U.S. patent application number 10/964821 was filed with the patent office on 2005-08-25 for wet type friction member and manufacturing method for the same.
This patent application is currently assigned to NSK-WARNER KABUSHIKI KAISHA. Invention is credited to Gu, Xiaoming, Maruo, Kenji.
Application Number | 20050186870 10/964821 |
Document ID | / |
Family ID | 34612398 |
Filed Date | 2005-08-25 |
United States Patent
Application |
20050186870 |
Kind Code |
A1 |
Maruo, Kenji ; et
al. |
August 25, 2005 |
Wet type friction member and manufacturing method for the same
Abstract
A friction plate 22 is formed by pasting a friction member 25 to
a core plate 23 of a metal. Numeral 24 designates a spline teeth
fitted to a torque transmitting member. The friction member has a
nonwoven cloth including aramide fiber and at least one of carbon
fiber, carbonized fiber, cellulose fiber and rayon. A
thermo-hardening resin includes a friction conditioner, and is
impregnated to the friction member. Further, a distribution rate of
the friction conditioner is made to be high at a friction surface
and is gradually lowered toward a bottom surface. Further, in
manufacturing the wet type friction member, a roll, an ultrasonic
wave transmitter, a vacuuming apparatus on the like is used.
Inventors: |
Maruo, Kenji; (Shizuoka,
JP) ; Gu, Xiaoming; (Shizuoka, JP) |
Correspondence
Address: |
SUGHRUE MION, PLLC
2100 PENNSYLVANIA AVENUE, N.W.
SUITE 800
WASHINGTON
DC
20037
US
|
Assignee: |
NSK-WARNER KABUSHIKI KAISHA
|
Family ID: |
34612398 |
Appl. No.: |
10/964821 |
Filed: |
October 15, 2004 |
Current U.S.
Class: |
442/59 ;
442/327 |
Current CPC
Class: |
D04H 1/425 20130101;
D04H 1/587 20130101; D04H 1/4242 20130101; F16D 69/02 20130101;
Y10T 442/60 20150401; D04H 1/43835 20200501; Y10T 442/2344
20150401; Y10T 442/20 20150401; D04H 1/4258 20130101; D04H 1/4342
20130101; Y10T 428/24994 20150401; D04H 1/64 20130101 |
Class at
Publication: |
442/059 ;
442/327 |
International
Class: |
D04H 005/00 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 15, 2003 |
JP |
P.2003-354505 |
Claims
1. A wet type friction member, comprising: a nonwoven cloth
including aramide fiber and at least one of carbon fiber,
carbonized fiber, cellulose fiber and rayon; and a thermo-hardening
resin having a friction conditioner, the thermo-hardening resin
being impregnated to the non-woven cloth.
2. The wet type friction member as set forth in claim 1, wherein a
distribution rate of the friction conditioner is high at a friction
surface of the friction member and gradually becomes lower toward a
bottom surface thereof.
3. A manufacturing method for a wet type friction member which has
a nonwoven cloth including aramide fiber and at least one of,
carbon fiber, carbonized fiber, cellulose fiber and rayon; and a
thermo-hardening resin including a friction conditioner and
impregnated to the nonwoven cloth, the method comprising steps of:
supplying the thermo-hardening resin including the friction
conditioner onto the nonwoven cloth; and impregnating the
thermo-hardening resin into the nonwoven cloth via a diffusing
unit.
4. The manufacturing method for the wet type friction member as set
forth in claim 3, wherein a distribution rate of the friction
conditioner is high at a friction surface of the friction member
and gradually becomes lower toward a bottom surface thereof.
5. The manufacturing method for the wet type friction member as set
forth in claim 3, wherein a surface of the nonwoven cloth supplied
with the thermo-hardening resin including the friction conditioner
is aside of as sliding surface of the friction member.
6. The manufacturing method for the wet type friction member as set
forth in claim 3, wherein the diffusing unit makes the nonwoven
cloth passed between rolls so as that the thermo-hardening resin
including the friction conditioner is impregnated into the nonwoven
cloth by pressing the roll.
