U.S. patent application number 10/660935 was filed with the patent office on 2005-02-17 for sheet surface treating and ink-jet printing paper.
This patent application is currently assigned to Hymo Corporation. Invention is credited to Kamada, Osamu, Ono, Motosuke, Sugiyama, Toshiaki.
Application Number | 20050034829 10/660935 |
Document ID | / |
Family ID | 17382690 |
Filed Date | 2005-02-17 |
United States Patent
Application |
20050034829 |
Kind Code |
A1 |
Sugiyama, Toshiaki ; et
al. |
February 17, 2005 |
Sheet surface treating and ink-jet printing paper
Abstract
There is provided a treating agent for a sheet surface
comprising a graft copolymer composed of a back bone polymer and
branch polymer, either of which is a polymer having vinyl alcohol
units, and the other of which is a polymer having cationic groups,
the treating agent is applied onto a pulp sheet or plastic sheet,
and the coated sheet is used in ink jet printing. Cationic groups
are introduced by graft copolymerization using
di(meth)allylamine-based and/or (meth)acryl-based monomer.
Alternatively, the graft copolymer of the present invention is
obtained by grafting N-vinylcarboxylic acid amide monomer followed
by hydrolysis thereof. A formula weight ratio of vinylalcohol units
and the introduced cationic groups of 1:20 to 2:1 is preferable in
terms of balanced performance.
Inventors: |
Sugiyama, Toshiaki; (Tokyo,
JP) ; Ono, Motosuke; (Tokyo, JP) ; Kamada,
Osamu; (Tokyo, JP) |
Correspondence
Address: |
OSTROLENK, FABER, GERB & SOFFEN, LLP
Attorneys at Law
1180 Avenue of the Americas
New York
NY
10036-8403
US
|
Assignee: |
Hymo Corporation
|
Family ID: |
17382690 |
Appl. No.: |
10/660935 |
Filed: |
September 12, 2003 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10660935 |
Sep 12, 2003 |
|
|
|
09508573 |
Mar 13, 2000 |
|
|
|
6669815 |
|
|
|
|
09508573 |
Mar 13, 2000 |
|
|
|
PCT/JP98/04090 |
Sep 10, 1998 |
|
|
|
Current U.S.
Class: |
162/135 ;
162/168.1; 162/168.2 |
Current CPC
Class: |
B41M 5/5245 20130101;
B41M 5/5254 20130101; D21H 17/44 20130101; B41M 5/52 20130101 |
Class at
Publication: |
162/135 ;
162/168.1; 162/168.2 |
International
Class: |
D21H 021/16 |
Foreign Application Data
Date |
Code |
Application Number |
Sep 11, 1997 |
JP |
9-262940 |
Claims
1. A treating agent for a sheet surface, comprising a copolymer
comprising a polymer moiety having vinyl alcohol units and a
polymer moiety having cationic groups, said copolymer being a graft
copolymer in which said respective polymer moieties are a back bone
polymer and a branch polymer, either of which has the vinyl alcohol
units, and the other of which has the cationic groups.
2. A treating agent for a sheet surface according to claim 1,
wherein said back bone polymer of said graft copolymer is derived
from a water-soluble or water-dispersible polymer having vinyl
alcohol units, and said branch polymer is composed of at least one
repeating unit selected from the group consisting of a repeating
unit represented by the following formula (1), a repeating unit
represented by the following formula (2), a repeating unit
represented by the following formula (3) and a repeating unit
represented by the following formula (4): [Formula (1)] 5(wherein,
R.sub.1 and R.sub.2 represent H or CH.sub.3, R.sub.3 and R.sub.4
represent hydrogen, alkyl groups having 1.about.4 carbon atoms or
benzyl groups, and X.sup.- represents a counter ion); [Formula (2)]
6(wherein, A represents O or NH, B represents C.sub.2H.sub.4,
C.sub.3H.sub.6 or C.sub.3H.sub.5OH, R.sub.5 represents H or
CH.sub.3, R.sub.6 and R.sub.7 represent alkyl groups having
1.about.4 carbon atoms, R.sub.8 represents hydrogen, an alkyl group
having 1.about.4 carbon atoms or a benzyl group, and X.sup.-
represents a counter ion); [Formula (3)] 7(wherein, R.sub.9
represents H or CH.sub.3, and X.sup.- represents a counter ion);
and [Formula (4)] 8(wherein, R.sub.10 and R.sub.11 represent H or
CH.sub.3, and X.sup.- represents a counter ion).
3. A treating agent for a sheet surface according to claim 2,
wherein said branch polymer comprises at least one repeating unit
selected from the group consisting of the repeating unit
represented by said formula (1) and the repeating unit represented
by said formula (2).
4. A treating agent for a sheet surface according to claim 3,
wherein said branch polymer comprises the repeating unit
represented by said formula (1) and the repeating unit represented
by said formula (3) and/or the repeating unit represented by said
formula (4).
5. A treating agent for a sheet surface according to claim 2,
wherein said graft copolymer is obtained by radical polymerization
of a monomer composition generating at least one repeating unit
selected from the group consisting of the repeating unit
represented by said formula (1), the repeating unit represented by
said formula (2), the repeating unit represented by said formula
(3), and the repeating unit represented by said formula (4) in the
presence of the water-soluble or water-dispersible polymer having
vinyl alcohol units.
6. A treating agent for a sheet surface according to any one of
claims 2 to 5 wherein, the formula weight ratio of the vinyl
alcohol units of said water-soluble or water-dispersible polymer
having vinyl alcohol units and the cationic groups is from 1:20 to
2:1.
7. A treating agent for a sheet surface according to any one of
claims 2 to 5, wherein the proportion of the vinyl alcohol units
contained in said water-soluble or water-dispersible polymer having
vinyl alcohol units is from 70 mol % to 100 mol %.
8. A treating agent for a sheet surface according to any one of
claims 5 to 7, wherein, in said radical polymerization reaction,
the pH of the reaction system is from 1.0 to 6.0.
9. A treating agent for a sheet surface according to any one of
claims 2 to 8, wherein the degree of polymerization of said
water-soluble or water-dispersible polymer having vinyl alcohol
units is from 100 to 2500.
10. A treating agent for a sheet surface according to any one of
claims 2 to 9, wherein said water-soluble or water-dispersible
polymer having vinyl alcohol units is grafted by 40% or more by
radical polymerization.
11. A treating agent for a sheet surface according to any one of
claims 2 to 10, wherein 10 times weight of methanol is added to a
polymer aqueous solution, in which the concentration of the polymer
mixture after said grafting reaction is 20 wt %, to form
precipitate, and the amount of dry matter of the formed precipitate
is 60 wt % or less of the water-soluble or water-dispersible
polymer having vinyl alcohol units used as raw material.
12. A treating agent for a sheet surface according to any one of
claims 2 to 11, wherein the intrinsic viscosity of said polymer
mixture after grafting reaction in 2% ammonium sulfate aqueous
solution at 25.degree. C. is from 0.1 to 2.0 dl/g.
13. A treating agent for a sheet surface according to any one of
claims 2 to 12, wherein monomer generating the repeating unit
represented by said formula (1) is a salt of diallylamine, a salt
of diallylmonomethylamine, or a salt of diallyldimethylamine.
14. A treating agent for a sheet surface according to any one of
claims 2 to 12, wherein monomer generating the repeating unit
represented by said formula (2) is a salt or quaternary compound of
a dialkylaminoethyl(meth)- acrylate or a salt or quaternary
compound of a dialkylaminopropyl(meth)acr- ylamide.
15. A treating agent for a sheet surface according to anyone of
claims 2, 4 to 12, wherein monomer generating the repeating unit
represented by said formula (3) is N-vinylformamide or
N-vinylacetamide.
16. A treating agent for a sheet surface according to anyone of
claims 2, 4 to 12, wherein monomer generating the repeating unit
represented by said formula (4) is a monomer composition of
N-vinylformamide and acrylonitrile.
