U.S. patent application number 10/827376 was filed with the patent office on 2004-10-07 for electrophotographic photoreceptor, and image forming method and apparatus using the photoreceptor.
Invention is credited to Kami, Hidetoshi, Kurimoto, Eiji, Matsuyama, Akihiko, Niimi, Tatsuya, Suzuki, Tetsuro, Tamoto, Nozomu, Tamura, Hiroshi.
Application Number | 20040197688 10/827376 |
Document ID | / |
Family ID | 27481760 |
Filed Date | 2004-10-07 |
United States Patent
Application |
20040197688 |
Kind Code |
A1 |
Tamoto, Nozomu ; et
al. |
October 7, 2004 |
Electrophotographic photoreceptor, and image forming method and
apparatus using the photoreceptor
Abstract
An electrophotographic photoreceptor including an
electroconductive substrate, a photosensitive layer located
overlying the electroconductive substrate, and optionally a
protective layer overlying the photosensitive layer, wherein an
outermost layer of the photoreceptor includes a filler, a binder
resin and an organic compound having an acid value of from 10 to
700 mgKOH/g. The photosensitive layer can be the outermost layer. A
coating liquid for an outermost layer of a photoreceptor including
a filler, a binder resin, an organic compound having an acid value
of from 10 to 700 mgKOH/g and plural organic solvents. A method for
preparing a photoreceptor including forming a photosensitive layer,
and coating the coating liquid on the photosensitive layer. An
image forming method and apparatus and a process cartridge using
the photoreceptor are also provided.
Inventors: |
Tamoto, Nozomu; (Numazu-shi,
JP) ; Suzuki, Tetsuro; (Fuji-shi, JP) ;
Tamura, Hiroshi; (Susono-shi, JP) ; Niimi,
Tatsuya; (Numazu-shi, JP) ; Matsuyama, Akihiko;
(Isehara-shi, JP) ; Kurimoto, Eiji; (Numazu-shi,
JP) ; Kami, Hidetoshi; (Numazu-shi, JP) |
Correspondence
Address: |
OBLON, SPIVAK, MCCLELLAND, MAIER & NEUSTADT, P.C.
1940 DUKE STREET
ALEXANDRIA
VA
22314
US
|
Family ID: |
27481760 |
Appl. No.: |
10/827376 |
Filed: |
April 20, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10827376 |
Apr 20, 2004 |
|
|
|
09985347 |
Nov 2, 2001 |
|
|
|
Current U.S.
Class: |
430/66 ; 430/970;
524/81 |
Current CPC
Class: |
Y10S 430/103 20130101;
G03G 5/14704 20130101; G03G 5/0514 20130101; G03G 5/051 20130101;
G03G 5/0507 20130101; G03G 5/14708 20130101 |
Class at
Publication: |
430/066 ;
430/970; 524/081 |
International
Class: |
G03G 005/147 |
Foreign Application Data
Date |
Code |
Application Number |
Nov 8, 2000 |
JP |
2000-340884 |
Nov 10, 2000 |
JP |
2000-342902 |
Aug 27, 2001 |
JP |
2001-255906 |
Oct 10, 2001 |
JP |
2001-312206 |
Claims
1. An electrophotographic photoreceptor comprising: an
electroconductive substrate; a photosensitive layer located
overlying the electroconductive substrate; and optionally a
protective layer located overlying the photosensitive layer,
wherein an outermost layer of the photoreceptor comprises a filler,
a binder resin and an unsaturated polycarboxylic acid compound
having an acid value of from 10 to 700 mgKOH/g.
2. The electrophotographic photoreceptor according to claim 1,
wherein the photosensitive layer is the outermost layer
3-5. (Canceled)
6. The electrophotographic photoreceptor according to claim 1,
wherein a carboxylic group of said unsaturated polycarboxylic acid
compound is located at an end position of the unsaturated
polycarboxylic acid compound.
7. The electrophotographic photoreceptor according to claim 1,
wherein the unsaturated polycarboxylic acid compound has a number
average molecular weight of from 300 to 30,000.
8. The electrophotographic photoreceptor according to claim 1,
satisfying the following relationship:
0.1.ltoreq.(A.times.B/C).ltoreq.20 wherein A represents a content
of the organic compound in the outermost layer in units of grams, B
represents the acid value of the unsaturated polycarboxylic acid
compound in units of mgKOH/g, and C represents a content of the
filler in the outermost layer in units of grams.
9. The electrophotographic photoreceptor according to claim 1,
wherein the filler is an inorganic filler.
10. The electrophotographic photoreceptor according to claim 9,
wherein the inorganic filler is a metal oxide.
11. The electrophotographic photoreceptor according to claim 10,
wherein the metal oxide has a resistivity not less than 10.sup.10
.OMEGA..multidot.cm.
12. The electrophotographic photoreceptor according to claim 10,
wherein the metal oxide has a pH not less than 5 at an isoelectric
point of the metal oxide.
13. The electrophotographic photoreceptor according to claim 9,
wherein the inorganic filler has a surface that is treated with a
surface treating agent.
14. The electrophotographic photoreceptor according to claim 13,
wherein the surface is a surface treated with a surface treating
agent selected from the group consisting of titanate coupling
agents and aluminum coupling agents.
15. The electrophotographic photoreceptor according to claim 13,
wherein a ratio (Ws/Wf) of a weight (Ws) of the surface treating
agent to a weight (Wf) of the filler is from 0.02 to 0.30.
16. The electrophotographic photoreceptor according to claim 1,
wherein the filler has an average primary particle diameter of from
0.01 .mu.m to 0.9 .mu.m.
17. The electrophotographic photoreceptor according to claim 1,
wherein the filler is included in the outermost layer in an amount
of from 0.1% to 50% by weight based on total solid components of
the outermost layer.
18. The electrophotographic photoreceptor according to claim 1,
wherein the binder resin comprises a resin selected from the group
consisting of polycarbonate resins and polyarylate resins.
19. The electrophotographic photoreceptor according to claim 1,
wherein the binder resin comprises a charge transport polymer.
20. The electrophotographic photoreceptor according to claim 1,
wherein the outermost layer further comprises a charge transport
material.
21. The electrophotographic photoreceptor according to claim 20,
wherein the photosensitive layer comprises a charge transport
material, and wherein the charge transport material in the
outermost layer has an ionization potential not greater than an
ionization potential of the charge transport material in the
photosensitive layer.
22. The electrophotographic photoreceptor according to claim 1,
wherein the outermost layer further comprises an antioxidant.
23. The electrophotographic photoreceptor according to claim 22,
wherein the antioxidant comprises both a hindered phenol structure
and a hindered amine structure.
24. The electrophotographic photoreceptor according to claim 23,
wherein the antioxidant comprises a compound having the following
formula: 30
25. The electrophotographic photoreceptor according to claim 22,
wherein the antioxidant is included in the outermost layer in an
amount of from 0.1 to 20% by weight based on the filler in the
outermost layer, and wherein the amount is greater than an amount
of the organic compound in the outermost layer.
26. A coating liquid for an outermost layer of an
electrophotographic photoreceptor, comprising: a filler; an organic
compound having an acid value of from 10 to 700 mgKOH/g; a binder
resin; and plural organic solvents.
27. The coating liquid according to claim 26, prepared by mixing
the filler, the organic compound, the binder resin and plural
organic solvents using a ball mill containing alumina balls.
28. A method for preparing an electrophotographic photoreceptor,
comprising: mixing a filler, an organic compound having an acid
value of from 10 to 700 mg/KOH/g, and a binder resin to prepare an
outermost layer coating liquid; forming a photosensitive layer
overlying an electroconductive substrate; and coating the outermost
layer coating liquid overlying the photosensitive layer by a spray
coating method and drying the coated liquid to form an outermost
layer overlying the photosensitive layer.
29. The method according to claim 28, wherein the outermost layer
coating step is performed at least twice.
30. An image forming method comprising: charging a photoreceptor;
irradiating the photoreceptor with light to form an electrostatic
latent image on a surface of the photoreceptor; developing the
electrostatic latent image with a toner to form a toner image on
the photoreceptor; transferring the toner image onto a receiving
material optionally via an intermediate transfer medium, wherein
the photoreceptor comprises: an electroconductive substrate; a
photosensitive layer located overlying the electronconductive
substrate; and optionally a protective layer located overlying the
photosensitive layer, wherein an outermost layer of the
photoreceptor comprises a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g.
31. The image forming method according to claim 30, wherein the
photosensitive layer is the outermost layer.
32. The image forming method according to claim 30, wherein the
irradiating step includes digitally irradiating light using at
least one member selected from the group consisting of a laser
diode and a light emitting diode.
33. An image forming apparatus comprising: a photoreceptor; a
charger configured to charge the photoreceptor; an image irradiator
configured to irradiate the photoreceptor with light to form an
electrostatic latent image on the photoreceptor; an image developer
configured to develop the electrostatic latent image with a toner
to form a toner image on the photoreceptor; and an image transferer
configured to transfer the toner image onto a receiving material
optionally via an intermediate transfer medium, wherein the
photoreceptor comprises: an electroconductive substrate; a
photosensitive layer located overlying the electroconductive
substrate; and optionally a protective layer located overlying the
photosensitive layer, wherein an outermost layer of the
photoreceptor comprises a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g.
34. The image forming apparatus according to claim 33, wherein the
photosensitive layer is the outermost layer.
35. The image forming apparatus according to claim 33, further
comprising one of a laser diode and a light emitting diode
configured to emit light used by the image irradiator to digitally
irradiate the photoreceptor.
36. The image forming apparatus according to claim 33, wherein the
charger is a charging roller.
37. The image forming apparatus according to claim 36, wherein the
charging roller is configured to charge the photoreceptor while
close to but not touching an image forming area of the surface of
the photoreceptor.
38. The image forming apparatus according to claim 36, wherein the
charger is configured to charge the photoreceptor by applying a DC
voltage overlapped with an AC voltage to the surface of the
photoreceptor.
39. The image forming apparatus according to claim 33, further
comprising: a lubricant applicator configured to apply a lubricant
to the surface of the photoreceptor.
40. The image forming apparatus according to claim 39, wherein the
lubricant comprises at least one of zinc stearate and
fluorine-containing compounds.
41. The image forming apparatus according to claim 33, wherein the
toner comprises a lubricant.
42. The image forming apparatus according to claim 41, wherein the
lubricant comprises at least one of zinc stearate and
fluorine-containing compounds.
43. The image forming apparatus according to claim 33, including
the intermediate transfer medium, four sets of the photoreceptor,
and four sets of the image developer, wherein each of the four sets
of image developers includes a cyan toner, a magenta toner, a
yellow toner and a black toner to form a cyan toner image, a
magenta toner image, a yellow toner image and a black toner image
on the respective photoreceptor in parallel, wherein the cyan,
magenta, yellow and black toner images are transferred on the
intermediate transfer medium to form a full color image, and
wherein the full color toner image is transferred on the receiving
material.
44. A process cartridge comprising: a photoreceptor; and a housing
configured to contain the photoreceptor therein, wherein the
photoreceptor comprises: an electroconductive substrate; a
photosensitive layer located overlying the electroconductive
substrate; and optionally a protective layer located overlying the
photosensitive layer, wherein an outermost layer of the
photoreceptor comprises a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g.
45. The process cartridge according to claim 44, wherein the
photosensitive layer is the outermost layer.
46. The process cartridge according to claim 44, further comprising
at least one of: a charger configured to charge the photoreceptor;
an image irradiator configured to irradiate the photoreceptor with
light to form an electrostatic latent image on the photoreceptor;
an image developer configured to develop the electrostatic latent
image with a toner to form a toner image on the photoreceptor; an
image transferer configured to transfer the toner image onto a
receiving material optionally via an intermediate transfer medium;
a cleaner configured to clean a surface of the photoreceptor; and a
lubricant applicator configured to apply a lubricant to the surface
of the photoreceptor.
Description
FIELD OF THE INVENTION
[0001] The present invention relates to an electrophotographic
photoreceptor. In addition, the present invention relates to an
electrophotographic image forming method and apparatus using the
photoreceptor. Further, the present invention relates to a process
cartridge for electrophotographic image forming apparatus, which
includes the photoreceptor.
DISCUSSION OF THE BACKGROUND
[0002] Recently the growth of information processing system using
electrophotography is remarkable. In particular, digital copiers
capable of recording digital information using light after
converting information to digital signals have been drastically
improving in recording qualities and reliability. In addition, the
technique has been applied to full color laser printers and copiers
by being combined with a high speed recording technique. In the
light of this background, a need exists for a photoreceptor which
not only produces high quality images but also has high
durability.
[0003] As the photoreceptor used for such laser printers and
digital copiers, photoreceptors using an organic photosensitive
material have been widely used because of having advantages such as
good productivity and low pollution.
[0004] Specific examples of the organic photoreceptors include the
photoreceptors including one of the following photosensitive
layers:
[0005] (1) organic photoconductive resin layers typified by a
poly-N-vinylcarbazole resin;
[0006] (2) charge transfer complex type photosensitive layers
typified by a combination of poly-N-vinylcarbazole (PVK) with
2,4,7-trinitrofluorenon (TNF);
[0007] (3) pigment dispersion type photosensitive layers typified
by a combination of phthalocyanine and a binder resin; and
[0008] (4) functionally-separated photosensitive layer typified by
a combination of a charge generation material and a charge
transport material.
[0009] Among these photoreceptors, the functionally-separated
photoreceptors attract considerable attention now.
[0010] The electrophotographic image forming methods typically
include the following processes:
[0011] (1) charging an electrophotographic photoreceptor in a dark
place (charging process);
[0012] (2) irradiating the charged photoreceptor with imagewise
light to form an electrostatic latent image thereon (light
irradiating process);
[0013] (3) developing the latent image with a developer including a
toner mainly constituted of a colorant and a binder to form a toner
image thereon (developing process);
[0014] (4) optionally transferring the toner image onto an
intermediate transfer medium (first transfer process);
[0015] (5) transferring the toner image onto a receiving material
such as a receiving paper ((second) transfer process);
[0016] (6) heating the toner image to fix the toner image on the
receiving material (fixing process); and
[0017] (7) cleaning the surface of the photoreceptor (cleaning
process).
[0018] The mechanism of forming an electrostatic latent image in
the functionally-separated photosensitive layer, which has a charge
generation layer and a charge transport layer formed on the charge
generation layer, is as follows:
[0019] (1) when the photosensitive layer is exposed to light after
being charged, light passes through the transparent charge
transport layer and then reaches the charge generation layer;
[0020] (2) the charge generation material included in the charge
generation layer absorbs the light and generates a charge carrier
such as electrons and positive holes;
[0021] (3) the charge carrier is injected into the charge transport
layer and transported through the charge transport layer, which is
caused by the electric field formed by the charge on the
photosensitive layer;
[0022] (4) the charge carrier finally reaches the surface of the
photosensitive layer and neutralizes the charge thereon, resulting
in formation of an electrostatic latent image on the photosensitive
layer.
[0023] However, photosensitive layers of organic photoreceptors are
easily abraded when the photoreceptors are repeatedly used. When a
photosensitive layer is largely abraded, various image quality
problems such that the potential of the charged photoreceptor
decreases; the photosensitivity thereof deteriorates; background
fouling occurs in the resultant images; and image density decreases
tend to occur. Therefore the abrasion of photoreceptors have been a
big problem to be solved.
[0024] In addition, currently electrophotographic image forming
apparatus become smaller and smaller in size. Therefore the
diameter of photoreceptors used for such miniaturized image forming
apparatus also becomes smaller and smaller. Accordingly a need
exists for a photoreceptor having good durability.
[0025] In attempting to impart good durability to an organic
photoreceptor, the following methods have been proposed:
[0026] (1) a protective layer having lubricating property is formed
as an outermost layer of the photoreceptor;
[0027] (2) a crosslinked protective layer is formed as an outermost
layer of the photoreceptor; and
[0028] (3) a protective layer including a filler is formed as an
outermost layer of the photoreceptor.
[0029] In particular, the method (3) is effective. However, when an
electrical insulating filler is included in a protective layer, the
resistance of the protective layer increase, resulting in increase
of residual potential of the resultant photoreceptor. The increase
of residual potential is mainly caused by increase of the
resistance of the protective layer and increase of the number of
charge trap sites therein due to addition of the filler having high
insulating property. In contrast, when an electroconductive filler
is used, the resistance of the protective layer decreases, and
thereby the residual potential of the protective layer hardly
increase. However, a problem tends to occur such that the resultant
images have unclear outlines, i.e., blurred images are
produced.
[0030] In attempting to solve such a blurred image problem, a
method is proposed in which a photoreceptor having a protective
layer including an electroconductive filler is heated by a drum
heater to decrease moisture in the photoreceptor. By heating the
photoreceptor, the formation of blurred images can be avoided but
the diameter of the photoreceptor becomes large because a drum
heater has to be provided in the photoreceptor. Therefore, this
technique cannot be used for small-size photoreceptors typically
provided in current small image forming apparatus. In other words,
a photoreceptor having a small-diameter and good durability has not
yet been developed. In addition, when a drum heater is provided,
the resultant image forming apparatus becomes large in size.
Further, the image forming apparatus have other drawbacks such that
it is needed for the image forming apparatus to continuously work
the heater, resulting in increase of power consumption, and it
takes a long warm-up time.
[0031] When a photoreceptor has a high residual potential due to
use of a filler having high insulating property, the potential of a
lighted area of the photoreceptor increases, resulting in
deterioration of image density and half toner reproducibility of
the resultant images. In order to avoid such problems, the
potential of dark areas needs to be increased. However, when the
dark-area potential is increased, the electric field strength is
increased, and therefore not only undesired images such as
background fouling are produced, but also the life of the
photoreceptor is shortened.
[0032] In attempting to avoid increase of residual potential,
methods in which a photoconductive protective layer is formed have
been disclosed in Japanese Patent Publications Nos. (hereinafter
JPPs) 44-834, 43-16198 and 49-10258. However, imagewise light is
absorbed by the protective layer, and therefore the quantity of
light which reaches the photosensitive layer decreases, resulting
in decrease of the photosensitivity of the photoreceptor.
Therefore, this method is of little effect.
[0033] Japanese Laid-Open Patent Publication No. (hereinafter JOP)
57-30846 discloses a method in which a metal or a metal oxide
having an average particle diameter not greater than 0.3 .mu.m is
included as a filler in a protective layer to prepare a transparent
protective layer, resulting in prevention of increase of residual
potential. However, its effect of preventing increase of residual
potential is not insufficient, and therefore the problem cannot be
solved.
[0034] This is because the increase of residual potential is caused
by charge trapping due to the added filler and uneven dispersion of
the filler rather than deterioration of charge generation
efficiency. Even when a filler having an average particle diameter
not greater than 0.3 .mu.m is used, the transparency of the
resultant protective layer decreases if the filler aggregates. On
the contrary, when a filler having an average particle diameter not
less than 0.3 .mu.m is used, a transparent protective layer can be
formed if the filler is uniformly dispersed.
[0035] In addition, JOP 4-281461 discloses a method in which a
charge transport material is included in a protective layer
together with a filler in attempting to prepare a photoreceptor
capable of preventing increase of residual potential while having a
good mechanical strength. To include a charge transport material in
a protective layer improves the charge mobility and therefore the
increase of residual potential can be improved to some extent.
However, when a filler is added, residual potential is remarkably
increased, which is caused by the increase of resistance of the
protective layer and the number of charge trap sites in the
protective layer. Therefore, there is a limit to improvement of the
increase of residual potential only by increasing the charge
mobility. Accordingly, the demand for a photoreceptor having good
durability cannot be satisfied only by this method.
[0036] In addition, in attempting to improve the increase of
residual potential, a method in which a Lewis acid is included in a
protective layer (JOP 53-133444); a method in which an organic
proton acid is included in a protective layer (JOP 55-157748); and
a method in which an electron accepting material is included in a
protective layer (JOP 2-4275), have been disclosed.
[0037] It is considered that these methods are aimed to improve the
charge injection at the interface between the protective layer and
the charge transport layer, and portions having a low resistance
are formed in the protective layer, such that the charge can reach
the surface of the protective layer, resulting in decrease of
residual potential. The residual potential increase problem can be
improved to some extent by these methods, but the increase of
residual potential of a durable photoreceptor having a protective
layer including a filler cannot be avoided by these methods because
the reason for the residual potential increase problem occurred for
such a durable photoreceptor is different from the reason for the
residual potential increase problem improved by these methods
mentioned above. In addition, when an organic acid is included in a
protective layer in combination with a filler, the dispersion of
the filler in the protective layer tends to deteriorate and
therefore the resultant images are blurred. Thus, these methods
produce adverse effects.
[0038] JOP 2000-66434 discloses a method in which a wax having an
acid value not greater than 5 mgKOH/g is included in a protective
layer. However, the effect of adding a filler in the outermost
layer is not described in JOP 2000-66434. In addition, as can be
understood from the below-mentioned description, a satisfactory
effect cannot be exerted by this method against a photoreceptor
including a filler in the outermost layer to improve its
durability.
[0039] Japanese Patent No. 2,884,812 (i.e., JOP 4-295855) discloses
a method that a layer including a graft copolymer resin having an
acid value of from 30 to 260 mgKOH/g is formed on the surface of a
photosensitive layer. Increase of residual potential can be
prevented. However, this technique intends to improve the
lubrication property and releasability of the surface of the
photoreceptor, and in addition the photoreceptor does not include a
filler in the outermost layer, which is different from the
photoreceptor of the present invention. Further, the durability of
the photoreceptor is not discussed therein.
[0040] Namely, the outermost layer consists of a graft polymer, and
therefore the construction of the outermost layer is different from
the outermost layer of the photoreceptor of the present invention,
in which a filler is included to improve the durability
thereof.
[0041] In addition, JOP 9-281718 discloses a photoreceptor having a
photosensitive layer which includes a titanylphthalocyanine, a
polycarbonate and a resin having an acid value of from 1 to 50
mgKOH/g. This technique intends to heighten the y-properties of a
single-layer photoreceptor. Therefore, the photoreceptor is
different from the photoreceptor of the present invention, in which
a protective layer including a filler is formed on a photosensitive
layer. Namely, the durability of the photoreceptor is not discussed
therein.
