U.S. patent application number 11/016992 was filed with the patent office on 2005-05-12 for heat treated profile extruded hook.
This patent application is currently assigned to 3M Innovative Properties Company. Invention is credited to Ausen, Ronald W., Miller, Philip, Seth, Jayshree, Unruh, William C..
Application Number | 20050101926 11/016992 |
Document ID | / |
Family ID | 33313086 |
Filed Date | 2005-05-12 |
United States Patent
Application |
20050101926 |
Kind Code |
A1 |
Ausen, Ronald W. ; et
al. |
May 12, 2005 |
Heat treated profile extruded hook
Abstract
A method for forming a unitary polymeric projection or fastener
comprising a thin, strong flexible backing, and a multiplicity of
thin spaced hook members projecting from the upper surface of the
unitary backing the method generally including extruding a
thermoplastic resin through a die plate which die plate is shaped
to form a base layer and spaced ridges, ribs or hook elements
projecting above a surface of the base layer. When the die forms
the spaced ridges or ribs the cross sectional shape of the hook
members are formed by the die plate while the initial hook member
thickness is formed by transversely cutting the ridges at spaced
locations along their lengths to form discrete cut portions of the
ridges. Subsequently longitudinal stretching of the backing layer
(in the direction of the ridges on the machine direction) separates
these cut portions of the ridges, which cut portion then form
spaced apart hook members. The extruded hook members or cut rib
hook members are then heat treated resulting in shrinkage of at
least a portion of at least the hook head portion thickness by from
5 to 90 percent, preferably 30 to 90 percent.
Inventors: |
Ausen, Ronald W.; (St. Paul,
MN) ; Unruh, William C.; (Inver Grove Heights,
MN) ; Miller, Philip; (Eagan, MN) ; Seth,
Jayshree; (Woodbury, MN) |
Correspondence
Address: |
3M INNOVATIVE PROPERTIES COMPANY
PO BOX 33427
ST. PAUL
MN
55133-3427
US
|
Assignee: |
3M Innovative Properties
Company
|
Family ID: |
33313086 |
Appl. No.: |
11/016992 |
Filed: |
December 20, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11016992 |
Dec 20, 2004 |
|
|
|
10619048 |
Jul 14, 2003 |
|
|
|
10619048 |
Jul 14, 2003 |
|
|
|
10411042 |
Apr 10, 2003 |
|
|
|
10411042 |
Apr 10, 2003 |
|
|
|
10316686 |
Dec 11, 2002 |
|
|
|
10316686 |
Dec 11, 2002 |
|
|
|
10214051 |
Aug 7, 2002 |
|
|
|
10214051 |
Aug 7, 2002 |
|
|
|
10050403 |
Jan 15, 2002 |
|
|
|
Current U.S.
Class: |
604/358 ;
24/442 |
Current CPC
Class: |
B29C 48/08 20190201;
A44B 18/0049 20130101; B29C 48/12 20190201; B29C 48/00 20190201;
A44B 18/0065 20130101; Y10T 24/2792 20150115; Y10T 24/2783
20150115; Y10T 24/27 20150115; A61F 13/625 20130101 |
Class at
Publication: |
604/358 ;
024/442 |
International
Class: |
D01D 005/20 |
Claims
1-69. (canceled)
70. A fastener strip of a resiliently flexible, thermoplastic resin
comprising a base layer having generally parallel upper and lower
major surfaces, with spaced upstanding integral polymeric
projections projecting from the upper surface of said base, wherein
the base layer has a substantially continuous thickness across its
width and wherein at least a first portion of the projections on
the upper surface have a thickness or molecular orientation, less
than at least another second portion of the projections on the same
upper surface.
71. The fastener strip of claim 70 wherein a portion of the
upstanding projections have a molecular orientation of less than 10
percent.
72. The fastener strip of claim 71 wherein a portion of the
upstanding projections have a molecular orientation different than
another portion of the upstanding projection.
73. The fastener strip of claim 70 wherein the projections comprise
hook members having a stem portion and a hook head portion where
the hook members having a height from said upper surface of less
than 5000 .mu.m and each comprising a stem portion attached at one
end to said base, and a head portion at the end of said stem
portion opposite said base, at least the head portions having a
thickness from 50 to 1500 .mu.m, a first direction generally
parallel to the surfaces of said base.
74. A fastener strip according to claim 73 wherein said stem
portion has a width in the range of 50 to 500 .mu.m in a second
direction generally at a right angle to said first direction and
parallel to the surfaces of said backing; said head portion having
a width greater than said stem portion and a total width of from
100 to 5000 .mu.m in said second direction.
75. The fastener strip according to claim 74 wherein the hook
members are provided at a density of at least 10 per square
centimeter.
76. A fastener strip according to claim 72 wherein a portion of the
upstanding projections have a molecular orientation of from 20 to
100 percent.
77. A diaper having a fastener strip of claim 70.
78. A disposable absorbent article comprising a fastener tab or
patch formed of a thermoplastic resin comprising a base layer
having generally parallel upper and lower major surfaces, with
spaced upstanding integral polymeric projections projecting from
the upper surface of said base, wherein the base layer has a
substantially continuous thickness across its width and a degree of
molecular orientation in more than one direction and wherein said
upstanding polymeric projections have a density of less than 150
projections per square centimeter and the fastener tab or patch has
a base layer thickness of less than 75 microns and an area of 10 cm
or greater.
79. A disposable absorbent article comprising a fastener tab or
patch wherein the polymeric projections have a density of less than
60/cm.sup.2.
80. A disposable absorbent article comprising a fastener tab or
patch wherein the polymeric projections have a density of less than
50/cm.sup.2.
81. A disposable absorbent article comprising a fastener tab or
patch wherein the polymeric projections have a density of less than
150/cm.sup.2 wherein the fastener tab has an area of from 20
cm.sup.2 to 100 cm.sup.2 and the disposable absorbent article is a
diaper.
82. A disposable absorbent article comprising a fastener tab or
patch wherein the polymeric projections have a density of less than
150/cm.sup.2 wherein the disposable absorbent article is a feminine
hygiene article and the hook fastener is a patch forming all or
part of the liquid impermeable backing attached to the garment.
83. The disposable absorbent article of claim 78 wherein said
fastener tab or patch has said projections having a height from
said upper surface of less than 1000 .mu.m and each comprising a
stem portion attached at one end to said base, and a head portion
at the end of said stem portion opposite said base, at least the
head portions having a thickness of from 50 to 200 .mu.m in a first
direction generally parallel to the surfaces of said base.
84. The disposable absorbent article of claim 83 wherein said stem
portion has a width in the range of 50 to 500 .mu.m in a second
direction generally at a right angle to said first direction and
parallel to the surfaces of said backing; said head portion having
a width greater than said stem portion and a total width of from
100 to 800 .mu.m in said second direction and an arm droop of from
100 to 500 .mu.m.
85. The disposable absorbent article of claim 83 wherein said
polymeric material is a thermoplastic resin and the hook head has
rounded corners.
86. The disposable absorbent article of claim 85 wherein said base
has a generally uniform thickness between said upper and lower
surfaces of between 30 to 200 .mu.m.
87. The disposable absorbent article of claim 86 wherein said
thermoplastic resin comprises polyethylene, polypropylene,
polypropylene-polyethylene copolymers or blends thereof.
88. The disposable absorbent article of claim 83 wherein at least
the hook head portion has a molecular orientation of less than 10
percent.
89. The disposable absorbent article of claim 88 wherein the hook
member base portion adjacent the base has a molecular orientation
of at least 10 percent.
90. The disposable absorbent article of claim 88 wherein the base
film layer has a degree of molecular orientation in at least one
direction.
91. The disposable absorbent article of claim 88 wherein the base
film layer has a degree of molecular orientation in two
directions.
92. The disposable absorbent article of claim 84 wherein the hook
portion thickness is less than a stem portion thickness below the
hook portion.
93. The disposable absorbent article of claim 84 wherein the hook
portion thickness is substantially the same as the stem portion
thickness below the hook portion.
94. The disposable absorbent article of claim 92 wherein the hook
portion has an arm extending past the stem portion the hook portion
arm increasing in thickness from a tip of the hook portion arm to a
portion of the hook portion arm adjacent the stem.
95. A garment comprising a low loft nonwoven surface and a
microhook mechanical fastener for engagement with the low loft
nonwoven material; the microhook mechanical fastener having at
least 50 hooks/cm.sup.2, where the hooks have a height of less than
100 .mu.m and an arm droop of from 50 to 700 .mu.m.
96. The garment of claim 95 wherein the garment is a disposable
garment.
97. The garment of claim 96 wherein the microhook has a density of
from 70 to 150 hooks/cm.
98. The garment of claim 96 wherein the microhook has an arm droop
of from 50 to 500 .mu.m.
99. The garment of claim 96 wherein the microhook has a Gurley
stiffness of from 10 to 2000.
100. The garment of claim 96 wherein the microhook has a Gurley
stiffness of from 10 to 200.
101. The garment of claim 96 wherein the microhook has a backing
with a thickness of from 200 to 1000 .mu.m.
Description
[0001] This is a continuation-in-part of application Ser. No.
10/411,042, filed Apr. 10, 2003, which is a continuation-in-part of
application Ser. No. 10/316,686, filed Dec. 11, 2002 (now
abandoned), which is a continuation-in-part of application Ser. No.
10/214,051, filed Aug. 7, 2002 (now abandoned), which is a
continuation-in-part of application Ser. No. 10/050,403, filed Jan.
15, 2002 (now abandoned), the disclosures of which are incorporated
herein by reference.
BACKGROUND AND SUMMARY
[0002] The present invention concerns molded hook fasteners for use
with hook and loop fasteners.
BACKGROUND OF THE INVENTION
[0003] There are a variety of methods known to form hook materials
for hook and loop fasteners. One of the first manufacturing methods
for forming hooks involved weaving loops of monofilaments into a
fibrous or film backing or the like followed by cutting the
filament loops to form hooks. These monofilament loops were also
heated to form headed structures such as disclosed in U.S. Pat.
Nos. 4,290,174; 3,138,841 or 4,454,183. These woven hooks are
generally durable and work well for repeated uses. However, they
are generally expensive and coarse to the touch.
