illustrates an article 144 including
passages 146, each of triangular cross-section, neither of which
changes in cross-sectional area along its length, and each of which
is slanted relative to the axis of the extruder and relative to
each other. FIG. 12f illustrates an article 148 including passages
150 each designed and arranged as in the article of claim 140 but
of larger cross-section initially, with cross section decreasing in
a downstream direction. FIG. 12g illustrates an article 152 having
fluid pathways 154 and 156, each of essentially circular cross
section and each arranged along the axis of the extruder.
Passageway 154 decreases in cross-sectional area in a downstream
direction until a midpoint of article 152, whereupon it begins
increasing in cross-sectional area and terminates in
cross-sectional area essentially identical to its starting
cross-sectional area. Passageway 154 provides for an increasing
pressure drop rate in the converging section and controlled cell
growth, if pressure is low enough, in the diverging section.
Passageway 156 begins and ends in similar cross-sectional area, but
increases in cross-sectional area towards the middle where it
reaches a maximum. FIG. 12h illustrates an article 158 including a
plurality of concentric, annular passages 160. A standard spider
arrangement rendering this arrangement feasible is not
illustrated.
[0128] FIG. 37, described in greater detail below, is a
cross-section of an annular die 201 of the invention that is
particularly useful in producing very smooth, thin microcellular
material in cylindrical or sheet form at very high pressure drop
rate during forming. That is, die 201 can receive a single-phase
solution and nucleate, followed almost immediately by shaping.
Nucleation and shaping are separate, but occur in rapid succession.
The die includes an annular fluid inlet 203, an annular fluid
outlet 205 and annular sections 207 and 210 adjoining inlet 203 and
outlet 205, respectively, and connecting the inlet and the outlet.
The more upstream annular section 207 has a constant radius and a
constant gap dimension of a size selected to define a nucleating
pathway. That is, section 207 is designed to receive a homogenous,
single-phase solution of polymeric material and blowing agent and
to subject the material to a rapid pressure drop to cause
nucleation. Section 210 is of a radius that increases in a
downstream direction but that, like section 207, includes a
constant gap dimension. The gap dimension of section 210 typically
is larger than the gap of section 207 and is sized to receive a
nucleated solution and to allow controlled cell growth to form
microcellular extrudate.
[0129] The die design of FIG. 37 has been identified in accordance
with the invention as one that allows good control in formation of
unexpectedly smooth, microcellular sheet material. Superior control
is achieved in die 201 as follows. When nucleated material is
allowed to grow in section 210, since section 210 includes a
constant width gap, growth of the sheet can occur only laterally.
Lateral growth of the sheeth is permitted due to the constantly
increasing radius of the annulus at section 210, allowing growth
without corrugation.
[0130] Although a variety of die geometries can be selected, a
tapered die, that is, one having a nucleating pathway(s) that
decrease(s) in cross-sectional area in a downstream direction can
be advantageous in many situations since more reasonable system
pressures and less blowing agent can be used which minimizes cell
connectivity. When used as, for example, a wire coating, resulting
microcellular material can be superior in having better water and
water vapor barrier properties. In the invention, the single-phase
solution is maintained in an unnucleated state prior to the
nucleating pathway. Where the nucleating pathway decreases in
cross-sectional dimension in a downstream direction, the solution
is maintained in an unnucleated state between the mixing section at
which the single-phase solution is achieved and the beginning of
the decrease in cross-sectional dimension.
[0131] Pathways that decrease in cross-sectional area in a
downstream direction have been found to create relatively high
pressure drop rates across a relatively short length of the die, by
creating a nonlinear pressure/displacement curve that includes a
region of relatively high pressure drop rate without the need for
high initial pressure. Referring to FIG. 13, pressure drop profiles
are plotted. Curve 1 represents a typical pressure drop profile
through a parallel-landed (straight) nucleating pathway typical of
a standard extrusion die configuration. The typical pathway does
not change in cross-sectional area along its length, thus pressure
drop per unit length is constant throughout the pathway, i.e., the
pressure drop curve has a constant negative slope. Curve 5
represents an exemplary critical solubility level of blowing agent
in polymeric material, that is, the pressure above which a
single-phase solution can exist and below which nucleation will
occur.
[0132] The cross-sectional area of a nucleating pathway can change
(e.g. decrease) at an essentially constant rate, or at a variable
rate, for example a rate which increases. That is, the nucleating
region can be a passageway of an essentially straight, increasing
or decreasing taper or can be of an increasing or decreasing taper
and also have a convex or concave wall or a wall having regions of
differing taper. Thus, in one aspect, the invention provides a
method involving continuously decreasing the pressure within
successive, continuous portions of a flowing, single-phase stream
at a rate which increases, while causing nucleation.
[0133] The present invention involves, according to one aspect, the
recognition that it is desirable to maximize the pressure drop rate
dP/dt across curve 5. Ideally, pressure drop would be
instantaneous, as in curve 2. Of course, this is impossible. In a
parallel-landed nucleating pathway, to increase dP/dt from, for
example, 1.4 GPa/sec (curve 1) to approximately 25 GPa/sec (curve
3), initial pressure necessarily must be higher than 10,000 psi,
which is unacceptable in extrusion apparatus. Curve 3 could be
achieved, for example, by using the same die but drastically
increasing flow rate, or by decreasing die diameter.
[0134] The nucleator of the invention including a tapered
(decreasing cross-sectional area in a downstream direction)
nucleating pathway solves the problem of achieving high pressure
drop rates and sufficient overall pressure drop at acceptable
system operating pressures. This is because the tapered nucleating
pathway of the invention creates, in material urged therethrough, a
pressure profile of curve 4. As the amount of taper increases from
zero (parallel land) to a positive value, the slope of the pressure
drop rate curve becomes non-linear where the pressure drop per unit
length in the pathway increases. The result is a portion A of curve
4, through the critical solubility concentration, having a
relatively steep slope (approximately 25 GPa/sec) where the curve
represents an overall pressure drop of only 4000 psi through the
nucleating pathway. Therefore, only 4000 psi need be established
upstream of the pathway and a 25 GPa/sec pressure drop rate is
achieved from a point above the solubility pressure threshold of
the fluid stream to atmosphere. As described, significantly higher
pressure drop rates are achievable in accordance with the
invention.
[0135] Curves 1-4 are based on pressure calculations through the
nucleating pathways based on rheological data obtainable from
typical foamable polymeric material.
[0136] The pressure profile (curve 4) achievable with the tapered
nucleating pathway can facilitate formation of closed-cell
microcellular material under conditions in which, in prior art
processes, open-cell material was formed. At a given dP/dt and melt
temperature, increasing the percent blowing agent above a critical
level can increase cell connectivity in microcellular material.
That is, under certain conditions, too much blowing agent can cause
cells to rupture. In connection with one set of embodiments,
therefore, it has been found that it is desirable to use only that
amount of blowing agent necessary, and lower levels of blowing
agent are necessary when using the tapered nucleating pathway of
the invention, in particular, blowing agent at levels substantially
below saturation levels. This approach is in contrast with most
prior art approaches which typically involved maximizing blowing
agent concentration with the goal of thereby achieving maximum cell
densities since more blowing agent creates, theoretically, more
nucleation sites. In one set of preferred embodiments, in which
pressure drop rate is high, blowing agent is present in the
polymeric stream within the extruder at a level of less than about
4% by weight, more preferably less than about 3% by weight, and
more preferably still less than about 2% by weight, and more
preferably still less than about 1% by weight. In embodiments in
which extremely high pressure drop rate is used, blowing agents can
be present in amounts of about or less than about 0.5% by weight.
In another embodiment, blowing agent is present in the solution in
an amount less than about 80 percent by weight saturation
concentration as determined at the lowest pressure in the system
after the point of blowing agent injection prior to the nucleating
pathway.