17. A treating agent for a sheet surface according to claim 1,
wherein said graft copolymer is a graft copolymer in which vinyl
ester of carboxylic acid is graft copolymerized with a polymer of a
monomer containing N-vinylcarboxylic acid amide or a hydrolysis
product of said polymer as the back bone polymer raw material to
form the branch polymer, and the branch polymer is made to contain
vinyl alcohol units by hydrolyzing the resulting graft
copolymer.
18. A paper for ink jet printing prepared by coating a coating
color comprising the treating agent for a sheet surface according
to any one of claims 1 to 17, a filler, and a binder onto a sheet
surface.
19. A paper for ink jet printing prepared by making a treating
solution comprising the treating agent for a sheet surface
according to any one of claims 1 to 17 penetrate into a sheet
surface.
20. A paper for ink jet printing according to claim 18 or claim 19,
wherein said paper comprises the treating agent for a sheet surface
of 0.02 to 5 g/m.sup.2.
21. (deleted)
Description
TECHNICAL FIELD
[0001] The present invention relates to a treating agent for a
sheet surface and a paper for ink jet printing which is applied
with the treating agent.
BACKGROUND ART
[0002] Ink jet printing is a non-contact printing method that
offers numerous advantages including high-speed printing, printing
at low noise levels, ease of performing color printing, or the
like, and consequently has been rapidly popularized for use in
printers and plotters. Ink jet printing allows printing on ordinary
printing paper, coated paper, PPC paper (paper for plain paper
copy), medium-quality paper and even plastic film.
[0003] As a paper for use in ink jet printing, there is a coated
paper for obtaining a high image quality, which has a coating layer
containing synthetic silica or the like. In contrast, as low-priced
common-use paper, one obtained by penetrate-treating paper with
starch or the like by means of a size press is used. Common-use
paper has the major problem of the occurrence of so-called
feathering when it is printed with an aqueous ink which is used in
the ink jet printing.
[0004] Since the ink used for the ink jet printing is both aqueous
and anionic, a cationic waterproofing agent is applied to the
surface of the paper. Although it is effective to coat or
penetrate-treat paper with a cationic polymer to improve water
resistance, this results in the occurrence of the problem of
decreased color density during printing.
[0005] Various methods have been proposed to inhibit this decrease
in color density, examples of which include a method wherein
nonionic resin fine particles are combined with nonionic, anionic
or cationic water-soluble polymer and coated (Japanese Patent
Laid-Open Publication No. 9-1925), a method wherein emulsion
particles are coated which are synthesized by copolymerization of
acrylonitrile and acrylic esters to increase printing density
(Japanese Patent Laid-Open Publication No. 8-50366), a method
wherein cationic emulsion particles of acrylic esters are coated
(Japanese Patent Laid-Open Publication No. 9-99632), and a method
wherein colloidal silica and a water-soluble polymer are coated for
the purpose of improving dye color development and printing density
(Japanese Patent Laid-Open Publication No. 9-109544).
[0006] However, since all of these methods use water-insoluble fine
particles, they bond weakly with the ink dye for ink jet printing,
and the water-soluble cationic polymer that is used in combination
with them does not demonstrate adequate water resistance.
[0007] In addition, the use of a mixture of polymer having vinyl
alcohol units such as polyvinyl alcohol and a cationic polymer for
ink jet printing paper is known. Polyvinyl alcohol has a good
film-forming ability, and has the effect of inhibiting decreases in
color density. On the other hand, cationic polymers have the effect
of increasing water resistance.
[0008] However, polyvinyl alcohol and cationic polymer have poor
miscibility, and it is difficult to apply their mixture uniformly
in the microscopic state. Consequently, these substances have
shortcomings that include large decreases in color density, thereby
requiring further improvement.
[0009] The use of a copolymer comprising a polymer moiety having
vinyl alcohol units and a polymer moiety having cationic monomer
units for ink jet printing paper as being useful in the present
invention has heretofore been unknown.
[0010] Moreover, due to the considerable increase in viscosity that
occurs when a conventional cationic polymer or the like is mixed
into a coating color, it is necessary to dilute with water at the
time of application. Thus, the polymer concentration is unable to
be increased, and the coated amount of the polymer ends up being
low, which had previously presented a problem. A surface treating
agent that is able to effectively solve the problems of decreased
quality, namely decreased color density, feathering and
insufficient water resistance as mentioned above has yet to be
developed. In addition, the light resistance of printed ink images
or characters is also insufficient.
DISCLOSURE OF THE INVENTION
[0011] An object of the present invention is to provide a treating
agent for a sheet surface that improves water resistance and light
resistance without decreasing color density during printing when
printing with an aqueous ink, for example, one used in ink jet
printing.
[0012] Another object of the present invention is to provide a
treating agent for a sheet surface that prevents the problem of
feathering that particularly occurs with common-use paper for ink
jet printing.
[0013] A further object of the present invention is to provide a
treating agent for a sheet surface that prevents the occurrence of
the considerable increase in viscosity when mixed with coating
colors and can be applied in a sufficient polymer
concentration.
[0014] A still further object of the present invention is to
provide a coated paper for ink jet printing that improves water
resistance and light resistance without decreasing color density
during printing. A still further object of the present invention is
to provide a common-use paper for ink jet printing that prevents
feathering without decreasing color density during printing, and
improves water resistance and light resistance.
[0015] As a result of earnest studies to solve the above-mentioned
problems, the inventors of the present invention found that
miscibility between polyvinyl alcohol and cationic polymers, which
had presented a problem in the prior art, is improved by using a
copolymer comprising a polymer moiety having vinyl alcohol units
and a polymer moiety having cationic groups, especially a graft
copolymer containing vinyl alcohol units for either a back bone
polymer or branch polymers while the other has cationic groups, and
that by treating sheet surface such as paper, offering an excellent
printing without decreasing color density as well as better water
resistance and light resistance than current commercially available
paper, thereby leading to completion of the present invention.
Furthermore, the occurrence of feathering can be prevented
thereby.
[0016] In the preferred embodiments, the copolymer has the polymer
moieties which are a back bone polymer and a branch polymer, and is
a graft copolymer composed of the back bone polymer and branch
polymer, either of which is a polymer having vinyl alcohol units,
and the other of which is a polymer having cationic groups.
[0017] Furthermore, the present invention is to provide the above
described treating agent for a sheet surface, in which the back
bone polymer of the graft copolymer is composed of water-soluble or
water-dispersible polymer having vinyl alcohol units, and the
branch polymer is composed of at least one repeating unit selected
from the group consisting of a repeating unit represented by the
following formula (1), a repeating unit represented by the
following formula (2), a repeating unit represented by the
following formula (3) and a repeating unit represented by the
following formula (4):
[0018] [Formula (1)] 1
[0019] (wherein, R.sub.1 and R.sub.2 represent H or CH.sub.3,
R.sub.3 and R.sub.4 represent hydrogen, alkyl groups having
1.about.4 carbon atoms or benzyl groups, and X.sup.- represents a
counter ion);
[0020] [Formula (2)] 2
[0021] (wherein, A represents O or NH, B represents C.sub.2H.sub.4,
C.sub.3H.sub.6 or C.sub.3H.sub.5OH, R.sub.5 represents H or
CH.sub.3, R.sub.6 and R.sub.7 represent alkyl groups having
1.about.4 carbon atoms, R.sub.8 represents hydrogen, an alkyl group
having 1.about.4 carbon atoms or a benzyl group, and X.sup.-
represents a counter ion);
[0022] [Formula (3)] 3
[0023] (wherein, R.sub.9 represents H or CH.sub.3 and X.sup.-
represents a counter ion); and
[0024] [Formula (4)] 4
[0025] (wherein, R.sub.10 and R.sub.11 represent H or CH.sub.3, and
X.sup.- represents a counter ion).
[0026] In the preferred embodiments, the branch polymer comprises
at least one repeating unit selected from the group consisting of
the repeating unit represented by the formula (1) and the repeating
unit represented by the formula (2). Furthermore, in the preferred
embodiments the branch polymer comprises the repeating unit
represented by the formula (1) and the repeating unit represented
by the formula (3) and/or the repeating unit represented by the
formula (4).