[0004] For use in disposable garments and the like, it was
generally desirable to provide hooks that were inexpensive and less
abrasive. For these uses and the like, the solution was generally
the use of continuous extrusion methods that simultaneously formed
the backing and the hook elements, or precursors to the hook
elements. With direct extrusion molding formation of the hook
elements, see for example U.S. Pat. No. 5,315,740, the hook
elements must continuously taper from the backing to the hook tip
to allow the hook elements to be pulled from the molding surface.
This generally inherently limits the individual hooks to those
capable of engaging only in a single direction while also limiting
the strength of the engaging head portion of the hook element.
[0005] An alternative direct molding process is proposed, for
example, in U.S. Pat. No. 4,894,060, which permits the formation of
hook elements without these limitations. Instead of the hook
elements being formed as a negative of a cavity on a molding
surface, the basic hook cross-section is formed by a profiled
extrusion die. The die simultaneously extrudes the film backing and
rib structures. The individual hook elements are then formed from
the ribs by cutting the ribs transversely followed by stretching
the extruded strip in the direction of the ribs. The backing
elongates but the cut rib sections remain substantially unchanged.
This causes the individual cut sections of the ribs to separate
each from the other in the direction of elongation forming discrete
hook elements. Alternatively, using this same type extrusion
process, sections of the rib structures can be milled out to form
discrete hook elements. With this profile extrusion, the basic hook
cross section or profile is only limited by the die shape and hooks
can be formed that extend in two directions and have hook head
portions that need not taper to allow extraction from a molding
surface. This is extremely advantageous in providing higher
performing and more functionably versatile hook structures.
However, a limitation with this method of manufacture is in forming
hook structures that are extremely narrow in the extrusion
direction of the ribs or the cut direction. Cutting the formed ribs
at very closely spaced intervals is difficult at commercially
acceptable production speeds. Further, when the cut length is
extremely closely spaced the previously cut portions of the ribs
tend to fuse due to the heat created by the cutting operation. As
such, there is a need to improve this process so as to allow for
production of narrower hook profiles and formation of the narrower
hook profiles at commercially acceptable production speeds.
BRIEF DESCRIPTION OF THE INVENTION
[0006] The present invention provides a method for forming
preferably a unitary polymeric hook fastener comprising a thin,
strong flexible backing, and a multiplicity of thin, spaced hook
members projecting from the upper surface of the unitary backing.
The method of the invention generally can be used to form thin
upstanding projections, which may or may not be hook members that
project upwardly from the surface of a unitary film backing of at
least a uniaxially oriented polymer. The hook members each comprise
a stem portion attached at one end to the backing, and a head
portion at the end of the stem portion opposite the backing. The
head portion can also extend from a side of a stem portion or be
omitted entirely to form alternative projections which can be other
forms than a hook member. For hook members, the head portion
preferably projects past the stem portion on at least one of two
opposite sides. At least the hook head portions have been heat
treated so as to decrease the hook head thickness and thereby
reducing or eliminating molecular orientation in at least the hook
head in the machine direction. Generally, the hook members suitable
for use in the invention method, both before and after treatment,
have a height dimension from the upper surface of the backing of
less than 5000 .mu.m. The stem and head portions generally have a
thickness dimension of less than 1500 .mu.m in a first direction
parallel to the surfaces of the backing. The stem portions each
have a width dimension in the range of 50 to 500 .mu.m in a second
direction, generally at a right angle to the first direction and
parallel to the surfaces of the backing, and the head portions each
have a width dimension in the second direction that is between 50
and 2000 .mu.m greater than the width dimension of the stem portion
and a total width of less than 5000 .mu.m. There are generally at
least 10, preferably 20 to 200 or 20 to 300 hook members per square
centimeter of the base.
[0007] The fastener is preferably made by a novel adaptation of a
known method of making hook fasteners as described, for example, in
U.S. Pat. Nos. 3,266,113; 3,557,413; 4,001,366; 4,056,593;
4,189,809 and 4,894,060 or alternatively 6,209,177, the substance
of which are incorporated by reference in their entirety. The
preferred method generally includes extruding a thermoplastic resin
through a die plate which die plate is shaped to form a base layer
and spaced ridges, ribs or hook elements projecting above a surface
of the base layer. These ridges generally form the cross-section
shapes of the desired projection to be produced, which is
preferably a hook member. When the die forms the spaced ridges or
ribs the cross sectional shape of the hook members are formed by
the die plate while the initial hook member thickness is formed by
transversely cutting the ridges at spaced locations along their
lengths to form discrete cut portions of the ridges. Subsequently
longitudinal stretching of the backing layer (in the direction of
the ridges on the machine direction) separates these cut portions
of the ridges, which cut portion then form spaced apart hook
members. The extruded hook members or cut rib hook members are then
heat treated resulting in shrinkage of at least a portion of at
least the hook head portion thickness by from 5 to 90 percent,
preferably 30 to 90 percent. In an alternative embodiment, the heat
treatment is continued to likewise shrink at least a portion of the
stem portion of the hook members. The resulting heat treated
projections, preferably hooks, are substantially upstanding or
rigid such that they do not droop toward the base layer or are able
to penetrate a fibrous or like substrate. In a particular preferred
embodiment, the extruded thermoplastic resin contains an immiscible
phase to increase the extent of molecular orientation in the
thermoplastic polymer or increase the degree of hook member or
projection shrinkage when heat treated.
BRIEF DESCRIPTION OF THE DRAWINGS
[0008] The present invention will be further described with
reference to the accompanying drawings wherein like reference
numerals refer to like parts in the several views, and wherein:
[0009] FIG. 1 schematically illustrates a method for making the
hook fastener portion of FIG. 4.
[0010] FIGS. 2 and 3 illustrate the structure of a strip at various
stages of its processing in the method illustrated in FIG. 1.
[0011] FIG. 4 is an enlarged perspective view of a hook
fastener.
[0012] FIGS. 5a and 5b are enlarged fragmentary side and end views,
respectively, of one hook member in the hook fastener portion of
FIG. 4.
[0013] FIGS. 6a and 6b are views of FIGS. 5a and 5b, respectively,
after limited heat treating of the hook member.
[0014] FIGS. 7a and 7b are views of FIGS. 5a and 5b, respectively,
after heat treating of the entire hook member.
[0015] FIGS. 8 and 9 are enlarged fragmentary sectional views of
alternate embodiments of hook portions that can be used in hook
fastener portions according to the present invention;
[0016] FIG. 10 is an alternative embodiment of individual extruded
hook elements that can be heat treated in accordance with the
invention method.
[0017] FIG. 11 is a cross-sectional view of a fully heat treated
alternative hook member in accordance with the invention.
[0018] FIG. 12 is a cross-sectional view of a heat treated hook
member in accordance with the invention.
[0019] FIG. 13 is a cross-sectional view of a fully heat treated
hook member in accordance with the invention.
[0020] FIG. 14 is a cross-sectional view of a fully heat treated
hook member in accordance with the invention.
[0021] FIG. 15 is a perspective view of a disposable garment using
a preferred hook member according to the present invention.
[0022] FIG. 16 is a perspective view of a disposable garment using
a preferred hook member according to the present invention.
[0023] FIG. 17 is a perspective view of a disposable garment using
a preferred hook member according to the present invention.
[0024] FIG. 18 is a perspective view of a feminine hygiene
article.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
[0025] Referring now to FIG. 4 is an exemplary polymeric hook
fastener portion, which can be produced, or heat treated according
to the present invention is generally designated by the reference
numeral 10. The hook fastener portion 10 comprises a thin strong
flexible film-like backing 11 having generally parallel upper and
lower major surfaces 12 and 13, and a multiplicity of spaced hook
members 14 projecting from at least the upper surface 12 of the
backing 11. The backing can have planar surfaces or surface
features as could be desired for tear resistance or reinforcement.
As is best seen in FIG. 5, the hook members 14 each comprise a stem
portion 15 attached at one end to the backing 11 and preferably
having tapered sections 16 that widen toward the backing 11 to
increase the hook anchorage and breaking strengths at their
junctures with the backing 11, and a head portion 17 at the end of
the stem portion 15 opposite the backing 11. The sides 34 of the
head portion 17 can be flush with the sides 35 of the stem portion
15 on two opposite sides. The head portion 17 has hook engaging
parts or arms 36, 37 projecting past the stem portion 15 on one or
both sides 38. The hook member shown in FIGS. 5a and 5b has a
rounded surface 18 opposite the stem portion 15 to help the head
portion 17 enter between loops in a loop fastener portion. The head
portion 17 also has transverse cylindrically concave surface
portions 19 at the junctures between the stem portion 15 and the
surfaces of the head portion 17 projecting over the backing 11.
[0026] With reference to FIGS. 5a and 5b, there is shown a single
representative one of the small hook members 14 on which its
dimensions are represented by reference numerals between
dimensional arrows. The height dimension is 20. The stem and head
portions 15 and 17 have a thickness dimension 21, which as shown is
the same, and the head portions 17 have a width dimension 23 and an
arm droop 24. The stem portion has a width dimension 22 at its base
before flaring 16 to the base film 11. The thickness as shown is
for a rectilinear shaped hook, with other shapes the thickness can
be measured as the shortest distance between two opposing sides 34
or 35. Likewise, the width dimension can be measured as the
shortest distance between two opposing sides.
[0027] FIGS. 8 and 9 illustrate two of many alternate shapes that
could be used for the hook members in alternate embodiments of the
hook members that can be heat treated in accordance with the
invention method.
[0028] The hook member 25 illustrated in FIG. 8 differs from the
hook member 14 of FIG. 5 in that its head portion 26 projects
farther on opposite sides from its stem portion 27 and is generally
uniformly thick so that it can more easily bend to engage with or
disengage from loops on a loop fastener portion.
[0029] The hook member 30 illustrated in FIG. 9 differs from the
hook member 14 of FIG. 5 in that its head portion 31 projects from
only one side of its stem portion 32 and will thus cause
significantly greater peel forces when peeled away from the
direction the head portion 31 projects than when it is peeled
toward the direction the head portion 31 projects.
