U.S. patent application number 11/057567 was filed with the patent office on 2005-07-07 for method and apparatus for forming and heat treating structural assemblies.
This patent application is currently assigned to The Boeing Company. Invention is credited to Coleman, Gary W., Fischer, John R., Matsen, Marc R., Mull, Elizabeth M., Nansen, David S..
Application Number | 20050145309 11/057567 |
Document ID | / |
Family ID | 32093368 |
Filed Date | 2005-07-07 |
United States Patent
Application |
20050145309 |
Kind Code |
A1 |
Coleman, Gary W. ; et
al. |
July 7, 2005 |
Method and apparatus for forming and heat treating structural
assemblies
Abstract
There are provided an apparatus and an associated method for
manufacturing superplastically formed structural assemblies from
preforms. The apparatus includes first and second co-operable dies
structured to define a die cavity therebetween for at least
partially receiving the preform, at least one heater in thermal
communication with the die cavity for heating the preform to a
forming temperature, and at least one injector in fluid
communication with the die cavity. The injector is structured for
injecting pressurized gas into the die cavity to urge the preform
against one of the dies to form the preform into the structural
assembly. Further, at least one of the injectors is structured for
injecting a quenchant into the die cavity to thereby heat treat the
structural assembly while distortion of the structural assembly is
being at least partially restrained by at least one of the
dies.
Inventors: |
Coleman, Gary W.;
(Snohomish, WA) ; Fischer, John R.; (Winthrop,
WA) ; Matsen, Marc R.; (Seattle, WA) ; Mull,
Elizabeth M.; (Seattle, WA) ; Nansen, David S.;
(Bellevue, WA) |
Correspondence
Address: |
ALSTON & BIRD LLP
BANK OF AMERICA PLAZA
101 SOUTH TRYON STREET, SUITE 4000
CHARLOTTE
NC
28280-4000
US
|
Assignee: |
The Boeing Company
|
Family ID: |
32093368 |
Appl. No.: |
11/057567 |
Filed: |
February 14, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11057567 |
Feb 14, 2005 |
|
|
|
10277903 |
Oct 22, 2002 |
|
|
|
6884966 |
|
|
|
|
Current U.S.
Class: |
148/654 |
Current CPC
Class: |
B21D 26/055 20130101;
B29C 51/10 20130101; B29C 51/12 20130101; B29C 35/04 20130101; B29C
2791/007 20130101; B29C 51/424 20130101; B29C 51/14 20130101; B29C
51/42 20130101 |
Class at
Publication: |
148/654 |
International
Class: |
B21J 001/06 |
Claims
1. An apparatus for forming a structural assembly from at least one
preform, comprising: first and second co-operable dies structured
to define a die cavity therebetween for at least partially
receiving the at least one preform; at least one heater in thermal
communication with said die cavity for heating the at least one
preform to a forming temperature; and at least one injector in
fluid communication with said die cavity, wherein at least one of
said at least one injector is structured for injecting pressurized
gas into said die cavity to urge the at least one preform at least
partially against at least one of said first and second dies to
thereby form the at least one preform into the structural assembly,
and wherein at least one of said at least one injector is
structured for injecting a quenchant into said die cavity to
thereby heat treat the structural assembly while distortion of the
structural assembly is being at least partially restrained by at
least one of said first and second dies.
2. An apparatus according to claim 1 wherein said at least one
injector for injecting a quenchant comprises a tubular member
comprising a plurality of nozzles structured to spray said
quenchant onto the structural assembly.
3. An apparatus according to claim 1 further comprising a valve in
fluid communication with said die cavity, said valve being
structured to maintain the pressure within said die cavity below a
predetermined pressure; and wherein said at least one injector for
injecting a quenchant comprises a tubular member defining a
plurality of apertures in fluid communication with said valve.
4. An apparatus according to claim 1, further comprising at least
one drain connected to said die cavity for conveying fluid from
said die cavity.
5. An apparatus according to claim 1 further comprising a sealing
frame having first and second portions, said first portion of said
sealing frame being attached to said first die, said second portion
of said sealing frame being attached to said second die, and
wherein said first and second portions of said sealing frame are
structured to at least partially engage the at least one preform so
as to seal said die cavity.
6. An apparatus according to claim 5 wherein said at least one
injector for injecting a quenchant is sealably attached to at least
one of said first and second portions of said sealing frame.
7. An apparatus according to claim 1 further comprising at least
one susceptor and wherein said at least one heater comprises at
least one induction coil structured to induce an electromagnetic
field within at least a portion of said at least one susceptor.
8. An apparatus according to claim 7 wherein said at least one
susceptor has a Curie temperature at which said at least one
susceptor becomes paramagnetic.
9. An apparatus according to claim 8 wherein the Curie temperature
of said at least one susceptor is about equal to the forming
temperature of the at least one preform.
10. An apparatus according to claim 1 wherein at least one of said
first and second dies comprises at least one sensor for measuring
at least one of the temperature and pressure inside said die
cavity.
11. An apparatus for forming a structural assembly from at least
one preform, comprising: first and second co-operable dies
structured to define a die cavity therebetween for at least
partially receiving the at least one preform, at least one of said
first and second dies defining a forming surface for shaping the at
least one preform into the structural assembly; at least one heater
in thermal communication with said die cavity for heating the at
least one preform to a forming temperature; and at least one
injector in fluid communication with said die cavity, wherein at
least one of said at least one injector is structured for injecting
pressurized gas into said die cavity to pressurize said die cavity
and to urge the at least one preform at least partially against
said forming surface of at least one of said first and second dies
to form the at least one preform into the structural assembly, and
wherein at least one of said at least one injector is structured
for injecting a quenchant into said die cavity to thereby heat
treat the structural assembly while the structural assembly is
being urged at least partially against said forming surface of at
least one of said first and second dies to thereby reduce
distortion of the structural assembly.
12. An apparatus according to claim 11 wherein said at least one
injector for injecting a quenchant comprises a tubular member
comprising a plurality of nozzles structured to spray said
quenchant onto the structural assembly.
13. An apparatus according to claim 11 further comprising a valve
in fluid communication with said die cavity, said valve being
structured to maintain the pressure within said die cavity below a
predetermined pressure; and wherein said at least one injector for
injecting a quenchant comprises a tubular member defining a
plurality of apertures in fluid communication with said valve.
14. An apparatus according to claim 11 wherein at least one of said
first and second dies defines at least one aperture in fluid
communication with said die cavity, said aperture being structured
to drain said quenchant from said die cavity.