[0137] Referring now to FIG. 14, an extrusion system 102 for
extruding microcellular material onto wire according to one
embodiment of the invention is illustrated schematically. Extrusion
system 102 is similar to extrusion system 80 of FIG. 3, or can be
similar to extrusion system 30 of FIG. 1 in that it can including a
nucleator that is spaced from a shaping die. In the preferred
embodiment illustrated, system 102 includes a constriction 164 that
is a nucleating pathway having an entrance 166 and an exit 168, and
the nucleating pathway 164 decreases in cross-sectional area in a
downstream direction. Nucleating pathway 164 communicates with a
crosshead die 170 arranged to receive extruded, nucleated
microcellular material from exit 168 of nucleating pathway 164 and
to apply the material to the exterior surface of a wire and allow
the material to foam into microcellular material. A wire payoff 172
is positioned to feed wire 174 into the crosshead 170. A take-up
arrangement 176 is positioned to receive wire coated with
microcellular material from the crosshead. Wire payoffs and
take-ups are known, and standard arrangements can be used in the
invention. Although not shown, the system can include components
such as wire preheaters, a cooling trough between the crosshead and
take-up, and sensors such as capacitance sensors and thickness
sensors arranged to sense dimensional and electrical
characteristics of the coated wire.
[0138] Although a pressure type die is illustrated, a tube-type
tooling design can be used in the invention. A pressure type design
is a die and tip design in which the wire is exposed to polymer
flow behind the die. A tube type design is one in which the wire is
not exposed to polymer until the wire exits from the die.
[0139] The aspect of the invention that provides a system for
extruding microcellular material onto wire is advantageous for the
following reasons. Foam material is advantageous relative to solid
material for wire insulation because foamed material provides
enhanced electrical properties with increased void fraction (less
material per unit volume). However, in any foaming technique, if
the thickness of the material formed is less than the maximum cell
size, holes will exist in the material. This is unacceptable in
typical wire coating applications since holes would allow moisture
ingress and compromise electrical performance. Physical properties
of such material would also be compromised. In the very thin
insulation wall thicknesses of Category 5 and similar wires it has
been difficult or impossible to form foamed insulation on wire.
[0140] The present invention provides an arrangement in which
microcells can be created in a manner in which the cellular
structure is a relatively hermetic barrier to moisture as well as
providing the required physical properties appropriate for category
5 applications.
[0141] The invention provides, according to one aspect, a method
involving continuously extruding microcellular material onto a wire
substrate in which the microcellular material has a void fraction
of less than 50%, preferably less than about 30%, more preferably
still less than about 20%. An article comprising a wire and a
coating of microcellular material around the wire having a void
fraction of less than about 50%, more preferably less than about
30%, and more preferably still less than about 20%, is provided as
well in accordance with the invention.
[0142] A single or tandem extruder, as described, can be adapted to
carry out all of the techniques of the invention, including wire
coating. An arrangement can be adapted for wire coating by the
addition of a crosshead die assembly, where the assembly is defined
as an adapter, transfer tube, and wire handling system comprised of
a payoff, wire straightener, preheater, cooling trough, puller, and
winder.
[0143] Uniformity of cell structure is important in this
arrangement for uniform capacitance, high velocity of propagation
resulting from low dielectric constant, good mechanical strength,
and low water absorbance. Compared to a solid material, a foamed
material with similar characteristics will provide relatively less
combustible mass and hence byproducts of combustion, making
microcellular foam coated wires less hazardous.
[0144] In connection with formation of microcellular coatings on
wires, particularly thin microcellular material is produced. This
advantage is not limited to the coatings produced on wires, but
involves recognition of conditions necessary for producing thin
material that can be applied to free-standing sheet, tubes, and
other thin articles. According to this aspect of the invention,
microcellular material, preferably essentially closed-cell
material, of thickness less than about 4 mm, preferably less than
about 3 mm, more preferably less than about 1 mm is produced. In
some embodiments extremely thin microcellular material is produced,
namely material of less than about 0.5 mm in thickness, more
preferably less than about 0.25 mm in thickness, more preferably
still less than about 0.2 mm in thickness. In some particularly
preferred embodiments material on the order of 0.1 mm in thickness
is produced. All of these embodiments can include essentially
closed-cell material.
[0145] As noted, the invention encompasses a variety of products
shaped from very thin microcellular material. These materials can
include articles such as wire coatings, described above, tubes,
hose straws, and the like.
[0146] One aspect of the invention involves production of foamed,
preferably microcellular foamed, crystalline and semi-crystalline
polymeric material formed by continuous polymer extrusion. In
preferred embodiments crystalline and semi-crystalline polymeric
material is foamed as microcellular material with a blowing agent
that is essentially solely carbon dioxide, preferably supercritical
carbon dioxide. As noted above, the prior art generally teaches
that the expansion of nucleation sites, or cell growth, may be
minimized by, for example, cooling the melt prior to extrusion or
by quenching the material upon exposure to atmosphere in order to
freeze cell growth. Alternatively, the prior art teaches that such
expansion may be controlled by the use of viscosity modifiers or
foam-controllability additives. Such additives increase the
controllability of foaming by generally functioning to increase
melt strength and/or melt elasticity. Crystalline and
semi-crystalline materials require much higher operating
temperatures than amorphous materials, as it is necessary to
operate at the Tm or above in order to prevent crystallization of
such materials in, for example, an extruder. Such conditions are
contrary to the prior art, which teaches that with regard to the
production of amorphous microcellular material such as, for
example, polystyrene, it is necessary to minimize the difference
between the Tg and the extrusion temperature of an amorphous
polymer in order to prevent expansion of cells beyond the
microcellular range.
[0147] In general, the difference between the required operating
temperature and the Tg of crystalline and semi-crystalline
materials is much greater than for amorphous polymers, as shown by
a comparison of such values in Table A. For example, the difference
between the Tg and a typical operating temperature for extruding
polystyrene is about 40.degree. C., whereas for LDPE it is about
135.degree. C., and for PET it is about 155.degree. C. In the
table, Tg and Tm refer to values of polymeric material free of
blowing agent. While not wishing to be bound by any theory, it is
likely that operating temperature can be slightly below Tm because
of viscosity modification by the blowing agent.
1TABLE A* Operating Material Tg Tm Temperature Delta Material Type
(.degree. C.) (.degree. C.) (.degree. C.) (.degree. C.) Polystyrene
amorphous 90-100 n/a 140 40-50 Low Density semi-crystalline -110
115 110 220 Polyethylene High Density semi-crystalline -110 134 145
255 Polyethylene Polypropylene semi-crystalline -10 165 180 190
Polyethylene semi-crystalline 70 260 230 160 Terephthalate Nylon
6-6 semi-crystalline 50 240 *T.sub.g and Tm from "Principals of
Polymer Processing", Tadmore, Z., Gogos, C., John Wiley & Sons,
New York, 1979, p. 38.
[0148] Surprisingly, crystalline and semi-crystalline microcellular
materials can be produced according to the method of the present
invention without the need to cool the melt to temperatures near
the Tg, and without the use of viscosity or foam-controllability
modifiers, as taught in the prior art. The present invention
involves the discovery that well-controlled extrusion of
microcellular material may be achieved, even at temperatures well
above the Tg of a polymer, by operating at particularly high
pressure drop rates. Such high pressure drop rates facilitate the
continuous formation of crystalline and semi-crystalline
microcellular materials. Although not wishing to be bound by any
theory, it is believed that a reduction in the internal force
associated with each nucleation site may be achieved by reducing
the size of the nucleation sites and maintaining very small cells
during foaming. This can be achieved, in turn, by creating many
sites of nucleation. Under comparable processing conditions, a
nucleated solution having more numerous, and smaller, nucleation
sites will produce relatively smaller cells, since blowing agent
distributed among more numerous cells results in less blowing agent
per cell, therefore smaller cells during growth. Further, since the
expansion force acting on an interior wall of a gaseous cell at a
constant pressure increases with the square of the cell diameter, a
smaller cell experiences much less expansion force per unit area of
cell wall than does a larger cell. Smaller sites contain less
entrained gas, and therefore have a lower internal pressure than
larger sites. A reduction in the internal pressure results in
reduced cell expansion.
[0149] It is theorized that the prior art teaching of cooling the
melt for the purpose of increasing melt strength also achieves such
a reduction in the expansion force by reducing the energy
associated with the molecules of gas contained in each nucleation
site. The reduced energy associated with the gas entrained therein
results in a reduction in the internal pressure and reduced cell
expansion upon extrusion to atmosphere.
