U.S. patent application number 10/655345 was filed with the patent office on 2004-06-10 for biological active coating components, coatings, and coated surfaces.
This patent application is currently assigned to REACTIVE SURFACES, LTD.. Invention is credited to McDaniel, C. Steven.
Application Number | 20040109853 10/655345 |
Document ID | / |
Family ID | 34526064 |
Filed Date | 2004-06-10 |
United States Patent
Application |
20040109853 |
Kind Code |
A1 |
McDaniel, C. Steven |
June 10, 2004 |
Biological active coating components, coatings, and coated
surfaces
Abstract
Disclosed herein are novel coatings and paints comprising a
biomolecule composition, wherein the biomolecule composition
comprises a phosphoric triester hydrolase. Also disclosed herein
are methods of detoxification of a surface contaminated with an
organophosphorus compound by contacting the surface with such a
coating or paint. Also disclosed herein are novel coating and paint
components derived from microorganisms.
Inventors: |
McDaniel, C. Steven;
(Austin, TX) |
Correspondence
Address: |
C. Steven McDaniel
McDaniel & Associates, P.C.
P.O. Box 2244
Austin
TX
78767-2244
US
|
Assignee: |
REACTIVE SURFACES, LTD.
|
Family ID: |
34526064 |
Appl. No.: |
10/655345 |
Filed: |
September 4, 2003 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
60409102 |
Sep 9, 2002 |
|
|
|
Current U.S.
Class: |
424/94.6 ;
424/185.1; 424/423; 424/94.63 |
Current CPC
Class: |
A62D 3/02 20130101; C12N
9/16 20130101; C12N 11/16 20130101; A62D 2101/02 20130101; A62D
5/00 20130101; C09D 5/00 20130101; C09D 7/48 20180101; C09J 11/02
20130101; C09D 5/34 20130101; A62D 2101/26 20130101 |
Class at
Publication: |
424/094.6 ;
424/423; 424/094.63; 424/185.1 |
International
Class: |
A61K 038/46; A61K
038/48; A61K 039/00 |
Claims
What is claimed is:
1. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
2. The coating of claim 1, wherein the active biomolecule comprises
a proteinaceous molecule.
3. The coating of claim 2, wherein the proteinaceous molecule binds
a ligand, contacts a living organism, or a combination thereof.
4. The coating of claim 3, wherein the proteinaceous molecule binds
a ligand.
5. The coating of claim 4, wherein the ligand comprises an antigen,
a substrate, an inhibitor, or a combination thereof.
6. The coating of claim 5, wherein the ligand comprises a chemical
toxic to humans.
7. The coating of claim 6, wherein the ligand comprises an
organophosphorus compound.
8. The coating of claim 2, wherein the proteinaceous molecule
comprises a peptide, a polypeptide, a protein, or a combination
thereof.
9. The coating of claim 8, wherein the proteinaceous molecule
comprises an enzyme, an antibody, a receptor, a transport protein,
structural protein, or a combination thereof.
10. The coating of claim 8, wherein the proteinaceous molecule
comprises an enzyme.
11. The coating of claim 10, wherein the enzyme comprises an
oxidoreductase, a transferase, a hydrolase, a lyase, an isomerase,
a ligase, or a combination thereof.
12. The coating of claim 11, wherein the enzyme comprises a
hydrolase.
13. The coating of claim 12, wherein the hydrolase comprises an
esterase.
14. The coating of claim 13, wherein the esterase comprises a
phosphoric triester hydrolase.
15. The coating of claim 14, wherein the phosphoric triester
hydrolase comprises an aryldialkylphosphatase, a
diisopropyl-fluorophosphatase, or a combination thereof.
16. The coating of claim 14, wherein the phosphoric triester
hydrolase comprises a combination of phosphoric triester
hydrolases.
17. The coating of claim 15, wherein the phosphoric triester
hydrolase comprises an aryldialkylphosphatase.
18. The coating of claim 15, wherein the aryldialkylphosphatase
comprises an organophosphorus hydrolase, a human paraoxonase, an
animal carboxylase, or a functional equivalent thereof.
19. The coating of claim 15, wherein the aryldialkylphosphatase
comprises an organophosphorus hydrolase or a functional equivalent
thereof.
20. The coating of claim 19, wherein the organophosphorus hydrolase
comprises an Agrobacterium radiobacter P230 organophosphate
hydrolase, a Flavobacterium balustinum parathion hydrolase, a
Pseudomonas diminuta phosphotriesterase, a Flavobacterium sp opd
gene product, a Flavobacterium sp. parathion hydrolase opd gene
product, or a functional equivalent thereof.
21. The coating of claim 20, wherein the organophosphorus hydrolase
comprises a functional equivalent of Agrobacterium radiobacter P230
organophosphate hydrolase, a Flavobacterium balustinum parathion
hydrolase, a Pseudomonas diminuta phosphotriesterase, a
Flavobacterium sp opd gene product, or a Flavobacterium sp.
parathion hydrolase opd gene product.
22. The coating of claim 21, wherein the functional equivalent is a
structural analog.
23. The coating of claim 22, wherein the structural analog
comprises a Co.sup.2+, Fe.sup.2+, Cu.sup.2+, Mn.sup.2+, Cd.sup.2+,
or Ni.sup.2+ at the enzyme active site.
24. The coating of claim 21, wherein the functional equivalent is a
sequence analog.
25. The coating of claim 21, wherein the sequence analog is an
alteration in sequence length.
26. The coating of claim 24, wherein the sequence analog lacks a
leader peptide sequence.
27. The coating of claim 24, wherein the sequence analog is a
fusion protein.
28. The coating of claim 20, wherein the organophosphorus hydrolase
comprises a Pseudomonas diminuta phosphotriesterase, or a
functional equivalent thereof.
29. The coating of claim 28, wherein the organophosphorus hydrolase
comprises a Pseudomonas diminuta phosphotriesterase.
30. The coating of claim 28, wherein the organophosphorus hydrolase
comprises a Pseudomonas diminuta phosphotriesterase functional
equivalent.
31. The coating of claim 28, wherein the Pseudomonas diminuta
phosphotriesterase functional equivalent comprises a sequence
analog.
32. The coating of claim 31, wherein the sequence analog comprises
an amino acid substitution.
33. The coating of claim 32, wherein the sequence analog is H55C,
H57C, C59A, G60A, S61A, I106A, I106G, W131A, W131F, W131K, F132A,
F132H, F132Y, L136Y, L140Y, H201C, H230C, H254A, H254R, H254S,
H257A, H257L, H257Y, L271A, L271Y, L303A, F306A, F306E, F306H,
F306K, F306Y, S308A, S308G, Y309A, M317A, M317H, M317K, M317R,
H55C/H57C, H55C/H201C, H55C/H230C, H57C/H201C, H57C/H230C,
A80V/S365P, I106A/F132A, I106A/S308A, I106G/F132G, I106G/S308G,
F132Y/F306H, F132H/F306H, F132H/F306Y, F132Y/F306Y, F132A/S308A,
F132G/S308G, L182S/V310A, H201C/H230C, H254R/H257L,
H55C/H57C/H201C, H55C/H57C/H230C, H55C/H201C/H230C,
I106A/F132A/H257Y, I106A/F132A/H257W, I106G/F132G/S308G,
L130M/H257Y/I274N, H257Y/I274N/S365P, H55C/H57C/H201C/H230C,
I106G/F132G/H257Y/S308G, or A14T/A80V/L185R/H257Y/I274N.
34. The coating of claim 17, wherein the aryidialkylphosphatase
comprises a human paraoxonase or a functional equivalent
thereof.
35. The coating of claim 34, wherein the human paraoxonase
comprises an HPON1 gene product or a functional equivalent
thereof.
36. The coating of claim 35, wherein the human paraoxonase
comprises a HPON1 gene product functional equivalent.
37. The coating of claim 28, wherein the HPON1 gene product
functional equivalent comprises a sequence analog.
38. The coating of claim 37, wherein the sequence analog comprises
an amino acid substitution.
39. The coating of claim 38, wherein the sequence analog is E32A,
E48A, E52A, D53A, D88A, D107A, H114N, D121A, H133N, H154N, H160N,
W193A, W193F, W201A, W201F, H242N, H245N, H250N, W253A, W253F,
D273A, W280A, W280F, H284N, or H347N.
40. The coating of claim 17, wherein the aryidialkylphosphatase
comprises an animal carboxylase.
41. The coating of claim 40, wherein the animal carboxylase
comprises an insect carboxylase or a functional equivalent
thereof.
42. The coating of claim 41, wherein the insect carboxylase
comprises a Plodia interpunctella carboxylase, Chrysomya putoria
carboxylase, Lucilia cuprina carboxylase, Musca domestica
carboxylase carboxylase, or a functional equivalent thereof.
43. The coating of claim 15, wherein the phosphoric triester
hydrolase comprises a diisopropyl-fluorophosphatase.
44. The coating of claim 43, wherein the
diisopropyl-fluorophosphatase comprises an organophosphorus acid
anhydrolase, a squid-type DFPase, a Mazur-type DFPase, or a
functional equivalent thereof.
45. The coating of claim 44, wherein the
diisopropyl-fluorophosphatase comprises an organophosphorus acid
anhydrolase or a functional equivalent thereof.
46. The coating of claim 45, wherein the organophosphorus acid
anhydrolase comprises an Altermonas organophosphorus acid
anhydrolase, a prolidase, or a functional equivalent thereof.
47. The coating of claim 46, wherein the organophosphorus acid
anhydrolase comprises an Altermonas organophosphorus acid
anhydrolase or a functional equivalent thereof.
48. The coating of claim 47, wherein the Altermonas
organophosphorus acid anhydrolase comprises an Alteromonas sp JD6.5
organophosphorus acid anhydrolase, an Alteromonas haloplanktis
organophosphorus acid anhydrolase, an Altermonas undina
organophosphorus acid anhydrolase, or a functional equivalent
thereof.
49. The coating of claim 46, wherein the organophosphorus acid
anhydrolase comprises a prolidase or a functional equivalent
thereof.
50. The coating of claim 49, wherein the prolidase comprises a
human prolidase, a Mus musculus prolidase, a Lactobacillus
helveticus prolidase, an Escherichia coli prolidase, an Escherichia
coli aminopeptidase P, or a functional equivalent thereof.
51. The coating of claim 44, wherein the
diisopropyl-fluorophosphatase comprises a squid-type DFPase, or a
functional equivalent thereof.
52. The coating of claim 51, wherein the squid-type DFPase
comprises a Loligo vulgaris DFPase, a Loligo pealei DFPase, a
Loligo opalescens DFPase, or a functional equivalent thereof.
53. The coating of claim 52, wherein the squid-type DFPase
comprises a Loligo vulgaris DFPase, or a functional equivalent
thereof.
54. The coating of claim 53, wherein the squid-type DFPase
comprises a Loligo vulgaris DFPase, or a functional equivalent
thereof.
55. The coating of claim 54, wherein the squid-type DFPase
comprises a Loligo vulgaris DFPase functional equivalent.
56. The coating of claim 55, wherein the Loligo vulgaris DFPase
functional equivalent comprises a sequence analog.
57. The coating of claim 56, wherein the sequence analog comprises
an amino acid substitution.
58. The coating of claim 57, wherein the sequence analog is H181 N,
H224N, H274N, H219N, H248N, or H287N.
59. The coating of claim 57, wherein the sequence analog is an
alteration in sequence length.
60. The coating of claim 59, wherein the sequence analog is a
fusion protein.
61. The coating of claim 44, wherein the
diisopropyl-fluorophosphatase comprises a Mazur-type DFPase or a
functional equivalent thereof.
62. The coating of claim 61, wherein the Mazur-type DFPase
comprises a mouse liver DFPase, a hog kidney DFPase, a Bacillus
stearothermophilus strain OT DFPase, an Escherichia coli DFPase, or
a functional equivalent thereof.
63. The coating of claim 1, wherein the phosphoric triester
hydrolase comprises a Plesiomonas sp. strain M6 mpd gene product, a
Xanthomonas sp. phosphoric triester hydrolase, a Tetrahymena
phosphoric triester hydrolase, or a functional equivalent
thereof.
64. The coating of claim 2, wherein the proteinaceous molecule
contacts a living organism.
65. The coating of claim 64, wherein the proteinaceous molecule
comprises a ligand capable of binding to an active biomolecule of
the living organism.
66. The coating of claim 65, wherein the active biomolecule of the
living organism comprises a receptor, an enzyme, a transport
protein, or a combination thereof.
67. The coating of claim 1, wherein the biomolecular composition
comprises 0.001% to 40% of the coating composition by weight or
volume.
68. The coating of claim 1, wherein the active biomolecule
comprises 0.001% to 40% of the coating composition by weight or
volume.
69. The coating of claim 1, wherein the biomolecule composition
comprises a microorganism based particulate material.
70. The coating of claim 69, wherein the microorganism based
particulate material a whole cell material.
71. The coating of claim 70, wherein the microorganism based
particulate material is a cell fragment microorganism based
particulate material.
72. The coating of claim 1, wherein the coating comprises a
buffer.
73. The coating of claim 21, wherein the buffer comprises a
bicarbonate.
74. The coating of claim 1, wherein the coating is 5 um to 1500 um
thick upon the surface.
75. The coating of claim 1, wherein the coating is 15 um to 500 um
thick upon the surface.
76. The coating of claim 1, wherein the coating comprises a
paint.
77. The coating of claim 1, wherein the coating comprises a clear
coating.
78. The coating of claim 77, wherein the clear coating comprises a
lacquer, a varnish, a shellac, a stain, a water repellent coating,
or a combination thereof.
79. The coating of claim 1, wherein the coating comprises a
multicoat system.
80. The coating of claim 79, wherein the multicoat system comprises
2 to 10 layers.
81. The coating of claim 80, wherein one layer of the multicoat
system comprises the biomolecular composition.
82. The coating of claim 80, wherein a plurality of layers of the
multicoat system comprise the biomolecular composition.
83. The coating of claim 80, wherein each layer of the multicoat
system is coating is 15 um to 150 um thick.
84. The coating of claim 79, wherein the multicoat system comprises
a sealer, a water repellent, a primer, an undercoat, or a
topcoat.
85. The coating of claim 79, wherein the multicoat system comprises
a topcoat.
86. The coating of claim 85, wherein the topcoat comprises the
biomolecular composition.
87. The coating of claim 1, wherein the coating comprises a binder,
a liquid component, a colorant, an additive, or a combination
thereof.
88. The coating of claim 1, wherein the coating undergoes film
formation.
89. The coating of claim 88, wherein film formation occurs at
ambient conditions.
90. The coating of claim 88, wherein film formation occurs at
baking conditions.
91. The coating of claim 90, wherein baking conditions is between
40.degree. C. and 50.degree. C.
92. The coating of claim 90, wherein baking conditions is between
40.degree. C. and 65.degree. C.
93. The coating of claim 90, wherein baking conditions is between
40.degree. C. and 110.degree. C.
94. The coating of claim 88, wherein the coating comprises a
volatile component and a non-volatile component.
95. The coating of claim 94, wherein the coating undergoes film
formation by loss of part of the volatile component.
96. The coating of claim 94, wherein the volatile component
comprises a volatile liquid component.
97. The coating of claim 96, wherein the volatile liquid component
comprises a solvent, a thinner, a diluent, or a combination
thereof.
98. The coating of claim 94, wherein the non-volatile component
comprises a binder, a colorant, a plasticizer, a coating additive,
or a combination thereof.
99. The coating of claim 88, wherein film formation occurs by
crosslinking of a binder.
100. The coating of claim 99, wherein film formation occurs by
crosslinking of a plurality of binders.
101. The coating of claim 88, wherein film formation occurs by
irradiating the coating.
102. The coating of claim 1, wherein the coating produces a
self-cleaning film.
103. The coating of claim 1, wherein the coating is a non-film
forming coating.
104. The coating of claim 103, wherein the non-film forming coating
comprises a non-film formation binder.
105. The coating of claim 103, wherein the non-film forming coating
comprises a coating component in a concentration that is
insufficient to produce a solid film.
106. The coating of claim 105, wherein the coating component
comprises a binder that contributes to thermoplastic film
formation.
107. The coating of claim 105 wherein the coating component
contributes to thermosetting film formation.
108. The coating of claim 107, wherein the coating component
comprises a binder, catalyst, initiator, or combination
thereof.
109. The coating of claim 105, wherein the coating component has a
concentration of 0%.
110. The coating of claim 110, wherein the coating produces a
temporary film.
111. The coating of claim 110, wherein the temporary film has a
poor resistance to a coating remover.
112. The coating of claim 110, wherein the temporary film has a
poor scrub resistance, a poor solvent resistance, a poor water
resistance, a poor weathering property, a poor adhesion property,
or a combination thereof.
113. The coating of claim 1, wherein the coating comprises an
architectural coating, an industrial coating, a specification
coating, or a combination thereof.
114. The coating of claim 1, wherein the coating comprises an
architectural coating.
115. The coating of claim 114, wherein the architectural coating
comprises a wood coating, a masonry coating, an artist's coating,
or a combination thereof.
116. The coating of claim 114, wherein the architectural coating
has a pot life of at least 12 months at ambient conditions.
117. The coating of claim 114, wherein the architectural coating
undergoes film formation at ambient conditions.
118. The coating of claim 1, wherein the coating comprises an
industrial coating.
119. The coating of claim 118, wherein the industrial coating
comprises an automotive coating, a can coating, sealant coating, a
marine coating, or a combination thereof.
120. The coating of claim 119, wherein the industrial coating
undergoes film formation at baking conditions.
121. The coating of claim 1, wherein the coating comprises a
specification coating.
122. The coating of claim 121, wherein the specification coating
comprises a pipeline coating, traffic marker coating, aircraft
coating, a nuclear power plant coating, or a combination
thereof.
123. The coating of claim 1, wherein the coating comprises a
water-borne coating.
124. The coating of claim 123, wherein the water-borne coating is a
latex coating.
125. The coating of claim 123, wherein the water-borne coating has
a density of 1.20 kg/L to 1.50 kg/L.
126. The coating of claim 1, wherein the coating comprises a
solvent-borne coating.
127. The coating of claim 126, wherein the solvent-borne coating
has a density of 0.90 kg/L to 1.2 kg/L.
128. The coating of claim 1, wherein the coating has a viscosity
during application of 72 Ku to 95 Ku.
129. The coating of claim 1, wherein the coating has a viscosity
prior to application of 100 P to 1000 P.
130. The coating of claim 1, wherein the coating has a viscosity
during application of 0.5 P to 2.5 P.
131. The coating of claim 1, wherein the coating has a viscosity of
100 P to 1000 P upon a surface immediately after application.
132. The coating of claim 1, wherein the coating comprises a
binder.
133. The coating of claim 132, wherein the binder comprises a
thermoplastic binder, a thermosetting binder, or a combination
thereof.
134. The coating of claim 133, wherein the coating comprises a
thermoplastic binder.
135. The coating of claim 134, wherein the coating produces a film
by thermoplastic film formation.
136. The coating of claim 133, wherein the coating comprises a
thermosetting binder.
137. The coating of claim 136, wherein the coating produces a film
by thermosetting film formation.
138. The coating of claim 132, wherein the binder comprises an
oil-based binder.
139. The coating of claim 138, wherein the oil-based binder
comprises an oil, an alkyd, an oleoresinous binder, a fatty acid
epoxide ester, or a combination thereof.
140. The coating of claim 139, wherein the coating produces a layer
15 um to 25 .mu.m thick upon the vertical surface or 15 um to 40
.mu.m thick upon the horizontal surface.
141. The coating of claim 132, wherein the binder comprises an
oil.
142. The coating of claim 132, wherein the binder comprises an
alkyd.
143. The coating of claim 132, wherein the binder comprises an
oleoresinous binder.
144. The coating of claim 132, wherein the binder comprises a fatty
acid epoxide ester.
145. The coating of claim 132, wherein the binder comprises a
polyester resin.
146. The coating of claim 145, wherein the polyester resin
comprises a hydroxy-terminated polyester.
147. The coating of claim 145, wherein the polyester resin
comprises a carboxylic acid-terminated polyester.
148. The coating of claim 145, wherein the coating comprises a
urethane, an amino resin, or a combination thereof.
149. The coating of claim 132, wherein the binder comprises a
modified cellulose.
150. The coating of claim 149, wherein the modified cellulose
comprises a cellulose ester.
151. The coating of claim 149, wherein the modified cellulose
comprises a nitrocellulose.
152. The coating of claim 149, wherein the coating comprises an
amino binder, an acrylic binder, urethane binder, or a combination
thereof.
153. The coating of claim 132, wherein the binder comprises a
polyamide.
154. The coating of claim 153, wherein the coating comprises an
epoxide.
155. The coating of claim 132, wherein the binder comprises an
amino resin.
156. The coating of claim 155, wherein the coating comprises an
acrylic binder, an alkyd resin, a polyester binder, or a
combination thereof.
157. The coating of claim 132, wherein the binder comprises an
urethane binder.
158. The coating of claim 157, wherein the coating comprises a
polyol, an amine, an epoxide, a silicone, a vinyl, a phenolic, a
triacrylate, or a combination thereof.
159. The coating of claim 132, wherein the binder comprises a
phenolic resin.
160. The coating of claim 159, wherein the coating comprises an
alkyd resin, an amino resin, a blown oil, an epoxy resin, a
polyamide, a polyvinyl resin, or a combination thereof.
161. The coating of claim 132, wherein the binder comprises an
epoxy resin.
162. The coating of claim 161, wherein the coating comprises an
amino resin a phenolic resin, a polyamide, a ketimine, an aliphatic
amine, or a combination thereof.
163. The coating of claim 161, wherein the epoxy resin comprises a
cycloaliphatic epoxy binder.
164. The coating of claim 163, wherein the coating comprises a
polyol.
165. The coating of claim 132, wherein the binder comprises a
polyhydroxyether binder.
166. The coating of claim 165, wherein the coating comprises an
epoxide, a polyurethane comprising an isocyanate moiety, an amino
resin, or a combination thereof.
167. The coating of claim 132, wherein the binder comprises an
acrylic resin.
168. The coating of claim 167, wherein the coating comprises an
epoxide, a polyurethane comprising an isocyanate moiety, an amino
resin, or a combination thereof.
169. The coating of claim 132, wherein the binder comprises a
polyvinyl binder
170. The coating of claim 169, wherein the coating comprises an
alkyd, an urethane, an amino-resin, or a combination thereof.
171. The coating of claim 132, wherein the binder comprises a
rubber resin.
172. The coating of claim 171, wherein the rubber resin comprises a
chlorinated rubber resin, a synthetic rubber resin, or a
combination thereof.
173. The coating of claim 171, wherein the coating comprises an
acrylic resin, an alkyd resin, a bituminous resin, or a combination
thereof.
174. The coating of claim 132, wherein the binder comprises a
bituminous binder.
175. The coating of claim 174, wherein the coating comprises an
epoxy resin.
176. The coating of claim 132, wherein the binder comprises a
polysulfide binder.
177. The coating of claim 176, wherein the coating comprises a
peroxide, a binder comprising an isocyanate moiety, or a
combination thereof.
178. The coating of claim 132, wherein the binder comprises a
silicone binder.
179. The coating of claim 178, wherein the coating comprises an
organic binder.
180. The coating of claim 1, wherein the coating comprises a liquid
component.
181. The coating of claim 180, wherein the liquid component
comprises a solvent, a thinner, a diluent, a plasticizer, or a
combination thereof.
182. The coating of claim 180, wherein the liquid component
comprises a liquid organic compound, an inorganic compound, water,
or a combination thereof.
183. The coating of claim 180, wherein the liquid component
comprises a liquid organic compound.
184. The coating of claim 183, wherein the liquid organic compound
comprises a hydrocarbon, an oxygenated compound, a chlorinated
hydrocarbon, a nitrated hydrocarbon, a miscellaneous organic liquid
component, a plasticizer, or a combination thereof.
185. The coating of claim 184, wherein the liquid organic compound
comprises a hydrocarbon.
186. The coating of claim 185, wherein the hydrocarbon comprises an
aliphatic hydrocarbon, a cycloaliphatic hydrocarbon, a terpene, an
aromatic hydrocarbon, or a combination thereof.
187. The coating of claim 186, wherein the hydrocarbon comprises an
aliphatic hydrocarbon.
188. The coating of claim 187, wherein the aliphatic hydrocarbon
comprises a petroleum ether, pentane, hexane, heptane, isododecane,
a kerosene, a mineral spirit, a VMP naphthas, or a combination
thereof.
189. The coating of claim 186, wherein the hydrocarbon comprises a
cycloaliphatic hydrocarbon.
190. The coating of claim 189, wherein the cycloaliphatic
hydrocarbon comprises cyclohexane, methylcyclohexane,
ethylcyclohexane, tetrahydronaphthalene, decahydronaphthalene, or a
combination thereof.
191. The coating of claim 186, wherein the hydrocarbon comprises a
terpene.
192. The coating of claim 191, wherein the terpene comprises wood
terpentine oil, pine oil, .alpha.-pinene, .beta.-pinene, dipentene,
D-limonene, or a combination thereof.
193. The coating of claim 186, wherein the hydrocarbon comprises an
aromatic hydrocarbon.
194. The coating of claim 193, wherein the aromatic hydrocarbon
comprises benzene, toluene, ethylbenzene, xylene, cumene, a type I
high flash aromatic naphthas, a type II high flash aromatic
naphthas, mesitylene, pseudocumene, cymol, styrene, or a
combination thereof.
195. The coating of claim 184, wherein the liquid organic compound
comprises an oxigenated compound.
196. The coating of claim 195, wherein the oxigenated compound
comprises an alcohol, an ester, a glycol ether, a ketone, an ether,
or a combination thereof.
197. The coating of claim 196, wherein the oxigenated compound
comprises an alcohol.
198. The coating of claim 197, wherein the alcohol comprises
methanol, ethanol, propanol, isopropanol, 1-butanol, isobutanol,
2-butanol, tert-butanol, amyl alcohol, isoamyl alcohol, hexanol,
methylisobutylcarbinol, 2-ethylbutanol, isooctyl alcohol,
2-ethylhexanol, isodecanol, cylcohexanol, methylcyclohexanol,
trimethylcyclohexanol, benzyl alcohol, methylbenzyl alcohol,
furfuryl alcohol, tetrahydrofurfuryl alcohol, diacetone alcohol,
trimethylcyclohexanol, or a combination thereof.
199. The coating of claim 196, wherein the oxigenated compound
comprises an ester.
200. The coating of claim 199, wherein the ester comprises methyl
formate, ethyl formate, butyl formate, isobutyl formate, methyl
acetate, ethyl acetate, propyl acetate, isopropyl acetate, butyl
acetate, isobutyl acetate, sec-butyl acetate, amyl acetate, isoamyl
acetate, hexyl acetate, cyclohexyl acetate, benzyl acetate, methyl
glycol acetate, ethyl glycol acetate, butyl glycol acetate, ethyl
diglycol acetate, butyl diglycol acetate, 1-methoxypropyl acetate,
ethoxypropyl acetate, 3-methoxybutyl acetate, ethyl
3-ethoxypropionate, isobutyl isobutyrate, ethyl lactate, butyl
lactate, butyl glycolate, dimethyl adipate, glutarate, succinate,
ethylene carbonate, propylene carbonate, butyrolactone, or a
combination thereof.
201. The coating of claim 196, wherein the oxigenated compound
comprises a glycol ether.
202. The coating of claim 201, wherein the glycol ether comprises
methyl glycol, ethyl glycol, propyl glycol, isopropyl glycol, butyl
glycol, methyl diglycol, ethyl diglycol, butyl diglycol, ethyl
triglycol, butyl triglycol, diethylene glycol dimethyl ether,
methoxypropanol, isobutoxypropanol, isobutyl glycol, propylene
glycol monoethyl ether, 1-isopropoxy-2-propanol, propylene glycol
mono-n-propyl ether, propylene glycol n-butyl ether, methyl
dipropylene glycol, methoxybutanol, or a combination thereof.
203. The coating of claim 196, wherein the oxigenated compound
comprises a ketone.
204. The coating of claim 203, wherein the ketone comprises
acetone, methyl ethyl ketone, methyl propyl ketone, methyl
isopropyl ketone, methyl butyl ketone, methyl isobutyl ketone,
methyl amyl ketone, methyl isoamyl ketone, diethyl ketone, ethyl
amyl ketone, dipropyl ketone, diisopropyl ketone, cyclohexanone,
methylcylcohexanone, trimethylcyclohexanone, mesityl oxide,
diisobutyl ketone, isophorone, or a combination thereof.
205. The coating of claim 196, wherein the oxigenated compound
comprises an ether.
206. The coating of claim 205, wherein the ether comprises diethyl
ether, diisopropyl ether, dibutyl ether, di-sec-butyl ether, methyl
tert-butyl ether, tetrahydrofuran, 1,4-dioxane, metadioxane, or a
combination thereof.
207. The coating of claim 184, wherein the liquid organic compound
comprises a chlorinated hydrocarbon.
208. The coating of claim 207, wherein the chlorinated hydrocarbon
comprises methylene chloride, trichloromethane, tetrachloromethane,
ethyl chloride, isopropyl chloride, 1,2-dichloroethane,
1,1,1-trichloroethane, trichloroethylene, 1,1,2,2-tetrachlorethane,
1,2-dichloroethylene, perchloroethylene, 1,2-dichloropropane,
chlorobenzene, or a combination thereof.
209. The coating of claim 184, wherein the liquid organic compound
comprises a nitrated hydrocarbon.
210. The coating of claim 209, wherein the nitrated hydrocarbon
comprises a nitroparaffin, N-methyl-2-pyrrolidone, or a combination
thereof.
211. The coating of claim 184, wherein the liquid organic compound
comprises a miscellaneous organic liquid.
212. The coating of claim 209, wherein the miscellaneous organic
liquid comprises carbon dioxide; acetic acid, methylal,
dimethylacetal, N,N-dimethylformamide, N,N-dimethylacetamide,
dimethylsulfoxide, tetramethylene suflone, carbon disulfide,
2-nitropropane, N-methylpyrrolidone, hexamethylphosphoric triamide,
1,3-dimethyl-2-imidazolidinone, or a combination thereof.
213. The coating of claim 184, wherein the liquid organic compound
comprises a plasticizer.
214. The coating of claim 213, wherein the plasticizer comprises an
adipate, an azelate, a citrate, a chlorinated plasticizer, an
epoxide, a phosphate, a sebacate, a phthalate, a polyester, a
trimellitate, or a combination thereof.
215. The coating of claim 180, wherein the liquid component
comprises an inorganic compound.
216. The coating of claim 215, wherein the inorganic compound
comprises ammonia, hydrogen cyanide, hydrogen fluoride, hydrogen
cyanide, sulfur dioxide, or a combination thereof.
217. The coating of claim 180, wherein the liquid component
comprises water.
218. The coating of claim 217, wherein the liquid component further
comprises methanol, ethanol, propanol, isopropyl alcohol,
tert-butanol, ethylene glycol, methyl glycol, ethyl glycol, propyl
glycol, butyl glycol, ethyl diglycol, methoxypropanol,
methyldipropylene glycol, dioxane, tetrahydorfuran, acetone,
diacetone alcohol, dimethylformamide, dimethyl sulfoxide,
ethylbenzene, tetrachloroethylene, p-xylene, toluene, diisobutyl
ketone, tricholorethylene, trimethylcyclohexanol, cyclohexyl
acetate, dibutyl ether, trimethylcyclohexanone,
1,1,1-tricholoroethane, hexane, hexanol, isobutyl acetate, butyl
acetate, isophorone, nitropropane, butyl glycol acetate,
2-nitropropane, methylene chloride, methyl isobutyl ketone,
cyclohexanone, isopropyl acetate, methylbenzyl alcohol,
cyclohexanol, nitroethane, methyl tert-butyl ether, ethyl acetate,
diethyl ether, butanol, butyl glycolate, isobutanol, 2-butanol,
propylene carbonate, ethyl glycol acetate, methyl acetate, methyl
ethyl ketone, or a combination thereof.
219. The coating of claim 87, wherein the coating comprises a
colorant.
220. The coating of claim 219, wherein the colorant comprises a
pigment, a dye, a combination thereof.
221. The coating of claim 220, wherein the colorant comprises a
pigment.
222. The coating of claim 221, wherein the biomolecule composition
comprises 0.001% to 100% of the pigment.
223. The coating of claim 222, wherein the pigment volume
concentration of the coating is 20% to 60%.
224. The coating of claim 221, wherein the pigment comprises a
corrosion resistance pigment, a camouflage pigment, a color
property pigment, an extender pigment, or a combination
thereof.
225. The coating of claim 224, wherein the pigment comprises a
corrosion resistance pigment.
226. The coating of claim 225, wherein the corrosion resistance
pigment comprises aluminum flake, aluminum triphosphate, aluminum
zinc phosphate, ammonium chromate, barium borosilicate, barium
chromate, barium metaborate, basic calcium zinc molybdate, basic
carbonate white lead, basic lead silicate, basic lead
silicochromate, basic lead silicosulfate, basic zinc molybdate,
basic zinc molybdate-phosphate, basic zinc molybdenum phosphate,
basic zinc phosphate hydrate, bronze flake, calcium barium
phosphosilicate, calcium borosilicate, calcium chromate, calcium
plumbate, calcium strontium phosphosilicate, calcium strontium zinc
phosphosilicate, dibasic lead phosphite, lead chromosilicate, lead
cyanamide, lead suboxide, lead sulfate, mica, micaceous iron oxide,
red lead, steel flake, strontium borosilicate, strontium chromate,
tribasic lead phophosilicate, zinc borate, zinc borosilicate, zinc
chromate, zinc dust, zinc hydroxy phosphite, zinc molybdate, zinc
oxide, zinc phosphate, zinc potassium chromate, zinc
silicophosphate hydrate, zinc tetraoxylchromate, or a combination
thereof.
227. The coating of claim 225, wherein the coating is a metal
surface coating.
228. The coating of claim 225, wherein the coating is a primer.
229. The coating of claim 224, wherein the pigment comprises a
camouflage pigment.
230. The coating of claim 229, wherein the camouflage pigment
comprises an anthraquinone black, a chromium oxide green, or a
combination thereof.
231. The coating of claim 224, wherein the pigment comprises a
color property pigment.
232. The coating of claim 231, wherein the color property pigment
comprises a black pigment, a brown pigment, a white pigment, a
pearlescent pigment, a violet pigment, a blue pigment, a green
pigment, a yellow pigment, an orange pigment, a red pigment, a
metallic pigment, or a combination thereof.
233. The coating of claim 232, wherein the color property pigment
comprises aniline black; anthraquinone black; carbon black; copper
carbonate; graphite; iron oxide; micaceous iron oxide; manganese
dioxide, azo condensation, benzimidazolone, iron oxide; metal
complex brown; antimony oxide; basic lead carbonate; lithopone;
titanium dioxide; white lead; zinc oxide; zinc sulphide; titanium
dioxide and ferric oxide covered mica, bismuth oxychloride crystal
dioxanine violet, carbazol Blue; carbazole Blue; cobalt blue;
copper phthalocyanine; dioxanine Blue; indanthrone; phthalocyanin
blue; Prussian blue; ultramarine; chrome green; chromium oxide
green; halogenated copper phthalocyanine; hydrated chromium oxide;
phthalocyanine green; anthrapyrimidine; arylamide yellow; barium
chromate; benzimidazolone yellow; bismuth vanadate; cadmium sulfide
yellow; complex inorganic color pigment; diarylide yellow; disazo
condensation; flavanthrone; isoindoline; isoindolinone; lead
chromate; nickel azo yellow; organic metal complex; quinophthalone;
yellow iron oxide; yellow oxide; zinc chromate; perinone orange;
pyrazolone orange; anthraquinone; benzimidazolone; BON arylamide;
cadmium red; cadmium selenide; chrome red; dibromanthrone;
diketopyrrolo-pyrrole pigment; disazo condensation pigment; lead
molybdate; perylene; pyranthrone; quinacridone; quinophthalone; red
iron oxide; red lead; toluidine red; tonor pigment; .beta.-naphthol
red; aluminum flake; aluminum non-leafing, gold bronze flake, zinc
dust, stainless steel flake, nickel flake, nickel powder, or a
combination thereof.
234. The coating of claim 224, wherein the pigment comprises an
extender pigment.
235. The coating of claim 234, wherein the extender pigment
comprises a barium sulphate, a calcium carbonate, a kaolin, a
calcium sulphat, a silicate, a silica, an alumina trihydrate; or a
combination thereof.
236. The coating of claim 87, wherein the coating comprises an
additive.
237. The coating of claim 236, wherein the additive comprises
0.001% to 20.0% by weight, of the coating.
238. The coating of claim 236, wherein said additive comprises an
accelerator, an adhesion promoter, an antifoamer, anti-insect
additive, an antioxidant, an antiskinning agent, a buffer, a
catalyst, a coalescing agent, a corrosion inhibitor, a defoamer, a
dehydrator, a dispersant, a drier, electrical additive, an
emulsifier, a filler, a flame/fire retardant, a flatting agent, a
flow control agent, a gloss aid, a leveling agent, a marproofing
agent, a preservative, a silicone additive, a slip agent, a
surfactant, a light stabilizer, a rheological control agent, a
wetting additive, or a combination thereof.
239. The coating of claim 236, wherein the additive comprises a
preservative.
240. The coating of claim 239, wherein the preservative comprises
an in-can preservative, an in-film preservative, or a combination
thereof.
241. The coating of claim 239, wherein the preservative comprises a
biocide.
242. The coating of claim 241, wherein the biocide comprises a
bactericide, a fungicide, an algaecide, or a combination
thereof.
243. The coating of claim 236, wherein the additive comprises a
wetting additive, a dispersant, or a combination thereof.
244. The coating of claim 236, wherein the additive comprises an
anti-foamer, a defoamer, or a combination thereof.
245. The coating of claim 238, wherein the additive comprises a
rheological control agent.
246. The coating of claim 245, wherein the rheological control
agent comprises a thickener, a viscosifier, or a combination
thereof.
247. The coating of claim 238, wherein the additive comprises a
corrosion inhibitor.
248. The coating of claim 247, wherein said corrosion inhibitor
comprises an in-can corrosion inhibitor, a flash corrosion
inhibitor, or a combination thereof.
249. The coating of claim 238, wherein the additive comprises a
light stabilizer.
250. The coating of claim 249, wherein the light stabilizer
comprises a UV absorber, a radical scavenger, or a combination
thereof.
251. The coating of claim 1, wherein the coating is a multi-pack
coating.
252. The coating of claim 251, wherein the coating is stored in a
two to five containers prior to application to the surface.
253. The coating of claim 251, wherein 0.001% to 100% of the
biomolecular composition is stored in a container of a multi-pack
coating, and at least one additional coating component is stored in
another container of a multi-pack coating.
254. The coating of claim 253, wherein the container comprising the
biomolecular composition further comprises an additional coating
component.
255. The coating of claim 254, wherein the additional coating
component comprises a preservative, a wetting agent, a dispersing
agent, a buffer, a liquid component, a rheological modifier, or a
combination thereof.
256. The coating of claim 255, wherein the additional coating
component comprises glycerol.
257. A method of detoxification of a surface contaminated with an
organophosphorus compound, comprising the steps of: contacting a
surface contaminated with an organophosphorous compound with a
coating comprising a biomolecule composition, wherein the
biomolecule composition comprises a phosphoric triester
hydrolase.
258. The method of claim 257, wherein said organophosphorus
compound comprises a chemical warfare agent.
259. The method of claim 258, wherein the chemical warfare agent
comprises a persistent agent.
260. The method of claim 258, wherein the chemical warefare agent
comprises a G-agent, a V agent, or a combination thereof.
261. The method of claim 260, wherein said G-agent comprises soman,
sarin, cyclosarin, tabun, or a combination thereof.
262. The method of claim 260, wherein said V-agent comprises VX,
Russian VX, or a combination thereof.
263. The method of claim 257, wherein said organophosphorus
compound comprises a pesticide.
264. The method of claim 263, wherein the pesticide comprises a
persistent organophosphorous compound.
265. The method of claim 258, wherein the pesticide comprises
bromophos-ethyl, chlorpyrifos, chlorfenvinphos, chlorothiophos,
chlorpyrifos-methyl, coumaphos, crotoxyphos, crufomate, cyanophos,
diazinon, dichlofenthion, dichlorvos, dursban, EPN, ethoprop,
ethyl-parathion, etrimifos, famphur, fensulfothion, fenthion,
fenthrothion, isofenphos, jodfenphos, leptophos-oxon, malathion,
methyl-parathion, mevinphos, paraoxon, parathion, parathion-methyl,
pirimiphos-ethyl, pirimiphos-methyl, pyrazophos, quinalphos,
ronnel, sulfopros, sulfotepp, trichloronate, or a combination
thereof.
266. The method of claim 257, wherein the method further comprises
the step of contacting the surface with a caustic agent; a
decontaminating foam, a combination of baking condition heat and
carbon dioxide, or a combination thereof.
267. A method of detoxification of an organophosphorus compound,
comprising the steps of: contacting an organophosphorous compound
with a coating comprising a biomolecule composition, wherein the
biomolecule composition comprises a phosphoric triester
hydrolase.
268. A method of reducing the concentration of an organophosphorus
compound upon a surface, comprising the steps of: applying to the
surface a coating comprising a biomolecule composition, wherein the
biomolecule composition comprises a phosphoric triester hydrolase,
and contacting the surface with an organophosphorus compound.
269. A coating comprising 0.001% to 40% by weight or volume a
biomolecule composition, wherein the biomolecule composition
comprises an active biomolecule.
270. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises a proteinaceous molecule that
binds a ligand.
271. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises an enzyme.
272. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises a phosphoric triester
hydrolase.
273. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises an organophosphorus
hydrolase.
274. A coating comprising a biomolecule composition, wherein the
biomolecule composition comprises an organophosphorus hydrolase and
a buffer.
275. A coating comprising a microorganism based particulate
material, wherein the microorganism based particulate material that
comprises an active biomolecule.
276. A coating comprising a whole cell particulate material,
wherein the particulate material comprises an active
biomolecule.
277. A coating comprising 0.001% to 40% by weight or volume of a
whole cell particulate material, wherein the whole cell particulate
material comprises an active biomolecule.
278. A coating comprising a whole cell particulate material,
wherein the particulate material comprises an enzyme.
279. A coating comprising a whole cell particulate material,
wherein the particulate material comprises a phosphoric triester
hydrolase.
280. A coating comprising a whole cell particulate material,
wherein the particulate material comprises an organophosphorus
hydrolase.
281. A coating comprising a whole cell particulate material,
wherein the particulate material comprises an organophosphorus
hydrolase and a buffer.
282. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises an active biomolecule.
283. A coating, the improvement comprising inclusion of 0.001% to
40% by weight or volume a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
284. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises a proteinaceous molecule that binds a ligand.
285. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises an enzyme.
286. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises a phosphoric triester hydrolase.
287. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises an organophosphorus hydrolase.
288. A coating, the improvement comprising inclusion of a
biomolecule composition, wherein the biomolecule composition
comprises an organophosphorus hydrolase and a buffer.
289. A coating, the improvement comprising inclusion of a
microorganism based particulate material, wherein the microorganism
based particulate material that comprises an active
biomolecule.
290. A coating, the improvement comprising inclusion of a whole
cell particulate material, wherein the particulate material
comprises an active biomolecule.
291. A coating, the improvement comprising inclusion of 0.001% to
40% by weight or volume of a whole cell particulate material,
wherein the whole cell particulate material comprises an active
biomolecule.
292. A coating, the improvement comprising inclusion of a whole
cell particulate material, wherein the particulate material
comprises an enzyme.
293. A coating, the improvement comprising inclusion of a whole
cell particulate material, wherein the particulate material
comprises a phosphoric triester hydrolase.
294. A coating, the improvement comprising inclusion of a whole
cell particulate material, wherein the particulate material
comprises an organophosphorus hydrolase.
295. A coating, the improvement comprising inclusion of a whole
cell particulate material, wherein the particulate material
comprises an organophosphorus hydrolase and a buffer.
296. A water-borne paint comprising a biomolecule composition,
wherein the biomolecule composition comprises an active
biomolecule.
297. A solvent-borne paint comprising a biomolecule composition,
wherein the biomolecule composition comprises an active
biomolecule.
298. A latex paint comprising a whole cell particulate material,
wherein the whole cell particulate material comprises a phosphoric
triester hydrolase.
299. An oil-based paint comprising a whole cell particulate
material, wherein the whole cell particulate material comprises a
phosphoric triester hydrolase.
300. A latex paint comprising a whole cell particulate material and
a buffer, wherein the whole cell particulate material comprises a
phosphoric triester hydrolase.
301. An oil-based paint comprising a whole cell particulate
material and a buffer, wherein the whole cell particulate material
comprises a phosphoric triester hydrolase.
302. An latex paint comprising 0.001% to 40% by weight or volume of
a whole cell particulate material, wherein the whole cell
particulate material comprises a phosphoric triester hydrolase.
303. An oil-based paint comprising 0.001% to 40% by weight or
volume of a whole cell particulate material, wherein the whole cell
particulate material comprises a phosphoric triester hydrolase.
304. A multi-pack latex paint, wherein one container comprises
0.001% to 40%, by weight or volume of the paint, a whole cell
particulate material, wherein the whole cell particulate material
comprises a phosphoric triester hydrolase.
305. A multi-pack oil-based paint, wherein one container comprises
0.001% to 40%, by weight or volume of the paint, a whole cell
particulate material, wherein the whole cell particulate material
comprises a phosphoric triester hydrolase.
306. A multi-pack latex paint, wherein one container comprises
0.001% to 40%, by weight or volume of the paint, a whole cell
particulate material, wherein the whole cell particulate material
comprises a phosphoric triester hydrolase, and wherein the
container comprising the whole cell particulate material further
comprises a preservative, a wetting agent, a dispersing agent, a
buffer, a liquid component, a rheological modifier, or a
combination thereof.
307. A multi-pack oil-based paint, wherein one container comprises
0.001% to 40%, by weight or volume of the paint, a whole cell
particulate material, wherein the whole cell particulate material
comprises a phosphoric triester hydrolase, and wherein the
container comprising the whole cell particulate material further
comprises a preservative, a wetting agent, a dispersing agent, a
buffer, a liquid component, a rheological modifier, or a
combination thereof.
308. A two-pack latex paint, wherein one container comprises 100
parts by volume paint, wherein a second container comprises three
parts by volume of a biomolecular composition comprising a whole
cell particulate material, wherein the whole cell particulate
material comprises an organophosphorus hydrolase, and wherein each
part of the biomolecular composition comprises 1 mg of whole cell
particulate material and 50% glycerol.
309. An two-pack oil-based paint, wherein one container comprises
100 parts by volume paint, wherein a second container comprises
three parts by volume of a biomolecular composition comprising a
whole cell particulate material, wherein the whole cell particulate
material comprises an organophosphorus hydrolase, and wherein each
part of the biomolecular composition comprises 1 mg of whole cell
particulate material and 50% glycerol.
310. A two-pack latex paint, wherein one container comprises 100
parts by volume paint, wherein a second container comprises three
parts by volume of a biomolecular composition comprising a whole
cell particulate material, wherein the whole cell particulate
material comprises an organophosphorus hydrolase, wherein each part
of the biomolecular composition comprises 1 mg of whole cell
particulate material, wherein the paint comprises a buffer, and
wherein the buffer comprises ammonium bicarbonate, a monobasic
buffer, a dibasic phosphate buffer, Trizma base, a five
zwitterionic buffer, or a combination thereof.
311. An two-pack oil-based paint, wherein one container comprises
100 parts by volume paint, wherein a second container comprises
three parts by volume of a biomolecular composition comprising a
whole cell particulate material, wherein the whole cell particulate
material comprises an organophosphorus hydrolase, wherein each part
of the biomolecular composition comprises 1 mg per mililiter of
whole cell particulate material, wherein the paint comprises a
buffer, and wherein the buffer comprises ammonium bicarbonate, a
monobasic buffer, a dibasic phosphate buffer, Trizma base, a five
zwitterionic buffer, or a combination thereof.
312. A non-film forming coating comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
313. An elastomer comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
314. A filler comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
315. An adhesive comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
316. A sealant comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
317. A material applied to a textile, comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
318. A wax comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
319. A surface treatment comprising a biomolecule composition,
wherein the biomolecule composition comprises an active
biomolecule.
320. A surface treatment of claim 319, wherein the surface
treatment is a coating, a paint, a non-film forming coating, an
elastomer, an adhesive, an sealant, a material applied to a
textile, or a wax.
321. The surface treatment of claim 320, wherein the surface
treatment comprises a pH indicator.
Description
[0001] This application claims the benefit of Provisional Patent
Application Entitled "Bioactive Protein Paint Additive, Paint, and
Painted Various," Ser. No. 60/409,102, filed Sep. 9, 2002,
incorporated herein in its entirety by reference.
BACKGROUND OF THE INVENTION
[0002] A. Field of the Invention
[0003] The present invention relates generally to the field of
biological molecules as components of coatings conferring an
activity or other advantage to the coating proteinaceous molecule
related to the biological molecule. More specifically, the present
invention relates to proteins as such components of coatings. In
one specific regard, the present invention relates to protein
compositions capable of organophosphorus detoxification, and
methods of reducing organophosphorus compounds on surfaces. More
specifically, the present invention relates to coatings such as
paints that degrade organophosphorus compounds such as pesticides
and chemical warfare agents. The present invention further relates
to paint and coating compositions and methods of their use to
detoxify organophosphorus chemical warfare agents.
[0004] B. Description of the Related Art
[0005] Organophosphorus compounds ("organophosphate compounds" or
"OP compounds") and organosulfur ("OS") compounds are used
extensively as insecticides and are highly toxic to many organisms,
including humans. OP compounds function as nerve agents. The
primary effects of exposure to these agents are very similar,
including inhibition of acetylcholinesterase and
butyrylcholinesterase, with the subsequent breakdown of the normal
operation of the autonomic and central nervous systems (Gallo and
Lawryk, 1991).
[0006] Over 40 million kilograms of OP pesticides are used in the
United States annually (Mulchandani, A. et al., 1999a). The number
of people accidentally poisoned by OP pesticides has been estimated
to be upwards of 500,000 persons a year (LeJeune, K. E. et al.,
1998). Depending on the toxicity to the organism (e.g., humans),
repeated, prolonged and/or low-dose exposure to an OP compound can
cause neurotoxicity and delayed cholinergic toxicity. High-dose
exposure can produces a fatal response (Tuovinen, K. et al.,
1994).
[0007] Arguably of greater danger to humans, however, is the fact
that some of the most toxic OP compounds are used as chemical
warfare agents ("CWA"). Chemical warfare agents are classified into
G agents, such as GD ("soman"), GB ("sarin"), GF ("cyclosarin") and
GA ("tabun"), and the methyl phosphonothioates, commonly known as V
agents, such as VX and Russian VX ("R-VX" or "VR"). The most
important CWAs are as follows: tabun (O-methyl
dimethylamidophosphorylcyanide), which is the easiest to
manufacture; sarin ("isopropyl methylphosphonofluoridate"), which
is a volatile substance mainly taken up through inhalation; soman
("pinacolyl methylphosphonofluoridate"), a moderately volatile
substance that can be taken up by inhalation or skin contact;
cyclosarin ("cyclohexyl methylphosphonofluoridate"), a substance
with low volatility that is taken up through skin contact and
inhalation of the substance as a gas or aerosol; and VX ("O-ethyl
S-diisopropylaminomethyl methylphosphonothioate") and its isomeric
analog R-VX ["O-isobutyl S-(2-diethylamino)-methylphosphonothioate,
R-VX or VR"], both of which can remain on material, equipment and
terrain for long periods, such as weeks, with R-VX being an
especially persistent substance. All CWAs are colorless liquids
with volatility varying from VX to sarin. VX is an involatile
oil-like liquid, while sarin is a water-like, easily volatilized
liquid. By addition of a thickener (e.g., a variety of carbon
polymers), soman or other more volatile agents may be made to be
less volatile and more persistent.
[0008] The CWAs are extremely toxic and have a rapid effect. Such
agents enter the body through any of the following manners:
inhalation, direct contact to the skin with a gas or with a
contaminated surface, or through ingestion of contaminated food or
drink. The poisoning effect takes longer when the agents enter
through the skin, but is much faster when they are inhaled because
of the rapid diffusion in the blood from the lungs. These toxins
are fat-soluble and can penetrate the skin, but take longer to
reach the deep blood vessels. Because of this, the first symptoms
may not appear for 20-30 minutes after initial contact with a
contaminated surface. This increases the danger for personnel
entering a contaminated area, because the contamination may not be
detected for 30 minutes or more (depending on concentrations) after
the contaminated area is entered.
[0009] The first and most important method of protection from nerve
agents is to prevent exposure. For military personnel and other
first responders, masks and full body protective gear are
available, but this equipment has certain drawbacks. Impermeable
suits and even some air permeable suits are bulky and hot. The
equipment inhibits free movement and tasks are harder and take
longer to complete. In addition to those factors, hard physical
work in these suits this may cause heat stress or even collapse.
There may also be long delays before decontamination can be
completed so the protective gear must be worn for long periods.
This makes for a marginally acceptable first defense against a
chemical warfare agent attack. Decontamination is also
time-consuming so the equipment must often be destroyed and new
equipment provided. It is also difficult to provide everyone with
such protective equipment in the general population, and the
effectiveness of such equipment diminishes during use. Tasks
requiring detailed work using fingers and hands such as keystrokes
on a keyboard, or pushing buttons on phones or equipment can be
severely hampered by such bulky protective gear.
[0010] In addition to direct contact with a gaseous agent during an
attack, surfaces that are exposed to the gas retain their toxicity
for long periods of time. The OP nerve agents are soluble in
materials such as paint, plastics, and rubber, allowing agents to
remain in those materials and be released over long time periods.
Nerve agents with thickening agents are even more persistent and
difficult to decontaminate from a painted surface such as a wall,
vehicle, or even a computer keyboard. It is understood that on
painted metal surfaces, soman may persist for from one to five
days, and that the less volatile VX may persist for 12 to 15 days.
Under certain environmental conditions, OP compounds have been
shown to persist indefinitely. On surfaces that are convoluted such
as the surface of a military vehicle, the hidden surfaces that are
less exposed to the environment can be especially difficult to
decontaminate. Decontamination also requires detection, which is
often not possible, and so resources and time may be wasted
treating uncontaminated surfaces.
[0011] Historically, most approaches to chemical agent
decontamination have focused on the treatment of surfaces after
chemical exposure, whether real or merely suspected, has occurred.
There are several current methods of decontamination of surfaces.
One method is post-exposure washing with hot water with or without
addition of detergents or organic solvents, such as caustic
solutions (e.g., DS2, bleach) or foams (e.g., Eco, Sandia, Decon
Green). Additional types of methods are anapplication of use of
intensive heat and carbon dioxide applied for sustained periods,
and incorporation of oxidizing materials (e.g., TiO.sub.2 and
porphyrins) into coatings that, when exposed to sustained high
levels of UV light, degrade chemical agents (Buchanan, J. H. et
al., 1989; Fox, M. A., 1983). Chemical agent resistant coatings
("CARCs") have been developed to withstand repeated decontamination
efforts with such caustize and organic solvents. However, the
resulting "decontaminated" materials are often still contaminated.
Moreover, many decontamination procedures aerosolize contaminants
on surfaces to be cleaned. In addition, it is often hard to clean
certain kinds of surfaces such as those with rough texture, or with
deep crevasses and other hard to reach areas that must often
"self-decontaminate."
[0012] Although each of these approaches can be effective under
specific conditions, a number of additional limitations exist.
Caustic solutions degrade surfaces, create personnel handling and
environmental risks, and require transport and mixing logistics.
Additionally, alkaline solutions, such as a bleaching agent, is
both relatively slow in chemically degrading VX OPs and can produce
decontamination products nearly as toxic as the OP itself (Yang,
Y.-C. et al., 1990). While foams may have both non-specific
biocidal and chemical decontamination properties, they require
transport and mixing logistics, may have personnel handling and
environmental risks, and are not effective on sensitive electronic
equipment or interior spaces. CARCs have been shown to become
porous after sustained UV light exposure that can create a sponge
effect that may actually trap chemical agents and delay
decontamination. Moreover, these approaches are not well suited for
decontamination of convoluted surfaces. Decontamination with heat
and carbon dioxide presents logistical requirements and does not
allow rapid reclamation of equipment. UV-based approaches can be
costly and have logistical requirements, including access to
UV-generating equipment and power, as well as the production of
toxic byproducts of degradation (Yang, Y.-C. et al., 1992;
Buchanan, J. H. et al., 1989; Fox, M. A., 1983).
[0013] One attempted solution to the problem of surface
contamination has been to provide paints with shedding ("chalking")
properties such as an acrylic surface that may shed, or at least
not be penetrated by a CWA, making decontamination easier. This has
been unsatisfactory solution, however, because the area remains
contaminated and there is no way to know if the surface is or is
not poisonous. In addition, shedding coatings over existing painted
surfaces require additional materials and labor over a single
coating. Shedding may or may not occur over timeframes necessary to
protect personnel from residual nerve agents on contaminated
surfaces, and in many instances may require washing despite the
shedding characteristic.
[0014] Various enzymes have been identified that detoxify OP
compounds, such as organophosphorus hydrolase ("OPH"),
organophosphorus acid anhydrolase ("OPAA"), and DFPase, which
detoxifies O,O-diisopropyl phosphorofluoridate ("DFP"). A number of
civilian (e.g., Texas A&M University, private sector), and
military laboratories [e.g., the Army research facilities at
Edgewood (SBCCOM)] have worked on enzyme-based detection or
decontamination systems for OP compounds. Various approaches taken
in such laboratories include dispersion systems or immobilization
systems of one or more OP degrading enzymes for use in detection or
decontamination of OP compounds, as well as for convenience of
handling of the enzyme preparation.
[0015] Sensors of OP compounds using an OP compound degrading
enzyme have been described primarily for the detection of OP
pesticides. OP compound sensors have been described that detect pH
changes upon OP compound degradation using recombinant Escherichia
coli cells expressing OPH cryoimmobilized in poly(vinyl)alcohol gel
spheres (Rainina, E. I. et al., 1996). Endogenously expressed OPH
from whole Flavobacterium sp. cells or cell membranes have been
described as immobilized to glass membrane using poly(carbamoyl
sulfonate) and poly(ethyleneimine) to produce a sensor of pH
changes due to OP compound degradation (Gaberlein, S. et al.,
2000a). OP compound sensors have been described that detect pH
changes upon OP compound degradation using recombinant Escherichia
coli cells, expressing OPH cytosolically or at the cell surface,
that were fixed behind a polycarbonate membrane (Mulchandani, A. et
al., 1998a; Mulchandani, A. et al., 1998b). An OP compound sensor
has been described that detects optical changes upon OP compound
degradation using recombinant Escherichia coli cells, expressing
OPH at the cell surface, that were admixed in low melting point
agarose and applied to membrane that was affixed to a fiber optic
sensor (Mulchandani, A. et al., 1998c).
[0016] An OP compound sensor has been described that detects pH
changes upon OP compound degradation using purified OPH chemically
cross-linked with bovine serum albumin by glutaraldehyde on an
electrode's glass membrane and covered with a dialysis membrane
(Mulchandani, P. et al., 1999). Such chemically cross-linked OPH
has been placed on a nylon membrane, and the membrane affixed to a
fiber optic sensor to detect optical changes upon OP compound
degradation (Mulchandani, A. et al., 1999a). Purified OPH has been
immobilized by glutaraldehyde to glass-beads having aminopropyl
groups in the construction of an OP compound degradation sensor
(Mulchandani, P. et al., 2001a). An OP compound sensor has been
described that detects optical changes upon OP compound degradation
using recombinant Moraxella sp. cells, expressing OPH at the cell
surface, that were admixed in 75% (w/w) graphite powder and 25%
(w/w) mineral oil and placed into an electrode cavity (Mulchandani,
P. et al., 2001b). Purified OPH was attached to silica beads by
glutaraldehyde or N-.gamma.-maleimidobutyrylozy succinimide ester
linkages, and the beads placed as a layer on a glass slide to
construct a sensor (Singh, A. K. et al., 1999). Purified OPH has
been labeled with fluorescein isothiocyanate and absorbed to
poly(methyl methacrylate) beads that were placed on a nylon
membrane to construct a sensor that detects OP compound cleavage by
decreased fluorescence (Rogers, K. R. et al., 1999). Purified OPH
has been immobilized by placement within a poly(carbamoyl
sulfonate) prepolymer that was allowed to polymerize on a
heat-sealing film in the construction of a sensor (Gaberlein, S. et
al., 2000b). A purified fusion protein comprising OPH and a FLAG
octapeptide sequence was immobilized to magnetic particles (Wang,
J. et al., 2001). Additional sensors using OPH have been described
(Mulchandani, A. et al., 2001).
[0017] Different OP compound degrading enzyme compositions have
been described, primarily for the detoxification of OP pesticides
(Chen, W. and Mulchandani, A., 1998; LeJeune, K. E. et al., 1998a).
A parathion hydrolase enzyme degrading cell extract has been
immobilized onto silica beads and porous glass (Munnecke, D. M.,
1979; Munnecke, D. M., 1978). OPH has also been immobilized onto
porous glass and silica beads (Caldwell, S. R. and Raushel, F. M.,
1991b). Purified OPH has been mixed with fire fighting foams in an
attempt to create a readily dispersible decontamination composition
(LeJeune, K. E., and Russell, A. J., 1999; LeJeune, K. E. et al.,
1998b). Purified OPH has been incorporated into micelles in an OP
compound degradation device (Komives, C. et al., 1994). Purified
OPH has been encapsulated in a liposome for use in OP compound
degradation (Pei, L. et al., 1994; Petrikovics, I. et al., 1999).
OPH enzyme supported by glass wool in a biphasic solvent and gas
phase reactor for OP compound detoxification has been described
(Yang, F. et al., 1995). Purified OPH has also been immobilized
onto trityl agarose and nylon (Caldwell, S. R. and Raushel, F. M.,
1991a). Recombinant Escherichia coli cells co-expressing OPH and a
surface expressed cellulose-binding domain have been immobilized to
cellulose supports (Wang, A. A. et al., 2002). Partly purified OPH,
acetylcholinesterase or butyrylcholinesterase has been incorporated
into polyurethane foam sponges (Havens, P. L. and Rase, H. F.,
1993; Gordon, R. K. et al., 1999). Partly purified or purified OPH
has been incorporated into solid polyurethane foam (LeJeune, K. E.
and Russell, A. J., 1996; LeJeune, K. E. et al., 1997; LeJeune, K.
E. et al., 1999). Recombinant Escherichia coli cells expressing OPH
have been immobilized in a poly(vinylalcohol) cryogel (Hong, M. S.
et al., 1998; Efremenko, E. N. et al., 2002; Kim, J.-W. et al.,
2002). Purified OPH has been immobilized in polyethylene glycol
hydrogels (Andreopoulos, F. M. et al., 1999). Recombinant
Escherichia coli expressing OPH at the cell surface has been
immobilized to polypropylene fabric by absorption of the cells to
the fabric (Mulchandani, A. et al., 1999b). Purified OPH was
immobilized to mesoporous silica by
Tris-(methoxy)carboxylethylsilane or
Tris-(methoxy)aminopropylsilane (Lei, C. et al., 2002). A fusion
protein comprising OPH and a cellulose-binding domain has been
immobilized to cellulose supports (Richins, R. D. et al., 2000).
Sonicated Escherichia coli cells expressing a fusion protein
comprising OPH, a green fluorescent protein, and a polyhistidine
sequence as an affinity tag, have been attached to a
nickel-iminodiacetic acid-agarose bead resin (Wu, C.-F. et al.,
2002). A fusion protein comprising OPH and a polyhistidine sequence
as an affinity tag has been attached to a chitosan film (Chen, T.
et al., 2001). A purified fusion protein comprising an elastin-like
polypeptide and OPH has shown to reversibly bind to the hydrophobic
surface of polystyrene plates at temperatures above 37.degree. C.
(Shimazu, M. et al., 2002).
[0018] In addition to OPH, other OP compound enzyme compositions
have been described. Purified OPAA has been encapsulated in a
liposome for use in OP compound degradation (Petrikovics, I. et
al., 2000a; Petrikovics, I. et al., 2000b). Purified OPAA has been
mixed with fire fighting foams, detergents, and a skin care lotion
in an attempt to create a readily dispersible decontamination
composition (Cheng, T.-C. et al., 1999). Purified squid-type DFPase
has been encapsulated in erythrocytes for use in OP compound
degradation (McGuinn, W. D. et al., 1993). Purified squid-type
DFPase has been coupled to agarose beads (Hoskin, F. C. G. and
Roush, A. H., 1982). Purified squid-type DFPase has also been
incorporated into a polyurethane matrix (Drevon, G. F. et al.,
2002; Drevon, G. F. et al., 2001; Drevon, G. F. and Russell, A. J.,
2000).
[0019] U.S. Patent Publication No. US 2002/0106361 A1 discusses a
marine anti-fungal enzyme for use in a marine coating. However, the
substrate for the enzyme was incorporated into the marine coating,
and the enzyme was in a marine environment as the organism from
which it was obtained. Immobilized enzymes in an latex are
discussed in the April, 2002 edition of "Emulsion Polymer
Technologies," by the Paint Research Association website
http://www.pra.org.uk/publications/emulsion/emulsion
highlights-2002.htm.
[0020] However, to date, there has been limited success in using
these and other approaches to harness the potential of these
enzymes in systems that can be readily and cost effectively used in
field-based military or civilian applications. Thus, despite the
current understanding of the various OP compound degrading
compositions and techniques, whether based on caustic chemicals or
enzymes, there is a clear and present need for compositions and
methods that can readily be used in OP compound degradation. This
is particularly true for the detoxification of OP chemical warfare
agents. In particular, compositions and methods are needed that
will detoxify surfaces contaminated with OP compounds.
SUMMARY OF THE INVENTION
[0021] The present invention provides compositions and methods for
their use as components of surface treatments such as coatings.
More specifically, the present invention provides compositions and
methods for incorporating biological molecules into coatings in a
manner to retain biological activity conferred by such biological
molecule.
[0022] The present invention provides compositions and methods
capable of effective decontamination of OP compounds, as well as
prophalactic protection of buildings, equipment, and personel that
contact such objects, from OP compounds, including CWAs. As they
relate to detoxification of OPs, the compositions and methods
disclosed herein differ substantially from prior efforts, which
focus on enzymatic detoxification of chemical compounds by
application of a decontamination composition or method to the site
of contamination after contact with the chemical compound. The
preferred embodiments of the present invention represent a paradigm
shift in chemical decontamination. They demonstrate usable
compositions and methods for prophylactic protection of a site
prior to contact with a chemical by prior application of a
protective coating comprising an enzyme composition of the present
invention. While prophylactic treatment with the coatings of the
invention are a preferred embodiment, such a coating can also be
used to coat a surface after contamination occurs. A preferred
coating comprises a paint. Specifically, a paint comprising a
preferred enzyme composition of the present invention degrades an
organophosphorus compound, including a chemical warfare agent, into
a significantly less toxic compound. Another preferred coating
comprises a clear coat, a textile treatment, a wax, elastomer, or a
sealant.
[0023] Further, the present disclosure is the first composition of
which Applicant is aware that comprises a bioactive molecule such
as an enzyme composition that retains activity after being admixed
with paint. In addition, it still retains activity after the paint
is applied to a surface, and renders the surface bioactive.
[0024] In light of these and additional disclosures herein, it is
now possible to produce paints and other coatings that detoxify
chemical compounds for extended periods. Remarkably, a preferred
enzyme composition of the present invention remained stable in the
coating for an extended period of time (e.g., months) at ambient
conditions. It is contemplated that the extended period of activity
may further comprise time periods in excess of a year. In
particular, stabilized embodiments of the enzyme composition are
designed to enhance the life time of the biomolecule composition in
a coating and on a surface. In a preferred embodiment, the
invention comprises at least one polymer-based compound that
provides prophylactic protection and continuous detoxification of
an organophosphorus nerve agent.
[0025] In certain embodiments, it is contemplated that the
compositions and methods of the present invention may be used to
produce self-decontaminating surfaces that remain active for
extended periods. In a specific aspect, it is contemplated that
such a self-decontaminating surface will not need additional
decontamination compositions or methods to effect decontamination,
thereby minimizing logistical requirement. In a particular aspect,
it is contemplated that the compositions and methods of the present
invention may be easily applied in advance of, during or after
exposure to a chemical compound. In another preferred aspect, the
compositions and methods of the present invention will be used in
conjunction with existing other decontamination compositions and
methods. In a preferred facet, the compositions and methods of the
present invention are applied in advance of, during or after a
field-based military operation to protect troops against a chemical
warfare agent.
[0026] A recombinant phosphoric triester hydrolase may be produced
using specific expression vectors in a variety of host cells. In
the practice of the present invention, any of the described cells,
nucleic acid sequences, genes, gene fragments, vectors and
transcriptional or translational signals may be used, or any others
that are known in the art. In preferred facets, the enzyme is grown
in bacterial, fungal, plant (e.g., corn), or insect cells. In
preferred embodiments, an expression vector includes an opd DNA
fragment in the correct orientation and reading frame with respect
to the promoter sequence to allow translation of the opd gene or
gene fragment. In a specific aspect, the expression vector produces
heterologous expression of the opd gene or gene fragment. In
particularly preferred embodiments of the composition, the enzyme
is an OPH enzyme. In other preferred embodiments the enzyme is an
OPAA enzyme. In other preferred embodiments, the enzyme is a
DFPase. Examples of the cloning and expression of exemplary opd
gene and gene fragments are described (McDaniel, S. et al., 1988;
McDaniel, 1985; Wild, J. R. et al., 1986; each incorporated herein
in its entirety by reference).
[0027] In general embodiments, a biomolecule of the present
invention refers to a compound comprising one or more chemical
moieties normally produced by a living organism such as an amino
acid, a nucleic acid, a sugar, a lipid, or a combination thereof.
The invention provides a coating comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule. A biomolecule typically has a function in or
upon a living organism, such as binding another molecule,
catalyzing a chemical reaction, or a combination thereof. Specific
examples of such activity by a biomolecule include an antibody
binding an antigen, a cell receptor binding a ligand, an enzyme
binding a substrate, a transport protein may bind a ligand, etc. In
some aspects, binding a ligand may be a desired activity such as,
for example, to sequester an undesired molecule, such as a toxin,
to the biomolecule. Often, a biomolecule's activity further
comprises a specific chemical reaction in addition to a
physical/chemical affinity for another molecule. For example, an
enzyme may accelerate a chemical reaction upon the bound substrate,
a cell receptor may change conformation and/or become enzymatically
active or inactive toward a second substrate, a transport protein
may mitigate the movement of a molecule, etc. In another example, a
biomolecule may comprise a ligand that induces or inhibits such
activity in an enzyme, a cell receptor, a transport protein, and
the like.
[0028] An "active biomolecule" refers to biomolecule that retains
these types of properties in a coating of the present invention.
The ability to confer bioactivity to a coating provides numerous
uses in addition to the preferred bioactivity of detoxification of
OP compounds.
[0029] Further, disclosed herein is the discovery that an active
biomolecule may function in a coating in environments differing
from the native environment of the organism from which it was
obtained or derived. For example, an active biomolecule may retain
activity in a coating under conditions of temperature, salinity,
pH, moisture, or a combination thereof that differ from the
organism's native environment.
[0030] The ability of a biomolecule to retain its function as an
active biomolecule in a composition of the present invention,
particularly a coating, may be detected and measured by any
technique known to one of ordinary skill the art, including the
various assays described herein.
[0031] A further disclosure of the present invention is the
preparation of an active biomolecule with a limited number of
processing and/or purification steps from other cellular molecules
of the organism in which it was produced. Typically, the organism
is a microorganism. The combination of an active biomolecule and
such cellular molecules is known herein as a "biomolecule
composition." It is contemplated that the inclusion of such
cellular molecules may provide a protective or stabilizing effect
for the activity of the active biomolecule. An example would be the
protective encapsulation of an active biomolecule by a cell wall
and/or cell membrane of the organism. Such additional cellular
molecules contribute to the particulate nature of a biomolecule
composition, which may grant utility for such material as a
particulate component of a coating or paint, such as a pigment, an
dispersant, a rheological agent, or a combination thereof.
[0032] The invention provides various additional embodiments. In
general embodiments, a biomolecular composition comprises 0.001% to
40% of the coating composition by weight or volume, including all
intermediate ranges and combinations thereof. In other embodiments,
the biomolecule composition comprises a microorganism based
particulate material. In some aspects, the microorganism based
particulate material comprises a whole cell material. In
alternative aspects, the microorganism based particulate material
is a cell fragment microorganism based particulate material. In
certain aspects, the active biomolecule comprises 0.001% to 40% of
the coating composition by weight or volume, including all
intermediate ranges and combinations thereof.
[0033] In certain embodiments, the active biomolecule comprises a
proteinaceous molecule. In some aspects, a proteinaceous molecule
comprises a peptide, a polypeptide, a protein, or a combination
thereof. In specific aspects, the proteinaceous molecule comprises
an enzyme, an antibody, a receptor, a transport protein, a
structural protein, or a combination thereof. In other embodiments,
the proteinaceous molecule binds a ligand, contacts a living
organism, or a combination thereof. In particular aspects, the
proteinaceous molecule binds a ligand. The ligand may comprise an
antigen, a substrate, an inhibitor, or a combination thereof. In
certain preferred facets, the ligand comprises a chemical toxic to
humans, such as, for example, an organophosphorus compound. In
further aspects, the proteinaceous molecule contacts a living
organism. In particular facets, the proteinaceous molecule
comprises a ligand capable of binding to an active biomolecule of
the living organism. In specific facets, the active biomolecule of
the living organism comprises a receptor, an enzyme, a transport
protein, or a combination thereof.
[0034] In certain embodiments, the active biomolecule comprises a
combination of active biomolecules. The combination of biomolecules
may be of the same type, such as a combination of enzymes. The
combination may be of different biomolecules or may be of different
types of biomolecules such as a receptor ligand and an enzyme, a
receptor and an antibody, an enzyme and an combination of
antibodies, etc. All iterations of active biomolecules may be
selected to confer to a coating a combination of bioactivities as
desired. In general embodiments, a composition of the present
invention may comprise 1 to 100 or more different selected
biomolecules of interest, including all intermediate ranges and
combinations thereof.
[0035] In some embodiments, the proteinaceous molecule comprises an
enzyme. In particular embodiments, the enzyme comprises an
oxidoreductase, a transferase, a hydrolase, a lyase, an isomerase,
a ligase, or a combination thereof. In certain aspects, the enzyme
comprises a hydrolase. In further aspects, the hydrolase comprises
an esterase. In specific aspects, the esterase comprises a
phosphoric triester hydrolase. The phosphoric triester hydrolase
may comprise, for example, an aryldialkylphosphatase, a
diisopropyl-fluorophosphatase, or a combination thereof.
[0036] In one preferred embodiment, the combination of biomolecules
comprises a combination of phosphoric triester hydrolases. The
combination of phosphoric triester hydrolases may be of the similar
types, such as, for example, an organophosphorus hydrolase that
possesses an enzymatic activity superior in, for example, binding
affinity and/or rate of substrate cleavage in combination with one
or more additional an organophosphorus hydrolases, each with a
different enzymatic activity relative to the substrate. The
combination of phosphoric triester hydrolases may comprise
phosphoric triester hydrolases of different types, such as, for
example, a Mazur-type DFPase and an aryldialkylphosphatase, or an
OPAA and a human paraoxonase, or an organophosphorus hydrolase, a
human paraoxonase and an animal carboxylase, etc. All iterations of
selection of phosphoric triester hydrolases are contemplated to
produce a coating with a combination of phosphoric triester
hydrolase activities as desired.
[0037] In certain embodiments, the phosphoric triester hydrolase
comprises an aryldialkylphosphatase. In some aspects, the
aryldialkylphosphatase comprises an organophosphorus hydrolase, a
human paraoxonase, an animal carboxylase, or a functional
equivalent thereof. In additional aspects, the
aryldialkylphosphatase comprises an organophosphorus hydrolase or a
functional equivalent thereof. In specific aspects, the
organophosphorus hydrolase comprises an Agrobacterium radiobacter
P230 organophosphate hydrolase, a Flavobacterium balustinum
parathion hydrolase, a Pseudomonas diminuta phosphodiesterase, a
Flavobacterium sp opd gene product, a Flavobacterium sp. parathion
hydrolase opd gene product, or a functional equivalent thereof. In
certain facets, the organophosphorus hydrolase comprises a
functional equivalent of Agrobacterium radiobacter P230
organophosphate hydrolase, a Flavobacterium balustinum parathion
hydrolase, a Pseudomonas diminuta phosphodiesterase, a
Flavobacterium sp opd gene product, or a Flavobacterium sp.
parathion hydrolase opd gene product. In particular facets, the
functional equivalent is a structural analog, a sequence analog, or
a combination thereof. In specific facets, the functional
equivalent is a structural analog. In further facets, the
structural analog comprises a Co.sup.2+, Fe.sup.2+, Cu.sup.2+,
Mn.sup.2+, Cd.sup.2+ or Ni.sup.2+ at the enzyme active site. In
other facets, the functional equivalent is a sequence analog. In
other facets, the functional equivalent is a structural analog. In
particular facets, the sequence analog is an alteration in sequence
length. In specific facets, the sequence analog lacks a leader
peptide sequence, the sequence analog comprises a fusion protein,
or a combination thereof.
[0038] In certain embodiments, the organophosphorus hydrolase
comprises a Pseudomonas diminuta phosphotristerase, or a functional
equivalent thereof. In some aspects, the organophosphorus hydrolase
comprises a Pseudomonas diminuta phosphotristerase. In other
embodiments, a preferred organophosphorus hydrolase comprises a
Pseudomonas diminuta phosphotristerase functional equivalent. In
certain aspects the Pseudomonas diminuta phosphotristerase
functional equivalent comprises a sequence analog, a structural
analog, or a combination thereof. In particular facets, the
Pseudomonas diminuta phosphodiesterase functional equivalent
comprises a sequence analog. In some facets, the sequence analog
comprises an amino acid substitution. In specific facets, the
sequence analog comprises H55C, H57C, C59A, G60A, S61A, I106A,
I106G, W131A, W131F, W131K, F132A, F132H, F132Y, L136Y, L140Y,
H201C, H230C, H254A, H254R, H254S, H257A, H257L, H257Y, L271A,
L271Y, L303A, F306A, F306E, F306H, F306K, F306Y, S308A, S308G,
Y309A, M317A, M317H, M317K, M317R, H55C/H57C, H55C/H201C,
H55C/H230C, H57C/H201C, H57C/H230C, A80V/S365P, I106A/F132A,
I106A/S308A, I106G/F132G, I106G/S308G, F132Y/F306H, F132H/F306H,
F132H/F306Y, F132Y/F306Y, F132A/S308A, F132G/S308G, L182S/V310A,
H201C/H230C, H254R/H257L, H55C/H57C/H201C, H55C/H57C/H230C,
H55C/H201C/H230C, I106A/F132A/H257Y, I106A/F132A/H257W,
I106G/F132G/S308G, L130M/H257Y/I274N, H257Y/I274N/S365P,
H55C/H57C/H201C/H230C, I106G/F132G/H257Y/S308G,
A14T/A80V/L185R/H257Y/I27- 4N, or a combination thereof.
[0039] In additional embodiments, the aryldialkylphosphatase
comprises a paraoxonase, such as, for example, a human paraoxonase
or a functional equivalent thereof. In some aspects, the human
paraoxonase comprises an HPON1 gene product or a functional
equivalent thereof. In certain facets, the human paraoxonase
comprises a HPON1 gene product functional equivalent. In specific
facets, the HPON1 gene product functional equivalent comprises a
sequence analog. In particular facets, the sequence analog
comprises an amino acid substitution. In further facets, the
sequence analog is E32A, E48A, E52A, D53A, D88A, D107A, H114N,
D121A, H133N, H154N, H160N, W193A, W193F, W201A, W201F, H242N,
H245N, H250N, W253A, W253F, D273A, W280A, W280F, H284N, H347N or a
combination thereof.
[0040] In further embodiments, the aryldialkylphosphatase comprises
an animal carboxylase. In particular aspects, the animal
carboxylase comprises an insect carboxylase or a functional
equivalent thereof. In additional aspects, the insect carboxylase
comprises a Plodia interpunctella carboxylase, Chrysomya putoria
carboxylase, Lucilia cuprina carboxylase, Musca domestica
carboxylase carboxylase, or a functional equivalent thereof.
[0041] In other embodiments, the phosphoric triester hydrolase
comprises a diisopropyl-fluorophosphatase. In some aspects, the
diisopropyl-fluorophosphatase comprises an organophosphorus acid
anhydrolase, a squid-type DFPase, a Mazur-type DFPase, or a
functional equivalent thereof. In further aspects, the
diisopropyl-fluorophosphatase comprises an organophosphorus acid
anhydrolase or a functional equivalent thereof. In additional
aspects, the organophosphorus acid anhydrolase comprises an
Altermonas organophosphorus acid anhydrolase, a prolidase, or a
functional equivalent thereof. In some facets, the organophosphorus
acid anhydrolase comprises an Altermonas organophosphorus acid
anhydrolase or a functional equivalent thereof. In particular
facets, the Altermonas organophosphorus acid anhydrolase comprises
an Alteromonas sp JD6.5 organophosphorus acid anhydrolase, an
Alteromonas haloplanktis organophosphorus acid anhydrolase, an
Altermonas undina organophosphorus acid anhydrolase, or a
functional equivalent thereof. In additional facets, the
organophosphorus acid anhydrolase comprises a prolidase or a
functional equivalent thereof. In specific facets, the prolidase
comprises a human prolidase, a Mus musculus prolidase, a
Lactobacillus helveticus prolidase, an Escherichia coli prolidase,
an Escherichia coli aminopeptidase P, or a functional equivalent
thereof.
[0042] In certain embodiments, the diisopropyl-fluorophosphatase
comprises a squid-type DFPase, or a functional equivalent thereof.
In some aspects, the squid-type DFPase comprises a Loligo vulgaris
DFPase, a Loligo pealei DFPase, a Loligo opalescens DFPase, or a
functional equivalent thereof. In specific aspects, the squid-type
DFPase comprises a Loligo vulgaris DFPase, or a functional
equivalent thereof. In some facets, the squid-type DFPase comprises
a Loligo vulgaris DFPase, or a functional equivalent thereof. In
additional facets, the squid-type DFPase comprises a Loligo
vulgaris DFPase functional equivalent. In particular facets, the
Loligo vulgaris DFPase functional equivalent comprises a sequence
analog. In continuing facets, the sequence analog. comprises an
amino acid substitution. In some facets, the sequence analog is
H181N, H224N, H274N, H219N, H248N, or H287N. In other facets, the
sequence analog is an alteration in sequence length. In specific
facets, the sequence analog is a fusion protein.
[0043] In other embodiments, the diisopropyl-fluorophosphatase
comprises a Mazur-type DFPase, or a functional equivalent thereof.
In some aspects, the Mazur-type DFPase comprises a mouse liver
DFPase, a hog kidney DFPase, a Bacillus stearothermophilus strain
OT DFPase, an Escherichia coli DFPase, or a functional equivalent
thereof.
[0044] In additional embodiments, the phosphoric triester hydrolase
comprises a Plesiomonas sp. strain M6 mpd gene product, a
Xanthomonas sp. phosphoric triester hydrolase, a Tetrahymena
phosphoric triester hydrolase, or a functional equivalent
thereof.
[0045] In other embodiments, the coating is 5 um to 1500 um thick
upon the surface, including all intermediate ranges and
combinations thereof. In some aspects, the coating is 15 um to 500
um thick upon the surface, including all intermediate ranges and
combinations thereof. In particular aspects, the coating comprises
a multicoat system. In an additional aspect, the multicoat system
comprises 2 to 10 layers. In a particular facet, one layer of the
multicoat system comprises the biomolecular composition. In a
further aspect, a plurality of layers of the multicoat system
comprises the biomolecular composition. In some facets, each layer
of the multicoat system is a coating 15 um to 500 um thick,
including all intermediate ranges and combinations thereof. In
other facets, each layer of the multicoat system is a coating 15 um
to 150 um thick, including all intermediate ranges and combinations
thereof. In particular aspects, the multicoat system comprises a
sealer, a water repellent, a primer, an undercoat, a topcoat, or a
combination thereof. In specific facets, the multicoat system
comprises a topcoat. In particular facets, the topcoat comprises
the biomolecular composition.
[0046] In some embodiments, the coating comprises a paint. In other
embodiments, the coating comprises a clear coating. In some
aspects, the clear coating comprises a lacquer, a varnish, a
shellac, a stain, a water repellent coating, or a combination
thereof. In general aspects, the coating comprises a binder, a
liquid component, a colorant, an additive, or a combination
thereof. In some facets, the coating comprises a buffer. In
particular aspects, the buffer comprises a bicarbonate.
[0047] In certain embodiments, the coating undergoes film
formation. In general aspects, film formation occurs at ambient
conditions, baking conditions, or a combination thereof. In
particular aspects, film formation occurs at baking conditions. In
other aspects, baking conditions is between 40.degree. C. and
110.degree. C., including all intermediate ranges and combinations
thereof. Examples of specific intermediate ranges for baking
conditions include 40.degree. C. and 50.degree. C., or 40.degree.
C. and 65.degree. C. In general aspects, the coating comprises a
volatile component and a non-volatile component. In general facets,
the coating undergoes film formation by loss of part of the
volatile component. In other facets, the volatile component
comprises a volatile liquid component. In particular facets, the
volatile liquid component comprises a solvent, a thinner, a
diluent, or a combination thereof. In other aspects, the
non-volatile component comprises a binder, a colorant, a
plasticizer, a coating additive, a biomolecular composition of the
present invention, or a combination thereof. In certain aspects,
film formation occurs by crosslinking of a binder. In some facets,
film formation occurs by crosslinking of a plurality of binders. In
further facets, film formation occurs by irradiating the coating.
In some facets, the coating produces a self-cleaning film upon film
formation.
[0048] In certain alternative embodiments, the coating is a
non-film forming coating. In particular aspects, the non-film
forming coating comprises a non-film formating binder. In some
aspects, the non-film forming coating comprises a coating component
in a concentration that is insufficient to produce a solid film. In
some facets, the coating component comprises a binder that
contributes to thermoplastic film formation, thermosetting film
formation, or a combination thereof. In particular facets, the
coating component comprises a binder, catalyst, initiator, or
combination thereof. Though the concentration which is insufficient
for a coating component to produce film formation in a coating may
be empirically determined by an assay, such as those described
herein for film formation, such an insufficient concentration may
easily achieved by selection of a concentration of 0%, wherein the
coating lacks the film-forming component.
[0049] In other alterative embodiments, the coating produces a
temporary film. In specific aspects, the temporary film has a poor
resistance to a coating remover. In particular facets, the
temporary film has a poor scrub resistance, a poor solvent
resistance, a poor water resistance, a poor weathering property, a
poor adhesion property, or a combination thereof. A poor resistance
and/or poor quality property for a coating can be empirically
determined by assays described herein.
[0050] In general embodiments, the coating comprises an
architectural coating, an industrial coating, a specification
coating, or a combination thereof. In additional aspects, the
coating comprises an architectural coating. In particular aspects,
the architectural coating comprises a wood coating, a masonry
coating, an artist's coating, or a combination thereof. In some
facets, the architectural coating has a pot life of at least 12
months at ambient conditions. In general aspects, the architectural
coating undergoes film formation at ambient conditions. In other
aspects, the coating comprises an industrial coating. In further
aspects, the industrial coating comprises an automotive coating, a
can coating, sealant coating, a marine coating, or a combination
thereof. In particular facets, the industrial coating undergoes
film formation at baking conditions. In additional aspects, the
coating comprises a specification coating. In particular facets,
the specification coating comprises a camouflage coating, a
pipeline coating, traffic marker coating, aircraft coating, a
nuclear power plant coating, or a combination thereof. In
particular facets, the specification coating comprises a camouflage
coating. In specific facets, the camouflage coating comprises a
camouflage pigment.
[0051] In many embodiments, a coating comprises a water-borne
coating, a solvent borne coating, or a powder coating. In
particular aspects, the coating comprises a water-borne coating. In
certain facets, the water-borne coating is a latex coating. In
additional facets, the water-borne coating has a density of 1.20
kg/L to 1.50 kg/L, including all intermediate ranges and
combinations thereof. In other aspects, the coating comprises a
solvent-borne coating. In further facets, the solvent-borne coating
has a density of 0.90 kg/L to 1.2 kg/L, including all intermediate
ranges and combinations thereof.
[0052] In general embodiments, the coating has a viscosity during
application of 72 Ku to 95 Ku, including all intermediate ranges
and combinations thereof. In further aspects, the coating has a
viscosity prior to application of 100 P to 1000 P, including all
intermediate ranges and combinations thereof. In particular
aspects, the coating has a viscosity during application of 0.5 P to
2.5 P, including all intermediate ranges and combinations thereof.
In other aspects, the coating has a viscosity of 100 P to 1000 P,
including all intermediate ranges and combinations thereof, upon a
surface immediately after application.
[0053] In many embodiments, the coating comprises a binder. In many
aspects, the binder comprises a thermoplastic binder, a
thermosetting binder, or a combination thereof. In certain aspects,
the coating comprises a thermoplastic binder. In particular facets,
such a coating produces a film by thermoplastic film formation. In
other aspects, the coating comprises a thermosetting binder. In
further facets, such a coating produces a film by thermosetting
film formation.
[0054] In some embodiments, the binder comprises an oil-based
binder. In particular aspects, the oil-based binder comprises an
oil, an alkyd, an oleoresinous binder, a fatty acid epoxide ester,
or a combination thereof. In further facets, such an oil-based
binder coating produces a layer 15 um to 25 .mu.m thick upon the
vertical surface, including all intermediate ranges and
combinations thereof, or 15 um to 40 .mu.m thick upon the
horizontal surface, including all intermediate ranges and
combinations thereof. In further aspects, the binder comprises an
oil. In other aspects, the binder comprises an alkyd. In specific
aspects, the binder comprises an oleoresinous binder. In some
aspects, the binder comprises a fatty acid epoxide ester.
[0055] In other embodiments, the binder comprises a polyester
resin. In certain aspects, polyester resin comprises a
hydroxy-terminated polyester. In other aspects, the polyester resin
comprises a carboxylic acid-terminated polyester. In additional
facets, the coating comprises a polyester resin and a urethane, an
amino resin, or a combination thereof.
[0056] In some embodiments, the binder comprises a modified
cellulose. In certain aspects, the modified cellulose comprises a
cellulose ester, a nitrocellulose or a combination thereof. In
certain facets, the modified cellulose comprises a cellulose ester.
In other facets, the modified cellulose comprises a nitrocellulose.
In further aspects, the coating comprises a modified cellulose and
an amino binder, an acrylic binder, urethane binder, or a
combination thereof.
[0057] In additional embodiments, the binder comprises a polyamide.
In specific aspects, the coating comprises a polyamide and an
epoxide.
[0058] In certain embodiments, the binder comprises an amino resin.
In some aspects, the coating comprises an amino resin and an
acrylic binder, an alkyd resin, a polyester binder, or a
combination thereof.
[0059] In additional embodiments, the binder comprises an urethane
binder. In particular aspects, the coating comprises an urethane
binder and a polyol, an amine, an epoxide, a silicone, a vinyl, a
phenolic, a triacrylate, or a combination thereof.
[0060] In some embodiments, the binder comprises a phenolic resin.
In further aspects, the coating comprises a phenolic resin and an
alkyd resin, an amino resin, a blown oil, an epoxy resin, a
polyamide, a polyvinyl resin, or a combination thereof.
[0061] In other embodiments, the binder comprises an epoxy resin.
In additional aspects, the coating comprises an epoxy resin and an
amino resin, a phenolic resin, a polyamide, a ketimine, an
aliphatic amine, or a combination thereof. In particular facets,
the epoxy resin comprises a cycloaliphatic epoxy binder. In further
facets, the coating comprises cycloaliphatic epoxy binder and a
polyol.
[0062] In additional embodiments, the binder comprises a
polyhydroxyether binder. In further aspects, the coating comprises
a polyhydroxyether binder and an epoxide, a polyurethane comprising
an isocyanate moiety, an amino resin, or a combination thereof.
[0063] In further embodiments, the binder comprises an acrylic
resin. In additional aspects, the coating comprises an acrylic
resin and an epoxide, a polyurethane comprising an isocyanate
moiety, an amino resin, or a combination thereof.
[0064] In some embodiments, the binder comprises a polyvinyl
binder. In further embodiments, the coating comprises a polyvinyl
binder and an alkyd, an urethane, an amino-resin, or a combination
thereof.
[0065] In certain embodiments, the binder comprises a rubber resin.
In some aspects, the rubber resin comprises a chlorinated rubber
resin, a synthetic rubber resin, or a combination thereof. In
additional facets, the coating comprises a rubber resin and an
acrylic resin, an alkyd resin, a bituminous resin, or a combination
thereof.
[0066] In specific embodiments, the binder comprises a bituminous
binder. In additional aspects, the coating comprises a bituminous
binder and an epoxy resin.
[0067] In further embodiments, the binder comprises a polysulfide
binder. In specific aspects, the coating comprises a polysulfide
binder and a peroxide, a binder comprising an isocyanate moiety, or
a combination thereof.
[0068] In additional embodiments, the binder comprises a silicone
binder. In further aspects, the coating comprises a silicone binder
and an organic binder.
[0069] In many embodiments, the coating comprises a liquid
component. In general aspects, the liquid component comprises a
solvent, a thinner, a diluent, a plasticizer, or a combination
thereof. In other aspects, the liquid component comprises a liquid
organic compound, an inorganic compound, water, or a combination
thereof.
[0070] In some embodiments, the liquid component comprises a liquid
organic compound. In certain aspects, the liquid organic compound
comprises a hydrocarbon, an oxygenated compound, a chlorinated
hydrocarbon, a nitrated hydrocarbon, a miscellaneous organic liquid
component, a plasticizer, or a combination thereof.
[0071] In particular embodiments, the liquid organic compound
comprises a hydrocarbon. In certain aspects, the hydrocarbon
comprises an aliphatic hydrocarbon, a cycloaliphatic hydrocarbon, a
terpene, an aromatic hydrocarbon, or a combination thereof. In
additional facets, the hydrocarbon comprises an aliphatic
hydrocarbon. In further facets, the aliphatic hydrocarbon comprises
a petroleum ether, pentane, hexane, heptane, isododecane, a
kerosene, a mineral spirit, a VMP naphtha or a combination thereof.
In other aspects, the hydrocarbon comprises a cycloaliphatic
hydrocarbon. In some facets, the cycloaliphatic hydrocarbon
comprises cyclohexane, methylcyclohexane, ethylcyclohexane,
tetrahydronaphthalene, decahydronaphthalene, or a combination
thereof. In other aspects, the hydrocarbon comprises a terpene. In
additional facets, the terpene comprises wood terpentine oil, pine
oil, .alpha.-pinene, .beta.-pinene, dipentene, D-limonene, or a
combination thereof. In particular aspects, the hydrocarbon
comprises an aromatic hydrocarbon. In some facets, the aromatic
hydrocarbon comprises benzene, toluene, ethylbenzene, xylene,
cumene, a type I high flash aromatic naphtha, a type II high flash
aromatic naphtha, mesitylene, pseudocumene, cymol, styrene, or a
combination thereof.