[0030] A first embodiment method for forming a hook fastener
portion, such as that of FIG. 4, is schematically illustrated in
FIG. 1. Generally, the method includes first extruding a strip 50
shown in FIG. 2 of thermoplastic resin from an extruder 51 through
a die 52 having an opening cut, for example, by electron discharge
machining, shaped to form the strip 50 with a base 53 and elongate
spaced ribs 54 projecting above an upper surface of the base layer
53 that have the cross sectional shape of the hook portions or
members to be formed. The strip 50 is pulled around rollers 55
through a quench tank 56 filled with a cooling liquid (e.g.,
water), after which the ribs 54 (but not the base layer 53) are
transversely slit or cut at spaced locations along their lengths by
a cutter 58 to form discrete portions 57 of the ribs 54 having
lengths corresponding to about the desired thicknesses of the hook
portions to be formed, as is shown in FIG. 3. The cut can be at any
desired angle, generally from 90.degree. to 30.degree. from the
lengthwise extension of the ribs. Optionally, the strip can be
stretched prior to cutting to provide further molecular orientation
to the polymers forming the ribs and/or reduce the size of the ribs
and the resulting hook members formed by slitting of the ribs. The
cutter 58 can cut using any conventional means such as
reciprocating or rotating blades, lasers, or water jets, however
preferably it cuts using blades oriented at an angle of about 60 to
80 degrees with respect to lengthwise extension of the ribs 54.
[0031] After cutting of the ribs 54, the base 53 of the strip 50 is
longitudinally stretched at a stretch ratio of at least 2 to 1, and
preferably at a stretch ratio of about 4 to 1, preferably between a
first pair of nip rollers 60 and 61 and a second pair of nip
rollers 62 and 63 driven at different surface speeds. Optionally,
the strip 50 can also be transversely stretched to provide biaxial
orientation to the base 53. Roller 61 is preferably heated to heat
the base 53 prior to stretching, and the roller 62 is preferably
chilled to stabilize the stretched base 53. Stretching causes
spaces between the cut portions 57 of the ribs 54, which then
become the hook portions or members 14 for the completed hook
fastener portion 10. The formed hook members are then heat treated
preferably by a non-contact heat source 64. The temperature and
duration of the heating should be selected to cause shrinkage or
thickness reduction of at least the head portion by from 5 to 90
percent. The heating is preferably accomplished using a non-contact
heating source which can include radiant, hot air, flame, UV,
microwave, ultrasonics or focused IR heat lamps. This heat treating
can be over the entire strip containing the formed hook portions or
can be over only a portion or zone of the strip. Or different
portions of the strip can be heat treated to more or less degrees
of treatment. In this manner, it is possible to obtain on a single
strip hook containing areas with different levels of performance
without the need to extrude different shaped rib profiles. This
heat treatment can change hook elements continuously or in
gradients across a region of the hook strip. In this manner, the
hook elements can differ continuously across a defined area of the
hook member. Further, the hook density can be the same in the
different regions coupled with substantially the same film backing
caliper or thickness (e.g., 50 to 500 microns). The caliper can
easily be made the same as the hook strip will have the same basis
weight and same relative amount of material forming the hook
elements and backing in all regions despite the difference in the
shape of the hooks caused by the subsequent heat treating. The
differential heat treatment can be along different rows or can cut
across different rows, so that different types of hooks, such as
hooks having different hook thicknesses, can be obtained in a
single or multiple rows in the machine direction or the lengthwise
direction of the hook strip. The heat treatment can be performed at
any time following creation of the hook element, such that
customized performance can be created without the need for
modifying the basic hook element manufacturing process.
[0032] FIG. 6 shows a hook member of the FIG. 5 hook after it has
been heat treated to cause a reduction in the thickness 21' of the
hook head portion 17'. The other dimensions of the hook member can
also change which is generally as a result of conservation of mass.
The height 20' generally increases a slight amount and the head
portion width 23' increases as does the arm droop 24'. The stem and
head portions now have a thickness dimension 21' that is nonuniform
and tapers from the base to the head portion due to the incomplete
heat treatment along the entire hook member 14'. Generally the
untreated portion has a uniform thickness corresponding to the
original thickness 21, the generally fully heat treated portion
will have a uniform thickness 21' with a transition zone separating
the untreated and treated portions. In this embodiment, the
incomplete heat treatment also results in variation of the
thickness 21' of the hook head portion from the arm tip to the arm
portion adjacent the stem 15'. All other numbered elements in FIGS.
6a and 6b correspond to the numbered elements of FIGS. 5a and
5b.
[0033] Reduction in the hook member thickness is caused by
relaxation of at least the melt flow induced molecular orientation
of the hook head and/or stem portion which is in the machine
direction, which generally corresponds to the thickness direction.
Also, further reduction in thickness can occur where there is
stretch induced molecular orientation, as where the ribs are
stretched longitudinally prior to cutting. Melt induced molecular
orientation is created by the melt extrusion process as polymer,
under pressure and shear forces, is forced through the die
orifice(s). The rib or ridge forming sections of the die create the
molecular orientation in the formed ribs. This molecular
orientation extends longitudinally or in the machine direction
along the ribs or ridges. When the ribs or ridges are cut, the
molecular orientation extends generally in the thickness dimension
of the cut ribs, or cut hook members, however, the molecular
orientation can extend at an angle of from about 0 to 45 degrees to
the hook member thickness. The initial molecular orientation in the
hook members is generally at least 10 percent, preferably 20 to 100
percent (as defined below). When the hook members are heat treated
in accordance with the invention, the molecular orientation of the
hook members decrease and the hook member thickness dimension
decreases. The amount of thickness reduction depends primarily on
the amount of hook member molecular orientation extending in the
machine direction or hook thickness dimension. The heat treatment
conditions, such as time of treatment, temperature, the nature of
the heat source and the like can also effect the hook member
thickness reduction. As the heat treatment progresses, the
reduction in hook member, or projection thickness extends from the
hook head portion, or top of the projection, to the stem portion,
or down the projection to the base, until the entire hook member
thickness has been reduced. Generally, the thickness reduction is
substantially the same in the stem and the hook head portions when
both are fully heat treated or partially heat treated to the same
extent. When only a part of the hook head portion and/or hook head
portion and stem portion are heat treated, there is a transition
zone where the thickness increases from the upper heat treated
portion, generally the head portion, to the substantially non-heat
treated portion of the stem portion, or stem portion and part of
the hook head portion, which have a substantially unreduced
thickness. When the thickness dimension shrinks, the width of the
treated portion generally increases, while the overall hook member
height increases slightly and the arm droop increases. The end
result is a hook thickness that can either, not be economically
produced directly, or cannot be produced at all by conventional
methods. The heat treated projection, generally the hook head, and
optionally stem, is also characterized by a molecular orientation
level of less than 10 percent, preferably less than 5 percent where
the base film layer orientation is substantially unreduced.
Generally, the hook member stem or projection orientation
immediately adjacent the base film layer will be 10 percent or
higher, preferably 20 percent or higher.
[0034] FIG. 7 is a schematic view of a hook member of the FIG. 5
hook, where the entire hook member has been subjected to heat
treatment. In this case, both the hook head portion 17" and the
stem portion 15" have shrunk in the thickness direction with
corresponding increases in the width dimensions 23" and 22" and arm
droop 24". In this case, both the stem and head portion have a
generally uniform thickness dimension 21", which is less than the
initial hook member width dimension 21. The tapered section 16" is
generally larger than the initial tapered section 16 due the
thickness reduction in the stem portion.
[0035] The heat treatment is generally carried out at a temperature
near or above the polymer melt temperature. As the heat gets
significantly above the polymer melt temperature, the treatment
time decreases so as to minimize any actual melting of the polymer
in the hook head portion or top of the projection. The heat
treatment is carried out at a time sufficient to result in
reduction of the thickness of the hook head, and/or stem, but not
such that there is a significant deformation of the backing or melt
flow of the hook head portion or top of the projection. Heat
treatment can also result in rounding of the hook head portion
edges, improving tactile feel for use in garment applications.
[0036] Unexpectedly it has been discovered, that for high
performance microhook engagement with certain low cost or low loft
loop fabrics, that this heat treatment substantially increases
engagement of the microhooks to the loop fabrics. A particularly
preferred novel, microhook member producible by the invention
method has been discovered where the hook members have a height of
less than 1000 .mu.m, preferably from 300 to 800 .mu.m, and at
least a head portion with a thickness of from 50 to 200 .mu.m,
preferably 50 to 180 .mu.m. The other dimensions for this improved
microhook include a stem width, as defined above, of from 50 to 500
.mu.m, a head portion width of from 100 to 800 .mu.m, and an arm
droop of from 50 to 700 .mu.m, preferably 100 to 500 .mu.m, and a
hook density of at least 50 and preferably from about 70 to 150, up
to 300, hooks per square centimeter. This novel microhook hook
portion exhibits improved overall performance to a variety of low
loft loop fabrics.
[0037] In certain applications, it has unexpectedly been discovered
that very low hook densities are desirable. For example, hook
densities of less than 100, preferably less than 70 and even less
than 50 hook per square centimeter are desirable when used to
attach to low loft nonwovens using a relatively large area flexible
hook tab or patch. This low spacing has been found to increase the
hooking efficiency of the individual hook element, particularly
relative to low cost and otherwise ineffective nonwoven materials
not traditionally used as loop products. The hook tab or patch can
be made flexible by suitable selection of the polymer forming the
base layer and/or by stretching the base layer at an angle
transverse to the longitudinal stretching. This transverse
stretching creates biaxial orientation in the base layer reducing
its thickness, for example from 20 .mu.m to 100 .mu.m, preferably
30 .mu.m to 60 .mu.m. Biaxial orientation also reduces the hook
density to the desired range for low density hook application.
Examples of suitable uses for this low density hook element, as a
tab or patch, are illustrated in FIGS. 15-18. In FIG. 15, a large
area fastening tab is attached to a carrier substrate 92, which is
attached to a diaper 90 as is known in the art. The fastening tab
could be of a size of from 5 to 100 cm.sup.2, preferably 20 to 70
cm.sup.2 and can be attached directly to a low loft nonwoven 95
forming the outer cover of the diaper. Typically, this low loft
nonwoven would be a spunbond web, a bonded carded or air laid web,
a spunlace web or the like. FIG. 16 is a variation of this
fastening tab type construction for a diaper 95, however, where the
hook tab 96 is directly bonded to the diaper 95, either at an ear
cutout portion or at the edge region of the diaper. FIG. 17 is a
further embodiment of a large area hook tab 98 used with a pull up
type diaper design. In this embodiment, the hook tab 98 would
engage a suitable mating region 99 on the opposite face of the pull
up diaper. Of course, these two elements could be reversed. In both
cases, the mating region could be a nonwoven used to form the
nonwoven outer cover of the diaper or the nonwoven fluid permeable
topsheet. FIG. 18 is an embodiment of the invention hook material
being used as a large area patch 101 on a feminine hygiene article
100. The patch could be used as the primary attachment element to
the undergarment, optionally a secondary attachment element 103
could be provided on attachment wings 102. The use of the low
density hook element as a large area patch could also be used on a
diaper where the patch could form a part or all of the diaper outer
cover.