15. An apparatus according to claim 11 further comprising a sealing
frame having first and second portions, said first portion being
attached to said first die, said second portion being attached to
said second die, and wherein said first and second portions of said
sealing frame are structured to at least partially engage the at
least one preform so as to seal said die cavity.
16. An apparatus according to claim 15 wherein said at least one
injector for injecting a quenchant is sealably attached to at least
one of said first and second portions of said sealing frame.
17. An apparatus according to claim 11 further comprising at least
one susceptor and wherein said at least one heater comprises at
least one induction coil structured to induce an electromagnetic
field within at least a portion of said susceptor.
18. An apparatus according to claim 17 wherein said at least one
susceptor has a Curie temperature at which said at least one
susceptor becomes paramagnetic.
19. An apparatus according to claim 18 wherein the Curie
temperature of said at least one susceptor is about equal to the
forming temperature of the at least one preform.
20. An apparatus according to claim 11 wherein at least one of said
first and second dies comprises at least one sensor for measuring
at least one of the temperature and pressure inside said die
cavity.
21. A method of manufacturing a structural assembly, comprising:
forming at least one preform against at least one of first and
second dies to form the preform into the structural assembly; and
aging the structural assembly according to a predetermined aging
schedule and concurrently at least partially restraining distortion
of the structural assembly using at least one of the first and
second co-operable dies.
22. A method according to claim 21 wherein said forming step
comprises heating the at least one preform to a forming temperature
and injecting pressurized gas at least partially against the at
least one preform so as to urge the at least one preform at least
partially against at least one of the first and second dies to
thereby form the structural assembly.
23. A method according to claim 22 wherein said heating step
comprises energizing at least one induction coil to induce an
electromagnetic field in at least one susceptor.
24. A method according to claim 23 wherein said heating step
comprises heating the at least one susceptor to the Curie
temperature of the at least one susceptor.
25. A method according to claim 21 wherein said aging step
comprises heating the structural assembly according to a
predetermined temperature schedule by energizing at least one
induction coil to induce an electromagnetic field in at least one
susceptor.
26. A product obtained by the method of claim 21.
27. A product according to claim 26 wherein the structural assembly
is formed of at least one of the group consisting of aluminum and
aluminum alloys.
28-40. (canceled)
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to structural assemblies and,
more particularly, relates to an apparatus and associated method
for forming and heating treating structural assemblies.
[0003] 2. Description of Related Art
[0004] Superplastic forming ("SPF") is a process used to form
structural assemblies having complex three-dimensional shapes, such
as the two- and three-sheet assemblies 11, 12 illustrated in FIGS.
1A and 1B, respectively. These assemblies are formed from plastics,
metals and metal alloys, including aluminum, titanium, and alloys
thereof, that exhibit superplastic behavior at certain
temperatures, i.e., large elongations (up to 2,000 percent).
[0005] During the SPF process, an "SPF pack" (also referred to
herein as a "preform") is formed of a single sheet or two or more
stacked sheets of material. The SPF pack is placed into a shaping
die and heated to a sufficiently high temperature within the
superplasticity range of the material to soften the sheet or sheets
of material. Pressurized heated gas is then injected against and/or
into the SPF pack, causing the pack to inflate and fill the die,
thereby forming a structural assembly. Once inflated, the portions
of any sheets of material that are in contact with an adjacent
sheet of material will join through brazing or diffusion bonding.
The structural assembly is then cooled and removed from the die and
final machining steps are performed, such as edge trimming, to form
the finished structural assembly. Advantageously, the SPF process
can be used to form structural assemblies that can satisfy narrow
shape and tolerance requirements without substantial additional
machining. Such combined cycles for forming are described in U.S.
Pat. No. 5,410,132 entitled "Superplastic Forming Using Induction
Heating," which issued on Apr. 25, 1995; U.S. Pat. No. 5,420,400
entitled "Combined Inductive Heating Cycle for Sequential Forming
the Brazing," which issued on May 30, 1995; U.S. Pat. No. 5,700,995
entitled "Superplastically Formed Part," which issued on Dec. 23,
1997; U.S. Pat. No. 5,705,794 entitled "Combined Heating Cycles to
Improve Efficiency in Inductive Heating Operations," which issued
on Jan. 6, 1998; U.S. Pat. No. 5,914,064 entitled "Combined Cycle
for Forming and Annealing" which issued on Jun. 22, 1999; and U.S.
Pat. No. 6,337,471 entitled "Combined Superplastic Forming and
Adhesive Bonding" which issued on Jan. 8, 2002, each of which is
assigned to the assignee of the present invention and is
incorporated herein by reference.
[0006] For some materials, the high temperatures of the SPF process
reduce the material properties, such as strength, toughness, and
corrosion resistance, of the material. Thus, a subsequent heat
treating process may be required after the structural assembly has
been superplastically formed in order to restore these material
properties. For example, structural assemblies formed of aluminum
alloys often require heat treatment, such as quenching, after
superplastic forming to restore the strength and toughness of the
material. Undesirably, temperature gradients in the structural
assembly during the heat treating process can result in shape and
dimensional distortion of the assembly, which can require further
machining and/or forming operations to bring the assembly back into
compliance with the required shape and dimensional tolerances.
These additional machining and forming operations can be time and
labor intensive, which can adversely affect the overall cost of the
finished assembly.
[0007] Thus, there exists a need for an apparatus and associated
method for producing complex structural assemblies that exhibit
high material properties, including high strength, toughness, and
corrosion resistance, and that can consistently satisfy narrow
shape and dimensional tolerances, as are typically required in the
aerospace and automotive industries. The apparatus must be cost
effective, and should be easily adaptable to variations in the
configurations of the structural assembly.