[0072] In other embodiments, the liquid organic compound comprises
an oxygenated solvent. In certain aspects, the oxygenated solvent
comprises an alcohol, an ester, a glycol ether, a ketone, an ether,
or a combination thereof. In some aspects, the oxygenated solvent
comprises an alcohol. In further aspects, the alcohol comprises
methanol, ethanol, propanol, isopropanol, 1-butanol, isobutanol,
2-butanol, tert-butanol, amyl alcohol, isoamyl alcohol, hexanol,
methylisobutylcarbinol, 2-ethylbutanol, isooctyl alcohol,
2-ethylhexanol, isodecanol, cylcohexanol, methylcyclohexanol,
trimethylcyclohexanol, benzyl alcohol, methylbenzyl alcohol,
furfuryl alcohol, tetrahydrofurfuryl alcohol, diacetone alcohol,
trimethylcyclohexanol, or a combination thereof. In other aspects,
the oxygenated solvent comprises an ester. In particular facets,
the ester comprises methyl formate, ethyl formate, butyl formate,
isobutyl formate, methyl acetate, ethyl acetate, propyl acetate,
isopropyl acetate, butyl acetate, isobutyl acetate, sec-butyl
acetate, amyl acetate, isoamyl acetate, hexyl acetate, cyclohexyl
acetate, benzyl acetate, methyl glycol acetate, ethyl glycol
acetate, butyl glycol acetate, ethyl diglycol acetate, butyl
diglycol acetate, 1-methoxypropyl acetate, ethoxypropyl acetate,
3-methoxybutyl acetate, ethyl 3-ethoxypropionate, isobutyl
isobutyrate, ethyl lactate, butyl lactate, butyl glycolate,
dimethyl adipate, glutarate, succinate, ethylene carbonate,
propylene carbonate, butyrolactone, or a combination thereof. In
certain aspects, the oxygenated solvent comprises a glycol ether.
In other facets, the glycol ether comprises methyl glycol, ethyl
glycol, propyl glycol, isopropyl glycol, butyl glycol, methyl
diglycol, ethyl diglycol, butyl diglycol, ethyl triglycol, butyl
triglycol, diethylene glycol dimethyl ether, methoxypropanol,
isobutoxypropanol, isobutyl glycol, propylene glycol monoethyl
ether, 1-isopropoxy-2-propanol, propylene glycol mono-n-propyl
ether, propylene glycol n-butyl ether, methyl dipropylene glycol,
methoxybutanol, or a combination thereof. In specific aspects, the
oxygenated solvent comprises a ketone. In some facets, the ketone
comprises acetone, methyl ethyl ketone, methyl propyl ketone,
methyl isopropyl ketone, methyl butyl ketone, methyl isobutyl
ketone, methyl amyl ketone, methyl isoamyl ketone, diethyl ketone,
ethyl amyl ketone, dipropyl ketone, diisopropyl ketone,
cyclohexanone, methylcylcohexanone, trimethylcyclohexanone, mesityl
oxide, diisobutyl ketone, isophorone, or a combination thereof. In
particular aspects, the oxygenated solvent comprises an ether. In
additional facets, the ether comprises diethyl ether, diisopropyl
ether, dibutyl ether, di-sec-butyl ether, methyl tert-butyl ether,
tetrahydrofuran, 1,4-dioxane, metadioxane, or a combination
thereof.
[0073] In some embodiments, the liquid organic compound comprises a
chlorinated hydrocarbon. In specific aspects, the chlorinated
hydrocarbon comprises methylene chloride, trichloromethane,
tetrachloromethane, ethyl chloride, isopropyl chloride,
1,2-dichloroethane, 1,1,1-trichloroethane, trichloroethylene,
1,1,2,2-tetrachlorethane, 1,2-dichloroethylene, perchloroethylene,
1,2-dichloropropane, chlorobenzene, or a combination thereof.
[0074] In further embodiments, the liquid organic compound
comprises a nitrated hydrocarbon. In specific aspects, the nitrated
hydrocarbon comprises a nitroparaffin, N-methyl-2-pyrrolidone, or a
combination thereof.
[0075] In additional embodiments, the liquid organic compound
comprises a miscellaneous organic liquid. In some aspects, the
miscellaneous organic liquid comprises carbon dioxide, acetic acid,
methylal, dimethylacetal, N,N-dimethylformamide,
N,N-dimethylacetamide, dimethylsulfoxide, tetramethylene suflone,
carbon disulfide, 2-nitropropane, N-methylpyrrolidone,
hexamethylphosphoric triamide, 1,3-dimethyl-2-imidazolidinone, or a
combination thereof.
[0076] In specific embodiments, the liquid organic compound
comprises a plasticizer. In general facets, the plasticizer
comprises an adipate, an azelate, a citrate, a chlorinated
plasticizer, an epoxide, a phosphate, a sebacate, a phthalate, a
polyester, a trimellitate, or a combination thereof.
[0077] In other embodiments, the liquid component comprises an
inorganic compound. In specific aspects, the inorganic compound
comprises ammonia, hydrogen cyanide, hydrogen fluoride, hydrogen
cyanide, sulfur dioxide, or a combination thereof.
[0078] In many embodiments, the liquid component comprises water.
In particular aspects, the liquid component comprising water
further comprises methanol, ethanol, propanol, isopropyl alcohol,
tert-butanol, ethylene glycol, methyl glycol, ethyl glycol, propyl
glycol, butyl glycol, ethyl diglycol, methoxypropanol,
methyldipropylene glycol, dioxane, tetrahydorfuran, acetone,
diacetone alcohol, dimethylformamide, dimethyl sulfoxide,
ethylbenzene, tetrachloroethylene, p-xylene, toluene, diisobutyl
ketone, tricholorethylene, trimethylcyclohexanol, cyclohexyl
acetate, dibutyl ether, trimethylcyclohexanone,
1,1,1-tricholoroethane, hexane, hexanol, isobutyl acetate, butyl
acetate, isophorone, nitropropane, butyl glycol acetate,
2-nitropropane, methylene chloride, methyl isobutyl ketone,
cyclohexanone, isopropyl acetate, methylbenzyl alcohol,
cyclohexanol, nitroethane, methyl tert-butyl ether, ethyl acetate,
diethyl ether, butanol, butyl glycolate, isobutanol, 2-butanol,
propylene carbonate, ethyl glycol acetate, methyl acetate, methyl
ethyl ketone, or a combination thereof.
[0079] In general embodiments, the coating comprises a colorant. In
some aspects, the colorant comprises a pigment, a dye, a pH
indicator, or a combination thereof. In specific aspects, the
colorant comprises a pigment. In some aspects, the biomolecule
composition comprises 0.001% to 100% of the pigment, including all
intermediate ranges and combinations thereof. In particular facets,
the pigment volume concentration of the coating is 20% to 60%,
including all intermediate ranges and combinations thereof. In
other aspects, the pigment comprises a corrosion resistance
pigment, a camouflage pigment, a color property pigment, an
extender pigment, or a combination thereof. In particular aspects,
the pigment comprises a corrosion resistance pigment. In some
facets, the corrosion resistance pigment comprises aluminum flake,
aluminum triphosphate, aluminum zinc phosphate, ammonium chromate,
barium borosilicate, barium chromate, barium metaborate, basic
calcium zinc molybdate, basic carbonate white lead, basic lead
silicate, basic lead silicochromate, basic lead silicosulfate,
basic zinc molybdate, basic zinc molybdate-phosphate, basic zinc
molybdenum phosphate, basic zinc phosphate hydrate, bronze flake,
calcium barium phosphosilicate, calcium borosilicate, calcium
chromate, calcium plumbate, calcium strontium phosphosilicate,
calcium strontium zinc phosphosilicate, dibasic lead phosphite,
lead chromosilicate, lead cyanamide, lead suboxide, lead sulfate,
mica, micaceous iron oxide, red lead, steel flake, strontium
borosilicate, strontium chromate, tribasic lead phophosilicate,
zinc borate, zinc borosilicate, zinc chromate, zinc dust, zinc
hydroxy phosphite, zinc molybdate, zinc oxide, zinc phosphate, zinc
potassium chromate, zinc silicophosphate hydrate, zinc
tetraoxylchromate, or a combination thereof. In specific facets,
the coating comprising the corrosion resistance pigment is a metal
surface coating, a primer, or a combination thereof. In other
aspects, the pigment comprises a camouflage pigment. In specific
facets, the camouflage pigment comprises an anthraquinone black, a
chromium oxide green, or a combination thereof. In some aspects,
the pH indicator is a colorimetric or a fluorimetric indicator.
Examples of colorimetric include Alizarin, Alizarin S, Brilliant
Yellow, Lacmoid, Neutral Red, Rosolic Red, or a combination
thereof. In specific instances, the colorimetric indicator is a pH
indicator that undergoes a color change between pH 8 to pH 9. For
example the following fluorimetric indicators are SNARF-1, BCECF,
HPTS, Fluroescein, or a combination thereof. In certain
embodiments, the fluorescence indicator have reduced fluorescence
at a lower pH. In specific instances, the fluorimetric indicator is
a pH indicator that undergoes a fluorescence change between pH 8 to
pH 9. Additional pH indicators are described, for example, in
"Using Acid-Base Indicators to Visually Estimate the Ph of
Solutions" by Marcia L. Gillette, Chemical Education Resources,
Incorporated, 1995.
[0080] In further embodiments, the pigment comprises a color
property pigment. In additional aspects, the color property pigment
comprises a black pigment, a brown pigment, a white pigment, a
pearlescent pigment, a violet pigment, a blue pigment, a green
pigment, a yellow pigment, an orange pigment, a red pigment, a
metallic pigment, or a combination thereof. In particular facets,
the color property pigment comprises aniline black, anthraquinone
black, carbon black; copper carbonate, graphite, iron oxide,
micaceous iron oxide, manganese dioxide, azo condensation,
benzimidazolone, iron oxide, metal complex brown, antimony oxide,
basic lead carbonate, lithopone, titanium dioxide, white lead, zinc
oxide, zinc sulphide, titanium dioxide and ferric oxide covered
mica, bismuth oxychloride crystal, dioxanine violet, carbazol Blue,
carbazole Blue, cobalt blue, copper phthalocyanine, dioxanine Blue,
indanthrone, phthalocyanin blue, Prussian blue, ultramarine, chrome
green, chromium oxide green, halogenated copper phthalocyanine,
hydrated chromium oxide, phthalocyanine green, anthrapyrimidine,
arylamide yellow, barium chromate, benzimidazolone yellow, bismuth
vanadate, cadmium sulfide yellow, complex inorganic color pigment,
diarylide yellow, disazo condensation, flavanthrone, isoindoline,
isoindolinone, lead chromate, nickel azo yellow, organic metal
complex, quinophthalone, yellow iron oxide, yellow oxide, zinc
chromate, perinone orange, pyrazolone orange, anthraquinone,
benzimidazolone, BON arylamide, cadmium red, cadmium selenide,
chrome red, dibromanthrone, diketopyrrolo-pyrrole pigment, disazo
condensation pigment, lead molybdate, perylene, pyranthrone,
quinacridone, quinophthalone, red iron oxide, red lead, toluidine
red, tonor pigment, .beta.-naphthol red, aluminum flake, aluminum
non-leafing, gold bronze flake, zinc dust, stainless steel flake,
nickel flake, nickel powder, or a combination thereof.
[0081] In general embodiments, the pigment comprises an extender
pigment. In some aspects, the extender pigment comprises a barium
sulphate, a calcium carbonate, a kaolin, a calcium sulphate, a
silicate, a silica, an alumina trihydrate, or a combination
thereof.
[0082] In general embodiments, the coating comprises an additive.
In some aspects, the additive comprises 0.001% to 20.0% by weight,
including all intermediate ranges and combinations thereof, of the
coating. In specific facets, the additive comprises an accelerator,
an adhesion promoter, an antifoamer, anti-insect additive, an
antioxidant, an antiskinning agent, a buffer, a catalyst, a
coalescing agent, a corrosion inhibitor, a defoamer, a dehydrator,
a dispersant, a drier, electrical additive, an emulsifier, a
filler, a flame/fire retardant, a flatting agent, a flow control
agent, a gloss aid, a leveling agent, a marproofing agent, a
preservative, a silicone additive, a slip agent, a surfactant, a
light stabilizer, a Theological control agent, a wetting additive,
or a combination thereof. In additional aspects, the additive
comprises a preservative. In specific aspects, the preservative
comprises an in-can preservative, an in-film preservative, or a
combination thereof. In general aspects, the preservative comprises
a biocide. In particular facets, the biocide comprises a
bactericide, a fungicide, an algaecide, or a combination thereof.
In other aspects, the additive comprises a wetting additive, a
dispersant, or a combination thereof. In further aspects, the
additive comprises an anti-foamer, a defoamer, or a combination
thereof. In additional aspects, the additive comprises a
rheological control agent. In particular facets, the Theological
control agent comprises a thickener, a viscosifier, or a
combination thereof. In specific aspects, the additive comprises a
corrosion inhibitor. In some facets, the corrosion inhibitor
comprises an in-can corrosion inhibitor, a flash corrosion
inhibitor, or a combination thereof. In particular aspects, the
additive comprises a light stabilizer. In specific facets, the
light stabilizer comprises a UV absorber, a radical scavenger, or a
combination thereof.
[0083] In some embodiments, the coating is a multi-pack coating. In
particular aspects, the coating is stored in a two to five
containers prior to application to the surface. In specific
aspects, 0.001% to 100% of the biomolecular composition, including
all intermediate ranges and combinations thereof, is stored in a
container of a multipack coating, and at least one additional
coating component is stored in another container of a multipack
coating. In some aspects, the container comprising the biomolecular
composition further comprises an additional coating component. In
particular facets, the additional coating component comprises a
preservative, a wetting agent, a dispersing agent, a buffer, a
liquid component, a rheological modifier, or a combination thereof.
In specific facets, the additional coating component comprises
glycerol.
[0084] The invention provides a method of detoxification of a
surface contaminated with an organophosphorus compound, comprising
the step of: contacting a surface contaminated with an
organophosphorous compound with a coating comprising a biomolecule
composition, wherein the biomolecule composition comprises a
phosphoric triester hydrolase. In some aspects, the method further
comprises the step of contacting the surface with a caustic agent;
a decontaminating foam, a combination of baking condition heat and
carbon dioxide, or a combination thereof.
[0085] The invention provides a method of detoxification of an
organophosphorus compound, comprising the step of: contacting an
organophosphorous compound with a coating comprising a biomolecule
composition, wherein the biomolecule composition comprises a
phosphoric triester hydrolase. In some aspects, the method further
comprises the step of contacting the organophosphorus compound with
a caustic agent; a decontaminating foam, a combination of baking
condition heat and carbon dioxide, or a combination thereof.
[0086] The invention provides methods of reducing the concentration
of an organophosphorus compound upon a surface, comprising the
steps of: applying to the surface a coating comprising a
biomolecule composition, wherein the biomolecule composition
comprises a phosphoric triester hydrolase, and contacting the
surface with an organophosphorus compound. In some aspects, the
method further comprises the step of contacting the surface with a
caustic agent; a decontaminating foam, a combination of baking
condition heat and carbon dioxide, or a combination thereof.
[0087] In certain embodiments, the organophosphorus compound
comprises a chemical warfare agent. In some aspects, the chemical
warfare agent comprises a persistent agent. In additional aspects,
the chemical warfare agent comprises a G-agent, a V agent, or a
combination thereof. In particular facets, the G-agent comprises
soman, sarin, cyclosarin, tabun, or a combination thereof. In
further facets, the V-agent comprises VX, Russian VX, or a
combination thereof. In other facets, the organophosphorus compound
comprises a pesticide. In particular facets, the pesticide
comprises a persistent organophosphorous compound. In general
facets, the pesticide comprises bromophos-ethyl, chlorpyrifos,
chlorfenvinphos, chlorothiophos, chlorpyrifos-methyl, coumaphos,
crotoxyphos, crufomate, cyanophos, diazinon, dichlofenthion,
dichlorvos, dursban, EPN, ethoprop, ethyl-parathion, etrimifos,
famphur, fensulfothion, fenthion, fenthrothion, isofenphos,
jodfenphos, leptophos-oxon, malathion, malaoxon, methyl-parathion,
mevinphos, paraoxon, parathion, parathion-methyl, pirimiphos-ethyl,
pirimiphos-methyl, pyrazophos, quinalphos, ronnel, sulfopros,
sulfotepp, trichloronate, or a combination thereof.
[0088] The invention provides a coating or a paint comprising, in
various aspects, 0.001% to 40% by weight or volume a biomolecule
composition, including all intermediate ranges and combinations
thereof, wherein the biomolecule composition comprises an active
biomolecule. The invention provides a coating or a paint comprising
a biomolecule composition that comprise, in various aspects, a
proteinaceous molecule that binds a ligand, an enzyme, a phosphoric
triester hydrolase, an organophosphorus hydrolase, an
organophosphorus hydrolase and a buffer, or a combination thereof.
The invention further provides a coating or a paint comprising, in
various further aspects, a microorganism based particulate
material, a whole cell material, or a combination thereof, wherein
the material comprises an active biomolecule, an enzyme, a
phosphoric triester hydrolase, an organophosphorus hydrolase, an
organophosphorus hydrolase and a buffer, or a combination thereof.
The invention specifically provides a coating or paint comprising
0.001% to 40% by weight or volume, including all intermediate
ranges and combinations thereof, a microorganism based particulate
material, a whole cell material, or a combination thereof, wherein
the material comprises an active biomolecule.
[0089] The invention provides a coating or paint, the improvement
comprising inclusion of a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
[0090] The invention provides a coating or paint, the improvement
comprising inclusion of 0.001% to 40% by weight or volume a
biomolecule composition, wherein the biomolecule composition
comprises an active biomolecule, a proteinaceous molecule that
binds a ligand, an enzyme, a phosphoric triester hydrolase, an
organophosphorus hydrolase, an organophosphorus hydrolase and a
buffer, or any combination thereof.
[0091] The invention provides a coating or paint, the improvement
comprising inclusion of a microorganism based particulate material,
wherein the microorganism based particulate material that comprises
an active biomolecule.
[0092] The invention provides a coating or paint, the improvement
comprising inclusion of a whole cell particulate material, wherein
the particulate material comprises an active biomolecule.
[0093] The invention provides a coating or paint, the improvement
comprising inclusion of 0.001% to 40% by weight or volume of a
whole cell particulate material, including all intermediate ranges
and combinations thereof, wherein the whole cell particulate
material comprises an active biomolecule.
[0094] The invention provides a coating or paint, the improvement
comprising inclusion of a whole cell particulate material, wherein
the particulate material comprises an enzyme.
[0095] The invention provides a coating or paint, the improvement
comprising inclusion of a whole cell particulate material, wherein
the particulate material comprises a phosphoric triester
hydrolase.
[0096] The invention provides a coating or paint, the improvement
comprising inclusion of a whole cell particulate material, wherein
the particulate material comprises an organophosphorus
hydrolase.
[0097] The invention provides a coating or paint, the improvement
comprising inclusion of a whole cell particulate material, wherein
the particulate material comprises an organophosphorus hydrolase
and a buffer.
[0098] The invention provides a water-borne or a solvent-borne
coating or paint comprising a biomolecule composition, wherein the
biomolecule composition comprises an active biomolecule.
[0099] The invention provides a latex or oil-based coating or paint
comprising a whole cell particulate material, wherein the whole
cell particulate material comprises a phosphoric triester
hydrolase. In certain aspect the coating or paint comprises a
buffer.
[0100] The invention provides a latex or oil-based coating or paint
comprising a whole cell particulate material and a buffer, wherein
the whole cell particulate material comprises a phosphoric triester
hydrolase. In specific aspects, the coating or paint comprises
0.001% to 40% by weight or volume, including all intermediate
ranges and combinations thereof, of a whole cell particulate
material, wherein the whole cell particulate material comprises a
phosphoric triester hydrolase. In certain aspects the coating or
paint is a multipack coating. In some facets, one container of the
multipack coating comprises 0.001% to 40%, by weight or volume of
the coating or paint, including all intermediate ranges and
combinations thereof, the whole cell particulate material. In
certain aspects, the container comprising the whole cell
particulate material further comprises a preservative, a wetting
agent, a dispersing agent, the buffer, a liquid component, a
rheological modifier, or a combination thereof.
[0101] The invention provides a two-pack a latex or oil-based
coating or paint, wherein one container comprises 100 parts by
volume coating or paint, wherein a second container comprises 3
parts by volume of a biomolecular composition comprising a whole
cell particulate material, wherein the whole cell particulate
material comprises an organophosphorus hydrolase, and wherein each
part of the biomolecular composition comprises 1 mg of whole cell
particulate material and 50% glycerol and/or a buffer, and wherein
the buffer comprises ammonium bicarbonate, a monobasic buffer, a
dibasic phosphate buffer, Trizma base, a 5 zwitterionic buffer, or
a combination thereof.
[0102] The invention also provides a non-film forming coating
comprising a biomolecule composition, wherein the biomolecule
composition comprises an active biomolecule.
[0103] The invention provides an elastomer comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
[0104] The invention provided a filler comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
[0105] The invention provides an adhesive comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
[0106] The invention provides a sealant comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
[0107] The invention provides a material applied to a textile,
comprising a biomolecule composition, wherein the biomolecule
composition comprises an active biomolecule.
[0108] The invention provides a wax comprising a biomolecule
composition, wherein the biomolecule composition comprises an
active biomolecule.
[0109] The invention provides a surface treatment comprising a
biomolecule composition, wherein the biomolecule composition
comprises an active biomolecule. In certain embodiments, the
surface treatment is a coating, a paint, a non-film forming
coating, an elastomer, an adhesive, an sealant, a material applied
to a textile, or a wax. In other aspects, the surface treatment
comprises a pH indicator.
DETAILED DESCRIPTION OF THE INVENTION
[0110] One skilled in the art will readily appreciate that the
present invention is well adapted to carry out the objects and
obtain the ends and advantages mentioned as well as those inherent
therein. It should be understood, however, that the enzyme
compositions, enzymes, microorganism-based particulate materials,
compounds, coatings, paints, films, methods, procedures, and
techniques described herein are presently representative of
preferred embodiments. These techniques are intended to be
exemplary, are given by way of illustration only, and are not
intended as limitations on the scope. Other objects, features, and
advantages of the present invention will be readily apparent to one
skilled in the art from the following detailed description;
specific examples and claims; and various changes, substitutions,
other uses and modifications that may be made to the invention
disclosed herein without departing from the scope and spirit of the
invention or as defined by the scope of the appended claims.
[0111] As used herein other than the claims, the terms "a," "an,"
"the," and "said" means one or more. As used herein in the
claim(s), when used in conjunction with the words "comprises" or
"comprising," the words "a," "an," "the," or "said" may mean one or
more than one. As used herein "another" may mean at least a second
or more.
[0112] All patents and publications mentioned in this specification
are indicative of the levels of those skilled in the art to which
the invention pertains. All patents and publications so referenced
are herein incorporated by reference to the same extent as if each
individual publication was specifically and individually indicated
to be incorporated by reference.
[0113] As would be known to one of ordinary skill in the art, many
variations of nomenclature are commonly used to refer to a specific
chemical composition. Accordingly, several common alternative names
may be provided herein in quotations and parentheses/brackets, or
other grammatical technique, adjacent to a chemical composition's
preferred designation when referred to herein. Additionally, many
chemical compositions referred to herein are further identified by
a Chemical Abstracts Service registration number. As would be known
to those of ordinary skill in the art, the Chemical Abstracts
Service provides a unique numeric designation, denoted herein as
"CAS No.," for specific chemicals and some chemical mixtures, which
unambiguously identifies a chemical composition's molecular
structure.
[0114] In various embodiments described herein, exemplary values
are specified as a range. Examples of such ranges cited herein
include, for example, a size of a biomolecule, a tempature for
growth and/or preparation of a microorganism, a chemical moiety's
content in a coating component, a coating component's content in a
coating composition and/or film, a coating component's mass, a
glass transition temperature ("T.sub.g"), a temperature for a
chemical reaction (e.g., film formation, chemical modification of a
coating component), the thickness of a coating and/or film upon a
surface, etc. It will be understood that herein the phrase
"including all intermediate ranges and combinations thereof
associated with a given range is all integers and sub-ranges
comprised within a cited range. For example, citation of a range
"0.03% to 0.07%, including all intermediate ranges and combinations
thereof is specific values within the sited range, such as, for
example, 0.03%, 0.04%, 0.05%, 0.06%, and 0.07%, as well as various
combinations of such specific values, such as, for example, 0.03%,
0.06% and 0.07%, 0.04% and 0.06%, or 0.05% and 0.07%, as well as
sub-ranges such as 0.03% to 0.05%, 0.04% to 0.07%, or 0.04% to
0.06%, etc. Additionally, example 12 provides additional
descriptions of specific numeric values within a cited range.
[0115] A. Biomolecules
[0116] As used herein, a "biomolecule composition" of the present
invention refers to a composition comprising a biomolecule. As used
herein, a "biomolecule" refers to a compound comprising of one or
more chemical moieties typically synthesized in living organisms,
including but not limited to, an amino acid, a nucleotide, a
polysaccharide or simple sugar, a lipid, or a combination thereof.
A preferred biomolecule of the present invention comprises a
proteinaceous molecule. As used herein a "proteinaceous molecule"
comprises a polymer formed from amino acids, such as a peptide or a
polypeptide. Examples of proteinaceous molecules include an enzyme,
an antibody, a receptor, a transport protein, structural protein,
or a combination thereof. Examples of a peptide include inhibitory
peptides of 3-15 amino acids.
[0117] In addition to the sources described herein for
biomolecules, reagents, living cells, etc., one of ordinary skill
in the art may obtain such materials and/or chemical formulas
thereof for use in the present invention from convenient source
such as a public database, a biological depository, and/or a
commercial vendor. For example, various nucleotide sequences,
including those that encode amino acid sequences, may be obtained
at a public database, such as the Entrez Nucleotides database found
at: http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=Nucleotide,
which includes sequences from other databases including GenBank,
RefSeq, and PDB. In another example, various amino acid sequences
may be obtained at a public database, such as the Entrez databank
found at: http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=Protein,
which includes sequences from other databases including SwissProt,
PIR, PRF, PDB, GenBank, and RefSeq. Additional examples of such
databases are listed at:
http://www.rcsb.org/pdb/links.html#Databases, and numerous nucleic
acid sequences and/or encoded amino acid sequences can be obtained
from such sources. In a further example, biological materials that
comprise, or are capable of comprising such biomolecules (including
living cells), may be obtained from a depository such as the
American Type Culture Collection ("ATCC"), P.O. Box 1549 Manassas,
Va. 20108, USA. In an additional example, biomolecules, chemical
reagents, biological materials, and equipment may be obtained, as
is well known to those of ordinary skill in the art, from
commercial vendors such as Amersham Biosciences.RTM., 800
Centennial Avenue, P.O. Box 1327, Piscataway, N.J. 08855-1327 USA;
BD Biosciences.RTM., including Clontech.RTM., Discovery
Labware.RTM., Immunocytometry Systemse and Pharmingene, 1020 East
Meadow Circle, Palo Alto, Calif. 94303-4230 USA; Invitrogen, 1600
Faraday Avenue, PO Box 6482, Carlsbad, Calif. 92008 USA; New
England Biolabs.RTM., 32 Tozer Road, Beverly, Mass. 01915-5599 USA;
Merck.RTM., One Merck Drive, P.O. Box 100, Whitehouse Station, N.J.
08889-0100 USA; Novagene.RTM., 441 Charmany Dr., Madison, Wis.
53719-1234 USA; Promega.RTM., 2800 Woods Hollow Road, Madison Wis.
53711 USA; Pfizer.RTM., including Pharmacia.RTM., 235 East 42nd
Street, New York, N.Y. 10017 USA; Quiagen.RTM., 28159 Avenue
Stanford, Valencia, Calif. 91355 USA; Sigma-Aldrich.RTM., including
Sigma, Aldrich, Fluka, Supelco and Sigma-Aldrich Fine Chemicals, PO
Box 14508, Saint Louis, Mo. 63178 USA; Stratagene.RTM., 11011 N.
Torrey Pines Road, La Jolla, Calif. 92037 USA, etc.
[0118] In addition to those techniques specifically described
herein, one of ordinary skill in the art may manipulate a cell,
nucleic acid sequence, amino acid sequence, and the like, in light
of the present disclosures, using standard techniques known in the
art [see, for example, In "Molecular Cloning" (Sambrook, J., and
Russell, D. W., Eds.) 3rd Edition, Cold Spring Harbor, N.Y.: Cold
Spring Harbor Laboratory Press, 2001; In "Current Protocols in
Molecular Biology" (Chanda, V. B. Ed.) John Wiley & Sons, 2002;
In "Current Protocols in Nucleic Acid Chemistry" (Harkins, E. W.
Ed.) John Wiley & Sons, 2002; In "Current Protocols in Protein
Science" (Taylor, G. Ed.) John Wiley & Sons, 2002; In "Current
Protocols in Cell Biology" (Morgan, K. Ed.) John Wiley & Sons,
2002; In "Current Protocols in Pharmacology" (Taylor, G. Ed.) John
Wiley & Sons, 2002; In "Current Protocols in Cytometry"
(Robinson, J. P. Ed.) John Wiley & Sons, 2002; In "Current
Protocols in Immunology" (Coico, R. Ed.) John Wiley & Sons,
2002].
[0119] B. Enzymes
[0120] The selection of a biomolecule for use in the present
invention depends on the desired property that is to be conferred
to a composition of the present invention. A preferred biomolecule
of the present invention comprises an enzyme, as enzymatic activity
is a preferred property to be conferred to a biomolecule
composition, coating and/or paint in the present invention. As used
herein, the term "enzyme" refers to a molecule that possesses the
ability to accelerate a chemical reaction, and comprises one or
more chemical moieties typically synthesized in living organisms,
including but not limited to, an amino acid, a nucleotide, a
polysaccharide or simple sugar, a lipid, or a combination thereof.
As used herein, the term "bioactive" refers to the ability of an
enzyme to accelerate a chemical reaction differentiating such
activity from a like ability of a composition, and/or a method that
does not comprise an enzyme to accelerate a chemical reaction.
[0121] In preferred embodiments, an enzyme comprises a
proteinaceous molecule. It is contemplated that any proteinaceous
molecule that functions as an enzyme, whether identical to the
wild-type amino acid sequence encoded by an isolated gene, a
functional equivalent of such a sequence, or a combination thereof,
may be used in the present invention. As used herein, a "wild-type
enzyme" refers to an amino acid sequence that functions as an
enzyme and is identical to the sequence encoded by an isolated gene
from a natural source. As used herein, a "functional equivalent" to
the wild-type enzyme is a proteinaceous molecule comprising a
sequence and/or a structural analog of a wild-type enzyme's
sequence and/or structure and functions as an enzyme. The
functional equivalent enzyme may possess similar or the same
enzymatic properties, such as catalyzing chemical reactions of the
wild-type enzyme's EC classification, or may possess other desired
enzymatic properties, such as catalyzing the desirable chemical
reactions of an enzyme that is related to the wild-type enzyme by
sequence and/or structure. Examples of a functional equivalent of a
wild-type enzyme are described herein, and include mutations to a
wild-type enzyme sequence, such as a sequence truncation, an amino
acid substitution, an amino acid modification, a fusion protein, or
a combination thereof, wherein the altered sequence functions as an
enzyme.
[0122] In certain embodiments, an enzyme may comprise a simple
enzyme, a complex enzyme, or a combination thereof. As known
herein, a "simple enzyme" is an enzyme wherein the chemical
properties of moieties found in its amino acid sequence is
sufficient for producing enzymatic activity. As known herein, a
"complex enzyme" is an enzyme whose catalytic activity functions
only when an apo-enzyme is combined with a prosthetic group, a
co-factor, or a combination thereof. An "apo-enzyme" is a
proteinaceous molecule and is catalytically inactive without the
prosthetic group and/or co-factor. As known herein, a "prosthetic
group" or "co-enzyme" is non-proteinaceous molecule that is
attached to the apo-enzyme to produce a catalytically active
complex enzyme. As known herein, a "holo-enzyme" is a complex
enzyme that comprises an apo-enzyme and a co-enzyme. As known
herein, a "co-factor" is a molecule that acts in combination with
the apo-enzyme to produce a catalytically active complex enzyme. In
some aspects, a prosthetic group is one or more bound metal atoms,
a vitamin derivative, or a combination thereof. Examples of metal
atoms that may be used as a prosthetic group and/or a co-factor
include Ca, Cd, Co, Cu, Fe, Mg, Mn, Ni, Zn, or a combination
thereof. Usually the metal atom is an ion, such as Ca.sup.2+,
Cd.sup.2+, Co.sup.2+, Cu.sup.2+, Fe.sup.+2, Mg.sup.2+, Mn.sup.2+,
Ni.sup.2+, Zn.sup.2+, or a combination thereof. As known herein, a
"metalloenzyme" is a complex enzyme that comprises an apo-enzyme
and a prosthetic group, wherein the prosthetic group comprises a
metal atom. As known herein, a "metal activated enzyme" is a
complex enzyme that comprises an apo-enzyme and a co-factor,
wherein the co-factor comprises a metal atom.
[0123] A chemical that binds a proteinaceous molecule is known
herein as a "ligand." As used herein, "bind" or "binding" refers to
a physical contact between the proteinaceous molecule at a specific
region of the proteinaceous molecule and the ligand in a reversible
fashion. Examples of binding interactions are well known in the
art, and include such interactions as a ligand known as an
"antigen" binding an antibody, a ligand binding a receptor, and the
like. A portion of the proteinaceous molecule wherein substrate
binding occurs is known herein as a "binding site." A ligand that
is acted upon by the enzyme in the accelerated chemical reaction is
known herein as a "substrate." A contact between the enzyme and a
substrate in a fashion suitable for the accelerated chemical
reaction to proceed is known herein as "substrate binding." A
portion of the enzyme involved in the chemical interactions that
contributed to the accelerated chemical reaction is known herein as
an "active site."
[0124] A chemical that slows or prevents the enzyme from conducting
the accelerated chemical reaction is known herein as an
"inhibitor." A contact between the enzyme and the inhibitor in a
fashion suitable for slowing or preventing the accelerated chemical
reaction to proceed upon a target substrate is known herein as
"inhibitor binding." In some embodiments, inhibitor binding occurs
at a binding site, an active site, or a combination thereof. In
some aspects, an inhibitor's binding occurs without the inhibitor
undergoing the chemical reaction. In specific aspects, the
inhibitor may also be a substrate such as in the case of an
inhibitor that precludes the enzyme from catalyzing the chemical
reaction of a target substrate for the period of time inhibitor
binding occurs at an active and/or binding site. In other aspects,
an inhibitor undergoes the chemical reaction at a rate that is
slower relative to a target substrate.
[0125] In some embodiments, enzymes may be described by the
classification system of The International Union of Biochemistry
and Molecular Biology ("IUBMB"). The IUBMB classifies enzymes by
the type of reaction catalyzed and enumerates each sub-class by a
designated enzyme commission number ("EC"). The IUBMB
classification of various enzymes may be obtained using the
computerized database at http:H/www.chem.qmw.ac.uk/iubmb/enzyme/.
Based on these broad categories, an enzyme may comprise an
oxidoreductase (EC 1), a transferase (EC 2), a hydrolase (EC 3), a
lyase (EC 4), an isomerase (EC 5), a ligase (EC 6), or a
combination thereof. Often, an enzyme may be able to catalyze
multiple reactions, and thus have multiple EC classifications.
[0126] Generally, the chemical reaction catalyzed by an enzyme
alters a moiety of a substrate. As used herein, a "moiety" or
"group," in the context of the field of chemistry, refers to a
chemical sub-structure that is a part of a larger molecule.
Examples of moiety include an acid halide, an acid anhydride, an
alcohol, an aldehyde, an alkane, an alkene, an alkyl halide, an
alkyne, an amide, an amine, an arene, an aryl halide, a carboxylic
acid, an ester, an ether, a ketone, a nitrile, a phenol, a sulfide,
a sulfonic acid, a thiol, etc.
[0127] An oxidoreductase catalyzes an oxido-reduction of a
substrate, wherein the substrate is either a hydrogen donor and/or
an electron donor. An oxidoreductase is generally classified by the
substrate moiety that is the donor or acceptor. Examples of
oxidoreductases include an oxidoreductase that acts on a donor
CH--OH moiety, (EC 1.1); an donor aldehyde or a donor oxo moiety,
(EC 1.2); a donor CH--CH moiety, (EC 1.3); a donor CH--NH.sub.2
moiety, (EC 1.4); a donor CH--NH moiety, (EC 1.5); a donor
nicotinamide adenine dinucleotide ("NADH") or a donor nicotinamide
adenine dinucleotide phosphate ("NADPH"), (EC 1.6); a donor
nitrogenous compound, (EC 1.7); a donor sulfur moiety, (EC 1.8); a
donor heme moiety, (EC 1.9); a donor diphenol or a related moiety
as donor, (EC 1.10); a peroxide as an acceptor, (EC 1.11); a donor
hydrogen, (EC 1.12); a single donor with incorporation of molecular
oxygen ("oxygenase"), (EC 1.13); a paired donor, with incorporation
or reduction of molecular oxygen, (EC 1.14); a superoxide radical
as an acceptor, (EC 1.15); an oxidoreductase that oxidises a metal
ion, (EC 1.16); an oxidoreductase that acts on a donor CH.sub.2
moiety, (EC 1.17); a donor iron-sulfur protein, (EC 1.18); a donor
reduced flavodoxin, (EC 1.19); a donor phosphorus or donor arsenic
moiety, (EC 1.20); an oxidoreductase that acts on an X--H and an
Y--H to form an X-Y bond, (EC 1.21); as well as a other
oxidoreductase, (EC 1.97) [Is this the right number?]; or a
combination thereof.
[0128] A transferase catalyzes the transfer of a moiety from a
donor compound to an acceptor compound. A transferase is generally
classified based on the chemical moiety transferred. Examples of
transferases include an transferase that catalyzes the transfer of
a one-carbon moiety, (EC 2.1); an aldehyde or a ketonic moiety, (EC
2.2); an acyl moiety, (EC 2.3); a glycosyl moiety, (EC 2.4); an
alkyl or an aryl moiety other than a methyl moiety, (EC 2.5); a
nitrogenous moiety, (EC 2.6); a phosphorus-containing moiety, (EC
2.7); a sulfur-containing moiety, (EC 2.8); a selenium-containing
moiety, (EC 2.9); or a combination thereof.
[0129] A hydrolase catalyses the hydrolysis of a chemical bond. A
hydrolase is generally classified based on the chemical bond
cleaved or the moiety released or transferred by the hydrolysis
reaction. Examples of hydrolases include a hydrolase that catalyzes
the hydrolysis of an ester bond, (EC 3.1); a glycosyl
released/transferred moiety, (EC 3.2); an ether bond, (EC 3.3); a
peptide bond, (EC 3.4); a carbon-nitrogen bond, other than a
peptide bond, (EC 3.5); an acid anhydride, (EC 3.6); a
carbon-carbon bond, (EC 3.7); a halide bond, (EC 3.8); a
phosphorus-nitrogen bond, (EC 3.9); a sulfur-nitrogen bond, (EC
3.10); a carbon-phosphorus bond, (EC 3.11); a sulfur-sulfur bond,
(EC 3.12); a carbon-sulfur bond, (EC 3.13); or a combination
thereof.
[0130] A lyase catalyzes the cleavage of a chemical bond by
reactions other than hydrolysis or oxidation. A lyase is generally
classified based on the chemical bond cleaved. Examples of lyases
include a lyase that catalyzes the cleavage of a carbon-carbon
bond, (EC 4.1); a carbon-oxygen bond, (EC 4.2); a carbon-nitrogen
bond, (EC 4.3); a carbon-sulfur bond, (EC 4.4); a carbon-halide
bond, (EC 4.5); a phosphorus-oxygen bond, (EC 4.6); a other lyase,
(EC 4.99) [Is this the right number?]; or a combination
thereof.
[0131] An isomerase catalyzes a change within one molecule.
Examples of isomerases include a racemase or an epimerase, (EC
5.1); a cis-trans-isomerases, (EC 5.2); an intramolecular
isomerase, (EC 5.3); an intramolecular transferase, (EC 5.4); an
intramolecular lyase, (EC 5.5); a other isomerases, (EC 5.99); or a
combination thereof.
[0132] A ligase catalyses the formation of a chemical bond between
two substrates with the hydrolysis of a diphosphate bond of a
triphosphate such as ATP. A ligase is generally classified based on
the chemical bond created. Examples of lyases include a ligase that
form a carbon-oxygen bond, (EC 6.1); a carbon-sulfur bond, (EC
6.2); a carbon-nitrogen bond, (EC 6.3); a carbon-carbon bond, (EC
6.4); a phosphoric ester bond, (EC 6.5); or a combination
thereof.
[0133] 1. Preferred Enzymes
[0134] A preferred enzyme for use in the present invention
comprises a hydrolase. A preferred hydrolase comprises an esterase.
A preferred esterase comprises an esterase that catalyzes the
hydrolysis of an organophosphorus compound. Examples of such
preferred esterases are those identified by enzyme commission
number EC 3.1.8, the phosphoric triester hydrolases. As used
herein, a phosphoric triester hydrolase catalyzes the hydrolytic
cleavage of an ester from a phosphorus moiety. Examples of a
phosphoric triester hydrolase include an aryldialkylphosphatase, a
diisopropyl-fluorophosphatase, or a combination thereof.
[0135] An aryldialkylphosphatase (EC 3.1.8.1) is also known by its
systemic name "aryltriphosphate dialkylphosphohydrolase," and
various enzymes in this category have been known in the art by
names such as "organophosphate hydrolase"; "paraoxonase";
"A-esterase"; "aryltriphosphatase"; "organophosphate esterase";
"esterase B1"; "esterase E4"; "paraoxon esterase";
"pirimiphos-methyloxon esterase"; "OPA anhydrase";
"organophosphorus hydrolase"; "phosphotriesterase"; "PTE";
"paraoxon hydrolase"; "OPH"; and "organophosphorus acid anhydrase."
An aryldialkylphosphatase catalyzes the following reaction: aryl
dialkyl phosphate+H.sub.2O=an aryl alcohol+dialkyl phosphate.
Examples of an aryl dialkyl phosphate include an organophosphorus
compound comprising a phosphonic acid ester, a phosphinic acid
ester, or a combination thereof.
[0136] A diisopropyl-fluorophosphatase (EC 3.1.8.2) is also known
by its systemic name "diisopropyl-fluorophosphate fluorohydrolase,"
and various enzymes in this category have been known in the art by
names such as "DFPase"; "tabunase"; "somanase"; "organophosphorus
acid anhydrolase"; "organophosphate acid anhydrase"; "OPA
anhydrase"; "diisopropylphosphofluoridase";
"dialkylfluorophosphatase"; "diisopropyl phosphorofluoridate
hydrolase"; "isopropylphosphorofluoridase"; and
"diisopropylfluorophosphonate dehalogenase." A
diisopropyl-fluorophosphat- ase catalyzes the following reaction:
diisopropyl fluorophosphate+H.sub.2O- =fluoride+diisopropyl
phosphate. Examples of a diisopropyl fluorophosphates include an
organophosphorus compound comprising a phosphorus-halide, a
phosphorus-cyanide, or a combination thereof.
[0137] Examples of phosphoric triester hydrolases and cleaved OP
compounds and bond types are shown at Table 1.
1TABLE 1 Phosphoric Triester Hydrolases OP Compound Phosphoryl
Bond-Type and Phosphoryl Bond Types Cleaved by Enzyme Various OP
Sarin, VX, Pesticides Soman R-VX Tabun Enzyme P-C P-O P-F P-S P-CN
OPH.sup.a,b,c,d,e,f,g - + + + + Human + + + - +
Paraoxonase.sup.h,i,j OPAA-2.sup.k,l - + + - + Squid DFPase.sup.m -
- + - - .sup.aDumas, D. P. et al., 1989a; .sup.bDumas, D. P. et
al., 1989b; .sup.cDumas, D. P. et al., 1990; .sup.dDave, K. I. et
al., 1993; .sup.eChae, M. Y. et al., 1994; .sup.fLai, K. et al.,
1995; .sup.gKolakowski, J. E. et al., 1997; .sup.hHassett, C. et
al., 1991; .sup.iJosse, D. et al., 2001; .sup.jJosse, D. et al.,
1999; .sup.kDeFrank, J. J. et al. 1993; .sup.lCheng, T. -C. et al.,
1996; .sup.mHoskin, F. C. G. and Roush, A. H., 1982.
[0138] A preferred substrate for a composition of the present
invention comprises an organophosphorus compound. As used herein,
an "organophosphorus compound" is a compound comprising a
phosphoryl center, and further comprises two or three ester
linkages. In some aspects, the type of phosphoester bond and/or
additional covalent bond at the phosphoryl center classifies an
organophosphorus compound. In embodiments wherein the phosphorus is
linked to an oxygen by a double bond (P.dbd.O), the OP compound is
known as an "oxon OP compound" or "oxon organophosphorus compound."
In embodiments wherein the phosphorus is linked to a sulfur by a
double bond (P.dbd.S), the OP compound is known as a "thion OP
compound" or "thion organophosphorus compound." Additional examples
of bond-type classified OP compounds include a phosphonocyanate,
which comprises a P--CN bond; a phosphoroamidate, which comprises a
P--N bond; a phosphotriester, which comprises a P--O bond; a
phosphodiester, which comprises a P--O bond; a phosphonofluoridate,
which comprises a P--F bond; and a phosphonothiolate, which
comprises a P--S bond. A "dimethyl OP compound" comprises two
methyl moieties covalently bonded to the phosphorus atom, such as,
for example, malathion. A "diethyl OP compound" comprises two
ethoxy moieties covalently bonded to the phosphorus atom, such as,
for example, diazinon.
[0139] In general embodiments, an OP compound comprises an
organophosphorus nerve agent or an organophosphorus pesticide. As
used herein, a "nerve agent" is an inhibitor of a cholinesterase,
including but not limited to, an acetyl cholinesterase, a butyl
cholinesterase, or a combination thereof. The toxicity of an OP
compound depends on the rate of release of its phosphoryl center
(e.g., P--C, P--O, P--F, P--S, P--CN) from the target enzyme
(Millard, C. B. et al., 1999). Preferred nerve agents are
inhibitors of a cholinesterase (e.g., acetyl cholinesterase) whose
catalytic activity is often critical for health and survival in
animals, including humans.
[0140] Certain OP compounds are so toxic to humans that they have
been adapted for use as chemical warfare agents, such as tabun,
soman, sarin, cyclosarin, VX, and R-VX. A CWA may be in airborne
form and such a formulation is known herein as an "OP-nerve gas."
Examples of airborne forms include a gas, a vapor, an aerosol, a
dust, or a combination thereof. Examples of an OP compounds that
may be formulated as an OP nerve gas include tabun, sarin, soman,
VX, GX, or a combination thereof.
[0141] In addition to the initial inhalation route of exposure
common to such agents, CWAs, especially persistent agents such as
VX and thickened soman, pose threats through dermal absorption [In
"Chemical Warfare Agents: Toxicity at Low Levels," (Satu M. Somani
and James A. Romano, Jr., Eds.) p. 414, 2001]. As used herein, a
"persistent agent" is a CWA formulated to be non-volatile and thus
remain as a solid or liquid while exposed to the open air for more
than three hours. Often after release, a persistent agent may
convert from an airborne dispersal form to a solid or liquid
residue on a surface, thus providing the opportunity to contact the
skin of a human. The toxicities for common OP chemical warfare
agents after contact with skin are shown at Table 2.
2TABLE 2 LD.sub.50 Values* of Common Organophosphorus Chemical
Warfare Agents Common OP Estimated human LD.sub.50 - percutaneous
CWA (skin) administration Tabun 1000 milligrams ("mg") Sarin 1700
mg Soman 100 mg VX 10 mg *LD.sub.50 - the dose need to kill 50% of
individuals in a population after administration, wherein the
individuals weigh approximately 70 kg.
[0142] In some embodiments, an OP compound may be a particularly
poisonous organophosphorus nerve agent. As used herein, a
"particularly poisonous" agent is a composition with a LD.sub.50 of
35 mg/kg or less for an organism after percutaneous ("skin")
administration of the agent. Examples of a particularly poisonous
OP nerve agent include tabun, sarin, cyclosarin, soman, VX, R-VX,
or a combination thereof.
[0143] As used herein, "detoxification," "detoxify," "detoxified,"
"degradation," "degrade," and "degraded" refers to a chemical
reaction of a compound that produces a chemical byproduct that is
less harmful to the health or survival of a target organism
contacted with the chemical product relative to contact with the
parent compound. OP compounds may be detoxified using chemical
hydrolysis or through enzymatic hydrolysis (Yang, Y.-C. et al.,
1992; Yang, Y.-C. et al., 1996; Yang, Y.-C. et al., 1990; LeJeune,
K. E. et al., 1998a). In general embodiments, the enzymatic
hydrolysis is a specifically targeted reaction wherein the OP
compound is cleaved at the phosphoryl center's chemical bond
resulting in predictable byproducts that are acidic in nature but
benign from a neurotoxicity perspective (Kolakowski, J. E. et al.,
1997; Rastogi, V. K. et al., 1997; Dumas, D. P. et al., 1990;
Raveh, L. et al., 1992). By comparison, chemical hydrolysis can be
much less specific, and in the case of VX may produce some quantity
of byproducts that approach the toxicity of the intact agent (Yang,
Y.-C. et al., 1996; Yang, Y.-C. et al., 1990). In preferred facets,
an enzyme composition of the present invention degrades a CWA, a
particularly poisonous organophosphorus nerve agent, or a
combination thereof into byproduct that is not particularly
poisonous.
[0144] Many OP compounds are pesticides that are not particularly
poisonous to humans, though they do possess varying degrees of
toxicity to humans and other animals. Examples of an OP pesticide
include bromophos-ethyl, chlorpyrifos, chlorfenvinphos,
chlorothiophos, chlorpyrifos-methyl, coumaphos, crotoxyphos,
crufomate, cyanophos, diazinon, dichlofenthion, dichlorvos,
dursban, EPN, ethoprop, ethyl-parathion, etrimifos, famphur,
fensulfothion, fenthion, fenthrothion, isofenphos, jodfenphos,
leptophos-oxon, malathion, methyl-parathion, mevinphos, paraoxon,
parathion, parathion-methyl, pirimiphos-ethyl, pirimiphos-methyl,
pyrazophos, quinalphos, ronnel, sulfopros, sulfotepp,
trichloronate, or a combination thereof. In some embodiments, a
composition of the present invention degrades a pesticide into a
byproduct that is less toxic to an organism. In specific aspects,
the organism is an animal, such as a human.
[0145] a. OPH
[0146] Organophosphorus hydrolase (E.C.3.1.8.1) has been also
refered to in that art as "organophosphate-hydrolyzing enzyme,"
"phosphotriesterase," "PTE," "organophosphate-degrading enzyme,"
"OP anhydrolase," "OP hydrolase," "OP thiolesterase,"
"organophosphorus triesterase," "parathion hydrolase,"
"paraoxonase," "DFPase," "somanase," "VXase," and "sarinase." As
used herein, this type of enzyme will be referred to herein as
"organophosphorus hydrolase" or "OPH."
[0147] The initial discovery of OPH was from two bacterial strains
from the closely related genera: Pseudomonas diminuta and
Flavobacterium spp. (McDaniel, S. et al., 1988; Harper, L. et al.,
1988), which encoded identical organophosphorus degrading opd genes
on large plasmids (Genbank accession no. M20392 and Genbank
accession no. M22863) (copending U.S. patent application Ser. No.
07/898,973, incorporated herein in its entirety by reference). It
is likely that Pseudomonas diminuta was derived from the
Flavobacterium spp. Subsequently, other such OPH encoding genes
have been discovered. The use of any opd gene or their gene product
in the described compositions and methods is contemplated. Examples
of opd genes and gene products that may be used include the
Agrobacterium radiobacter P230 organophosphate hydrolase gene, opdA
(Genbank accession no. AY043245; Entrez databank no. AAK85308); the
Flavobacterium balustinum opd gene for parathion hydrolase (Genbank
accession no. AJ426431; Entrez databank no. CAD19996); the
Pseudomonas diminuta phosphodiesterase opd gene (Genbank accession
no. M20392; Entrez databank no. AAA98299; Protein Data Bank entries
1JGM, 1DPM, 1EYW, 1EZ2, 1HZY, 1IOB, 1IOD, 1PSC and 1PTA); the
Flavobacterium sp opd gene (Genbank accession no. M22863; Entrez
databank no. AAA24931; ATCC 27551); the Flavobacterium sp.
parathion hydrolase opd gene (Genbank accession no. M29593; Entrez
databank no. AAA24930; ATCC 27551); or a combination thereof
(Horne, I. et al., 2002; Somara, S. et al., 2002; McDaniel, C. S.
et al., 1988a; Harper, L. L. et al., 1988; Mulbry, W. W. and Karns,
J. S., 1989).
[0148] Because OPH possesses the desirable property of cleaving a
broad range of OP compounds (Table 1), it is the OP detoxifying
enzyme that has been most studied and characterized, with the
enzyme obtained from Pseudomonas being the target of focus for most
studies. This OPH was initially purified following expression from
a recombinant baculoviral vector in insect tissue culture of the
Fall Armyworm, Spodoptera frugiperda (Dumas, D. P. et al., 1989b).
Purified enzyme preparations have been shown to be able to detoxify
via hydrolysis a wide spectrum of structurally related insect and
mammalian neurotoxins that function as acetylcholinesterase
inhibitors. Of great interest, this detoxification ability included
a number of organophosphorofluoridate nerve agents such as sarin
and soman. This was the first recombinant DNA construction encoding
an enzyme capable of degrading these potent nerve gases. This
enzyme was capable of degrading the common organophosphorus
insecticide analog (paraoxon) at rates exceeding 2.times.10.sup.7
M.sup.-1 (mole enzyme), which is equivalent to the most
catalytically efficient enzymes observed in nature. The purified
enzyme preparations are capable of detoxifying sarin and the less
toxic model mammalian neurotoxin O,O-diisopropyl
phosphorofluoridate ("DFP") at the equivalent rates of 50-60
molecules per molecule of enzyme-dimer per second. In addition, the
enzyme can hydrolyze soman and VX at approximately 10% and 1% of
the rate of sarin, respectively. The breadth of substrate utility
(e.g., V agents, sarin, soman, tabun, cycosarin, OP pesticides) and
the efficiency for the hydrolysis exceeds the known abilities of
other prokaryotic and eukaryotic organophosphorus acid anydrases,
and it is clear that this detoxification is due to a single enzyme
rather than a family of related, substrate-limited proteins.
[0149] The X-ray crystal structure of Pseudomonas OPH has been
determined (Benning, M. M. et al., 1994; Benning, M. M. et al.,
1995; Vanhooke, J. L. et al., 1996). Each OPH monomer's active site
binds two atoms of Zn.sup.2+; however, OPH is usually prepared
wherein Co.sup.2+ replaces Zn.sup.2+, which enhances catalytic
rates. Examples of the catalytic rates (k.sub.cat) and
specificities (k.sub.cat/K.sub.m) for Co.sup.2+ substituted OPH
against various OP compounds are shown at Table 3 below.
3TABLE 3 Catalytic Activity of Wild-Type OPH binding Co.sup.2+
k.sub.cat (s.sup.-1) k.sub.cat/K.sub.m (M.sup.-1 s.sup.-1) OP
Pesticide Substrate Paraoxon 15000.sup.a 1.3 .times. 10.sup.8 OP
CWA Substrates Sarin 56.sup.b 8 .times. 10.sup.4 Soman 5.sup.b 1
.times. 10.sup.4 VX 0.3.sup.b 7.5 .times. 10.sup.2 R-VX 0.5.sup.c
105 Tabun* 77.sup.d 7.6 .times. 10.sup.5 *Wild-type Zn.sup.2+ OPH
was used in obtaining these kinetic parameters; .sup.adiSioudi, B.
et al., 1999a; .sup.bKolakoski J. E. et al., 1997; .sup.cRastogi,
V. K. et al., 1997; .sup.dRaveh, L. et al., 1992.
[0150] The phosphoryl center of OP compounds is chiral, and
Pseudomonas OPH preferentially binds and/or cleaves S.sub.p
enantiomers over R.sub.p enantiomers of the chiral phosphorus in
various substrates by a ratio of about 10:1 to about 90:1
(Chen-Goodspeed, M. et al., 2001a; Hong, S.-B. and Raushel, F. M.,
1999a; Hong, S.-B. and Raushel, F. M., 1999b). CWAs such as VX,
sarin, and soman are usually prepared and used as a mixture of
sterioisomers of varying toxicity, with VX and sarin having two
enantomers each, with the chiral center around the phosphorus of
the cleavable bond. Soman possesses four enantomers, with one
chiral center based on the phosphorus and an additional chiral
center based on a pinacolyl moeity [In "Chemical Warfare Agents:
Toxicity at Low Levels" (Satu M. Somani and James A. Romano, Jr.,
Eds.) pp 26-29, 2001; Li, W.-S. et al., 2001; Yang, Y.-C. et al.,
1992; Benshop, H. P. et al., 1988]. The S.sub.P enantiomer of sarin
is about 10.sup.4 times faster in inactivating acetylcholinesterase
than the R.sub.P enantiomer (Benschop, H. P. and De Jong, L. P. A.
1988), while the two S.sub.p enantiomers of soman is about 10.sup.5
times faster in inactivating acetylcholinesterase than the R.sub.p
enantiomers (Li, W.-S. et al., 2001; Benschop, H. P. et al., 1984).
Wild-type organophosphorus hydrolase seems to have greater
specificity for the less toxic enantiomers of sarin and soman. OPH
is about 9-fold faster cleaving an analog of the R.sub.p enantiomer
of sarin relative to an analog of the S.sub.p enantiomer, and about
10-fold faster in cleaving analogs of the R.sub.c enantiomers of
soman relative to analogs of the S.sub.c enantiomers (Li, W.-S. et
al., 2001).
[0151] b. Paraoxonase
[0152] Human paraoxonase (EC 3.1.8.1), is a calcium dependent
protein, and is also known as an "arylesterase" or aryl-ester
hydrolase" (Josse, D. et al., 1999; Vitarius, J. A. and Sultanos,
L. G., 1995). Examples of the human paraoxonase ("HPON1") gene and
gene products can be accessed at (Genbank accession no. M63012;
Entrez databank no. MB59538) (Hassett, C. et al., 1991).
[0153] C. Carboxylases
[0154] It is contemplated that a carboxylase gene isolated from an
animal may be used as an organophosphate hydrolase in the present
invention. As used herein, a "carboxylase" or "ali-esterase" (EC
3.1.1.1) is an enzyme that hydrolytically cleaves carboxylic esters
(e.g., C--O bonds). As is well known to those of ordinary skill in
the art, most genes in eukaryatic organisms have multiple alleles
which comprise varient nucleotide and/or expressed protein
sequences for a particular gene. Certain insect species have been
identified with reduced carboxylase activity and enhanced
resistance to OP compounds such as malathion or diazinon. Examples
of insect species include Plodia interpunctella, Chrysomya putoria,
Lucilia cuprina, and Musca domestica. In particular, an allele of a
carboxylase gene possessing organophosphate hydrolase (EC 3.1.8.1)
activity is thought to be responsible for OP compound resistance.
Examples of such carboxylase genes include alleles isolated from
Lucilia cuprina (Genbank accession no. U56636; Entrez databank no.
AAB67728), Musca domestica (Genbank accession no. AF133341; Entrez
databank no. MD29685), or a combination thereof (Claudianos, C. et
al., 1999; Campbell, P. M. et al., 1998; Newcomb, R. D. et al.,
1997). Additionally, carboxylases or carbamoyl lyases are useful
against the carbamate nerve agents, and are specifically
contemplated for use in biomolecule composition of the present
invention for use against such agents.
[0155] d. OPAAs, Prolidases, Aminopeptideases and PepQ
[0156] Organophosphorus acid anhydrolases (E.C.3.1.8.2), known as
"OPAAs," have been isolated from microorganisms and identified as
enzymes that detoxify OP compounds (Serdar, C. M. and Gibson, D.
T., 1985; Mulbry, W. W. et al., 1986; DeFrank, J. J. and Cheng,
T.-C., 1991). The better-characterized OPAAs have been isolated
from Altermonas species, such as Alteromonas sp JD6.5, Alteromonas
haloplanktis and Altermonas undina (ATCC 29660) (Cheng, T.-C. et
al., 1996; Cheng, T.-C. et al., 1997; Cheng, T. C. et al., 1999;
Cheng, T.-C. et al., 1993). Examples of OPM genes and gene products
that may be used include the Alteromonas sp JD6.5 opaA gene,
(GeneBank accession no. U29240; Entrez databank no. AAB05590); the
Alteromonas haloplanktis prolidase gene (GeneBank accession no.
U56398; Entrez databank AAA99824; ATCC 23821); or a combination
thereof (Cheng, T. C. et al., 1996; Cheng, T.-C. et al., 1997). The
wild-type encoded OPAA from Alteromonas sp JD6.5 is 517 amino
acids, while the wild-type encoded OPAA from Alteromonas
haloplanktis is 440 amino acids (Cheng, T. C. et al., 1996; Cheng,
T.-C. et al., 1997). The Alteromonas OPAAs accelerates the
hydrolysis of phosphotriesters and phosphofluoridates, including
cyclosarin, sarin and soman (Table 4).
4TABLE 4 Catalytic Activity of Wild-Type OPAAS k.sub.cat (s.sup.-1)
per species OPAA per OP Substrate A. sp JD6.5 A. haloplanktis A.
undina OP Compound Substrate DFP 1650.sup.a 575.sup.a 1239.sup.a OP
CWA Substrates Sarin 611.sup.a 257.sup.a 376.sup.a Cyclosarin
1650.sup.a 269.sup.a 1586.sup.a Soman 3145.sup.a 1389.sup.a
2496.sup.a Tabun 85.sup.a 113.sup.a 292.sup.a .sup.aCheng, T. C. et
al., 1999
[0157] Similar to OPH, OPAA from Alteromonas sp JD6.5 ("OPAA-2")
has a general binding and cleavage preference up to 112:1 for the
S.sub.p enantiomers of various p-nitrophenyl phosphotriesters
(Hill, C. M. et al., 2000). Additionally, OPAA from Alteromonas sp
JD6.5 is over 2 fold faster at cleaving an S.sub.p enantiomer of a
sarin analog, and over 15-fold faster in cleaving analogs of the
R.sub.c enantiomers of soman relative to analogs of the S.sub.c
enantiomers (Hill, C. M. et al., 2001).
[0158] Additionally, a prolidase ("imidodipeptidase," "proline
dipeptidase," "peptidase D," "g-peptidase"), PepQ and/or
aminopeptidase P gene or gene product with OPAA activity, or a
functional equivalent thereof may be used in the present invention.
OPAAs possess sequence and structural similarity to human
prolidase, Escherichia coli aminopeptidase P and Escherichia coli
PepQ (Cheng, T.-C. et al., 1997; Cheng, T.-C. et al., 1996). A
prolidase or a PepQ protein (E.C. 3.4.13.9) hydrolyzes a C--N bond
of a dipeptide with a prolyl residue at the carboxyl-terminus, and
OPAAs are also classified as prolidases. An aminopeptidase P (EC
3.4.11.9) hydrolyzes the C--N amino bond of a proline at the
penultimate position from the amino terminus of an amino acid
sequence. Partly purified human and porcine prolidase demonstrated
the ability to cleave DFP and G-type nerve agents (Cheng, T.-C. et.
al., 1997). Examples of prolidase genes and gene products include
the Mus musculus prolidase gene (GeneBank accession no. D82983;
Entrez databank no. BAB11685); the Homo sapien prolidase gene
(GeneBank accession no. J04605; Entrez databank AAA60064); the
Lactobacllus helveticus prolidase ("PepQ") gene (GeneBank accession
no. AF012084; Entrez databank MC24966); the Escherichia coli
prolidase ("pepQ") gene (GeneBank accession no. X54687; Entrez
databank CM38501); the Escherichia coli aminopeptidase P ("pepP")
gene (GeneBank accession no. D00398; Entrez databank BM00299;
Protein Data Bank entries 1A16, 1AZ9, 1JAW and 1M35); or a
combination thereof (Ishii, T. et al., 1996; Endo, F. et al., 1989;
Nakahigashi, K. and Inokuchi, H., 1990; Yoshimoto, T. et al.,
1989).
[0159] e. Squid-Type DFPases
[0160] As used herein, a "squid-type DFPase" (EC 3.1.8.2) refers to
an enzyme that catalyzes the cleavage of both DFP and soman, and is
isolated from organisms of the Loligo genus. Generally, a
squid-type DFPase cleaves DFP at a faster rate than soman.
Squid-type DFPases include, for example, a DFPase from Loligo
vulgaris, Loligo pealei, Loligo opalescens, or a combination
thereof (Hoskin, F. C. G. et al., 1984; Hoskin, F. C. G. et al.,
1993; Garden, J. M. et al., 1975).
[0161] A well-characterized example of a squid-type DFPase includes
the DFPase that has been isolated from the optical ganglion of
Loligo vulgaris (Hoskin, F. C. G. et al., 1984). This squid-type
DFPase cleaves a variety of OP compounds, including DFP, sarin,
cyclosarin, soman, and tabun (Hartleib, J. and Ruterjans, H.,
2001a). The gene encoding this squid-type DFP has been isolated,
and can be accessed at GeneBank accession no. AX018860
(International patent publication: WO 9943791-A). Further, this
enzyme's X-ray crystal structure has been determined (Protein Data
Bank entry 1E1A) (Koepke, J. et al., 2002; Scharff, E. I. et al.,
2001). This squid-type DFPase binds two Ca.sup.2+ ions, which are
important in catalytic activity and enzyme stability (Hartleib, J.
et al., 2001). Both the DFPase from Loligo vulgaris and Loligo
pealei are susceptible to proteolytic cleavage into a 26-kDa and 16
kDa fragments, and the fragments from Loligo vulgaris are capable
of forming active enzyme when associated together (Hartleib, J. and
Ruterjans, H., 2001a).
[0162] f. Mazur-Type DFPases
[0163] As used herein, a "Mazur-type DFPase" (EC 3.1.8.2) refers to
an enzyme that catalyzes the cleavage of both DFP and soman.
Generally, Mazur-type DFPases cleaves soman at a faster rate than
DFP. Examples of a Mazur-type DFPases include the DFPase isolated
from mouse liver (Billecke, S. S. et al., 1999), which may be the
same as the DFPase known as SMP-30 (Fujita, T. et al., 1996;
Billecke, S. S. et al., 1999; Genebank accession no. U28937; Entrez
databank MC52721); a DFPase isolated from rat liver (Little, J. S.
et al., 1989); a DFPase isolated from hog kidney; a DFPase isolated
from Bacillus stearothermophilus strain OT, a DFPase isolated from
Escherichia coli (ATCC25922) (Hoskin, F. C. G. et al., 1993;
Hoskin, F. C. G, 1985); or a combination thereof.
[0164] g. Other Phosphoric Triester Hydrolases
[0165] It is contemplated that any phosphoric triester hydrolase
that is known in the art may be used in preferred embodiments of
the present invention. An example of an additional phosphoric
triester hydrolase includes the product of the gene, mpd, (GenBank
accession number AF338729; Entrez databank AAK14390) isolated from
Plesiomonas sp. strain M6 (Zhongli, C. et al., 2001). Other
examples include the phosphoric triester hydrolase identified in a
Xanthomonas sp. (Tchelet, R. et al., 1993); Tetrahymena (Landis, W.
G. et al., 1987); certain plants such as Myriophyllum aquaticum,
Spirodela origorrhiza L, Elodea Canadensis and Zea mays (Gao, J. et
al., 2000; Edwards, R. and Owen, W. J., 1988); and in hen liver and
brain (Diaz-Alejo, N. et al., 1998). Additional, cholinesterases
(e.g., an acetyl cholinesterase) with OP degrading activity have
been identified in insects resistant OP pesticides (see, for
example, Baxter, G. D. et al., 1998; Baxter, G. D. et al., 2002;
Rodrigo, L., et al., 1997, Vontas, J. G., et al., 2002; Walsh, S.
B., et al., 2001; Zhu, K. Y., et al., 1995), and are contemplate
for use a bimolecular composition of the present invention.
[0166] 2. Functional Equivalents of Wild-Type Enzymes
[0167] It is possible to optimize a proteinaceous molecule with a
defined amino acid sequence and/or length for one or more
properties. An alteration in a desirable property is possible
because such molecules can be manipulated, for example, by chemical
modification, as described herein or as would be known to one of
ordinary skill in the art, in light of the present disclosures. As
used herein "alter" or "alteration" may result in an increase or a
decrease in the measured value for a particular property. As used
herein a "property," in the context of an proteinaceous molecule,
includes, but is not limited to, a ligand binding property, a
catalytic property, a stability property, a property related to
environmental safety, or a combination thereof. Examples of a
catalytic property that may be altered include a kinetic parameter,
such as K.sub.m, a catalytic rate (k.sub.cat) for a substrate, an
enzyme's specificity for a substrate (k.sub.cat/K.sub.m), or a
combination thereof. Examples of a stability property that may be
altered include thermal stability, half-life of activity, stability
after exposure to a weathering condition, or a combination thereof.
Examples of a property related to environmental safety include an
alteration in toxicity, antigenicity, bio-degradability, or a
combination thereof. However, as would be readily apparent to one
of ordinary skill in the art, an alteration to increase an enzyme's
catalytic rate for a substrate, an enzyme's specificity for a
substrate, a proteinaceous molecule's thermal stability, a
proteinaceous molecule's half-life of activity, or a proteinaceous
molecule's stability after exposure to a weathering condition may
be preferred for some applications, while a decrease in toxicity
and/or antigenicity for a proteinaceous molecule may be preferred
in additional applications. An enzyme comprising a chemical
modification that function as an enzyme of the present invention is
a "functional equivalent" to, and "in accordance" with, an
un-modified enzyme.
[0168] It is also understood by those of skill in the art that
there is a limit to the number of chemical modifications that can
be made to an enzyme of the present invention before a preferred
property is undesirably altered. However, in light of the
disclosures herein of assays for determining whether a composition
possesses one or more desirable properties, including, for example,
a preferred enzymatic activity, a stability property, etc., and
that which is known in the art regarding such assays, it is well
within the ability of one of ordinary skill in the art to determine
whether a given chemical modification to an enzyme of the present
invention produces a molecule that still possesses a suitable set
of properties for use in a particular application. In certain
aspects, a functional equivalent enzyme comprising a plurality of
different chemical modifications can be produced in accordance with
the present invention.
[0169] It is particularly contemplated that a functional equivalent
enzyme comprising a structural analog and/or sequence analog may
possess an enhanced desirable property and/or a reduced undesirable
property, in comparison to the enzyme upon which it is based. All
such functional equivalent enzymes described herein, or as would be
known to one of ordinary skill in the art in light of the present
disclosures, are considered part of the present invention. As used
herein, a "structural analog" refers to one or more chemical
modifications to the peptide backbone or non-side chain chemical
moieties of a proteinaceous molecule. In certain aspects, a
subcomponent of an enzyme such as an apo-enzyme, a prosthetic
group, a co-factor, or a combination thereof, may be modified to
produce a functional equivalent structural analog. In particular
facets, such an enzyme sub-component that does not comprise a
proteinaceous molecule may be altered to produce a functional
equivalent structural analog of an enzyme when combined with the
other sub-components. As used herein, a "sequence analog" refers to
one or more chemical modifications to the side chain chemical
moieties, also known herein as a "residue" of one or more amino
acids that define a proteinaceous molecule's sequence. Often such a
"sequence analog" comprises an amino acid substitution, which is
generally produced by recombinant expression of a nucleic acid
comprising a genetic mutation to produce a mutation in the
expressed amino acid sequence.
[0170] As used herein, an "amino acid may be a common or uncommon
amino acid. The common amino acids include: alanine (Ala, A);
arginine (Arg, R); aspartic acid (a.k.a. aspartate; Asp, D);
asparagine (Asn, N); cysteine (Cys, C); glutamic acid (a.k.a.
glutamate; Glu, E); glutamine (Gln, Q); glycine (Gly, G); histidine
(His, H); isoleucine (Ile, I); leucine (Leu, L); lysine (Lys, K);
methionine (Met, M); phenylalanine (Phe, F); proline (Pro, P);
serine (Ser, S); threonine (Thr, T); tryptophan (Trp, W); tyrosine
(Tyr, Y); and valine (Val, V). Common amino acids are often
biologically produced in the biological synthesis of a peptide or a
polypeptide. An uncommon amino acid refers to an analog of a common
amino acid, as well as a synthetic amino acid whose side chain is
chemically unrelated to the side chains of the common amino acids.
Various uncommon amino acids are well known to those of ordinary
skill in the art though it is contemplated that in general
embodiments, an enzyme of the present invention will be
biologically produced, and thus lack or possess relatively few
uncommon amino acids prior to any subsequent non-mutation based
chemical modifications.
[0171] As is well known in the art, the side chains of amino acids
comprise moieties with specific chemical and physical properties.
Certain side chains contribute to a ligand binding property, a
catalytic property, a stability property, a property related to
environmental safety, or a combination thereof. For example,
cysteines can form covalent bonds between different parts of a
contiguous amino acid sequence, or between non-contiguous amino
acid sequences to confer enhanced stability to a secondary,
tertiary or quaternary structure. In an additional example, the
presence of hydrophobic or hydrophilic side chains exposed to the
outer environment can alter the hydrophobicity or hydrophilicity of
part of a proteinaceous sequence such as in the case of a
transmembrane domain that is embedded in a lipid layer of a
membrane. In another example, hydrophilic side chains may be
exposed to the environment surrounding a proteinaceous molecule,
which can enhance the overall solubility of a proteinaceous
molecule in a polar liquid, such as water or a liquid component of
a coating. In a further example, various acidic, basic,
hydrophobic, hydrophilic, and/or aromatic side chains present at or
near a binding site of a proteinaceous structure can affect the
affinity for a proteinaceous sequence for binding a ligand and/or a
substrate, based on the covalent, ionic, Van der Waal forces,
hydrogen bond, hydrophilic, hydrophobic, and/or aromatic
interactions at a binding site. Such interactions by residues at or
near an active site also contribute to a chemical reaction that
occurs at the active site of an enzyme to produce enzymatic
activity upon a substrate. As used herein, a residue is "at or
near" another residue or group of residues when it is within 15
.ANG., 14 .ANG., 13 .ANG., 12 .ANG., 11 .ANG., 10 .ANG., 9 .ANG., 8
.ANG., 7 .ANG., 6 .ANG., 5 .ANG., 4 .ANG., 3 .ANG., 2 .ANG., or 1
.ANG. the residue or group of residues such as residues identified
as contributing to the active site and/or binding site.
[0172] Identification of an amino acid whose chemical modification
would likely change a desirable property of a proteinaceous
molecule can be accomplished using such methods as a chemical
reaction, mutation, X-ray crystallography, nuclear magnetic
resonance ("NMR"), computer based modeling or a combination
thereof. Selection of an amino acid on the basis of such
information can then be used in the rational design of a mutant
proteinaceous sequence that would possess an altered desired
property. Preferred alterations include those that alter enzymatic
activity to produce a functional equivalent of an enzyme.
[0173] For example, many residues of a proteinaceous molecule that
contribute to the properties of a proteinaceous molecule comprise
chemically reactive moieties. These residues are often susceptible
to chemical reactions that can inhibit their ability to contribute
to a desirable property of the proteinaceous molecule. Thus, a
chemical reaction can be used to identify one or more amino acids
comprised within the proteinaceous molecule that may contribute to
a desirable property. The identified amino acids then can be
subject to modifications such as amino acid substitutions to
produce a functional equivalent. Examples of amino acids that can
be so chemically reacted include Arg, which can be reacted with
butanedione; Arg and/or Lys, which can be reacted with
phenylglyoxal; Asp and/or Glu, which can be reacted with
carbodiimide and HCl; Asp and/or Glu, which can be reacted with
N-ethyl-5-phenylisoxazoliu- m-3'-sulfonate ("Woodward's reagent
K"); Asp and/or Glu, which can be reacted with 1,3-dicyclohexyl
carbodiimide; Asp and/or Glu, which can be reacted with
1-ethyl-3-(3-dimethylaminopropyl)carbodiimide ("EDC"); Cys, which
can be reacted with p-hydroxy mercuribenzoate; Cys, which can be
reacted with dithiobisnitrobenzoate ("DTNB"); Cys, which can be
reacted with iodoacetamide; His, which can be reacted with
diethylpyrocarbonate ("DEPC"); His, which can be reacted with
diazobenzenesulfonic acid ("DBS"); His, which can be reacted with
3,7-bis(dimethylamino)phenothiazi- n-5-ium chloride ("methylene
blue"); Lys, which can be reacted with dimethylsuberimidate; Lys
and/or Arg, which can be reacted with 2,4-dinitrofluorobenzene; Lys
and/or Arg, which can be reacted with trinitrobenzene sulfonic acid
("TNBS"); Trp, which can be reacted with 2-hydroxy-5-nitrobenzyl
bromide 1-ethyl-3(3-dimethylaminopropyl); Trp, which can be reacted
with 2-acetoxy-5-nitrobenzyl chloride; Trp, which can be reacted
with N-bromosucinimide; Tyr, which can be reacted with
N-acetylimidazole ("NAI"); or a combination thereof (Hartleib, J.
and Ruterjans, H., 2001b; Josse, D. et al., 1999; Josse, D. et al.,
2001).
[0174] In an additional example, the secondary, tertiary and/or
quaternary structure of a proteinaceous molecule may be modeled
using techniques known in the art, including X-ray crystallography,
nuclear magnetic resonance, computer based modeling, or a
combination thereof to aid in the identification of active-site,
binding site, and other residues for the design and production of a
mutant form of an enzyme (Bugg, C. E. et al., 1993; Cohen, A. A.
and Shatzmiller, S. E., 1993; Hruby, V. J., 1993; Moore, G. J.,
1994; Dean, P. M., 1994; Wiley, R. A. and Rich, D. H., 1993). The
secondary, tertiary and/or quaternary structures of a proteinaceous
molecule may be directly determined by techniques such as X-ray
crystallography and/or nuclear magnetic resonance to identify amino
acids most likely affect one or more desirable properties.
Additionally, many primary, secondary, tertiary, and/or quaternary
structures of proteinaceous molecules can be obtained using a
public computerized database. An example of such a databank that
may be used for this purpose is the Protein Data Bank (PDB), which
is an international repository of the 3-dimensional structures of
many biological macromolecules, and can be accessed at
http://www.rcsb.org/pdb/index.html. Additional examples of such
databases are listed at:
http://www.rcsb.org/pdb/links.html#Database- s.
[0175] Computer modeling can be used to identify amino acids most
likely to affect one or more desirable properties. Often, a
structurally related proteinaceous molecule comprises primary,
secondary, tertiary and/or quaternary structures that are
evolutionarily conserved in the wild-type protein sequences of
various organisms. As would be known to those of ordinary skill in
the art, the secondary, tertiary and/or quaternary structure of a
proteinaceous molecule can be modeled using a computer to overlay
the proteinaceous molecule's amino acid sequence, which is also
known as the "primary structure," onto the computer model of a
described primary, secondary, tertiary, and/or quaternary structure
of another, structurally related proteinaceous molecule. Often the
amino acids that may participate in an active site, a binding site,
a transmembrane domain, the general hydrophobicity and/or
hydrophilicity of a proteinaceous molecule, the general positive
and/or negative charge of a proteinaceous molecule, etc, may be
identified by such comparative computer modeling.
[0176] In embodiments wherein an amino acid of particular interest
have been identified using such techniques, functional equivalents
may be created using mutations that substitute a different amino
acid for the identified amino acid of interest. Examples of
substitutions of an amino acid side chain to produce a "functional
equivalent" proteinaceous molecule are also known in the art, and
may involve a conservative side chain substitution a
non-conservative side chain substitution, or a combination thereof,
to rationally alter a property of a proteinaceous molecule.
Examples of conservative side chain substitutions include, when
applicable, replacing an amino acid side chain with one similar in
charge (e.g., an arginine, a histidine, a lysine); similar in
hydropathic index; similar in hydrophilicity; similar in
hydrophobicity; similar in shape (e.g., a phenylalanine, a
tryptophan, a tyrosine); similar in size (e.g., an alanine, a
glycine, a serine); similar in chemical type (e.g., acidic side
chains, aromatic side chains, basic side chains); or a combination
thereof. Conversely, when a change to produce a non-conservative
substitution is contemplated to alter a property of proteinaceous
molecule, and still produce a "functional equivalent" proteinaceous
molecule, these guidelines can be used to select an amino acid
whose side-chains relatively non-similar in charge, hydropathic
index, hydrophilicity, hydrophobicity, shape, size, chemical type,
or a combination thereof. Various amino acids have been given a
numeric quantity based on the characteristics of charge and
hydrophobicity, called the hydropathic index (Kyte, J. and
Doolittle, R. F. 1982), which can be used as a criterion for a
substitution. The hydropathic index of the common amino acids are:
Arg (-4.5); Lys (-3.9); Asn (-3.5); Asp (-3.5); Gln (-3.5); Glu
(-3.5); His (-3.2); Pro (-1.6); Tyr (-1.3); Trp (-0.9); Ser (-0.8);
Thr (-0.7); Gly (-0.4); Ala (+1.8); Met (+1.9); Cys (+2.5); Phe
(+2.8); Leu (+3.8); Val (+4.2); and Ile (+4.5). Additionally, a
value has also been given to various amino acids based on
hydrophilicity, which can also be used as a criterion for
substitution (U.S. Pat. No. 4,554,101). The hydrophilicity values
for the common amino acids are: Trp (-3.4); Phe (-2.5); Tyr (-2.3);
Ile (-1.8); Leu (-1.8); Val (-1.5); Met (-1.3); Cys (-1.0); Ala
(-0.5); His (-0.5); Pro (-0.5+/-0.1); Thr (-0.4); Gly (0); Asn
(+0.2); Gln (+0.2); Ser (+0.3); Asp (+3.0+/-0.1); Glu (+3.0+/-0.1);
Arg (+3.0); and Lys (+3.0). In aspects wherein an amino acid is
being conservatively substituted for an amino acid whose
hydropathic index or hydrophilic value is similar, the difference
between the respective index and/or value is preferably within
+/-2, more preferably within +/-1, and most preferably within
+/-0.5. In aspects wherein an amino acid is being
non-conservatively substituted for an amino acid whose hydropathic
index or hydrophilic value is similar, the difference between the
respective index and/or value is preferably greater than +/-0.5,
more preferably greater than +/-1, and most preferably greater than
+/-2.
[0177] In certain embodiments, a functional equivalent may be
produced by a non-mutation based chemical modification to an amino
acid, a peptide or a polypeptide. Examples of chemical
modifications include, when applicable, a hydroxylation of a
proline or a lysine; a phosphorylation of a hydroxyl group of a
serine and/or a threonine; a methylation of an alpha-amino group of
a lysine, an arginine and/or a histidine (Creighton, T. E., 1983);
adding a detectable label such as a fluorescein isothiocyanate
compound ("FITC") to a lysine side chain and/or a terminal amine
(Rogers, K. R. et al., 1999); covalent attachment of a poly
ethylene glycol (Yang, Z. et al., 1995; Kim, C. et al., 1999; Yang,
Z. et al., 1996; Mijs, M. et al., 1994); an acylatylation of an
amino acid, particularly at the N-terminus; an amination of an
amino acid, particularly at the C-terminus (Greene, T. W. and Wuts,
P. G. M. "Productive Groups in Organic Synthesis," Second Edition,
pp. 309-315, John Wiley & Sons, Inc., USA, 1991); a deamidation
of an asparagine or a glutamine to an aspartic acid or glutamic
acid, respectively; a derivation of an amino acid by a sugar
moiety, a lipid, a phosphate, or a farnysyl group; an aggregation
(e.g., a dimerization) of a plurality of proteinaceous molecules,
whether of identical sequence or varying sequences; a cross-linking
of a plurality of proteinaceous molecules of the present invention
using a cross-linking agent [e.g., a
1,1-bis(diazoacetyl)-2-phenylethane; a glutaraldehyde; a
N-hydroxysuccinimide ester; a 3,3'-dithiobis
(succinimidyl-propionate); a bis-N-maleimido-1,8-octane]; an
ionization of an amino acid into an acidic, basic or neutral salt
form; an oxidation of an amino acid; or a combination thereof of
any of the forgoing. Such modifications may produce a desirable
alteration in a property of a proteinaceous molecule, as would be
known to those of ordinary skill in the art. For example, it is
contemplated that a N-terminal glycosylation may enhance a
proteinaceous molecule's stability (Powell, M. F. et al., 1993). In
an additional example, it is contemplated that substitution of a
beta-amino acid isoserine for a serine may enhance the
aminopeptidase resistance a proteinaceous molecule (Coller, B. S.
et al., 1993).
[0178] A proteinaceous molecule for use in the present invention
may comprise a proteinaceous molecule longer or shorter than the
wild-type amino acid sequences specifically disclosed herein, or
that would be known to those of ordinary skill in the art in light
of the present disclosure. For example, an enzyme comprising longer
or shorter sequences is encompassed as part of the present
invention, insofar as it retains enzymatic activity. In some
embodiments, a proteinaceous molecule for use in the present
invention may comprise one or more peptide and/or polypeptide
sequences. In certain embodiments, a modification to a
proteinaceous molecule may add and/or subtract one or two amino
acids from a peptide and/or polypeptide sequence. In other
embodiments, a change to a proteinaceous molecule may add and/or
remove one or more peptide and/or polypeptide sequences. Often a
peptide or a polypeptide sequence may be added or removed to confer
or remove a specific property from the proteinaceous molecule, and
numerous examples of such modifications to a proteinaceous molecule
are described herein, particularly in reference to fusion proteins.
In particular, the native OPH of Pseudomonas diminuta is produced
with a short amino acide sequence at its N-terminas that promotes
the exportation of the protein through the cell membrane and is
later cleaned. Thus, in certain embodiment, this signal sequence
amino acide sequence is deleted by genetic modification in the DNA
construction placed into Escherichia coli host cells in order to
enhance its production.
[0179] As used herein, a "peptide" comprises a contiguous molecular
sequence from 3 to 100 amino acids in length, including all
intermediate ranges and combinations thereof. A sequence of a
peptide may be 3 to 100 amino acids in length, including all
intermediate ranges and combinations thereof. As used herein a
"polypeptide" comprises a contiguous molecular sequence 101 amino
acids or greater. Examples of a sequence length of a polypeptide
include 101 to 10,000 amino acids, including all intermediate
ranges and combinations thereof. As used herein a "protein" is a
proteinaceous molecule comprising a contiguous molecular sequence
three amino acids or greater in length, matching the length of a
biologically produced proteinaceous molecule encoded by the genome
of an organism.
[0180] It is recognized that removal of one or more amino acids
from an enzyme's sequence may reduce or eliminate a detectable,
desirable property such asenzymatic activity, and therefore would
not be preferred. However, it is further contemplated that a longer
sequence, particularly a proteinaceous molecule that consecutively
or non-consecutively comprises or even repeats one or more
enzymatic sequences disclosed herein, or as would be known to those
of ordinary skill in the art in light of the present disclosure,
would be encompassed within the present invention. Additionally,
fusion proteins may be bioengineered to comprise a wild-type
sequence and/or a functional equivalent of an enzyme sequence and
an additional peptide or polypeptide sequence that confers a
desirable property and/or function.
[0181] a. OPH Functional Equivalents
[0182] Using recombinant DNA technology, wild-type and mutant forms
of the opd gene have been expressed, predominantly in Escherichia
coli, for further characterization and analysis. Unless otherwise
noted, the various OPH enzymes, whether wild-type or mutants, that
act as functional equivalents were prepared using the OPH genes and
encoded enzymes first isolated from Pseudomonas diminuta and
Flavobacterium spp.
[0183] OPH normally binds two atoms of Zn.sup.2+ per monomer when
endogenously expressed. While binding Zn.sup.2+, this enzyme is one
of the most stable dimeric enzymes known, with a thermal
temperature of melting ("T.sub.m") of approximately 75.degree. C.
and a conformational stability of approximately 40 killocalorie per
mole ("kcal/mol") (Grimsley, J. K. et al., 1997). However,
structural analogs have been made wherein Co.sup.2+, Fe.sup.2+,
Cu.sup.2+, Mn.sup.2+, Cd.sup.2+, or Ni.sup.2+ are bound instead to
produce enzymes with altered stability and rates of activity
(Omburo, G. A. et al., 1992). For example, Co.sup.2+ substituted
OPH does possess a reduced conformational stability (.about.22
kcal/mol). But this reduction in thermal stability is offset by the
superior catalytic activity of Co.sup.2+ substituted OPH in
degrading various OP compounds. For example, five-fold or greater
rates of detoxification of sarin, soman, and VX were measured for
Co.sup.2+ substituted OPH relative to OPH binding Zn.sup.2+
(Kolakoski, J. E. et al., 1997). It is contemplated that structural
analogs of an OPH sequence may be prepared comprising a Zn.sup.2+,
Co.sup.2+, Fe.sup.2+, Cu.sup.2+, Mn.sup.2+, Cd.sup.2+, Ni.sup.2+,
or a combination thereof. Generally, changes in the bound metal can
be achieved by using cell growth media during cell expression of
the enzyme wherein the concentration of a metal present is defined,
and/or removing the bound metal with a chelator (e.g.,
1,10-phenanthroline; 8-hydroxyquinoline-5-sulfphonic acid;
ethylenediaminetetraacetic acid) to produce an apo-enzyme, followed
by reconstitution of a catalytically active enzyme by contact with
a selected metal (Omburo, G. A. et al., 1992; Watkins, L. M. et
al., 1997a; Watkins, L. M. et al., 1997b). It is further
contemplated that structural analogs of an OPH sequence may be
prepared to comprise only one metal atom per monomer.
[0184] In an additional example, OPH structure analysis has been
conducted using NMR (Omburo, G. A. et al., 1993). In a further
example, the X-ray crystal structure for OPH has been determined
(Benning, M. M. et al., 1994; Benning, M. M. et al., 1995;
Vanhooke, J. L. et al., 1996), including the structure of the
enzyme while binding a substrate, further identifying residues
involved in substrate binding and catalytic activity (Benning, M.
M. et al., 2000). From these structure evaluations, the amino acids
His55, His57, His201, His230, Asp301, and the carbamylated lysine,
Lys169, have been identified as coordinating the binding of the
active site metal. Additionally, the positively charged amino acids
His55, His57, His201, His230, His254, and His257 are
counter-balanced by the negatively charged amino acids Asp232,
Asp233, Asp235, Asp 253, Asp301, and the carbamylated lysine Lys169
at the active site area. A water molecule and amino acids His55,
His57, Lys169, His201, His230, and Asp301 are thought to be
involved in direct metal binding. The amino acid Asp301 is thought
to aid a nucleophilic attack by a bound hydroxide upon the
phosphorus to promote cleavage of an OP compound, while the amino
acid His354 may aid the transfer of a proton from the active site
to the surrounding liquid in the latter stages of the reaction
(Raushel, F. M., 2002). The amino acids His254 and His257 are not
thought to be direct metal binding amino acids, but may be residues
that interact (e.g., a hydrogen bond, a Van der Waal interaction)
with each other and other active site residues, such as residues
that directly contact a substrate or bind a metal atom. In
particular, amino acid His254 is thought to interact with the amino
acids His230, Asp232, Asp233, and Asp301. Amino acid His257 is
thought to be a participant in a hydrophobic substrate-binding
pocket. The active site pocket comprises various hydrophobic amino
acids, Trp131, Phe132, Leu271, Phe306, and Tyr309. These amino
acids may aid the binding of hydrophobic OP compounds (Benning, M.
M. et al., 1994; Benning, M. M. et al., 1995; Vanhooke, J. L. et
al., 1996). Electrostatic interactions may occur between phosphoryl
oxygen, when present, and the side chains of Trp131 and His201.
Additionally, the side chains of amino acids Trp131, Phe132, and
Phe306 are thought to be orientated toward the atom of the cleaved
substrate's leaving group that was previously bonded to the
phosphorus atom (Watkins, L. M. et al., 1997a).
[0185] Substrate binding subsites known as the small subsite, the
large subsite, and the leaving group subsite have been identified
(Benning, M. M. et al., 2000; Benning, M. M. et al., 1994; Benning,
M. M. et al., 1995; Vanhooke, J. L. et al., 1996). The amino acids
Gly60, Ile106, Leu303, and Ser308 are thought to comprise the small
subsite. The amino acids Cys59 and Ser61 are near the small
subsite, but with the side chains thought to be orientated away
from the subsite. The amino acids His254, His257, Leu271, and
Met317 are thought to comprise the large subsite. The amino acids
Trp131, Phe132, Phe306, and Tyr309 are thought to comprise the
leaving group subsite, though Leu271 is sometimes considered part
of this subsite as well (Watkins, L. M. et al., 1997a). Comparison
of this opd product with the encoded sequence of the opdA gene from
Agrobacterium radiobacter P230 revealed that the large subsite
possessed generally larger residues that affected activity,
specifically the amino acids Arg254, Tyr257, and Phe271 (Horne, I.
et al., 2002). Few electrostatic interactions are apparent from the
X-ray crystal structure of the inhibitor bound by OPH, and it is
thought that hydrophobic interactions and the size of the subsites
affect substrate specificity, including steriospecificity for a
stereoisomer, such as a specific enantiomer of an OP compound's
chiral chemical moiety (Chen-Goodspeed, M. et al., 2001b).
[0186] Using the sequence and structural knowledge of OPH, numerous
mutants of OPH comprising a sequence analog have been specifically
produced to alter one or more properties relative to a substrate's
cleavage rate (k.sub.cat) and/or specificity (k.sub.cat/K.sub.m).
Examples of OPH sequence analog mutants include H55C, H57C, C59A,
G60A, S61A, I106A, I106G, W131A, W131F, W131K, F132A, F132H, F132Y,
L136Y, L140Y, H201C, H230C, H254A, H254R, H254S, H257A, H257L,
H257Y, L271A, L271Y, L303A, F306A, F306E, F306H, F306K, F306Y,
S308A, S308G, Y309A, M317A, M317H, M317K, M317R, H55C/H57C,
H55C/H201C, H55C/H230C, H57C/H201C, H57C/H230C, A80V/S365P,
I106A/F132A, I106A/S308A, I106G/F132G, I106G/S308G, F132Y/F306H,
F132H/F306H, F132H/F306Y, F132Y/F306Y, F132A/S308A, F132G/S308G,
L182S/V310A, H201C/H230C, H254R/H257L, H55C/H57C/H201C,
H55C/H57C/H230C, H55C/H201C/H230C, I106A/F132A/H257Y,
I106A/F132A/H257W, I106G/F132G/S308G, L130M/H257Y/I274N,
H257Y/I274N/S365P, H55C/H57C/H201C/H230C, I106G/F132G/H257Y/S308G,
or A14T/A80V/L185R/H257Y/I274N (Li, W.-S. et al., 2001; Gopal, S.
et al., 2000; Chen-Goodspeed, M. et al., 2001a; Chen-Goodspeed, M.
et al., 2001b; Watkins, L. M. et al., 1997a; Watkins, L. M. et al.,
1997b; diSioudi, B. et al., 1999; Cho, C. M.-H. et al., 2002; Shim,
H. et al., 1996; Raushel, F. M., 2002; Wu, F. et al., 2000a;
diSioudi, B. D. et al., 1999).
[0187] For example, the sequence and structural information has
been used in production of mutants of OPH possessing cysteine
substitutions at the metal binding histidines His55, His57, His201,
and His230. OPH mutants H55C, H57C, H201C, H230C, H55C/H57C,
H55C/H201C, H55C/H230C, H57C/H201C, H57C/H230C, H201C/H230C,
H55C/H57C/H201C, H55C/H57C/H230C, H55C/H201C/H230C,
H57C/H201C/H230C, and H55C/H57C/H201C/H230C were produced binding
either Zn.sup.2+; Co.sup.2+ or Cd.sup.2+. The H57C mutant had
between 50% (i.e., binding Cd.sup.2+, Zn.sup.2+) and 200% (i.e.,
binding Co.sup.2+) wild-type OPH activity for paraoxon cleavage.
The H201C mutant had about 10% activity, the H230C mutant had less
than 1% activity, and the H55C mutant bound only one atom of
Co.sup.2+ and possessed little detectable activity, but may still
be useful if possessing a desirable property (e.g., enhanced
stability) (Watkins, L. M., 1997b).
