U.S. patent application number 10/919736 was filed with the patent office on 2005-01-27 for cosmetic films.
This patent application is currently assigned to Coty Inc.. Invention is credited to Amato, Steven W., Barone, Salvatore, Hoyte, Wayne M., Naranjo, Alexander, Patel, Shirish.
Application Number | 20050019359 10/919736 |
Document ID | / |
Family ID | 23124611 |
Filed Date | 2005-01-27 |
United States Patent
Application |
20050019359 |
Kind Code |
A1 |
Amato, Steven W. ; et
al. |
January 27, 2005 |
Cosmetic films
Abstract
The present invention includes a cosmetic film. The film
includes butylphthalimide isopropylphthalimide, one or more primary
film forming polymers and one or more secondary film forming
resins.
Inventors: |
Amato, Steven W.; (North
Plainfield, NJ) ; Hoyte, Wayne M.; (Parlin, NJ)
; Naranjo, Alexander; (Mine Hill, NJ) ; Patel,
Shirish; (Guttenberg, NJ) ; Barone, Salvatore;
(Staten Island, NY) |
Correspondence
Address: |
SCHWEGMAN, LUNDBERG, WOESSNER & KLUTH, P.A.
P.O. BOX 2938
MINNEAPOLIS
MN
55402
US
|
Assignee: |
Coty Inc.
|
Family ID: |
23124611 |
Appl. No.: |
10/919736 |
Filed: |
August 17, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10919736 |
Aug 17, 2004 |
|
|
|
10152314 |
May 20, 2002 |
|
|
|
60292424 |
May 21, 2001 |
|
|
|
Current U.S.
Class: |
424/401 ;
424/70.13; 424/70.16; 424/70.17 |
Current CPC
Class: |
A61K 8/731 20130101;
A61K 8/86 20130101; A61Q 3/02 20130101; A61K 8/4913 20130101; A61K
8/891 20130101; A61K 8/8164 20130101; A61K 8/895 20130101; A61K
2800/594 20130101; A61K 8/85 20130101 |
Class at
Publication: |
424/401 ;
424/070.13; 424/070.16; 424/070.17 |
International
Class: |
A61K 007/04; A61K
007/06; A61K 007/11; A61K 031/74 |
Claims
1. A cosmetic film, comprising butylphthalimide
isopropylphthalimide; one or more primary film forming polymers and
one or more secondary film forming resins.
2. The cosmetic film of claim 1, further comprising a modifying
plasticizer.
3. The cosmetic film of claim 1 wherein the secondary film-forming
polymers are selected from the group consisting of polyurethanes,
polyacryls, polymethacryls, cellulosic polymers, styrene-acryl
copolymers, polystyrene-polyacryl mixtures, polysiloxanes,
polyesters, polyethers, cellulose acetate propionate,
urethane-acryl copolymers, siloxane-urethane copolymers, vinyl
acetate polymers, and mixtures thereof.
4. The cosmetic film of claim 1 wherein the secondary film forming
polymers are selected from a group consisting of acrylic-silicone
resin, polyester resin, and polyamide resin.
5. The cosmetic film of claim 2 wherein the modifying plasticizer
is selected from the group consisting of
N-ethyl-o/p-Toluenesulfonamide, di-(2-ethylhexyl)adipate,
diisobutyladipate, glyceryl tribenzoate, pentaerytritrol
tetrabenzoate, diisopropyl adipate, trimethylolethane tribenzoate,
pentaerythyl tetrabenzoate, glyceryl trioctanoate, dipropylene
glycol dibenzoate, benzyl laurate myristate/palmitate,
2,2,4-trimethyl-1,3-pentanediol diisobutyrate, sucrose acetate
isobutyrate, butyl benzyl phthalate, propylene glycol dibenzoate,
dipropylene glycol dibenzoate, propylene glycol monobenzoate,
2,2,4-trimethyl-1,3-pentanediol dibenzoate, 2-ethylhexyl benzoate,
diisopropyl adipate, N-alkyl toluene sulfonamide, benzyl benzoate,
glyceryl triacetate, and acetyl tributyl citrate.
6. The cosmetic film of claim 1, further comprising one or more
solvents.
7. The cosmetic film of claim 6 wherein the solvent is selected
from a group consisting of ethyl acetate, methyl acetate, n-butyl
acetate, iso-butyl acetate, propyl acetate, iso-propyl acetate,
amyl acetate, ethanol, isopropanol, n-amyl alcohol, n-butyl
alcohol, iso-butanol, cellosolve, butyl cellosolve, ethyl
cellosolve, n-butanol, xylene, aromatic ethers, ketones, methyl
ethyl ketone, alkanes, cyclopentane, hexane, heptane, cyclohexane,
cyclic ethers, phenylated solvents, chlorinated hydrocarbons, and
toluene.
8. A nail enamel, comprising: butylphthalimide
isopropylphthalimide; a secondary film forming polymer;
nitrocellulose; and a polyester resin.
9. A colored nail enamel, consisting essentially of
butylphthalimide isopropylphthalimide in a concentration of about 1
to 10 percent by weight; ethyl acetate in a concentration of about
37 to 39 percent weight; butyl acetate in a concentration of about
19 to 26 percent weight; nitrocellulose in a concentration of about
11 to 14 percent weight; isopropyl alcohol in a concentration of
about 5 to 6 percent by weight; optionally, polyester resin in a
concentration of about 12 percent by weight; optionally,
tosylamide/epoxy resin in a concentration of about 8 to 10 percent
by weight; stearalkonium hectorite in a concentration of about 0.5
to 2 percent by weight; optionally, acrylic copolymer in a
concentration of about 1.5 percent by weight; and coloring agents
in a concentration effective to produce color.
10. A nail enamel, comprising: a plasticizer and butylphthalimide
isopropylphthalimide (BIP) in a concentration effective for
imparting to the nail enamel, adhesion, hardness and flexibility
that is retained for at least about 7 days, when the nail enamel is
applied to a nail.
