U.S. patent application number 10/463461 was filed with the patent office on 2004-12-23 for cyanoacrylate compositions.
This patent application is currently assigned to LOCTITE (R&D) LTD.. Invention is credited to Birkett, David P., Kelly, Ruth A., Kneafsey, Brendan J., Misiak, Hanns R., Mulcahy, Kieran, Tierney, Fergal W., Woolfson, Harry J..
Application Number | 20040260045 10/463461 |
Document ID | / |
Family ID | 33517106 |
Filed Date | 2004-12-23 |
United States Patent
Application |
20040260045 |
Kind Code |
A1 |
Kneafsey, Brendan J. ; et
al. |
December 23, 2004 |
CYANOACRYLATE COMPOSITIONS
Abstract
This invention relates to cyanoacrylate-containing compositions
that include, in addition to the cyanoacrylate component, certain
accelerators to improve fixture speeds on certain substrates.
Inventors: |
Kneafsey, Brendan J.;
(Hermitage Park, IE) ; Kelly, Ruth A.; (Dublin,
IE) ; Tierney, Fergal W.; (Celbridge, IE) ;
Birkett, David P.; (Naas, IE) ; Misiak, Hanns R.;
(Dublin, IE) ; Mulcahy, Kieran; (Naas, IE)
; Woolfson, Harry J.; (Dublin, IE) |
Correspondence
Address: |
HENKEL LOCTITE CORPORATION
1001 Trout Brook Crossing
Rocky Hill
CT
06067
US
|
Assignee: |
LOCTITE (R&D) LTD.
|
Family ID: |
33517106 |
Appl. No.: |
10/463461 |
Filed: |
June 18, 2003 |
Current U.S.
Class: |
526/307.3 ;
524/555; 524/556; 526/209; 526/213; 526/89 |
Current CPC
Class: |
C09J 4/00 20130101; C08K
5/10 20130101; C09J 4/00 20130101; C08F 22/32 20130101; C08F 222/32
20130101 |
Class at
Publication: |
526/307.3 ;
524/556; 524/555; 526/209; 526/213; 526/089 |
International
Class: |
C08F 002/00 |
Claims
1. A cyanoacrylate adhesive composition comprising: a cyanoacrylate
component; and an accelerator represented by the following chemical
structure 16 wherein R is a member selected from the group
consisting of hydrogen, alkyl, alkyloxy, alkyl thioethers,
haloalkyl, carboxylic acid and esters thereof, sulfinic, sulfonic
and sulfurous acids and esters, phosphinic, phosphonic and
phosphorous acids and esters thereof, X is [optional, but when
present is] an aliphatic or aromatic hydrocarbyl linkage, which may
be substituted by oxygen or sulfur, Z is a single or double bond, n
is 1-12, m is 1-4, and p is 1-3.
2. The composition of claim 1, wherein the accelerator is
represented by the following chemical structure 17wherein R, X, n,
m, and p are as defined above.
3. The composition of claim 1, wherein the accelerator is
represented by the following chemical structure 18wherein R, Z, n,
and p are as defined above, R' is the same as R, and g is 1-12.
4. The composition of claim 1, wherein the accelerator is
represented by the following chemical structure 19wherein n and m
combined are greater than or equal to 12.
5. The composition according to claim 1, wherein the cyanoacrylate
component is selected from materials within the structure
H.sub.2C.dbd.C(CN)--COOR, wherein R is selected from C.sub.1-15
alkyl, alkoxyalkyl, cycloalkyl, alkenyl, aralkyl, aryl, allyl and
haloalkyl groups.
6. The composition according to claim 1, wherein the cyanoacrylate
component comprises ethyl-2-cyanoacrylate.
7. The composition according to claim 1, further comprising an
additional accelerator component selected from the group consisting
of calixarenes, oxacalixarenes, silacrowns, cyclodextrins, crown
ethers, poly(ethyleneglycol) di(meth)acrylates, ethoxylated hydric
compounds, and combinations thereof.
8. The composition according to claim 1, wherein the accelerator is
used in an amount within the range of from about 0.01% by weight to
about 5% by weight based on the total composition.