[0188] In an additional example, the sequence and structural
information has been used in production of mutants of OPH
possessing altered metal binding and/or bond-type cleavage
properties. OPH mutants H254R, H257L, and H254R/H257L have been
made to alter amino acids that are thought to interact with nearby
metal-binding amino acids. These mutants also reduced the number of
metal ions (i.e., Co.sup.2+, Zn.sup.2+) binding the enzyme dimer
from four to two, while still retaining 5% to greater than 100%
catalytic rates for the various substrates. These reduced metal
mutants possess enhanced specificity for larger substrates such as
NPPMP and demeton-S, and reduced specificity for the smaller
substrate diisopropyl fluorophosphonate (diSioudi, B. et al.,
1999). In a further example, the H254R mutant and the H257L mutant
each demonstrated a greater than four-fold increase in catalytic
activity and specificity against VX and its analog demeton S. The
H257L mutant also demonstrated a five-fold enhanced specificity
against soman and its analog NPPMP (diSioudi, B. D. et al.,
1999).
[0189] In an example, specific mutants of OPH (a
phosphotriesterase), were designed and produced to aid
phosphodiester substrates to bind and be cleaved by OPH. These
substrates either comprised a negative charge and/or a large amide
moiety. A M317A mutant was created to enlarge the size of the large
subsite, and M317H, M317K, and M317R mutants were created to
incorporate a cationic group in the active site. The M317A mutant
demonstrated a 200-fold cleavage rate enhancement in the presence
of alkylamines, which were added to reduce the substrate's negative
charge. The M317H, M317K, and M317R mutants demonstrated modest
improvements in rate and/or specificity, including a 7-fold
k.sub.cat/K.sub.m improvement for the M317K mutant (Shim, H. et
al., 1998).
[0190] In a further example, the W131K, F132Y, F132H, F306Y, F306H,
F306K, F306E, F132H/F306H, F132Y/F306Y, F132Y/F306H, and
F132H/F306Y mutants were made to add or change the side chain of
active site residues to form a hydrogen bond and/or donate a
hydrogen to a cleaved substrate's leaving group, to enhance the
rate of cleavage for certain substrates, such as
phosphofluoridates. The F132Y, F132H, F306Y, F306H, F132H/F306H,
F132Y/F306Y, F132Y/F306H, and F132H/F306Y mutants all demonstrated
enhanced enzymatic cleavage rates, of about three- to ten-fold
improvement, against the phosphonofluoridate, diisopropyl
fluorophosphonate (Watkins, L. M. et al., 1997a).
[0191] In an additional example, OPH mutants W131F, F132Y, L136Y,
L140Y, L271Y and H257L were designed to modify the active site size
and placement of amino acid side chains to refine the structure of
binding subsites to specifically fit the binding of a VX substrate.
The refinement of the active site structure produced a 33% increase
in cleavage activity against VX in the L136Y mutant (Gopal, S. et
al., 2000).
[0192] Various mutants of OPH have been made to alter the
steriospecificity, and in some cases, the rate of reaction, by
substitutions in substrate binding subsites. For example, the C59A,
G60A, S61A, I106A, W131A, F132A, H254A, H257A, L271A, L303A, F306A,
S308A, Y309A, and M317A mutants of OPH have been produced to alter
the size of various amino acids associated with the small subsite,
the large subsite and the leaving group subsite, in order to alter
enzyme activity and selectivity, including sterioselectivity, for
various OP compounds. The G60A mutant reduced the size of the small
subsite, and decreased both rate (k.sub.cat) and specificity
(k.sub.cat/K.sub.a) for R.sub.p-enantiomers, thereby enhancing the
overall specificity for some S.sub.p-enantiomers to over 11,000:1.
Mutants I106A and S308A, which enlarged the size of the small
subsite, as well as mutant F132A, which enlarged the leaving group
subsite, all increased the reaction rates for R.sub.p-enantiomers
and reduced the specificity for S.sub.p-enantiomers
(Chen-Goodspeed, M. et al., 2001a).
[0193] Additional mutants I106A/F132A, I106A/S308A, F132A/S308A,
I106G, F132G, S308G, I106G/F132G, I106G/S308G, F132G/S308G, and
I106G/F132G/S308G were produced to further enlarge the small
subsite and leaving group subsite. These OPH mutants demonstrated
enhanced selectivity for R.sub.p-enantiomers. Mutants H254Y, H254F,
H257Y, H257F, H257W, H257L, L271Y, L271F, L271W, M317Y, M317F, and
M317W were produced to shrink the large subsite, with the H257Y
mutant, for example, demonstrating a reduced selectivity for
S.sub.p-enantiomers (Chen-Goodspeed, M. et al., 2001b). Further
mutants I106A/H257Y, F132A/H257Y, I106A/F132A/H257Y,
I106A/H257Y/S308A, I106A/F132A/H257W, F132A/H257Y/S308A,
I106G/H257Y, F132G/H257Y, I106G/F132G/H257Y, I106G/H257Y/S308G, and
I106G/F132G/H257Y/S308G were made to simultaneously enlarge the
small subsite and shrink the large subsite. Mutants such as H257Y,
I106A/H257Y, I106G, I106A/F132A, and I106G/F132G/S308G were
effective in altering steriospecificity for S.sub.p:R.sub.p
enantiomer ratios of some substrates to less than 3:1 ratios.
Mutants including F132A/H257Y, I106A/F132A/H257W,
I106G/F132G/H257Y, and I106G/F132G/H257Y/S308G demonstrated a
reversal of selectivity for S.sub.p:R.sub.p enantiomer ratios of
some substrates to ratios from 3.6:1 to 460:1. In some cases, such
a change in steriospecificity was produced by enhancing the rate of
catalysis of a less preferred R.sub.p enantiomer with little change
on the rate of S.sub.p enantiomer cleavage (Chen-Goodspeed, M. et
al., 2001b; Wu, F. et al., 2000a).
[0194] Such alterations in sterioselectivity can enhance OPH
performance against a specific OP compound that is a preferred
target of detoxification, including a CWA. Enlargement of the small
subsite by mutations that substitute the Ile106 and Phe132 residues
with the less bulky amino acid alanine and/or reduction of the
large subsite by a mutation that substitutes His257 with the
bulkier amino acid phenylalanine increased catalytic rates for the
S.sub.p-isomer; and decreased the catalytic rates for the
R.sub.p-isomers of a sarin analog, thus resulting in a triple
mutant, I106A/F132A/H257Y, with a reversed sterioselectivity such
as a S.sub.p:R.sub.p preference of 30:1 for the isomers of the
sarin analog. A mutant of OPH designated G60A has also been created
with enhanced steriospecificity relative to specific analogs of
enantiomers of sarin and soman (Li, W.-S. et al., 2001; Raushel, F.
M., 2002). Of greater interest, these mutant forms of OPH have been
directly assayed against sarin and soman nerve agents, and
demonstrated enhanced detoxification rates for racemic mixtures of
sarin or soman enantiomers. Wild-type OPH has a k.sub.cat for sarin
of 56 s.sup.-1, while the I106A/F132A/H257Y mutant has k.sub.cat
for sarin of 1000 s.sup.-1. Additionally, wild-type OPH has a
k.sub.cat for soman of 5 s.sup.-1, while the G60A Mutant has
k.sub.cat for soman of 10 s.sup.-1 (Kolakoski, Jan E. et al. 1997;
Li, W.-S. et al., 2001).
[0195] It is also possible to produce a mutant enzyme with an
enhanced enzymatic property against a specific substrate by
evolutionary selection rather than rational design. Such techniques
can screen hundreds or thousands of mutants for enhanced cleavage
rates against a specific substrate. The mutants identified may
possess substitutions at amino acids that have not been identified
as directly comprising the active site, or its binding subsites,
using techniques such as NMR, X-ray crystallography and computer
structure analysis, but still contribute to activity for one or
more substrates. For example, selection of OPH mutants based upon
enhanced cleavage of methyl parathion identified the A80V/S365P,
L182S/V310A, I274N, H257Y, H257Y/I274N/S365P, L130M/H257Y/I274N,
and A14T/A80V/L185R/H257Y/I274N mutants as having enhanced
activity. Amino acids Ile274 and Val310 are within 10 .ANG. of the
active site, though not originally identified as part of the active
site from X-ray and computer structure analysis. However, mutants
with substitutions at these amino acids demonstrated improved
activity, with mutants comprising the I274N and H257Y substitutions
particularly active against methyl parathion. Additionally, the
mutant, A14T/A80V/L185R/H257Y/I274N, further comprising a L185R
substitution, was most active having a 25-fold improvement against
methyl parathion (Cho, C. M.-H. et al., 2002).
[0196] In an example, a functional equivalent of OPH may be
prepared that lacks the first 29-31 amino acids of the wild-type
enzyme. The wild-type form of OPH endogenously or recombinantly
expressed in Pseudomonas or Flavobacterium removes the first
N-terminal 29 amino acids from the precursor protein to produce the
mature, enzymatically active protein (Mulbry, W. and Karns, J.,
1989; Serdar, C. M. et al., 1989). Recombinant expressed OPH in
Gliocladium virens apparently removes part or all of this sequence
(Dave, K. I. et al., 1994b). Recombinant expressed OPH in
Streptomyces lividans primarily has the first 29 or 30 amino acids
removed during processing, with a few percent of the functional
equivalents having the first 31 amino acids removed (Rowland, S. S.
et al., 1992). Recombinant expressed OPH in Spodoptera frugiperda
cells has the first 30 amino acids removed during processing (Dave,
K. I. et al., 1994a).
[0197] The 29 amino acid leader peptide sequence targets OPH enzyme
to the cell membrane in Escherichia coli, and this sequence is
partly or fully removed during cellular processing (Dave, K. I. et
al., 1994a; Miller, C. E., 1992; Serdar, C. M. et al., 1989;
Mulbry, W. and Karns, J., 1989). The association of OPH comprising
the leader peptide sequence with the cell membrane in Escherichia
coli expression systems seems to be relatively weak, as brief 15
second sonication releases most of the activity into the
extracellular environment (Dave, K. I. et al., 1994a). For example,
recombinant OPH often is expressed without this leader peptide
sequence to enhance enzyme stability and expression efficiency in
Escherichia coli (Serdar, C. M., et al. 1989). In another example,
recombinant expression efficiency in Pseudomonas putida for OPH was
improved by retaining this sequence, indicating that different
species of bacteria may have varying preferences for a signal
sequence (Walker, A. W. and Keasling, J. D., 2002). However, it is
contemplated that one of ordinary skill in the art can easily
modify the length of an enzymatic sequence to optimize expression
or other properties in a particular organism, or select a cell with
a relatively good ability to express a biomolecule, in light of the
present disclosures and methods known in the art (see U.S. Pat.
Nos. 6,469,145, 5,589,386 and 5,484,728)
[0198] In an example, recombinant OPH sequence-length mutants have
been expressed wherein the first 33 amino acids of OPH have been
removed, and a peptide sequence M-I-T-N-S added at the N-terminus
(Omburo, G. A. et al., 1992; Mulbry, W. and Karns, J., 1989). Often
removal of the 29 amino acid sequence is used when expressing
mutants of OPH comprising one or more amino acid substitutions such
as the C59A, G60A, S61A, I106A, W131A, F132A, H254A, H257A, L271A,
L303A, F306A, S308A, Y309A, M317A, I106A/F132A, I106A/S308A,
F132A/S308A, I106G, F132G, S308G, I106G/F132G, I106G/S308G,
F132G/S308G, I106G/F132G/S308G, H254Y, H254F, H257Y, H257F, H257W,
H257L, L271Y, L271W, M317Y, M317F, M317W, I106A/H257Y, F132A/H257Y,
I106A/F132A/H257Y, I106A/H257Y/S308A, I106A/F132A/H257W,
F132A/H257Y/S308A, I106G/H257Y, F132G/H257Y, I106G/F132G/H257Y,
I106G/H257Y/S308G, and I106G/F132G/H257Y/S308G mutants
(Chen-Goodspeed, M. et al., 2001a). In a further example, LacZ-OPH
fusion protein mutants lacking the 29 amino acid leader peptide
sequence and comprising an amino acid substitution mutant such as
W131F, F132Y, L136Y, L140Y, H257L, L271L, L271Y, F306A, or F306Y
have been recombinantly expressed (Gopal, S. et al., 2000).
[0199] In an additional example, OPH mutants that comprise
additional amino acid sequences are also known in the art. An OPH
fusion protein lacking the 29 amino acid leader sequence and
possessing an additional C-terminal flag octapeptide sequence was
expressed and localized in the cytoplasm of Escherichia coli (Wang,
J. et al., 2001). In another example, nucleic acids encoding
truncated versions of the ice nucleation protein ("InaV") from
Pseudomonas syringae have been used to construct vectors that
express OPH-InaV fusion proteins in Escherichia coli. The InaV
sequences targeted and anchored the OPH-InaV fusion proteins to the
cells' outer membrane (Shimazu, M. et al., 2001a; Wang, A. A. et
al., 2002). In a further example, a vector encoding a similar
fusion protein was expressed in Moraxella sp., and demonstrated a
70-fold improved OPH activity on the cell surface compared to
Escherichia coli expression (Shimazu, M. et al., 2001b). In a
further example, fusion proteins comprising the signal sequence and
first nine amino acids of lipoprotein, a transmembrane domain of
outer membrane protein A ("Lpp-OmpA"), and either a wild-type OPH
sequence or an OPH truncation mutant lacking the first 29 amino
acids has been expressed in Escherichia coli. These OPH-Lpp-OmpA
fusion proteins were targeted and anchored to the Escherichia coli
cell membrane, though the OPH truncation mutant had only 5% to 10%
the activity of the wild-type OPH sequence (Richins, R. D. et al.,
1997; Kaneva, I. et al., 1998). In one example, a fusion protein
comprising N-terminus to C-terminus, a (His)6 polyhistidine tag, a
green fluorescent protein ("GFP"), an enterokinase recognition
site, and an OPH sequence lacking the 29 amino acid leader sequence
has been expressed within Escherichia coli cells (Wu, C.-F. et al.,
2000b, Wu, C.-F. et al., 2002). A similar fusion protein a (His)6
polyhistidine tag, an enterokinase recognition site, and an OPH
sequence lacking the 29 amino acid leader sequence has also been
expressed within Escherichia coli cells (Wu, C.-F. et al., 2002).
Additionally, variations of these GFP-OPH fusion proteins have been
expressed within Escherichia coli cells where an second
enterokinase recognition site was placed at the C-terminus of the
OPH gene fragment sequence, followed by a second OPH gene fragment
sequence (Wu, C.-F. et al., 2001b). The GFP sequence produced
fluorescence that was proportional to both the quantity of the
fusion protein, and the activity of the OPH sequence, providing a
fluorescent assay of enzyme activity and stability in GFP-OPH
fusion proteins (Wu, C.-F. et al., 2000b, Wu, C.-F. et al.,
2002).
[0200] In a further example, a fusion protein comprising an
elastin-like polypeptide ("ELP") sequence, a polyglycine linker
sequence, and an OPH sequence was expressed in Escherichia coli
(Shimazu, M. et al., 2002). In an additional example, a
cellulose-binding domain at the N-terminus of an OPH fusion protein
lacking the 29 amino acid leader sequence, and a similar fusion
protein wherein OPH possessed the leader sequence, where both
predominantly excreted into the external medium as soluble proteins
by recombinant expression in Escherichia coli (Richins, R. D. et
al., 2000).
[0201] b. Paraoxonase Functional Equivalents
[0202] Various chemical modifications to the amino acid residues of
the recombinantly expressed human paraoxonase have been used to
identify specific residues including tryptophans, histidines,
aspartic acids, and glutamic acids as of importance to enzymatic
activity for the cleavage of phenylacetate, paraoxon,
chlorpyrifosoxon, and diazoxon. Additionally, comparison to
conserved residues in human, mouse, rabbit, rat dog, chicken, and
turkey paraoxonase enzymes was used to further identify amino acids
for the production of specific mutants. Site-directed mutagenesis
was used to alter the enzymatic activity of human paraoxonase
through conservative and non-conservative substitutions, and thus
clarify the specific amino acids of particular importance for
enzymatic activity. Specific paraoxonase mutants include the
sequence analogs E32A, E48A, E52A, D53A, D88A, D107A, H114N, D121A,
H133N, H154N, H160N, W193A, W193F, W201A, W201F, H242N, H245N,
H250N, W253A, W253F, D273A, W280A, W280F, H284N, or H347N.
[0203] The various paraoxonase mutants generally had different
enzymatic properties. For example, W253A had a 2-fold greater
k.sub.cat; and W201F, W253A and W253F each had a 2 to 4 fold
increase in k.sub.cat, though W201F also had a lower substrate
affinity. A non-conservative substitution mutant W280A had 1%
wild-type paraoxonase activity, but the conservative substitution
mutant W280F had similar activity as the wild-type paraoxonase
(Josse, D. et al., 1999; Josse, D. et al., 2001).
[0204] c. Squid-Type DFPase Functional Equivalents
[0205] Various chemical modifications to the amino acid residues of
the recombinantly expressed squid-type DFPase from Loligo vulgaris
has been used to identify which specific types of residues of
modified arginines, aspartates, cysteines, glutamates, histidines,
lysines, and tyrosines, are important to enzymatic activity for the
cleavage of DFP. Modification of histidines generally reduced
enzyme activity, and site-directed mutagenesis was used to clarify
which specific histidines are of importance for enzymatic activity.
Specific squid-type DFPase mutants include the sequence analogs
H181N, H224N, H274N, H219N, H248N, or H287N.
[0206] The H287N mutant lost about 96% activity, and is thought to
act as a hydrogen acceptor in active site reactions. The H181N and
H274N mutants lost between 15% and 19% activity, and are thought to
help stabilize the enzyme. The H224N mutant gained about 14%
activity, indicating that alterations to this residue may also
affect activity (Hartleib, J. and Ruterjans, H., 2001b).
[0207] In a further example of squid-type DFPase functional
equivalents, recombinant squid-type DFPase sequence-length mutants
have been expressed wherein a (His)6 tag sequence and a thrombin
cleavage site has been added to the squid-type DFPase (Hartleib, J.
and Ruterjans, H., 2001a). In an additional example, a polypeptide
comprising amino acids 1-148 of squid-type DFPase has been admixed
with a polypeptide comprising amino acids 149-314 of squid-type
DFPase to produce an active enzyme (Hartleib, J. and Ruterjans, H.,
2001a).
[0208] 3. Combinations of Biomolecules
[0209] It is contemplated that in various embodiments, a
composition of the present invention may comprise one or more
selected biomolecules, with an enzyme being a preferred
biomolecule. It is contemplated that in specific embodiments, a
composition of the present invention may comprise an endogenously
expressed wild-type enzyme, a recombinant enzyme, or a combination
thereof. In specific aspects, a recombinant enzyme comprises a
wild-type enzyme, a functional equivalent enzyme, or a combination
thereof. Numerous examples of enzymes with different properties are
described herein, and any such enzyme as would be known to one of
ordinary skill in the art is contemplated for inclusion in a
composition of the present invention.
[0210] It is contemplated that a combination of biomolecules may be
selected for inclusion in the biomolecule composition, coating
and/or paint, to optimize one or more properties of such a
composition of the present invention. Thus, a composition of the
present invention may comprise 1 to 100 or more different selected
biomolecules of interest, including all intermediate ranges and
combinations thereof. For example, as various enzymes have
differing binding properties, catalytic properties, stability
properties, properties related to environmental safety, etc, one
may select a combination of enzymes to confer the a more desirable
range of properties to a composition of the present invention. In a
specific example, it is contemplated that phosphoric triester
hydrolases, with differing but desirable abilities to cleave the
chiral centers of OP compounds, may be admixed to confer a more
desirable range of catalytic properties to a composition of the
present invention than would be achieved by the selection of a
single phosphoric triester hydrolase.
[0211] C. Recombinantly Produced Enzymes
[0212] In certain aspects, an enzyme of the present invention may
be biologically produced in cell, tissue and/or organism
transformed with a genetic expression vector. As used herein, an
"expression vector" refers to a carrier nucleic acid molecule, into
which a nucleic acid sequence can be inserted, wherein the nucleic
acid sequence is capable of being transcribed into a ribonucleic
acid ("RNA") molecule after introduction into a cell. Usually an
expression vector comprises deoxyribonucleic acid ("DNA"). As used
herein, an "expression system" refers to an expression vector, and
may further comprise additional reagents needed to promote
insertion of a nucleic acid sequence, introduction into a cell,
transcription and/or translation. As used herein, a "vector,"
refers to a carrier nucleic acid molecule into which a nucleic acid
sequence can be inserted for introduction into a cell. Certain
vectors are capable of replication of the vector and/or any
inserted nucleic acid sequence in a cell. For example, a viral
vector may be used in conjunction with either an eukaryotic or
prokaryotic host cell, particularly one that is permissive for
replication or expression of the vector. A cell that is capable of
being transformed with a vector is known herein as a "host
cell."
[0213] In general embodiments, the inserted nucleic acid sequence
encodes for at least part of a gene product. In some embodiments
wherein the nucleic acid sequence is transcribed into an RNA
molecule, the RNA molecule is then translated into a proteinaceous
molecule. As used herein, a "gene" refers to a nucleic acid
sequence isolated from an organism, and/or man-made copies or
mutants thereof, that comprises a nucleic acid sequence capable of
being transcribed and/or translated in an organism. A "gene
product" is the transcribed RNA and/or translated proteinaceous
molecule from a gene. Often, only partial nucleic acid sequences of
a gene, known herein as a "gene fragment," are used COME BACK to
produce a part of the gene product. Many gene and gene fragment
sequences are known in the art, and are both commercially available
and/or publicly disclosed at a database such as Genbank. It is
contemplated that a gene and/or a gene fragment can be used to
recombinantly produce an enzyme for use in the present invention.
It is further contemplated that a gene and/or a gene fragment can
be use in construction of a fusion protein comprising an enzyme,
for use in the present invention.
[0214] In certain embodiments, a nucleic acid sequence such as a
nucleic acid sequence encoding an enzyme, or any other desired RNA
or proteinaceous molecule (as well as a nucleic acid sequence
comprising a promoter, a ribosome binding site, an enhancer, a
transcription terminator, an origin of replication, or other
nucleic acid sequences described herein or would be known by one of
ordinary skill in the art in light of the present disclosures) may
be recombinantly produced or synthesized using any method or
technique known to those of ordinary skill in the art in various
combinations. [In "Molecular Cloning" (Sambrook, J., and Russell,
D. W., Eds.) 3rd Edition, Cold Spring Harbor, N.Y.: Cold Spring
Harbor Laboratory Press, 2001; In "Current Protocols in Molecular
Biology" (Chanda, V. B. Ed.) John Wiley & Sons, 2002; In
"Current Protocols in Cell Biology" (Morgan, K. Ed.) John Wiley
& Sons, 2002; In "Current Protocols in Nucleic Acid Chemistry"
(Harkins, E. W. Ed.) John Wiley & Sons, 2002; In "Current
Protocols in Protein Science" (Taylor, G. Ed.) John Wiley &
Sons, 2002; In "Current Protocols in Pharmacology" (Taylor, G. Ed.)
John Wiley & Sons, 2002; In "Current Protocols in Cytometry"
(Robinson, J. P. Ed.) John Wiley & Sons, 2002; In "Current
Protocols in Immunology" (Coico, R. Ed.) John Wiley & Sons,
2002]. For example, a gene and/or a gene fragment encoding the
enzyme of interest may be isolated and/or amplified through
polymerase chain reaction ("PCR.TM.") technology. Often such
nucleic acid sequence is readily available from a public database
and/or a commercial vendor, as previously described.
[0215] Nucleic acid sequences, called codons, encoding for each
amino acid are well known in the art, and used to copy and/or
mutate a nucleic acid sequence to produce a desired mutant in an
expressed amino acid sequence. Codons comprise nucleotides such as
adenine ("A"), cytosine ("C"), guanine ("G"), thymine ("T") and
uracil ("U"). The common amino acids are generally encoded by the
following codons: alanine is encoded by GCU, GCC, GCA, or GCG;
arginine is encoded by CGU, CGC, CGA, CGG, AGA, or AGG; aspartic
acid is encoded by GAU or GAC; asparagine is encoded by AAU or AAC;
cysteine is encoded by UGU or UGC; glutamic acid is encoded by GAA
or GAG; glutamine is encoded by CAA or CAG; glycine is encoded by
GGU, GGC, GGA, or GGG; histidine is encoded by CAU or CAC;
isoleucine is encoded by AUU, AUC, or AUA; leucine is encoded by
UUA, UUG, CUU, CUC, CUA, or CUG; lysine is encoded by AAA or AAG;
methionine is encoded by AUG; phenylalanine is encoded by UUU or
UUC; proline is encoded by CCU, CCC, CCA, or CCG; serine is encoded
by AGU, AGC, UCU, UCC, UCA, or UCG; threonine is encoded by ACU,
ACC, ACA, or ACG; tryptophan is encoded by UGG; tyrosine is encoded
by UAU or UAC; and valine is encoded by GUU, GUC, GUA, or GUG.
[0216] A mutation in a nucleic acid encoding a proteinaceous
molecule may be introduced into the nucleic acid sequence through
any technique known to one of ordinary skill in the art. As would
be well understood by those of ordinary skill in the art, such a
mutation may be bioengineered to a specific region of a nucleic
acid comprising one or more codons using a technique such as
site-directed mutagenesis or cassette mutagenesis. Numerous
examples of phosphoric triester hydrolase mutants have been
produced using site-directed mutagenesis or cassette mutagenesis,
and are described herein.
[0217] It is contemplated that for recombinant expression, the
choice of codons may be made to mimic the host cell's molecular
biological activity, in order to optimize the efficiency of
expression from an expression vector. For example, codons may be
selected to match the preferred codons used by a host cell in
expressing endogenous proteins. In some aspects, the codons
selected may be chosen to approximate the G-C content of an
expressed gene and/or a gene fragment in a host cell's genome, or
the G-C content of the genome itself. In other aspects, a host cell
may be genetically altered to recognize more efficiently use a
variety of codons, such as Escherichia coli host cells that are
dnaY gene positive (Brinkmann, U. et al., 1989).
[0218] 1. General Expression Vector Components and Use
[0219] An expression vector may comprise specific nucleic acid
sequences such as a promoter, a ribosome binding site, an enhancer,
a transcription terminator, an origin of replication, or other
nucleic acid sequence described herein or would be known by one of
ordinary skill in the art in light of the present disclosures, in
various combinations. A nucleic acid sequence can be "exogenous,"
which means that it is foreign to the cell into which the vector is
being introduced or that the sequence is homologous to a sequence
in the cell, but in a position within the host cell nucleic acid in
which the sequence is ordinarily not found. An expression vector
may have one or more nucleic acid sequences removed by restriction
enzyme digestion, modified by mutagenesis, and/or replaced with
another more appropriate nucleic acid sequence, for transcription
and/or translation in a host cell suitable for the expression
vector selected.
[0220] One of skill in the art can construct a vector through
standard recombinant techniques, which are well known and routine
in the art. Further, one of skill in the art would know how to
express a vector to transcribe a nucleic acid sequence and/or
translate its cognate proteinaceous molecule. One of skill in the
art would further understand the conditions under which to incubate
all of the above described host cells to maintain them and to
permit replication of a vector. Also understood and known are
techniques and conditions that would allow large-scale production
of a vector, as well as production of a nucleic acid sequence
encoded by a vector into an RNA molecule and/or translation of the
RNA molecule into a cognate proteinaceous molecule.
[0221] In certain embodiments, a cell may express multiple gene
and/or gene fragment products from the same vector, and/or express
more than one vector. Often this occurs simply as part of the
normal function of a multi-vector expression system. For example,
one gene or gene fragment is often used to produce a repressor that
suppresses the activity of a promoter that controls the expression
of a gene or a gene fragment of interest. The repressor gene and
the desired gene may be on different vectors. However, multiple
gene, gene fragment and/or expression systems may be used to
express an enzymatic sequence of interest and another gene or gene
fragment that is desired for a particular function. In an example,
recombinant Pseudomonas putida has co-expressed OPH from one
vector, and the multigenes encoding the enzymes for converting
p-nitrophenol to .beta.-ketoadipate from a different vector. The
expressed OPH catalyzed the cleavage of parathion to p-nitrophenol.
The additionally expressed recombinant enzymes converted the
p-nitrophenol, which is a moderately toxic compound, to
.beta.-ketoadipate, thereby detoxifying both an OP compound and the
byproducts of its hydrolysis (Walker, A. W. and Keasling, J. D.,
2002). In a further example, Escherichia coli cells expressed a
cell surface targeted INPNC-OPH fusion protein from one vector to
detoxify OP compounds, and co-expressed from a different vector a
cell surface targeted Lpp-OmpA-cellulose binding domain fusion
protein to immobilize the cell to a cellulose support (Wang, A. A.
et al., 2002). In an additional example, a vector co-expressed an
antisense RNA sequence to the transcribed stress response gene
.sigma..sup.32 and OPH in Escherichia coli. The antisense
.sigma..sup.32 RNA was used to reduce the cell's stress response,
including proteolytic damage, to an expressed recombinant
proteinaceous molecule. A six-fold enhanced specific activity of
expressed OPH enzyme was seen (Srivastava, R. et al., 2000). In a
further example, multiple OPH fusion proteins were expressed from
the same vector using the same promoter but separate ribosome
binding sites (Wu, C.-F. et al., 2001b).
[0222] As is well known to those of skill in the art, an expression
vector generally comprises a plurality of functional nucleic acid
sequences that either comprise a nucleic acid sequence with a
molecular biological function in a host cell, such as a promoter,
an enhancer, a ribosome binding site, a transcription terminator,
etc, and/or encode a proteinaceous sequence, such as a leader
peptide, a polypeptide sequence with enzymatic activity, a peptide
or polypeptide with a binding property, etc. A nucleic acid
sequence may comprise a "control sequence," which refers to a
nucleic acid sequence necessary for the transcription and possibly
translation of an operatively linked coding sequence in a
particular host cell. As used herein, an "operatively linked" or
"operatively positioned" nucleic acid sequence refers to the
placement of one nucleic acid sequence into a functional
relationship with another nucleic acid sequence. Vectors and
expression vectors may further comprise one or more nucleic acid
sequences that serve other functions as well and are described
herein.
[0223] The various functional nucleic acid sequences that comprise
an expression vector are operatively linked so to position the
different nucleic acid sequences for optimal function in a host
cell. In certain cases, the functional nucleic acid sequences may
be contiguous such as placement of a nucleic acid sequence encoding
a leader peptide sequence in correct amino acid frame with a
nucleic acid sequence encoding a polypeptide comprising a
polypeptide sequence with enzymatic activity. In other cases, the
functional nucleic acid sequences may be non-contiguous such as
placing a nucleic acid sequence comprising an enhancer distal to a
nucleic acid sequence comprising such sequences as a promoter, a
encoded proteinaceous molecule, a transcription termination
sequence, etc. One or more nucleic acid sequences may be
operatively linked using methods well known in the art,
particularly ligation at restriction sites that may pre-exist in a
nucleic acid sequence or be added through mutagenesis.
[0224] A "promoter" is a control sequence that is a region of a
nucleic acid sequence at which initiation and rate of transcription
are controlled. In the context of a nucleic acid sequence
comprising a promoter and an additional nucleic acid sequence,
particularly one encoding a gene or gene fragment's product, the
phrases "operatively linked," "operatively positioned," "under
control," and "under transcriptional control" mean that a promoter
is in a correct functional location and/or orientation in relation
to the additional nucleic acid sequence to control transcriptional
initiation and/or expression of the additional nucleic acid
sequence. A promoter may contain genetic elements at which
regulatory proteins and molecules may bind such as RNA polymerase
and other transcription factors. A promoter employed may be
constitutive, tissue-specific, inducible, and/or useful under the
appropriate conditions to direct high level expression of the
introduced nucleic acid sequence, such as is advantageous in the
large-scale production of a recombinant proteinaceous molecule.
Examples of a promoter include a lac, a tac, an amp, a heat shock
promoter of a P-element of Drosophila, a baculovirus polyhedron
gene promoter, or a combination thereof. In a specific example, the
nucleic acids encoding OPH have been expressed using the polyhedron
promoter of a baculoviral expression vector (Dumas, D. P. et al.,
1990). In a further example, a Cochiobolus heterostrophus promoter,
prom1, has been used to express a nucleic acid encoding OPH (Dave,
K. I. et al., 1994b).
[0225] The promoter may be endogenous or heterologous. An
"endogenous promoter" comprises one naturally associated with a
gene or sequence, as may be obtained by isolating the 5' non-coding
sequences located upstream of the coding segment and/or exon.
Alternatively, certain advantages will be gained by positioning the
coding nucleic acid sequence under the control of a "heterologous
promoter" or "recombinant promoter," which refers to a promoter
that is not normally associated with a nucleic acid sequence in its
natural environment.
[0226] A specific initiation signal also may be required for
efficient translation of a coding sequence by the host cell. Such a
signal may include an ATG initiation codon ("start codon") and/or
an adjacent sequence. Exogenous translational control signals,
including the ATG initiation codon, may need to be provided. One of
ordinary skill in the art would readily be capable of determining
this and providing the necessary signals. It is well known that the
initiation codon must be "in-frame" with the reading frame of the
desired coding sequence to ensure translation of the entire insert.
The exogenous translational control signal and/or an initiation
codon can be either natural or synthetic. The efficiency of
expression may be enhanced by the inclusion of an appropriate
transcription enhancer.
[0227] A promoter may or may not be used in conjunction with an
"enhancer," which refers to a cis-acting regulatory sequence
involved in the transcriptional activation of a nucleic acid
sequence. An enhancer may be one naturally associated with a
nucleic acid sequence, located either downstream or upstream of
that sequence. A recombinant or heterologous enhancer refers also
to an enhancer not normally associated with a nucleic acid sequence
in its natural environment. Such a promoter and/or enhancer may
include a promoter and/or enhancer of another gene, a promoter
and/or enhancer isolated from any other prokaryotic, viral, or
eukaryotic cell, a promoter and/or enhancer not "naturally
occurring," i.e., a promoter and/or enhancer comprising different
elements of different transcriptional regulatory regions, and/or
mutations that alter expression. In addition to producing a nucleic
acid sequence comprising a promoter and/or enhancer synthetically,
a sequence may be produced using recombinant cloning and/or nucleic
acid amplification technology, including PCR.TM., in connection
with the compositions disclosed herein (U.S. Pat. No. 4,683,202,
U.S. Pat. No. 5,928,906).
[0228] It will be important to employ a promoter and/or enhancer
that effectively directs the expression of the nucleic acid
sequence in the cell type, chosen for expression. Those of skill in
the art of molecular biology generally know the use of promoters,
enhancers, and cell type combinations for expression. Furthermore,
it is contemplated the control sequences that direct transcription
and/or expression of sequences within non-nuclear organelles,
including eukaryotic organelles such as mitochondria, chloroplasts,
and the like, can be employed as well.
[0229] Vectors can include a multiple cloning site ("MCS"), which
is a nucleic acid region that contains multiple restriction enzyme
sites, any of which can be used in conjunction with standard
recombinant technology to digest the vector. "Restriction enzyme
digestion" refers to catalytic cleavage of a nucleic acid molecule
with an enzyme which functions only at specific locations in a
nucleic acid molecule. Many of these restriction enzymes are
commercially available. Use of such enzymes is widely understood by
those of skill in the art. Frequently, a vector is linearized or
fragmented using a restriction enzyme that cuts within the MCS to
enable an exogenous nucleic acid sequence to be ligated to the
vector. "Ligation" refers to the process of forming phosphodiester
bonds between two nucleic acid fragments, which may or may not be
contiguous with each other. Techniques involving restriction
enzymes and ligation reactions are well known to those of skill in
the art of recombinant technology.
[0230] A "fusion protein," as used herein, is an expressed
contiguous amino acid sequence comprising a proteinaceous molecule
of interest and one or more additional peptide or polypeptide
sequences. The additional peptide or polypeptide sequence generally
provides an useful additional property to the fusion protein,
including but not limited to, targeting the fusion protein to a
particular location within or external to the host cell (e.g., a
signal peptide); promoting the ease of purification and/or
detection of the fusion protein (e.g., a tag, a fusion partner);
promoting the ease of removal of one or more additional sequences
from the peptide or polypeptide of interest (e.g., a protease
cleavage site); and separating one or more sequences of the fusion
protein to allow optimal activity or function of the sequence(s)
(e.g., a linker sequence).
[0231] As used herein a "tag" is a peptide sequence operatively
associated to the sequence of another peptide or polypeptide
sequence. Examples of a tag include a His-tag, a strep-tag, a
flag-tag, a T7-tag, a S-tag, a HSV-tag, a polyarginine-tag, a
polycysteine-tag, a polyaspartic acid-tag, a polyphenylalanine-tag,
or a combination thereof. A His-tag is 6 or 10 amino acids in
length, and can be incorporated at the N-terminus, C-terminus or
within an amino acid sequence for use in detection and
purification. A His tag binds affinity columns comprising nickel,
and is eluted using low pH conditions or with imidazole as a
competitor (Unger, T. F., 1997). A strep-tag is 10 amino acids in
length, and can be incorporated at the C-terminus. A strep-tag
binds streptavidin or affinity resins that comprise streptavidin. A
flag-tag is 8 amino acids in length, and can be incorporated at the
N-terminus or C-terminus of an amino acid sequence for use in
purification. A T7-tag is 11 or 16 amino acids in length, and can
be incorporated at the N-terminus or within an amino acid sequence
for use in purification. A S-tag is 15 amino acids in length, and
can be incorporated at the N-terminus, C-terminus or within an
amino acid sequence for use in detection and purification. A
HSV-tag is 11 amino acids in length, and can be incorporated at the
C-terminus of an amino acid sequence for use in purification. The
HSV tag binds an anti-HSV antibody in purification procedures
(Unger, T. F., 1997). A polyarginine-tag is 5 to 15 amino acids in
length, and can be incorporated at the C-terminus of an amino acid
sequence for use in purification. A polycysteine-tag, is 4 amino
acids in length, and can be incorporated at the N-terminus of an
amino acid sequence for use in purification. A polyaspartic
acid-tag can be 5 to 16 amino acids in length, and can be
incorporated at the C-terminus of an amino acid sequence for use in
purification. A polyphenylalanine-tag is 11 amino acids in length,
and can be incorporated at the N-terminus of an amino acid sequence
for use in purification.
[0232] In one example, a (His)6 tag sequence has been used to
purify fusion proteins comprising GFP-OPH or OPH using immobilized
metal affinity chromatography ("IMAC") (Wu, C.-F. et al., 2000b;
Wu, C.-F. et al., 2002). In a further example, a (His)6 tag
sequence followed by a thrombin cleavage site has been used to
purify fusion proteins comprising squid-type DFPase using IMAC
(Hartleib, J. and Ruterjans, H., 2001a). In a further example, an
OPH fusion protein comprising a C-terminal flag has been expressed
(Wang, J. et al., 2001).
[0233] As used herein a "fusion partner" is a polypeptide that is
operatively associated to the sequence of another peptide or
polypeptide of interest. Properties that a fusion partner can
confer to a fusion protein include, but are not limited to,
enhanced expression, enhanced solubility, ease of detection, and/or
ease of purification of a fusion protein. Examples of a fusion
partner include a thioredoxin, a cellulose-binding domain, a
calmodulin binding domain, an avidin, a protein A, a protein G, a
glutathione-S-transferase, a chitin-binding domain, an ELP, a
maltose-binding domain, or a combination thereof. Thioredoxin can
be incorporated at the N-terminus or C-terminus of an amino acid
sequence for use in purification. A cellulose-binding domain binds
a variety of resins comprising cellulose or chitin (Unger, T. F.,
1997). A calmodulin-binding domain binds affinity resins comprising
calmodulin in the presence of calcium, and allows elution of the
fusion protein in the presence of ethylene glycol tetra acetic acid
("EGTA") (Unger, T. F., 1997). Avidin is useful in purification or
detection. A protein A or a protein G binds a variety of
anti-bodies for ease of purification. Protein A is generally bound
to an IgG sepharose resin (Unger, T. F., 1997). Streptavidin is
useful in purification or detection. Glutathione-S-transferase can
be incorporated at the N-terminus of an amino acid sequence for use
in detection or purification. Glutathione-S-transferase binds
affinity resins comprising glutathione (Unger, T. F., 1997). An
elastin-like polypeptide comprises repeating sequences (e.g., 78
repeats) which reversibly converts itself, and thus the fusion
protein, from an aqueous soluble polypeptide to an insoluble
polypeptide above an empirically determined transition temperature.
The transition temperature is affected by the number of repeats,
and can be determined spectrographically using techniques known in
the art, including measurements at 655 nano meters ("nm") over a
4.degree. C. to 80.degree. C. range (Urry, D. W. 1992; Shimazu, M.
et al., 2002). A chitin-binding domain preferable comprises an
intein cleavage site sequence, and can be incorporated at the
C-terminus for purification. The chitin-binding domain binds
affinity resins comprising chitin, and an intein cleavage site
sequence allows the self-cleavage in the presence of thiols at
reduced temperature to release the peptide or polypeptide sequence
of interest (Unger, T. F., 1997). A maltose-binding domain can be
incorporated at the N-terminus or C-terminus of an amino acid
sequence for use in detection or purification. A maltose-binding
domain sequence usually further comprises a ten amino acid poly
asparagine sequence between the maltose binding domain and the
sequence of interest to aid the maltose-binding domain in binding
affinity resins comprising amylose (Unger, T. F., 1997).
[0234] In an example, a fusion protein comprising an elastin-like
polypeptide sequence and an OPH sequence has been expressed
(Shimazu, M. et al., 2002). In a further example, a
cellulose-binding domain-OPH fusion protein has also been
recombinantly expressed (Richins, R. D. et al., 2000). In an
additional example, a maltose binding protein-E3 carboxylesterase
fusion protein has been recombinantly expressed (Claudianos, C. et
al., 1999)
[0235] A protease cleavage site promotes proteolytic removal of the
fusion partner from the peptide or polypeptide of interest. Often,
a fusion protein is bound to an affinity resin, and cleavage at the
cleavage site promotes the ease of purification of a peptide or
polypeptide of interest with most or all of the tag or fusion
partner sequence removed (Unger, T. F., 1997). Protease cleavage
sites are well known in the art, and examples of protease cleavage
sites include the factor Xa cleavage site, which is four amino
acids in length; the enterokinase cleavage site, which is five
amino acids in length; the thrombin cleavage site, which is six
amino acids in length; the rTEV protease cleavage site, which is
seven amino acids in length; the 3C human rhino virus protease,
which is eight amino acids in length; and the PreScission.TM.
cleavage site, which is eight amino acids in length. In an example,
an enterokinase recognition site was used to separate an OPH
sequence from a fusion partner (Wu, C.-F. et al., 2000b; Wu, C.-F.
et al., 2001b).
[0236] In an eukaryotic expression system (e.g., a fungal
expression system), the "terminator region" or "terminator" may
also comprise a specific DNA sequence that permits site-specific
cleavage of the new transcript so as to expose a polyadenylation
site. This signals a specialized endogenous polymerase to add a
stretch of adenosine nucleotides ("polyA") of about about 200 in
number to the 3' end of the transcript. RNA molecules modified with
this polyA tail appear to more stable and are translated more
efficiently. Thus, in other embodiments involving an eukaryote, it
is preferred that that terminator comprises a signal for the
cleavage of the RNA, and it is more preferred that the terminator
signal promote polyadenylation of the message. The terminator
and/or polyadenylation site elements can serve to enhance message
levels and/or to minimize read through from the cassette into other
sequences.
[0237] A terminator contemplated for use in the invention include
any known terminator of transcription described herein or known to
one of ordinary skill in the art, including but not limited to, for
example, a termination sequence of a gene, such as for example, a
bovine growth hormone terminator or a viral termination sequence,
such as for example a SV40 terminator. In certain embodiments, the
termination signal may be a lack of transcribable or translatable
sequence, such as due to a sequence truncation. In one example, a
trpC terminator from Aspergillus nidulans has been used in the
expression of recombinant OPH (Dave, K. I. et al., 1994b).
[0238] In expression, particularly eukaryotic expression, one will
typically include a polyadenylation signal to effect proper
polyadenylation of the transcript. The nature of the
polyadenylation signal is not believed to be crucial to the
successful practice of the invention, and/or any such sequence may
be employed. Preferred embodiments include the SV40 polyadenylation
signal and/or the bovine growth hormone polyadenylation signal,
convenient and/or known to function well in various target cells.
Polyadenylation may increase the stability of the transcript or may
facilitate cytoplasmic transport.
[0239] In order to propagate a vector in a host cell, it may
contain one or more origins of replication sites ("ori"), which is
a specific nucleic acid sequence at which replication is initiated.
Alternatively an autonomously replicating sequence ("ARS") can be
employed if the host cell is yeast.
[0240] Various types of prokaryotic and/or eukaryotic expression
vectors are known in the art. Examples of types of expression
vectors include a bacterial artificial chromosome ("BAC"), a
cosmid, a plasmid [e.g., a pMB1/colE1 derived plasmid such as
pBR322, pUC18; a Ti plasmid of Agrobacterium tumefaciens derived
vector (Rogers, S. G. et al., 1987)], a virus (e.g., a
bacteriophage such as a bacteriophage M13, an animal virus, a plant
virus), or a yeast artificial chromosome ("YAC"). Some vectors,
known herein as "shuttle vectors" may employ control sequences that
allow it to be replicated and/or expressed in both prokaryotic and
eukaryotic cells [e.g., a wheat dwarf virus ("WDV") pW1-11 or
pW1-GUS shuttle vector (Ugaki, M. et al., 1991)]. An expression
vector operatively linked to a nucleic acid sequence encoding an
enzymatic sequence of the present invention may be constructed
using techniques known to those of skill in the art in light of the
present disclosures [In "Molecular Cloning" (Sambrook, J., and
Russell, D. W., Eds.) 3rd Edition, Cold Spring Harbor, N.Y.: Cold
Spring Harbor Laboratory Press, 2001; In "Current Protocols in
Molecular Biology" (Chanda, V. B. Ed.) John Wiley & Sons, 2002;
In "Current Protocols in Nucleic Acid Chemistry" (Harkins, E. W.
Ed.) John Wiley & Sons, 2002; In "Current Protocols in Protein
Science" (Taylor, G. Ed.) John Wiley &. Sons, 2002; In "Current
Protocols in Cell Biology" (Morgan, K. Ed.) John Wiley & Sons,
2002].
[0241] Numerous expression systems exist that comprise at least a
part or all of the compositions discussed above. Prokaryote- and/or
eukaryote-based systems can be employed for use with the present
invention to produce nucleic acid sequences, or their cognate
polypeptides, proteins and peptides. Many such systems are widely
available, including those provide by commercial vendors, as would
be known to those of skill in the art. For example, an insect
cell/baculovirus system can produce a high level of protein
expression of a heterologous nucleic acid sequence, such as
described in U.S. Pat. Nos. 5,871,986, 4,879,236, both incorporated
herein by reference, and which can be bought, for example, under
the name MAXBAC.RTM. 2.0 from INVITROGEN.RTM. and BACPACK.TM.
BACULOVIRUS EXPRESSION SYSTEM FROM CLONTECH.RTM.. In an addition
example of an expression system include STRATAGENE.RTM.'s COMPLETE
CONTROL.TM. Inducible Mammalian Expression System, which involves a
synthetic ecdysone-inducible receptor, or its pET Expression
System, an Escherichia coli expression system. Another example of
an inducible expression system is available from INVITROGEN.RTM.,
which carries the T-REX.TM. (tetracycline-regulated expression)
System, an inducible mammalian expression system that uses the
full-length CMV promoter. INVITROGEN.RTM. also provides a yeast
expression system called the Pichia methanolica Expression System,
which is designed for high-level production of recombinant proteins
in the methylotrophic yeast Pichia methanolica. In a specific
example, E3 carboxylesterase enzymatic sequences and phosphoric
triester hydrolase functional equivalents have been recombinantly
expressed in a BACPACK.TM. Baculovirus Expression System From
CLONTECH.RTM. (Newcomb, R. D. et al., 1997; Campbell, P. M. et al.,
1998). In certain embodiments, a biomolecule may be expressed in a
plant cell (e.g., a corn cell), using techniques such as those
described in U.S. Pat. Nos. 6,504,085, 6,136,320, 6,087,558,
6,034,298, 5,914,123, and 5,804,694.
[0242] 2. Prokaryotic Expression Vectors and Use
[0243] In preferred embodiments, a prokaryote such as a bacterium
comprises a host cell. In specific aspects, the bacterium host cell
comprises a Gram-negative bacterium cell. Various prokaryotic host
cells have been used in the art with expression vectors, and it is
contemplated that any prokaryotic host cell known in the art may be
used to express a peptide or polypeptide comprising an enzyme
sequence of the present invention.
[0244] An expression vector for use in prokaryotic cells generally
comprises nucleic acid sequences such as, a promoter, a ribosome
binding site (e.g., a Shine-Delgarno sequence), a start codon, a
multiple cloning site, a fusion partner, a protease cleavage site,
a stop codon, a transcription terminator, an origin of replication,
a repressor, and/or any other additional nucleic acid sequence that
would be used in such an expression vector, as would be known to
one of ordinary skill in the art [Makrides, S. C., 1996; Hannig, G.
and Makrides, S. C., 1998; Stevens, R. C., 2000; In "Molecular
Cloning" (Sambrook, J., and Russell, D. W., Eds.) 3rd Edition, Cold
Spring Harbor, N.Y.: Cold Spring Harbor Laboratory Press, 2001; In
"Current Protocols in Molecular Biology" (Chanda, V. B. Ed.) John
Wiley & Sons, 2002; In "Current Protocols in Nucleic Acid
Chemistry" (Harkins, E. W. Ed.) John Wiley & Sons, 2002; In
"Current Protocols in Protein Science" (Taylor, G. Ed.) John Wiley
& Sons, 2002; In "Current Protocols in Cell Biology" (Morgan,
K. Ed.) John Wiley & Sons, 2002].
[0245] A promoter generally is positioned 10 to 100 nucleotides 5'
to a nucleic acid sequence comprising a ribosome binding site.
Examples of promoters that have been used in a prokaryotic cell
includes a T5 promoter, a lac promoter, a tac promoter, a trc
promoter, an araBAD promoter, a P.sub.L promoter, a T7 promoter, a
T7-lac operator promoter, and variations thereof. The T5 promoter
is regulated by the lactose operator. A lac promoter (e.g., a lac
promoter, a lacUV5 promoter), a tac promoter (e.g., a tacI
promoter, a tacII promoter), a T7-lac operator promoter or a trc
promoter are each suppressed by a lacI repressor, a more effective
lacI.sup.Q repressor or an even stronger lacI.sup.Q1 repressor
(Glascock, C. B. and Weickert, M. J., 1998).
Isopropyl-.beta.-D-thiogalactoside ("IPTG") is used to induce lac,
tac, T7-lac operator and trc promoters. An araBAD promoter is
suppressed by an araC repressor, and is induced by 1-arabinose. A
P.sub.L promoter or a T7 promoter are each suppressed by a
.lambda.clts857 repressor, and induced by a temperature of
42.degree. C. Nalidixic acid may be used to induce a P.sub.L
promoter.
[0246] In an example, recombinant amino acid substitution mutants
of OPH have been expressed in Escherichia coli using a lac promoter
induced by IPTG (Watkins, L. M. et al., 1997b). In another example,
recombinant wild type and a signal sequence truncation mutant of
OPH was expressed in Pseudomonas putida under control of a lactac
and tac promoters (Walker, A. W. and Keasling, J. D., 2002). In a
further example, an OPH-Lpp-OmpA fusion protein has been expressed
in Escherichia coli strains JM105 and XL1-Blue using a constitutive
lpp-lac promoter or a tac promoter induced by IPTG and controlled
by a lacI.sup.Q repressor (Richins, R. D. et al., 1997; Kaneva, I.
et al., 1998; Mulchandani, A. et al., 1999b). In an additional
example, a cellulose-binding domain-OPH fusion protein has also
been recombinantly expressed under the control of a T7 promoter
(Richins, R. D. et al., 2000). In a further example, recombinant
Altermonas sp. JD6.5 OPAA has been expressed under the control of a
trc promoter in Escherichia coli (Cheng, T.-C. et al., 1999). In an
additional example, a (His)6 tag sequence-thrombin cleavage
site-squid-type DFPase has been expressed using a Ptac promoter in
Escherichia coli (Hartleib, J. and Ruterjans, H., 2001a).
[0247] A ribosome binding site is important for transcription
initiation, and is usually positioned 4 to 14 nucleotides 5' from
the start codon. A start codon signals initiation of transcription.
A multiple cloning site comprises restriction sites for
incorporation of a nucleic acid sequence encoding a peptide or
polypeptide of interest.
[0248] A stop codon signals translation termination. The vectors or
constructs of the present invention will generally comprise at
least one termination signal. A "termination signal" or
"terminator" is comprised of the DNA sequences involved in specific
termination of an RNA transcript by an RNA polymerase. Thus, in
certain embodiments a termination signal that ends the production
of an RNA transcript is contemplated. A terminator may be necessary
in vivo to achieve desirable message levels. A transcription
terminator signals the end or transcription and often enhances mRNA
stability. Examples of a transcription terminator include a rrnB T1
or a rrnB T2 transcription terminator (Unger, T. F., 1997). An
origin of replication regulates the number of expression vector
copies maintained in a transformed host cell.
[0249] A selectable marker usually provides a transformed cell
resistance to an antibiotic. Examples of a selectable marker used
in a prokaryotic expression vector include a .beta.-lactamase,
which provides resistance to antibiotic such as an ampicillin or a
carbenicillin; a tet gene product, which provides resistance to a
tetracycline, or a Km gene product, which provides resistance to a
kanamycin. A repressor regulatory gene suppresses transcription
from the promoter. Examples of repressor regulatory genes include
the lacI, lacI.sup.q, or lacI.sup.Q1 repressors (Glascock, C. B.
and Weickert, M. J., 1998). Often, the host cell's genome, or
additional nucleic acid vector co-transfected into the host cell,
may comprise one or more of these nucleic acid sequences, such as,
for example, a repressor.
[0250] It is contemplated that an expression vector for a
prokaryotic host cell will comprise a nucleic acid sequence that
encodes a periplasmic space signal peptide. In preferred aspects,
this nucleic acid sequence will be operatively linked to a nucleic
acid sequence comprising an enzymatic peptide or polypeptide of the
present invention, wherein the periplasmic space signal peptide
directs the expressed fusion protein to be translocated into a
prokaryotic host cell's periplasmic space. Fusion proteins secreted
in the periplasmic space may be obtained through simplified
purification protocols compared to non-secreted fusion proteins. A
periplasmic space signal peptide are usually operatively linked at
or near the N-terminus of an expressed fusion protein. Examples of
a periplasmic space signal peptide include the Escherichia coli
ompA, ompT, and maleI leader peptide sequences and the T7 caspid
protein leader peptide sequence (Unger, T. F., 1997).
[0251] Mutated and/or recombinantly altered bacterium that release
a peptide or polypeptide comprising an enzyme sequence of the
present invention into the environment may be particularly
advantageous for purification and/or contact of enzyme with a
target chemical substrate. It is contemplated that a strain of
bacteria, such as, for example, a bacteriocin-release protein
mutant strain of Escherichia coli, may be used to promote release
of expressed proteins targeted to the periplasm into the
extracellular environment (Van der Wal, F. J. et al., 1998). In
other aspects, it is contemplated that a bacterium may be
transfected with an expression vector that produces a gene and/or a
gene fragment product that promotes the release of a protenaceous
molecule of interest from the periplasm into the extracellular
environment. For example, a plasmid encoding the third topological
domain of TolA has been described as promoting the release of
endogenous and recombinantly expressed proteins from the periplasm
(Wan, E. W. and Baneyx, F., 1998).
[0252] D. Host Cells
[0253] Many host cells from various cell types and organisms are
available and would be known to one of skill in the art. As used
herein, the terms "cell," "cell line," and "cell culture" may be
used interchangeably. All of these terms also include their
progeny, which is any and all subsequent generations. It is
understood that all progeny may not be identical due to deliberate
or inadvertent mutations. In the context of expressing a
heterologous nucleic acid sequence, "host cell" refers to a
prokaryotic or eukaryotic cell, and it includes any transformable
organism that is capable of replicating a vector and/or expressing
a heterologous gene and/or gene fragment encoded by a vector. A
host cell can, and has been, used as a recipient for vectors. A
host cell may be "transfected" or "transformed," which refers to a
process by which exogenous nucleic acid sequence is transferred or
introduced into the host cell. A transformed cell includes the
primary subject cell and its progeny. Techniques for transforming a
cell are extremely well known in the art, and include, for example
calcium phosphate precipitation, cell sonication,
diethylaminoethanol ("DEAE")-dextran, direct microinjection,
DNA-loaded liposomes, electroporation, gene bombardment using high
velocity microprojectiles, receptor-mediated transfection,
viral-mediated transfection, or a combination thereof [In
"Molecular Cloning" (Sambrook, J., and Russell, D. W., Eds.) 3rd
Edition, Cold Spring Harbor, N.Y.: Cold Spring Harbor Laboratory
Press, 2001; In "Current Protocols in Molecular Biology" (Chanda,
V. B. Ed.) John Wiley & Sons, 2002].
[0254] Once a suitable expression vector is transformed into a
cell, the cell may be grown in an appropriate environment, and in
some cases, used to produce a tissue or whole multicellular
organism. As used herein, the terms "engineered" and "recombinant"
cells or host cells are intended to refer to a cell into which an
exogenous nucleic acid sequence has been introduced. Therefore,
engineered cells are distinguishable from naturally occurring cells
that do not contain a recombinantly introduced exogenous nucleic
acid sequence. Engineered cells are thus cells having a nucleic
acid sequence introduced through the hand of man. Recombinant cells
include those having an introduced cDNA or genomic gene and/or a
gene fragment positioned adjacent to a promoter not naturally
associated with the particular introduced nucleic acid sequence, a
gene, and/or a gene fragment. An enzyme or proteinaceous molecule
produced from the introduced gene and/or gene fragment is referred
to as a recombinant enzyme or recombinant proteinaceous molecule,
respectively. All tissues, offspring, progeny or descendants of
such a cell, tissue, and/or organism that comprise the transformed
nucleic acid sequence thereof are considered part of the present
invention.
[0255] Though it is possible to purify an expressed enzyme from
cellular material, the discovery disclosed herein of the properties
of an enzyme composition comprising, in preferred embodiments, an
enzyme expressed and retained, whether naturally or through
recombinant expression, within a cell. In preferred embodiments, an
enzyme is produced using recombinant nucleic acid expression
systems in the cell. Cells are known herein based on the type of
enzyme expressed within the cell, whether endogenous or
recombinant, so that, for example, a cell expressing an enzyme of
interest would be known as an enzyme cell, a cell expressing a
phosphoric triester hydrolase would be known herein as a
"phosphoric triester hydrolase.sup.+ cell," etc. Additional
examples of such nomenclature include an
aryldialkylphosphatase.sup.+ cell, an OPH.sup.+ cell, an OPAA.sup.+
cell, a human paraoxonase.sup.+ cell, a carboxylase.sup.+ cell, a
prolidase.sup.+ cell, an aminopeptideases.sup.+ cell, a PepQ.sup.+
cell, a mpd product.sup.+ cell, a "B" esterase.sup.+ cell, an
acetycholinesterase.sup.+ cell, a butyrylcholinesterase.sup.+ cell,
diisopropyl-fluorophosphatase.sup.+ cell, Mazur-type DFPase.sup.+
cell, or a squid-type DFPase.sup.+ cell, respectively denoting
cells that comprise, an aryldialkylphosphatase, an OPH, a OPAA, a
human paraoxonase, a carboxylase, a prolidase, an aminopeptidease,
a PepQ, a mpd product, a "B" esterase, an acetycholinesterase, a
butyrylcholinesterase, a diisopropyl-fluorophosphatase, a
Mazur-type DFPase, or a squid-type DFPase, etc.
[0256] In preferred embodiments, an enzyme.sup.+ cell comprises a
bacterial cell, a yeast cell, an insect cell, a plant cell, or a
combination thereof. In preferred aspects, the cell comprises a
cell wall. Contemplated enzyme.sup.+ cells that comprise cell walls
include, but are not limited to, a bacterial cell, a fungal cell, a
plant cell, or a combination thereof. In preferred facets, a
microorganism comprises the enzyme.sup.+ cell. Examples of
contemplated microorganisms include a bacterium, a fungus, or a
combination thereof. Examples of a bacterial host cell that have
been used with expression vectors include an Aspergillus niger, a
Bacillus (e.g., B. amyloliquefaciens, B. brevis, B. licheniformis,
B. subtilis), an Escherichia coli, a Kluyveromyces lactis, a
Moraxella sp., a Pseudomonas (e.g., fluorescens, putida),
Flavobacterium cell, a Plesiomonas cell, an Alteromonas cell, or a
combination thereof. Examples of a yeast cell include a
Streptomyces lividans cell, a Gliocladium virens cell, a
Saccharomyces cell, or a combination thereof.
[0257] Host cells may be derived from prokaryotes or eukaryotes,
depending upon whether the desired result is replication of the
vector or expression of part or all of the vector-encoded nucleic
acid sequences. Numerous cell lines and cultures are available for
use as a host cell, and they can be obtained through the American
Type Culture Collection, which is an organization that serves as an
archive for living cultures and genetic materials. An appropriate
host can be determined by one of skill in the art based on the
vector backbone and the desired result. A plasmid or cosmid, for
example, can be introduced into a prokaryote host cell for
replication of many vectors. Examples of a bacterial cell used as a
host cell for vector replication and/or expression include DH5a,
JM109, and KC8, as well as a number of commercially available
bacterial hosts such as Novablue.TM. Escherichia coli cells
(NOVAGENE.RTM.), SURE.RTM. Competent Cells and SOLOPACK.TM. Gold
Cells (STRATAGENE.RTM.). However, Escherichia coli.cells have been
the most common cell types used to express both wild type and
mutant forms of OPH (Dumas, D. P. et al., 1989a; Dave, K. I. et
al., 1993; Lai, K. et al., 1994; Wu, C.-F. et al., 2001a). In an
example, the OPH I106A/F132A/H257Y and G60A mutants have been
expressed in Escherichia coli BL-21 host cells (Kuo, J. M. and
Raushel, F. M., 1994; Li, W.-S. et al., 2001). In a further
example, maltose-binding domain-E3 carboxylesterase and phosphoric
triester hydrolase functional equivalents have been expressed in
Escherichia coli TB1 cells (Claudianos, C. et al., 1999). In
another example, the OPH mutants designated W131F, F132Y, L136Y,
L140Y, H257L, L271Y, F306A, and F306Y each have been expressed in
Novablue.TM. Escherichia coli cells (Gopal, S. et al., 2000). In an
addition example, OPAA from Alteromonas sp JD6.5 has been
recombinantly expressed in Escherichia coli cells (Hill, C. M.,
2000). In a further example, recombinant Altermonas sp. JD6.5 OPAA
has been expressed in Escherichia coli (Cheng, T.-C. et al., 1999).
In a further example, the mpd gene has been recombinantly expressed
in Escherichia coli, and the encoded enzyme demonstrated methyl
parathion degradation activity (Zhongli, C. et al., 2001). In an
additional example, a recombinant squid-type DFPase fusion protein
has been expressed Escherichia coli BL-21 cells (Hartleib, J. and
Ruterjans, H., 2001a). Alternatively, bacterial cells such as
Escherichia coli LE392 could be used as host cells for phage
viruses. Of course, one of skill in the art may select a bacterium
species to express a proteinaceous molecule due to a particular
desirable property. In an example, Moraxella sp. that degrades
p-nitrophenol, a toxic cleavage product of parathion and methyl
parathion, has been used to recombinantly express an OPH-InaV
fusion protein. The resulting recombinant bacterial degrades both
toxic OP compounds and their cleavage byproduct (Shimazu, M. et
al., 2001b).
[0258] Examples of eukaryotic host cells for replication and/or
expression of a vector include yeast cells HeLa, NIH3T3, Jurkat,
293, Cos, CHO, Saos, and PC12. In an example, OPH has been
expressed in the host yeast cells of Streptomyces lividans
(Steiert, J. G. et al., 1989). In another example, OPH has been
expressed in host insect cells, including Spodoptera frugiperda sf9
cells (Dumas, D. P. et al., 1989b; Dumas, D. P. et al., 1990). In a
further example, OPH has been expressed in the cells of Drosophila
melanogaster (Phillips, J. P. et al., 1990). In an additional
example, OPH has been expressed in the fungus Gliocladium virens
(Dave, K. I. et al., 1994b). In a further example, the gene for
human paraoxonase, PON1, has been recombinantly expressed in human
embryonic kidney cells (Josse, D. et al., 2001; Josse, D. et al.,
1999). In a further example, E3 carboxylesterase and phosphoric
triester hydrolase functional equivalents have been expressed in
host insect Spodoptera frugiperda sf9 cells (Campbell, P. M. et
al., 1998; Newcomb, R. D. et al., 1997). In an additional example,
a phosphoric triester hydrolase functional equivalent of a
butyrylcholinesterase has been expressed in Chinese hamster ovary
("CHO") cells (Lockridge, O. et al., 1997). In certain embodiments,
an eukaryotic cell that may be selected for expression is a plant
cell, such as, for example, a corn cell.
[0259] E. Production of Expressed Proteinaceous Molecules
[0260] It is contemplated that any size flask or fermentor may be
used to grow a tissue or organism that can express a recombinant
proteinaceous molecule of the present invention. In certain
embodiments, bulk production of compositions with enzymatic
sequences is contemplated.
[0261] In an example, a fusion protein comprising, N-terminus to
C-terminus, a (His)6 polyhistidine tag, a green fluorescent protein
("GFP"), an enterokinase recognition site, and a OPH lacking the 29
amino acid leader sequence, has been expressed in Escherichia coli.
The GFP sequence produced fluorescence that was proportional both
the quantity of the fusion protein, and the activity of the OPH
sequence. The fusion protein was more soluble than OPH expressed
without the added sequences, and was expressed within the cells
(Wu, C.-F. et al., 2000b; Wu, C.-F. et al., 2001a).
[0262] It is contemplated that the temperature selected may
influence the rate and/or quality of recombinant enzyme production.
It is contemplated that in some embodiments, expression of an
enzyme may be conducted at 4.degree. C. to 50.degree. C., including
all intermediate ranges and combinations thereof. Such combinations
may include a shift from one temperature (e.g., 37.degree. C.) to
another temperature (e.g., 30.degree. C.) during the induction of
the expression of proteinaceous molecule. For example, both
eukaryotic and prokaryotic expression of OPH may be conducted at
temperatures 30.degree. C., which has increased the production of
enzymatically active OPH by reducing protein misfolding and
inclusion body formation in some instances (Chen-Goodspeed, M. et
al., 2001b; Wang, J. et al., 2001; Omburo, G. A. et al., 1992;
Rowland, S. S. et al., 1991). In an additional example, prokaryotic
expression of recombinant squid-type DFPase fusion protein at
30.degree. C. also enhanced yields of active enzyme (Hartleib, J.
and Ruterjans, H., 2001a). It is contemplated that fed batch growth
conditions at 30.degree. C., in a minimal media, using glycerol as
a carbon source, will be suitable for expression of various
enzymes.
[0263] F. Processing of Expressed Proteinaceous Molecules
[0264] After production of a biomolecule by a living cell, the
composition comprising the biomolecule may undergo one or more
processing steps to prepare a biomolecule composition of the
present invention. Examples of such steps include permeabilizing,
disrupting, sterilizing, concentrating, drying, resuspending, or a
combination thereof. Various embodiments of a biomolecule
composition of the present invention are contemplated after one or
more such processing steps. However, it is further contemplated
that each processing step will increase economic costs and/or
reduce total biomolecule yield, so that embodiments comprising
fewer steps are preferred. It is further contemplated that the
order of steps may be varied and still produce a biomolecule
composition of the present invention.
[0265] In certain embodiments, a biomolecule composition of the
present invention may comprise various cellular components (e.g.,
cell wall material, cell membrane material, nucleic acids, sugars,
polysacharrides, peptides, polypeptides, proteins, lipids, etc).
Such a biomolecule composition of the present invention is known
herein as a "crude cell preparation". A--"a crude cell preparation
comprises the biomolecule within or otherwise in contact with a
cell and/or cellular debris. In certain aspects, it is contemplated
that the total content of desired biomolecule (e.g., an active
biomolecule) may range from 0.0001% to 99.9999% of a crude cell
preparation, including all intermediate ranges and combinations
thereof, by volume or dry weght, depending upon factors such as
expression efficiency of the biomolecule in the cell and the amount
of processing and/or purification steps. A higher content of
desired biomolecule in the biomolecular composition is preferred.
But, in certain embodiments, it is also preferred that the
biomolecule composition comprise cellular components, particularly
cell wall and/or cell membrane material, to provide material that
may be protective to the biomolecule, enhances the particulate
nature of the biomolecule composition, or a combination thereof.
Thus, the biomolecule composition may comprise 0.0001% to 99.9999%
of cellular components, including all intermediate ranges and
combinations thereof, by volume or dry weight. However, in certain
embodiments, lower ranges of cellular components is preferred, as
the biomolecular composition would therefore comprise a greater
percentage of a desired biomolecule.
[0266] In embodiments wherein the cellular material is derived from
a microorganism, such as through expression of the biomolecule by a
microorganism, the biomolecular composition is known herein as a
"microorganism based particulate material". The association of a
biomolecule with a cell or cellular material is generally produced
through endogenous expression, expression due to recombinant
engineering, or a combination thereof. In preferred embodiments, a
crude cell preparation comprises a biomolecule partly or whole
encapsulated by a cell membrane and/or cell wall, whether naturally
so and/or through recombinant engineering. Such a biomolecule
(e.g., the active biomolecule) encapsulated within or as a part of
a cell wall and/or cell membrane is referred to herein as a "whole
cell material" or "whole cell particulate material".
[0267] It is contemplated that a biomolecule prepared as a crude
cell preparation may have greater stability than a preparation
wherein the biomolecule has been substantially separated from a
cell membrane and/or cell wall. It is further contemplated that a
biomolecule prepared as a crude cell preparation, wherein the
biomolecule is localized between the cell wall and cell membrane
and/or within the cell so that the cell wall separates the
biomolecule from the extracellular environment, may have greater
stability than a preparation wherein the biomolecule has been
substantially separated from a cell membrane and/or cell wall.
[0268] Additionally, it is contemplated that a biomolecule
composition of the present invention may be encapsulated using a
microencapsulation technique as would be known to one of ordinary
skill in the art. Such encapsulation may enhance or confer the
particulate nature of the biomolecule composition, provide
protection to the biomolecule, increase the average particle size
to a desired range, allow release of the biomolecule from the
encapsulating material, alter surface charge, hydrophobicity,
hydrophilicity, solubility and/or disperability of the particulate
material, or a combination thereof. Examples of microencapulation
(e.g., microsphere) compositions and techniques are described in
Wang, H. T. et al., J. of Controlled Resease 17:23-25, 1991; and
U.S. Pat. Nos. 4,324,683, 4,839,046, 4,988,623, 5,026,650,
5,153,131, 6,485,983, 5,627,021 and 6,020,312).
[0269] 1. Cell Permeabilization/Disruption
[0270] In preferred aspects, a biomolecular composition of the
present invention comprises a crude cell preparation wherein the
cell membrane and/or cell wall has been altered through a
permeablizating process, a disruption process, or a combination
thereof. An example of such an altered crude cellular preparation
includes disrupted cells, permeabilized cells, or a combination
thereof. As used herein, a "disrupted cell" is a crude cell
preparation wherein wherein the cell membrane and/or cell wall has
been altered through a disruption process. As used herein, a
"permeabilized cell" is a crude cell preparation wherein the cell
membrane and/or cell wall has been altered through a
permeabilizating process. It is contemplated that a biomolecule
composition of the present invention prepared as a crude cellular
preparation may have greater stability than a preparation wherein
the biomolecule has been substantially purified from the cell wall
and/or membrane.
[0271] A processing step may comprise a permeabilizing step,
wherein a cell is contacted with a permeabilizing agent such as
dimethyl sulfoxide ("DMSO"), ethylenediaminetetraacetic acid
("EDTA"), tributyl phosphate, or a combination thereof. A
permeabilizing step may increase the mass transport of a substrate
into the interior of a cell, where an enzyme localized inside the
cell can catalyze a chemical reaction with the substrate.
(Martinez, M. B. et al., 1996; Martinez, M. B. et al., 2001; Hung,
S.-C. and Liao, J. C., 1996). Cell permeabilizing using EDTA
(Leduc, M. et al., 1985).
[0272] OP compound degradation rate has been limited by OPH
intracellularly expressed in whole cells (Elashvili, I. and
DeFrank, J. J., 1996; Elashvili, I. et al., 1998; Hung, S.-C. and
Liao, J. C., 1996; Richins, R. et al., 1997). However, it is
contemplated that a composition of the present invention comprising
a whole cell particulate material will provide protection from
diffusion of compounds that may damage a biomolecule, while
allowing sufficient permeability to allow biomolecule function.
[0273] In some embodiments, a processing step comprises disrupting
a cell. A cell may be disrupted by any method known in the art,
including, for example, a chemical method, a mechanical method, a
biological method, or a combination thereof. Examples of a chemical
cell disruption method include suspension in a solvent for certain
cellular components. In specific facets, such a solvent may
comprise an organic solvent (e.g., acetone), a volatile solvent, or
a combination thereof. In a particular facet, a cell be be
disrupted by acetone (Wild, J. R. et al., 1986; Albizo, J. M. and
White, W. E., 1986). In certain preferred facets, the cells are
disrupted in a volatile solvent for ease in evaporation. Examples
of a mechanical cell disruption method include pressure (e.g.,
processing through a French press), sonication, mechanical
shearing, or a combination thereof. An example of a pressure cell
disruption method includes processing through a French press.
Examples of a biological cell disruption method include contacting
the cell with one or more enzymes (e.g., lysozyme) that weaken,
damage, and/or permeabilize a cell membrane, cell wall or
combination thereof. Biological material comprising a proteinaceous
molecule of the present invention may be homogenized, sheared,
undergo one or more freeze thaw cycles, be subjected to enzymatic
and/chemical digestion of cellular materials (e.g., cell walls,
sugars, etc), undergo extraction with organic or aqueous solvents,
etc, to weaken interactions between the proteinaceous molecule and
other cellular materials and/or partly purify the proteinaceous
molecule. A processing step may comprise sonicating a composition
comprising an enzyme. Other dissepting and drying will be done by
freezedrying with or without a cryoprotector (typically a
sugar).
[0274] 2. Sterilization
[0275] A processing step may comprise sterilizing an enzyme
composition of the present invention. Sterilizing kills living
matter, and may be desirable as continued post expression growth of
a host cell and/or a contaminating organism may detrimentally
affect the composition. For example, one or more properties of a
coating may be undesirably altered by the presence of a living
organism. Additionally, sterilizing reduces the ability of a living
recombinant organism to be introduced into the environment, when
such an event is not desired. Sterilizing may be accomplished by
any method known in the art. Examples of sterilizing may include
contacting the living matter with a toxin, irradiating the living
matter, heating the living matter above 100.degree. C., or a
combination thereof. It is preferred that sterilizing comprises
irradiating the living matter, as radiation generally does not
leave a toxic residue, and is not contemplated to detrimentally
affect the enzymes stability such as that which might occur during
heating. Examples of radition include infrared ("IR") radiation,
ionizing radiation, microwave radiation, ultra-violet ("UV")
radiation, particle radiation, or a combination thereof. Particle
radiation, UV radiation and/or ionizing radiation are preferred,
and particle radiation is particularly preferred. Examples of
particle radiation include alpha radiation, electron beam/beta
radiation, neutron radiation, proton radiation, or a combination
thereof.
[0276] 3. Concentrating a Biomolecule Composition
[0277] A processing step may comprise concentrating a biomolecule
composition of the present invention. As used herein,
"concentrating" refers to any process wherein the volume of a
composition is reduced. Often, undesired components that comprise
the excess volume are removed, the desired composition is localized
to a reduced volume, or a combination thereof.
[0278] For example, it is contemplated that a concentrating step
may be used to reduce the amount of a growth and/or expression
medium component from a composition of the present invention. It is
contemplated that nutrients, salts and other chemicals that
comprise a biological growth and/or expression medium may be
unnecessary and/or unsuitable in a composition of the present
invention, and reducing the amount of such compounds is preferred.
A growth medium may promote undesirable microorganism growth in a
composition of the present invention, while salts or other
chemicals may undesirably alter the formulation of a coating.
[0279] Concentrating a biomolecule composition may be by any method
known in the art, including, for example, filtrating, a
gravitational force, a gravimetric force, or a combination therof.
An example of a gravitational force is normal gravity. An example
of a gravimetric force is the force exerted during centrifugation.
Often a gravitational or gravimetric force is used to concentrate a
composition comprising the desired biomolecule from undesired
components that are retained in the volume of a liquid medium.
After cells are localized to the bottom of a centrufugation devise,
the media may be removed via such techniques as decanting,
aspiration, etc.
[0280] 4. Drying a Biomolecule Composition
[0281] In additional embodiments, the disrupted cells and/or cell
debris are dried, ground and/or milled to a powder. In specific
facets, the cells added to the paint comprise disrupted cells, cell
debris, and/or powder. The powder may be Preferrably stored at room
temperature without need for dessication.
[0282] 5. Resuspending Biomolecule Composition
[0283] A purification step may comprise resuspending a precipitated
composition comprising an enzyme from cell debris.
[0284] The invention provides, in certain preferred embodiments, a
composition comprising a coating and an enzyme prepared by the
following steps: obtaining a culture of cells that express the
enzyme; concentrating the cells and removing the culture media;
disrupting the cell structure; drying the cells; and adding the
cells to the coating. In some aspects, the composition is prepared
by the additional step of suspending the disrupted cells in a
solvent prior to adding the cells to the coating.
[0285] In certain aspects, the composition is prepared by adding
the cell culture powder to glycerol, admixing with glycerol and/or
suspending in glycerol. In other facets, the glycerol is at a
concentration of about 50%. In specific facets, the cell culture
powder comprised in glycerol at a concentration of about 3 mg of
the milled powder to 3 ml of 50% glycerol. In certain facets, the
composition is prepared by adding the powder comprised in glycerol
to the paint at a concentration of about 3 ml glycerol comprising
powder to 100 ml of paint. The powder may also be added to a liquid
component such as glycerol prior to addition to the paint. The
numbers are exemplary only and do not limit the use of the
invention. The concentration was chosen merely to be compatible
with the amount of substance that can be added to one example of
paint without affecting the integrity of the paint itself. Any
compatible amount may used within the scope of the present
invention.
[0286] 6. Temperatures
[0287] It is contemplated that in some embodiments, processing of
an enzyme composition may be conducted at 4.degree. C. to
50.degree. C., including all intermediate ranges and combinations
thereof. In preferred embodiments, a processing step may comprise
maintaining a composition comprising an enzyme at a temperature
less than the optimum temperature for the activity of a living
organism and/or enzyme that may detrimentially affect an enzyme of
the present invention. Often 37.degree. C. is the maximum
temperature for the processing of a eukarotic biomolecule (e.g., an
enzyme). Thus temperatures less than 37.degree. C. are preferred,
temperatures less than 30.degree. C. are more preferred,
temperatures less than 20.degree. C. even more preferred,
temperatures less than 10.degree. C. are particularly preferred,
and temperatures of 4.degree. C. more preferred.
[0288] 7. Other Processing Steps
[0289] In other embodiments, a proteinaceous molecule of the
present invention may be a purified a proteinaceous molecule. A
"purified proteinaceous molecule" as used herein refers to any
proteinaceous molecule of the present invention removed in any
degree from other extraneous materials (e.g., cellular material,
nutrient or culture medium used in growth and/or expression, etc).
In certain aspects, removal of other extraneous material may
produce a purified proteinaceous molecule of the present invention
wherein its concentration has been enhanced 2- to 10,000-fold or
more, including all intermediate ranges and combinations thereof,
from its original concentration in a material (e.g., a recombinant
cell, a nutrient or culture medium, etc). In other embodiments, a
purified proteinaceous molecule of the present invention may
comprise 0.001% to 100%, including all intermediate ranges and
combinations thereof of a composition comprising a proteinaceous
molecule of the present invention. The degree or fold of
purification may be determined using any method known to those of
skill in the art or described herein. For example, it is
contemplated that techniques such as measuring specific activity of
a fraction by an assay described herein, relative to the specific
activity of the source material, or fraction at an earlier step in
purification, may be used.
[0290] Techniques for preparation of a proteinaceous molecule of
the present invention are described herein. However, it is
contemplated that one or more additional methods for purification
of biologically produced molecule(s) that are known in the art or
described herein may be applied to obtain a purified proteinaceous
molecule of the present invention [Azzoni, A. R. et al., 2002; In
"Current Protocols in Molecular Biology" (Chanda, V. B. Ed.) John
Wiley & Sons, 2002; In "Current Protocols in Nucleic Acid
Chemistry" (Harkins, E. W. Ed.) John Wiley & Sons, 2002; In
"Current Protocols in Protein Science" (Taylor, G. Ed.) John Wiley
& Sons, 2002; In "Current Protocols in Cell Biology" (Morgan,
K. Ed.) John Wiley & Sons, 2002; In "Current Protocols in
Pharmacology" (Taylor, G. Ed.) John Wiley & Sons, 2002; In
"Current Protocols in Cytometry" (Robinson, J. P. Ed.) John Wiley
& Sons, 2002; In "Current Protocols in Immunology" (Coico, R.
Ed.) John Wiley & Sons, 2002]. A biological material comprising
a proteinaceous molecule of the present invention may be
homogenized, sheared, undergo one or more freeze thaw cycles, be
subjected to enzymatic and/chemical digestion of cellular materials
(e.g., cell walls, sugars, etc), undergo extraction with organic or
aqueous solvents, etc, to weaken interactions between the
proteinaceous molecule and other cellular materials and/or partly
purify the proteinaceous molecule. A processing step may comprise
sonicating a composition comprising an enzyme.
[0291] Cellular materials may be further fractionated to separate a
proteinaceous molecule of the present invention from other cellular
components using chromatographic e.g., affinity chromatography
(e.g., antibody affinity chromatography, lectin affinity
chromatography), fast protein liquid chromatography, high
performance liquid chromatography "HPLC"), ion-exchange
chromatography, exclusion chromatography; or electrophoretic (e.g.,
polyacrylamide gel electrophoresis, isoelectric focusing) methods.
It is contemplated that a proteinaceous molecule of the present
invention may be precipitated using antibodies, salts, heat
denaturation, centrifugation and the like. A purification step may
comprise dialyzing a composition comprising an enzyme from cell
debris.
[0292] For example, the molecular weight of a proteinaceous
molecule can be calculated when the sequence is known, or estimated
when the approximate sequence and/or length is known. SDS-PAGE and
staining (e.g., Coomassie Blue) has been commonly used to determine
the success of recombinant expression and/or purification of OPH,
as described (Kolakowski, J. E. et al., 1997; Lai, K. et al.,
1994).
[0293] In certain embodiments, an enzyme may be in the form of a
crystal. In other aspects, one or more enzyme crystals may be
cross-linked for from an crosslinked enzyme crystal ("CLEC")
(Hoskin, F. C. G. et al., 1999).
[0294] G. Coatings
[0295] In preferred embodiments, a coating comprises a biomolecule
composition of the present invention. A coating ("coat," "surface
coat," "surface coating") is "a liquid, liquefiable or mastic
composition that is converted to a solid protective, decorative, or
functional adherent film after application as a thin layer" ("Paint
and Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook" (Koleske, J. V. Ed.), p. 696, 1995; and in "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D16-00, 2002). Additionally, a
thin layer is 5 um to 1500 um thick, including all intermediate
ranges and combinations thereof. However, in most embodiments, it
is contemplated that a coating will form a thin layer 15 um to 150
um thick, including all intermediate ranges and combinations
thereof. Examples of a coating of the present invention include a
clear coating or a paint.
[0296] A surface is the outer layer of any solid object. As would
be known to those of ordinary skill in the art, the term
"substrate," in the context of a coating, is synonymous with the
term "surface." However, as "substrate" has a different meaning to
those of skill in arts of enzymology and coatings, the term
"surface" will be preferentially used herein for clarity. A surface
wherein a coating has been applied, whether or not film formation
has occurred, is known herein as a "coated surface."
[0297] As is known to those of ordinary skill in the art, a coating
generally comprises one or more materials that contribute to the
properties of the coating, the ability of a coating to be applied
to a surface, the ability of the coating to undergo film formation,
and/or the properties of the produced film. Examples of such
coating components include a binder, a liquid component, a
colorizing agent, an additive, or a combination thereof, and such
materials are contemplated for used in a coating of the present
invention. A coating typically comprises a material often referred
to as a "binder," which is the primary material in a coating
capable of film formation. Often the binder is the coating
component that dominates conferring a physical and/or chemical
property to a coating and/or film. Examples of properties of a
binder typically affects include chemical reactivity, minimum film
formation temperature, minimum T.sub.g, volume fraction solids, a
rheological property (e.g., viscosity), film moisture resistance,
film UV resistance, film heat resistance, film weathering
resistance, adherence, film hardness, film flexibility, or a
combination thereof. Consequently, different categories of coatings
may be identified herein by the binder used in the coating. For
example, a binder may be an oil, a chlorinated rubber, or an
acrylic, and examples of a coating comprising such binders include
an oil coating, a chlorinated rubber-topcoat, an acrylic-lacquer,
etc.
[0298] In most embodiments, a coating will comprise a liquid
component (e.g., a solvent, a diluent, a thinner), which often
confers and/or alters the coating's rheological properties (e.g.,
viscosity) to ease the application of the coating to a surface. In
some embodiments, a coating will comprise a colorizing agent (e.g.,
a pigment), which usually functions to alter an optical property of
a coating and/or film. In certain preferred embodiments, a
microorganism based particulate material of the present invention
is a colorizing agent. In particularly preferred embodiments, a
colorizing agent comprising a microorganism based particulate
material of the present invention is an extender, a pigment, or a
combination thereof. In other preferred embodiments, a coating
comprises a colorizing agent that comprises a microorganism based
particulate material of the present invention. A coating will often
comprise an additive which is a composition incorporated into a
coating to reduce and/or prevent the development of a physical,
chemical, and/or aesthetic defect in the coating and/or film;
confer some addition desired property to a coating and/or film; or
a combination thereof. Examples of an additive include an
accelerator, an adhesion promoter, an antioxidant, an antiskinning
agent, a coalescing agent, a defoamer, a dispersant, a drier, an
emulsifier, a fire retardant, a flow control agent, a gloss aid, a
leveling agent, a marproofing agent, a slip agent, a thickener, a
UV stabilizer, a viscosity control agent, a wetting agent, or a
combination thereof. In certain preferred embodiments, a
microorganism based particulate material of the present invention
is an additive. In particularly preferred embodiments, an additive
comprising a microorganism based particulate material of the
present invention comprises a viscosity control agent, a
dispersant, or a combination thereof. In other preferred
embodiments, a coating comprises an additive that comprises a
microorganism based particulate material of the present invention.
A contaminant is a material that is unintentionally added to a
coating, and may be volatile and/or non-volatile component of a
coating and/or film. As would be known to those of ordinary skill
in the art, a coating component may be categorized as possessing
more than one defining characteristic, and thereby simultaneously
functioning in a coating composition as a combination of a binder,
a liquid component, a colorizing agent, and/or additive. Different
coating compositions are described herein as examples of coatings
with varying sets of properties.
[0299] In certain embodiments, a coating may be stored in a
container ("pot") prior to application. In certain aspects, the
coating is a multi-pack coating which is a coating wherein
different components are stored in a plurality of containers.
Typically, this is done to reduce film formation during storage for
certain types of coatings. The components are admixed prior to
and/or during application. However, in certain embodiments, it is
specifically contemplated that a coating comprising a microorganism
based particulate material of the present invention is a multi-pack
coating. In specific aspects, the coating is a two-pack coating,
three-pack coating, four-pack coating, five-pack coating, or more
wherein the coating components are stored in separate containers.
In certain aspects, 0.001% to 100%, including all intermediate
ranges and combinations thereof, of the microorganism based
particulate material is stored in a separate container from a
coating component. It is contemplated that separate storage may
reduce undesirable microorganism growth in the coating component,
damage to the microorganism-based particulate material of the
present invention by the coating component, increase the storage
life ("pot life") of a coating, reduce the amount of a preservative
in a coating, or a combination thereof. In certain facets, it is
contemplated that the coating components of a container holding the
microorganism based particulate material of the present invention
may further include a coating component such as a preservative, a
wetting agent, a dispersing agent, a liquid component, a
rheological modifier, or a combination thereof. It is contemplated
that a preservative may reduce undesirable growth of a
microorganism, whether the microorganism is derived from the
microorganism based particulate material of the present invention
or a contaminating microorganism. It is contemplated that a wetting
agent, a dispersing agent, a liquid component, a rheological
modifier, or a combination thereof, may promote ease of admixing of
coating components in a multi-pack coating. In certain aspects, a
three-pack coating or four-pack coating may be used, wherein the
first container and the second container contain coating components
separated to reduced film formation during storage, and a third
container comprises 0.001% to 100%, including all intermediate
ranges and combinations thereof, of the microorganism based
particulate material. In certain facets, a multi-pack coating may
be used to separate two or more preparations of the microorganism
based particulate material of the present invention such as to
reduce damage by different species of microorganisms to each other
during storage.
[0300] A coating may be applied to a surface using any technique
known in the art. A in the context of a coating, "application,"
"apply," or "applying" is the process of transferring of a coating
to a surface to produce a layer of coating upon the surface. As
known herein, an "applicator" is a devise that is used to apply the
coating to a surface. Examples of an applicator include a brush, a
roller, a pad, a rag, a spray applicator, etc. Application
techniques that are contemplated as suitable for a user of the
present invention of little or no particular skill include, for
example, dipping, pouring, siphoning, brushing, rolling, padding,
ragging, spraying, etc. Certain types of coatings may be applied
using techniques contemplated as more suitable for a skilled
artisan such as anodizing, electroplating, and/or laminating of a
polymer film onto a surface.
[0301] In certain embodiments, the layer of coating undergoes film
formation ("curing," "cure"), which is the physical and/or chemical
change of a coating to a solid that is a preferred solid when in
the form of a layer upon the surface. In certain aspects, a coating
may be prepared, applied and cured at an ambient condition, a
baking condition, or a combination thereof. An ambient condition is
a temperature range between -10.degree. C. to 40.degree. C.,
including all intermediate ranges and combinations thereof. As used
herein, a "baking condition" or "baking" is contacting a coating
with a temperature above 40.degree. C. and/or raising the
temperature of a coating above 40.degree. C., typically to promote
film formation. Examples of baking the coating include contacting a
coating and/or raising the temperature of coating to 40.degree. C.
to 300.degree. C., or more, including all intermediate ranges and
combinations thereof. Various coatings described herein or as would
be known to one of ordinary skill in the art may be applied and/or
cured at ambient conditions, baking conditions, or a combination
thereof.
[0302] It is contemplated that in general embodiments, a coating
comprising a microorganism based particulate material of the
present invention may be prepared, applied and cured at any
temperature range described herein or would be known to one of
ordinary skill in the art in light of the present disclosures. An
example of such a temperature range is -100.degree. C. to
300.degree. C., or more, including all intermediate ranges and
combinations thereof. However, a microorganism based particulate
material may further comprise a desired biomolecule (e.g., a
colorant, an enzyme), whether endogenously or recombinantly
produced, that may have a reduced tolerance to temperature. It is
contemplated that the preferred temperature that can be tolerated
by a biomolecule will vary depending on the specific biomolecule
used in a coating, and will generally be within the range of
temperatures tolerated by the living organism from which the
biomolecule was derived. For example, it is preferred for a coating
comprising a microorganism based particulate material of the
present invention, wherein the microorganism based material
comprises an desired enzyme, that the coating is prepared, applied
and cured at -100.degree. C. to 110.degree. C., including all
intermediate ranges and combinations thereof. For example, it is
contemplated that a temperature of -100.degree. C. to 40.degree. C.
including all intermediate ranges and combinations thereof, will be
suitable for many enzymes (e.g., a wild-type sequence and/or a
functional equivalent) derived from an eukaryote, while
temperatures up to, for example -100.degree. C. to 50.degree. C.
including all intermediate ranges and combinations thereof, may be
tolerated by enzymes derived from many prokaryotes.
[0303] The type of film formation that a coating may undergo
depends upon the coating components. A coating may comprise, for
example, volatile coating components, non-volatile coating
components, or a combination thereof. In certain aspects, the
physical process of film formation comprises loss of 1% to 100%,
including all intermediate ranges and combinations thereof, of a
volatile coating component. In general embodiments, a volatile
component is lost by evaporation. In certain aspects, loss of a
volatile coating component during film formation reaction is
promoted by baking the coating. Examples of volatile coating
components include a coalescing agent, a solvent, a thinner, a
diluent, or a combination thereof. A non-volatile component of the
coating remains upon the surface. In specific aspects, the
non-volatile component forms a film. Examples of non-volatile
coating components include a binder, a colorizing agent, a
plasticizer, a coating additive, or a combination thereof. In
specific aspects, a coating component may undergo a chemical change
to form a film. In general embodiments, a binder undergoes a
cross-linking (e.g., polymerization) reaction to produce a film. In
general embodiments, a chemical film formation reaction occurs
spontaneously under ambient conditions. In other aspects, a
chemical film formation reaction is promoted by irradiating the
coating, heating the coat, or a combination thereof. In some
embodiments, irradiating the coating comprises exposing the coating
to electromagnetic radiation, particle radiation, or a combination
thereof. Examples of electromagnetic radiation used to irradiate a
coating include UV radiation, infrared radiation, or a combination
thereof. Examples of particle radiation used to irradiate a coating
include electron-beam radiation. Often irradiating the coating
induces an oxidative and/or free radical chemical reaction that
cross-links of one or more coating components.
[0304] However, in some alternate embodiments, it is contemplated
that a coating undergoes a reduced amount of film formation than
such a solid film is not produced, or does not undergo film
formation to a measurable extent during the period of time it is
used on a surface. Such a coating is referred to herein as a
"non-film forming coating." Such a non-film forming coating may be
prepared, for example, by increasing the non-volatile component in
a thermoplastic coating (e.g., increasing plasticizer content in a
liquid component), reducing the amount of a coating component that
contributes to the film formation chemical reaction (e.g., a
binder, a catalyst), reducing the contact with an external a curing
agent (e.g., radiation, baking), selection of a non-film formation
binder produced from components that lack crosslinking moieties,
selection of a non-film formation binder that lack sufficient size
to undergo thermoplastic film formation, or a combination thereof.
As used herein, a "non-film formation binder" refers to a molecule
that is chemically similar to a binder, but lacks sufficient size
and/or crosslinking moiety to undergo film formation. For example,
a coating may be prepared by selection of an oil-based binder that
lacks sufficient double bonds to undergo sufficient crosslinking
reactions to produce a film. In another example, a non-film
formation binder may be selected that lacks sufficient crosslinking
moieties such as an epoxide, an isocyanate, a hydroxyl, a carboxyl,
an amine, an amide, a silicon moiety, etc., to produce a film by
thermosetting. Such a non-film formation binder may be prepared by
chemical modification of a binder, such as, for example, a
crosslinking reaction with a small molecule (e.g., less than 1 kDa)
that comprises a moiety capable of reaction with a binder's
crosslinking moiety, to produce a chemically blocked binder moiety
that is inert to a further crosslinking reaction. In another
example, a thermoplastic binder typically comprises a molecule 29
kDa to 1000 kDa or more in size. Film formation may be reduced or
prevented by selection of a like molecule that is too small to
effectively undergo thermoplastic film formation. An example would
be selection of a non-film formation binder molecule between 1 kDa
to 29 kDa in molecular weight, including all intermediate ranges
and combinations thereof.