11. The nail enamel of claim 10, wherein the resin is either a
tosylamide/epoxy resin or a polyester resin.
12. The nail enamel of claim 10 wherein the nail enamel is
substantially free of cracking for at least about 7 days after
application to a nail.
13. The nail enamel of claim 1 wherein the enamel is substantially
free of phthalates.
14. A colored nail enamel, comprising: ethyl acetate; butyl
acetate; nitrocellulose; isopropyl alcohol; tosylamide/epoxy resin;
butylphthalimide isopropylphthalimide in a concentration of about 1
to about 10 percent by weight; and coloring agents.
15. (Cancel)
16. (Cancel)
17. (Cancel)
18. (Cancel)
19. (Cancel)
20. (Cancel)
21. A cosmetic film, comprising butylphthalimide
isopropylphthalimide.
22. A cosmetic film, comprising butylphthalimide.
23. A cosmetic film, comprising isopropylphthalimide.
Description
TECHNICAL FIELD
[0001] The present invention relates to compositions useful as
cosmetic films formed from plasticizers alternative to replace
phthalates. The compositions herein are particularly useful as
coatings for mammalian nails, and are useful as basecoat, topcoat
and colored nail polish compositions.
BACKGROUND OF THE INVENTION
[0002] Nail polish compositions have long been promoted as having
long wear, good adhesion, and/or resistance to chipping. While some
nail polish compositions have provided better wear than others, a
need remains for nail polish compositions providing long wear and
employing plasticizers other than phthalate compounds.
[0003] Nail polish has, over the decades, been developed to have
multi-faceted functionality. In addition to having functionality,
polish must be aesthetically pleasing when applied to fingernails
and toenails in order to provide a desired color to the nails. The
polish must also be resistant to chipping, cracking, splintering
and peeling when subjected to a wide range of environments. Over
the years, nail polishes have been developed which have these
properties to varying degrees.
[0004] Nail polishes have typically included pigments and dyes that
are suspended in a viscous matrix. The viscous matrix typically
includes a film forming component and a plasticizer, namely dibutyl
phthalate. The nail polish has also included an adhesion promoter,
a polymeric component formed by the condensation polymerization of
formaldehyde or other sulfonamide formaldehyde resin.
[0005] It has been observed over the years that phthalates and
aldehyde condensation product exposure has been undesirable for
some users because the users are sensitized to these materials.
There has been an effort to replace the polymeric component with
other materials that do not cause a sensitization. However, the
replacement materials have produced a nail polish that is deficient
in features such as high gloss, defined color, long wear, chip
resistance, nail flexibility and adherence.
SUMMARY OF THE INVENTION
[0006] One embodiment of the present invention includes a cosmetic
film. The film includes butylphthalimide isopropylphthalimide, one
or more primary film forming polymers and one or more secondary
film forming resins.
[0007] Another embodiment of the present invention includes a nail
enamel. The clear nail enamel includes butylphthalimide
isopropylphthalimide. The nail enamel also includes a secondary
film-forming polymer, nitrocellulose and a polyester resin.
[0008] One other nail enamel embodiment of the present invention is
a colored nail enamel, that includes butylphthalimide
isopropylphthalimide in a concentration of about 1 to 10 percent by
weight; ethyl acetate in a concentration of about 37 to 39 percent
by weight; butyl acetate in a concentration of about 19 to 26
percent by weight; nitrocellulose in a concentration of about 11 to
14 percent by weight; isopropyl alcohol in a concentration of about
5 to 6 percent by weight; optionally, polyester resin in a
concentration of about 10 to 12 percent by weight; optionally,
tosylamide/epoxy resin in a concentration of about 8 to 10 percent
by weight; stearalkonium hectorite in a concentration of about 0.5
to 2 percent by weight; acrylic copolymer in a concentration of
about 1.5 percent by weight; and coloring agents in a concentration
effective to produce color.
[0009] Another embodiment of the present invention includes a nail
enamel that includes a plasticizer and butylphthalimide
isopropylphthalimide (BIP) in a concentration effective for
imparting to the nail enamel, adhesion, hardness and flexibility
that is retained for at least about seven days, when the nail
enamel is applied to a nail.
[0010] The present invention also includes a colored nail enamel,
comprising: ethyl acetate; butyl acetate; nitrocellulose; isopropyl
alcohol; tosylamide/epoxy resin; butylphthalimide
isopropylphthalimide in a concentration of about 1 to about 10
percent by weight; and coloring agents.
[0011] The present invention also includes a method for making a
cosmetic film that has a hardness, adhesion, and flexibility,
gloss, and long shelf life, comprising:
[0012] providing one or more primary film forming polymers;
[0013] providing one or more secondary film forming resins;
[0014] providing butylphthalimide isopropylphthalimide;
[0015] and blending the primary film forming polymer, secondary
film forming resin and butylphthalimide isopropylphthalimide (BIP),
wherein the BIP has a weight percent concentration of about 1 to 10
weight percent to make a cosmetic film having a hardness, adhesion,
flexibility, gloss and long shelf life.
[0016] Another embodiment of the present invention is a method for
coating nails. The method includes providing a cosmetic film that
includes butylphthalimide isopropylphthalimide and applying the
cosmetic film to one or more mammalian nail.
[0017] One other embodiment includes a colored nail enamel. The
colored nail enamel includes an acetate, nitrocellulose,
butylphthalimide isopropylphthalimide, tosylamide/epoxy resin and
coloring agents.
[0018] Other embodiments include cosmetic films that comprise
butylphthalimide isopropylphthalimide; films that comprise
butylphthalimide; and films that comprise isopropylphthalimide.
DETAILED DESCRIPTION
[0019] One embodiment of the present invention includes a nail
enamel composition that comprises butylphthalimide
isopropylphthalimide, BIP. The nail enamel of the present invention
is, for some embodiments, free of phthalates and, for some
embodiments, free of aldehyde condensation products. The nail
enamel composition also includes one or more primary film forming
polymers and one or more secondary film forming resins. The nail
enamel compositions of the present invention include primary film
forming polymers and combinations thereof in an amount ranging from
about 5 to 20% by weight, and, for some embodiments, in the range
of about 9 to 14% by weight.