[0042] On the other hand, blurred images are also produced due to
ozone and NOx. It is known that antioxidants are effective at
improving the blurred images of this kind. JOP 8-292585 discloses a
method in which at least one antioxidant selected from hindered
phenol derivatives and hindered amine derivatives is included in
the photoreceptor to reduce the chance that blurred images are
produced. It is know that this method is effective at improving the
blurred images caused by reactive gasses such as ozone and NOx.
However, residual potential of the resultant photoreceptor
increases. In particular, when a filler is included in an outermost
layer, residual potential seriously increases, resulting in
deterioration of initial image qualities. Therefore this technique
cannot be used for a photoreceptor having a protective layer
including a filler because residual potential thereof seriously
increases and high quality images cannot be produced.
[0043] Thus, a photoreceptor having a protective layer including a
filler is known. In addition, a method in which an acid is added to
the protective layer to reduce residual potential is also known.
However, a technique by which serious increase of residual
potential due to addition of a filler in a protective layer can be
improved has not been discovered. Therefore there is adesire for
aphotoreceptor capable of producing high quality images while
having good durability.
[0044] In order to produce high quality images on photoreceptors in
which a filler is included in the outermost layer to improve their
durability, it is needed to prevent formation of blurred images and
increase of residual potential. In addition, it is also important
that charges in photoreceptors linearly move toward the surface of
the photoreceptors without being obstructed by the filler included
therein. Therefore, it is needed that the filler in the protective
layer is well dispersed therein. When the filler included in a
protective layer agglomerates, movement of the charges injected
into the protective layer from the photosensitive layer are
obstructed by the filler when the charges move toward the surface
of the protective layer. Therefore a toner image formed of
scattered toner particles is formed, resulting in deterioration of
resolution of the toner image.
[0045] In addition, when imagewise light irradiates such a
protective layer including an agglomerated filler, the light is
scattered by the filler, resulting in deterioration of
light-transmittance, and thereby resolution of the resultant image
deteriorates.
[0046] Further, the dispersion of a filler included in a protective
layer largely influences the abrasion resistance of the
photoreceptor. When a filler seriously agglomerates (i.e., a filler
is poorly dispersed), not only the abrasion resistance of the
resultant photoreceptor deteriorates but also uneven abrasion
tendsto occur. Therefore a desired durability cannot be imparted to
the resultant photoreceptor.
[0047] Therefore, in order to provide a photoreceptor in which a
filler is included in a protective layer to improve the durability
of the photoreceptor and which can produce high quality images, it
is important not only to prevent occurrence of blurred images and
increase of residual potential but also to improve dispersion of
the filler in the protective layer. Namely, it is important not to
form aggregates of the filler used, i.e., to prepare a coating
liquid in which the filler is well dispersed.
[0048] However, a solution by which these problems are solved at
the same time has not been discovered. Namely, when a filler is
included in an outermost layer of a photoreceptor to improve its
durability, blurred images tend to be produced and residual
potential tends to increase, and therefore a problem in that high
quality images cannot be produced still remains. As mentioned
above, a drum heater has to be provided in an image forming
apparatus to prevent such a blurred image problem. However, a drum
heater cannot be provided in a small-sized photoreceptor, which is
especially desired to have good durability. Therefore, there is no
small-size photoreceptor having good durability and capable of
producing high quality images. To install a drum heater is an
obstruction to a small-size image forming apparatus and having low
electric power consumption.
SUMMARY OF THE INVENTION
[0049] Accordingly, an object of the present invention is to
provide a durable photoreceptor which can stably produce high
quality images without blurring wile preventing increase of
residual potential even when repeatedly used for a long period of
time.
[0050] Another object of the present invention is to provide an
image forming method by which high quality images can be stably
produced at a high speed for a long period of time without
frequently changing the photoreceptor.
[0051] A further object of the present invention is to provide a
small-size image forming apparatus and a process cartridge by which
high quality images can be stably produced at a high speed for a
long period of time without frequently changing the
photoreceptor.
[0052] Briefly these objects and other objects of the present
invention as hereinafter will become more readily apparent can be
attained by an electrophotographic photoreceptor including at least
an electroconductive substrate, one or more photosensitive layers
formed overlying the substrate and optionally a protective layer
formed overlying the photosensitive layer, wherein the outermost
layer includes at least a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g.
[0053] The outermost layer is defined as the layer furthest away
from the substrate. The photosensitive layer can be the outermost
layer. "Overlying" can include direct contact and allow for
intermediate layers.
[0054] A layer such as an undercoat layer may be formed between the
substrate and the photosensitive layer. In addition, a layer such
as intermediate layer may be formed between the photosensitive
layer and the protective layer.
[0055] It is preferable that the organic compound having an acid
value in the specified range has at least one hydrophilic group.
More preferably the hydrophilic group is a carboxyl group. The
organic compound is preferably an unsaturated polycarboxylic acid
type wetting dispersant. The number average molecular weight of the
organic compound is preferably from 300 to 30,000.
[0056] The photoreceptor preferably satisfies the following
relationship:
0.1.ltoreq.(A.times.B/C).ltoreq.20
[0057] wherein A represents the content of the organic compound
having an acid value of from 10 to 700 mgKOH/g in the outermost
layer in units of grams; B represents the acid value of the organic
compound in units of mgKOH/g; and C represents the content of the
filler in the outermost layer in units of grams.
[0058] The filler preferably includes an inorganic pigment. The
inorganic pigment is preferably a metal oxide, which preferably has
a specific resistance (i.e., resistivity) not less than 10.sup.10
.OMEGA..multidot.cm. The pH of the metal oxide at its isoelectric
point is preferably not less than 5.
[0059] It is preferable that the surface of the inorganic pigment
is subjected to a treatment preferably using a material selected
from the group consisting of titanate coupling agents and aluminum
coupling agents. The ratio (Ws/Wf) of a weight (Ws) of the surface
treating agent to a weight (Wf) of the filler is from 0.02 to 0.30.
The average primary particle diameter of the filler is preferably
form 0.01 to 0.9 .mu.m.
[0060] The content of the filler is preferably from 0.1 to 50% by
weight base on total solid components of the outermost layer.
[0061] The binder resin preferably includes a resin selected from
the group consisting of polycarbonate resins and polyarylate
resins. In addition, a charge transport polymer can be used as the
binder resin.
[0062] The outermost layer preferably includes an antioxidant,
which is preferably a compound having both a hindered phenol
structure and a hindered amine structure therein.
[0063] In another aspect of the present invention, a coating liquid
for an outermost layer of a photoreceptor is provided which
includes a filler, a binder resin, a compound having an acid value
of from 10 to 700 mgKOH/g, and a mixture of two or more organic
solvents. It is preferable that the coating liquid is dispersed by
a ball mill containing alumina balls as a dispersion element.
[0064] In yet another aspect of the present invention, a method for
preparing a photoreceptor is provided in which the coating liquid
mentioned above is coated by a spray coating method. The outermost
layer is preferably formed by performing spray coating at least
twice.
[0065] In a further aspect of the present invention, an image
forming method is provided which includes the steps of charging a
photoreceptor, irradiating the photoreceptor with light to form an
electrostatic latent image thereon, developing the latent image
with a developer to form a toner image, and transferring the toner
image on a receiving material, wherein the photoreceptor is the
photoreceptor mentioned above.
[0066] In a still further aspect of the present invention, an image
forming apparatus is provided which includes a photoreceptor, a
charger configured to charge the photoreceptor, an image irradiator
configured to irradiate the photoreceptor with light to form an
electrostatic latent image on the photoreceptor, an image developer
configured to develop the latent image with a developer to form a
toner image thereon, and a transferer configured to transfer the
toner image on a receiving material optionally via an intermediate
transfer medium, wherein the photoreceptor is the photoreceptor of
the present invention.
[0067] Preferably the image irradiator irradiates the photoreceptor
using a laser diode or a light emitting diode. In addition, the
charger is preferably a charging roller, and the charger is
preferably a proximity charging roller, which charges the
photoreceptor while a small gap is formed between the charger and
the photoreceptor and a DC voltage overlapped with an AC voltage is
applied.
[0068] The toner preferably includes a lubricant, and/or the image
forming apparatus further has a lubricant applying device
configured to apply a lubricant, such as zinc stearate and
fluorine-containing compounds, to the surface of the
photoreceptor.
[0069] The image forming apparatus may be a tandem type image
forming apparatus having four photoreceptors in which cyan,
magenta, yellow and black images are formed on the respective
photoreceptor in parallel to form a full color image. In this case,
an intermediate transfer medium is preferably used.
[0070] In a still further aspect of the invention, a process
cartridge is provided which includes at least a photoreceptor and a
housing, wherein the photoreceptor is the photoreceptor of the
present invention.
[0071] These and other objects, features and advantages of the
present invention will become apparent upon consideration of the
following description of the preferred embodiments of the present
invention taken in conjunction with the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0072] Various other objects, features and attendant advantages of
the present invention will be more fully appreciated as the same
becomes better understood from the detailed description when
considered in connection with the accompanying drawings in which
like reference characters designate like corresponding parts
throughout and wherein:
[0073] FIGS. 1 to 5 are schematic views illustrating the cross
sections of typical embodiments of the photoreceptor of the present
invention;
[0074] FIG. 6 is a schematic view illustrating an embodiment of the
image forming apparatus of the present invention and for explaining
the image forming method of the present invention;
[0075] FIG. 7 is a schematic view illustrating another embodiment
of the image forming apparatus of the present invention and for
explaining the image forming method of the present invention;
[0076] FIG. 8 is a schematic view illustrating yet another
embodiment of the image forming apparatus of the present invention
and for explaining the image forming method of the present
invention;
[0077] FIG. 9 is a schematic view illustrating an embodiment of the
process cartridge of the present invention; and
[0078] FIG. 10 is an X-ray diffraction spectrum of the titanyl
phthalocyanine used in Example 18 of the present application;
DETAILED DESCRIPTION OF THE INVENTION
[0079] As mentioned above, it is known that a filler is included in
an outermost layer of a photoreceptor to impart high durability to
the photoreceptor, i.e., to improve the abrasion resistance of the
photoreceptor. However, the method has drawbacks such that residual
potential increases, and image qualities deteriorate, e.g., blurred
images are produced.
[0080] As a result of the present inventors' investigation, it is
found that by including a highly insulative filler in an outermost
layer, production of blurred images can be avoided, and increase of
residual potential, which is caused by adding the highly insulative
filler, can be avoided by including an organic compound having an
acid value of from 10 to 700 mgKOH/g. In addition, the dispersion
of the filler is also improved by adding such an organic compound,
the resultant photoreceptor can produce high quality images. Thus,
the present invention is made.
[0081] In the present invention, increase of residual potential can
be prevented by using an organic filler having an acid value of
from 10 to 700 mgKOH/g together with a highly insulative filler.
Increase of residual potential is mainly caused by addition of such
a filler. In particular, when the filler is a hydrophilic metal
oxide having many polar groups, the tendency is strengthened. In
addition, when the filler is highly insulative, the tendency is
further strengthened.
[0082] One of the reasons why increase of residual potential can be
prevented by adding an organic compound having an acid value of
from 10 to 700 mgKOH/g is considered to be that the resistance of
the layer (the filler) is decreased by adding such an organic
compound. In addition, another reason is considered to be that when
the organic compound is a wetting dispersant having a hydrophilic
group, the compound can be adsorbed on the polar groups present on
the surface of the filler, which serves as charge trap sites, and
thereby serious increase of residual potential can be avoided.
[0083] By adding an organic compound having an acid value of from
10 to 700 mgKOH/g, dispersion of the filler used together with the
organic compound can be improved as well as reduction of residual
potential. In particular, when the filler is a hydrophilic metal
oxide, the effect can be enhanced. By improving dispersion of the
filler in the outermost layer, imagewise light irradiated to the
outermost layer to form a latent image is hardly scattered by the
outermost layer, and thereby images having high resolution and good
evenness can be produced.
[0084] In addition, by adding such an organic compound, the
following effects are also exerted:
[0085] (1) the reproducibility of dot toner images can be improved,
resulting in improvement of resolution of the resultant images;
[0086] (2) the abrasion resistance of the outermost layer can be
improved and uneven abrasion can be avoided;
[0087] (3) production of coating defects can be avoided;
[0088] (4) life of the coating liquid can be prolonged, resulting
in improvement of qualitative stability of the resultant
photoreceptor; etc.
[0089] Therefore, according to the present invention, an
electrophotographic photoreceptor which can produce high quality
images while having high durability (i.e., high quality images can
be stably produced even when repeatedly used), and a coating liquid
for the outermost layer of the photoreceptor, are provided. In
addition, according to the present invention, an
electrophotographic image forming method and apparatus, and a
process cartridge for an image forming apparatus, by which high
quality images can be stably produced even when images are
repeatedly produced, are provided.
[0090] The present invention will be explained in detail.
[0091] As mentioned above, when a filler is included in an
outermost layer of a photoreceptor to improve the abrasion
resistance of the photoreceptor, residual potential of the
photoreceptor typically increases. In addition, blurred images are
formed and resolution is decreased and therefore image qualities
deteriorate. Therefore, it is difficult to provide a photoreceptor
having good durability and capable of producing high quality
images. This is because the blurred image problem can be prevented
by heightening the resistance of the outermost layer, and residual
potential can be decreased by decreasing the resistance of the
outermost layer, resulting in trade-off therebetween.
[0092] However, by the present invention, the abrasion resistance
can be improved, increase of residual potential can be prevented
and in addition dispersion of the filler in the outermost layer can
be improved and thereby a photoreceptor having high durability and
capable of producing high quality images can be provided. The
increase of residual potential is caused mainly by polar groups
present on the surface of the filler and the high resistance filler
in the outermost layer. One of the reasons why the increase of
residual potential can be prevented is considered that by including
an organic compound having an acid value of from 10 to 700 mgKOH/g
in the outermost layer, the resistance of the filler can be
decreased. In particular, when the organic compound is a wetting
dispersant having a hydrophilic group such as a carboxyl group, the
effect can be dramatically enhanced.
[0093] Namely, the increased residual potential of a photoreceptor
having an outermost layer including a filler to improve the
abrasion resistance can be decreased by adding such an organic
compound in the outermost layer. When such an organic compound is
added to a layer including no filler, there is no effect on the
residual potential of the layer.
[0094] In particular, when a polycarboxylic acid is used as the
organic compound, the effect can be further enhanced. The reason is
considered to be that the polycarboxylic acid is adsorbed on the
surface of the filler used. When the polycarboxylic acid is
adsorbed on the filler, the dispersion of the filler in the layer
can also be improved. Polycarboxylic acid compounds can exert the
effect more effectively than other organic acids. Therefore
polycarboxylic acids are preferably used in the present
invention.
[0095] When fillers having a low resistance or acidic fillers are
used, a chance that blurred images are produced increases but
residual potential of the photoreceptor hardly increases.
Therefore, such fillers have been used for conventional
photoreceptors. Namely, conventional photoreceptors have a drawback
such that blurred images tend to be produced.
[0096] To the contrary, in the present invention a filler which has
a relatively high resistance and which is basic is used, and
therefore the blurred image problem can be prevented. However, the
residual potential of the resultant photoreceptor tends to
increase. The increased residual potential can be decreased by
adding a polycarboxylic acid compound therein. Thus, a
photoreceptor which has a low residual potential and which hardly
produce blurred images can be provided.
[0097] In the present invention, the effect can be exerted by using
a combination of a filler (in particular, a highly insulative
filler) with a polycarboxylic acid compound. By using such a
combination, increase of residual potential and blurred image
problems can be prevented while the filler is dispersed uniformly
in the outermost layer. Therefore a photoreceptor having high
durability and which can produce high quality images can be
provided.
[0098] In order to improve the abrasion resistance of an outermost
layer, to prevent the blurred image problem and to form a uniform
outermost layer without coating defects, it is preferable to use a
metal oxide, and more preferably a metal oxide having high
insulating property, as the filler in the outermost layer. However,
metal oxides typically have polar groups on the surface thereof.
Therefore the residual potential of the resultant photoreceptor
tends to increase. Accordingly electroconductive metal oxides have
been typically used for the outermost layers of conventional
photoreceptors, while the blurred image problem is prevented by
providing a drum heater which heats the photoreceptors to remove
moisture from the photoreceptor.
[0099] Organic compounds having an acid value of from 10 to 700
mgKOH/g for use in the present invention, and preferably wetting
dispersants having a hydrophilic group such as a carboxyl group,
have an affinity to hydrophilic metal oxides. In particular, when
such an organic compound is adsorbed on the polar groups present on
the surface of the filler used, which polar groups serve as trap
sites, the residual potential of the resultant photoreceptor can be
effectively and dramatically decreased.
[0100] The thus decreased residual potential can be maintained even
after long repeated use. Therefore the photoreceptor has good
durability. Since the residual potential (i.e., the potential of a
lighted area of the photoreceptor) is decreased, the potential of a
dark area of the photoreceptor can be set so as to be relatively
low. Therefore, the electric field strength can be decreased, and
thereby a chance of producing undesired images can be reduced.
Accordingly the photoreceptor has good durability.
[0101] In order to prevent production of blurred images which are
caused by ozone and NOx included in an atmosphere surrounding the
photoreceptor, an additive such as antioxidants is typically
included in the photoreceptor. To add an antioxidant in a
photoreceptor increases the residual potential of the
photoreceptor. However, the photoreceptor of the present invention
has an excess ability to decrease the residual potential, and
therefore even when such an antioxidant is added, the increase of
the residual potential can be prevented while the blurred image
problem is prevented. Therefore, the photoreceptor of the present
invention has good durability.
[0102] By using a combination of a filler with an organic compound
having an acid value of from 10 to 700 mgKOH/g, the dispersion of
the filler in the resultant layer can also be improved. When a
hydrophilic inorganic filler, which typically has a poor affinity
to organic solvents and binder resins, the filler tends to
agglomerate in the coating liquid and the resultant layer. In
particular, when metal oxides are used as the filler, this
agglomeration problem tends to occur although metal oxides are
advantageous in view of abrasion resistance, light scattering and
film quality of the resultant layer.
[0103] By including an organic compound having an acid value of
from 10 to 700 mgKOH/g (in particular, a wetting dispersant having
a hydrophilic group such as a carboxyl group), the affinity of the
added inorganic filler to organic solvents and binder resins can be
improved. Therefore, the dispersion of the filler in the resultant
layer can dramatically be enhanced.
[0104] In order to improve the dispersion of a filler in a layer,
it is important to wet the filler with the solvent and binder resin
used, resulting in stabilization of the filler. By including an
organic compound having an acid value of from 10 to 700 mgKOH/g (in
particular, a wetting dispersant having a hydrophilic group such as
a carboxyl group), the hydrophilic group is adsorbed on the polar
groups present on the surface of the filler while the hydrophobic
group of the wetting dispersant has an affinity to the binder
resin, and thereby the wettability of the filler is dramatically
improved, resulting in improvement of dispersion of the filler. In
addition, the agglomeration of the filler in the coating liquid can
also be prevented and therefore the life of the coating liquid can
be prolonged.
[0105] When a basic filler is used as the filler, an organic
compound having an acid value of from 10 to 700 mgKOH/g is adsorbed
on the filler more effectively than in the case in which an acidic
filler is used. Therefore the dispersion of the filler can be
dramatically improved. In particular, in the present invention,
when a metal oxide having a pH not less than at the isoelectric
point thereof is used as the filler, dispersion of the filler can
be dramatically improved and in addition the effect on decrease of
residual potential can be effectively enhanced. Therefore, it is
preferable to use such a metal oxide as the filler. Basic fillers
are advantageous against acidic fillers because the resultant
photoreceptor hardly produce blurred images.
[0106] As can be understood from the above description, by using a
combination of a basic filler with an organic compound having an
acid value of from 10 to 700 mgKOH/g, the following effects can be
exerted:
[0107] (1) dispersion of the filler in the coating liquid and the
resultant layer can be improved;
[0108] (2) increase of residual potential of the resultant
photoreceptor can be prevented; and
[0109] (3) the blurred image problem can be prevented, and thereby
high quality images can be produced.
[0110] Since dispersion of the filler in the resulting outermost
layer is improved in the present invention, the charges injected to
the outermost layer can easily reach the surface of the outermost
layer. Therefore, the resultant electrostatic latent image consists
of high resolution dot images, and the resultant toner image has
high resolution. Therefore images having good resolution can be
produced.
[0111] To the contrary, when the filler in the outermost layer is
agglomerated, straight movement of the charges injected to the
layer is obstructed by the agglomerated filler, resulting in
deterioration of resolution of the resultant images.
[0112] In addition, by improving dispersion of the filler in the
outermost layer, scattering of light used for recording images can
be prevented. Namely, the light transmittance of the outermost
layer can be improved, resulting in improvement of photosensitivity
and prevention of uneven density images. In addition, the resultant
outermost layer has good abrasion resistance, good resistance to
uneven abrasion and less coating defects. Since the outermost layer
has high light transmittance, the photoreceptor can be used for
image forming apparatus using light having a relatively short
wavelength for recording images. Namely, by using a visible laser
for recording latent images on such a photoreceptor, it is possible
to produce images having excellent image qualities. In addition,
since the filler is stably dispersed in a coating liquid, an
outermost layer in which the filler is uniformly dispersed can be
stably formed, and thereby a photoreceptor having good durability
and capable of producing high quality images even when repeatedly
used for a long period of time can be stably produced.
[0113] Next, the photoreceptor of the present invention will be
explained referring to drawings.
[0114] FIG. 1 is a schematic view illustrating the cross section of
an embodiment of the photoreceptor of the present invention.
[0115] In FIG. 1, a single-layer photosensitive layer 33 including
a charge generation material (hereinafter a CGM) and a charge
transport material (hereinafter a CTM) as main components is formed
on an electroconductive substrate 31. The photosensitive layer 33,
which is the outermost layer of this photoreceptor, includes a
filler, a binder resin and an organic compound having an acid value
of from 10 to 700 mgKOH/g as well as the CGM and CTM. The filler
may be included uniformly in the photosensitive layer 33 or
included such that the concentration of the filler increase in the
upward direction of the photosensitive layer 33.