SUMMARY OF THE INVENTION
[0008] The present invention provides an apparatus for forming a
structural assembly from at least one preform. The apparatus
includes first and second co-operable dies structured to define a
die cavity therebetween for at least partially receiving the at
least one preform, at least one heater in thermal communication
with said die cavity for heating the at least one preform to a
forming temperature, and at least one injector in fluid
communication with said die cavity. At least one of the injectors
is structured for injecting pressurized gas into the die cavity to
urge the at least one preform at least partially against at least
one of the first and second dies to thereby form the preform into
the structural assembly. Further, at least one of the injectors is
structured for injecting a quenchant into the die cavity to thereby
heat treat the structural assembly while distortion of the
structural assembly is being at least partially restrained by at
least one of the dies. According to one embodiment of the
invention, each injector includes a tubular member with a plurality
of nozzles that are structured to spray the quenchant onto the
structural assembly. The apparatus can also include a valve in
fluid communication with the die cavity and structured to maintain
the pressure within the die cavity below a predetermined pressure,
wherein the tubular members define a plurality of apertures in
fluid communication with the valve. At least one of the first and
second dies can include at least one drain connected to the cavity
for conveying fluid from the cavity as a result of gravity or
pressure inside the die cavity. The apparatus can also include a
sealing frame. The sealing frame has first and second portions
attached to the first and second dies, respectively, and structured
to at least partially engage the preform to seal the die cavity.
Each injector can also be sealably attached to either or both
portions of the sealing frame. In another embodiment, the apparatus
includes at least one susceptor, and the heater includes an
induction coil that is structured to induce an electromagnetic
field within at least a portion of the susceptor. The susceptor can
have a Curie temperature at which the susceptor becomes
paramagnetic, and the Curie temperature can be about equal to the
forming temperature of the preform. The dies can include at least
one sensor for measuring the temperature and/or pressure inside the
die cavity.
[0009] The present invention also provides another apparatus for
forming a structural assembly from at least one preform. The
apparatus includes first and second co-operable dies structured to
define a die cavity therebetween for at least partially receiving
the at least one preform. At least one of the dies defines a
forming surface for shaping the preform into the structural
assembly. The apparatus also includes at least one heater in
thermal communication with the die cavity for heating the preform
to a forming temperature and at least one injector in fluid
communication with the die cavity. At least one of the injectors is
structured for injecting pressurized gas into the die cavity to
pressurize the die cavity and to urge the preform at least
partially against the forming surface to form the preform into the
structural assembly. Further, at least one of the injectors is
structured for injecting a quenching fluid into the die cavity to
thereby heat treat the structural assembly while the structural
assembly is being urged against the forming surface to thereby
reduce distortion of the structural assembly. According to one
embodiment of the invention, each injector includes a tubular
member with a plurality of nozzles that are structured to spray the
quenchant onto the structural assembly. The apparatus can also
include a valve in fluid communication with the die cavity and
structured to maintain the pressure within the die cavity below a
predetermined pressure, wherein the tubular members define a
plurality of apertures in fluid communication with the valve. At
least one of the first and second dies can define at least one
aperture in fluid communication with the die cavity and structured
to drain the quenchant therefrom as a result of gravity or pressure
inside the die cavity. The apparatus can also include a sealing
frame. The sealing frame has first and second portions attached to
the first and second dies, respectively, and structured to at least
partially engage the preform to seal the die cavity. Each injector
can also be sealably attached to the either or both portions of the
sealing frame. In another embodiment, the apparatus includes at
least one susceptor, and the heater includes an induction coil that
is structured to induce an electromagnetic field within at least a
portion of the susceptor. The susceptor can have a Curie
temperature at which the susceptor becomes paramagnetic, and the
Curie temperature can be about equal to the forming temperature of
the preform. The dies can include at least one sensor for measuring
the temperature and/or pressure inside the die cavity.
[0010] The present invention also provides a method of
manufacturing a structural assembly and a structural assembly
obtained thereby. The method includes providing at least one
preform, for example, by at least partially friction stir welding
the preform. The preform is positioned between first and second
co-operable dies and formed into the structural assembly using at
least one of the first and second dies, for example, by heating the
preform and injecting pressurized gas to urge the preform at least
partially against one or both of the dies. The preform can be
heated by energizing an induction coil to induce an electromagnetic
field in at least one susceptor, for example, to the Curie
temperature of the susceptor. In one embodiment, coolant is
circulated through the at least one induction coil. The preform can
also be solution heat treated.
[0011] According to one aspect, the structural assembly is quenched
with a quenchant. Distortion of the structural assembly is reduced
by at least partially constraining the structural assembly
concurrently with the quenching step using at least one of first
and second co-operable dies. In another embodiment, quenching
includes injecting the quenchant through a plurality of nozzles of
an injector onto the structural assembly. The structural assembly
can be cooled by quenching to a second temperature less than about
300.degree. F. and at a rate of at least 100.degree. F. per
second.
[0012] After forming, and in addition to or instead of quenching,
the structural assembly can be aged by heating the structural
assembly according to a predetermined temperature schedule within
the dies. For example, the structural assembly can be heated by
energizing the induction coil to induce an electromagnetic field in
the susceptor. Concurrently, the dies can be used to restrain
distortion of the structural assembly.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] The foregoing and other advantages and features of the
invention, and the manner in which the same are accomplished, will
become more readily apparent upon consideration of the following
detail description of the invention taken in conjunction with the
accompanying drawings, which illustrate preferred and exemplary
embodiments and which are not necessarily drawn to scale,
wherein:
[0014] FIG. 1A is a fragmentary perspective view illustrating a
two-sheet superplastically formed structural assembly, as is known
in the art;
[0015] FIG. 1B is a fragmentary perspective view illustrating a
three-sheet superplastically formed structural assembly, as is
known in the art;
[0016] FIG. 2A is an elevation view illustrating the forming
apparatus for superplastically forming a structural assembly,
according to one embodiment of the present invention;
[0017] FIG. 2B is a plan view illustrating the forming apparatus
for superplastically forming a structural assembly, according to
another embodiment of the present invention;
[0018] FIG. 2C is a section view illustrating the forming apparatus
of FIG. 2B as seen along line 2C-2C of FIG. 2B;
[0019] FIG. 2D is a section view illustrating the forming apparatus
of FIG. 2B as seen along line 2D-2D of FIG. 2B;
[0020] FIG. 2E is a fragmentary perspective view illustrating a
die, according to one embodiment of the present invention;
[0021] FIG. 3A is a section view illustrating a forming apparatus,
according to another embodiment of the present invention;
[0022] FIG. 3B is a fragmentary elevation view illustrating an
injector for supplying quenchant to the die cavity, according to
one embodiment of the present invention;
[0023] FIG. 4A is a section view illustrating the forming apparatus
of FIG. 2B as seen along line 4A-4A of FIG. 2B;
[0024] FIG. 4B is a section view illustrating the first and second
portions of the sealing frame, according to one embodiment of the
present invention;
[0025] FIG. 5 is a perspective view illustrating a preform that can
be superplastically formed to manufacture a structural assembly
according to one embodiment of the present invention;
[0026] FIG. 6 is a perspective view illustrating a structural
assembly that has been superplastically formed from the preform of
FIG. 5;
[0027] FIG. 7 is a perspective view illustrating another preform
that can be superplastically formed to manufacture a structural
assembly according to another embodiment of the present
invention;
[0028] FIG. 8 is a perspective view illustrating a structural
assembly that has been superplastically formed from the preform of
FIG. 7;
[0029] FIG. 9A is an elevation view illustrating a susceptor having
an induced electromagnetic field, according to one embodiment of
the present invention;
[0030] FIG. 9B is an elevation view illustrating the susceptor of
FIG. 9A wherein a portion of the susceptor has reached its Curie
temperature and become paramagnetic;
[0031] FIG. 10 is a forming profile for aluminum alloys,
illustrating the temperature and pressure within the die cavity
during the forming processes, according to one embodiment of the
present invention;
[0032] FIG. 10A is an aging profile for aluminum alloys,
illustrating the temperature and pressure within the die cavity
during the aging processes, according to one embodiment of the
present invention;
[0033] FIG. 111 is a flow chart illustrating the operations
performed in manufacturing a structural assembly according to one
embodiment of the present invention; and
[0034] FIG. 12 is a flow chart illustrating the operations
performed in manufacturing a structural assembly according to
another embodiment of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0035] The present invention now will be described more fully
hereinafter with reference to the accompanying drawings, in which
some, but not all embodiments of the invention are shown. This
invention may be embodied in many different forms and should not be
construed as limited to the embodiments set forth herein; rather,
these embodiments are provided so that this disclosure will be
thorough and complete, and will fully convey the scope of the
invention to those skilled in the art. Like numbers refer to like
elements throughout.