[0150] Semicrystalline and crystalline microcellular materials that
can be processed according to the method include polyolefins such
as polyethylene and polypropylene, crosslinkable polyolefins,
polyesters such as PET, polyamides such as Nylons, etc., and
copolymers of these that are crystalline. In particular, unmodified
standard production grade material can be used in contrast to
standard prior art materials which, it typically has been taught,
require modifications such as incorporation of foam-controllability
additives including components of other polymer families (e.g.
polycarbonate in polyethylene terephthalate) (see, for example,
Boone, G. (Eastman Chemical Co.), "Expanded Polyesters for Food
Packaging", Conference Proceedings of Foam Conference, 1996, Sep.
10-12, Somerset, N.J.). These additives increase the
controllability of foaming by generally functioning to increase
melt strength and/or melt elasticity. In this aspect, microcellular
material can be made having preferred average cell sizes, maximum
cell sizes, and cell densities as described above, and can be
processed according to techniques and systems described herein.
Examples of material that do not include foam-controllability
modifiers include Eastman 9663 PET and Wellman 61802 PET. According
to the method, semicrystalline or crystalline microcellular
material may be made having preferred average cell sizes, maximum
cell sizes, and cell densities as described below.
[0151] Production of such crystalline or semi-crystalline material
is facilitated by a method of the invention that involves melting
the material and maintaining its temperature at least above the
recrystallization temperature of the material. Preferably, a
flowing fluid polymeric material is established by elevating the
temperature of the material to at least the approximately Tm of the
polymer or higher, and then extruding the material into ambient
conditions while foaming and shaping the material into an extrudate
shape at a die temperature at least about 100.degree. F. (at least
about 37.8.degree. C.) above Tg, preferably at least about
120.degree. F. (at least about 48.9.degree. C.), more preferably at
least about 150.degree. F. (at least about 65.6.degree. C.) above
Tg of the crystalline or semi-crystalline polymer. In some
embodiments foaming and shaping occurs at a die temperature even
higher relative to Tg, for example at least about 200.degree. F.
(at least about 93.3.degree. C.) above Tg, at least about
250.degree. F. (at least about 121.degree. C.), or at least about
300.degree. F. (at least about 149.degree. C.) above Tg. In this
context, Tg and Tm refer to values of the polymer without addition
of blowing agent.
[0152] This aspect of the invention facilitates a method of
continuously extruding crystalline or semi-crystalline material
from an extruder at a throughput rate of at least about 10 lbs/hr,
preferably at least about 25 lbs/hr, more preferably at least about
40 lbs/hr, and in particularly high throughput rates at least 60,
80, or 100 lbs/hr. These high throughput rates are representative
of a surprisingly advantageous result achieved not only with
crystalline and semi-crystalline materials, but with other
materials in the invention described herein.
[0153] Another aspect of the invention involves production of
foamed, preferably microcellular foamed, low intrinsic viscosity
(I.V.), standard production grade, polyethylene terephthalate (PET)
of low density. The prior art teaches that, in production of foamed
polymeric material, one generally needs to use material of a
minimum I.V. for the support of cellular structure. It is known
that higher I.V. material will have a higher melt elasticity and
melt strength, both of which could contribute to the support of
cell growth. The invention involves production of such material via
higher concentration of blowing agent, for example blowing agent at
greater than 3% by weight (which provides capability of operating
at lower temperatures), higher pressure drop rates, for example
greater than 0.5 GPa/sec (which provides efficient nucleation of
many small cells leading to better control of growth), or both. In
particular, the invention involves production of foamed PET of I.V.
less than one, or in some cases less than 0.8. In another aspect,
the invention involves production of crystalline or
semi-crystalline microcellular material, such as PET, of density of
less than 8 lbs/ft.sup.3. In another aspect, the invention involves
production of foamed crystalline or semi-crystalline microcellular
material, such as PET, essentially free of foam-controllability
modifiers.
[0154] Another aspect of the invention involves continuous
extrusion of microcellular polymeric material including filler in
minimum amounts. Addition of filler is expected to have an effect
opposite that of addition of flow-control modifiers, that is, to
weaken melt strength. Using high pressure drop rates of the
invention, microcellular material, including crystalline and
semicrystalline material, having filler in an amount of at least
about 10% by weight based on the weight of the entire mixture, or
at least about 25%, or at least about 35%, or at least about 50%
can be achieved. "Filler", as used herein, includes those fillers
known to those skilled in the art to be present in, for example,
filled polyolefin. Typical fillers include talc, flame retardant,
etc.
[0155] Selection of geometry and number of pathways for nucleating
pathways of the nucleator or nucleating die of the invention can be
made with consideration of the following physical principles.
Nucleation is the beginning state in the creation of cells by phase
separation in a material. The final cell density, number of cells
in a unit volume of a original material, depends on the number of
nucleation sites. The product density is a function of cell density
and cell size, or alternatively, void fraction. The cell size is
also related to the number of nucleation sites and amount of gas
present, etc. Therefore, control of the nucleation number is very
important in continuous microcellular processing. Classical
nucleation theory shows the nucleation rate (N; 1/sec) as a
function of many parameters according to equation 1
N=C.multidot..function.exp(-.DELTA.G/kT) (1)
[0156] where C is the concentration of gas molecules, f is the
frequency factor for molecules of gas joining the nucleus [1/sec],
.DELTA.G is the activation energy for nucleation, k is Boltzmann
constant, and T is the temperature. .DELTA.G can be defined
according to equation 2
.DELTA.G=(16.pi..gamma..sup.3)/(3(.DELTA.P).sup.2) (2)
[0157] where g is surface energy and .DELTA.P is the pressure drop
relative to saturation pressure. Equation (1) shows that the
nucleation rate is proportional to the concentration of gas
molecules, and cell density is higher with higher nucleation
temperatures and larger pressure drops.
[0158] One must also consider the kinetic aspects between the
nucleation and the diffusion. The characteristic nucleation time is
a function of the characteristic length (diameter of cells),
nucleation rate and the gas diffusivity. The characteristic
diffusion time is a function of characteristic length and
diffusivity. It is necessary that characteristic diffusion time,
.DELTA.t.sub.d, is much greater than characteristic nucleation
time, .DELTA.t.sub.n, to maximize cell density by avoiding
competition for dissolved gas between nucleation and cell growth.
Dimensionless analysis show the criteria in equation (3):
.DELTA.t.sub.m/.DELTA.t.sub.d.about.D/(N.multidot.d.sup.5)1 (3)
[0159] where D is diffusivity, N is nucleation rate, and d is
characteristic length.
[0160] From equation (1), it can be seen that the concentration of
gas molecules and the magnitude of the pressure drop relative to
the saturation pressure are important parameters for control of
cell density. In continuous microcellular processing, the maximum
amount of gas concentration and diffusivity depend upon the kind of
gas and polymer. When the polymer and gas are given, pressure drop
is an important process variable which can be determined by
principles well known for flow through pipes. Equation (4) shows
that pressure drop depends on parameters of the power-law viscosity
model, diameter of pipe, land length of pipe and volumetric flow
rate:
.DELTA.p=4m.multidot.{[(8(3.+-.1/n)Q)/(.pi.d.sup.3)].sup.n.multidot.L}/d
(4)
[0161] where .DELTA.P is pressure drop, m and n are power law
constants; L is land length of pipe; d is the diameter of pipe and
Q is volumetric flow rate.
[0162] The pressure drop rate is another important factor for the
nucleation in continuous microcellular processing. Pressure drop
rate can be determined by calculating the pressure drop and the
residence time of flow in the pipe. Equation (5) shows that
pressure drop rate dP/dt is a function of viscosity, pipe diameter,
and volumetric flow rate:
dP/dt=16m.multidot.{[8(3.+-.1/n)Q)/(.pi.d.sup.3)].sup.n.multidot.Q}/.pi.d.-
sup.3 (5)
[0163] The design of nucleation devices is constrained by the shear
rate of a polymer flow, because the flow may become unstable in the
high shear rate region.
[0164] The function and advantage of these and other embodiments of
the present invention will be more fully understood from the
examples below. The following examples are intended to illustrate
the benefits of the present invention, but do not exemplify the
full scope of the invention.