9. The composition according to claim 7, wherein the additional
accelerator component is used in an amount within the range of from
about 0.01% by weight to about 5% by weight based on the total
composition.
10. The composition according to claim 1, further comprising
additives selected from the group consisting of free radical
stabilizers, anionic stabilizers, plasticizers, thixotropy
conferring agents, thickeners, dyes, toughening agents, thermal
degradation enhancers, and combinations thereof.
11. (Cancelled).
12. Reaction products of the composition according to claim 1.
13. A method of bonding together two substrates, at least one of
which is constructed of a material selected from the group
consisting of wood and ceramic, comprising the steps of: applying a
cyanoacrylate-containing adhesive composition according to claim 1,
to at least one of the substrates and mating together the
substrates for a time sufficient to permit the adhesive to
fixture.
14. A method of preparing a cyanoacrylate-containing composition
according to claim 1, comprising the steps of: providing a
cyanoacrylate component, and combining therewith with mixing an
accelerator component.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] This invention relates to cyanoacrylate-containing
compositions that include, in addition to the cyanoacrylate
component, a certain accelerator to improve fixture speeds on
certain substrates.
[0003] 2. Brief Description of Related Technology
[0004] Cyanoacrylate adhesive compositions are well known, and
widely used as quick setting, instant adhesives with a wide variety
of uses. See H. V. Coover, D. W. Dreifus and J. T. O'Connor,
"Cyanoacrylate Adhesives" in Handbook of Adhesives, 27, 463-77, I.
Skeist, ed., Van Nostrand Reinhold, N.Y., 3rd ed. (1990). See also
G. H. Millet "Cyanoacrylate Adhesives" in Structural Adhesives:
Chemistry and Technology, S. R. Hartshorn, ed., Plenun Press, New
York, p. 249-307 (1986).
[0005] Nonetheless, various techniques have been used to improve
further the fixture times of such adhesive compositions for certain
applications where it is important to be able to secure one
substrate to another quickly, while allowing the bond strength to
develop over time. In addition, substrates constructed of certain
materials have proven in the past difficult to bond, irrespective
of the application to which the adhesive and the substrate are to
be placed.
[0006] To combat these issues, Henkel Loctite Corporation [then
Loctite Corporation, at least in part through its Loctite (Ireland)
Ltd. affiliate] developed a technology based on calixarene and
oxacalixarene compounds. Generally, the addition of such materials
to a cyanoacrylate allow for accelerated fixturing of substrates
to-be-bonded together. See U.S. Pat. Nos. 4,556,700, 4,622,414,
4,636,539, 4,695,615, 4,718,966, and 4,855,461.
[0007] In addition to calixarene compounds, Henkel Loctite
Corporation also developed technology based on the addition of
silacrown compounds to cyanoacrylate adhesive compositions to
accelerate fixturing. For instance, U.S. Pat. No. 4,906,317 (Liu)
is directed to cyanoacrylate adhesive compositions which include
silacrown compounds as additives to give substantially reduced
fixture and cure times on de-activating substrates such as wood.
The silacrown compounds are preferably employed at levels of about
0.1-5% by weight of the composition.
[0008] Henkel KGaA developed technology based on the addition to
cyanoacrylate compositions of cyclodextrins to accelerate
fixturing. In U.S. Pat. No. 5,312,864 (Wenz), the acceleration of
the setting properties of a cyanoacrylate adhesive composition by
adding thereto a hydroxyl group derivative of an .alpha.-, .beta.-
or .gamma.-cyclodextrin which is at least partly soluble in the
cyanoacrylate is described.
[0009] Other approaches have also been investigated, such as in
U.S. Pat. No. 4,837,260 (Sato), in which it is reported the use of
crown ethers in cyanoacrylate adhesive compositions.
