U.S. patent application number 10/797378 was filed with the patent office on 2004-11-11 for antistatic polymers, blends, and articles.
This patent application is currently assigned to Noveon IP Holdings Corp.. Invention is credited to Bialke, Julie Vaughn, Canady, John B., Hsu, Shui-Jen Raymond, Lubnin, Alexander V., Masler, William F. III, Valentino, Beth A..
Application Number | 20040225052 10/797378 |
Document ID | / |
Family ID | 24439263 |
Filed Date | 2004-11-11 |
United States Patent
Application |
20040225052 |
Kind Code |
A1 |
Bialke, Julie Vaughn ; et
al. |
November 11, 2004 |
Antistatic polymers, blends, and articles
Abstract
This invention relates to latex polymers and blends of such
latex polymers used to produce gloves, coatings, binders for papers
and nonwovens, and other articles having superior electrostatic
dissipative properties. Such articles have a surface resistivity
value below 1.times.10.sup.11 ohms/square per square, a static
decay time of less than 1 second, or both. The blends comprise one
or more (1) polymers (in latex, solution or dispersion form) of (a)
at least one reactive macromer of at least one alkylene oxide
having at least one functional group capable of free-radical
transformation, (b) optionally at least one ethylenically
unsaturated monomer having at least one carboxylic acid group, and
(c) optionally one or more free radically polymerizable comonomers,
and (2) one or more other polymer latexes or dispersions of such
polymers as natural rubber, conjugated-diene-containing polymers,
hydrogenated styrene-butadiene triblock copolymers,
chlorosulfonated polyethylenes, ethylene copolymers, acrylic and/or
methacrylic ester copolymers, vinyl chloride copolymers, vinylidene
chloride copolymers, polyisobutylenes, polyurethanes, polyureas,
and poly(urethane-u rea)s. Also suitable for making antistatic
articles such as gloves by coagulant dipping processes, even in the
absence of said (2) other polymer latexes or dispersions, are (1)
polymers (in latex, solution or dispersion form) of (a) at least
one reactive macromer of at least one alkylene oxide having at
least one functional group capable of free-radical transformation,
wherein said macromer comprises less than about 10 wt. % of total
polymer weight in the (1) latex, solution or dispersion polymers,
(b) optionally at least one ethylenically unsaturated monomer
having at least one carboxylic acid group, and (c) one or more free
radically polymerizable comonomers.
Inventors: |
Bialke, Julie Vaughn;
(Akron, OH) ; Canady, John B.; (Akron, OH)
; Hsu, Shui-Jen Raymond; (Westlake, OH) ; Lubnin,
Alexander V.; (Copley, OH) ; Masler, William F.
III; (Hinckley, OH) ; Valentino, Beth A.;
(Broadview Hts., OH) |
Correspondence
Address: |
NOVEON IP HOLDINGS CORP.
9911 BRECKSVILLE ROAD
CLEVELAND
OH
44141-3247
US
|
Assignee: |
Noveon IP Holdings Corp.
|
Family ID: |
24439263 |
Appl. No.: |
10/797378 |
Filed: |
March 10, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10797378 |
Mar 10, 2004 |
|
|
|
09609077 |
Jun 30, 2000 |
|
|
|
6794475 |
|
|
|
|
Current U.S.
Class: |
524/501 ;
526/319 |
Current CPC
Class: |
C08F 290/062 20130101;
C09D 155/005 20130101 |
Class at
Publication: |
524/501 ;
526/319 |
International
Class: |
C08F 118/02 |
Claims
What is claimed is:
1. A polymer comprising: polymerized units of at least one reactive
macromer of at least one alkylene oxide having at least one
functional group capable of free-radical transformation, wherein
said macromer comprises less than about 10 wt. % of total polymer
weight and has a molecular weight (average) from about 100 to about
10,000, and said macromer has the formulaX--(Y--O)n--Zwherein Y is
a straight or branched chain alkylene radical having 1 to 6 carbon
atoms, X is a functional group capable of free-radical
transformation, Z is H, C.sub.mH.sub.2m+1, phosphate, or the same
as X, m is 1 to 8, and n varies in order to achieve said molecular
weight (average).
2. A polymer of claim 1, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether,
vinylbenzyl, vinylsulfonic ester, or mercaptan, and Z is hydrogen
or methyl.
3. A polymer of claim 2, wherein said macromer comprises
polymerized units of methoxy polyethylene oxide (meth)acrylate, at
least one ethylenically unsaturated monomer having at least one
carboxylic acid group, and at least one other comonomer, and said
macromer has a molecular weight (average) from about 100 to about
5,000.
4. A polymer of claim 3, wherein said ethylenically unsaturated
monomer having at least one carboxylic acid group comprises acrylic
acid, methacrylic acid or a mixture thereof, and said other
comonomer comprises one or more of acrylic acid esters, methacrylic
acid esters, unsaturated nitrites, styrenic monomers, vinyl esters,
vinyl ethers, and conjugated dienes.
5. A polymer of claim 4, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
6. A polymer of claim 1, wherein said polymer is in latex, solution
or dispersion form.
7. A blend comprising: one or more one of a polymer (1) (in latex,
solution or dispersion form) comprising polymerized units of at
least one reactive macromer of at least one alkylene oxide having
at least one functional group capable of free-radical
transformation, wherein said macromer has a molecular weight
(average) from about 100 to about 10,000, and said macromer has the
formulaX--(Y--O).sub.n--Zwherein Y is a straight or branched chain
alkylene radical having 1 to 6 carbon atoms, X is a functional
group capable of free-radical transformation, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, m is 1 to 8, and n
varies in order to achieve said molecular weight (average), and (2)
one or more one other polymer latexes, solutions or
dispersions.
8. A blend of claim 7, wherein said polymer (1) also includes
polymerized units of at least one ethylenically unsaturated monomer
having at least one carboxylic acid group.
9. A blend of claim 8, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether, vinyl
benzyl, vinylsulfonic acid, or mercaptan, and Z is hydrogen or
methyl.
10. A blend of claim 9, wherein said macromer comprises polymerized
units of methoxy polyethylene oxide (meth)acrylate, acrylic acid or
methacrylic acid or a mixture thereof, and at least one other
comonomer, and said macromer has a molecular weight (average) from
about 100 to about 5,000.
11. A blend of claim 10, wherein said other comonomer comprises one
or more of acrylic acid esters, methacrylic acid esters,
unsaturated nitriles, styrenic monomers, vinyl esters, vinyl
ethers, and conjugated dienes.
12. A blend of claim 11, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
13. A blend of claim 8, wherein said (2) other polymer comprises
one or more of natural rubber, conjugated-diene-containing polymer,
hydrogenated styrene-butadiene triblock copolymer, chlorosulfonated
polyethylene, ethylene copolymer, acrylic ester copolymer,
methacrylic ester copolymer, vinyl chloride copolymer, vinylidene
chloride copolymer, polyisobutylene, polyurethane, polyurea, and
poly(urethane-urea).
14. A blend of claim 13, wherein said (2) other polymer comprises
one or more of (a) a butadiene-containing copolymer wherein said
copolymer comprises polymerized units of butadiene and at least one
comonomer of acrylonitrile and styrene, and (b)
polychlorobutadiene.
15. A blend of claim 14, wherein said butadiene-containing
copolymer comprises a nitrile rubber comprising polymerized units
of butadiene, acrylonitrile, and methacrylic acid.
16. A process comprising: (A) preparing one or more polymers (in
latex, solution or dispersion form) comprising polymerized units of
at least one reactive macromer of at least one alkylene oxide
having at least one functional group capable of free-radical
transformation, wherein said macromer comprises less than about 10
wt. % of total polymer weight and has a molecular weight (average)
from about 100 to about 10,000, and said macromer has the
formulaX--(Y--O).sub.n--Zwherein Y is a straight or branched chain
alkylene radical having 1 to 6 carbon atoms, X is a functional
group capable of free-radical transformation, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, m is 1 to 8, and n
varies in order to achieve said molecular weight (average); (B)
compounding one or more of said polymers with other ingredients,
and making an article; and (C) curing said article.
17. A process of claim 16, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether,
vinylbenzyl, vinylsulfonic ester, or mercaptan, and Z is hydrogen
or methyl.
18. A process of claim 17, wherein said macromer comprises
polymerized units of methoxy polyethylene oxide (meth)acrylate, at
least one ethylenically unsaturated monomer having at least one
carboxylic acid group, and at least one other comonomer, and said
macromer has a molecular weight (average) from about 100 to about
5,000.
19. A process of claim 18, wherein said ethylenically unsaturated
monomer having at least one carboxylic acid group comprises acrylic
acid, methacrylic acid or a mixture thereof, and said other
comonomer comprises one or more of acrylic acid esters, methacrylic
acid esters, unsaturated nitriles, styrenic monomers, vinyl esters,
vinyl ethers, and conjugated dienes.
20. A process of claim 19, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
21. A process of claim 16, wherein at least one salt is added
during said process.
22. A process of claim 21, wherein said salt comprises
LiNO.sub.3.
23. A process of claim 16, wherein said article is made by a
process comprising one or more of dipping, impregnation,
saturation, spraying and coating of a substrate.
24. A process of claim 23, wherein said substrate is one or more of
a glove mold, paper or other non-woven material, fibrous material,
rubber, plastic, and wood.
25. A process of claim 24, wherein said article comprises a
glove.
26. A process comprising: (A) preparing a blend of one or more of
polymer (1) (in latex, solution or dispersion form) comprising
polymerized units of (a) at least one reactive macromer of at least
one alkylene oxide having at least one functional group capable of
free-radical transformation, wherein said macromer has a molecular
weight (average) from about 100 to about 10,000, and said macromer
has the formulaX--(Y--O).sub.n--Zwherein Y is a straight or
branched chain alkylene radical having 1 to 6 carbon atoms, X is a
functional group capable of free-radical transformation, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, m is 1 to 8, and n
varies in order to achieve said molecular weight (average), and (2)
one or more other polymer latexes, solutions or dispersions; (B)
compounding said blend with other ingredients, and making an
article; and (C) curing said article.
27. A process of claim 26, wherein said polymer (1) also includes
polymerized units of at least one ethylenically unsaturated monomer
having at least one carboxylic acid group.
28. A process of claim 27, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether, vinyl
benzyl, vinylsulfonic acid, or mercaptan, and Z is hydrogen or
methyl.