[0027] In addition, in the preferred embodiments, the graft
copolymer can be obtained by radical polymerization of a monomer
composition generating at least one repeating unit selected from
the group consisting of the repeating unit represented by the
formula (1), the repeating unit represented by the formula (2), the
repeating unit represented by the formula (3), and the repeating
unit represented by the formula (4) in the presence of the
water-soluble or water-dispersible polymer having vinyl alcohol
units.
[0028] Furthermore, in the preferred embodiments, the formula
weight ratio of vinyl alcohol units of the water-soluble or
water-dispersible polymer having vinyl alcohol units and the
cationic groups is from 1:20 to 2:1.
[0029] Still further, the proportion of vinyl alcohol units
contained in the water-soluble or water-dispersible polymer having
vinyl alcohol units is preferably from 70 mol % to 100 mol %.
[0030] In the radical polymerization reaction, the pH of the
reaction system may be preferably from 1.0 to 6.0.
[0031] Furthermore, the degree of polymerization of the
water-soluble or water-dispersible polymer having vinyl alcohol
units may be preferably from 100 to 2500.
[0032] Further, in the preferred embodiments, the water-soluble or
water-dispersible polymer having vinyl alcohol units may be grafted
by 40% or more by radical polymerization.
[0033] In addition, 10 times weight of methanol is added to a
polymer aqueous solution in which the concentration of the polymer
mixture after the grafting reaction is 20 wt %, to form
precipitate, and the amount of dry matter of the formed precipitate
may be preferably 60 wt % or less of the water-soluble or
water-dispersible polymer having vinyl alcohol units used as raw
material.
[0034] Further, the intrinsic viscosity of the polymer mixture
after grafting reaction in 2% aqueous ammonium sulfate solution at
25.degree. C. may preferably be from 0.1 to 2.0 dl/g.
[0035] Still further, monomer generating the repeating unit
represented by the formula (1) may preferably be a salt of
diallylamine, a salt of diallylmonomethylamine, or a salt of
diallyldimethylamine.
[0036] In addition, monomer generating the repeating unit
represented by the formula (2) may preferably be a salt or
quaternary compound of a dialkylaminoethyl(meth)acrylate or a salt
or quaternary compound of a dialkylaminopropyl(meth)acrylamide.
[0037] In addition, in the preferred embodiments monomer generating
the repeating unit represented by the formula (3) is
N-vinylformamide or N-vinylacetamide.
[0038] Furthermore, monomer generating the repeating unit
represented by the formula (4) may preferably be a monomer
composition of N-vinylformamide and acrylonitrile.
[0039] Still further, the present invention is to provide the above
treating agent for a sheet surface, in which the graft copolymer is
a graft copolymer in which vinyl ester of carboxylic acid is graft
copolymerized with a polymer of a monomer containing
N-vinylcarboxylic acid amide or a hydrolysis product of the polymer
as the back bone polymer raw material to form the branch polymer,
and the branch polymer is made to contain vinyl alcohol units by
hydrolyzing the resulting graft copolymer.
[0040] Furthermore, the present invention is to provide a paper for
ink jet printing prepared by coating a coating color comprising the
above described treating agent for a sheet surface, a filler, and a
binder onto a sheet surface.
[0041] Further, the present invention is to provide a paper for ink
jet printing prepared by making a treating solution comprising the
above mentioned treating agent for a sheet surface penetrate into a
sheet surface.
[0042] Furthermore, the paper preferably comprises the treating
agent for a sheet surface of 0.02 to 5 g/m.sup.2.
BEST MODE FOR CARRYING OUT THE INVENTION
[0043] The present invention is described in detail
hereinafter.
[0044] The treating agent for a sheet surface according to the
present invention comprises a copolymer comprising a polymer moiety
having vinyl alcohol units and a polymer moiety having cationic
groups. Examples of such a copolymer include a block copolymer, a
graft copolymer or the like.
[0045] Especially, a graft copolymer in which the polymer moieties
are a back bone polymer and branch polymers, either the back bone
polymer or branch polymer is a polymer having vinyl alcohol units,
and the other is a polymer having cationic groups, may be
preferably used for the treating agent for a sheet surface
according to the present invention. Particularly, a graft copolymer
having vinyl alcohol units for its back bone polymer may be
preferably used. The graft copolymer of the present invention can
be obtained by grafting monomers having a structure necessary on a
water-soluble or water-dispersible polymer having vinyl alcohol
units or by following hydrolysis.
[0046] The water-soluble or water-dispersible polymer containing
vinyl alcohol units that serves as the raw material of the present
invention may be preferably obtained by alkaline hydrolysis of a
homopolymer of vinyl ester of carboxylic acid, or a copolymer of a
vinyl ester of carboxylic acid with copolymerizable monomers. Since
polyvinyl alcohol, a hydrolysis product of polyvinyl acetate, is
widely used in practical terms, polyvinyl alcohol that is a
hydrolysis product of polyvinyl acetate may be most preferably used
in the present invention as well.
[0047] Examples of vinyl esters of carboxylic acids include vinyl
formate, vinyl acetate, vinyl propionate, vinyl butyrate and vinyl
benzoate.
[0048] In addition, typical examples of the above-mentioned
copolymerizable monomers include nonionic, cationic or anionic
monomers such as ethylene, styrene, salts or quaternary compounds
of dimethylaminopropyl(meth)acrylamide, salts or quaternary
compounds of diallylamine, N-vinylformamide, N-vinylacetamide,
vinylsulfonate, acrylamido-2-methyl-propanesulfonate, (meth)acrylic
acid, itaconic acid, dimethylacrylamide and
N-isopropylacrylamide.
[0049] Vinyl alcohol units are typically formed within the polymer
by alkaline hydrolysis of a homopolymer or copolymer of these
monomers.
[0050] In the present invention, the vinyl alcohol units in the
water-soluble or water-dispersible polymer having vinyl alcohol
units are preferably 70.about.100 mol %, more preferably
85.about.100 mol %, and are considered to become the back bone
polymer of the graft copolymer. In the case the vinyl alcohol units
are outside this range, the grafting rate decreases, thereby
preventing the object of the present invention from being
achieved.
[0051] The degree of polymerization of the water-soluble or
water-dispersible polymer having vinyl alcohol units such as
polyvinyl alcohol is preferably 100 to 2500, and more preferably
300 to 2000, and a polymer having an arbitrary degree of
polymerization can be used according to the objective.
[0052] It is preferable that the branch polymers of the graft
copolymer contain cationic repeating units represented by the
above-mentioned formula (1), formula (2), formula (3), or formula
(4). These repeating units may be present in the branch polymers
either alone or a plurality of kinds thereof simultaneously.
[0053] In the present invention, a graft copolymer composed of a
polymer moiety having vinyl alcohol units and a polymer moiety
having cationic groups can be realized by polymerizing monomer
composition generating the cationic repeating units represented by
the above-mentioned formula (1) and/or formula (2) in the presence
of the water-soluble or water-dispersible polymer having vinyl
alcohol units that serves as the back bone polymer.
[0054] In addition, a monomer composition comprising a monomer
generating the repeating unit represented by the above mentioned
formula (1) and a monomer generating the repeating unit represented
by the above mentioned formula (3) and/or a monomer generating the
repeating unit represented by the above mentioned formula (4) can
be used as a monomer composition in the present invention. By
forming the branch polymer of these monomers followed by alkali or
acid hydrolyzing it, a graft copolymer of the present invention can
be obtained, which is introduced with the repeating units
represented by the above mentioned formulas (1) and (3) and/or
(4).
[0055] A graft copolymer having as its branch polymers cationic
repeating units represented by the above-mentioned formulas (3) or
(4) can be obtained by graft copolymerizing N-vinylcarboxylic acid
amide monomer or a monomer composition of N-vinylcarboxylic acid
amide monomer and acrylonitrile instead of the repeating units
represented by the formula (1) or formula (2) to the
above-mentioned water-soluble or water-dispersible polymer having
vinyl alcohol units, followed by hydrolysis thereof.