[0116] FIG. 2 is a schematic view illustrating the cross section of
another embodiment of the photoreceptor of the present
invention.
[0117] In FIG. 2, a charge generation layer (hereinafter a CGL) 35
including a CGM as a main component and a charge transport layer
(hereinafter a CTL) 37 including a CTM as a main component are
overlaid on an electroconductive substrate 31 in this order.
[0118] The CTL 37, which is the outermost layer of this
photoreceptor, includes a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g as well as
the CTM. The filler may be included uniformly in the CTL 37 or
included such that the concentration of the filler increases in the
upward direction of the CTL 37.
[0119] FIG. 3 is a schematic view illustrating the cross section of
yet another embodiment of the photoreceptor of the present
invention.
[0120] In FIG. 3, a photosensitive layer 33 which includes a CGM
and a CTM as main components is formed on an electroconductive
substrate 31, and a protective layer 39 is formed on the
photosensitive layer 33. The protective layer 39, which is the
outermost layer of this photoreceptor, includes at least a filler,
a binder resin and an organic compound having an acid value of from
10 to 700 mgKOH/g.
[0121] FIG. 4 is a schematic view illustrating the cross section of
a further embodiment of the photoreceptor of the present
invention.
[0122] In FIG. 4, a CGL 35 including a CGM as a main component and
a CTL 37 including a CTM as a main component are overlaid on an
electroconductive substrate 31 in this order. In addition, a
protective layer 39 is formed on the CTL 37. In this case, the
protective layer 39, which is the outermost layer of the
photoreceptor, includes at least a filler, a binder resin and an
organic compound having an acid value of from 10 to 700
mgKOH/g.
[0123] FIG. 5 is a schematic view illustrating the cross section of
a still further embodiment of the photoreceptor of the present
invention.
[0124] In FIG. 5, a CTL 37 including a CTM as a main component and
a CGL 35 including a CGM as a main component are overlaid on an
electroconductive substrate 31 in this order. In addition, a
protective layer 39 is formed on the CGL 35. In this case, the
protective layer 39, which is the outermost layer of this
photoreceptor, includes at least a filler, a binder resin and an
organic compound having an acid value of from 10 to 700
mgKOH/g.
[0125] Suitable materials for use as the electroconductive
substrate 31 include materials having a volume resistance not
greater than 10.sup.10 .OMEGA..multidot.cm. Specific examples of
such materials include plastic cylinders, plastic films or paper
sheets, on the surface of which a metal such as aluminum, nickel,
chromium, nichrome, copper, gold, silver, platinum and the like, or
a metal oxide such as tin oxides, indium oxides and the like, is
deposited or sputtered. In addition, a plate of a metal such as
aluminum, aluminum alloys, nickel and stainless steel can be used.
A metal cylinder can also be used as the substrate 31, which is
prepared by tubing a metal such as aluminum, aluminum alloys,
nickel and stainless steel by a method such as impact ironing or
direct ironing, and then treating the surface of the tube by
cutting, super finishing, polishing and the like treatments.
Further, endless belts of a metal such as nickel, stainless steel
and the like, which have been disclosed, for example, in Japanese
Laid-Open Patent Publication No. 52-36016, can also be used as the
substrate 31.
[0126] Furthermore, substrates, in which a coating liquid including
a binder resin and an electroconductive powder is coated on the
supports mentioned above, can be used as the substrate 31. Specific
examples of such an electroconductive powder include carbon black,
acetylene black, powders of metals such as aluminum, nickel, iron,
nichrome, copper, zinc, silver and the like, and metal oxides such
as electroconductive tin oxides, ITO and the like. Specific
examples of the binder resin include known thermoplastic resins,
thermosetting resins and photo-crosslinking resins, such as
polystyrene, styrene-acrylonitrile copolymers, styrene-butadiene
copolymers, styrene-maleic anhydride copolymers, polyesters,
polyvinyl chloride, vinyl chloride-vinyl acetate copolymers,
polyvinyl acetate, polyvinylidene chloride, polyarylates, phenoxy
resins, polycarbonates, cellulose acetate resins, ethyl cellulose
resins, polyvinyl butyral resins, polyvinyl formal resins,
polyvinyl toluene, poly-N-vinyl carbazole, acrylic resins, silicone
resins, epoxy resins, melamine resins, urethane resins, phenolic
resins, alkyd resins and the like resins.
[0127] Such an electroconductive layer can be formed by coating a
coating liquid in which an electroconductive powder and a binder
resin are dispersed or dissolved in a proper solvent such as
tetrahydrofuran, dichloromethane, methyl ethyl ketone, toluene and
the like solvent, and then drying the coated liquid.
[0128] In addition, substrates, in which an electroconductive resin
film is formed on a surface of a cylindrical substrate using a
heat-shrinkable resin tube which is made of a combination of a
resin such as polyvinyl chloride, polypropylene, polyesters,
polyvinylidene chloride, polyethylene, chlorinated rubber and
fluorine-containing resins, with an electroconductive material, can
also be used as the substrate 31.
[0129] Next, the photosensitive layer of the photoreceptor of the
present invention will be explained.
[0130] In the present invention, the photosensitive layer may be a
single-layered photosensitive layer or a multi-layered
photosensitive layer.
[0131] At first, the multi-layered photosensitive layer including
the CGL 35 and the CTL 37 will be explained.
[0132] The CGL 35 includes a CGM as a main component. In the CGL
35, known charge generation materials can be used. Specific
examples of such CGMs include azo pigments such as monoazo
pigments, disazo pigments, asymmetric disazo pigments and trisazo
pigments; phthalocyanine pigments such as titanyl phthalocyanine,
copper phthalocyanine, vanadyl phthalocyanine, hydroxygallium
phthalocyanine and metal free phthalocyanine; perylene pigments,
perynone pigments, indigo pigments, pyrrolopyrrole pigments,
anthraquinone pigments, quinacridone pigments, quinone type
condensed polycyclic compounds, squaric acid type dyes, and the
like pigments and dyes. These CGMs can be used alone or in
combination.
[0133] Suitable binder resins, which are optionally mixed in the
CGL coating liquid, include polyamide, polyurethane, epoxy resins,
polyketone, polycarbonate, silicone resins, acrylic resins,
polyvinyl butyral, polyvinyl formal, polyvinyl ketone, polystyrene,
polysulfone, poly-N-vinylcarbazole, polyacrylamide, polyvinyl
benzal, polyester, phenoxy resins, vinyl chloride-vinyl acetate
copolymers, polyvinyl acetate, polyphenylene oxide, polyamides,
polyvinyl pyridine, cellulose resins, casein, polyvinyl alcohol,
polyvinyl pyrrolidone, and the like resins.
[0134] The content of the binder resin in CGL 35 is preferably from
0 to 500 parts by weight, and preferably from 10 to 300 parts by
weight, per 100 parts by weight of the charge generation material
included in the CGL 35.
[0135] The CGL 35 can be prepared, for example, by the following
method:
[0136] (1) a CGM is mixed with a proper solvent optionally together
with a binder resin;
[0137] (2) the mixture is dispersed using a ball mill, an attritor,
a sand mill or a supersonic dispersing machine to prepare a coating
liquid; and
[0138] (3) the coating liquid is coated on an electroconductive
substrate and then dried to form a CGL.
[0139] A binder resin can be mixed before or after the dispersion
process.
[0140] Suitable solvents for use in the CGL coating liquid include
isopropanol, acetone, methyl ethyl ketone, cyclohexanone,
tetrahydrofuran, dioxane, ethyl cellosolve, ethyl acetate, methyl
acetate, dichloromethane, dichloroethane, monochlorobenzene,
cyclohexane, toluene, xylene, ligroin, and the like solvents. In
particular, ketone type solvents, ester type solvents and ether
type solvents are preferably used. These solvents can be used alone
or in combination.
[0141] The CGL coating liquid includes a CGM, a solvent and a
binder resin as main components, but may include additives such as
sensitizers, dispersants, surfactants and silicone oils.
[0142] The CGL coating liquid can be coated by a coating method
such as dip coating, spray coating, bead coating, nozzle coating,
spinner coating and ring coating methods. The thickness of the CGL
35 is preferably from 0.01 to 5 .mu.m, and more preferably from 0.1
to 2 .mu.m.
[0143] The CTL 37 can be formed, for example, by the following
method:
[0144] (1) a CTM and a binder resin are dispersed or dissolved in a
proper solvent to prepare a CTL coating liquid; and
[0145] (2) the coating liquid is coated and dried to form a
CTL.
[0146] The CTL coating liquid may include one or more additives
such as plasticizers, leveling agents, antioxidants and the like,
if desired.
[0147] CTMs are classified into positive-hole transport materials
and electron transport materials.
[0148] Specific examples of the electron transport materials
include electron accepting materials such as chloranil, bromanil,
tetracyanoethylene, tetracyanoquinodimethane,
2,4,7-trinitro-9-fluorenon, 2,4,5,7-tetranitro-9-fluorenon,
2,4,5,7-tetanitroxanthone, 2,4,8-trinitrothioxanthone,
2,6,8-trinitro-4H-indeno[1,2-b]thiophene-4-on- e,
1,3,7-trinitrodibenzothiphene-5,5-dioxide, benzoquinone derivatives
and the like.
[0149] Specific examples of the positive-hole transport materials
include known materials such as poly-N-carbazole and its
derivatives, poly-.gamma.-carbazolylethylglutamate and its
derivatives, pyrene-formaldehyde condensation products and their
derivatives, polyvinyl pyrene, polyvinyl phenanthrene, polysilane,
oxazole derivatives, oxadiazole derivatives, imidazole derivatives,
monoarylamines, diarylamines, triarylamines, stilbene derivatives,
.alpha.-phenyl stilbene derivatives, benzidine derivatives,
diarylmethane derivatives, triarylmethane derivatives,
9-styrylanthracene derivatives, pyrazoline derivatives, divinyl
benzene derivatives, hydrazone derivatives, indene derivatives,
butadiene derivatives, pyrene derivatives, bisstilbene derivatives,
enamine derivatives, and the like.
[0150] These CTMs can be used alone or in combination.
[0151] Specific examples of the binder resin for use in the CTL 37
include known thermoplastic resins and thermosetting resins, such
as polystyrene, styrene-acrylonitrile copolymers, styrene-butadiene
copolymers, styrene-maleic anhydride copolymers, polyester,
polyvinyl chloride, vinyl chloridevinyl acetate copolymers,
polyvinyl acetate, polyvinylidene chloride, polyarylate, phenoxy
resins, polycarbonate, cellulose acetate resins, ethyl cellulose
resins, polyvinyl butyral resins, polyvinyl formal resins,
polyvinyl toluene, poly-N-vinyl carbazole, acrylic resins, silicone
resins, epoxy resins, melamine resins, urethane resins, phenolic
resins, alkyd resins and the like. Among these resins,
polycarbonate and polyarylate are preferable.
[0152] The content of the CTM in the CTL 37 is preferably from 20
to 300 parts by weight, and more preferably from 40 to 150 parts by
weight, per 100 parts by weight of the binder resin included in the
CTL 37. The thickness of the CTL 37 is preferably not greater than
25 .mu.m in view of resolution of the resultant images and response
(i.e., photosensitivity) of the resultant photoreceptor. In
addition, the thickness of the CTL 37 is preferably not less than 5
.mu.m in view of charge potential. The lower limit of the thickness
changes depending on the image forming system for which the
photoreceptor is used.
[0153] Suitable solvents for use in the CTL coating liquid include
tetrahydrofuran, dioxane, toluene, dichloromethane,
monochlorobenzene, dichloroethane, cyclohexanone, methyl ethyl
ketone, acetone and the like solvents.
[0154] Next, the single-layered photosensitive layer 33 will be
explained. The photosensitive layer 33 can be formed by coating a
coating liquid in which a CGM, a CTL and a binder resin are
dissolved or dispersed in a proper solvent, and then drying the
coated liquid. As the CGM and CTM, the CGMs and CTLs mentioned
above for use in the CGL 35 and CTL 37 can be used.
[0155] Suitable binder resins for use in the photosensitive layer
33 include the resins mentioned above for use in the CTL 37. The
resins mentioned above for use in the CGL 35 can be added as a
binder resin. In addition, the charge transport polymer materials
can also be used as a binder resin.
[0156] The content of the CGM is preferably from 5 to 40 parts by
weight, and more preferably from 10 to 30 parts by weight, per 100
parts by weight of the binder resin included in the photosensitive
layer 33. The content of the CTM is preferably from 0 to 190 parts,
and more preferably from 50 to 150 parts by weight, per 100 parts
by weight of the binder resin included in the photosensitive layer
33.
[0157] The single-layered photosensitive layer 33 can be formed by
coating a coating liquid in which a CGM, a binder and a CTM are
dissolved or dispersed in a solvent such as tetrahydrofuran,
dioxane, dichloroethane, cyclohexane, toluene, methyl ethyl ketone
and acetone by a coating method such as dip coating, spray coating,
bead coating and ring coating.
[0158] The photosensitive layer coating liquid may include
additives such as plasticizers, leveling agents, antioxidants and
lubricants. The thickness of the photosensitive layer 33 is
preferably from about 5 to about 25 .mu.m.
[0159] When the CTL 37 or photosensitive layer 33 is the outermost
layer, the CTL 37 or photosensitive layer 33 further includes a
filler, and an organic compound having an acid value of from 10 to
700 mgKOH/g. When a protective layer 39 is formed thereon, the
protective layer includes a filler, a binder resin and an organic
compound having an acid value of from 10 to 700 mgKOH/g.
[0160] As the filler added to the outermost layer of the
photoreceptor to improve the abrasion resistance of the
photoreceptor, organic fillers and inorganic fillers can be used.
Suitable organic fillers include powders of fluorine-containing
resins such as polytetrafluoroethylene, silicone resin powders,
amorphous carbon powders, etc.
[0161] Specific examples of the inorganic fillers include powders
of metals such as copper, tin, aluminum and indium; metal oxides
such as silica, tin oxide, zinc oxide, titanium oxide, alumina,
zirconia, indium oxide, antimony oxide, bismuth oxide, calcium
oxide, tin oxide doped with antimony, indium oxide doped with tin;
metal fluoride such as tin fluoride, calcium fluoride and aluminum
fluoride; potassium titanate, boron nitride, etc.
[0162] Among these fillers, inorganic fillers are preferably used
because of having high hardness and low light scattering property.
Among the inorganic fillers, metal oxides are preferable because
they can impart good abrasion resistance to the photoreceptor and
thereby the resultant photoreceptor can produce high quality
images. In addition, when metal oxides are used, the qualities of
the coated film are good. Since the qualities of the coated film
influence on the image qualities and abrasion resistance of the
photoreceptor, to form a layer having good film qualities is needed
to prepare a photoreceptor having good durability and capable of
producing high quality images.
[0163] In order to avoid the blurred image problem, a filler having
a high electrical insulating property is preferably used. When an
electroconductive filler is included in the outermost layer of a
photoreceptor, the resistance of the outermost layer decreases and
charges formed on the outermost layer tend to move in the
horizontal direction, resulting in occurrence of the blurred image
problem. Therefore, fillers having a resistivity not less than
10.sup.10 .OMEGA..multidot.cm are preferably used in the
photoreceptor of the present invention to avoid the blurred image
problem (i.e., to form high resolution images) in the present
invention. Specific examples of such fillers include alumina,
zirconia, titanium oxide, silica, etc.
[0164] Fillers having a resistivity not greater than 10.sup.10
.OMEGA..multidot.cm are not preferable in the present invention
because the blurred image problem tends to occur.
[0165] It is possible to use two or more of these fillers to
control the resistance of the outermost layer.
[0166] The pH of the filler included in the photoreceptor
influences on the resolution of the images produced by the
resultant photoreceptor and dispersion of the filler in the
resultant layer. The reason is considered to be that an acid such
as hydrochloric acid remaining in the metal oxide filler used
influences such properties. When a large amount of an acid remains
in the filler used, the blurred image problem tends to occur, and
in addition dispersion of the filler in the resultant layer
deteriorates.
[0167] The charge property of the filler (metal oxide) used also
influences such properties. In general, particles dispersed in a
liquid have a positive or negative charge. In order to neutralize
the charge, ions having the opposite charge gather around the
particles, resulting in formation of an electric double layer, and
thereby the particles are stably dispersed in the liquid. The
potential (i.e., zeta potential) in a point around a particle
gradually decreases as the point gets away from the particle, and
the potential of a point far away from the particle is zero.
Therefore, the absolute value of the zeta potential increases, the
repulsion of the particles increases, resulting in stabilization of
the particles. To the contrary, as the zeta potential approaches
zero, the particles tend to agglomerate, and thereby the particles
become unstable.
[0168] The zeta potential largely changes depending on the pH of
the dispersion system. At a pH, the zeta potential becomes zero,
namely the dispersion system has an isoelectric point. Therefore,
the pH of the dispersion system is preferably far away from the
isoelectric point to increase the absolute value of the zeta
potential, resulting in stabilization of the dispersion system.
[0169] In the present invention, the pH of the filler used is
preferably not less than 5 at the isoelectric point because the
blurred image problem can be avoided. It is observed by the present
inventors that when a basic filler is used, the effect can be
further enhanced. Fillers having a high pH (i.e., basic fillers)
have a high zeta potential in an acidic dispersion system, and
therefore dispersion and stability of the filler is increased when
the filler is used in an acidic dispersion system.
[0170] In the present invention, by using a combination of a filler
having a pH not less than 5 at the isoelectric point with a wetting
dispersant having an acid value of from 10 to 700 mgKOH/g, the
wetting dispersant is effectively adsorbed on the filler, and
thereby the dispersion and stability of the filler can be
dramatically improved.
[0171] Among the organic compounds having an acid value of from 10
to 700 mgKOH/g for use in the present invention, wetting
dispersants having a hydrophilic group such as a carboxyl group can
be preferably used because of improving the wetting property of the
filler used by being adsorbed on the filler. In particular, by
using a basic metal oxide having a pH not less than 5 at the
isoelectric point as the filler, the stability of the wetting
property can be further improved. In addition, basic fillers have
an advantage against acidic fillers such that the blurred image can
be prevented. Thus, by using such a combination, a photoreceptor
capable of producing high quality images can be provided.
[0172] Specific examples of the metal oxides having a pH not less
than 5 at the isoelectric point include titanium oxide, zirconia,
alumina, etc. In view of the basic property, alumina has a
strongest basic property, and zirconia has a stronger basic
property than titanium oxide. Therefore it is preferable to use
alumina as the filler.
[0173] Among alumina, .alpha.-form alumina having a hexagonal
closest packing structure is preferable because of having high
light transmittance, high heat stability and good abrasion
resistance. Therefore, it is particularly preferable to use
.alpha.-form alumina because the blurred image problem can be
prevented and in addition the abrasion resistance, coating quality
and light transmittance of the resultant photoreceptor can be
improved.
[0174] In the present invention, the filler having a pH not less
than 5 can be used alone or in combination. In addition, a
combination of one or more fillers having a pH not less than 5 with
one or more fillers having a pH less than 5 can be used. Specific
examples of acidic fillers having a pH less than 5 include silica,
etc.
[0175] The surface of these fillers are preferably coated with a
surface treating agent to improve dispersion of the fillers. As
mentioned above, when the dispersion of the filler used
deteriorates, various problems occurs such that the transparency of
the resultant layer decreases, coating defects are produced, the
abrasion resistance of the layer deteriorates and uneven abrasion
of the resultant layer occurs. Therefore, a photoreceptor having
good durability and capable of producing high quality images cannot
be prepared.
[0176] As the surface treating agent, known surface treating agents
can be used. However, surface treating agents capable of
maintaining the pH of the filler to be treated after the treatment
are preferably used. The pH of a filler at the isoelectric point
can be changed by treating the filler with a surface treating
agent. Namely, when a filler is treated with an acidic surface
treating agent, the isoelectric point moves to the acidic side. To
the contrary, when a filler is treated with a basic surface
treating agent, the isoelectric point moves to the basic side.
Therefore, it is preferable to use a basic surface treating agent
because dispersion of the filler can be improved and the blurred
image can be prevented.
[0177] Suitable surface treating agents include titanate coupling
agents, aluminum coupling agents, zircoaluminate coupling agents,
etc. In addition, fillers treated with Al.sub.2O.sub.3, TiO.sub.2,
ZrO.sub.2, silicones, aluminum stearate or their mixtures can also
be preferably used because dispersion of the fillers can be
improved and the blurred image can be prevented.
[0178] When a filler treated with a silane coupling agent is used,
the blurred image problem tends to occur. However, by treating a
filler with a combination of one or more of the above-mentioned
treating agents with a silane coupling agent, there is a
possibility that the blurred image problem is not caused. Fillers
having a pH less than 5 can be used by being treated with one or
more of the basic treating agents mentioned above.
[0179] The weight ratio (ST/F) of the surface treating agent (ST)
to the filler (F) to be coated is from 2 to 30%, and preferable 3
to 20% although the preferable ratio changes depending on the
average primary particle diameter of the filler. When the amount of
the treating agent is too small, dispersibility of the filler
cannot be improved. To the contrary, when the amount of the
treating agent is too large, residual potential of the resultant
photoreceptor tends to increase.
[0180] The average primary particle diameter of the filler included
in the outermost layer is preferably from 0.01 to 0.9 .mu.m, and
more preferably from 0.1 to 0.5 .mu.m in view of light
transmittance and abrasion resistance of the resultant outermost
layer. When the average primary particle diameter is too small, the
filler tends to agglomerate and therefore abrasion resistance
deteriorates. To the contrary, when the average primary particle
diameter is too large, various problems occurs such that the filler
tends to precipitate in the coating liquid, image qualities
deteriorate and undesired images are produced.