[0020] In addition to the primary film forming polymer and
secondary film forming resin, the nail enamel compositions
according to the present invention also include at least one
plasticizer to soften and to plasticize the primary film forming
polymer. The plasticizer as well as combinations thereof, is in
either liquid or solid form.
[0021] In its product aspect, embodiments of the present invention
provide nail enamel compositions which are suitable for use as base
coats, color coats, clear coats and protective top coats while
maintaining the desirable characteristics of the nail enamel
compositions. The nail enamel compositions display good lastingness
and chip resistance, and are safe to use with frequent
applications.
[0022] The present invention includes a use of butylphthalimide
isopropylphthalimide, Pelemol BIP, as a plasticizer in nail enamel
compositions. Hereinafter, Pelemol BIP is referred to as BIP. While
Pelemol BIP is described herein, it is believed that
butylphthalimide and isopropylphthalimide, when obtained
separately, can be blended to obtain a plasticizer suitable for use
in the nail enamel of the present invention. It is also believed
that butylphthalimide and isopropylphthalimide are individually
usable as plasticizers in nail enamel compositions.
[0023] As used herein, the term, "cosmetic film" refers to a nail
enamel usable as a base coat, color coat, clear coat and protective
top coat. As used herein, "lacquer," "polish" and "enamel" are used
interchangeably.
[0024] Referred to herein are trade names for materials including,
but not limited to, polymers and optional components. The inventors
herein do not intend to be limited by materials described and
referenced by a certain trade name. Equivalent materials (e.g.,
those obtained from a different source under a different name or
catalog (reference) number) to those referenced by trade name may
be substituted and utilized in the methods described and claimed
herein. All percentages and ratios are calculated by weight unless
otherwise indicated. All percentages are calculated based on the
total composition unless otherwise indicated. All component or
composition levels are in reference to the active level of that
component or composition, and are exclusive of impurities, for
example, residual solvents or by-products, which may be present in
commercially available sources.
[0025] The cosmetic properties of the nail varnish of the present
invention include good adhesion to the surface of the nail. In
addition, the varnish film is homogeneous and glossy, and exhibits
a degree of flexibility that prevents premature cracking and
flaking off the nail. In order to obtain such properties, the
varnish film is sufficiently soft. This softness allows the film to
withstand impact and deformations of the matrix of the nail.
However, the film retains an acceptable degree of gloss and is
sufficiently hard to prevent scratches and cracks. Nail enamel
embodiments are believed to be resistant to cracking for at least
about ten days after application to a nail.
[0026] The film-forming polymers used in the lacquer of the present
invention are selected from polyurethanes, polyacryls,
polymethacryls, cellulosic polymers, styrene-acryl copolymers,
polystyrene-polyacryl mixtures, polysiloxanes, polyethers,
polyesters, urethane-acryl copolymers, cellulose acetate
propionate, siloxane-urethane copolymers,
polyurethane-polymethacryl mixtures, silicone-acryl copolymers,
vinyl acetate polymers, and mixtures thereof. Exemplary secondary
film forming resins usable in the formulations of the present
invention include, for example, toluene sulfonamide/epoxy resins,
e.g. tosylamide and non-drying alkyd resins, acrylic polymers and
copolymers, polyurethane, polyacryls, polymethacryls, cellulosic
polymers, styrene-acryl copolymers, polystyrene-polyacryl mixtures,
polysiloxanes, polyethers, polyesters, cellulose acetate
propionate, urethane-acryl copolymers, siloxane-urethane
copolymers, polyurethane-polymethacryl mixtures, silicone-acryl
copolymers, vinyl acetate polymers, and mixtures thereof. It is
also within the scope of the nail enamel compositions of the
present invention to include aldehyde condensation products such as
arylsulfonamide formaldehyde resins, specifically toluene
sulfonamide formaldehyde resin which is a condensation product of
formaldehyde and toluene sulfonamide. These secondary film forming
resins are added to the nail enamel compositions of the present
invention to strengthen and add acceptable wear characteristics to
the primary film forming polymer. In general, the amount of
secondary film forming resin ranges form about 2 to 20 percent by
weight of the composition, and preferably, about 5 to 12 percent of
the composition.
[0027] Nitrocellulose is a primary film-forming component in some
formulation embodiments of the present invention. A use of low
levels of nitrocellulose tends to result in the coated films being
easily damaged. On the other hand, a use of high levels of
nitrocellulose results in the coated film being too hard and
inflexible, resulting in undesirable peeling and hence poor wear
resistance.
[0028] Other satisfactory film-forming components include cellulose
acetate, cellulose acetate butyrate, cellulose acetate propionate,
vinyl polymers, polyurethanes, and mixtures of polyurethanes with
cellulose acetate butyrate or with nitrocellulose as well as
methacrylate and acrylate type polymers. The film-forming component
is present in an amount sufficient to provide a stable film upon
the nail following the application of the nail enamel to the nail.
In general, amounts of the film-forming component of about 8 to
about 40 weight percent for some embodiments, and about 10 to about
15 weight percent for other embodiments, are satisfactory. Examples
of nitrocellulose are the so called nitrocellulose RS 1/8 sec., RS
1/4 sec., and nitrocellulose 1/2 sec, and nitrocellulose RS 5-6
sec. and 60-80 sec., which have higher viscosities than the earlier
grades. The term "RS" refers to the brand of nitrocellulose with a
nitrogen content of about 11.2 to 12.8 percent with solubility in
esters, ketones, and glycol ethers manufactured by GreenTree
Technologies, previously known as Hercules, Inc. The terms 1/8
sec., 1/2 sec, 5-6 sec, and so forth represent viscosity and refer
to the time it takes for a ball to fall a given depth in the
material. Nitrocellulose is typically supplied in 70%
concentrations, wet with 30% ethyl or isopropyl alcohol. As used in
the present invention, the percentage of nitrocellulose in a given
composition is on a dry basis.