[0165] The following abbreviations have been adopted for purposes
of the following examples:
2 L = length of hole d = hole Diameter N = number in holes V.sub.f
= the velocity of the final extrudate A.sub.f = cross-sectional
area of the extrudate A.sub.o = the total cross sectional area of
all the holes r.sub.f = density of the microcellular plastic
r.sub.o = density of the plastic/CO.sub.2 solution before foaming M
= mass flow rate from the extruder output r.sub.o = the diameter of
each hole V.sub.o = velocity of unfoamed material at the exit g =
shear rate
EXAMPLE 1
[0166] The following example describes a process for determining
the critical dimensions of a die of this invention, using an
approximation analysis. This example will enable those skilled in
the art to develop alternative die designs that can be used to make
microcellular plastics, yet still fall within the spirit and scope
of the presently claimed invention.
[0167] If it is assumed that the plastic will expand uniformly in
all three directions, then the ratio of the density of the
microcellular plastic .rho..sub.f to the density of the unfoamed
plastic .rho..sub.0 may be written, as a first approximation,
as:
.rho..sub..function./.rho..sub.0=(1/a).sup.3 (6)
[0168] where a is the linear expansion ratio during foaming.
Equation 6 states that if one wishes to decrease the density by a
factor of two, the linear expansion ratio must be about 1.26.
[0169] If the die consists of a large number of circular holes
through which the plastic is extruded, the area ratio of the holes
to the total final area of the extrudate determines the final
density, to a first approximation. The continuity relationship
demands that:
M=.rho..sub..function.A.sub..function.V.sub..function.=.rho..sub.0A.sub.0V-
.sub.0 (7)
[0170] Where .rho.=density, A=area, V=velocity, sub-f=foamed, and
sub-0=unfoamed. If one assumes that V.sub.f=a V.sub.0, the area
ratio may be expressed as:
A.sub..function./A.sub.0=a.sup.2 (8)
[0171] where A.sub.0 is the area of each hole, A.sub.i, times the
number of the holes N. The number of holes required to provide a
desired density reduction is thus:
N=A.sub..function./(a.sup.2A.sub.i) (9)
[0172] If one assumes that an extruder can process at a mass flow
rate of M, the flow rate through each hole can be computed. The
volume flow rate per hole q.sub.i is related to the mass flow rate
as:
q.sub.i=M/N.rho..sub.0 (10)
[0173] The flow rate through a single hole is related to the
pressure drop .DELTA.p as:
q.sub.i=[(.pi.r.sub.0.sup.3)/(1/n+3)][(r.sub.0/2m)(.DELTA.p/L)].sup.1/n
(11)
[0174] Where L=length of a hole, r.sub.0=radius of the hole, and m
and n are materials constants for a power law viscosity model given
by:
.eta.=m(.gamma.).sup.n-1 (12)
[0175] Equation (9) can be solved for .DELTA.p over the length of
the hole. Using the above equations, one can calculate the
approximate number of holes required to process a given plastic at
a given flow rate and at required pressure drop and pressure drop
rate. For example, if one wants to make a polystyrene microcellular
foam with a specific gravity of 0.3 and if the flow rate is 200
lbs/hr, one could use 130 holes, each having a diameter of 0.018
inches. The pressure drop and the pressure drop rate are calculated
to be 44 MPa and 4 GPa/s, respectively, through the holes, assuming
that m is 17,420 Ns.sup.0.3/m.sup.2 and n is 0.3, which are the
values reported for impact grade polystyrene at 430.degree. D
(Novacor/Monsanto 3350). Since viscosity is affected by the
concentration of CO.sub.2 and temperature of operation, the actual
viscosity data should be used to refine these calculations.
Furthermore, the pressure in the holes must be high enough to keep
the plastic/gas solution as a single phase until the plastic exits
the die. In practice, the pressure will decrease throughout the
length of the holes and therefore, the high pressure drop rate is
essential.
EXAMPLE 2
Tandem Wire Extrusion System for Microcellular Material
[0176] A tandem extrusion line (Akron Extruders, Canal Fulton,
Ohio) was arranged including a 2 inch, 32/1 L/D primary extruder
and a 2.5 inch, 34/1 L/D secondary extruder. An injection system
for injection of CO.sub.2 into the primary was placed at a distance
of approximately 20 diameters from the feed section. The injection
system included 4 equally-spaced circumferentially,
radially-positioned ports, each port including 176 orifices, each
orifice of 0.02 inch diameter, for a total of 704 orifices.
[0177] The primary extruder was equipped with a two-stage screw
including conventional first-stage feed, transition, and metering
sections, followed by a multi-flighted (four flights) mixing
section for blowing agent dispersion. The screw was designed for
high-pressure injection of blowing agent with minimized pressure
drop between the first-stage metering section and point of blowing
agent injection. The mixing section included 4 flights unbroken at
the injection ports so that the orifices were wiped (opened and
closed) by the flights. At a screw speed of 80 RPM each orifice was
wiped by a flight at a frequency of 5.3 wipes per second. The
mixing section and injection system allowed for very rapid
establishment of a single-phase solution of blowing agent and
polymeric material.
[0178] The injection system included air-actuated control valve to
precisely meter a mass flow rate of blowing agent at rates from 0.2
to 12 lbs/hr at pressures up to 5500 psi.
[0179] The secondary extruder was equipped with a deep channel,
three-flighted cooling screw with broken flights, which provided
the ability to maintain a pressure profile of microcellular
material precursor, between injection of blowing agent and entrance
to the point of nucleation (the die, in this case) varying by no
more than about 1500 psi, and in most cases considerably less.
[0180] The system was equipped, at the exit of the secondary
extruder, with a 90 degree adapter and transfer tube mounted
horizontally to allow wire to be fed through a Genca LoVOl.TM.
(Clearwater, Fla.) crosshead mounted at the end of the transfer
tube. A die with an exit O.D. of 0.0291 inch was used having a 7
degree included taper. A 0.021 inch diamond tip was used.
[0181] 24 AWG solid copper wire was fed to the crosshead utilizing
a standard payoff system, straightener, and preheater before the
crosshead. A cooling trough, nip roll puller, and winder were
placed downstream of the crosshead to cool and take up the
wire.
[0182] A bleed valve was positioned in the transfer tube to provide
appropriate flow volume control for thin coating of small wire.
EXAMPLE 3
Extrusion of Microcellular, Flame-Retardant High-Density
Polyethylene onto 24 AWG Solid Copper Wire
[0183] Polyethylene pellets (Union Carbide UNIGARD-HP.TM. DGDA-1412
Natural, 1.14 g/cc) were gravity-fed from the hopper of the primary
screw into the extrusion system of Example 2. Primary screw speed
was 15 RPM giving a total output (bleed and die) of approximately
15 lbs/hr of microcellular material. Secondary screw speed was 3
RPM. Barrel temperatures of the secondary extruder were set to
maintain a melt temperature of 336.degree. F. measured at the end
of the secondary extruder. CO.sub.2 blowing agent was injected at a
rate of 0.54 lbs/hr resulting in 3.6 wt % blowing agent in the
melt. Pressure profile between the injection ports and the inlet of
the crosshead was maintained between 3400 and 4040 psi.
Approximately 1.2 lbs/hr fluid microcellular material precursor
flowed through the crosshead, which could be controlled by
adjustment of the bleed valve.
[0184] FIGS. 15 and 16 are photocopies of SEM images of cross
sections of microcellular wire coating, following removal of wire,
according to this example, showing substantially uniform cells of
approximately 20 microns average size, with maximum cell size of
approximately 25 microns. Material density was approximately 0.96
g/cc, and cell density was approximately 40.times.10.sup.6
cells/cc. Average coating thickness was approximately 0.005
inch.
EXAMPLE 4
Extrusion of Very Thin Microcellular Flame-Retardant Polyolefin
Wire Coating onto a 24 AWG Solid Copper Wire
[0185] Flame-retardant filled polyolefin was extrusion coated onto
24 AWG solid copper wire as an extremely thin, microcellular
insulating coating.
[0186] A tandem extrusion system similar to that of example 2 was
used in this example. The system included a 1.5 inch, 33:1 L/D
primary extruder, a 2 inch, 24:1 L/D secondary extruder, a
cross-head with a pressure-type die (0.0393 inch diameter), wire
payoff, wire preheater, wire straightener, cooling trough, belt
capstan type puller, and winder. A desiccating drying hopper was
used to pre-condition polymer pellets to remove excess
moisture.
[0187] Flame-retardant filled polyolefin pellets were gravity-fed
from the desiccating hopper into the extrusion system. Primary
screw speed was 40 RPM giving a calculated mass flow rate of 27.1
lb/hr (no bleed port in use). Secondary screw speed was 8 RPM.