[0305] In other alternative embodiments, a coating may undergo film
formation, but produce a film whose properties makes it more suited
for a temporary use. Such a temporary film will generally possess a
poor and/or low rating for a property that would confer longevity
in use. For example, a film with a poor scrub resistance, a poor
solvent resistance, a poor water resistance, a poor weathering
property (e.g., UV resistance), a poor adhesion property, or a
combination thereof, may be selected as a temporary film. In one
aspect, a film may have poor adhesion for a surface, allowing ease
of removal by stripping and/or peeling. In another example, a film
may have a poor resistance to an environmental factor, and
subsequently fail (e.g., crack, peel, chalk, etc.) to remain a
viable film upon the surface. For example, a film that undergoes
chalking is specifically contemplated. Chalking is the erosion a
coating, typically by degradation of the binder due to various
environmental forces (e.g., UV irradiation). It is contemplated
that in some embodiments, chalking may be desirable, to expose
remove a contaminant from the surface of a film and/or expose a
component of the film (e.g., a biomolecular composition of the
present invention) to the surface of the coating. A self-cleaning
coating is a film with a desirable chalking property. It is further
contemplated that in many aspects the layer of non-film forming
coating, a temporary film and/or a self-cleaning film may be
removed from a surface with ease. In such embodiments, a non-film
forming coating, a temporary film, a self-cleaning film, or a
combination thereof would be more suitable for a temporary use upon
a surface, due to the ability to be applied as a layer and easily
removed when its presence is no longer desired. In these
embodiments, it is contemplated that the non-film forming coating,
the temporary film, the self-cleaning film, or a combination
thereof, is desired for a use upon a surface that lasts a temporary
period of time, such as, for example, 1 to 60 seconds, 1 to 24
hours, 1 to 7 days, 1 to 10 weeks, 1 to 6 months, including all
intermediate ranges and combinations thereof, respectively.
[0306] In some embodiments, a plurality of coating layers, known
herein as a "multicoat system" ("multicoating system"), may be
applied upon a surface. The coating selected for use in a specific
layer may differ from an additional layer of the multicoat system.
This selection of coatings with differing components and/or
properties is typically done to sequentially confer, in a desired
pattern, the properties of differing coatings to a coated surface
and/or multicoat system. Examples of a coating that may be selected
for use, either alone or in a multicoat system, include a sealer, a
water repellent, a primer, an undercoat, a topcoat, or a
combination thereof. A sealer is coating applied to a surface to
reduce or prevent absorption by the surface of a subsequent coating
layer and/or a coating component thereof, and/or to prevent damage
to the subsequent coating layer by the surface. A water repellant
is a coating applied to a surface to repel water. A primer is a
coating that is applied to increase adhesion between the surface
and a subsequent layer. In typical embodiments a primer-coating, a
sealer-coating, a water repellent-coating, or a combination thereof
is applied to porous surface. Examples of a porous surface include
drywall, wood, plaster, masonry, damaged and/or degraded film,
corroded metal, or a combination thereof. In certain aspects, the
porous surface is not coated or lacks a film prior to application
of a primer, sealer, water repellent, or combination thereof. An
undercoat is a coating applied to surface to provide a smooth
surface for a subsequent coat. A topcoat ("finish") is a coating
applied to a surface for a protective and/or decorative purpose. Of
course, a sealer, water repellent, primer, undercoat, and/or
topcoat may possess additional protective, decorative, and/or
functional properties. Additionally, the surface a sealer, water
repellent, primer, undercoat, and/or topcoat are applied to may be
a coated surface such as a coating and/or film of a layer of the a
multicoat system. In certain embodiments, a multicoat system may
comprise any combination of a sealer, water repellent, primer,
undercoat, and/or topcoat. For example, a multicoat system may
comprise any of the following combinations: a sealer, a primer and
a topcoat; a primer and topcoat; a water repellent, a primer,
undercoat, and topcoat; an undercoat and topcoat; a sealer, an
undercoat, and a topcoat; a sealer and topcoat; a water repellent
and topcoat, etc. In particular aspects, a coating layer may
comprise properties that would be a combination of those associated
with different coating types such as a sealer, water repellent,
primer, undercoat, and/or topcoat. In such instances, such a
combination coating and/or film is designated by a backslash "/"
separating the individual coating designations encompassed by the
layer. Examples of such a coating layer comprising a plurality of
functions include a sealer/primer coating, a
sealer/primer/undercoat coating, a sealer/undercoat coating, a
primer/undercoat coating, a water repellant/primer coating, an
undercoat/topcoat coating, a primer/topcoat coating, a
primer/undercoat/topcoat coating, etc. In embodiments wherein the
coated surface comprises a particular type of coating, then the
coated surface may be known herein by the type of coating such as a
"painted surface," a "clear coated surface," a "lacquered surface,"
a "varnished surface," a "water repellant/primered surface," an
"primer/undercoat-topcoated surface," etc.
[0307] In specific aspects, a multicoat system may comprise a
plurality of layers of the same type, such as, for example, 1 to 10
layers, including all intermediate ranges and combinations thereof,
of a sealer, water repellent, primer, undercoat, topcoat, or any
combination thereof. In specific facets, a multicoat system
comprises a plurality of layers of the same coating type, such as,
for example, 1 to 10 layers, including all intermediate ranges and
combinations thereof, of a sealer, water repellent, primer,
undercoat, or topcoat. In embodiment where a coating does not
comprise a multicoat system, but a single layer of coating applied
to a surface, such a layer, regardless of typical function in a
multicoat system, is regarded herein as a topcoat.
[0308] 1. Paints
[0309] A paint is a "pigmented liquid, liquefiable or mastic
composition designed for application to a substrate in a thin layer
which is converted to an opaque solid film after application. Used
for protection, decoration or identification, or to serve some
functional purpose such as the filling or concealing of surface
irregularities, the modification of light and heat radiation
characteristics, etc." ["Paint and Coating Testing Manual,
Fourteenth Edition of the Gardner-Sward Handbook" (Koleske, J. V.
Ed.), p. 696, 1995]. However, as certain coatings disclosed herein
are non-film forming coatings, this definition is modified herein
to encompass a coating with the same properties of a film forming
paint, with the exception that it does not produce a solid film. In
particular embodiments, a non-film forming paint possesses a hiding
power sufficient to concealing surface feature comparable to an
opaque film.
[0310] Hiding power is the ability of a coating and/or film to
prevent light from being reflected from a surface, particularly to
convey the suface's visual pattern. Opacity is the hiding power of
a film. An example of hiding power would be the ability of a
paint-coating to visually block the appearance of grain and color
of a wooden surface, as opposed to a clear varnish-coating allowing
the relatively unobstructed apperance of wood to pass through the
coating. Standard techniques for determining the hiding power of a
coating and/or film (e.g., paint, a powder coating) are described,
for example, in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
E284-02b, D344-97, D2805-96a, D2745-00 and D6762-02a 2002; "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D5007-99, D5150-92 and
D6441-99, 2002; and "Paint and Coating Testing Manual, Fourteenth
Edition of the Gardner-Sward Handbook" (Koleske, J. V. Ed.), pp.
481-506, 1995.
[0311] 2. Clear-Coatings
[0312] A clear-coating is a coating that is not opaque and/or does
not produce an opaque solid film after application. A clear-coating
and/or film may be transparent or semi-transparent (e.g.,
translucent). A clear-coating may be colored or non-colored. In
certain embodiments, reducing the content of a pigment in a paint
composition may produce a clear-coating. Additionally, a
clear-coating may comprise a lacquer, a varnish, a shellac, a
stain, a water repellent coating, or a combination thereof. Though
some opaque coatings are referred to in the art as a lacquer, a
varnish, a shellac, or a water repellent coating, all such opaque
coatings are considered as paints herein (e.g., a lacquer-paint, a
varnish-paint, a shellac-paint, a water repellent paint).
[0313] a. Varnishes
[0314] A varnish is a thermosetting coating that converts to a
transparent or translucent solid film after application. In general
embodiments, a varnish is a wood-coating. A varnish comprises an
oil and a dissolved binder. In general embodiments, the oil
comprises a drying oil, wherein the drying oil functions as an
additional binder. In other embodiments, the binder is solid at
room temperature prior to dissolving into the oil and/or an
additional liquid component of the varnish. Examples of a
dissolvable binder include resins obtained from a natural source
(e.g., a Congo resin, a copal resin, a damar resin, a kauri resin),
a synthetic resin, or a combination thereof. In specific aspects,
the additional liquid component comprises a solvent such as a
hydrocarbon solvent. In some facets, the solvent is added to reduce
viscosity of the varnish. A varnish may further comprise a coloring
agent, including a pigment, for such purposes as conferring or
altering a color, gloss, sheen, or a combination thereof. A varnish
undergoes thermosetting film formation by oxidative cross-linking.
In certain aspects, a varnish may additionally undergo
film-formation by evaporation of a volatile component. The
dissolved binder generally functions to shorten the time to
film-formation relative to certain measures (e.g., dryness,
hardness), though the final cross-linking reaction time may not be
significantly or measurably shortened. Standards for determining a
varnish-coating and/or film's properties are described in, for
example, "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D154-85, 2002.
[0315] b. Lacquers
[0316] A lacquer is a thermoplastic, solvent-borne coating that
converts to a transparent or translucent solid film after
application. In general embodiments, a lacquer is a wood-coating. A
lacquer-coating comprises a thermoplastic binder dissolved in a
liquid component comprising an active solvent. Examples of a
thermoplastic binder include a cellulosic binder (e.g.,
nitrocellulose, cellulose acetate), a synthetic resin (e.g., an
acrylic), or a combination thereof. In certain aspects, a liquid
component comprises an active solvent, a latent solvent, diluent, a
thinner, or a combination thereof. In certain embodiments, a
lacquer is nonaqueous dispersion ("NAD") lacquer, wherein the
content of solvent is not sufficient to fully dissolve the
thermoplastic binder. In certain aspects, a lacquer may comprise an
additional binder (e.g., an alkyd), a colorant, a plasticizer, or a
combination thereof. Film formation of a lacquer occurs by loss of
the volatile components, typically through evaporation.
[0317] Standards for a lacquer-coating and/or film's composition
(e.g., a lacquer, a pigmented-lacquer, a nitrocellulose lacquer, a
nitrocellulose-alkyd lacquer), physical and/or chemical properties
(e.g., heat and cold resistance, hardness, film-formation time,
stain resistance, particulate material dispersion), and procedures
for testing a lacquer's composition/properties, are described in,
for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D333-01, D2337-01, D3133-01, D365-01, D2091-96,
D2198-02, D2199-82, D2571-95 and D2338-02, 2002.
[0318] C. Shellacs
[0319] A shellac is similar to a lacquer, but the binder does not
comprise a nitrocellulose binder, and the binder is soluble in
alcohol, and the binder is obtained from a natural source. A
preferred binder comprises Laciffer lacca beetle secretion. In
general embodiments, a shellac comprises a liquid component (e.g.,
alcohol). In specific aspects, the additional liquid component
comprises a solvent. In some facets, the liquid component is added
to reduce viscosity of the varnish. In other embodiments, a shellac
undergoes rapid film formation. Standards for a shellac-coating
and/or film's composition and properties are described in, for
example, "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D29-98 and D360-89, 2002.
[0320] d. Stains
[0321] A stain a clear or semitransparent coating formulated to
change the color of surface. In general embodiments, a stain is a
wood-coating designed to color or protect a wood surface but not
conceal the grain pattern or texture. A stain comprises a binder
such as an oil, an alkyd, or a combination thereof. Often a stain
comprises a low solid content. A low solids content for a wood
stain is less than 20% volume of solids. The low solid content of a
stain promotes the ability of the coating to penetrate the material
of the wooden surface. This property is often used to, for example,
to promote the incorporation of a fungicide that may be comprised
within the stain into the wood. In certain alternative aspects, a
stain comprises a high solids content stain, wherein the solid
content is 20% or greater, may be used on a surface to produce a
film possessing the property of little or no flaking. In other
alternative aspects, a water-borne stain may be used such as a
stain comprising a water-borne alkyd. A stain typically further
comprises a liquid component (e.g., a solvent), a fungicide, a
pigment, or a combination thereof. In other aspects, a stain
comprises a water repellent hydrophobic compound so it functions as
a water repellent-coating ("stain/water repellent-coating").
Examples of a water repellent hydrophobic compound a stain may
comprise include a silicone oil, a wax, or a combination thereof.
Examples of a fungicide include a copper soap, a zinc soap, or a
combination thereof. Examples of a pigment include a pigment that
is similar in color to wood. Examples of such pigments include a
red pigment (e.g., a red iron oxide) a yellow pigment (e.g., a
yellow iron oxide), or a combination thereof. Standards procedures
for testing a stain's (e.g., an exterior stain) properties, are
described in, for example, in "ASTM Book of Standards, Volume
06.02, Paint--Products and Applications; Protective Coatings;
Pipeline Coatings," D6763-02, 2002.
[0322] e. Water Repellent-Coatings
[0323] A water repellent-coating is a coating that comprises
hydrophobic compounds that repel water. A water repellent-coating
is typically applied to a surface susceptible to water damage, such
as metal, masonry, wood, or a combination thereof. A water
repellent-coating typically comprises a hydrophobic compound and a
liquid component. In specific embodiments, a water
repellent-coating comprises 1% to 65% hydrophobic compound,
including all intermediate ranges and combinations thereof.
Examples of a hydrophobic compound that may be selected include an
acrylic, a siliconate, a metal-searate, a silane, a siloxane, a
parafinnic wax, or a combination thereof. A water repellent may be
a water-borne coating, or a solvent-borne coating. A solvent-borne
water repellent-coating typically comprises a solvent that
dissolves the hydrophobic compound. Examples of solvents include an
aliphatic, an aromatic, a chlorinated solvent, or a combination
thereof.
[0324] In certain embodiments, a water repellent-coating, undergoes
film formation, penetrates pores, or a combination thereof. In
certain aspects, an acrylic-coating, a silicone-coating, or a
combination thereof, undergoes film formation. In other aspects, a
metal-searate, a silane, a siloxane, a parafinnic wax, or a
combination thereof, penetrates pores in a surface. In some facets,
a water repellent-coating (e.g., a silane, a siloxane) covalently
bonds to a surface and/or pore (e.g., masonry). Standards for a
water repellent-coating and/or film's composition and properties
are described in, for example, "ASTM Book of Standards, Volume
06.02, Paint--Products and Applications; Protective Coatings;
Pipeline Coatings," D2921-98, 2002; and in "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 748-750, 1995. Alternatively, standards
for a sealer-coating (e.g., a floor sealer) and/or film's
composition and properties are described in, for example, "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D1546-96, 2002;
[0325] 3. Coating Categories by Use
[0326] In light of the present disclosures, one of ordinary skill
in the art may prepare and apply a coating of the present invention
to any surface. However, it is preferred that the coating
components and methods described herein are selected for a
particular application to provide a coating and/or film with
properties best suited for a particular use. For example, a coating
used in an external environment would preferably comprise a coating
component of superior UV resistance than a coating used in interior
environment. In another example, a film used upon a surface of a
washing machine would preferably comprise a component that confers
superior moisture resistance than a component of a film for use
upon a ceiling surface. In a further example, a coating applied to
the surface of an assembly line manufactured product would
preferably comprise components suitable for application by a spray
applicator. Various properties of coating components are described
herein to provide guidance to the selection of specific coating
compositions with a suitable set of properties for a particular
use.
[0327] A coating of the present invention may be classified by its
preferred end use, including, for example, as an architectural
coating, an industrial coating, a specification coating, or a
combination thereof. An architectural coating is "an organic
coating intended for on-site application to interior or exterior
surfaces of residential, commercial, institutional, or industrial
buildings, in contrast to industrial coatings. They are protective
and decorative finishes applied at ambient conditions" ["Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook" (Koleske, J. V. Ed.), p. 686, 1995)] An industrial
coating is a coating applied in a factory setting, typically for a
protective and/or aesthetic purpose. A specification coating
("specification finish coating") is a coating formulated to a
"precise statement of a set of requirements to be satisfied by a
material, produce, system, or service that indicates the procedures
for determining whether each of the requirements are satisfied"
["Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook" (Koleske, J. V. Ed.), p. 891, 1995]. Often,
a coating may be categorized as a combination of an architectural
coating, an industrial coating, and/or a specification coating. For
example, a coating for the metal surfaces of ships may be
classified as specification coating, as specific criteria of water
resistance and corrosion resistance are required in the film, but
typically such a coating can be classified as an industrial
coating, since it would typically be applied in a factory. Various
examples of an architectural coating, an industrial coating and/or
a specification coating and coating components are described
herein. Additionally, architectural coatings, industrial coatings,
specification coatings are known to those of ordinary skill in the
art, and are described, for example, in "Paint and Surface
Coatings: Theory and Practice" 2.sup.nd Edition, pp. 190-192, 1999;
in "Paints, Coatings and Solvents" 2.sup.nd Edition, pp. 330-410,
1998; in "Organic Coatings: Science and Technology, Volume 1: Film
Formation, Components, and Appearance" 2.sup.nd Edition, pp. 138
and 317-318.
[0328] a. Architectural Coatings
[0329] An architectural coating ("trade sale coating," "building
coating," "decorative coating," "house coating") is a coating
suitable to coat surface materials commonly found as part of
buildings and/or associated objects (e.g., furniture). Examples of
a surface an architectural coating is typically applied to include,
a plaster surface, a wood surface, a metal surface, a composite
particle board surface, a plastic surface, a coated surface (e.g.,
a painted surface), a masonry surface, a floor, a wall, a ceiling,
a roof, or a combination thereof. Additionally, an architectural
coating may be applied to an interior surface, an exterior surface,
or a combination thereof. An interior coating generally possesses
properties such as minimal odor (e.g., no odor, very low VOC), good
blocking resistance, print resistance, good washability (e.g., wet
abrasion resistance), or a combination thereof. An exterior coating
typically is selected to possess good weathering properties.
Examples of coating type commonly used as an architectural coating
include an acrylic-coating, an alkyd-coating, a vinyl-coating, a
urethane-coating, or a combination thereof. In certain aspects, a
urethane-coating is applied to a piece of furniture. In other
facets, an epoxy-coating, a urethane-coating, or a combination
thereof, is applied to a floor. In some embodiments, an
architectural coating is a multicoat system. In certain aspects, an
architectural coating is a high performance architectural coating
("HIPAC"). A HIPAC is architectural coatings that produce a film
with a combination of good abrasion resistance, staining
resistance, chemical resistance, detergent resistance, and mildew
resistance. Examples of binders suitable for producing a HIPAC
include a two-pack epoxide or urethane, or a moisture cured
urethane. In general embodiments, an architectural coating
comprises a liquid component, an additive, or a combination
thereof. In certain aspects, an architectural coating is a
water-borne coating or a solvent-borne coating. In other aspects,
an architectural coating comprises a pigment. In preferred aspects,
such an architectural coating is formulated to comprise a reduced
amount or lack a toxic coating component. Examples of a toxic
coating component include a heavy metal (e.g., lead), formaldehyde,
a nonyl phenol ethoxylate surfactant, a crystalline silicate, or a
combination thereof.
[0330] In certain embodiments, a water-borne coating has a density
of 1.20 kg/L to 1.50 kg/L, including all intermediate ranges and
combinations thereof. In other embodiments, a solvent-borne coating
has a density of 0.90 kg/L to 1.2 kg/L, including all intermediate
ranges and combinations thereof. The density of a coating can be
empirically determined, for example, as described in "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D1475-98, 2002. In certain
embodiments, the course particle content of an architectural
coating, by weight, is 0.5% or less. The coarse particle (e.g.,
coarse contaminants, pigment agglomerates) content of a coating can
be empirically determined, for example, as described in "ASTM Book
of Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D185-84, 2002. In some embodiments, the viscosity for an
architectural coating at relatively low shear rates used during
typical application, in Krebs Units ("Ku"), is 72 Ku to 95 Ku,
including all intermediate ranges and combinations thereof.
[0331] In typical use, an architectural coating is often stored in
a container for months or even years prior to first use, and/or
between different uses. In many embodiments, it will be preferred
that a building coating will retain a desirable set properties of a
coating, film formation, film, or a combination thereof, for a
period of 12 months or greater in a container at ambient
conditions. Properties that are preferred for storage include
settling resistance, skinning resistance, coagulation resistance,
viscosity alteration resistance, or a combination thereof. Storage
properties can be empirically determined for a coating (e.g., an
architectural coating) as described, for example, in "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D869-85 and D1849-95,
2002.
[0332] It is preferred that application and/or film formation of an
architectural coating occurs at ambient conditions to provide ease
of use to a casual user of the coating, as well as reduce potential
damage to the target surface and the surrounding environment (e.g.,
unprotected people and objects). In general embodiments, it is
preferred that an architectural coating does not undergo film
formation by a temperature greater than 40.degree. C. to reduce
possible heat and fire damage. In other embodiments, it is
preferred that an architectural coating is suitable to be applied
by using hand-held applicator. Hand-held applicators are generally
can be used without difficulty by most users of a coating, and
examples include a brush, a roller, a sprayer (e.g., a spray can),
or a combination thereof.
[0333] Specific procedures for determining the suitability of a
coating and/or film for use as an architectural coating (e.g., a
water-borne coating, a solvent-borne coating, an interior coating,
an exterior paint, a latex paint), and specific assays for
properties typically desired in an architectural coating (e.g.,
blocking resistance, hiding power, print resistance, washability,
weatherability, corrosion resistance) have been described, for
example, in "ASTM Book of Standards, Volume 06.02, Paint--Products
and Applications; Protective Coatings; Pipeline Coatings,"
D5324-98, D5146-98, D3730-98, D1848-88, D5150-92, D2064-91,
D4946-89, D6583-00, D3258-00, and D3450-00, 2002; "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D660-93, D4214-98, D772-86,
D662-93, and D661-93, 2002; and in "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook" (Koleske,
J. V. Ed.), pp. 696-705, 1995.
[0334] (1) Wood Coatings
[0335] As is well known to those of ordinary skill in the art, a
wood coating is often selected to protect the wood from damage, as
well as aesthetic purposes. For example, wood is susceptible to
damage from bacteria and fungi. Examples of fungi that damage wood
include Aureobasidium pullulans, and Ascomycotina, Deutermycotina,
Basidiomycetes, Coniophora puteana, Serpula lacrymans, and
Dacrymyces stillatus. It is preferred that a wooden surface is
impregnated with a preservative such as a fungicide, prior to
application of a coating of the present invention. However, most
wood that is contemplated as a surface for a coating of the present
invention is provided this way from wood suppliers. Specific
procedures for determining the presence of a preservative and/or
water repellent in wood have been described, for example, in "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D2921-98, 2002.
[0336] Typically, wood surfaces are coated with a paint, a varnish,
a stain, or a combination thereof. Often, the choice of coating is
based on the ability of a coating to protect the wood from damage
by moisture. Generally, a paint, a varnish, and a stain generally
have progressively greater permeability to moisture, and moisture
penetration of a wooden surface can which can lead to undesirable
alterations in wood structure (e.g., splitting); undesirable
alteration in piece of wood's dimension ("dimensional movement")
such as shrinking, swelling, and/or warping; promote the growth of
a microorganism such as fungi (e.g., wet rot, dry rot); or a
combination thereof. Additionally, UV light irradiation damages a
wood surface by depolymerizing lignin comprised in the wood. It is
preferred that in embodiments wherein a wood surface is irradiated
by UV light (e.g., sunlight), the wood coating comprises a UV
protective agent such as a pigment that absorbs UV light. An
example of a UV absorbing pigment includes a transparent iron
oxide.
[0337] A preferred paint for use on a wood surface comprises an
oil-paint, an alkyd-paint, or a combination thereof. A preferred
alkyd-paint for use on a wood surface comprises a solvent-borne
paint. A preferred paint system comprises a combination of a
primer, an undercoat, and a topcoat. A film produced by a paint is
often moisture impermeable. A film produced by paint upon a wooden
surface may crack, flake, trap moisture that can encourage wood
decay, be expensive to repair, or a combination thereof.
[0338] (2) Masonry Coatings
[0339] Masonry coatings refer to coatings used on a masonry
surface, such as, for example, stone, brick, tile, cement-based
materials (e.g., concrete, mortar), or a combination thereof. In
general embodiments, a masonry coating is selected to confer
resistance to water (e.g., salt water), resistance to acid
conditions, alteration of appearance (e.g., color, brightness), or
a combination thereof. Typically, a masonry coating comprises a
multicoat system. In specific embodiments, a masonry multicoat
system comprises a primer, a topcoat, or a combination thereof.
Examples of a masonry primer include a rubber primer (e.g., a
styrene-butadiene copolymer primer). In certain embodiments, a
topcoat comprises a water-borne coating or a solvent borne coating.
Examples of a water-borne coating that may be selected for a
masonry topcoat include a latex coating, a water reducible
polyvinyl acetate-coating, or a combination thereof. In certain
aspects, a solvent-borne topcoat comprises a thermoplastic coating,
a thermosetting coating, or a combination thereof. Examples of a
thermosetting coating include an oil, an alkyd, a urethane, an
epoxy, or a combination thereof. In certain aspects, a
thermosetting coating is a multi-pack coating, such as, for
example, an epoxy, a urethane, or a combination thereof. In
specific aspects, a thermosetting coating undergoes film formation
at ambient conditions. In other aspects, a thermosetting coating
undergoes film formation at film formation at an elevated
temperature such as a baking alkyd, a baking acrylic, a baking
urethane, or a combination thereof. Examples of a thermoplastic
coating include an acrylic, cellulosic, a rubber-derivative, a
vinyl, or a combination thereof. In specific aspects, a
thermoplastic coating is a lacquer.
[0340] A masonry surface that is basic in pH, such as, for example,
cement-based material and/or a calcareous stone (e.g., marble,
limestone) may be damaging to certain coatings. Specific procedures
for determining the pH of a masonry surface have been described,
for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D4262, 2002. Due to porosity and/or contact with an
external environment, a masonry surface often accumulates dirt and
other loose surface contaminants, which are preferably removed
prior to application of a coating. Specific procedures for
preparative cleaning (e.g., abrading, acid etching) of a masonry
surface (e.g., sandstone, clay brick, concrete) have been
described, for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D4259-88, D4260-88D, 5107-90, D5703-95, D4261-83, and
D4258-83, 2002. In certain embodiments, moisture at or near a
masonry surface may be undesirable during application of a coating
(e.g., a solvent-borne coating). Specific procedures for
determining the presence of such moisture upon a masonry surface
have been described, for example, in "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D4263-83, 2002. Specific procedures
for determining the suitability of a coating and/or film,
particularly in conferring water resistance to a masonry surface,
have been described, for example, in "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D6237-98, D4787-93, D5860-95,
D6489-99, D6490-99, and D6532-00, 2002. Additional procedures for
determining the suitability of a coating and/or film for use as a
masonry coating have been described, for example, in "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 725-730, 1995.
[0341] (3) Artist's Coatings
[0342] Artist coatings refer to a coating used by artists for a
decorative purpose. Often, an artist's coating (e.g., paint) is
selected for durability for decades or centuries at ambient
conditions, usually indoors. Coatings such as an alkyd coating, an
oil coating, an oleoresinous coating, an emulsion (e.g., acrylic
emulsion) coating, or a combination thereof, are typically selected
for use as an artist's coating. Specific standards for physical
properties, chemical properties, and/or procedures for determining
the suitability (e.g., lightfastness) of a coating and/or film for
use as an artist's coating have been described, for example, in
"ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D4236-94,
D5724-99, D4302-99, D4303-99, D4941-89, D5067-99, D5098-99,
D5383-02, D5398-97, D5517-00, and D6801-02a, 2002; and in "Paint
and Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 706-710, 1995.
[0343] b. Industrial Coatings
[0344] An industrial coating is a coating applied to a surface of a
manufactured product in a factory setting. An industrial coating
typically undergoes film formation to produce a film with a
protective and/or aesthetic purpose. Industrial coatings share some
similarities to an architectural coating, such as comprising
similar coating components, being applied to the same material
types of surfaces, being applied to an interior surface, being
applied to an exterior surface, or a combination thereof. Examples
of coating types that are commonly used for an industrial coating
include an epoxy-coating, a urethane-coating, alkyd-coating, a
vinyl-coating, chlorinated rubber-coating, or a combination
thereof. Examples of a surface commonly coated by an industrial
coating include metal (e.g., aluminum, zinc, copper, an alloy,
etc); glass; plastic; cement; wood; paper; or a combination
thereof. An industrial coating may be storage stable for 12 months
or more, applied at ambient conditions, applied using a hand-held
applicator, undergo film formation at ambient conditions, or a
combination thereof.
[0345] However, an industrial coating often does not meet one or
more of these characteristics previously described as preferred for
an architectural coating. For example, an industrial coating may
have a storage stability of only days, weeks, or months, as due to
a more rapid use rate in coating factory prepared items. An
industrial coating may be applied and/or undergo film formation at
baking conditions. An industrial coating may be applied using
techniques such as, for example, spraying by a robot, anodizing,
electroplating, and/or laminating of a coating and/or film onto a
surface. In some embodiments, an industrial coating undergoes film
formation by irradiating the coating with non-visible light
electromagnetic radiation and/or particle radiation such as UV
radiation, infrared radiation, electron-beam radiation, or a
combination thereof.
[0346] In certain embodiments, an industrial coating comprises an
industrial maintenance coating, which is a coating that produces a
protective film with excellent heat resistance (e.g., 121.degree.
C. or greater), solvent resistance (e.g., an industrial solvent, an
industrial cleanser), water resistance (e.g., salt water, acidic
water, alkali water), corrosion resistance, abrasion resistance
(e.g., mechanical produced wear), or a combination thereof. An
example of an industrial maintenance coating includes a
high-temperature industrial maintenance coating, which is applied
to a surface intermittently or continuously contacted with a
temperature of 204.degree. C. or greater. An additional example of
an industrial maintenance coating is an industrial maintenance
anti-graffiti coating, which is a two-pack clear coating applied to
an exterior surface that is intermittently contacted with a solvent
and abrasion. Examples of coating types that are commonly used for
an industrial maintenance coating include an epoxy-coating, a
urethane-coating, alkyd-coating, a vinyl-coating, chlorinated
rubber-coating, or a combination thereof.
[0347] Industrial coatings (e.g., coil coatings) and their use are
well known to those of ordinary skill in the art (see, for example,
in "Paint and surface coatings: Theory and Practice," 2.sup.nd
Edition, pp. 502-528, 1999; in "Paints, Coatings and Solvents,"
2.sup.nd Edition, pp. 330-410, 1998; in "Organic Coatings: Science
and Technology, Volume 1: Film Formation, Components, and
Appearance," 2.sup.nd Edition, pp. 138, 317-318). Standard
procedures for determining the properties of an industrial coating
(e.g., an industrial wood coating, an industrial water-reducible
coating) have been described, for example, in "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D4712-87a, D6577-00a,
D2336-99, D3023-98, D3794-00, D4147-99, and D5795-95, 2002.
[0348] (1) Automotive Coatings
[0349] Automotive coatings refer to coatings used on automotive
vehicles, particularly those for civilian use. The manufacturers of
a vehicle typically require that a coating conform to specific
properties of weatherability (e.g., UV resistance) and/or
appearance. Typically, an automotive coating comprises a multicoat
system. In specific embodiments, an automotive multcoat system
comprises a primer, a topcoat, or a combination thereof. Examples
of an automotive rimer include a nonweatherable primer, which lack
sufficient UV resistance for single layer use, or a weatherable
primer, which possesses sufficient UV resistance to be used without
an additional layer. Examples of a topcoat include an interior
topcoat, an exterior topcoat, or a combination thereof.
[0350] Examples of a nonweatherable automotive primer include a
primer applied by electrodeposition, a conductive ("electrostatic")
primer, or a nonconductive primer. In certain embodiments, a primer
is applied by electrodeposition, wherein a metal surface is
immersed in a primer, and electrical current promotes application
of a primer component (e.g., a binder) to the surface. An example
of a metal primer suitable for electrodeposition application
includes a primer comprising an epoxy binder comprising an amino
moiety, a blocked isocyanate urethanebinder, and a 75% to 95%
aqueous liquid component. In other embodiments, a primer is a
conductive primer, which allows additional coating layers to be
applied using electrostatic techniques. A conductive primer
typically is applied to a plastic surface, including a flexible
plastic surface or a nonflexible plastic surface. Such primers vary
in their respective flexibility property to better suit use upon
the surface. An example of a flexible plastic conductive primer
includes a primer comprising polyester binder, a melamine binder
and a conductive carbon black pigment. An example of a nonflexible
plastic primer includes a primer that comprises an epoxy ester
binder and/or an alkyd binder, a melamine binder and conductive
carbon black pigment. In certain embodiments, a melamine binder may
be partly or fully replaced with an aromatic isocyanate urethane
binder, wherein the coating is a two-pack coating. A nonconductive
primer is similar to a conductive primer, except the carbon-black
pigment is absent or reduced in content. In certain embodiments, a
nonconductive primer is a metal primer, a plastic primer, or a
combination thereof. In specific aspects, the nonconductive primer
comprises a pigment for colorizing purposes.
[0351] Examples of a weatherable automotive primer include a
primer/topcoat or a conductive primer. An example of a
primer/topcoat includes a flexible plastic primer, with suitable
weathering properties (e.g., UV resistance) to function as a single
layer topcoat. Examples of a flexible plastic primer include a
primer comprising an acrylic and/or polyester binder and a melamine
binder. In certain embodiments, a melamine binder may be partly or
fully replaced with an aliphatic isocyanate urethane binder,
wherein the coating is a two-pack coating. A weatherable conductive
primer typically is similar to a weatherable primer/topcoat,
including a conductive pigment. In specific aspects, a weatherable
automotive primer comprises a pigment for colorizing purposes.
[0352] An interior automotive topcoat typically is applied to a
metal surface, a plastic surface, a wood surface, or a combination
thereof. In certain aspects, an interior automotive topcoat is part
of a multicoat system further comprising a primer. Examples of an
interior automotive topcoat include a coating comprising a urethane
binder, an acrylic binder, or a combination thereof.
[0353] An exterior automotive topcoat is typically is applied to a
metal surface, a plastic surface, or a combination thereof. In
certain aspects, an exterior automotive topcoat is part of a
multicoat system further comprising a primer, sealer, undercoat, or
a combination thereof. In certain embodiments, an exterior
automotive topcoat comprises a binder capable of thermosetting in
combination with a melamine binder. Examples of such a
thermosetting binder include an acrylic binder, an alkyd binder, a
urethane binder, polyester binder, or a combination thereof. In
certain embodiments, a melamine binder may be partly or fully
replaced with an urethane binder, wherein the coating is a two-pack
coating. In typical embodiments, an exterior automotive topcoat
further comprises a light stabilizer, a UV absorber, or a
combination thereof. In general aspects, an exterior automotive
topcoat further comprises a pigment.
[0354] Specific procedures for determining the suitability of a
coating (e.g., a nonconductive coating) and/or film for use as an
automotive coating, including spray application suitability,
coating VOC content and film properties (e.g., corrosion
resistance, weathering) have been described, for example, in "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D5087-02, D6266-00,
and D6675-01, 2002; and "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D5066-91, D5009-02, D5162-01, and D6486-01, 2002; and in
"Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 711-716,
1995.
[0355] (2) Can Coatings
[0356] Can coatings refer to coatings used on a container (e.g., an
aluminum container, a steel container), for food, chemicals, or a
combination thereof. The manufacturers of a can typically require
that a coating conform to specific properties of corrosion
resistance, inertness (e.g., to prevent flavor alterations in food,
a chemical reaction with a container's contents, etc), appearance,
durability, or a combination thereof. Typically, a can coating
comprises an acrylic-coating, an alkyd-coating, an epoxy-coating, a
phenolic-coating, a polyester-coating, a poly(vinyl
chloride)-coating, or combination thereof. Though a can may be made
of the same or similar material, different surfaces of a can may
require coatings of differing properties of inertness, durability
and/or appearance. For example, a coating for a surface of the
interior of a can that contacts the container's contents may be
selected for a chemical inertness property, a coating for a surface
at the end of a can may be selected for a physical durability
property, or a coating for a surface on the exterior of a can may
be selected for an aesthetic property. To meet the varying can
surface requirements, a can coating may comprise a multicoat
system. In specific embodiments, a can multicoat system comprises a
primer, a topcoat, or a combination thereof. In certain
embodiments, an epoxy-coating, a poly(vinyl chloride-coating), or a
combination thereof is selected as a primer for a surface at the
end of a can. In other embodiments, an oleoresinous-coating, a
phenolic-coating, or a combination thereof is selected as a primer
for a surface in the interior of a can. In some aspects, a
water-borne epoxy and acrylic-coating is selected as a topcoat for
a surface of an interior of a can. In addition embodiments, an
acrylic-coating, an alkyd-coating, a polyester-coating, or a
combination thereof is selected as an exterior coating. In certain
facets, a can coating (e.g., a primer, a topcoat) will further
comprise an amino resin, a phenolic resin, or a combination thereof
for cross-linking in a thermosetting film formation reaction. In
certain embodiments, a can coating is applied to a surface by spray
application. In other embodiments, a can coating undergoes film
formation by UV irradiation. Specific procedures for determining
the suitability of a coating and/or film for use as a can coating,
have been described, for example, in "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 717-724, 1995.
[0357] (3) Sealant Coatings
[0358] Sealant coatings refer to coatings used to fill a joint to
reduce or prevent passage of a gas (e.g., air), water, a small
material (e.g., dust), a temperature change, or a combination
thereof. A sealant coating ("sealant") may be thought of as a
coating that bridges by contact two or more surfaces. A joint is a
gap or opening between two or more surfaces, which may or may not
be of the same material type (e.g., metal, wood, glass, masonry,
plastic, etc). In typical embodiments, a joint has a width, depth,
breadth, or a combination thereof, of 0.64 mm to 5.10 mm, including
all intermediate ranges and combinations thereof.
[0359] In certain embodiments, a sealant coating comprises an oil,
a butyl, an acrylic, a blocked styrene, a polysulfide, a urethane,
a silicone, or a combination thereof. A sealent may be a
solvent-borne coating or a water-borne coating (e.g., a latex). In
certain aspects, a sealant comprises a latex (e.g., an acrylic
latex). In other embodiments, a sealant is selected for
flexibility, as one or more of the joint surfaces may move during
normal use. Examples of a flexible sealant include a silicone, a
butyl, an acrylic, a blocked styrene, an acrylic latex, or a
combination thereof. An oil sealent typically comprises a drying
oil, an extender pigment, a thixotrope, and a drier. A
solvent-borne butyl sealent typically comprises a polyisobytylene
and/or a polybutene, an extender pigment (e.g., talc, calcium
carbonate), a liquid component, and an additive (e.g., an adhesion
promoter, an antioxidant, a thixotrope). A solvent-borne acrylic
sealent typically comprises a polymethylacrylate (e.g., polyethyl,
polybutyl), a colorant, a thixotrope, an additive, and a liquid
component. A solvent-borne blocked styrene sealant typically
comprises styrene, styrene-butadiene, isoprene, or a combination
thereof, and a liquid component. A solvent-borne acrylic sealant,
blocked styrene sealant, or a combination thereof typically is
selected for aspects wherein UV resistance is desired. A urethane
sealant may be a one-pack or two-pack coating. A solvent-borne
one-pack urethane sealant typically comprises an urethane that
comprises a hydroxyl moiety, a filler, a thixotrope, an additive,
an adhesion promoter, and a liquid component. A solvent-borne
two-pack urethane sealent typically comprises a polyether that
comprises an isocyanate moiety in one-pack and a binder comprising
a hydroxyl moiety in a second pack. A solvent-borne two-pack
urethane sealent typically also comprises a filler, an adhesion
promoter, an additive (e.g., a light stabilizer), or a combination
thereof. In certain aspects, a solvent-borne urethane sealent is
selected for a sealent with a good abrasion resistance. A
polysulfide sealant may be a one-pack or two-pack coating. A
solvent-borne one-pack polysulfide sealant typically comprises an
urethane that comprises a hydroxyl moiety, a filler, a thixotrope,
an additive, an adhesion promoter, and a liquid component. A
solvent-borne two-pack polysulfide sealent typically comprises a
first pack, which typically comprises a polysulfide, an opacifing
pigment, a colorizer (e.g., a pigment), clay, a thixotrope (e.g., a
mineral), and a liquid component; and a second pack, which
typically comprises a curing agent (e.g., lead peroxide), an
adhesion promoter, an extender pigment, and a light stabilizer. A
silicone sealant typically comprises a polydimethyllsiloxane and a
methyltriacetoxy silane, a methyltrimethoxysilane, a
methyltricyclorhexylaminosilane, or a combination thereof. A
water-borne acrylic latex sealant typically comprises a
thermoplastic acrylic, a filler, a surfactant, a thixotrope, an
additive, and a liquid component. Procedures for determining the
suitability of a coating and/or film for use as an sealant coating
have been described, for example, in "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 735-740, 1995.
[0360] (4) Marine Coatings
[0361] A marine coating is a coating used on a surface that
contacts water, or a surface that is part of a structure
continually near water (e.g., a ship, a dock, an drilling platform
for fossil fuels, etc). Typically, such surfaces comprise metal,
such as aluminum, high tensile steel, mild steel, or a combination
thereof. For embodiments wherein a surface contacts water, the type
of marine coating is selected to resist fouling, corrosion, or a
combination thereof. Fouling is an accumulation of aquatic
organisms, including microorganisms, upon a marine surface. Fouling
can damage a film, and as many marine coatings are formulated with
a preservative, an anti-corrosion property (e.g., an anticorrosion
pigment), or a combination thereof, as such damage often leads to
corrosion of metal surfaces. Additionally, a marine coating may be
selected to resist fire, such as a coating applied to a surface of
a ship. Further properties that are often desirable for a marine
coating include chemical resistance, impact resistance, abrasion
resistance, friction resistance, acoustic camouflage,
electromagnetic camouflage, or a combination thereof.
[0362] To achieve the various properties of a marine coating, often
a multicoat system is used. For metal surfaces, a primer known as a
blast primer is typically applied to the surface within seconds of
blast cleaning. Examples of a blast primer include a polyvinyl
butyral ("PVB") and phenolic resin coating, a two-pack epoxy
coating, or a two-pack zinc and ethyl silicate coating. A marine
metal surface undercoat or topcoat typically comprises an alkyd
coating, a bitumen coating, a polyvinyl coating, or a combination
thereof. Marine coatings and their use are well known to those of
ordinary skill in the art (see, for example, in "Paint and Surface
Coatings: Theory and Practice," 2.sup.nd Edition, pp. 529-549,
1999; in "Paints, Coatings and Solvents," 2.sup.nd Edition, pp.
252-258, 1998; in "Organic Coatings: Science and Technology, Volume
1: Film Formation, Components, and Appearance," 2.sup.nd Edition,
pp.138, 317-318). Specific procedures for determining the
purity/properties of a marine coating, anti-fouling coating, or
coating component thereof (e.g., cuprous oxide, copper powder,
organotin) under marine conditions (e.g., submergence, water based
erosion, seawater biofouling resistance, barnacle adhesion
resistance) and/or film have been described, for example, in "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D3623-78a, D4938-89,
D4939-89, D5108-90, D5479-94, D6442-99, D6632-01, D4940-98, and
D5618-94, 2002; and "ASTM Book of Standards, Volume 06.03,
Paint--Pigments, Drying Oils, Polymers, Resins, Naval Stores,
Cellulosic Esters, and Ink Vehicles," D912-81 and D964-65,
2002.
[0363] c. Specification Coatings
[0364] It is contemplated that, in light of the present
disclosures, a specification coating may be formulated by selection
of coating components one of ordinary skill in the art to fulfill a
set of requirements prescribed by a consumer. Examples a
specification finish coating include a military specified coating,
a Federal agency specified coating (e.g., Department of
Transportation), a state specified coating, or a combination
thereof. A specification coating such as a CARC, a camouflage
coating, or a combination thereof would be preferred in certain
embodiments for incorporation of a biomolecule composition of the
present invention. A camouflage coating is a coating that is
formulated with materials (e.g., pigments) that reduce the visible
differences between the appearance of a coated surface from the
surrounding enviroment. Often, as would be known to one of ordinary
skill in the art, a camouflage coating is formulated to reduce the
detection of an coated surface by devise that measures nonvisible
light (e.g., infrared radiation). Various sources of specification
coating requirements are described in, for example, "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 891-893, 1995).
[0365] (1) Pipeline Coatings
[0366] An example of a specification coating is a pipeline (e.g., a
metal pipeline) coating used to convey a fossil fuel. A pipeline
coating must possess corrosion resistance, and an example of a
pipeline coating includes a coal tar-coating, a
polyethylene-coating, an epoxy powder-coating, or a combination
thereof. A coal tar-coating may comprise, for example, a coal tar
mastic-coating, a coal tar epoxide-coating, a coal tar
urethane-coating, a coal tar enamel-coating, or a combination
thereof. A coal tar mastic-coating typically comprises an extender,
a vicosifier, or a combination thereof. In general aspects, a coal
tar mastic-coating layer is 127 mm to 160 mm thick, including all
intermediate ranges and combinations thereof. In embodiments
wherein superior water resistance is desired, a coal tar
epoxide-coating may be selected. In embodiments wherein rapid film
formation is desired (e.g., pipeline repair), a coal tar
urethane-coating may be selected. In embodiments wherein good water
resistance, heat resistance up to 82.degree. C., bacterial
resistance, poor UV resistance, or a combination thereof, is
suitable, a coal tar enamel may be selected. In embodiments wherein
cathodic protection, physical durability, or a combination thereof
is desired, an epoxide powder-coating may be selected. In certain
embodiments, an electrostatic spray applicator may be used to apply
the powder coating. In certain embodiments, a pipeline coating
comprises a multicoat system. In specific aspects, a pipeline
multicoat system comprises an epoxy powder primer, a two-pack epoxy
primer, a chlorinated rubber primer, or a combination thereof and a
polyethylene topcoat. Specific procedures for determining the
suitability of a coating and/or film for use as a pipeline coating,
including coating storage stability (e.g., settling) and film
properties (e.g., abrasion resistance, water resistance,
flexibility, weathering, film thickness, impact resistance,
chemical resistance, cathodic disbanding resistance, heat
resistance) have been described, for example, in "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," G6-88, G9-87, G10-83,
G11-88, G12-83, G13-89, G20-88, G70-81, G8-96, G17-88, G18-88,
G19-88, G42-96, G55-88, G62-87, G80-88, G95-87, and D6676-01e1,
2002; and in "Paint and Coating Testing Manual, Fourteenth Edition
of the Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 731-734,
1995.
[0367] (2) Traffic Marker Coatings
[0368] A traffic marker coating is a coating (e.g., a paint) used
to very visibly conveys information on a surface usually subjected
to weathering and abrasion (e.g., a pavement). A traffic marker
coating may be a solvent-borne coating or a water-borne coating.
Examples of a solvent-borne traffic marker coating include an
alkyd, a chlorinated rubber, or a combination thereof. In certain
aspects, a solvent-borne coating is applied by spray application.
In some embodiments, a traffic marker coating is a two-pack
coating, such as, for example, an epoxy-coating, a
polyester-coating, or a combination thereof. In other embodiments,
a traffic marker coating comprises a thermoplastic coating, a
thermosetting coating, or a combination thereof. Examples of a
combination thermoplastic/thermosetting coating include a
solvent-borne alkyd and/or solvent-borne chlorinated
rubber-coating. Examples of a thermoplastic coating include a
maleic-modified glycerol ester-coating, a hydrocarbon-coating, or a
combination thereof. In certain aspects, a thermoplastic coating
comprises a liquid component, wherein the liquid component
comprises a plasticizer, a pigment, and an additive (e.g., a glass
bead).
[0369] Specific procedures for determining the suitability of a
coating and/or film for use as a traffic marker paint, including
coating storage stability (e.g., settling), glass bead properties
(e.g., reflectance), film durability (e.g., adhesion, pigment
retention, solvent resistance, fuel resistance) and particularly
relevant film visual properties (e.g., retroreflectance,
fluorescence) have been described, for example, in "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D713-90, D868-85, D969-85,
D1309-93, D2205-85, D2743-68, D2792-69, D4796-88, D4797-88,
D1155-89, D1214-89, and D4960-89, 2002; in "ASTM Book of Standards,
Volume 06.01, Paint--Tests for Chemical, Physical, and Optical
Properties; Appearance," F923-00, E1501-99e1, E1696-02, E1709-00e1,
E1710-97, E1743-96, E2176-01, E808-01, E809-02, E810-01, E811-95,
D4061-94, E2177-01, E991-98, and E1247-92, 2002; and in "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 741-747, 1995.
[0370] (3) Aircraft Coatings
[0371] An aircraft coating protects and/or decorates a surface
(e.g., metal, plastic) of an aircraft. Typically, an aircraft
coating is selected for excellent weathering properties, excellent
heat and cold resistance (e.g., -54.degree. C. to 177.degree. C.),
or a combination thereof. Specific procedures for determining the
suitability of a coating and/or film for use as aircraft coating,
are described in, for example, in "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 683-695, 1995.
[0372] (4) Nuclear Power Plant Coatings
[0373] An additional example of a specification coating is a
coating for a nuclear power plant, which generally must possess
particular properties (e.g., gamma radiation resistance, chemical
resistance), as described in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D5962-96, D5163-91, D5139-90, D5144-00, D4286-90,
D3843-00, D3911-95, D3912-95, D4082-02, D4537-91, D5498-01, and
D4538-95, 2002.
[0374] H. Coating Components
[0375] In addition to the disclosures herein, the preparation
and/or chemical syntheses of coating components, other than the
microbial-based particulate matter of the present invention
disclosed herein, are well known to those ordinary skill in the art
[see, for example, "Paint and Coating Testing Manual, Fourteenth
Edition of the Gardner-Sward Handbook," (Koleske, J. V., Ed.)
(1995); "Paint and Surface Coatings, Theory and Practice, Second
Edition," (Lambourne, R. and Strivens, T. A., Eds.) (1999); Wicks,
Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic Coatings, Science
and Technology, Volume 1: Film Formation, Components, and
Appearance," (1992); Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P.
"Organic Coatings, Science and Technology, Volume 2: Applications,
Properties and Performance," (1992); "Paints, Coatings and
Solvents, Second, Completely Revised Edition," (Stoye, D. and
Freitag, W., Eds.) (1998); "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," (2002); "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," (2002); "ASTM Book of Standards, Volume 06.03,
Paint--Pigments, Drying Oils, Polymers, Resins, Naval Stores,
Cellulosic Esters, and Ink Vehicles," (2002); and "ASTM Book of
Standards, Volume 06.04, Paint--Solvents; Aromatic Hydrocarbons,"
(2002)].
[0376] However, as would be known to one of ordinary skill in the
art, coating components are typically obtained from commercial
vendors, which is a preferred method of obtaining a coating
component due to ease and reduced cost. As would be known to one of
ordinary skill in the art, texts as, for example, Flick, E. W.
"Handbook of Paint Raw Materials, Second Edition," 1989, describes
over 4,000 coating components (e.g., an antifoamer, an antiskinning
agent, a bactericide, a binder, a defoamer, a dispersant, a drier,
an extender, a filler, a flame/fire retardant, a flatting agent, a
fungicide, a latex emulsion, an oil, a pigment, a preservative, a
resin, a rheological/viscosity control agent, a silicone additive,
a surfactant, a titanium dioxide, etc) provided by commercial
vendors; and Ash, M. and Ash, I. "Handbook of Paint and Coating Raw
Materials, Second Edition," 1996, which describes over 18,000
coating components (e.g., an accelerator, an adhesion promoter, an
antioxidant, an antiskinning agent, a binder, a coalescing agent, a
defoamer, a diluent, a dispersant, a drier, an emulsifier, a fire
retardant, a flow control agent, a gloss aid, a leveling agent, a
marproofing agent, a pigment, a slip agent, a thickener, a UV
stabilizer, viscosity control agent, a wetting agent, etc) provided
by commercial vendors.
[0377] Specific commercial vendors are referred to herein as
examples, and include Acima.TM. AG, Im Ochsensand, CH-9470
Buchs/SG; Air Products and Chemicals, Inc., 7201 Hamilton
Boulevard, Allentown, Pa. 18195-1501; Avecia Inc., 1405 Foulk Road,
PO Box 15457, Wilmington, Del. 19850-5457, U.S.A.; Bayer
Corporation, 100 Bayer Rd., Pittsburgh, Pa. 15205-9741, U.S.A.;
Buckman Laboratories, Inc., 1256 North McLean Blvd., Memphis, Term.
38108-0305, U.S.A.; BYK-Chemie GmbH, Abelstrasse 45, P.O. Box
100245, D-46462 Wesel, Germany; Ciba Specialty Chemicals, 540 White
Plains Road, P.O. Box 2005, Tarrytown, N.Y. 10591-9005, U.S.A.;
Clariant LSM (America) Inc., 200 Rodney Building, 3411 Silverside
Road, Wilmington, Del. 19810 U.S.A.; Cognis Corporation, 5051
Estecreek Drive, Cincinnati, Ohio 45232-1446, U.S.A.; Condea Servo
LLC., 4081 B Hadley Road, South Plainfield, N.J. 07080-1114,
U.S.A.; Cray Valley Limited, Waterloo Works, Machen, Caerphilly
CF838YN United Kingdom; Dexter Chemical L.L.C., 845 Edgewater Road
Bronx, N.Y. 10474, U.S.A.; Dow Chemical Company, 2030 Dow Center,
Midland, Mich. 48674 U.S.A.; Elementis Specialties, Inc., PO Box
700, 329 Wyckoffs Mill Road, Hightstown, N.J. 08520 U.S.A.;
Goldschmidt Chemical Corp., 914 East Randolph Road PO Box 1299
Hopewell, Va. 23860 U.S.A.; Hercules Incorporated, 1313 North
Market Street, Wilmington, Del. 19894-0001, U.S.A.; International
Specialty Products, 1361 Alps Road, Wayne, N.J. 07470, U.S.A.;
Octel-Starreon LLC USA, North American Headquarters, 8375 South
Willow Street, Littleton, Colo. 80124, U.S.A.; Rohm and Haas
Company, 100 Independence Mall West, Philadelphia, Pa. 19106-2399,
U.S.A.; Solvay Advanced Functional Minerals, Via Varesina
2-4,1-21021 Angera (VA); Troy Corporation, 8 Vreeland Road, PO Box
955, Florham Park, N.J., 07932 U.S.A.; R. T. Vanderbilt Company,
Inc., 30 Winfield Street, Norwalk, Conn. 06855, U.S.A; Union
Carbide Chemicals and Plastics Co., Inc., 39 Old Ridgebury Road,
Danbury, Conn. 06817-0001, U.S.A.
[0378] 1. Binders
[0379] A binder ("polymer," "resin," "film former") is a molecule
capable of film formation. Film formation is a physical and/or
chemical change of a binder in a coating, wherein the change
converts the coating into a film. Often, a binder converts into a
film through a polymerization reaction, wherein a first binder
molecule covalently bonds with at least a second binder molecule to
form a larger molecule, known as a "polymer." As this process is
repeated a plurality of times, the composition converts from a
coating comprising a binder into a film comprising a polymer.
[0380] A binder may comprise a monomer, an oligomer, a polymer, or
a combination thereof. A monomer is a single unit of a chemical
species that can undergo a polymerization reaction. However, a
binder itself is often a polymer, as such larger binder molecules
are more suitable for formulation into a coating capable of both
being easily applied to a surface and undergoing an additional
polymerization reaction to produce a film. An oligomer comprises 2
to 25 polymerized monomers, including all intermediate ranges and
combinations thereof.
[0381] A homopolymer is a polymer that comprises monomers of the
same chemical species. A copolymer is a polymer that comprises
monomers of at least two different chemical species. A linear
polymer is an unbranched chain of monomers. A branched polymer is a
branched ("forked") chain of monomers. A network ("cross-linked")
polymer is a branched polymer wherein at least one branch forms an
interconnecting covalent bond with at least one additional polymer
molecule.
[0382] A thermoplastic binder and/or coating reversibly softens
and/or liquefies when heated. Film formation for a thermoplastic
coating generally comprises a physical process, typically the loss
of the volatile (e.g., liquid) component from a coating. As a
volatile component is removed, a solid film may be produced through
entanglement of the binder molecules. In many aspects, a
thermoplastic binder is generally a higher molecular mass than a
comparable thermosetting binder. In many aspects, a thermoplastic
film is often susceptible to damage by a volatile component that
can be absorbed by the film, which can soften and/or physically
expand the film. In certain facets, a thermoplastic film may be
removed from a surface by use of a volatile component. However, in
many aspects, damage to a thermoplastic film may be repaired by
application of a thermoplastic coating into the damaged areas and
subsequent film formation.
[0383] A thermosetting binder undergoes film formation by a
chemical process, typically the cross-linking of a binder into a
network polymer. In certain embodiments, a thermosetting binder
does not possess significant thermoplastic properties.
[0384] The glass transition temperature is the temperature wherein
the rate of increase of the volume of a binder or a film changes.
Binders and films often do not convert from solid to liquid
("melt") at a specific temperature ("T.sub.m"), but rather possess
a specific glass transition temperature wherein there is an
increase in the rate of volume expansion with increasing
temperature. At temperatures above the glass transition
temperature, a binder or film becomes increasingly rubbery in
texture until it becomes a viscous liquid. In certain embodiments
described herein, a binder, particularly a thermoplastic binder,
may be selected by its glass transition temperature, which provides
guidance to the temperature range of film formation, as well as
thermal and/or heat resistance of a film. The lower the T.sub.g,
the "softer" the resin, and generally, the film produced from such
a resin. A softer film typically possesses greater flexibility
(e.g., crack resistance) and/or poorer resistance to dirt
accumulation than a harder film.
[0385] In certain embodiments, a coating comprises a low molecular
weight polymer, a high molecular weight polymer, or a combination
thereof. Examples of a low molecular weight polymer include an
alkyd, an amino resin, a chlorinated rubber, an epoxide resin, an
oleoresinous binder, a phenolic resin, a urethane, a polyester, an
urethane oil, or a combination thereof. Examples of a high
molecular weight polymer include a latex, a nitrocellulose, a
non-aqueous dispersion polymer ("NAS"), a solution acrylic, a
solution vinyl, or a combination thereof. Examples of a latex
include an acrylic, a polyvinyl acetate ("PVA"), a
styrene/butadiene, or a combination thereof.
[0386] In addition to the disclosures herein, a binder, methods of
binder preparation, commercial vendors of binder, and techniques
for using an binder in a coating known to those of ordinary skill
in the art may be applied in the practice of the present invention
(see, for example, Flick, E. W. "Handbook of Paint Raw Materials,
Second Edition," pp. 287-805 and 879-998, 1989; in "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 23-29, 39-67, 74-84, 87,
268-285, 410, 539-540, 732, 735-736, 741, 770, 806-807, 845-849,
and 859-861, 1995; in "Paint and Surface Coatings, Theory and
Practice, Second Edition," (Lambourne, R. and Strivens, T. A.,
Eds.), pp. 2-3,7-10, 21, 24-40, 40-54, 60-71, 76, 81-86, 352, 358,
381-394, 396, 398, 405, 433-448, 494-497, 500, 537-540, 700-702,
and 734, 1999; Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P.
"Organic Coatings, Science and Technology, Volume 1: Film
Formation, Components, and Appearance," pp. 39, 49-57, 62, 65-67,
67, 76-80, 83, 91, 104-118, 155, 168, 178, 182-183, 200, 202-203,
209, 214-216, 220 and 250, 162-186, 215-216 and 232, 59-60,
183-184, 133-143, 39,144-161, 203, 219-220 and 239, 23, 110,
120-132, 122-130, 198, 202-203, 209 and 220, 60-62, 83-103,
164-167, 173, 177-178, 184-187, 195, 206, and 216-219, 1992; Wicks,
Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic Coatings, Science
and Technology, Volume 2: Applications, Properties and
Performance," pp. 13-14, 18-19, 26, 33-34, 36, 41, 57, 77, 92, 95,
116-119, 143-145, 156, 161-165, 179-180,191-193, 197-203, 210-211,
213-214, 216, 219-222, 230-239, 260-263, 269-271, 276-284, 288-293,
301-307, 310, 315-316, 319-321, and 325-346, 1992; and in "Paints,
Coatings and Solvents, Second, Completely Revised Edition," (Stoye,
D. and Freitag, W., Eds.) pp. 5, 11-22, 37-50, 54-55, 72, 80-87,
96-98, 108, 126, and 136, 1998.
[0387] a. Oil-Based Binders
[0388] Certain binders, such as, for example, an oil (e.g., a
drying oil), an alkyd, an oleoresinous binder, a fatty acid epoxide
ester, or a combination thereof, are prepared and/or synthesized
from an oil and/or a fatty acid, and undergo film formation by
thermosetting oxidative cross-linking of fatty acids, and will be
referred to herein as an "oil-based binder." These types of binders
often possess similar properties (e.g., solubility, viscosity). An
oil-based binder coating often further comprises a drier, an
antiskinning agent, an alkylphenolic resin, a pigment, an extender,
a liquid component (e.g., a solvent), or a combination thereof. A
drier, such as a primary drier, secondary drier, or a combination
thereof, may be selected to promote film formation. In certain
facets, an oil-based binder coating may comprise an anti-skinning
agent, which is typically used to control undesirable
film-formation caused by a primary drier and/or oxidation. A liquid
component may be selected, for example, to alter a rheological
property (e.g., flow), wetting and/or dispersion of particulate
material, or a combination thereof. In certain embodiments, a
liquid component comprises a hydrocarbon. In particular
embodiments, the hydrocarbon comprises an aliphatic hydrocarbon, an
aromatic hydrocarbon (e.g., toluene, xylene), or a combination
thereof. In some facets, the liquid component comprises, by weight,
5% to 20% of an oil-based binder coating, including all
intermediate ranges and combinations thereof.
[0389] In alternative embodiments, an oil-based temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
inclusion of an antioxidant, reduction of the amount of a drier,
selection of a oil-based binder that comprises fewer or no double
bonds, or a combination thereof.
[0390] An oil-based binder coating may be selected for embodiments
wherein a relatively low viscosity is desired, such as, for
example, application to a corroded metal surface, a porous surface
(e.g., wood), or a combination thereof, due to the penetration
power of a low viscosity coating. In certain facets, it is
preferred that application of an oil-binder coating produces a
layer is less than 25 .mu.m on vertical surfaces and 40 .mu.m on
horizontal surfaces to reduce shrinkage, wrinkling. Additionally,
in aspects wherein the profile of the wood surface is to be
retained, a such a thin film thickness is preferred. In specific
aspects, an oil-binder coating may be selected as a wood stains, a
topcoat, or a combination thereof. In particular facets, a wood
stain comprises an oil (e.g., linseed oil) coating, an alkyd, or a
combination thereof. Often, wood coating comprises a
lightstabilizer (e.g., UV absorber).
[0391] (1) Oils
[0392] An oil is a polyol esterified to at least one fatty acid. A
polyol ("polyalcohol," "polyhydric alcohol") is an alcohol
comprising more than one hydroxyl moiety per molecule. In certain
embodiments, an oil comprises an acylglycerol esterified to one
fatty acid ("monacylglycerol"), two fatty acids ("diacylglycerol"),
or three fatty acids ("triacylglycerol," "triglyceride").
Typically, however, an oil will comprise a triacylglycerol. A fatty
acid is an organic compound comprising a hydrocarbon chain that
includes a terminal carboxyl moiety. A fatty acid may be
unsaturated, monounsaturated, and polyunsaturated referring to
whether the hydrocarbon chain possess no carbon double bonds, one
carbon double bond, or a plurality of carbon double bonds (e.g., 2,
3, 4, 5, 6, 7, or 8 double bonds), respectively.
[0393] In typical use in a coating, a plurality of fatty acids
forms covalent cross-linking bonds to produce a film in coatings
comprising oil binders and/or other binders comprising a fatty
acid. Usually oxidation through contact with atmospheric oxygen is
used to promote film formation. Exposure to light also enhances
film formation. The ability of an oil to undergo film formation by
chemical cross-linking is related to the content of chemically
reactive double bonds available in its fatty acids. Oils are
generally a mixture of chemical species, comprising different
combinations of fatty acids esterified to glycerol. The overall
types and percentages of particular fatty acids that are comprised
in oils affect the ability of the oil to be used as a binder. Oils
can be classified as a drying oil, a semi-drying oil, or a
non-drying oil depending upon the ability of the oil to cross-link
into a dry film without additives (e.g., driers) at room
temperature and atmospheric oxygen. A drying oil forms a dry film
to touch upon cross-linking, a semi-drying oil forms a sticky
("tacky") film to touch upon cross-linking, while a non-drying oil
does not produce a tacky or dry film upon cross-linking. In certain
facets, it is contemplated that film-formation of a non-chemically
modified oil-binder coating will typically take from 12 hours to 24
hours at room temperature, air, and lighting. Procedures for
selection and testing of drying oils for a coating are described
in, for example, "ASTM Book of Standards, Volume 06.03,
Paint--Pigments, Drying Oils, Polymers, Resins, Naval Stores,
Cellulosic Esters, and Ink Vehicles," D555-84, 2002.
[0394] Drying oils comprise at least one polyunsaturated fatty acid
to promote cross-linking. Polyunsaturated fatty acids ("polyenoic
fatty acids") include, but are not limited to,
7,10,13-hexadecatrienoic ("16:3 n-3"); linoleic
["9,12-octadecadienoic," "18:2(n-6)"]; .gamma.-linolenic
["6,9,12-octadecatrienoic," "18:3(n-6)"]; a trienoic 20:3(n-9);
dihomo-.gamma.-linolenic ["8,11,14-eicosatrienoic," "20:3(n-6)"];
arachidonic ["5,8,11,14-eicosatetraenoic," "20:4(n-6)"]; a licanic,
("4-oxo 9c11t13t-18:3"); 7,10,13,16-docosatetraenoic ["22:4(n-6)"];
4,7,10,13,16-docosapentaenoic ["22:5(n-6)"]; .alpha.-linolenic
["9,12,15-octadecatrienoic," "18:3(n-3)"]; stearidonic
["6,9,12,15-octadecatetraenoic," "18:4(n-3)"];
8,11,14,17-eicosatetraenoi- c ["20:4(n-3)"];
5,8,11,14,17-eicosapentaenoic ["EPA," "20:5(n-3)"];
7,10,13,16,19-docosapentaenoic ["DPA," "22:5(n-3)"];
4,7,10,13,16,19-docosahexaenoic ["DHA," "22:6(n-3)"];
5,8,11-eicosatrienoic ["Mead acid," "20:3(n-9)"]; taxoleic
("all-cis-5,9-18:2"); pinolenic ("all-cis-5,9,12-18:3"); sciadonic
("all-cis-5,11,14-20:3"); dihomotaxoleic ("7,11-20:2"); cis-9,
cis-15 octadecadienoic ("9,15-18:2"); retinoic; or a combination
thereof.
[0395] Drying oils can be further characterized as non-conjugated
or conjugated drying oils depending upon whether their most
abundant fatty acid comprises a polymethylene-interrupted double
bond or a conjugated double bond, respectively. A
polymethylene-interrupted double bond is two double bonds separated
by two or more methylene moieties. A polymethylene-interrupted
fatty acid is a fatty acid comprising such a configuration of
double bonds. Examples of polymethylene-interrupted fatty acids
include taxoleic, pinolenic, sciadonic, dihomotaxoleic, cis-9,
cis-15 octadecadienoic, retinoic, or a combination thereof.
[0396] A conjugated double bond is a moiety wherein a single
methylene moiety connects pair of carbon chain double bonds. A
conjugated fatty acid is a fatty acid comprising such a pair of
double bonds. A conjugated double bond is more prone to
cross-linking reactions than non-conjugated double bonds. A
conjugated diene fatty acid, a conjugated triene fatty acid or a
conjugated tetraene fatty acid, possesses only two, three or four
conjugated double bonds, respectively. An example of a common
conjugated diene fatty acid is a conjugated linoleic. Examples of a
conjugated triene fatty acid include an octadecatrienoic, a
licanic, or a combination thereof. Examples of an octadecatrienoic
acid include an .alpha.-eleostearic comprising the 9c, 11t, 13t
isomer, a calendic comprising a 8t, 10t, 12c isomer, a catalpic
comprising the 9c, 11t, 13c isomer, or a combination thereof. An
example of a conjugated tetraene fatty acid is .alpha.-parinaric
comprising the 9c, 11t, 13t, 15c isomer, and .beta.-parinaric
comprising the 9t, 11t, 13t, 15t isomer, or a combination
thereof.
[0397] Oils for use in coatings are generally obtained from
renewable biological sources, such as plants, fish or a combination
thereof. Examples of plant oils commonly used in coatings or
coating components include cottonseed oil, linseed oil, oiticica
oil, safflower oil, soybean oil, sunflower oil, tall oil, rosin,
tung oil, or a combination thereof. An example of a fish oil
commonly used in coatings or coating components include caster oil.
A colder environment generally promotes a higher polyunsaturated
fatty acid content in an organism (e.g., sunflowers). Cottonseed
oil comprises about 36% saturated fatty acids, 24% oleic, and 40%
linoleic. Castor oil comprises about 3% saturated fatty acids, 7%
oleic, 3% linoleic, and 87% ricinoleic
("12-hydroxy-9-octadecenoic"). Linseed oil comprises about 10%
saturated fatty acids, 20% to 24% oleic ("cis-9-octadecenoic"), 14%
to 19% linoleic, and 48% to 54% linolenic. Oiticica oil comprises
about 16% saturated fatty acids, 6% oleic, and 78% licanic.
Safflower oil comprises about 11% saturated fatty acids, 13% oleic,
75% linoleic, and 1% linolenic. Soybean oil comprises about 14% to
15% saturated fatty acids, 22% to 28% oleic, 52% to 55% linoleic,
and 5% to 9% linolenic. Tall oil, which is a product of paper
production and generally is not in the form of a triglyceride,
often comprises about 3% saturated fatty acids, 30% to 35% oleic,
35% to 40% linoleic, 2% to 5% linolenic, and 10% to 15% of a
combination of pinolenic and conjugated linoleic. Rosin is a
combination of acidic compounds isolated during paper production,
such as, for example, abietic acid, neoabietic acid, dihydroabietic
acid, tetraabietic acid, isodextropimaric acid, dextropimaric acid,
dehydroabietic acid, and levopimaric acid. Tung oil comprises about
5% saturated fatty acids, 8% oleic, 4% linoleic, 3% linolenic, and
80% .alpha.-elestearic. Standards for physical properties, chemical
properties, and/or procedures for testing the purity/properties of
various oils (e.g., caster, linseed, oiticica, safflower, soybean,
sunflower, tall, tung, rosin, dehydrated caster, boiled linseed, a
drying oil, a fish oil, a heat-bodied drying oil) for use in a
coating are described, for example in "ASTM Book of Standards,
Volume 06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D555-84, D960-02a,
D961-86, D234-82, D601-87, D1392-92, D1462-92, D12-88, D1981-02,
D5768-95, D3169-89, D260-86, D124-88, D803-02, D1541-97, D1358-86,
D1950-86, D1951-86, D1952-86, D1954-86, D1958-86, D464-95, D465-01,
D1959-97, D1960-86, D1962-85, D1964-85, D1965-87, D1966-69,
D1967-86, D3725-78, D1466-86, D890-98, D1957-86, D1963-85,
D5974-00, D1131-97, D1240-02, D889-99, D509-98, D269-97, D1065-96,
and D804-02, 2002.
[0398] In certain embodiments, an oil comprises a chemically
modified oil, which is an oil altered by a reaction thought to
promote limited cross-linking. Generally, such a modified oil
possesses an altered property, such as a higher viscosity, which
may be more suitable for a particular coating application. Examples
of a chemically modified oil include a bodied oil, a blown oil, a
dimer acid, or a combination thereof. A bodied oil ("heat bodied
oil," "stand oil") is produced, for example, by heating a
nonconjugated oil (e.g., 320.degree. C.) or a conjugated oil (e.g.,
240.degree. C.) in an chemically unreactive atmosphere to promote
limited cross-linking. A blown oil is produced, for example, by
passing air through a drying oil at, for example, 150.degree. C. A
dimer acid is produced, for example, by acid catalyzed dimerization
or oligomerization of a polyunsaturated acid.
[0399] In certain embodiments, an oil comprises a synthetic
conjugated oil, which is an oil altered by a reaction thought to
produce a conjugated double bond in a fatty acid of the oil.
Conjugated fatty acids have been produced from nonconjugated fatty
acids by alkaline hydroxide catalyzed reactions. However, a
synthetic conjugated oil is generally semi-drying in air catalyzed
film formation at room temperature, and a coating comprising such
an oil is typically cured by baking. Additionally richinoleic acid,
which is prevalent in castor oil, can be dehydrogenated to produce
a mixture of conjugated and non-conjugated fatty acids.
Dehydrogenated castor oil comprises about 2% to 4% saturated fatty
acids, 6% to 8% oleic, 48% to 50% linoleic, and 40% to 42%
conjugated linoleic.
[0400] Certain other compounds comprising a fatty acid and polyol
are classified herein as an oil for use as a binder such as a high
ester oil, a maleated oil, or a combination thereof. A high ester
oil comprises a polyol capable of comprising greater than three
fatty acid esters per molecule and at least one fatty acid ester.
However, a high ester oil comprising four or more fatty acid esters
per molecule is preferred. Examples of such a polyol include a
pentaerythritiol, a dipentaerythritiol, a tripentaerythritiol, or a
styrene/allyl alcohol copolymer. These high ester oils generally
form films more rapidly than acylglycerol based oil, as the
opportunity for cross-linking reactions between fatty acids
increases with the number of fatty acids attached to a single
polyol. A maleated oil is an oil modified by a chemical reaction
with maleic anhydride. Maleic acid and an unsaturated or
polyunsaturated fatty acid react to produce a fatty acid with
additional acid moieties. A maleated oil generally is more
hydrophilic and/or has a faster film formation time than a
comparative non-maleated oil.
[0401] (2) Alkyd Resins
[0402] In certain embodiments, a binder can comprise an alkyd
resin. In general embodiments, an alkyd-coating may be selected as
an architectural coating, a metal coating, a plastic coating, a
wood coating, or a combination thereof. In certain aspects, an
alkyd coating may be selected for use as a primer, an undercoat, a
topcoat, or a combination thereof. In particular aspects, an alkyd
coating comprises a pigment, an additive, or a combination
thereof.
[0403] An alkyd resin comprises a polyester prepared from a polyol,
a fatty acid, and a polybasic ("polyfunctional") organic acid or
acid anhydride. An alkyd resin is generally produced by first
preparing monoacylpolyol, which is a polyol esterified to one fatty
acid. The monoacylpolyol is polymerized by ester linkages with a
polybasic acid to produce an alkyd resin of desired viscosity in a
solvent. Examples of a polyol include 1,3-butylene glycol;
diethylene glycol; dipentaerythritol; ethylene glycol; glycerol;
hexylene glycol; methyl glucoside; neopentyl glycol;
pentaerythritol; pentanediol; propylene glycol; sorbitol;
triethylene glycol; trimethylol ethane; trimethylol propane;
trimethylpentanediol; or a combination thereof. In certain aspects,
a polyol comprises ethylene glycol; glycerol; neopentyl glycol;
pentaerythritol; trimethylpentanediol; or a combination thereof.
Examples of a polybasic acid or an acid anhydride include adipic
acid, azelaic acid, chlorendic anhydride, citric acid, fumaric
acid, isophthalic acid, maleic anhydride, phthalic anhydride,
sebacic acid, succinic acid, trimelletic anhydride, or a
combination thereof. In certain aspects, a polybasic acid or an
acid anhydride comprises isophthalic acid, maleic anhydride,
phthalic anhydride, trimelletic anhydride, or a combination
thereof. Examples of a fatty acid include abiatic, benzoic,
caproic, caprylic, lauric, linoleic, linolenic, oleic, a
tertiary-butyl benzoic acid, a fatty acid from an oil/fat (e.g.,
castor, coconut, cottonseed, tall, tallow), or a combination
thereof. In certain aspects, a fatty acid comprises benzoic, a
fatty acid from tall oil, or a combination thereof. In specific
aspects, an oil is used in the reaction directly as a source of a
fatty acid and/or a polyol. Examples of an oil include castor oil,
coconut oil, corn oil, cottonseed oil, dehydrated castor oil,
linseed oil, safflower oil, soybean oil, tung oil, walnut oil,
sunflower oil, menhaden oil, palm oil, or a combination thereof. In
some aspects, an oil comprises coconut oil, linseed oil, soybean
oil, or a combination thereof.
[0404] In addition to the standards and analysis techniques
previously described for an oil, standards for physical properties,
chemical properties, and/or procedures for testing the
purity/properties of various fatty acids (e.g., coconut, corn,
cottonseed, dehydrated caster, linseed, soybean, tall oil fatty
acids, rosin fatty acids) and a polyol (e.g., pentaerythritol,
hexylene glycol, ethylene glycol, diethylene glycol, propylene
glycol, dipropylene glycol) and acid anhydrides (e.g., phthalic
anhydride, maleic anhydride) for use in an alkyd or other coating
components are described, for example, in "ASTM Book of Standards,
Volume 06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D1537-60, D1538-60,
D1539-60, D1841-63, D1842-63, D1843-63, D5768-95, D1981-02,
D1982-85, D1980-87, D804-02, D1957-86, D464-95, D465-01, D1963-85,
D5974-00, D1466-86, D2800-92, D1585-96, D1467-89, and D1983-90,
2002; and in "ASTM Book of Standards, Volume 06.04,
Paint--Solvents; Aromatic Hydrocarbons," D2403-96, D3504-96,
D2930-94, D3366-95, D3438-99, D2195-00, D2636-01, D2693-02,
D2694-91, D5164-91, D1257-90, and D1258-95, 2002. Further, the
composition, properties and/or purity of an alkyd resin and/or a
solution comprising an alkyd resin selected for use in a coating
such as phthalic anhydride content, isophthalic acid content,
unsaponifiable matter content, fatty acid content/identification,
polyhydric alcohol content/identification, glycerol, ethylene
glycol and/or pentaerythirol content, and silicon content can be
empirically determined by procedures known to those of ordinary
skill in the art (see, for example, "ASTM Book of Standards, Volume
06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D2689-88, D563-88,
D2690-98, D2998-89, D1306-88, D1397-93, D1398-93, D2455-89,
D1639-90, D1615-60, and D2456-91, 2002).
[0405] (i) Oil Length Alkyd Binders
[0406] In specific embodiments, an alkyd resin may be selected
based on the materials used in its preparation, which typically
affect the alkyd's properties. In general aspects, an alkyd resin
is often classified and/or selected for use in a particular
application by its oil content, as the oil content affects the
alkyd resin properties. Oil content is the amount of oil relative
to the solvent-free alkyd resin. Based on oil content, an alkyd
resin may be classified as a very long oil alkyd resin, a long oil
alkyd resin, a medium oil alkyd resin, or a short oil alkyd resin.
Generally, the greater the oil content classification of an alkyd
resin that is comprised in a coating, the greater the ease of brush
application, the slower the rate of film formation, the greater the
film's flexibility, the poorer the chemical resistance of the film,
the poorer the retention of gloss in exterior environments, or a
combination thereof. A short oil alkyd, a medium oil alkyd, a long
oil alkyd, and a very long oil alkyd has an oil content range of 1%
to 40%, 40% to 60%, 60% to 70%, and 70% to 85%, respectively,
including all intermediate ranges and combinations thereof,
respectively. In typical embodiments, a short oil alkyd, a medium
oil alkyd, a long oil alkyd, and a very long oil alkyd resin and/or
coating comprise 50%, 45% to 50%, 60% to 70%, or 85% to 100%
nonvolatile component, respectively.
[0407] In certain embodiments, a short oil alkyd coating may be
selected as an industrial coating. In certain aspects, a short oil
alkyd is synthesized from an oil, wherein the oil comprises castor,
dehydrated castor, coconut, linseed, soybean, tall, or a
combination thereof. In some aspects, the oil of a short oil alkyd
comprises a saturated fatty acid. Examples of a saturated fatty
acid include, but are not limited to, caproic ("hexanoic," "6:0");
caprylic ("octanoic," "8:0"); lauric ("dodecanoic," "12:0"); or a
combination thereof. In particular facets, a short oil alkyd
coating comprises a solvent, wherein the solvent comprises an
aromatic hydrocarbon, isobutanol, VMP naphtha, xylene, or a
combination thereof. In other facets, the aromatic solvent
comprises a high boiling aromatic solvent. In some aspects, a short
oil alkyd is insoluble or poorly soluble in an aliphatic
hydrocarbon. In further embodiments, a short oil alkyd coating
undergoes film formation by baking.
[0408] In certain embodiments, a medium oil alkyd coating may be
selected as a farm implement coating, a railway equipment coating,
a maintenance coating, or a combination thereof. In certain
aspects, a medium oil alkyd is synthesized from an oil, wherein the
oil comprises linseed, safflower, soybean, sunflower, tall, or a
combination thereof. In some aspects, the oil of a medium oil alkyd
comprises a monounsaturated fatty acid (e.g., oleic acid). In
particular facets, a medium oil alkyd coating comprises a solvent,
wherein the solvent comprises an aliphatic hydrocarbon, an aromatic
hydrocarbon, or a combination thereof.
[0409] In certain embodiments, a tall oil alkyd coating may be
selected as an architectural coating, a maintenance coating, a
primer, a topcoat, or a combination thereof. In certain aspects, a
tall oil alkyd is synthesized from an oil, wherein the oil
comprises linseed, safflower, soybean, sunflower, tall, or a
combination thereof. In some aspects, the oil of a long oil alkyd
comprises a polyunsaturated fatty acid. In particular facets, a
tall oil alkyd coating comprises a solvent, wherein the solvent
comprises an aliphatic hydrocarbon.
[0410] In certain embodiments, a very long oil alkyd coating may be
selected as a latex architectural coating, a wood stain, or a
combination thereof. In certain aspects, a very long oil alkyd is
synthesized from an oil, wherein the oil comprises linseed,
soybean, tall, or a combination thereof. In some aspects, the oil
of a long oil alkyd comprises a polyunsaturated fatty acid. In
particular facets, a very long oil alkyd coating comprises a
solvent, wherein the solvent comprises an aliphatic
hydrocarbon.
[0411] (ii) High Solid Alkyd Coatings
[0412] A high solid alkyd possesses a reduced viscosity, a lower
average molecular weight, or a combination thereof. A high solid
alkyd may be selected for embodiments wherein a reduced quantity
liquid content (e.g., solvent) of a coating is desired. In some
embodiments, a high solid alkyd coating comprises an enamel
coating. In other aspects, a high solid long or very long oil alkyd
coating comprises an architectural coating. In further aspects, a
high solid medium oil alkyd coating comprises a transportation
coating. In further aspects, a high solid short oil alkyd coating
comprises an industrial coating. Additional, various chemical
moieties may be incorporated in an alkyd to modify a property.
Examples of such moieties include an acrylic, a benzoic acid, an
epoxide, an isocyanate, a phenolic, a polyamide, a rosin, a
silicon, a styrene (e.g., a paramethyl styrene), a vinyl toluene,
or a combination thereof. In certain embodiments, a benzoic acid
modified high solid alkyd coating comprises a coating for a tool.
In other embodiments, a phenolic modified high solid alkyd coating
comprises a primer. A silicone modified alkyd coating may be
selected for improved weather resistance, heat resistance, or a
combination thereof. In specific aspects, a silicone modified alkyd
coating may comprise an additional binder capable of cross-linking
with the silicone moiety (e.g., a melamine formaldehyde resin). In
specific facets, a silicone modified alkyd coating may be selected
as a coil coating, an architectural coating, a metal coating, an
exterior coating, or a combination thereof. In certain facets, a
high solid silicon-modified alkyd coating may substitute an
oxygenated compound (e.g., a ketone, an ester) for an aromatic
hydrocarbon liquid component. However, a high solid
silicon-modified alkyd coating, to achieve cross-linking during
film-formation, should comprise an additional binder capable of
cross-linking. In further embodiments, a silicone modified high
solid alkyd coating comprises a maintenance coating, a topcoat, or
a combination thereof.
[0413] (iii) Uralkyd Coatings
[0414] An uralkyd binder ("uralkyd," "urethane alkyd," "urethane
oil," "urethane modified alkyd") is an alkyd binder, with the
modification that compound comprising plurality of diisocyanate
moieties partly or fully replacing the dibasic acid (e.g., phthalic
anhydride) in the synthesis reactions. Examples of an isocyanate
comprising compounds include a 1,6-hexamethylene diisocyanate
("HDI"), a toluene diisocyanate ("TDI"), or a combination thereof.
An uralkyd binder may be selected for embodiments wherein a
superior abrasion resistance, superior resistance to hydrolysis, or
a combination thereof, relative to an alkyd, is desired in a film.
However, an uralkyd binder prepared using TDI often has greater
viscosity in a coating, inferior color retention in a film, or a
combination thereof, relative to an alkyd binder. Additionally, an
uralkyd binder prepared using an aliphatic isocyanate generally
possesses superior color retention to an uralkyd prepared from TDI.
An uralkyd coating tends to undergo film formation faster than a
comparable alkyd binder, due to a generally greater number of
available conjugated double bonds, an increased T.sub.g in an
uralkyd binder prepared using an aromatic isocyanate, or a
combination thereof. A film comprising an uralkyd binder tends to
develop a yellow to brown color. An uralkyd binder is often used in
preparation of an architectural coating such as a varnish, an
automotive refinish coating, or a combination thereof. Examples of
a surface where an uralkyd coating may be applied include a
furniture surface, a wood surface, or a floor surface.
[0415] (iv) Water-Borne Alkyd Coatings
[0416] In general embodiments, an alkyd coating is a solvent-borne
coating. However, an alkyd (e.g., a chemically modified alkyd) may
be combined with a coupling solvent and water to produce a
water-borne alkyd coating. Examples of a coupling solvent that may
confer water reducibility to an alkyd resin includes ethylene
glucol monobutyether, propylene glycol monoethylether, propylene
glycol monopropylether, an alcohol whose carbon content is four
carbon atoms (e.g., s-butanol), or a combination thereof. In
certain embodiments, a water-borne long oil alkyd coating may be
selected as a stain, an enamel, or a combination thereof. In other
embodiments, a water-borne medium oil alkyd coating may be selected
as an enamel, an industrial coating, or a combination thereof. In
further facets, a water-borne medium oil alkyd coating may undergo
film formation by air oxidation. In other embodiments, a
water-borne short oil alkyd coating may be selected as an enamel,
an industrial coating, or a combination thereof. In further facets,
a water-borne short oil alkyd coating may undergo film formation by
baking.
[0417] (3) Oleoresinous Binders
[0418] An oleoresinous binder is a type of binder prepared from
heating a resin and an oil. Examples of a resin typically used in
the preparation of an oleoresinous binder include resins obtained
from a biological source (e.g., a wood resin, a bitumen resin); a
fossil source (e.g., copal resin, a Kauri gum resin, a rosin resin,
a shellac resin); a synthetic source (e.g., a rosin derivative
resin, a phenolic resin, an epoxy resin); or a combination thereof.
An example of an oil typically used in the preparation of an
oleoresinous binder includes a vegetable oil, particularly an oil
that is comprises a polyunsaturated fatty acid such as tung,
linseed, or a combination thereof. The type of resin and oil used
can identify an oleoresinous binder such as a copal-tung
oleoresinous binder, a rosin-linseed oleoresinous binder, etc. An
oleoresinous binder generally are used in clear varnishes such as a
lacquer, as well as in applications as a primer, an undercoat, a
marine coating, or a combination thereof. In addition to the
standards and analysis techniques previously described for an oil,
standards for physical properties, chemical properties, and/or
procedures for testing the purity/properties (e.g., glass
transition temperature, molecular weight, color stability) of a
hydrocarbon resin (e.g., a synthetic source resin) for use in an
oleoresinous binder or other coating component are described, for
example, in "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," E28-99, D6090-99, D6440-01, D6493-99, D6579-00,
D6604-00, and D6605-00, 2002.
[0419] Similar to alkyd resins, oleoresinous binders can be
categorized by oil length as a short oil or long oil oleoresinous
binder, depending whether oil length is 1% to 67% or 67% to 99%
oil, including all intermediate ranges and combinations thereof,
respectively. Short oil oleoresinous binders generally dry fast and
form relatively harder, less flexible films, and are used, for
example, for floor varnishes. Long oil oleoresinous binders
generally dry slower and form relatively more flexible films, and
are used, for example, as an undercoat, exterior varnish, or
combination thereof.
[0420] (4) Fatty Acid Epoxy Esters
[0421] In certain facets, an epoxy coating may be cured by fatty
acid oxidation rather than epoxide moiety or hydroxyl moiety
cross-linking reactions. A fatty acid epoxide ester resin is an
ester of an epoxide resin and a fatty acid, which can be used to
produce an ambient cure coating that undergoes film formation by
oxidative reactions as an oil-based coating. In certain
embodiments, an epoxy resin may be selected with an epoxy
equivalent weight of 800 to 1000, including all intermediate ranges
and combinations thereof. Short, medium, and long oil epoxide ester
resins comprise 30% to 50%, 50% to 70%, or 70% to 90% fatty acid
esterification, including all intermediate ranges and combinations
thereof, respectively, with similar, though sometimes superior,
properties relative to an analogous alkyd. An epoxide ester resin
is inferior in chemical resistance than a film produced by an epoxy
and a curing agent comprising an amine. An epoxy ester resin may be
selected as a substitute for an alkyd, a marine coating, an
industrial maintenance coating, a floor topcoat, or a combination
thereof.
[0422] b. Polyester Resins
[0423] A polyester resin ("polyester," "oil-free alkyd") is a
polyester chemical, other than an alkyd resin, capable as use as a
binder. A polyester resin is chemically very similar to an alkyd,
though the oil content is 0%. Consequently, a polyester-coating
does not form cross-linking bonds by fatty acids oxidation during
thermosetting film formation, but rather is combined with an
additional binder to form a cross-linked film. The selection of a
polyester and additional binder combination is generally determined
by the polyester's crosslinkable moieties. For example, a
hydroxy-terminated polyester is a polyester produced by an
esterification reaction comprising a molar excess of a polyol, and
may be crosslinked with a urethane, an amino resin, or a
combination thereof. A hydroxy-terminated polyester's hydroxyl
moiety may react with a urethane's isocyanate moiety such as at
ambient conditions or low-bake conditions, while such a polyester
generally undergoes film formation at baking temperatures with an
amino resin. In another example, a "carboxylic acid-terminated
polyester" is a polyester produced by an esterification reaction
comprising an molar excess of a polycarboxylic acid, and may be
crosslinked with a urethane, an amino resin, a 2-hydroxylakylamide,
or a combination thereof.
[0424] In general embodiments, a polyester-coating possesses
superior color retention, flexibility, hardness, weathering, or a
combination thereof, relative to an alkyd-coating. In some
embodiments, a polyester resin may be selected to produce a coating
for a metal surface. Generally, a polyester-coating possesses a
superior adhesion property on a metal surface than a thermosetting
acrylic-coating. Often, a polyester-coating is a thermosetting
coating, particularly in embodiments for use upon a metal surface.
However, a polyester-coating generally comprises an ester linkage
that is susceptible to hydrolysis, therefore, applications wherein
such a polyester-coating contacts water is less preferred.
[0425] A polyester resin is generally prepared by an acid catalyzed
esterification of a polyacid (e.g., a polycarboxylic acid, an
aromatic polyacid) and a polyalcohol. A "polyacid" ("polybasic
acid") is a chemical comprising more than one acid moiety.
Typically, a polyacid used in the preparation of a polyester
comprise two acidic moieties, such as, for example, an aromatic
dibasic acid, an anhydride of an aromatic dibasic acid, an
aliphatic dibasic acid, or a combination thereof. Usually, a
polyester resin comprises a plurality of polycarboxylic acids
and/or polyalcohols, and such a polyester resin is known herein as
a "copolyester resin." Examples of polycarboxylic acids commonly
used to prepare a polyester resin includes adipic acid ("AA");
azelic acid ("AZA"); dimerized fatty acid; dodecanoic acid;
hexahydrophthalic anhydride ("HHPA"); isophthalic acid ("IPA");
phthalic anhydride ("PA"); sebacid acid; terephthalic acid;
trimellitic anhydride; or a combination thereof. Examples of a
polyalcohol commonly used to prepare a polyester resin include
1,2-propanediol; 1,4-butanediol; 1,4-cyclohexanedimethanol
("CHDM"); 1,6-hexanediol ("HD"); diethylene glycol; ethylene
glycol; glycerol; neopentyl glycol ("NPG"); pentaerythitol ("PE");
trimethylolpropane ("TMP"); or a combination thereof. In certain
embodiments, a polyester may be selected that has been synthesized
by an acid catalyzed esterification reaction between a plurality of
polyalcohols comprising two hydroxy moieties (a "diol"), a
polyalcohol comprising three hydroxy moieties (a "triol"), and a
dibasic acid. An example of a diol includes
1,4-cyclohexanedimethanol; 1,6-hexanediol; neopentyl glycol; or a
combination thereof. An example of a triol includes
trimethylolpropane. An example of a polyol comprising four hydroxy
moieties (a "tetraol") includes pentaerythitol. In addition to the
standards and analysis techniques previously described for an oil,
an alkyd, a polyol, an acid anhydride standards for physical
properties, chemical properties, and/or procedures for testing the
purity/properties of an polyester are described, for example, in
"ASTM Book of Standards, Volume 06.03, Paint--Pigments, Drying
Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D2690-98 and D3733-93, 2002.
[0426] The selection of a polyacid and/or a polyalcohol often
affects a property of the polyester resin, such as the resistance
of the polyester resin to hydrolysis, and similarly the water
resistance of a coating and/or film comprising such a polyester
resin. In embodiments wherein a polyester-coating is desired with a
superior water resistance property relative to other types of
polyester-coatings, it is preferred that the coating comprises a
polyester prepared with a polyol that is more difficult to
esterify, and thus generally more difficult to hydrolyze. Examples
of such polyols include neopentyl glycol, trimethylolpropane
1,4-cyclohexanedimethanol, or a combination thereof.
[0427] In general embodiments, a polyester-coating is a
solvent-borne coating. However, a polyester suitable for a
water-borne coating is known to one of ordinary skill in the art. A
water-borne polyester-coating generally comprises a polyester
resin, wherein the acid number of the polyester resin is 40 to 60
including all intermediate ranges and combinations thereof, and
wherein the acid moieties have been neutralized by an amine, and
wherein the coating comprises liquid component that comprises a
co-solvent. An additional water-borne binder (e.g., an an amino
resin) may be used to produce thermosetting film formation. In
specific aspects, a water-borne polyester-coating produces a film
of excellent hardness, gloss, flexibility, or a combination
thereof.
[0428] In alternative embodiments, a polyester temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of a polyester that that comprises fewer or no
crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the polyester or additional binder, or a
combination thereof.
[0429] c. Modified Cellulose Binders
[0430] In some embodiments, a chemically modified cellulose
molecule ("modified cellulose," "cellulosic") may be used as a
coating component (e.g., a binder). Cellulose is a polymer of
anhydroglucose monomers that is insoluble in water and organic
solvents. Various chemically modified forms of cellulose with
enhanced solubility have been used as a coating component. Examples
of chemically modified cellulose ("modified cellulose,"
"cellulosic") include a cellulose ester, a nitrocellulose, or a
combination thereof. Examples of a cellulose ester include
cellulose acetate ("CA"), cellulose butyrate, cellulose acetate
butyrate ("CAB"), cellulose acetate propionate ("CAP"), a hydroxy
ethyl cellulose, a carboxy methyl cellulose, cellulose
acetobutyrate, ethyl cellulose, or a combination thereof. A
cellulose ester coating typically produces films with excellent
flame resistance, toughness, clarity, or a combination thereof. In
certain embodiments, a cellulose ester coating is selected as a
topcoat, a clear coating, a lacquer, or a combination thereof. A
cellulose ester is often selected for embodiments wherein the
coating comprises an automotive coating, a furniture coating, a
wood surface coating, cable coating, or a combination thereof. A
cellulose ester coating may be a thermoplastic coating, a
thermosetting coating, or a combination thereof.