[0029] In one embodiment, the resins include Shin-Etsu KP-543
(acrylic-silicone resin), Uniplex 670P (polyester resin), PCI Group
Inc. Lacq-Hard LH-75 (polyamide resin).
[0030] Suitable plasticizers are incorporated in the formulation to
provide flexibility while exhibiting the wear and chip resistance
and shelf stability needed for the composition. Without intending
to be limited by theory, it is believed that plasticizers cause a
composition to become more easily deformed. Typically, plasticizers
are needed in the compositions of the present invention. The
compositions of the present invention may comprise from 0% to about
15%, for some embodiments, from 0% to about 10%, and in some
embodiments, from about 0% to about 7%, by weight of the
composition, of a plasticizer. One or more plasticizers are
optionally added to the present compositions.
[0031] In one embodiment, the plasticizers include camphor, castor
oil, Unitex Chemical Corporation Uniplex 108
(N-ethyl-o/p-Toluenesulfonamide), Uniplex 125A (di-(2-ethylhexyl)
adipate), Uniplex 165 (diisobutyl Adipate), Uniplex 260 (Glyceryl
Tribenzoate), Uniplex 552 (Pentaerytritrol tetrabenzoate), Phoenix
Chemical Inc. Pelemol DIA (diisopropyl adipate), Pelemol TMEB-35
(Trimethylolethane Tribenzoate), Pelemol PTB-35 (Pentaerythyl
Tetrabenzoate), Pelemol GTO (Glyceryl Trioctanoate), Alzo
International Dermol DPG-2B (Dipropylene glycol dibenzoate), Dermol
B-246 (Benzyl Laurate Myristate/Palmitate), Eastman Chemical
Corporation TXIB (2,2,4-trimethyl-1,3-pentanediol diisobutyrate),
SAIB (Sucrose acetate isobutyrate), Ferro Santicizer 160 (Butyl
Benzyl Phthalate), Velsicol Chemical Corporation Benzoflex 284
(Propylene glycol dibenzoate, Dipropylene glycol dibenzoate,
propylene glycol monobenzoate) Benzoflex 354
(2,2,4-trimethyl-1,3-pentanediol dibenzoate), Velate 368
(2-ethylhexyl benzoate), CasChem DIPA (diisopropyl adipate).
[0032] For some embodiments, plasticizers include Unitex Chemical
Corporation Uniplex PX5-115 (N-Alkyl Toluenesulfonamide), Phoenix
Chemical Inc. Pelemol B166 (B1enzyl Benzoate), Eastman Chemical
Corporation Triacetin (Glyceryl triacetate), Uniplex 82 Acetyl
Tributyl Citrate.
[0033] The nail enamel compositions of the present invention
include one or more solvents such as those generally used in
conventional nail enamel compositions. Examples of these solvents
include ethyl acetate, methyl acetate, n-butyl acetate, iso-butyl
acetate, propyl acetate, iso-propyl acetate, amyl acetate, ethanol,
isopropanol, n-amyl alcohol, n-butyl alcohol, iso-butanol,
cellosolve, butyl cellosolve acetate, cellosolve acetate, methyl
cellosolve acetate, butyl cellosolve, ethyl cellosolve, n-butanol,
xylene, aromatic (containing phenyl groups), ethers, ketones for
example acetone, methyl ethyl ketone, alkanes for example, pentane,
cyclopentane, hexane, heptane, cyclohexane, cyclic ethers for
example, tetrahydrofuran and 1,4-dioxane, phenylated solvents for
example, xylene, chlorinated hydrocarbons for example, methylene
chloride, chloroform, glycol ethers, N-methylpyrrolidone alkyl
lactate, and methylchloroform. It is also contemplated that
toluene, if desired, can be included as a solvent or diluent for
use in a nail enamel composition in accordance with the
compositions of the present invention.
[0034] The aforementioned solvents can be used alone or in mixtures
thereof. In general, the amount of solvent used in the compositions
of the present invention range from about 53 to 82% by weight, and,
for some embodiments about 65 to 75% by weight. For some
embodiments, organic solvents are selected from alcohols and esters
having between one and about twenty-five carbon atoms. For some
embodiments, alcohols are monohydric. It is also contemplated that,
if desired, monohydric alcohols are selected from ethanol,
iso-propanol, and n-propanol. For some embodiments, esters are
selected from ethyl acetate and butyl acetate. For other
embodiments, it is contemplated that polyhydric alcohols are
usable.
[0035] The following are examples and Laboratory test results of
enamels made according to the invention. These examples and test
results are presented in order to illustrate features of particular
embodiments of the present invention and are not intended to limit
the scope of the present invention.
1TABLE 1 EXAMPLE 1 Clear Topcoat 1A 1B 1C Weight Weight Weight
Ingredient percent percent percent Ethyl Acetate 40.00 40.00 40.00
Butyl Acetate 21.00 21.00 21.00 Nitrocellulose (dry) 14.00 14.00
14.00 Isopropyl alcohol 6.00 6.00 6.00 Polyester resin 12.00 12.00
12.00 (75% solids) Dibutyl phthalate 7.00 -- -- Butylphthalimide --
7.00 -- Isopropylphthalimide Acetyl tributylcitrate -- -- 7.00
[0036] The clear topcoat 1 B is a topcoat formulation of the
present invention, having a butylphthalimide isopropylphthalimide,
BIP, concentration of 7.00 percent by weight. The clear topcoat 1A
is a control, having a dibutyl phthalate component. The clear
topcoat IC is a control, having an acetyl tributylcitrate
component.
[0037] Comparative mechanical film properties of Example 1 of the
present invention were measured using a hardness test, adhesion
test, and flexibility test as described herein.
[0038] Hardness: Using the Erichsen Pendulum Damping Tester Model
299/300 according to Persoz. (NFT 30-016). A standard 6.0 mils wet
film thickness (W.F.T) Bird film applicator (MCD Industries) was
used to apply films onto (4 ins X 6 ins) clean glass plates. The
tests were conducted on the films after air-drying at ambient
temperature for the specified times below.