Barrel set point temperatures of the secondary extruder were set to
maintain a melt temperature of 400.degree. F. (204.degree. C.) at
the end of the extruder. CO.sub.2 blowing agent was injected at a
rate of 0.1 lb/hr resulting in a 0.9% by polymer weight blowing
agent in the material. Pressure profile between the injection ports
and the inlet to the cross-head was maintained between 4100 psi and
3600 psi, respectively. The estimated pressure before the die was
1500 psi. The wire line speed was approximately 600 fpm. With a
cooling trough initial quench distance of 10 inches from the die
exit, a 0.016 inch thick coating of microcellular material, with a
density reduction of 48% (calculated material density of nominally
0.73 g/cc) of material was produced. Relocation of the cooling
trough initial quench distance to 91 inches from the die exit
(under otherwise identical conditions) resulted in a 0.013 inch
thick coating with a density reduction of 27% (calculated material
density of nominally 1.04 g/cc) of the solid material.
[0188] FIGS. 17 and 18 are photocopies of SEM images of
cross-sections of the resultant 0.016 inch thick microcellular wire
coating, following removal of the wire (for ease of creation of the
required fracture profile). Cell sizes range from about 8 to about
10 microns in diameter. FIGS. 19 and 20 are photocopies of SEM
images of cross-sections of the 0.013 inch thick microcellular wire
coating, following removal of the wire. Cell sizes range from about
5 to about 10 microns in diameter.
[0189] The microcellular wire coatings of this example essentially
surround and are secured to the conductor (wire) with no
discernable gap between the inner surface of the microcellular
coating and the outer surface of the conductor. FIG. 24 is a
photocopy of an optical micrograph of a wire coating sample,
without wire removed, mounted in epoxy and sectioned to reveal
cross-sectional detail of the microcellular coating and wire. The
light area in FIG. 24 is the copper conductor and the darker region
is the microcellular wire coating.
[0190] The 0.016 inch thick wire coating samples were subjected,
prior to removal of wire, to UL 444 Section 6.2 Crash Resistance
Tests and all samples passed.
EXAMPLE 5
Extrusion of Very Thin Microcellular Flame-Retardant Polyolefin
Wire Coating onto a 24 AWG Solid Copper Wire
[0191] Flame-retardant filled polyolefin pellets were gravity fed
from the hopper into a tandem extrusion system of example 4.
Primary screw speed was 55 RPM giving a calculated mass flow rate
of 13.7 lbs/hr onto the wire and 17.8 lbs/hr through a bleed port.
Secondary screw speed was set at 11 RPM. Barrel set point
temperatures of the secondary extruder were set to maintain a melt
temperature of 400.degree. F. (204.degree. C.) at the end of the
extruder. CO.sub.2 blowing agent was injected at a nominal rate of
0.1 lbs per hour resulting in 0.7% by polymer weight blowing agent
in the material. Pressure profile between the injection ports and
the inlet to the cross-head was maintained between 4900 psi and
4100 psi. The estimated pressure before the die was 2000 psi. Wire
line speed was approximately 820 fpm. A die with a 0.032 inch
diameter was used. With cooling trough initial quench distance of
19 inches from the die exit, a 0.007 inch thick coating of
microcellular material with a density reduction of 20% (from the
solid material, calculated material density of nominally 1.13 g/cc)
was produced.
[0192] FIGS. 21 and 22 are photocopies of SEM images of
cross-sections of the resulting 0.007 inch thick microcellular wire
insulating coating, following removal of the wire. Cell sizes range
from about 5 to about 10 microns in diameter.
[0193] FIG. 23 is a photocopy of an optical micrograph of the wire
coating sample of this example (without wire removed) mounted in
epoxy and sectioned to reveal cross-sectional detail of the
microcellular coating and wire (light copper conductor; dark:
microcellular wire coating). The coating essentially surrounds and
secures the conductor with no discernable gap.
[0194] The 0.007 inch thick wire coating samples were subjected to
the UL 444 Section 6.2 pressure resistance test and all samples
past.
EXAMPLE 6
Tandem Extrusion System for Microcellular Material
[0195] An Akron tandem extrusion line was arranged as in Example 2
but did not include the adapter, transfer tube, crosshead, die,
wire payoff and winder, and bleed valve of Example 2. Instead,
mounted at the end of the secondary extruder were a die adapter and
a cylindrical rod die with a 0.080 exit orifice and a 0.60 land
length. The die adapter was equipped with taps for measurement of
melt temperature and pressure just prior to entry into the die.
[0196] The system included instrumentation allowing measurement of
pressure and temperature of the melt stream at least six locations
throughout the tandem system between a location just prior to the
blowing agent injection ports to the point of entry into the die to
precisely monitor material conditions. Along the screw, melt
temperature was measured with infrared equipment to avoid
disruption of the melt stream.
EXAMPLE 7 (COMPARATIVE)
Extrusion of Non-Microcellular Polyethylene Terephthalate (PET)
[0197] PET pellets (Wellman, 0.8 IV, bottle-grade resin) were dried
in a Conair (Franklin, Pa.) drying system at 350 F for 4 hours
prior to use. The pellets were gravity-fed from the drying hopper
into an extrusion system of Example 6. Primary screw speed was 26
RPM giving a total output of approximately 53 lbs/hr of material.
Secondary screw speed was 5 RPM. Barrel temperatures of the
secondary extruder were set to maintain a melt temperature of
532.degree. F. measured at the end of the secondary extruder.
CO.sub.2 blowing agent was injected at a rate of 1.0 lb/hr
resulting in 2.0% blowing agent in the melt. Pressure profile
between the injection ports and the inlet of the die was maintained
between 2910 and 3100 psi. The pressure drop rate across the die
was 2.2 GPa/sec.
[0198] FIG. 25 is a photocopy of an SEM image of the cross section
of the extrudate, showing relatively large, non-uniform cells of
approximately 100 to 300 microns average size.
EXAMPLE 8
Extrusion of Microcellular Polyethylene Terephthalate (PET)
[0199] Parameters and equipment were selected as in Example 7, with
the exception that primary screw speed was 41 RPM, giving a total
output of approximately 85 lbs/hr of microcellular material,
CO.sub.2 blowing agent was injected at a rate of 1.7 lb/hr
resulting in 2.0 wt % blowing agent in the melt, and pressure
profile between the injection ports and the inlet of the die was
maintained between 3210 and 3430 psi. The pressure drop rate across
the die was 3.9 GPa/sec.
[0200] FIG. 26 is a photocopy of an SEM image of the cross section
of the extrudate, showing substantially uniform cells of
approximately 20 microns average size, with maximum cell size of
approximately 40 microns. Material density was approximately 40
lbs/ft.sup.3, and cell density was approximately 2.5.times.10.sup.8
cells/cm3.
[0201] This example, taken with example 7, demonstrates
experimentally that high pressure drop rates, with fixed wt %
blowing agent and melt temperatures, yields higher cell densities
with smaller cells.
EXAMPLE 9 (COMPARATIVE)
Extrusion of Flame Retardant Polyethylene (FRPE)
[0202] FRPE pellets (Union Carbide UNIGARD-HP.TM. DGDA-1412
Natural, 1.14 g/cc) were gravity-fed from the hopper of the primary
extruder into a system of Example 6 including, additionally, a 90
degree adapter and transfer tube mounted horizontally at the exit
of the secondary extruder with a Genca LoVOl.TM. (Clearwater, Fla.)
crosshead at the end of the transfer tube. A bleed valve was
positioned in the transfer tube to provide appropriate flow volume
control through the die.
[0203] Primary screw speed was 25 RPM giving a total output of
approximately 32 lbs/hr of material. Secondary screw speed was 8
RPM. Barrel temperatures of the secondary extruder were set to
maintain a melt temperature of 331.degree. F. measured at the end
of the secondary extruder. CO.sub.2 blowing agent was injected at a
rate of 0.84 lb/hr resulting in 2.6 wt % blowing agent in the melt.
Pressure profile between the injection ports and the inlet of the
die was maintained between 2800 and 2280 psi. The pressure drop
rate across the die was 0.48 GPa/sec.