[0010] More recently, Loctite (R&D) Ltd. investigated other
ways in which to accelerate the curing of cyanoacrylate adhesive
compositions. In U.S. Pat. No. 6,294,629 (O'Dwyer), a cyanoacrylate
adhesive composition is provided with a first accelerator component
selected from calixarenes and oxacalixarenes, silacrowns,
cyclodextrins, crown ethers, and combinations thereof; and a second
accelerator component selected from poly(ethyleneglycol)
di(meth)acrylates, ethoxylated hydric compounds, and combinations
thereof.
[0011] And Henkel Loctite Corporation developed a cyanoacrylate
adhesive composition, based on a cyanoacrylate component; and an
accelerator component consisting essentially of (i) calixarenes,
oxcalixarenes, or a combination thereof, and (ii) at least one
crown ether, where the composition exhibits a fixturing speed of
less than 20 seconds for bonding two substrates, at least one of
which is constructed of a material selected from steel, epoxy glass
or balsawood, as described in U.S. Pat. No. 6,475,331
(O'Connor).
[0012] Notwithstanding the state-of-the-technology it would be
desirable to provide alternative technologies to improve the
fixturing speed of cyanoacrylates.
SUMMARY OF THE INVENTION
[0013] The present invention is directed to a cyanoacrylate-based
composition, which includes beyond the cyanoacrylate component,
1
[0014] I, as an accelerator, where R is hydrogen, alkyl, alkyloxy,
alkyl thioethers, haloalkyl, carboxylic acid and esters thereof,
sulfinic, sulfonic and sulfurous acids and esters, phosphinic,
phosphonic and phosphorous acids and esters thereof, X is optional,
but when present is an aliphatic or aromatic hydrocarbyl linkage,
which may be substituted by oxygen or sulfur, and Z is a single or
double bond, such as 2
[0015] II, where R and X are as defined above, and n is 1-12, m is
1-4, and p is 1-3.
[0016] For instance, a particularly desirable chemical class
embraced by these structures is 3
[0017] III, where R, Z and n are as defined above, and R' is the
same as R, where g is the same as n.
[0018] A particularly desirable chemical within this class as an
accelerator component is 4
[0019] IV, where n and m combined is greater than or equal to
12.
[0020] The inclusion of these accelerators into a cyanoacrylate
composition provides for a demonstrated improved fixture speeds,
particularly on substrates constructed of certain woods, and
ceramic and combinations thereof, without sacrificing shelf
life.
[0021] This invention is also directed to a method of bonding
together two substrates, at least one of which is constructed of
certain woods, and ceramic, and combinations thereof. The method
includes applying to at least one of the substrates a composition
as described above, and thereafter mating together the
substrates.
[0022] In addition, the present invention is directed to reaction
products of the inventive compositions.
[0023] Also, the invention is directed to a method of preparing the
inventive compositions.
[0024] The invention will be more fully understood by a reading of
the section entitled "Detailed Description of the Invention", which
follows.
BRIEF DESCRIPTION OF THE FIGURE
[0025] FIG. 1 shows a comparative chart of Samples A-D, where MDF
is medium density fiberboard, ABS is acrylonitrile butadiene
styrene copolymer, Al is aluminum and SS is stainless steel.
DETAILED DESCRIPTION OF THE INVENTION
[0026] As noted above, this invention is directed to a
cyanoacrylate-based composition, which includes beyond the
cyanoacrylate component, 5
[0027] I, as an accelerator, where R is hydrogen, alkyl, alkyloxy,
alkyl thioethers, haloalkyl, carboxylic acid and esters thereof,
sulfinic, sulfonic and sulfurous acids and esters, phosphinic,
phosphonic and phosphorous acids and esters thereof, X is optional,
but when present is an aliphatic or aromatic hydrocarbyl linkage,
which may be substituted by oxygen or sulfur, and Z is a single or
double bond, such as 6
[0028] II, where R and X are as defined above.
[0029] For instance, a particularly desirable chemical class
embraced by these structures is 7
[0030] III, where R, Z and n are as defined above, and R' is the
same as R, and g is the same as n.
[0031] A particularly desirable chemical within this class as an
accelerator component is 8
[0032] IV, where n and m combined are greater than or equal to
12.