[0181] The content of the filler in a layer is preferably from 0.1
to 50% by weight, and more preferably from 5 to 30% by weight. When
the content is too low, the abrasion resistance is hardly
improved.
[0182] When the content is too high, problems occur such that
residual potential increases, the blurred image problem occurs, and
resolution of the resultant images deteriorates. In addition, since
the interaction between filler particles increases, dispersion of
the filler deteriorates, and thereby the filler tends to be
released from the layer, resulting in deterioration of the abrasion
resistance.
[0183] When one or more of these fillers are included in the
outermost layer, the resultant photoreceptor has good durability
but the residual potential of the photoreceptor increases. In order
to decrease the residual potential, an organic compound having an
acid value of from 10 to 700 mgKOH/g is added to the outermost
layer. The acid value is defined as the amount in units of
milligrams of potassium hydroxide needed to neutralize carboxyl
groups included in a compound of 1 gram. When such an organic
compound is used, the organic compound may be a solid or a liquid
in which the organic compound is dissolved in an organic solvent,
etc.
[0184] Suitable compounds for use as the compound having an acid
value of from 10 to 700 mgKOH/g include known organic fatty acids,
resins and copolymers having a high acid value, etc., but are not
limited thereto.
[0185] Specific examples of such compounds include saturated or
unsaturated fatty acids and aromatic carboxylic acids such as
lauric acid, stearic acid, arachidic acid, behenic acid, adipic
acid, oleic acid, maleic acid, maleic anhydride, salicylic acid,
phthalic acid, isophthalic acid, terephthalic acid; pyromellitic
acid; and other carboxylic acids. However, when these compounds are
used, there is occasionally a case that dispersion of the filler
becomes unstable, and the resultant images is slightly blurred.
[0186] Polymers, copolymers and oligomers, which have a saturated
or unsaturated hydrocarbon skeleton and which have also at least
one carboxyl group, can be preferably used as such an organic
compound because not only increase of residual potential can be
prevented but dispersion of the filler can be improved.
[0187] Specific examples of such polymers, copolymers and oligomers
include saturated polyester, unsaturated polyester, unsaturated
polyester having a carboxyl group on its end portion; polymers,
copolymers and oligomers of acrylic acid, methacrylic acid,
acrylate and methacrylate; styrene-acrylic acid copolymers,
styrene-acrylic acid-acrylate copolymers, styrene-methacrylic acid
copolymers, styrene-methacrylic acid-acrylate copolymers,
styrene-maleic acid copolymers, styrene-maleic anhydride
copolymers, etc.
[0188] In order to decrease the residual potential of the resultant
photoreceptor and to improve the dispersion and stability of the
filler used, organic compounds, in particular wetting dispersants,
which have a hydrophobic group such as hydrocarbon groups and a
hydrophilic group such as a carboxyl group and which have an acid
value of from 10 to 700 mgKOH/g are preferably used. The reason why
the increase of the residual potential can be prevented is
considered to be that the compounds have a proper acid value and
are easily adsorbed on the filler used.
[0189] When a filler is added to an outermost layer, the polar
groups present on the surface of the filler serve as charge trap
sites, resulting in increase of the residual potential of the
resultant photoreceptor. When such a wetting dispersant as
mentioned above is added thereto, the hydrophilic group (such as a
carboxyl group) of the wetting dispersant tends to be adsorbed on
the polar groups of the filler, resulting in decrease of the
residual potential.
[0190] On the other hand, in order to improve dispersion of a
filler in a layer including a binder resin, the affinity of the
filler to the binder resin should be heightened to wet the filler
with the binder resin. In addition, interaction between the filler
particles should be decreased to improve the stability of the
filler.
[0191] The wetting dispersants having the above-mentioned
structure, i.e., a structure like a surfactant, which includes both
a hydrophobic group and a hydrophilic group therein, are used, the
hydrophilic group is adsorbed on the polar groups, which serve as
trap sites, while the hydrophobic group has an affinity to the
binder resin. Thus, the wettability of the filler can be improved.
In addition, the molecules adsorbed on the filler cause electric
repulsion and steric hindrance, resulting in prevention of contact
of the filler particles, and thereby the dispersion stability of
the filler can be improved.
[0192] Thus, wetting dispersants, which are defined to have both a
wetting ability of improving the wettability of a filler and a
dispersing ability of improving the dispersion stability of the
filler, can be preferably used to impart both wettability and
dispersion stability to the filler. When one of the wetting ability
and dispersing ability is lacked, problems occur such that
dispersion is not satisfactory, dispersion efficiency is not
satisfactory and/or dispersion stability is not satisfactory.
[0193] These wetting dispersants have good ability to be adsorbed
on a filler and a structure which can produce good steric hindrance
effect, and therefore the filler used can be imparted with good
dispersion stability. Therefore, such wetting dispersants are
preferably used.
[0194] As the hydrophilic group, --SO.sub.3Na, --COOK, --COONa,
--COO--, --COOH, --OH, --O--, --CH.sub.2CH.sub.2O--, a quaternary
ammonium salt group, etc. can be exemplified. In the present
invention, when the hydrophilic group is a carboxyl group (i.e.,
--COOH), the wetting dispersant effectively imparts high
dispersibility to the filler while not affecting the electrostatic
properties of the resultant photoreceptor and the image qualities
of images produced by the photoreceptor. Therefore wetting
dispersants having a carboxyl group can be preferably used. The
desired effect of the hydrophilic group such as a carboxyl group
can be exerted even when one hydrophilic group is included in an
organic molecular structure including a hydrophobic group such as
hydrocarbon groups. However, when a polycarboxylic acid which has a
number of carboxyl groups therein is used, the anionic property of
the compound increases, and thereby the dispersion stability of the
filler can be further improved and in addition, dispersion
efficiency can be dramatically improved.
[0195] In addition, when a polycarboxylic acid is used,
precipitation of the filler used can be prevented because the
carboxyl groups in the polycarboxylic acid have an affinity to each
other. Further, when a hydrophilic group such as a carboxyl group
is located at the end position of the molecule of a wetting
dispersant, the dispersant is easily adsorbed on the filler used.
Therefore such wetting dispersants are preferably used in the
present invention. In addition, addition of a wetting dispersant
having a hydrophilic group at the end position thereof has an
effect on prevention of precipitation of the filler used. Specific
examples of such polycarboxylic type wetting dispersants include
BYK-P104 manufactured by BYK CHEMIE Co., etc.
[0196] In addition, to allow a wetting dispersant to be effectively
adsorbed on a filler improves dispersion of the filler and
decreases residual potential, and in addition improves the abrasion
resistance of the resultant outermost layer. The reason is
considered to be as follows.
[0197] In general, since a filler has a poor affinity to a binder
resin, i.e., the adhesion of the filler to the binder resin is
poor, the filler tends to be easily released from the binder resin.
By adding one or more of the wetting dispersants mentioned above,
the affinity of the filler to the binder resin can be enhanced,
resulting in prevention of releasing of the filler from the binder
resin, and thereby the abrasion resistance of the resultant layer
can be improved.
[0198] The molecular weight of the organic compound having an acid
value of from 10 to 700 mgKOH/g, such as the wetting dispersants
mentioned above, for use in the present invention is preferably
from 300 to 30,000, and more preferably from 400 to 10,000 in
number average molecular weight. Namely, polymers and oligomers are
preferably used. When the molecular weight is too low, desired
steric hindrance cannot be produced when the dispersant is adsorbed
on a filler, resulting in increase of interaction between filler
particles, and thereby the dispersion and dispersion stability of
the filler are deteriorated. To the contrary, when the molecular
weight is too high, wettability and an ability to be adsorbed on a
filler deteriorate. In addition, plural filler particles are
adsorbed on a wetting dispersant polymer, resulting in
agglomeration of the filler particles.
[0199] The acid value of the organic compound for use in the
present invention is preferably from 10 to 700 mgKOH/g, and more
preferably from 30 to 400 mgKOH/g. When the acid value is too high,
the resistance of the filler tends to be excessively decreased,
resulting in occurrence of the blurred image problem. To the
contrary, when the acid value is too low, the addition quantity has
to be increased, and in addition increase of residual potential
cannot be fully prevented. It is preferable that the addition
quantity of the organic compound should be determined while
considering the acid value of the organic compound. However, when
organic compounds having different acid values in the range of from
10 to 700 mgKOH/g are used while the content of each organic
compounds is constant, the residual potential decreasing effect
does not necessarily depend on the acid value thereof. This is
because the residual potential decreasing effect also depends on
the ability of the compound to be absorbed on the filler.
[0200] The content of the organic compound having an acid value of
from 10 to 700 mgKOH/g in the outermost layer is preferably
determined so as to satisfy the following relationship:
0.1.ltoreq.(A.times.B/C).ltoreq.20,
[0201] more preferably, the following relationship:
0.8.ltoreq.(A.times.B/C).ltoreq.15,
[0202] and even more preferably, the following relationship:
1.5.ltoreq.(A.times.B/C).ltoreq.8,
[0203] wherein A represents the content of the organic compound in
units of grams, B represents the acid value of the organic compound
in units of mgKOH/g, and C represents the content of the filler
used in units of grams.
[0204] However, the organic compound should be added in a minimum
amount such that the desired effects can be exerted.
[0205] When the content is too high, problems tend to occur such
that dispersion of the filler used deteriorates and the blurred
image problem occurs. When the content is too low, dispersion of
the filler used and decrease of residual potential cannot be
sufficiently improved.
[0206] As the binder resin for use in the protective layer 39,
binder resins mentioned above for use in the CTL 37 can be used.
Since dispersion of the filler used is influenced by the specie of
the binder resin used, it is preferable to use a binder resin which
does not adversely affect the dispersion of the filler used. When a
filler having a basic isoelectric point is used, an acidic binder
resin is preferably used to improve the dispersion of the filler.
To the contrary, when a filler having an acidic isoelectric point
is used, a basic binder resin is preferably used to improve the
dispersion of the filler.
[0207] Even when the same filler is used in the outermost layer,
the abrasion resistance of the layer changes depending on the
binder resin used. Thus, binder resins largely influence filler
dispersion of the resultant layer, residual potential and abrasion
resistance of the resultant photoreceptor, and resolution of images
produced by the resultant photoreceptor.
[0208] Specific examples of the binder resin for use in the
protective layer include polymers and copolymers such as polyester,
polycarbonate, acrylic resins, polyethyleneterephthalate,
polybutyleneterephthalate, acrylic and methacrylic copolymers,
styrene-acrylic copolymers, polyarylate, polyacrylate, polystyrene,
epoxy resins, ABS resins, ACS resins, olefin-vinyl monomer
copolymers, chlorinated polyether, aryl resins, phenolic resins,
polyacetal, polyamide, polyamideimide, polyallysulfone,
polybutylene, polyethersulfone, polyethylene, polyimide,
polymethylpentene, polypropylene, polyphenyleneoxide, polysulfone,
AS resins, butadiene-styrene copolymers, polyurethane, polyvinyl
chloride, polyvinylidene chloride, etc. In addition, thermosetting
resins and photo-crosslinking resins can also be used. Among these
resins, polycarbonate resins and polyarylate are preferably used.
Further, charge transport polymers can be preferably used as the
binder resin to prepare a photoreceptor which has good durability
and which can produce high quality images. The charge transport
polymer will be explained later.
[0209] It is preferable to include a CTM in the protective layer 39
to improve the charge injection property and charge transport
property of the layer and to prevent increase of residual potential
and deterioration of photosensitivity of the resultant
photoreceptor.
[0210] Specific examples of the CTM for use in the protective layer
39 include CTMs mentioned above for use in the CTL 37. In this
case, it is preferable that the ionization potential of the CTM
used in the protective layer 39 is equal to or less than the
ionization potential of the CTM included in the photosensitive
layer (or CTL) because the charge injection property of the
protective layer can be improved and increase of residual potential
and deterioration of photosensitivity can be prevented. Ionization
potential of a CTM can be measured by a spectrographic method, an
electrochemical method, or the like method.
[0211] The protective layer preferably includes a charge transport
polymer, which has both a binder resin function and a charge
transport function, because the resultant protective layer has good
abrasion resistance and the resultant photoreceptor can produce
high quality image. A charge transport polymer can be used alone as
the binder resin. In addition, a charge transport polymer can be
used in combination with one or more of the binder resins mentioned
above and/or one or more of the low molecular weight CTMs mentioned
above.
[0212] Suitable charge transport polymers include known charge
transport polymer materials. Among these materials, polycarbonate
resins having a triarylamine group in their main chain and/or side
chain are preferably used. In particular, charge transport polymers
having the following formulae of from (1) to (10) are preferably
used: 1
[0213] wherein R.sub.1, R.sub.2 and R.sub.3 independently represent
a substituted or unsubstituted alkyl group, or a halogen atom;
R.sub.4 represents a hydrogen atom, or a substituted or
unsubstituted alkyl group; R.sub.5, and R.sub.6 independently
represent a substituted or unsubstituted aryl group; r, p and q
independently represent 0 or an integer of from 1 to 4; k is a
number of from 0.1 to 1.0 and j is a number of from 0 to 0.9; n is
an integer of from 5 to 5000; and X represents a divalent aliphatic
group, a divalent alicyclic group or a divalent group having the
following formula: 2
[0214] wherein R.sub.101 and R.sub.102 independently represent a
substituted or unsubstituted alkyl group, a substituted or
unsubstituted aryl group, or a halogen atom; t and m represent 0 or
an integer of from 1 to 4; v is 0 or 1; and Y represents a linear
alkylene group, a branched alkylene group, a cyclic alkylene group,
--O--, --S--, --SO--, --SO.sub.2--, --CO--, --CO--O-Z-O--CO-- (Z
represents a divalent aliphatic group), or a group having the
following formula: 3
[0215] wherein a is an integer of from 1 to 20; b is an integer of
from 1 to 2000; and R.sub.103 and R.sub.104 independently represent
a substituted or unsubstituted alkyl group, or a substituted or
unsubstituted aryl group, wherein R.sub.101, R.sub.102, R.sub.103
and R.sub.104 may be the same or different from the others. 4
[0216] wherein R.sub.7 and R.sub.8 independently represent a
substituted or unsubstituted aryl group; Ar.sub.1, Ar.sub.2 and
Ar.sub.3 independently represent an arylene group; and X, k, j and
n are defined above in formula (1). 5
[0217] wherein R.sub.9 and R.sub.10 independently represent a
substituted or unsubstituted aryl group; Ar.sub.4, Ar.sub.5 and
Ar.sub.6 independently represent an arylene group; and X, k, j and
n are defined above in formula (1). 6
[0218] wherein R.sub.11 and R.sub.12 independently represent a
substituted or unsubstituted aryl group; Ar.sub.7, Ar.sub.8 and
Ar.sub.9 independently represent an arylene group; p is an integer
of from 1 to 5; and X, k, j and n are defined above in formula (1).
7
[0219] wherein R.sub.13 and R.sub.14 independently represent a
substituted or unsubstituted aryl group; Ar.sub.10, Ar.sub.11 and
Ar.sub.12 independently represent an arylene group; X.sub.1 and
X.sub.2 independently represent a substituted or unsubstituted
ethylene group, or a substituted or unsubstituted vinylene group;
and X, k, j and n are defined above in formula (1). 8
[0220] wherein R.sub.15, R.sub.16, R.sub.17 and R.sub.18
independently represent a substituted or unsubstituted aryl group;
Ar.sub.13, Ar.sub.14, Ar.sub.15 and Ar.sub.16 independently
represent an arylene group; Y.sub.1, Y.sub.2 and Y.sub.3
independently represent a substituted or unsubstituted alkylene
group, a substituted or unsubstituted cycloalkylene group, a
substituted or unsubstituted alkyleneether group, an oxygen atom, a
sulfur atom, or a vinylene group; u, v and w independently
represent 0 or 1; and X, k, j and n are defined above in formula
(1). 9
[0221] wherein R.sub.19 and R.sub.20 independently represent a
hydrogen atom, or substituted or unsubstituted aryl group, and
R.sub.19 and R.sub.20 optionally share bond connectivity to form a
ring; Ar.sub.17, Ar.sub.18 and Ar.sub.19 independently represent an
arylene group; and X, k, j and n are defined above in formula (1).
10
[0222] wherein R.sub.21 represents a substituted or unsubstituted
aryl group; Ar.sub.20, Ar.sub.21, Ar.sub.22 and Ar.sub.23
independently represent an arylene group; and X, k, j and n are
defined above in formula (1). 11
[0223] wherein R.sub.22, R.sub.23, R.sub.24 and R.sub.25
independently represent a substituted or unsubstituted aryl group;
Ar.sub.24, Ar.sub.25, Ar.sub.26, Ar.sub.27 and Ar.sub.28
independently represent an arylene group; and X, k, j and n are
defined above in formula (1). 12
[0224] wherein R.sub.26 and R.sub.27 independently represent a
substituted or unsubstituted aryl group; Ar.sub.29, Ar.sub.30 and
Ar.sub.31 independently represent an arylene group; and X, k, j and
n are defined above in formula (1).
[0225] Specific compounds of the polycarbonate having a
triarylamine group in their main chain and/or side chain are as
follows but are not limited thereto: 131415161718192021
[0226] These charge transport polymers having a triarylamine group
in their main chain and/or side chain include homopolymers, random
copolymers, alternating copolymers, and block copolymers. Since
these charge transport polymers are used as a binder resin, the
polymers are needed to have a film formability. Therefore, the
polystyrene-conversion weight average molecular weight thereof,
which can be measured by a gel permeation chromatography method, is
preferably from 10,000 to 500,000, and more preferably from 50,000
to 400,000.
[0227] These charge transport polymers have been disclosed in JOPs
8-269183, 9-71642, 9-104746, 9-272735, 11-29634, 9-235367, 9-87376,
9-110976, 9-268226, 9-221544, 9-227669, 9-157378, 9-302084,
9-302085, and 2000-26590.
[0228] The thickness of the protective layer is preferably 0.1 to
10 .mu.m, and more preferably from 2 to 6 .mu.m. When the thickness
is too thin, satisfactory durability cannot be necessarily
obtained. When the thickness is too thick, there is a case in which
the residual potential increases and/or the resolution of the
produced images deteriorates.
[0229] The protective layer 39 may include one or more additives
such as plasticizers, leveling agents, lubricants, etc.
[0230] The outermost layer of the photoreceptor of the present
invention preferably includes an antioxidant. Suitable antioxidants
for use in the outermost layer include known antioxidants,
ultraviolet absorbents and photo-stabilizers, such as phenol
compounds, hindered phenol compounds, hindered amine compounds,
paraphenylenediamine compounds, hydroquinone compounds,
sulfur-containing organic compounds, phosphorus-containing organic
compounds, benzophenone compounds, salicylate compounds,
benzotriazole compounds, quenchers (metal complexes), etc.
[0231] Among these antioxidants, compounds having both a hindered
phenol structure and a hindered amine structure are preferably used
to prevent the resultant photoreceptor from being deteriorated by
an active gas such as ozone and NOx and to stably produce good
images.
[0232] The hindered phenol structure is defined as a structure in
which a bulky atomic group is present on both ortho positions of
the hydroxyl group of phenol. The hindered amine structure is
defined as a structure in which a bulky atomic group is present
near the nitrogen atom of an amine. Aromatic amines and aliphatic
amines are included in hindered amines. In the present invention
hindered amines including a 2,2,6,6-tetramethylpiperidine structure
are more preferably used.
[0233] The reason why these compounds prevent the resultant
photoreceptor from being deteriorated by an active gas is not
clear, but is considered to be as follows. Since a bulky atomic
group is present, steric hindrance is produced and thereby the heat
vibration of the nitrogen atom of the amine structure or the
hydroxyl group of the phenol structure can be prevented and the
radical state of the compound can be stabilized. Therefore the
influence of the active gases can be prevented.
[0234] In the present invention, known compounds having both a
hindered phenol structure and a hindered amine structure can be
used. Among such compounds,
1-[2-{3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy}ethyl]-4--
{3-(3,5-di-t-butyl-4-hydroxylphenyl)propionyloxy}-2,2,6,6-tetramethylpyrid-
ine, whose formula is shown below as a formula (11), is preferably
used because of being useful for preventing deterioration of
resolution due to ozone and NOx gases. 22
[0235] When a filler is included in an outermost layer of a
photoreceptor, active gasses such as ozone and NOx gases tend to be
adsorbed on the filler and therefore the blurred image problem
occurs more frequently than in the case of a photoreceptor having
an outermost layer including no filler. By including such a
compound having the above-mentioned formula in the outermost layer,
the blurred image problem can be prevented. Namely, by using such a
compound together with a filler, image qualities can be further
improved.
[0236] The content of the compound having both a hindered phenol
structure and a hindered amine structure is preferably from 0.1 to
20% by weight, and more preferably from 1 to 15% by weight, based
on the weight of the filler used. When the content is too low, the
effect on preventing the blurred image problem due to active gasses
such as ozone and NOx gasses is decreased when the photoreceptor is
repeatedly used. To the contrary, when the content is too high,
problems such that abrasion resistance deteriorates and residual
potential increases tend to occur.
[0237] In the outermost layer of the photoreceptor of the present
invention, the content of the compound having both a hindered
phenol structure and a hindered amine structure is preferably not
less than the organic compound having an acid value of from 10 to
700 mgKOH/g to enhance the effect to prevent the blurred image
problem due to active gasses and products generated due to corona
discharging.
[0238] When the coating liquid for the outermost layer is prepared,
a filler is preferably dispersed in an organic solvent together
with an organic compound having an acid value of from 10 to 700
mgKOH/g using a dispersion device such as ball mills, attritors,
sand mills, shakers or supersonic dispersion machines. Among these
dispersion devices, ball mills are preferable because the filler is
effectively contacted with the organic compound having the specific
acid value and impurities are hardl mixed from outside.
[0239] Suitable organic solvents for use in the outermost layer
coating liquid include tetrahydrofuran, dioxane, toluene,
dichloromethane, monochlorobenzene, dichloroethane, cyclohexanone,
methyl ethyl ketone, acetone, etc. A solvent having high viscosity
is preferable when a coating liquid is prepared, and a volatile
solvent is preferable in view of drying. Therefore it is preferable
to select a solvent fulfilling such requirements. It is preferable
to use a mixture solvent if there is no solvent fulfilling such
requirements. This method is useful for improving the dispersion
and dispersion stability of the filler used and the film qualities
of the resultant layer.