[0431] A cellulose ester may be selected by the properties
associated with the degree and/or type of esterification.
Typically, solubility in a liquid component and/or combinability
with an addition binder is increased by partial esterification of
an anhydroglucose's hydroxy moieties. For example, for a cellulose
acetate butyrate, properties such as compatibility, diluent
tolerance, flexibility (e.g., lower T.sub.g), moisture resistance,
solubility, or a combination thereof, increases with greater
butyrate esterification. However, decreased hydroxyl content alters
properties in a cellulose ester. For example, a cellulose acetate
butyrate comprising a hydroxy content of 1% or below has limited
solubility in most solvents, while a hydroxy content of 5% or
greater allows solubility in many alcohols, and the increased
number of hydroxy moieties allows a greater degree of cross-linking
reactions with binders such as, for example, an amino binder, an an
acrylic binder, urethane binder, or a combination thereof. A
cellulose acetate butyrate acrylic-coating may be selected as
lacquers, an automotive coating, a coating comprising a metallic
pigment (e.g., aluminum), or a combination thereof. A cellulose
acetate butyrate acrylic-coating may comprise a liquid component
that comprises greater amounts of an aromatic hydrocarbon solvent
with the selection of a CAB with greater butyrate ester content.
Though not a cellulosic, sucrose esters may be similarly used as
cellulose ester, particularly CAB.
[0432] In some embodiments, in a cellulose ester comprising an
acetyl ester (e.g., comprises cellulose acetate, cellulose acetate
butyrate, cellulose acetate propionate), the acetyl content will
range from 0.1% to 40.5% acetate, including all intermediate ranges
and combinations thereof. In certain aspects, the acetyl content of
a cellulose acetate, a cellulose acetate butyrate, or a cellulose
acetate propionate will range from 39.0% to 40.5%, 1.0% to 30.0%,
or 0.3% to 3.0%, respectively, including all intermediate ranges
and combinations thereof, respectively. In many aspects, in a
cellulose ester comprising a butyryl ester (e.g., cellulose acetate
butyrate), the butyryl content will range from 15.0% to 55.0%
butyryl, including all intermediate ranges and combinations
thereof. In other aspects, in a cellulose ester comprising a
propionyl ester (e.g., cellulose acetate propionate), the propionyl
content will range from 40.0% to 47.0% propionyl, including all
intermediate ranges and combinations thereof. In other embodiments,
the hydroxyl content of a cellulose acetate, a cellulose acetate
butyrate, or a cellulose acetate propionate will range from 0% to
5.0%, including all intermediate ranges and combinations
thereof.
[0433] A nitrocellulose ("cellulose nitrate") resin comprises a
cellulose molecule wherein a hydroxyl moiety has been nitrated. A
nitrocellulose for use in a coating typically comprises an average
of 2.15 to 2.25 nitrates per anhydroglucose monomer, and is soluble
in an ester, a ketone, or a combination thereof. Additionally,
nitrocellulose is soluble in a combination of a ketone, an ester,
and an alcohol and/or hydrocarbon. A nitrocellulose may be selected
as a lacquer, an automotive primer, automotive topcoat, a wood
topcoat, or a combination thereof. Nitrocellulose coatings are
typically a thermoplastic coating.
[0434] Standard procedures for determining physical and/or chemical
properties (e.g., acetyl content, ash, apparent acetyl content,
butyryl content, carbohydrate content, carboxyl content, color and
haze, combined acetyl, free acidity, heat stability, hydroxyl
content, intrinsic viscosity, solution viscosity, moisture content,
propionyl content, sulfur content, sulfate content, metal content),
of a cellulose and/or a modified cellulose (e.g., cellulose
acetate, cellulose acetate propionate, cellulose acetate butyrate,
methylcellulose, sodium carboxymethylcellulose, ethylcellulose,
hydroxypropyl methylcellulose, hydroxyethylcellulose,
hydroxypropylcellulose) have been described, for example, in "ASTM
Book of Standards, Volume 06.03, Paint--Pigments, Drying Oils,
Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D1695-96 D817-96, D871-96, D1347-72, D1439-97, D914-00,
D2363-79, D2364-01, D5400-93, D1343-95, D1795-96, D2929-89,
D3971-89, D4085-93, D1926-00, D4794-94, D3876-96, D3516-89,
D5897-96, D5896-96, D6188-97, D1348-94, and D1696-95, 2002.
Specific procedures for determining purity/properties of a
nitrocellulose (e.g., nitrogen content) have been described, for
example, in "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D301-95 and D4795-94, 2002.
[0435] In alternative embodiments, a modified cellulose temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of a modified cellulose that that comprises
fewer or no crosslinkable moieties, selection of an addition binder
that comprises fewer or no crosslinkable moieties, reducing the
concentration of the modified cellulose or additional binder, or a
combination thereof.
[0436] d. Polyamide and Amidoamine Binders
[0437] A polyamide ("fatty nitrogen compound," "fatty nitrogen
product") is a reaction product of a polyamine and a dimerized
and/or trimerized fatty acid. In typical embodiments, a polyamide
is an oligomer. An amide resin comprises a terminal amine moiety
capable of cross-linking with an epoxy moiety, and it is
particularly preferred that a polyamide binder is combined with an
epoxide binder. In other aspects, a polyamide may be considered an
additive (e.g., a curing agent, a hardening agent, a coreactant) of
an epoxide coating. A polyamine-epoxy coating may be used as an
industrial coating (e.g., an industrial maintenance coating), a
marine coating, or a combination thereof. A polyamide-epoxide
coating may be applied to a surface such as, for example, wood,
masonry, metal (e.g., steel), or a combination thereof. However, it
is preferred that any surface is thoroughly cleaned prior to
application to promote adhesion. Such surface preparation are well
known to those of ordinary skill in the art, and include, for
example, removal of rust, degraded film, grease, etc. A
polyamide-epoxy coating typically is a solvent-borne coating.
Examples of solvents for a polyamide include an alcohol, an
aromatic hydrocarbon, a glycol ether, a ketone, or a combination
thereof. In certain embodiments, a polyamide-epoxy coating may
comprise a two-pack coating, wherein coating component(s)
comprising the polyamide resin are stored in one container, and
coating components comprising the epoxy resin are stored in a
second container. Such a two-pack coating is admixed immediately
before application, as the stoichiometric mix ratio of resin is
formulated to promote a rapid cure. However, in other embodiments,
a polyamide-epoxy coating may be a single container coating. Such a
solvent-borne polyamine-epoxy coating may be formulated for a
storage life of a year or more. An aluminum and or stainless steel
container is suitable, though a carbon steel container may alter
coating and/or film color. However, such a coating typically
undergoes film formation in stages, wherein the liquid component is
physically lost by evaporation while thermosetting produces a
physically durable film in about 8 to 10 hours, a chemically
resistant film in three to four days, and final cross-linking
completed in about three weeks. In some embodiments, a
polyamine-epoxy coating may undergo chalking upon exterior
weathering.
[0438] Though a polyamide is prepared from a fatty acid, it is not
classified as an oil-based binder herein due to the chemistry of
film formation for polyamide binder. The dimerized ("dibasic") or
trimerized fatty acid generally comprises a polyunsaturated fatty
acid, a monounsaturated fatty acid, or a combination thereof. In
certain aspects, the fatty acid is a linseed oil fatty acid,
soybean oil fatty acid, tall oil fatty acid, or a combination
thereof. In specific facets, the fatty acid is an 18-carbon fatty
acid. However, to reduce the volatile organic compounds of
solvent-borne coating, a polyamide binder may be partly or fully
substituted, such as 0% to 100% substitution, including all
intermediate ranges and combinations thereof, with an amidoamine
binder. An amidomine binder differs from a polyamide binder by the
use of a fatty acid rather than a dimerized fatty acid in the
synthesis of the resin. The selection of the polyamine in the
preparation of a polyamide can affect the properties of the
polyamide. The polyamine may be linear (e.g., diethylenetriamine),
branched or cyclic (e.g., aminoethylpiperazine). Standards for
physical properties, chemical properties, and/or procedures for
testing the purity/properties (e.g., amine value) of a polyamide
and/or an amidoamine are described, for example, in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D2071-87, D2073-92, D2082-92, D2072-92, D2074-92, D2075-92,
D2076-92, D2077-92, D2078-86, D2079-92, D2080-92, D2081-92, and
D2083-92, 2002.
[0439] In general embodiments, a polyamine comprises a polyethylene
amine. A polyamide produced from diethylenetriamine can be prepared
to comprise a varying amount, typically 35% to 85%, including all
intermediate ranges and combinations thereof, of an imidazoline
moiety. In other embodiments, the amount of amine moiety capable of
cross-linking with an epoxy moiety may vary from 100 to 400 amine
value, including all intermediate ranges and combinations thereof.
However, the amine value is converted into units known as "active
hydrogen equivalent weight," which varies from 550 to 140,
including all intermediate ranges and combinations thereof, for
comparison to the epoxy resins epoxide equivalent weight for
determining the stoichiometric mix ratio of a polyamide-epoxy
combination. The stoichiometric mix ratio affects coating and film
properties. As the polyamide to epoxy stoichiometric mix ratio
increases from a ratio of less than one to a ratio of greater than
one, properties such as excellent impact resistance, excellent
chemical resistance, or a combination thereof, decrease while film
flexibility increases. Examples of polyamide to epoxy
stoichiometric mix ratio include 2:1 to 1:2, including all
intermediate ranges and combinations thereof.
[0440] In alternative embodiments, a polyamide and/or amidoamine
temporary coating (e.g, a non-film forming coating) may be
produced, for example, by selection of a polyamide and/or
amidoamine that that comprises fewer or no crosslinkable moieties,
selection of an addition binder that comprises fewer or no
crosslinkable moieties, reducing the concentration of the polyamide
and/or amidoamine or additional binder, selection of a
stoichiometric ratio that is less suitable for crosslinking
reactions, or a combination thereof.
[0441] e. Amino Resins
[0442] An amino resin ("amino binder," "aminoplast," "nitrogen
resin") is a reaction product of formaldehyde, an alcohol and a
nitrogen compound such as, for example, urea, melamine ("1:3:5
triamino triazine"), benzoguanamine, glucoluril, or a combination
thereof. An amino resin may be used to a thermosetting coating. An
amino resin comprises an alkoxymethyl moiety capable of
cross-linking with a hydroxyl moiety of an additional binder such
as an acrylic binder, an alkyd resin, a polyester binder, or a
combination thereof, and it is preferred that an amino resin is
combined with a binder that comprises a hydroxyl moiety in a
coating. In aspects wherein the coating comprises an amino resin
and an alkyd resin, it is preferred that the amino:alkyd resin
ratio is 1:1 to 1:5, including all intermediate ranges and
combinations thereof. An amino resin coating typically is a
solvent-borne coating. Examples of solvents for an amino resin
include an alcohol (e.g., butanol, isobutanol, methanol,
isopropanol), a ketone, hydroxyl functional glycol ether, or a
combination thereof. Additionally, an amino resin generally
possesses limited solubility in a hydrocarbon (e.g., xylene), which
may be added to a solvent-borne coating's liquid component. In
certain aspects, an amino resin coating may be a water-borne
coating, wherein, water is a solvent for an amino resin comprising
a plurality of methylol moieties. In other embodiments, a
water-borne amino resin coating may comprise a water-reducible
coating, particularly wherein the liquid component comprises a
glycol ether, an alcohol, or a combination thereof. In certain
embodiments, an amino coating comprises an acid catalyst.
[0443] An amino resin coating generally is cured by baking at a
temperature of 82.degree. C. and 204.degree. C., including all
intermediate ranges and combinations thereof. Baking generally
promotes reactions between amino resins, though it does improve the
reaction rate between an amino resin and an additional binder. It
is preferred that in embodiments wherein the coating comprises an
additional binder, the additional resin comprises less hydroxyl
moieties and/or the amino resin is polar amino resin (e.g., a
conventional amino resin) a when cured by baking than embodiments
wherein an acid catalyst is used. An amino resin coating undergoes
rapid film formation, typically lasting 30 seconds and 30 minutes,
wherein a higher temperature and/or acid catalyst shortens film
formation time. An amino resin prepared from urea is generally
undergoes film formation faster than an amino resin prepared from
melamine. However, an amino resin coating generally produces an
alcohol (e.g., methanol, butanol) and formaldehyde during film
formation as byproducts.
[0444] An amino resin for use in a coating may be classified by
content of a liquid component (e.g., a solvent) as a high solids
amino resin or a conventional amino resin. The liquid component is
generally used to reduce the viscosity of the resin for coating
preparation. A high solids amino resin comprises 80% to 100%, by
weight, an amino resin, with the balance a liquid component. A high
solids amino resin is are relatively less polar, less polymeric,
lower in viscosity, or a combination thereof, relative to a
conventional amino resin. The lower viscosity allows the use of
little or no liquid component. Additionally, a high solids amino
resin may be water-soluble and/or water reducible. A conventional
amino resin comprises less than 80% amino resin, by weight, with
the balance a liquid component. Properties of a high solids or
conventional amino resin selected for use in a coating such as the
amount of amino resin and liquid component, the amount of unreacted
formaldehyde in the resin preparation, the viscosity of the resin,
the ability of the resin to accept additional liquid component as a
solvent, can be empirically determined by procedures known to those
of ordinary skill in the art (see, for example, "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D4277-83, D1545-98, D1979-97, and D1198-93, 2002; and "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D2369-01e1, 2002).
[0445] In embodiments wherein an amino resin coating comprise an
amino resin prepared from urea, the coating may be used as wood
coating (e.g., furniture coating), an industrial coating (e.g., an
appliance coating), an automotive primer, a clear coating, or a
combination thereof. However, an amino resin film, wherein the
resin was prepared from urea, generally produces a film with poor
resistance to moisture, and is preferred as an internal coating
and/or as part of a multicoat system. In certain embodiments, an
amino resin prepared from melamine, generally produces films with
good resistance to moisture, temperature, UV irradiation, or a
combination thereof. A melamine-based amino coating may be applied
to a metal surface. In specific aspects, such a melamine amino
resin coating may be an automotive coating, a coil coating, a metal
container coating, or a combination thereof. In embodiments wherein
an amino resin coating comprise an amino resin prepared from
benzoguanamine, the film produced generally possesses poor
weathering resistance, good corrosion resistance, water resistance,
detergent resistance, flexibility, hardness, or a combination
thereof. A benzoguanamine amino resin may be used as an industrial
coating, particularly for indoor applications (e.g., an appliance
coating). In embodiments wherein an amino resin coating comprise an
amino resin prepared from, glycoluril, a higher baking temperature
and/or acid catalyst may be used during film formation, but less
byproducts may be released. A glycoluril-based amino-coating
typically produces a film with excellent corrosion resistance,
humidity resistance, or a combination thereof. A glycoluril-based
amino-coating may be selected as a metal coating.
[0446] In alternative embodiments, an amino resin temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of an amino resin that that comprises fewer or no
crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the amino resin and/or additional binder,
selection of a binder ratio that is less suitable for crosslinking
reactions, using a bake cured amino resin coating at temperatures
less than is needed for curing (e.g., ambient conditions) or a
combination thereof.
[0447] f. Urethane Binders
[0448] A urethane binder ("polyurethane binder," "urethane,"
"polyurethane") is a binder comprising prepared from compounds that
comprise an isocyanate moiety. The urethane binder's urethane
moiety can form intermolecular hydrogen bonds between urethane
binder polymers, and these non-covalent bonds confer useful
properties in a coating or film comprising an urethane binder. The
hydrogen bonds can be broken by mechanical stress, but will reform,
thereby conferring a property of abrasion resistance. Additionally,
a urethane binder can form some hydrogen bonds with water,
conferring a plasticizing property to the coating. In certain
embodiments, a urethane binder comprises an isocyanate moiety. The
isocyanate moiety is highly reactive (e.g., crosslinkable) with a
moiety comprising a chemically reactive hydrogen. Examples of a
chemically reactive hydrogen moiety include a hydroxyl moiety, an
amine moiety, or a combination thereof. Examples of an additional
binder include a polyol, an amine, an epoxide, silicone, vinyl,
phenolic, or a combination thereof. In certain embodiments, a
urethane coating is a thermosetting coating. In specific aspects, a
urethane coating comprises a catalyst (e.g., dibutyltin dilaurate,
stannous octoate, zinc octoate). In specific facets, the coating
comprises 10 to 100 parts per million catalyst, including all
intermediate ranges and combinations thereof. In some embodiments,
such a coating will undergo film formation at ambient conditions or
slightly greater temperatures. A binder comprising an isocyanate
moiety is often selected to produce a coating with durability in an
external environment. A urethane coating typically possesses good
flexibility, toughness, abrasion resistance, chemical resistance,
water resistance, or a combination thereof. An aliphatic urethane
coating may be selected for the additional property of good
lightfastness.
[0449] In general embodiments, a urethane binder may be selected
based on the materials used in its preparation, which typically
affect the urethane binder's properties. An example of a urethane
binder includes an aromatic isocyanate urethane binder, an
aliphatic isocyanate urethane binder, or a combination thereof.
Aliphatic isocyanate urethane binders are often selected for
embodiments wherein a superior exterior durability, color
stability, good lightfastness, or a combination thereof relative to
an aromatic isocyanate binder is desired. Examples of an aliphatic
isocyanate urethane binder includes a hydrogenated
bis(4-isocyanatophenyl)methane ("4,4'dicyclohexylmethane
diisocyanate," "HMDI"), HDI, a combination of 2,2,4-trimethyl
hexamethylene diisocyanate and 2,4,4-trimethyl hexamethylene
diisocyanate ("TMHDI"), 1,4-cyclohexane diisocyanate ("CHDI"),
isophorone diisocyanate ("3-isocyanatomethyl-3,5,5-
-trimethylcyclohexyl isocyanate," "IPDI"), or a combination
thereof. In certain aspects, a HDI derived binder is prepared from
excess HDI reacted with water, known as "HDI biuret." In certain
aspects, a HDI derived binder may be prepared from a
1,6-hexamethylene diisocyanate isocyanurate, wherein such a HDI
derived binder produces a coating with generally superior heat
resistance and/or exterior durability is desired relative to other
HDI derived binders. As would be known to one of ordinary skill in
the art, standards for physical properties, chemical properties,
and/or procedures for testing the purity/properties of urethane
precursor components (e.g., toluene) and urethane resins (e.g.,
isocyanate moieties) for use in a coating are described, for
example in "ASTM Book of Standards, Volume 06.04, Paint--Solvents;
Aromatic Hydrocarbons," D5606-01, 2002; and "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D3432-89 and D2572-97, 2002.
[0450] In certain embodiments, a urethane coating comprises a
urethane binder capable of a self-crosslinking reaction. An example
is a moisture-cure urethane, which comprises an isocyanate moiety.
Contact between an isocyanate moiety and a water molecule produces
an amine moiety capable of bonding with an isocyanate moiety of
another urethane binder molecule in a linear polymerization
reaction. In certain aspects, a moisture cure urethane coating is
baked at 100.degree. C. to 140.degree. C., including all
intermediate ranges and combinations thereof, to promote
crosslinking reactions between the linear polymers. In certain
embodiments, a moisture-cure urethane coating is a solvent-borne
coating. In specific aspects, a moisture-cure urethane coating
comprises a dehydrator. In general aspects, moisture-cure urethane
coating typically is a one-pack coating, prepared for storage of
the coating in anhydrous conditions.
[0451] In certain embodiments, an urethane coating comprises a
blocked isocyanate urethane binder, wherein the isocyanate moiety
has been chemically modified by a hydrogen donor to be inert until
contacted with a baking temperature. Such a blocked isocyanate
urethane coating typically is a one-pack coating, as it is designed
for stability at ambient conditions. Additionally, a blocked
isocyanate urethane coating may be a powder coating.
[0452] In certain embodiments, a urethane coating comprises an
additional binder. In certain embodiments, a urethane may be
combined with a binder such as an amine, an epoxide, silicone,
vinyl, phenolic, a polyol, or a combination thereof, wherein the
binder comprises a reactive hydrogen moiety. In specific
embodiments, selection of a second binder to crosslink with the
urethane binder affects coating and/or film properties. In certain
aspects, a coating comprising a urethane and an epoxide, vinyl,
phenolic, or a combination thereof produces a film with good
chemical resistance. In other aspects, a coating comprising a
urethane and a silicone produces a coating with good thermal
resistance. In some aspects, a coating comprises a urethane and a
polyol. A primary hydroxyl moiety, secondary hydroxyl moiety, and
tertiary hydroxyl moiety of a polyol are respectively the fastest,
moderate, and slowest to react with a urethane. Steric hindrance
from a neighboring moiety may slow the reaction with a hydroxyl
moiety. In an additional example, use of a polyol may increase
flexibility of a urethane coating. Often, a selected polyol has a
molecular weight from 200 Da to 3000 Da, including all intermediate
ranges and combinations thereof. Generally, a lower molecular
weight polyol increases the hardness property, lowers the
flexibility property, or a combination thereof, of a urethane
polyol film. Examples of a polyol include a glycol, a triol (e.g.,
1,4-butane-diol, diethylene glycol, trimethylolpropane), a tetraol,
a polyester polyol, a polyether polyol, an acrylic polyol, a
polylactone polyol, or a combination thereof. Examples of a
polyether polyol include a poly (propylene oxide) homopolymer
polyol, a poly (propylene oxide) and ethylene oxide copolymer
polyol, or a combination thereof.
[0453] In certain embodiments, a urethane binder comprises a
thermoplastic urethane binder. Typically, a thermoplastic urethane
binder is from 40 kDa to 100 kDa, including all intermediate ranges
and combinations thereof. In particular aspects, a thermoplastic
urethane binder comprises little or no isocyanate moieties. In
general aspects, a thermoplastic urethane coating is a solvent
borne coating. In specific facets, a thermoplastic urethane coating
is a lacquer, a high gloss coating, or a combination thereof.
[0454] In certain embodiments, a urethane binder is an urethane
acrylate ("acrylated urethane") binder. An urethane acrylate binder
generally comprises an acrylate moiety at an end of the polymeric
binder. The acrylate moiety is typically part of an acrylate
monomer, wherein the monomer comprises a hydroxyl moiety (e.g., a
2-hydroxy-ethyl acrylate). An urethane acrylate coating generally
comprises another binder for crosslinking reactions. Examples of a
suitable binder include a triacrylate (e.g., teimethylolpropane). A
urethane acrylate coating generally also comprises a viscosifier,
wherein the viscosifier reduces viscosity. Examples of such a
viscosifer include an acrylate monomer, a N-vinyl pyrrolidone, or a
combination thereof. A urethane acrylate coating is cured by
irradiation. Examples of irradiation include UV light, electron
beam, or a combination thereof. In embodiments wherein UV light is
a curing agent, a urethane acrylate coating typically comprises a
photoinitiator. Examples of a suitable initiator include
2,2,-diethoxyacetophenone, a combination of benzophenone and an
amine synergist, or a combination thereof. In specific facets, an
urethane acrylate coating is applied to a plastic surface. In other
facets, an urethane acrylate coating floor coating, an electronic
circuit board coating, or a combination thereof.
[0455] In alternative embodiments, a urethane temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of a urethane resin that that comprises fewer or no
crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the a urethane resin and/or additional binder,
using a bake cured a urethane resin coating at temperatures less
than is needed for curing (e.g., ambient conditions), selection of
size range for a thermoplastic urethane resin coating that is less
suitable for film formation (e.g., 1 kDa to 40 kDa), or a
combination thereof.
[0456] (1) Water-Borne Urethanes
[0457] The previous discussion of urethane coatings focused on
solvent-borne urethane coating. A water-borne urethane coating
typically is comprises a water-dispersible urethane binder such as
a cationic modified urethane binder and/or anionic modified
urethane binder. A cationic modified urethane binder is a urethane
binder chemically modified by an diol comprising an amine, such as,
for example, diethanolamine, methyl diethanolamine,
N,N-bis(hydroxyethyl)-.alpha.-amin- opyridine, lysine,
N-hydroxyethylpiperidine, or a combination thereof. An anionic
modified urethane binder is a urethane binder chemically modified
by an diol comprising a carboxylic acid such as dimethylolpropionic
acid (2,2-bis(hydroxymethyl) propionic acid), dihydroxybenzoic
acid, and/or a sulfonic acid (e.g.,
2-hydroxymethyl-3-hydroxy-propanesulfonic acid), or a combination
thereof.
[0458] (2) Urethane Powder Coatings
[0459] A urethane powder coating refers to a polyester and/or
acrylic coating, wherein the binder has been modified to comprise a
urethane moiety. Such a coating is typically a thermosetting, bake
cured coating, an industrial coating (e.g., an appliance coating),
or a combination thereof.
[0460] g. Phenolic Resins
[0461] A phenolic resin ("phenolic binder," "phenolic") is reaction
product of a phenolic compound and an aldehyde. A preferred
aldehyde is formaldehyde, and such a phenolic resin is known as a
"phenolic formaldehyde resin" ("PF resin"). The properties of a
phenolic resin are affected by the phenolic compound and reaction
conditions used during synthesis. A resole resin ("resole
phenolic") is prepared by a reaction of a molar excess of a
phenolic compound with formaldehyde under alkaline conditions. A
novolac resin ("novolac phenolic") is prepared by a reaction of a
molar excess of formaldehyde with a phenolic compound under acidic
conditions. Examples of phenolic compounds used in preparing a
phenolic resin include phenol; orthocresol ("o-cresol");
metacresol, paracresol ("p-cresol"); a xylenol (e.g., 4-xylenol);
bisphenol-A ["2,2-bis (4-hydroxylphenyl) propane"; "diphenylol
propane"); p-phenylphenol; p-tert-butylphenol; p-tert-amylphenol;
p-tert-octyl phenol; p-nonylphenol; or a combination thereof. As
would be known to one of ordinary skill in the art, standards for
physical properties, chemical properties, and/or procedures for
testing the purity/properties of various compounds used in phenolic
resins (e.g., bisphenol A, a phenol, a cresol, formaldehyde) for
use in a coating are described, for example in "ASTM Book of
Standards, Volume 06.04, Paint--Solvents; Aromatic Hydrocarbons,"
D6143-97, D3852-99, D4789-94, D2194-02, D2087-97, D2378-02,
D2379-99, D2380-99, D1631-99, D6142-97, D4493-94, D4297-99, and
D4961-99, 2002. As would be known to one of ordinary skill in the
art, standards for physical properties, chemical properties, and/or
procedures for testing the purity/properties of phenolic resins for
use in a coating are described, for example in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D1312-93, D4639-86, D4706-93, D4613-86 and D4640-86, 2002.
[0462] In alternative embodiments, a phenolic resin temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of a phenolic resin that that comprises fewer
or no crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the a phenolic resin and/or additional binder,
using a bake cured a phenolic resin coating at temperatures less
than is needed for curing (e.g., ambient conditions), or a
combination thereof.
[0463] (1) Resole
[0464] A resole resin is the more commonly used PF resin. A
solvent-borne phenolic formaldehyde coating typically comprises an
alcohol, an ester, a glycol ether, a ketone, or a combination
thereof, as a PF solvent. However, a phenolic resin prepared from
phenolic compound comprising an alkyd moiety, such as, for example,
p-tert-butyl phenol p-tert-amyl phenol p-tert-octyl phenol, or a
combination thereof, typically has solubility in an aromatic
compound and/or able to tolerate an aliphatic diluent. Often, a
phenolic-resin coating comprises an additional binder such as an
alkyd resin, an amino resin, a blown oil, an epoxy resin, a
polyamide, a polyvinyl resin [e.g., poly(vinyl butyral)], or a
combination thereof. An example of a phenolic-resin coating
includes a varnish, an industrial coating, or a combination
thereof. A phenolic resin-coating may be selected for embodiments
wherein a film possessing solvent resistance, corrosion resistant,
of a combination thereof, is desired. Examples of surfaces wherein
such properties are often desirable include a surface of a metallic
container (e.g., a can, a pipeline, a drum, a tank), a coil
coating, or a combination thereof. In specific aspects, a phenolic
coating produces a film 0.2 to 1.0 mil thick, including all
intermediate ranges and combinations thereof. In specific aspects,
coating comprising a phenolic-binder and additional binder
undergoes thermosetting cross-linking reactions between the binders
during film formation. In certain embodiments, a phenolic-resin
coating undergoes cure by baking, such as, for example, 135.degree.
C. to 204.degree. C., including all intermediate ranges and
combinations thereof. In specific aspects, a baking cure time is
one minute to four hours, with shorter cure times at high
temperatures. A phenolic-resin film generally possesses excellent
hardness property (e.g., glass-like), excellent resistance to
solvents, water, acids, salt, electricity, heat resistance, as well
as thermal resistance up to 370.degree. C. for a period of
minutes.
[0465] However, a phenolic-resin film is poorly resistant to alkali
unless made from a coating that also comprised an epoxy binder. In
certain embodiments, a phenolic-epoxy coating comprises a binder
ratio of 15:85 to 50:50 phenolic binder:epoxy binder, including all
intermediate ranges and combinations thereof. In certain aspects, a
phenolic-epoxy coating possesses superior flexibility, toughness,
or a combination thereof relative to a phenolic coating. In
specific facets, a phenolic-epoxy coating is cured at 200.degree.
C. for 10 to 12 minutes.
[0466] In other aspects, a phenolic coating comprises a blown oil,
an alkyd, or a combination thereof. In some aspects, such a coating
comprises a phenolic resin prepared from p-tert-butylphenol
p-tert-amylphenol p-tert-octyl phenol, or a combination thereof. In
specific aspects, such a coating is applied to electrical coil,
electrical equipment, or a combination thereof.
[0467] (2) Novolak
[0468] In other aspects, wherein a film is desired, it novolak
coating may be used. However, a novolak resin is generally a
non-film forming resin. In is particularly preferred that the
coating comprise an epoxy resin. It is also preferred that the
coating comprise a basic catalyst. A film produced from such a
novolak-epoxy coating typically possesses good resistance to
chemicals, water, heat, or a combination thereof. In specific
facets, a novolak-epoxy coating may be a high solids coating, a
powder coating, a pipeline coating, or a combination thereof.
[0469] A novolak resin prepared from phenolic compound comprising
an alkyd moiety such as p-tert-butylphenol p-tert-amylphenol
p-tert-octyl phenol, or a combination thereof, typically has
solubility in an oil. Additionally, a PF resin may be modified by
reaction with an oil to produce an oil modified PF resin, which is
also oil soluble. An alkyd phenol-formaldehyde resin, an oil
modified phenol-formaldehyde resin, is generally a non-film forming
resin. A coating capable of producing a film may be formulated by
combining such a resin with a drying oil, an alkyd, or a
combination thereof. In specific aspects, an alkyd
phenol-formaldehyde resin, an oil modified phenol-formaldehyde
resin undergoes cross-linking with an oil and/or an alkyd. Such a
coating may further comprise a liquid component (e.g., a solvent),
a drier, a UV absorber, an anti-skinning agent, or a combination
thereof. In certain facets, such a coating undergoes film formation
under ambient conditions or by baking. In particular aspects, such
a coating comprises a varnish, a wood coating, or a combination
thereof. In specific facets, such a coating comprises a
pigment.
[0470] h. Epoxy Resins
[0471] An epoxy resin ("epoxy binder," "epoxy") is a compound
comprising an epoxide ("oxirane") moiety. An epoxide resin may be
used in a thermosetting coating, thermoplastic coating, or a
combination thereof. An epoxide coating typically is a solvent
borne coating, though examples of a water-borne and powder epoxy
coating are described herein. An epoxide coating generally
possesses excellent properties of adhesion, corrosion resistance,
chemical resistance, or a combination thereof. An epoxide coating
may be selected for various surfaces, particularly a metal
surface.
[0472] An epoxide resin (e.g., a bisphenol A epoxy resin) generally
comprises one or two epoxide moieties per resin molecule. An
epoxide resin may additionally comprise a monomer, oligomer, or
polymer of repeating chemical units, each generally lacking an
epoxide moiety, but comprising a hydroxy moiety. The number of
monomer(s) present is expressed "n" value, wherein an average
increase of one monomer per epoxide resin molecule increase the n
value by one. The chemical and/or physical properties of an epoxide
resin are affected by the n value. For example, as the n value
increases, the chemical reactions selected for film formation in a
thermosetting coating may become more dominated by reactions with
the increasing numbers of hydroxyl moieties, and less dominated by
the epoxide moieties. Often, an epoxide resin is classified by an
epoxide equivalent weight, which is the grams of resin required to
provide 1 M epoxide moiety equivalent. In certain embodiments, the
epoxide equivalent weight is 182 to 3050, including all
intermediate ranges and combinations thereof. Additionally, an
epoxide resin may be used in a thermoplastic coating, particularly
wherein the n value is greater than 25. In certain embodiments, an
epoxide resin may possess an n value of 0 to 250, including all
intermediate ranges and combinations thereof. As would be known to
one of ordinary skill in the art, standards for physical
properties, chemical properties, and/or procedures for testing the
purity/properties of epoxy resins (e.g., epoxy moiety content) for
use in a coating are described, for example in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D4142-89, D1652-97, D1726-90, D1847-93, and D4301-84, 2002.
[0473] An epoxide moiety is chemically reactive with a variety of
other moieties, such as, for example, an amine, a carboxyl, a
hydroxyl or a phenol. An epoxide coating may comprise an additional
binder capable of undergoing a cross-linking reaction with the
epoxide during film formation. Various such additional binders are
known to those of ordinary skill in the art, and are often referred
to as a "curing agent" or "hardener." The selection of a curing
agent and/or an epoxide can affect whether the coating undergoes
film formation at ambient conditions or by baking.
[0474] In alternative embodiments, an epoxide resin temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of an epoxide resin that that comprises fewer
or no crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the an epoxide resin and/or additional binder,
using a bake cured an epoxide resin at temperatures less than is
needed for curing (e.g., ambient conditions), not irradiating the
coating, or a combination thereof.
[0475] (1) Ambient Condition Curing Epoxies
[0476] In certain embodiments, a curing agent suitable for curing
at ambient conditions comprises an amine moiety such as a polyamine
adduct, which is an epoxy resin modified to comprise an amine
moiety, a polyamide, a ketimine, an aliphatic amine, or a
combination thereof. Examples of an aliphatic amine include
ethylene diamine ("EDA"), diethylene triamine ("DETA"), triethylene
tetraamine ("TETA"), or a combination thereof. Selection of a
polyamine adduct generally produces a film with excellent solvent
resistance, corrosion resistance, acid resistance, flexibility,
impact resistance, or a combination thereof. Selection of a
polyamide generally produces a film with superior adhesion,
particularly to a moist or poorly prepared surface, good solvent
resistance, excellent corrosion resistance, good acid resistance,
superior flexibility retention, superior impact resistance
retention, or a combination thereof. A ketimine is a reaction
product of a primary amine and a ketone, and produces a coating
and/or film with similar properties as a polyamine or amine adduct.
However, the pot life is longer with a ketimine, and moisture
(e.g., atmospheric humidity) activates this cure agent. Examples of
an epoxide selected for curing at ambient conditions includes a low
mass epoxide resins with an n value from 0 to 2.0, including all
intermediate ranges and combinations thereof. In certain
embodiments, an epoxy resin may be selected with an epoxy
equivalent weight of 182 to 1750, including all intermediate ranges
and combinations thereof. In specific aspects, the greater the n
value of an epoxide resin, the longer the pot life in a two-pack
coating, the greater the coating leveling property, the lower the
film solvent resistance, the lower the film chemical resistance,
the greater the film flexibility, or a combination thereof. In
certain aspects, an ambient curing epoxide coating is a two-pack
coating, wherein the epoxide resin is in one container and the
curing agent in a second container. In typical aspects, the pot
life upon admixing the coating components is two hours to two days.
An ambient cure epoxide may be selected for an industrial coating
(e.g., industrial maintenance coating), a marine coating, an
aircraft primer, a pipeline coating, a HIPAC, or a combination
thereof.
[0477] (2) Bake Curing Epoxies
[0478] In other embodiments, a curing agent suitable for curing by
baking includes an amino resin (e.g., a urea or melamine-based
amino resin), a phenolic resin, or a combination thereof. Since
baking is generally needed to promote film formation, an epoxy
coating comprising such a curing agent typically is a one-pack
coating. In certain embodiments, an epoxy resin may be selected
with an epoxy equivalent weight of 1750 to 3050, including all
intermediate ranges and combinations thereof. An epoxy resin
coating that comprises an amino resin cure agent typically is
selected for a lower cure temperature. Such a coating may be
selected as a can coating, a metal coating, an industrial coating
(e.g., equipment, appliances), or a combination thereof. An epoxy
coating comprises an phenolic resin cure agent typically possesses
greater chemical resistance and/or solvent resistance, and is
typically selected for a can coating, a pipeline coating, a wire
coating, an industrial primer, or a combination thereof. Examples
of an epoxide selected for curing by baking includes a higher mass
epoxide resins with an n value from 9.0 to 12.0, including all
intermediate ranges and combinations thereof. In certain
embodiments, a heat-cured epoxy coating is a water-borne coating.
Such a water-borne coating comprises a higher mass epoxide resin
modified to comprise a terpolymer that comprises monomers of
styrene, methacrylic, acrylate, or a combination thereof, and an
amino resin, a phenolic resin, or a combination thereof. Such a
water-borne coating is typically selected as a can coating.
[0479] (3) Electrodeposition Epoxies
[0480] Another example of a water-borne epoxide coating is an
electrodeposition epoxy coating. In certain embodiments, an epoxy
resin may be selected with an epoxy equivalent weight of 500 to
1500, including all intermediate ranges and combinations thereof.
An anionic and/or cationic epoxy resin is electrically attracted to
a surface for application. The surface removed from the coating
bath, and the coating is baked cured into a film upon the surface.
Such a water-borne coating may be selected for an automotive
primer, described elsewhere herein.
[0481] (4) Powder Coating Epoxies
[0482] An epoxy coating may be a powder coating, wherein the
various nonvolatile coating components are admixed. Examples of
typical admixed components include an epoxy resin, a curing agent,
and a pigment, an additive, or a combination thereof. In certain
embodiments, an epoxy resin may be selected with an epoxy
equivalent weight of 550 to 750, including all intermediate ranges
and combinations thereof. The mixture is then melted, cooled, and
powderized. The powder coating is typically applied by attraction
to an electrostatic charge of a surface. The thermosetting coating
is cured by baking. An epoxy powder coating may be selected as a
pipe coating, an electrical devise coating, an industrial coating
(e.g., appliance coating, automotive coating, furniture coating),
or a combination thereof.
[0483] (5) Cycloaliphatic Epoxies
[0484] A cycloaliphatic epoxy binder possesses a ring structure,
rather than the linear structure for the epoxy embodiments
described above. Examples of a cycloaliphatic epoxide is ERL-4221
("3,4-epoxycyclohexylmet- hyl 3,4-epoxycyclohexane carboxylate"),
which has an epoxy equivalent weight of 131 to 143,
bis(3,4-epoxycyclohexylmethyl) adipate, which has an epoxy
equivalent weight of 190 to 210, 2-(3,4-epoxycyclohexyl-5,5-spir-
o-3,4-epoxy)cyclohexane-m-dioxane, which has an epoxy equivalent
weight of 133-154, 1-vinyl-epoxy-3,4-epoxycyclohexane, which has an
epoxy equivalent weight of 70 to 74, or a combination thereof.
Usually, a cycloaliphatic epoxy coating is combined with another
binder, such as a polyol, a polyol modified to comprise a carboxyl
moiety, or a combination thereof. An acid may be used to initiate
crosslinking, particularly with a polyol. A cycloaliphatic epoxy
polyol coating may comprise a triflic acid salt (e.g.,
diethylammonium triflate) to produce a one-pack coating with a pot
life of up to eight months. In certain embodiments, a
cycloaliphatic epoxy coating is a UV radiation cured coating,
wherein the coating comprises a compound that-converts to a strong
acid upon UV irradiation (e.g., an onium salt). In certain aspects,
a UV radiation cured cycloaliphatic epoxy coating is a one-pack
coating. A UV radiation cured cycloaliphatic epoxy coating
generally possesses excellent flame resistance, water resistance,
or a combination thereof, and may be selected as a can coating or
an electrical equipment coating. A compound comprising a carboxyl
moiety (e.g., a carboxyl modified polyol) readily crosslinks with a
cycloaliphatic epoxy binder. However, such a cycloaliphatic epoxy
coating comprising such an additional binder generally has a short
pot life (e.g., less than eight hours). In certain aspects, a
cycloaliphatic epoxy carboxylic acid binder coating is a two-pack
coating. A cycloaliphatic epoxy carboxylic acid polyol coating
generally possesses excellent adhesion, toughness, gloss, hardness,
solvent resistance, or a combination thereof.
[0485] i. Polyhydroxyether Binders
[0486] A polyhydroxyether binder ("polyhydroxyether resin,"
"phenoxy binder," "phenoxy") chemically resembles a bisphenol A
epoxy resin, though a polyhydroxyether binder lacks an epoxide
moiety, and about 30 kDa in size. A polyhydroxyether coating is
typically a thermoplastic coating. The polyhydroxyether binder
comprises a hydroxyl moiety, and can be cross-linked with an
additional binder such as an epoxide, a polyurethane comprising an
isocyanate moiety, an amino resin, or a combination thereof. A
thermosetting polyhydroxyether coating typically possesses
excellent physical resistance properties, excellent chemical
resistance, modest solvent resistance, or a combination thereof. In
alternative embodiments, a polyhydroxyether binder temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of a polyhydroxyether binder that that
comprises fewer or no crosslinkable moieties, selection of an
addition binder that comprises fewer or no crosslinkable moieties,
reducing the concentration of the a polyhydroxyether binder and/or
additional binder, or a combination thereof.
[0487] j. Acrylic Resins
[0488] An acrylic resin ("acrylic polymer," "acrylic binder,"
"acrylic") is a binder comprising a polymer of an acrylate ester
monomer, a methacrylate ester monomer, or combination thereof. An
acrylic-coating generally possesses a superior property of water
resistance and/or exterior use durability than a polyester-coating.
Other properties that an acrylic-coating typically possesses
include color stability, chemical resistance, resistance to a UV
light, or a combination thereof. An acrylic resin may further
comprise an additional monomer to confer a desirable property to
the resin, coating and/or film. For example, a styrene, a
vinyltoluene, or a combination thereof, generally improve alkali
resistance. Examples of such properties include the acrylic resin's
chemical reactivity (e.g., cross-linkability), acidity, alkalinity,
hydrophobicity, hydrophilicity, glass transition temperature, or a
combination thereof. However, a thermoplastic acrylic film
generally possesses poor solvent (e.g., acetone, toluene)
resistance. Like other thermoplastic films, a thermoplastic acrylic
film is generally easy to repair by application of additional
acrylic coating to an area of solvent damage. An acrylic-coating is
often suitable for various surfaces (e.g., metal), and examples of
such coatings include an aerosol lacquer, an automotive coating, an
architectural coating, a clear coating, a coating for external
environment, an industrial coating, or a combination thereof. An
acrylic resin may be used to prepare a thermoplastic coating, a
thermosetting coating, or a combination thereof. In certain
aspects, an acrylic-coating is selected for use as a thermosetting
coating, particularly in embodiments for use upon a metal surface.
Acrylic resins generally are soluble in a solvent with a similar
solubility parameter. Examples of solvents typically used to
dissolve an acrylic resin include an aromatic hydrocarbon (e.g.,
toluene, a xylene); a ketone (e.g., methyl ethyl ketone), an ester,
or a combination thereof.
[0489] The thermoplastic and/or thermosetting properties of an
acrylic resin are related to the monomers that are comprised in the
selected resin. Examples of an acrylate ester monomer include a
butylacrylate, an ethylacrylate ("EA"), ethylhexylacrylate ("EHA"),
or a combination thereof. Examples of a methacrylate ester monomer
include a butylmethacrylate ("BMA"), an ethylmethacrylate, a
methylmethacrylate ("MMA"), or a combination thereof. Standards for
physical properties, chemical properties, and/or procedures for
empirically determining the purity/properties of various acrylic
monomers (e.g., acrylate esters, 2-ethylhexyl acrylate, n-butyl
acrylate, ethyl acrylate, methacrylic acid, acrylic acid, methyl
acrylate) are known to those of ordinary skill in the art (see, for
example, "ASTM Book of Standards, Volume 06.04, Paint--Solvents;
Aromatic Hydrocarbons," D3362-93, D3125-97, D4415-91, D3541-91,
D3547-91, D3548-99, D3845-96, D4416-89, and D4709-02, 2002).
[0490] In alternative embodiments, an acrylic resin temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of an acrylic resin that that comprises fewer
or no crosslinkable moieties, selection of an addition binder that
comprises fewer or no crosslinkable moieties, reducing the
concentration of the an acrylic resin and/or additional binder,
using a bake cured an acrylic resin coating at temperatures less
than is needed for curing (e.g., ambient conditions), selection of
size range for a thermoplastic acrylic resin coating that is less
suitable for film formation (e.g., 1 kDa to 75 kDa), selection of a
thermoplastic acrylic resin with T.sub.g that is lower than the
temperature ranges herein and/or 20.degree. C. lower than the
temperature range of use, or a combination thereof.
[0491] (1) Thermoplastic Acrylic Resins
[0492] A strait acrylic resin ("strait acrylic polymer," "strait
acrylic binder") is a homopolymer or copolymer comprising an
acrylate ester monomer and/or a methacrylate ester monomer. A
strait acrylic resin may be used to formulate a thermoplastic
coating, as cross-linking reactions are absent or limited without
additional reactive moieties in the monomers. Generally, a
thermoplastic film produced from an acrylic resin-coating will
possess a lower elongation, an increased hardness, an increased
tensile strength, greater UV resistance (e.g., chalk resistance),
color retention, a greater T.sub.g, or a combination thereof, with
increasing methacrylate ester monomer content in the acrylic resin.
However, the ester of a monomer may comprise various alcohol
moieties, and an alcohol moiety of larger size generally reduces
the T.sub.g. Examples a T.sub.g value for a homopolymer strait
acrylic resins with the include -100.degree. C., poly(octadecyl
methacrylate); -72.degree. C., poly(tetradecyl methacrylate);
-65.degree. C., poly(lauryl methacrylate); -60.degree. C.,
poly(heptyl acrylate); -60.degree. C., poly(n-decyl methacrylate);
-55.degree. C., poly(n-butyl acrylate); -50.degree. C.,
poly(2-ethoxyethyl acrylate); -50.degree. C., poly(2-ethylbutyl
acrylate); -50.degree. C., poly(2-ethylhexyl acrylate); -45.degree.
C., poly(propyl acrylate); -43.degree. C., poly(isobutyl acrylate);
-38.degree. C., poly(2-heptyl acrylate); -24.degree. C., poly(ethyl
acrylate); -20.degree. C., poly(n-octyl methacrylate); -20.degree.
C., poly(sec-butyl acrylate); -20.degree. C., poly(ethylthioethyl
methacrylate); -10.degree. C., poly(2-ethylhexyl methacrylate);
-5.degree. C., poly(n-hexyl methacrylate); -3.degree. C.,
poly(isopropyl acrylate); 6.degree. C., poly(methyl acrylate);
11.degree. C., poly(2-ethylbutyl methacrylate); 16.degree. C.,
poly(cyclohexyl acrylate); 20.degree. C., poly(n-butyl
methacrylate); 35.degree. C., poly(hexadecyl acrylate); 35.degree.
C., poly(n-propyl methacrylate); 43.degree. C., poly(t-butyl
acrylate); 53.degree. C., poly(isobutyl methacrylate); 54.degree.
C., poly(benzyl methacrylate); 60.degree. C., poly(sec-butyl
methacrylate); 65.degree. C., poly(ethyl methacrylate); 79.degree.
C., poly(3,3,5-trimethylcyclohexylmethacrylate); 81.degree. C.,
poly(isopropyl methacrylate); 94.degree. C., poly(isobornyl
acrylate); 104.degree. C., poly(cyclohexyl methacrylate);
105.degree. C., poly(methyl methacrylate); 107.degree. C.,
poly(t-butyl methacrylate); and 110.degree. C., poly(phenyl
methacrylate). Additionally, an estimated T.sub.g of a copolymer
comprising one or more monomers of an acrylate and/or methyacrylate
monomer can be made by using the following equation:
1/T.sub.g=W.sub.1/T.sub.g1+W.sub.2/T.sub.g2, wherein W.sub.1 and
W.sub.2 are the are the molecular weight ratios of the first and
second monomer, respectively; and wherein T.sub.g1 and T.sub.g2 are
glass transition temperatures of the first and second monomer,
respectively (Fox, T. G., 1956). For many embodiments (e.g.,
solvent-borne coatings), it is contemplated that a T.sub.g of
40.degree. C. to 60.degree. C., including all intermediate ranges
and combinations thereof, will be suitable.
[0493] The thermoplastic properties of an acrylic resin are also
related to the molecular mass of the selected resin. Increasing the
polymer size of an acrylic resin promotes physical polymer
entanglement during film formation. Typically, a thermoplastic film
produced from an acrylic-coating will possess a lower flexibility,
an increased exterior durability, an increased hardness, an
increased solvent resistance, an increased tensile strength, a
greater T.sub.g, or a combination thereof, with increasing polymer
size of the acrylic resin. However, increasing polymer size of an
acrylic resin generally increases viscosity of a solution
comprising a dissolved acrylic resin, which may make application to
a surface more difficult, such as cobwebbing of coating during
spray application and the changes of film properties generally will
reach a plateau at 100 kDa. In most embodiments, it is contemplated
that an acrylic resin will range in mass from 75 kDa to 100 kDa,
including all intermediate ranges and combinations thereof.
[0494] Examples of such a thermoplastic acrylic-coating include a
lacquer. In specific facets, the lacquer possesses a good, high, or
spectacular gloss. In specific aspects, such a thermoplastic
acrylic-coating further comprises a pigment. In specific aspects, a
wetting agent is less preferred in a coating comprising an acrylic
resin and a pigment, due to the ease of dispersion of a pigment
with an acrylic resin. In certain aspects, a thermoplastic
acrylic-coating may be selected to coat a metal surface, a plastic
surface, or a combination thereof. However, in particular aspects,
a thermoplastic acrylic coating is an automotive coating. Such an
automotive coating may comprise an acrylic binder with a high
temperature T.sub.g to produce a film of sufficient durability
(e.g., hardness) for external use and contact with heated surfaces.
In certain aspects, a thermoplastic acrylic coating comprises a
binder with a T.sub.g to 90.degree. C. to 110.degree. C., including
all intermediate ranges and combinations thereof. In additional
aspects, an automotive coating comprises a plasticizer, a metallic
pigment, or a combination thereof. In specific aspects, a binder
for an automotive coating comprises a methylmethacrylate ester
monomer. In specific facets, an automotive coating comprises
poly(methyl methacrylate).
[0495] (2) Water-Borne Thermoplastic Acrylic Coatings
[0496] The thermoplastic acrylic coatings described above are
solvent-borne coatings. In other embodiments, a thermoplastic
acrylic resin may be a waterborne coating. A water-borne acrylic
("acrylic latex") typically is an emulsion, wherein the acrylic
binder is dispersed in the liquid component. In general
embodiments, an emulsifier (e.g., a surfactant) promotes
dispersion. In certain embodiments, an acrylic latex coating
comprises 0% to 20% coalescent per weight of binder. In most
embodiments, it is contemplated that a water-borne acrylic resin
will range in mass from 100 kDa to 1000 kDa, including all
intermediate ranges and combinations thereof. In certain
embodiments, a water-borne acrylic coating comprises an associative
thickener ("rheology modifier"), which may enhance flow,
brushability, splatter resistance, film build, or a combination
thereof. A water-borne acrylic may be selected as an architectural
coating. An associative thickener forms a network with acrylic
resin latex particles by hydrophobic interactions. Hydroxyethyl
cellulose ("HEC") changes the coating rheology by promoting
flocculation, which tends to reduce gloss, flow, or a combination
thereof. Selection of an acrylic resin with smaller size, greater
hydrophobicity, or a combination thereof, and an associative
thickener may produce higher gloss, better flow, lower roller
splatter, or a combination thereof.
[0497] (i) Architectural Coatings
[0498] A flat interior coating typically comprises a vinyl acetate
and a lesser amount of acrylate (e.g., butyl acrylate) monomers,
which generally produces a film with suitable scrub resistance. A
copolymer of acrylate and methacrylate may be selected for a
semigloss or gloss coating. In certain embodiments, the acrylate
resin has a T.sub.g to 20.degree. C. to 50.degree. C., including
all intermediate ranges and combinations thereof. In some aspects,
such a coating generally possesses good block resistance good print
resistance, or a combination thereof. An acrylic resin that
comprises a monomer that comprises a ureide moiety may be selected
for enhanced film adhesion (e.g., to a coated surface), blistering
resistance, or a combination thereof. An acrylic resin that
comprises a styrene monomer may be selected for enhanced film water
resistance.
[0499] An exterior latex coating typically produces a film with
greater flexibility than an interior latex due to temperature
changes and/or dimensional movement of a substrate (e.g., wood). In
certain embodiments, the acrylic resin has a T.sub.g to 10.degree.
C. to 35.degree. C., including all intermediate ranges and
combinations thereof. The selection of a T.sub.g may be influences
by the selection of the amount particulate material (e.g., pigment)
in the coating to achieve a particular visual appearance. For
example, a higher the pigment volume content ("PVC") that is
typically selected to reduce gloss. However, to retain properties
such as flexibility, a binder with a lower a T.sub.g may be
selected for combination with the higher PVC. For example, flat
exterior latex a coating generally possesses a pigment volume
content of 40% to 60% and a T.sub.g of 10.degree. C. to 15.degree.
C., including all intermediate ranges and combinations thereof,
respectively. In another example, a semigloss or gloss exterior
latex binder of a coating generally possesses a T.sub.g of
20.degree. C. to 35.degree. C., including all intermediate ranges
and combinations thereof, respectively. In other embodiments, the
exterior latex binder particle size is selected to be relatively
small such as 90 nm to 110 nm, including all intermediate ranges
and combinations thereof. In certain facets, a smaller latex
particle size promotes adhesion of the coating and/or film,
particularly to a surface that comprises a degraded (e.g.,
chalking) film. In certain other embodiments, a larger latex
particle size may be selected to increase the coating and/or film's
build (e.g., thickness). In certain aspects, a larger latex
particle size ranges from, for example 325 nm to 375 nm, including
all intermediate ranges and combinations thereof.
[0500] (ii) Industrial Coatings
[0501] A water-borne thermoplastic acrylic latex industrial coating
typically comprises a binder with a T.sub.g of 30.degree. C. to
70.degree. C., including all intermediate ranges and combinations
thereof. Such a coating typically is applied to a metal surface,
and thus often further comprises a surfactant, an additive, or a
combination thereof to improve an anti-corrosion property. In
specific aspects, the industrial coating comprises an
anti-corrosion pigments, anti-corrosion pigment enhancers, or a
combination thereof. In contrast, a water-borne acrylic latex
industrial maintenance coating typically is similar to an exterior
flat architectural coating in selection of binders, though they
preferably comprise anti-corrosion pigments, anti-corrosion pigment
enhancers, and other anti-corrosion components for use on a metal
surface.
[0502] (3) Thermosetting Acrylic Resins
[0503] Unless otherwise noted, the following thermosetting acrylic
resins and/or coatings are preferably solvent-borne coatings. In
certain embodiments an acrylic coating comprises a thermosetting
acrylic resin. A thermosetting acrylic coating typically possesses
superior hardness, superior toughness, superior temperature
resistance, superior resistance to a solvent, superior resistance
to a stain, superior resistance to a detergent, higher application
of solids, relative to a thermoplastic acrylic coating. The average
size of a thermosetting acrylic resin is typically less than a
thermoplastic acrylic resin, which promotes a relatively lower
viscosity and/or higher application of solids in a solution
comprising a thermosetting acrylic resin. In certain embodiments, a
thermosetting acrylic resin is from 10 kDa to 50 kDa, including all
intermediate ranges and combinations thereof.
[0504] A thermosetting acrylic resin comprises a moiety capable of
undergoing a cross-linking reaction. A monomer may comprise the
moiety, and be incorporated into the polymer structure of an
acrylic resin during resin synthesis (e.g., a styrene, a
vinyltoluene), and/or the acrylic resin may be chemically modified
after polymerization to comprise a chemical moiety. In additional
embodiments, an acrylic resin may be selected to comprise chemical
moieties, such as an amine, a carboxyl, an epoxy, a hydroxyl, an
isocyanate, or a combination thereof, to confer a desirable
property to the acrylic resin produced. Examples of such properties
include the acrylic resin's chemical reactivity (e.g.,
crosslinkability), acidity, alkalinity, hydrophobicity,
hydrophilicity, glass transition temperature, or a combination
thereof. In general embodiments, an acrylic resin comprising a
carboxyl moiety, a hydroxyl moiety, or a combination thereof,
promotes a crosslinking reaction with another binder. In other
embodiments, an acrylic resin may be chemically modified to
comprise a methylol and/or methylol ether group, which is a resin
capable of self-crosslinking.
[0505] (i) Acrylic-Epoxy Combinations
[0506] In certain embodiments, a thermosetting acrylic resin may be
combined with an epoxide resin. In general embodiments, an acrylic
resin comprising a carboxyl moiety may be selected for
cross-linking with an epoxy resin. In specific aspects, an acrylic
resin comprises 5% to 20% including all intermediate ranges and
combinations thereof, of a monomer that comprises a carboxyl
moiety, such as of an acrylic acid monomer, a methacrylic acid
monomer, or a combination thereof. The carboxyl moiety may undergo
a cross-linking reaction with an epoxide resin (e.g., a bisphenol
A/epichlorohydrin epoxide resin) during film formation. In certain
aspects, an epoxide resin cross-linked with an acrylic resin
generally produces a film with good hardness, good alkali
resistance, greater solvent resistance to a film, poorer UV
resistance, or a combination thereof.
[0507] A thermosetting acrylic-epoxy coating may be selected for
application to a metal surface. Examples of surfaces that an
acrylic-epoxy coating is selected for use include an indoor
surface, an indoor metal surface (e.g., an appliance), or a
combination thereof. In certain aspects, an epoxide resin
cross-linked with an acrylic resin generally produces a film with
good hardness, good alkali resistance, greater solvent resistance
to a film, poorer UV resistance, or a combination thereof. In some
facets, an acrylic resin may be combined with an aliphatic epoxide
resin to produce a film with relatively superior UV resistance than
a bisphenol A/epichlorohydrin based epoxide resin. In another
facet, an acrylic resin polymerized with an allyl glycidyl ether
monomer, a glycidyl acrylate monomer, a glycidyl methacrylate
monomer, or a combination thereof, may undergo a cross-linking
reaction with an epoxide resin during film formation. In specific
facets, a film produced from cross-linking an epoxide other than a
bisphenol A/epichlorohydrin epoxide resin and an acrylic resin
comprising an allyl glycidyl ether monomer, a glycidyl acrylate
monomer, a glycidyl methacrylate monomer, or a combination thereof
possesses a relatively superior UV resistance.
[0508] In certain embodiments, an acrylic epoxy coating comprises a
catalyst to promote cross-linking during film formation. In
specific aspects, the catalyst is a base such as a dodecyl
trimethyl ammonium chloride, a tri(dimethylaminomethyl) phenol, a
melamine-formaldehyde resin, or a combination thereof. In other
embodiments, an acrylic epoxy coating is cured by baking at
150.degree. C. to 190.degree. C., including all intermediate ranges
and combinations thereof. In particular aspects, film formation
time of an acrylic epoxy coating is from 15 minutes to 30 minutes,
including all intermediate ranges and combinations thereof. In
certain embodiments, a thermosetting coating comprises an acrylic
epoxide melamine-formaldehyde coating, wherein an acrylic resin, an
epoxide resin and a melamine-formaldehyde resin undergo
cross-linking during film formation.
[0509] (ii) Acrylic-Amino Combinations
[0510] In other embodiments, a thermosetting acrylic resin may be
combined with an amino resin. In general embodiments, an acrylic
resin comprising an acid (e.g., carboxyl) moiety, a hydroxyl
moiety, or a combination thereof, may be selected for cross-linking
with an amino resin. An acrylic amino coating, wherein the acrylic
resin comprises an acid moiety, may be cured by baking at, for
example 150.degree. C. for 30 minutes. However, an acid moiety
acrylic amino coating is typically undergoes a greater degree of
reactions between amino resins, which reduces properties such as
toughness. In specific aspects, an acrylic resin comprises a
monomer that comprises a hydroxyl moiety such as a hydroxyethyl
acrylate ("HEA"), a hydroxyethyl methacrylate ("HEMA"), or a
combination thereof. An acrylic amino coating, wherein the acrylic
resin comprises a hydroxyl moiety, typically comprises an acid
catalyst to promote curing by baking at, for example 125.degree. C.
for 30 minutes. An acrylic amino coating, wherein the amino resin
was prepared from urea, generally produces a film with lower gloss,
less chemical resistance, or a combination thereof, than an amino
resin prepared from another nitrogen compound. Selection of a
melamine and/or benzoguanamine based amino coating generally
produces a film with excellent weathering resistance, excellent
solvent resistance, good hardness, good mar resistance, or a
combination thereof, and such an acrylic amino coating may be
selected for an automotive topcoat.
[0511] (iii) Acrylic-Urethane Combinations
[0512] In other embodiments, a thermosetting acrylic resin may be
combined with an urethane resin. In general embodiments, an acrylic
resin comprising an acid moiety, a hydroxyl moiety, or a
combination thereof, may be selected for crosslinking with an
urethane resin. In specific embodiments, an acrylic resin comprises
a hydroxyl moiety, such as, for example, a moiety provided by a HEA
monomer, a HEMA monomer, or a combination thereof. Selection of an
aliphatic isocyanate urethane (e.g., hexamethylene diisocyanate
based) generally produces a film with superior color, weathering,
or a combination thereof relative to other urethanes. An acrylic
urethane coating may comprise a catalyst, such as, for example,
triethylene diamine, zinc naphthenate, dibutyl tin-di-laurate, or a
combination thereof. An acrylic urethane coating cures at ambient
conditions. However, an acrylic urethane coating typically is a
two-pack coating to separate the reactive binders until
application. An acrylic urethane coating generally produces a film
with good weathering, good hardness, good toughness, good chemical
resistance, or a combination thereof. An acrylic urethane coating
may be selected an aircraft coating, an automotive coating, an
industrial coating (e.g., an industrial maintenance coating), or a
combination thereof.
[0513] (iv) Water-Borne Thermosetting Acrylics
[0514] In other embodiments, a thermosetting acrylic coating may be
a waterborne coating (e.g., a latex coating). Typically, such a
thermosetting acrylic coating comprises an acrylic resin with a
hydroxyl moiety, an acid moiety, or a combination thereof. An
acrylic resin may further comprise an additional monomer such as a
styrene, a vinyltoluene, or a combination thereof. The acrylic
resin typically is combined in a coating with an amino resin, an
epoxy resin, or a combination thereof as previously described. A
film produced from a water-borne thermosetting acrylic coating is
similar in properties as a solvent-borne counterpart. Such a
coating may be selected for surfaces such as masonry, wood, metal,
or a combination thereof.
[0515] k. Polyvinyl Binders
[0516] A polyvinyl binder ("polyvinyl," "vinyl binder," "vinyl") is
a binder comprising a polymer of a vinyl chloride monomer, a vinyl
acetate monomer, or combination thereof. A solvent-borne polyvinyl
coating may comprise a ketone, ester, chlorinated hydrocarbon,
nitroparaffin, or a combination thereof, as a solvent. A
solvent-borne polyvinyl coating may comprise a hydrocarbon (e.g.,
aromatic, aliphatic) as a diluent. A polyvinyl binder is generally
insoluble in an alcohol, however, in embodiments wherein a
solvent-borne polyvinyl coating that comprises an additional
alcohol soluble binder, alcohol may comprise 0% to 20% of the
liquid component. In embodiments wherein solvent-borne polyvinyl
coating is cured by baking, a glycol ether and/or glycol ester may
be used in the liquid component to enhance a Theological property.
In other embodiments, the liquid component of a polyvinyl coating
may comprise a plasticizer (e.g., a phthalate, a phosphate, a
glycol ester), wherein the plasticizer if 1 to 25 parts per hundred
parts polyvinyl binder, including all intermediate ranges and
combinations thereof, for a non-plastisol or non-organosol coating.
A polyvinyl-coating may be used to prepare a thermoplastic coating,
a thermosetting coating, or a combination thereof. In specific
aspects, a thermoplastic polyvinyl binder coating possesses a
T.sub.g of 50.degree. C. to 85.degree. C., including all
intermediate ranges and combinations thereof. However, in some
aspects, a polyvinyl-coating/film possesses moderate resistance to
heat, UV irradiation, or a combination thereof. In specific
aspects, a polyvinyl-coating comprises a light stabilizer, a
pigment, or a combination thereof. In particular facets, the light
stabilizer, the pigment (e.g., titanium dioxide), or the
combination thereof, improves the polyvinyl-coating and/or film's
resistance to heat, UV irradiation, or a combination thereof.
[0517] In embodiments wherein a polyvinyl coating comprises a
solvent-borne coating, it is contemplated that a polyvinyl resin
will range in mass from 2 kDa to 45 kDa, including all intermediate
ranges and combinations thereof. A typical solvent-borne polyvinyl
coating comprises a polyvinyl resin, a liquid component wherein the
liquid component comprises a solvent, and a plasticizer. A
solvent-borne polyvinyl coating may additionally comprise a
colorizing agent (e.g., a pigment), a light stabilizer, an
additional binder, a cross-linker, or a combination thereof.
[0518] A polyvinyl binder typically possesses excellent adhesion
for a plastic surface, an acrylic and/or acrylic coated surface,
paper, or a combination thereof. A thermoplastic polyvinyl coating
may be selected as a lacquer, a topcoat of a can coating (e.g., can
interior surface), or a combination thereof. In some embodiments,
an polyvinyl-coating may be selected to produce a film with such
properties, for example, as excellent water resistance, excellent
resistance to various solvents (e.g., an aliphatic hydrocarbon, an
alcohol, an oil), excellent resistance to acid pH, excellent
resistance to basic pH, inertness relative to food, or a
combination thereof.
[0519] In many aspects, a polyvinyl resin is a copolymer that
comprises a combination of a vinyl chloride monomer and vinyl
acetate monomer. Often during resin synthesis (e.g.,
polymerization), a polyvinyl resin is prepared to further comprise
monomers with specific chemical moieties to confer a property such
as solubility in water, solubility in a solvent, compatibility with
another coating component (e.g., a binder), or a combination
thereof. In certain embodiments, a polyvinyl resin comprises a
monomer comprising carboxyl moiety, a hydroxyl moiety (e.g., a
hydroxyalkyl acrylate monomer), a monomer comprising an epoxy
moiety, a monomer comprising a maleic acid, or a combination
thereof. A carboxyl moiety may confer an increased adhesion
property (e.g., excellent adhesion to metal). However, a polyvinyl
resin comprising a carboxyl moiety is generally not compatible with
a basic pigment. A thermosetting polyvinyl coating comprising a
polyvinyl binder that comprises a carboxyl moiety and a polyvinyl
binder that comprises an epoxy moiety generally possesses one or
more excellent physical properties (e.g., flexibility), and may be
selected as a coil coating. A hydroxyl moiety may confer
cross-linkability, compatibility with another coating component, an
increased adhesion property (e.g., good adhesion to aluminum), or a
combination thereof. Additionally, after polymer synthesis, a
polyvinyl resin can be chemically modified to comprise such a
specific chemical moiety. In some embodiments, a polyvinyl resin is
chemically modified to comprise a secondary hydroxyl moiety, an
epoxy moiety, a carboxyl moiety, or a combination thereof. A
polyvinyl resin comprising a secondary hydroxyl moiety may be
combined with another binder such as an alkyd, an urethane, an
amino-formaldehyde, or a combination thereof. A thermosetting
polyvinyl amino-formaldehyde coating comprising a polyvinyl binder
that comprises a hydroxyl moiety generally possesses good corrosion
resistance, water resistance, solvent resistance, chemical
resistance, and may be selected as a can coating, a coating for an
interior wood surface, or a combination thereof. Standards for
physical properties, chemical properties, and/or procedures for
testing the purity/properties of various polyvinyl monomers (e.g.,
vinyl acetate) and polyvinyl resins (e.g., polymer components,
polymer mass, shear viscosity for a higher mass resin, chlorine
content) are described, for example, in "ASTM Book of Standards,
Volume 06.04, Paint--Solvents; Aromatic Hydrocarbons," D2190-97,
D2086-02, D2191-97, and D2193-97, 2002; "ASTM Book of Standards,
Volume 06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D4368-89, D3680-89,
and D1396-92, 2002; and in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2621-87, 2002.
[0520] In alternative embodiments, a polyvinyl resin temporary
coating (e.g, a non-film forming coating) may be produced, for
example, by selection of a polyvinyl resin that that comprises
fewer or no crosslinkable moieties, selection of an addition binder
that comprises fewer or no crosslinkable moieties, reducing the
concentration of the a polyvinyl resin and/or additional binder,
using a bake cured a polyvinyl resin coating at temperatures less
than is needed for curing (e.g., ambient conditions), selection of
size range for a plastisol or organisol polyvinyl resin coating
that is less suitable for film formation (e.g., 1 kDa to 60 kDa),
selection of a polyvinyl resin with T.sub.g that is lower than the
temperature ranges herein and/or 20.degree. C. lower than the
temperature range of use, or a combination thereof.
[0521] (1) Plastisols and Organisols
[0522] A polyvinyl resin of 60 kDa to 110 kDa, including all
intermediate ranges and combinations thereof, may be selected for
use as an organosol or a plastisol. A plastisol is coating
comprising a vinyl homopolymer binder and a liquid component,
wherein the liquid component comprises a plasticizer comprising a
minimum of 55 parts or more of plasticizer per hundred parts of
homopolymer binder in the coating. In certain embodiments, a
plastisol comprises, by weight, 0% to 10% including all
intermediate ranges and combinations thereof, of a thinner (e.g.,
an aliphatic hydrocarbon). A plastisol coating typically comprises
an additional vinyl binder. A plastisol may comprise a pigment,
however, a low oil absorption pigment is preferred to avoid
undesirable increase in coating viscosity given the liquid
component used for a plastisol.
[0523] An organosol is similar to a plastisol, except the less than
55 parts of plasticizer per hundred parts of homopolymer binder is
used in the coating. In typical embodiments, the liquid component
of comprises a weak solvent that may act as a dispersant and a
thinner (e.g., a hydrocarbon). In typical aspects, the reduced
content of plasticizer produced a film with a superior hardness
property relative to a plastisol. In additional embodiments, the
nonvolatile component of an organisol is 50% to 55%, including all
intermediate ranges and combinations thereof. An organosol coating
typically comprises a second binder. In specific aspects, the
second binder is a vinyl copolymer, an acrylic, or a combination
thereof. In certain aspects, the second binder comprises a carboxyl
moiety, a hydroxyl moiety, or a combination thereof. In further
aspects, an organisol may comprise a third binder. In specific
facets, the third binder comprises an amino resin, a phenolic resin
prepared from formaldehyde, or a combination thereof. In additional
facets, a second binder that comprises a hydroxyl moiety may
undergo a thermosetting cross-linking reaction with a third binder.
An organisol may comprise a pigment suitable for general polyvinyl
coatings.
[0524] A plastisol or organisol typically is cured by baking. In
general embodiments, baking is at a temperature of 175.degree. C.
to 180.degree. C., including all intermediate ranges and
combinations thereof. In general embodiments, a plastisol or
organisol comprises a heat stabilizer. The heat stabilizer may
protect a vinyl binder during baking. Examples of a suitable heat
stabilizer include a combination of a metal salt of an organic acid
and an epoxidized oil or a liquid epoxide binder. However, in an
embodiment wherein the plastisol or organisol comprises a binder
that comprises an carboxyl moiety, a metal salt is less preferred
due to possible gellation of the coating, and may be substituted
with a merapto tin and/or tin ester compound.
[0525] In embodiments wherein a plastisol or organisol comprise a
binder with good adhesion properties for a surface such as a binder
comprising carboxy moiety, the plastisol or organisol may be used
as a single layer coating. For example, such an organisol may be
selected to coat the end of a can. However, a plastisol or
organisol typically is part of a multicoat system that comprises a
primer to promote adhesion. In specific aspects, the primer
comprises a vinyl resin comprising a carboxy moiety. In specific
facets, the primer further comprises a thermosetting binder such as
an amino-formaldehyde, phenolic, or a combination thereof, to
enhance solvent resistance. In certain facets, it is preferred that
a primer or other coat layer of a multicoat system possesses good
solvent resistance to the plasticizers of the organosol and/or
plastisol coat layer.
[0526] (2) Powder Coatings
[0527] A polyvinyl binder may be selected as a powder coating.
Typically, coating components such as a polyvinyl binder and a
plasticizer, colorizing agent, additive, or a combination thereof,
admixed to prepare a powder coating. Such a powder coating is
usually applied by a fluidized bed applicator, a spray applicator,
or a combination thereof. In some aspects, the coating components
are melted then ground into a powder. Such a powder coating is
usually applied by an electrostatic spray applicator. The coating
is cured by baking. A polyvinyl powder coating may be selected to
coat a metal surface.
[0528] (3) Water-Borne Coatings
[0529] The previous discussions of polyvinyl coatings focused upon
solvent-borne and powder coatings. A polyvinyl binder with a
T.sub.g of 75.degree. C. to 85.degree. C., including all
intermediate ranges and combinations thereof, may be selected for
use in a dispersion waterborne coating. The liquid component may
comprise a cosolvent such as a glycol ether, a plasticizer, or a
combination thereof. Examples of a cosolvent include ethylene
glycol monobutyl ether. The dispersion water-borne polyvinyl
coating may be used as described for a solvent-borne polyvinyl
coating. In another example, an organisol may be prepared with a
plasticizer as a latex coating. Such a latex is suitable for
selection as a primer coating. The latex coating is cured by
baking.
[0530] I. Rubber Resins
[0531] In certain embodiments, a coating may comprise a rubber
resin as a binder. A rubber may be either obtained from a
biological source ("natural rubber"), synthesized from petroleum
("synthetic rubber"), or a combination thereof. Examples of
synthetic rubber include polymers of styrene monomers, butadiene
monomers, or a combination thereof. In alternative embodiments, a
rubber temporary coating (e.g, a non-film forming coating) may be
produced, for example, by selection of rubber resin that that
comprises fewer or no crosslinkable moieties, selection of an
addition binder that comprises fewer or no crosslinkable moieties,
reducing the concentration of the a rubber resin and/or additional
binder, or a combination thereof.
[0532] (1) Chlorinated Rubber Resins
[0533] In general embodiments, a rubber resin comprises a
chlorinated rubber resin, wherein a rubber isolated from a
biological source has been chemically modified by reaction with
chlorine to produce a resin comprising 65% to 68% chlorine by
weight, including all intermediate ranges and combinations thereof.
A chlorinated rubber resins generally are in a molecular weight
range of 3.5 kDa to 20 kDa, including all intermediate ranges and
combinations thereof. A chlorinated rubber coating may comprise
another binder, such as, for example, an acrylic resin, an alkyd
resin, a bituminous resin, or a combination thereof. In specific
aspects, a chlorinated rubber resin comprises 10% to 50%, by
weight, including all intermediate ranges and combinations thereof,
of the binder when in combination with an acrylic resin, an alkyd
resin, or a combination thereof. In general embodiments, a
chlorinated rubber coating is a solvent-borne coating. In certain
aspects, a chlorinated rubber coating comprises a liquid component,
such as, for example, a solvent, a diluent, a thinner, a
plasticizer, or a combination thereof. A chlorinated rubber coating
may be a thermoplastic coating. To reduce the T.sub.g of a film
produced from a chlorinated rubber resin, the liquid component
generally comprises a plasticizer. In certain aspects, a
chlorinated rubber coating comprises 30% to 40%, by weight,
including all intermediate ranges and combinations thereof, of
plasticizer. In certain facets, a plasticizer is selected for water
resistance (e.g., hydrolysis resistance) such as a
bisphenoxyethylformal. In certain facets, a chlorinated rubber
coating comprises light stabilizer, an epoxy resin, an epoxy
plasticizer (e.g., epoxidized soybean oil), or combination thereof,
to chemically stabilize a chlorinated resin, coating and/or film.
In other embodiments, a chlorinated rubber coating comprises a
pigment, an extender, or a combination thereof. In particular
aspects, the pigment is a corrosion resistant pigment. A
chlorinated rubber film are generally has good chemical resistance
(e.g., acid resistance, alkali resistance), water resistance, or a
combination thereof. Coatings comprising chlorinated rubber resins
may be used, for example, on surfaces that contact gaseous, liquid
and/or solid external environments. Examples of such uses include a
coating for an architectural coating (e.g., a masonry coating), a
traffic marker coating, a marine coating (e.g., a marine vehicle, a
swimming pool), a metal primer, a metal topcoat, or a combination
thereof.
[0534] (2) Synthetic Rubber Resins
[0535] Examples of synthetic rubber include polymers comprising a
styrene monomer, a methylstyrene (e.g., .alpha.-methylstyrene)
monomer, or a combination thereof. A polystyrene and/or
polymethylstyrene coating may be a solvent-borne coating. Examples
of a solvent include an aliphatic hydrocarbon, an aromatic
hydrocarbon, a ketone, an ester, or a combination thereof. A
polystyrene and/or polymethylstyrene coating may possess good water
resistance, good chemical resistance, or a combination thereof. A
polystyrene and/or polymethylstyrene coating may be selected as a
primer, a lacquer, a masonry coating, or a combination thereof. A
polystyrene homopolymer has a T.sub.g of 100.degree. C., and in
certain embodiments, a polystyrene coating is bake cured. Standards
for physical properties, chemical properties, and/or procedures for
testing the purity/properties of a styrene monomer, a methylstyrene
monomer, (e.g., .alpha.-methylstyrene), a resin comprising a
styrene and/or methylstyrene monomer, are described, for example,
in "ASTM Book of Standards, Volume 06.04, Paint--Solvents; Aromatic
Hydrocarbons," D2827-00, D6367-99, D6144-97, D4590-00, D2119-96,
D2121-00, and D2340-96, 2002.
[0536] Similar to the variability of T.sub.g previously described
for a thermoplastic acrylic resin, a styrene copolymer with a lower
a T.sub.g than polystyrene or other altered properties can be
produced from polymerization with other monomers such as a
butadiene monomer, an acrylic monomer, a maleate ester, an
acrylonitrile, an allyl alcohol, a vinyltoluene, or a combination
thereof. For example, a butadiene monomer decreases lightfastness,
but confers self-crosslinkability to the resin. In another example,
an acrylic resin increases the resin's solubility in an alcohol. In
a further example, an allyl alcohol monomer confers
crosslinkability in combination with a polyol. In certain
embodiments, a styrene-butadiene copolymer resin may be selected.
In certain aspects, a styrene-butadiene resin comprises a carboxyl
moiety to improve an adhesion property, dispersibility in a liquid
component, or a combination thereof. In particular facets, a
styrene-butadiene coating comprises an emulsifier to increase
dispersion in a liquid component, a light stabilizer, or a
combination thereof. A styrene-butadiene coating may be a
thermosetting coating, due to oxidative crosslinking of a butadiene
double bond moiety. However, styrene-butadiene film may have poor
chalking resistance, poor color stability, poor UV resistance, or a
combination thereof. A styrene-butadiene coating may be selected as
a corrosion resistant primer, a wood primer, or a combination
thereof. A styrene-vinnyltoluene-acrylate copolymer coating may be
selected for an exterior coating, a traffic marker paint, a metal
coating (e.g., a metal lacquer), a masonry coating, or a
combination thereof.
[0537] m. Bituminous Binders
[0538] A bituminous binder ("bituminous") is a binder comprising a
hydrocarbon soluble in carbon disulfide, is black or dark colored,
and is obtained from a bitumen deposit and/or as a product of
petroleum processing. A bituminous binder typically is used in
asphalt, tar, and other construction materials. However, in certain
embodiments, a bituminous binder may be used in a coating of the
present invention, particularly in embodiments wherein good
resistance to a chemical such as a petroleum based solvent, an oil,
water, or a combination thereof, is desired. Examples of a
bituminous binder include a coal tar, a petroleum asphalt, a pitch,
an asphaltite, or a combination thereof. In certain embodiments, a
coal tar and/or pitch is combined with an epoxy resin to form a
thermosetting coating. Such as coating may be selected as a
pipeline coating. In other embodiments, an asphaltite and/or
petroleum asphalt may be selected for use as an automotive coating
(e.g., an underbody part coating). An asphaltite and/or petroleum
asphalt coating may further comprise an additional binder such as
an epoxy. In certain aspects, an asphaltite and/or petroleum
asphalt coating is a solvent-borne coating. In specific aspects, an
asphaltite and/or petroleum asphalt coating comprises a
plasticizer. In further aspects, an asphaltite and/or petroleum
asphalt coating comprises a wax to increase abrasion
resistance.
[0539] In further embodiments, bituminous coating may be selected
as a roof coating. Typically, a bituminous roof coating comprises
an extender, a thixotrope, or a combination thereof. Examples of a
thixotrope additive include asbestos, a silicon extender, a
celluosic, a glass fiber, or a combination thereof. In some
aspects, a bituminous roof coating comprises a solvent-borne
coating or a water-borne coating. Examples of solvents that may be
selected include a mineral spirit, an aliphatic hydrocarbon (e.g.,
a naphtha, a mineral spirit), an aromatic solvent (e.g., xylene,
toluene) or a combination thereof. A bituminous roof coating may be
selected as a primer, a topcoat, or a combination thereof. A
bituminous roof topcoat typically further comprises a metallic
pigment.
[0540] In certain aspects, a solvent-borne or water-borne
bituminous coating is an emulsion comprising water and a bituminous
binder. In specific facets, the emulsion further comprises a
solvent, an extender (e.g., a silica), an emusifier (e.g., a
surfactant), or a combination thereof. The extender typically
functions to stabilize the emulsion. In particular facets, the
emulsion bituminous coating is a roof coating, a road coating, a
sealer, a primer, a topcoat, or a combination thereof. In facets
wherein an emulsion bituminous coating is selected as a sealer, an
additional binder may be added to increase solvent resistance.
[0541] In alternative embodiments, a bituminous temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of an addition binder that comprises fewer or no
crosslinkable moieties, reducing the concentration of the a
bituminous resin and/or additional binder, or a combination
thereof.
[0542] n. Polysulfide Binders
[0543] A polysulfide binder is a polymer produced from a reaction
of sodium polysufide, bis(2-chlorethyl)formal and
1,2,3-trichloropropane. Typically, a polysulfide binder is 1 kDa to
8 kDa, including all intermediate ranges and combinations thereof.
A polysulfide binder comprises a thiol ("mercaptan") moiety capable
of crosslinking with an additional binder. A polysulfide may
undergo crosslinking by an oxidative reaction with an additional
binder comprising a peroxide (e.g., dicumen hydroperoxide), a
manganese dioxide, p-quinonedioxime, or a combination thereof. A
polysulfide binder may be crosslinked with a glycidyl epoxide,
though a tertiary amine is preferably part of the coating to
promote this reaction. A polysulfide may undergo crosslinking with
a binder comprising an isocyanate moiety, though it is preferred
that the binder comprise a plurality of isocyanates. A polysulfide
film typically possesses excellent UV resistance, good general
weatherability properties, good chemical resistance, or a
combination thereof.
[0544] In alternative embodiments, a polysulfide temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of an addition binder that comprises fewer or no
crosslinkable moieties, reducing the concentration of the a
bituminous resin and/or additional binder, or a combination
thereof.
[0545] o. Silicone Binders
[0546] The previous described binders are molecules based on
carbon, and are considered herein as "organic binders". A silicone
binder ("silicone") is a binder molecule based on silicone.
Examples of a silicone binder include a polydimethyllsiloxane and a
methyltriacetoxy silane, a methyltrimethoxysilane, a
methyltricyclorhexylaminosilane, a fluorosilicone, a
trifluoropropyl methyl polysiloxane, or a combination thereof. In
general embodiments, a silicone binder comprises a crossreactive
silicon moiety, examples of which are described below. A silicone
coating may be selected for excellent resistance to irradiation
(e.g., UV, infrared, gamma), excellent weatherability, excellent
biodegradation resistance, flame resistance, excellent dielectric
property, which is poor electrical conductivity with little
detrimental effect on an electrostatic field, or a combination
thereof. In specific aspects, a silicon coating is an industrial
coating. In particular facets, a silicon coating is applied to an
appliance part, a furnace part, a jet engine part, an incinerator
part, or a missile part. In other embodiments, a silicon coating
comprises an organic binder. In particular aspects, a silicon
organic binder coating possesses superior heat resistance to an
organic binder coating. In other aspects, the greater the silicon
binder to organic binder ratio, the greater the crosslinking
reactions, greater film hardness, reduced flexibility, or a
combination thereof.
[0547] In general embodiments, a silicone coating is a
thermosetting coating. Often, a silicon coating is a multi-pack
coating due to a limited pot life one the coating components are
admixed. The crosslinking reaction depends upon the binder's
specific silicon moiety. A plurality of binders may be used, each
comprising one or more crosslinking moieties. A binder comprising
crosslinking SiOH and HOSi moieties generally comprises a cure
agent such as a lead octoate, a zinc octoate, or a combination
thereof. In general aspects, the thermosetting SiOH and HOSi
silicon coating is bake cured (e.g., 250.degree. C. for one hour).
A binder comprising crosslinking SiOH and HSi moieties typically
comprises a tin catalyst. A binder comprising crosslinking SiOH and
ROSi moieties, wherein. RO is an alkoxy moiety, also typically
comprises a tin catalyst. A coating prepared using SiOH and ROSi
silicon binder typically further comprises an iron oxide, a glass
microballon, or a combination thereof to improve heat resistance.
This type of silicon may be selected for rocket and jet engine
parts. A binder comprising crosslinking SiOH and CH.sub.3COOSi
moieties is moisture cured, and typically comprises a tin catalyst
(e.g., an organotin compound). A binder comprising crosslinking
SiOH and R.sub.2NOSi moieties, wherein R.sub.2NO is an oxime
moiety, is also moisture cured, and typically comprises a tin
catalyst. The moisture cured silicon coatings may be selected for.
one-pack silicon coatings, though film formation is generally
slower than other types of silicon thermosetting coatings. A binder
comprising crosslinking SiCH.dbd.CH.sub.2 and R.sub.2NOSi moieties,
wherein R.sub.2NO is an oxime moiety, typically comprises a
platinum catalyst, and may be bake cured. A film produced by a
SiCH.dbd.CH.sub.2 and R.sub.2NOSi silicon coating possesses
excellent toughness, flame resistance, or a combination thereof.
Such a coating may be selected for a rocket part. However, coating
components such as a rubber, a tin compound (e.g., an organotin),
or a combination thereof, may inhibit platinum catalyzed film
formation in this silicon coating.
[0548] In certain embodiments, a silicone coating is a
solvent-borne coating. Examples of liquid components that may
function as a silicon solvent include a chlorinated hydrocarbon
(e.g., 1,1,1-trichloroethane), an aromatic hydrocarbon (e.g., a VMP
naphtha, xylene), an aliphatic hydrocarbon, or a combination
thereof. A silicone binder typically is insoluble or poorly soluble
in an oxigenated compound such as an alcohol, a ketone, or a
combination thereof, of relatively low molecular weight (e.g.,
ethanol, isopropanol, acetone). However, a fluorosilicone, which is
a silicone binder that comprises a fluoride moiety, may be combined
with a liquid component comprising a ketone such as methyl ethyl
ketone, methyl isobutyl ketone, or a combination thereof. A
fluorosilicone binder may be selected for producing a film with
excellent solvent resistance. A silicon coating often comprises a
pigment. In specific embodiments, a pigment comprises zinc oxide,
titanium dioxide, zinc orthotitanate, or a combination thereof,
which may improve a film's resistance to extreme temperature
variations, such as those of outerspace. In specific embodiments, a
silicon coating may comprise a silica extender (e.g., fumed
silica), which often increases durability.
[0549] In certain embodiments, a silicon binder comprises a
trifluoropropyl methyl polysiloxane binder. In certain aspects, a
trifluoropropyl methyl polysiloxane binder may be selected for
producing a film with excellent resistance to petroleum products
(e.g., automotive fuel, aircraft fuel), but poor resistance to an
acid or an alkali, particularly at baking conditions.
[0550] In alternative embodiments, a silicon temporary coating
(e.g, a non-film forming coating) may be produced, for example, by
selection of an addition binder that comprises fewer or no
crosslinkable moieties, reducing the concentration of the a silicon
resin and/or additional binder, using a bake-cured silicon coating
at non-baking conditions, inclusion of a rubber, a tin compound
(e.g., an organotin), or a combination thereof.
[0551] 2. Liquid Components
[0552] A liquid component is a chemical composition that is in a
liquid state while comprised in a coating and/or film. A liquid
component is typically added to a coating composition, for example,
to improve a rheological property for ease of application, alter
the period of time that thermoplastic film formation occurs, alter
an optical property (e.g., color, gloss) of a film, alter a
physical property of a coating (e.g., reduce flammability) and/or
film (e.g., increase flexibility), or a combination thereof.
[0553] As would be known to those of ordinary skill in the art,
often a liquid component comprises a volatile liquid that is partly
or fully removed (e.g., evaporated) from the coating during film
formation. Examples of a volatile liquid include a volatile organic
compound ("VOC"), water, or a combination thereof. In many
embodiments, 0% to 100%, including all intermediate ranges and
combinations thereof, of the liquid component is lost during film
formation. Various environmental laws and regulations have
encouraged the reduction of volatile organic compound use in
coatings [see "Paint and Coating Testing Manual, Fourteenth Edition
of the Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 3-12,
1995]. As a consequence, a coating may comprise a solvent-borne
coating, which typically comprises a VOC and was the coating
usually selected prior to enactment of the environmental laws, a
high solids coating, which is generally a solvent-borne coating
formulated with a minimum amount of a VOC, a water-borne coating,
which comprises water and typically even less VOC, or a powder
coating, which comprises little or no VOC.
[0554] In many embodiments, a liquid component may comprise a
liquid composition classified based upon function such as a
solvent, a thinner, a diluent, a plasticizer, or a combination
thereof. A solvent is a liquid component used to dissolve one or
more coating components. A thinner is a liquid component used to
reduce the viscosity of a coating, and often additionally confers
one or more properties to the coating, such as, for example,
dissolving a coating component (e.g., a binder), wetting a
colorizing agent, acting as an antisettling agent, stabilizing a
coating in storage, acting as an antifoaming agent, or a
combination thereof. A diluent is a liquid component that does not
dissolve a binder.
[0555] Liquid components can be classified, based on their chemical
composition, as an organic compound, an inorganic compound, or a
combination thereof. Preferred organic compounds include a
hydrocarbon, an oxygenated compound, a chlorinated hydrocarbon, a
nitrated hydrocarbon, a miscellaneous organic liquid component, or
a combination thereof. A hydrocarbon consists of or consists
essentially of one or more carbon and/or hydrogen atoms. Examples
of a hydrocarbon include an aliphatic hydrocarbon, an aromatic
hydrocarbon, a naphthene, a terpene, or a combination thereof. An
oxygenated compound comprises of one or more carbon, hydrogen
and/or oxygen atoms. Examples of an oxygenated compound include an
alcohol, an ether, an ester, a glycol ester, a ketone, or a
combination thereof. A chlorinated hydrocarbon comprises one or
more carbon, hydrogen and/or chlorine atoms, but does not comprise
an oxygen atom. A nitrated hydrocarbon comprises one or more
carbon, hydrogen and/or nitrogen atoms, but does not comprise an
oxygen atom. A miscellaneous organic liquid component is a liquid
other than a chlorinated hydrocarbon and/or a nitrated hydrocarbon
that comprises one or more carbon, hydrogen and/or other atoms. In
certain aspects, a miscellaneous organic liquid component does not
comprise an oxygen atom. Preferred inorganic compounds include
ammonia, hydrogen cyanide, hydrogen fluoride, hydrogen cyanide,
sulfur dioxide, or a combination thereof. However, an inorganic
compound generally is used at temperatures less than room
temperature, and at pressures greater than atmospheric
pressure.
[0556] In certain embodiments, a liquid component may comprise an
azeotrope. An azeotrope ("azeotropic mixture") is a solution of two
or more liquid components at concentrations that produces a
constant boiling point for the solution. An azeotrope BP ("A-BP")
is the boiling point of an azeotrope. Often, the boiling point
("BP") of the majority component of an azeotrope is higher than the
A-BP, and in some embodiments, such an azeotrope evaporates from a
coating faster than a similar coating that does not comprise the
azeotrope. However, in some aspects, a coating comprising an
azeotrope with a superior evaporation property may possess a lower
flash point temperature, a lower explosion limit, a reduced coating
flow, greater surface defect formation, or a combination thereof,
relative to a similar coating that does not comprise the azeotrope.
Alternatively, an azeotrope may be selected for embodiments wherein
a component's BP is increased. In specific aspects, a coating
comprising such an azeotrope may have a relatively slower
evaporation rate than a similar coating that does not comprise the
azeotrope. It is contemplated that the greater the percentage of
liquid component is an azeotrope, the greater the conference of an
azeotrope's property to a coating. Thus, a specific range of 50% to
100%, 90% to 100%, or 95% to 100%, including all intermediate
ranges and combinations thereof, is sequentially more preferred in
embodiments wherein an azeotrope's property is desired as a
property of a coating.
[0557] In some embodiments, a chemically non-reactive ("inert")
liquid component may be selected. Typically, a liquid component is
selected that is inert relative to a particular chemical reaction
to prevent an undesirable chemical reaction with other coating
components. An example of such an undesirable chemical reaction is
a binder-liquid component reaction that is inhibitory to a desired
binder-binder film-formation reaction. Examples of a liquid
component that are generally inert in an acetal formation reaction
include benzene, hexane, or a combination thereof. An example of a
liquid component that is generally inert in a decarboxylation
reaction includes quinoline. Examples of a liquid component that
are generally inert in a dehydration reaction include benzene,
toluene, xylene, or a combination thereof. An example of a liquid
component that is generally inert in a dehydrohalogenation reaction
includes quinoline. Examples of a liquid component that are
generally inert in a diazonium compound coupling reaction include
ethanol, glacial acetic acid, methanol, pyridine, or a combination
thereof. Examples of a liquid component that are generally inert in
a diazotization reaction include benzene, dimethylformamide,
ethanol, glacial acetic acid, or a combination thereof. Examples of
a liquid component that are generally inert in an esterification
reaction include benzene, dibutyl ether, toluene, xylene, or a
combination thereof. Examples of a liquid component that are
generally inert in a Friedel-Crafts reaction include benzene,
carbon disulfide, 1,2-dichloroethane, nitrobenzene,
tetrachloroethane, tetrachloromethane, or a combination thereof. An
example of a liquid component that is generally inert in a Grignard
reaction includes diethyl ether. Examples of a liquid component
that are generally inert in a halogenation reaction include
dichlorobenzene, glacial acetic acid, nitrobenzene,
tetrachloroethane, tetrachloromethane, trichlorobenzene, or a
combination thereof. Examples of a liquid component that are
generally inert in a hydrogenation reaction include an alcohol,
dioxane, a hydrocarbon, glacial acetic acid, or a combination
thereof. Examples of a liquid component that are generally inert in
a ketene condensation reaction include acetone, benzene, diethyl
ether, xylene, or a combination thereof. Examples of a liquid
component that are generally inert in a nitration reaction include
dichlorobenzene, glacial acetic acid, nitrobenzene, or a
combination thereof. Examples of a liquid component that are
generally inert in an oxidation reaction include glacial acetic
acid, nitrobenzene, pyridine, or a combination thereof. Examples of
a liquid component that are generally inert in a sulfonation
reaction include dioxane, nitrobenzene, or a combination
thereof.