2TABLE 2 Average # oscillations Time interval after initial
application 1A 1B 1C 2 Hrs 23 26 26 24 Hrs. 50 53 58 48 Hrs. 66 73
75 72 Hrs. 75 77 81 96 Hrs. 76 74 80 168 Hrs. 94 96 98
[0039] Adhesion: Using Cross-Cut Tape Test to meet the standards of
ASTM Test Method D-3359 on 6.0 mils (W.F.T) applied to (4 ins X 6
ins) clean glass panels. A standard 6.0 mils (W.F.T) Bird film
applicator (MCD Industries) was used to apply films onto (4 ins X 6
ins) clean glass plates. The tests were conducted on the films
after air-drying at ambient temperature for the specified times
below.
[0040] Ratings of adhesion test results according to the
classification: 5=Best; 1=worst
3TABLE 3 Time interval after initial application 1A 1B 1C 24 Hrs.
5B 5B 5B 48 Hrs. 5B 5B 5B 72 Hrs. 5B 5B 5B 96 Hrs. 5B 5B 5B 168
Hrs. 5B 5B 5B
[0041] Flexibility: According to standards of ASTM Test Method
D-522 and D 1737. A standard 6.0 mils (W.F.T) Bird film applicator
(MCD Industries) was used to 15 apply films onto clean aluminum
panels (6 ins X 4 ins Mill Finish 3105H24 supplied by Q-panel Lab
Products, Cleveland, Ohio). Coated panels were uniformly bent using
the BYK-Gardner Cylindrical Mandrel. The tests were conducted on
the films after air-drying at ambient temperature for the specified
times below.
4TABLE 4 Time interval after initial application 1A 1B 1C 24 Hrs.
Good Good Good 48 Hrs. Good Good Good 72 Hrs. Good Good Good 96
Hrs. Good Good Good 168 Hrs. Good Good Good
[0042] The mechanical tests illustrated that the topcoat
formulation performance of the formulation of the present invention
was at least as good, when measured in terms of hardness, adhesion,
and flexibility, as the performance of the topcoat free of BIP and
containing dibutyl phthalate and the topcoat free of BIP and
containing acetyl tributylcitrate. The topcoat formulation of the
present invention did not produce any adverse effects in users.
[0043] The following are examples of compositions of colored nail
enamel that demonstrate embodiments under the scope of the present
invention. There are other possible variations that are within the
scope and hence these examples are not to be construed as
limitations.
5TABLE 5 EXAMPLE 2 EXAMPLE 3 Red crme Mauve pearl shade nail enamel
shade nail enamel Ingredient Weight percent Weight percent Ethyl
Acetate 38.410 37.950 Butyl Acetate 25.600 25.300 Nitrocellulose
(dry) 12.010 11.860 Isopropyl alcohol 5.381 5.080 Tosylamide/epoxy
resin 8.532 9.080 *Butylphthalimide 7.498 6.850
Isopropylphthalimide Stearalkonium Hectorite 0.960 1.036 Phosphoric
acid 0.017 0.018 Benzophenone-1 0.175 0.188 Iron Oxide Red 0.100 --
Iron Oxide black 0.050 -- D&C Red No. 7 Calcium Lake 0.539 --
FD&C Yellow#5 Aluminum Lake 0.234 -- Titanium Dioxide 0.324
0.515 Dimethicone 0.170 0.176 Bismuth Oxychloride -- 0.400 Mica --
1.387 D&C Red No. 34 -- 0.160
[0044] Presented below is a summary of performance of specified
plasticizers when used with BIP. The BIP concentration used was
between 6.80 and 7.50 percent by weight. The first table shows
adhesion and hardness in a red creme shade of nail enamel, made
with polyester resin B75. The Pelemol GTO formulation displayed a
comparatively high hardness to the BIP formulation but a lower
adhesion. The BIP in each of polyester resin B75 and
tosylamide/epoxy resin E75 displayed slight cracking at 168 hours.
The Triacetin and BIP, Dermol DPG-2B and BIP, Pelemol DIA and BIP,
and Santicizer 160 and BIP formulations displayed an adhesion that
dropped off over time and a hardness that was comparatively low up
to about 48 hours, but became greater over time. These formulations
did not perform as well as the BIP formulation. The GTB and BIP,
TXIB and BIP, and BB and BIP formulations displayed strong adhesion
and hardness over the period of the test. A similar performance was
observed when a Tosylamide/Epoxy Resin E75 was substituted for the
Polyester Resin B75. These formulations displayed cracking within
24 to 48 hours.
[0045] In another test, plasticizer performance was measured in
conjunction with BIP in a 75/25 weight ratio and Polyester Resin
B75. The performance of the plasticizer with BIP in a 75/25 ratio
was comparable to performance, as measured by adhesion and
hardness, of formulations of plasticizers and full strength BIP.
The performance of plasticizers in a formulation with BIP in a
75/25 ratio and Tosylamide/Epoxy Resin E75 was, in some instances,
weaker than for full strength BIP formulations or the formulation
with BIP 75/25 and Polyester Resin B75. The Pelemol GTO displayed a
very low adhesion. Plasticizers that cracked within 24 to 48 hours
included Uniplex 365, Pelemol GTO, Uniplex 165A, and Benzoflex
284.
[0046] In one other test, plasticizers GTB, TXIB, BB and SAIB were
measured in a formulation that included BIP in a 50/50 ratio and
Polyester Resin B75 and with BIP in a 50/50 ratio and Tosylamide
Resin E75. The hardness and adhesion of enamels made with these
formulations was substantially the same as formulations made with
full strength BIP. Each of these formulations displayed cracking
within 24 to 48 hours. Testing of the nail enamel was performed
over a period of seven days. It is believed that the nail enamel
formulations that include BIP remain substantially free of cracks
for at least about 10 days.