[0240] Suitable dispersing elements include known media such as
zirconia, alumina, agate, glass, etc. Among these media, alumina is
preferable in view of dispersion efficiency and residual potential
decreasing effect. When zirconia is used as a dispersing element,
zirconia is abraded during the dispersion process, resulting in
contamination of zirconia in the coating liquid, and thereby
residual potential of the resultant photoreceptor tends to increase
and the filler tends to easily precipitate in the resultant coating
liquid.
[0241] When alumina is used as a dispersing element, the abrasion
amount of alumina is much less than zirconia, and therefore the
influence on residual potential is very little. Therefore alumina
is preferable as the dispersing element. In addition, it is
preferable to use alumina as a filler when alumina balls are used
as the dispersing element.
[0242] It is preferable to disperse a filler and an organic
compound having an acid value of from 10 to 700 mgKOH/g in an
organic solvent before mixing a binder resin to prevent
agglomeration and precipitation of the filler, i.e., to improve
dispersion of the filler. A binder resin, a CTM and an antioxidant
may be added in the mixture of the filler, organic compound and
solvent before the dispersion process, however dispersion of the
filler often deteriorates slightly. Therefore, it is preferable
that a solution in which the binder resin, CTM and antioxidant are
dissolved in an organic solvent is added to the dispersion of the
filler, organic compound and solvent.
[0243] The thus prepared outermost layer coating liquid can be
coated by a coating liquid such as dip coating methods, spray
coating methods, bead coating methods, nozzle coating methods,
spinner coating methods and ring coating methods. Among these
coating methods, dip coating methods, ring coating methods and
spray coating methods are preferably used for coating the
photosensitive layer or CTL, which is the outermost layer and
includes a filler, as shown in FIGS. 1 and 2. When a filler is
included such a photosensitive layer or CTL, the concentration of
the filler may change by gradation such that the concentration in
the surface portion is higher than that in the bottom portion of
the layer. Alternatively, the photosensitive or CTL may include
plural layers such that the concentration of the filler in a layer
is heightened by gradation in the upward (surface) direction.
[0244] On the other hand, when forming the protective layer, which
is the outermost layer and includes a filler, as shown in FIGS. 3
to 5, spray coating methods are preferably used. This is because
the layer thickness can be easily controlled, dispersion of the
filler in the resultant layer is good, and coating properties are
good. The protective layer may be formed by performing the coating
operation once, however it is preferable to perform the coating
operation plural times to form a protective layer in which a filler
is uniformly dispersed, resulting in decrease of residual
potential, and improvement of resolution of the resultant images
and abrasion resistance of the resultant protective layer. In
addition, coating properties can be improved, i.e., occurrence of
coating defects can be prevented.
[0245] In the photoreceptor of the present invention, an undercoat
layer may be formed between the substrate 31 and the photosensitive
layer (i.e., the photosensitive layer 33 in FIGS. 1 and 3, the CGL
35 in FIGS. 2 and 4, and the CTL in FIG. 5).
[0246] The undercoat layer typically includes a resin as a main
component. Since a photosensitive layer is typically formed on the
undercoat layer by coating a liquid including an organic solvent,
the resin in the undercoat layer preferably has good resistance to
general organic solvents.
[0247] Specific examples of such resins include water-soluble
resins such as polyvinyl alcohol resins, casein and polyacrylic
acid sodium salts; alcohol soluble resins such as nylon copolymers
and methoxymethylated nylon resins; and thermosetting resins
capable of forming a three-dimensional network such as polyurethane
resins, melamine resins, alkyd-melamine resins, epoxy resins and
the like.
[0248] The undercoat layer may include a fine powder of metal
oxides such as titanium oxide, silica, alumina, zirconium oxide,
tin oxide and indium oxide to prevent occurrence of moir in the
resultant images and to decrease residual potential of the
resultant photoreceptor.
[0249] The undercoat layer can also be formed by coating a coating
liquid using a proper solvent and a proper coating method mentioned
above for use in the photosensitive layer.
[0250] The undercoat layer may be formed using a silane coupling
agent, titanium coupling agent or a chromium coupling agent.
[0251] In addition, a layer of aluminum oxide which is formed by an
anodic oxidation method and a layer of an organic compound such as
polyparaxylylene or an inorganic compound such as SiO, SnO.sub.2,
TiO.sub.2, ITO or CeO.sub.2 which is formed by a vacuum evaporation
method is also preferably used as the undercoat layer.
[0252] The thickness of the undercoat layer is preferably 0 to 5
.mu.m.
[0253] In the photoreceptor of the present invention, an
intermediate layer may be formed between the undercoat layer and
the photosensitive layer, or the photosensitive layer and the
protective layer. The intermediate layer includes a resin as a main
component. Specific examples of the resin include polyamides,
alcohol soluble nylons, water-soluble polyvinyl butyral, polyvinyl
butyral, polyvinyl alcohol, and the like. The intermediate layer
can be formed by one of the above-mentioned known coating methods.
The thickness of the intermediate layer is preferably from 0.05 to
2 .mu.m.
[0254] In the photoreceptor of the present invention, one or more
additives such as antioxidants, plasticizers, lubricants,
ultraviolet absorbents, low molecular weight charge transport
materials and leveling agents can be used in one or more layers of
the CGL, CTL, undercoat layer, protective layer and intermediate
layers to improve the stability to withstand environmental
conditions, namely to avoid decrease of photosensitivity and
increase of residual potential.
[0255] Suitable antioxidants for use in the layers of the
photoreceptor include the following compounds but are not limited
thereto.
[0256] (a) Phenolic Compounds
[0257] 2,6-di-t-butyl-p-cresol, butylated hydroxyanisole,
2,6-di-t-butyl-4-ethylphenol,
n-octadecyl-3-(4'-hydroxy-3',5'-di-t-butylp- henol),
2,2'-methylene-bis-(4-methyl-6-t-butylphenol),
2,2'-methylene-bis-(4-ethyl-6-t-butylphenol),
4,4'-thiobis-(3-methyl-6-t-- butylphenol),
4,4'-butylidenebis-(3-methyl-6-t-butylphenol),
1,1,3-tris-(2-methyl-4-hydroxy-5-t-butylphenyl)butane,
1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene,
tetrakis-[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]metha-
ne, bis[3,3'-bis(4'-hydroxy-3'-t-butylphenyl)butyric acid]glycol
ester, tocophenol compounds, and the like.
[0258] (b) Paraphenylenediamine Compounds
[0259] N-phenyl-N'-isopropyl-p-phenylenediamine,
N,N'-di-sec-butyl-p-pheny- lenediamine,
N-phenyl-N-sec-butyl-p-phenylenediamine,
N,N'-di-isopropyl-p-phenylenediamine,
N,N'-dimethyl-N,N'-di-t-butyl-p-phe- nylenediamine, and the
like.
[0260] (c) Hydroquinone Compounds
[0261] 2,5-di-t-octylhydroquinone, 2,6-didodecylhydroquinone,
2-dodecylhydroquinone, 2-dodecyl-5-chlorohydroquinone,
2-t-octyl-5-methylhydroquinone,
2-(2-octadecenyl)-5-methylhydroquinone and the like.
[0262] (d) Organic Sulfur-Containing Compounds
[0263] dilauryl-3,3'-thiodipropionate,
distearyl-3,3'-thiodipropionate,
ditetradecyl-3,3'-thiodipropionate, and the like.
[0264] (e) Organic Phosphorus-Containing Compounds
[0265] triphenylphosphine, tri(nonylphenyl)phosphine,
tri(dinonylphenyl)phosphine, tricresylphosphine,
tri(2,4-dibutylphenoxy)p- hosphine and the like.
[0266] Suitable plasticizers for use in the layers of the
photoreceptor include the following compounds but are not limited
thereto:
[0267] (a) Phosphoric Acid Esters
[0268] triphenyl phosphate, tricresyl phosphate, trioctyl
phosphate, octyldiphenyl phosphate, trichloroethyl phosphate,
cresyldiphenyl phosphate, tributyl phosphate, tri-2-ethylhexyl
phosphate, triphenyl phosphate, and the like.
[0269] (b) Phthalic Acid Esters
[0270] dimethyl phthalate, diethyl phthalate, diisobutyl phthalate,
dibutyl phthalate, diheptyl phthalate, di-2-ethylhexyl phthalate,
diisooctyl phthalate, di-n-octyl phthalate, dinonylphthalate,
diisononylphthalate, diisodecyl phthalate, diundecyl phthalate,
ditridecyl phthalate, dicyclohexyl phthalate, butylbenzyl
phthalate, butyllauryl phthalate, methyloleyl phthalate, octyldecyl
phthalate, dibutyl fumarate, dioctyl fumarate, and the like.
[0271] (c) Aromatic Carboxylic Acid Esters
[0272] trioctyl trimellitate, tri-n-octyl trimellitate, octyl
oxybenzoate, and the like.
[0273] (d) Dibasic Fatty Acid Esters
[0274] dibutyl adipate, di-n-hexyl adipate, di-2-ethylhexyl
adipate, di-n-octyl adipate, n-octyl-n-decyl adipate, diisodecyl
adipate, dialkyl adipate, dicapryl adipate, di-2-etylhexyl azelate,
dimethyl sebacate, diethyl sebacate, dibutyl sebacate, di-n-octyl
sebacate, di-2-ethylhexyl sebacate, di-2-ethoxyethyl sebacate,
dioctyl succinate, diisodecyl succinate, dioctyl
tetrahydrophthalate, di-n-octyl tetrahydrophthalate, and the
like.
[0275] (e) Fatty Acid Ester Derivatives
[0276] butyl oleate, glycerin monooleate, methyl acetylricinolate,
pentaerythritol esters, dipentaerythritol hexaesters, triacetin,
tributyrin, and the like.
[0277] (f) Oxyacid Esters
[0278] methyl acetylricinolate, butyl acetylricinolate,
butylphthalylbutyl glycolate, tributyl acetylcitrate, and the
like.
[0279] (g) Epoxy Compounds
[0280] epoxydized soybean oil, epoxydized linseed oil, butyl
epoxystearate, decyl epoxystearate, octyl epoxystearate, benzyl
epoxystearate, dioctyl epoxyhexahydrophthalate, didecyl
epoxyhexahydrophthalate, and the like.
[0281] (h) Dihydric Alcohol Esters
[0282] diethylene glycol dibenzoate, triethylene glycol
di-2-ethylbutyrate, and the like.
[0283] (i) Chlorine-Containing Compounds
[0284] chlorinated paraffin, chlorinated diphenyl, methyl esters of
chlorinated fatty acids, methyl esters of methoxychlorinated fatty
acids, and the like.
[0285] (j) Polyester Compounds
[0286] polypropylene adipate, polypropylene sebacate, acetylated
polyesters, and the like.
[0287] (k) Sulfonic Acid Derivatives
[0288] p-toluene sulfonamide, o-toluene sulfonamide, p-toluene
sulfoneethylamide, o-toluene sulfoneethylamide, toluene
sulfone-N-ethylamide, p-toluene sulfone-N-cyclohexylamide, and the
like.
[0289] (l) Citric Acid Derivatives
[0290] triethyl citrate, triethyl acetylcitrate, tributyl citrate,
tributyl acetylcitrate, tri-2-ethylhexyl acetylcitrate,
n-octyldecyl acetylcitrate, and the like.
[0291] (m) Other Compounds
[0292] terphenyl, partially hydrated terphenyl, camphor, 2-nitro
diphenyl, dinonyl naphthalene, methyl abietate, and the like.
[0293] Suitable lubricants for use in the layers of the
photoreceptor include the following compounds but are not limited
thereto.
[0294] (a) Hydrocarbons
[0295] liquid paraffins, paraffin waxes, micro waxes, low molecular
weight polyethylenes, and the like.
[0296] (b) Fatty Acids
[0297] lauric acid, myristic acid, palmitic acid, stearic acid,
arachidic acid, behenic acid, and the like.
[0298] (c) Fatty Acid Amides
[0299] Stearic acid amide, palmitic acid amide, oleic acid amide,
methylenebisstearamide, ethylenebisstearamide, and the like.
[0300] (d) Ester Compounds
[0301] lower alcohol esters of fatty acids, polyhydric alcohol
esters of fatty acids, polyglycol esters of fatty acids, and the
like.
[0302] (e) Alcohols
[0303] cetyl alcohol, stearyl alcohol, ethylene glycol,
polyethylene glycol, polyglycerol, and the like.
[0304] (f) Metallic Soaps
[0305] lead stearate, cadmium stearate, barium stearate, calcium
stearate, zinc stearate, magnesium stearate, and the like.
[0306] (g) Natural Waxes
[0307] Carnauba wax, candelilla wax, beeswax, spermaceti, insect
wax, montan wax, and the like.
[0308] (h) Other Compounds
[0309] silicone compounds, fluorine compounds, and the like.
[0310] Suitable ultraviolet absorbing agents for use in the layers
of the photoreceptor include the following compounds but are not
limited thereto.
[0311] (a) Benzophenone Compounds
[0312] 2-hydroxybenzophenone, 2,4-dihydroxybenzophenone,
2,2',4-trihydroxybenzophenone, 2,2',4,4'-tetrahydroxybenzophenone,
2,2'-dihydroxy-4-methoxybenzophenone, and the like.
[0313] (b) Salicylate Compounds
[0314] phenyl salicylate,
2,4-di-t-butylphenyl-3,5-di-t-butyl-4-hydroxyben- zoate, and the
like.
[0315] (c) Benzotriazole Compounds
[0316] (2'-hydroxyphenyl)benzotriazole,
(2'-hydroxy-5'-methylphenyl)benzot- riazole,
(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole, and
the like.
[0317] (d) Cyano Acrylate Compounds
[0318] ethyl-2-cyano-3,3-diphenyl acrylate,
methyl-2-carbomethoxy-3-(param- ethoxy) acrylate, and the like.
[0319] (e) Quenchers (Metal Complexes)
[0320] nickel(2,2'-thiobis(4-t-octyl)phenolate)-n-butylamine,
nickeldibutyldithiocarbamate, cobaltdicyclohexyldithiophosphate,
and the like.
[0321] (f) HALS (Hindered Amines)
[0322] bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate,
bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate,
1-[2-{3-(3,5-di-t-butyl-4-
-hydroxyphenyl)propionyloxy}ethyl]-4-{3-(3,5-di-t-butyl-4-hydroxyphenyl)pr-
opionyloxy}-2,2,6,6-tetrametylpyridine,
8-benzyl-7,7,9,9-tetramethyl-3-oct-
yl-1,3,8-triazaspiro[4,5]undecane-2,4-dione,
4-benzoyloxy-2,2,6,6-tetramet- hylpiperidine, and the like.
[0323] Hereinafter the image forming method and image forming
apparatus of the present invention will be explained referring to
drawings.
[0324] FIG. 6 is a schematic view for explaining an embodiment of
the image forming method and apparatus of the present
invention.
[0325] In FIG. 6, numeral 1 denotes a photoreceptor. The
photoreceptor 1 is the photoreceptor of the present invention which
includes at least a photosensitive layer located on an
electroconductive substrate, wherein the outermost layer includes a
filler, a binder resin and an organic compound having an acid value
of from 10 to 700 mgKOH/g.
[0326] Around the photoreceptor 1, a discharging lamp 2, a charger
3 configured to charge the photoreceptor 1, an imagewise light
irradiator 5 configured to irradiate the photoreceptor 1 with
imagewise light to form an electrostatic latent image on the
photoreceptor 1, an image developer 6 configured to develop the
latent image with a toner to form a toner image on the
photoreceptor 1, a cleaning unit including a cleaning brush 14 and
a cleaning blade 15 configured to clean the surface of the
photoreceptor 1 are arranged while contacting or being set closely
to the photoreceptor 1. In addition, a lubricant applicator 50
configured to apply a lubricant such as zinc stearate and
fluorine-containing compounds, e.g., polytetrafluoroethylene, to
the surface of the photoreceptor 1 may be provided. The toner image
formed on the photoreceptor 1 is transferred on a receiving paper 9
fed by a pair of registration rollers 8 at the transfer device
(i.e., a pair of a transfer charger 10 and a separating charger
11). The receiving paper 9 having the toner image thereon is
separated from the photoreceptor 1 by a separating pick 12.
[0327] In the image forming apparatus of the present invention, a
pre-transfer charger 7 and a pre-cleaning charger 13 may be
arranged if desired.
[0328] Although the photoreceptor 1 has a cylindrical shape, but
sheet photoreceptors or endless belt photoreceptors can be
used.
[0329] As the charger 3, the pre-transfer charger 7, the transfer
charger 10, the separating charger 11 and the pre-cleaning charger
13, all known chargers such as corotrons, scorotrons, solid state
chargers, roller chargers and brush chargers can be used.
[0330] As the charging devices, non-contact chargers such as corona
chargers, and contact chargers such as charging rollers and
charging brushes are typically used. In the present invention, both
non-contact and contact chargers can be used. In particular, by
using charging rollers, the amount of generated ozone can be
drastically reduced, and therefore the photoreceptor can be
maintained to be stable and deterioration of image qualities can be
prevented when the photoreceptor is repeatedly used.
[0331] However, when a charging roller is repeatedly used while
contacting a photoreceptor, the charging roller tends to be
contaminated, and thereby the photoreceptor is also contaminated,
resulting in production of undesired images and deterioration of
abrasion resistance of the photoreceptor. In particular, when a
photoreceptor having good abrasion resistance is used, the surface
of the photoreceptor is hardly refaced. Therefore it is needed to
improve the contamination of the charging roller.
[0332] In the present invention, it is preferable to use a
proximity charger in which a charging roller is preferably set
closely to the photoreceptor of the present invention such that
pollutants do not adhere to the charging roller or the pollutants
can be easily removed. In this proximity charger, the gap between
the charging roller and the photoreceptor is preferably not greater
than 80 .mu.m, and preferably not greater than 50 .mu.m.
[0333] However, when this proximity charging roller is used, there
is a case in which charging becomes uneven and therefore the
photoreceptor is unevenly charged. In order to improve this uneven
charging problem, a DC voltage overlapped with an AC voltage is
preferably applied to the charging roller. By using this method,
contamination of the photoreceptor due to ozone, contamination of
the charging roller and uneven charging can be lightened at the
same time. Therefore, by using this method and a photoreceptor
having good abrasion resistance, the durability of the
photoreceptor can be further improved and high quality images can
be produced for a long period of time.
[0334] As the transfer device, the above-mentioned chargers can be
used. Among the chargers, a combination of the transfer charger 10
and the separating charger 11 as shown in FIG. 6 is preferably
used. In FIG. 6, a toner image formed on the photoreceptor 1 is
directly transferred onto the receving paper 9. However, it is
preferable to transfer a toner image on the photoreceptor 1 onto an
intermediate transfer medium and then retransfer the toner image
onto a paper to improve the durability of the photoreceptor and
produce high quality images.
[0335] Since the photoreceptor of the present invention has good
abrasion resistance, i.e., the photoreceptor is hardly refaced, the
pollutants adhered on the surface of the photoreceptor is hardly
removed. Among the pollutants adhered on the surface of the
photoreceptor, pollutants such as materials generated by charging
and external additives included in the toner used cause undesired
images particularly under high humidity conditions. In addition,
paper dust is also a pollutant, and not only causes undesired
images but deteriorates abrasion resistance and unevenly abrades
the photoreceptor. Therefore, the non-contact charging method
mentioned above in which the photoreceptor does not directly
contact a paper is preferable to produce high quality images.
[0336] In addition, the image forming method using an intermediate
transfer medium is particularly useful for producing full color
images. Namely, by transferring plural color toner images on an
intermediate transfer medium and then transferring the color toner
images on a receiving paper at the same time on a paper, a high
quality full color image with less positional variation of the
color images. However, this method needs four scanning processes to
form a full color image, and therefore a trouble which occurs is
that conventional photoreceptors have too low durability to be used
for the method.
[0337] The photoreceptor of the present invention not only has high
durability but can produce high quality images without blurring
without using a drum heater. Therefore, the photoreceptor is
preferably used for the image forming apparatus using an
intermediate transfer medium. As the intermediate transfer medium
in the present invention, various known media such as drum transfer
media and belt transfer media can be used.
[0338] Suitable light sources for use in the imagewise light
irradiator 5 and the discharging lamp 2 include fluorescent lamps,
tungsten lamps, halogen lamps, mercury lamps, sodium lamps, light
emitting diodes (LEDs), laser diodes (LDs), light sources using
electroluminescence (EL), and the like. In addition, in order to
obtain light having a desired wave length range, filters such as
sharp-cut filters, band pass filters, near-infrared cutting
filters, dichroic filters, interference filters, color temperature
converting filters and the like can be used.
[0339] The above-mentioned lamps can be used for not only the
processes mentioned above and illustrated in FIG. 6, but also other
processes using light irradiation, such as a transfer process
including light irradiation, a discharging process, a cleaning
process including light irradiation and a pre-exposure process. In
the discharging process, irradiating the photoreceptor with light
tends to fatigue the photoreceptor, resulting in deterioration of
charging properties and increase of residual potential of the
photoreceptor. Therefore, it is preferable to apply an opposite
bias to the photoreceptor in the charging process or cleaning
process to prolong the life of the photoreceptor.
[0340] When the toner image formed on the photoreceptor 1 by the
developing unit 6 is transferred onto the receiving paper 9, all of
the toner image are not transferred on the receiving paper 9, and
residual toner particles remain on the surface of the photoreceptor
1. The residual toner is removed from the photoreceptor 1 by the
fur blush 14 or the cleaning blade 15. The residual toner remaining
on the photoreceptor 1 can be removed by only a cleaning brush.
Suitable cleaning blushes include known cleaning blushes such as
fur blushes and mag-fur blushes.