[0204] FIG. 27 is a photocopy of an SEM image of the cross section
of the extrudate, showing cells of approximately 25 to 50 microns
average size. Material density was approximately 0.8 g/cc, and cell
density was approximately 15.times.10.sup.6 cells/cc The extrudate
included non-uniform cell distribution with cells significantly
larger in the center of the material as compared to areas near the
skin, with pronounced decrease in cell density near the center of
the extrudate.
EXAMPLE 10
Extrusion of Microcellular Flame Retardant Polyethylene (FRPE)
[0205] Parameters and equipment were selected as in Example 9, with
the exception that total output was approximately 27 lbs/hr of
microcellular material, CO.sub.2 blowing agent was present at 3.1
wt % blowing agent in the melt, and pressure profile between the
injection ports and the inlet of the die was maintained between
3520 and 3540 psi. The pressure drop rate across the die was 1.1
GPa/sec.
[0206] FIG. 28 is a photocopy of an SEM image of the cross section
of the extrudate, showing substantially uniform cells of
approximately 17-25 microns average size, with maximum cell size of
approximately 35 microns. Material density was approximately 0.85
g/cc, and cell density was approximately 61.times.10.sup.6
cells/cc.
[0207] This example, taken with example 9, demonstrates
experimentally that high pressure drop rates, with essentially
equal wt % blowing agent and melt temperatures, yields higher cell
densities with smaller cells.
EXAMPLE 11
Long Single Extrusion System for Microcellular Material
[0208] An NRM (Pawcatuck, Conn.) 4.5 inch 44/1 L/D long single
extrusion line was equipped with an injection system for injection
of CO.sub.2 placed at a distance of approximately 25 diameters from
the feed section. The injection system included 4 equally-spaced
circumferentially, radially-positioned ports, each port including
417 orifices, each orifice of 0.02 inch diameter, for a total of
1668 orifices.
[0209] The extruder was equipped with a two-stage screw including
conventional first-stage feed, barrier flight transition, and
metering sections, followed by a multi-flighted (six flights)
mixing section for blowing agent dispersion. The screw was designed
for high-pressure injection of blowing agent with minimized
pressure drop between the first-stage metering section and point of
blowing agent injection. The second stage of the screw included a
mixing section having 6 flights unbroken at the injection ports so
that the orifices were wiped (opened and closed) by the flights. At
a screw speed of 80 RPM each orifice was wiped by a flight at a
frequency of 8 wipes per second. The mixing section and injection
system allowed for very rapid establishment of a single-phase
solution of blowing agent and polymeric material. The injection
system included an air-actuated control valve to precisely meter a
mass flow rate of blowing agent at rates from 0.2 to 50 lbs/hr at
pressures up to 5500 psi.
[0210] The second stage of the screw was also equipped with a deep
channel, three-flighted cooling section with broken flights, which
provided the ability to cool the polymer melt stream.
[0211] The system included, at the end of the extruder, a die
adapter and a cylindrical annular die with a gap of 0.34 inch,
inner diameter of 0.4 inch, and land length of 2 inches. The die
adapter was equipped with taps for measurement of melt temperature
and pressure just prior to entry into the die.
[0212] The system included instrumentation allowing measurement of
pressure and temperature of the melt stream at least 7 locations
throughout the system between a location just prior to the blowing
agent injection ports to the point of entry into the die to
precisely monitor material conditions. Along the screw, melt
temperature was measured with infrared equipment to avoid
disruption of the melt stream.
EXAMPLE 12
Extrusion of Non-Microcellular Filled, Plasticized Polyvinyl
Chloride (PVC)
[0213] PVC pellets (approx. 1/3 wt % filler, highly-plasticized).
The pellets were gravity-fed from the hopper into the extrusion
system of Example 11. Primary screw speed was 30 RPM giving a total
output of approximately 246 lbs/hr of material. Barrel temperatures
of the cooling section were set to maintain a melt temperature of
approximately 300.degree. F. measured at the end of the extruder.
CO.sub.2 blowing agent was injected at a rate of 2.5 lbs/hr
resulting in 1.6 wt % blowing agent per weight PVC and plasticizer
in the melt. The pressure drop rate across the die was 0.3
GPa/sec.
[0214] FIG. 29 is a photocopy of an SEM image of the cross section
of the extrudate, showing very large, non-uniform cells of greater
than 200 microns. Material density was approximately 0.96 g/cc, and
cell density was approximately 3.times.10.sup.4 cells/cc.
EXAMPLE 13
Extrusion of Microcellular Filled Plasticized Polyvinyl Chloride
(PVC)
[0215] Systems and parameters were selected as in Example 12 with
the exception that die gap was 0.012 inch, inner diameter 0.538
inch, land length was 0.25 inch. Primary screw speed was 15 RPM
giving a total output of approximately 176 lbs/hr of material.
CO.sub.2 blowing agent was injected at a rate of 1.95 lb/hr
resulting in 1.7 wt % blowing agent per weight PVC and plasticizer
in the melt. The pressure drop rate across the die was 6.9
GPa/sec.
[0216] FIG. 30 is a photocopy of an SEM image of the cross section
of the extrudates, showing substantially uniform cells of
approximately 20 microns average size, with maximum cell size of
approximately 35 microns. Material density was approximately 0.88
g/cc, and cell density was approximately 8.times.10.sup.7
cells/cc.
[0217] This example, taken with example 12, demonstrates
experimentally that high pressure drop rates, with essentially
equal wt % blowing agent and melt temperatures, yields higher cell
densities with smaller cells.
EXAMPLE 14
Extrusion of Non-Microcellular Polypropylene
[0218] A system was used as in Example 6, with the exception that
the die land length was 1.2 inches. Polypropylene pellets
(PP1602-WF, Quantum Chemical, Cincinnati) were gravity-fed from the
hopper into the extrusion system. Primary screw speed was 11.5 RPM
giving a total output of approximately 14.4 lbs/hr of material.
Secondary screw speed was 4.8 RPM. Barrel temperatures of the
secondary extruder were set to maintain a melt temperature of
approximately 400.degree. F. measured at the end of the secondary
extruder. CO.sub.2 blowing agent was injected at a rate of 1.04
lb/hr resulting in 7.2 wt % blowing agent in the melt. Pressure
profile between the injection ports and the inlet of the die was
maintained between 890 and 1090 psi. The pressure drop rate across
the die was 0.15 GPa/sec.
[0219] FIG. 31 is a photocopy of an SEM image of the cross section
of the extrudates, showing relatively large cells of approximately
150 microns average size. Material density was approximately 0.57
g/cc, and cell density was approximately 322.times.10.sup.3
cells/cc.
EXAMPLE 15
Extrusion of Microcellular Polypropylene
[0220] System and parameters were as in Example 14 with the
following exceptions. The die diameter was 0.04 inch, die land
length was 0.688 inch. Primary screw speed was 60.5 RPM giving a
total output of approximately 45 lbs/hr of material. Secondary
screw speed was 20 RPM. CO.sub.2 blowing agent was injected at a
rate of 3.0 lb/hr resulting in 6.7 wt % blowing agent in the melt.
Pressure profile between the injection ports and the inlet of the
die was maintained between 2010 and 3420 psi. The pressure drop
rate across the die was 15 GPa/sec.
[0221] FIG. 32 is a photocopy of an SEM image of the cross section
of the extrudate, showing essentially uniform microcells of
approximately 20 microns average size. Material density was
approximately 0.44 g/cc, and cell density was approximately
246.times.10.sup.6 cells/cc.
EXAMPLE 16
Extrusion of Relatively Open-Celled Microcellular FRPE
[0222] Examples 16 and 17 demonstrate that increasing concentration
of CO.sub.2 results in interconnected cell structure.
[0223] A system was used as in Example 9 with the exception that a
straight cylindrical die with die diameter 0.06 and land length
0.688 inch was affixed to the transfer tube instead of the Genca
LoVol head.
[0224] Primary screw speed was 80.1 RPM giving a total output of
approximately 98.8 lbs/hr of material. Secondary screw speed was 28
RPM. Barrel temperatures of the secondary extruder were set to
maintain a melt temperature of approximately 340.degree. F.
measured at the end of the secondary extruder. CO.sub.2 blowing
agent was injected at a rate of 5.0 lb/hr resulting in 5.1 wt %
blowing agent in the melt. Pressure profile between the injection
ports and the inlet of the die was maintained between 2370 and 3940
psi. The pressure drop rate across the die was 7.5 GPa/sec.