29. A process of claim 28, wherein said macromer comprises
polymerized units of methoxy polyethylene oxide (meth)acrylate,
acrylic acid or methacrylic acid or a mixture thereof, and at least
one other comonomer, and said macromer has a molecular weight
(average) from about 100 to about 5,000.
30. A process of claim 29, wherein said other comonomer comprises
one or more of acrylic acid esters, methacrylic acid esters,
unsaturated nitrites, styrenic monomers, vinyl esters, vinyl
ethers, and conjugated dienes.
31. A process of claim 30, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
32. A process of claim 26, wherein said (2) other polymer comprises
one or more of natural rubber, conjugated-diene-containing polymer,
hydrogenated styrene-butadiene triblock copolymer, chlorosulfonated
polyethylene, ethylene copolymer, acrylic ester copolymer,
methacrylic ester copolymer, vinyl chloride copolymer, vinylidene
copolymer, polyisobutylene, polyurethane, polyurea, and
poly(urethane-urea).
33. A process of claim 32, wherein said (2) other polymer comprises
one or more of (a) a butadiene-containing copolymer wherein said
copolymer comprises polymerized units of butadiene and at least one
comonomer of acrylonitrile and styrene, and (b)
polychlorobutadiene.
34. A process of claim 33, wherein said butadiene-containing
copolymer comprises a nitrile rubber comprising polymerized units
of butadiene, acrylonitrile, and methacrylic acid.
35. A process of claim 26, wherein at least one salt is added
during said process.
36. A process of claim 35, wherein said salt comprises
LiNO.sub.3.
37. A process of claim 26, wherein said article is made by a
process comprising one or more of dipping, impregnation,
saturation, spraying and coating of a substrate.
38. A process of claim 37, wherein said substrate is one or more of
a glove mold, paper or other non-woven material, fibrous material,
rubber, plastic, and wood.
39. A process of claim 38, wherein said article comprises a
glove.
40. An article comprising one or more polymers comprising:
polymerized units of at least one reactive macromer of at least one
alkylene oxide having at least one functional group capable of
free-radical transformation, wherein said macromer comprises less
than about 10 wt. % of total polymer weight and has a molecular
weight (average) from about 100 to about 10,000, and said macromer
has the formulaX--(Y--O).sub.n--Zw- herein Y is a straight or
branched chain alkylene radical having 1 to 6 carbon atoms, X is a
functional group capable of free-radical transformation, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, m is 1 to 8, and n
varies in order to achieve said molecular weight (average).
41. An article of claim 40, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether,
vinylbenzyl, vinylsulfonic ester, or mercaptan, and Z is hydrogen
or methyl.
42. An article of claim 41, wherein said macromer comprises
polymerized units of methoxy polyethylene oxide (meth)acrylate, at
least one ethylenically unsaturated monomer having at least one
carboxylic acid group, and at least one other comonomer, and said
macromer has a molecular weight (average) from about 100 to about
5,000.
43. An article of claim 42, wherein said ethylenically unsaturated
monomer having at least one carboxylic acid group comprises acrylic
acid, methacrylic acid or a mixture thereof, and said other
comonomer comprises one or more of acrylic acid esters, methacrylic
acid esters, unsaturated nitrites, styrenic monomers, vinyl esters,
vinyl ethers, and conjugated dienes.
44. An article of claim 43, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
45. An article of claim 40, wherein said article is made by a
process comprising one or more of dipping, impregnation,
saturation, spraying and coating of a substrate.
46. An article of claim 45, wherein said substrate is one or more
of a glove mold, paper or other non-woven material, fibrous
material, rubber, plastic, and wood.
47. An article of claim 46, wherein said article comprises a
glove.
48. An article of claim 40, wherein said article is cured.
49. An article comprising one or more blends comprising: one or
more one of a polymer (1) comprising polymerized units of (a) at
least one reactive macromer of at least one alkylene oxide having
at least one functional group capable of free-radical
transformation, wherein said macromer has a molecular weight
(average) from about 100 to about 10,000, and said macromer has the
formulaX--Y--O).sub.n--Zwherein Y is a straight or branched chain
alkylene radical having 1 to 6 carbon atoms, X is a functional
group capable of free-radical transformation, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, m is 1 to 8, and n
varies in order to achieve said molecular weight (average), and (2)
one or more one other polymers.
50. An article of claim 49, wherein said polymer (1) also includes
polymerized units of at least one ethylenically unsaturated monomer
having at least one carboxylic acid group.
51. An article of claim 50, wherein Y has 2 to 4 carbon atoms, X
comprises acrylate, methacrylate, allyl ether, vinyl ether, vinyl
benzyl, vinylsulfonic acid, or mercaptan, and Z is hydrogen or
methyl.
52. An article of claim 51, wherein said macromer comprises
polymerized units of methoxy polyethylene oxide (meth)acrylate,
acrylic acid or methacrylic acid or a mixture thereof, and at least
one other comonomer, and said macromer has a molecular weight
(average) from about 100 to about 5,000.
53. An article of claim 52, wherein said other comonomer comprises
one or more of acrylic acid esters, methacrylic acid esters,
unsaturated nitriles, styrenic monomers, vinyl esters, vinyl
ethers, and conjugated dienes.
54. An article of claim 53, wherein X comprises acrylate or
methacrylate, and said other comonomer comprises one or more of
butadiene, acrylonitrile, styrene, methyl methacrylate, and n-butyl
acrylate.
55. An article of claim 49, wherein said (2) other polymer
comprises one or more of natural rubber,
conjugated-diene-containing polymer, hydrogenated styrene-butadiene
triblock copolymer, chlorosulfonated polyethylene, ethylene
copolymer, acrylic ester copolymer, methacrylic ester copolymer,
vinyl chloride copolymer, vinylidene chloride copolymer,
polyisobutylene, polyurethane, polyurea, and
poly(urethane-urea).
56. An article of claim 55, wherein said (2) other polymer
comprises one or more of (a) a butadiene-containing copolymer
wherein said copolymer comprises polymerized units of butadiene and
at least one comonomer of acrylonitrile and styrene, and (b)
polychlorobutadiene.
57. An article of claim 56, wherein said butadiene-containing
copolymer comprises a nitrile rubber comprising polymerized units
of butadiene, acrylonitrile, and methacrylic acid.
58. An article of claim 49, wherein said article is made by a
process comprising one or more of dipping, impregnation,
saturation, spraying and coating of a substrate.
59. An article of claim 58, wherein said substrate is one or more
of a glove mold, paper or other non-woven material, fibrous
material, rubber, plastic, and wood.
60. An article of claim 59, wherein said article comprises a
glove.
61. An article of claim 49, wherein said article is cured.
Description
FIELD OF THE INVENTION
[0001] This invention relates to polymers and their latexes,
solutions, dispersions and blends used to produce gloves and other
articles having superior electrostatic dissipative properties.
BACKGROUND OF THE INVENTION
[0002] Polymeric materials for use in electrostatic discharge
("ESD", "static dissipative" or "antistatic") applications fall
into two categories: rubbery or thermoplastic. Typically rubbery
and thermoplastic materials are used in different applications and
are made by different manufacturing methods. The ESD properties are
achieved by incorporating hydrophilic moieties, such as various
ethoxylates, or electroconductive fillers such as carbon black,
metals, or salts. Many of these systems have shortcomings.
Additives by their very nature can have widely variable results due
to non-uniform dispersion in the matrix. They also can lose
effectiveness if they extract from the matrix and/or deteriorate
over time.
[0003] Achieving ESD properties in articles that are designed to be
flexible rather than rigid provides further challenges. Some of the
traditional ingredients in the prior art such as carbon black,
metal powders and wires, electroconductive polymers, and inorganic
fillers, can stiffen an article. This is not important in plastic
applications, but will present a significant issue for articles
that must be flexible.
[0004] In addition, ingredients in a flexible matrix, by their very
nature, are more mobile than in a plastic matrix. Flexible articles
such as gloves and papers are designed to bend, flex, and stretch
under contact with moist skin. These conditions are more conducive
to creating motion at the molecular level, which could increase the
likelihood for water-soluble materials and fillers to bloom,
transfer or flake off the surface. Any particulate matter coming
off articles can potentially cause damage in a critical environment
where antistatic properties are desired, such as "clean room"
applications and electronics manufacturing.
[0005] Traditional materials for making ESD clean room articles
incorporate conductive fillers, fibers, ionic materials, carbon
black, or application of a surface coating. Shortcomings of these
articles include extraction or deterioration over time,
non-homogeneity, and a need for humidity to dissipate static
charges effectively. Many articles such as gloves used in a clean
room are manufactured under special conditions to minimize
particulate contamination. For example, additional post-leach or
water-soak processes in glove manufacturing will remove particulate
contamination.
[0006] Current gloves used in clean room environments typically are
made from latexes (also known as emulsions or latex emulsions) or
dispersions of natural rubbers, acrylonitrile-butadiene rubbers,
styrene-butadiene rubbers, polyvinylchlorides,
polychlorobutadienes, and polyurethanes. Latexes typically are
prepared by polymerization of monomers in a water medium, while
dispersions are prepared by distribution of polymers in a water
medium following polymerization. Gloves made from these polymers
under current standard conditions of compounding and processing
typically have a surface resistivity of 1.times.10.sup.11 to
1.times.10.sup.13 ohms/square and a static decay time greater than
1 second. Specialty gloves are currently on the market which offer
antistatic or conductive features, incorporate additives such as
carbon black during compounding, and have published surface
resistivity values as low as 1.times.10.sup.4 ohms/square.
[0007] The most accepted method of glove manufacturing is the
coagulant dipping process, followed by subsequent leaching and
curing cycles. In this process, a preheated and cleaned glove mold
(also called a "former") is dipped into a calcium nitrate salt
solution, and dried to tackiness. This salt-coated mold is dipped
into a compounded latex or polymer dispersion, causing the latex or
polymer dispersion to coagulate on the mold and form a glove. The
glove is then leached in water to remove the salt, dried and cured
to achieve final properties. Thus, an essential property of the
latex or polymer dispersion is its ability to coagulate, forming an
article.