[0036] Referring now to the drawings, and in particular to FIG. 2A,
there is illustrated a forming apparatus 10, according to one
embodiment of the present invention. The forming apparatus 10
includes first and second dies 20, 22, which are mounted on first
and second strongbacks 34, 36 respectively, that are secured using
a mechanical support structure comprising a base 18a and a pair of
lateral members 18b. A "strongback" is a stiff metallic plate that
acts as a mechanical constraint to keep the first and second dies
20, 22 together to thereby maintain the dimensional accuracy of the
structural assembly being formed. The first and second dies 20, 22
are co-operable and configured to define a die cavity 28
therebetween structured to at least partially receive and form at
least one SPF pack or preform 14, such as the one illustrated in
FIG. 5, into a structural assembly 16, such as the one shown in
FIG. 6. As illustrated in FIG. 2C, at least one of the first and
second dies 20, 22 includes a forming surface 24, which defines a
predetermined configuration structured to shape the preform 14 so
that the preform 14 is superplastically formed into a structural
assembly 16 having the desired configuration. As illustrated in
FIG. 3A, both the first and second dies 20, 22 can include a
respective forming surface 24a, b.
[0037] The first and second dies 20, 22 preferably are formed of a
material having a low thermal expansion, high thermal insulation,
and a low electromagnetic absorption. According to one embodiment
of the present invention, the dies 20, 22 are formed of cast
ceramic, for example, using a castable fusible silica product such
as Castable 120 available from Ceradyne Thermo Materials of
Scottdale, Ga. Castable 120 has a coefficient of thermal expansion
less than about 0.45/(.degree. F..times.106), a thermal
conductivity of about 4.3 Btu/(hr)(ft.sup.2)(.degree. F./in), and a
low electromagnetic absorption. The low thermal expansion of the
dies 20, 22 allows the dies 20, 22 to support large thermal
gradients without developing high stress gradients which can result
in spalling.
[0038] The dies 20, 22 are contained, at least partially within a
phenolic structure 30, which can be reinforced with fibers and/or
fiberglass reinforcing rods 32. The rods 32 can extend both
longitudinally and transversely through the phenolic structure 30
and the first and second dies 20, 22, as illustrated in FIGS. 2A
and 2C. To provide a post-stressed compressive state to the first
and second dies 20, 22, the rods 32 preferably are placed through
the phenolic structure 30 and secured within the first and second
dies 20, 22 at the time of casting. Thereafter, nuts 33 at the ends
of the rods 32 can be tightened to provide the post stressed
compressive state to prevent cracking or other damage to the dies
20, 22. The first and second dies 20, 22, the phenolic structure
30, and the reinforcement rods 32 are described in U.S. Pat. No.
5,683,608 entitled "Ceramic Die for Induction Heating Work Cells,"
which issued on Nov. 4, 1997, and which is assigned to the assignee
of the present invention and is incorporated herein by
reference.
[0039] As illustrated in FIGS. 4A and 4B, the forming apparatus 10
includes a sealing frame 40, which extends along the perimeter of
the die cavity 28 and seals the die cavity. As illustrated in FIG.
4B, the sealing frame 40 includes a first portion 42 secured to the
first die 20 and a second portion 44 secured to the second die 22.
The first and second portions 42, 44 of the sealing frame 40 are
contoured so as to engage the peripheral edge of the preform 14 to
provide a hermetic seal with the preform 14. The first and second
portions 42, 44 of the sealing frame 40 are urged into contact with
the preform 14 by closing the dies 20, 22 so that the first and
second portions 42, 44 are pressed firmly against the preform 14.
At least the periphery of the preform 14 can be heated prior to
being positioned within the die cavity 28 so that the preform 14
more easily conforms to the first and second portions 42, 44 of the
sealing frame 40. As illustrated in FIG. 4A, the forming apparatus
10 also can include an elastomeric seal 48 positioned between the
dies 20, 22 that prevents the release of gas or fluids from the die
cavity 28.
[0040] As illustrated in FIGS. 2C, 2D, and 3A, at least one of the
first and second dies 20, 22, includes a heater 64 for heating the
preform 14 to a forming temperature. The heater 64 can comprise any
known heating device including, for example, a gas or electric
oven. According to one embodiment, at least one of the first and
second dies 20, 22 includes at least one susceptor 70, as described
more fully below, and the heater 64 comprises at least one
induction coil 50, such as a solenoid coil, for inducing an
electromagnetic field in the susceptor. Each induction coil 50
includes a plurality of elongate tube sections 52 that are
interconnected by curved tube sections 54 to form a coil that is
positioned proximate to the die cavity 28 and the corresponding
susceptor 70 in which the electromagnetic field is to be induced.