[0038] Suitable polymeric materials from which the hook fastener
portion can be made include thermoplastic resins comprising
polyolefins, e.g. polypropylene and polyethylene, polyvinyl
chloride, polystyrene, nylons, polyester such as polyethylene
terephthalate and the like and copolymers and blends thereof.
Preferably the resin is a polypropylene, polyethylene,
polypropylene-polyethylene copolymer or blends thereof.
[0039] In a preferred embodiment, the orientable thermoplastic
resin is blended with a material that will form a distinct second
phase. The orientable thermoplastic resin constitutes a continuous
first phase, generally 50 percent or greater by volume of the
volume of the blend as extruded. The thermoplastic resin can be a
single resin or a homogeneous or a mechanically compatible blend.
Compatibility of polymer blends can be determined by using
differential scanning calorimetry (DSC) to measure the melting
points and glass transition temperatures of the polymer blend. If
two glass transition temperatures are detected by DSC due to the
constituent polymers in the blend, the blend is said to be
incompatible. If a single glass transition temperature,
intermediate between those of the component polymers, is detected,
the blend is said to be compatible. Mechanically compatible blends
represent a deviation from this generality, since they exhibit two
glass transition temperatures but have finer morphology, are
translucent and are extrudable without gross phase separation. Such
blends are useful in this invention. The distinct second phase is
generally a discontinuous phase but also could be a continuous
phase. The presence of a distinct second phase results in
substantial increases in the degree of heat shrinkage of the heat
treated projection or hook. The distinct second phase could
preferably be a gas, a nonparticulate diluent, a phase distinct
thermoplastic polymer, a tackifier or combination of these
materials.
[0040] Examples of preferred nonparticulate diluents that can be
used in combination with the thermoplastic resins include, but are
not limited to, mineral oils, petroleum jelly, low molecular weight
polyethylene, soft Carbowax and mixtures thereof. Mineral oils are
preferred among these diluents because of their relatively low
cost. The diluents may optionally be partially or entirely
extracted from the extruded hook film by known methods. The
diluents can be varied within a wide range within the starting
thermoplastic resin used for production of the film backed
fastener. The amount of diluents used is preferably in the range of
20-60% by weight, and more preferably 25-40% by weight of the
starting thermoplastic material. If the amount of diluent added to
the starting material is under 20% by weight, the increase in
shrinkage of the hook element or projection is reduced, while if it
is above 60% by weight it becomes more difficult to produce
flexible coherent film backed fasteners.
[0041] Physical or chemical blowing agents are useful in the
present invention to form distinct gas phases. A blowing agent may
be any material that is capable of forming a vapor at the
temperature and pressure at which the extrudate exits the die. A
blowing agent may be a physical blowing agent. A physical blowing
agent may be introduced, i.e., injected into the thermoplastic
material as a gas or supercritical fluid. Flammable blowing agents
such as pentane, butane and other organic materials may be used,
but non-flammable, non-toxic, non-ozone depleting blowing agents
such as carbon dioxide, nitrogen, water, SF.sub.6, nitrous oxide,
argon, helium, noble gases, such as xenon, air (nitrogen and oxygen
blend), and blends of these materials are preferred because they
are easier to use, e.g., fewer environmental and safety concerns.
Other suitable physical blowing agents include, e.g.,
hydrofluorocarbons (HFC), hydrochlorofluorocarbons (HCFC), and
fully- or partially fluorinated ethers.
[0042] If chemical blowing agents are used, they are preferably
added to the thermoplastic resin at a temperature below that of the
activation temperature of the blowing agent, and are typically
added to the thermoplastic resin feed at room temperature prior to
introduction to the extruder. The blowing agent is then mixed to
distribute it throughout the polymer in unactivated form, above the
melt temperature of the thermoplastic resin, but below the
activation temperature of the chemical blowing agent. Once
dispersed, the chemical blowing agent may be activated by heating
the mixture to a temperature above the activation temperature of
the agent. Activation of the blowing agent liberates gas either
through decomposition (e.g., exothermic chemical blowing agents
such as azodicarbonamide) or reaction (e.g., endothermic chemical
blowing agents such as sodium bicarbonate-citric acid mixtures),
such as N.sub.2, CO.sub.2 and/or H.sub.2O, yet cell formation is
restrained by the temperature and pressure of the system. Useful
chemical blowing agents typically activate at a temperature of
140.degree. C. or above.
[0043] Examples of chemical blowing agents include synthetic azo-,
carbonate-, and hydrazide based molecules, including
azodicarbonamide, azodiisobutyronitrile, benzenesulfonhydrazide,
4,4-oxybenzene sulfonyl-semicarbazide, p-toluene sulfonyl
semi-carbazide, barium azodicarboxylate,
N,N'-dimethyl-N,N'-dinitrosoterephthalamide and trihydrazino
triazine. Specific examples of these materials are Celogen OT (4,4'
oxybis (benzenesulfonylhydrazide)). Other chemical blowing agents
include endothermic reactive materials such as sodium
bicarbonate/citric acid bends that release carbon dioxide. Specific
examples include Reedy International Corp SAFOAM products.
[0044] When the extrudate exit temperature is at or below
50.degree. C. above the T.sub.m of the thermoplastic resin, the
increase in T.sub.m of the resin as the blowing agent comes out of
the solution causes crystallization of the thermoplastic resin,
which in turn arrests the growth and coalescence of the foam cells.
When exit temperatures are in excess of 50.degree. C. above the
T.sub.m of the thermoplastic resin, cooling of the resin may take
longer, resulting in non-uniform, unarrested cell growth.
[0045] The amount of blowing agent incorporated into the foamable
thermoplastic phase is generally chosen to yield a foam having a
void content in excess of 10%, more preferably in excess of 20%, as
measured by density reduction; [1-the ratio of the density of the
foam to that of the neat polymer].times.100.
[0046] Preferably, the formed foam is oriented such as by uniaxial
or biaxial stretching in mutually perpendicular directions at a
temperature above the alpha transition temperature and below the
melting temperature of the thermoplastic phase. Foams may be
stretched in one or both directions 3 to 50 times total draw ratio
(MD.times.CD) for biaxial stretching or 1 -10 times for uniaxial
stretching. Generally greater orientation is achievable using foams
of small cell size; foams having cell size of greater than 100
microns are not readily biaxially oriented more than 20 times
(MD.times.CD), while foams having a cell size of 50 microns or less
could be stretched up to 50 times total draw ratio. In addition
foams with small average cell size exhibit greater tensile strength
and elongation to break after stretching. Small cell sizes (100
microns or less) in combination with the orientation allows a foam
sheet thickness of 25 microns to 1000 microns, and foam sheets of
25 microns to 100 microns are readily prepared. This is extremely
desirable with hook structures, as a soft conformable backing is
obtained that can be used in many uses where contact with an active
wearer (e.g., a person) is desired or possible. Specifically, the
foamed hook can be used with disposable absorbent articles such as
diapers as a closure tab, which is soft to the touch and is
aesthetically pleasing due to its pearlescent appearance. Other
uses where a hook strip or tab would be in contact with a sensitive
surface would include medical wrap, sport wraps, headbands, produce
wraps and feminine hygiene articles. Suitable backings can have a
stiffness of from 10 to 2000 Gurley stiffness units, preferably
from 10 to 200 Gurley stiffness units.
[0047] Preferably, the foam can have cell sizes of 2 to 100
microns, preferably 5 to 50 microns. The foam may alternatively, or
additionally, have a cell size distribution with a polydispersity
from 1.0 to 2.0, preferably from 1.0 to 1.5, more preferably from
1.0 to 1.2.
[0048] For forming these foams, the thermoplastic orientable resins
are preferably high melt strength polyolefins, such as branched
polyolefins. These high melt strength polymers help control the
growth of the foam cells within the desired range necessary for
creating the discrete microstructures and prevent collapse of the
cells during surface microstructure formation if needed. Suitable
semi-crystalline materials include polyethylene, polypropylene,
polymethylpentene, polyisobutylene, polyolefin copolymers, Nylon 6,
Nylon 66, polyester, polyester copolymers, fluoropolymers, poly
vinyl acetate, poly vinyl alcohol, poly ethylene oxide,
functionalized polyolefins, ethylene vinyl acetate copolymers,
metal neutralized polyolefin ionomers available under the trade
designation SURLYN (E.I. DuPont de Nemours, Wilmington, Del.),
polyvinylidene fluoride, polytetrafluoroethylene, polyformaldehyde,
polyvinyl butyral, and copolymers having at least one
semi-crystalline compound. Preferred high melt strength polymers
are high melt strength polypropylenes which include homo- and
copolymers containing 50 weight percent or more propylene monomer
units, preferably at least 70 weight percent, and have a melt
strength in the range of 25 to 60 cN at 190.degree. C. Melt
strength may be conveniently measured using an extensional
rheometer by extruding the polymer through a 2.1 mm diameter
capillary having a length of 41.9 mm at 190.degree. C. and at a
rate of 0.030 cc/sec; the strand is then stretched at a constant
rate while measuring the force to stretch at a particular
elongation. Preferably the melt strength of the polypropylene is in
the range of 30 to 55 cN, as described in WO 99/61520.
[0049] Such high melt strength polypropylenes may be prepared by
methods generally known in the art. Reference may be made to U.S.
Pat. No. 4,916,198 which describes a high melt strength
polypropylene having a chain-hardening elongational viscosity
prepared by irradiation of linear propylene in a controlled oxygen
environment. Other useful methods include those in which compounds
are added to the molten polypropylene to introduce branching and/or
crosslinking such as those methods described in U.S. Pat. No.
4,714,716, WO 99/36466 and WO 00/00520. High melt strength
polypropylene may also be prepared by irradiation of the resin as
described in U.S. Pat. No. 5,605,936. Still other useful methods
include forming a bipolar molecular weight distribution as
described in J I Raukola, "A New Technology To Manufacture
Polypropylene Foam Sheet And Biaxial Oriented Foam Film", VTT
Publications 361, Technical Research Center of Finland, 1998 and in
U.S. Pat. No. 4,940,736.