[0033] The inclusion of such an accelerator into a cyanoacrylate
composition provides for a demonstrated improved fixture speeds,
particularly on substrates constructed of certain woods, such as
obechi, and ceramic, and combinations thereof, without sacrificing
shelf life.
[0034] The cyanoacrylate component includes cyanoacrylate monomers
which may be chosen with a raft of substituents, such as those
represented by H.sub.2C.dbd.C(CN)--COOR, where R is selected from
C.sub.1-15 alkyl, alkoxyalkyl, cycloalkyl, alkenyl, aralkyl, aryl,
allyl and haloalkyl groups. Desirably, the cyanoacrylate monomer is
selected from methyl cyanoacrylate, ethyl-2-cyanoacrylate, propyl
cyanoacrylates, butyl cyanoacrylates (such as
n-butyl-2-cyanoacrylate), octyl cyanoacrylates, allyl
cyanoacrylate, .beta.-methoxyethyl cyanoacrylate and combinations
thereof. A particularly desirable one is ethyl-2-cyanoacrylate.
[0035] The cyanoacrylate component should be included in the
compositions in an amount within the range of from about 50% to
about 99.98% by weight, with the range of about 90% to about 99% by
weight being desirable, and about 95% by weight of the total
composition being particularly desirable.
[0036] In addition to the accelerator embraced by the chemical
structures above, one or more additional accelerators may also be
included in the composition. Such accelerators may be selected from
calixarenes and oxacalixarenes, silacrowns, crown ethers,
cyclodextrins, poly(ethyleneglycol) di(meth)acrylates, ethoxylated
hydric compounds and combinations thereof.
[0037] Of the calixarenes and oxacalixarenes, many are known, and
are reported in the patent literature. See e.g. U.S. Pat. Nos.
4,556,700, 4,622,414, 4,636,539, 4,695,615, 4,718,966, and
4,855,461, the disclosures of each of which are hereby expressly
incorporated herein by reference.
[0038] For instance, as regards calixarenes, those within structure
V are useful herein: 9
[0039] where R.sup.1 is alkyl, alkoxy, substituted alkyl or
substituted alkoxy; R.sup.2 is H or alkyl; and n is 4, 6 or 8.
[0040] One particularly desirable calixarene is tetrabutyl
tetra[2-ethoxy-2-oxoethoxy]calix-4-arene ("TBTEOCA").
[0041] A host of crown ethers are known. For instance, examples
which may be used herein either individually or in combination, or
in combination with other first accelerators include 15-crown-5,
18-crown-6, dibenzo-18-crown-6,
benzo-15-crown-5-dibenzo-24-crown-8, dibenzo-30-crown-10,
tribenzo-18-crown-6, asym-dibenzo-22-crown-6, dibenzo-14-crown-4,
dicyclohexyl-18-crown-6, dicyclohexyl-24-crown-8,
cyclohexyl-12-crown-4, 1,2-decalyl-15-crown-5,
1,2-naphtho-15-crown-5, 3,4,5-naphtyl-16-crown-5,
1,2-methyl-benzo-18-crown-6, 1,2-methylbenzo-5,
6-methylbenzo-18-crown-6, 1,2-t-butyl-18-crown-6,
1,2-vinylbenzo-15-crown- -5, 1,2-vinylbenzo-18-crown-6,
1,2-t-butyl-cyclohexyl-18-crown-6, asym-dibenzo-22-crown-6 and
1,2-benzo-1,4-benzo-5-oxygen-20-crown-7. See U.S. Pat. No.
4,837,260 (Sato), the disclosure of which is hereby expressly
incorporated here by reference.
[0042] Of the silacrowns, again many are known, and are reported in
the literature. For instance, a typical silacrown may be
represented within the following structure (VI): 10
[0043] where R.sup.3 and R.sup.4 are organo groups which do not
themselves cause polymerization of the cyanoacrylate monomer,
R.sup.5 is H or CH.sub.3 and n is an integer of between 1 and 4.