[0558] A solvent-borne coating is a coating wherein 50% to 100%,
the including all intermediate ranges and combinations thereof, of
a coating's liquid component is not water. Generally, the liquid
component of a solvent-borne coating comprises an organic compound,
an inorganic compound, or a combination thereof. The liquid
component of a solvent-borne coating may function as a solvent, a
thinner, a diluent, a plasticizer, or a combination thereof. In
certain embodiments, a solvent-borne coating may comprise water. In
specific aspects, the water may function as a solvent, a thinner, a
diluent, or a combination thereof. The water component of a
solvent-borne coating may comprise 0% to 49.999%, the including all
intermediate ranges and combinations thereof, of the liquid
component. In certain embodiments, the water component of a
water-borne coating may be fully or partly miscible in the
non-aqueous liquid component. Examples of the percent of water that
is miscible, by weight at 20.degree. C., in various liquids
typically used in solvent-borne coatings include 0.01% water in
tetrachloroethylene; 0.02% water in ethylbenzene; 0.02% water in
p-xylene; 0.02% water in tricholorethylene; 0.05% water in
1,1,1-tricholoroethane; 0.05% water in toluene; 0.1% water in
hexane; 0.16% water in methylene chloride; 0.2% water in dibutyl
ether; 0.2% water in tetrahydronaphthalene; 0.42% water in
diisobutyl ketone; 0.5% water in cyclohexyl acetate; 0.5% water in
nitropropane; 0.6% water in 2-nitropropane; 0.62% water in butyl
acetate; 0.72% water in dipentene; 0.9% water in nitroethane; 1.2%
water in diethyl ether; 1.3% water in methyl tert-butyl ether; 1.4%
water in trimethylcyclohexanone; 1.65% water in isobutyl acetate;
1.7% water in butyl glycol acetate; 1.9% water in isopropyl
acetate; 2.4% water in methyl isobutyl ketone; 3.3% water in ethyl
acetate; 3.6% water in cyclohexanol; 4.0% water in
trimethylcyclohexanol; 4.3% water in isophorone; 5.8% water in
methylbenzyl alcohol; 6.5% water in ethyl glycol acetate; 7.2%
water in hexanol; 7.5% water in propylene carbonate; 8.0% water in
methyl acetate; 8.0% water in cyclohexanone; 12.0% water in methyl
ethyl ketone; 16.2% water in isobutanol; 19.7% water in butanol;
25.0% water in butyl glycolate; or 44.1% water in 2-butanol.
[0559] Various examples of such liquid components are described
herein, including properties often used to select a chemical
composition for use as a liquid component for a particular coating
composition. Additionally, standards for physical properties,
chemical properties, and/or procedures for testing
purity/properties, are described for various types of liquid
components (e.g., hydrocarbons, cycloaliphatic hydrocarbons,
aromatic hydrocarbons, alcohols, ketones, esters, glycol ethers,
mineral spirits, miscellaneous solvents, plasticizers) in, for
example, "ASTM Book of Standards, Volume 06.04, Paint--Solvents;
Aromatic Hydrocarbons," D4790-99, D268-01, D3437-99, D1493-97,
D235-02, D1836-02, D3735-02, D3054-98, D5309-02, D4734-98,
D2359-02, D4492-98, D4077-00, D3760-02, D6526-00, D841-02, D843-97,
D5211-01, D5471-97, D5871-98, D5713-00, D852-02, D1685-00,
D4735-02, D3797-00, D3798-00, D5135-02, D5136-00, D5060-95,
D3193-96, D3734-01, D1152-97, D770-95, D3622-95, D1007-00,
D1719-95, D304-95, D319-95, D2635-01, D1969-01, D2306-00, D1612-95,
D5008-01, D268-01, D1078-01, D329-02, D1363-94, D740-94, D2804-02,
D1153-94, D3329-99, D2917-02, D3893-99, D4360-90, D2627-02,
D2916-88, D2192-96, D4614-95, D3545-02, D3131-02, D3130-95,
D1718-98, D4615-95, D3540-90, D1617-90, D2634-02, D5137-01,
D3728-99, D4835-93, D4773-02, D3128-02, D331-95, D330-93, D4837-02,
D4773-02, D4836-95, D5776-99, D5808-95, D5917-02, D6069-01,
D6212-99, D6313-99, D6366-99, D6428-99, D6621-00, D6809-02,
D5399-95, D6229-01, D6563-00, D6269-98, D3257-01, D847-96,
D1613-02, D848-02, D1614-95, D4367-02, D4534-99, D2360-00,
D1353-02, D1492-02, D849-02, D3961-98, D1364-02, D3160-96, D1476-02
and D1722-98, D853-97, D5194-96, D363-90, D1399-95, D1468-93,
D3620-98, D3546-90, and D1721-97, 2002.
[0560] a. Solvents, Thinners, and Diluents
[0561] A coating may comprise a liquid component that may function
as a solvent, a thinner, a diluent or a combination thereof. In one
embodiment of a coating, a particular liquid component may function
as a solvent, while in another coating composition comprising, for
example, a different binder the same liquid component may function
as a thinner and/or a diluent. Whether a liquid component functions
primarily as a solvent, a thinner, or a diluent depends
considerably upon the particular solvent and/or rheological
property the liquid component confers to a specific coating
composition. For example, the ability of the liquid component to
function as a solvent, or lack thereof of such ability, relative to
the other coating components generally differentiates a solvent
from a diluent. A thinner is primarily included into a coating
composition in combination with a solvent and/or diluent to alter a
rheological property such as to reduce viscosity, enhance flow,
enhance leveling, or a combination thereof. In addition to the
ability of one of ordinary skill in the art to discern such
differences of use for a specific liquid composition in a coating,
examples of differing solubility properties for specific categories
of liquid components, and empirical techniques for determining the
solubility properties of a specific liquid component, relative to
another coating component, are described herein.
[0562] A solute is a coating component dissolved by a solvent
liquid component. A solute may be in solid, liquid or gas from
prior to being dissolved. Solvency ("solvent power") is the ability
of a solvent to dissolve a solute, maintain a solute in solution
upon addition of a diluent, and reduce the viscosity of a solution.
A solvent is typically used to produce a solvent-borne coating,
wherein the coating possesses desirable a Theological property for
application to a surface and/or creation of a film of a desirable
thickness. Additionally, a solvent may contribute to an appearance
property, a physical property, a chemical property, or a
combination thereof, of a coating and/or film. In most embodiments,
a solvent is a volatile component of a coating, wherein 50% to
100%, including all intermediate ranges and combinations thereof,
of the solvent is lost (e.g., evaporates) during film formation. In
certain aspects, the rate of solvent loss slows during application
and/or film formation. Such a change in solvent loss rate may
promote a desirable Theologically related property during
application and/or initial film formation, such as ease of
application, minimum sag, reduce excessive flow, or a combination
thereof, while still promoting a desirable rheologically related
property post-application, such as a desirable leveling property, a
desirable adhesion property, or a combination thereof.
[0563] Depending upon the ability of a liquid component to
dissolve, partly dissolve, or unsuccessfully dissolve a coating
component, a coating may comprise, a real solution, a colloidal
solution or a dispersion, respectively. Often the ability of a
liquid component to dissolve a coating component is detrimentally
affected by increasing particulate matter size and/or molecular
mass of the coating component. For example, a real solution
comprises a clear and/or homogenous liquid solution. In typical
embodiments, a real solution is produced when a potential solute of
1.0 nm or less in diameter is combined with a solvent. A colloidal
solution comprises a physically non-homogenous solution, which may
be a clear to opalescent in appearance. Often, a colloidal solution
is produced when a potential solute of between 1.0 nm to 100 nm
("0.1 .mu.m") in diameter is combined with a solvent. A dispersion
is a composition comprising two liquid and/or solid phases, which
is typically turbid to milky in appearance. Generally, a dispersion
is produced when a potential solute of greater than 0.1 .mu.m in
diameter is combined with a solvent. In many aspects, a coating
composition may comprise a combination of a real solution, a
colloidal solution and/or a dispersion, depending upon the various
solubility's of coating components and liquid components. For
example, a paint may comprise a real solution of a binder and a
liquid component, and a dispersion of a pigment within the liquid
component.
[0564] Depending upon other coating components, a liquid component
may function as an active solvent or a latent solvent. An active
solvent is capable of dissolving a solute. Additionally, an active
solvent often reduces viscosity of a coating composition. In
certain embodiments, an ester, a glycol ether, a ketone, or a
combination thereof may be selected for use as an active solvent. A
latent solvent, in pure form, does not demonstrate solute
dissolving ability. However, the latent solvent may demonstrate the
ability to dissolve a solute in a combination of an active solvent
and the latent solvent; confer a synergistic improvement in the
dissolving ability of an active solvent when combined with the
active solvent, or a combination thereof. In certain embodiments,
an alcohol may be selected for use as a latent solvent. In certain
embodiments, a latent solvent is a thinner. A diluent, whether in
pure form or in combination with an active solvent and/or a latent
solvent, does not demonstrate solute dissolving ability, but may be
combined with an active solvent and/or latent solvent to produce a
liquid component with a suitable ability to dissolve a coating
component. In certain embodiments, hydrocarbon may be selected for
use as a diluent. In particular aspects, a hydrocarbon diluent
comprises an aromatic hydrocarbon, an aliphatic hydrocarbon, or a
combination thereof. In particular facets, an aromatic hydrocarbon
diluent may be selected, due to a generally greater tolerance by a
many solvents relative to an aliphatic hydrocarbon. In certain
aspects, a diluent is used to alter a rheological property (e.g.,
reduce viscosity) of a coating composition, reduce cost of a
coating composition, or a combination thereof.
[0565] The ability of a solvent to dissolve a potential solute is
related to the intermolecular interactions between the solvent
molecules, between the potential solute molecules, between the
solvent and the potential solute, as well as the molecular size of
the potential solute. Examples of intermolecular interactions
include, for example, ionic ("Coulomb"), dipole-dipole
("directional"), ionic-dipole, induction ("permanent dipole/induced
dipole"), dispersion ("nonpolar," "atomic dipole," "London-Van der
Walls"), hydrogen bond, or a combination thereof. As is known to
those of ordinary skill in the art, the sum of intramolecular
interactions for a compound, relevant for the preparation of a
solution, is the solubility parameter (".delta."). The solubility
parameter is a measure of the total energy needed to separate
molecules of a liquid. Such a separation of molecules of a solvent
occurs during the incorporation of the molecules of a solute during
the dissolving process. The solubility parameter is the square root
of the molar energy of vaporization of a liquid divided by the
molar volume of a liquid, measured at 25.degree. C. Additionally,
the solubility parameter can also be expressed as the square root
of the sum of the squares of the dispersion (".delta..sub.d"),
polar (".delta..sub.p") and hydrogen bond (".delta..sub.h")
solubility parameters.
[0566] Often, preparation of a coating composition may be aided by
comparing the solubility parameter of a potential solvent and a
potential solute (e.g., a binder) to ascertain the theoretical
ability of a coating composition comprising a solution to be
created. In many embodiments, coating components, wherein at least
one coating component comprises a liquid, with a solubility
parameter that is less than an absolute value of 6 are able to form
a solution. The closer this value is to 0, the greater the general
ability to form a solution. Additionally, the lower the individual
absolute difference (e.g., six or less) between the dispersion
solubility parameters of coating components, the polar solubility
parameter of coating components, and/or the hydrogen bond
solubility parameter of coating components, the generally greater
ability to form a solution. The solubility parameter, dispersion
solubility parameter, polar solubility parameter, and hydrogen bond
solubility parameter, and methods for determining such values, and
additional methods for determining the theoretical ability of
coating components to form a solution have been described (see, for
example, in "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D3132-84, 2002).
[0567] However, due to exceptions to the ability of certain liquid
components and potential solute coating components to form
solutions, empirically determining the ability of a solute to
dissolve in a solvent may be desirable in certain embodiments.
Standard techniques for determining the ability of a liquid
component comprising one or more liquids to function as an active
solvent, a latent solvent, a diluent, or a combination thereof,
relative to one or more potential solutes are known to those of
ordinary skill in the art. For example, the solvency of a liquid
component comprising an active solvent (e.g., an oxygenated
compound), a latent solvent, a diluent (e.g., a hydrocarbon), or a
combination thereof, particularly for use in a lacquer coating, may
be determined as described in "ASTM Book of Standards, Volume
06.04, Paint--Solvents; Aromatic Hydrocarbons," D1720-96, 2002). In
an additional example, the solvency for a liquid component that
primarily comprises a hydrocarbon, and comprises little or lacks an
oxygenated compound, may be determined as described in "ASTM Book
of Standards, Volume 06.04, Paint--Solvents; Aromatic
Hydrocarbons," D1133-02, 2002). In a further example, the solvency
of a solution comprising liquid component and an additional coating
component (e.g., a binder) may be used to determined, as described
in "ASTM Book of Standards, Volume 06.03, Paint--Pigments, Drying
Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D1545-98, D1725-62, D5661-95, D5180-93, D6038-96,
D5165-93, and D5166-97, 2002. In a supplemental example, the
dilutability of a solution comprising liquid component (e.g., a
solvent and diluent) and an additional coating component (e.g., a
binder) may be used to determined, as described in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D5062-96, 2002.
[0568] In certain embodiments, a liquid component may be selected
on the basis of evaporation rate. The evaporation rate of a coating
directly affects a physical aspect of film formation caused by loss
of a liquid component, as well as the pot life of a coating, such
as after a coating container is opened. Though the evaporation rate
is known for various pure chemicals, one of ordinary skill in the
art can empirically determine the evaporation rate of a liquid
component and/or a coating, in "ASTM Book of Standards, Volume
06.01, Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D3539-87, 2002. Additionally, the boiling point range
of a liquid component often is useful in estimating whether the
liquid component will evaporate faster or slower relative to
another liquid component. Examples of methods for measuring a
boiling point for a liquid component (e.g., a hydrocarbon, a
chlorinated hydrocarbon) are described in "ASTM Book of Standards,
Volume 06.04, Paint--Solvents; Aromatic Hydrocarbons," D1078-01 and
D850-02e1, 2002. The evaporation rate is also related to the flash
point of a liquid component and/or coating. In certain embodiments,
a liquid component may be selected on the basis of flash point
and/or fire point, which is a measure of the danger of use of a
flammable coating composition in, for example, storage, application
in an indoor environment, etc. A flash point is the "lowest
temperature at which the liquid gives off enough vapor to form an
ignitable mixture with air to produce a flame when a source of
ignition is brought close to the surface of the liquid under
specified conditions of test at standard barometric pressure (760
mmHG, 101.3 kPa)," and a fire point is "the lowest temperature at
which sustained burning of the sample takes place for at least 5
seconds" ["Paint and Coating Testing Manual, Fourteenth Edition of
the Gardner-Sward Handbook" (Koleske, J. V. Ed.), pp. 140 and 142,
1995]. Examples of methods for measuring the flash point and/or
fire point for a liquid component and/or a coating are described in
and "ASTM Book of Standards, Volume 06.01, Paint--Tests for
Chemical, Physical, and Optical Properties; Appearance," D1310-01,
D3934-90, D3941-90, and D3278-96e1, 2002.
[0569] Though it is contemplated that most or all liquid component
will be lost from a coating composition during film formation, a
liquid component may still contribute to the visual properties of a
coating and/or film. In embodiments wherein a liquid component is
selected as a colorizing agent, the color and/or darkness of the
liquid may be empirically measured (see, for example, "ASTM Book of
Standards, Volume 06.04, Paint--Solvents; Aromatic Hydrocarbons,"
D1209-00, D1686-96, and D5386-93b, 2002); and "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D1544-98, 2002. In some
embodiments, a liquid component and/or coating may be selected on
the basis of odor (e.g., faint odor, pleasant odor, etc.). A
coating or coating component can be evaluated for suitability in a
particular application based on odor using, for example, techniques
described in "ASTM Book of Standards, Volume 06.04,
Paint--Solvents; Aromatic Hydrocarbons," D1296-01, 2002; and "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D6165-97, 2002.
[0570] (1) hydrocarbons
[0571] A hydrocarbon is typically obtained as a petroleum product,
a vegetable product, or a combination thereof. As a consequence of
imperfect purification (e.g., distillation) from these sources, a
hydrocarbon is often a mixture of chemical components. A
hydrocarbon may be selected as an active solvent to dissolve an oil
(e.g., a drying oil), an alkyd, an asphalt, a rosin, a petroleum
product, or a combination thereof. A hydrocarbon is more suitable
as a latent solvent or diluent in embodiments wherein an acrylic
resin, an epoxide resin, a nitrocellulose resin, an urethane resin,
or a combination thereof is to be dissolved. However, a hydrocarbon
generally is immiscible in water.
[0572] (i) Aliphatic Hydrocarbons
[0573] In general embodiments, an aliphatic hydrocarbon may be
selected as an active solvent for an alkyd, an oil, wax, a
polyisobutene, a polyethylene, a poly(butyl acrylate), a poly(butyl
methacrylate), a poly(vinyl ethers), or a combination thereof. In
other embodiments, an aliphatic hydrocarbon may be selected as a
diluent in combination with an additional liquid component. In
alternative embodiments wherein an aliphatic hydrocarbon is
selected as a non-solvent liquid component, a composition
comprising a polar binder, a cellulose derivative, or a combination
thereof, is usually insoluble. An aliphatic hydrocarbon is often
selected as a liquid component in embodiments wherein a chemically
inert liquid component is desired. Examples of an aliphatic
hydrocarbon include, a petroleum ether, pentane (CAS No. 109-66-0),
hexane (CAS No. 110-54-3), heptane (CAS No.142-82-5), isododecane
(CAS No. 13475-82-6), a kerosene, a mineral spirit, a VMP naphthas
or a combination thereof. A hexane, a heptane, or a combination
thereof, may be selected for a coating wherein rapid evaporation of
such a liquid component is desired (e.g., a fast drying lacquer).
An example of an azeotrope comprising an aliphatic hydrocarbon
includes an azeotrope comprising hexane. Examples of an azeotrope
comprising a majority of hexane (BP 65.degree. C. to 70.degree. C.)
include those comprising 2.5% isobutanol (azeotrope BP 68.3.degree.
C.); 5.6% water (A-BP 61.6.degree. C.); 21% ethanol (A-BP
58.7.degree. C.); 22% isopropyl alcohol (A-BP 61.0.degree. C.);
26.9% methanol (A-BP 50.0C); 37% methyl ethyl ketone (A-BP
64.2.degree. C.); or 42% ethyl acetate (A-BP 65.0.degree. C.).
[0574] As would be known to one of ordinary skill in the art, an
aliphatic hydrocarbon can comprise a petroleum distillation product
of heterogeneous chemical composition. Such an aliphatic
hydrocarbon may be classified by a physical and/or chemical
property (e.g., boiling point range, flash point, evaporation rate)
(see, for example, "ASTM Book of Standards, Volume 06.04,
Paint--Solvents; Aromatic Hydrocarbons," D235-02 and D3735, 2002).
In certain embodiments, such a petroleum distillation product
aliphatic hydrocarbon may be classified, for example, as a mineral
spirit, a VMP naphthas or a kerosene (e.g., deodorized kerosene). A
mineral spirit ("white spirit," "petroleum spirit") is a petroleum
distillation fraction with a boiling point between 149.degree. C.
to 204.degree. C., including all intermediate ranges and
combinations thereof; and a flash point of 38.degree. C. or
greater. A mineral spirit may further be classified as a regular
mineral spirit, which possesses the properties previously described
for a mineral spirit; a high flash mineral spirit, which possesses
a higher minimum flash point (e.g., 55.degree. C. or greater); a
low dry point mineral spirit ("Stoddard solvent"), which typically
evaporates 50% faster than a regular mineral spirit; or an odorless
mineral spirit, which generally possesses less odor than a regular
mineral spirit, but may also possess relatively weaker solvency
property. A mineral spirit may be selected for embodiments wherein
a solvent and/or diluent is desired for an alkyd coating, a
chlorinated rubber coating, an oil-coating, a vinyl chloride
copolymer coating, or a combination thereof. A VMP naphtha possess
a similar solvency property as a mineral spirit, but evaporates
faster with a BP of 121.degree. C. to 149.degree. C., including all
intermediate ranges and combinations thereof, and typically has a
flash point of 4.degree. C. or greater. A VMP naphtha may further
be classified as a regular VMP naphtha, which possesses the
properties previously described for a VMP naphtha; a high flash VMP
naphtha, which possesses a higher minimum flash point (e.g.,
34.degree. C. or greater); or an odorless VMP naphtha, which
generally possesses less odor than a regular mineral spirit. A VMP
naphtha may be selected for a coating that is spray applied, an
industrial coating, or a combination thereof. A petroleum ether is
a petroleum distillation fraction with a boiling point between
35.degree. C. to 80.degree. C., including all intermediate ranges
and combinations thereof, with a low flash point (e.g., -46.degree.
C.), and may be used in embodiments wherein rapid evaporation is
desired.
[0575] (ii) Cycloaliphatic Hydrocarbons
[0576] In embodiments wherein a cycloaliphatic hydrocarbon is
selected as a solvent, a composition comprising an oil, alkyd,
bitumen, rubber, or a combination thereof, usually can be
dissolved. In alternative embodiments wherein a cycloaliphatic
hydrocarbon is selected as a non-solvent liquid component, a
composition comprising a polar binder such as a urea-formaldehyde
binder, a melamine-formaldehyde binder, a phenol-formaldehyde
binder; a cellulose derivative, such as, a cellulose ester binder;
or a combination thereof, is usually insoluble. A cycloaliphatic
hydrocarbon is generally soluble in other organic solvents, but not
soluble in water. Examples of a cycloaliphatic hydrocarbon include
cyclohexane (CAS No. 110-82-7); methylcyclohexane (CAS
No.108-87-2); ethylcyclohexane (CAS No.1678-91-7);
tetrahydronaphthalene (CAS No. 119-64-2); decahydronaphthalene (CAS
No. 91-17-8); or a combination thereof. Tetrahydronaphthalene is
often selected for coatings wherein oxidation of a binder is
preferable during film formation; a high gloss is preferable in a
film, smooth surface is preferable in a film, or a combination
thereof. An example of an azeotrope comprising a cycloaliphatic
hydrocarbon includes an azeotrope comprising cyclohexane. Examples
of an azeotrope comprising a majority of cyclohexane (BP
80.5.degree. C. to 81.5.degree. C.) include those comprising 8.5%
water (A-BP 69.8.degree. C.); 10% butanol (A-BP 79.8.degree. C.);
14% isobutanol (A-BP 78.1.degree. C.); 20% propanol (A-BP
74.3.degree. C.); 37% methanol (A-BP 54.2.degree. C.); or 40%
methyl ethyl ketone (A-BP 72.0.degree. C.).
[0577] (iii) Terpene Hydrocarbons
[0578] A terpene typically possesses a superior solvency property,
stronger odor, or a combination thereof, relative to an aliphatic
hydrocarbon. Examples of a terpene include wood terpentine oil (CAS
No. 8008-64-2); pine oil (CAS No. 8000-41-7); .alpha.-pinene (CAS
No. 80-56-8); .beta.-pinene; dipentene (CAS No. 138-86-3);
D-limonene (CAS No. 5989-27-5); or a combination thereof. Dipentene
may be selected for embodiments wherein a superior solvency
property, a slower evaporation rate, or a combination thereof,
relative to a turpentine, is desired. Pine oil may be classified as
an oxygenated compound, but is described under hydrocarbons due to
convention by those of skill in the art. Pine oil generally
comprises a terpene alcohol. Pine oil may be selected for
embodiments wherein a greater range of solvency for solutes, a slow
evaporation rate, or a combination thereof, is desired. An example
of an azeotrope comprising a terpene includes an azeotrope
comprising .alpha.-pinene. An example of an azeotrope comprising a
majority of .alpha.-pinene (BP 154.0.degree. C. to 156.0.degree.
C.) includes an azeotrope comprising 35.5% cyclohexanol (A-BP
149.9.degree. C.).
[0579] As would be known to one of ordinary skill in the art, a
terpene hydrocarbon ("terpene") can comprise a by-product from
pines tree and/or citrus processing of heterogeneous chemical
composition. Such a terpene hydrocarbon (e.g., a terpentine) may be
classified by a physical and/or chemical property (see, for
example, "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D804-02, D13-02, D233-02, D801-02, D802-02, and
D6387-99, 2002. Examples of a terpentine include a gum turpentine,
a steam-distilled wood turpentine, a sulfate wood turpentine, a
destructively distilled wood turpentine, or a combination thereof.
Both a gum turpentine and a sulfate wood turpentine generally
comprise a combination of .alpha.-pinene and a lesser quantity of
.beta.-pinene. A steam-distilled wood terpentine generally
comprises .alpha.-pinene and a lesser component of dipentene and
one or more other terpenes. Destructively distilled wood turpentine
generally comprises various aromatic hydrocarbons and a lesser
quantity of one or more terpenes.
[0580] (iv) Aromatic Hydrocarbons
[0581] An aromatic hydrocarbon typically possesses a greater
solvency property and/or odor relative to other hydrocarbon types.
Examples of an aromatic hydrocarbon include benzene (CAS No.
71-43-2); toluene (CAS No.108-88-3; "methylbenzene"); ethylbenzene
(CAS No.100-41-4); xylene (CAS No. 1330-20-7); cumene
("isopropylbenzene"; CAS No. 98-82-8); a type I high flash aromatic
naphthas; a type II high flash aromatic naphthas; mesitylene (CAS
No. 108-67-8); pseudocumene (CAS No. 95-63-6); cymol (CAS No.
99-87-6); styrene (CAS No. 100-42-5); or a combination thereof.
Xylene typically comprises o-xylene (CAS No. 56004-61-6); m-xylene
(CAS No.108-38-3); p-xylene (CAS No. 41051-88-1); and trace
ethylbenzene. Toluene may be selected for embodiments wherein rapid
evaporation is desired. In specific aspects, toluene may be
selected for a spray applied coating, an industrial coating, or a
combination thereof. Xylene may be selected for embodiments wherein
a moderate evaporation rate is desired. In specific aspects, xylene
may be selected for an industrial coating. As would be known to one
of ordinary skill in the art, an aromatic hydrocarbon may comprise
a petroleum-processing product of heterogeneous chemical
composition such as a high flash aromatic naphtha (e.g., type I,
type II). A type I high flash aromatic naphtha and type II high
flash aromatic naphtha possess a minimum flash point of 38.degree.
C. and 60.degree. C., respectively. Standards for the
characteristic chemical an/or physical property of an aromatic
naphtha are known to those of ordinary skill in the art (see, for
example, "ASTM Book of Standards, Volume 06.04, Paint--Solvents;
Aromatic Hydrocarbons," D3734, 2002). A high flash naphtha
typically has a slow evaporation rate. In specific embodiments, a
high flash aromatic naphtha may be used in an industrial coating, a
coating that is baked, or a combination thereof. An example of a
high flash aromatic is Solvesso 100 (CAS No. 64742-95-6). Examples
of an azeotrope comprising an aromatic hydrocarbon include an
azeotrope comprising toluene or m-xylene. Examples of an azeotrope
comprising a majority of toluene (BP 110.degree. C. to 111.degree.
C.) include those comprising 27% butanol (A-BP 105.6.degree. C.);
or 44.5% isobutanol (A-BP 100.9.degree. C.). Examples of an
azeotrope comprising a majority of m-xylene (BP 137.0.degree. C. to
142.0.degree. C.) include those comprising 14% cyclohexanol (A-BP
143.0.degree. C.); or 40% water (A-BP 94.5.degree. C.).
[0582] (2) Oxygenated Compounds
[0583] An oxygenated compound ("oxygenated liquid compound") is
typically chemically synthesized by standard chemical manufacturing
techniques. As a consequence, an individual oxygenated compound is
typically an extremely homogenous chemical composition, with
singular, rather than a range of, chemical and physical properties.
The oxygen moiety of an oxygenated compound generally enhances the
strength and breadth of solvency for potential solutes relative to
a hydrocarbon. Additionally, an oxygenated compound typically has
some or complete miscibility with water. Examples of an oxygenated
compound include an alcohol, an ester, a glycol ether, a ketone, or
a combination thereof. As would be known to one of ordinary skill
in the art, a liquid component often comprises a combination of an
alcohol, an ester, a glycol ether, a ketone and/or an addition
liquid to produce suitable chemical and/or physical properties for
a coating and/or film.
[0584] (i) Alcohols
[0585] An alcohol comprises an alcohol moiety. However, a preferred
"alcohol" comprises a single hydroxyl moiety. The alcohol moiety
confers miscibility with water. Consequentially, increasing
molecular size of an alcohol comprising a single alcohol moiety
generally reduces miscibility with water. Alcohols typically
possess a mild and/or pleasant odor. An alcohol is typically a poor
primary solvent, though ethanol is an exception relative to a
solute comprising a phenolic and/or polyvinyl resin. An alcohol may
be selected as a latent solvent, co-solvent, a coupling solvent, a
diluent, or combination thereof such as with solute comprising a
nitrocellulose lacquer, melamine-formaldehyde, urea formaldehyde,
alkyd, or combination thereof. Examples of an alcohol include
methanol (CAS No. 67-56-1); ethanol (CAS No. 64-17-5); propanol
(CAS No. 71-23-8); isopropanol (CAS No. 67-63-0); 1-butanol (CAS
No. 71-36-3); isobutanol (CAS No. 78-83-1); 2-butanol (CAS No.
78-92-2); tert-butanol (CAS No. 75-65-0); amyl alcohol (CAS No.
71-41-0); isoamyl alcohol (123-51-3); hexanol (25917-35-5);
methylisobutylcarbinol (CAS No. 108-11-2); 2-ethylbutanol (CAS No.
97-95-0); isooctyl alcohol (CAS No. 26952-21-6); 2-ethylhexanol
(CAS No. 104-76-7); isodecanol (CAS No. 25339-17-7); cylcohexanol
(CAS No.108-93-0); methylcyclohexanol (CAS No. 583-59-5);
trimethylcyclohexanol; benzyl alcohol (CAS No.100-51-6);
methylbenzyl alcohol (CAS No. 98-85-1); furfuryl alcohol (CAS No.
98-00-0); tetrahydrofurfuryl alcohol (CAS No. 97-99-4); diacetone
alcohol (CAS No.123-42-2); trimethylcyclohexanol (116-02-9); or a
combination thereof. Furfuryl alcohol and tetrahydrofurfuryl
alcohol may be selected as a primary solvent for a polyvinyl
binder. Examples of an azeotrope comprising an alcohol include an
azeotrope comprising butanol, ethanol, isobutanol, or methanol.
Examples of an azeotrope comprising a majority of butanol (BP
117.7.degree. C.) include those comprising 97% butanol and 3%
hexane (A-BP 67.degree. C.); 32% p-xylene (A-BP 115.7.degree. C.);
32.8% butyl acetate (A-BP 117.6.degree. C.); 44.5% water (A-BP
93.degree. C.); or 50% isobutyl acetate (A-BP 114.5.degree. C.).
Examples of an azeotrope comprising a majority of ethanol (BP
78.3.degree. C.) include those comprising 4.4% water (A-BP
78.2.degree. C.); or 32% toluene (A-BP 76.7.degree. C.). Examples
of an azeotrope comprising a majority of isobutanol (BP
107.7.degree. C.) include those comprising 2.5% hexane (A-BP
68.3.degree. C.); 5% isobutyl acetate (A-BP 107.6.degree. C.); 17%
p-xylene (A-BP 107.5.degree. C.); 33.2% water (A-BP 89.9.degree.
C.); or 48% butyl acetate (A-BP 80.1.degree. C.). An example of an
azeotrope comprising a majority of methanol (BP 64.6.degree. C.)
includes an azeotrope comprising 30% methyl ethyl ketone (A-BP
63.5.degree. C.).
[0586] (ii) Ketones
[0587] A ketone comprises a ketone moiety. However, a preferred
ketone comprises a single ketone moiety. A ketone generally
possesses some miscibility with water, and a strong odor. In
general embodiments, a ketone may be selected as a primary solvent,
thinner, or combination thereof. Examples of a ketone include
acetone (CAS No. 67-64-1); methyl ethyl ketone (CAS No. 78-93-3);
methyl propyl ketone (CAS No. 107-87-9); methyl isopropyl ketone
(CAS No. 563-80-4); methyl butyl ketone (CAS No. 591-78-6); methyl
isobutyl ketone (CAS No. 108-10-1); methyl amyl ketone (CAS No.
110-43-0); methyl isoamyl ketone (CAS No. 110-12-3); diethyl ketone
(CAS No. 96-22-0); ethyl amyl ketone (CAS No. 541-85-5); dipropyl
ketone (CAS No. 110-43-0); diisopropyl ketone (CAS No. 565-80-0);
cyclohexanone (CAS No. 108-94-1); methylcylcohexanone (CAS No.
1331-22-2); trimethylcyclohexanone (CAS No. 873-94-9); mesityl
oxide (CAS No. 141-79-7); diisobutyl ketone (CAS No. 108-83-8);
isophorone (CAS No. 78-59-1); or a combination thereof. Acetone may
be selected for complete miscibility in water, fast evaporation, or
a combination thereof. In certain embodiments, acetone may be used
as a liquid component in an aerosol, a spay-applied coating, or a
combination thereof. In specific aspects, acetone may be used as a
thinner. In other aspects, acetone may be used in a coating wherein
nitrocellulose, an acrylic, or a combination thereof, is dissolved.
Methyl ethyl ketone, methyl isobutyl ketone, and isophorone may be
selected in embodiments wherein a fast evaporation rate, moderate
evaporation rate, or slow evaporation rate, respectively, is
desired. In specific facets, isophorone may be selected for a baked
coating, an industrial coating, or a combination thereof. Examples
of an azeotrope comprising a ketone include an azeotrope comprising
acetone, methyl ethyl ketone or methyl isobutyl ketone. Examples of
an azeotrope comprising a majority of acetone (BP 56.2.degree. C.)
include those comprising 12% methanol (A-BP 55.7.degree. C.); or
41% hexane (A-BP 49.8.degree. C.). Examples of an azeotrope
comprising a majority of methyl ethyl ketone (BP 79.6.degree. C.)
include those comprising 11% water (A-BP 73.5.degree. C.); 32%
isopropyl alcohol (A-BP 77.5.degree. C.); or 34% ethanol (A-BP
74.8.degree. C.). Examples of an azeotrope comprising a majority of
methyl isobutyl ketone (BP 114.degree. C. to 117.degree. C.)
include those comprising 24.3% water (A-BP 87.9.degree. C.); or 30%
butanol (A-BP 114.35.degree. C.).
[0588] (iii) Esters
[0589] An ester may comprise an alkyl acetate, an alkyl propionate,
a glycol ether acetate, or a combination thereof. An ester
generally possesses a pleasant odor. In general embodiments, an
ester possesses a solubility property that decreases with
increasing molecular weight. A glycol ester acetate typically
possesses a slow evaporation rate. In specific aspects, a glycol
ester acetate may be selected as a retarder solvent, a coalescent,
or a combination thereof. Examples of an ester include methyl
formate (CAS No. 107-31-3); ethyl formate (CAS No. 109-94-4); butyl
formate (CAS No. 592-84-7); isobutyl formate (CAS No. 542-55-2);
methyl acetate (CAS No. 79-20-9); ethyl acetate (CAS No. 141-78-6);
propyl acetate (CAS No. 109-60-4); isopropyl acetate (CAS No.
108-21-4); butyl acetate (CAS No. CAS-No. 123-86-4); isobutyl
acetate (CAS No. 110-19-0); sec-butyl acetate (CAS No. 105-46-4);
amyl acetate (CAS No. 628-63-7); isoamyl acetate (CAS No.
123-92-2); hexyl acetate (CAS No. 142-92-7); cyclohexyl acetate
(CAS No. 622-45-7); benzyl acetate (CAS No. 140-11-4); methyl
glycol acetate (CAS No. 110-49-6); ethyl glycol acetate (CAS
No.111-15-9); butyl glycol acetate (CAS No. 112-07-2); ethyl
diglycol acetate (CAS No.111-90-0); butyl diglycol acetate (CAS No.
124-17-4); 1-methoxypropyl acetate (CAS No. 108-65-6); ethoxypropyl
acetate (CAS No. 54839-24-6); 3-methoxybutyl acetate (CAS No.
4435-53-4); ethyl 3-ethoxypropionate (CAS No. 763-69-9); isobutyl
isobutyrate (CAS No.97-85-8); ethyl lactate (CAS No.97-64-3); butyl
lactate (CAS No.138-22-7); butyl glycolate (CAS No. 7397-62-8);
dimethyl adipate (CAS No. 627-93-0); glutarate (CAS No.119-40-0);
succinate (CAS No.106-65-0); ethylene carbonate (CAS No.96-49-1);
propylene carbonate (CAS No.108-32-7); butyrolactone (CAS
No.96-48-0); or a combination thereof. Ethylene carbonate and
propylene carbonate generally possess a high flash point, a slow
evaporation rate, a weak odor, or a combination thereof. Ethylene
carbonate is preferred for use in coatings at temperatures greater
than 25.degree. C. Examples of an azeotrope comprising an ester
include an azeotrope comprising butyl acetate, ethyl acetate or
methyl acetate. Examples of an azeotrope comprising a majority of
butyl acetate (BP 124.degree. C. to 128.degree. C.) include those
comprising 27% water (A-BP 90.7.degree. C.) or 35.7% ethyl glycol
(A-BP 125.8.degree. C.). Examples of an azeotrope comprising a
majority of ethyl acetate (BP 76.degree. C. to 77.degree. C.)
include those comprising 5% cyclohexanol (A-BP 153.8.degree. C.);
8.2% water (A-BP 70.4.degree. C.); 22% methyl ethyl ketone (A-BP
76.7.degree. C.); 23% isopropyl alcohol (A-BP 74.8.degree. C.); or
31% ethanol (A-BP 71.8.degree. C.). An example of an azeotrope
comprising a majority of methyl acetate (BP 55.0.degree.
C.-57.0.degree. C.) includes an azeotrope comprising 19% methanol
(A-BP 54.degree. C.).
[0590] (iv) Glycol Ethers
[0591] A glycol ether comprises an alcohol moiety and an ether
moiety. The glycol ether generally possesses good solvency, high
flash point, slow evaporation rate, mild odor, miscibility with
water, or a combination thereof. In some embodiments, a glycol
ether may be selected as a coupling solvent, a thinner, or a
combination thereof. In particular aspects, a glycol ether may be
selected as a liquid component of a lacquer. Examples of a glycol
ether include methyl glycol (CAS No.109-86-4); ethyl glycol (CAS
No.110-80-5); propyl glycol (CAS No. 2807-30-9); isopropyl glycol
(CAS No.109-59-1); butyl glycol (CAS No. 111-76-2); methyl diglycol
(111-77-3); ethyl diglycol (CAS No.111-90-0); butyl diglycol (CAS
No.112-34-5); ethyl triglycol (CAS No.112-50-5); butyl triglycol
(CAS No.143-22-6); diethylene glycol dimethyl ether (CAS
No.111-96-6); methoxypropanol (CAS No. 107-98-2); isobutoxypropanol
(CAS No. 23436-19-3); isobutyl glycol (CAS No. 4439-24-1);
propylene glycol monoethyl ether (CAS No. 52125-53-8);
1-isopropoxy-2-propanol (CAS No. 3944-36-3); propylene glycol
mono-n-propyl ether (CAS No. 30136-13-1); propylene glycol n-butyl
ether (CAS No. 5131-66-8); methyl dipropylene glycol (CAS No.
34590-94-8); methoxybutanol (CAS No. 30677-36-2); or a combination
thereof. An example of an azeotrope comprising a glycol ether
includes an azeotrope comprising ethyl glycol. An example of an
azeotrope comprising a majority of ethyl glycol (BP 134.degree. C.
to 137.degree. C.) includes an azeotrope comprising 50% dibutyl
ether (A-BP 127.degree. C.).
[0592] (v) Ethers
[0593] Examples of an ether include diethyl ether (CAS No.
60-29-7); diisopropyl ether (CAS No. 108-20-3); dibutyl ether (CAS
No. 142-96-1); di-sec-butyl ether (CAS No. 6863-58-7); methyl
tert-butyl ether (CAS No. 1634-04-4); tetrahydrofuran (CAS No.
109-99-9); 1,4-dioxane (CAS No. 123-91-1); metadioxane (CAS No.
505-22-6); or a combination thereof. Tetrahydrofuran may be
selected as a primary solvent for a polyvinyl binder. An example of
an azeotrope comprising an ether includes an azeotrope comprising
tetrahydrofuran. An example of an azeotrope comprising a majority
of tetrahydrofuran (BP 66.degree. C.) includes an azeotrope
comprising 5.3% water (A-BP 64.0.degree. C.).
[0594] (3) Chlorinated Hydrocarbons
[0595] A chlorinated hydrocarbon generally comprises a hydrocarbon,
wherein the hydrocarbon comprises a chloride atom moiety. A
chlorinated hydrocarbon generally possesses a very high degree of
non-flammability, and consequently lacks a flash point. A
chlorinated hydrocarbon may be selected for embodiments where high
flash point is desired. In particular facets, a chlorinated
hydrocarbon may be added to a liquid component to reduce the liquid
component's flash point. In certain facets, it is less preferred
that a chlorinated hydrocarbon be combined with a mineral spirit,
methylene chloride, or a combination thereof, wherein reduction of
the flash point is desired. In particular aspects, a chlorinated
hydrocarbon (e.g., methylene chloride, trichloroethylene) may be
selected as a solvent for removal of hydrophobic material from a
surface (e.g., grease, an undesired coating and/or film). However,
a chlorinated hydrocarbon may be less preferred due to an
environmental regulation or law. Examples of a chlorinated
hydrocarbon include methylene chloride (CAS No. 75-09-2;
"dichloromethane"); trichloromethane (CAS No. 67-66-3);
tetrachloromethane (CAS No. 56-23-5); ethyl chloride (CAS No.
75-00-3); isopropyl chloride (CAS No. 75-29-6); 1,2-dichloroethane
(CAS No.107-06-2); 1,1,1-trichloroethane (CAS No. 71-55-6;
"methylchloroform"); trichloroethylene (CAS No. 79-01-6);
1,1,2,2-tetrachlorethane (CAS No. 79-55-6); 1,2-dichloroethylene
(CAS No. 75-35-4); perchloroethylene (CAS No. 127-18-4);
1,2-dichloropropane (CAS No. 78-87-5); chlorobenzene (CAS
No.108-90-7); or a combination thereof. Methylene chloride may be
selected for embodiments wherein a fast evaporation rate is
desired. 1,1,1-trichloroethane may be selected for embodiments
wherein a photochemically inert liquid component is desired.
Additionally, methylene chloride may be selected as a coating
remover. Examples of an azeotrope comprising a chlorinated
hydrocarbon include an azeotrope comprising methylene chloride,
trichloroethylene or 1,1,1-trichloroethane. Examples of an
azeotrope comprising a majority of methylene chloride (BP
40.2.degree. C.) include those comprising 1.5% water (A-BP
38.1.degree. C.); 3.5% ethanol (A-BP 41.0.degree. C.); or 8%
methanol (A-BP 39.2.degree. C.). Examples of an azeotrope
comprising a majority of trichloroethylene (BP 86.7.degree. C.)
include those comprising 6.6% water (A-BP 72.9.degree. C.); 27%
ethanol (A-BP 70.9.degree. C.); or 36% methanol (A-BP 60.2.degree.
C.). An example of an azeotrope comprising a majority of
1,1,1-trichloroethane (BP 74.0.degree. C.) includes an azeotrope
comprising 4.3% water (A-BP 65.0.degree. C.).
[0596] (4) Nitrated Hydrocarbon
[0597] A nitrated hydrocarbon comprises a hydrocarbon, wherein the
hydrocarbon comprises a nitrogen atom moiety. Examples of a
nitrated hydrocarbon include a nitroparaffin,
N-methyl-2-pyrrolidone ("NMP"), or a combination thereof. Examples
of a nitroparaffin include nitroethane, nitromethane, nitropropane,
2-nitropropane ("2NP"), or a combination thereof. 2-nitropropane
may be selected for embodiments as a substitute for butyl acetate
relative to a solvent property, but wherein a greater evaporation
rate is desired. N-methyl-2-pyrrolidone may be selected for
embodiments wherein a strong solvent property, miscibility with
water, high flash point, biodegradability, low toxicity, or a
combination thereof is desired. In certain aspects,
N-methyl-2-pyrrolidone may be used in a water-borne coating, a
coating remover, or a combination thereof.
[0598] (5) Miscellaneous Organic Liquids
[0599] A miscellaneous organic liquid is a liquid comprising carbon
that are useful as a liquid component for a coating, but are not
readily classified as a hydrocarbon, an oxygenated compound, a
chlorinated hydrocarbon, a nitrated hydrocarbon, or a combination
thereof. Examples of a miscellaneous organic liquid include carbon
dioxide; acetic acid, methylal (CAS No. 109-87-5); dimethylacetal
(CAS No. 534-15-6); N,N-dimethylformamide (CAS No. 68-12-2);
N,N-dimethylacetamide (CAS No. 127-19-5); dimethylsulfoxide (CAS
No. 67-68-5); tetramethylene suflone (CAS No. 126-33-0); carbon
disulfide (CAS No. 75-15-0); 2-nitropropane (CAS No. 79-46-9);
N-methylpyrrolidone (CAS No. 872-50-4); hexamethylphosphoric
triamide (CAS No. 680-31-9); 1,3-dimethyl-2-imidazol- idinone (CAS
No. 80-73-9); or a combination thereof. As would be known to one of
ordinary skill in the art, carbon dioxide may function as a liquid
component when prepared under pressure and temperature conditions
to form a supercritical liquid. A supercritical liquid has
properties between that of a liquid and a gas, and can be used in
spray application of a coating wherein the appropriate pressure
conditions can be maintained. Supercritical carbon dioxide may be
formulated with a coating using the tradename technique Unicarb.TM.
(Union Carbide Chemicals and Plastics Co., Inc.). Supercritical
carbon dioxide may be selected as a substitute for a hydrocarbon
diluent in embodiments wherein chemical inertness,
non-flammability, rapid evaporation, or a combination thereof, is
desirable. In certain aspects, 0% to 30%, including all
intermediate ranges and combinations thereof, of a hydrocarbon
liquid component may be replaced with supercritical carbon
dioxide.
[0600] b. Plasticizers
[0601] In certain embodiments, a coating may comprise a
plasticizer. A plasticizer may be selected for embodiments wherein
the resin possesses an unsuitable brittleness and/or low
flexibility property upon film formation. Properties a plasticizer
typically confers to a coating and/or film include, for example,
enhancing a flow property of a coating, lowering a film-forming
temperature range, enhancing the adhesion property of a coating
and/or film, enhancing the flexibility property of a film, lowering
the T.sub.g, improving film toughness, enhancing film heat
resistance, enhancing film impact resistance, enhancing UV
resistance, or a combination thereof. Since a function of a
plasticizer typically is to alter a film's properties, most
plasticizer's possess a high (e.g., baking temperature) boiling
point, as such a compound is generally less volatile, with
increasing boiling point temperature. In certain aspects, a
plasticizer may function as a solvent, thinner, diluent,
plasticizer, or combination thereof, for a coating composition
and/or film at a temperature greater than ambient conditions.
[0602] A plasticizer is thought to interact with a binder by a
polar interaction, but is chemically inert relative to the binder.
A plasticizer typically will lower the T.sub.g of a binder below
the temperature a coating comprising the binder will be applied to
a surface. In many embodiments, a plasticizer have a vapor pressure
less than 3 mm at 200.degree. C., a mass of 200 Da to 800 Da, a
specific gravity of 0.75 to 1.35, a viscosity of 50 cSt to 450 cSt,
a flash point temperature greater than 120.degree. C., or a
combination thereof. Preferred plasticizers comprise an organic
liquid (e.g., an ester). Standards for physical properties,
chemical properties, and/or procedures for testing
purity/properties, are described for plasticizers (e.g., undesired
acidity, color, undesired copper corrosion, boiling point, ester
content, odor, undesirable water contamination) in, for example,
"ASTM Book of Standards, Volume 06.04, Paint--Solvents; Aromatic
Hydrocarbons," D1613-02, D1209-00, D849-02, D1078-01, D1617-90,
D1296-01, D608-90, and D1364-02, 2002; and "ASTM Book of Standards,
Volume 06.01, Paint--Tests for Chemical, Physical, and Optical
Properties; Appearance," D1544-98, 2002. Compatibility of a
plasticizer with a binder and/or a solvent has been described (see,
for example, Riley, H. E., "Plasticizers," Paint Testing Manual,
American Society for Testing Materials, 1972). Additionally,
techniques previously described for estimating solubility for
liquid and an additional coating component may be applied for a
plasticizer.
[0603] Various plasticizers comprise an ester of a monoalcohol and
an acid (e.g., a dicarboxylic acid). In many embodiments, the
monoalcohol comprises 4 to 13 carbons. In specific aspects, the
monoalcohol comprises butanol, 2-ethylhexanol, isononanol,
isooctyl, isodecyl, or a combination thereof. Examples of an acid
include an azelaic acid, a phthalic acid, a sebacic acid, a
trimellitic acid, an adipic acid, or a combination thereof.
Examples of such plasticizers include di(2-ethylhexyl) azelate
("DOZ"); di(butyl) sebacate ("DBS"); di(2-ethylhexyl) phthalate
("DOP"); di(isononyl) phthalate ("DINP"); dibutyl phthalate
("DBP"); butyl benzyl phthalate ("BBP"); di(isooctyl) phthalate
("DIOP"); di(idodecyl) phthalate ("DIDP"); tris(2-ethylhexyl)
trimellitate ("TOTM"); tris(isononyl) trimellitate ("TINTM");
di(2-ethylhexyl) adipate ("DOA"); di(isononyl) adipate ("DINA"); or
a combination thereof.
[0604] A plasticizer may be classified by a moiety, such as, for
example, as an adipate (e.g., DOA, DINA), an azelate (e.g., DOZ), a
citrate, a chlorinated plasticizer, an epoxide, a phosphate, a
sebacate (e.g., DBS), a phthalate (e.g., DOP, DINP, DIOP, DIDP), a
polyester, or a trimellitate (e.g., TOTM, TINTM). An example of a
citrate plasticizer includes acetyl tri-n-butyl citrate. Examples
of an epoxide plasticizer include an epoxy modified soybean oil
("ESO"), 2-ethylhexyl epoxytallate ("2EH tallate"), or a
combination thereof. Examples of a phosphate plasticizer include
isodecyl diphenyl phosphate, tricresyl phosphate ("TPC"), isodecyl
diphenyl phosphate, tri-2-ethylhexyl phosphate ("TOP"), or a
combination thereof. Tricresyl phosphate may function as a
plastizer, confer flame resistance, confer fungi resistance, or a
combination thereof to a coating. Examples of a polyester
plasticizer include an adipic acid polyester, an azelaic acid
polyester, or a combination thereof. In certain aspects, a
plasticizer is selected for water resistance (e.g., hydrolysis
resistance, inertness toward water) such as a
bisphenoxyethylformal.
[0605] C. Water-Borne Coatings
[0606] A water-borne coating ("water reducible coating") refers to
a coating wherein components such as a pigment, a binder, an
additive, or a combination thereof are dispersed in water. Often,
an additional solvent, surfactant, emulsifier, wetting agent,
dispersant, or a combination thereof promotes dispersion of a
coating component. A latex coating refers to a water-borne coating
wherein the binder is dispersed in water. Typically, a binder of a
latex coating comprises a high molecular weight binder. Often a
latex coating (e.g., a paint, a lacquer) is a thermoplastic
coating. Film formation occurs by loss of the liquid component,
typically through evaporation, and fusion of dispersed
thermoplastic binder particles. Often, a latex coating further
comprises a coalescing solvent (e.g., diethylene glycol monobutyl
ether) that promotes fusion of the binder particles. In some
embodiments, a film produced from a latex coating is more porous,
possesses a lower moisture resistance property, is less compact
(e.g., thicker), or a combination thereof, relative to a
solvent-borne coating comprising similar non-volatile components.
Specific procedures for determining the purity/properties of a
latex coating, coating component (e.g., solids content, nonvolatile
content, vehicles), and/or film have been described, for example,
in "ASTM Book of Standards, Volume 06.01, Paint--Tests for
Chemical, Physical, and Optical Properties; Appearance," D4747-02
and D4827-93, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D3793-00, 2002; and "ASTM Book of Standards, Volume
06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D5097-90 D4758-92,
and D4143-89, 2002.
[0607] In certain embodiments, a water-borne coating is a coating
wherein 50% to 100%, the including all intermediate ranges and
combinations thereof, of a coating's liquid component is water. In
general embodiments, the water component of a water-borne coating
may function as a solvent, a thinner, a diluent, or a combination
thereof. In certain embodiments, a water-borne coating may comprise
an additional non-aqueous liquid component. In specific aspects,
such an additional liquid component may function as a solvent, a
thinner, a diluent, a plasticizer, or a combination thereof. An
additional liquid component of a water-borne coating may comprise
0% to 49.999%, the including all intermediate ranges and
combinations thereof, of the liquid component. Examples of
additional liquid components in a water-borne coating include a
glycol ether, an alcohol, or a combination thereof.
[0608] In certain embodiments, an additional liquid component of a
water-borne coating may be fully or partly miscible in water.
Examples of a liquid that is completely miscible in water, and visa
versa, include methanol, ethanol, propanol, isopropyl alcohol,
tert-butanol, ethylene glycol, methyl glycol, ethyl glycol, propyl
glycol, butyl glycol, ethyl diglycol, methoxypropanol,
methyldipropylene glycol, dioxane, tetrahydorfuran, acetone,
diacetone alcohol, dimethylformamide or dimethyl sulfoxide.
Examples of a liquid that is partly miscible in water, by weight at
20.degree. C., include 0.02% ethylbenzene; 0.02%
tetrachloroethylene; 0.02% p-xylene; 0.035% toluene; 0.04%
diisobutyl ketone; 0.1% tricholorethylene; 0.19%
trimethylcyclohexanol; 0.2% cyclohexyl acetate; 0.3% dibutyl ether;
0.3% trimethylcyclohexanone; 0.44% 1,1,1-tricholoroethane; 0.53%
hexane; 0.58% hexanol; 0.67% isobutyl acetate; 0.83% butyl acetate;
1.2% isophorone; 1.4% nitropropane; 1.5% butyl glycol acetate; 1.7%
2-nitropropane; 2.0% methylene chloride; 2.0% methyl isobutyl
ketone; 2.3% cyclohexanone; 2.9% isopropyl acetate; 2.9%
methylbenzyl alcohol; 3.6% cyclohexanol; 4.5% nitroethane; 4.8%
methyl tert-butyl ether; 6.1% ethyl acetate; 6.9% diethyl ether;
7.5% butanol; 7.5% butyl glycolate; 8.4% isobutanol; 12.5%
2-butanol; 21.4% propylene carbonate; 23.5% ethyl glycol acetate;
24% methyl acetate; or 26.0% methyl ethyl ketone. Examples of an
azeotrope comprising a majority of water (BP 100.degree. C.)
include those comprising 16.1% isophorone (A-BP 99.5.degree. C.);
20% 2-ethylhexanol (A-BP 99.1.degree. C.); 20% cyclohexanol (A-BP
97.8.degree. C.); 20.8% butyl glycol (A-BP 98.8.degree. C.); or
28.8% ethyl glycol (A-BP 99.4.degree. C.).
[0609] 3. Colorants
[0610] A colorant ("colorizing agent") is a composition that
confers a desirable optical property to a coating. Examples of
desirable optical properties, depending upon the application of the
present invention, include a reflection property, a light
absorption property, a light scattering property, or a combination
thereof. A colorant that increases the reflection of light may
increase gloss. A colorant that increased light scattering may
increase the opacity and/or confer a color to a coating and/or
film. Light scattering of a broad spectrum of wavelengths can
confer a white color to a coating and/or film. Scattering of a
certain wavelength may confer a color associated with the
wavelength to a coating and/or film. Light absorption also affects
opacity and/or color. Light absorption over a broad spectrum
confers a black color to a coating and/or film. Absorbance of a
certain wavelength may eliminate the color associated with the
wavelength from the appearance of a coating and/or film. Examples
of colorants include pigments, dyes, extenders, or a combination
thereof. Colorants (e.g., pigments, dyes) and procedures for
determining the optical properties and physical properties (e.g.,
hiding power, transparency, light absorption, light scattering,
tinting strength, color, particle size, particle dispersion,
pigment content, color matching) of a colorant, coating component,
coating and/or film are described in, for example, (in "Industrial
Color Testing, Fundamentals and Techniques, Second, Completely
Revised Edition," 1995; "Colorants for Non-Textile Applications,"
2000). Various colorants are well known to those of ordinary skill
in the art, and are often identified by their Colour Index ("CI")
number (see, for example, "Colour Index International," 1971; and
"Colour Index International," 1997). In some cases, a common name
for a colorant encompasses several related colorants, which can be
differentiated by CI number.
[0611] a. Pigments
[0612] A pigment is a composition that is insoluble in the other
components of a coating, and further confers a desirable optical
properties, confers a property affecting the application of the
coating (e.g., a rheological property), confers a performance
property to a coating, reduces the cost of the coating, or a
combination thereof. In certain embodiment, a pigment confers a
performance property to a coating such as a desirable corrosion
resistance property, magnetic property, or a combination thereof.
Examples of a pigment include an inorganic pigment, an organic
pigment, or a combination thereof.
[0613] Pigments possess a variety of properties in addition to
color that aid in the selection of a particular pigment for a
specific application. Examples of such properties include a
tinctorial property, an insolubility property, a corrosion
resistance property, a durability property, a heat resistance
property, an opacity property, a transparency property, or a
combination thereof. A tinctorial property is the ability of a
composition to produce a color, wherein a greater tinctorial
strength indicating less of the composition is needed to achieve
the color. A insolubility property is the ability of a composition
to remain in a solid form upon contact with another coating
component (e.g., a liquid component), even during a curing process
involving chemical reactions (e.g., thermosetting, baking,
irradiation). A corrosion resistance property is the ability of a
composition to reduce the damage of a chemical (e.g., water, acid)
that contacts metal.
[0614] Pigments (e.g., extenders, titanium pigments, inorganic
pigments, surface modified pigments, bismuth vanadates, cadmium
pigments, cerium pigment, complex inorganic color pigments,
metallic pigments, benzimidazolone pigments, diketopyrrolopyrrole
pigments, dioxazine violet pigments, disazocondensation pigments,
isoindoline pigments, isoindolinone pigments, perylene pigments,
phthalocyanine pigments, quinacridone pigments, quinophthalone
pigments, thiazine pigments, oxazine pigments, zinc sulfide
pigments, zinc oxide pigments, iron oxide pigments, chromium oxide
pigments, cadmium pigments, cadmium sulfide, cadmium yellow,
cadmium sulfoselenide, cadmium mercury sulfide, bismuth pigments,
chromate pigments, chrome yellow, molybdate red, molybdate orange,
chrome orange, chrome green, fast chrome green, ultramarine
pigments, iron blue pigments, black pigments, carbon black,
specialty pigments, magnetic pigments, cobalt-containing iron oxide
pigments, chromium dioxide pigments, metallic iron pigments, barium
ferrite pigments, anti-corrosive pigments, phosphate pigments, zinc
phosphate, aluminum phosphate, chromium phosphate, metal
phosphates, multiphase phosphate pigments, borosilicate pigments,
borate pigments, chromate pigments, molybdate pigments, lead
cyanamide pigments, zinc cyanamide pigments, iron-exchange
pigments, metal oxide pigments, red lead pigment, red lead, calcium
plumbate, zinc ferrite pigments, calcium ferrite pigments, zinc
oxide pigments, powdered metal pigments, zinc dust, lead powder,
flake pigments, nacreous pigments, interference pigments, natural
pearl essence pigment, basic lead carbonate pigment, bismuth
oxychloride pigment, metal oxide-mica pigments, metal effect
pigments, transparent pigments, transparent iron oxide pigments,
transparent iron blue pigment, transparent cobalt blue pigment,
transparent cobalt green pigment, transparent iron oxide,
transparent zinc oxide, luminescent pigments, inorganic phosphor
pigments, sulfide pigments, selenide pigments, oxysulfide pigments,
oxygen dominant phosphor pigments, halide phosphor pigments, azo
pigments, monoazo yellow pigments, monoazo orange pigment, disazo
pigments, .beta.-naphthol pigments, naphthol AS pigments, salt-type
azo pigments, benzimidazolone pigments, disazo condensation
pigments, metal complex pigments, isoindolinone pigments,
isoindoline pigments, polycyclic pigments, phthalocyanine pigments,
quinacrindone pigments, perylene pigments, perinone pigments,
diketopyrrolo pyrrole pigments, thioindigo pigments,
anthrapyrimidine pigments, flavanthrone pigments, pyranthrone
pigments, anthanthrone pigments, dioxanzine pigments,
triarylcarbonium pigments, quinophthalone pigments) and their
chemical properties, physical properties and/or optical properties
(e.g., color, tinting strength, lightening power, scattering power,
hiding power, transparency, light stability, weathering resistance,
heat stability, chemical fastness, interactions with a binder), in
coating component, coating and/or film, and techniques for
determining such properties, are known to one of ordinary skill in
the art (see, for example, Solomon, D. H. and Hawthorne, D. G.,
"Chemistry of Pigments and Fillers," 1983; "High Performance
Pigments," 2002; "Industrial Inorganic Pigments," 2002; "Industrial
Organic Pigments, Second, Completely Revised Edition," 1993).
[0615] As would be known to one of ordinary skill in the art,
specific standards for physical properties, chemical properties,
purity, and/or procedures for testing the purity/properties of
various pigments (e.g., lead chromate, chromium oxide,
phthalocyanine green, a phthalocyanine blue, molybdate orange,
white zinc, zinc oxide, calcium carbonate, barium sulfate, aluminum
silicate, diatomaceous silica, magnesium silicate, mica, calcium
borosilicate, zinc hydroxy phosphite, aluminum powder, micaceous
iron oxide, zinc phosphate, basic lead silicochromate, strontium
chromate, ochre, lampblack, orange shellac, raw umber, burnt umber,
raw sienna, burnt sienna, bone black, carbon black, red iron oxide,
brown iron oxide, basic carbonate, white lead, white titanium
dioxide, iron blue, ultramarine blue, chrome yellow, chrome orange,
hydrated yellow iron oxide, zinc chromate yellow, red lead, para
red toner, toluidine red toner, chrome oxide green, zinc dust,
cuprous oxide, mercuric oxide, iron oxide, anhydrous aluminum
silicate, black synthetic iron oxide, gold bronze powder, aluminum
powder, strontium chromate pigment, basic lead silicochromate) for
use in a coating are described, for example in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D280-01, D2448-85, D126-87, D305-84, D3021-01, D3256-86, D2218-67,
D3280-85, D50-90, D79-86, D1199-86, D602-81, D715-86, D603-66,
D718-86, D604-81, D719-91, D605-82, D717-86, D607-82, D716-86,
D4288-02, D4487-90, D4462-02, D4450-85, D962-81, D5532-94,
D6280-98, D1648-86, D1649-01, D85-87, D209-81, D237-57, D763-01,
D765-87, D210-81, D561-82, D3722-82, D3724-01, D34-91, D81-87,
D1301-91, D1394-76, D261-75, D262-81, D1135-86, D211-67, D768-01,
D444-88, D3872-86, D478-02, D1208-96, D83-84, D49-83, D3926-80,
D475-67, D656-87, D970-86, D3721-83, D263-75, D520-00, D521-02,
D283-84, D284-88, D3720-90, D3619-77, D769-01, D476-00, D267-82,
D480-88, D1845-86, D1844-86, and D279-02, 2002; and in "ASTM Book
of Standards, Volume 06.01, Paint--Tests for Chemical, Physical,
and Optical Properties; Appearance," D5381-93 and D6131-972002.
[0616] (1) Corrosion Resistance Pigments
[0617] Addition of certain pigments may improve the corrosion
resistance of a coating and/or film, or specifically, the
protection of a metal surface coated with a coating and/or film
from corrosion. Often, a primer comprises such pigments. Examples
of corrosion resistance pigments include aluminum flake, aluminum
triphosphate, aluminum zinc phosphate, ammonium chromate, barium
borosilicate, barium chromate, barium metaborate, basic calcium
zinc molybdate, basic carbonate white lead, basic lead silicate,
basic lead silicochromate, basic lead silicosulfate, basic zinc
molybdate, basic zinc molybdate-phosphate, basic zinc molybdenum
phosphate, basic zinc phosphate hydrate, bronze flake, calcium
barium phosphosilicate, calcium borosilicate, calcium chromate,
calcium plumbate (CI Pigment Brown 10), calcium strontium
phosphosilicate, calcium strontium zinc phosphosilicate, dibasic
lead phosphite, lead chromosilicate, lead cyanamide, lead suboxide,
lead sulfate, mica, micaceous iron oxide, red lead (CI Pigment Red
105), steel flake, strontium borosilicate, strontium chromate (CI
Pigment Yellow 32), tribasic lead phophosilicate, zinc borate, zinc
borosilicate, zinc chromate (CI Pigment Yellow 36), zinc dust (CI
Pigment Metal 6), zinc hydroxy phosphite, zinc molybdate, zinc
oxide, zinc phosphate (CI Pigment White 32), zinc potassium
chromate, zinc silicophosphate hydrate, zinc tetraoxylchromate, or
a combination thereof.
[0618] The selection of a corrosion resistant pigment may be made
based on the mechanism of corrosion resistance it confers to a
coating and/or film. Corrosion often occurs as a cathodic process
wherein a metal surface acts as a cathode and passes electrons to
an electron accepter moiety of a corrosive chemical, such as, for
example, hydrogen, oxygen, or a combination thereof. Corrosion can
also occur as an anodic process wherein ionized metal atoms then
enter solution. Pigments such as, for example, mica, micaceous iron
oxide, metallic flake pigments (e.g., aluminum, bronze, steel), or
a combination thereof confer corrosion resistance to a coating
and/or film by acting as a physical barrier between a metal surface
and corrosive chemicals. However, a chemically reactive pigment
such as a metal flake pigment be used in an environment at or near
neutral pH (e.g., pH 6 to pH 8). Micaceous iron oxide can be
selected for a primer, a topcoat, or a combination thereof, and can
also function as a UV absorber. Aluminum flake may be selected for
an industrial coating, an automotive coating, an architectural
coating, a primer, or a combination thereof. Aluminum flake may
additionally confer heat resistance, moisture resistance, UV
resistance, or a combination thereof to a coating and/or film.
Aluminum flake may also be stearate modified for use in a topcoat.
However, aluminum flake may produce gas in a coating comprising
more than 0.15% water. A metallic zinc pigment (e.g., zinc flake,
zinc dust) acts by functioning as an anode instead of the metal
surface (e.g., steel). However, the effectiveness of a coating's
corrosion resistance fades as the zinc pigment is used up in
protective reactions. A metallic zinc primer may be selected for a
primer, particularly in combination with an epoxy topcoat, a
urethane topcoat, or a combination thereof.
[0619] Red lead and/or basic lead silicochromate can confer an
orange color, and may be selected for combination with an oil-based
coating (e.g., a primer), as the pigment chemically reacts with an
oil-based binder to produce a corrosion resistant lead soap in the
coating and/or film. Red lead and/or basic lead is typically
selected for a primer in an industrial steel coating.
[0620] A barium metaborate pigment acts by retarding an anodic
process. A barium metaborate pigment is usual chemically modified
by combination with silica to reduce solubility. A zinc borate
combined with a zinc phosphate, a modified barium metaborate, or
combination thereof demonstrates synergistic enhancement of
corrosion resistance, as well as flame retardancy.
[0621] Zinc potassium chromate may confer a yellow color as well as
an anticorrosive property. Zinc tetraoxylchromate can also confer a
yellow color, and is typically selected for use in a two pack
poly(viny butyryl) primer. Zinc oxide may be selected for an
oleoresinous coating, a water-borne coating, a primer, or a
combination thereof, and may be combined with a zinc chromate
and/or calcium borosilicate, and additionally may improve
thermosetting crosslinking density and/or act as a UV absorber.
Strontium chromate may confer a yellow color, and may be selected
for an aluminum surface, an aircraft primer, or a combination
thereof. Strontium chromate may be combined with a zinc chromate in
a water-borne coating, though it is preferred that total chromate
content is less from 0.001% to 2%. Ammonium chromate, barium
chromate and calcium chromate may be selected as a corrosion
inhibitor, particularly as a flash rust inhibitor.
[0622] A zinc molybdate, zinc phosphate, zinc hydroxy phosphite, or
a combination thereof may confer a white color. These zinc pigments
function by reducing an anodic process, though zinc hydroxy
phosphite may form corrosion resistant soap in an
oleoresinous-coating. Basic zinc molybdate typically is selected
for an alkyd-coating, an epoxide-coating, an epoxy ester-coating, a
polyester-coating, a solvent-borne coating, or a combination
thereof. Basic zinc molybdate-phosphate is similar to basic zinc
molybdate, though it may provide superior corrosion resistance for
a rusted steel surface. Basic calcium zinc molybdate may be
selected for a water-borne coating, a two-pack polyurethane
coating, a two-pack epoxy coating, or a combination thereof. A
combination of basic calcium zinc molybdate and zinc phosphate may
confer a superior adhesion property to a surface comprising iron,
and may be selected for a water-borne coating or a solvent-borne
coating. A zinc phosphate may be selected for an alkyd coating, a
water-reducible coating, a coating cured by an acid and baking, or
a combination thereof. A zinc phosphate is less preferred for a
marine coating for salt water embodiments. A modified zinc
phosphate, such as, for example, aluminum zinc phosphate, basic
zinc phosphate hydrate, zinc silicophosphate hydrate, basic zinc
molybdenum phosphate, or a combination thereof may confer improved
corrosion resistance for a salt water embodiment. Zinc hydroxy
phosphite may be selected for a solvent-borne coating.
[0623] An aluminum triphosphate typically confers a white color,
acts by chelating iron ions, and is preferred for a surface that
comprises iron. A grade I aluminum triphosphate is modified with
zinc and silicate, and may be selected for an alkyd-coating, an
epoxy coating, a solvent-borne coating, a primer, or a combination
thereof. A grade II aluminum triphosphate is modified with zinc and
silicate, and may be selected for a water-borne coating or a
solvent-borne coating. A grade III aluminum triphosphate is
modified with zinc, and may be selected for a water-borne coating
or a solvent-borne coating.
[0624] A silicate pigment such as barium borosilicate, calcium
borosilicate, strontium borosilicate, zinc borosilicate, a calcium
barium phosphosilicate, a calcium strontium phosphosilicate, a
calcium strontium zinc phosphosilicate, or a combination thereof,
typically acts through inhibiting an anodic or cathodic process, as
well as forming a corrosion resistant soap in an
oleoresinous-coating. A grade I and/or III calcium borosilicate may
be selected for a medium oil alkyd-coating, a long oil alkyd, an
epoxy ester-coating, a solvent-borne coating, an architectural
coating, an industrial coating, or a combination thereof, but is
less preferred for a marine coating, an epoxide-coating, a
water-borne coating, or a combination thereof. Calcium barium
phosphosilicate grade I pigment may be selected for a solvent-borne
epoxy-coating, to confer an antisettling property to a primer
comprising zinc, or a combination thereof. Calcium barium
phosphosilicate grade II pigment may be selected for a water-borne
coating, an alkyd-coating, or a combination thereof. Calcium
strontium phosphosilicate may be selected for a water-borne acrylic
lacquer, a water-borne sealant, or a combination thereof. In
aspects wherein a water-borne acrylic lacquer comprises calcium
strontium phosphosilicate, it is preferred that a 1:1 ratio of zinc
phosphate pigment is included. Calcium strontium zinc
phosphosilicate may be selected for an alkyd-coating, an epoxide
coating, a coating cured by a catalyst and baking, a water-borne
coating, or a combination thereof.
[0625] (2) Camouflage Pigments
[0626] A camouflage pigment refers to a pigment typically selected
to camouflage a surface (e.g., a military surface) from visual and,
more preferred, infrared detection. Examples of a camouflage
pigment include an anthraquinone black, a chromium oxide green, or
a combination thereof. A chromium oxide green may be selected for
embodiments wherein good chemical resistance, dull color, good heat
stability, good infrared reflectance, good light fastness, good
opacity, good solvent resistance, low tinctorial strength, or a
combination thereof, is suitable. Anthraquinone black (CI Pigment
Black 20) may be selected for good light fastness and moderate
solvent resistance, and is often selected for camouflage coatings,
due to its infrared absorption property.
[0627] (3) Color Property Pigments
[0628] A color property is the ability of a composition to confer a
visual color and/or metallic appearance to a coating and/or a
coated surface. Color pigments are often categorized by a common
name recognized within the art, which often encompasses several
specific color pigments, each identified by a CI number.
[0629] (i) Black Pigments
[0630] A black pigment is a pigment that confers a black color to a
coating. Examples of black pigments, identified by common name with
examples of specific pigments in parentheses, include aniline
black; anthraquinone black; carbon black; copper carbonate;
graphite; iron oxide; micaceous iron oxide; manganese dioxide; or a
combination thereof.
[0631] Aniline black (e.g., CI Pigment Black 1); may be selected
for a deep black color (e.g., strong light absorption, low light
scattering) and/or fastness. Coatings comprising aniline black
typically comprise relatively higher concentrations of binder, and
thus often possesses a matt property.
[0632] Anthraquinone black (e.g., CI Pigment Black 20) may be
selected for good light fastness and moderate solvent
resistance.
[0633] Carbon black (e.g., CI Pigment Black 6, CI Pigment Black 7,
CI Pigment Black 8) generally possesses properties such as chemical
stability, good light fastness, good solvent resistance, heat
stability, or a combination thereof. Carbon black is often
categorized into separate grades, based on the intensity of black
color ("jetness"). To reduce flocculation in preparing a coating
comprising a carbon black pigment, such pigments may be
incrementally added to a coating during preparation, chemically
modified by surface oxidation, chemically modified by an organic
compound (e.g., a carboxylic acid), or a combination thereof.
Additionally, a carbon black pigment may absorb certain other
coating components such as a metal soap drier. Typically,
increasing the concentration of the susceptible component by, for
example, two-fold will reduce this effect. A high jet channel black
pigment is often selected for use in an automotive coating wherein
a high jetness is desired. The other grades of carbon black
pigments are often selected for architectural coatings.
[0634] Graphite (e.g., CI Pigment Black 10) may be selected for
properties such as relative chemically inertness, low in color
intensity, low in tinctorial strength, an anti-corrosive property,
an increase in coating spreading rate, or a combination
thereof.
[0635] Iron oxide (e.g., CI Pigment Black 11) may be selected for
properties such as good chemical resistance, relative inertness,
good solvent resistance, limited heat resistance, low tinctorial
strength, or a combination thereof. Iron oxide possesses superior
floating resistance than carbon black, particularly in combination
with titanium dioxide.
[0636] Micaceous iron oxide may be selected for properties such as
relative inertness, grayish appearance, shiny appearance, function
as a UV absorber, function as an anti-corrosive pigment due to
resistance to oxygen and moisture passage. However, over-dispersal
of a micaceous iron oxide during coating preparation may damage the
pigment.
[0637] (ii) Brown Pigments
[0638] A brown pigment is a pigment that confers a brown color to a
coating. Examples of a brown pigment include azo condensation (CI
Pigment Brown 23, CI Pigment Brown 41, CI Pigment Brown 42);
benzimidazolone (CI Pigment Brown 25); iron oxide; metal complex
brown; or a combination thereof. A synthetically produced iron
oxide brown (CI Pigment Brown 6, CI Pigment Brown 7) may be
selected for embodiments wherein a rich brown color, good
lightfastness, or a combination thereof is suitable. A metal
complex brown (CI Pigment Brown 33) may be selected for embodiments
wherein high heat stability, good fastness, or a combination
thereof is suitable. A metal complex brown may be used, for
example, in a coil coating, a coating for a ceramic surface, or a
combination thereof.
[0639] (iii) White Pigments
[0640] A white pigment is a pigment that confers a white color to a
coating. Examples of a white pigment include antimony oxide; basic
lead carbonate (CI Pigment White 25); lithopone; titanium dioxide;
white lead; zinc oxide; zinc sulphide (CI Pigment White 7); or a
combination thereof.
[0641] Antimony oxide (CI Pigment White 11) is chemically inert,
and used in fire resistant coatings. In some embodiments, antimony
oxide may be combined with titanium dioxide, particularly in a
coating where chalking is undesirable and a white color in the
coating is desired.
[0642] Titanium dioxide (CI Pigment White 6) is resistant to heat,
many chemicals, and organic solvents, allowing use in many
different applications where such properties are desirable.
Titanium dioxide may be in the form of a crystal, such as an
anatase crystal, a rutile crystal, or a combination thereof. Rutile
is more opaque than anatase. Anatase has a greater ability to chalk
and is whiter in color than rutile. In aspects wherein chalking is
undesirable, a titanium dioxide crystal may be reacted with an
inorganic oxide to enhance chalking resistance. Examples of such
inorganic oxides include aluminum oxide, silicon oxide, zinc oxide,
or a combination thereof.
[0643] White lead (CI Pigment White 1) is chemically reactive with
acidic binders to form strong films with elastic properties, but
also chemically reacts with sulphur to become black in color. It is
less preferred in certain coatings due to the toxic nature of
lead.
[0644] Zinc oxide (CI Pigment White 4) confers desirable properties
such as resistance to mildew, as well as chemically reacting with
oleoresin binders in-film formation to enhance resistance to
abrasion, to enhance resistance to moisture, to enhance hardness,
and/or reduce chalking. However, these reactions may undesirably
occur during storage. In some embodiments, it may be combined with
titanium dioxide, particularly in a coating comprising an oleoresin
binder when chalking is undesirable and a white color in the
coating is desired.
[0645] Zinc sulfide (CI Pigment White 7) is chemically inert, and
confers a strong chalking property. In certain embodiments, a zinc
sulfide comprises a lithopone. A lithopone (CI Pigment White 5)
comprises a mixture of ZnS and barium sulphate (BaSO.sub.4),
usually from 30% to 60% ZnS and 70% to 40% BaSO.sub.4.
[0646] (iv) Pearlescent Pigments
[0647] A pearlescent pigment is a pigment that confers a pearl-like
appearance to a coating. Examples of a white pigment include
titanium dioxide and ferric oxide covered mica, bismuth oxychloride
crystal, or a combination thereof.
[0648] (v) Violet Pigments
[0649] A violet pigment is a pigment that confers a violet color to
a coating. However, a violet pigment is often used in combination
with a red pigment or a blue pigment to produce a desirable color
of an intermediate hue between red and blue. Additionally, a violet
pigment is often combined with titanium dioxide to balance the
slight yellow color of that white pigment. An example of a violet
pigment includes dioxanine violet (CI Pigment Violet 23; CI Pigment
Violet 37). A dioxazine violet may be selected for embodiments
wherein high heat stability, good light fastness, good solvent
fastness, or a combination thereof is suitable. CI Pigment Violet
23 ("carbazole violet") is relatively transparent and bluer than CI
Pigment 37, and is typically used in a metallic coating. A
dioxazine violet is susceptible to flocculation, loss in a powder
coating, or a combination thereof, due to small particle size.
[0650] (vi) Blue Pigments
[0651] A blue pigment is a pigment that confers a blue color to a
coating. Examples of a blue pigment include carbazol Blue;
carbazole Blue; cobalt blue; copper phthalocyanine; dioxanine Blue;
indanthrone; phthalocyanin blue; Prussian blue; ultramarine; or a
combination thereof.
[0652] A cobalt blue (CI Pigment Blue 36) may be selected for
embodiments wherein good chemical resistance, good lightfastness,
good solvent fastness, or a combination thereof, is suitable. An
indanthrone (CI Pigment Blue 60) may be selected for embodiments
wherein a redish-blue hue, good chemical resistance, good heat
resistance, good solvent fastness, transparency, superior
resistance to flocculation relative to a copper phthalocyanine, or
a combination thereof, is suitable.
[0653] A copper phthalocyanine (CI Pigment Blue 15, CI Pigment Blue
15:1, CI Pigment Blue 15:2, CI Pigment Blue 15:3, CI Pigment Blue
15:4, CI Pigment Blue 15:6, CI Pigment Blue 16) may be selected for
embodiments wherein good color strength, good tinctorial strength,
good heat stability, good lighffastness, good solvent resistance,
transparency, or a combination thereof, is suitable. CI Pigment
Blue 15 is redish in hue, but is chemically unstable upon contact
with an aromatic hydrocarbon, and converts to a greenish blue
compound. CI Pigment Blue 15:1 is form of CI Pigment Blue 15
chemically stabilized by chlorination, greener, and tinctorially
weaker than CI Pigment Blue 15. CI Pigment Blue 15:2 is modified
form of CI Pigment Blue 15 that is resistant to flocculation. CI
Pigment Blue 15:3 is greenish-blue, while CI Pigment Blue 15:4 is
modified form of CI Pigment Blue 15:3 that is resistant to
flocculation. CI Pigment Blue 16 is relatively transparent.
Examples of coatings wherein copper phthalocyanine are used include
a metallic automotive coating. However, as described above, a
copper phthalocyanine may be susceptible to flocculation due to
small primary particle size, and various modified forms are known
wherein flocculation is reduced. Examples of modifications used to
reduce flocculation adding a sulfonic acid moiety; a sulfonic acid
moiety and a long chain amine moiety; an aluminum benzoate; an
acidic binder (e.g., a rosin); a chloromethyl moiety; or a
combination thereof, to the phthalocyanine. A modified
phthalocyanine may be selected for embodiments wherein superior
color shade, dispersibility, gloss, or a combination thereof is
suitable.
[0654] A Prussian blue (CI Pigment Blue 27) may be selected for
embodiments wherein a strong color, good heat stability, good
solvent fastness, or a combination thereof is suitable. However, a
Prussian blue is chemically unstable in alkali conditions. An
ultramarine (CI Pigment Blue 29) may be selected wherein a strong
color, good heat stability, good light fastness, good solvent
resistance, or a combination thereof is suitable. However, an
ultramarine is chemically unstable in acidic conditions.
[0655] (vii) Green Pigments
[0656] A green pigment is a pigment that confers a green color to a
coating. However, often a "green pigment" comprises a mixture of a
yellow pigment and a blue pigment, with the properties of each
component pigment generally retained. Examples of a green pigment
include chrome green; chromium oxide green; halogenated copper
phthalocyanine; hydrated chromium oxide; phthalocyanine green; or a
combination thereof.
[0657] A chrome green ("Brunswick green," CI Pigment Green 15)
comprises a combination of a Prussian blue and/or a copper
phthalocyanine blue and a chrome yellow. A coating comprising a
chrome green may be susceptible to floating and flooding defects. A
chromium oxide green (CI Pigment Green 17) may be selected for
embodiments wherein good chemical resistance, dull color, good heat
stability, good infrared reflectance, good light fastness, good
opacity, good solvent resistance, low tinctorial strength, or a
combination thereof is suitable. A hydrated chromium oxide (CI
Pigment Green 18) is similar to chromium oxide, and may be selected
for embodiments wherein good light fastness, relatively brighter
appearance, relatively greater transparency, relatively less heat
stability, relatively less acid stability, or a combination
thereof, is suitable. A phthalocyanine green (CI Pigment Green 7,
CI Pigment Green 36) may be selected for embodiments wherein good
chemical resistance, good heat stability, good light fastness, good
solvent resistance, good tinctorial strength, color transparency,
or a combination thereof is suitable. CI Pigment Green 7 may be
selected for a bluish green color, while CI Pigment Green 36 may be
selected for a yellower-greenish color. A phthalocyanine green is
often selected for an automotive coating (e.g., a metallic
coating), an industrial coating, an architectural coating, a powder
coating, or a combination thereof.
[0658] (viii) Yellow Pigments
[0659] In certain embodiments, a coating may comprise a yellow
pigment. A "yellow pigment" is a pigment that confers a yellow
color to a coating. Examples of a yellow pigment include
anthrapyrimidine; arylamide yellow; barium chromate;
benzimidazolone yellow; bismuth vanadate (CI Pigment Yellow 184);
cadmium sulfide yellow (CI Pigment Yellow 37); complex inorganic
color pigment; diarylide yellow; disazo condensation; flavanthrone;
isoindoline; isoindolinone; lead chromate; nickel azo yellow;
organic metal complex; quinophthalone; yellow iron oxide; yellow
oxide; zinc chromate; or a combination thereof.
[0660] An anthrapyrimidine pigment (CI Pigment Yellow 108) may be
selected for embodiments wherein, moderate light fastness, moderate
solvent resistance, a dull color, transparency, or a combination
thereof is suitable.
[0661] An arylamide yellow ("Hansa.RTM. yellow," CI Pigment Yellow
1, CI Pigment Yellow 3, CI Pigment Yellow 65, CI Pigment Yellow 73,
CI Pigment Yellow 74, CI Pigment Yellow 75, CI Pigment Yellow 97,
CI Pigment Yellow 111) may be selected for embodiments wherein,
poor heat stability, good light fastness, poor solvent resistance,
moderate tinctorial strength, or a combination thereof is suitable.
CI Pigment 1 and CI Pigment 74 are mid-yellow in hue. CI Pigment
Yellow 3 is greenish in hue. CI Pigment Yellow 73 is mid-yellow in
hue, and resistant to recrystalization during dispersion. CI
Pigment 97 possesses superior solvent fastness than other arylamide
yellow pigments, and has been used in a stoving enamel, an
automotive coating, or a combination thereof. Other arylamide
yellow pigments may be used in a water-borne coating, a coating
comprising a white spirit liquid component, or a combination
thereof.
[0662] A benzimidiazolone yellow (CI Pigment Yellow 120, CI Pigment
Yellow 151, CI Pigment Yellow 154, CI Pigment Yellow 175, CI
Pigment Yellow 181, CI Pigment Yellow 194) may be selected for
embodiments wherein, good chemical resistance, good heat stability,
good light fastness, good solvent resistance, or a combination
thereof is suitable. A benzimidiazolone with larger particle size
been used in an automotive coating, a powder coating, or a
combination thereof.
[0663] A cadmium sulfide yellow (CI Pigment Yellow 37) may be
selected for embodiments wherein good stability in basic pH, good
heat stability, good light fastness, good opacity, good solvent
fastness, or a combination thereof is suitable. However, a cadmium
yellow comprises cadmium, which may limit suitability relative to
an environmental law or regulation.
[0664] A complex inorganic color pigment ("mixed phase metal
oxide," CI Pigment Yellow 53, CI Pigment Yellow 119, CI Pigment
Yellow 164); may be selected for embodiments wherein, good chemical
stability, good heat resistance, good light fastness, good opacity,
good solvent fastness, or a combination thereof is suitable.
However, a complex inorganic color pigment generally produces a
pale color, and is often combined with an additional pigment (e.g.,
an organic pigment). A complex inorganic color pigment is often
selected for an automotive coating, a coil coating, or a
combination thereof. A bismuth vanadate is similar to a complex
inorganic pigment, but possesses superior color of green-yellow
hue, poorer light fastness, and greater use in a powder coating. A
bismuth vanadate is often combined with a light stabilizer.
[0665] A diarylide yellow (CI Pigment Yellow 12, CI Pigment Yellow
13, CI Pigment Yellow 14, CI Pigment Yellow 17, CI Pigment Yellow
81, CI Pigment Yellow 83) may be selected for embodiments wherein,
good chemical resistance, poor light fastness, good solvent
resistance, good tinctorial strength, or a combination thereof is
suitable. A diarylide yellow is not stable at a temperature of
200.degree. C. or greater. CI Pigment Yellow 83 has superior light
fastness than other diarylide yellow pigments, and has been used in
an industrial coating, a powder coating, or a combination
thereof.
[0666] A diazo condensation pigment (CI Pigment Yellow 93, CI
Pigment Yellow 94, CI Pigment Yellow 95, CI Pigment Yellow 128, CI
Pigment Yellow 166) may be selected for embodiments wherein, good
chemical resistance, good heat stability, good solvent resistance,
good tinctorial strength, or a combination thereof is suitable. A
diazo condensation pigment typically is used in plastics, though CI
Pigment Yellow 128 has been used in a coating such as an automotive
coating.
[0667] A flavanthrone pigment (CI Pigment Yellow 24) may be
selected for embodiments wherein, good heat stability, moderate
light fastness, a reddish yellow hue superior to an
anthrapyrimidine, transparency, or a combination thereof is
suitable.
[0668] An isoindoline yellow pigment (CI Pigment Yellow 139, CI
Pigment Yellow 185) may be selected for embodiments wherein, good
chemical resistance, good heat stability, good light fastness, good
solvent resistance, moderate tinctorial strength, or a combination
thereof is suitable. An isoindolinone yellow pigment (CI Pigment
Yellow 109, CI Pigment Yellow 110, CI Pigment Yellow 173) typically
has been used in an automotive coating or an architectural coating.
An isoindoline yellow pigment may be selected for embodiments
wherein, good light fastness, good tinctorial strength, or a
combination thereof is suitable. However, an isoindoline pigment is
not stable in a basic pH. An isoindoline yellow pigment typically
has been used in an industrial coating.
[0669] A lead chromate (CI Pigment Yellow 34) may be selected for
embodiments wherein moderate heat stability, low oil absorption,
good opacity, good solvent resistance, or a combination thereof is
suitable. However, a lead chromate is susceptible to an acidic or a
basic pH, and a lower light fastness so that the pigment darkens
upon irradiation by light. The pH and lightfastness properties of
commercially produced lead chromate are often improved by treatment
of a lead chromate with silica, antimony, alumina, metal, or a
combination thereof. Additionally, a lead chromate comprises lead
and/or chromium, which may limit suitability relative to an
environmental law or regulation. A lead chromate may comprise a
lead sulfate, which is used to modify color. Examples of lead
chromates include a lemon chrome, which comprises from 20% to 40%
lead sulfate and is greenish yellow in color; a middle chrome,
which comprises little lead sulfate and is reddish yellow in color;
orange chrome, which comprises no detectable lead sulfate; and
primrose chrome, which comprises from 45% to 55% lead chrome and is
greenish yellow in color.
[0670] An organic metal complex (CI Pigment Yellow 129, CI Pigment
Yellow 153) may be selected for embodiments wherein good solvent
resistance is suitable. An organic metal complex typically is
transparent and dull in color.
[0671] A quinophthalone pigment (CI Pigment Yellow 138) may be
selected for embodiments wherein, good heat stability, good light
fastness, good solvent resistance, a reddish yellow hue, or a
combination thereof is suitable. A quinophthalone can be either
highly opaque or transparent. A quinophthalone pigment has been
used as a substitute for chrome as a pigment.
[0672] A yellow iron oxide (CI Pigment Yellow 42, CI Pigment Yellow
43) may be selected for embodiments wherein good covering power,
good disperability, good resistance to chemicals, good light
fastness, good solvent resistance, a yellow with greenish hue is
desired, or a combination thereof is suitable. A yellow iron oxide
can function as a U.V. absorber. However, a yellow iron oxide is
generally of duller color relative to other pigments, and is
susceptible to temperatures of 105.degree. C. or greater.
Additionally, a yellow iron oxide may comprise a .alpha.-crystal, a
.beta.-crystal, a .gamma.-crystal, or a combination thereof.
Overdispersion may damage the needle-shape crystal structure, which
can reduce the color intensity. Additionally, a transparent yellow
iron oxide can be prepared by selecting particles with minimum
size, and such a pigment is used, for example, in an automotive
coating or a wood coating.
[0673] (ix) Orange Pigments
[0674] In certain embodiments, a coating may comprise an orange
pigment. An "orange pigment" is a pigment that confers an orange
color to a coating. Examples of an orange pigment include perinone
orange; pyrazolone orange; or a combination thereof.
[0675] A perinone orange pigment (CI Pigment Orange 43) may be
selected for embodiments wherein very good resistance to heat, good
light fastness, good solvent resistance, high tinctorial strength,
or a combination thereof is suitable.
[0676] A pyrazolone orange pigment (CI Pigment Orange 13, CI
Pigment Orange 34) is similar to a diarylide yellow pigment, and
may be selected for embodiments wherein moderate resistance to
heat, poor light fastness, moderate solvent resistance, high
tinctorial strength, or a combination thereof is suitable. However,
CI Pigment Orange 34 possesses greater lighffastness relative to CI
Pigment Orange 13, and has been used in an industrial coating
and/or a replacement for chrome.
[0677] (x) Red Pigments
[0678] In certain embodiments, a coating may comprise a red
pigment. A "red pigment" is a pigment that confers a red color to a
coating. Examples of an red pigment include anthraquinone;
benzimidazolone; BON arylamide; cadmium red; cadmium selenide;
chrome red; dibromanthrone; diketopyrrolo-pyrrole pigment (CI
Pigment Red 254, CI Pigment Red 255, CI Pigment Red 264, CI Pigment
Red 270, CI Pigment Red 272); disazo condensation pigment (CI
Pigment Red 144, CI Pigment Red 166, CI Pigment Red 214, CI Pigment
Red 220, CI Pigment Red 221, CI Pigment Red 242); lead molybdate;
perylene; pyranthrone; quinacridone; quinophthalone; red iron
oxide; red lead; toluidine red; tonor pigment (CI Pigment Red 48,
CI Pigment Red 57, CI Pigment Red 60, CI Pigment Red 68);
.beta.-naphthol red; or a combination thereof.
[0679] A lead molybdate red pigment (CI Pigment Red 104) may be
selected for embodiments wherein good resistance to heat, moderate
resistance to basic pH, good opacity, excellent solvent resistance,
or a combination thereof is suitable. A molybdate red is bright in
color, and is often combined with an organic pigment to extend a
color range. However, a molybdate is easy to disperse, and
overdispersion may damage this pigment. Additionally, a molybdate
red comprising lead and/or chromium may have limited suitability
relative to an environmental law or regulation.
[0680] A cadmium red pigment (CI Pigment Red 108) may be selected
for embodiments wherein excellent resistance to heat, good
lightfastness, poor resistance to acidic pH, good opacity,
excellent solvent resistance, or a combination thereof is suitable.
However, a cadmium red comprises cadmium, and may have limited
suitability relative to an environmental law or regulation.
[0681] A red iron oxide pigment (CI Pigment Red 101, CI Pigment Red
102) may be selected for embodiments wherein excellent resistance
to heat, good lighffastness, poor resistance to acidic pH, good
opacity, excellent solvent resistance, or a combination thereof is
suitable. However, a cadmium red comprises cadmium, and may have
limited suitability relative to an environmental law or
regulation.
[0682] .beta.-naphthol red (CI Pigment Red 3) may be selected for
embodiments wherein modest heat resistance, good lightfastness,
modest solvent resistance, or a combination thereof is
suitable.
[0683] BON arylamide (CI Pigment Red 2, CI Pigment Red 5, CI
Pigment Red 12, CI Pigment Red 23, CI Pigment Red 112, CI Pigment
Red 146, CI Pigment Red 170) comprises various pigments that
generally have good lighffastness, good solvent resistance, or a
combination thereof.
[0684] Tonor pigment (CI Pigment Red 48, CI Pigment Red 57, CI
Pigment Red 60, CI Pigment Red 68) comprises various pigments that
generally have good solvent resistance, but often have poor acid
resistance, poor alkali resistance, or a combination thereof.
[0685] Benzimidazolone (CI Pigment Red 171, CI Pigment Red 175, CI
Pigment Red 176, CI Pigment Red 185, CI Pigment Red 208) comprises
various pigments that generally have good heat stability, excellent
solvent resistance, or a combination thereof.
[0686] Disazo condensation pigment (CI Pigment Red 144, CI Pigment
Red 166, CI Pigment Red 214, CI Pigment Red 220, CI Pigment Red
221, CI Pigment Red 242) comprises various pigments that generally
have excellent heat stability, good solvent resistance, or a
combination thereof.
[0687] Quinacridone (CI Pigment Red 122, CI Pigment Red 192, CI
Pigment Red 202, CI Pigment Red 207, CI Pigment Red 209) comprises
a various pigments that generally have bright color, excellent heat
stability, excellent solvent resistance, excellent chemical
resistance, good lighffastness, or a combination thereof.