[0008] The most widely used approach to render polymers antistatic
is incorporating a polyethyleneglycol (PEG) moiety into the
backbone of the polymer. PEG is a hydrophilic material and attracts
moisture into the article, thus reducing its resistivity. Since it
is polymerized into the backbone of the polymer, it is not
extractable. For example, U.S. Pat. No. 4,543,390 relates to graft
copolymers prepared by emulsion polymerization of certain
polyethyleneglycol monomers and optionally certain vinyl monomers
in the presence of rubbers. The graft copolymers subsequently are
blended with compatible thermoplastic resins. However, the
polyethyleneglycol monomers which render polymers antistatic also
yield polyvalent ion-stable polymer emulsions which are unsuitable
for glove making by coagulant dipping processes. See R. H. Ottewill
et al, Colloid & Polymer Science, Vol. 266, No. 6, p. 547
(1988), and R. H. Ottewill, Emulsion Polymerization and Emulsion
Polymers (Editors: P. A. Lovell and M. S. El-Aaser), J. Wiley &
Sons (1997). p. 104 (1997).
[0009] U.S. Pat. No. 4,302,558 and U.S. Pat. No. 4,384,078 relate
to antistatic graft copolymers obtained by graft-polymerizing a
vinyl or vinylidene monomer onto a rubber trunk polymer which
comprises a polyalkylene oxide monomer comprising 4 to 500 alkylene
oxide groups together with an ethylenic unsaturation, and a
conjugated diene and/or an alkyl acrylate. However, as shown in the
examples below, the graft copolymers are unsuitable for glove
making by coagulant dipping processes.
SUMMARY OF THE INVENTION
[0010] Unexpectedly, this invention demonstrates that blends of
certain PEG-containing latexes, solutions or dispersions with
typical glove-making latexes or dispersions are suitable for making
gloves and other articles by coagulant dipping processes. Also
unexpectedly, certain PEG-containing latexes, solutions or
dispersions are suitable for making gloves and other articles by
coagulant dipping processes even in the absence of said typical
glove-making latexes or dispersions. Further, articles made from
the compositions of this invention are inherently static
dissipative and will not bloom, rub-off or extract during use. In
particular, articles such as gloves made from the compositions of
this invention, and that meet ASTM examination standards for target
tensile and elongation properties, will also have a surface
resistivity value below 1.times.10.sup.11 ohms/square per square, a
static decay time of less than 1 second, or both.
[0011] The materials of the present invention suitable for making
antistatic articles by coagulant dipping processes are blends of
(A) one or more step (1) polymers (in latex, solution or dispersion
form) of (a) at least one reactive macromer of at least one
alkylene oxide having at least one functional group capable of
free-radical transformation, (b) optionally, one or more
ethylenically unsaturated monomers having at least one carboxylic
acid group, and (c) optionally, one or more free radically
polymerizable comonomers, and (B) one or more step (2) other
polymer latexes or dispersions of such polymers as natural rubber,
conjugated-diene-containing polymers, hydrogenated
styrene-butadiene triblock copolymers, chlorosulfonated
polyethylenes, ethylene copolymers, acrylic and/or methacrylic
ester copolymers, vinyl chloride copolymers, vinylidene copolymers,
polyisobutylenes, polyurethanes, polyureas, and
poly(urethane-urea)s. The term "free-radical transformation" means
being capable of reacting by a free-radical mechanism, examples
including free-radically polymerizable monomers, chain transfer
agents, or chain terminating agents.
[0012] Also suitable for making antistatic articles by coagulant
dipping processes, even in the absence of said step (2) other
polymer latexes or dispersions, are step (1) polymers (in latex,
solution or dispersion form) of (a) at least one reactive macromer
of at least one alkylene oxide having at least one functional group
capable of free-radical transformation, wherein said macromer
comprises less than about 10 wt. % of total polymer weight in the
step (1) latex, solution or dispersion (b) optionally, one or more
ethylenically unsaturated monomers having at least one carboxylic
acid group, and (c) one or more free radically polymerizable
comonomers.
DETAILED DESCRIPTION
[0013] The blends of the present invention comprise (A) one or more
step (1) polymers (in latex, solution or dispersion form) of (a) at
least one reactive macromer of at least one alkylene oxide having
at least one functional group capable of free-radical
transformation, (b) optionally, one or more ethylenically
unsaturated monomers having at least one carboxylic acid group, and
(c) optionally, one or more free radically polymerizable
comonomers, and (B) and one or more step (2) other polymer latexes
or dispersions.
[0014] In step (1) the (a) at least one reactive macromer of at
least one alkylene oxide having at least one functional group
capable of free-radical transformation is reacted to form latexes,
solutions or dispersions with (b) optionally, one or more
ethylenically unsaturated monomers having at least one carboxylic
acid group, and (c) optionally, one or more radically polymerizable
monomers, such as acrylic esters, methacrylic esters, conjugated
dienes, styrenic monomers, vinyl esters, vinyl ethers, conjugated
dienes, unsaturated nitrites and other polar monomers.
[0015] The following definitions apply throughout this
specification. All weight percentages of polymers, latexes, and
other materials are expressed on a dry weight basis. The term
"polymer" refers to homopolymers as well as copolymers. The term
"step (1) polymer" or "polymer (1)" means a latex-forming,
solution-forming or dispersion-forming polymer that is the primary
component of a respective step (1) latex, solution or dispersion.
Similarly, the terms "step (2) polymer" or "polymer (2)" means a
latex-forming or dispersion-forming polymer that is the primary
component of a respective step (2) other polymer latex or
dispersion. The term "step (1) composition" means a step (1) latex,
solution or dispersion. Similarly, the term "step (2) composition"
means a step (2) other polymer latex or dispersion. The term "other
polymer latex or dispersion" means a latex or dispersion other than
a step (1) polymer latex or dispersion. The term "polymerized
units" means polymerized monomeric molecules, e.g., polybutadiene
can be said to comprise polymerized units or molecules of butadiene
monomer.
[0016] Polymerized reactive macromer (a) typically may comprise
from about 0.1 wt. % to 100 wt. %, preferably from about 1 wt. % to
about 30 wt. %, of the step (1) polymer. Polymerized monomer (b)
typically may comprise from 0 wt. % to about 10 wt. %, preferably
from about 3 wt. % to about 7 wt. %, of the step (1) polymer.
Polymerized monomer (c) typically may comprise from 0 wt. % to
about 99 wt. %, preferably from about 1 wt. % to about 70 wt. %, of
the step (1) polymer.
[0017] One or more one step (1) compositions are then blended with
one or more step (2) compositions incorporating polymers such as
those of natural rubber, conjugated-diene-containing polymers,
hydrogenated styrene-butadiene triblock copolymers,
chlorosulfonated polyethylenes, ethylene copolymers, acrylic and/or
methacrylic ester copolymers, vinyl chloride copolymers, vinylidene
copolymers, polyisobutylenes, polyurethanes, polyureas, and
poly(urethane-urea)s. The step (2) compositions typically may
comprise from about 2 wt. % to about 99.5 wt. %, and preferably
from about 50 wt. % to about 99 wt. %, of the blend of step (1)
compositions and step (2) compositions.
[0018] Reactive macromers of alkylene oxides having at least one
functional group capable of free-radical transformation are well
known in the prior art. Such macromers have the formula (I):
X--(Y--O ).sub.n--Z (I)
[0019] wherein Y is a straight or branched chain alkylene radical
having 1 to 6 carbon atoms, preferably 2 to 4 carbon atoms, X is a
functional group capable of free-radical transformation, such as
acrylate, which may be represented by the formula
H.sub.2C.dbd.CHC(O)O--, methacrylate, which may be represented by
the formula H.sub.2C.dbd.C(CH.sub.3)C(O)O--, allyl ether, which may
be represented by the formula H.sub.2C.dbd.CHCH.sub.2O--- , vinyl
ether, which may be represented by the formula H.sub.2C.dbd.CHO--,
vinylbenzyl, vinylsulfonic ester, which may be represented by the
formula H.sub.2C.dbd.CHSO.sub.3--, or mercaptan, Z is H,
C.sub.mH.sub.2m+1, phosphate, or the same as X, and m is 1 to 8,
preferably 1 to 3. "n" may vary to achieve the desired molecular
weight (average) set forth below. Z is preferably H or methyl. X is
preferably acrylate or methacrylate. Examples of suitable reactive
monomers include methoxy polyethylene oxide (meth)acrylate (also
known as methoxypolyethylene glycol methacrylate or "MePEGMA"),
methoxy polyethylene oxide allyl ether, polyethylene oxide allyl
ether, butoxy polyethylene oxide (meth)acrylate, p-vinylbenzyl
terminated polyethylene oxide, polyethylene oxide di(meth)acrylate,
polyethylene oxide thiol, polyethylene oxide maleimide,
polyethylene oxide vinylsulfone, and the like. Mixtures of the
reactive macromers may also be used. Preferred reactive macromers
include methoxy polyethylene oxide (meth)acrylate, methoxy
polyethylene oxide allyl ether, and polyethylene oxide allyl ether.
Suitable reactive macromers may have molecular weights (average)
from about 100 to about 10,000, preferably from about 100 to about
5,000, and more preferably from about 300 to about 2,000.
[0020] Unexpectedly, it was discovered that the step (1)
compositions can be used without the step (2) compositions in
making articles such as gloves by the coagulant dipping process
described hereafter, provided that the amount of polymerized units
of at least one reactive macromer of at least one alkylene oxide
having at least one functional group capable of free-radical
transformation is present but comprises less than about 10 wt. %,
preferably less than about 8 wt. %, and more preferably less than
about 6 wt. % of total polymer weight in the step (1)
composition.
[0021] The step (1) compositions preferably include polymerized
units of at least one ethylenically unsaturated monomer having at
least one carboxylic acid group, and preferably one or two
carboxylic acid groups. Examples of such monomers include acrylic
acid, methacrylic acid, itaconic acid, maleic acid, maleic
anhydride, fumaric acid, crotonic acid, vinylacetic acid, mesaconic
acid, citraconic acid, 2-acrylamido-2-methylpropanesulfonic acid,
alkali metal salts of the above acids and amine or ammonium salts
thereof. Acrylic acid and methacrylic acid are preferred. The
polymerized ethylenically unsaturated monomers having at least one
carboxylic acid group typically may comprise from 0 wt. % to about
10 wt. %, preferably from about 3 wt. % to about 7 wt. %, of
polymer (1). Presence of the polymerized ethylenically unsaturated
monomer having at least one carboxylic acid group as part of
polymer (1) is desirable for the coagulant dipping processes
described hereafter, but not for other glove making processes known
to those skilled in the art.