6TABLE 6 EVALUATION OF PLASTICIZERS IN COMBINATION WITH BIP
Plasticizer and Polyester Resin B75 ADHESION HARDNESS Red crme
shade 24 h 48 h 72 h 144 h 168 h 2 h 24 h 48 h 72 h 144 h 168 h BIP
5 5 4 4 4 34 85 99 120 124 145 Dermol DPG-2B 5 3 3 3 2 41 97 107
129 145 142 Pelemol DIA 5 4 2 2 2 56 117 135 177 210 207 Santicizer
160 5 4 3 2 2 36 105 109 140 161 155 GTB 4 4 4 4 4 46 107 118 127
147 149 TXIB 4 4 4 4 4 70 149 164 166 187 184 BB 5 5 4 4 4 62 138
149 157 171 173 SAIB 3 2 2 2 2 64 159 159 168 213 226 Triacetin 5 5
5 4 3 37 75 87 109 137 141 Uniplex 365 5 5 4 4 3 68 106 108 124 143
141 Pelemol GTO 1 1 1 1 1 76 153 188 206 220 209 Uniplex 165A 3 3 2
2 2 98 150 162 168 185 173 Benzoflex 284 5 4 4 3 2 45 94 116 121
155 139 Acetyl tributyl citrate 5 4 4 4 3 48 121 133 155 163 165
Dibutyl phthalate 5 4 4 3 3 58 117 128 157 154 167
[0047]
7TABLE 7 Plasticizers and Tosylamide/Epoxy Resin E75 ADHESION
HARDNESS Red crme shade 24 h 48 h 72 h 144 h 168 h 2 h 24 h 48 h 72
h 144 h 168 h BIP 5 5 4 4 4 31 82 101 102 116 127 Dermol DPG-2B 5 5
5 5 5 38 97 106 128 141 142 Pelemol DIA 5 4 4 4 3 53 128 145 184
210 205 Santicizer 160 5 4 3 3 3 37 103 107 130 147 145 GTB 5 5 4 3
3 41 95 116 121 137 142 TXIB 4 4 4 3 3 58 128 148 151 176 172 BB 5
5 5 4 4 51 120 138 144 176 160 SAIB 3 3 2 2 2 57 149 171 182 176
213 Triacetin 5 5 5 4 4 34 71 94 92 141 137 Uniplex 365 5 5 4 3 3
58 107 118 126 142 141 Pelemol GTO 5 5 5 4 4 71 161 191 200 210 209
Uniplex 165A 3 2 2 2 2 88 140 164 174 184 181 Benzoflex 284 5 4 4 3
3 37 86 108 124 149 146 Acetyl tributyl citrate 5 5 5 5 4 33 110
128 146 152 155 Dibutyl phthalate 5 5 5 5 4 40 123 138 148 153
159
[0048]
8 TABLE 8 ADHESION HARDNESS Red crme shade 24 h 48 h 72 h 144 h 168
h 2 h 24 h 48 h 72 h 144 h 168 h Plasticizer/BIP in a 75/25 ratio
and Polyester Resin B75 Dermol DPG-2B 5 5 5 5 5 35 87 126 128 130
137 Pelemol DIA 3 2 2 2 2 44 116 147 154 165 155 Santicizer 160 5 5
5 5 5 37 98 131 144 155 148 Triacetin 5 5 5 5 5 37 86 93 119 133
133 Uniplex 365 5 5 5 5 5 61 136 140 147 162 168 Pelemol GTO 3 3 2
2 1 61 116 123 132 156 183 Uniplex 165A 5 5 5 5 5 83 151 168 175
180 186 Benzoflex 284 5 5 5 5 5 43 98 112 113 144 143
Plasticizer/BIP in a 75/25 ratio and Tosylamide Resin E75 Dermol
DPG-2B 5 4 3 3 3 41 89 123 136 141 135 Pelemol DIA 5 4 4 3 3 36 103
147 160 169 164 Santicizer 160 5 4 4 3 3 37 92 125 143 143 134
Triacetin 5 5 2 2 2 33 75 80 108 131 121 Uniplex 365 5 5 3 2 2 47
170 114 148 160 151 Pelemol GTO 0 0 0 0 0 54 100 103 110 130 128
Uniplex 165A 4 4 2 2 2 58 156 142 175 182 190 Benzoflex 284 4 4 3 2
2 35 88 95 126 141 140
[0049]
9 TABLE 9 ADHESION HARDNESS Red crme shade 24 h 48 h 72 h 144 h 168
h 2 h 24 h 48 h 72 h 144 h 168 h Plasticizer/BIP in a 50/50 Ratio
and Polyester Resin B75 GTB 5 5 5 4 4 30 85 109 109 120 158 TXIB 5
5 4 4 4 37 97 118 121 119 131 BB 5 5 4 4 3 37 96 115 119 126 143
SAIB 5 5 3 3 3 34 105 118 139 165 167 Plasticizer/BIP in a 50/50
Ratio and Tosylamide/Epoxy Resin E75 GTB 5 5 5 5 5 32 88 109 138
119 139 TXIB 5 5 5 5 4 36 94 118 128 135 143 BB 5 5 5 5 5 33 89 116
129 135 145 SAIB 5 5 5 5 5 36 103 138 148 166 174
[0050] The results for use of BIP to make a Pearl shade nail enamel
are shown below. The BIP showed very good values for adhesion and
hardness when used with all of the resins tested. The BIP
performance was better than Uniplex when used with Polyester Resin
B75. The BIP performance was better than Triacetin when used with
Tosylamide Epoxy Resin E75. A formulation of BIP in a 75/25 ratio
and Polyester Resin B75 displayed a performance better than Pelemol
GTO and Dermol DPG-2B, when used as the sole plasticizer. A 50/50
ratio of BIP with Polyester Resin B75 in one embodiment, and
Tosylamide Epoxy Resin E75, in another embodiment, displayed
results comparable to adhesion and hardness results shown with GTB,
TXIB, BB and SAIB.