7. The method for manufacturing a wet type friction member as set
forth in claim 3, wherein the diffusing unit impregnates the
thermo-hardening resin including the friction conditioner into the
nonwoven cloth by an ultrasonic transmitter in the impregnating
step.
8. The method for manufacturing a wet type friction memberasset
forth in claim 3, wherein the diffusing unit is installed with a
vacuuming apparatus on a lower side of the nonwoven cloth and the
thermo-hardening resin including the friction conditioner is
impregnated into the nonwoven cloth by sucking from the lower
side.
9. The manufacturing method for the wet type friction member as set
forth in claim 4, wherein a surface of the nonwoven cloth supplied
with the thermo-hardening resin including the friction conditioner
is a side of a sliding surface of the friction member.
10. The manufacturing method for the wet type friction member as
set forth in claim 4, wherein the diffusing unit makes the nonwoven
cloth passed between rolls so as that the thermo-hardening resin
including the friction conditioner is impregnated into the nonwoven
cloth by pressing the roll.
11. The method for manufacturing a wet type friction member as set
forth in claim 4, wherein the diffusing unit impregnates the
thermo-hardening resin including the friction conditioner into the
nonwoven cloth by an ultrasonic transmitter in the impregnating
step.
12. The method for manufacturing a wet type friction member as set
forth in claim 4, wherein the diffusing unit is installed with a
vacuuming apparatus on a lower side of the nonwoven cloth and the
thermo-hardening resin including the friction conditioner is
impregnated into the nonwoven cloth by sucking from the lower
side.
13. The manufacturing method for the wet type friction member as
set forth in claim 5, wherein the diffusing unit makes the nonwoven
cloth passed between rolls so as that the thermo-hardening resin
including the friction conditioner is impregnated into the nonwoven
cloth by pressing the roll.
14. The method for manufacturing a wet type friction member as set
forth in claim 5, wherein the diffusing unit impregnates the
thermo-hardening resin including the friction conditioner into the
nonwoven cloth by an ultrasonic transmitter in the impregnating
step.
15. The method for manufacturing a wet type friction member as set
forth in claim 5, wherein the diffusing unit is installed with a
vacuuming apparatus on a lower side of the nonwoven cloth and the
thermo-hardening resin including the friction conditioner is
impregnated into the nonwoven cloth by sucking from the lower side.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to a wet type friction member
which is used in a wet type multiplate clutch, a single plate
clutch of a wet type friction brake, a synchronizer ring, a lock up
clutch or the like for a vehicle and an industrial or construction
vehicle or the like and a manufacturing method for the same.
[0003] 2. Description of the Related Art
[0004] FIG. 1 is a sectional view showing a basic constitution of a
wet type multiplate clutch 10 using a wet type friction member.
Numeral 1 designates a clutch case. Numeral 11 designates a spline
groove. Numeral 21 designates a separator plate spline-engaged with
the spline groove 11. Numeral 22 designates a friction plate.
Numeral 3 designates a press plate. Numeral 5 designates a stop
ring and the friction plate 22 is spline-engaged with a hub (not
illustrated) which corresponds a counter member of transmitting
rotation from the clutch case 1. A transmitting member 2 is formed
by the separator plate 21, the friction plate 22, the press plate 3
and the like.
[0005] Numeral 4 designates a piston. In fastening the clutch, when
pressurized oil is introduced from a pressurized oil hole 61 to a
hydraulic operating chamber 6, a rotational force is transmitted by
pressing the piston 4 in a right direction and pressing the
transmitting member 2 to the stop ring 5. In releasing the clutch,
when the pressurized oil is drawn from the hydraulic operating
chamber 6, the piston 4 returns in a left direction by a return
spring 7. At this occasion, the oil is brought into a canceller 8
from an oil hole 81 to strengthen to return the piston 4 by a
centrifugal force thereof.
[0006] FIG. 2 is a front view taking out to show the friction plate
22, and a friction member 25 is pasted to a core plate portion 23
of a metal. Numeral 24 designates spline teeth provided at an inner
periphery of the core plate.