[0056] In this system, however, three types of polymers present in
the form of a mixture, namely polymer of cationic monomer that have
not been graft polymerized, the above-mentioned ungrafted
water-soluble or water-dispersible polymers having vinyl alcohol
units, and the formed graft copolymer. The present invention
effectively demonstrates prevention of feathering and improvement
of water resistance even this mixture is used as a treating agent
for a sheet surface.
[0057] The graft copolymer demonstrates good effects as a treating
agent for a sheet surface even if it is not isolated, but rather in
the state of a mixture with the polymers. Thus, in this case, a
complex isolation process is not required thereby further enhancing
the practical value of the present invention with respect to
decreased production cost and so forth.
[0058] The treating agent for a sheet surface of the present
invention can be prepared by radical polymerizing
di(meth)allylamine-based monomers generating the repeating unit
represented by the above-mentioned formula (1) and/or (meth)
acrylic cationic monomers generating the repeating unit represented
by the above-mentioned formula (2) after dissolving or dispersing
water-soluble or water-dispersible polymer having vinyl alcohol
units in an aqueous medium.
[0059] Examples of di (meth) allylamine-based monomers generating
the repeating unit represented by the above-mentioned formula (1)
referred to here include salts of di(meth)allylamine, salts or
quaternary compounds of di(meth)allylmonoalkylamines, and salts or
quaternary compounds of di (meth)allylbenzylamines. Examples of
salts referred to here include hydrochlorides, sulfates and
acetates. Examples of quaternary amine compounds include quaternary
compounds with methylhalides or benzylhalides.
[0060] Preferred examples include hydrochlorides, sulfates,
acetates and quaternary compounds from diallylamine,
diallylmonomethylamine, or diallylbenzylamine with
methylhalides.
[0061] Specific examples of these compounds include
monomethylbenzyldiallylammonium chloride, dimethyldiallylammonium
chloride, diallylamine hydrochloride, diallylamine sulfate and
diallylamine acetate, while dimethyldiallylammonium chloride is
particularly preferable.
[0062] In addition, specific examples of (meth)acrylic cationic
monomers generating the repeating unit represented by the
above-mentioned formula (2) referred to here include salts or
quaternary compounds of dialkylaminoethyl (meth) acrylate and salts
or quaternary compounds of dialkylaminopropyl(meth)acrylamides.
Examples of salts referred to here include hydrochlorides, sulfates
and acetates. Examples of quaternary amine compounds include
quaternary compounds with methylhalides and benzylhalides.
[0063] Specific examples of these compounds that are particularly
preferable include quaternary ammonium salts such as
(meth)acryloyloxyethyldimethylbenzylammonium chloride,
(meth)acryloyloxyethyltrimethylammonium chloride,
(meth)acryloylaminoprop- yldimethylbenzylammonium chloride and
(meth)acryloylaminopropyltrimethylam- monium chloride, while
dimethylaminoethyl(meth)acrylate salts, such as hydrochlorides,
sulfates and acetates, as well as dimethylaminopropyl (meth)
acrylamide salts, such as hydrochlorides, sulfates and acetates,
can be used preferably.
[0064] Furthermore, the repeating units represented by these
formulas (1) and/or (2) maybe introduced from alone or a mixture of
a plurality of kinds of monomers.
[0065] Together with the above-mentioned cationic monomers,
nonionic types of vinyl monomers can also be copolymerized.
[0066] In addition, cationic repeating units represented by the
above-mentioned formula (3) can be introduced by graft
copolymerizing N-vinylcarboxylic acid amide to water-soluble or
water-dispersible polymer having vinyl alcohol units using a
similar preparative method followed by hydrolysis thereof. On the
other hand, cationic repeating units represented by the
above-mentioned formula (4) can also be introduced by graft
copolymerizing N-vinylcarboxylic acid amide and acrylonitrile to
water-soluble or water-dispersible polymer having vinyl alcohol
units using a similar preparative method followed by hydrolysis
thereof. N-vinylacetamide or N-vinylformamide can be used for the
N-vinylcarboxylic acid amide. Further, in the above graft
copolymerization, the monomer generating the repeating unit
represented by the above mentioned formula (1) can be graft
copolymerized because of its hydrolysis resistance.
[0067] The grafting rate of graft copolymers can be analyzed by
nuclear magnetic resonance or infrared spectroscopy. In addition,
the weight ratio of methanol insoluble matter to the charged amount
of raw material polymer can be used as an indicator of the grafting
rate of the back bone polymer by utilizing the property in which
the solubility in methanol of the back bone polymer increases as a
result of grafting.
[0068] Namely, as grafting proceeds, the raw material polymer that
has become highly cationic also becomes soluble in methanol and is
filtered out. The weakly cationic grafted polymer becomes insoluble
in methanol and is measured. Thus, the difference between the
charged amount of raw material polymer and the amount of insoluble
matter is the amount of grafted polymer that has become highly
cationic, and is considered to indicate the minimum value of the
grafting rate of the raw material polymer.
[0069] More specifically, 10 times weight of methanol is added to a
polymer aqueous solution in which the concentration of polymer
mixture after performing the polymerization procedure of the
present invention (concentration calculated from the sum of the
amount of polymer such as polyvinyl alcohol charged as raw material
and the amount of charged monomers for graft copolymerization) is
20 wt %. The formed precipitate is filtered with No. 5B filter
paper and dried to a constant weight at 105.degree. C. to determine
the amount of insoluble matter. The weight ratio is then determined
between this amount of insoluble matter and the amount of charged
polymer (such as polyvinyl alcohol).
[0070] In the present invention, it is preferable that the amount
of insoluble matter be 60 wt % or less.
[0071] Namely, it is preferable that at least 40% of back bone
polymer charged as raw material be grafted.
[0072] Since homopolymers of cationic monomers are also soluble in
methanol, this assay method is only valid as an indicator of
grafting rate of the back bone polymer.
[0073] If a method is developed for determining the grafting rate
of the cationic monomers as well, it would be possible to more
specifically stipulate the desirable composition of graft
copolymer, the findings of the inventors of the present invention
only apply to the grafting ratio of the back bone polymer.
[0074] The formula weight ratio of the vinyl alcohol units of
water-soluble or water-dispersible polymer having vinyl alcohol
units serving as raw material in the present invention and the
above-mentioned cationic groups is selected from the range of 1:20
to 2:1. This range is preferably 1:20 to 1:1, and most preferably
1:20 to 1:2. Graft copolymer produced within this range is
particularly preferable as a treating agent for a sheet
surface.
[0075] If the amount of water-soluble or water-dispersible polymer
having vinyl alcohol units is less than 4.7 formula wt %, the
effect on color density is too large, making it unsuitable for use
as a treating agent for a sheet surface. If the amount of the
above-mentioned cationic groups is less than 33 formula wt %, it is
not practical as a result of low water resistance.
[0076] Graft copolymerization is carried out in a monomer solution
in the presence of water-soluble or water-dispersible polymer
having vinyl alcohol units in an aqueous medium. Although water
alone is preferably used as the aqueous medium, organic solvents
which mix uniformly with water, such as dimethylsulfoxide, ethanol
and N-methylpyrrolidone, may also be mixed with water.
[0077] For the polymerization method, the entire amount of monomer
is charged into a polymerization vessel in the presence of
water-soluble or water-dispersible polymer having vinyl alcohol
units followed by initiation of polymerization, or a portion of the
monomer is charged into the polymerization vessel, and remaining
monomer is then charged according to the progress of polymerization
after initiating polymerization. Either method may be suitably
employed.
[0078] The water-soluble or water-dispersible polymer having vinyl
alcohol units to serve as the back bone polymer is present in the
polymerization system in the dissolved or dispersed state at a
concentration of 2 to 25 wt %, while monomer to be grafted is
present in the polymerization system at a monomer concentration of
5 to 60 wt %. Cationic monomer is then graft copolymerized to the
back bone polymer by solution polymerization, reverse phase
emulsion polymerization, reverse phase suspension polymerization
and so forth, and particularly preferably by aqueous solution
polymerization.