10 TABLE 10 ADHESION HARDNESS Pearl shade 24 h 48 h 72 h 144 h 168
h 2 h 24 h 48 h 72 h 144 h 168 h Plasticizers and Polyester Resin
B75 BIP 5 5 5 5 5 37 82 118 120 138 146 GTB 5 5 5 5 5 43 104 102
128 144 143 TXIB 4 4 3 3 3 74 130 143 154 193 183 BB 5 5 5 5 5 64
140 157 154 175 168 SAIB 4 4 4 4 4 69 162 179 168 204 210 Dermol
DPG-2B 5 4 3 3 2 33 86 86 118 143 137 Pelemol DIA 5 4 3 3 2 40 112
111 153 186 176 Santicizer 160 5 4 3 3 2 45 114 125 132 156 166
Triacetin 5 5 5 5 5 35 83 108 122 147 143 Uniplex 365 5 5 5 5 5 66
128 160 149 157 168 Pelemol GTO 5 5 5 4 4 74 148 200 213 200 219
Uniplex 165A 2 2 2 2 2 88 143 154 148 176 159 Benzoflex 284 5 5 5 5
5 34 83 101 133 154 155 Acetyl tributyl citrate 5 5 5 5 5 42 108
129 154 159 160 Dibutyl phthalate 5 5 5 5 5 48 120 131 159 159 158
Plasticizers and Tosylamide/Epoxy Resin E75 BIP 5 5 5 5 5 27 78 101
112 129 134 GTB 5 5 5 5 5 32 98 116 118 113 146 TXIB 5 4 4 4 4 52
130 139 145 170 178 BB 5 5 5 5 5 48 117 138 141 160 168 SAIB 5 4 4
4 4 56 154 177 173 217 202 Dermol DPG-2B 5 5 5 4 4 32 74 86 119 134
138 Pelemol DIA 5 4 3 3 3 42 120 169 176 162 Santicizer 160 5 4 4 4
3 44 117 130 153 163 171 Triacetin 2 2 2 2 2 29 73 92 113 149 143
Uniplex 365 2 2 2 2 2 53 123 132 147 169 168 Pelemol GTO 5 5 5 4 4
74 148 200 213 200 209 Uniplex 165A 5 5 4 3 3 89 183 189 189 192
202 Benzoflex 284 5 5 5 5 5 34 83 101 133 154 155 Acetyl tributyl
citrate 5 5 5 5 5 33 110 128 146 152 155 Dibutyl phthalate 5 5 5 5
4 40 123 138 148 153 159
[0051]
11TABLE 11 Pearl shade Plasticizer/BIP in a 75/25 Ratio with
Polyester Resin B75 Dermol DPG-2B 5 4 3 2 3 31 75 109 115 127 124
Pelemol DIA 5 4 2 3 2 40 107 128 151 151 142 Santicizer 160 5 4 4 4
3 40 91 124 148 148 145 Triacetin 5 5 5 5 5 37 86 93 119 133 133
Uniplex 365 5 5 5 5 5 61 136 140 147 162 168 Pelemol GTO 3 3 2 2 1
61 116 123 132 156 183 Uniplex 165A 5 5 5 5 5 83 151 168 175 180
186 Benzoflex 284 5 5 5 5 5 43 98 112 113 144 143 Plasticizer/BIP
in a 75/25 Ratio with Tosylamide/Epoxy Resin E75 Dermol DPG-2B 5 5
4 4 3 30 69 110 123 131 120 Pelemol DIA 5 4 4 3 4 34 106 145 153
160 146 Santicizer 160 5 5 5 5 5 35 91 128 139 146 140 Triacetin 5
5 5 5 5 31 79 83 132 156 153 Uniplex 365 5 5 5 5 5 49 115 127 155
160 163 Pelemol GTO 5 5 5 5 5 52 126 139 137 192 190 Uniplex 165A 5
5 5 5 4.5 65 150 168 180 186 193 Benzoflex 284 5 5 5 5 5 33 87 94
122 140 139 Plasticizer/BIP in a 50/50 Ratio with Polyester Resin
B75 GTB 5 5 5 4 3 41 100 122 121 133 158 TXIB 5 5 4 4 4 37 97 118
121 119 131 BB 5 5 4 4 3 37 96 115 119 126 143 SAIB 5 5 3 3 3 34
105 118 139 165 167 Plasticizer/BIP in a 50/50 Ratio with
Tosylamide Epoxy Resin E75 GTB 5 5 5 5 5 37 86 114 128 140 153 TXIB
5 5 5 5 5 39 101 128 152 155 156 BB 5 5 5 5 5 43 102 118 129 153
139 SAIB 5 5 5 4 4 45 114 134 139 158 167
[0052] Additional examples using Pelemol BIP in combination with
Glyceryl Triacetate
12TABLE 12 FORMULA FORMULA FORMULA FORMULA FORMULA Red crme shade
EC FC GC HC.sup.1 IC.sup.2 Ethyl Acetate 41.271 41.238 41.386
41.262 41.262 Butyl Acetate 22.234 22.200 22.282 22.218 22.218
Nitrocellulose (dry) 1/4 sec R.S 9.603 9.603 6.005 9.603 9.603 1/2
sec R.S 2.407 2.407 6.005 2.407 2.407 Isopropyl alcohol 5.380 5.380
5.150 5.15 5.15 Tosylamide/epoxy resin 8.532 7.644 7.644 7.644
8.880 Butylphthalimide 7.498 7.498 7.498 2.983 4.488
isopropylphthalimide Acrylic-silicone copolymer 0.000 0.955 0.955
0.955 0.955 Glyceryl Triacetate 0.000 0.000 0.000 4.516 3.010
Stearalkonium Hectorite 0.960 0.960 0.960 0.960 0.960
Benzophenone-1 0.175 0.175 0.175 0.175 0.175 Iron Oxides 0.153
0.153 0.153 0.153 0.153 Phosphoric acid 0.017 0.017 0.017 0.017
0.017 D&C Red No. 6 0.673 0.673 0.673 0.673 0.673 D&C Red
No. 7 Calcium Lake 0.539 0.539 0.539 0.539 0.539 Titanium Dioxide
0.324 0.324 0.324 0.324 0.324 FD&C Yellow No. 5 Aluminum Lake
0.234 0.234 0.234 0.234 0.234 ratios of BIP/Glyceryl Triacetate C =
crme shade P = Pearl shade (1) Formula HC: Ratio of BIP/GTA - 40/60
(2) Formula IC: Ratio BIP/GTA- 60/40 (3) Formula HP: Ratio of
BIP/GTA 30/70 (4) Formula IP: Ratio of BIP/GTA 50/50
[0053]
13TABLE 13 TEST RESULTS Red Crme shade FORMULA FORMULA FORMULA