[0007] As a wet type friction member, in a conventional, a
so-called paper friction member in which paper is used as a base
material has mainly been used. The paper friction member is
fabricated by blending various friction conditioners to pulp,
making paper from the pulp, and impregnating and curing a binding
resin such as phenol resin or the like. Up to a current state, the
conventional paper friction member can be regarded to show
excellent functions to substantially meet requests of heat
resistance, .mu.-V characteristic, wear resistance between layers
and the like. Further, notation .mu., mentioned above, designates a
friction coefficient, and notation V designates a speed of sliding
with a counter member. As the .mu.-V characteristic, it is regarded
to be preferable to provide a positive gradient property in which
in accordance with an increase in V, also .mu. is increased.
DISCLOSURE OF THE INVENTION
Problems that the Invention is to Solve
[0008] Although the conventional paper friction member provides
with considerably excellent functions, however under a current
condition of increasing a load on the wet type friction member by
increasing an output of an engine of a vehicle, it becomes
difficult to simultaneously ensure functions to be satisfied of the
heat resistance, the .mu.-V characteristic, the wear resistance
between layers and the like.
[0009] The paper friction member is formed with pores by
intertwining fiber. Although, when the porosity is increased, the
heat resistance is improved, however the wear resistance between
layers (shear strength) is decreased. Conversely, although when the
porosity is decreased, the wear resistance between layers is
increased, the heat resistance is deteriorated. The both are
brought into a trade off relationship. In this way, a change in an
environment of use cannot be dealt with by the paper friction
member.
SUMMARY OF THE INVENTION
[0010] An object of the present invention is to solve the
above-described object, and provide a wet type friction member
which is a wet type friction member constituted by nonwoven cloth
including aramide resin, wherein the nonwoven cloth has at least
one of carbon fiber, carbonized fiber, cellulose and rayon, and a
thermo-hardening resin including a friction conditioner is
impregnated into the nonwoven cloth and a manufacturing method for
the same.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1 is a sectional view showing a constitution of a wet
type multiplate clutch;
[0012] FIG. 2 is a front view of a friction plate;
[0013] FIG. 3 is a view showing an embodiment of a method for
impregnating a thermo-hardening resin including a friction
conditioner into nonwoven cloth;
[0014] FIG. 4 is a view showing other embodiment similar to FIG.
3;
[0015] FIG. 5 is a view showing still other embodiment similar to
FIG. 4; and
[0016] FIG. 6 is an image view showing a situation of distributing
a friction conditioner at inside of nonwoven cloth.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
ADVANTAGES OF THE INVENTION
[0017] The nonwoven cloth can use a fiber longer than that used in
a paper friction member. Further, orientation of respective fibers
becomes random and therefore, after ensuring porosity, also shear
strength is excellent. Furthermore, in order to promote the heat
resistance, the nonwoven cloth is based on aramide fiber. Also, the
friction member is impregnated with the thermo-hardening resin
including the friction conditioner and therefore, three properties
of the .mu.-V characteristic, the wear resistance between layers
(shear strength) and the heat resistance can simultaneously be
promoted. Further, along with cooling performance of the nonwoven
cloth itself, a wear resistance to a counter member is also
promoted.
[0018] Further, the distribution rate of the friction conditioner
is made to be high at the friction surface and is gradually lowered
toward the bottom surface and therefore, also the heat resistance
is promoted by sufficiently ensuring pores and an effect of using
the nonwoven cloth can further be promoted.
BEST MODE FOR CARRYING OUT THE INVENTION
[0019] The present invention is a wet type friction member
constituted by impregnating a thermo-hardening resin including a
friction conditioner to nonwoven cloth including one kind or more
of other fibers based on aramide fiber and a manufacturing method
for the same. Further, the friction conditioner is included by a
large amount at a friction surface of the friction member and the
amount is reduced gradually toward a bottom surface.