[0022] Optionally one or more free radically (or "radically")
polymerizable comonomers may be useful in preparing polymer (1) of
the step (1) compositions. Examples of such radically polymerizable
comonomers include acrylic esters, methacrylic esters, unsaturated
nitrites, styrenic monomers, vinyl esters, vinyl ethers, conjugated
dienes, other monomers, and mixtures thereof.
[0023] Acrylic esters and methacrylic acid esters useful in
preparing the step (1) compositions include those having the
formula II: 1
[0024] wherein R.sub.1 is hydrogen or a methyl group, and R.sub.2
contains 1 to 12 carbon atoms and optionally also one or more
sulfur, nitrogen, halogen or oxygen atoms. Preferably R.sub.2 is an
ethyl or butyl group. Examples of suitable acrylate esters include
methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl
acrylate, n-butyl acrylate,. 2-ethylhexyl acrylate, and n-decyl
acrylate. Examples of suitable methacrylate esters include methyl
(meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate,
n-butyl (meth)acrylate, isopropyl (meth)acrylate, isobutyl
(meth)acrylate, n-amyl (meth)acrylate, n-hexyl (meth)acrylate,
isoamyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate,
2-hydroxypropyl (meth)acrylate, N,N-dimethylaminoethyl
(meth)acrylate, N,N-diethylaminoethyl (meth)acrylate,
t-butylaminoethyl (meth)acrylate, 2-sulfoethyl (meth)acrylate,
trifluoroethyl (meth)acrylate, glycidyl (meth)acrylate, benzyl
(meth)acrylate, allyl (meth)acrylate, 2-n-butoxyethyl
(meth)acrylate, 2-chloroethyl (meth)acrylate,
sec-butyl-(meth)acrylate, tert-butyl (meth)acrylate, 2-ethylbutyl
(meth)acrylate, cinnamyl (meth)acrylate, crotyl (meth)acrylate,
cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate,
2-ethoxyethyl (meth)acrylate, furfuryl (meth)acrylate,
hexofluoroisopropyl (meth)acrylate, methallyl (meth)acrylate,
3-methoxybutyl (meth)acrylate, 2-methoxybutyl (meth)acrylate,
2-nitro-2-methylpropyl (meth)acrylate, n-octyl (meth)acrylate,
2-ethylhexyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate,
2-phenylethyl (meth)acrylate, phenyl (meth)acrylate, propargyl
(meth)acrylate, tetrahydrofurfuryl (meth)acrylate, norbornyl
(meth)acrylate, acrylamide and its derivatives, and
tetrahydropyranyl (meth)acrylate. Mixtures of acrylic and
methacrylic acid esters may be used. The polymerized acrylic and
methacrylic acid esters typically may comprise from 0 wt. % to
about 50 wt. %, from 0 wt. % to about 20 wt. %, and more preferably
from 0 wt. % to about 10 wt. %, of polymer (1).
[0025] Suitable unsaturated nitrile monomers useful in preparing
the step (1) compositions include acrylonitrile or an alkyl
derivative thereof, the alkyl preferably having from 1 to 4 carbon
atoms, such as acrylonitrile, methacrylonitrile, and the like. Also
suitable are unsaturated monomers containing a cyano group such as
those having the formula III:
CH.sub.2.dbd.C(R)CO(O)CH.sub.2CH.sub.2CN (III)
[0026] wherein R is H or C.sub.nH.sub.2n+.sub.1 and n is 1 to 4
carbon atoms. Other examples of 10 unsaturated nitrile monomers
include CH.sub.2.dbd.C(CN).sub.2, CH.sub.3--CH.dbd.CH--CN,
NC--CH.dbd.CH--CN, 4-pentenenitrile, 3-methyl-4-pentenenitrile,
5-hexenenitrile, 4-vinyl-benzonitrile, 4-allyl-benzonitrile,
4-vinyl-cyclohexanecarbonitri- le, 4-cyanocyclohexene, and the
like. Mixtures of the unsaturated nitriles may also be used.
Acrylonitrile and methacrylonitrile are preferred. The polymerized
unsaturated nitrile monomers typically may comprise from 0 wt. % to
about 60 wt. %, preferably from about 5 wt. % to about 45 wt. %, of
polymer (1).
[0027] The "styrenic monomers" useful in preparing the step (1)
compositions may be defined as monomers containing a carbon-carbon
double bond in alpha-position to an aromatic ring. The styrenic
monomers may be represented by the following formulae: 2
[0028] wherein n is an integer from 0 to 2; R.sub.1, R.sub.2,
R.sub.3, R.sub.4, R.sub.5, R.sub.6, and R.sub.7 are selected from
the group consisting of H, CH.sub.3, C.sub.mH.sub.2m+1, OH,
OCH.sub.3, OC.sub.mH.sub.2m+.sub.1 COOH, COOCH.sub.3,
COOC.sub.mH.sub.2m+1, Cl and Br, m is an integer from 2 to 9, and
R.sub.8 is selected from the group consisting of H, CH.sub.3,
C.sub.mH.sub.2m+1, and C.sub.6H.sub.5.
[0029] Examples of suitable styrenic monomers useful in preparing
step (1) compositions include styrene, alpha-methylstyrene,
tertiary butylstyrene, ortho-, meta-, and para-methylstyrene,
ortho-, meta- and para-ethylstyrene, o-methyl-p-isopropylstyrene,
p-chlorostyrene, p-bromostyrene, o,p-dichlorostyrene,
o,p-dibromostyrene, ortho-, meta- and para-methoxystyrene, indene
and its derivatives, vinylnaphthalene, diverse vinyl
(alkyl-naphthalenes) and vinyl (halonaphthalenes) and mixtures
thereof, acenaphthylene, diphenylethylene, and vinyl anthracene.
Mixtures of styrenic monomers also may be used. Styrene is
preferred. The polymerized styrenic monomers typically may comprise
from 0 wt. % to about 65 wt. %, preferably from about 5 wt. % to
about 40 wt. %, of polymer (1).
[0030] Vinyl ester monomers derived from carboxylic acids
containing 1 to 14 carbon atoms also may be useful in preparing the
step (1) compositions. Examples of such vinyl ester monomers
include vinyl acetate, vinyl propionate, vinyl hexanoate, vinyl
2-ethylhexanoate, vinyl octanoate, vinyl pelargonate, vinyl
caproate, neo esters of vinyl alcohol, vinyl laurate, and the like,
as well as mixtures thereof. The polymerized vinyl ester monomers
typically may comprise from 0 wt. % to about 99.5 wt. %, preferably
from 0 wt. % to about 30 wt. %, of polymer (1).
[0031] Vinyl ethers may be useful in preparing the step (1)
compositions. Examples of vinyl ethers include methyl-, ethyl-,
butyl, iso-butyl vinyl ethers and the like. The polymerized vinyl
ether monomers typically may comprise from 0 wt. % to about 50 wt.
%, preferably from 0 wt. % to about 30 wt. %, of polymer (1).
[0032] Conjugated diene monomers containing 4 to 10 carbon atoms,
and preferably from 4 to 6 carbon atoms, also may be useful in
preparing the step (1) compositions. Examples of such conjugated
diene monomers include butadiene, isoprene, cis-1,3-pentadiene,
trans-1,3-pentadiene, cis-1,3-hexadiene, trans-1,3-hexadiene,
2-ethylbutadiene, 2-n-propylbutadiene, 2-i-propyl butadiene,
2-t-butylbutadiene, 2-amylbutadiene, 2-n-octylbutadiene,
4-methylpentadiene, cis-3-methylpentadiene,
trans-3-methylpentadiene, cis-2-methylpentadiene,
trans-2-methylpentadiene, 2,3-dimethylbutadiene, cis,cis-2,
4-hexadiene, cis,trans-2,4-hexadiene, trans,trans-2,4-hexadiene,
2-methyl-3-ethylbutadiene, 2-methyl-3-i-propylbutadiene,
2-methyl-3-n-butylbutadiene, myrcene, cis-1-phenylbutadiene,
trans-1-phenylbutadiene, 2-phenyl butadiene, 1,3- cyclopentadiene,
1,3-cyclohexadiene, 2-fluorobutadiene, 1-chlorobutadiene,
2-chlorobutadiene, 2,3-dichlorobutadiene, 2-bromobutadiene, sorbic
acid, cis-1-cyanobutadiene, 2-methoxybutadiene and like, as well as
mixtures thereof. Butadiene is more preferred. The polymerized
conjugated diene monomers typically may comprise from 0 wt. % to
about 99:5 wt. %, preferably from 0 wt. % to about 70 wt. %, of
polymer (1).
[0033] Other monomers may be useful in preparing the step (1)
compositions, including polar monomers such as hydroxyalkyl
(meth)acrylates, acrylamides and substituted acrylamides, sodium
styrene sulfonate and sodium vinyl sulfonate,
N-vinyl-2-pyrrolidone, N-vinyl caprolactam, diallyl phthalate,
dimethyl aminoethyl (meth)acrylate, and dimethylaminopropyl
methacrylamide. Dimethyl acrylamide, dimethyl aminoethyl
acrylamide, dimethyl aminoethyl (meth)acrylate, and
dimethylaminopropyl methacrylamide are preferred. Mixtures of polar
monomers also may be used. The polymerized polar monomers typically
may comprise from 0 wt. % to about 30 wt. %, preferably from about
1 wt. % to about 20 wt. %, of polymer (1).
[0034] The step (1) compositions may be prepared by free radical
polymerization methods well known to those skilled in the art, such
as described in "Emulsion Polymerization and Emulsion Polymers"
(Editors: P. A. Lovell and M. S. El-Aaser), J. Wiley & Sons
(1997).
[0035] The step (2) compositions and their preparation are
described in the prior art. Such step (2) compositions incorporate
well-known commercial polymers such as natural rubber,
conjugated-diene-containing polymers including butadiene-containing
copolymers with acrylonitrile and/or styrene such as nitrile
rubbers and SBR rubbers, polychlorobutadiene (Neoprene),
hydrogenated styrene-butadiene triblock copolymers (such as
Kraton.TM. copolymers from Shell Chemical), chlorosulfonated
polyethylene (such as Hypalon.TM. polymers from E. I. duPont),
ethylene copolymers (such as EPDM copolymers), acrylic and/or
methacrylic ester copolymers such as Hycar.RTM. acrylic copolymers
from BFGoodrich), vinyl chloride copolymers, vinylidene copolymers,
polyisobutylenes, polyurethanes, polyureas, and
poly(urethane-urea)s. Among preferred step (2) compositions are
those comprising conjugated-diene-containing polymers, such as
butadiene-containing copolymers with acrylonitrile and/or styrene
(e.g., nitrile rubbers), as well as polychlorobutadienes.