[0079] In addition, a graft copolymer can be obtained and used in a
similar application, where the graft copolymer has a polymer
structure having cationic groups for the back bone polymer, and a
polymer structure having vinyl alcohol units for the branch
polymers, by graft copolymerizing a vinyl ester of carboxylic acid
such as vinylacetate for composing the branch polymers with a
(co)polymer containing N-vinylcarboxylic acid amide and/or
hydrolysis product of the (co)polymer as back bone polymer,
followed by hydrolysis thereof.
[0080] The graft copolymerization of the present invention can be
performed by polymerizing under the above-mentioned conditions
using an ordinary radical generator.
[0081] Examples of ordinary radical generators that are used
preferably include azo-based initiators such as
2-2'-azobis-2-amidinopropane.multido- t.2 hydrochloride, sodium
4,4'-azobis-4-cyanovalerate and
2,2'-azobis-N,N'-dimethyleneisobutylamidine.multidot.2
hydrochloride.
[0082] In addition, in place of the use of these azo-based
initiators, oxidizing initiators such as tetravalent cerium
compounds or redox-type initiators in the manner of a combination
of ammonium persulfate and sodium hydrogen sulfite can be either
used in The amount of polymerization initiator used is normally
about 100 to 10,000 ppm relative to the amount of monomers.
[0083] If there is necessity to adjust molecular weight of polymer,
it is performed by using a general chain transfer agent such as
alcohols such as methanol, ethanol or isopropanol, or
sulfur-containing compounds such as 2-mercaptoethanol. The amount
used thereof is 0.1 to 200 wt % relative to the amount of monomers
in the case of alcohols, and 0.01 to 10 wt % relative to the amount
of monomers in the case of 2-mercaptoethanol.
[0084] The polymerization reaction is typically carried out at a
temperature of 10.degree. C. to 100.degree. C., and preferably
30.degree. C. to 80.degree. C., and within a pH range of 1.0 to
6.0, and particularly preferably pH 2.0 to 5.0 after removing
oxygen gas from the system. If the polymerization reaction is
carried out at a pH outside the above range, grafting reaction does
not proceed thereby preventing the object of the present invention
from being achieved.
[0085] The polymer mixture obtained by the graft copolymerization
having an intrinsic viscosity at 25.degree. C. in 2% ammonium
sulfate aqueous solution of 0.1 to 2.0 dl/g is preferable as a
treating agent for a sheet surface, while that having an intrinsic
viscosity of 0.2 to 0.5 dl/g is particularly preferable. If the
viscosity is outside the above range, it does not fall within the
suitable viscosity range during treating, thereby preventing the
obtaining of good treating.
[0086] Examples of sheets to be treated with the treating agent for
a sheet surface of the present invention include pulp sheet such as
high-quality paper, medium-quality paper, paper board, synthetic
paper and plastic sheet. It is also applicable to a composite sheet
comprising paper and synthetic paper, or the like.
[0087] The treating agent for a sheet surface according to the
present invention can be applied in other printing method using a
similar aqueous ink like the ink jet printing.
[0088] The amount in the case of treating a paper surface with the
treating agent of the present invention should be determined by
taking into consideration the required properties. In general, the
applied polymer content of the treating agent is within the range
of 0.02 to 5 g/m.sup.2. In the case of coated paper, the paper for
ink jet printing according to the present invention can be produced
by preparing a coating color composed of fillers, binders and the
treating agent for a sheet surface of the present invention and
coating a sheet surface with the coating color. In the case of
common-use paper, the paper for ink jet printing according to the
present invention can be produced by penetrate treating a sheet
surface with the treating agent for a sheet surface of the present
invention alone or in combination with oxidized starch, polyvinyl
alcohol or surface sizing agent and so forth.
[0089] The treating agent for a sheet surface according to the
present invention can be used in combination with other coating
agents, examples of which include ink charge neutralizing
substances such as cationic surface active agents, polycondensed
aluminum ions and polycondensed cationic polymers, water-soluble
polymers and latex such as oxidized starch, cationic starch,
modified starch and polyvinyl alcohol, and coating pigments or
fillers for ink jet printing such as fine synthetic silica,
alumina, talc, kaolin clay and calcium carbonate.
[0090] The paper for ink jet printing according to the present
invention can be obtained by treating a sheet surface with the
treating agent for a sheet surface according to the present
invention alone or a treating solution of the mixture of the
treating agent of the present invention with other coating agents
by use of a size press, a gate roll coater or a blade coater and so
forth.
[0091] The treating agent for a sheet surface of the present
invention can be obtained that is composed of a graft copolymer
comprising a back bone polymer (main chain) and branch polymers
(side chains), with one having a polymer structure having vinyl
alcohol units, while the other has a polymer structure having
cationic groups. Generally polyvinyl alcohol and cationic polymer
have a low level of miscibility with each other. On the other hand,
the roles of both differ when used as a treating agent for an ink
jet printing paper. The cationic polymer increases water
resistance, while the polyvinyl alcohol demonstrates the effect of
preventing a decrease in color density. Although both components
cannot be coated onto a paper surface as a uniform phase when in
the form of a simple mixture, in the presence of the graft
copolymer of the present invention, since the graft copolymer
itself is a uniform phase, especially in a case where a
water-soluble or water-dispersible binder like polyvinyl alcohol is
used as a binder, it improves the miscibility of the binder and
cationic polymer, thereby enabling various types of polymers to be
applied to a paper surface in a uniform state.
[0092] Moreover, the treating agent for a sheet surface of the
present invention is recognized to have an effect that prevents
increases in viscosity of a coating color during mixing, thereby
contributing to performance by allowing a large amount of polymer
to be coated onto the paper. The effect of preventing increases in
viscosity of a coating color is also surmised to be the result of
improved miscibility between the polyvinyl alcohol and cationic
polymer components. In this manner, as a result of having the
characteristic of allowing uniform coating of a large amount of
polymer, the paper for ink jet printing coated with the present
graft copolymer can be given desirable properties.
[0093] Embodiments
[0094] Although the following provides a detailed explanation of
the present invention according to its embodiments, the present
invention is not limited to the following embodiments provided its
gist is not exceeded.
SYNTHESIS EXAMPLE-1
[0095] 52.2 g of a 23% aqueous solution of polyvinyl alcohol
(abbreviated as PVA) (trade name: PVA205 (saponification index:
88%, degree of polymerization: 500) manufactured by Kurare Co.),
166 g of dimethyldiallylammonium chloride (DADMAC, concentration
65%, manufactured by Daiso Co.) (abbreviated as DDMC) and 44.6 g of
deionized water were added to a 500 ml four-neck flask equipped
with a thermometer, stirrer, nitrogen feed tube and condenser,
after which the pH of the raw material mixed liquid was adjusted to
3.5 with 2.4 g of 10% aqueous sulfuric acid, and the monomer
concentration was adjusted to 40.8%.
[0096] Nitrogen replacement was performed for 30 minutes while
stirring the raw material mixture and maintaining the temperature
at 60.degree. C. After then, 5.4 g (0.5 wt % per monomer) of a 10%
aqueous solution of polymerization initiator V-50
(2,2'-azobis-amidinopropane dihydrochloride: manufactured by Wako
Pure Chemical Industries Co.) were added to start
polymerization.
[0097] After maintaining the temperature at 60.degree. C. for 4
hours, 0.2 wt % per monomer of polymerization initiator V-50 was
further added, and the reaction continued for 8 hours after its
initiation. After cooling, 130 g of deionized water were added to
being the total amount to 400 g and obtain a uniform reaction
product. The polymer concentration as determined from the total of
PVA and DDMC was 30%. This polymer mixture was designated as
Sample-1.
[0098] The cation equivalent value of the Sample-1 (pure polymer
content) was measured by colloidal titration. At this time, the
formula weight ratio of hydroxyl groups as determined from the
saponification index of PVA and cation groups as determined by
colloidal titration was 26:74.
[0099] In addition, the intrinsic viscosity of the Sample--1 at
25.degree. C. in 2% ammonium sulfate aqueous solution was
measured.
[0100] In addition, after removing 3.6 g of a 20% solution thereof,
36.0 g of methanol were added to form precipitate. The insoluble
precipitate that formed at this time was filtered with No. 5B
filter paper. After drying it for 1 hour at 105.degree. C., the
dried precipitate was weighed to calculate the weight ratio (%
insoluble matter) of methanol-insoluble matter relative to the
polyvinyl alcohol charged as raw material.