FORMULA FORMULA EC FC GC HC IC Hardness: 2 Hrs. 25 26 24 22 23 24
Hrs. 60 65 61 55 53 48 Hrs. 72 80 77 63 67 72 Hrs. 83 91 88 70 74
144 Hrs. 119 119 119 96 101 168 Hrs. 122 139 136 119 122 Adhesion:
24 Hrs. 5 5 5 5 5 48 Hrs. 5 5 5 5 5 72 Hrs. 5 5 5 5 5 144 Hrs. 4 5
5 5 5 168 Hrs. 4 5 5 5 5 Flexibility: 24 Hrs. Ok Ok Ok Ok Ok 48
Hrs. Ok Ok Ok Ok Ok 72 Hrs. Ok Cracked Ok Ok Ok 144 Hrs. Stretched
Cracked Ok Ok Ok 168 Hrs. Cracked Cracked Cracked Cracked Cracked
ratios of BIP/Glyceryl Triacetate C = crme shade P = Pearl shade
(1) Formula HC: Ratio of BIP/GTA - 40/60 (2) Formula IC: Ratio
BIP/GTA- 60/40 (3) Formula HP: Ratio of BIP/GTA 30/70 (4) Formula
IP: Ratio of BIP/GTA 50/50
[0054]
14TABLE 14 FORMULA FORMULA FORMULA FORMULA FORMULA Pearl shade EP
FP GP HP.sup.3 IP.sup.4 Ethyl Acetate 40.581 40.576 40.576 40.576
40.576 Butyl Acetate 21.853 21.849 21.849 21.849 21.849
Nitrocellulose (dry) 1/4 sec R.S 11.858 11.858 5.929 11.858 11.858
1/2 sec R.S 5.929 Isopropyl alcohol 5.082 5.082 5.082 5.082 5.082
Tosylamide/epoxy resin (solids) 9.081 8.081 8.081 8.081 8.081
Butylphthalimide 6.854 6.854 6.854 2.081 3.427 isopropylphthalimide
Acrylic-silicone copolymer solids) 0.000 1.009 1.009 1.009 1.009
Glyceryl Triacetate 0.000 0.000 0.000 4.772 3.427 Stearalkonium
Hectorite 1.036 1.036 1.036 1.036 1.036 Bismuth Oxychloride 0.40
0.40 0.40 0.40 0.40 Dimethicone 0.176 0.176 0.176 0.176 0.176 Iron
Oxides 0.811 0.811 0.811 0.811 0.811 Benzophenone-1 0.188 0.188
0.188 0.188 0.188 Phosphoric acid 0.018 0.018 0.018 0.018 0.018
Mica 1.387 1.387 1.387 1.387 1.387 D&C Red No. 34 0.160 0.160
0.160 0.160 0.160 Titanium Dioxide 0.515 0.515 0.515 0.515
0.515
[0055]
15TABLE 51 TEST RESULTS Pearl shade FORMULA FORMULA FORMULA FORMULA
FORMULA EP FP GP HP.sup.3 IP.sup.4 Hardness: 2 Hrs. 21 25 24 21 22
24 Hrs. 64 64 63 49 51 48 Hrs. 76 84 81 64 68 72 Hrs. 99 98 93 74
77 144 Hrs. 126 121 126 109 108 168 Hrs. 128 140 139 125 126
Adhesion: 24 Hrs. 5 5 5 5 5 48 Hrs. 5 5 5 5 5 72 Hrs. 5 5 5 5 5 144
Hrs. 5 5 5 5 5 168 Hrs. 5 5 5 5 5 Flexibility: 24 Hrs. Ok Ok Ok Ok
Ok 48 Hrs. Ok Ok Ok Ok Ok 72 Hrs. Ok Ok Ok Ok Ok 144 Hrs. Stretched
Stretched Stretched Ok Ok 168 Hrs. Sl. Cracked Sl. Cracked
Stretched Ok Ok
[0056] Testing of the red creme shade and the pearl shade was
performed to confirm that BIP formulations are usable in
formulations containing a variety of types and concentrations of
coloring agents. The red creme formulations displayed lesser
adhesion and flexibility than pearl shade formulations. This
performance parallels a tendency for the red creme shade to chip
more easily in phthalate-based formulations.
[0057] The nail enamel embodiments of the present invention are
made by blending the BIP into the formulation alone, or,
optionally, with other plasticizers. Other ingredients are added in
accordance with methods known to those skilled in the art. The nail
enamel is dispensed into containers. The containers typically have
applicators that are an integral part of the container or that are
packaged with the container. One type of applicator is a brush. The
enamel is applied to nails as a base coat or a topcoat.
[0058] A consumer use study was conducted on the mauve pearl shade.
The study included seven test subjects. The two products tested
included a formulation that included BIP and that was
phthalate-free and a formulation that included phthalates. There
was no difference detected between the two products for overall
wear and chipping. Gloss and appearance were also comparable,
although a preference for the gloss of the BIP containing formula
was noted in the laboratory.
[0059] Each of any foregoing patents, patent applications and
references described herein is incorporated by reference in its
entirety. Having described particular embodiments in accordance
with the present invention, it is believed that other
modifications, variations and changes will be suggested to those
skilled in the art in view of the teachings set forth herein. It
is, therefore, to be understood that all such variations,
modifications, and changes are believed to fall within the scope of
the present invention as defined by the appended claims.
* * * * *