[0050] A second distinct phase can be formed by a blend of two or
more incompatible thermoplastic polymers. Compatibility can be
determined by using differential scanning calorimetry (DSC) to
measure the melting points and glass transition temperatures of the
polymer blend. If two glass transition temperatures are detected by
DSC due to the constituent polymers in a blend, the blend is said
to be incompatible. If a single glass transition temperature,
intermediate between those of the component polymers, is detected,
the blend is said to be compatible. Phase distinct polymer blends
can be prepared from blends of olefinic polymers with non-olefinic
polymers. Examples of olefinic polymers include polypropylene,
polyethylene, propylene-ethylene random and impact copolymers,
polybutenes and polyethylenevinylacetates. Examples of non-olefinic
polymers include polystyrenes, polyamides, polyurethanes and
polyesters. Block copolymers such as styrene-isoprene-styrene (SIS)
and styrene-ethylenebutylene-styrene (SEBS) are useful as one of
the constituents of the blends.
[0051] The backing of the fastener must be thick enough to allow it
to be attached to a substrate by a desired means such as sonic
welding, heat bonding, sewing or adhesives, including pressure
sensitive or hot melt adhesives, and to firmly anchor the stems and
provide resistance to tearing when the fastener is peeled open.
However, when a fastener is used on a disposable garment, the
backing should not be so thick that it is stiffer than necessary.
Generally, the backing has a Gurley stiffness of 10 to 2000,
preferably 10 to 200 so as to allow it to be perceived as soft when
used either by itself or laminated to a further carrier backing
structure such as a nonwoven, woven or film-type backing, which
carrier backing should also be similarly soft for use in disposable
absorbent articles. The optimum backing thickness will vary
depending upon the resin from which the hook fastener portion is
made, but will generally be between 20 .mu.m and 1000 .mu.m, and is
preferably 20 to 200 .mu.m for softer backings.
[0052] An alternative method for extruding hook members from a die
is described in U.S. Pat. No. 6,209,177 which results in hook
fastening portions such as shown in FIG. 10. Each of the hook
members comprises a stem portion 41 projecting from the surface of
the backing 42 and a hook head 43 projecting from an end of the
stem portion 41 sideways in at least one direction. A thickness of
the hook member 40, which is perpendicular to a projecting
direction of the hook head portion 43 of the hook member 40,
gradually increases from a top portion of the hook head portion 43
toward a rising base end of the stem portion 41. With these hook
members 40 each hook member 40 is molded independently of each
other and integral with the surface of the backing substrate 42, in
contrast to cutting of ribs and drawing of the backing substrate.
The molten resin is extruded through a die plate however in this
method a face of the die includes an ascending/descending member
vertically reciprocating in sliding contact with a front of the die
face interrupting polymer flow to the die elements forming the
ridges. During extrusion molding the molten resin constantly forms
the base while the ascending and descending movement of an
ascending/descending member interrupts flow to the rib section
resulting in a vertical line of a plurality of separate hook
members 40 continuously extending from the backing substrate
42.
[0053] The invention microhooks generally have been formed to be
particularly useful in engaging with low profile nonwoven
laminates. Most notably improved engagement has been unexpectedly
discovered where the hooks have relatively low arm droop, and the
ratio of the arm droop to the thickness of the nonwoven portion of
a nonwoven laminate is less than 1.5, preferably less than 1.3 and
most dramatically when less than 1.0. The peel force (135 degree)
is generally above 120 grams/2.5 cm, preferably greater than 200
grams/2.5 cm.
[0054] Suitable low profile nonwoven laminates are laminates of a
nonwoven fabric or web to a film or a higher strength nonwoven
fabric or web. A "nonwoven fabric or web" is a web of individual
fibers or threads which are randomly associated fibers that are not
associated in a regular manner such as in a knitted fabric.
Nonwoven fabrics or webs can be formed from processes such as, for
example, meltblowing, spunbonding, spunlace and bonded carded
webs.
[0055] In a preferred embodiment, the laminate is a film/nonwoven
laminate where the nonwoven fabric, preferably a spunbond web, is
thermally or extrusion bonded to a film. The film can have a center
bonding layer which is made from a polymer which more easily bonds
to the nonwoven, such as a semi-crystalline/amorphous with a base
layer of another polymer, such as a polyolefin. Pigments can also
be used in the base layer.
[0056] Suitable bonding layers include polymers such as disclosed
in European Patent Application EP 0444671 A3, European Patent
application EP 0472946 A2, European Patent Application EP 0400333
A2, U.S. Pat. No. 5,302,454 and U.S. Pat. No. 5,368,927 and other
bonding polymers include ethylene-n-butyl acetate, ethylene/vinyl
acetate copolymers, ethylene/methyl acetate copolymers, ethyl
acrylic acid and other copolymers, and terpolymers of
polypropylene, polyethylene and polybutylene as well as elastomers
such as styrene conjugated diene block copolymer such as SEBS,
SEPS, SBS, and urethanes.
[0057] A base layer used with bonding layer may be a polypropylene
polymer or copolymer. Since this layer is relatively thick, the
majority of opacity if desired may be added to this layer through
the use of opacifiers such as, for example, TiO.sub.2 or
CaCO.sub.3. The nonwoven and the film or higher strength nonwoven
component are preferably bonded together using thermal point
bonding (heat or ultrasonic bonding). The point bonding if used
should be at a density that would allow hooks to penetrate into the
nonwoven, generally 30 percent or less, and preferably 20 percent
or less. The lower bond area limit depends on the integrity of the
laminate and the bond strength at the points but it is generally
greater than 1 to 2 percent. A compatible tackifying resin may also
be added to the bonding layer.
[0058] The nonwoven used in the laminates preferably is produced by
meltblowing or spunbonding processes, which processes are well
known in the art. The extruded fibers were generally deposited on a
moving foraminous mat or belt to form the nonwoven fabric. The
fibers produced in the spunbond and meltblown processes have
average fiber diameters of less than 75 microns and less. Meltblown
fibers are able to be produced having average fiber diameter of 10
microns and less, to about 1 micron. Spunbond fibers are generally
25 microns or more and are preferred for use to engage with the
invention microhooks due to their greater strength. The nonwoven
portion of the laminate generally has a thickness of from 100 to
300 microns, preferably from 100 to 200 microns and has a basis
weight of from 10 to 50 g/m.sup.2.
Test Methods
[0059] 135 Degree Peel Test
[0060] The 135 degree peel test was used to measure the amount of
force that was required to peel a sample of the mechanical fastener
hook material from a sample of loop fastener material. A 5.1
cm.times.12.7 cm piece of a loop test material was securely placed
on a 5.1 cm.times.12.7 cm steel panel by using a double-coated
adhesive tape. The loop material was placed onto the panel with the
cross direction of the loop material parallel to the long dimension
of the panel. A 1.9 cm.times.2.5 cm strip of the mechanical
fastener to be tested was cut with the long dimension being in the
machine direction of the web. A 2.5 cm wide paper leader was
attached to the smooth side of one end of the hook strip. The hook
strip was then centrally placed on the loop so that there was a 1.9
cm.times.2.5 cm contact area between the strip and the loop
material and the leading edge of the strip was along the length of
the panel. The strip and loop material laminate was then rolled by
hand, twice in each direction, using a 1000 gram roller at a rate
of approximately 30.5 cm per minute. The sample was then placed in
a 135 degree peel jig. The jig was placed into the bottom jaw of an
Instron.TM. Model 1122 tensile tester. The loose end of the paper
leader was placed in the upper jaw of the tensile tester. A
crosshead speed of 30.5 cm per minute and a chart recorder set at a
chart speed of 50.8 cm per minute was used to record the peel force
as the hook strip was peeled from the loop material at a constant
angle of 135 degrees. An average of the four highest peaks was
recorded in grams. The force required to remove the mechanical
fastener strip from the loop material was reported in grams/2.54
cm-width. A minimum of 10 tests were run and averaged for each hook
and loop combination.
[0061] Two different loop materials were used to measure the
performance of the mechanical fastener hook material. Loop material
`A` is a nonwoven loop made similar to that described in U.S. Pat.
No. 5,616,394 Example 1, available from the 3M Company as KN-1971.
Loop material `B` is a knitted loop-made similar to that described
in U.S. Pat. No. 5,605,729, Example 1 available from the 3M Company
as XML-01-160. The loop test materials were obtained from a supply
roll of the material after unwinding and discarding several
revolutions to expose "fresh" material. The loop test material thus
obtained was in a relatively compressed state and was used
immediately in the peel test before any significant relofting of
the loops could occur.
[0062] 135 Degree Peel Test for Low Profile Loops
[0063] A 135 degree peel test was used to measure the amount of
force that was required to peel a sample of the mechanical fastener
hook material from a sample of low profile loop fastener material.
A 1.9 cm.times.2.5 cm strip of the mechanical fastener to be tested
was cut with the long dimension being in the machine direction of
the web. A 2.5 cm wide paper leader was attached to the smooth side
of one end of the hook strip. The hook materials were fastened to
the low profile loop material using the following procedure: The
hook material, with hook side down, was placed onto the low profile
loop backsheet material of a diaper. A 4.1 kg weight measuring 7.6
cm.times.7.6 cm with medium grit abrasive paper on the bottom
surface, was placed on top of the hook material. To engage the hook
with the backsheet loop material, the diaper was held securely flat
and the weight was twisted 45 degrees to the right, then 90 degrees
to the left, then 90 right and then 45 degrees left. The weight was
then removed and the diaper was held firm against the surface of a
135 degree jig stand mounted into the lower jaw of an Instron.TM.
Model 1122 tensile tester. The loose end of the paper leader
attached to the hook material was placed in the upper jaw of the
tensile tester. A crosshead speed of 30.5 cm per minute and a chart
recorder set at a chart speed of 50.8 cm per minute was used to
record the peel force as the hook strip was peeled from the loop
material at a constant angle of 135 degrees. An average of the four
highest force peaks was recorded in grams and was reported in
grams/2.54 cm-width. 10 different locations were tested on each
diaper with the average of the 10 being reported in Table 4.
[0064] Three different low profile loop materials were used to
measure the performance of the mechanical fastener hook material.