[0036] Suitable step (2) compositions include those described in
the following U.S. Patents, all of which are incorporated herein by
reference. For example, U.S. Pat. No. 4,920,176 relates to emulsion
polymerization in order to prepare nitrile rubber (NBR) latexes.
Generally, nitrile latexes comprise polymerized units of butadiene,
acrylonitrile, and acrylic acid or methacrylic acid. Additional
comonomers can be included to change or improve polymer properties.
These include vinylpyridine, acrylic and methacrylic ester
monomers, chlorobutadiene, cross-linking agents, styrenic monomers,
and the like.
[0037] A review article by D. P. Tate and T. W. Bethea,
Encyclopedia of Polymer Science and Engineering, Vol. 2, p.537,
further describes polymers and copolymers of conjugated dienes such
as butadiene rubber (BR), acrylate-butadiene rubber (ABR),
chloroprene rubber (CR), isoprene rubber (IR), and
styrene-butadiene rubber (SBR).
[0038] U.S. Pat. Nos. 4,292,420 and 6,020,438 relate to emulsion
polymerization in order to prepare vinyl chloride latexes. Rigid
polyvinylchloride can be softened by the use of plasticizers, such
as 2-ethylhexyl phthalate, or by copolymerizing vinyl chloride with
"soft" monomers (the so-called internal plasticization monomers),
which render soft copolymers with vinyl chloride. Such "soft"
monomers include long-chain acrylic and methacrylic esters, vinyl
esters, vinyl ethers, acrylamides, and methacrylamides, and are
exemplified by butyl acrylate, 2-ethylhexyl methacrylate, vinyl
propionate, n-octylacrylamide and the like.
[0039] U.S. Pat. No. 6,017,997 relates to preparation of waterborne
polyurethane, polyurea, and poly(urethane-urea) dispersions
("PUD"). Generally PUD comprises polymerized units of diisocyanate
and hydrophylic moiety, together with diol, diamine, or both diol
and diamine. However, all four units can have pre-polymerization
functionality (i.e., number of reactive groups) higher than two.
Diisocyanates can be aliphatic, such as 1,6-hexamethylene
diisocyanate, cyclohexane-1,4 (or -1,3)-diisocyanate, isophorone
diisocyanate, bis-(4-isocyanatocyclohexyl)-methane, 1,3- and 1
,4-bis(isocyanatomethyl)cyclohexane
bis-(4-isocyanato-3-methyl-cyclohexyl- )-methane, tetramethyl
xylylene diisocyanate, and the like. Diisocyanates can also be
aromatic, such as 2,4-diisocyanato toluene, 2,6-diisocyanato
toluene, 4,4-diisocyanato diphenyl methane, and the like.
[0040] The following exemplary diols (or polyols) can be used in
preparing the aforesaid PUD:
[0041] (1) Polyesters of (a) dibasic carboxylic acids, such as
succinic acid, adipic acid, suberic acid, azelaic acid, sebacic
acid, phthalic acid, isophthalic acid, and the like, and (b)
dihydric alcohols, which include ethylene glycol, propylene glycol,
butylene glycol, 1,6-hexanediol, neopentyl glycol,
1,4-bis-hydroxymethylcyclohexane, 2-methyl-1,3-propanediol;
2,2,4-trimethyl-1,3-pentanediol, polypropylene glycol, dibutylene
glycol, and the like.
[0042] (2) Polycarbonate polyols containing hydroxyl groups,
including those obtained from the reaction of diols, such as
1,3-propanediol, 1,4-butanediol and/or 1,6-hexanediol, diethylene
glycol, triethylene glycol or tetraethylene glycol with
diarylcarbonates or phosgene.
[0043] (3) Polyether polyols including polymers of alkylene oxides,
such as ethylene oxide, propylene oxide, butylene oxide, styrene
oxide, tetrahydrofuran, epichlorohydrin, and the like.
[0044] (4) Polyacetal polyols prepared by reacting aldehydes, such
as formaldehyde with glycols, such as diethylene glycol,
triethylene glycol, ethoxylated
4,4'-dihydroxy-diphenyidimethylmethane, 1,6-hexanediol, and the
like.
[0045] Diamines useful in preparing the aforesaid PUD include
hydrazine, 1,2-diaminoethane, 1,6-diaminohexane,
2-methyl-1,5-pentanediamine, 2,2,4-trimethyl-1,6-hexanediamine, and
the like.
[0046] In order to enable a PUD to make a stable dispersion in an
aqueous medium, a hydrophilic moiety having anionic or potential
anionic groups and, optionally, hydrophilic ethylene oxide units,
is chemically incorporated into the PUD. The most preferred
hydrophylic moiety is dimethylol propionic acid.
[0047] Well-known initiators are used in preparing the step (1)
compositions and step (2) compositions, preferably a persulfate
initiator, and most preferably sodium persulfate. Other initiators
suitable for use include ammonium persulfate, potassium persulfate,
peroxides, azo compounds, and known redox initiators such as
tert-butyl hydroxy peroxide/sodium formaldehyde sulfoxylate. The
initiator for preparing both step (1) compositions and step (2)
compositions is preferably present in an amount from about 0.2 wt.
% to about 2 wt. % based on the total weight of the polymer.
[0048] Well-known crosslinking and branching agents may be useful
in preparing the step (1) compositions and step (2) compositions,
such as multifunctional (meth)acrylates, (meth)acrylamides, and
vinyl and allyl ethers. Examples include ethylene glycol
dimethacrylate, 1.6-hexanedioldiacrylate, methylene bis-acrylamide,
polybutadiene diacrylates, polyurethane diacrylates,
trimethylolpropane trimethacrylate, pentaerythritol tetraallyl
ether, allyl methacrylate, allyl acryloxypropionate,
4-acryloxybenzophenone, diallyl maleate, divinylbenzene, and the
like. Mixtures of crosslinking and branching agents may also be
used.
[0049] Another optional ingredient in the preparation of the step
(1) compositions and step (2) compositions is a chain transfer
agent. Useful agents include alcohols, mercaptans, halogenated
compounds and mixtures thereof. Preferred agents are mercaptans.
Where used, the chain transfer agent is present in an amount from
about 0.1 wt. % to about 3 wt. %, preferably from about 0.1 wt. %
to about 0.5 wt. % based on the total weight of the polymer.
[0050] Yet another optional ingredient in the preparation and
processing of the step (1) compositions is one or more salts. The
salts may be added at any time during polymerization, blending with
step (2) compositions, compounding, curing, or post-processing of
the compositions including during manufacture of articles. Suitable
salts include LiCl, LiNO.sub.3, LiOH, LiCF.sub.3SO.sub.3,
Li.sub.2SO.sub.4, and the like. Lithium nitrate is preferred. Salts
typically may be used at a concentration from about 0.5 wt. % to
about 10 wt. % based on the total weight of the polymer.
[0051] A step (1) composition is blended into a step (2)
composition, or vice versa, with mild stirring. Additives such as
activators, stabilizers, plasticizers, cross-linking and branching
agents, curing agents, such as sulfur, colorants, pigments,
colorants, neutralizing agents, waxes, slip and release agents,
antimicrobial agents, surfactants, metals, antioxidants, UV
stabilizers, antiozonants, and the like, can optionally be added to
the separate latexes, to blends of the two latexes, or during
manufacture of articles. Other additives may be used as appropriate
in order to make dipped articles (especially flexible articles,
such as gloves), or to impregnate, saturate, spray or coat papers,
non-woven materials, textiles, wood, and a variety of other
substrates. Applications include gloves; papers and non-wovens;
fibrous materials such as textiles; rubber and plastic films,
sheets, composites, and other articles such as walk-off mats; inks;
adhesives; and other compositions and articles typically used in
electronics, clean rooms, and automotive areas. Such articles made
at least partially or even wholly (but appropriately compounded
with additives, such as those described above) from the
compositions of the present invention are inherently static
dissipative and will not bloom, rub-off or extract during use.
Articles, such as gloves made from the compositions of this
invention and that meet ASTM examination standards for target
tensile and elongation properties, will also have a surface
resistivity value below 1.times.10.sup.11 ohms/square, a static
decay time of less than 1 second, or both.
[0052] The blends of the step (1) compositions and step (2)
composition are particularly useful in the manufacture of articles
such as gloves, by a coagulant dipping process, since they can
readily coagulate on glove molds coated with salts such as calcium
nitrate. This finding was unexpected, since PEG typically is used
to make salt-stable latexes, i.e., latexes that do not coagulate
readily. Coagulating dipping is well known to those skilled in the
art of glove making and is described in the Kirk-Othmer
Encyclopedia of Chemical Technology Third Edition, Vol. 20, pp.
453-454, as well as in the following examples. However, the step
(1) and step (2) compositions can also be used in solvent dipping
processes well known to those skilled in the art. Suitable solvents
may be selected according to solubility of polymers and may include
toluene, tetrahydrofuran, and N,N-dimethylformamide.
[0053] Also unexpected was the finding that the step (1)
composition can be used without the step (2) composition in the
coagulant dipping process, provided that the amount of at least one
reactive macromer of at least one alkylene oxide having at least
one functional group capable of free-radical transformation
comprises less than about 10 wt. % of total polymer weight in the
step (1) composition.
EXAMPLES
[0054] The following examples are presented for the purpose of
illustrating the invention disclosed herein in greater detail.
However, the examples are not to be construed as limiting the
invention here in any manner, the scope of the invention being
defined by the appended claims.
Test Methods
[0055] 1. Surface Resistivity Measurements on Antistatic Films and
Coatings Equipment:
[0056] Monroe Electronics Model 272 with Monroe 96101A-1 concentric
ring probe (conforms to ASTM D257 and ESD 11.11 specification for
5lb. concentric ring probes).
[0057] Test method:
[0058] Place glove on insulated plate.
[0059] Set meter to read "ohms/square @ 100 v".