Examples of suitable R.sup.3 and R.sup.4 groups are R groups,
alkoxy groups, such as methoxy, and aryloxy groups, such as
phenoxy. The R.sup.3 and R.sup.4 groups may contain halogen or
other substituents, an example being trifluoropropyl. However,
groups not suitable as R.sup.4 and R.sup.5 groups are basic groups,
such as amino, substituted amino and alkylamino.
[0044] Specific examples of silacrown compounds useful in the
inventive compositions include: 11
[0045] dimethylsila-11-crown-4 (VII); 12
[0046] dimethylsila-14-crown-5 (VIII); 13
[0047] and dimethylsila-17-crown-6 (IX).
[0048] See e.g., U.S. Pat. No. 4,906,317 (Liu), the disclosure of
which is hereby expressly incorporated herein by reference.
[0049] Many cyclodextrins may be used in connection with the
present invention. For instance, those described and claimed in
U.S. Pat. No. 5,312,864 (Wenz), the disclosure of which is hereby
expressly incorporated herein by reference, as hydroxyl group
derivatives of an .alpha., .beta. or .gamma.-cyclodextrin which is
at least partly soluble in the cyanoacrylate would be appropriate
choices for use herein as the first accelerator component.
[0050] For instance, poly(ethylene glycol) di(meth)acrylates
suitable for use herein include there within structure X below:
14
[0051] where n is greater than 3, such as within the range of 3 to
12, with n being 9 as particularly desirable. More specific
examples include PEG 200 DMA, (where n is about 4) PEG 400 DMA
(where n is about 9), PEG 600 DMA (where n is about 14), and PEG
800 DMA (where n is about 19), where the number (e.g., 400)
represents the average molecular weight of the glycol portion of
the molecule, excluding the two methacrylate groups, expressed as
grams/mole (i.e., 400 g/mol). A particularly desirable PEG DMA is
PEG 400 DMA.
[0052] And of the ethoxylated hydric compounds (or ethoxylated
fatty alcohols that may be employed), appropriate ones may be
chosen from those within structure XI: 15
[0053] where C.sub.m can be a linear or branched alkyl or alkenyl
chain, m is an integer between 1 to 30, such as from 5 to 20, n is
an integer between 2 to 30, such as from 5 to 15, and R may be H or
alkyl, such as C.sub.1-6 alkyl.
[0054] Commercially available examples of materials within
structure XI include those offered under the DEHYDOL tradename from
Cognis Deutschland GmbH & Co. KG, Dusseldorf, Germany, such as
DEHYDOL 100.
[0055] The accelerator embraced by structures I-IV should be
included in the compositions in an amount within the range of from
about 0.01% to about 10% by weight, with the range of about 0.1 to
about 0.5% by weight being desirable, and about 0.4% by weight of
the total composition being particularly desirable.
[0056] Additives may be included in the inventive compositions to
confer additional physical properties, such as improved shelf-life
stability, flexibility, thixotropy, increased viscosity, color,
improved toughness, and enhanced resistance to thermal degradation.
Such additives therefore may be selected from free radical
stabilizers, anionic stabilizers, gelling agents, thickeners [such
as polymethyl methacrylate (PMMA)], thixotropy conferring agents
(such as fumed silica), dyes, toughening agents, thermal
degradation enhancers, plasticizers and combinations thereof.
[0057] In another aspect of the invention, there is provided a
method of bonding together two substrates, at least one of which is
constructed of materials, such as certain woods, cotton and cork.
The method includes applying to at least one of the substrates a
composition as described above, and thereafter mating together the
substrates for a time sufficient to permit the adhesive to fixture.
For many applications, the substrate should become fixed in less
than 30 seconds, and depending on substrate as little as 1-3
seconds.
[0058] In yet another aspect of the invention, there is provided
reaction products of the so-described compositions.
[0059] In still another aspect of the invention, there is provided
a method of preparing the so-described compositions. The method
includes providing a cyanoacrylate component, and combining
therewith with mixing a first and second accelerator component.
[0060] In an additional aspect of the invention, there is provided
a method of bonding together two substrates, at least one of which
is constructed of a material selected from the group consisting of
wood, cotton and cork, using the compositions of this invention.
