U.S. patent application number 10/896261 was filed with the patent office on 2004-12-23 for hydrogen generation system.
Invention is credited to Corbett, Timothy J., Liu, Qin, Mann, L. Chris, Prasad, Ravi.
Application Number | 20040258966 10/896261 |
Document ID | / |
Family ID | 29419638 |
Filed Date | 2004-12-23 |
United States Patent
Application |
20040258966 |
Kind Code |
A1 |
Mann, L. Chris ; et
al. |
December 23, 2004 |
Hydrogen generation system
Abstract
Hydrogen generation system. A source of sodium borohydride is
carried on a flexible substrate that moves from a feed roll to a
takeup roll. A reaction among sodium borohydride, a catalyst and
water evolves hydrogen and forms a by-product that is removed from
the reaction area.
Inventors: |
Mann, L. Chris; (Corvallis,
OR) ; Corbett, Timothy J.; (Corvallis, OR) ;
Liu, Qin; (Corvallis, OR) ; Prasad, Ravi;
(Corvallis, OR) |
Correspondence
Address: |
HEWLETT-PACKARD COMPANY
Intellectual Property Administration
P. O. Box 272400
Fort Collins
CO
80527-2400
US
|
Family ID: |
29419638 |
Appl. No.: |
10/896261 |
Filed: |
July 20, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10896261 |
Jul 20, 2004 |
|
|
|
10157279 |
May 28, 2002 |
|
|
|
6790416 |
|
|
|
|
Current U.S.
Class: |
429/421 ;
429/444; 429/515; 48/118.5 |
Current CPC
Class: |
B01J 16/005 20130101;
H01M 2250/30 20130101; H01M 8/04216 20130101; Y02E 60/50 20130101;
H01M 8/04208 20130101; Y02B 90/10 20130101; B01J 7/02 20130101;
C01B 3/065 20130101; Y02E 60/36 20130101; F17C 11/005 20130101;
H01M 8/065 20130101; Y02E 60/32 20130101; B01J 19/22 20130101 |
Class at
Publication: |
429/019 ;
048/118.5 |
International
Class: |
H01M 008/06; C10J
003/20 |
Claims
What is claimed is:
1-14 (Canceled)
15. Fuel cell system comprising: a fuel cell; and a hydrogen
generator connected to deliver hydrogen to the fuel cell, the
hydrogen generator comprising: means for contracting sodium
borohydride, water, and catalyst; and means for moving reactants
away from a reaction zone.
16. Electronic devices system comprising; a hydrogen generator for
generating hydrogen; a fuel cell for receiving the hydrogen to
generate electricity; and an electronic device connected to receive
electrical energy from the fuel cell, the hydrogen generator
comprising; means for contracting sodium borohydride, water, and
catalyst to release hydrogen; and means for moving reactants away
from a reaction zone.
17. Fuel cartridge comprising; replaceable structure including
sodium borohydride, water, and a catalyst; and means for
contracting the sodium borohydride, water, and catalyst to release
hydrogen and further including means for moving reactants into and
away from a reaction zone.
18-20 (Canceled)
Description
BACKGROUND OF THE INVENTION
[0001] This invention relates to hydrogen generation, and more
particularly, to a system for the catalytic hydrolysis of sodium
borohydride.
[0002] As is well known, fuel cells combine hydrogen and oxygen to
generate electricity. In some applications, it is necessary to
precisely and accurately meter hydrogen, on demand, to a fuel cell
to control the electrical output. An example is a miniaturized PEM
fuel cell.
[0003] It is also known that hydrogen can be evolved from reactive
solutions such as by the catalytic hydrolysis of sodium
borohydride, NaBH.sub.4. A prior art approach for generating
hydrogen on demand for use in fuel cells utilized pumps to deliver
an aqueous solution of sodium borohydride to a catalyst bed. There
are, however, problems with this approach. A stoichiometric sodium
borohydride aqueous solution has high viscosity that makes it
difficult to pump in a precise manner. Sometimes nonreactive
chemicals were added to lower the viscosity or a nonstoichiometric
ratio was used to aid pumping. Alternatively, a strong base, such
as sodium hydroxide, was added to the sodium borohydride solution
in an effort to stabilize it. The resulting solution was then
caustic making handling more difficult.
[0004] Another problem with the prior art approach is that the
hydrolysis reaction generates a by-product, sodium metaborate,
NaBO.sub.4, that must be removed. Sodium metaborate tends to pick
up water and to gel when allowed to cool. Its presence hinders
access to the catalyst and makes the water needed for the reaction
less available. If this reaction product is allowed to cool and
gel, it cannot be readily pumped away.
[0005] Another approach to evolving hydrogen from sodium
borohydride is to heat the material to generate hydrogen as needed.