[0060] Place concentric ring on smooth glove surface; wait 30 to 60
seconds for reading.
[0061] Record ohms/square @100v.
[0062] 2. Static Decay Measurements
[0063] Equipment: Monroe 268A+ charged plate monitor and male
"banana plug" connected to AC ground.
[0064] Test method:
[0065] Place glove on plate and fold glove in half so that fingers
are on top.
[0066] Set meter to measure decay time from 1000v to 100v.
[0067] Charge plate to just over 1000v.
[0068] Set plate control to "decay".
[0069] Using the "banana plug", touch the tip firmly to the top of
the glove (usually one of the fingers, so that there are 4 layers
of the glove between the plate and the grounding probe).
[0070] Record time.
[0071] 3. Total solids was measured using a LabWave 9000.TM. (CEM
Corporation) Moisture/Solids Analyzer
[0072] 4. pH was measured using an Acumet Basic pH Meter (Fisher
Scientific)
[0073] 5. Brookfield viscosity was measured at 60 rpm using a
Brookfield Viscometer (Brookfield Engineering Laboratories,
Inc.)
[0074] 6. Surface tension was measured using a Fisher Surface
Tensiomat Model 21.
[0075] 7. Particle size was measured using a Submicron Particle
Sizer Autodilute.sup.PAT Model 370 (NICOMP Particle Sizing
Systems).
Abbreviations
[0076] The following abbreviations are used in the examples
below:
[0077] APS=ammonium persulfate
[0078] DMEA=dimethylethanolamine
[0079] DP=degree of polymerization
[0080] DTAHQ=2,5-di(tert-amyl) hydroquinone
[0081] EDTA Na.sub.3=trisodium ethylenediaminetetraacetate
trihydrate
[0082] MAA=methacrylic acid
[0083] MePEGMA=methoxypolyethylene glycol methacrylate, also known
as methoxy polyethylene oxide (meth)acrylate
[0084] MMA=methyl (meth)acrylate
[0085] n-BA=n-butyl acrylate
[0086] SFS=sodium formaldehyde sulfoxylate
[0087] t-BHP=t-butyl hydroperoxide
Example 1
Step (1) Latex Emulsion Copolymer of 10 Wt. % MePEGMA,
Acrylonitrile, Butadiene and Methacrylic Acid
[0088] A 3-liter pressure rated glass stirred reactor was charged
with 563 grams soft water, 3.5 grams n-dodecyl mercaptan, 4.5 grams
20 wt. % aqueous solution of sodium n-dodecyl benzene sulfonate (as
a surfactant), and 0.3 grams sodium salt of polymerized alkyl
naphthalene sulfonic acid such as Daxad.TM. 17 (as a surfactant). A
monomer premix was made using 1.6 grams n-dodecyl mercaptan, 167
grams acrylonitrile, 120 grams 50 wt. % aqueous solution of MePEGMA
with an average DP.about.20 ("DP.about.20" means having an average
number of ethylene glycol units of about 20), 346 grams butadiene,
and 28 grams methacrylic acid. A reducing solution was made by
dissolving 0.8 gram EDTA Na.sub.3 (as a chelator), 0.5 gram sodium
ferric ethylenediaminetraacetate (as a reducing agent), and 2.3
grams sodium formaldehyde sulfoxylate (as a reducing agent) in 72
grams water. A soap solution was made by mixing 86 grams 20 wt. %
aqueous solution of sodium n-dodecyl benzene sulfonate, 5.5 grams
sodium salt of polymerized alkyl naphthalene sulfonic acid, and 251
grams water. Prior to initiation, 5% of the total monomer premix
weight was added to the reactor. At 35.degree. C., a solution of 4
grams APS in 50 grams water was added to the reactor. Immediately
following APS addition, the reducing solution was proportioned into
the reactor over a period of about 6 hours. After 30 minutes, the
remaining monomer premix and soap solution were proportioned into
the reactor over a period of about 5 hours. When the premix and
soap metering were complete, 30 grams 20 wt. % aqueous solution of
sodium n-dodecyl benzene sulfonate, and a solution of 4 grams APS
in 40 grams soft water was added to the reactor. Reaction
temperature was increased to 45.degree. C. When the monomer
conversion to polymer reached 92%, a solution of 1 gram
hydroxylamine sulfate in 35 grams water was added to stop the
reaction and the reactor cooled to 30.degree. C. The reactor was
vented and the following added to the reactor: 75 grams 15 wt. %
aqueous solution of 2-amino-2-methyl-1-propano- l (as a pHing
agent), 2 grams 50 wt. % aqueous solution of DTAHQ (as a
shortstopping agent), and 6 grams 40 wt. % aqueous solution of
4,4'-thiobis(3-methyl-6-tertiary butyl phenol) (as an antioxidant).
The residual monomers were removed by applying heat and vacuum.
[0089] The emulsion polymer obtained had 40 wt. % total solids, pH
8.2, 22 cP Brookfield viscosity, 34 dynes/cm surface tension, and
143 nm particle size.
[0090] An attempt to make a glove using the Example 1 latex and the
compounding and coagulant dipping procedures of Example 5 failed
because the latex did not coagulate on the glove former.
Example 2
Step (1) Latex Emulsion Copolymer of 10 Wt. % MePEGMA, Styrene,
n-Butyl Acrylate, Methyl Methacrylate and Methacrylic Acid
[0091] A monomer premix was made by mixing 150 grams water, 0.6
gram lithium hydroxide monohydrate, 11 grams disodium salt of
dodecyl (sulfophenoxy) benzenesulfonic acid, 120 grams styrene, 288
grams n-butyl acrylate, 144 grams methyl methacrylate, 50 grams 50%
aqueous solution of MePEGMA having an average number of ethylene
glycol units of about 20 (or in other words DP.about.20), 3 grams
N-dodecyl mercaptan, and 18 grams methacrylic acid. Initiator
solution-A was made by dissolving 1.2 grams sodium persulfate in 18
grams water. Initiator solution-B was made by dissolving 1.5 grams
sodium persulfate in 60 grams water. 480 grams water, 0.12 gram
lithium hydroxide monohydrate, and 1.33 grams disodium salt of
dodecyl (sulfophenoxy) benzenesulfonic acid were charged to a
3-liter reaction vessel and heated to 78.degree. C. Initiator
solution-A then was added to the reaction vessel, followed by
proportioning the monomer premix into the reaction vessel over a
period of about 3 hours. After 30 minutes, initiator solution-B was
proportioned into the reaction vessel over a period of about 4
hours. After completion of the initiator feed, 20 grams 30% aqueous
solution of lithium nitrate was added to the reaction vessel, and
the temperature was maintained at 78 C for about one hour. The
reaction vessel then was cooled to 40.degree. C. 2.1 grams 17%
aqueous solution of t-BHP (as an initiator) and 18.6 grams 2.2%
aqueous solution of sodium metabisulfite (as a reducing agent) were
added to the reaction vessel about 5 minutes apart. After about 30
minutes, the reaction vessel was cooled to room temperature and
filtered through 100-micron cloth. The pH of the product emulsion
was adjusted to about 8 using ammonium hydroxide.
[0092] The emulsion copolymer obtained had 43 wt. % total solids,
12 cP Brookfield viscosity, and 138 nm particle size.
Example 3
Step (2) Nitrile Rubber Copolymer Latex of Butadiene, Acrylonitrile
and Methacrylic Acid
[0093] A 15-gallon pressure-rated stainless steel stirred reactor
was charged with 23,800 grams water, 10,180 grams butadiene, 4,130
grams acrylonitrile, 995 grams methacrylic acid, 7.7 grams EDTA
NA.sub.3, 660 grams 20 wt. % aqueous solution of sodium n-dodecyl
benzene sulfonate, 115 grams sodium salt of polymerized alkyl
naphthalene sulfonic acid, and 80 grams n-dodecyl mercaptan. At
35.degree. C., a solution of 52 grams APS in 450 grams water was
added to the reactor. When the monomer conversion reached 40%, 880
grams 20 wt. % aqueous solution of sodium n-dodecyl benzene
sulfonate, 15 grams n-dodecyl mercaptan, and 200 grams water were
added to the reactor. At 70% monomer conversion to copolymer, 880
grams 20 wt. % aqueous solution of sodium n-dodecyl benzene
sulfonate, 31 grams n-dodecyl mercaptan, a solution of 25.9 grams
SFS in 500 grams water, and 100 grams water were added to the
reactor. When the monomer conversion reached 94%, a shortstop
solution was added and the reactor cooled to 25.degree. C. The
reactor was vented and the following added to the reactor: 1,204
grams 15 wt. % aqueous solution of DMEA, 61 grams 50 wt. % aqueous
solution of DTAHQ, and 153 grams 40 wt. % aqueous solution of
4,4'-thiobis(3-methyl-6-tertiary butyl phenol). The residual
monomers were removed by applying heat and vacuum.
[0094] The emulsion copolymer obtained had 36 wt. % total solids,
pH 8, 10 cP Brookfield viscosity, 29 dynes/cm surface tension, and
125 nm particle size.
Example 4
Blending of Step (1) and Step (2) Latexes
[0095] Step (1) polymer latexes from either Example 1 or Example 2
were blended with the step (2) nitrile rubber latex of Example 3
using mild agitation. The ratios of the step (1) to step (2)
polymers ranged from 10%/90% respectively to 50%/50% respectively
on a dry weight basis with 10% increments. Optionally, lithium
nitrate was added to the Example 1 or Example 2 polymer latex prior
to blending. The amount of lithium nitrate used is indicated in
Table 3.
Example 5
Compounding and Coagulant Dipping Procedures to Make Antistatic
Gloves
[0096] The blended latexes of Example 4 were compounded by
sequential mixing of the following ingredients as indicated in
Table 1 (the last four ingredients were solutions or
dispersions):
1 TABLE 1 Content Weight Ingredient (phr) (grams) Latex from
Example 4 100 348.0 Water -- 11.0 KOH (4 wt. %) 0.7 26.2 Butyl
Zimate (50 wt. %) 1 3.0 Sulfur (68 wt. %) 1 2.2 Zinc Oxide (60 wt.
%) 1.3 2.5
[0097] The following procedure was used to make gloves from the
above compounded latex:
[0098] Dip glove former into warm calcium nitrate solution with
specific gravity range 1.14 to 1.22 gram/ml.
[0099] Thoroughly dry former at 140.degree. F.