In one embodiment, the tube sections 52 are formed of 1.0 inch
diameter copper tubing with a 0.0625 inch wall thickness. Lightly
drawn copper tubing can be used so that the tube sections 52 can be
adjusted as necessary to correspond to the configuration of the
corresponding die 20, 22. Each curved tube section 54, which can be
formed of a flexible, non-conductive material such as plastic,
preferably connects tube sections 52 that are disposed within only
one of the two dies 20, 22 so that the dies 20, 22 can be opened to
expose the die cavity 28 without disconnecting the tube sections 52
connected by the respective curved tube section 54. The tube
sections 52 of the two dies 20, 22 can also be electrically
connected by pin connections 55, as shown in FIG. 4A, which can be
disconnected when the dies 20, 22 are opened to expose the die
cavity 28. The pin connections 55 are preferably formed of a
conductive material such as brass or copper.
[0041] The induction coil 50 is capable of being energized by one
or more power supplies 56. Preferably, the power supplies 56
provide an alternating current to the induction coil 50, e.g.,
between about 3 and 10 kHz. As illustrated in FIG. 9A, this
alternating current through the induction coil 50 induces an
electromagnetic field within the susceptor 70 that heats the
susceptor and, thus, the preform 14 and the structural assembly 16.
The temperature of the susceptor 70 and the preform 14 can be
determined by monitoring the power supplied by the one or more
power supplies 56, as described in U.S. application Ser. No.
10/094,494, entitled "Induction Heating Process Control," filed
Mar. 8, 2002, and which is assigned to the assignee of the present
invention and is incorporated herein by reference.
[0042] Due to the low electromagnetic absorption of the dies 20,
22, the induction coil 50 induces an electromagnetic field within
the susceptor 70 without inducing an appreciable electromagnetic
field in the dies 20, 22. Therefore, the susceptor 70 can be heated
to high temperatures without heating the dies 20, 22, thereby
saving energy and time. Additionally, the low thermal conductivity
of the ceramic dies 20, 22 reduces heat loss from the die cavity 28
and, thus, the preform 14 and/or structural assembly 16.
[0043] As illustrated in FIG. 2E, the induction coil 50 preferably
defines a passage 58 for circulating a cooling fluid, such as
water, from a coolant source 60. A pump (not shown) circulates the
cooling fluid from the coolant source 60 through the passage 58.
The cooling fluid cools the induction coil 50 to prevent the coil
from overheating. In addition, because the induction coil 50
preferably is uniformly positioned relative to the susceptor 70,
the induction coil will not only uniformly heat the susceptor 70,
but the coolant will transfer heat away from the susceptor 70,
thereby cooling the susceptor 70.
[0044] The at least one susceptor 70 preferably is cast within the
corresponding first and second dies 20, 22. The thickness of the
cast ceramic between the susceptor 70 and forming surface 24 of the
corresponding die 20, 22 can vary, but preferably is about 0.75
inches thick. The susceptor 70 is formed of a material that is
characterized by a Curie temperature at which the susceptor becomes
paramagnetic, for example, a ferromagnetic alloy such as an alloy
comprising iron and nickel. Susceptors having Curie temperatures at
which each susceptor becomes non-magnetic, or paramagnetic, are
described in U.S. Pat. No. 5,728,309 entitled "Method for Achieving
Thermal Uniformity in Induction Processing of Organic Matrix
Composites or Metals," which issued on Mar. 17, 1998; U.S. Pat. No.
5,645,744 entitled "Retort for Achieving Thermal Uniformity in
Induction Processing of Organic Matrix Composites or Metals," which
issued on Jul. 8, 1997; and U.S. Pat. No. 5,808,281 entitled
"Multilayer Susceptors for Achieving Thermal Uniformity in
Induction Processing of Organic Matrix Composites or Metals," which
issued on Sep. 15, 1998, each of which is assigned to the assignee
of the present invention and is incorporated herein by reference.
The susceptor 70 can define a contoured surface and can include an
oxidation resistant nickel aluminide coating, which can be
flame-sprayed or otherwise disposed on the surface of the susceptor
70. A description of a susceptor with a nickel aluminide coating is
provided in U.S. application Ser. No. 10/032,625, entitled "Smart
Susceptors with Oxidation Control," filed Oct. 24, 2001, and which
is assigned to the assignee of the present invention and is
incorporated herein by reference.
[0045] As illustrated in FIGS. 9A and 9B, the susceptor 70 is
heated through eddy current heating to the Curie temperature of the
susceptor 70, whereupon the susceptor 70 becomes paramagnetic and
does not heat further. If some portions of the susceptor 70 are
heated more quickly than other portions, the hotter portions will
reach the Curie temperature and become paramagnetic before the
other, cooler portions of the susceptor 70. As illustrated in FIG.
9B, the eddy currents will then flow through the cooler magnetic
portions, i.e., around the hotter, paramagnetic portions of the
susceptor 70, causing the cooler portions to also become heated to
the Curie temperature. Therefore, even if some portions of the
susceptor 70 heat at different rates, the entire susceptor 70 is
heated to a uniform Curie temperature.
[0046] Eddy current heating of the susceptor 70 results from eddy
currents that are induced in the susceptor by the electromagnetic
field generated by the induction coil 50. The flow of the eddy
currents through the susceptor 70 results in resistive losses and
heating of the susceptor 70. Preferably, the susceptor 70 acts as a
magnetic shield that prevents the induction coil 50 from inducing
an electromagnetic field in the preform 14 and/or structural
assembly 16. As such, the induction coil 50 does not heat the
preform 14 and/or structural assembly 16 directly, but rather heats
the susceptor 70 which, in turn, acts as a heat sink for heating
the preform 14 and/or the structural assembly 16.
[0047] Preferably, the Curie temperature of the susceptor 70 is
equal to a forming temperature of the preform 14, i.e., the
temperature at which the preform 14 becomes superplastically
formable. Thus, the susceptor 70 can be used to heat the preform 14
uniformly to the forming temperature so that the preform 14 can be
formed into a structural assembly 16. The susceptor 70 can be
formed of a variety of materials including cobalt, iron, nickel,
and alloys thereof, and the composition of the susceptor 70 can be
designed to achieve a desired Curie temperature that is appropriate
for a particular type of preform material. For example, susceptors
with Curie temperatures between about 860.degree. F. and
1005.degree. F. can be used for processing preforms that are formed
of aluminum and aluminum alloys. In one embodiment, the susceptor
70 is formed of an alloy comprising 50% iron and 50% nickel. This
iron-nickel alloy has a Curie temperature of about 968.degree. F.,
at which temperature aluminum and certain aluminum alloys can be
superplastically formed. Preferably, the Curie temperature is also
equal to a heat-treatment temperature of the preform material,
e.g., a temperature at which the preform material can be solution
heat treated. For example, aluminum can be solution heat treated at
temperatures between about 860.degree. F. and 1005.degree. F. Thus,
the preform 14 can be held at the forming temperature, e.g.,
968.degree. F., for a predetermined period of time, such as about
30 to 45 minutes for aluminum and aluminum alloys, and thereby
solution heat treated.