[0688] Perylene (CI Pigment Red 123, CI Pigment Red 149, CI Pigment
Red 178, CI Pigment Red 179, CI Pigment Red 190, CI Pigment Red
224) comprises a various pigments that generally have excellent
heat stability, excellent solvent resistance, excellent
lightfastness, or a combination thereof.
[0689] Anthraquinone (CI Pigment Red 177) has a bright color, good
heat stability, good solvent resistance, good lightfastness, or a
combination thereof.
[0690] Dibromanthrone (CI Pigment Red 168) has a bright color,
moderate heat stability, good solvent resistance, excellent
lighffastness, or a combination thereof.
[0691] Pyranthrone (CI Pigment Red 216, CI Pigment Red 226) has a
dull color, moderate heat stability, good solvent resistance, poor
lightfastness in combination with titanium dioxide, or a
combination thereof.
[0692] Diketopyrrolo-pyrrole pigment (CI Pigment Red 254, CI
Pigment Red 255, CI Pigment Red 264, CI Pigment Red 270, CI Pigment
Red 272) comprises a various pigments that generally have a bright
color, good opacity, excellent heat stability, excellent solvent
resistance, or a combination thereof.
[0693] (xi) Metallic Pigments
[0694] In certain embodiments, a coating may comprise a metallic
pigment. A "metallic pigment" is a pigment that confers a metallic
appearance to a coating, and as previously described, is often a
corrosion resistance pigment. A metallic pigment may be selected
for a topcoat, particularly to confer a metallic appearance, a
primer, particularly to confer a corrosion resistance property, an
automotive coating, an industrial coating, or a combination
thereof. Metallic flake pigments are preferred for embodiments
wherein UV and/or infrared resistance is to be conferred to a
coating. Additionally, as some enzymes comprise a metal atom in the
active site, inclusion of a metallic pigment and/or other
composition comprising a metal during coating preparation, or
addition later (e.g., a multipack coating) may stimulate a desired
enzyme activity. Examples of a metallic pigment include aluminum
flake (CI Pigment Metal 1); aluminum non-leafing, gold bronze
flake, zinc dust, stainless steel flake, nickel (e.g., flake,
powder), or a combination thereof.
[0695] (4) Extender Pigments
[0696] An extender pigment ("inert pigment," "extender," "inert,"
"filler") is a substance that is insoluble in the other components
of a coating, and further confers a desirable optical property
(e.g., opacity, gloss), a Theological property, physical property,
an antisettling property, or a combination thereof, to the coating
and/or film. An extender pigment is often white or near white in
color, and typically are used to provide a cheap partial substitute
for a more expensive white pigment (e.g., titanium dioxide). Often
an extender has a refractive index below 1.7. In some aspects, an
extenders refractive index is 1.30 to 1.70, including all
intermediate ranges and combinations thereof. Examples of an
inorganic extender include a barium sulphate (CI Pigment White 21,
CI Pigment White 22); 1); a calcium carbonate (CI Pigment White
18); a calcium sulphate; a silicate (CI Pigment White 19, CI
Pigment White 26); a silica (CI Pigment White 27); or a combination
thereof.
[0697] Calcium carbonate ("calcite," "whiting," "limestone," CI
Pigment White 18) is generally chemically inert with the exception
of reactions with an acid. Calcium carbonate may be used in a
water-borne coating or a solvent-borne coating. Properties
specifically associated with calcium carbonate include conferring
settling resistance, sag resistance, or a combination thereof.
Precipitated calcium carbonate obtained from processing of
limestone, and may have superior opacity.
[0698] Kaolin ("china clay") is typically selected for a latex
coating, an alkyd coating, an architectural coating, or a
combination thereof. In addition to the typical properties of an
extender (e.g., opacity), kaolin can confer scrub resistance to a
coating.
[0699] Talc is a hydrated magnesium aluminum silicate, and is
soluble in water. Talc may be selected for an architectural coating
(e.g., interior, exterior), a primer, a traffic marker coating, an
industrial coating, or a combination thereof. Talc comprising a
platy particle shape can confer chemical resistance, water
resistance, improved flow property, or a combination thereof.
[0700] Silica is silicon dioxide, and may be classified as
crystalline silica, diatomaceous silica or synthetic silica.
Crystalline silica is produced from crushed and ground quartz, and
may be selected for an architectural coating, an industrial
coating, a primer, a latex coating, a powder coating, or a
combination thereof. Crystalline silica may confer burnish
resistance to a coating and/or film. Diatomaceous silica
("diatomaceous earth," "diatomite") is the mineral fossil of
diatoms which were single celled aquatic plants. Diatomaceous
silica may be selected for an architectural coating, a latex
coating, or a combination thereof. Diatomaceous silica may also
function as a flattening agent. Synthetic silica is produced from
chemical reactions, and includes, for example, precipitated silica,
fumed silica, or a combination thereof. Precipitated silica may be
selected for an industrial coating, a solvent-borne coating, or a
combination thereof. Precipitated silica may also function as a
flattening agent. Fumed silica may be selected for an industrial
coating. Fumed silica may also function as a flattening agent, a
rheology modifier, or a combination thereof.
[0701] Mica is a hydrous silica aluminum potassium silicate, and
typically comprises plate shaped particles. Mica may be selected
for an architectural coating, an exterior coating, a traffic marker
coating, a primer, or a combination thereof. Mica may also confer
durability, moisture resistance, corrosion resistance, heat
resistance, chemical resistance, cracking resistance, sagging
resistance, or a combination thereof, to a coating and/or film.
[0702] Barium sulfate may be classified as baryte or a blanc fixe.
Baryte may be selected for an automotive coating, an industrial
coating, a primer, an undercoat, or a combination thereof. Blanc
fixe has good opacity for an extender, and may be selected for an
automotive coating, an industrial coating, or a combination
thereof.
[0703] Wollastonite is a calcium metasilicate, and may be selected
for a latex coating. Wollasonite may also function as an alkali pH
buffer. Surface modified wollasonite may be selected for an
industrial coating.
[0704] Nepheline syenite is an anhydrous sodium potassium aluminum
silicate, and may be selected for an architectural coating, a latex
coating, an interior coating, an exterior coating, or a combination
thereof. Nepheline syenite may function may confer cracking
resistance, scrub resistance, or a combination thereof.
[0705] Sodium aluminosilicate may be selected for a latex coating,
an architectural coating, or a combination thereof. Sodium
aluminosilicate may also function as a flattening agent.
[0706] Alumina trihydrate may be selected for an architectural
coating, a thermoplastic coating, a thermosetting coating, or a
combination thereof. Alumina trihydrate may confer flame retardancy
to a film.
[0707] b. Dyes
[0708] A dye is a composition that is soluble in the other
components of a coating, and further confers a desirable color
property to the coating. It is contemplated that many of the
compounds that give a microorganism derived particulate material of
the present invention color such as photosynthetic pigment and/or
carotenoid pigment, will be partly or fully soluble in many
non-aqueous liquids described herein. It is further contemplated
that a microorganism derived particulate material of the present
invention is added to a coating comprising such a liquid component,
the material may act as a dye, as well as a pigment and/or
extender, due to the dissolving of colored compounds into the
liquid component.
[0709] 4. Coating Additives
[0710] A coating additive is any material which is added to a
coating to confer a desirable property other than that described
for a binder, a liquid component, a colorizing agent, or a
combination thereof. It is contemplated that, in addition to the
examples of additives described herein, any additive known to one
of ordinary skill in the art, in light of the present disclosures,
may be included in a composition of the present invention.
[0711] Examples of coating additives include a microorganism based
particulate material of the present invention, as well as an
antifloating agent, an antiflooding agent, an antifoaming agent, an
antisettling agent, an antiskinning agent, a catalyst, a corrosion
inhibitor, a film-formation promoter, a leveling agent, a matting
agent, a neutralizing agent, a preservative, a thickening agent, a
wetting agent, or a combination thereof. The content for an
individual coating additive in a coating generally is 0.001% to
20.0%, including all intermediate ranges and combinations thereof.
However, in most embodiments, it is contemplated the concentration
of a single additive in a coating will comprise between 0.001% and
10.0%, including all intermediate ranges and combinations
thereof.
[0712] a. Preservatives
[0713] A coating may comprise a preservative to reduce or prevent
the deterioration of a coating and/or film by a microorganism. As
would be known to one of ordinary skill in the art, a microorganism
is generally considered a contaminant capable damaging a film
and/or coating the point of suitable usefulness in a given
embodiment. A surprising and unexpected aspect of the present
invention is the discovery of the suitability of a microorganism
based particulate material of the present invention for use as a
purposefully added coating component. However, it is preferred that
a coating comprising a microorganism based particulate material of
the present invention also comprises a preservative. It is
contemplated that continued growth of a microorganism from the
microorganism base particulate material of the present invention
would be detrimental to a coating and/or film, and a preservative
may reduce or prevent such growth. It is further contemplated that
a contaminating microorganism could use the microorganism based
particulate material of the present invention as a readily
available source of nutrients for growth, and a preservative may
reduce or prevent such growth. It is also contemplated that the
amount of preservative added to a coating comprising a
microorganism based particulate material of the present invention
may be increased relative to a preservative content of a similar
coating lacking such an added microorganism based particulate
material. In certain aspects, it is contemplated that the amount of
preservative may be increased 1.1 to 10-fold or more, including all
intermediate ranges and combinations thereof, the amount of an
example of a preservative content described herein or as would be
known to one of ordinary skill in the art in light of the present
disclosures.
[0714] Examples of preservatives include a biocide, which kills an
organism, a biostatic, which reduces or prevents the growth of an
organism, or a combination thereof. Examples of a biocide include,
for example, a bactericide, a fungicide, an algaecide, or a
combination thereof. Examples of bacteria commonly found to
contaminate a coating and/or film include Pseudomonas spp.,
Aerobacter spp., Enterobacter spp., Flavobacterium spp. (e.g.,
Flavobacterium marinum), Bacillus spp., or a combination thereof.
Examples of fungi commonly found to contaminate a coating and/or
film include Aureobasidium pullulans, Alternaria dianthicola, Phoma
pigmentivora, or a combination thereof. Examples of algae commonly
found to contaminate a coating and/or film include Oscillotoria
sp., Scytonema sp., Protoccoccus sp., or a combination thereof.
Techniques are known to those of ordinary skill in the art for
determining microbial contamination of a coating and/or coating
component (see, for example, "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D5588-97, 2002).
[0715] In addition to the disclosures herein, a preservative and
use of a preservative in a coating is known to those of skill in
the art, and all such materials and techniques for using a
preservative in a coating may be applied in the practice of the
present invention (see, for example, Flick, E. W. "Handbook of
Paint Raw Materials, Second Edition," 263-285 and 879-998, 1989; in
"Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp 261-267 and
654-661, 1995; in "Paint and Surface Coatings, Theory and Practice,
Second Edition," (Lambourne, R. and Strivens, T. A., Eds.), pp.
193-194, 371-382 and 543-547, 1999; Wicks, Jr., Z. W., Jones, F.
N., Pappas, S. P. "Organic Coatings, Science and Technology, Volume
1: Film Formation, Components, and Appearance," pp. 318-320, 1992;
Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic Coatings,
Science and Technology, Volume 2: Applications, Properties and
Performance," pp.145, 309, 319-323 and 340-341, 1992; and in
"Paints, Coatings and Solvents, Second, Completely Revised
Edition," (Stoye, D. and Freitag, W., Eds.) pp 6,127 and 165,
1998.
[0716] A coating, film, surface, or a combination thereof may be
detrimentally affected by the presence of a living microorganism.
For example, a living microorganism can alter viscosity due to
damage to a cellulosic viscosifier; alter a rheological property by
increasing the gelling of a coating; produce an undesirable color
alteration ("discoloration") by production of a colorizing agent;
produce undesirable gas and increase foam; produce an undesirable
odor; lower pH; damage a preservative; produce slime; reduce
adhesion by a film; increase corrosion of a metal surface by
moisture production by an organism; increase corrosion of a metal
surface by film damage; damage a wooden surface by colonization
(e.g., fungal colonization); or a combination thereof. These
changes can lead to the coating and/or film becoming unsuitable for
use. The undesirable growth of a microorganism is generally more
prevalent in a water-borne coating, as the solvent component of a
solvent borne-coating usually acts as a preservative. However, a
film is generally susceptible to such damage by growth of a
microorganism after loss of a solvent (e.g., evaporation) during
film formation. Additionally, various bacteria (e.g., Bacillus
spp.) and fungi produce spores, which are cells that are relatively
durable to unfavorable conditions (e.g., cold, heat, dehydration, a
biocide), and may persist in a coating and/or film for months or
years prior to germinating into a damaging colony of cells.
[0717] In certain embodiments, a preservative may comprise an
in-can preservative, an in-film preservative, or a combination
thereof. An in-can preservative is a composition that reduces or
prevents the growth of a microorganism prior to film formation.
Addition of an in-can preservative during a water-borne coating
production typically occurs with the introduction of water to a
coating composition. Typically, an in-can preservative is added to
a coating composition for function during coating preparation,
storage, or a combination thereof. An in-film preservative is a
composition that reduces or prevents the growth of a microorganism
after film formation. In many embodiments, an in-film preservative
is the same chemical as an in-can preservative, but added to a
coating composition at a higher (e.g., two-fold) concentration for
continuing activity after film formation.
[0718] Examples of preservatives that have been used in coatings
include a metal compound (e.g., an organo-metal compound) biocide,
an organic biocide, or a combination thereof. Examples of a metal
compound biocide include barium metaborate, which is a fungicide
and bactericide; copper(II) 8-quinolinolate, which is a fungicide;
phenylmercuric acetate, tributyltin oxide, which is less preferred
for use against Gram-negative bacteria; tributyltin benzoate, which
is a fungicide and bactericide; tributyltin salicylate, which is a
fungicide; zinc 2-pyridinethiol-N-oxide, which is a fungicide; zinc
oxide, which is a fungistatic/fungicide and algaecide; a
combination of zinc-dimethyldithiocarbamate and zinc
2-mercaptobenzothiazole, which acts as a fungicide; zinc
2-pyridinethiol-N-oxide, which is a fungicide; a metal soap; or a
combination thereof. Examples of metals comprised in a metal soap
biocide include copper, mercury, tin, zinc, or a combination
thereof. Examples of an organic acid comprised in a metal soap
biocide include a butyl oxide, a laurate, a naphthenate, an
octoate, a phenyl acetate, a phenyl oleate, or a combination
thereof.
[0719] An example of an organic biocide that acts as an algaecide
includes
2-methylthio-4-tert-butylamino-6-cyclopropylamino-s-triazine.
Examples of an organic biocide that acts as a bactericide include a
combination of 4,4-dimethyl-oxazolidine and
3,4,4-trimethyloxazolidine; 5-hydroxy-methyl-1-aza-3,7-dioxabicylco
(3.3.0.) octane; 2(hydroxymethyl)-aminoethanol;
2-(hydroxymethyl)-amino-2-methyl-1-propano- l;
hexyhydro-1,3,5-tri-ethyl-5-triazine;
1-(3-chloroallyl)-3,5,7-triaza-1-- azonia-adamantane chloride;
1-methyl-3,5,7-triaza-1-azonia-adamantane chloride;
p-chloro-m-cresol; an alkylamine hydrochloride;
6-acetoxy-2,4-dimethyl-1,3-dioxane;
5-chloro-2-methyl-4-isothiazolin-3-on- e;
2-methyl-4-isothiazolin-3-one;
1,3-bis(hydroxymethyl)-5,5-dimethylhydan- toin;
hydroxymethyl-5,5-dimethylhydantoin; or a combination thereof.
Examples of an organic biocide that acts as a fungicide include a
parabens; 2-(4-thiazolyl)benzimidazole;
N-trichloromethyl-thio-4-cyclohex- ene-1,2-d icarboximide;
2-n-octyl-4-isothiazoline-3-one;
2,4,5,6-tetrachloro-isophthalonitrile; 3-iodo-2-propynyl butyl
carbamate; N-(trichloromethyl-thio)phthalimide;
tetrachloroisophthalonitrile; potassium
N-hydroxy-methyl-N-methyl-dithiocarbamate; sodium
2-pyridinethiol-1-oxide; or a combination thereof. Examples of a
parbens include butyl parahydroxybenzoate; ethyl
parahydroxybenzoate; methyl parahydroxybenzoate; propyl
parahydroxybenzoate; or a combination thereof. Examples of an
organic biocide that acts as an bactericide and fungicide include
2-mercaptobenzo-thiazole; a combination of
5-chloro-2-methyl-3(2H)-isothiazoline and
2-methyl-3(2H)-isothiazolone; a combination of
4-(2-nitrobutyl)-morpholine and 4,4'-(2-ethylnitrotrimethy- lene
dimorpholine;
tetra-hydro-3,5-di-methyl-2H-1,3,5-thiadiazine-2-thione- ;
potassium dimethyldithiocarbamate; or a combination thereof. An
example of an organic biocide that acts as an algaecide and
fungicide includes diiodomethyl-p-tolysulfone. Examples of an
organic biocide that acts as an algaecide, bactericide and
fungicide include glutaraldehyde; methylenebis(thiocyanate);
1,2-dibromo-2,4-dicyanobutane; 1,2-benzisothiazoline-3-one;
2-(thiocyanomethyl-thio)benzothiazole; or a combination thereof. An
example of an organic biocide that acts as an algaecide,
bactericide, fungicide and molluskicide includes
2-(thiocyanomethyl-thio)benzothiozole and methylene
bis(thiocyanate).
[0720] In certain embodiments an environmental law or regulation
may encourage the selection of an organic biocide such as a
benzisothiazolinone derivative. An example of a benzisothiazolinone
derivative is Busan.TM. 1264 (Buckman Laboratories, Inc.),
Proxel.TM. GXL (Avecia Inc.), or Preventol.RTM. VP OC 3068 (Bayer
Corporation), which comprises 1,2-benzisothiazolinone (CAS No.
2634-33-5). In the case of Busan.TM. 1264, the primary use is a
bactericide and/or fungicide at 0.03% to 0.5% in a water-borne
coating.
[0721] Often, a preservative is a proprietary commercial
formulation and/or a compound sold under a tradename. Examples
include organic biocides under the tradename Nuosept.RTM.
(International Specialty Products), which are typically used in a
water-borne coating. Specific examples of a Nuosept.RTM. biocide
includes Nuosept.RTM. 95, which comprises a mixture of bicyclic
oxazolidines, and is typically added to 0.2% to 0.3% concentration
to a coating composition; Nuosept.RTM. 145, which comprises an
amine reaction product, and is typically added to 0.2% to 0.3%
concentration to a coating composition; Nuosept.RTM. 166, which
comprises 4,4-dimethyloxazolidine, and is typically added to 0.2%
to 0.3% concentration to a basic pH water-borne coating
composition; or a combination thereof. A further example is
Nuocide.RTM. (International Specialty Products) biocides, which are
typically used fungicides and/or algaecides. Examples of a
Nuocide.RTM. biocide is Nuocide.RTM. 960, which comprises 96%
tetrachlorisophthalonitrile (CAS No.1897-45-6), and is typically
used at 0.5% to 1.2% in a water-borne or solvent-borne coating as a
fungicide; Nuocide.RTM. 2010, which comprises chlorothalonil and
IPBC at 30%, and is typically used at 0.5% to 2.5% in a coating as
a fungicide and algaecide; Nuocide.RTM. 1051 and Nuocide.RTM. 1071,
each which comprises 96%
N-cyclopropyl-N-(1-dimethylethyl)-6-(methylthio)-1,3,-
5-triazine-2,4-diamine, and is typically used as an algaecide in
antifouling coatings at 1.0% to 6.0% or water-based coatings at
0.05% to 0.2%, respectively; and Nuocide.RTM. 2002, which comprises
chlorothalonil and a triazine compound at 30%, and is typically
used at 0.5% to 2.5% in a coating and/or a film as a fungicide and
algaecide.
[0722] An additional example of a tradename biocide for coatings
includes Vancide.RTM. (R. T. Vanderbilt Company, Inc.). Examples of
a Vancide.RTM. biocide include Vancide.RTM. TH, which comprises
hexahydro-1,3,5-triethyl- -s-triazine, and is generally used in a
water-borne coating; Vancide.RTM. 89, which comprises
N-trichloromethylthio-4-cyclohexene-1,2-dicarboximide and related
compounds such as captan, and is used as a fungicide in a coating
composition; or a combination thereof. A bactericide and/or
fungicide for coatings, particularly a water-borne coating, is a
Dowicil.TM. (Dow Chemical Company). Examples of a Dowicil.TM.
biocide include Dowicil TMQK-20, which comprises
2,2-dibromo-3-nitrilopropionamid- e (CAS No.10222-01-2), and is
used as a bactericide at 100 ppm to 2000 ppm in a coating;
Dowicil.TM. 75, which comprises 1-(3-chloroallyl)-3,5,7-tri-
aza-1-azoniaadamantane chloride (CAS No. 51229-78-8), and is used
as a bactericide at 500 ppm to 1500 ppm in a coating; Dowicil.TM.
96, which comprises 7-ethyl bicyclooxazolidine (CAS No. 7747-35-5),
and is used as a bactericide at 1000 ppm to 2500 ppm in a coating;
Bioban.TM. CS-1135, which comprises 4,4-dimethyloxazolidine (CAS
No. 51200-87-4), and is used as a bactericide at 100 ppm to 500 ppm
in a coating; or a combination thereof. An additional example of a
tradename biocide for coatings includes Kathon.RTM. (Rohm and Haas
Company). An example of a Kathon.RTM. biocide includes Kathon.RTM.
LX, which typically comprises
5-chloro-2-methyl-4-isothiazolin-3-one (CAS no 26172-55-4) and
2-methyl-4-isothiazolin-3-one (CAS no 2682-20-4) at 1.5%, and is
added from 0.05% to 0.15% in a coating. Examples of tradename
fungicides and algaecides include those described for
Fungitrol.RTM. (International Specialty Products), which are often
formulated for solvent-borne and water-borne coatings, and in-can
and film preservation. An example is Fungitrol.RTM. 158, which
comprises 15% tributyltin benzoate (15%) and 21.2% alkylamine
hydrochlorides, and is typically used at 0.35% to 0.75% in a
water-borne coating for in-can and film preservation. An additional
example is Fungitrol.RTM. 11, which comprises
N-(trichloromethylthio) phthalimide, and is typically used at 0.5%
to 1.0% as a fungicide for solvent-borne coating. A further example
is Fungitrol.RTM. 400, which comprises 98% 3-iodo-2-propynl N-butyl
carbamate ("IPBC") (Cas No. 55406-53-6), and is typically used at
0.15% to 0.45% as a fungicide for a water-borne or a solvent-borne
coating.
[0723] As would be known to one of ordinary skill in the art,
determination of whether damage to a coating and/or film is due to
microorganisms (e.g., film algal defacement, film fungal
defacement), as well as the efficacy of addition of a preservative
to a coating and/or film composition in reducing microbial damage
to a coating and/or film, may be empirically determined by
techniques such as those that are described in "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D3274-95, D4610-98, D2574-00,
D3273-00, D3456-86, D5589-97, and D5590-00, 2002; and in "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 654-661, 1995. Examples of
microorganisms typically selected in such procedures as positive
controls of a coating and/or film damaging microorganism include,
for example, Aspergillus oyzae (ATCC 10196), Aspergillus flavus
(ATCC 9643), Aspergillus niger (ATCC 9642), Pseudomonas aeruginosa
(ATCC 10145), Aureobasidium pullulans (ATCC 9348), Penicillium
citrinum (ATCC 9849), Penicillium funiculosum (ATCC 9644), or a
combination thereof.
[0724] b. Wetting Additives and Dispersants
[0725] It is contemplated that one or more types of particulate
matter may be incorporated into a coating composition of the
present invention. As is known to those of ordinary skill in the
art, physical force and/or chemical additives are used to promote a
desirable level of dispersion of particulate matter in a coating
composition, for purposes such as coating homogeneity and ease of
application. Depending upon whether such an additive is admixed
earlier or latter in a coating composition, such an additive is
known as a wetting agent or a dispersant, respectively, though it
is common that an additive has dual classification. A wetting agent
and/or a dispersant often can be used to reduce the particulate
matter grinding time during coating preparation, improve wetting of
particulate matter, improve dispersion of particulate matter,
improve gloss, improve leveling, reduce flooding, reduce floating,
reduce viscosity, reduce thixotropy, or a combination thereof.
[0726] (1) Wetting Additives
[0727] As is known to those of ordinary skill in the art,
preparation of a coating comprising particulate material often
comprises a step wherein the particulate material is dispersed in
an additional coating component. An example of this type of
dispersion step is the dispersion of a pigment into a combination
of a liquid component and a binder to form a material known as a
millbase. A wetting additive ("wetting agent") is a composition
added to promote dispersion of particulate material during coating
preparation.
[0728] In certain embodiments, a wetting agent is a molecule that
comprises a polar region and a nonpolar region. An example is an
ethylene oxide molecule comprising a hydrophobic moiety. Such a
wetting agent is thought to act by reducing interfacial tension
between a liquid component and particulate matter. In specific
aspects, a wetting agent comprises a surfactant. Examples of such a
wetting agent include pine oil, which is typically added at 1% to
5% of the total coating liquid component, including all
intermediate ranges and combinations thereof. Other examples of
wetting agents include a metal soap, such as, for example, calcium
octoate, zinc octoate, aluminum stearate, zinc stearate, or a
combination thereof. An additional example of a wetting agent is
bis(2-ethylhexyl)sulfosuccinate ("Aerosol OT") (Cas No. 577-11-7);
(octylphenoxy)polyethoxyethanol octylphenyl-polyethylene glycol
("Igepal-630") (Cas no. 9036-19-5); nonyl phenoxy poly (ethylene
oxy) ethanol ("Tergitol NP-14") (Cas No. 9016-45-9); ethylene
glycol octyl phenyl ether ("Triton X-100") (CAS No. 9002-93-1); or
a combination thereof.
[0729] Often a wetting agent and/or dispersant is a proprietary
formulation and/or commonly available under a trade name. Examples
include an Anti-Terra.RTM. or Disperbyk.RTM. (BYK-Chemie GmbH) and
EnviroGem.RTM. or Surfynol.RTM. (Air Products and Chemicals, Inc.)
wetting agents and/or dispersants. An example is Anti-Terra.RTM.-U,
which comprises a 50% solution of an unsaturated polyamine amide
salt and a lower molecular weight acid, dissolved in xylene and
isobutanol, and preferred for used in a solvent-borne coating.
Anti-Terra.RTM.-U is typically added from 1% to 2% to an inorganic
pigment, 1% to 5% to an organic pigment, and at 0.5% to 1.0% to
titanium dioxide, and 30% to 50% to a bentonite. An example of a
Disperbyk.RTM. is Disperbyk.RTM., which comprises a polycarboxylic
acid polymer alkylolammonium salt and water, and is added to 0.3%
to 1.5% to the solvent-borne or water-borne coating composition. A
further example is Disperbyk.RTM.-101, which comprises a 52%
solution of a long chain polyamine amide salt and a polar acidic
ester, dissolved in a mineral spirit and butylglycol, and preferred
for used in a solvent-borne coating. The ranges for addition to
particulate material for Disperbyk.RTM.-101 is similar to
Anti-Terra.RTM.-U. An additional example is Disperbyk.RTM.-108,
which comprises over 97% of a hydroxyfunctional carboxylic acid
ester that includes moieties with pigment affinity, and is
typically added from 3% to 5% to an inorganic pigment, 5% to 8% to
an organic pigment. However, Disperbyk.RTM.-108 is typically added
at 0.8% to 1.5% to titanium dioxide, or 8% to 10% to a carbon
black, and is preferred for coatings lacking a non-aqueous solvent.
A supplemental example is EnviroGem.RTM. AD01, which comprises a
non-ionic wetting agent with a defoaming property, and is added to
0.1% to 2% to a water-borne coating composition. An additional
example is Surfynol.RTM. TG (Air Products and Chemicals, Inc.),
which comprises a non-ionic wetting agent, and is added to 0.5% to
5% to a water-borne coating composition. A further example is
Surfynol.RTM. 104 (Air Products and Chemicals, Inc.), which
comprises a non-ionic wetting agent, dispersant, and defoamer, and
is added to 0.05% to 3% to a water-borne coating composition.
[0730] (2) Dispersants
[0731] As is known to those of ordinary skill in the art,
maintenance of the dispersal of particulate matter comprised within
a coating composition is often promoted by the addition of a
dispersant. A dispersant ("dispersing additive," "deflocculant,"
"antisettling agent") is a composition that is added to promote
continuing dispersal of particulate matter. In specific aspects, a
dispersant is added to a coating composition to reduce or prevent
flocculation. Flocculation is the process wherein a plurality of
primary particles that have been previously dispersed form an
agglomerate. In other aspects, a dispersant is added to a coating
composition to prevent sedimentation of particulate matter.
Standard procedures to determining the degree of settling by
particulate matter in a coating (e.g., paint) are described, for
example, in "ASTM Book of Standards, Volume 06.02, Paint--Products
and Applications; Protective Coatings; Pipeline Coatings," D869-85,
2002.
[0732] Often a dispersant is a compound comprising phosphate, such
as, for example, tetra-potassium pyrophosphate or "TKPP" (CAS No.
7320-34-5). Examples of a tradename/proprietary phosphate compounds
are those known as a Strodex.TM. (Dexter Chemical L.L.C.),
including Strodex.TM. PK-90, Strodex.TM. PK-0VOC, and/or
Strodex.TM. MOK-70, which comprise a phosphate ester
surfactant.
[0733] In some aspects, a dispersant may be a particulate material.
Examples include Winnofil.RTM. SPT Premium, Winnofil.RTM. S,
Winnofil.RTM. SPM, and Winnofil.RTM. SPT (Solvay Advanced
Functional Minerals), which comprise 97.4% calcium carbonate (CAS
No.471-34-1) coated with 2.6% fatty acid (CAS No. 64755-01-7) and
generally used at 2% to 3%.
[0734] Various preparations of modified montmorillonite clay are
known in the art as a dispersant. Examples include those under the
name Bentone.RTM. (Elementis Specialties, Inc). Bentone.RTM.) 34
(Elementis Specialties, Inc), which comprises tetraallkyl ammonium
bentonite, and is prepared with 33% or more polar solvent prior to
addition to a coating composition. M-P-A.RTM. 14 (Elementis
Specialties, Inc.), which comprises a montmorillonite clay modified
by and organic chemical, and is prepared with 33% or more polar
solvent prior to addition to a solvent-borne coating composition.
Bentone.RTM. SD-1 (Elementis Specialties, Inc.), which comprises a
montmorillonite clay modified by and organic chemical, and
typically added from 0.2% to 2% by weight to a solvent-borne
coating composition, particularly those comprising an aliphatic
liquid component.
[0735] A further example of a dispersant is a castor wax
formulation under the trade names Crayvallac.RTM. SF,
Crayvallac.RTM. MT, and Crayvallac.RTM. AntiSettle CVP (Cray Valley
Limited), each of which are typically added from 0.2% to 1.5% as a
dispersant, thixotropy additive, anti-sagging agent, or a
combination thereof. Crayvallac.RTM. AntiSettle CVP comprises
caster wax ("hydrogenated caster oil"), and is suitable for a
solvent free epoxy-coating and a mineral spirit liquid component.
Crayvallac.RTM. SF and Crayvallac.RTM. MT each comprise amide
modified caster wax, and may be used in an epoxy-coating, an
acrylic-coating, a chlorinated rubber-coating, or a combination
thereof. Crayvallac.RTM. SF and Crayvallac.RTM. MT are preferred
for use with a liquid component comprising an aromatic hydrocarbon,
an alcohol, a glycol ether, or a combination thereof with
Crayvallac.RTM. MT being also preferred for use with a mineral
spirit.
[0736] c. Buffers
[0737] In certain embodiments, it is preferred to maintain a
coating's pH within a certain range. A coating may be acidic, which
is a pH between 0 and 7, including all intermediate ranges and
combinations thereof, or basic, which is a pH between 7 and 14,
including all intermediate ranges and combinations thereof. A
neutral pH is pH 7.0, and it is contemplated that a coating may
have a neutral pH, or a pH that is near neutral, which is a pH
between 6.5 and 7.5, including all intermediate ranges and
combinations thereof. A buffer may be added to maintain a coating's
pH as acidic, basic, neutral, or near neutral. In certain aspects,
a basic pH is preferred to optimize the function of a preferred
enzyme, such as, for example, OPH. Examples of buffers include a
bicarbonate (e.g., an ammonium bicarbonate), a monobasic phosphate
buffer, a dibasic phosphate buffer, Trizma base, a 5 zwitterionic
buffer, triethanolamine, or a combination thereof. In particular
facets, a buffer such as a bicarbonate, may provide a ligand or
co-substrate (e.g., water) on activator (e.g., carbon dioxide) to
an enzyme to promote an enzymatic reaction.
[0738] d. Rheology Modifiers
[0739] A rheology modifier ("rheology control agent," "rheology
additive," "thickener and rheology modifier," "TRM," "rheological
and viscosity control agent," "viscosifier," "viscosity control
agent," "thickener") is a composition that alters (e.g., increases,
decreases, maintains) a rheological property of a coating. A
thickener ("thickening agent") increases and/or maintains
viscosity. A rheological property is a property of flow and/or
deformation. Examples of a rheological property include viscosity,
brushability, leveling, sagging, or a combination thereof.
Viscosity is a measure of a fluid's resistance to flow (e.g., a
shear force). Brushability is the ease a coating can be applied
using an applicator (e.g., a brush). Leveling is the ability of a
coating to flow into and fill uneven areas of coating thickness
(e.g., brush marks) after application to a surface and before
sufficient film formation to end such flow. Sagging is the
gravitationally induced downward flow of a coating after
application to a surface and before sufficient film formation to
end such flow. It is specifically contemplated that a microorganism
based particulate material of the present invention may be added to
a coating as a rheology modifier.
[0740] A rheology modifier that alters viscosity (e.g., increases,
decreases, maintains) is known as a "viscosifier." During
application, a coating is usually subjected to a shear force
10.sup.3 s.sup.-1 to 10.sup.4 s.sup.-1 by techniques such as brush
application, and a shear force up to or greater than 10.sup.6
s.sup.-1 by techniques including, for example, blade application,
high-speed roller application, spray application, or a combination
thereof. As would be known to one of ordinary skill in the art, a
coating typically is formulated to possess a viscosity upon the
shear force of application that promotes the ease of application.
An example of a coating viscosity during application is between 0.5
P ("50 mPa s") to 2.5 P ("250 mPa s"), including all intermediate
ranges and combinations thereof. In certain aspects, a coating may
possess a viscosity greater or lower than this range, however, it
is contemplated such a viscosity may make the coating more
difficult to apply using the above application techniques.
Post-preparation and/or post-application, a coating is usually
subjected to a shear force of 10 s.sup.-1 to 10.sup.-3 s.sup.-1
produced, for example, by forces such as gravity, capillary
pressure, or a combination thereof. In embodiments wherein a
coating's viscosity is too high at these levels of shear force,
leveling during and/or after application may be undesirably low. In
embodiments wherein a viscosity is to low at these levels of shear
force, a coating may suffer in-can settling, sagging during or
after application, or a combination thereof. A preferred viscosity
of a coating post-preparation and/or application is between 100 P
("10 Pa s") to 1000 P ("100 Pa s"), the including all intermediate
ranges and combinations thereof. Of course, the viscosity of a
coating will change post-application in embodiments wherein film
formation occurs; however, the post-application viscosity refers to
the viscosity prior to completion of film formation, and may be
determined immediately post-application (e.g., within seconds,
within minutes) as appropriate to the coating, as would be known to
one of ordinary skill in the art. In certain aspects, a coating may
possess a viscosity greater or lower than this range, however, it
is contemplated such a viscosity may make the coating more prone to
sagging and/or settling defects.
[0741] A rheology modifier is typically added to alter and/or
maintain a rheology property within a desired range
post-formulation, during application, post-application, or a
combination thereof. In specific embodiments, a rheology modifier
alters viscosity at or above 10.sup.3 s.sup.-1 and/or at or below
10 s.sup.-1. Viscosity, including non-Newtonian (e.g.,
shear-thinning) viscosity for coatings and/or coating components
(e.g., binders, binder solutions, vehicles) upon formulation with
or without a viscosity modifier can be empirically determined,
particularly for shear rates comparable to application techniques
(e.g., blade, brush, roller, spray) by standard techniques such as
in "ASTM Book of Standards, Volume 06.01, Paint--Tests for
Chemical, Physical, and Optical Properties; Appearance," D562-01,
D2196-99, D4287-00, D4212-99, D1200-94, D5125-97, and D5478-98,
2002; "ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D4958-97,
2002; and "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D1545-98, D1725-62, D6606-00 and D6267-98, 2002.
Additionally, other rheological properties can be determined to aid
formulation of a coating of the present invention using techniques
known to those of ordinary skill in the art. For example, brush
drag, which is the resistance during coating (e.g., a latex)
application using a brush, can be determined by standard
techniques, such as, for example, in "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D4040-99, 2002. In an additional
example, leveling and sagging can be empirically determined for a
coating by standard techniques such as in "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D4062-99 and D4400-99, 2002.
[0742] As would be known to one of ordinary skill in the art, the
addition of a coating component to a coating composition typically
alters a rheological property, and many coating components have
multiple classifications to include function as a rheology
modifier. Examples of coating components more commonly added for
function as a rheology modifier includes an inorganic rheology
modifier, an organometallic rheology modifier, an organic rheology
modifier, or a combination thereof. An example of an inorganic
rheology modifier includes a silicate such as a montmorillonite
silicate. An example of a montomorillonite silicate includes
aluminum silicate, a bentonite, magnesium silicate, or a
combination thereof. A silicate rheology modifier typically confers
a superior washfastness property, a superior abrasion resistance
property, or a combination thereof, to a coating relative to an
organic rheology modifier. An example of an organic rheology
modifier includes a cellulose ether, a hydrogenated oil, a
polyacrylate, a polyvinylpyrrolidone, a urethane, or a combination
thereof. Organic rheology modifiers of a polymeric nature (e.g., a
cellulose ether, a urethane, a polyacrylate, etc.) are sometimes
used as an associative thickener, and are preferred for a latex
coating. An organic rheology modifier typically confers a greater
water retention capacity property ("open time") to a coating
relative to a silicate rheology modifier. A common example of a
cellulose ether is a methyl cellulose, a hydroxyethyl cellulose, or
a combination thereof. An example of a hydroxyethyl cellulose
includes Natrosol.RTM. (Hercules Incorporated); Cellosize.TM. (Dow
Chemical Company); or a combination thereof. An example of
hydrogenated oil includes hydrogenated castor oil. An example of a
urethane rheology modifier ("associative thickener") includes a
hydrophobically modified ethylene oxide urethane ("HEUR"), which
comprises a polyethylene glycol block covalently linked by
urethane, and has both a hydrophilic and hydrophobic regions
capable of use in an aqueous environment. An example of a HEUR
includes a block of polyethylene oxide linked by an urethane and
modified with a nonyl phenol hydrophobe (Rohm and Haas Company).
Often a urethane rheology modifier confers a superior leveling
property over another type of organic rheology modifier. An example
of an organometallic rheology modifier includes a titanium chelate,
a zirconium chelate, or a combination thereof.
[0743] In addition to the disclosures herein, a rheology modifier
and use of a rheology modifier in a coating is known to those of
skill in the art, and such compositions and techniques may be
included in the practice of the present invention (see, for
example, Flick, E. W. "Handbook of Paint Raw Materials, Second
Edition," 808-843 and 879-998, 1989; in "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp 268-285 and 348-349, 1995; in "Paint and
Surface Coatings, Theory and Practice, Second Edition," (Lambourne,
R. and Strivens, T. A., Eds.), pp. 73, 218, 227, 352, 558-559 and
718, 1999; Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic
Coatings, Science and Technology, Volume 2: Applications,
Properties and Performance," pp. 42, 215, 293, 315, 320 and
323-328, 1992; and in "Paints, Coatings and Solvents, Second,
Completely Revised Edition," (Stoye, D. and Freitag, W., Eds.) pp
6, 128 and 166-167, 1998.
[0744] e. Defoamers
[0745] A coating sometimes comprises a gas capable of forming a
bubble ("foam") that can undesirably alter a physical and/or
aesthetic property. Undesirable gas incorporation into a coating
composition is often a side affect of coating preparation
processes, and a particular bane of latex coatings. Often, a
wetting agent and/or a dispersant used in a coating may promote
creation or retention of foam. Additionally, microorganisms can
produce gas, and in certain embodiments, a coating comprising a
microorganism based particulate material of the present invention
may also comprise a defoamer. A defoamer ("antifoaming agent,"
"antifoaming additive") is a composition that releases gas (e.g.,
air) and/or reduces foaming in a coating during production,
application, film formation, or a combination thereof. A defoamer
often acts by lowering the surface tension around a bubble,
allowing merging of a bubble with a second bubble, which produces a
larger and less stable bubble that collapses.
[0746] Examples of a defoamer include an oil (e.g., a mineral oil,
a silicon oil), a fatty acid ester, dibutyl phosphate, a metallic
soap, a siloxane, a wax, an alcohol comprising between six to ten
carbons, or a combination thereof. An example of an oil defoamer is
pine oil. In some aspects, an antifoaming agent is combined with an
emulsifier, a hydrophobic silica, or a combination thereof.
Examples of a tradename defoamer is a TEGO.RTM. Foamex 8050
(Goldschmidt Chemical Corp.), which comprises a polyether siloxane
copolymer and fumed silica, and typically is used at 0.1% to 0.5%
during coating preparation; and BYK.RTM.-31 (BYK-Chemie), which
comprises a paraffin mineral oil and hydrophobic compounds, and
typically is used at 0.1% to 0.5% in a coating.
[0747] f. Catalysts
[0748] A catalyst is an additive that promotes film formation by
catalyzing a cross-linking reaction in a thermosetting coating.
Examples of a catalyst include a drier, an acid or a base, and the
selection of the type of catalyst is specific to the chemistry of
the film formation reaction.
[0749] (1) Driers
[0750] A drier ("siccative") catalyzes is an oxidative film
formation reaction, such as those that occur in an oil-based
coating. In addition to the disclosures herein, an drier and use of
an drier in a coating is known to those of skill in the art, and
such materials and techniques for using an drier in a coating may
be applied in the practice of the present invention (see, for
example, Flick, E. W. "Handbook of Paint Raw Materials, Second
Edition," pp. 73-93 and 879-998, 1989; in "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp 30-35, 1995; in "Paint and Surface
Coatings, Theory and Practice, Second Edition," (Lambourne, R. and
Strivens, T. A., Eds.), pp. 190-192, 1999; Wicks, Jr., Z. W.,
Jones, F. N., Pappas, S. P. "Organic Coatings, Science and
Technology, Volume 1: Film Formation, Components, and Appearance,"
pp. 138, 317-318, 1992; Wicks, Jr., Z. W., Jones, F. N., Pappas, S.
P. "Organic Coatings, Science and Technology, Volume 2:
Applications, Properties and Performance" pp. 138,197-198, 330,
344, 1992; and in "Paints, Coatings and Solvents, Second,
Completely Revised Edition," (Stoye, D. and Freitag, W., Eds.) pp.
11, 48, 165, 1998.
[0751] A drier may comprise a metal drier, an alternative drier, a
feeder drier, or a combination thereof. Usually a drier comprising
a metal ("a metal drier") catalyzes the oxidative reaction.
Examples of a metal typically used in a drier includes aluminum,
barium, bismuth, calcium, cerium, cobalt, iron, lanthanum, lead,
manganese, neodymium, potassium, vanadium, zinc, zirconium, or a
combination thereof. Examples of types of metal driers include an
inorganic metal salt, a metal-organic acid salt ("soap"), or a
combination thereof. A "salt" is the composition formed between the
anion of an acid and the cation of a base. Typically, the acid and
base of a salt interact by an ionic bond. Examples of organic acids
used in such a soap include a monocarboxylic acid of 7 to 22 carbon
atoms. Examples of such a monocarboxylic acid include a linoleate,
a naphthenate, a neodecanoate, an octoate, a rosin, a synthetic
acid, a tallate, or a combination thereof. Examples of a drier
comprising a synthetic acid include those under the tradenames
Troymax.TM. (Troy Corporation). Though most driers are water
insoluble, water dispersible driers can be prepared by combining a
surfactant with a naphthenate drier and/or a synthetic acid drier.
However, water dispersible driers are typically obtained under a
tradename such as, for example, Troykyd.RTM. Calcium WD,
Troykyd.RTM. Cobalt WD, Troykyd.RTM. Manganese WD Troykyd.RTM.
Zirconium WD (Troy Corporation). Additionally, a potassium soap,
lithium soap, or a combination thereof, has limited aqueous
solubility.
[0752] A primary drier ("surface drier," "active drier," "top
drier") acts at the coating-external environment interface. A
secondary drier ("auxiliary drier," "through drier") acts
throughout the coating. Examples of primary driers include metal
driers comprising cobalt, manganese, vanadium, or a combination
thereof. Examples of secondary driers include metal driers
comprising aluminum, barium, calcium, cerium, iron, lanthanum,
lead, manganese, neodymium, zinc, zirconium, or a combination
thereof. A rare earth drier comprises lanthanum, neodymium, cerium,
or a combination thereof.
[0753] In many embodiments, it is contemplated that a coating will
comprise from 0.01% to 0.1%, including all intermediate ranges and
combinations thereof, of an individual metal of a primary drier, by
weight of the non-volatile components of a coating composition. In
many embodiments, it is contemplated that a coating will comprise
from 0.1% to 1.0%, including all intermediate ranges and
combinations thereof, of an individual metal of a secondary drier,
by weight of the non-volatile components of a coating composition.
Standard physical and/or chemical properties for various driers
comprising a metal (e.g., calcium, cerium, cobalt, iron, lead,
manganese, nickel, rare earth, zinc, zirconium), and procedures for
determining various metals' content for a driers are described in,
for example, "ASTM Book of Standards, Volume 06.04,
Paint--Solvents; Aromatic Hydrocarbons," D600-90, 2002; and "Volume
06.01, Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2373-85, D2374-85, D2375-85, D2613-01, D3804-02,
D3969-01, D3970-80, D3988-85, and D3989-01, 2002; and ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D564-87, 2002.
[0754] It is particularly preferred that in embodiments wherein a
secondary drier is used, it is combined with a primary drier, as
the activity of most secondary driers are often very limited when
acting without the presence of a primary drier. Skinning is
film-formation disproportionately at the coating-external
environment interface. Skinning often results in undesirable
wrinkle formation ("wrinkling") in the film. A primary drier
undesirably promotes skinning when acting without the presence of a
secondary drier. In certain aspects, zinc may be selected for
reducing wrinkling in thick films. In other aspects, calcium and/or
zirconium may be selected instead of lead, which may be limited due
to an environmental law or regulation. In some facets, an iron
drier, rare earth drier, or combination thereof, may be selected
for use during film formation by baking. However, an iron drier may
darken a coating. In further aspects, an aluminum drier may be
selected for an alkyd-coating.
[0755] An alternative drier is a type of drier developed for use in
a high solid and/or water-borne coating, due to the inefficiency of
a metal-soap drier in these types of coatings. Often, an
alternative drier is combined with a metal-soap drier. An example
of a metal soap drier include a 1,10-phenanthronine,
2,2'-dipyridyl. A feeder drier is a type of drier designed to
prolong the pot life of a coating in embodiments wherein a metal
soap drier is absorbed by a coating component such as a carbon
black pigment, an organic red pigment, or a combination thereof. A
feeder drier dissolves over time into the coating, thereby
providing a continual supply of drier. An example a feeder drier
include a tradename composition such as Troykyd.RTM. Perma Dry
(Troy Corporation).
[0756] (2) Acids
[0757] An acid catalyzes amino resin cross-linking between a
plurality of amino resins and/or an amino resin and an addition
resin, though an acid is more effective in promoting cross-linking
between the additional resin and an amino resin. A coating may
comprise a strong acid, a weak acid, or a combination thereof.
Examples of an acid include a strong acid or a weak acid. The rate
of curing is typically accelerated by selection of a strong acid
over a weak acid. Examples of a strong acid include,
p-toluenesulfonic acid ("PTSA"), dodecylbenzenesulfonic acid
("DDBSA"), or a combination thereof. Examples of a weak acid
include phenyl acid phosphate ("PAP"), butyl acid phosphate
("BAP"), or a combination thereof.
[0758] (3) Bases
[0759] A base catalyzes cross-linking between an acrylic resin and
an epoxy resin in-film formation. In specific aspects, the base
comprises, for example, a dodecyl trimethyl ammonium chloride, a
tri(dimethylaminomethyl) phenol, a melamine-formaldehyde resin, or
a combination thereof.
[0760] (iv) Urethane Catalysts
[0761] In specific aspects, a urethane coating comprises a catalyst
to accelerate the reaction between an isocyanate moiety and a
reactive hydrogen moiety. Examples of such a urethane catalyst
include a tin compound, a zinc compound, a tertiary amine, or a
combination thereof. Examples of a zinc compound include zinc
octoate, zinc naphthenate, or a combination thereof. Examples of a
tin compound include dibutyltin dilaurate, stannous octoate, or a
combination thereof. An example of a tertiary amine includes a
triethylene diamine.
[0762] g. Antiskinning Agent
[0763] An antiskinning agent is a composition, other than a drier,
that reduces film-formation at the coating-external environment
interface, reduce shrinkage ("wrinkling"), or a combination
thereof. Such antiskinning agents are often used to protect
coatings from undesired film-formation after a container of coating
has been opened, during normal film-formation, or a combination
thereof. Examples of antiskinning agents, with commonly used
coating concentrations in parentheses, include butyraloxime (0.2%),
cyclohexanone oxime, dipentene, exkin 1, exkin 2, exkin 3, guaiacol
(0.001% to 0.1%), methyl ethyl ketoxime (0.2%), pine oil (1% to
2%), or a combination thereof. Generally, an antiskinning agent
acts by reducing the rate of film-formation and/or promotes even
film-formation throughout a coating by slowing an oxidative
reaction that occurs as part of film formation. Examples of
antioxidant antiskinning agents include a phenolic antioxidant, an
oxime, or a combination thereof. Example of a phenolic antioxidant
includes guaiacol, 4-tert-butylphenol, or a combination thereof.
Oximes tend to evaporate such as during film formation, are
colorless, do not affect a coating's color property, and generally
do not significantly alter the time of film-formation. Examples of
an oxime include, butyraldoxime, methyl ethyl ketoxime,
cyclohexanone oxime, or a combination thereof. In certain facets,
an oxime is used to slow skinning promoted by a copper drier.
[0764] h. Light Stabilizers
[0765] A coating, a film and/or a surface may be undesirably
altered by contact with an environmental agent such as, for
example, oxygen, pollution, water (e.g., moisture), and/or
irradiation with light (e.g., UV light). To reduce such damaging
alterations to a coating and/or film, it is contemplated that a
coating composition may comprise a light stabilizer. A light
stabilizer ("stabilizer") is a composition that reduces or prevents
damage to a coating, film and/or surface by an environmental agent.
Such agents may alter the color, cause a separation between two
layers of film ("delamination"), promote chalking, promote crack
formation, reduce gloss, or a combination thereof. This is a
particular problem for a film in an exterior environment, such as,
for example, an automotive film. Additionally, wood surfaces are
susceptible to damage by environmental agents, particularly UV
light.
[0766] Typically, a light stabilizer may comprise a UV absorber, a
radical scavenger, or a combination thereof. A UV absorber is a
composition that absorbs UV light. Examples of UV absorbers include
a hydroxybenzophenone, a hydroxyphenylbenzotriazole, a
hydrozyphenyl-S-triazine, an oxalic anilide, yellow iron oxide, or
a combination thereof. A hydroxyphenylbenzotriazole generally
demonstrates the broadest range of UV wavelength absorption, and
converts the absorbed UV light into heat. Additionally, a
hydroxyphenylbenzotriazole and/or a hydrozyphenyl-S-triazine
usually have the longest effective use in a film due to a higher
resistance to photochemical reactions, relative to a
hydroxybenzophenone or an oxalic anilide.
[0767] A radical scavenger light stabilizer (e.g., a sterically
hindered amine) is a composition that chemically reacts with a
radical ("free radical"). Examples of a sterically hindered amine
("hindered amine light stabilizer," "HALS") include the ester
derivatives of decanedioic acid, such as HALS I
["bis(1,2,2,6,6,-pentamethyl-4-poperidinyl) ester"], which is used
in non-acid catalyzed coatings; HALS II ["bis(2,2,6,6,-tetramethy-
l-1-isooctyloxy-4-piperidinyl) ester"], which is typically used in
an acid catalyzed coating.
[0768] For embodiments wherein a coating, film, and/or surface is
primarily located in-doors, a range of 1% to 3%, including all
intermediate ranges and combinations thereof, of a light stabilizer
relative to binder content is contemplated. A range of 1% to 5%,
including all intermediate ranges and combinations thereof, of a
light stabilizer relative to binder content is contemplated for
exterior uses. Additionally, a combination of a UV absorber and a
radical scavenger light stabilizer are contemplated in some
embodiments, as the heat released by a UV absorber may promote
radical formation. Light stabilizers are often commercially
produced, and examples of UV absorber and/or a radical scavenger
light stabilizer sold under a tradename include Tinuvin.RTM. (Ciba
Specialty Chemicals) or Sanduvor.RTM. [Clariant LSM (America)
Inc.].
[0769] i. Corrosion Inhibitors
[0770] A coating comprising a liquid component that comprises
water, particularly a water-borne coating, may promote corrosion in
a container comprising iron, particularly at the lining, seams,
handle, etc. A corrosion inhibitor reduces corrosion by water or
another chemical. Examples of a corrosion inhibitor includes a
chromate, a phosphate, a molybdate, a wollastonite, a calcium
ion-exchanged silica gel, a zinc compound, a borosilicate, a
phosphosilicate, a hydrotalcite, or a combination thereof.
[0771] In certain embodiments, a corrosion inhibitor is an in-can
corrosion inhibitor, a flash corrosion inhibitor, or a combination
thereof. An in-can corrosion inhibitor ("can-corrosion inhibitor")
is a composition that that reduces or prevents such corrosion.
Examples of an in-can corrosion inhibitor are sodium nitrate,
sodium benzoate, or a combination thereof. These compounds are
typically used at a concentration of 1% each in a coating
composition. In-can corrosion inhibitor are often commercially
produced, and an example includes SER-AD.RTM. FA179 (Condea Servo
LLC.), typically used at 0.3% in a coating composition. A flash
corrosion inhibitor ("flash rust inhibitor") is a composition that
reduces or prevents corrosion produced by application of a coating
comprising water to a metal surface (e.g., an iron surface). Often,
in-can corrosion inhibitors at increased concentrations are added
to a coating composition to act as a flash corrosion inhibitor. An
example of a flash corrosion inhibitor includes sodium nitrite,
ammonium benzoate, 2-amino-2-methyl-propan-1-ol ("AMP"),
SER-AD.RTM. FA179 (Condea Servo LLC.), or a combination thereof.
Standard procedures to determining the effectiveness of corrosion
inhibition by a coating comprising a flash rust inhibitor are
described, for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D5367-00, 2002.
[0772] j. Dehydrators
[0773] In some embodiments, preventing moisture from contacting
coating component such as a binder, solvent, pigment, or a
combination thereof, may be desired. For example, certain urethane
coatings undergo film-formation in the presence of moisture, as
well as produce a film with increased yellowing, increased hazing
and/or decreased gloss. A dehydrator may be added during coating
production and/or storage to minimalize contact with moisture.
Examples of a dehydrator include Additive TI (Bayer Corporation),
Additive OF (Bayer Corporation), or a combination thereof. Additive
TI comprises a compound with one reactive isocyanate moiety, and it
is capable of reacting with compounds with a chemically reactive
hydrogen such as water, an alcohol, a phenol, or an amide. However,
in a preferred reaction with water, the reaction products are
carbon dioxide and toluenesulfonamide. The toluenesulfonamide is
generally inert relative to a urethane binder, and soluble in many
non-aqueous liquid components. In certain embodiments, a urethane
coating may comprise 0.5% to 4% Additive TI. Additive OF is a
dehydrator generally used in a urethane coating. In certain
embodiments, a urethane coating may comprise 1% to 3% Additive
OF.
[0774] k. Electrical Additives
[0775] In some embodiments, it is desirable to include an additive
to alter an electrical property of a coating (e.g., electrical
conductivity, electrical resistance). Examples of an additive to
alter an electrical property of a coating and/or coating component
include an anti-static additive, an electrical resistance additive,
or a combination thereof. An anti-static additive may be included
in a coating composition comprising a flammable component to reduce
the chance of an electrostatic spark occurring and igniting the
coating. An anti-static additive is a composition that increases
the electrical conductivity of a coating. An example of a flammable
component is a hydrocarbon solvent. Examples of an anti-static
additive include Stadis.RTM. 425 (Octel-Starreon LLC USA),
Stadis.RTM. 450 (Octel-Starreon LLC USA), or a combination thereof.
An electrical resistance additive is a composition that reduces the
resistance to electricity by a coating. An electrical resistance
additive may be included in a coating to improve the ability of a
coating to be applied to a surface using an electrostatic spray
applicator. For example, an oxygenated compound (e.g., a glycol
ether) often possesses a high electrical conductivity, which can
make use of an electrostatic spray applicator to apply a coating
comprising an oxigenated compound relatively more difficult than a
similar coating lacking an oxigenated compound. Examples of an
electrical resistance additive include Ramsprep, Byk-ES 80
(BYK-Chemie GmbH), or a combination thereof. Byk-ES 80 comprises,
for example, an unsaturated acidic carboxylic acid ester
alkylolammonium salt, and typically is added between 0.2% and 2% to
a coating composition. Additionally, techniques for determining an
electrical property (e.g., electrical resistance) of a coating
comprising an electrical additive are known to those of ordinary
skill in the art (see, for example, "ASTM Book of Standards, Volume
06.01, Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D5682-95, 2002).
[0776] I. Anti-Insect Additives
[0777] Certain coatings may serve a protective role for a surface
or surrounding environment against insects, and thus may comprise
an anti-insect agent. An example of a surface where a coating
comprising an anti-insect agent may be desirable is a wooden
surface. Examples of an area where coating comprising an
anti-insect agent may be desirable would be a storage facility,
such as a cargo hold of a ship or railcar. An anti-insect agent is
a composition that, upon contact, is detrimental to the well-being
(e.g., life, reproduction) of an invertebrate pest (e.g., an
insect, an arachnid, etc). Examples of anti-insect additives that
have been used in coatings include copper naphthenate, tributyl tin
oxide, zinc oxide, 6-chloro epoxy hydroxy naphthalene, 1-dichloro
2,2'bis-(p-chlorophenyl)ethane, or a combination thereof.
[0778] 5. Coating Preparation
[0779] As would be known to one of ordinary skill in the art, a
coating may comprise insoluble particulate material. Particulate
material may comprise a primary particle, an agglomerate, an
aggregate, or a combination thereof. A primary particle is a single
particle not in contact with a second particle. An agglomerate is
two or more particles in contact with each other, and generally can
be separated by a dispersion technique, a wetting agent, a
dispersant, or a combination thereof. An aggregate is two or more
particles in contact with each other, which are generally difficult
to separate by a dispersion technique, a wetting agent, a
dispersant, or a combination thereof.
[0780] Usually, a pigment, an extender, certain types of rheology
modifiers, certain types of dispersants, or a combination thereof
are the major sources of particulate material in a coating. In the
present invention, microorganism derived particulate material will
also be a source of particulate material in a coating. In certain
embodiments, a micoorganism-based particulate matter of the present
invention may be used in combination with and/or as a substitute
for a pigment, an extender, a rheology modifier, a dispersant, or a
combination thereof. In specific facets, a micoorganism-based
particulate matter of the present invention may substitute for
0.001% to 100%, including all intermediate ranges and combinations
thereof, of a pigment, an extender, a rheology modifier, a
dispersant, or a combination thereof. It is contemplated that any
technique used in the preparation of a coating that comprises a
pigment, extender or any other form of particulate material
described herein or would be known to one of ordinary skill in the
art may be applied in the preparation of a coating comprising the
microorganism derived particulate material of the present
invention. Incorporation of particulate materials (e.g., pigments),
assays for determining a rheological property and/or a related
property (e.g., viscosity, flow, molecular weight, component
concentration, particle size, particle shape, particle surface
area, particle spread, dispersion, flocculation, solubility, oil
absorption values, CPVC, hiding power, corrosion resistance, wet
abrasion resistance, stain resistance, optical properties,
porosity, surface tension, volatility, settling, leveling, sagging,
slumping, draining, floating, flooding, cratering, foaming,
splattering,) of a coating component and/or a coating (e.g.,
pigment, binder, vehicle, surfactant, dispersant, paint) and
procedures for determining such properties, as well as procedures
for large scale (e.g., industrial) coating preparation (e.g.,
wetting, pigment dispersion into a vehicle, milling, letdown) are
described in, for example, in Patton, T. C. "Paint Flow and Pigment
Dispersion, A Rheological Approach to Coating and Ink Technology,"
1979.
[0781] In many embodiments, dispersion of the particulate material
is promoted by application of physical force (e.g., impact, shear)
to the composition. Techniques such as grinding and/or milling are
typically used to apply physical force for dispersion of
particulate matter. Though it is contemplated that such application
of physical force may be used in the dispersal of the microorganism
based particulate material of the present invention, such force may
damage the structural integrity of the cell wall and/or cell
membrane that confers size and shape to the material. The average
particle size and shape will be altered by the degree of damage to
the cell wall and/or cell membrane, which may alter a physical
property, a chemical property, an optical property, or a
combination thereof, of a microorganism based particulate material
of the present invention. Examples of a physical property that may
be altered by cell fragmentation include a Theological property,
such as the contribution to viscosity, flow, etc., the tendency to
form a primary particle, an agglomerate, an aggregate, etc. An
example of a chemical property that may be altered includes
allowing greater contact between amine and hydroxyl moieties of
internally located biomolecules (e.g., a proteinaceous molecule)
with a coating component, which may undergo a chemical reaction
(e.g., crosslinking) with a binder. An example of an optical
property that may be altered includes an alteration in the gloss
characteristic of a coating and/or film by a reduction in particle
size due to cell fragmentation.
[0782] A preferred embodiment of the microorganism based
particulate material is the material in the form of a "whole cell
material," which refers to particulate material resembling an
intact living cell upon microscopic examination, in contrast to
cell fragments of varying shape and size. It is contemplated that
such whole cell particulate material of the present invention will
encapsulate an expressed biomolecule (e.g., an enzyme) located in
and/or internal to a cell wall and/or cell membrane. In certain
aspects, the encapsulation of a biomolecule by a whole cell
particle may provide greater protection of the biomolecule from a
coating component (e.g., a solvent, a binder, an additive), a
coating related chemical reaction (e.g., thermosetting film
formation), a potentially damaging agent a coating and/or film may
contact (e.g., a chemical, a solvent, a detergent, etc.), or a
combination thereof, relative to a biomolecule located on the
external surface of a cell or otherwise not comprised within and/or
encapsulated by a cell wall and/or cell membrane. As would be known
to those of ordinary skill in the art, any preparation of a
microorganism will comprise a certain percentage of cell fragments,
which comprise pieces of a cell wall, cell membrane, and other cell
components (e.g., an expressed biomolecule). The whole cell
microorganism based particulate material of the present invention
will comprise 50% to 100%, including all intermediate ranges and
combinations thereof of whole cell material. The percentage of
whole cell material and cell fragments may be determined by any
applicable technique known to one of ordinary skill in the art such
as microscopic examination, centrifugation, etc, as well as any
technique described herein for determining the properties of a
pigment, extender, or other particulate material either alone or
comprises in a coating. It is contemplated that in some aspects,
cell fragments may be used as microorganism based particulate
material. The cell fragment microorganism based particulate
material of the present invention will comprise 50% to 100%,
including all intermediate ranges and combinations thereof of cell
fragment material.
[0783] For example, during typical preparation of a water-borne
and/or solvent-borne coating comprising particulate material such
as a pigment and/or extender, the particulate material is dispersed
into a paste known as a "grind" or "millbase." A combination of a
binder and a liquid component know as a "vehicle" is used to
disperse the particulate material into the grind. Often, a wetting
additive is included to promoted dispersion of the particulate
material. Additional vehicle and/or additives are admixed with the
grind in a stage refered to as the "letdown" to produce a coating
of a desired composition and/or properties. These techniques and
others for coating preparation are well known to those of ordinary
skill in the art [see, for example, in "ASTM Book of Standards,
Volume 06.01, Paint--Tests for Chemical, Physical, and Optical
Properties; Appearance," D6619-00, 2002; in "Paint and Surface
Coatings, Theory and Practice, Second Edition," (Lambourne, R. and
Strivens, T. A., Eds.), pp. 286-329, 1999; and in "Paints, Coatings
and Solvents, Second, Completely Revised Edition," (Stoye, D. and
Freitag, W., Eds.) pp. 178-193, 1998.] It is specifically
contemplated that these techniques may be used in preparing a
coating comprising the microorganism based particulate matter of
the present invention, wherein the particulate matter of the
present invention is treated as a pigment, extender, or other such
particulate material dispersed into a coating.
[0784] In another example, the effectiveness of the convertion of
agglomerates and/or an aggregates into primary particles in the
grind (e.g., pigments, pigment-vehicle combinations, pastes), and
latter stages (e.g., lacquer, paint) are typically measured to
insure quality, using techniques such as, for example, those
described in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
D1210-96, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D2338-02, D1316-93, and D2067-97, 2002; and in "ASTM
Book of Standards, Volume 06.03, Paint--Pigments, Drying Oils,
Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D185-84, 2002. It is specifically contemplated that
these techniques for the preparation of coatings comprising a
pigment, exender, or other particulate material may be used in the
practice of the present invention in the preparation of a coating
comprising a microorganism based particulate material of the
present invention.
[0785] In a further example, a microorganism based particulate
material of the present invention may be adapted for use in
standard coating formulation techniques to optimize a coating
composition for desired properties. As is known to those of
ordinary skill in the art, the pigment volume concentration is the
volume of pigment in the total volume solids of a dry film. The
volume solids is the fractional volume of binder and pigment in the
total volume of a coating. It is contemplated that in calculating
the PVC, the content of a microorganism based particulate material
of the present invention would be included in this or related
calculations as a pigment or extender. A related calculation to the
PVC that is specifically contemplated is the critical pigment
volume concentration ("CPVC") is the formulation of pigment and
binder wherein the coating comprises the minimum amount of binder
to fill the voids between the pigment particles. A pigment to
binder concentration that exceeds the CVPC threshold produces a
coating with empty spaces wherein gas (e.g., air, evaporated liquid
component), may be trapped. Various properties rapidly change above
the CPVC. For example, corrosion resistance, scrub resistance,
stain resistance, opacity, moisture resisitance, rigidity, gloss,
or a combination thereof, are more rapidly reduced above the CPVC,
while reflectance is often increased. However, in certain
embodiments, coating may be formulated above the CPVC and still
preduce a film suitable for given use upon a surface. Standard
procedures for determining CPVC are known to those of ordinary
skill in the art [see, for example, in "ASTM Book of Standards,
Volume 06.01, Paint--Tests for Chemical, Physical, and Optical
Properties; Appearance," D1483-95, D281-95, and D6336-98, 2002; and
in "Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 252-258,
1995].
[0786] The physical and/or optical properties of a coating are
affected by the size of particulate material comprised within the
coating. For example, inclusion of a physically hard particulate
material, such as a silica extender, may increase the abrasion
resistance of a film. In another example, gloss is reduced when
particulate material of a larger average particle size increases
the roughness of the surface of a coating and/or film. Standard
procedures for determining particle properties (e.g., size, shape)
are known to those of ordinary skill in the art (see, for example,
"ASTM Book of Standards, Volume 06.03, Paint--Pigments, Drying
Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D1366-86 and D3360-96, 2002; and in "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 305-332, 1995).
[0787] It is also contemplated that a biomolecule composition,
particularly one prepared as a particulate or powder material, may
be incorporated into a powder coating. Specific procedures for
determining the properties (e.g., particle size, surface coverage,
optical properties) of a powder coating and/or film have been
described, for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D3451-01, D2967-02a, D4242-02, D5382-02 and D5861-95,
2002.
[0788] In some embodiments, the dispersion of particulate material
("fineness of grind") in a coating is, in Hegman units ("Hu"), 0.0
Hu to 8.0 Hu, including all intermediate ranges and combinations
thereof. The dispersion of particulate material content of a
coating can be empirically determined, for example, as described in
"ASTM Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D1210-96, 2002. The
size of particulate matter in a coating can affect gloss, with
smaller particle size generally more conducive for a higher gloss
property of a coating and/or film. It is contemplated that a whole
cell particulate material of the present invention will possess
similar size and shape as the organism from which it was derived.
For example, E. coli is about 2 .mu.m in length and 0.8 .mu.m in
diameter, maize cells vary more in size, but a size of about 65
.mu.m in diameter may be found in some cell types, and Saccaromyces
cerivsia is about 10 .mu.m in diameter. Of course, processing and
purifying techniques may reduce the particle size by fragmentation
of the cell wall and membrane, and it is contemplated that a
biomolecule composition of the present invention may be prepared to
an average particle size for a specific purpose (e.g., gloss). In
certain facets, a visibly coarse and/or low gloss coating (e.g., a
low gloss finish, a flat latex paint) has a dispersion of
particulate material of 2.0 Hu to 4.0 Hu. A particle size of 100
.mu.m to 50 .mu.m is associated with a dispersion of 0.0 Hu to 4.0
Hu. In some aspects, a semi-gloss or gloss coating has a dispersion
of particulate material of 5.0 Hu to 7.5 Hu. A particle size of 50
.mu.m to 40 .mu.m, 40 .mu.m to 26 .mu.m, 26 .mu.m to 13 .mu.m, and
13 .mu.m to 6 .mu.m is associated with a dispersion of 4.0 Hu to
5.0 Hu, 5.0 Hu to 6.0 Hu, 6.0 Hu to 7.0 Hu, and 7.0 Hu to 7.5 Hu,
respectively. In other aspects, a high gloss coating has a
dispersion of particulate material of 7.5 Hu to 8.0 Hu. A particle
size of 6 .mu.m to 3 .mu.m and 3 .mu.m to 0.1 .mu.m is associated
with a dispersion of 7.5 Hu to 7.75 Hu and 7.75 Hu to 8.0 Hu,
respectively. In embodiments wherein a coating comprises a
combination of particulate materials, wherein the different
particulate materials such as a combination of a microorganism
derived particulate material of the present invention and one or
more of different pigments, with each type of particulate material
possessing a different average particle size, it is contemplated
that the gloss will be affected most by the particle size of the
largest type of particulate material added. However, gloss can also
be empirically determined for a coating and/or film, as described
herein or as would be known to one of ordinary skill in the art in
light of the present disclosures.
[0789] 6. Empirically Determining the Properties of Biomolecule,
Coatings and/or Film
[0790] A coating with a desired set of properties for a particular
use may be prepared by varying the ranges and/or combinations of
coating components, and such coating selection and preparation is
within the ability of one of ordinary skill in the art in light of
the present disclosures. For example, as would be known to those of
ordinary skill in the art, a variety of assays are available to
measure various properties of a coating, coating application,
and/or a film to determine the degree of suitability of a coating
composition for use in a particular application.
[0791] It is contemplated that in general embodiments, a coating
comprising a microorganism derived particulate material of the
present invention may be subjected to one or more of such assays.
Additionally, a microorganism derived particulate material may
further comprise a desired biomolecule (e.g., a colorant, an
enzyme), whether endogenously or recombinantly produced, that may
confer a desired property to a coating and/or film of the present
invention. As used herein, "bioactivity" refers to desired property
such as color, enzymatic activity, etc, conferred to a coating by a
biomolecule of a microorganism derived particulate material of the
present invention. As used herein, "bioactivity resistance" refers
to the ability of a biomolecule to confer a desired property during
and/or after contact with a stress condition normally assayed for
in a standard coating and/or film assay procedure. Examples of such
a stress condition includes, for example, a temperature (e.g., a
baking condition), contact with a coating component (e.g., an
organic liquid component), contact with a chemical reaction (e.g.,
thermosetting film formation), contact with coating and/or film
damaging agent (e.g., weathering, detergents, solvents), etc. In
specific facets, wherein a microorganism derived particulate
material of the present invention that comprises a desired
biomolecule, a biomolecule may possess a greater bioactivity
resistance such as as determined with standard assay procedure,
than a purified or partly purified-like biomolecule.
[0792] It is contemplated that such bioactivity resistance may be
determined using a standard procedure for a coating and/or film
described herein or as would be known to one of ordinary skill in
the art in light of the present disclosures. In one example, it is
contemplated that a microorganism derived particulate material may
comprise a desired colorant such as a chlorophyll, a caroteinoid,
etc, which may undergo a desired or undesired change in its optical
characteristics (e.g., color, opacity) upon baking at a particular
temperature. Various procedures for measuring the visual properties
of a coating and/or film are described herein or would be known to
those of ordinary skill in the art in light of the present
disclosures may be used to determine the properties and/or
tolerances of any such colorant.
[0793] In an additional example, any assay described herein or
would be known to one of ordinary skill in the art in light of the
present disclosures may be used to determine the bioactivity
resistance wherein an enzyme retains detectable enzymatic activity
upon contact with a condition typically encounter in a standard
assay. Additionally, in certain aspects, it is contemplated that a
coating and/or film comprising an enzyme may lose part of all of a
detectable, desirable bioactivity during the period of time of
contact with standard assay condition, but regain part or all of
the enzymatic bioactivity after return to non-assay conditions. An
example of this process is the thermal denaturation of an enzyme at
an elevated temperature range into a configuration with lowered or
absent bioactivity, followed by refolding of an enzyme, upon return
to a preferred temperature range for the enzyme, into a
configuration possessing part or all of the enzymatic bioactivity
detectable prior to contact with the elevated temperature. In
another example, an enzyme may demonstrate such an increase in
bioactivity upon removal of a solvent, chemical, etc.
[0794] In some embodiments, an enzyme identified as having a
desirable enzymatic property for one or more target substrates may
be selected for incorporation into a composition of the present
invention. The determination of an enzymatic property may be
conducted using any technique described herein or known to those of
ordinary skill in the art, in light of the present disclosures. For
example, the determination of the rate of cleavage of a substrate,
with or without a competitive or non-competitive enzyme inhibitor,
can be utilized in determining the enzymatic properties of an
enzyme, such as V.sub.max, K.sub.m, K.sub.cat/K.sub.m and the like,
using analytical techniques such as Lineweaver-Burke analysis,
Bronsted plots, etc (Dumas, D. P. et al., 1989a; Dumas, D. P. et
al., 1989b; Dumas, D. P. et al., 1990; Caldwell, S. R. and Raushel,
F. M., 1991c; Donarski, W. J. et al., 1989; Raveh, L. et al., 1992;
Shim, H. et al., 1998; Watkins, L. M. et al., 1997a; diSioudi, B.
et al., 1999; Hill, C. M., 2000; Hartleib, J. and Ruterjans, H.,
2001b; Lineweaver, H. and Burke, D., 1934; Segel, I. H., 1975). It
is contemplated that any such analysis may be used to identify an
enzyme with a specifically desirable enzymatic property for one or
more substrates.
[0795] In a specific example, phosphoric triester hydrolases have
demonstrated the ability to degrade a wide variety of OP compounds.
Methods for measuring the ability of an enzyme to degrade an OP
compound are known to those of ordinary skill in the art. It is
contemplated that any such technique may be utilized to determine
enzymatic activity of a composition of the present invention for a
particular OP compound.
[0796] Techniques for measuring the kinetics of enzymatic
detoxification for various OP-compounds comprising a P--S bond at
the phosphorous center (e.g., an OP-phosphonothiolate) such as VX
["EA 1701," "TX60," "O-ethyl-S-(diisopropylaminoethyl)
methylphosphonothioate"]; Russian VX ["R-VX,"
"O-isobutyl-S-(diisopropylaminoethyl) methylphosphonothioate"],
tetriso ["O, O-diisopropyl S-(2-diisoprpylaminoethyl)
phosphorothiolate"], echothiophate ("phospholine,"
"O,O-diethyl-phosphorothiocholine"), malathion ["phosphothion,"
"S-(1,2-dicarbethoxyethyl)-O,O-dimethyl dithiophosphate"],
dimethoate ["Cygon.RTM.," "Dimetate.RTM.,"
"O,O-dimethyl-S-(N-methylcarbomoyl-methyl- )phosphorodithioate"],
EA 5533 ["OSDMP," "O,S-diethyl methylphosphonothioate"], IBP
("Kitazin P," "O,O-diisopropyl-S-benzylphos- phothioate"), acephate
("O,S-dimethyl acetyl phosphoroamidothioate"), azinophos-ethyl
["S-(3,4-dihydro-4-oxobenzo (d)-1,2,3-triazin-3-yl
methyl-O,O-diethyl) phosphorothioate"], demeton S ["VX analogue,"
"O,O-diethyl-S-2-ethylthiolethylphosphorothioate"], malathion
["Phosphothion," "S-(1,2-dicarbethoxyethyl)-O,O-dimethyl
dithiophosphate"], and phosalone
["0,0-diethyl-S-(6-chloro-2-oxobenzoxazo- lin-3-yl-methyl)
phosphorod ithioate"], have been described (see, for example,
diSioudi, B. D. et al., 1999; Hoskin, F. C. G. et al., 1995;
Watkins, L. M. et al., 1997a; Kolakowski, J. E. et al., 1997;
Gopal, S. et al., 2000; and Rastogi, V. K. et al., 1997).
[0797] Techniques for measuring the kinetics of enzymatic
detoxification for various OP-compounds comprising a P--F bond at
the phosphorous center (e.g., an OP-phosphonofluoridate) such as
soman ("1,2,2-trimethylpropyl-m- ethylphosphonofluoridate"), sarin
("isopropylmethylphosphonofluoridate"), DFP ("O,O-diisopropyl
phosphorofluoridate"), alpha
("1-ethylpropylmethylphosphonofluoridate"), and mipafox
("N,N'-diisopropylphosphorofluorodiamidate") have been described
(see, for example Dumas, D. P. et al., 1990; Li, W.-S. et al.,
2001; diSioudi, B. D. et al., 1999; Hoskin, F. C. G. et al., 1995;
Gopal, S. et al., 2000; and DeFrank, J. and Cheng, T., 1991).
[0798] A technique for measuring the kinetics of enzymatic
detoxification for an OP-compound comprising a P--CN bond at the
phosphorous center (e.g., an OP-phosphonocyanate) such as tabun
("ethyl N,N-demethylamidophosphorocyanidate") has been described
(see, for example, Raveh, L. et al., 1992).
[0799] Techniques for measuring the kinetics of enzymatic
detoxification for various OP-compounds comprising a P--O bond at
the phosphorous center (e.g., an OP-triester) such as paraoxon
("diethyl p-nitrophenylphosphate"- ), the soman analogue
O-pinacolyl p-nitrophenyl methylphosphonate, the sarin analogue
O-isopropyl p-nitrophenyl methylphosphonate, NPPMP
("p-nitrophenyl-o-pinacolyl methylphosphonate"), coumaphos ["O.
O-diethyl
O-(3-chloro-4-methyl-2-oxo-2H-1benzyran-7-yl)phosphorothioate],
cyanophos ["O,O-dimethyl p-cyanophenyl phosphorothioate"], diazinon
("O,O-diethyl O-2-iso-propyl-4-methyl-6-pyrimidyl
phosphorothiate"), dursban ("O,O-diethyl
0-3,5,6-trichloro-2-pyridyl phosphorothioate"), fensulfothion
{"O,O-diethyl [p-(methylsulfinyl)phenyl] phosphorothioate"},
parathion ("O,O-diethyl O-p-nitrophenyl phosphorothioate"), methyl
parathion ("O,O-dimethyl p-nitrophenyl phosphorothioate"), ethyl
parathion ["O,O-diethyl-O-(4-nitrophenyl)phosph- orothioate"], EPN
("O-ethyl 0-(4-nitrophenyl) phenylphosphonothioate"), DEPP
("diethylphenylphosphate"), NPEPP
("p-nitrophenylethylphenylphosphin- ate") have been described (see,
for example, Dumas, D. P. et al., 1990; Li, W.-S. et al., 2001;
diSioudi, B. D. et al., 1999; Watkins, L. M. et al., 1997a; Gopal,
S. et al., 2000; Mulbry, W. and Karns, J., 1989; Hong, S.-B. and
Raushel, F. M., 1996; and Dumas, D. P. et al., 1989b).
[0800] In one example, the cleavage rate of a phosphonothiolate OP
substrate comprising a P--S bond can be measured using a method
known as the Ellman reaction. All such substrates produce a P--S
bond cleavage product comprising a free thiol group, which can
chemically react with the Ellman's reagent,
5,5'-dithio-bis-2-nitrobenzoic acid ("DTNB"). This reaction
produces 5'-thiol-2-nitrobenzoate anions with a maximum absorbency
at 412 nm. P--S cleavage can be determined by the appearance of the
free thiol group, measured using a spectrophotometer (Rastogi, V.
H. et al., 1997; Gopal, S. et al., 2000; diSioudi, B. et al., 1999;
Watkins, L. M. et al., 1997a; Hoskin, F. C. G. et al., 1995; Chae,
M. Y. et al., 1994; Ellman, G. L. et al., 1961).
[0801] In an additional example, the cleavage of an OP substrate
can be measured by detecting the production of a cleavage product
that comprises a released ion. In a further example, the cleavage
of a phosphonofluoridate can be measured by the release of cleavage
product comprising a fluoride ion (F.sup.-) using a fluoride ion
specific electrode and a pH/mV meter (Hartleib, J. and Ruterjans,
H., 2001a; Gopal, S. et al., 2000; diSioudi, B. et al., 1999;
Watkins, L. M. et al., 1997a; DeFrank, J. and Cheng, T., 1991;
Dumas, D. P. et al., 1990; Dumas, D. P. et al., 1989a). In another
example, the cleavage of a phosphonocyanate can be measured by the
release of a cleavage product comprising a cyanide ion (CN.sup.-)
using a cyanide selective electrode with a pH meter (Raveh, L. et
al., 1992).
[0802] In another example, cleavage of an OP substrate can be
measured, for example, by .sup.31P NMR spectroscopy. For example,
the disappearance of VX and the formation of the cleavage product
ethyl methylphosphonic acid ("EMPA"), has been measured using this
technique (Kolakowski, J. E. et al., 1997; Lai, K. et al., 1995).
In another example, the disappearance of tabun and the appearance
of the N,N-dimethylamindophosph- osphoric acid cleavage product has
been measured by .sup.31P NMR spectroscopy (Raveh, L. et al.,
1992). In a further example, the disappearance of DFP and
appearance of a F.sup.- cleavage product has been determined using
.sup.19F.sup.- and .sup.31P NMR spectroscopy (Dumas, D. P. et al.,
1989a).
[0803] The cleavage of many OP compounds' such as paraoxon,
coumaphos, cyanophos, diazinon, dursban, fensulfothion, parathion,
methyl parathion, DEPP, and various phosphodiesters, can be
determined by measuring the production of a cleavage product
spectrophotometrically at visible or UV wavelengths (Dumas, D. P.
et al., 1989b). For example, the cleavage of DEPP can be measured
at 280 nm, using a spectrophotometer to detect a phenol cleavage
product (Watkins, L. M. et al., 1997a; Hong, S.-B. and Raushel, F.
M., 1996). In a further example, various phosphodiesters (e.g.,
ethyl-4-nitrophenyl phosphate) have been made to evaluate OPH
cleavage rates, and their cleavage measured at 280 nm by the
production of a substituted phenol cleavage product (Shim, H. et
al., 1998). In a further example, paraoxon is often used as to
measure OPH activity, because it is both rapidly hydrolyzed by the
enzyme and produces a visible cleavage product. To determine
kinetic properties, the production of paraoxon's cleavage product,
p-nitrophenol, is measured with a spectrophotometer at 400 nm or
420 nm (Dumas, D. P. et al., 1990; Kuo, J. M. and Raushel, F. M.,
1994; Watkins, L. M. et al., 1997a; Gopal, S. et al., 2000). In an
additional example, NPPMP cleavage can also be measured by the
release of p-nitrophenol as a cleavage product (diSioudi, B. et
al., 1999). In a further example, chiral and non-chiral
phosphotriesters have been created to produce p-nitrophenol as a
cleavage product, and thus adapt the method used in measuring
paraoxon cleavage in determining the general binding and/or
cleavage preference of an enzyme for a phosphoryl group S.sub.p
enantiomer, R.sub.p enantiomer or non-chiral substrate
(Chen-Goodspeed, M. et al., 2001a; Chen-Goodspeed, M. et al.,
2001b; Wu, F. et al., 2000a; Steubaut, W. et al., 1975). In an
example, chiral sarin and soman analogues have been created wherein
the fluoride comprising moiety of the P--F bond has been replaced
by p-nitrophenol, allowing detection of the CWA analogs' cleavage
rates using the adapted method for paraoxon cleavage measurement
(Li, W.-S. et al., 2001).
[0804] Other techniques are known to those of skill in the art for
measuring OP detoxification activity, such as, for example,
determining the loss of acetylcholinesterase inhibitory potency of
an OP compound due to contact with an enzyme (Hoskin, F. C. G.,
1990; Luo, C. et al., 1999; Ashani, Y. et al., 1998).
[0805] General procedures for empirically determining the
purity/properties of various coating components and/or coating
compositions are known to those of ordinary skill in the art, and
may be applied in the practice of the present invention. Such
procedures include measurement of density, volume solids and/or
specific gravity, of a coating component and/or coating
composition, for purposes such as verification of component
identity, aid in coating formulation, maintaining coating batch to
batch consistency, etc. Examples of standard techniques for
determining density of various solvents, liquids (e.g., a liquid
coating), pigments, coatings (e.g., a powder coating) include those
described in "ASTM Book of Standards, Volume 06.04,
Paint--Solvents; Aromatic Hydrocarbons," D2935-96, D1555M-00,
D1555-95, and D3505-96, 2002; "ASTM Book of Standards, Volume
06.01, Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D1475-98 and D215-91, 2002; "ASTM Book of Standards,
Volume 06.03, Paint--Pigments, Drying Oils, Polymers, Resins, Naval
Stores, Cellulosic Esters, and Ink Vehicles," D153-84 and D153-84,
2002; "ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D5965-02,
2002; and "Paint and Coating Testing Manual, Fourteenth Edition of
the Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 289-304,
1995.
[0806] Standard surface specification and/or procedures for
preparing a surface (e.g., glass, wood, steel) for empirically
measuring a physical and/or visual property of a coating (e.g., a
paint, a varnish, a lacquer) and/or film are known to those of
ordinary skill in the art (see, for example, "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D3891-96, D609-00, and D2201-99,
2002; and "ASTM Book of Standards, Volume 06.02, Paint--Products
and Applications; Protective Coatings; Pipeline Coatings," D358-98,
D4227-99, and D4228-99, 2002). Specific procedures for preparing a
metal surface and an evaluating a coating (e.g., a primer, a paint)
applied to a metal surface are known to those of ordinary skill in
the art (see, for example, "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D3276-00, D5161-96, D4417-93, D3322-82, D2092-95,
D5065-01, D5723-95, D6386-99, and D6492-99, 2002). Specific
procedures for evaluating a coating applied to a plastic surface
are known to those of ordinary skill in the art (see, for example,
"ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D3002-02,
2002).
[0807] Standard procedures for determining the stability of a
coating (e.g., a water-borne coating, a UV irradiation cured
coating) in a container prior and/or after opening the container
are known to those of ordinary skill in the art (see, for example,
"ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D2243-95 and
D4144-94, 2002).
[0808] Standard procedures for evaluating an applicator (e.g., a
brush, a roller, a fabric, a spray applicator, an electrocoat bath)
and/or a coating being applied by an applicator are known to those
of ordinary skill in the art (see, for example, "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D6737-01, D5913-96,
D5959-96, D5301-92, D5068-02, D5069-92, D4707-97, D5286-01,
D6337-98, D4285-83, and D5327-97, 2002; and "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D1978-91, D5794-95, D4370-01,
D4399-90, and D4584-86, 2002.
[0809] Standard procedures for preparing a coating (e.g., a paint,
a varnish, a lacquer) and/or film layer upon a surface for
empirically measuring a physical and/or visual property are known
to those of ordinary skill in the art (see, for example, "ASTM Book
of Standards, Volume 06.01, Paint--Tests for Chemical, Physical,
and Optical Properties; Appearance," D3924-80, D823-95, and
D4708-99, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D6206-97, D1734-93, and D4400-99, 2002; and "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 415-423, 1995.
[0810] Standard procedures. for empirically determining the degree
and duration of film formation of various coating compositions are
known to those of ordinary skill in the art, and may be applied in
the practice of the present invention. Example of a standard
technique for determining the degree/duration of film formation by
loss of a volatile coating component and/or a cross-linking
reaction for a coating (e.g., an oil-coating, a UV cured coating,
an thermosetting powder coating) include those described in "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D3539-87, D1640-95
and D5895-01e1, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D4217-02, D3732-82, D2091-96, D711-89, D4752-98, and
D5909-96a, 2002; "ASTM Book of Standards, Volume 06.03,
Paint--Pigments, Drying Oils, Polymers, Resins, Naval Stores,
Cellulosic Esters, and Ink Vehicles," D2575-70 and D2354-98, 2002;
and "Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 407-414, 1995.
Additionally, the temperature generated by a film formation
reaction by a coating (e.g., a wood coating) may also be determined
by one of ordinary skill in the art (see, for example, "ASTM Book
of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D3259-95, 2002). Further,
standard techniques for evaluating baking conditions on an organic
coating and/or film are known to those of ordinary skill in the
art, (see, for example, "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2454-95, 2002).
[0811] In embodiments wherein film formation at room temperature is
preferred in a coating, a standard procedure that would be known to
one of ordinary skill in that art may be used for measuring film
formation rate and/or stages (see for example, "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D1640-95, 2002. In certain aspects
wherein the ability of an oil to undergo film formation is to be
determined, a standard procedure described in "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D1955-85, 2002, may be used. In embodiments wherein the hardness of
a film produced by a coating composition is measured (e.g., an
organic coating), a standard procedure such as, for example, "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D3363-00, D4366-95,
and D1474-98, 2002.
[0812] Examples of a standard technique for determining the coating
and/or film thickness after application to various surface types
are described in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D1212-91, D4414-95, D1005-95, D1400-00, D1186-01, and
D6132-97, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D5235-97, D4138-94, D2200-95, and D5796-99, 2002; and
"Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 424-438,
1995.
[0813] Examples of a standard technique for determining the
adhesion of a coating and/or film to various surface types are
described in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
D3359-02, D5179-98, and D2197-98, 2002; "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D4541-02 D3730-98, D4145-83,
D4146-96, and D6677-01, 2002; and "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 513-524, 1995. Additionally, standard
procedures for determining the ability of one or more layers of a
multicoat system to function (e.g., adhere, weather) together are
described in, for example, "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D5064-01, 2002.
[0814] Various standard techniques for determining the physical
properties (e.g., flexibility, tensile strength, toughness, impact
resistance, hardness, mar resistance, blocking resistance) relevant
to the durability of a film and/or the degree of film formation are
known to those of ordinary skill in the art. Such procedures may be
used to empirically characterize a film, and determine whether a
coating composition produces a film suitable for a given
application. Flexibility is the film's ability to undergo stress
from bending and/or flexing without discernable damage (e.g.,
cracking). Examples of a standard technique for determining the
flexibility of a film under mechanical or temperature stress are
described in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
D522-93a and D4145-83, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D4145-83, D4146-96, and D1211-97, 2002; and "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 547-554, 1995. Related to
flexibility is the tensile strength of a film, which is the ability
of a film to undergo tensile deformation without developing
discernable damage (e.g., cracking, tearing). Examples of a
standard technique for determining the tensile strength of a film
are described in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2370-98 and D522-93a, 2002; and "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 534-545, 1995. Toughness is the film's
ability to undergo strain imposed in a short period of time (e.g.,
one second or less) without discernable damage (e.g., breaking,
tearing). Examples of a standard technique for determining the
toughness of a film (e.g., a film for a pipeline) are described in
"ASTM Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D2794-93, 2002;
"ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," G14-88,
2002; and "Paint and Coating Testing Manual, Fourteenth Edition of
the Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 547-554,
1995. Impact resistance is the ability of a film to undergo impact
with an indenter without developing discernable damage at the
dimple site (e.g., cracking). Examples of a standard technique for
determining the impact resistance of a film (e.g., a film for a
pipeline) are described in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2794-93, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," G13-89 and G14-88, 2002; and "Paint and Coating Testing
Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 553-554, 1995. Hardness is the film's
ability to undergo an applied static force without developing
discernable damage (e.g., a scratch, an indentation). Examples of a
standard technique for determining the hardness of a film are
described in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearancei"
D1640-95, D1474-98, D2134-93, D4366-95, and D3363-00, 2002; and
"Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp. 555-584, 1995.
Mar resistance ("mar abrasion resistance") is the film's ability to
undergo an applied dynamic force without developing a change in the
film surface appearance (e.g., gloss) due to a permanent
deformation (e.g., an indentation). Examples of a standard
technique for determining the mar resistance of a film are
described in "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
D5178-98 and D6037-96, 2002; and "Paint and Coating Testing Manual,
Fourteenth Edition of the Gardner-Sward Handbook," (Koleske, J. V.
Ed.), pp. 525-533 and 579-584, 1995. Abrasion resistance ("wear
abrasion resistance") is the film's ability to undergo an applied
dynamic force (e.g., washing) without removal of film material.
Examples of a standard technique for determining the abrasion
resistance (e.g., burnish resistance) of a film are described in
"ASTM Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D968-93 and
D4060-01, 2002; "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D3170-01, D4213-96, D5181-91, D4828-94, D2486-00,
D3450-00, D6736-01, and D6279-99e1, 2002; and "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 525-533, 1995. Blocking resistance
("block resistance") is the ability of a film to resist adhering to
a second film, particularly when the two films are pressed together
(e.g., a coated door and coated doorframe). Examples of a standard
technique for determining the blocking resistance of a film are
described in "ASTM Book of Standards, Volume 06.02, Paint--Products
and Applications; Protective Coatings; Pipeline Coatings," D2793-99
and D3003-01, 2002. Abrasion resistance ("wear abrasion
resistance") is the film's ability to undergo an applied dynamic
force (e.g., washing) without removal of film material. Slip
resistance is a coating's (e.g., a floor coating) slipperiness, and
can be evaluated as described in "Paint and Coating Testing Manual,
Fourteenth Edition of the Gardner-Sward Handbook," (Koleske, J. V.
Ed.), pp. 600-606, 1995.
[0815] Weathering resistance is film's ability to endure and/or
protect a surface from an external environmental condition.
Examples of environmental conditions that may damage a film and/or
surface include contact with varying conditions of temperature,
moisture, sunlight (e.g., UV resistance), pollution, biological
organisms, or a combination thereof. Examples of a standard
technique for determining the weathering resistance of a film
(e.g., an automotive film, an external architectural film, a
varnish, a wood coating, a steel coating) by evaluating the degree
of damage (e.g., fungal growth, color alteration, dirt
accumulation, gloss loss, chalking, cracking, blistering, flaking,
erosion, surface rust), are described in "ASTM Book of Standards,
Volume 06.01, Paint--Tests for Chemical, Physical, and Optical
Properties; Appearance," D4141-01, D1729-96, D660-93, D661-93,
D662-93, D772-86, D4214-98, D3274-95, D714-02, D1654-92, D2244-02,
D523-89, D1006-01, D1014-95, and D1186-01, 2002; "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D3719-00, D610-01,
D1641-97, D2830-96, and D6763-02, 2002; and "Paint and Coating
Testing Manual, Fourteenth Edition of the Gardner-Sward Handbook,"
(Koleske, J. V. Ed.), pp. 619-642, 1995. Additionally, standard
techniques are known to those of ordinary skill in the art for
determining the resistance of a film to artificial weathering
conditions. These procedures are used to contact a film with a
simulated weathering condition (e.g., heat, moisture, light, UV
irradiation) at an accelerated timetable are described in "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D822-01, D4587-01,
D5031-01, D6631-01, D6695-01, D5894-96, and D4141-01, 2002; "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D5722-95, D3361-01 and
D3424-01, 2002; and "Paint and Coating Testing Manual, Fourteenth
Edition of the Gardner-Sward Handbook" (Koleske, J. V. Ed.), pp.