[0341] When the cleaning process is performed, the surface of the
photoreceptor tends to be acceleratedly abraded or hurt, resulting
in production of undesired images. In addition, when the surface of
the photoreceptor is contaminated due to insufficient cleaning, not
only undesired images are produced but the life of the
photoreceptor is seriously shortened. In particular, in the case of
the photoreceptor having an outermost layer including a filler to
improve the abrasion resistance thereof, the pollutants adhered to
the outermost layer are hardly removed. Therefore, a filming
problem in which a toner film is formed on the surface of the
photoreceptor occurs and production of undesired images is
accelerated. Therefore, to improve the cleaning ability of the
surface of the photoreceptor is very effective for prolonging the
life of the photoreceptor and producing high quality images.
[0342] As the method for improving the cleaning ability of a
photoreceptor, methods in which the friction coefficient of the
surface of the photoreceptor is decreased are known. The friction
coefficient decreasing methods include a method in which a
lubricant is included in the surface of a photoreceptor and a
method in which a lubricant is applied to a photoreceptor from
outside.
[0343] The former method has an advantage in that various devices
can be arranged around a photoreceptor relatively freely. Therefore
this method is advantageously used for small-size photoreceptors.
However, the method has a drawback in that the friction coefficient
increases after long repeated use. To the contrary, in the latter
method, the friction coefficient of the photoreceptor can be stably
maintained although it is needed to provide a lubricant
applicator.
[0344] Another friction coefficient decreasing method is to include
a lubricant in the toner used. The lubricant included in the toner
adheres to the photoreceptor in the developing process. This method
has advantages in that various devices can be arranged around a
photoreceptor relatively freely and the friction coefficient of the
photoreceptor can be stably maintained. Therefore this method is
effective for prolonging the life of the photoreceptor and
producing high quality images.
[0345] Suitable lubricants for use in the present invention include
lubricating liquid such as silicone oils and fluorine-containing
oils; fluorine-containing resins such as polytetrafluoroethylene
(PTFE), perfluoroalkylvinyl ether (PFA) and polyvinylidene fluoride
(PVDF); silicone resins, polyolefin resins, silicone greases,
fluorine-containing greases, paraffin waxes, fatty acid esters,
fatty acid metal salts such as zinc stearate, graphite, molybdenum
disulfide, and the like lubricating liquids, solids and
powders.
[0346] When a lubricant is included in a toner, the lubricant is
needed to be a powder. In this case, zinc stearate is preferably
used because of hardly producing adverse effects. The content of
zinc stearate in a toner is preferably from 0.01 to 0.5% by weight,
and more preferably from 0.1 to 0.3% by weight.
[0347] When the photoreceptor 1 which is previously charged
positively (or negatively) is exposed to imagewise light, an
electrostatic latent image having a positive or negative charge is
formed on the photoreceptor 1. When the latent image having a
positive (or negative) charge is developed with a toner having a
negative (or positive) charge, a positive image can be obtained. In
contrast, when the latent image having a positive (negative) charge
is developed with a toner having a positive (negative) charge, a
negative image (i.e., a reversal image) can be obtained. As the
developing method, known developing methods can be used. In
addition, as the discharging methods, known discharging methods can
also be used.
[0348] The photoreceptor of the present invention has high
durability, and therefore is preferably used for small size
photoreceptors. Namely, the photoreceptor of the present invention
is very useful for so-called tandem-type electrophotographic image
forming apparatus which include plural photoreceptors and
corresponding developing units to form plural color toner images in
parallel.
[0349] Tandem type electrophotographic image forming apparatus
typically include yellow, magenta, cyan and black toners and
corresponding developing units and photoreceptors. Such tandem-type
image forming apparatus have an advantage such that full color
images can be produced at a much higher speed than conventional
full color image forming apparatus.
[0350] FIG. 7 is a schematic view illustrating an embodiment of the
tandem type image forming apparatus of the present invention.
However, the tandem type image forming apparatus of the present
invention is not limited thereto.
[0351] In FIG. 7, the tandem type image forming apparatus has a
cyan image forming unit 76C, a magenta image forming unit 76M, a
yellow image forming unit 76Y and a black image forming unit 76K.
Drum photoreceptors 71C, 71M, 71Y and 71K rotate in the direction
indicated by the respective arrow. Around the photoreceptors 71C,
71M, 71Y and 71K, chargers 72C, 72M, 72Y and 72K, image developers
74C, 74M, 74Y and 74K, and cleaners 75C, 75M, 75Y and 75K are
arranged in this order in the clockwise direction. As the chargers,
the above-mentioned chargers which can uniformly charge the surface
of the photoreceptors are preferably used. Imagewise light
irradiators 73C, 73M, 73Y and 73K irradiate with laser light a
surface point of the respective photoreceptors located between the
chargers and the image developers to form an electrostatic latent
image on the respective photoreceptor. The four image forming units
76C, 76M, 76Y and 76K are arranged along an intermediate transfer
belt 80. The intermediate transfer belt 80 contacts the respective
photoreceptor 71C, 71M, 71Y or 71K at an image transfer point
located between the respective image developer and the respective
cleaner to receive color images formed on the photoreceptors. At
the backside of each image transfer point of the intermediate
transfer belt 80, transfer brushes 81C, 81M, 81Y and 81K are
arranged to apply a transfer bias to the intermediate transfer belt
80.
[0352] The above-mentioned tandem type image forming apparatus can
transfer plural color images at the same time, and therefore full
color images can be produced at a high speed. Since the image
forming apparatus needs at least four photoreceptors, the apparatus
becomes large in size. In addition, the abrasions of the four
photoreceptors tend to be different when the consumption of the
color toners is different, resulting in occurrence of problems such
that color reproducibility deteriorates and undesired images are
produced.
[0353] The photoreceptor of the present invention has good abrasion
resistance. Therefore, when the photoreceptor is used as a small
size photoreceptor, the difference in abrasion amount between the
four photoreceptors can be minimized, and thereby deterioration of
photosensitivity and production of undesired images can be
prevented, resulting in formation of high quality full color
images. In addition, since it is not needed to use a drum heater
for preventing the blurred image problem, the tandem type image
forming apparatus can be minimized. Therefore, the tandem type
image forming apparatus of the present invention can produce full
color images at a high speed while the size of the apparatus is
almost the same as the conventional monochrome image forming
apparatus.
[0354] Namely, by using the photoreceptor of the present invention
for a combination of the above-mentioned tandem type image forming
method and the intermediate transfer method, the life of the
photoreceptor can be further prolonged while high quality full
color images can be produced for a long period of time.
[0355] In FIG. 7, numerals 77, 78 and 79 denote a receiving paper,
a feeding roller configured to feed the receiving paper 77, and a
pair of registration rollers configured to timely feed the
receiving paper to the image transfer points. Numeral 82 denotes a
fixer to fix the full color toner image on the receiving paper.
[0356] FIG. 8 is a schematic view illustrating another embodiment
of the image forming apparatus of the present invention. In this
embodiment, a belt-shaped photoreceptor 21 is used. The
photoreceptor 21 is the photoreceptor of the present invention and
includes at least a photosensitive layer on an electroconductive
substrate, wherein the outermost layer includes at least a filler,
a binder resin and an organic compound having an acid value of from
10 to 700 mgKOH/g.
[0357] The belt-shaped photoreceptor 21 is rotated by rollers 22a
and 22b. The photoreceptor 21 is charged with a charger 23, and
then exposed to imagewise light emitted by an imagewise light
irradiator 24 to form an electrostatic latent image on the
photoreceptor 21. The latent image is developed with a developing
unit 29 to form a toner image on the photoreceptor 21. The toner
image is transferred onto a receiving paper (not shown) using a
transfer charger 25. After the toner image transferring process,
the surface of the photoreceptor 21 is cleaned with a cleaning
brush 27 after performing a pre-cleaning light irradiating
operation using a pre-cleaning light irradiator 26. Then the
photoreceptor 21 is discharged by being exposed to light emitted by
a discharging light source 28. In the pre-cleaning light
irradiating process, light irradiates the photoreceptor 21 from the
side of the substrate thereof. In this case, the substrate has to
be light-transmissive.
[0358] The image forming apparatus of the present invention is not
limited to the image forming units as shown in FIGS. 6-8. For
example, in FIG. 8, the pre-cleaning light irradiating operation
can be performed from the photosensitive layer side of the
photoreceptor 21. In addition, the light irradiation in the light
image irradiating process and the discharging process may be
performed from the substrate side of the photoreceptor 21.
[0359] Further, a pre-transfer light irradiation operation, which
is performed before the transferring of the toner image, and a
preliminary light irradiation operation, which is performed before
the imagewise light irradiation, and other light irradiation
operations may also be performed.
[0360] The above-mentioned image forming unit may be fixedly set in
a copier, a facsimile or a printer. However, the image forming unit
may be set therein as a process cartridge. The process cartridge
means an image forming unit which includes at least a photoreceptor
and a housing. The process cartridge may include one or more of a
charger, an imagewise light irradiator, an image developer, an
image transferer, a cleaner, and a discharger.
[0361] FIG. 9 is a schematic view illustrating an embodiment of the
process cartridge of the present invention. In FIG. 9, the process
cartridge includes a photoreceptor 16, a charger 17 configured to
charge the photoreceptor 16, a cleaning brush 18 configured to
clean the surface of the photoreceptor 16, an imagewise light
irradiator 19 configured to irradiate the photoreceptor 16 with
imagewise light to form an electrostatic latent image on the
photoreceptor 16, an image developer (a developing roller) 20
configured to develop the latent image with a toner, an image
transferer 60 configured to transfer the toner image onto a
receiving paper 61, and a housing 100. The photoreceptor 16 is the
photoreceptor of the present invention, and includes at least a
photosensitive layer on an electroconductive substrate, wherein the
outermost layer includes at least a filler, a binder resin and an
organic compound having an acid value of from 10 to 700 mgKOH/g.
The process cartridge of the present invention is not limited
thereto. For example, a lubricant applicator 101 configured to
apply a lubricant to the surface of the photoreceptor 16 can be
provided therein.
[0362] Having generally described this invention, further
understanding can be obtained by reference to certain specific
examples which are provided herein for the purpose of illustration
only and are not intended to be limiting. In the descriptions in
the following examples, the numbers represent weight ratios in
parts, unless otherwise specified.
EXAMPLES
[0363]
1 Protective Layer Coating Liquid Preparation Example 1 The
following filler, organic compound having an acid of from 10 to 700
mgKOH/g, and organic solvents were mixed and dispersed for 12 hours
using a ball mill containing alumina balls to prepare a dispersion.
Then the binder resin and CTM were dissolved in the residue of the
solvents and mixed with the above-prepared dispersion.
.alpha.-alumina 3 (SUMICORUNDUM AA-03 from Sumitomo Chemical Co.,
Ltd., average primary particle diameter of about 0.3 .mu.m,
resistivity of not less than 10.sup.10 .OMEGA. .multidot. cm, and
pH of from 8 to 9) Polyester resin 0.6 (acid value of about 35
mgKOH/g) Cyclohexanone 80 Tetrahydrofuran 220 Polycarbonate resin 6
(Z-form polycarbonate resin from Teijin Chemical Co., Ltd.) CTM
having the following formula (12) 4 (ionization potential of about
5.4 eV) 23 (12) The pH of the filler is the pH at the isoelectric
point of zeta potential. The zeta potential was measured using a
zeta potential meter manufactured by Otsuka Electric Co., Ltd. In
addition, the ionization potential was measured with respect to a
film of the CTM using an instrument AC-1 manufactured by Riken
Keiki Co., Ltd. Thus, a protective layer coating liquid 1 was
prepared. Protective Layer Coating Liquid Preparation Example 1 The
procedure for preparation of the protective layer coating liquid 1
was repeated except that the polyester resin was replaced with the
following acrylic resin. Acrylic resin 0.3 (DIANAL BR-605 from
Mitsubishi Rayon Co., Ltd., acid value of about 65 mgKOH/g) Thus a
protective layer coating liquid 2 was prepared. Protective Layer
Coating Liquid Preparation Example 3 The procedure for preparation
of the protective layer coating liquid 2 was repeated except that
the acrylic resin was replaced with the following styrene-acrylic
resin. Styrene-acrylic resin 0.2 (FB-1522 from Mitsubishi Rayon
Co., Ltd., acid value of about 200 mgKOH/g) Thus a protective layer
coating liquid 3 was prepared. Protective Layer Coating Liquid
Preparation Example 4 The procedure for preparation of the
protective layer coating liquid 3 was repeated except that the
styrene-acrylic resin was replaced with the following acrylic
acid-hydroxyethyl methacrylate copolymer. Acrylic acid-hydroxyethyl
methacrylate copolymer 0.2 (acid value of about 130 mgKOH/g) Thus a
protective layer coating liquid 4 was prepared. Protective Layer
Coating Liquid Preparation Example 5 The procedure for preparation
of the protective layer coating liquid 3 was repeated except that
the styrene-acrylic resin was replaced with the following
methacrylic acid-butyl methacrylate copolymer. Methacrylic
acid-butyl methacrylate copolymer 0.2 (acid value of about 95
mgKOH/g) Thus a protective layer coating liquid 5 was prepared.
Protective Layer Coating Liquid Preparation Example 6 The procedure
for preparation of the protective layer coating liquid 3 was
repeated except that the styrene-acrylic resin was replaced with
the following monocarboxylic acid derivative. Monocarboxylic acid
ester compound having a carboxyl group 0.12 at the end position
(acid value of about 160 mgKOH/g, and solid content of 25%) Thus a
protective layer coating liquid 6 was prepared. Protective Layer
Coating Liquid Preparation Example 7 The procedure for preparation
of the protective layer coating liquid 6 was repeated except that
the monocarboxylic acid derivative was replaced with the following
wetting dispersant. Wetting dispersant 0.03 (DISPERBYK-111 from BYK
Chemie, copolymer including an acid group, acid value of about 129
mgKOH/g, and solid content of not less than 90%) Thus a protective
layer coating liquid 7 was prepared. Protective Layer Coating
Liquid Preparation Example 8 The procedure for preparation of the
protective layer coating liquid 7 was repeated except that the
filler was replaced with the following filler. Titanium oxide 3
(CR-97 from Ishihara Sangyo Kaisha, Ltd., average primary particle
diameter of 0.3 .mu.m) Thus a protective layer coating liquid 8 was
prepared. Protective Layer Coating Liquid Preparation Example 9 The
procedure for preparation of the protective layer coating liquid 7
was repeated except that the wetting dispersant was replaced with
the following wetting dispersant. Wetting dispersant 0.06
(BYK-P104S from BYK Chemie, solution of copolymer of an unsaturated
polycarboxylic acid polymer with a polysiloxane, acid value of
about 150 mgKOH/g, and solid content of 50%) Thus, a protective
layer coating liquid 9 was prepared. Protective Layer Coating
Liquid Preparation Example 10 The procedure for preparation of the
protective layer coating liquid 9 was repeated except that the
wetting dispersant was replaced with the following wetting
dispersant. Wetting dispersant 0.06 (BYK-P104 from BYK Chemie,
solution of unsaturated polycarboxylic acid polymer, acid value of
about 180 mgKOH/g, and solid content of 50%) Thus a protective
layer coating liquid 10 was prepared. Protective Layer Coating
Liquid Preparation Example 11 The procedure for preparation of the
protective layer coating liquid 10 was repeated except that the
wetting dispersant was replaced with the following wetting
dispersant. Wetting dispersant 0.03 (BYK-P105 from BYK Chemie,
solution of unsaturated polycarboxylic acid polymer, acid value of
about 365 mgKOH/g, and solid content of about 98%) Thus a
protective layer coating liquid 11 was prepared. Protective Layer
Coating Liquid Preparation Example 12 The procedure for preparation
of the protective layer coating liquid 10 was repeated except that
the addition amount of the wetting dispersant BYK-P104 was changed
from 0.06 parts to 0.01 parts. Thus a protective layer coating
liquid 12 was prepared. Protective Layer Coating Liquid Preparation
Example 13 The procedure for preparation of the protective layer
coating liquid 10 was repeated except that the addition amount of
the wetting dispersant BYK-P104 was changed from 0.06 parts to 0.2
parts. Thus a protective layer coating liquid 13 was prepared.
Protective Layer Coating Liquid Preparation Example 14 The
procedure for preparation of the protective layer coating liquid 10
was repeated except that the filler was replaced with the following
filler. .alpha.-alumina 3 (AKP-50 from Sumitomo Chemical Co., Ltd.,
average primary particle diameter of about 0.2 .mu.m. Thus a
protective layer coating liquid 14 was prepared. Protective Layer
Coating Liquid Preparation Example 15 The procedure for preparation
of the protective layer coating liquid 10 was repeated except that
the filler was replaced with the following filler. .alpha.-alumina
3 (SUMICORUNDUM AA-07 from Sumitomo Chemical Co., Ltd., average
primary particle diameter of about 0.9 .mu.m. Thus a protective
layer coating liquid 15 was prepared. Protective Layer Coating
Liquid Preparation Example 16 The procedure for preparation of the
protective layer coating liquid 10 was repeated except that the
filler was replaced with the following filler. .delta.-alumina 2
(ALUMINUM OXIDE C from Nippon Aerosil Co., average primary particle
diameter of about 0.013 .mu.m and pH of from 8 to 9). Thus a
protective layer coating liquid 16 was prepared. Protective Layer
Coating Liquid Preparation Example 17 The procedure for preparation
of the protective layer coating liquid 10 was repeated except that
the filler was replaced with the following filler. Titanium oxide 3
(CR-97 from Ishihara Sangyo Kaisha, Ltd., average primary particle
diameter of about 0.3 .mu.m, resistivity of not less than 10.sup.10
.OMEGA. .multidot. cm, and pH of from 6 to 7) Thus a protective
layer coating liquid 17 was prepared. Protective Layer Coating
Liquid Preparation Example 18 The procedure for preparation of the
protective layer coating liquid 10 was repeated except that the
filler was replaced with the following filler. .alpha.-alumina
coated with a titanate coupling agent 3 (.alpha.-alumina: AA-03
from Sumitomo Chemical Co., Ltd., average primary particle diameter
of about 0.3 .mu.m) Thus a protective layer coating liquid 18 was
prepared. Protective Layer Coating Liquid Preparation Example 19
The procedure for preparation of the protective layer coating
liquid 10 was repeated except that the filler was replaced with the
following filler. Titanium oxide coated with aluminum stearate 3
(titanium oxide: MT150HD from Tayca Corp., average primary particle
diameter of about 0.03 .mu.m) Thus a protective layer coating
liquid 19 was prepared. Protective Layer Coating Liquid Preparation
Example 20 The procedure for preparation of the protective layer
coating liquid 10 was repeated except that the filler was replaced
with the following filler. Titanium oxide coated with a silane
coupling agent 3 (titanium oxide: MT100SA from Tayca Corp., average
primary particle diameter of about 0.015 .mu.m) Thus a protective
layer coating liquid 20 was prepared. Protective Layer Coating
Liquid Preparation Example 21 The procedure for preparation of the
protective layer coating liquid 10 was repeated except that the
addition amount of the filler was changed from 3 parts to 10 parts.
Thus a protective layer coating liquid 21 was prepared. Protective
Layer Coating Liquid Preparation Example 22 The procedure for
preparation of the protective layer coating liquid 10 was repeated
except that the CTM was replaced with the following CTM. CTM having
the following formula (13) 4 (Ionization potential of 5.5 eV) 24
(13) Thus a protective layer coating liquid 22 was prepared.
Protective Layer Coating Liquid Preparation Example 23 The
procedure for preparation of the protective layer coating liquid 10
was repeated except that the polycarbonate resin (binder resin) and
the CTM were replaced with the following charge transport polymer.
Charge transport polymer having the following formula (14) 9
(weight average molecular weight of 150,000, ionization potential
of 5.4 eV) 25 (14) Thus, a protective layer coating liquid 23 was
prepared. Protective Layer Coating Liquid Preparation Example 24
The procedure for preparation of the protective layer coating
liquid 10 was repeated except that cyclohexanone was not added
(i.e., only tetrahydrofuran was used as a solvent). Thus, a
protective layer coating liquid 24 was prepared. Protective Layer
Coating Liquid Preparation Example 25 The procedure for preparation
of the protective layer coating liquid 10 was repeated except that
the alumina balls included in the ball mill were changed to
zirconia balls. Thus, a protective layer coating liquid 25 was
prepared. Protective Layer Coating Liquid Preparation Example 26
The procedure for preparation of the protective layer coating
liquid 10 was repeated except that the dispersion machine was
changed from the ball mill to a shaker. Thus, a protective layer
coating liquid 26 was prepared. Protective Layer Coating Liquid
Comparative Example 1 The procedure for preparation of the
protective layer coating liquid 10 was repeated except that the
wetting dispersant BYK-P104 was not added. Thus, a comparative
protective layer coating liquid 1 was prepared. Protective Layer
Coating Liquid Comparative Example 2 The procedure for preparation
of the comparative protective layer coating liquid 1 was repeated
except that the filler was replaced with the following filler.
Titanium oxide 3 (CR-97 from Ishihara Sangyo Kaisha, Ltd., average
particle diameter of about 0.3 .mu.m) Thus, a comparative
protective layer coating liquid 2 was prepared. Protective Layer
Coating Liquid Comparative Example 3 The procedure for preparation
of the comparative protective layer coating liquid 1 was repeated
except that the filler was replaced with the following filler.
.alpha.-alumina treated with a titanate coupling agent 3
(.alpha.-alumina: AA-03 from Sumitomo Chemical Co., Ltd., average
particle diameter of about 0.3 .mu.m) Thus, a comparative
protective layer coating liquid 3 was prepared. Protective Layer
Coating Liquid Comparative Example 4 The procedure for preparation
of the comparative protective layer coating liquid 1 was repeated
except that the filler was replaced with the following filler.
Titanium oxide treated with a silane coupling agent 2 (titanium
oxide: MT-100SA from Tayca Corp., average particle diameter of
about 0.015 .mu.m) Thus, a comparative protective layer coating
liquid 4 was prepared. Protective Layer Coating Liquid Comparative
Example 5 The procedure for preparation of the comparative
protective layer coating liquid 1 was repeated except that the
addition quantity of the filler was changed from 3 parts to 1 part.