Embodiment 1
[0020] A wet type friction member of the present invention is
constituted by nonwoven cloth based on 20 through 80% of aramide
fiber and comprising at least one of 0 through 50 weight % of
carbon fiber, 0 through 50 weight % of carbonized fiber, 0 through
50 weight % of cellulose fiber and 0 through 50% of rayon and the
like (aramide fiber is necessarily included and therefore, two
kinds of more of fibers when aramide fiber is added), with regard
to the nonwoven cloth, the friction member is impregnated with a
thermo-hardening resin of 30 through 100 weight % relative to a
weight of the nonwoven cloth and a friction conditioner of 1
through 15 weight % relative to the thermo-hardening resin,
further, the porosity is set to 35 through 65%.
[0021] Further, although the carbon fiber is constituted only by
carbon, the carbonized fiber indicates to include a compound of
carbon.
[0022] As the thermo-hardening resin, phenol resin, denatured
phenol resin reformed by oil, rubber, epoxy resin or the like,
melanin resin, epoxy resin, polyimide resin, unsaturated polyester
resin or the like is conceived. Also, as the friction conditioner,
an inorganic powder-like substance of diatom earth, graphite,
activated carbon, molybdenum disulphide, silica powder or the like
and an organic powder-like substance of cashew dust, fluorine resin
powder, spherical phenol resin cured powder or the like is
adaptable.
[0023] Although various methods of impregnating the
thermo-hardening resin including the friction conditioner to the
nonwoven cloth are conceivable, three kinds of the methods are
shown as embodiments in FIG. 3 through FIG. 5.
[0024] According to the method shown in FIG. 3, a thermo-hardening
resin 40 including a friction conditioner is supplied onto the
nonwoven cloth 30 to pass between rolls 51, 51 and the
thermo-hardening resin 40 including the friction conditioner is
impregnated into the nonwoven cloth 30 by pressing the
thermo-hardening resin 40. An arrow mark R indicates a direction of
advancing the nonwoven cloth.
[0025] The method shown in FIG. 4 is provided with an ultrasonic
wave transmitter 52 and the thermo-hardening resin 40 including the
friction conditioner is impregnated into the nonwoven cloth 30 by
ultrasonic vibration.
[0026] The method shown in FIG. 5 is installed with a vacuuming
apparatus 53 on a lower side of the nonwoven cloth 30 and the
thermo-hardening resin 40 is impregnated into the nonwoven cloth by
sucking the thermo-hardening resin 40 including the friction
conditioner from a lower side.
[0027] FIG. 6 shows an image of a distribution of the friction
conditioner in the nonwoven cloth 30. Notation A designates a
friction surface side of the friction member 25. Notation B
designates a bottom surface side on a side opposed thereto (side
adhered to the core plate). Numeral 41 designates a friction
conditioner included in the friction member (i.e., in the nonwoven
cloth). A thickness of the friction member is designated by
notation H, and a surface layer 31, a middle layer 32, and a bottom
layer 33 are defined by depths of thirds of the thickness H.
[0028] Although the thermo-hardening resin is uniformly impregnated
in nonwoven cloth, since the thermo-hardening resin including the
friction conditioner is impregnated, a large amount of the friction
conditioner stays at the surface layer and is not considerably
brought into the bottom layer. Such a property is utilized for the
present invention.
[0029] The surface layer includes 50 through 80 weight % of the
friction conditioner, the middle layer includes 20 through 50
weight % thereof, and the bottom layer includes 0 through 20 weight
% thereof. By constituting in this way, the .mu.-V characteristic
between the friction coefficient .mu. and the sliding speed V is
improved to particularly achieve the positive gradient property in
which when V is increased and also .mu. is increased. When the
.mu.-V characteristic is of the positive gradient property, there
is achieved an effect that judder is not brought about.
[0030] A large amount of the friction conditioner is blended at the
portion of the surface layer 31 so as to achieve a sufficient
friction force and obtain the positive gradient property of the
.mu.-V characteristic. Further, a small amount of the friction
conditioner is blended at the bottom layer 33 to promote heat
resistance by sufficiently ensuring pores.
* * * * *