[0225] FIG. 33 is a photocopy of an SEM image of the cross section
of the extrudate, showing relatively open-cell microcellular
material having cells of approximately 10-20 microns average size.
Material density was approximately 0.85 g/cc, and cell density was
approximately 196.times.10.sup.6 cells/cc.
EXAMPLE 17
Extrusion of Relatively Closed-Cell Microcellular FRPE
[0226] A system was used as in Example 16. Primary screw speed was
30.2 RPM giving a total output of approximately 39.4 lbs/hr of
material. Secondary screw speed was 8 RPM. Barrel temperatures of
the secondary extruder were set to maintain a melt temperature of
approximately 340.degree. F. measured at the end of the secondary
extruder. CO.sub.2 blowing agent was injected at a rate of 1.08
lb/hr resulting in 2.7 wt % blowing agent in the melt. Pressure
profile between the injection ports and the inlet of the die was
maintained between 1640 and 2810 psi. The pressure drop rate across
the die was 2.1 GPa/sec.
[0227] FIG. 34 is a photocopy of an SEM image of the cross section
of the extrudate, showing relatively closed-cell microcellular
material having cells of approximately 20 microns average size.
Material density was approximately 0.76 g/cc (relatively lower).
Cell density was approximately 119.times.10.sup.6 cells/cc.
Moisture absorption was less than one-half that of the open-celled
material of Example 16. Lower material density and lower moisture
absorption indicate a relatively more closed-cell structure.
EXAMPLE 18
Flat Pressure Profile Extrusion System Including Multi-Hole
Nucleator
[0228] Parameters and equipment were selected as in Example 6, with
the following exceptions. The screw was designed such that at a
screw speed of 59 RPM each orifice was wiped by a flight at a
frequency of 3.9 wipes per second.
[0229] A multi-hole nucleator (66, FIG. 1) included 88 cylindrical
nucleating pathways that did not change in cross-sectional
dimension along their length. Each nucleating pathway had a hole
diameter of 0.031 inch and a land length of 0.394 inch.
[0230] Additionally, the extrudate stands were cooled at exit from
the die using a water spray located at approximately one inch from
the die face. The water temperature used in the spray system was
approximately 70.degree. F.
EXAMPLE 19
Extrusion of Microcellular Polyethylene Terephthalate (PET) Using
Multi-Hole Nucleator
[0231] This example demonstrates production foamed, low I.V.,
unmodified standard production grade, crystalline polymeric
material of low density. PET pellets were obtained and processed as
in Example 7. A system was used as in Example 18. Primary screw
speed was 59 RPM giving a total output of approximately 116 lbs/hr
of material. Secondary screw speed was 18 RPM. Barrel temperatures
of the secondary extruder were set to maintain a melt temperature
of approximately 451.degree. F. measured at the end of the
secondary extruder. CO.sub.2 blowing agent was injected at a rate
of 7.6 lbs/hr resulting in 6.5% blowing agent in the melt. A
single-phase solution of CO.sub.2 blowing agent and polymer was
created in less than one second after injection of the blowing
agent, specifically within approximately 0.6 second. The pressure
drop rate across the multi-hole nucleator was 0.80 GPa/sec. A very
flat pressure profile was maintained between the pressure achieved
after injection and the inlet of the nucleating pathways of the
multi-hole nucleator was between 4100 and 4520 psi, in a very flat
profile (FIG. 35).
[0232] FIG. 36 is a photocopy of an SEM image of the cross section
of the extrudate, showing substantially uniform cells of
approximately 40 microns average size, with maximum cell size of
about 65 microns. Material density was approximately 5
lbs/ft.sup.3, and cell density was approximately 4.5.times.10.sup.8
cells/cm.sup.3.
EXAMPLES 20 AND 21
Extrusion of Microcellular Unfilled, Polyvinylchloride (PVC)
[0233] Systems and parameters were selected as in Example 11 with
the following exceptions. The extruder was equipped with a rod die
with a straight land and exit into ambient. PVC pellets with
plasticizer were obtained and extruded.
Example 20
[0234] a flow rate of 132 lbs/hr was established. CO.sub.2 blowing
agent was injected to establish blowing agent at 7.5 wt %. The
pressure drop rate across the die was 2.75 GPa/S. The die had a
circular opening of 95 mils diameter and a land length of 1.52
inches. Microcellular material having average cell size of 60
microns was produced.
Example 21
[0235] a flow rate of 271 lbs/hr was established. CO.sub.2 blowing
agent at 6.83% was introduced and the pressure drop rate was 4.17
GPa/S. The die was the same as in Example 20. Microcellular
material having average cell size of 45 microns resulted.
EXAMPLES 22-26
Extrusion of Microcellular, Filled Polyvinylchloride (PVC)
[0236] Systems, parameters and materials were selected as in
Examples 20 and 21 with the exception that an annular straight land
die into ambient conditions was used, and PVC pellets including
approx. 1/3 wt % filler (plasticized) were used. The table below
sets forth parameters and results. Gas % is on the basis of lbs of
CO.sub.2 per lb of PVC and plasticizer.
3 Ex. Flow dP/dt .DELTA.P Gap Land Cell No. lb/hr GPa/s Gas % psi
mils in. .mu.'s 22 241 .33 3.06 2880 34 2 80 23 235 .36 3.94 3190
34 2 25 24 293 1.41 2.41 3640 20 .85 50 25 296 1.33 3.24 3400 20
.85 30 26 166 6.76 4.66 4570 12 .25 15
EXAMPLE 27
Extrusion of Microcellular Material from an Annular Nucleator
Separated from an Adjustable Gap Lip Die by a Residence Chamber
[0237] An NRM (Pawcatuck, Conn.) 2.5 inch 42/1 L/D long single
extrusion line was equipped with an injection system for injection
of CO.sub.2 placed at a distance of approximately 18 diameters from
the feed section. The injection system included 4 equally-spaced
circumferentially, radially-positioned ports, each port including
305 orifices, each orifice of 0.02 inch diameter, for a total of
1220 orifices.
[0238] The extruder was equipped with a two-stage screw including
conventional first-stage feed, barrier flight transition, and
metering sections, followed by a multi-flighted (six flights)
mixing section for blowing agent dispersion. The screw was designed
for high-pressure injection of blowing agent with minimized
pressure drop between the first-stage metering section and point of
blowing agent injection. The second stage of the screw included a
mixing section having 6 flights unbroken at the injection ports so
that the orifices were wiped (opened and closed) by the flights.
The mixing section and injection system allowed for very rapid
establishment of a single-phase solution of blowing agent and
polymeric material.
[0239] The injection system included an air-actuated control valve
to precisely meter a mass flow rate of blowing agent at rates from
0.2 to 12 lbs/hr at pressures up to 5500 psi.
[0240] The second stage of the screw also included a cooling
section equipped with a deep channel, three-flighted then
two-flighted cooling section with broken flights, which provided
the ability to cool the polymer melt stream.
[0241] The system included, at the end of the extruder, a die
adapter and a cylindrical annular die with a gap of 0.020 in, inner
diameter of 0.88 inch, and land length of 0.45-0.65 inches. The die
adapter was equipped with taps for measurement of melt temperature
and pressure just prior to entry into the die.
[0242] The system included instrumentation allowing measurement of
pressure and temperature of the melt stream at least 7 locations
throughout the system between a location just prior to the blowing
agent injection ports to the point of entry into the die to
precisely monitor material conditions. Along the screw, melt
temperature was measured with infrared equipment to avoid
disruption of the melt stream. An adjustable gap lip section
downstream from a nucleator for the purpose of controlling the
thickness of foamed sheet was used. The die is shown in FIG. 37 and
includes a mandrel 200 consisting of a fixed section 202 and an
adjustable section 204. The adjustable section can be positioned
away from the fixed section by placing circular shims at locations
206. The die outer body 208 is fixed. The die shown has an annular
flow channel 210 diverging from the die centerline by an angle 212
of 45.degree.. Experiments were also performed with a die with a
70.degree. diverging angle. The gap opening 214 is adjustable from
20 mils to 50 mils by the use of shims without changing the
nucleator annular gap 216 from a typical value of 20 mils.