The method includes applying the compositions to at least one of
the substrates and mating together the substrates for a time
sufficient to permit the composition to fixture.
[0061] These aspects of the invention will be further illustrated
by the examples which follow.
EXAMPLES
[0062] We prepared four samples to evaluate their fixture speeds on
a variety of substrates. The samples were prepared by mixing
together the constituents in any order for a sufficient period of
time to ensure substantial homogeneity of the constituents.
Ordinarily, about 30 minutes would suffice, depending of course on
the quantity of the constituents used. The constituents of these
samples are listed below in Table 1.
1TABLE 1 Component Sample Type Identity A B C D CA Ethyl-2-CA
82.4983 82.4983 82.3983 82.3983 Accelerator Compound IV 0.5 0.5 0.4
-- TBTEOCA -- -- 0.2 0.2 PEG 400 DMA -- -- -- 0.4 Plasticizer
Glycerol 12.5 12.5 12.5 12.5 triacetate Stabilizer HQ 0.5 0.5 0.5
0.5 Thickener PMMA 4.0 4.0 4.0 4.0
[0063] We applied each of Samples A-D to the substrates listed
below in Table 2, and measured their fixture speeds in bonding the
substrates (each being made from the same material) to one another.
The fixture speed is the time from joining the two substrates (each
of which being about 1 inch wide and being aligned with about a 0.5
inch overlap) sufficient to hold a 3 kg weight. The results are
illustrated below in Table 2 and shown in FIG. 1.
2 TABLE 2 Physical Sample/(secs) Properties Substrate A B C D
Fixture Paper 40 40 10 10 Times MOF 40 40 25 40 Obechi 10 10 15 15
Yellow Pine 30 30 25 20 Ash 10 10 10 15 W. Deal 40 40 15 40 Limba
10 10 10 15 Ceramic/butt 10 10 15 15 Balsa 3 3 3 3 Cardboard 10 10
5 5 Polycarbonate 25 25 25 25 ABS 3 3 3 3 Aluminum 3 3 3 3
Stainless 3 3 3 3 steel
[0064] As can be seen from Table 2 and FIG. 1, Samples A and B
(cyanoacrylate with compound IV) demonstrates improved fixture
speeds on certain substrates, namely the woods, obechi; ash and
limba, and ceramic, as compared with Sample D, which is the
cyanoacrylate with the combination of the noted calixarenes and
polyethylene glycol dimethacrylate.
[0065] In addition, the combination of the accelerator used in the
present invention together with the noted calixarene (Sample C)
improves fixture speed compared with the combination of the noted
calixarene together with the noted polyethylene glycol
dimethacrylate on certain substrates namely, MDF, ash, white deal
and limba.
3TABLE 3 Physical Sample Properties A B C D Viscosity (MPas) 32 32
34.4 34.1 GBMS Bond 13.57 +/- 12.70 +/- 13.86 +/- 12.70 +/-
Strength 24 hr. 1.56 1.54 1.00 1.15 (N/mm2)
[0066] The results shown in Table 3 illustrate that the inventive
compositions (Samples A-C) behave as adhesives, yielding bond
strength comparable to the control composition (Sample D), while
demonstrating with reference to Table 2 improved fixture speeds on
certain substrates, namely the woods, obechi, ash and limba, and
ceramic.
[0067] In Table 4, stability data for Samples A-D filled in
aluminum tubes and aged at 82.degree. C. for the specified period
of time is shown. The results in Table 4 demonstrate that the
inventive compositions retain the benefits noted above even after
ageing under the noted conditions.
4TABLE 4 Aged Sample Data A B C D 3 days @ 82.degree. C. Viscosity
(Mps) 36 35.7 35.3 36.5 Ratio 1.13 1.12 1.04 1.07 Fixture time
40-50 40-50 5-10 10-15 (secs) on paper 6 days @ 82.degree. C.
Viscosity (Mps) 38.2 39.4 40.3 39.2 Ratio 1.19 1.23 1.17 1.15
Fixture time 80-100 80-100 15-20 30-40 (secs) on paper
* * * * *