A problem with this approach is high parasitic loss and another
problem may be material compatibility issues.
SUMMARY OF THE INVENTION
[0006] The hydrogen generation system of the invention includes a
source of sodium borohydride along with a source of water and a
catalyst such as ruthenium. Structure is provided for contacting
sodium borohydride, water and catalyst to release hydrogen and to
move the reactants into and away from a reaction zone.
A BRIEF DESCRIPTION OF THE DRAWING
[0007] FIG. 1 is a block diagram of an exemplary embodiment of the
system of the invention.
[0008] FIG. 2 is perspective view of one embodiment of the
invention.
[0009] FIG. 3 is a perspective view of another embodiment of the
invention.
[0010] FIG. 4 is a perspective view of yet another embodiment of
the invention.
[0011] FIG. 5 is a block diagram of a fuel cell utilizing a
hydrogen generator to generate electricity.
[0012] FIG. 6 is a block diagram of an electronic device receiving
electricity from a fuel cell.
DESCRIPTION OF THE PREFERRED EMBODIMENT
[0013] In one embodiment, a solution of sodium borohydride and
water is encapsulated and supported on a flexible substrate. In
this embodiment, the solution is encapsulated in rupturable
microspheres, and the flexible substrate includes the catalyst
thereon. This embodiment further includes means to rupture the
microspheres to allow the solution to contact the catalyst. In this
embodiment, the rupturing means includes rollers forming a nip
therebetween.
[0014] In another aspect, the aqueous sodium borohydride solution
is encapsulated in a penetratable compartment carried on a flexible
substrate and the system further includes a catalyst-containing
structure for penetrating the compartment to allow the catalyst to
contact the solution. In this embodiment, the catalyst-containing
structure forms spike-like elements extending from a roller. In
these preferred embodiments, the flexible substrate moves from a
supply roll to a take-up roll, and in this way the sodium
metaborate by-product is removed from the reaction zone.
[0015] In another embodiment, the sodium borohydride is supported
in solid form on a flexible substrate for contact with a
catalyst-coated element, and the system further includes structure
for supplying water to contact the sodium borohydride and catalyst.
In this embodiment, it is preferred that the catalyst-coated
element be hollow and perforated and that water is supplied to the
interior of the element. A suitable catalyst for all of these
above-described embodiments is ruthenium.
[0016] The hydrogen generation system of the present invention
accurately meters hydrogen on demand and the sodium metaborate
reaction product is removed from the reaction zone so as not to
interfere with the hydrolysis reaction.
[0017] With reference first to FIG. 1, block 7 represents a source
of sodium borohydride, water, and a catalyst. These materials are
contacted to one another in a reaction zone 8 to generate hydrogen
and a reaction product, sodium metaborate 9, is removed from the
reaction zone 8 so that the reaction is not impeded.
[0018] Another embodiment of the invention is shown in FIG. 2. A
thin, flexible film is supported to move from a feed roll 12 onto a
take-up roll 14. A suitable film 10 is porous polypropylene film or
expanded polytetrafluoroethylene (PTFE). The flexible film 10
supports on its surface a plurality of cells 16 that contain
therewithin a reactive solution such as NaBH.sub.4 and water. The
flexible film 10 and cells 16 form a structure analogous to bubble
wrap. In addition to the feed roll 12 and take-up roll 14, there is
provided a pair of rolls 18 and 20 through the nip of which passes
the film 10 along with the cells 16. The roll 18 includes structure
to penetrate the cells 16 as they pass through the nip between the
rolls 18 and 20. As shown in FIG. 2, spikes 22 are provided on the
surface of the roll 18 to rupture the cells 16. Other structures
such as ridges may be used to penetrate the cells 16. Preferably,
the spikes 22 are coated with a suitable catalyst such as ruthenium
to catalyze the hydrolysis reaction.
[0019] In operation, the film structure 10 advances toward the
take-up roll 14. As the film 10 passes through the nip formed by
the rollers 18 and 20, the spikes 22 rupture the cells 16 allowing
an aqueous solution of sodium borohydride to come into contact with
the catalyst on the spikes 22. The catalyst, such as ruthenium,
catalyzes an hydrolysis reaction so that hydrogen gas is released.
The sodium metaborate, NaBO.sub.4, by-product (shown in FIG. 1) is
carried away from the reaction zone at the rolls 18 and 20 onto the
take-up roll 14. In this way, the sodium metaborate by-product is
disposed of. It will be appreciated by those skilled in the art
that the rate of hydrogen evolution is controlled by the speed of
the film 10 past the roll 18 and the relative density of the cells
16 on the film 10.