Thus, a comparative protective layer coating liquid 5 was prepared.
Protective Layer Coating Liquid Comparative Example 6 The procedure
for preparation of the protective layer coating liquid 2 was
repeated except that the polyester resin was replaced with the
following polyester resin. Polyester resin 0.6 (acid value of 7
mgKOH/g) Thus, a comparative protective layer coating liquid 6 was
prepared. Protective Layer Coating Liquid Comparative Example 7 The
procedure for preparation of the comparative protective layer
coating liquid 6 was repeated except that the addition amount of
the polyester resin was changed from 0.6 parts to 1.2 parts. Thus,
a comparative protective layer coating liquid 7 was prepared.
Protective Layer Coating Liquid Comparative Example 8 The procedure
for preparation of the comparative protective layer coating liquid
6 was repeated except that the filler was replaced with the
following filler. .delta.-alumina 2 (ALUMINUM OXIDE C from Nippon
Aerosil Co., average primary particle diameter of 0.013 .mu.m)
Thus, a comparative protective layer coating liquid 8 was prepared.
Protective Layer Coating Liquid Comparative Example 9 The procedure
for preparation of the comparative protective layer coating liquid
6 was repeated except that the filler was replaced with the
following filler. .alpha.-alumina treated with a titanate coupling
agent 3 (.alpha.-alumina: AA-03 from Sumitomo Chemical Co., Ltd.,
average primary particle diameter of 0.03 .mu.m) Thus, a
comparative protective layer coating liquid 9 was prepared.
Protective Layer Coating Liquid Comparative Example 10 The
procedure for preparation of the comparative protective layer
coating liquid 6 was repeated except that the polyester resin was
replaced with the following wetting dispersant. Wetting dispersant
0.06 (DISPERBYK-103 from BYK Chemie, solution of copolymer having
affinity to the pigment, solid content of about 40%) Thus, a
comparative protective layer coating liquid 10 was prepared.
Methods of evaluating the protective layer coating liquids are as
follows. Average particle diameter of protective layer coating
liquids The average particle diameter of the solid components in
each protective layer coating liquid was measured using an
instrument, CAPA500 manufactured by Horiba Ltd. Precipitation of
filler used Each of the protective layer coating liquids was
observed whether the filler was precipitated at the bottom of the
coating liquid after being settled for one day after the
preparation. The coating liquids were evaluated by being classified
to the following four precipitation grades: .circleincircle.: the
coating liquid had no precipitation. .largecircle.: a small amount
of the filler was precipitated. .DELTA.: the filler was
precipitated and the upper part of the liquid was clear. X: almost
all the filler particles were precipitated and the entire part of
the liquid was clear.
[0364] The results are shown in Table 1.
2 TABLE 1 Addi- PD*.sup.3 PD*.sup.4 tion of Of Pre- AV*.sup.1
amount filler Liquid cipi- Filler (mgKOH/g) *.sup.2 (parts) (.mu.m)
(.mu.m) tation Example 1 Alumina 35 0.60 0.3 0.71 .largecircle. 2
Alumina 65 0.30 0.3 0.65 .largecircle. 3 Alumina 200 0.20 0.3 0.61
.largecircle. 4 Alumina 130 0.20 0.3 0.59 .largecircle. 5 Alumina
95 0.20 0.3 0.50 .circleincircle. 6 Alumina 160 0.12 0.3 0.53
.circleincircle. 7 Alumina 129 0.03 0.3 0.47 .circleincircle. 8
Titanium 129 0.03 0.3 0.51 .circleincircle. oxide 9 Alumina 150
0.06 0.3 0.48 .circleincircle. 10 Alumina 180 0.06 0.3 0.42
.circleincircle. 11 Alumina 365 0.03 0.3 0.39 .circleincircle. 12
Alumina 180 0.01 0.3 0.57 .circleincircle. 13 Alumina 180 0.20 0.3
0.40 .circleincircle. 14 Alumina 180 0.06 0.2 0.37 .circleincircle.
15 Alumina 180 0.06 0.9 1.06 .largecircle. 16 Alumina 180 0.06
0.013 0.21 .circleincircle. 17 Titanium 180 0.06 0.3 0.46
.circleincircle. oxide 18 Alumina 180 0.06 0.3 0.36
.circleincircle. treated with titanate coupling agent 19 Titanium
180 0.06 0.03 0.27 .circleincircle. oxide treated with aluminum
stearate 20 Titanium 180 0.06 0.015 0.31 .largecircle. oxide
treated with silane coupling agent 21 Alumina 180 0.06 0.3 0.62
.largecircle. 22 Alumina 180 0.06 0.3 0.45 .circleincircle. 23
Alumina 180 0.06 0.3 0.52 .circleincircle. 24 Alumina 180 0.06 0.3
0.70 .largecircle. 25 Alumina 180 0.06 0.3 0.51 .largecircle. 26
Alumina 180 0.06 0.3 0.48 .largecircle. Compar- 1 Alumina -- 0 0.3
1.23 X ative Example 2 Titanium -- 0 0.3 1.15 X oxide 3 Alumina 0
0.3 0.88 .DELTA. treated with titanate coupling agent 4 Titanium 0
0.015 0.51 X oxide treated with silane coupling agent 5 Alumina --
0 0.3 1.16 X 6 Alumina 7 0.60 0.3 1.08 X 7 Alumina 7 1.20 0.3 0.96
X 8 Alumina 7 0.60 0.013 0.58 X 9 Alumina 7 0.60 0.3 0.75
.largecircle. treated with titanate coupling agent 10 Alumina --
0.06 0.3 0.92 X *.sup.1Acid value of the organic compound
*.sup.2Addition amount of the organic compound *.sup.3Average
primary particle diameter of the filler *.sup.4Average particle
diameter of the solid components in the coating liquid
[0365] As can be understood from Table 1, by adding an organic
compound having an acid value of from 10 to 700 mgKOH/g, the
average particle diameter of the solid components of the coating
liquids can be decreased, and thereby precipitation of the filler
can be prevented and dispersion of the filler can be improved. In
addition, a wetting dispersant is used as the organic compound
having an acid value of from 10 to 700 mgKOH/g, dispersion of the
filler can be further improved and stability of the dispersion of
the filler can also be enhanced.
[0366] To the contrary, when such an organic compound is not added
or an organic compound having an acid value less than 10 mgKOH/g is
added, the average particle diameter of the solid components
increases and precipitation of the filler increases (i.e.,
dispersion of the filler seriously deteriorates due to
agglomeration of the filler).
Example 1
[0367] Each of the following undercoat layer coating liquid, a CGL
coating liquid and a CTL coating liquid was coated on an aluminum
cylinder by dip coating and then dried to overlay an undercoat
layer having a thickness of 3.5 .mu.m, a CGL having a thickness of
0.2 .mu.m, and CTL having a thickness of 23 .mu.m.
3 Undercoat layer coating liquid Titanium dioxide 400 Melamine
resin 65 Alkyd resin 120 2-butanone 400 CGL coating liquid
Polyvinyl butyral 5
[0368] Bisazo pigment having the following formula (15)
4 26 (15) 2-butanone 200 Cyclohexanone 400
[0369] CTL Coating Liquid
5 Polycarbonate 10 (Z-form polycarbonate from Teijin Chemical Co.,
Ltd.) CTM having formula (12) 10 (ionization potential of 5.4 eV)
10 Tetrahydrofuran 100
[0370] Then the following protective layer coating liquid was
coated by spray coating on the CTL and then dried to form a
protective layer having a thickness of about 4 .mu.m.
6 Protective layer coating liquid .alpha.-alumina 3 (SUMICORUNDUM
AA-03 from Sumitomo Chemical Co., Ltd., average primary particular
diameter of 0.3 .mu.m, resistivity of not less than 10.sup.10
.OMEGA. .multidot. cm, and pH of from 8 to 9) Polyester resin 0.8
(acid value of about 35 mgKOH/g) CTM having formula (12) 4
Polycarbonate resin 6 (Z-form polycarbonate resin from Teijin
Chemical Co., Ltd.) Tetrahydrofuran 220 Cyclohexanone 80 Thus, a
photoreceptor 1 was prepared.
Example 2
[0371] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin included in the protective
layer coating liquid was replaced with the following polyester
resin.
7 Polyester resin 0.6 (acid value of about 50 mgKOH/g) Thus, a
photoreceptor 2 was prepared.
Example 3
[0372] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin included in the protective
layer coating liquid was replaced with the following acrylic
resin.
8 Acrylic resin 0.5 (DIANAL BR-605 from Mitsubishi Rayon Co., Ltd.,
acid value of about 65 mgKOH/g) Thus, a photoreceptor 3 was
prepared.
Example 4
[0373] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin included in the protective
layer coating liquid was replaced with the following acrylic
resin.
9 Acrylic acid-hydroxyetyl methacrylate copolymer 0.3 (acid value
of about 100 mgKOH/g) Thus, a photoreceptor 4 was prepared.
Example 5
[0374] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin included in the protective
layer coating liquid was replaced with the following compound.
10 Ester compound having a carboxyl group at the 0.12 end position
(acid value of about 160 mgKOH/g, and solid content of about 25%)
Thus, a photoreceptor 5 was prepared.
Example 6
[0375] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin included in the protective
layer coating liquid was replaced with the following wetting
dispersant.
11 Wetting dispersant 0.03 (BYK-P104 from BYK Chemie, unsaturated
polycarboxylic acid polymer solution, acid value of about 180
mgKOH/g, and solid content of about 50%) Thus, a photoreceptor 6
was prepared.
Example 7
[0376] The procedure for preparation of the photoreceptor 6 was
repeated except that the addition amount of the wetting dispersant
included in the protective layer coating liquid was changed from
0.03 to 0.06.
[0377] Thus, a photoreceptor 7 was prepared.
Example 8
[0378] The procedure for preparation of the photoreceptor 6 was
repeated except that the addition amount of the wetting dispersant
included in the protective layer coating liquid was changed from
0.03 to 0.09.
[0379] Thus, a photoreceptor 8 was prepared.
Example 9
[0380] The procedure for preparation of the photoreceptor 6 was
repeated except that the wetting dispersant included in the
protective layer coating liquid was replaced with the following
wetting dispersant.
12 Wetting dispersant 0.01 (BYK-P105 from BYK Chemie, unsaturated
polycarboxylic acid polymer, acid value of about 365 mgKOH/g, and
solid content of about 98%) Thus, a photoreceptor 9 was
prepared.
Example 10
[0381] The procedure for preparation of the photoreceptor 9 was
repeated except that the addition amount of the wetting dispersant
included in the protective layer coating liquid was changed from
0.01 to 0.03.
[0382] Thus, a photoreceptor 10 was prepared.
Example 11
[0383] The procedure for preparation of the photoreceptor 9 was
repeated except that the addition amount of the wetting dispersant
included in the protective layer coating liquid was changed from
0.01 to 0.2.
[0384] Thus, a photoreceptor 11 was prepared.
Example 12
[0385] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
13 Titanium oxide 3 (CR-97 from Ishihara Sangyo Kaisha, Ltd.,
average primary particle diameter of about 0.3 .mu.m, resistivity
of not less than 10.sup.10 .OMEGA. .multidot. cm, and pH of from 6
to 7) Thus, a photoreceptor 12 was prepared.
Example 13
[0386] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
14 .alpha.-alumina 3 (AKP-50 from Sumitomo Chemical Co., Ltd.,
average primary particle diameter of about 0.2 .mu.m) Thus, a
photoreceptor 13 was prepared.
Example 14
[0387] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
15 .alpha.-alumina 3 (SUMICORUNDUM AA-07 from Sumitomo Chemical
Co., Ltd., average primary particle diameter of about 0.9 .mu.m)
Thus, a photoreceptor 14 was prepared.
Example 15
[0388] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
16 .alpha.-alumina with a titanate coupling agent 2.5 (SUMICORUNDUM
AA-03 from Sumitomo Chemical Co., Ltd. treated with a titanate
coupling agent in an amount of 5% by weight, average primary
particle diameter of about 0.3 .mu.m) Thus, a photoreceptor 15 was
prepared.
Example 16
[0389] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
17 Titanium oxide treated with a silane coupling agent 2 (MT100SA
from Tayca Corp. treated with a silane coupling agent in an amount
of 20% by weight, average primary particle diameter of about 0.015
.mu.m) Thus, a photoreceptor 16 was prepared.
Example 17
[0390] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
18 Silica 2 (KMPX100 from Shin-Etsu Silicone Co., Ltd., average
primary particle diameter of about 0.1 .mu.m, resistivity of not
less than 10.sup.10 .OMEGA. .multidot. cm, and pH of from 4 to 5)
Thus, a photoreceptor 17 was prepared.
Example 18
[0391] The procedure for preparation of the photoreceptor 7 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
19 Tin oxide 3 (S-1 from Mitsubishi Metal Corp., average primary
particle diameter of about 0.15 .mu.m, resistivity of less than
10.sup.10 .OMEGA. .multidot. cm, and pH of from 4 to 5) Thus, a
photoreceptor 18 was prepared.
Example 19
[0392] The procedure for preparation of the photoreceptor 7 was
repeated except that the addition amount of the filler was changed
from 3 to 10 parts.
[0393] Thus, a photoreceptor 19 was prepared.
Example 20
[0394] The procedure for preparation of the photoreceptor 7 was
repeated except that the CTM included in the protective layer was
replaced with the following compound.
20 CTM having the following formula (16) 4 (ionization potential of
5.3 eV) 27 (16) Thus, a photoreceptor 20 was prepared.
Example 21
[0395] The procedure for preparation of the photoreceptor 7 was
repeated except that the CTM included in the protective layer was
replaced with the following compound.
21 CTM having formula (13) 4 (ionization potential of 5.5 eV) Thus,
a photoreceptor 21 was prepared.
Example 22
[0396] The procedure for preparation of the photoreceptor 8 was
repeated except that the CTM having formula (12) was not added to
the protective layer coating liquid.
[0397] Thus, a photoreceptor 22 was prepared.
Example 23
[0398] The procedure for preparation of the photoreceptor 22 was
repeated except that the addition quantity of the wetting
dispersant included in the protective layer coating liquid was
changed from 0.09 to 0.2.
[0399] Thus, a photoreceptor 23 was prepared.
Example 24
[0400] The procedure for preparation of the photoreceptor 7 was
repeated except that the binder resin included in the protective
layer coating liquid was replaced with the following resin.
22 Polyarylate resin 10 (U-POLYMER U6000 from Unitika Ltd.) Thus, a
photoreceptor 24 was prepared.
Example 25
[0401] The procedure for preparation of the photoreceptor 7 was
repeated except that the binder resin and the CTM included in the
protective layer coating liquid were replaced with the following
charge transport polymer.
23 Charge transport polymer having formula (14) 20 (weight average
molecular weight of 150,000 and ionization potential of 5.4 eV)
Thus, a photoreceptor 25 was prepared.
Example 26
[0402] The procedure for preparation of the photoreceptor 8 was
repeated except that the following antioxidant was added to the
protective layer coating liquid.
24 Antioxidant having formula (11) 0.24 Thus, a photoreceptor 26
was prepared.
Example 27
[0403] The procedure for preparation of the photoreceptor 26 was
repeated except that the antioxidant was replaced with the
following antioxidant.
[0404] Antioxidant having the following formula (17) 0.22 28
[0405] Thus, a photoreceptor 27 was prepared.
Example 28
[0406] The procedure for preparation of the photoreceptor 26 was
repeated except that the addition amount of the antioxidant
included in the protective layer coating liquid was changed from
0.24 to 0.08.
[0407] Thus, a photoreceptor 28 was prepared.
Example 29
[0408] The procedure for preparation of the photoreceptor 1 was
repeated except that the CGL coating liquid, CTL coating liquid and
protective layer coating liquid were replaced with the following
coating liquids, respectively, and the thickness of the CTL and
protective layer was changed to about 20 .mu.m and about 5 .mu.m,
respectively.
25 CGL coating liquid Titanyl phthalocyanine having such an X-ray 8
diffraction spectrum as shown in FIG. 10 Polyvinyl butyral 5
2-butanone 400 CTL coating liquid Polycarbonate 10 (C-form
polycarbonate resin from Teijin Chemical 8 Co., Ltd.) CTM having
formula (16) Toluene 70 Protective layer coating liquid
.alpha.-alumina 3 (AKP-50 from Sumitomo Chemical Co., Ltd., average
particle diameter of about 0.2 .mu.m) Wetting dispersant 0.06
(BYK-P104 from BYK Chemie, unsaturated polycarboxylic acid polymer
solution, acid value of about 180 mgKOH/g, and solid content of
about 50%) Polycarbonate resin 6 (C-form polycarbonate resin from
Teijin Chemical 4 Co., Ltd.) CTM having formula (16)
Tetrahydrofuran 250 Cyclohexanone 50 Thus, a photoreceptor 29 was
prepared.
Example 30
[0409] The procedure for preparation of the photoreceptor 29 was
repeated except that the wetting dispersant included in the
protective layer coating liquid was replaced with the following
compound.
26 Ester compound having a carboxyl group at the 0.12 end position
(acid value of about 160 mgKOH/g, and solid content of about 25%)
Thus, a photoreceptor 30 was prepared.
Example 31
[0410] The procedure for preparation of the photoreceptor 29 was
repeated except that the addition amount of the wetting dispersant
was changed from 0.06 to 0.1 parts.
[0411] Thus, a photoreceptor 31 was prepared.
Example 32
[0412] The procedure for preparation of the photoreceptor 29 was
repeated except that the filler included in the protective layer
coating liquid was changed to the following filler.
27 .alpha.-alumina 1 (SUMICORUNDUM AA-03 from Sumitomo Chemical
Co., Ltd., average particle diameter of about 0.3 .mu.m,
resistivity of not less than 10.sup.10 .OMEGA. .multidot. cm, and
pH of from 8 to 9) Thus, a photoreceptor 32 was prepared.
Example 33
[0413] The procedure for preparation of the photoreceptor 29 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
28 Titanium oxide 3 (CR-97 from Ishihara Sangyo Kaisha, Ltd.,
average particle diameter of about 0.3 .mu.m, resistivity of not
less than 10.sup.10 .OMEGA. .multidot. cm, and pH of from 6 to 7)
Thus, a photoreceptor 33 was prepared.
Example 34
[0414] The procedure for preparation of the photoreceptor 29 was
repeated except that the filler included in the protective layer
coating liquid was replaced with the following filler.
29 Spherical silicone resin particles 3 (TOSPEARL 105 from Toshiba
Silicone Co., Ltd., average particle diameter of about 0.5 .mu.m)
Thus, a photoreceptor 34 was prepared.
Example 35
[0415] The procedure for preparation of the photoreceptor 29 was
repeated except that the binder resin and CTM included in the
protective layer coating liquid were replaced with the following
charge transport polymer.
30 Charge transport polymer having formula (14) 20 (Weight average
molecular weight of 150,000, and ionization potential of 5.4 eV)
Thus, a photoreceptor 35 was prepared.
Example 36
[0416] The procedure for preparation of the photoreceptor 29 was
repeated except that the following antioxidant was further added to
the protective layer coating liquid.
31 Antioxidant having formula (11) 0.24 Thus, a photoreceptor 36
was prepared.
Example 37
[0417] The procedure for preparation of the undercoat layer and CGL
of the photoreceptor 29 was repeated. The following CTL coating
liquid was coated on the CGL and dried to form a CTL having a
thickness of about 25 .mu.m, which is the outermost layer.
32 CTL coating liquid Polycarbonate 10 (Z-form polycarbonate from
Teijin Chemical Co., Ltd.) 8 CTM having formula (12)
.alpha.-alumina 1.5 (SUMICORUNDUM AA-03 from Sumitomo Chemical Co.,
Ltd., average primary particle diameter of 0.3 .mu.m) Wetting
dispersant 0.04 (BYK-P104 from BYK Chemie, unsaturated
polycarboxylic acid polymer solution, acid value of 180 mgKOH/g,
and solid content of about 50%) Tetrahydrofuran 80 Cyclohexanone 15
Thus, a photoreceptor 37 having no protective layer was formed.
Comparative Example 1
[0418] The procedure for preparation of the photoreceptor 1 was
repeated except that the polyester resin in the protective layer
coating liquid was replaced with the following resin.
33 Polyester resin 0.6 (acid value of 7 mgKOH/g) Thus a comparative
photoreceptor 1 was prepared.
Comparative Example 2
[0419] The procedure for preparation of the comparative
photoreceptor 1 was repeated except that the addition amount of the
polyester resin in the protective layer coating liquid was changed
from 0.6 to 1.2 parts.
[0420] Thus a comparative photoreceptor 2 was prepared.
Comparative Example 3
[0421] The procedure for preparation of the comparative
photoreceptor 1 was repeated except that the filler in the
protective layer coating liquid was replaced with the following
filler.
34 .delta.-alumina 2 (ALUMINUM OXIDE C from Nippon Aerosil Co.,
average primary particle diameter of about 0.013 .mu.m) Thus a
comparative photoreceptor 3 was prepared.
Comparative Example 4
[0422] The procedure for preparation of the comparative
photoreceptor 1 was repeated except that the filler in the
protective layer coating liquid was replaced with the following
filler.
35 .alpha.-alumina treated with a titanate coupling agent 3
(.alpha.-alumina: AA-03 from Sumitomo Chemical Co., Ltd., average
primary particle diameter of about 0.3 .mu.m) Thus a comparative
photoreceptor 4 was prepared.
Comparative Example 5
[0423] The procedure for preparation of the photoreceptor 7 was
repeated except that the wetting dispersant in the protective layer
coating liquid was removed therefrom.
[0424] Thus a comparative photoreceptor 5 was prepared.
Comparative Example 6
[0425] The procedure for preparation of the comparative
photoreceptor 5 was repeated except that the filler in the
protective layer coating liquid was replaced with the following
filler.