Loop material `C` is the nonwoven side (i.e. outward facing side)
of the backsheet of a Loving Touch diaper size 3. Loop material `D`
is the nonwoven side (i.e. outward facing side) of the backsheet of
a Walgreens Supreme diaper size 4. Loop material `E`, was cut from
a Leggs Sheer Energy B nylon stocking. The fabric was stretched by
hand approximately 200% and then attached to a 5 cm.times.15 cm
steel panel using double-coated adhesive tape. The thickness of the
fabric was measured in the stretched condition using an optical
microscope. Twelve measurements were averaged to obtain a thickness
of 239 microns.
[0065] Hook Dimensions
[0066] The dimensions of the Example and Comparative Example hook
materials were measured using a Leica microscope equipped with a
zoom lens at a magnification of approximately 25.times.. The
samples were placed on a x-y moveable stage and measured via stage
movement to the nearest micron. A minimum of 3 replicates were used
and averaged for each dimension. In reference to the Example and
Comparative Example hooks, as depicted generally in FIGS. 5, 6, 7,
11, 12, 13 and 14 hook width is indicated by distance 23, hook
height is indicated by distance 20, arm droop is indicated by
distance 24, and hook thickness is indicated by distance 21.
[0067] Molecular Orientation and Crystallinity
[0068] The orientation and crystallinity of the Example and
comparative example hook materials were measured using X-ray
diffraction techniques. Data was collected using a Bruker
microdiffractometer (Bruker AXS, Madison, Wis.), using copper
K.sub..alpha. radiation, and HiSTAR.TM. 2-dimensional detector
registry of scattered radiation. The diffractometer was fitted with
a graphite incident beam monochromator and a 200 micrometer pinhole
collimator. The X-ray source consisted of a Rigaku RU200 (Rigaku
USA, Danvers, Mass.) rotating anode and copper target operated at
50 kilovolts (kV) and 100 milliamperes (mA). Data was collected in
transmission geometry with the detector centered at 0 degrees
(2.theta.) and a sample to detector distance of 6 cm. Test
specimens were obtained by cutting thin sections of the hook
materials in the machine direction after removing the hook arms.
The incident beam was normal to the plane of the cut sections and
thus was parallel to the cross direction of the extruded web. Three
different positions were measured using a laser pointer and digital
video camera alignment system. Measurements were taken near the
center of the head portion 17, near the midpoint of the stem
portion 15, and as close as possible to the bottom of the stem
portion 17 just slightly above the surface 12 of the backing 11.
The data was accumulated for 3600 seconds and corrected for
detector sensitivity and spatial linearity using GADDS.TM. software
(Bruker AXS Madison, Wis.). The crystallinity indices were
calculated as the ratio of crystalline peak area to total peak area
(crystalline+amorphous) within a 6 to 32 degree (2.theta.)
scattering angle range. A value of one represents 100 percent
crystallinity and value of zero corresponds to completely amorphous
material (0 percent crystallinity). The percent molecular
orientation was calculated from the radial traces of the
two-dimensional diffraction data. Background and amorphous
intensities were assumed to be linear between the 2.theta.
positions defined by traces (A) and (C) defined below. The
background and amorphous intensities in trace (B) were interpolated
for each element and subtracted from the trace to produce (B').
Plot of trace (B') has constant intensity in absence of orientation
or oscillatory intensity pattern when preferred orientation
present. The magnitude of the crystalline fraction possessing no
preferred orientation is defined by the minimum in the oscillatory
pattern. The magnitude of the oriented crystalline fraction is
defined by the intensity exceeding the oscillatory pattern minimum.
The percent orientation was calculated by integration of the
individual components from trace (B').
[0069] Trace (A): leading background edge and amorphous intensity,
12.4-12.8 degrees (2.theta.) radially along .chi., 0.5 degree step
size.
[0070] Trace (B): random and oriented crystalline fractions,
background scattering, and amorphous intensity; 13.8-14.8 degrees
(2.theta.) radially along .chi., 0.5 degree step size.
[0071] Trace (C): trailing background edge and amorphous intensity;
15.4 to 15.8 degrees (2.theta.) radially along .chi., 0.5 degree
step size.
[0072] Trace (B'): random and oriented crystalline fractions
obtained by subtraction of amorphous and background intensity from
trace (B).
[0073] scattering angle center of trace (A): (12.4 to 12.8)
deg.=12.6 deg. 2.theta.
[0074] center of trace (B): (13.8 to 14.8) deg.=14.3 deg.
2.theta.
[0075] center of trace (C): (15.4 to 15.8) deg.=15.6 deg.
2.theta.
Interpolation constant=(14.3-12.6)(15.6-12.6)=0.57
[0076] for each array element [i]:
Intensity.sub.(amorphous+background)[i]=[(C[i]-A[i])*0.57]+A[i]
B'[i]=B[i]-Intensity.sub.(amorphous+background)[i]
[0077] From a plot of B'[i] versus [i]:
B'.sub.(random)[i]=intensity value of minimum in oscillatory
pattern
B'.sub.(oriented)[i]=B'[i]-B'.sub.(random)[i]
[0078] Using a Simpson's Integration technique and the following
areas the percent of oriented material was calculated.
B'[i]=total crystalline area (random+oriented)=Area.sub.(total)
B'.sub.(oriented)[i]=oriented crystalline
area=Area.sub.(oriented)
B'.sub.(random)[i]=random crystalline area=Area.sub.(random)
% oriented
material=(Area.sub.(oriented)/Area.sub.(total)).times.100
COMPARATIVE EXAMPLE C1
[0079] A mechanical fastener hook material web was made using the
apparatus shown in FIG. 1. A polypropylene/polyethylene impact
copolymer (SRC7-644, 1.5 MFI, Dow Chemical) was extruded with a
6.35 cm single screw extruder (24:1 L/D) using a barrel temperature
profile of 177.degree. C.-232.degree. C.-246.degree. C. and a die
temperature of approximately 235.degree. C. The extrudate was
extruded vertically downward through a die having an opening cut by
electron discharge machining. After being shaped by the die, the
extrudate is quenched in a water tank at a speed of 6.1 meter/min
with the water being maintained at approximately 10.degree. C. The
web was then advanced through a cutting station where the ribs (but
not the base layer) were transversely cut at an angle of 23 degrees
measured from the transverse direction of the web. The spacing of
the cuts was 305 microns. After cutting the ribs, the base of the
web was longitudinally stretched at a stretch ratio of
approximately 4.1 to 1 between a first pair of nip rolls and a
second pair of nip rolls to further separate the individual hook
elements to approximately 8 hooks/cm. There were approximately 10
rows of ribs or cut hooks per centimeter. The upper roll of the
first pair of nip rolls was heated to 143.degree. C. to soften the
web prior to stretching. The general profile of this hook is
depicted in FIG. 5.
EXAMPLE 1
[0080] The web of comparative example C1 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a 36 cm wide ribbon flame burner Aerogen (Alton
Hampshire, UK) at a speed of 90 meter/minute with a burner to film
gap of 8 mm. The flame power was 74 kj/hour. The smooth base film
side of the web was supported on a chill roll maintained at
approximately 18.degree. C. The general profiles of the resulting
heat treated hook are depicted in FIGS. 6a and 6b. The performance
of the hook material web against nonwoven loop material `A` was
measured using a 135.degree. peel test with the results shown in
Table 1 below. The peel force of the heat-treated web was
approximately 63% greater than the non-heated Comparative Example
1.
EXAMPLE 2
[0081] The web of Comparative Example C1 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a bank of 6-1000 watt 1 micron wavelength
infrared bulbs at a speed of 2.1 meter/min. The hook to bulb
spacing was approximately 2.5 cm. The smooth base film side of the
web was supported on a chill roll maintained at approximately
66.degree. C. The general profiles of the resulting heat treated
hook are depicted in FIGS. 7a and 7b. The performance of the hook
material web against nonwoven loop material `A` was measured using
a peel test with the results shown in Table 1 below. The
135.degree. peel force of the heat-treated web was approximately
206% greater than the non-heat treated Comparative Example C1.
COMPARATIVE EXAMPLE C2
[0082] A mechanical fastener hook material web was made as in
Comparative Example 1 except the web was extruded at a speed of 9.1
meter/min to increase the amount of melt flow induced molecular
orientation in the extrudate. The general profile of this hook is
depicted in FIG. 5.
EXAMPLE 3
[0083] The web of Comparative Example C2 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a bank of 6-2000 watt 1 micron wavelength
infrared bulbs at a speed of 3.0 meter/min. The hook to bulb
spacing was approximately 1.6 cm. The smooth base film side of the
web was supported on a chill roll maintained at approximately
66.degree. C. The performance of the hook material web against
nonwoven loop material `A` was measured using a peel test with the
results shown in Table 1 below. The 135.degree. peel force of the
heat-treated web was approximately 37% greater than the non-heat
treated Comparative Example C2.
COMPARATIVE EXAMPLE C3
[0084] A mechanical fastener hook material web was made as in
Comparative Example 1 except the extrudate was pulled from the die
lip at a 20 degree angle from vertical so as to produce a
cross-sectional profile as shown in FIG. 11. Hook spacing was 16
rows of hooks per centimeter.
EXAMPLE 4
[0085] The web of Comparative Example C3 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a bank of 3-4500 watt 3 micron wavelength
infrared bulbs at a speed of 10.0 meter/min producing hook members
such as shown in FIG. 11 with a hook head portion 77 and stem
portion 75 and a base 73. The hook to bulb spacing was
approximately 2.5 cm. The smooth base film side of the web was
supported on a chill roll maintained at approximately 66.degree. C.
The performance of the hook material web against nonwoven loop
material `A` was measured using a 135.degree. peel test with the
results shown in Table 1 below. The peel force of the heat-treated
web was approximately 254% greater than the non-heat treated
Comparative Example C3.
EXAMPLE 5
[0086] The web of Comparative Example C3 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a perforated metal plate at a speed of 25.0
meter/min producing hook members having a profile substantially as
shown in FIG. 11. Hot air at a temperature of approximately
185.degree. C., provided by a 15 kW electric heater, was blown
through the perforations in the metal plate onto the hook side of
the web at a velocity of approximately 3350 meter/min. The hooks
were approximately 46 cm from the perforated plate. The smooth base
film side of the web was supported on a chill roll at approximately
149.degree. C. After heat treatment the web was cooled by passing
the web over a chill roll maintained at 11.degree. C. The
performance of the hook material web against nonwoven loop material
`A` was measured using a 135.degree. peel test with the results
shown in Table 1 below. The peel force of the heat-treated web was
approximately 136% greater than the non-heat treated Comparative
Example C3.