[0100] Dip glove former into latex compound. (Latex compound should
be well mixed and should sit for one (1) day prior to dipping.)
Leach in warm water (120.degree. F) for two minutes.
[0101] Dry and cure at 2200.degree. F.-260.degree. F. for up to
thirty minutes.
[0102] Leach at 90.degree. F. for five minutes.
[0103] Strip glove from mold.
[0104] The ESD properties for gloves manufactured by the method
above are presented in Tables 2, 3, and 5 (except for Examples 6
and 7 which are controls).
Examples 6-17
ESD Properties of Gloves
[0105] Examples 6 and 7 are controls. The glove in Example 6 was
made from the step (2) nitrile rubber latex of Example 3 using the
methods of Example 5. No step (1) latex was employed in Example 6.
Example 7 is a comparison glove from Ansell obtained through
commercial channels.
[0106] Examples 8 to 17 were performed using a step (1) polymer
latex made by the method of Example 1 (except for variation of
monomer concentrations on a dry weight basis as shown in the second
and third columns of Table 2 below). The respective step (1)
latexes in each example were blended with the step (2) nitrile
rubber latex of Example 3 using the blending method of Example 4.
Variations in amounts of step (1) latex are set forth in the fourth
column of Table 2 below, with the relative amount of step (1) latex
being expressed as a weight percentage of the blend of step (1) and
step (2) latexes on a dry weight basis. The blend of step (1) and
step (2) latexes then was compounded and used to make gloves
according to the method of Example 5. Each glove was tested for
surface resistivity and static decay as set forth in the fifth and
sixth columns of Table 2 below.
[0107] Control Example 6 (containing no step (1) polymer) and
control Example 7 (a comparative sample glove from Ansell) have
inferior surface resistivity and static decay. In comparison,
Examples 8-17 show superior static decay, surface resistivity, or
both.
2TABLE 2 Step (1) Polymer MePEGMA Butadiene (wt. % of Surface
Static (wt. % of (wt. % of blend with Resistivity Decay step (1)
step (1) step (2) (ohms/sq) (sec) of No. latex)* latex)* latex)**
of Glove Glove 6 Latex from Example 3 0 1.9E12 1.6 7 Glove from
Ansell -- 1.8E12 1.35 8 10 57.6 10 1.5E10 0.3 9 10 57.6 20 2.9E9
0.5 10 10 57.6 30 2.8E10 1.0 11 10 57.6 40 3.0E9 0.1 12 10 57.6 50
3.3E9 0.2 13 15 52.6 10 5.3E10 1.9 14 15 52.6 20 7.5E10 1.1 15 15
52.6 30 1.7E10 0.6 16 15 52.6 40 1.6E10 0.3 17 15 52.6 50 1.1E10
0.2 *All step (1) latexes contain 27.8 wt. % acrylonitrile and 4.6
wt. % methacrylic acid on a dry weight basis. **All weight
percentages are expressed on a dry weight basis.
Examples 18-22
[0108] Examples 18 to 21 were performed using a step (1) polymer
latex made by the method of Example 2 (except for variation of
monomer concentrations on a dry weight basis as shown in Table 3
below). In each of Examples 18 to 21, the total of all monomer
weight percentages is 100 wt. % each respective step (1) polymer.
The step (1) latex of each example was blended with the step (2)
nitrile rubber latex of Example 3 using the blending method of
Example 4. The ratio of step (1) latex to step (2) latex was the
same in each of Examples 18-21 and was about 1:4 on a dry weight
basis. The blend of step (1) and step (2) latexes then was
compounded and used to make gloves according to the method of
Example 5. Each glove was tested for surface resistivity and static
decay as set forth in the eighth and ninth columns of Table 3
below. Examples 18-21 show superior static decay, surface
resistivity, or both.
[0109] As with Examples 18-21, the Example 22 total of all monomer
weight percentages is 100 wt. % of the step (1) polymer. A polymer
solution rather than a latex was produced. Then 2 wt. % of this
Example 22 step (1) solution was blended with the step (2) nitrile
rubber latex of Example 3 using the blending method of Example 4.
The blend was then compounded and used to make a glove according to
the method of Example 5. Tests of this glove for surface
resistivity and static decay produced superior results that are set
forth in the eighth and ninth columns of Table 3 below.
3TABLE 3 Surface Static Resistivity Decay Ex. MePEGMA n-BA Styrene
MMA MAA LiNO.sub.3 (Ohms/sq) (sec) of No. (wt. %) (wt. %) (wt. %)
(wt. %) (wt. %) (wt. %)* of Glove Glove 18 10 43 20 24 3 1 1.1 E8
0.1 19 10 43 20 24 3 2 4.4 E8 0.1 20 15 50 14 18 3 1.25 1.2 E8 0.1
21 15 58 10 14 3 2 6.4 E9 0.13 22 100 0 0 0 0 1 3.1 E10 0.16
*Lithium nitrate concentration is expressed as wt. % based on 100
wt. % total amount of step (1) monomers.
Example 23
Step (1) Latex Emulsion Copolymer of 0.5 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0110] A 15-gallon pressure-rated stainless steel stirred reactor
was charged with 23,800 grams water, 10,100 grams butadiene, 4,130
grams acrylonitrile, 995 grams methacrylic acid, 153 grams 50 wt. %
aqueous solution of MePEGMA having an average number of ethylene
glycol units of about 20 (or in other words or in other words
DP.about.20), 7.7 grams EDTA NA.sub.3, 660 grams 20 wt. % aqueous
solution of sodium n-dodecyl benzene sulfonate, 115 grams sodium
salt of polymerized alkyl naphthalene sulfonic acid, and 80 grams
n-dodecyl mercaptan. At 35.degree. C., a solution of 52 grams APS
in 450 grams water was added to the reactor. When the monomer
conversion to copolymer reached 40%, 880 grams 20 wt. % aqueous
solution of sodium n-dodecyl benzene sulfonate, 15 grams n-dodecyl
mercaptan, and 200 grams water were added to the reactor. At 70%
conversion, 880 grams 20 wt. % aqueous solution of sodium n-dodecyl
benzene sulfonate, 31 grams n-dodecyl mercaptan, a solution of 25.9
grams SFS in 500 grams water, and 100 grams water were added to the
reactor. When the monomer conversion reached 94%, a shortstop
solution was added and the reactor cooled to 25.degree. C. The
reactor was vented and the following added to the reactor: 1,204
grams 15 wt. % aqueous solution of DMEA, 61 grams 50 wt. % aqueous
solution of DTAHQ, and 153 grams 40 wt. % aqueous solution of
4,4'-thiobis(3-methyl-6-tertiary butyl phenol). The residual
monomers were removed by applying heat and vacuum.
[0111] The emulsion polymer obtained had 36 wt. % total solids, pH
8, 10 cP Brookfield viscosity, 29 dynes/cm surface tension, and 125
nm particle size.
Example 24
Step (1) Latex Emulsion Copolymer of 1 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0112] An emulsion copolymer was prepared in a manner identical to
Example 23 with the exception that 306 grams 50 wt. % aqueous
solution of MePEGMA with an average DP.about.20, and 10,022 grams
butadiene were used, and the latex was neutralized with 1,182 grams
15 wt. % aqueous solution of 2-amino-2-methyl-1-propanol instead of
DMEA.
[0113] The emulsion polymer obtained had 36 wt. % total solids, pH
8.2, 11 cP Brookfield viscosity, 32 dynes/cm surface tension, and
122 nm particle size.
Example 25
Step (1) Latex Emulsion Copolymer of 1.5 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0114] An emulsion copolymer was prepared in a manner identical to
Example 23 with the exception that 459 grams 50 wt. % aqueous
solution of MePEGMA with an average DP-20, and 9,945 grams
butadiene were used, and the latex was neutralized with 920 grams
15 wt. % 2-amino-2-methyl-1-propanol.
[0115] The emulsion polymer obtained had 39 wt. % total solids, pH
8.3, 22 cP Brookfield viscosity, 32 dynes/cm surface tension, and
131 nm particle size.
Example 26
Step (1) Latex Emulsion Copolymer of 2 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0116] An emulsion copolymer was prepared in a manner identical to
Example 23 with the exception that 581 grams 50 wt. % aqueous
solution of MePEGMA with an average DP.about.20, and 9,880 grams
butadiene were used, and the latex was neutralized with 1,050 grams
15 wt. % aqueous solution of 2-amino-2-methyl-1 -propanol.
[0117] The emulsion polymer obtained had 40 wt. % total solids,
pH=8.1, 16 cP Brookfield viscosity, 32 dynes/cm surface tension,
and 132 nm particle size.
Example 27
Step (1) Latex Emulsion Copolymer of 2 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0118] A 15-gallon pressure-rated stainless steel stirred reactor
was charged with 23,800 grams water, 8,430 grams butadiene, 6,120
grams acrylonitrile, 460 grams methacrylic acid, 581 grams 50 wt. %
aqueous solution of MePEGMA with an average DP.about.20, 7.7 grams
EDTA Na.sub.3, 1,020 grams 20 wt. % aqueous solution of sodium
n-dodecyl benzene sulfonate, 115 grams sodium salt of polymerized
alkyl naphthalene sulfonic acid, and 107 grams n-dodecyl mercaptan.
At 35.degree. C., a solution of 49 grams APS in 450 grams water was
added to the reactor. When the monomer conversion to copolymer
reached 40%, 920 grams 20 wt. % aqueous solution of sodium
n-dodecyl benzene sulfonate, 15 grams n-dodecyl mercaptan, and 200
grams water were added to the reactor. At 70% conversion, 550 grams
20 wt. % aqueous solution of sodium n-dodecyl benzene sulfonate, 46
grams n-dodecyl mercaptan, a solution of 17 grams SFS in 500 grams
water, and 100 grams water were added to the reactor. When the
monomer conversion 20 reached 94%, a shortstop solution was added
and the reactor cooled to 25.degree. C. The reactor was vented and
the following added to the reactor: 850 grams 15 wt. % aqueous
solution 2-amino-2-methyl-1-propanol, 61 grams 50 wt. % aqueous
solution of DTAHQ, and 153 grams 40 wt. % aqueous solution of
4,4'-thiobis(3-methyl-6-tertia- ry butyl phenol). The residual
monomers were removed by applying heat and vacuum.