36 Titanium oxide 3 (CR-97 from Ishihara Sangyo Kaisha, Ltd.,
average primary particle diameter of about 0.3 .mu.m) Thus a
comparative photoreceptor 6 was prepared.
Comparative Example 7
[0426] The procedure for preparation of the comparative
photoreceptor 5 was repeated except that the filler in the
protective layer coating liquid was replaced with the following
filler.
37 .alpha.-alumina treated with a titanate coupling agent 3
(.alpha.-alumina: AA-03 from Sumitomo Chemical Co., Ltd., average
primary particle diameter of about 0.3 .mu.m) Thus a comparative
photoreceptor 7 was prepared.
Comparative Example 8
[0427] The procedure for preparation of the comparative
photoreceptor 5 was repeated except that the filler in the
protective layer coating liquid was replaced with the following
filler.
38 Titanium oxide treated with a silane coupling agent 2 (titanium
oxide: MT-100SA from Tayca Corp., average primary particle diameter
of about 0.015 .mu.m) Thus a comparative photoreceptor 8 was
prepared.
Comparative Example 9
[0428] The procedure for preparation of the comparative
photoreceptor 5 was repeated except that the addition amount of the
filler was changed from 3 to 1 part.
[0429] Thus a comparative photoreceptor 9 was prepared.
Comparative Example 10
[0430] The procedure for preparation of the comparative
photoreceptor 5 was repeated except that the CTM in the protective
layer coating liquid was not included.
[0431] Thus a comparative photoreceptor 10 was prepared.
Comparative Example 11
[0432] The procedure for preparation of the photoreceptor 7 was
repeated except that the wetting dispersant in the protective layer
coating liquid was replaced with the following wetting
dispersant.
39 Wetting dispersant 0.06 (DISPERBYK-103 from BYK Chemie, solution
of a copolymer having an affinity to the filler used, acid value of
0 mgKOH/g, and solid content of about 40%) Thus a comparative
photoreceptor 11 was prepared.
Comparative Example 12
[0433] The procedure for preparation of the comparative
photoreceptor 11 was repeated except that the addition amount of
the wetting dispersant in the protective layer coating liquid was
changed from 0.06 to 0.12.
[0434] Thus a comparative photoreceptor 12 was prepared.
Comparative Example 13
[0435] The procedure for preparation of the photoreceptor 37 was
repeated except that the wetting dispersant in the protective layer
coating liquid was removed therefrom.
[0436] Thus a comparative photoreceptor 13 was prepared.
Comparative Example 14
[0437] The procedure for preparation of the photoreceptor 37 was
repeated except that the wetting dispersant in the protective layer
coating liquid was replaced with the following resin.
40 Polyester resin 0.6 (acid value of 7 mgKOH/g) Thus a comparative
photoreceptor 14 was prepared.
Comparative Example 15
[0438] The procedure for preparation of the photoreceptor 37 was
repeated except that the filler in the protective layer coating
liquid was removed therefrom.
[0439] Thus a comparative photoreceptor 15 was prepared.
[0440] Evaluation method
[0441] Each of the photoreceptors 1 to 37 and comparative
photoreceptors 1 to 15 was set in a process cartridge, and the
cartridge was set in an image forming apparatus, IMAGIO MF2200
manufactured by Ricoh Co., Ltd., which had been modified such that
a charging roller was used as the charger and a laser diode
emitting light having a wavelength of 655 nm was used as a light
source for the imagewise light irradiator. A running test in which
10,000 images were continuously produced was performed while the
pre-cleaning light irradiation process was not performed.
[0442] At the beginning and end of the running test, the
lighted-area potential (VL) of each photoreceptor was measured at
the developing section, and the qualities of the images produced by
each photoreceptor were visually evaluated. In addition, the
abrasion quantity of each photoreceptor was also determined by
measuring the thickness of the layers of the photoreceptor before
and after the running test.
[0443] With respect to the photoreceptor, which could produce good
images even after the 10,000-copy running test, the running test
was continued to produce 50,000 copies in total.
[0444] The results are shown in Table 2.
41 TABLE 2 Initial 10,000.sup.th 50,000.sup.th image image image
Image Image AB Image P.sub.L(-V) quality P.sub.L(-V) quality
(.mu.m) quality Example 1 85 .circleincircle. 105 .circleincircle.
0.51 .circleincircle. 2 80 .circleincircle. 100 .circleincircle.
0.48 .circleincircle. 3 90 .circleincircle. 115 .circleincircle.
0.46 .circleincircle. 4 65 .circleincircle. 85 .circleincircle.
0.43 .circleincircle. 5 70 .circleincircle. 95 .circleincircle.
0.44 .circleincircle. 6 85 .circleincircle. 110 .circleincircle.
0.56 .circleincircle. 7 70 .circleincircle. 90 .circleincircle.
0.41 .circleincircle. 8 55 .circleincircle. 75 .circleincircle.
0.42 .circleincircle. 9 90 .circleincircle. 115 .circleincircle.
0.51 .circleincircle. 10 65 .circleincircle. 80 .circleincircle.
0.38 .circleincircle. 11 50 .circleincircle. 70 .circleincircle.
0.52 .circleincircle. 12 65 .circleincircle. 85 .circleincircle.
0.63 .circleincircle. 13 70 .circleincircle. 90 .circleincircle.
0.43 .circleincircle. 14 70 .circleincircle. 95 .circleincircle.
0.59 .circleincircle. 15 80 .circleincircle. 100 .circleincircle.
0.41 .circleincircle. 16 65 .circleincircle. 85 .largecircle. 0.52
Not produced 17 60 .circleincircle. 80 .largecircle. 0.57 Not
produced 18 60 .largecircle. 80 .DELTA. 0.55. Not produced 19 90
.circleincircle. 130 .largecircle.(ID) 0.78 Not produced 20 65
.circleincircle. 85 .circleincircle. 0.43 .circleincircle. 21 80
.circleincircle. 100 .circleincircle. 0.41 .circleincircle. 22 90
.circleincircle. 115 .circleincircle. 0.33 .circleincircle. 23 60
.circleincircle. 80 .circleincircle. 0.34 .circleincircle. 24 60
.circleincircle. 80 .circleincircle. 0.38 .circleincircle. 25 70
.circleincircle. 95 .circleincircle. 0.45 .circleincircle. 26 75
.circleincircle. 95 .circleincircle. 0.42 .circleincircle. 27 80
.circleincircle. 100 .circleincircle. 0.45 .circleincircle. 28 65
.circleincircle. 85 .circleincircle. 0.45 .circleincircle. 29 65
.circleincircle. 85 .circleincircle. 0.47 .circleincircle. 30 70
.circleincircle. 90 .circleincircle. 0.50 .circleincircle. 31 60
.circleincircle. 80 .circleincircle. 0.44 .circleincircle. 32 60
.circleincircle. 80 .circleincircle. 0.61 .circleincircle. 33 70
.circleincircle. 90 .circleincircle. 0.65 .circleincircle. 34 75
.circleincircle. 100 .circleincircle. 0.84 .largecircle. 35 65
.circleincircle. 95 .circleincircle. 0.43 .circleincircle. 36 70
.circleincircle. 90 .circleincircle. 0.44 .circleincircle. 37 75
.circleincircle. 100 .circleincircle. 0.54 .circleincircle. Compar-
1 205 X 190 X 1.02 Not tive produced Example 2 190 X 185 X 0.98 Not
produced 3 215 X 205 X 0.93 Not produced 4 220 X 215 X 0.84 Not
produced 5 270 X 260 X 0.97 Not produced 6 210 X 200 X 0.98 Not
produced 7 275 X 260 X 0.88 Not produced 8 195 X 190 X 0.84 Not
produced 9 160 X 210 X 1.01 Not produced 10 360 X -- Not -- Not
produced produced 11 210 X 200 X 0.91 Not produced 12 240 X 210 X
0.93 Not produced 13 200 X 190 X 0.88 Not produced 14 195 X 180 X
0.85 Not produced 15 50 .circleincircle. 70 .circleincircle. 1.61
X(BF) P.sub.L: Potential of a lighted area of a photoreceptor which
is exposed to imagewise light. AB: Abrasion quantity of the
outermost layer .circleincircle.: The image qualities are good and
hardly deteriorate .largecircle.: Resolution slightly deteriorates
but the image qualities are still acceptable .largecircle.(ID):
Image density slightly decreases but the image qualities are still
acceptable .DELTA.: Resolution apparently deteriorates X: Image
density seriously deteriorates X(BF): The image has serious
background fouling
[0445] As can be understood from Table 2, the photoreceptors of the
present invention, which have an outermost layer including a filler
and an organic compound having an acid value of from 10 to 700
mgKOH/g, has a low potential after being exposed to imagewise
light. In addition, even after the 10,000-copy running test, the
lighted-area potential thereof hardly increases, and thereby the
photoreceptors can produce high quality images. Further, the
abrasion quantity of the outermost layer of the photoreceptors is
small, namely, the photoreceptors have good abrasion
resistance.
[0446] However, when an acidic filler or a filler treated with an
acidic treating agent is used, resolution of the resultant images
deteriorates. It is found that it is preferable to use a filler
having a pH not less than 5 in the outermost layer. In addition,
when an electroconductive filler is used, the resultant initial
images are blurred. Further, it is found that when a filler is
included in the outermost layer in a very large amount, resolution
of the resultant images deteriorates.
[0447] When a CTM is not included in the protective layer (i.e.,
outermost layer), the residual potential of the resultant
photoreceptor increases. However, even when the outermost layer has
no CTM, increase of residual potential can be avoided if the
addition amount of the organic compound having an acid value of
from 10 to 700 mgKOH/g is increased.
[0448] To the contrary, when such an organic compound is not
included or an organic compound having an acid value less than 10
mgKOH/g is used, the lighted-area potential is very high even at
the beginning of the running test, resulting in occurrence of a
problem in which the image density seriously decreases. In
addition, the abrasion quantity of the outermost layer of the
comparative photoreceptors is very large, namely the comparative
photoreceptors have poor abrasion resistance.
[0449] It is also found that a photoreceptor of the present
invention capable of producing good images even after 10,000-copy
running test can produce good images even after 50,000-copy running
test. Namely, the photoreceptor of the present invention capable of
producing good images after 10,000-copy running test has good
durability. However, if a photoreceptor including no filler in the
outermost layer can produce good images at the begging and end of
the 10,000-copy running test, the photoreceptor cannot produce good
images after 50,000-copy running test because of having poor
abrasion resistance.
Examples 38 to 68
[0450] The photoreceptors which could produce good images after the
50,000-copy running test were then subjected to NOx gasses exposure
test in which the photoreceptors were settled for 24 hours in an
atmosphere including NOx gasses in an amount of about 20 ppm. Then
images were produced by setting each of the photoreceptors in the
modified IMAGIO MF2200 mentioned above.
[0451] The results are shown in Table 3.
42 TABLE 3 Image Photo- quality receptor 50,000.sup.th After NOx
Example No. image exposure test 38 1 .circleincircle. Good
.largecircle. Resolution slightly deteriorates 39 2
.circleincircle. Good .largecircle. Ditto 40 3 .circleincircle.
Good .largecircle. Ditto 41 4 .circleincircle. Good
.circleincircle. Good 42 5 .circleincircle. Good .DELTA. Resolution
deteriorates 43 6 .circleincircle. Good .largecircle. Resolution
slightly deteriorates 44 7 .circleincircle. Good .DELTA. Resolution
deteriorates 45 8 .circleincircle. Good .DELTA. Ditto 46 9
.circleincircle. Good .largecircle. Resolution slightly
deteriorates 47 10 .circleincircle. Good .DELTA. Resolution
deteriorates 48 11 .circleincircle. Good X Blurred image problem
occurred 49 12 .circleincircle. Good .DELTA. Resolution
deteriorates 50 13 .circleincircle. Good .DELTA. Ditto 51 14
.circleincircle. Good .largecircle. Resolution slightly
deteriorates 52 15 .circleincircle. Good .largecircle. Ditto 53 20
.circleincircle. Good .DELTA. Resolution deteriorates 54 21
.circleincircle. Good .DELTA. Ditto 55 22 .circleincircle. Good
.circleincircle. Good 56 23 .circleincircle. Good .DELTA.
Resolution deteriorates 57 24 .circleincircle. Good .largecircle.
Resolution slightly deteriorates 58 25 .circleincircle. Good
.largecircle. Ditto 59 26 .circleincircle. Good .circleincircle.
Good 60 27 .circleincircle. Good .largecircle. Resolution slightly
deteriorates 61 28 .circleincircle. Good .largecircle. Ditto 62 29
.circleincircle. Good .largecircle. Ditto 63 30 .circleincircle.
Good .largecircle. Ditto 64 31 .circleincircle. Good .DELTA.
Resolution deteriorates 65 32 .circleincircle. Good
.circleincircle. Good 66 33 .circleincircle. Good .largecircle.
Resolution slightly deteriorates 67 34 .circleincircle. Good
.largecircle. Ditto 68 35 .circleincircle. Good .circleincircle.
Good 69 36 .circleincircle. Good .DELTA. Resolution deteriorates
.circleincircle.: Image qualities are good and hardly deteriorate.
.largecircle.: Image qualities slightly deteriorate but are still
acceptable. .DELTA.: Image qualities apparently deteriorate. X:
Image densities seriously deteriorate.
[0452] As can be understood from Table 3, the resolution of the
images produced by the photoreceptors tends to deteriorate in
general. However, when an antioxidant having both a hindered phenol
structure and a hindered amine structure is included, the
deterioration of resolution can be prevented. It is observed that
the deterioration of resolution can also be prevented by using a
proper organic compound having an acid value of from 10 to 700
mgKOH/g and/or a proper binder resin. In addition, it is also found
that when a CTM is not included in the outermost layer, the
deterioration can also be lightened.
Example 70
[0453] The photoreceptor 26 was set in a process cartridge, and the
cartridge was set in an image forming apparatus, IMAGIO MF2200 from
Ricoh Co., Ltd., which had been modified such that a charging
roller was used as the charger and a laser diode emitting light
having a wavelength of 655 nm was used as the light source for the
imagewise light irradiator. A running test in which 100,000 images
were continuously produced while the pre-cleaning light irradiation
process was not performed.
[0454] At the beginning and end of the running test, the
lighted-area potential (V.sub.L) of each photoreceptor was measured
at the developing section, and the qualities of the images produced
by each photoreceptor were visually evaluated. In addition, the
abrasion quantity of each photoreceptor was also determined by
measuring the thickness of the layers of the photoreceptor before
and after the running test.
Example 71
[0455] The procedure for image formation in Example 70 was repeated
except that a polytetrafluoroethylene tape having a thickness of 50
.mu.m was wound around both the edge portions of the charging
roller to perform proximity charging.
Example 72
[0456] The procedure for image formation in Example 71 was repeated
except that a DC voltage of -750 V overlapped with an AC voltage
having a peak-to-peak voltage of 1.8 kV and a frequency of 2 kHz
was applied to the charging roller.
Example 72
[0457] The procedure for image formation in Example 72 was repeated
except that the developer included zinc stearate in an amount of
0.1 parts by weight per 100 parts by weight of the toner.
[0458] The results are shown in Table 4.
43 TABLE 4 Initial At the end of image running test PR Image Image
AB*.sup.2 No.* P.sub.L(-V) quality P.sub.L(-V) quality (.mu.m) Ex.
70 26 70 .circleincircle. Good 110 .DELTA. Background 3.87 fouling,
black streak image Ex. 71 26 70 .circleincircle. Good 110
.largecircle. Slightly 3.71 uneven image density Ex. 72 26 70
.circleincircle. Good 120 .circleincircle. Good 4.13 Ex. 73 26 70
.circleincircle. Good 120 .circleincircle. Good 2.04 PR No.*:
Photoreceptor Number AB*.sup.2: Abrasion quantity of outermost
layer
[0459] As can be understood from Table 4, background fouling and
black streak images tend to be produced when the charging roller
contacts the surface of the photoreceptor. By performing proximity
charging, such problems can be avoided but slightly uneven density
images are produced. The uneven density images can be prevented
when a DC voltage overlapped with an AC voltage is applied to the
charger. When such a DC voltage overlapped with an AC voltage is
applied, the abrasion amount of the photoreceptor increases. The
abrasion problem can be prevented by including zinc stearate in the
developer (toner).
Example 74
[0460] Four pieces of the photoreceptor 26 were set in a tandem
type full color laser printer manufactured by Ricoh Co., Ltd. which
uses a charging roller as a charger and a laser diode emitting
light having a wavelength of 655 nm as an imagewise light source to
perform a 100,000-copy running test. A polytetrafluoroethylene tape
having a thickness of 50 .mu.m was wound around both the edge
portions of the charger to perform proximity charging; a DC voltage
of -750 V overlapped with an AC voltage having a peak-to-peak
voltage of 1.8 kV and a frequency of 2 kHz was applied to the
charger; and zinc stearate was included in the developer in an
amount of 0.1 parts by weight per 100 parts by weight of the
toner.
[0461] The images at the beginning and end of the running test were
evaluated.
Comparative Example 16
[0462] The procedure for image formation in Example 74 was repeated
except that the photoreceptor 26 was replaced with the comparative
photoreceptor 16.
Example 75
[0463] The following undercoat layer coating liquid, CGL coating
liquid, and CTL coating liquid were coated by dip coating on a
nickel seamless belt and dried one by one to form an undercoat
layer having a thickness of 3.5 .mu.m, a CGL having a thickness of
0.2 .mu.m and a CTL having a thickness of 22 .mu.m.
44 Undercoat layer coating liquid Titanium dioxide 400 Melamine
resin 65 Alkyd resin 120 2-butanone 400 CGL coating liquid
Polyvinyl butyral 2 Trisazo pigment having the following formula
(18) 6 29 (18) 2-butanone 120 Cyclohexanone 240 CTL layer coating
liquid Polycarbonate resin 10 (A-form polycarbonate resin from
Teijin Chemical Co., Ltd.) CTM having formula (13) 7 (ionization
potential of 5.4 eV) Tetrahydrofuran 100 Then the following
protective layer coating liquid was coated on the CTL by spray
coating and dried to form a protective layer having a thickness of
about 5 .mu.m. Protective layer coating liquid .alpha.-alumina 2
(SUMICORUNDUM AA-03 from Sumitomo Chemical Co., Ltd., average
primary particle diameter of 0.3 .mu.m) Wetting dispersant 0.06
(BYK-P104 from BYK Chemie, unsaturated polycarboxylic acid polymer
solution, acid value of about 180 mgKOH/g, solid content of about
50%) CTM having formula (13) 4 Polycarbonate resin 6 (A-form
polycarbonate resin from Teijin Chemical Co., Ltd.) Tetrahydrofuran
220 Cyclohexanone 80 Thus a photoreceptor 38 was prepared.
Comparative Example 17
[0464] The procedure for preparation of the photoreceptor 38 was
repeated except that the thickness of the CTL was changed to 27
.mu.m and the protective layer was not formed.
[0465] Thus a comparative photoreceptor 16 was prepared.
[0466] Each of the photoreceptor 38 and comparative photoreceptor
16 was set in a full color copier, modified IPSIO COLOR 5000, using
a laser diode emitting light having a wavelength of 780 nm and an
intermediate transfer medium to perform a 25,000-copy running test.
The images at the beginning and end of the running test were
evaluated.
[0467] The results are shown in Table 5.
45 TABLE 5 Image qualities Photo- Initial 25,000.sup.th receptor
No. image image Ex. 74 Photore- .circleincircle. Good
.circleincircle. Good ceptor 26 Comp. Comp. .circleincircle. Good X
Background fouling Ex. 16 Photore- occurred. Color ceptor 15
reproduction deteriorated. Ex. 75 Photore- .circleincircle. Good
.circleincircle. Good ceptor 38 Comp. Comp. .circleincircle. Good X
Background fouling Ex. 17 Photore- occurred. Resolution ceptor 16
deteriorated.
[0468] As can be understood from Table 5, the photoreceptor of the
present invention can produce images in which the color tones of
the images are well reproduced. However, the comparative
photoreceptor including no filler in the outermost layer produced
images having background fouling. In addition, the comparative
photoreceptor 15 produces color images having poor color
reproducibility, which is caused by deterioration of the
photosensitivity thereof, after long repeated use.
[0469] In addition, when the photoreceptor of the present invention
is used for a full color printer using an intermediate transfer
medium, good full color images can be produced after long repeated
use. When a comparative photoreceptor including no filler in the
outermost layer was used, background fouling was produced and
resolution deteriorated.
[0470] Effects of the Present Invention
[0471] As mentioned above, the residual potential increase problem
of a photoreceptor, which includes a filler in the outermost layer
to enhance its durability, can be prevented by including an organic
compound having an acid value of from 10 to 700 mhKOH/g. Such
organic compounds, particularly wetting dispersants having such a
specific acid value, not only prevent increase of residual
potential but improve dispersion of the filler used together
therewith (i.e., prevent precipitation of the filler). Thereby the
light scattering and uneven abrasion can be prevented and abrasion
resistance can be improved. Therefore a photoreceptor having a high
durability and capable of producing high quality images can be
provided.
[0472] I addition, since occurrence of coating defects can also be
prevented and the coating liquid has long life, the photoreceptor
having a high durability and capable of producing high quality
images can be stably manufactured.
[0473] Further, basic fillers, which have not been used because of
causing the high residual potential problem, can also be used in
the present invention, the blurred image problem can be prevented.
Therefore, an image forming method and apparatus by which high
quality images can be stably produced without using a drum heater
even when repeatedly used for a long period of time and which has
an advantages such that it is hardly necessary to frequently
replace the photoreceptor can be provided.
[0474] This document claims priority and contains subject matter
related to Japanese Patent Applications Nos. 2000-340884,
2000-342902 and 2001-255906, filed on Nov. 8, 2000, Nov. 10, 2000
and Aug. 27, 2001, respectively, incorporated herein by
reference.
[0475] Having now fully described the invention, it will be
apparent to one of ordinary skill in the art that many changes and
modifications can be made thereto without departing from the spirit
and scope of the invention as set forth therein.
* * * * *