[0243] The variable gap lip die was used to investigate the
influence of die gap opening on product thickness. As an example,
polystyrene with 6% by weight CO.sub.2 at a flow rate of
approximately 84 lb/hr at a melt temperature of approximately
246.degree. F. was shaped in the 70.degree. diverging die at a die
lip gap openings of 25 mils and 50 mils. The pressure measured
approximately at location 218 for the 25 mil-gap was, as expected,
higher (2710 psi) than the pressure (2060 psi) measured for the
50-mil gap. In these experiments, the foamed sheet thickness
increased from 100 mils for the die with the 25-mil gap to 150 mils
for the die with the 50-mil gap. The differences in cell size and
cell density between these two die lip gaps were not considered
significant.
EXAMPLE 28
Extrusion of Microcellular PET Using a Converging Die
[0244] This example demonstrates production of foamed, low I.V.,
unmodified standard production grade, crystalline polymeric
material of very low density. Parameters and equipment were
selected as in Example 6, with the following exceptions. The screw
was designed such that at a screw speed of 53 RPM each orifice was
wiped by a flight at a frequency of 3.5 wipes per second.
[0245] A die with an exit OD of 0.040 inch and an 18.4 degree
included taper was used. The taper length of this die was 0.750
inch. Mounted on the outside of the taper length section of the die
was a brass cooling block. This cooling block contained channels
that allowed flow of heat transfer oil around the die taper length
for control of the temperature of the die along the taper
length.
[0246] PET pellets were obtained and processed as in Example 7. A
system was used as in Example 18. Primary screw speed was 53 RPM
giving a total output of approximately 96 lbs/hr of material.
Secondary screw speed was 18 RPM. Barrel temperatures of the
secondary extruder were set to maintain a melt temperature of
approximately 472.degree. F. measured at the end of the secondary
extruder. CO.sub.2 blowing agent was injected at a rate of 6.0
lbs/hr resulting in 6.3% blowing agent in the melt. A single-phase
solution of CO.sub.2 blowing agent and polymer was created in less
than one second after injection of the blowing agent, specifically
within approximately 0.6 second. The pressure drop rate across the
converging die was 14.9 GPa/sec. A very flat pressure profile was
maintained between the pressure achieved after injection and the
inlet of the nucleating pathways of the multi-hole nucleator was
between 3,580 and 3,250 psi, in a very flat profile.
[0247] FIG. 38 is a photocopy of an SEM image of the cross section
of the extrudate, showing substantially uniform cells of
approximately 40 microns average size, with maximum cell size of
about 65 microns. Material density was approximately 3.2
lbs/ft.sup.3, and cell density was approximately 7.3.times.10.sup.8
cells/cm.sup.3.
EXAMPLE 29
A Tandem Extrusion Line for Microcellular Material
[0248] A tandem extrusion line including a 27 mm 40:1 L/D
counter-rotating twin screw primary extruder (American Leistritz
Extruder, Sommervile, N.J.) and a 21/2 46:1 L/D single screw
secondary extruder (Akron Extruders, Canal Fulton, Ohio) were
arranged in a right angle configuration. A weight loss feeder
capable of supplying up to 100 lb/hr was mounted over the feed
throat of the primary extruder. Polymer pellets at a precisely
controlled output were metered out of the weight loss feeder and
gravity fed to the primary extruder. An injection system for the
injection of CO.sub.2 into the secondary was placed at
approximately 8 diameters from the inlet to the secondary. The
injection system included 4 equally spaced circumferential,
radially-positioned ports, each port including 131 orifices, each
orifice of 0.02 inch diameter, for a total of 524 orifices.
[0249] The twin screw primary extruder was equipped with matched
pair of screws employing conventional feeding, melting, mixing,
venting and pressure building sections. The screw pair was designed
for dispersion of high filler loading levels and pressure
generation. The outlet of this primary extruder was connected to
the inlet of the secondary extruder using a short connecting
adapter about 8 inches in length.
[0250] An injection system included an air actuated control valve
to precisely meter a mass flow rate of blowing agent at rates from
0.2 to 21 lbs/hr at pressures up to 5500 psi.
[0251] The secondary extruder was equipped with a specially
designed screw to provide melt feeding, blowing agent dispersion
and cooling of the polymer/blowing agent blend. The melt feeding
section was a shallow single flighted section designed to provide a
uniform polymer flow and polymer seal prior to blowing agent
injection. This section was followed by a multi-flighted blowing
agent dispersion section that included six flights unbroken at the
injection ports so that the orifices were wiped (opened and closed)
by the flights. At a screw speed of 35 rpm, each orifice was wiped
at a frequency of 3.5 wipes per second. The cooling section of the
screw was a deep channel, three flighted sections which provided to
cool the polymer and maintain the pressure profile of the
microcellular material precursor, between injection of blowing
agent and entrance to the point of nucleation (the die in this
case) varying by no more than about 1,500 psi.
[0252] The system was equipped, at exit from the secondary
extruder, with a die adapter and a 10 inch wide flat die
(Production Components, Eau Claire, Wis.) (FIG. 37). The die
adapter was equipped with taps for measurement of melt temperature
and pressure just prior to entry into the die. The flat die
included a conventional coathanger type flow distribution channel
and a flex lip adjustment system and die lip set that provided exit
gaps from 0.000 to 0.040 inches with a 0.188 inch land length.
[0253] Also provided was a conventional three roll stack and
tension winder. The three roll stack was equipped with 6 inch
diameter rolls and temperature control units that provided roll
temperature adjustment from 65.degree. F. to 200.degree. F.
EXAMPLE 30
Extrusion of a Very Thin Polypropylene Sheet
[0254] Polypropylene pellets containing 30 weight percent talc were
metered into the tandem extrusion line described in example 29.
[0255] The weight loss feeder was adjusted to provide an output of
60 lb/hr. Screw speeds were set at approximately 330 rpm on the
primary and 38 rpm on the secondary. Secondary barrel temperatures
were set to maintain a melt temperature of 350.degree. F. at
entrance to the die. CO.sub.2 blowing agent was injected at a
nominal rate of 0.84 lb/hr resulting in a 2.0% by polymer weight
blowing agent in the material. The die gap was adjusted to 0.004
inches. The nip of the three roll stack was set to 0.015 inches and
placed approximately 11/2 inches from the die exit. Roll
temperatures were set at 75.degree. F.
[0256] The above conditions produced a product that was 0.020 inch
thick by 10 inches wide at a density of 0.67 g/cc. Based on a
nominal solid material density of 1.14 g/cc, the achieved density
reduction is 41%. The calculated pressure drop across the die land
length is approximately X GPa/s.
[0257] FIGS. 39 and 40 are photocopies of SEM cross sections of
this thin microcellular sheet showing cell sizes from 15 to 35
microns.
EXAMPLE 31
Extrusion of a Very Thin Polypropylene Sheet
[0258] Polypropylene pellets containing 30 weight percent talc were
metered into the tandem extrusion line described in example 29.
[0259] The weight loss feeder was adjusted to provide an output of
60 lb/hr. Screw speeds were set at 333 rpm on the primary and 38
rpm on the secondary. Secondary barrel temperatures were set to
maintain a melt temperature of 330.degree. F. at entrance to the
die. CO.sub.2 blowing agent was injected at a nominal rate of 0.84
lb/hr resulting in a 2% by polymer weight blowing agent in the
material. The die gap was adjusted to 0.004 inches. The nip of the
three roll stack was set to 0.015 inches and placed approximately
11/2 inches from the die exit. Roll temperatures were set at
75.degree. F.
[0260] The above conditions produced a product that was 0.15 inch
thick by 10 inches wide at a density of 0.80 g/cc. Based on a
nominal solid material density of 1.14 g/cc, the achieved density
reduction is 30%. The calculated pressure drop across the die land
length is approximately 0.87 GPa/s.
[0261] FIGS. 41 and 42 are photocopies of SEM cross sections of
this thin microcellular sheet showing cell sizes ranging from 15 to
35 microns.
[0262] Those skilled in the art would readily appreciate that all
parameters listed herein are meant to be exemplary and that actual
parameters will depend upon the specific application for which the
methods and apparatus of the present invention are used. It is,
therefore, to be understood that the foregoing embodiments are
presented by way of example only and that, within the scope of the
appended claims and equivalents thereto, the invention may be
practiced otherwise than as specifically described.
* * * * *