[0101] Polymer properties are shown in Table 1.
SYNTHESIS EXAMPLES-2
[0102] The same polymerization procedure as the Synthesis Example-1
was performed except for using the charged amounts of PVA205 and
DDMC shown in Table 1 to obtain Samples-2.
[0103] The properties of the polymer are shown in Table 1.
SYNTHESIS EXAMPLES-3, 4
[0104] The same polymerization procedures as the Synthesis
Example-1 were performed except for using PVA105 (saponification
index: 98%, degree of polymerization: 500) manufactured by Kurare
Co. as polyvinyl alcohol and using the charged amounts of PVA105
and DDMC shown in Table 1 to obtain Samples-3 and 4.
[0105] The properties of these polymers are shown in Table 1.
COMPARATIVE SYNTHESIS EXAMPLE-1
[0106] Polymerization of DDMC was performed according to the same
procedure as the Synthesis Example-1 without adding PVA to obtain
polydimethyldiallylammonium chloride (P-DDMC), and a polymer
mixture obtained by mixing an equal amount of PVA as that used in
the Synthesis Example-1 with the P-DDMC was designated as
Comparative Sample-1. The Comparative Sample-1 separated into 2
phases, and again separated into 2 phases within 1 day even after
mixed with a homogenizer.
[0107] The cation equivalent value, the intrinsic viscosity, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Comparative Sample-1 were measured in accordance with the
same procedure as Synthesis Example-1. Polymer properties are shown
in Table 1.
[0108] Furthermore, a polymer mixture obtained by mixing an equal
amount of the Sample-1 with the Comparative Sample-1 did not
separate into 2 phases and was designated as Mixed Sample-1
according to the present invention.
COMPARATIVE SYNTHESIS EXAMPLES-2.about.4
[0109] The same polymerization procedures as the Comparative
Synthesis Example-1 were performed using the charged amounts of PVA
and P-DDMC shown in Table 1 to obtain Comparative
Samples-2.about.4.
[0110] The properties of these polymers are shown in Table 1.
1TABLE 1 Formula Cationic weight ratio Equivalent Intrinsic
Insoluble Name of Kind of VA:Cationic Value Viscosity Matter Sample
PVA Monomer Group (meq/g) (g/dl) (%) Sample-1 PVA205 DDMC 26:74
5.57 0.39 25 Sample-2 PVA205 DDMC 33:67 5.37 0.20 40 Sample-3
PVA105 DDMC 21:79 5.70 0.30 10 Sample-4 PVA105 DDMC 50:50 4.71 0.51
50 Comparative PVA205 DDMC 26:74 5.57 0.40 100 Sample-1 Comparative
PVA205 DDMC 33:67 5.37 0.21 100 Sample-2 Comparative PVA105 DDMC
21:79 5.70 0.30 100 Sample-3 Comparative PVA105 DDMC 50:50 4.71
0.50 100 Sample-4 DDMC: dimethyldiallylammonium chloride VA:
vinylalcohol units
EXAMPLES 1.about.5
COMPARATIVE EXAMPLES 1.about.5
[0111] (Application of treating agent for a sheet surface)
[0112] Synthetic powdered silica (Nipseal HD-2, manufactured by
Nippon Silica Kogyo Co.), polyvinyl alcohol (PVA105 (saponification
index: 98%, degree of polymerization: 500) manufactured by Kurare
Co.), the treating agents for a sheet surface (Samples-1.about.4 or
Comparative Samples-1.about.4) were mixed in the proportion of a
weight ratio of 50:45:5 to prepare coating colors having a
concentration of 25%.
[0113] After coating 8.0 g/m.sup.2 (Sample and Comparative Sample
polymer amount of 0.4 g/m.sup.2) of these coating colors onto
commercially available PPC papers (Stoeckigt sizing degree: approx.
20 seconds) using a wire bar (PDSO4, manufactured by Wavestar Co.),
the coated papers were dried for 2 minutes at 105.degree. C. and
then used in printing and later testing.
[0114] (Printing of Test Paper and Measurement of Water and Light
Resistance)
[0115] Cyan, magenta, yellow and black patterns and characters were
printed on the coated test papers using the BJC-600J ink jet
printer manufactured by Canon Co.
[0116] Color densities after printing were measured with an NR-3000
calorimeter (manufactured by Nihon Denshoku Co.) indicating as L*,
a* and b*. Cyan was evaluated with the value of -b*, magenta with
the value of a*, yellow with the value of b* and black with the
value of L*.
[0117] Changes in color densities before and after water resistance
and light resistance tests were measured using an RD-918 Macbeth
reflection densitometer.
[0118] The water resistance test was performed by measuring color
density before and after immersing a solid-printed test piece in
deionized water (flowing water) moving at 300 ml/min for 10
minutes, and then calculating the rate A, B and C of residual
color. A: not changed, B: slightly blurred, C: significantly
blurred
[0119] The light resistance test was conducted by illuminating a
solid-printed test piece for 40 hours at an illumination intensity
of 500 W/m.sup.2, wavelength of 300.about.800 nm and temperature of
50.degree. C. using a light resistance tester (manufactured by
Shimadzu Co., XS-180CPS), measuring the color density before and
after illumination, and calculating the rate A, B and C of residual
color. A: not changed, B: slightly faded, C: faded.
[0120] The results of each measurement are shown in Table 2.
2 TABLE 2 Water Light Color Density Resistance Resistance C M Y B
Name of Sample C M Y B C M Y B (-b*) (a*) (b*) (L*) Example 1 Mixed
Sample-1 A B A A A B A A 43.1 64.1 75.0 33.5 Example 2 Sample-1 A B
A A A B A A 43.4 64.0 75.1 33.0 Example 3 Sample-2 A B A A A B A A
43.2 64.4 75.8 33.5 Example 4 Sample-3 A B A A A B A A 43.1 64.0
75.9 33.0 Example 5 Sample-4 A B A A A B A A 44.1 63.8 75.5 33.2
Comparative Comparative B C A B A C A A 42.3 63.0 73.2 35.4 Example
1 Sample-1 Comparative Comparative B C A B A C A A 42.6 63.7 73.0
35.0 Example 2 Sample-2 Comparative Comparative B C A B A C A A
39.5 62.1 72.0 35.5 Example 3 Sample-3 Comparative Comparative B C
A B A C A A 44.2 64.0 73.5 34.6 Example 4 Sample-4 Comparative
Comparative A B A A A B A A 33.8 49.0 52.3 27.5 Example 5 Sample-1*
C: cyan, M: magenta, Y: yellow, B: black *Coating color having a
concentration of 25% was prepared by mixing synthetic silica,
polyvinyl alcohol, and Comparative Sample-1 in a weight ratio of
50:45:10.
SYNTHESIS EXAMPLES-5.about.8
[0121] A 23% aqueous solution of polyvinyl alcohol (abbreviated as
PVA) (trade name: PVA117 (saponification index: 98%, degree of
polymerization: 1700) manufactured by Kurare Co.) and monomers
having the compositions described in Table 3 were charged into a
500 ml four-neck flask equipped with a thermometer, stirrer,
nitrogen feed tube and condenser, after which the pH was adjusted
to 3.5 and the monomer concentration was adjusted to 20% by
addition of deionized water. Nitrogen replacement within the system
was performed for 30 minutes while stirring the raw material
mixture and maintaining the temperature at 60.degree. C. Next, 0.3
wt % (permonomer) of ammonium peroxodisulfate and 0.01 wt % (per
monomer) of sodium hydrogen sulfite were added to initiate
polymerization. The reaction was allowed to continue for 4 hours
while maintaining the reaction system at 60 and then cooled to
obtain a uniform product. These polymer mixtures were designated as
Samples-5.about.8.
[0122] The cation equivalent values, the intrinsic viscosities, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Samples-5.about.8 were measured by the same procedures as
the Synthesis Example-1. Polymer properties are shown in Table
3.