[0048] As illustrated in FIG. 2B, the forming apparatus 10
preferably includes injectors 80, 90 for injecting pressurized gas
and quenching fluid into the die cavity 28. Each injector 80, 90
comprises a passage such as a pipe or other tubular member that
extends to, and is fluidly connected to, the die cavity 28. Each
injector 80, 90 can also be sealably attached to the first and/or
second portions 42, 44 of the sealing frame 40 so that the sealing
frame 40 forms a hermetic seal around the injectors 80, 90.
Although separate injectors 80, 90 are provided for injecting the
pressurized gas and the quenching fluid in the illustrated
embodiments, a combination injector (not shown) can alternatively
be provided for injecting both the gas and the fluid.
[0049] The gas injector 80 is fluidly connected to a pressurized
gas source 86 and extends into the die cavity 28. The gas injector
80 defines at least one gas port 83 through which heated
pressurized gas can be injected into the die cavity 28. Thus, the
pressurized gas source 86 is fluidly connected to the die cavity 28
so that pressurized gas from the gas source 86 can be injected into
the die cavity 28 to form the preform 14. A pressure regulator 82,
which is fluidly connected to the pressurized gas source and the
gas injector 80, is configured to control the flow of gas into the
die cavity 28 and thereby regulate the pressure in the die cavity
28 to a preselected pressure. For example, the pressure inside the
die cavity 28 would not exceed about 300 psi when superplastically
forming aluminum and aluminum alloys. One or more apertures 114 can
fluidly connect the die cavity 28 to a condenser 118 for receiving
the pressurized gas from the die cavity 28, and a valve 116 can
regulate the flow of the pressurized gas from the die cavity 28 to
the condenser 118.
[0050] According to one embodiment, as illustrated in FIG. 2C, when
superplastically forming a preform 14, such as a single sheet of
material or a relatively simply multi-sheet forming pack, as
illustrated in FIGS. 5 and 7, the preform 14 is positioned within
the die cavity 28 such that the preform is disposed between the
injector 80 and the forming surface 24 of the corresponding die or
dies 20, 22. As discussed above, the periphery of the preform 14 is
secured using the first and second portions 42, 44 of the sealing
frame 40. In this position, the preform 14 divides the die cavity
28 into two portions or sections 28a, 28b. One portion 28a includes
the injectors 80, 90 and the other portion 28b includes the forming
surface 24. Thus, as gas enters the die cavity 28 from the gas
injector 80, the gas flows into the first portion 28a of the die
cavity 28 and increases the pressure in the first portion 28a so
that it exceeds the pressure in the second portion 28b. The preform
14, which is heated to its superplastic forming temperature, is
urged by the high pressure in the first portion 28a against the
forming surface 24 of the dies 20, 22, thus, superplastically
forming the structural assembly 16. As the preform 14 is urged
toward the forming surface 24, the volume of the first portion 28a
of the die cavity 28 increases and the volume of the second portion
28b of the die cavity decreases. Gas present in the second portion
28b of the die cavity 28 can be released through a gas outlet (not
shown). Alternatively, the gas in the second portion 28b can seep
out of the die cavity 28 through unsealed gaps in the dies 20, 22,
or the gas can be compressed within the second portion 28b of the
die cavity 28.
[0051] Alternatively, the preform 14 can include a multi-sheet
sealed forming pack in which one or more of the edges of the
preform 14 have been welded using fusion or friction stir welding.
A preform 14 comprises multi-sheet seal forming pack formed with
friction stir welding and/or fusion welding is described in U.S.
application Ser. No. 09/818,325 entitled "Application of Friction
Stir Welding to Superplastically Formed Structural Assemblies,"
which was filed on Mar. 27, 2001, and which is assigned to the
assignee of the present invention and is hereby incorporated by
reference. Such preforms 14 typically have internal plumbing (not
shown) which can be connected to the gas port 83 of the injector 80
using suitable fittings, as is well known in the art. Such preforms
are superplastically formed by injecting the heated pressurized gas
through the injector 80 and the gas port 83 and into the plumbing
and interior of the preform to thereby fill the preform and urge it
against the forming surfaces 24 of the first and second dies 20,
22.
[0052] Similarly, the quench injectors 90 are fluidly connected to
a quenching fluid source 98, thus fluidly connecting the quenching
fluid source 98 to the die cavity 28. In the illustrated
embodiments, the quench injectors 90 extend through the die cavity
28, but in other embodiments, each injector 90 can terminate within
the die cavity 28. As shown in FIG. 3B, each quench injector 90
includes a plurality of nozzles 94 that are configured to direct
the quenching fluid in the direction of the forming surface 24,
i.e., toward the structural assembly 16. If the combination
injectors are used, the nozzles 94 can also function as the gas
port 83. The quenching fluid or "quenchant" can comprise a cooling
liquid, including, but not limited to, water, glycol, oils, salt
solutions, and mixtures thereof. The quenching fluid can also
comprise a gas, such as air, or a liquid-gas mixture, i.e., a
2-phase mist of liquid and gas. The forming apparatus 10 can also
provide a quenching reservoir 104 that is fluidly connected to the
injectors 90. A valve 102 is configured to control the flow of the
quenching fluid from the injectors 90 into the reservoir 104, so
that the reservoir 104 can be selectively connected to the
injectors 90. Further, at least one drain reservoir 112 can be
fluidly connected to the die cavity 28 by apertures 110 to receive
the quenching fluid therefrom.