COMPARATIVE EXAMPLE C4
[0087] A mechanical fastener hook material web was made as in
comparative example 1 except the opening in the die was shaped as
shown in FIG. 14 (after heat treating) and the spacing of the cuts
was 267 microns prior to stretching the web.
EXAMPLE 6
[0088] The web of comparative example C4 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a bank of 3-4500 watt 3 micron wavelength
infrared bulbs at a speed of 10.0 meter/min producing hook members
90 such as shown in FIG. 14. The hook to bulb spacing was
approximately 2.5 cm. The smooth base film side of the web was
supported on a chill roll maintained at approximately 66.degree. C.
The performance of the hook material web against nonwoven loop
material `A` and knitted loop material `B` was measured using a
135.degree. peel test with the results shown in Table 1 below. The
peel force of the heat-treated web using loop material `A` was
approximately 112% greater than the non-heat treated Comparative
Example C4 and 32% greater when using loop material `B`.
COMPARATIVE EXAMPLE C5
[0089] A mechanical fastener hook material web was made as in
Comparative Example 1 except a high density polyethylene resin
(D450 4.5 MI, 0.942 density, Chevron Philips) blended with 2% MB50
silicone/PP masterbatch (Dow Corning) processing aid was used to
form the extrudate at a melt temperature of approximately
238.degree. C. The opening in the die was shaped to produce the
profile 80 depicted in FIG. 12. After quenching the extrudate and
cutting of the ribs the web was oriented in the machine direction
3.5:1.
COMPARATIVE EXAMPLE C6
[0090] A mechanical fastener hook material web, available from the
3M Corporation as KN-3425, was made similar to Comparative Example
1. The dimensions of the hook material are shown in Table 3.
EXAMPLE 7
[0091] The web of Comparative Example C5 was subjected to a
non-contact heat treatment on the hook side of the web by passing
said web underneath a bank of 6-2000 watt 1 micron wavelength
infrared bulbs at a speed of 4.0 meter/min producing hook member
85, substantially as shown in FIG. 13. The hook to bulb spacing was
approximately 1.6 cm. The smooth base film side of the web was
supported on a chill roll maintained at approximately 66.degree. C.
The performance of the hook material web against nonwoven loop
material `A` was measured using a 135.degree. peel test with the
results shown in Table 1 below. The peel force of the heat-treated
web was approximately 151% greater than the non-heat treated
Comparative Example C5.
EXAMPLE 8
[0092] A web was made similar to Comparative Example C3 except the
extrudate was pulled from the die lip at a 20 degree angle from
vertical so as to produce a slightly different cross-sectional
profile. The web was subjected to a non-contact heat treatment on
the hook side of the web by passing said web underneath a
perforated metal plate at a speed of 25.0 meter/min producing hook
members having a profile substantially as shown in FIG. 11. Hot air
at a temperature of approximately 185.degree. C., provided by a 15
kW electric heater, was blown through the perforations in the metal
plate onto the hook side of the web at a velocity of approximately
3350 meter/min. The hooks were approximately 46 cm from the
perforated plate. The smooth base film side of the web was
supported on a chill roll at approximately 149.degree. C. After
heat treatment the web was cooled by passing the web over a chill
roll maintained at 11.degree. C. The dimensions of the resulting
heat-treated hook material are shown in Table 3 below and the peel
performance against low profile loops is shown in Table 4. The peel
force of the heat-treated web was approximately 62% and 60% greater
respectively, for low profile loops `C` and `D`, than the non-heat
treated Comparative Example C6.
EXAMPLE 9
[0093] A web was made similar to Comparative Example C3 except the
extrudate was pulled vertically from the die lip. The web was
subjected to a non-contact heat treatment on the hook side of the
web by passing said web underneath a perforated metal plate at a
speed of 25.0 meter/min producing hook members having a profile
substantially as shown in FIG. 11. Hot air at a temperature of
approximately 185.degree. C., provided by a 15 kW electric heater,
was blown through the perforations in the metal plate onto the hook
side of the web at a velocity of approximately 3350 meter/min. The
hooks were approximately 46 cm from the perforated plate. The
smooth base film side of the web was supported on a chill roll at
approximately 149.degree. C. After heat treatment, the web was
cooled by passing the web over a chill roll maintained at
11.degree. C. The dimensions of the resulting heat-treated hook
material are shown in Table 3 below and the peel performance
against low profile loops is shown in Table 4. The peel force of
the heat-treated web was approximately 140% and 107% greater
respectively, for low profile loops `C` and `D`, than the non-heat
treated Comparative Example C6.
EXAMPLE 10
[0094] A web was made similar to Comparative Example C3 except a
different die plate was used to produce a tapered stem having a
larger width at the base of the stem than at the top of the stem.
The web was subjected to a non-contact heat treatment on the hook
side of the web using the following procedure. A 13 cm.times.43 cm
piece of web was placed onto a 13 cm.times.43 cm steel plate (1.3
cm thick), hook-side up, and edge clamped to prevent the web from
shrinking. Hot air from a Master brand hot air gun at 400.degree.
C. was blown vertically down onto the web by passing the air gun
uniformly over the web for about 10 seconds. The dimensions of the
resulting heat-treated hook material are shown in Table 3 below and
the peel performance against low profile loops is shown in Table 4.
The peel force of the heat-treated web was approximately 321% and
177% greater respectively, for low profile loops `C` and `D`, than
the non-heat treated Comparative Example C6.
EXAMPLE 11
[0095] A web was made similar to the web of Comparative Example C1
except the base of the web was longitudinally stretched at a
stretch ratio of approximately 3.65 to 1 between a first pair of
nip rolls and a second pair of nip rolls to further separate the
individual hook elements to approximately 8.5 hooks/cm. There were
approximately 15 rows of ribs or cut hooks per centimeter. The web
was then subjected to a non-contact heat treatment on the hook side
of the web by passing said web underneath a perforated metal plate
at a speed of 8.9 meter/min producing hook members having a profile
similar to those in Example 9 and shown in FIG. 11. Hot air at a
temperature of approximately 185.degree. C., provided by a 15 kW
electric heater, was blown through the perforations in the metal
plate onto the hook side of the web at a velocity of approximately
3350 meter/min. The hooks were approximately 46 cm from the
perforated plate. The smooth base film side of the web was
supported on a chill roll at approximately 149.degree. C. After
heat treatment the web was cooled by passing the web over a chill
roll maintained at 11.degree. C.
EXAMPLE 12
[0096] A web was made similar to the web of Example 11 except the
web was longitudinally stretched at a stretch ratio of
approximately 2.5 to 1 between a first pair of nip rolls and a
second pair of nip rolls prior to the cutting step to increase
orientation of the web prior to cutting of the ribs. The upper roll
of the first pair of nip rolls was heated to 143.degree. C. to
soften the web prior to stretching. After stretching, the web was
cut as in Example 11 and then longitudinally stretched at a stretch
ratio of approximately 3.65 to 1 between a first pair of nip rolls
and a second pair of nip rolls to further separate the individual
hook elements to approximately 8.5 hooks/cm. The web was then
subjected to a non-contact heat treatment on the hook side of the
web as described in Example 11.
1TABLE 1 Hook Hook Arm Hook Peel Force Peel Force Hook width Height
Droop Thickness Loop `A` Loop `B` Material (.mu.m) (.mu.m) (.mu.m)
(.mu.m) (grams) (grams) C1 536 573 217 340 202 -- 1 663 582 301 85
329 -- 2 682 606 341 179 619 -- C2 479 512 147 309 164 -- 3 703 678
229 133 225 -- C3 395 514 128 274 270 -- 4 483 641 193 171 955 -- 5
481 665 172 180 638 -- C4 611 819 262 257 382 541 6 774 992 399 154
811 716 C5 448 500 143 341 186 -- 7 547 526 174 201 466 --
[0097] Comparative Example C2 and Example 3 were measured to show
the change in molecular orientation and crystallinity due to heat
treatment of the webs of the invention. The results are shown in
Table 2 below. When heat is applied to the oriented hook elements,
the molecular orientation decreases dramatically from the top down
to the base, and crystallinity increases due to annealing
effects.
2TABLE 2 Crystalline % Molecular % Molecular % Molecular Index
Orientation Orientation Orientation Hook Material (top) (top)
(body) (base) C2 0.30 36.3 52.0 85.6 3 0.39 0.0 0.0 80.4
EXAMPLE 13
[0098] To obtain a fastener web having low hook density, a web was
made similar to the web of Example 9 except C104
polypropylene/polyethylene impact copolymer (1.2 MFI, Dow Chemical,
Midland, Mich.) was used as the extrudate. A white color
concentrate (50:50 TiO2/PP) was added to the extruder at a 1%
loading. The web was quenched and cut as in Example 9. The general
profile of the individual hook elements is shown in FIG. 11. The
web was then subjected to a biaxial stretching (2.times.2) using a
KARO 4 pantograph stretcher (Bruckner GmbH). A 115 mm.times.115 mm
sample of the web was preheated at a temperature of 130.degree. C.
for 60 seconds followed by 2.times.2 stretching at a stretch rate
of 100%/second. The hook spacing in the machine direction was
approximately 21.3 hooks/cm and 7 hooks/cm in the cross direction.
The web was then subjected to a non-contact heat treatment on the
hook side of the web using the following procedure. A 13
cm.times.43 cm piece of web was placed onto a 13 cm.times.23 cm
steel plate (1.3 cm thick), hook-side up, and edge clamped to
prevent the web from shrinking. Hot air from a 14.5 amperage Master
brand hot air gun at 400.degree. C. with a vent setting of 50%, was
blown vertically down onto the web by passing the air gun uniformly
over the web for about 20 seconds. The dimensions of the resulting
heat-treated hook material are shown in Table 3 below.
EXAMPLE 14
[0099] To obtain a fastener web having even lower hook density, a
web was made similar to the web of Example 13 except the web was
subjected to a 3.times.3 biaxial stretching using a KARO 4
pantograph stretcher. The hook spacing in the machine direction was
approximately 12.3 hooks/cm and 4.3 hook/cm in the cross direction.
The dimensions of the resulting heat-treated hook material are
shown in Table 3 below.
[0100] Table 3 below shows the effect of non-contact heat treatment
on hook dimensions. Hook thickness decreases dramatically upon the
application of heat to hooks having significant molecular
orientation.