[0119] The emulsion polymer obtained had 45 wt. % total solids, pH
8.2, 20 cP Brookfield viscosity, 32 dynes/cm surface tension, and
126 nm particle size.
Example 28
Step (1) Latex Emulsion Copolymer of 1 Wt. % MePEGMA, Butadiene,
Acrylonitrile, Methacrylic Acid, and Methyl Methacrylate
[0120] A 15-gallon pressure-rated stainless steel stirred reactor
was charged with 27,900 grams water, 10,247 grams butadiene, 4,374
grams acrylonitrile, 608 grams methacrylic acid, 324 grams 50 wt. %
aqueous solution of MePEGMA with an average DP.about.20, 810 grams
methyl methacrylate, 8.1 EDTA Na.sub.3, 699 grams 20 wt. % aqueous
solution of sodium n-dodecyl benzene sulfonate, 122 grams sodium
salt of polymerized alkyl naphthalene sulfonic acid, and 85 grams
n-dodecyl mercaptan. At 35.degree. C., a solution of 55 grams APS
in 450 grams water was added to the reactor. When the monomer
conversion to copolymer reached 40%, 932 grams 20 wt. % aqueous
solution of sodium n-dodecyl benzene sulfonate, 16 grams n-dodecyl
mercaptan, and 200 grams water were added to the reactor. At 70%
conversion, 932 grams 20 wt. % aqueous solution of sodium n-dodecyl
benzene sulfonate, 32 grams n-dodecyl mercaptan, a solution of 27.5
grams SFS in 500 grams water, and 100 grams water were added to the
reactor. When the monomer conversion reached 91%, a shortstop
solution was added and the reactor cooled to 25.degree. C. The
reactor was vented and the following added to the reactor: 518
grams 20 wt. % aqueous solution of 2-amino-2-methyl-1-propanol, 65
grams 50 wt. % aqueous solution of DTAHQ, and 162 grams 40 wt. %
aqueous solution of 4,4'-thiobis(3-methyl-6-tertiary butyl phenol).
The residual monomers were removed by applying heat and vacuum.
[0121] The emulsion polymer obtained had 36 wt. % total solids, pH
8.2, 10 cP Brookfield viscosity, 33 dynes/cm surface tension, and
123 nm particle size.
Example 29
Step (1) Latex Emulsion Copolymer of 2 Wt. % MePEGMA, Butadiene,
Acrylonitrile and Methacrylic Acid
[0122] A 15-gallon pressure-rated stainless steel stirred reactor
was charged with 27,900 grams water, 7,630 grams butadiene, 7,290
grams acrylonitrile, 972 grams methacrylic acid, 8.1 EDTA Na.sub.3,
769 grams 20 wt. % aqueous solution of sodium n-dodecyl benzene
sulfonate, 122 grams sodium salt of polymerized alkyl naphthalene
sulfonic acid, and 85 grams n-dodecyl mercaptan. At.35.degree. C.,
a solution of 55 grams APS in 450 grams water was added to the
reactor. When the monomer conversion to copolymer reached 40%, 932
grams 20 wt. % aqueous solution of sodium n-dodecyl benzene
sulfonate, 308 grams 50 wt. % aqueous solution of MePEGMA with an
average DP-7, 16 grams n-dodecyl mercaptan, and 200 grams water
were added to the reactor. At 70% conversion, 932 grams 20 wt. %
aqueous solution of sodium n-dodecyl benzene sulfonate, 32 grams
n-dodecyl mercaptan, a solution of 27.5 grams SFS in 500 grams
water, and 100 grams water were added to the reactor. When the
monomer conversion reached 94%, a shortstop solution was added and
the reactor cooled to 25.degree. C. The reactor was vented and the
following added to the reactor: 2,258 grams 20 wt. % aqueous
solution of 2-amino-2-methyl-1-prop- anol, 65 grams 50 wt. %
solution of 2,5-di(tert-amyl) hydroquinone (DTAHQ), and 162 grams
40 wt. % solution of 4,4'-thiobis(3-methyl-6-terti- ary butyl
phenol). The residual monomers were removed by applying heat and
vacuum.
[0123] The emulsion polymer obtained had 38 wt. % total solids, pH
8.2, 225 cP Brookfield viscosity, 34 dynes/cm surface tension, and
140 nm particle size.
Examples 30-34
Step (1) Latex Emulsion Copolymers of 2 to 6 Wt. % MePEGMA,
Butadiene, Acrylonitrile and Methacrylic Acid
[0124] The emulsions of Examples 30-34 were prepared in a manner
identical to Example 29, except for the differences in the
variables listed in Table 4. The levels of each monomer unit in
their respective copolymers are based on the dry weight of the
respective copolymers. All of the emulsions were neutralized with
2-amino-2-methyl-1-propanol to pH of about 8.0 -8.5.
4TABLE 4 Timing of MePEGMA Acrylonitrile MMA Addition MePEGMA
MePEGMA Butadiene (wt. % (wt. % MAA (at % (wt. % of average (wt. %
of of step of (wt. % of conversion Ex. step (1) degree step (1) (1)
step (1) step (1) to No. latex)* of polymerization latex)* latex)*
latex* latex)* copolymer) 23 0.5 20 66 27 0 6.5 0 24 1 20 65.5 27 0
6.5 0 25 1.5 20 65 27 0 6.5 0 26 2 20 64.6 27 0 6.5 0 27 2 20 55 40
0 3 0 28 1 20 63 27 5 4 0 29 2 7 47 45 0 6 44 30 2 7 67 27 0 4 70
31 2 45 67 27 0 4 0 32 4 20 65 27 0 4 41 33 6 7 63 27 0 4 0 34 6 7
43 45 0 6 70 *All weight percentages are expressed on a dry weight
basis.
[0125] Each step (1) latex of Examples 23-34 was compounded and
used to make gloves according to the method of Example 5. Each
glove was tested for surface resistivity and static decay, and test
results are set forth in the second and third columns of Table 5
below.
Example 35
Step (1) Latex Emulsion Copolymer of 5 Wt. % MePEGMA, Styrene,
Butadiene, Methacrylic Acid
[0126] Example 35 was performed using a step (1) polymer latex made
by the method of Example 1, except that the following monomer
amounts were used: 65.4 wt. % Butadiene, 25 wt. % Styrene, 4.6 wt.
% Methacrylic Acid, and 5% MePEGMA (DP.about.20). The step (1)
latex of Example 35 was blended with the step (2) nitrile rubber
latex of Example 3 in a 1:1 weight ratio by the method of Example
4. The blend was compounded and used to make gloves according to
the method of Example 5. The glove was tested for surface
resistivity and static decay, and test results are set forth in the
second and third columns of Table 5 below.
[0127] Control Example 6 (containing no step (1) polymer) and
Control Example 7 (a comparative sample glove from Ansell) have
inferior surface resistivity and static decay. It is also noted
that an attempt failed to make a glove using the step (1) latex of
Example 1 (copolymer of 10% MePEGMA, acrylonitrile, butadiene and
methacrylic acid) using the compounding and coagulate dipping
procedures of Example 5, since the latex did not coagulate glove
former. In comparison, Examples 23-35 show superior surface
resistivity, static decay, or both.
5TABLE 5 Example Surface Resistivity Static Decay (sec) No.
(ohms/sq) of Glove of Glove 6 (Latex from Example 3) 1.9 E12 1.6 7
(Glove from Ansell) 1.8 E12 1.35 23 1.7 E11 0.7 24 2.0 E10 0.63 25
2.8 E9 0.13 26 2.5 E9 0.17 27 1.4 E9 0.13 28 9.0 E10 0.3 29 7.4 E10
0.03 30 3.5 E10 0.13 31 4.3 E10 0.13 32 1.1 E11 0.37 33 3.8 E10 0.1
34 9.7 E7 <0.1 35 3.2 E7 <0.1
Example 36
Core-Shell Emulsion Polymerization as Comparison
[0128] In a comparison example, 80 wt. % of the nitrile rubber
latex made in Example 3 was used as seeds, and 20 wt. % of the
monomer mixture used in Example 18 was polymerized over the seeds
in an emulsion polymerization process.
[0129] A monomer premix was made by mixing 175 grams water, 0.7
gram lithium hydroxide monohydrate, 12.4 grams disodium salt of
dodecyl (sulfophenoxy) benzenesulfonic acid, 24 grams styrene, 60.2
grams n-butyl acrylate, 28.57 grams 50 wt. % aqueous solution of
MePEGMA, 33.6 grams methyl methacrylate, 0.7 gram n-dodecyl
mercaptan, and 4.2 grams methacrylic acid. Initiator solution-A was
made by dissolving 1.4 grams sodium persulfate in 21 grams water.
Initiator solution-B was made by dissolving 1.75 grams sodium
persulfate in 35 grams water. 1.56 grams disodium salt of dodecyl
(sulfophenoxy) benzenesulfonic acid and 1400 grams emulsion
copolymer (40% solids) made in Example 3 were charged to a 3-liter
reaction vessel and heated to 78.degree. C. Initiator solution-A
was then added to the reaction vessel, followed by proportioning
the monomer premix and initiator solution-B into the reaction
vessel for a period of one hour and 2.5 hours respectively. After
completion of the initiator feed, 23.3 grams 30 wt. % aqueous
solution of lithium nitrate was added to the reaction vessel, and
the temperature was maintained at 78.degree. C. for about one hour.
The reaction vessel was then cooled to 40.degree. C.2.2 grams 17
wt. % aqueous solution of t-BHP and 21.7 grams 3.2% aqueous
solution of sodium meta-bisulfite were added to the reaction
vessel. After 30 minutes, the reaction vessel was cooled to room
temperature, and the emulsion was filtered through 100-micron
cloth.
[0130] An attempt to make a glove using the Example 36 latex and
the compounding and coagulant dipping procedures of Example 5
failed because the latex did not coagulate on the glove former.
Example 37
Core-Shell Emulsion Polymerization as Comparison
[0131] The process was the same as that of Example 36, except that
20 wt. % of the monomer mixture used in Example 20 was polymerized
over 80 wt. % of the nitrile rubber latex made in Example 3.
[0132] An attempt to make a glove using the Example 37 latex and
the compounding and coagulant dipping procedures of Example 5
failed because the latex did not coagulate on the glove former.
While in accordance with the patent statutes the best mode and
preferred embodiment has been set forth, the scope of the invention
is not limited thereto, but rather by the scope of the attached
claims.
* * * * *