[0053] In operation, the quenching fluid or "quenchant" enters the
die cavity 28 at a temperature that is less than the temperature of
the structural assembly 16 so as to rapidly cool the structural
assembly 16. For example, the quenching fluid can comprise liquid
water at room temperature, i.e., about 70.degree. F. The phase and
temperature of the quenching fluid depends on the material forming
the preform 14 and the desired material properties of the
structural assembly 16. Preferably, the quenching fluid is able to
absorb sufficient heat from the structural assembly 16 so as to
cool the structural assembly 16 at a rate that causes quenching of
the structural assembly 16 and yields the desired material
properties. The rate of cooling of the structural assembly 16 will
depend on a variety of factors, including the forming temperature
of the structural assembly 16, the temperature of quenching fluid,
the heat capacities of the structural assembly 16 and the quenching
fluid, the mass and surface area of the structural assembly 16, and
the rate at which the quenching fluid is sprayed onto the
structural assembly 16. In one embodiment, the structural assembly
16 is quenched so that the temperature of the structural assembly
is reduced at a rate of at least 100.degree. F. per second from a
temperature of about 980.degree. F. to less than about 300.degree.
F. and, more preferably, to less than about 150.degree. F.
[0054] The pressure in the die cavity 28 during quenching can be
regulated by adjusting the valve 102. For example, during
initiation of the quenching process, the quenching fluid may be
rapidly vaporized as the relatively cool fluid contacts the heated
injectors 90, resulting in an increase in pressure in the injectors
90 and the die cavity 28. By opening the valve 102 during the
quenching process, the quenching fluid can be received by the
reservoir 104, and the increase in pressure can be controlled. The
valve 102 can be closed as the flow of quenching fluid becomes
established, the injectors 90 cool, and the pressure in the
injectors 90 stabilizes.
[0055] Preferably, the die cavity 28 is maintained at an elevated
pressure during quenching by the injectors 90 so that the
structural assembly 16 is held securely against the forming surface
24 of the corresponding die or dies 20, 22, thereby constraining,
or at least reducing, deformation of the structural assembly 16
during the quenching process. Thus, pressure inside the structural
assembly 16 presses the structural assembly 16 against the dies 20,
22 during the quenching operation, and the dies 20, 22 constrain
the structural assembly 16 by resisting deformation thereof. As the
quenching fluid is sprayed on the structural assembly 16, gas
and/or quenching fluid can be released from the die cavity 28 so
that the pressure in the die cavity 28 does not exceed a
predetermined maximum. The gas and/or quenching fluid are drained
from the die cavity 28 through the apertures 110 to the drain
reservoir 112. Preferably, the apertures 110 fluidly connect to the
die cavity 28 at the lowest portions of the die cavity 28 so that
gravity draws the quenching fluid through the apertures 110.
Similarly, the gas and/or the vaporized quenching fluid can be
released from the die cavity 28 through the apertures 114 to the
condenser 118. For example, gas injected into the die cavity 28
from the gas source 86 during the forming process can be released
through the apertures 114. Vaporized quenching fluid can condense
in the condenser 118 and be reclaimed, for example, for re-use as
the quenching fluid. Preferably, the apertures 114 are connected to
the condenser 118 via a valve 116, which can be adjusted to control
the release of the quenching fluid from the die cavity 28.
Alternatively, the gas and the quenching fluid can be released from
one or more common apertures (not shown), which can also be used as
the gas ports 83 and/or the nozzles 94 of the combination injector
for injecting the pressurized gas and the quenching fluid.
[0056] After forming and after or instead of quenching, the
structural assembly 16 can also be aged in the forming apparatus 10
by heating the structural assembly 16 according to a predetermined
temperature schedule, i.e., by heating the structural assembly 16
to an appropriate aging temperature for a predetermined duration.
The aging temperature and duration of aging depend on the material
forming the structural assembly 16 and the desired mechanical
properties, as is well known in the art. The structural assembly 16
can be heated for aging by placing the dies 20, 22 and the
structural assembly 16 in an oven. Alternatively, the induction
coil 50 can reheat the structural assembly 16. If the aging
temperature is different than the forming temperature, the
structural assembly 16 can be transferred to a secondary set of
dies (not shown) containing a second susceptor (not shown) that can
be used to control the temperature of the structural assembly
16.
[0057] The forming apparatus 10 can be used to form structural
assemblies 16 of various configurations from preforms 14 of
different types. For example, the preform 14 and structural
assembly 16 shown in FIGS. 2C and 2D are shown individually in
FIGS. 5 and 6, respectively. The preform 14 is a flat sheet
comprised of aluminum from which flanges 15 extend perpendicularly.
The flanges 15 can be formed, for example, by friction stir welding
the flanges 15 to the flat sheet or by machining a monolithic piece
of stock material. In other embodiments, the preform 14 and, hence,
the structural assembly 16, can be formed of a variety of metals
and metal alloys. However, the preform 14 and structural assembly
16 preferably are formed of a metal or metal alloy having a high
strength to weight ratio, including, for example, aluminum alloys,
titanium, and titanium alloys. In addition, preforms can comprise
built-up structures of multiple sheets, angles, channels, tubes,
other stock shapes, or specially prepared shapes, each of which can
comprise different materials. For example, FIG. 7 illustrates a
preform 14a that comprises a first member 18, which is a flat
sheet, and a second member 19, which is a preformed shape. The
multiple members 18, 19 of the built-up preform 14a can be
assembled using bolts, rivets, crimps, various welded connections,
including weld joints formed of fusion and/or friction stir
welding. The built-up preform 14a is then superplastically formed
as described above to form a structural assembly 16a as shown in
FIG. 8. The structural assembly 16a can define angles, channels,
pockets, and the like and the material characteristics of the
structural assembly 16a, such as thickness and material type, can
vary throughout the structural assembly 16a. Thus, the structural
assembly 16 formed according to the present invention may be formed
in a variety of complex three-dimensional shapes having fine
details and satisfying narrow tolerances, and can be used in a
variety of applications, including the primary or secondary
structure of an aircraft.
[0058] Many variations of the forming apparatus 10 of the present
invention are possible. In this regard, the forming surface 24 of
the forming apparatus 10 can be defined by part or all of the first
die 20 and the second die 22, and the injectors 90 can be directed
toward either or both dies 20, 22. For example, the forming surface
24 of the forming apparatus 10 illustrated in FIGS. 2C and 2D is
defined by only the first die 20. Alternatively, as illustrated in
FIG. 3, the forming surfaces 24 are defined by both the first and
second dies 20, 22. Two preforms 14 are formed in the forming
apparatus by urging each preform 14 against a corresponding one of
the dies 20, 22. The preforms 14 are configured on opposite sides
of the injectors 90 so that the preforms 14 are urged outward
against the dies 20, 22 and quenched by quenching fluid that is
sprayed outward from the injectors 90. Additionally, as described
above, the forming apparatus 10 can also be used to produce
structural assemblies by injecting gas into and expanding a sealed
pack comprising multiple members.