3TABLE 3 Hook Hook Arm Hook Hook width Height Droop Thickness
Hooks/cm Stem Width Stem Width Material (.mu.m) (.mu.m) (.mu.m)
(.mu.m) CD (base) (.mu.m) (top) (.mu.m) C6 521 485 246 343 10 232
231 8 487 511 176 101 14 233 242 9 544 426 136 98 14.2 227 279 10
384 645 112 122 18.9 247 153 11 470 555 113 143 14.7 240 228 12 449
487 117 70 23.8 196 217 13 571 617 135 94 7.0 -- -- 14 607 617 132
113 4.3 -- --
[0101] The thicknesses of the low profile loops `C` and `D` were
determined from scanning electron microscopic (SEM) photos. The
nonwoven diaper backsheets were carefully cut with a razor and SEM
photos were taken of the cross-section. The distance from the
loop/film interface to the top of the loop pile was measured with a
ruler from the photographs and converted to microns. Three
locations were measured for three different replicates. The nine
readings were averaged and are reported below.
[0102] Table 4 below shows that as the ratio of hook arm droop to
loop thickness decreases, the peel force to thin, low profile
nonwoven loops increases dramatically.
4TABLE 4 Loop Thickness Arm Droop/Loop Peel Force Hook (.mu.m)
Thickness Ratio (gms/2.5 cm) Material Loop C Loop D Loop E Loop C
Loop D Loop E Loop C Loop D Loop E C6 133 154 239 1.85 1.6 1.03 78
110 308 8 133 154 239 1.32 1.14 0.74 126 176 409 9 133 154 239 1.02
0.88 0.57 187 228 533 10 133 154 239 0.84 0.73 0.47 328 305 542
[0103] Table 5 below shows the peel force of low hook density
examples 13 and 14 peeled from low profile nonwoven loop `C` using
the 135 Degree Peel Test for Low Profile Loops described above. The
actual number of individual hooks per tab was calculated and then
divided into the peel force to obtain the peel force per individual
hook member.
5TABLE 5 Hook Peel Force Loop # Hooks/ Peel Force/individual
Material `C` (grams/2.54 cm) test tab hook (grams/hook) 13 152 722
0.21 14 116 256 0.51
CONTROL EXAMPLE 15
[0104] A mechanical fastener hook material web was made using the
apparatus shown in FIG. 1. A polyethylene resin (DFDB 6005, 0.2
MFI, 0.92 density, Dow Chemical Corp., Midland, Mich.) pigmented
with 1% TiO.sub.2 color concentrate (15100P, Clariant Corp.,
Minneapolis, Minn.) was extruded with a 6.35 cm single screw
extruder (24:1 L/D) using a barrel temperature profile of
177.degree. C.-232.degree. C.-246.degree. C. and a die temperature
of approximately 235.degree. C. The extrudate was extruded
vertically downward through a die having an opening cut by electron
discharge machining. After being shaped by the die, the extrudate
was quenched in a water tank at a speed of 6.1 meter/min with the
water being maintained at approximately 10.degree. C. The web was
then advanced through a cutting station where the ribs (but not the
base layer) were transversely cut at an angle of 23 degrees
measured from the transverse direction of the web. The spacing of
the cuts was 305 microns. After cutting the ribs, the base of the
web was longitudinally stretched at a stretch ratio of
approximately 3 to 1 between a first pair of nip rolls and a second
pair of nip rolls to further separate the individual hook elements
to approximately 10 hooks/cm. There were approximately 15 rows of
ribs or cut hooks per centimeter. The upper roll of the first pair
of nip rolls was heated to 100.degree. C. to soften the web prior
to stretching. The general profile of this hook is depicted in FIG.
11. The web was then subjected to a non-contact heat treatment on
the hook side of the web using the following procedure. A 13
cm.times.43 cm piece of web was placed onto a 13 cm.times.43 cm
steel plate (1.3 cm thick), hook-side up, and edge clamped to
prevent the web from shrinking. Hot air from a Master brand hot air
gun at 400.degree. C. was blown vertically down onto the web by
passing the air gun uniformly over the web for about 10 seconds.
The width (thickness) of the hooks was measured before and after
heat treating and is shown in Table 6 below.
EXAMPLE 16
[0105] A hook web was made similar to that of Control Example 15
except 50% polypropylene/polyethylene impact copolymer (C104 1.2
MFI, Dow Chemical Corp., Midland, Mich.) was blended with the DFDB
6005 polyethylene resulting in a composition of PE:PP/PE:TiO2
concentrate (15100P) in a ratio of 49.5:49.5:1.0. The web was heat
treated in the same manner as Control Example 15. The decrease in
hook thickness after heat treatment of the blended hook material
was 9.1% greater than the non-blended hook material.
CONTROL EXAMPLE 17
[0106] A hook web was made similar to that of Control Example 15
except 99% polypropylene/polyethylene impact copolymer (C104)
pigmented with 1 % TiO.sub.2 color concentrate (15100P) was used as
the extrudate. The die plate used was described in Example 10. The
spacing of the cuts was 250 microns. The web was heat treated in
the same manner as Control Example 15. The performance of the hook
material web against nonwoven loop material `A` was measured using
a peel test with the results shown in Table 6 below.
EXAMPLE 18
[0107] A hook web was made similar to that of Control Example 17
except 10% SIS block copolymer (KRATON 1119, Kraton Polymers,
Houston, Tex., USA) was blended with the C104 polypropylene
resulting in a composition of PP:SIS:TiO.sub.2 concentrate (15100P)
in a ratio of 89:10:1. The web was heat treated in the same manner
as Control Example 17. The decrease in hook thickness after heat
treatment of the blended hook material was 7.5% greater than the
non-blended hook material. The 135.degree. peel force of the
heat-treated blended web was approximately 68% greater than the
non-blended Control Example 17.
CONTROL EXAMPLE 19
[0108] A hook web was made similar to that of Control Example 15
except 99% polypropylene/polyethylene impact copolymer (SRC-7644,
Dow Chemical Co., Midland, Mich.) pigmented with 1% TiO.sub.2 color
concentrate (15100P) was used as the extrudate and different
cutting conditions were used to produce a thicker hook. The web was
heat treated in the same manner as Control Example 15. The
performance of the hook material web against nonwoven loop material
`A` was measured using a 135.degree. peel test with the results
shown in Table 6 below.
EXAMPLE 20
[0109] A hook web was made similar to that of Control Example 19
except 5% KRATON 1119, 5% FORAL NC tackifier (Hercules Chemical,
Wilmington, Del.) and 1% 15100P TiO.sub.2 was blended with 89%
SRC-7644 polypropylene/polyethylene impact copolymer to form the
extrudate. The web was heat treated in the same manner as Control
Example 15. The decrease in hook thickness after heat treatment of
the blended hook material was 13.4% greater than the non-blended
hook material. The 135.degree. peel force of the heat-treated
blended web was approximately 63% greater than the non-blended
Control Example 19.
EXAMPLE 21
[0110] A hook web was made similar to that of Example 20 except a
precompounded resin blend consisting of 65% 5D45 polypropylene (0.7
g/min MFI, Dow Chemical Co., Midland, Mich.), 35% mineral oil
(Superla White No.31, Chevron Texaco, San Ramon, Calif., USA) and
0.1% Millad 3988 nucleating agent (Milliken Chemical Co., Inman
S.C.) was to form the extrudate. The web was heat treated in the
same manner as Control Example 15. The decrease in hook thickness
after heat treatment of the blended hook material was 69.3%.
EXAMPLE 22
[0111] A hook web was made similar to that of Control Example 17
except a coextrusion process was used to produce a web wherein the
hook rails were foamed and the base film layer was unfoamed. A
blend of 49% C104 copolymer, 49% FH3400 polypropylene and 2%
chemical blowing agent concentrate (FM1307H) was extruded with a
3.8 cm single screw extruder (28:1 L/D) using a "humped" barrel
temperature profile of 135.degree. C.-210.degree. C.-177.degree. C.
to form the hook rails. 100% 7C06 impact copolymer (Union Carbide
Corp., Danbury, Conn.) was used to form the non-foamed base film
layer and was extruded with a 6.35 cm single screw extruder (24:1
L/D) using a sloped barrel profile of 204.degree. C. in the feed
zone to 232.degree. C. in the last zone. The melt streams of the
two extruders were fed to a three layer coextrusion feedblock
(Cloeren Co., Orange, Tex.) with the third layer inlet blocked such
that a two layer output resulted. The feedblock was mounted onto an
extrusion die equipped with a profiled die lip. The feedblock and
die were maintained at 204.degree. C. After being shaped by the die
lip, the extrudate was quenched in a water tank at a speed of 4.6
meter/min with the water being maintained at approximately
16.degree. C.-20.degree. C. The resulting structure had a
non-foamed base film layer with upstanding hook rails that were
foamed approximately 70% of their height as measured from the top
downward towards the base. The resulting structure had a 10%
overall void content. The mean cell size of the foam cells in the
foamed portion was 50 microns. The web was then advanced through a
cutting station where the ribs (but not the base layer) were
transversely cut at an angle of 23 degrees measured from the
transverse direction of the web. The spacing of the cuts was 250
microns. After cutting the ribs, the base of the web was
longitudinally stretched at a stretch ratio of approximately 3 to 1
between a first pair of nip rolls and a second pair of nip rolls to
further separate the individual hook elements to approximately 10
hooks/cm. The upper roll of the first pair of nip rolls was heated
to 100.degree. C. to soften the web prior to stretching. There were
approximately 15 rows of ribs or cut hooks per centimeter. The base
film layer had a thickness of approximately 75 microns. The web was
heat treated in the same manner as Control Example 15. The decrease
in hook thickness after heat treatment of the hook material was
75%. The performance of the hook material web against nonwoven loop
material `B` was measured using a 135.degree. peel test for low
profile loops with the results shown in Table 6 below. The
135.degree. peel force of the heat-treated foamed web was
approximately 82% greater than the non-heat treated foamed web.
6TABLE 6 Heat Peel Peel Initial Treated % Change Force Force Hook
Hook in Hook Loop `A` Loop `B` Hook Thickness Thickness Thickness
(grams/ (grams/ Material (.mu.m) (.mu.m) (.mu.m) 2.5 cm) 2.5 cm)
Control 15 281 144 48.7 16 292 123 57.8 Control 17 254 146 42.4 419
18 254 129 49.5 706 Control 19 330 143 56.6 550 20 330 98 70.0 896
21 336 103 69.3 22 305 76 75 209
* * * * *