COMPARATIVE SYNTHESIS EXAMPLES-5.about.8
[0123] With the exception of polymerizing at the pH values
described in Table 3, monomers were polymerized using the same
procedure as the Synthesis Examples-5.about.8 to obtain Comparative
Samples-5.about.8. The pH values thereof were adjusted with
hydrochloric acid and sodium hydroxide.
[0124] The Comparative Samples-5.about.8 separated into 2phases,
and again separated into 2 phases within 1 day even when mixed with
a homogenizer.
[0125] The cation equivalent values, the intrinsic viscosities, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Comparative Samples-5.about.8 were measured by the same
procedures as the Synthesis Example-1. Polymer properties are shown
in Table 3.
3TABLE 3 Formula Cationic weight ratio Equivalent Intrinsic
Insoluble Name of VA:Cationic Kind of Polymerization Value
Viscosity Matter Sample Group Monomer pH (meq/g) (g/dl) (%)
Sample-5 25:75 DAMC 2.5 4.70 0.39 35 Sample-6 25:75 DPMC 3.5 4.50
0.39 20 Sample-7 25:75 DABC 3.5 3.50 0.41 10 Sample-8 25:75 DPBC
4.5 3.30 0.42 44 Comparative 25:75 DAMC 0.0 4.70 0.40 99 Sample-5
Comparative 25:75 DPMC 7.0 4.50 0.41 99 Sample-6 Comparative 25:75
DABC 0.5 3.50 0.42 98 Sample-7 Comparative 25:75 DPBC 6.5 3.30 0.39
98 Sample-8 DAMC: acryloyloxyethyltrimethylammonium chloride DPMC:
acryloylaminopropyltrimethylammonium chloride DABC:
acryloyloxyethylbenzyldimethylammonium chloride DPBC:
acryloylaminopropylbenzyldimethylammonium chloride VA: vinylalcohol
units
EXAMPLE-6.about.9
COMPARATIVE EXAMPLE-6.about.9
[0126] (Evaluation Test for Treating Agent for a Sheet Surface)
[0127] Polyvinyl alcohol (trade name: PVA105 (saponification index:
98%, degree of polymerization: 500) manufactured by Kurare Co.),
oxidized starch (Ace C, manufactured by Oji Cornstarch Co.) and
treating agents (Samples--5.about.8, Comparative
Samples--5.about.8) were mixed in a weight ratio of 0.3:2.7:1 and
coated and immersed in the amount of 4.0 g/m.sup.2 as the amount of
solid content (Sample and Comparative Sample polymer amount of 1.0
g/m.sup.2) in the same manner as the Examples-1.about.5 followed by
drying, printing and testing after printing.
[0128] The results of water resistance, light resistance and
evaluating color densities as described above are shown in Table 4.
In addition, the degrees of feathering were evaluated by visual
inspection using a magnifying glass.
[0129] .circleincircle.: feathering is not recognized, .DELTA.:
feathering is recognized, X: feathering is significantly
recognized
4 TABLE 4 Water Light Color Density Name of Resistance Resistance C
M Y B Sample C M Y B C M Y B (-b*) (a*) (b*) (L*) Feathering
Example 6 Sample-5 A B A A A B A A 45.6 64.0 74.1 33.0
.circleincircle. Example 7 Sample-6 A B A A A B A A 46.1 64.4 74.8
33.5 .circleincircle. Example 8 Sample-7 A B A A A B A A 46.7 64.0
74.9 33.0 .circleincircle. Example 9 Sample-8 A B A A A B A A 46.8
63.8 74.5 33.2 .circleincircle. Comparative Comparative B C A B A C
A A 43.8 63.2 73.2 35.4 X Example 6 Sample-5 Comparative
Comparative B C A B A C A A 44.1 63.4 73.1 35.0 .DELTA. Example 7
Sample-6 Comparative Comparative B C A B A C A A 44.0 63.1 72.8
35.5 X Example 8 Sample-7 Comparative Comparative B C A B A C A A
44.2 64.0 73.5 33.6 .DELTA. Example 9 Sample-8 C: cyan, M: magenta,
Y: yellow, B: black
SYNTHESIS EXAMPLES-9.about.10
[0130] A 20% aqueous solution of polyvinyl alcohol (abbreviated as
PVA) (trade name: PVA105 (saponification index: 98%, degree of
polymerization: 500) manufactured by Kurare Co.) and
N-vinylcarboxylic acid amide monomers having the compositions
described in Table 5 were charged into a 500 ml four-neck flask
equipped with a thermometer, stirrer, nitrogen feed tube and
condenser, after which the pH was adjusted to 5.5 and the total
concentration of PVA105 and monomers was adjusted to 20% by
addition of deionized water.
[0131] Nitrogen replacement within the system was performed for 30
minutes while stirring the raw material mixture and maintaining the
temperature at 60.degree. C. Next, 0.5 wt % (per monomer) of
polymerization initiator V-50 was added to initiate polymerization.
After maintaining at 60.degree. C. for 4 hours, 0.2 wt % (per
monomer) of polymerization initiator V-50 was added, and the
reaction was allowed to continue for 8 hours from the time of
initiation to obtain a uniform product.
[0132] This polymer mixture was alkaline hydrolyzed to hydrolyze
95% of the N-- vinylcarboxylic acid amide unit therein to obtain
vinylamino units. The mixtures of hydrolyzed polymers were
designated as Samples-9 and -10.
[0133] The cation equivalent values, the intrinsic viscosities, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Samples--9.about.10 were measured by the same procedures as
the Synthesis Example-1. Polymer properties are shown in Table
5.
COMPARATIVE SYNTHESIS EXAMPLES-9.about.10
[0134] Polymerization of N-vinylcarboxylic acid amide monomer was
performed according to the same procedure as the Synthesis
Examples-9.about.10 without adding PVA to obtain
poly-N-vinylcarboxylic acid amide, and a polymer mixture was
obtained by mixing an equal amount of PVA as that used in the
Synthesis Examples-9.about.10 with the poly-N-vinylcarboxylic acid
amide. This polymer mixture was alkaline hydrolyzed to hydrolyze
95% of the N-vinylcarboxylic acid amide units therein to obtain a
mixed polymer of cationic polymer having vinylamino units and PVA.
These polymer mixtures were designated as Comparative
Samples-9.about.10. The Comparative Samples-9 and -10 separated
into 2 phases, and again separated into 2 phases within 1 day even
after mixed with a homogenizer.
[0135] The cation equivalent value, the intrinsic viscosities, the
weight ratio (% insoluble matter) of methanol-insoluble matter of
the Comparative Samples-9.about.10 were measured by the same
procedures as the Synthesis Example-1. Polymer properties are shown
in Table 5.
5TABLE 5 Formula Cationic In- weight ratio Equivalent Intrinsic
soluble Name of VA:Cationic Kind of Value Viscosity Matter Sample
Group Monomer (meq/g) (g/dl) (%) Sample-9 25:75 NVF 10.00 0.38 29
Sample-10 33:67 NVA 9.40 0.41 31 Comparative 25:75 NVF 10.00 0.40
100 Sample-9 Comparative 33:67 NVA 9.40 0.40 100 Sample-10 NVF:
N-vinylformamide NVA: N-vinylacetamide VA: vinylalcohol units
SYNTHESIS EXAMPLES 11.about.12
[0136] A23% aqueous solution of polyvinylalcohol (trade name:
PVA105 (saponification index: 98%, degree of polymerization: 500)
manufactured by Kurare Co.) and monomer compositions described in
Table 6 were charged into a 500 ml four-neck flask equipped with a
thermometer, stirrer, nitrogen feed tube and condenser, after which
the pH was adjusted to 5.0 and the total concentration of PVA105
and monomers was adjusted to 30% by addition of deionized
water.
[0137] Nitrogen replacement within the system was performed for 30
minutes while stirring the raw material mixture and maintaining the
temperature at 60.degree. C. Next, 0.3 wt % (permonomer) of
hydroxylamine hydrochloride as a crosslinking preventor, 0.5 wt %
(per monomer) of 2-mercaptoethanol as a chain transfer agent, and
0.5 wt % (per monomer) of polymerization initiator V-50 were added
to initiate polymerization.