643-653, 1995.
[0816] Standard techniques for determining a film's resistance to
damage by various chemicals are known to those of ordinary skill in
the art. Examples of chemicals that can be used in such procedures
include an acid (e.g., 3% acetic acid), a base, an alcohol (e.g.,
50% ethyl alcohol, hydrochloric acid, sulfuric acid), a detergent
(e.g., a sodium phosphate solution), gasoline, a glycol based
antifreeze, an oil (e.g., a vegetable oil, a lubricating petroleum
oil, a grease), a solvent, water (e.g., a salt solution, a salt
vapor), a polish abrasive, another coating (e.g., graffiti), or a
combination thereof. Standard techniques for determining the
chemical resistance of a film (e.g., an architectural film, an
automotive film, a paint, a lacquer, a varnish, a traffic-coating,
a metal surface-film) by evaluating possible damage (e.g., adhesion
loss, alteration of gloss, blistering, discoloration, loss of
hardness, staining, swelling, wrinkling) are described in, for
example, "ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings," D1308-02,
D2571-95, D2792-69, D4752-98, D3260-01, D6137-97, D6686-01,
D6688-01, and D6578-00, 2002; "ASTM Book of Standards, Volume
06.01, Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D2370-98, D2248-01a, and D870-02, 2002; "ASTM Book of
Standards, Volume 06.03, Paint--Pigments, Drying Oils, Polymers,
Resins, Naval Stores, Cellulosic Esters, and Ink Vehicles,"
D1647-89, 2002; and "Paint and Coating Testing Manual, Fourteenth
Edition of the Gardner-Sward Handbook," (Koleske, J. V. Ed.), pp.
662-666, 1995. Additionally, examples of a standard technique for
determining the solvent resistance of a film are described in "ASTM
Book of Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D4752-98 and D5402-93,
2002.
[0817] Standard techniques for determining a film's and/or
surface's (e.g., metal, wood) resistance to water permeability
and/or damage (e.g., corrosion, blistering, adhesion reduction,
hardness alteration, color alteration, gloss alteration) by contact
with water and/or moisture are described in, for example, "ASTM
Book of Standards, Volume 06.01, Paint--Tests for Chemical,
Physical, and Optical Properties; Appearance," D870-02, D1653-93,
D1735-02, D2247-02, and D4585-99, 2002; and "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D2065-96, D2921-98,
D3459-98, and D6665-01, 2002.
[0818] Standard techniques for determining a film's resistance to
damage by a temperature greater than ambient condition are known to
those of ordinary skill in the art. Thermal resistance is the
film's ability to undergo stress from a temperature at or below
200.degree. C. without discernable damage, while heat resistance is
the film's ability to undergo stress from a temperature above
200.degree. C. (e.g., fire resistance, fire retardancy, flame
resistance) without discernable damage. Standard techniques for
determining the thermal and/or heat resistance of a film (e.g., a
metal-film, a wood-lacquer) by evaluating possible damage (e.g.,
adhesion loss, alteration of gloss, blistering, chalking,
discoloration) are described in, for example, "ASTM Book of
Standards, Volume 06.01, Paint Tests for Chemical, Physical, and
Optical Properties; Appearance," D2370-98, D2485-91, D1360-98,
D4206-96, and D3806-98, 2002; and "ASTM Book of Standards, Volume
06.02, Paint--Products and Applications; Protective Coatings;
Pipeline Coatings," D1211-97 and D6491-99, 2002.
[0819] In some embodiments, it may be desirable to measure the
component composition of a coating and/or film such as to verify
the presence, absence and/or amount of one or more coating
components in a particular formulation. Standard procedures for
sampling a coating and/or film, and analyzing the material
composition (e.g., a pigment, a binder, liquid component, toxic
material), have been described in, for example, "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D2371-85, D5380-93, D2372-85,
D2698-90, D3723-84, D4451-02, D4563-02, D5145-90, D3925-02,
D2348-02, D2245-90, D3624-85a, D3717-85a, D2349-90, D2350-90,
D2351-90, D2352-85, D3271-87, D3272-76, D4017-02, D3792-99,
D4457-02, D6133-00, D6191-97, D4764-01, D3718-85a, D3335-85a,
D6580-00, E848-94, D4834-88, D4358-84, D2621-87, D3618-85a,
D6438-99, D4359-90, D3168-85, and D4948-89, 2002; "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D5702-02, 2002; and "ASTM
Book of Standards, Volume 06.03, Paint--Pigments, Drying Oils,
Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D1469-00, 2002.
[0820] The nonvolatile content of a coating component and/or
coating ("total solids content") can provide an estimate, for
example, of the volume of film that will be produced by a coating
or coating component (e.g., a paint, a clear coating, an
electrocoat bath applied coating, a binder solution, an emulsion, a
varnish, an oil, a drier, a solvent) and/or the surface area a
coating can cover relative to a film's thickness. The nonvolatile
content of coating and/or coating component can be determined by
any technique known in the art (see, for example, "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D6093-97, D2697-86, D1259-85,
D1644-01, D2832-92, and D4209-82 D5145-90, 2002; "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D4713-92, D5095-91, 2002;
and "ASTM Book of Standards, Volume 06.03, Paint--Pigments, Drying
Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and Ink
Vehicles," D4139-82, 2002. Additionally, the volatile component of
a coating can provide an estimate, for example, of VOC release
and/or thermoplastic film formation time. The nonvolatile content
of coating and/or coating component (e.g., a paint, a clear
coating, an automotive coating, an emulsion, a binder solution, a
varnish, an oil, a drier, a solvent) can be determined by any
technique known in the art (see, for example, "ASTM Book of
Standards, Volume 06.01, Paint--Tests for Chemical, Physical, and
Optical Properties; Appearance," D2369-01e1, D2832-92, D3960-02,
D4140-82, D4209-82, D5087-02 and D6266-00a, 2002; and "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D5403-93, 2002.
[0821] Standard procedures for determining the visual appearance of
a coating component, coating and or film (e.g., reflectance,
retroreflectance, fluorescence, photoluminescent light
transmission, color, tinting strength, whiteness, measurement
instruments, computerized data analysis) have been described, for
example, in "ASTM Book of Standards, Volume 06.01, Paint--Tests for
Chemical, Physical, and Optical Properties; Appearance," E284-02b,
E312-02, E805-01a, E179-96, E991-98, E1247-92, E308-01, E313-00,
E808-01, E1336-96, E1341-96, E1347-97, E1360-90, D332-87, D387-00,
E1455-97, E1477-98a, E1478-97 E1164-2, E1331-96, E1345-98,
E1348-02, E1349-90, D5531-94, D3964-80, E1651-94, E1682-96,
E1708-95, E1767-95, E1808-96, E1809-01, E2022-01, E2072-00,
E2073-02, E2152-01, E2153-01, D1544-98, E259-98, D3022-84,
D1535-01, E2175-01, E2214-02, and E2222-02, 2002; "ASTM Book of
Standards, Volume 06.02, Paint--Products and Applications;
Protective Coatings; Pipeline Coatings," D4838-88 and D5326-94a,
2002; and "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles," D2090-98, D2090-98 and D6166-97, 2002. Specific
techniques for matching two or more colored coatings and/coating
components to minimalize differences (e.g., metamerism) have been
described, for example, in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," D4086-92a, E1541-98 D2244-022002. Specific techniques
for determining differences in the color of a coatings and/coating
components, particularly to insure color consistency of a coating
composition, "ASTM Book of Standards, Volume 06.01, Paint--Tests
for Chemical, Physical, and Optical Properties; Appearance,"
D1729-96, D2616-96, E1499-97, and D3134-97, 2002.
[0822] Gloss is the film's "angular selectivity of reflectance,
involving surface-reflected light, responsible for the degree to
which reflected highlights or images of objects may be seen as
superimposed on a surface" ("ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," E284-02b, 2002). An example of a high gloss coating
would be a paint film with a glass-like surface apparance, as
opposed to a low-gloss ("flat") paint. Standard techniques for
determining the gloss (e.g., specular gloss, sheen, haze, image
clarity, waviness, directionality) of a coating and/or film are
described, for example, in "ASTM Book of Standards, Volume 06.01,
Paint--Tests for Chemical, Physical, and Optical Properties;
Appearance," E284-02b, D523-89, D4449-90, E167-96, E430-97,
D4039-93, D5767-95, and D2244-02, 2002; "ASTM Book of Standards,
Volume 06.02, Paint--Products and Applications; Protective
Coatings; Pipeline Coatings," D3928-00a, 2002; and "Paint and
Coating Testing Manual, Fourteenth Edition of the Gardner-Sward
Handbook," (Koleske, J. V. Ed.), pp. 470-480, 1995.
[0823] 7. Preferred Use of the Invention
[0824] In certain embodiments, the compositions and methods of the
present invention have use in three primary markets that will
benefit from a susceptible surface covered with a
self-decontaminating coating: domestic military, friendly foreign
military/civilian, and domestic civilian. It is contemplated that
for military use, a self-decontaminating coating has utility on a
surface of a vehicle, a trailer, a barrack, a decontamination
shelter, a piece of equipment (e.g., a piece of electronic
equipment) or a combination thereof.
[0825] It is further contemplated that a biomolecular composition
of the present invention may have dual military and/or civilian use
in a method for facilitating the disposal of a chemical waste,
including but not limited to, a CWA, a pesticide or a combination
thereof. A particular dual use embodiment of the present invention
includes coating a surface that may be in a facility where there
would be an unexceptable delay to the use of a piece of equipment,
a space (e.g., a room, a command center, a computer center), a
vehicle (e.g., a public transportation vehicle, an emergency
vehicle) or a combination thereof if the facility was subjected to
or suspected of exposure to, a dangerous chemical (e.g., a nerve
agent). In some aspects, the piece of equipment, the space, and/or
the vehicle may be used by a military personnel, an emergency
personel or a combination thereof. In specific facets, the piece of
equipment, the space, and/or the vehicle is a critical piece of
equipment, space and/or vehicle. It is contemplated that such a
facility may be contacted with a chemical from a chemical weapon
attack (e.g., a CWA gas attack), an accidental release of a
chemical, or a combination thereof. Examples of such facilities
include a control room at a military base, an airport, a nuclear
power plant, a hospital, or a combination thereof. It is an aspect
of the disclosure that a facility (i.e., a space, a vehicle, a
piece of equipment) that may be subject to exposure to a chemical
(e.g., a nerve agent) may be coated with the disclosed compositions
and would then be detoxified and safe after contact with the
chemical.
[0826] Civilian applications contemplated include a coating of a
surface in contact with air, such as for example, a ventilation
intake or an air filter, as well as a surface (e.g., an interior
surface, an exterior surface) comprised in a hospital clean room, a
community safe room, a control room for a nuclear plant, a control
room for a chemical plant, a control room for a power plant, a
control room for a water plant, a government building, an
industrial building, a facility for public transportation (e.g., a
train, a subway, a plane, an airport), and a surface of an
equipment by a first responder, or any combination of the
forgoing.
[0827] It is contemplated that for each formulation of a coating
and a biomolecular composition of the present invention, enzymatic
decontamination parameters based on chemical (e.g., CWA simulant)
degradation assessment will be established in a range of exterior
weathering conditions. If a specific formulation of enzyme
composition in a coating remains active after exposure to exterior
weathering conditions, there is a significant utility for using the
bioactive painted surfaces in exterior and field application. For
example, it is contemplated that a biomolecular composition of the
present invention incorporated in standard formulations of
water-based or latex-based paint will result in minimal to no
changes in the durability of the paint based on standard exterior
weathering conditions. In a general aspect of the present
invention, a weathering study may indicate a need to reformulate a
composition to improve a particular property (e.g., enhance
biomolecular composition stability). In this aspect, it is
contemplated that standard methods, known to those of skill in the
art (e.g., encapsulation), may be used to increase stability and
re-test the resulting formulation. Application of such methods can
be used to modify various formulations to produce a composition
with one or more properties optimized to a particular application,
as described herein and as would be know to one of ordinary skill
in the art in light of the present disclosures.
[0828] 8. Combinations of Decontamination Compositions and
Methods
[0829] In certain embodiments, a composition or method of the
present invention may be combined with another composition method
for decontamination (e.g., detoxification, degradation) of a
chemical. In preferred aspects, the additional composition or
method comprises one for decontamination of a pesticide or chemical
warfare agent. Such additional compositions and methods are known
in the art (Yang, Y. C. et al., 1992), and may be applied prior,
during and/or after application of a composition and/or method of
the present invention. In particularly preferred embodiments, such
a combination of a composition and/or method disclosed herein with
a traditional composition and/or method produces greater
decontamination than that achieved without such a combination.
[0830] Additional compositions that are contemplated include, but
are not limited to, a caustic agent; a decontaminating foam (e.g.,
Sandia, Decon Green); an application of intensive heat and carbon
dioxide for a sustained period; an incorporation of a material into
a coating that, when exposed to sustained high levels of UV light,
degrades a chemical; a chemical agent resistant coating; or a
combination thereof. Examples of a caustic agent include, a
bleaching agent, DS2, or a combination thereof.
[0831] As used herein, a "caustic agent" is a composition capable
of destroying usually via a chemical reaction, a material,
unfortunately including animal tissue such as skin. Thus,
application of a caustic agent is often accompanied by the wearing
of protective gear for those not contaminated or suspected of being
contaminated, as would be understood by those of ordinary skill in
the art. Certain caustic agents, such as for example, a bleaching
agent or decontamination solution 2 ("DS2"), have specifically been
formulated and/or used to decontaminate chemical warfare agents.
Both G agents and VX can be decontaminated with these caustic
agents. As used herein, a "bleaching agent" refers to a reactive
chemical compound capable breaking a double bond in another
chemical compound, which is often a useful property for degrading a
toxic or otherwise undesirable chemical. Examples of a bleaching
agent include a bleach powder, a bleach solution, or a combination
thereof. A bleach powder may comprise, but is not limited to,
Ca(OCl)Cl and Ca(OCl).sub.2 ("high test hypochlorite," "HTH");
Ca(OCl).sub.2 and CaO ("super tropical bleach," "STB");
Ca(OCl).sub.2 and MgO ("Dutch powder"); or a combination thereof. A
bleach solution may comprise, but is not limited to, NaOCl
("bleach"), usually 2% to 6% wt in water; a HTH slurry, usually 7%
HTH wt in water; a STB slurry, usually 7% to 70% wt in water;
activated solution of hypochlorite ("ASH"), usually 0.5%
Ca(OCl).sub.2 and 0.5% sodium dihydrogen phosphate buffer and 0.05%
detergent in water; self-limited activated solution of hypochlorite
("SLASH"), usually 0.5% Ca(OCl).sub.2 and 1.0% sodium citrate and
0.2% citrate acid and 0.05% detergent in water; or a combination
thereof. Bleach, Dutch powder, ASH and SLASH are generally applied
to skin and equipment for decontamination, while HTH and STB are
generally applied to equipment and terrain for decontamination. VX
is preferably decontaminated at an acid pH, wherein it is more
soluble (Yang, Y. C. et al., 1992).
[0832] DS2 was developed to function at various temperatures (i.e.,
-25.degree. C. to 52.degree. C.), particularly those below the
freezing point of most aqueous compositions. It usually comprises
70% diethylenetriamine
(H.sub.2NCH.sub.2CH.sub.2NHCH.sub.2CH.sub.2NH.sub.2), 28% ethylene
glycol monomethyl ether (CH.sub.3OCH.sub.2CH.sub.2OH), and 2%
sodium hydroxide (NaOH). DS2 is noncorrosive to many metals, but is
damaging to many paints, leathers, rubber materials, plastics and
skin. Contact with a paint is generally limited to 30 minutes or
less. An aqueous rinse is generally used to remove DS2, and
exposure to air and/or water degrades DS2 (Yang, Y. C. et al.,
1992).
[0833] Various other decontamination compositions and methods are
known to those of skill in the art. Examples of a decontaminating
foam include Sandia, Decon Green, or a combination thereof.
Examples of an incorporation of a material include incorporation of
TiO.sub.2 and porphyrins into acetonitrile coatings that, when
exposed to a sustained high level of UV light in an oxygen
environment (e.g., air), degrade a chemical agent (e.g., mustard).
Addition of water to the acetonitrile coating comprising TiO.sub.2
and porphyrins will aid the degradation of VX to non-toxic
compounds (Buchanan, J. H. et al., 1989; Fox, M. A., 1983).
Additionally, CARCs have been developed to withstand repeated
decontamination efforts.
[0834] Decontamination compositions are often prepared and packaged
in equipment for easy of handling. Such an equipment packages
include, but are not limited to, kits (e.g., a towelette package)
and delivery apparatus (e.g., a sprayer). Examples of specific
decontamination equipment packages that may be used in combination
with a composition or method of the present invention include a
ABC-M11 portable decontamination apparatus, which comprises DS2, a
devise for spraying DS2, and a vehicle mounting bracket; a
ABC-M12A1 power-driven, skid-mounted decontamination apparatus,
which comprises a personnel shower unit, a pump, a tank, a M2 water
heater, and delivers water, foam, DS2, STB, and/or deicing liquid;
a M258A1 personal decontamination kit, which comprises towelettes
soaked with a decontamination solution (i.e., 72% ethanol, 10%
phenol, 5% NaOH, 0.2% ammonia, and 12% water), ampules of a
decontaminating solution (5% ZnCl.sub.2, 45% ethanol, 50% water)
for adding to a towlette soaked with chloramines-B
(PhS(O).sub.2NClNa), packing foil, and a plastic carrying case; a
M280 individual equipment decontamination kit, which comprises
twenty fold the contents of the M258A1 kit; a M291 skin
decontamination kit, which comprises six XE-555 resin (i.e.,
styrene/divinyl benzene copolymer, a strong acid cation-exchange
resin and a strong base anion-exchange resin for absorption and
chemical detoxification) filled fiber pads packaged in foil; a M13
portable decontamination apparatus, which comprises DS2, a
container and an equipment/vehicle mount, and is capable of
dispensing DS2; a M17 lightweight, transportable decontamination
apparatus, which comprises hoses, cleaning jets, personnel showers,
a collapsible rubberized fabric tank, and is capable of dispensing
water; or a combination thereof. The ABC-M11, M13 and M280
decontamination equipment packages are generally used for equipment
(e.g., vehicles), the M258A1 and M17 decontamination equipment
packages are generally used for equipment and/or personnel, and the
ABC-M12A1 and M291 decontamination equipment packages are generally
used for personnel (Yang, Y. C. et al., 1992).
[0835] 9. Removing a Coating or Film
[0836] In certain embodiments, it may be desirable to remove a
coating and/or film from a surface such as a non-film forming
coating, a temporary film, a self-cleaning film, a coating and/or
film that has been damaged, contaminated with an OP compound, or is
otherwise no longer desired or no longer is suitable for use.
Various coating removers (e.g., a paint remover) are known to those
of ordinary skill in the art, and often comprise solvents described
herein capable of dissolving a coating component (e.g., a binder)
integral to a film's structural integrity. Standard procedures for
determining the effectiveness of a coating remover have been
described, for example, in "ASTM Book of Standards, Volume 06.02,
Paint--Products and Applications; Protective Coatings; Pipeline
Coatings," D6189-97, 2002.
EXAMPLE 1
Assay for Active Phosphoric Triester Hydrolase Expression in
Cells
[0837] Routine analysis of parathion hydrolysis in whole cells is
accomplished by suspending cultures in 10 milli-Molar ("mM") Tris
hydrocholoride at pH 8.0 comprising 1.0 mM sodium EDTA ("TE
buffer"). Cell-free extracts are assayed using sonicated extracts
in 0.5 milliLiters ("ml") of TE buffer. The suspended cells or cell
extracts are incubated with 10 microLiters (".mu.l") of substrate,
specifically 100 .mu.g of parathion in 10% methanol, and
p-nitrophenol production is monitored at a wavelength of 400 nm. To
induce the opd gene under lac control, 1.0 .mu.mol of
isopropyl-.beta.-D-thiogalactopyranoside (Sigma) per ml is added to
the culture media.
EXAMPLE 2
Preparation of Enzyme Powder
[0838] In a typical preparation, a single colony of bacteria that
expresses the opd gene is selected and cultured in a rich media.
After growth to saturation, the cells are concentrated by
centrifugation at 7000 rotations per minute ("rpm") for 10 minutes
for example. The cell pellet is then resuspended in a volatile
organic solvent such as acetone one or two times in order to
dessicate the cells and to remove a substantial portion of the
water contained in the cell pellet. The pellet may then be ground
or milled to a powder form. The powder may be frozen or stored at
ambient conditions for future use, or may be added immediately to a
surface coating formulation. Additionally, the powder may be freeze
dried, combined with a cryoprotectant (e.g., cryopreservative), or
a combination thereof.
EXAMPLE 3
Two-Pack OPH Paint Coating: OPH Powder and Latex Paint
[0839] In an example of use of the powder prepared as described in
Example 2, 3 mg of the milled powder was added to 3 ml of 50%
glycerol. The suspension was then added to 100 ml of Olympic.RTM.
premium interior flat latex paint (Olympic.RTM., One PPG Place,
Pittsburg, Pa. 15272 USA). This paint with biomolecular composition
was then used to demonstrate the activity of the paint biomolecular
composition in hydrolysis of a pesticide or a nerve agent
analog.
EXAMPLE 4
Application of OPH Paint to a Surface
[0840] In a first set of assays, a paint product as prepared in
Example 3 was applied to a hard, metal surface. The surface used in
the present example was a non-galvanized steel surface that was
cleaned through being degreased, and pretested with a primer coat.
A control surface was painted with the identical paint with no
biomolecular composition. Paraoxon, an organophosphorus nerve gas
analog was used as an indicator of enzyme activity. Paraoxon, which
is colorless, is degraded to form p-nitrophenol, which is yellow in
color, plus diethyl phosphate, thus giving a visual indication of
enzyme activity. In multiple assays, the surface with control paint
remained white, indicating no production of p-nitrophenol, and the
surface painted with the paint and biomolecular composition turned
yellow within minutes, indicating an active OPH enzyme in the
paint. This demonstration has shown that the surface remains active
for more than 65 days, which was the maximum duration of the
protocol.
[0841] In a further demonstration, the surfaces were treated as
described above and each surface was then treated with paraoxon, an
OP insecticide. Approximately 100 flies were then placed on each
surface under a plastic cover. In each procedure, within three
hours, virtually all the flies on the control surface with no paint
biomolecular composition were killed by the paraoxon. In contrast,
only approximately 5% of the flies on the enzyme comprising surface
had died.
[0842] In a demonstration of enzyme stability in the paint, a
series of wood dowels were dipped into the paint with OPH enzyme
composition. The dowels were then placed in tubes containing
paraoxon to indicate enzyme activity as described above. In each
case, a positive yellow color was seen except in those dowels
painted with no biomolecular composition as controls. The control
solution remained clear in every case.
[0843] In order to demonstrate the shelf life of both the dry
biomolecular composition and the paint with biomolecular
composition, the biomolecular composition was aged from 0 to 20
days prior to mixing in the paint. The mixed paint and biomolecular
composition was then also aged from 0 to 20 prior to painting
individual dowels. The enzyme composition retained strong activity
after 20 days aging prior to being mixed in the paint, and for 20
days after mixing the maximum time used in the assay.
EXAMPLE 5
Buffered Enzyme Paint
[0844] As the hydrolysis reaction that degrades nerve agents
proceeds, the local pH decreases. Without limiting the invention to
any particular mechanism, it is contemplated that due to the law of
mass action, or to the optimum pH of the enzyme, the reaction is
slower as the pH decreases. Because this effect could prevent or
inhibit some surfaces from becoming completely decontaminated,
active paint formulations have been prepared that include one or
more buffering agents.
[0845] In initial procedures, the following compositions were used:
10 mg enzyme powder as described in Example 2,100 .mu.l 0.1 M
buffer, 800 .mu.l H.sub.2O, and 100 .mu.l paraoxon for a 1000 .mu.l
reaction volume.
[0846] Reactions were run for 1.5 to 2 hours and both pH and
product concentration were measured. The concentration of product
(p-nitrophenol) is measured by absorbance at 400 nm.
[0847] Ammonium bicarbonate, both monobasic and dibasic phosphate
buffers, Trizma base and five zwitterionic buffers have been used
in the active paint compositions. All the buffers were effective at
allowing the reaction to proceed further to completion, thus
demonstrating the advantage of addition of a buffering agent to the
active paint compositions.
EXAMPLE 6
NATO Demonstration of Soman Detoxification Using OPH-Painted
Surfaces
[0848] At the Sep. 22, 2002, meeting of the NATO Army Armaments
Group in Cazaux, France, painted metal surfaces were assayed with
soman using standard NATO procedures and protocols. For the assays,
10 cm.times.10 cm metal plates primed with standard NATO
specification paints were coated with paint containing OPH. Control
plates plus two different versions of the OPH enzyme composition
differing in soman detoxification specificity were used. These
surfaces were allowed to dry for several hours at room temperature
and then assayed according to standard NATO assay protocol
(described below), modified to account for the unique character of
the surfaces treated with a paint comprising OPH.
[0849] The form of OPH in the biomolecular composition contains
both the changes of the previously described H254R mutant and the
H257L mutant, and is corresponding designated the "H254R, H257L
mutant." The H254R, H257L mutant demonstrates a several-fold
enhanced rates of R-VX catalysis relative to either the H254R
mutant or the H257L mutant, and a 20-fold enhancement of activity
relative to wild-type OPH. This version of the OPH biomolecular
composition has been assayed in paints treated with soman or R-VX,
and are described below.
[0850] Following standard protocols, OPD painted surfaces were
uniformly contaminated with an isopropanol solution containing the
chemical warfare agent soman. The concentration of soman on each
contaminated surface was 1.0 mg/cm.sup.2. The contaminated plates
were maintained at or slightly above room temperature
(.gtoreq.20.degree. C.) without any forced air-flow for various
periods of time. A zero-time, 15 minutes, 30 minutes, and 45
minutes sample was taken for each control and biomolecular
composition-containing plate series. In order to terminate the
reaction and isolate residual soman on the plate surface, each
plate was submerged in a container of isopropanol at the end-point
and placed on a shaker to thoroughly extract any residual nerve
agent. The solubilized portions were then quantified for soman.
These assays showed that both the forms of OPH biomolecular
composition were highly effective in detoxifying soman on metal
surfaces. The two different OPH biomolecular compositions assayed
detoxified the soman at levels over 65% and 77% after 45 minutes
(Nato Army Armaments Group Project Group 31 on Non-Corrosive,
Biotechnology-Based Decontaminants for CBW Agents, 2002).
Additional assays with a CWA simulant indicated that had the NATO
assay run for one to two hours, substantially all of the soman
would have been detoxified.
EXAMPLE 7
Aberdeen Proving Ground
[0851] A demonstration of an OPH biomolecular composition has been
conducted at SBCCOM in Aberdeen, Md. In these assays, a primed
wooden stick was coated with paint containing OPH biomolecular
composition. The painted sticks used were 2 milimeter ("mm") in
diameter.times.15 mm in length. By estimating that the paint layer
was 0.25 mm thick, the resulting surface area was approximately 125
mm.sup.2. After coating the stick with paint containing OPH
biomolecular composition and allowing the paint to dry, the coated
stick was inserted into a microfuge tube containing 100 .mu.l of
3.24 mM Russian-VX agent in saline and 900 .mu.l phosphate buffer
at pH 8.3. The tubes containing R-VX and the painted sticks were
allowed to sit overnight in a hood at room temperature. Appropriate
controls were run simultaneously.
[0852] The following morning, the contents of the microfuge tubes
were assayed for free thiols by the Ellman method. 10 mM DTNB
[molecular weight ("MW") 396.3] was prepared in 10 mM phosphate
buffer at pH 8.0 for use as the indicator of enzyme activity. OPH
paint's cleavage of R-VX releases a free thiol that reacts with
DNTP to produce a colored product detectable spectrophotometrically
at 405 nm. Ten .mu.l of the microfuge tube contents, 100 .mu.l DTNB
solution and 890 .mu.l phosphate buffer at pH 8.3 were read for
thiol release at 405 nm using a Varian Carey 300 Spectrophotometer.
The spectrophotometer was blanked with an unpainted stick control
reaction. The molar equivalent of the R-VX hydrolyzed was
determined using an extinction coefficient of 14,150 and the
Beer-Lambert equation to calculate the product concentration.
Results indicated that overnight exposure to OPH paint coated
sticks resulted in decontamination of Russian VX from 32.4 .mu.M in
the original tube to less than 1 .mu.M.
EXAMPLE 8
NATO Protocols for Organophosphorus CWA Decontamination
[0853] This example describes a method for determining the
decontamination properties of a coating, specifically paint,
comprising an phosphoric triester hydrolase biomolecular
composition of the present invention. NATO assay requirements will
be followed as closely as possible. Although actual assaying
protocols among NATO countries vary somewhat, standard to all is
the level of contamination. For exterior surfaces it is 10 grams
per meter squared ("g/m.sup.2"). For interiors it is 1 g/m.sup.2.
Basic elements of NATO assaying procedures are as follows:
[0854] A. Coated Surface
[0855] A 10.times.10 cm metal plate coated with a coating that may
comprise a biomolecular composition of the present invention.
[0856] B. Contamination
[0857] Usually achieved with a multi-channel micropipette that can
dispense 1 .mu.l drops, with 100 drops per 10.times.10 cm metal
plate.
[0858] C. Incubation
[0859] The plates will be placed into a sealed incubator, at
25.degree. C. or 30.degree. C., for a period ranging from 30
minutes to 3 hours.
[0860] D. Decontamination
[0861] The decontamination protocol varies according to the system
being assayed. For example, spraying of decontamination solutions
will last between 5 seconds to 20 seconds, depending on the
pressure of the system.
[0862] E. Sampling
[0863] For standard solution-based decontamination, the assays will
be normally prepared in a way that run-off decontaminant will be
collected after it comes in contact with the plates and the CWA
agent or CWA simulant. A set of plates will be removed for analysis
at intervals, with the most common being 15 minutes and 30 minutes.
Any residual liquid on the plates will be added to the run-off. For
enzyme biomolecular composition assays, the plates will be not
rinsed after decontamination, although the rinse is standard with
other decontaminants. This rinsate would also be collected for
analysis. A set of plates without decontamination will be used as 0
minute, 15 minute, and 30 minute controls.
[0864] F. Analysis
[0865] The run-off liquid and rinsate will be immediately extracted
with a solvent, such as, for example, chloroform, hexane, etc.,
known to dissolve the CWA agent or CWA simulant. The plates
themselves can be subjected to two types of analysis: contact
hazard and off-gas hazard. For contact hazard, the plates will be
covered with an absorbent material. For example, the French
government uses silica gel TLC plates, and the government of the
USA uses a dental dam as the absorbant material. In either case,
the absorbant material is held in place with a weight and incubated
for 15 minutes to 30 minutes at 25.degree. C. or 30.degree. C. The
absorbent will be removed and extracted with solvent. The plates
will be then extracted with solvent to determine residual agent
absorbed into the paint, and thus the contact hazard. If surface
decontamination efficiency, specifically the amount of residual
agent detectable, is the only variable being assessed, the plates
will be immediately extracted with solvent, eliminating the contact
hazard step. All of the solvent samples will be analyzed by Gas
Chromatography ("GC") with a flame photometric detector ("FPD") and
a phosphorus filter for nerve agents. Some countries use Gas
Chromatography-Mass Spectrometry ("GC-MS") for the analysis.
EXAMPLE 9
Large-Scale Batch Fermentation to Produce OPH
[0866] Batch Culture-Rich Medium comprised 24 g/L yeast extract; 12
g/L casein hydrolysate; 4 ml/L glycerol; 2.31 g/L KH.sub.2PO.sub.4;
12.54 g/L K.sub.2HPO.sub.4; 0.24 g/L COCl.sub.2.6H.sub.2O; 2 g/L
glucose; 0.2 ml/L PPG2000; and 100 .mu.g/ml ampicillin.
[0867] Batch Culture--5 L scale was grown at the following
conditions: 30.degree. C.; 400-450 rpm agitation; DO controlled at
20%; uncontrolled initial pH between 6.8-6.9; 5 Lpm (1 vvm)
aeration; and atmospheric pressure. Over a time period of 0 to 50
hours, the Escherichia coli strain's growth was measured by optical
density at 600 nm, the specific paraoxonase activity was determined
(.mu.mol ml.sup.-1 min.sup.-1), the volumetric paraoxonase activity
was determined (.mu.mol ml.sup.-1 min.sup.-1), the pH measured over
a range of pH 6 to pH 9, the agitation measured over a range of 0
rpm to 500 rpm, and the dissolved oxygen measured over a range of
0% to 100%.
[0868] Batch Culture--400 L scale was grown at the following
conditions: 30.degree. C.; 150-200 rpm agitation; DO at 0-100%;
uncontrolled initial pH 6.58; 200-300 Lpm (0.5-0.75 vvm) aeration;
and tank pressure at 0-10 psi. Over a time period of 0 to 30 hours,
the Escherichia coli strain's growth was measured by optical
density at 600 nm, the specific paraoxonase activity was determined
(.mu.mol ml.sup.-1 min.sup.-1), the volumetric paraoxonase activity
was determined (.mu.mol ml.sup.-1 min.sup.-1), the pH measured over
a range of pH 6 to pH 8, the agitation measured over a range of 0
rpm to 200 rpm, the dissolved oxygen measured over a range of 0% to
100%, the aeration rate measured over a range of 0 to 300 Lpm, and
the tamk pressure measured over a range of 0 psi to 12 psi.
EXAMPLE 10
Large-Scale Fed-Batch Fermentation to Produce OPH
[0869] Fed Batch Culture-Defined Medium comprised 13.3 g/L
KH.sub.2PO.sub.4; 4 g/L (NH.sub.4).sub.2SO.sub.4; 1.7 g/L citric
acid; 10 g/L glycerol; 1.2 g/L MgSO.sub.4.7H.sub.2O; 0.024 g/L
MnCl.sub.2.4H.sub.2O; 2.26 mg/L CuCl.sub.2--H.sub.2O; 5 mg/L
H.sub.3BO.sub.3; 4.5 mg/LThiamine.HCl; 4 mg/L
Na.sub.2MoO.sub.4.7H.sub.2O- ; 0.06 g/L Fe(III) citrate; 8.4 mg/L
EDTA; 4 mg/L CoCl.sub.2.6H.sub.2O; 8 mg/L
Zn(acetate).sub.2.H.sub.2O; and 100 .mu.g/ml ampicillin.
[0870] Feed: 500 g/L carbon source and 10 g/L
MgSO.sub.4.7H.sub.2O.
[0871] Batch Culture--5 L scale was grown at the following
conditions: 30.degree. C.; 200-1000 rpm agitation; DO controlled at
20%; pH controlled at 6.5; 5 Lpm (1 vvm) aeration; and atmospheric
pressure. Feed was initiated as the 16.sup.th hour, with the feed
rate profile a constant rate with stepwise increments. Over a time
period of 0 to 70 hours, the Escherichia coli strain's growth was
measured by optical density at 600 nm, the specific paraoxonase
activity was determined (.mu.mol ml.sup.-1 min.sup.-1), the
volumetric paraoxonase activity was determined (.mu.mol ml.sup.-1
min.sup.-1), the pH measured over a range of pH 6 to pH 9, and the
addition of the feed measured from 0 ml to 1000 ml.
EXAMPLE 11
Coating Formulation
[0872] It is contemplated that any described coating composition
may be altered (e.g., by direct addition and/or coating component
substitution) to incorporate the biomolecular composition of the
present invention. The previous embodiments of the invention
primarily described compositions and techniques for preparing,
testing, and using a coating prepared de novo. However, it is
contemplated that the biomolecular composition of the present
invention may be incorporated into a standard coating by direct
addition, as described in Example 3. In specific aspects, it is
contemplated that such added biomolecular composition may comprise
0.001% to 40% or more, including all intermediate ranges and
combinations thereof, by weight or volume, of the final composition
produced by a combination of a coating and the biomolecular
composition of the present invention.
[0873] Alternatively, it is contemplated that a previously
described coating composition may be altered by substitution
("replacement") of one or more coating components, particularly a
binder and/or a particulate material coating component (e.g., a
pigment, a rheological control agent, a dispersant) by the
biomolecular composition of the present invention. It is
contemplated that 0.001% to 100%, including all intermediate ranges
and combinations thereof, of the binder and/or particulate material
coating component may be substituted by biomolecular composition of
the present invention. Additionally, the concentration of a
biomolecular composition of the present invention may exceed 100%,
by weight or volume, of the substituted coating component. In
specific aspects, a coating component may be substituted with a
biomolecular composition of the present invention equivalent to
0.001% to 500%, including all intermediate ranges and combinations
thereof, of the coating component. For example, a 20% (e.g., 2 kg)
of a dispersant may be replaced by 10% (e.g., 1 kg) of the
biomolecular composition of the present invention to produce a
coating with similar dispersion properties as a non-substituted
formulation. In an addition example, 70% of a specific pigment
(e.g., 7 kg) may be replaced by the equivalent of 127% (e.g., 12.7
kg) of the biomolecular composition of the present invention to
produce a coating with similar hiding power as a non-substituted
formulation. The various assays described herein, or as would be
known to one of ordinary skill in the art in light of the present
disclosures, may be used to determine the properties of a coating
and/or film produced by direct addition and/or coating component
substitution by the biomolecular composition of the present
invention.
[0874] The following is an example of a exterior gloss alkyd house
paint that comprises various particulate materials (e.g., silica, a
shading pigment, bentonite clay) that may incorporate a biomolecule
composition of the present invention. This example of an exterior
gloss alkyd house paint comprises a grind and a letdown. The grind
comprises by weight or volume: a first alkyd 232.02 lb or 29.9
gallons; a second alkyd 154.2 lb or 20 gallons; an aliphatic
solvent (e.g., duodecane) 69.55 lb or 1.7 gallons; lecithin 7.8 lb
or 0.91 gallons; TiO2 185.25 lb or 5.43 gallons; 10 micron silica
59.59 lb or 2.7 gallons; bentonite clay 18.00 lb or 1.44 gallons; a
second alkyd 97.22 lb or 12.61 gallons; a first alkyd 69.84 lb or
9.00 gallons; and mildewcide 7.8 lb or 0.82 gallons. The letdown
comprises by weight or volume: aliphatic solvent (e.g., dudecane)
19.50 lb or 3.00 gallons; a first drier (e.g., 12% solution cobalt)
2.00 lb or 0.23 gallons; a second drier (e.g., 18% solution Zr)
2.92 lb or 0.32 gallons; a third drier 3 (e.g., 10% solution Ca)
8.00 lb or 0.98 gallons; methyl ethyl ketoxime (Anti skinning
agent) 3.22 lb or 0.42 gallons; an aliphatic solvent 9.75 lb or
1.50 gallons; and a shading pigment 0.3 lb or 0.04 gallons. In some
embodiments, the particulate material of the coating formulation
may be partly or fully substituted by the biomolecule composition
of the present invention. In other embodiments, the above
formulation may be enhanced by direct addition of a biomolecule
composition of the present invention.
[0875] In another example, the following exterior flat latex house
paint may be modified to incorporate a biomolecule composition of
the present invention. This example of an exterior flat latex house
paint formulation, in typical order of addition, by weight or
volume: water, 244.5 lb or 29.47 gallons; hydroxyethylcellulose, 3
lb or 0.34 gallons; glycols, 60 lb or 6.72 gallons; polyacrylate
dispersant, 6.8 lb or 0.69 gallons; biocides, 10 lb or 1 gallons;
non-ionic surfactant, 1 lb or 0.11 gallons; titanium dioxide, 225
lb or 6.75 gallons; silicate mineral, 160 lb or 7.38 gallons;
calcined clay, 50 lb or 2.28 gallons; acrylic latex, @ 60%, 302.9
lb or 34.42 gallons; coalescent, 9.3 lb or 1.17 gallons; defoamers,
2 lb or 0.26 gallons; ammonium hydroxide, 2.2 lb or 0.29 gallons;
2.5% HEC solution, 76 lb or 9.12 gallons. In some embodiments, the
particulate material (e.g., silicate mineral, calcined clay,
titanium dioxide) of this coating formulation may be partly or
fully substituted by the biomolecule composition of the present
invention. In other embodiments, the above formulation may be
enhanced by direct addition of a biomolecule composition of the
present invention.
[0876] It is contemplated that any such previously described
coating formulation may be modified to incorporate a biomolecular
composition of the present invention. Examples of described coating
compositions include over 200 industrial water-borne coating
formulations (e.g., air dry coatings, air dry or force air dry
coatings, anti-skid of non-slip coatings, bake dry coatings, clear
coatings, coil coatings, concrete coatings, dipping enamels,
lacquers, primers, protective coatings, spray enamels, traffic and
airfield coatings) described in "Industrial water-based paint
formulations," 1988, over 550 architectural water-borne coating
formulations (e.g., exterior paints, exterior enamels, exterior
coatings, interior paints, interior enamels, interior coatings,
exterior/interior paints, exterior/interior enamels,
exterior/interior primers, exterior/interior stains), described in
"Water-based trade paint formulations," 1988, the over 400 solvent
borne coating formulations (e.g., exterior paints, exterior
enamels, exterior coatings, exterior sealers, exterior fillers,
exterior primers, interior paints, interior enamels, interior
coatings, interior primers, exterior/interior paints,
exterior/interior enamels, exterior/interior coatings,
exterior/interior varnishes) described in "Solvent-based paint
formulations," 1977; and the over 1500 prepaint specialties and/or
surface tolerant coatings (e.g., fillers, sealers, rust
preventives, galvanizers, caulks, grouts, glazes, phosphatizers,
corrosion inhibitors, neutralizers, graffiti removers, floor
surfacers) described in Prepaint Specialties and Surface Tolerant
Coatings, by Ernest W. Flick, Noyes Publications, 1991.
EXAMPLE 12
Ranges
[0877] To provide a description of the present invention that is
both concise and clear, various examples of ranges have been
identified herein with the phrase "including all intermediate
ranges and combinations thereof. Examples of specific values (e.g.,
%, kDa, .degree. C., .mu.m, kg/L, Ku) that can be within a cited
range by the reference to "including all intermediate ranges and
combinations thereof include 0.000001, 0.00001, 0.0001, 0.001,
0.002, 0.003, 0.004, 0.005, 0.006, 0.007, 0.008, 0.009, 0.01, 0.02,
0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.10, 0.15, 0.20, 0.25,
0.30, 0.35, 0.40, 0.45, 0.50, 0.55, 0.60, 0.65, 0.70, 0.75, 0.80,
0.85, 0.90, 0.95,1.0,1.1, 1.2, 1.30, 1.31, 1.32, 1.33, 1.34, 1.35,
1.36, 1.37, 1.38, 1.39, 1.40, 1.41, 1.42, 1.43, 1.44, 1.45, 1.46,
1.47, 1.48, 1.49, 1.50, 1.51, 1.52, 1.53, 1.54, 1.55, 1.56, 1.57,
1.58, 1.59, 1.60, 1.61, 1.62, 1.63, 1.64, 1.65, 1.66, 1.67, 1.68,
1.69, 1.70, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8,
2.9, 3.0, 3.1, 3.2, 3.3, 3.4, 3.5, 3.6, 3.7, 3.8, 3.9, 4.0, 4.1,
4.2, 4.3, 4.4, 4.5, 4.6, 4.7, 4.8, 4.9, 5.0, 5.1, 5.2, 5.3, 5.4,
5.5, 5.6, 5.7, 5.8, 5.9, 6.0, 6.1, 6.2, 6.3, 6.4, 6.5, 6.6, 6.7,
6.8, 6.9, 7.0, 7.1, 7.2, 7.3, 7.4, 7.5, 7.6, 7.7, 7.8, 7.9, 8.0,
8.1, 8.2, 8.3, 8.4, 8.5, 8.6, 8.7, 8.8, 8.9, 9.0, 9.1, 9.2, 9.3,
9.4, 9.5, 9.6, 9.7, 9.8, 9.9, 10.0, 11, 12, 13, 14, 15, 16, 17, 18,
19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35,
36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52,
53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69,
70, 71, 72, 73, 74, 75, 76, 77, 78, 79, 80, 81, 82, 83, 84, 85, 86,
87, 88, 89, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 100, 101, 102,
103, 104, 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, 115,
116, 117, 118, 119, 120, 121, 122, 123, 124, 125, 126, 127, 128,
129, 130, 131, 132, 133, 134, 135, 136, 137, 138, 139, 140, 141,
142, 143, 144, 145, 146, 147, 148, 149, 150, 151, 152, 153, 154,
155, 156, 157, 158, 159, 160, 161, 162, 163, 164, 165, 166, 167,
168, 169, 170, 171, 172, 173, 174, 175, 176, 177, 178, 179, 180,
181, 182, 183, 184, 185, 186, 187, 188, 189, 190, 191, 192, 193,
194, 195, 196, 197, 198, 199, 200, 201, 202, 203, 204, 205, 206,
207, 208, 209, 210, 211, 212, 213, 214, 215, 216, 217, 218, 219,
220, 221, 222, 223, 224, 225, 226, 227, 228, 229, 230, 231, 232,
233, 234, 235, 236, 237, 238, 239, 240, 241, 242, 243, 244, 245,
246, 247, 248, 249, 250, 275, 300, 325, 350, 375, 400, 425, 450,
475, 500, 525, 550, 575, 600, 625, 650, 675, 700, 725, 750, 775,
800, 825, 850, 875, 900, 925, 950, 975, 1000, 1050, 1100, 1150,
1200, 1250, 1300, 1350, 1400, 1450, 1500, 1600, 1700, 1800, 1900,
2000, 3000, 4000, 5000, 6000, 7000, 8000, 9000, 10,000, or
more.
[0878] However, general ranges for each type of unit (e.g., %, kDa,
.degree. C., .mu.m, kg/L, Ku) are contemplated. Examples of values
that can be within a cited percentage range, as applicable, include
0.001% to 100%, including all intermediate ranges and combinations
thereof. Examples of values that can be within a cited molecular
mass range, as applicable, in kilo Daltons ("kDa"), include 0.50
kDa to 110 kDa, including all intermediate ranges and combinations
thereof. Examples of values that can be within a cited temperature
range, as applicable, in degrees Celsius (".degree. C."), that can
be within a cited range include of 0.degree. C. to 500.degree. C.,
including all intermediate ranges and combinations thereof.
Examples of values that can be within a thickness range (e.g.,
coating and/or film thickness upon a surface), as applicable, in
micrometers (".mu.m"), that can be within a cited range include of
1 .mu.m to 2000 .mu.m, including all intermediate ranges and
combinations thereof. Examples of values that can be within a cited
density range, as applicable, in kilograms per liter ("kg/L"),
include 0.50 kg/L to 20 kDa, including all intermediate ranges and
combinations thereof. Examples of values that can be within a cited
shear rate range, as applicable, in Ku, include 20 Ku to 300 Ku,
including all intermediate ranges and combinations thereof.
EXAMPLE 13
Elastomers
[0879] It is contemplated that a biomolecular composition may also
be incorporated into an elastomer. Elastomers ("rubbers") are
polymers that can undergo large, but reversible, deformations upon
a relatively low physical stress. It is contemplated that an
elastomer composition may incorporate a biomolecular composition of
the present invention, such as by preparation with the biomolecular
composition and/or direct addition such as by a multi-pack
composition. Elastomers (e.g., tire rubbers, polyurethane
elastomers, polymers ending in an anionic diene, segmented
polyerethane-urea copolymers, diene triblock polymers with
styrene-alpha-methylstyrene copolymer end blocks,
poly(p-methylstyrene-b-- p-methylstyrene),
polydimethylsiloxane-vinyl monomer block polymers, chemically
modified natural rubber, polymers from hydrogenated polydienes,
polyacrylic elastomers, polybutadienes, trans-polyisoprene,
polyisobutene, cis-1,4-polybutadiene, polyolefin thermoplastic
elastomers, block polymers, polyester thermoplastic elastomer,
thermoplastic polyurethane elastomers) and techniques of elastomer
synthesis and elastomer property analysis have been described, for
example, in Walker, B. M., ed., Handbook of Thermoplastic
Elastomers, Van Nostrand Reinhold Co., New York, 1979; Holden, G.,
ed., et. al., Thermoplastic Elastomers, 2.sup.nd Ed., Hanser
Publishers, Verlag, 1996.
EXAMPLE 14
Fillers and Filled Polymers
[0880] A filler is a bulk material in a composition. Extender
pigments are used as a filler for coatings. In certain embodiments,
a biomolecular composition may be used as a filler for various
compositions. Examples of compositions that use fillers that are
contemplated herein for incorporation of a biomolecular composition
of the present invention, include a composition comprising a
polymer, thermoplastic material, a thermostat material, an
elastomer, or a combination thereof. Such filler comprising
materials have been described in Gerard, J. F., ed., Fillers and
Filled Polymenrs-Macromolecular Symposia 169, Wiley-VCH, Verlag,
2001; Slusarski, L., ed., Fillers for the New
Millenium-Macromolecular Symposia 194, Wiley-VCH, Verlag, 2003; and
Landrock, A. H., Adhesives Technology Handbook, Noyes Publications,
N.J., 1985.
EXAMPLE 15
Adhesives and Sealants
[0881] An adhesive is a composition that is capable of holding at
least two surfaces together in a strong and permanent manner. A
sealant is a composition capable of attaching to at least two
surfaces, filling the space between them to provide a barrier or
protective coating. In certain embodiments, a biomolecular
composition may be used as a component of an adhesive or a sealant,
such as, for example, by direct addition, substitution of an
adhesive or sealant component (e.g., a particulate material), or a
combination thereof.
[0882] Examples of adhesives and sealants (e.g., caulks, acrylics,
elastomers, phenolic resin, epoxy, polyurethane, anarobic and
structural acrylic, high-temperature polymers, water-based
industrial type adhesives, water-based paper and packaging
adhesives, water-based coatings, hot melt adhesives, hot melt
coatings for paper and plastic, epoxy adhesives, plastisol
compounds, construction adhesives, flocking adhesives, industrial
adhesives, general purpose adhesives, pressure sensitive adhesives,
sealants, mastics, urethanes,) for various surfaces (e.g., metal,
plastic, textile, paper), adhesive and sealant components (e.g.,
antifoams, antioxidants, extenders, fillers, pigments, flame/fire
retardants, oils, polymer emulsions, preservatives, bactericides,
fungicides, resins, rheological/viscosity control agents, starches,
waxes, acids, aluminum silicates, antiskinning agents, calcium
carbonates, catalysts, cross-linking agents, curing agents, clays,
corn starch, starch derivatives, defoamers, antifoams, dispersing
agents, emulsifying agents, epoxy resin diluents, lattices,
polybutenes, polyvinyl acetates, preservatives, acrylic resins,
epoxy resins, ester gums, ethylene/vinyl acetate resins, maleic
resins, natural resins, phenolic resins, polyamide resins,
polyethylene resins, polypropylene resins, polyterpene resins,
powder coating resins, radiation coating resins, urethane resins,
vinyl chloride resins, emulsion resins, dispersion resins, resin
esters, rosins, silicas, silicon dioxide, stabilizers,
surfactants/surface active agents, talcs, thickeners, thixotropic
agents, waxes) techniques of preparation and assays for properties,
have been described in Skeist, I., ed., Handbook of Adhesives,
3.sup.rd Ed., Van Nostrand Reinhold, New York, 1990; Satriana, M.
J. Hot Melt Adhesives: Manufacture and Applications, Noyes Data
Corporation, New Jersey, 1974; Petrie, E. M., Handbook of Adhesives
and Sealants, McGraw-Hill, New York, 2000; Hartshorn, S. R., ed.,
Structural Adhesives-Chemistry and Technology. Plenum Press, New
York, 1986; Flick, E. W., Adhesive and Sealant Compound
Formulations, 2.sup.nd Ed., Noyes Publications, New Jersey, 1984;
Flick, E., Handbook of Raw Adhesives 2.sup.nd Ed., Noyes
Publications, New Jersey, 1989; Flick, E., Handbook of Raw
Adhesives, Noyes Publications, New Jersey, 1982; Dunning, H. R.,
Pressure Sensitive Adhesives-Formulations and Technology, 2.sup.nd
Ed., Noyes Data Corporation, New Jersey, 1977; and Flick, E. W.,
Construction and Structural Adhesives and Sealants, Noyes
Publications, New Jersey, 1988.
EXAMPLE 16
Textiles
[0883] It is contemplated that a biomolecular composition may also
be incorporated into a material applied to a textile, such as, for
example, a textile finish. Materials for application to a textile,
textile finishes (e.g., soil-resistant finishes, stain-resistant
finishes) and finish components (e.g., antioxidants, defoamers,
antimicrobials, wetting agents, flame retardants, softeners, soil
repellents, hand modifiers, antistatic agents, biocides, fixatives,
scouring agents, dispersants, defoamers, anticracking agents,
binders, stiffeners, cohesive agents, fiber lubricants,
emulsifiers, antistats, yarn to hard surface lubricants) as well as
assays for determining their properties are described, for example,
in Johnson, K., Antistatic Compositions for Textiles and Plastics,
Noyes Data Corporation, New Jersey, 1976; Rouette, H. K.,
Encyclopedia of Textile Finishing, Springer, Verlag, 2001; "Textile
Finishing Chemicals: An Industrial Guide", by Ernest W. Flick,
Noyes Publications, 1990; and "Handbook of Fiber Finish
Technology", by Philip E. Slade, Marcel Dekker, 1998. A specific
example of a textile finish is the trademark formulations of water
repellent and/or oil repellent finish known as Scotchguard.TM. (3M
Corporate Headquarters, Maplewood, Minn., U.S.A.).
EXAMPLE 17
Waxes
[0884] It is contemplated that a biomolecular composition may also
be incorporated into a material applied to a surface after
manufacture, such as, for example, a wax. Waxes (e.g., natural
waxes, fossil waxes, earth waxes, peat waxes, montana waxes,
lignite paraffins, petroleum waxes, synthetic waxes, commercial
modified, blended, and compounded waxes, emulsifiable waxes, waxy
alcohols, waxy acids, metallic soaps, compounded waxes, paraffin
wax compounds, ethyl cellulose and wax mixtures, compositions with
resins and rubber) and methods of wax preparation and assays for
wax properties have been described, for example, in Warth, A. H.,
The Chemistry and Technology of Waxes, Reinhold Publishing
Corporation, New York, 1956; Bennet, H., Industrial Waxes Volume II
Compounded Waxes and Technology, Chemical Publishing Co., New York,
1975.
EXAMPLE 18
Additional OPAAs
[0885] It additional embodiment is it contemplated that the
following organisms produce an OPAA that may be used in a
biomolecular composition of the present invention: Acinetobacter
calcoaceticus ATCC 19606, Aeromonas hydrophila ATCC 7966, Aeromonas
proteolytica, Arm. A isolate 1, Arm. A isolate 2, Bacillus subtilis
(fr. Zuberer), Bacillus subtilis, ATCC 18685, Bacillus subtilis
BRB41, Bacillus subtilis Q, Bacillus thuringensis (fr. Zuberer),
Burkholderia cepacia LB400, Burkholderia cepacia T, Citrobacter
diversus, Citrobacter freundii ATCC 8090, Edwardsiella tarda ATCC
15947, Enterobacter aerogenes ATCC 13048, Enterobacter cloacae
96-3, Enterobacter liquefaciens 363, Enterobacter liquefaciens 670,
Erwinia carotovora EC189-67, Erwinia herbicola, Erwinia herbicola
(agglomerans), Escherichia coli E63, Hafnia alvei ATCC 13337,
Klebsiella pneumoniae ATCC 13883, Lactobacillus casei 686,
Lactococcus lactis subsp. lactis pIL253, Proteus morganaii, Proteus
vulgaris ATCC 13315, Pseudomonas aeriginosa ATCC 10145, Pseudomonas
aeriginosa ATCC 27853, Pseudomonas flourescens, Pseudomonas putida
ATCC 18633, Pseudomonas putida PpY101, Pseudomonas sp. P,
Salmonella typhimurium ATCC 14028, Serratia marcescens ATCC 8100,
Serratia marcescens HY, Serratia marcescens Nima, Shigella flexneri
ATCC 12022, Shigella sonnei ATCC 25931, Staphylococcus aureus ATCC
25923, Staphylococcus sp. S, Streptococcus faecalis ATCC 19433,
Vibrio parahaemolyticus TAMU 109, Yersinia enterocolitica ATCC
9610, Yersinia enterocolitica TAMU 84, Yersinia frederiksenii TAMU
91, Yersinia intermedia ATCC 29909, Yersinia intermedii TAMU 86,
Yersinia kristensenia ATCC 33640, Yersinia kristensenia TAMU 95,
Yersinia sp. ATCC 29912, Vibrio proteolyticus ATCC 15338, Thermus
sp. ATCC 31674, Streptomyces cinnamonensis subsp. Proteolyticus
ATCC 19893, Deinococcus proteolyticus ATCC 35074, Clostridium
proteolyticum ATCC 49002, Aeromonas jandaei ATCC 49568, Aeromonas
veronii biogroup sobria ATCC 9071, Pseudoaltermonas haloplanktis
ATCC 23821, Xanthomonas campestris ATCC 33913, Pseudoalteromonas
espejiana ATCC 27025, Shewanella putrefasciens ATCC 8071,
Stenotrophomonas maltophilus ATCC 13637, Ochrobactrum anthropi ATCC
19286, Desulfovibrio vulgaris, or a combination thereof.
EXAMPLE 19
Dowel Assay--Paraoxonase
[0886] This example describes assay procedure for quantitative
assessment of surface activity of a composition comprising a
biomolecular composition using medicine sticks/dowels. The
equipment used is a U.V. Spectrophotometer, a U.V. 1 cm pathlength
cuvettes, 3 ml and 100 .mu.l volume, and 1.5 ml eppendorf tubes.
The reagents used include paraoxon (MW 275.21, ChemService
cat#PS-610), 99% CHES ("2-[cyclohexylamino]ethane- sulfonic acid"),
(MW 207.3, Sigma cat # C-2880), and CoCL.sub.2 6H.sub.2O (MW 237.9,
Sigma cat # C-3169). 1 M CoCl.sub.2, sterile, can be prepared as
23.79 g COCl.sub.2 per 100 ml ddH.sub.2O that is filter sterilized
or autoclaved. 200 mM CHES, pH 9.0, sterile can be prepared as 4.15
g+80 ml ddH.sub.2O, pH to 9.0 with NaOH, where the total volume
with ddH.sub.2O is 100 ml, and can be filter sterilized or
autoclaved. The assay buffer is 20 mM CHES, pH 9.0, 50 .mu.M
COCl.sub.2.
[0887] In a 1.5 mL Eppendorf tube add: paraoxon to 1 mM (ex: 126
.mu.l of 12 mM paraoxon) and assay buffer to 1.5 ml (ex: 1374 p,
CHES buffer). Add a 5 mm length of treated stick to start the
reaction, mix by inverting. Take 10 .mu.l samples at 1 minute
intervals, diluting with 90 .mu.L CHES buffer into a 100 .mu.l
cuvette. Record the absorbance at 400 nm (A.sub.400 nm), blanking
against CHES buffer+paraoxon. A small amount of hydrolysis of
paraoxon without biomolecular composition may occur. Mix by
inversion before each time point.
[0888] Alternatively, in a 3 ml cuvette, add:paraoxon to 1 mM (ex:
168 .mu.l of 12 mM paraoxon), and assay buffer to 2.0 ml (ex: 1832
.mu.l CHES buffer). Add a 5 (or 15 mm) length of treated stick to
start the reaction. Record the (A.sub.400 nm) at the following time
points: 0, 15, 30, 45, 60, 120, 180, 240, 300, 360, 420 and 480
minutes. Mix by inversion at regular intervals. If absorbances
above 2.5 are observed, dilute 10 .mu.L samples with 90 .mu.L CHES
buffer in a 100 .mu.L cuvette, as for fast reactions, above.
[0889] The following results (Table 5) demonstrate 90% degradation
of the paraxon over the time frame of measurement by a paroxonase
bimolecular additive of the present invention as determined by the
dowel assay.
5TABLE 5 Results Time Replicates (seconds) A B C umoles p-NP Std
Dev 0 0.0218 0.0218 0.0224 0.0220 0.0003 120 0.1794 0.1518 0.1253
0.1522 0.0271 240 0.4359 0.3953 0.3418 0.3910 0.0472 360 0.7529
0.6541 0.6218 0.6763 0.0683 480 0.9494 0.8971 0.8894 0.9120 0.0327
600 0.9724 0.9688 0.9659 0.9690 0.0032 720 0.9706 0.9706 0.9729
0.9714 0.0014 840 0.9700 0.9694 0.9782 0.9725 0.0049 960 0.9535
0.9535 0.9435 0.9502 0.0058 1080 0.9600 0.9935 0.9912 0.9816 0.0187
1200 0.9500 0.9665 0.9682 0.9616 0.0101 p-NP = reaction product
REFERENCES
[0890] "ASTM Book of Standards, Volume 06.01, Paint--Tests for
Chemical, Physical, and Optical Properties; Appearance" (2002) ASTM
International, West Conshohocken, Pa., U.S.A.
[0891] "ASTM Book of Standards, Volume 06.02, Paint--Products and
Applications; Protective Coatings; Pipeline Coatings" (2002) ASTM
International, West Conshohocken, Pa., U.S.A.
[0892] "ASTM Book of Standards, Volume 06.03, Paint--Pigments,
Drying Oils, Polymers, Resins, Naval Stores, Cellulosic Esters, and
Ink Vehicles" (2002) ASTM International, West Conshohocken, Pa.,
U.S.A.
[0893] "ASTM Book of Standards, Volume 06.04, Paint--Solvents;
Aromatic Hydrocarbons" (2002) ASTM International, West
Conshohocken, Pa., U.S.A.
[0894] "Paint and Coating Testing Manual, Fourteenth Edition of the
Gardner-Sward Handbook" (Koleske, J. V., Ed.) (1995) American
Society for Testing and Materials, Philadelphia, Pa., U.S.A.
[0895] "Paint and Surface Coatings, Theory and Practice, Second
Edition" (Lambourne, R. and Strivens, T. A., Eds.) (1999) Woodhead
Publishing Ltd., Cambridge, England.
[0896] "Paints, Coatings and Solvents, Second, Completely Revised
Edition" (Stoye, D. and Freitag, W., Eds.) (1998) Wiley-Vch, New
York, U.S.A.
[0897] Albaret, A. et al., Prot. Struct. Funct. Genet. 28:543-555,
1997.
[0898] Albizo, J. M. and White, W. E. "The Hydrolysis of GD and VX
by Acetone Dried Preparations of Cured and Plasmid-Containing
Pseudomonas Diminuta" Chemical Research, Development &
Engineering Center Scientific conference on Chemical Defense
Research, November 18-21, pp. 643-649, 1986.
[0899] Andreopoulos, F. M. et al., Biotech. Bioeng. 65(5):579-588,
1999.
[0900] Andreopoulos, F. M. et al., Biotech. Bioeng. 65(5):579-588,
1999.
[0901] Ash, M. and Ash, I. "Handbook of Paint and Coating Raw
Materials, Second Edition" (1996) Ashgate Publishing Company,
Brookfield, Vt., U.S.A.
[0902] Ashani, et al., Biochem. Pharm. 55:159-168, 1998.
[0903] Azzoni, A. R. et al., Biotech. Bioeng. 80(3):268-276,
2002.
[0904] Baxter, G. D. et al., Insect Biochem. and Molec. Bio.,
28:581-589 (1998).
[0905] Baxter, G. D. et al., Insect Biochem. and Molecular Bio.,
32:815-820 (2002).
[0906] Bennet, H., Industrial Waxes Volume II Compounded Waxes and
Technology, Chemical Publishing Co, New York, 1975.
[0907] Benning, M. M. et al., Biochem. 33:15001-15007, 1994.
[0908] Benning, M. M. et al., Biochem. 34:7973-7978, 1995.
[0909] Benning, M. M. et al., J. Biol. Chem. 275:30556-30560,
2000.
[0910] Benschop, H. P. and De Jong, L. P. A. Acc. Chem. Res.
21:368-374, 1988.
[0911] Benschop, H. P. et al., Toxic. and Applied Pharm. 72:61-74,
1984.
[0912] Billecke, S. S. et al., Chemico-Biological Interactions
119-120, 251-256, 1999.
[0913] Brinkmann, U. et al., Gene 85:109-114, 1989.
[0914] Broomfield, C. A., et al., Chemico-Biochem. Interactions.,
119-120:413-418 (1999).
[0915] Bugg, C. E. et al., Sci. Am., 269:92-98, 1993.
[0916] Caldwell, S. R. and Raushel, F. M., Appl. Biochem Biotech
31:59-74, 1991b.
[0917] Caldwell, S. R. and Raushel, F. M., Biochem. 30:744-7450,
1991c.
[0918] Caldwell, S. R. and Raushel, F. M., Biotech. Bioeng.
37:103-109, 1991a.
[0919] Campbell, P. M. et al., Biochem. Molec. Biol. 28:139-150,
1998.
[0920] Chae, M. Y. et al., Bioorg. Med. Chem. Lett. 4:1473-1478,
1994.
[0921] Chen, T. et al., Biomacromolecules 2:456-462, 2001.
[0922] Chen, W. and Mulchandani, A. Tibtech 16:71-76, 1998.
[0923] Cheng, T.-C. et al., Appl. Environ. Microbiol.
62(5):1636-1641, 1996.
[0924] Cheng, T.-C. et al., Applied and Environ. Microbio.
59(9):3138-3140, 1993.
[0925] Cheng, T.-C. et al., Chemico-Biological Interactions
119-120:455-462, 1999.
[0926] Cheng, T.-C. et al., J. Ind. Microbiol. 18:49-55, 1997.
[0927] Chen-Goodspeed, M. et al., Biochemistry 40:1332-1339,
2001b.
[0928] Chen-Goodspeed, M. et al., Biochemistry, 40:1325-1331,
2001a.
[0929] Chiang, T. et al., Bull. Env. Contam. Toxicol. 34:809-814,
1985.
[0930] Cho, C. M. et al., Applied and Enviro. Microbio., 2026-2030,
2002.
[0931] Claudianos, C. et al., Insect Biochem. and Molecular Bio.
29:675-686, 1999.
[0932] Cohen, A. A. and Shatzmiller, S. E., J. Mol. Graph.
11:166-173, 1993.
[0933] Coller, B. S. et al., J. Biol. Chem. 268:20741-20743,
1993.
[0934] Combes, D. et al., J. Mol. Biol. 300:727-742, 2000.
[0935] Cousin, X. et al., J. Biol. Chem. 271(25):15099-15108,
1996.
[0936] Creighton, T. E. Proteins: Structure and Molecular
Properties, W. H. Freeman & Co., San Francisco, pp 79-86,
1983.
[0937] Dave, K. I. et al., Appl. Microbiol. Biotechnol. 41:352-358,
1994b.
[0938] Dave, K. I. et al., Biotechnol. Appl. Biochem. 19:271-284,
1994a.
[0939] Dave, K. I. et al., Chemical-Biological Interactions
87:55-68, 1993.
[0940] Dean, P. M., BioEssays, 16:683-687, 1994.
[0941] DeFrank, J. J. and Cheng, T.-C., J. Bacteriol 173:1938-1943,
1991.
[0942] DeFrank, J. J. et al., Chem.-Biol. Interact. 87:141-148,
1993.
[0943] Desai, U. A. et al., Protein Expr Purif 25(1):195-202,
2002.
[0944] Diaz-Alejo, N. et al., Chem.-Biol. Interact. 108(3):187-196,
1998.
[0945] diSioudi, B. D. et al., Chemico-Biological Interactions
119-120:211-223, 1999b.
[0946] diSioudi, B. et al., Biochemistry 38:2866-2872, 1999a.
[0947] Donarski, W. J. et al., Biochemistry 28:4650-4655, 1989.
[0948] Drevon, G. F. and Russell, A. J., Biomacromolecules
1:571-576, 2000.
[0949] Drevon, G. F. et al., Biomacromolecules 2:664-671,-2001.
[0950] Drevon, G. F. et al., Biotechnology and Bioengineering
79(7):785-794, 2002.
[0951] Dumas, D. P. et al., Biotech. Appl. Biochem. 11:235-243,
1989a.
[0952] Dumas, D. P. et al., Arch. Biochem. Biophys. 277:155-159,
1990.
[0953] Dumas, D. P. et al., Experientia, 46:729-731, 1990.
[0954] Dumas, D. P. et al., The Journal of Bio. Chem.
264(33):19659-19665, 1989b.
[0955] Dunning, H. R., Pressure Sensitive Adhesives-Formulations
and Technology, 2.sup.nd Ed., Noyes Data Corporation, New Jersey,
1977.
[0956] Duysen, E. G., J. Pharm. Exp. Ther. 302:751-758, 2002.
[0957] Edwards, R and Owen, W. J., Planta 175:99-106, 1998.
[0958] Efremenko, E. N. et al., J. Biochem. Biophys Methods
51:195-201, 2002.
[0959] Elashvili, I. and Defrank, J. J. "Phosphonate transporter
mutation enhances the utilization of diisopropylphosphate (DIPP)
and diisopropyl fluorophosphates (DFP) in Escherichia coli K-12.
Proceedings of 1996 US Army ERDEC Scientific conference on chemical
Defense Research, U.S. Army ERDEC, Aberdeen Proving Ground,
Aberdeen, Md.
[0960] Elashvili, I. et al., Appl Environ Microbiol
64(7):2601-2608, 1998.
[0961] Ellman, G. L. et al., Biochem Pharmacol 7:88-95, 1961.
[0962] Endo, F. et al., J. Biol. Chem. 264(8):4476-4481, 1989.
[0963] Flick, E. W. "Handbook of Paint Raw Materials, Second
Edition" (1989) Noyes Data Corporation/Noyes Publications, Park
Ridge, N.J., U.S.A.
[0964] Flick, E. W., "Prepaint Specialties and Surface Tolerant
Coatings," Noyes Publications (1991).
[0965] Flick, E. W., "Textile Finishing Chemicals: An Industrial
Guide," Noyes Publications (1996).
[0966] Flick, E. W., Adhesive and Sealant Compound Formulations,
2.sup.nd Ed., Noyes Publications, New Jersey 1984.
[0967] Flick, E. W., Construction and Structural Adhesives and
Sealants, Noyes Publications, New Jersey, 1988.
[0968] Flick, E. W., Industrial Surfactants, Noyes Publications,
New Jersey, 1988.
[0969] Flick, E., Contemporary Industrial Coatings-Environmentally
Safe Formulations, Noyes Publications, New Jersey, 1985.
[0970] Flick, E., Engineering Resins-An Industrial Guide, Noyes
Publications, New Jersey, 1988.
[0971] Flick, E., Handbook of Raw Adhesives, 2.sup.nd Ed., Noyes
Publications, New Jersey, 1989.
[0972] Flick, E., Handbook of Raw Adhesives, Noyes Publications,
New Jersey, 1982.
[0973] Flick, E., Water-Soluble Resins-An Industrial Guide, Noyes
Publications, New Jersey, 1986.
[0974] Fox, M. A., Acc. Chem. Res. 16:314-321, 1983.
[0975] Fox, T. G., Bulletin of the American Physics Society, 1:123,
1956.
[0976] Fujita, T. et al., Biochim. Biophys. Acta 1308 (1):49-57,
1996.
[0977] Gaberlein, S. et al., Analyst 125:2274-2279, 2000.
[0978] Gaberlein, S. et al., Appl Microbiol Biotechnol 54:652-658,
2000a.
[0979] Gallo, M. A. and Lawryk, N.J. (1991) Organic phosphorous
pesticides. In: The Handbook of Pesticide Toxicology (Eds. Hayes,
W. J. Jr. and Laws, E. R) Academic Press, San Diego, Calif. pp.
920-925.
[0980] Gao, J. et al., J. Agric. Food Chem. 48:614-6120, 2000.
[0981] Garden, J. M. et al., Comp. Biochem. Physiol. 52C:95-98,
1975.
[0982] Gerard, J. F., ed., Fillers and Filled
Polymenrs-Macromolecular Symposia 169, Wiley-VCH, Verlag, 2001.
[0983] Gillette, M. L., "Using Acid-Base Indicators to Visually
Estimate the pH of Solutions,38 Chemical Education Resources, Inc.
(1985).
[0984] Glascock, C. B. and Weickert, M. J. Gene, 223(1-2):221-231,
1998.
[0985] Gopal, S. et al., Biochem. and Biophys. Research Comm.
279:516-519, 2000.
[0986] Gordon, R. K. et al., Chemico-Biological Interactions
119-120:463-470, 1999.
[0987] Grauso, M. et al., FEBS Letter 424:279-284, 1998.
[0988] Greene, T. W. and Wuts, P. G. M. Second Edition, pp.
309-315, John Wiley & Sons, Inc., USA, 1991.
[0989] Grimsley, J. K. "Enhancement of OPH production" Final
report, U.S. Army Project DAAG-55-97-C-0005, 1997.
[0990] Grimsley, J. K. et al., Biochemistry 36(47):14366-14374,
1997.
[0991] Grimsley, J. K. et al., Biotechnology Intl. 2:235-242,
1999.
[0992] Hannig, G. and Makrides, S.C. TIBTECH 16:54-60, 1998.
[0993] Harel, M. et al., J. Am. Chem. Soc. 118:2340-2346, 1996.
[0994] Harel, M. et al., Proc Natl Acad Sci USA 89(22):10827-10831,
1992.
[0995] Harper, L. et al., Appl. Env. Micro. 54:2586-2589, 1988.
[0996] Hartleib, J. and Ruterjans, H Biochim et Biophys Acta
1546:312-324, 2001b.
[0997] Hartleib, J. and Ruterjans, Prot. Expression and
Purification 21:210-219, 2001a.
[0998] Hartleib, J. et al., Biochem J 353:579-589, 2001.
[0999] Hartshorn, S. R., ed., Structural Adhesives-Chemistry and
Technology, Plenum Press, New York, 1986.
[1000] Hassett, C. et al., Biochemistry 30:10141-10149, 1991.
[1001] Havens, P. L. and Rase, H. F. Ind. Eng. Chem. Res.
32:2254-2258, 1993.
[1002] Hill, C. M. et al., Bioorganic Chemistry, 29:27-35,
2001.
[1003] Hill, C. M. et al., Bioorganic Medicinal Chemistry Letters
10:1285-1288, 2000.
[1004] Holden, G., ed., et. al., Thermoplastic Elastomers, 2.sup.nd
Ed., Hanser Publishers, Verlag, 1996.
[1005] Hong, M. S. et al., Bioremediation Journal 2(2):145-157,
1998.
[1006] Hong, S.-B. and Raushel, F. M Chemico-Bio. Interact.
119-120:225-234, 1999b.
[1007] Hong, S.-B. and Raushel, F. M. Biochem. 35:10904-10912,
1996.
[1008] Hong, S.-B. and Raushel, F. M. Biochem. 38:1159-1165,
1999a.
[1009] Horne, I. et al., Appl. Environ. Microbiol. 68(7):3371-3376,
2002.
[1010] Hoskin, F. C. G. "An organophosphorus detoxifying enzyme
unique to squid." In: Squid as Experimental Animals (Eds. Gilbert,
D. L., Adelman W. J. Jr. and Arnold, J. M.), pp. 469-480. Plenum
Press, New York, 1990.
[1011] Hoskin, F. C. G. and Roush, A. H., Science 215:1255-1257,
1982.
[1012] Hoskin, F. C. G. et al., Biochemical Pharmacology
46(7):1223-1227, 1993.
[1013] Hoskin, F. C. G. et al., Fundam. Appl. Toxicol. 4:5165-5172,
1984.
[1014] Hoskin, F. C. G. et al., Biochemical Pharmacology
34(12):2069-2072, 1985.
[1015] Hoskin, F. C. G. et al., Biochemical Pharmacology
49(5):711-715, 1995.
[1016] Hoskin, F. C. G. et al., Chemico-Biological Interactions
119-120:399-404, 1999.
[1017] Hoskin, F. C. G. et al., Chemico-Biological Interactions
119-120:439-444, 1999.
[1018] Hruby, V. J., Biopolymers, 33:1073-1082, 1993.
[1019] Hung, S.-C. and Liao, J. C., Appl. Biochem. Biotechnol.
56(1):37-47, 1996.
[1020] In "Chemical Warfare Agents: Toxicity at Low Levels" (Satu
M. Somani and James A. Romano, Jr., Eds.) CRC Press, Boca Raton,
2001. Chapter 1, Health Effects of Low-Level Exposure to Nerve
Agents, p 2.
[1021] In "Chemical Warfare Agents: Toxicity at Low Levels" (Satu
M. Somani and James A. Romano, Jr., Eds.) CRC Press, Boca Raton,
2001. Chapter 14, Emergency Response to a Chemical Warfare Agent
Incident: Domestic Preparedness, First Response, and Public Health
Considerations, p 414.
[1022] In "Chemical Warfare Agents: Toxicity at Low Levels" (Satu
M. Somani and James A. Romano, Jr., Eds.) CRC Press, Boca Raton,
2001. Chapter 2, Toxicokinetics of Nerve Agents, pp 26-29.
[1023] In "Colour Index International" 3.sup.rd Ed. Pigment and
Solvent Dyes, Society of Dyers and Colourists American Association
of Textile Chemists and Colorists, 1997.
[1024] In "Colour Index International" 3.sup.rd Ed. Society of
Dyers and Colourists American Association of Textile Chemists and
Colorists, 1971.
[1025] In "Current Protocols in Cell Biology" (Morgan, K. Ed.) John
Wiley & Sons, 2002.
[1026] In "Current Protocols in Cytometry". (Robinson, J. P. Ed.)
John Wiley & Sons, 2002.
[1027] In "Current Protocols in Immunology" (Coico, R. Ed.) John
Wiley & Sons, 2002.
[1028] In "Current Protocols in Molecular Biology" (Chanda, V. B.
Ed.) John Wiley & Sons, 2002.
[1029] In "Current Protocols in Nucleic Acid Chemistry" (Harkins,
E. W. Ed.) John Wiley & Sons, 2002.
[1030] In "Current Protocols in Pharmacology" (Taylor, G. Ed.) John
Wiley & Sons, 2002.
[1031] In "Current Protocols in Protein Science" (Taylor, G. Ed.)
John Wiley & Sons, 2002.
[1032] In "Industrial water-based paint formulations" by Ernest W.
Flick, Park Ridge, N. J. Noyes, (1988), xvi, 277; p. 25.
[1033] In "Molecular Cloning" (Sambrook, J., and Russell, D. W.,
Eds.) 3rd Edition, Cold Spring Harbor, N.Y.: Cold Spring Harbor
Laboratory Press, 2001.
[1034] In "Organic Coatings: Science and Technology" 2.sup.nd
edition, by Zeno W. Wicks Jr., Frank N. Jones, S. Peter Pappas,
Publisher: Wiley-Interscience (John Wiley & Sons, Inc. 605
Third Avenue, New York, N.Y.) Table 31.1 Exterior White House
Paint, p. 562.
[1035] In "Paint and surface coatings: Theory and Practice"
2.sup.nd Edition (Lambourne, R. and Strivens, T. A. William, Eds)
Andrew Publishing, Woodhead Publishing Ltd, Abington Hall,
Abington, Cambridge CB1 6AH, England, 1999.
[1036] In "Paints, Coatings and Solvents" 2.sup.nd Edition (Stoye,
D. and Freitag, W., Eds) Wiley-Vch, New York, 1998.
[1037] Ishii, T. et al., Biochim. Biophys. Acta 1308(1):15-16,
1996.
[1038] Johnson, K., Antistatic Compositions for Textiles and
Plastics, Noyes Data Corporation, New Jersey, 1976.
[1039] Josse, D. et al., Chemico-Biological Interactions
119-120:71-78, 1999.
[1040] Josse, D. et al., J. Appl. Toxicol. 21:S7-S11, 2001.
[1041] Kaneva, I. et al., Biotechnol. Prog. 14:275-278, 1998.
[1042] Kim, C. et al., Biotechnol Bioeng 65:108-113, 1999.
[1043] Kim, J.-W. et al., Biotechnol. Prog. 18:429-436, 2002.
[1044] Koepke, J. et al., Acta. Cryst. D58:1757-1759, 2002.
[1045] Kolakowski, J. E. et al., Biocatal. Biotransform.
15:297-312, 1997.
[1046] Komives, C. et al., Biotechnol. Prog. 10:340-343, 1994.
[1047] Kuo, J. M. and Raushel, F. M., Biochemistry 33:4265-4272,
1994.
[1048] Kyte, J. and Doolittle, R. F. J. Mol. Biol., 157:105-132,
1982.
[1049] Lai, K. et al., Arch. Biochem. Biophys. 318:59-64, 1995.
[1050] Lai, K. et al., J. Biol. Chem. 269:16579-16584, 1994.
[1051] Landis, W. G. et al., J. Appl. Toxicol. 7:3541, 1987.
[1052] Landrock, A. H., Adhesives Technology Handbook, Noyes
Publications, New Jersey, 1985.
[1053] Leduc, M. et al., J. Bacteriol. 161:627-635, 1985.
[1054] Lee, J. Y., et al., Biotech. & Bioeng. 43:1146-1152
(1994).
[1055] Lei, C. et al., J Am Chem Soc 124:11242-11243, 2002.
[1056] LeJeune, K. E. and Russell, A. J. Biotech. and Bioeng. 51
(4):450-457, 1996.
[1057] LeJeune, K. E. and Russell, A. J., Biotech and Bioeng
62(6):559-665, 1999.
[1058] LeJeune, K. E. et al., Ann. NY Acad. Sci. 864:153-170,
1998a.
[1059] LeJeune, K. E. et al., Biotechnology and Bioengineering
54(2):105-114, 1997.
[1060] LeJeune, K. E. et al., Biotechnology and Bioengineering
64(2):250-254, 1999.
[1061] LeJeune, K. E., Wild, J. R., Russell, A. J. "Nerve agents
degraded by enzymatic foams" 395(6697):27-28, 1998b.
[1062] Lenz, D. E. et al., Biochim Biophys. Acta, 321:189-196,
1973.
[1063] Lewis, V. E. et al., Biochemistry 27:1591-1597, 1988.
[1064] Li, W.-S. et al., Bioorganic & Medicinal Chemistry,
9:2083-2091, 2001.
[1065] Lineweaver, H. and Burke, D. "J. Am. Chem. Soc. 56:658-666,
1934.
[1066] Little, J. S. et al., Biochem Pharmacol 38(1):23-29,
1989.
[1067] Lockridge, O. et al., Biochemistry 36:786-795, 1997.
[1068] Luo, C. et al., Biochemistry 38:9937-9947, 1999.
[1069] Main, A. R., Biochem J. 74:10-20, 1960.
[1070] Makrides, S. C. Microbiol. Rev. 60:512-538, 1996.
[1071] Martinez, M. B. et al., Biochem 35(4):1179-1186, 1996.
[1072] Martinez, M. B. et al., Biochem 40(40):11965-11974,
2001.
[1073] Masson, P. et al., J. Physiology (Paris), 92:357-362,
1999.
[1074] McClellan, J. S. et al., Eur. J. Biochem. 258:419-429,
1998.
[1075] McDaniel, S. and Wild, J. Arch. Env. Contam. Toxic.
17:189-194, 1988.
[1076] McDaniel, S. et al., J. Bact. 170:2306-2311, 1988a.
[1077] McDaniel, S., Ph.D. Dissertation, Texas A&M University,
1985.
[1078] McGuinn, W. D. et al., Fundamental and Applied Toxicology
21:38-43, 1993.
[1079] McTiernan, C. et al., Proc. Natl. Acad. Sci. 84:6682-6686,
1987.
[1080] Mehrotra, K. N., and Phokela, A., Indian J. Entomol.
34:355-358, 1974.
[1081] Millard, C. B. et al., Biochemistry 37(1):237-247, 1998.
[1082] Millard, C. B. et al., Biochemistry, 38:7032-7039, 1999.
[1083] Millard, C. B. et al., Biochemistry. 34(49):15925-15933,
1995.
[1084] Millard, C. B. et al., Biochemistry. 34(49):15925-15933.,
1995.
[1085] Miller, C. E. Ph.D. dissertation, Texas A&M University,
1992.
[1086] Moore, G. J., Trends Pharmacol. Sci., 15:124-129, 1994.
[1087] Mulbry, W. and Karns, J., J. Bacteriol. 171:6740-6746,
1989.
[1088] Mulbry, W. et al., Appl. Env. Micro. 51:926-930, 1986.
[1089] Mulchandani, A. et al., Anal Chem 70:4140-4145, 1998b.
[1090] Mulchandani, A. et al., Anal Chem 70:5042-5046, 1998c.
[1091] Mulchandani, A. et al., Biosensors & Bioelectronics
16:225-230, 2001.
[1092] Mulchandani, A. et al., Biotechnol. Progr 5:130-134,
1999a.
[1093] Mulchandani, A. et al., Biotechnology and Bioengineering
63(2):216-223, 1999b.
[1094] Mulchandani, A. et al., Electroanalysis 10:733-737,
1998a.
[1095] Mulchandani, P. et al., Biosensors & Bioelectronics
14:77-85, 1999.
[1096] Mulchandani, P. et al., Biosensors & Bioelectronics
16:433-437, 2001b.
[1097] Mulchandani, P. et al., Environ Sci Technol 35:2562-2565,
2001a.
[1098] Munnecke, D. M., Biotechnol. Bioeng. 21:2247-2261, 1979.
[1099] Munnecke, D. M., Process Biochemistry 13:14-16, 31,
1978.
[1100] Nakahigashi, K. and Inokuchi, H. Nucleic Acids Res.
18(21):6439, 1990.
[1101] Nato Army Armaments Group Project Group 31 on Non-Corrosive,
Biotechnology-Based Decontaminants for CBW Agents, Decision Sheet
AC/225(PG/31)DS(2002)2, 26 September, 2002.
[1102] Newcomb, R. D. et al., Proc. Natl. Acad. Sci. USA
94:7464-7468, 1997.
[1103] Nijs, M. et al., Appl Biochem Biotechnol 49:75-91, 1994.
[1104] Ollis, D. L. et al., Protein Engineering 5:197-211,
1992.
[1105] Omburo, G. A. et al., Biochemistry 32:9148-9155, 1993.
[1106] Omburo, G. A. et al., J. Biol. Chem. 267:13278-13283,
1992.
[1107] Pei, L. et al., Toxicology and Applied Pharmacology
124:296-301, 1994.
[1108] Petrie, E. M., Handbook of Adhesives and Sealants,
McGraw-Hill, New York, 2000.
[1109] Petrikovics, I. et al., Toxicology and Applied Pharmacology
156:56-63, 1999.
[1110] Petrikovics, I. et al., Drug Delivery 7:83-89, 2000b.
[1111] Petrikovics, I. et al., Toxicological Sciences 57:16-21,
2000a.
[1112] Phillips, J. P. et al., Proc. Natl. Acad. Sci. U.S.A.
87:1-5, 1990.
[1113] Powell, M. F. et al., Pharma. Res., 10:1268-1273, 1993.
[1114] Rainina, E. I. et al., Biosensors Bioelectronics
11:991-1000, 1996.
[1115] Rastogi, V. et al., Biochem. and Biophys. Research Comm.
241:294-296, 1997.
[1116] Raushel, Frank M., Microbiology, 5:288-295, 2002.
[1117] Raveh, L. et al., Biochemical Pharmacology 44(2):397-400,
1992.
[1118] Richins, R. D. et al., Biotechnology and Bioengineering
69(6):592-596, 2000.
[1119] Richins, R. D. et al., Nature Biotechnology 15:984-987,
1997.
[1120] Rodrigo, L. et al., Biochem J. 321:595-601, 1997.
[1121] Rogers, K. R. et al., Biotech Prog 15:517-521, 1999.
[1122] Rogers, S. G. et al., Enzymology 153: 253-292, 1987.
[1123] Rouette, H. K., Encyclopedia of Textile Finishing,
Springer-Verlag, Berlin Heidelberg, 2001.
[1124] Rowland, S. S. et al., Appl Environ Microbiol 57(2):440-444,
1991.
[1125] Rowland, S. S. et al., Appl. Microbiol. Biotechnol.
38:94-100, 1992.
[1126] Russell, R. J. et al., Analytical Chemistry 71:4909-4912,
1999.
[1127] Satriana, M. J., Hot Melt Adhesives: Manufacture and
Applications, Noyes Data Corporation, New Jersey, 1974.
[1128] Scharff, E. I. et al., Acta Cryst. D57:148-149, 2001.
[1129] Segel, I. H. Biochemical Calculations: How to Solve
Mathmatical Problems in General Biochemistry 2.sup.nd Edition, John
Wiley & Sons, Inc., New York, 1976.
[1130] Serdar, C. M. and Gibson, D. Bio/Technology 3:567-571,
1985.
[1131] Serdar, C. M. et al., Appl Environ Microbiol 44:246-249,
1982.
[1132] Serdar, C. M. et al., Bio/Technology 7:1151-1155, 1989.
[1133] Shafferman, A. et al., Biochem. J. 318:833-840, 1996.
[1134] Shim, H. et al., J. Biol. Chem. 273(28):17445-17450,
1998.
[1135] Shimazu, M. et al., Biotech and Bioeng 76(4):318-324,
2001b.
[1136] Shimazu, M. et al., Biotechnol. Prog. 17:76-80, 2001a.
[1137] Shimazu, M. et al., Biotechnology and Bioengineering
81(11):74-79, 2002.
[1138] Singh, A. K. et al., Biosensors & Bioelectronics
14:703-713, 1999.
[1139] Skeist, I., ed., Handbook of Adhesives, 3.sup.rd Ed., Van
Nostrand Reinhold, New York, 1990.
[1140] Slade, P. E., et al., "Handbook of Fiber Finish Technology,"
Marcel Dekker (1998).
[1141] Slusarski, L., ed., Fillers for the New
Millenium-Macromolecular Symposia 194, Wiley-VCH, Verlag, 2003.
[1142] Somara, S. et al., Indian J Exp Biol 40(7):774-779,
2002.
[1143] Soreq, H. et al., Proc. Natl. Acad. Sci. 87:9688-9692,
1990.
[1144] Srivastava, R. et al., Applied Environ Microbio
66(10):4366-5371, 2000.
[1145] Standard Practice for Cyclic Salt Fog/UV Exposure of Painted
Metal, (Alternation Exposures in a Fog/Dry Cabinet and a
UV/Condensation Cabinet) (ASTM D5894-96).
[1146] Standard Practice for Modifies Salt Spray (Fog) Testing.
Appendix A5: Dilute Electrolyte Cyclic Fog/Dry Test (ASTM
G85-94).
[1147] Standard Practice for Operating Light and Water-Exposure
Apparatus (Fluorescent UV-Condensation Type) for Exposure of
Nonmetallic Materials. (ASTM G53-88).
[1148] Standard Test Method for Evaluation of Painted or Coated
Specimens Subjected to Corrosive Environments (ASTM D1654-92).
[1149] Steiert, J. G. et al., Bio/Technology 7:65-68, 1989.
[1150] Steurbaut, W., DeKimpe, N., Schreyen, L., Dejonckheere, W.
Bull Soc. Chim Belg. 84:791, 1975.
[1151] Stevens, R. C. Structure Fold Des. 8(9):R177-R185, 2000.
[1152] Storkebaum, W. and Witzel, H., Forschungsber. Landes
Nordrhein-Westfalen 2523:1-23, 1975.
[1153] Sussman, J. S. et al., Science 253:872-879, 1991.
[1154] Tchelet, R. et al., Soil. Biol. Biochem. 25:1665-1671,
1993.
[1155] Tomasek, P. H., et al., J. Bacteriology, 171(7):4038-4044
(1989).
[1156] Tuovinen, K. et al., Fundam Appl. Toxicol 23:578-584,
1994.
[1157] Ugaki, M. et al., Nucl. Acid Res., 19:371-377, 1991.
[1158] Unger, T. F. The Scientist, 11 (17):20, 1997.
[1159] Urry, D. W., Prog Biophys Mol Biol 57:23-57, 1992.
[1160] van der Wal, F. J. et al., Appl. Environ. Microbiol.,
64(2):392-398, 1998.
[1161] Vanhooke, J. L. et al., Biochemistry 35:6020-6025, 1996.
[1162] Vitarius, J. A. and Sultatos, L. G. Life Sciences,
56(2):124-134, 1995.
[1163] Vontas, J. G., et al., Insect Molec. Bio., 11 (4):329-336
(2002).
[1164] Walker, A. W. and Keasling, J. D. Biotech. and Bioeng.
78(7):715-721, 2002.
[1165] Walker, B. M., ed., Handbook of Thermoplastic Elastomers,
Van Nostrand Reinhold Co., New York, 1979.
[1166] Walsh, S. B., et al., Biochem. J., 359:175-181 (2001).
[1167] Wan, E. W. and Baneyx, F. Protein Expr. Purif. 14(1):13-22,
1998.
[1168] Wang, A. A. et al., Applied and Environ. Microbio.
68(4):1684-1689, 2002.
[1169] Wang, J. et al., Biomacromolecules 2:700-705, 2001.
[1170] Warth, A. H., The Chemistry and Technology of Waxes,
Reinhold Publishing Corporation, New York, 1956.
[1171] Watkins, L. M. et al., J. Biol. Chem. 272(41):25596-25601,
1997a.
[1172] Watkins, L. M. et al., Proteins: Struct., Funct., and Gen.
29:553-561, 1997b.
[1173] Whitehouse, L. W., and Ecobichon, D. J., Pestic. Biochem.
Phys. 5:314-322, 1975.
[1174] Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic
Coatings, Science and Technology, Volume 1: Film Formation,
Components, and Appearance" (1992) John Wiley & Sons, Inc., New
York, U.S.A.
[1175] Wicks, Jr., Z. W., Jones, F. N., Pappas, S. P. "Organic
Coatings, Science and Technology, Volume 2: Applications,
Properties and Performance" (1992) John Wiley & Sons, Inc., New
York, U.S.A.
[1176] Wierdl, M. et al., Biochem. Pharm. 59:773-781, 2000.
[1177] Wild, J. R. et al., Proc. U.S. Army Chem. Res. Devel. Eng.
Center Sci. Conf. Chem. Defense Res. 18-21 Nov., p. 629-634,
1986.
[1178] Wiley, R. A. and Rich, D. H. Med. Res. Rev., 13:327-384,
1993.
[1179] Wu, C.-F. et al., Appl Microbiol Biotechnol 54:78-83,
2000b.
[1180] Wu, C.-F., Biotechnol. Prog. 17:606-611, 2001a.
[1181] Wu, C.-F., Biotechnology and Bioengineering 75(1):100-103,
2001b.
[1182] Wu, C.-F., Biotechnology and Bioengineering 77(2):212-218,
2002.
[1183] Wu, F. et al., J. Am. Chem. Soc. 122:10206-10207, 2000a.
[1184] Xu, B. et al., J. Ferment. Bioeng. 81:473-481, 1996.
[1185] Yang, F. et al., Biotechnol. Prog. 11:471-474, 1995.
[1186] Yang, Y.-C. et al., Chem. Rev. 92:1729-1743, 1992.
[1187] Yang, Y.-C. et al., J. Am. Chem. Soc. 112:6621-6627,
1990.
[1188] Yang, Y.-C. et al., J. Org. Chem. 61:8407-8413, 1996.
[1189] Yang, Z. et al., Biotechnol Bioeng 45:10-17, 1995.
[1190] Yang, Z. et al., Enzyme Microb Technol 18:82-89, 1996.
[1191] Yoshimoto, T. et al., J. Biochem. 105(3):412-416, 1989.
[1192] Zhang, Y. et al., Biotech. Bioengineering 64:221-231,
1998.
[1193] Zhongli, C. et al., Applied and Environmental Microbiology
67(10):4922-4925, 2001.
[1194] Zhu, K. Y., et al., Insect Biochem. Molec., 25(10):1129-1138
(1995).
* * * * *