[0020] The arrangement illustrated in FIG. 2 allows the cells 16 to
contain a stoichiometric sodium borohydride solution since no
pumping of a viscous solution is required and the waste by-product
is removed from the reaction zone. It is contemplated that the film
10 will be configured to be a replaceable cartridge for ease of
use.
[0021] Another embodiment of the invention is shown in FIG. 3. This
embodiment is similar to that discussed above in conjunction with
FIG. 2. In the embodiment of FIG. 3, glass or polymer microspheres
24 are disposed on the flexible membrane 10. Each of the
microspheres 24 contains an aqueous sodium borohydride solution.
The membrane 10 is doped with a metallic catalyst such as
ruthenium. As the membrane 10 passes through the rolls 18 and 20
the microspheres 24 are crushed allowing the aqueous sodium
borohydride solution to contact the catalyst (not shown) carried on
the film 10. As with the embodiment of FIG. 2, hydrogen gas is
released. Alternatively, the catalyst could be on the surface of
the rolls 18 and/or 20 instead of being on the membrane 10.
[0022] It is preferred that the microspheres 24 be affixed to the
substrate 10 having a consistent concentration (number of
microspheres per area). With a consistent concentration of
microspheres 24, the rate of hydrogen gas evolution can be
controlled precisely by controlling the speed of the membrane 10.
As with the embodiment of FIG. 2 the evolved hydrogen gas may be
supplied to a fuel cell such as a PEM fuel cell (not shown). Unlike
the embodiment of FIG. 2, the roll 18 may have a smooth surface for
crushing the microspheres 24.
[0023] The system illustrated in FIG. 3 can respond to changes in
hydrogen demand very quickly. Additionally, the sodium metaborate
waste by-product will be carried away from the reaction site. In
fact, the reaction site will remain clean because the reactants and
catalysts are continually being replenished.
[0024] Yet another embodiment of the invention is shown in FIG. 4.
As with the earlier embodiments, a flexible carrier film 10 moves
from a feed roll 12 to a take up roll 14. The film 10 carries on
its surface a solid hydrogen source such as solid sodium
borohydride. Suitable films 10 are flexible, porous, as thin as
possible, and nonreactive to the catalysts, sodium borohydride, its
by-product, hydrogen and water. It is also preferred that the film
10 not absorb water and be as low cost as possible. Porous
polypropylene film, such as Celgard.TM. is suitable. Also suitable
is expanded PTFE. It may be desirable to provide a binder or an
overcoat to hold the sodium borohydride in place on the film 10.
Suitable binder or overcoat materials should also be nonreactive to
the compounds mentioned above and be flexible while allowing water
to reach the sodium borohydride. Suitable overcoat materials are
hydrocarbon polymers and more polar polymers such as polyvinyl
alcohol and polyethyleneimine. A shrink-wrap kind of process might
be used with the Celgard.TM. film to keep the sodium borohydride in
place.
[0025] The carrier film 10 is brought into contact with
catalyst-coated rods 30 as it moves from the feed roll 12 to takeup
roll 14 as shown. A suitable catalyst is ruthenium. It is preferred
that the rods 30 be hollow and perforated so that water can be
pumped through the openings and reach the sodium borohydride on the
film 10. The rods 30 may also be connected to an electrical circuit
adapted to heat the rods 30 if desired. The rods 30 are preferably
made of a nonreactive metal such as stainless steel onto which the
catalyst coating is applied. The rods 30 are housed in a chamber 32
having hydrogen outlet 34 to connect, for example, to a fuel cell
(not shown).
[0026] In operation, the solid sodium borohydride carried on the
film 10 comes into contact with the catalyst coated rods 30 along
with water preferably supplied through the rods 30. The resulting
reaction, as with the previous embodiments, generates hydrogen and
a sodium metaborate by-product. This reaction by- product will be
carried out of the enclosure 32 and onto the take up roll 14.
[0027] Before use, the carrier film 10 on the feed roll 12 may be
configured as a replaceable cartridge and may be stored in a
flexible, impermeable bag. Similarly, after use the take up roll 14
may also be enclosed in a flexible, impermeable bag.
[0028] With reference now to FIG. 5, a fuel cell 40 such as a PEM
fuel cell receives hydrogen from a hydrogen generator 42 to
generate electricity. Suitable hydrogen generators 42 are those
shown in FIGS. 2, 3, and 4. In another aspect, the invention
illustrated in FIG. 6 is an electronic device 44 which is powered
by electricity from fuel cell 40, which in turn receives hydrogen
from a hydrogen generator 42. The electronic device 44 may be any
electronic device such as cellphones, cam corders, computers, and
personal digital assistants.
[0029] It is recognized that modifications and variations of this
invention will become apparent to those skilled in the art and it
is intended that all such modifications and variations be included
within the scope of the attended claims.
* * * * *