[0138] After maintaining at 60.degree. C. for 6 hours, an
equivalent amount of hydrochloric acid as that of N-vinylformamide
used was added, and the reaction was allowed to continue for 5
hours at 90.degree. C. The obtained polymers were designated as
Samples-11 and 12.
[0139] The cation equivalent values, the intrinsic viscosities, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Samples-11.about.12 were measured by the same procedure as
the Synthesis Example-1. In addition, amidine proportions of the
products were measured by NMR method. Polymer properties are shown
in Table 6.
COMPARATIVE SYNTHESIS EXAMPLES-11.about.12
[0140] Polymerization of monomer compositions described in Table 6
was performed according to the same procedure as the Synthesis
Examples-11.about.12 without adding PVA, and a polymer mixture was
obtained by mixing an equal amount of PVA as that used in the
Synthesis Examples-11.about.12 with the obtained products followed
by the reaction with hydrochloric acid. These polymer mixtures were
designated as Comparative Samples-11.about.12. Polymer properties
are shown in Table 6.
6TABLE 6 Formula Cationic weight ratio Equivalent Intrinsic
Insoluble Polymer Name of VA:Cationic NVF/AN Polymerization Value
Viscosity Matter composition Sample Group mol ratio pH (meq/g)
(g/dl) (%) P/Q/R % Sample-11 25:75 60/40 5.0 7.20 0.35 25 44/39/17
Sample-12 33:67 60/40 5.0 6.71 0.42 34 49/28/23 Comparative 25:75
60/40 5.0 7.15 0.32 98 45/40/15 Sample-11 Comparative 33:67 60/40
5.0 6.76 0.39 97 48/30/22 Sample-12 NVF: N-vinylformamide AN:
acrylonitrile VA: vinylalcohol units P: mol % of primary amino
groups Q: mol % of amidine groups R: mol % of cyano groups
EXAMPLES 10.about.13
COMPARATIVE EXAMPLE 10.about.13
[0141] (Application of Treating Agent)
[0142] The same procedures as in the Examples-1.about.5 were
repeated except for using the treating agents for a sheet surface
of Samples-9.about.12 and Comparative Samples--9.about.12 to obtain
coating colors. The coated papers were dried and then used in
printing and later testing.
[0143] (Printing of Test Paper and Measurement of Water and Light
Resistance)
[0144] Evaluation testing was performed in the same manner as the
Examples-1.about.5, and the color densities, water resistance and
light resistance of each sample were evaluated. The results of each
measurement are shown in Table 7.
7 TABLE 7 Water Light Color Density Name of Resistance Resistance C
M Y B Sample C M Y B C M Y B (-b*) (a*) (b*) (L*) Example 10
Sample-9 A B A A A B A A 44.4 63.9 73.3 33.2 Example 11 Sample-10 A
B A A A B A A 45.2 64.5 73.8 33.5 Example 12 Sample-11 A A A A A A
A A 43.3 65.0 72.8 33.7 Example 13 Sample-12 A A A A A A A A 45.0
65.0 73.1 33.0 Comparative Comparative B C A B A C A A 42.3 63.0
73.2 35.4 Example 10 Sample-9 Comparative Comparative B C A B A C A
A 42.6 63.7 73.0 35.0 Example 11 Sample-10 Comparative Comparative
B C A B A C A A 42.1 63.3 73.0 35.3 Example 12 Sample-11
Comparative Comparative B C A B A C A A 42.0 63.6 73.1 35.2 Example
13 Sample-12 C: cyan, M: magenta, Y: yellow, B: black
SYNTHESIS EXAMPLES 13.about.14
[0145] A 20% aqueous solution of N-vinylformamide was charged into
a 500 ml four-neck flask equipped with a thermometer, stirrer,
nitrogen feed tube and condenser, after which the pH was adjusted
to 5.5.
[0146] Nitrogen replacement within the system was performed for 30
minutes while stirring the raw material and maintaining the
temperature at 60.degree. C. Next, 0.3 wt % (per monomer) of
hydroxylamine hydrochloride as a crosslinking preventor, 0.5 wt %
(per monomer) of 2-mercaptoethanol as a chain transfer agent, and
0.5 wt % (per monomer) of V-50 as a polymerization initiator were
added to initiate polymerization.
[0147] After maintaining at 60.degree. C. for 6 hours, an
equivalent amount of hydrochloric acid as that of N-vinylformamide
used was added, and the reaction was allowed to continue for 5
hours at 90.degree. C. The reaction solution was added with a large
amount of acetone and removed water contained, and powdered
polyvinylamine hydrochloride was obtained.
[0148] After that, the obtained polyvinylamine hydrochloride and
vinylacetate monomer composition described in Table 8 were charged
into a 500 ml four-neck flask equipped with a thermometer, stirrer,
nitrogen feed tube and condenser, after which the pH was adjusted
to 3.5 and the total concentration of polyvinylamine hydrochloride
and vinyl acetate monomer was adjusted to 25% by addition of
deionized water.
[0149] Nitrogen replacement within the system was performed for 30
minutes while stirring the raw material and maintaining the
temperature at 60.degree. C. Next, 0.5 wt % (per monomer) of
ammonium peroxodisulfate as a polymerization initiator was added to
initiate polymerization.
[0150] After maintaining at 60 for 4 hours, 0.2 wt % (per monomer)
of polymerization initiator V-50 was added, and the reaction was
allowed to continue for 8 hours.
[0151] The obtained polymer was alkaline hydrolyzed followed by
neutralization with hydrochloric acid to obtain a graft copolymer
comprising a back bone polymer having 95 mol % of vinylamino units
(in the form of hydrochloride) and branch polymers comprising
polyvinyl alcohol (95 mol % hydrolysis product of
polyvinylacetate). The hydrolysis products of the polymer mixture
were designated as Samples-13 and 14.
[0152] The cation equivalent values, the intrinsic viscosities, and
the weight ratio (% insoluble matter) of methanol-insoluble matter
of the Samples-13.about.14 were measured by the same procedure as
the Synthesis Example-1. Polymer properties are shown in Table
8.
8TABLE 8 Formula Cationic weight ratio Equivalent Intrinsic
Insoluble Name of VA:Cationic Value Viscosity Matter Sample Group
(meq/g) (g/dl) (%) Sample-13 25:75 9.88 0.35 36 Sample-14 33:67
9.25 0.44 33 VA: vinylalcohol units
EXAMPLES 14.about.15
[0153] (Application of Treating Agent)
[0154] The same procedures as in the Examples-1.about.5 were
repeated except for using treating agents for a sheet surface of
Samples-13.about.14 to obtain coating colors. The coated papers
were dried and then used in printing and later testing.
[0155] (Printing of Test Paper and Measurement of Water and Light
Resistance)
[0156] Evaluation testing was performed in the same manner as the
Examples-1.about.5, and the color densities, water resistance and
light resistance of each sample were evaluated. The results of each
measurement are shown in Table 9.
9 TABLE 9 Water Light Color Density Name Resistance Resistance C M
Y B of Sample C M Y B C M Y B (-b*) (a*) (b*) (L*) Example 14
Sample-13 A B A A A B A A 45.4 64.7 73.5 33.1 Example 15 Sample-14
A B A A A B A A 45.3 64.5 73.8 33.6 C: cyan, M: magenta, Y: yellow,
B: black
INDUSTRIAL APPLICABILITY
[0157] The treating agent for a sheet surface of the present
invention is composed of a copolymer obtained by polymerizing
di(meth)allylamine-based monomers and/or (meth)acryl-based cationic
monomers and so forth in the presence of, for example, a
water-soluble or water-dispersible polymer containing vinyl alcohol
units by radical polymerization, etc. According to the present
invention, feathering, a particular problem of common-use paper, is
prevented, water resistance and light resistance are improved
without decreasing color density during printing, and there is
strong bonding with the ink dye, thereby allowing the present
invention to be preferably used as a treating agent for an ink jet
printing paper. The present invention has a significant
applicability in the industrial field.
* * * * *