[0059] There is shown in FIG. 10 a forming profile for aluminum
alloys according to one embodiment of the present invention, which
indicates the pressure and temperature variation within the die
cavity 28 during the forming processes. As illustrated, the
temperature of the preform 14 in the die cavity 28 and the pressure
in the die cavity 28 begin at initial conditions, which can be
ambient conditions. The temperature in the die cavity 28 is
increased in a 15 minute time period to 980.degree. F. by
energizing the induction coils 50 and thereby heating the susceptor
70 and, thus, the preform 14. The pressure in the die cavity 28 is
gradually increased to 300 psi by injecting gas through the
injector 80, thereby urging the preform 14 toward the forming
surface 24 of the forming apparatus 10 to superplastically form the
structural assembly 16. Although forming may be accomplished in
less time, the structural assembly 16 is held at the forming
temperature for approximately 30 minutes, thereby effecting a
solution heat treatment of the structural member 16. Approximately
45 minutes after the start of the process, water is injected into
the die cavity 28 through the injectors 90. During the initial flow
of the water into the injectors 90, the valve 102 is open so that
the quenching fluid flows through the injectors 90 and into the
reservoir 104. As the temperature of the injectors 90 decreases,
the valve 102 is closed and the quenching fluid flows through the
nozzles 94 to impinge on the structural assembly 16 and thereby
reduce the temperature of the structural assembly 16 to its initial
temperature at a rate of about 100.degree. F. per second. The
quenching fluid and gas in the die cavity 28 are drained through
the apertures 110, 114 to the reservoir 112 and the condenser 118,
and the pressure in the die cavity 28 is reduced to its initial
condition.
[0060] Similarly, the structural assembly 16 can be aged in the die
cavity 28, for example, after the structural assembly 16 has been
formed or formed and quenched in the die cavity 28. FIG. 10A
illustrates an aging profile for aluminum alloys according to one
embodiment of the present invention, indicating the pressure and
temperature variation within the die cavity 28 during the aging
processes. As illustrated, the temperature of the structural
assembly 16 in the die cavity 28 and the pressure in the die cavity
28 begin at initial conditions, which can be ambient conditions.
The temperature in the die cavity 28 is increased in a 15 minute
time period to 350.degree. F. by energizing the induction coils 50
and thereby heating the susceptor 70 and, thus, the structural
assembly 16. The pressure in the die cavity 28 is increased to 300
psi by injecting gas through the injector 80, thereby maintaining
the structural assembly 16 against the forming surface 24 of the
forming apparatus 10. A nine-hour aging process is illustrated at a
temperature of 350.degree. F. and 300 psi, but other durations,
temperatures, and pressures can also be used. Also, the initial
temperature and pressure can be higher than ambient conditions, for
example, if the die cavity 28 is not cooled or depressurized to
ambient conditions after forming and/or quenching or cooling. Thus,
the structural assembly 16 can be aged after the forming process,
with or without an intervening quenching process. For structural
assemblies 16 formed of aluminum or aluminum alloys, it may be
preferable to age the structural assembly 16 only after quenching
or otherwise cooling the structural assembly 16 at a controlled
rate. Alternatively, for other materials, such as some
aluminum-lithium alloys, no quenching cycle may be necessary
between the forming and aging processes.
[0061] Referring to FIG. 11, there are illustrated the operations
performed in manufacturing a structural assembly according to one
embodiment of the present invention. The method includes providing
at least one preform. See Block 200. According to one embodiment,
the at least one preform is at least partially friction stir
welded. See Block 202. The at least one preform is positioned
between first and second co-operable dies. See Block 204. Next, the
at least one preform is formed into the structural assembly using
at least one of the first and second dies. See Block 206. According
to one embodiment, the at least one preform is heated according to
a first predetermined temperature schedule. See Block 208. Heating
can include energizing at least one induction coil to induce an
electromagnetic field in at least one susceptor. See Block 210. The
at least one susceptor can be heated to the Curie temperature of
the susceptor. See Block 212. According to one embodiment, the at
least one preform is solution heat treated at a second
predetermined temperature schedule. See Block 214. According to
another embodiment, coolant is circulated through the at least one
induction coil. See Block 216. Pressurized gas can also be injected
at least partially against the at least one preform so as to urge
the at least one preform at least partially against at least one of
said first and second dies to thereby form the structural assembly.
See Block 218. The method also includes quenching the structural
assembly with a quenchant. See Block 220. The quenchant can be
injected through a plurality of nozzles of an injector onto the
structural assembly. See Block 222. In one embodiment, quenching
cools the structural assembly to a second temperature less than
about 300.degree. F. See Block 224. In another embodiment,
quenching cools the structural assembly at a rate of at least
100.degree. F. per second. See Block 226. Concurrently with the
quenching step, distortion of the structural assembly is reduced by
at least partially constraining the structural assembly using at
least one of the first and second co-operable dies. See Block 228.
The structural assembly can also be aged according to a third
predetermined temperature schedule. See Block 230.
[0062] Referring now to FIG. 12, there are illustrated the
operations performed in manufacturing a structural assembly
according to another embodiment of the present invention. The
method includes providing a structural assembly at a first
temperature. See Block 300. The structural assembly is quenched
with a quenchant to a second temperature lower than the first
temperature. See Block 302. The quenchant can be injected through a
plurality of nozzles of an injector onto the structural assembly.
See Block 304. In one embodiment of the invention, the structural
assembly is cooled to a second temperature less than about
300.degree. F. See Block 306. In another embodiment, the structural
assembly is cooled at a rate of at least 100.degree. F. per second.
See Block 308. Concurrently with the quenching step, distortion of
the structural assembly is at least partially restrained using at
least one of first and second co-operable dies. See Block 310. The
structural assembly can also be aged according to a predetermined
temperature schedule. See Block 312.
[0063] Many modifications and other embodiments of the invention
will come to mind to one skilled in the art to which this invention
pertains having the benefit of the teachings presented in the
foregoing descriptions and the associated drawings. Therefore, it
is to be understood that the invention is not to be limited to the
specific embodiments disclosed and that modifications and other
embodiments are intended to be included within the scope of the
appended claims. Although specific terms are employed herein, they
are used in a generic and descriptive sense only and not for
purposes of limitation.
* * * * *