U.S. patent application number 10/267999 was filed with the patent office on 2004-04-08 for imaging members.
This patent application is currently assigned to Xerox Corporation. Invention is credited to Fu, Min-Hong, Fuller, Timothy J., Prosser, Dennis J., Tong, Yuhua, VanDusen, Susan M., Yanus, John F..
Application Number | 20040067427 10/267999 |
Document ID | / |
Family ID | 32042858 |
Filed Date | 2004-04-08 |
United States Patent
Application |
20040067427 |
Kind Code |
A1 |
Tong, Yuhua ; et
al. |
April 8, 2004 |
Imaging members
Abstract
A member including for example, a substrate, a charge generating
layer, a charge transport layer comprising a synthesized mixture of
N,N,N',N'-Tetra-p-tolyl-biphenyl-4,4'-diamine
N,N'-Diphenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-p-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-m-tolyl-biphenyl-4,4'diamine
N-Phenyl-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N,N',N'-tri-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N'-m-tolyl-N-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N-m-tolyl-N'-p-tolyl-biphenyl-4,4'-diamine,
and a film forming binder
Inventors: |
Tong, Yuhua; (Webster,
NY) ; Yanus, John F.; (Webster, NY) ; Fuller,
Timothy J.; (Pittsford, NY) ; Fu, Min-Hong;
(Webster, NY) ; Prosser, Dennis J.; (Walworth,
NY) ; VanDusen, Susan M.; (Williamson, NY) |
Correspondence
Address: |
Patent Documentation Center
Xerox Corporation
Xerox Square 20th Floor
100 Clinton Ave. S.
Rochester
NY
14644
US
|
Assignee: |
Xerox Corporation
|
Family ID: |
32042858 |
Appl. No.: |
10/267999 |
Filed: |
October 8, 2002 |
Current U.S.
Class: |
430/58.8 ;
399/159; 430/58.75; 430/96 |
Current CPC
Class: |
G03G 5/061443
20200501 |
Class at
Publication: |
430/058.8 ;
430/058.75; 430/096; 399/159; 430/120 |
International
Class: |
G03G 005/047 |
Claims
What is claimed is:
1. An imaging member comprising an improved electrophotographic
imaging member comprising a flexible supporting substrate having an
electrically conductive layer, a charge blocking layer, a
charge-generating layer, a charge transporting layer comprising a
synthesized mixture of at least four different symmetric and/or
unsymmetric charge transport molecules represented by: 7 wherein
R.sub.1, R.sub.2, R.sub.3, R.sub.4 are aryl groups comprising from
about 6 to about 30 carbon atoms, or a halogen; A is a aromatic
group bridge connecting two nitrogen atoms, comprising from about 6
to about 30 carbon atoms, or a halogen.
2. An imaging member according to claim 1 wherein the charge
transport layer comprises a synthesized mixture comprising
N,N,N',N'-Tetra-p-tolyl-- biphenyl-4,4'-diamine
N,N'-Diphenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-p-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-m-tolyl-biphenyl-4,4'diamine
N-Phenyl-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N,N',N'-tri-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N'-m-tolyl-N-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine,
and N
N'-Bis-(4-butyl-phenyl)-N-m-tolyl-N'-p-tolyl-biphenyl-4,4'-diamine
dispersed in an inactive resin binder.
3. An imaging member according to claim 1 wherein the charge
transport layer is dispersed in a solvent comprising
tetrahydrofuran, toluene, methylene chloride and mixtures
thereof.
4. An imaging member according to claim 1 wherein the charge
transport layer comprises said binder in an amount of from about 20
to about 80 percent by weight.
5. An imaging member according to claim 1 wherein the charge
transport layer comprises said binder in an amount of from about 33
to about 55 percent by weight.
6. An imaging member according to claim 1 wherein the charge
transport layer comprises a charge transport material in an amount
of from about 20 to about 80 percent by weight.
7. An electrophotographic imaging member according to claim 1
wherein said film forming binder comprises a polycarbonate.
8. An electrophotographic imaging member wherein the polycarbonate
is selected from the group consisting of
poly(4,4'-isopropylidene-diphenylen- e)carbonate,
poly(2,2-bis-(4-hydroxy-3-methylphenyl)-propane, and
poly(4,4'-diphenyl-1,1'-cyclohexane carbonate).
9. An image forming device comprising at least a photoreceptor and
a charging device which charges the photoreceptor, wherein the
photoreceptor comprises a substrate, a charge generating layer, a
charge transport layer a synthesized mixture of at least four
different symmetric and/or unsymmetric charge transport molecules
represented by: 8wherein R.sub.1, R.sub.2, R.sub.3, R.sub.4 are
aryl groups comprising from 6 about to about 30 carbon atoms, or a
halogen; A is an aromatic group bridge connecting two nitrogen
atoms, with, for example, from about 6 to about 30 carbon atoms, or
a halogen, and a binder.
10. The image forming device according to claim 9 wherein the
charge transport layer is comprised of a synthesized mixture of
N,N,N',N'-Tetra-p-tolyl-biphenyl-4,4'-diamine
N,N'-Diphenyl-N,N'-di-m-tol- yl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-p-tolyl-bipheny- l-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-m-tolyl-biphenyl-4,4'diam- ine
N-Phenyl-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N,N',N'-tri-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N'-m-tolyl-N-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine,
and
N,N'-Bis-(4-butyl-phenyl)-N-m-tolyl-N'-p-tolyl-biphenyl-4,4'-diamine
e dispersed in an inactive resin binder.
11. The image forming device according to claim 9, wherein the
photoreceptor is in the form of a belt.
12. An image forming device according to claim 9, wherein the
photoreceptor is in the form of a drum.
13. An imaging member according to claim 1 wherein the
photogenerating layer has a thickness of from about 3 micrometers
to about 50 micrometers.
14. An imaging process comprising providing a member comprising a
supporting layer and a photogenerating layer, a charge transport
layer, the charge transport layer comprising a synthesized mixture
of N,N,N',N'-Tetra-p-tolyl-biphenyl-4,4'-diamine
N,N'-Diphenyl-N,N'-di-m-tol- yl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-p-tolyl-bipheny- l-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N,N'-di-m-tolyl-biphenyl-4,4'diam- ine
N-Phenyl-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N,N',N'-tri-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N'-m-tolyl-N-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N-m-tolyl-N',N'-di-p-tolyl-biphenyl-4,4'-diamine
N-(4-Butyl-phenyl)-N'-phenyl-N,N'-di-m-tolyl-biphenyl-4,4'-diamine
N,N'-Bis-(4-butyl-phenyl)-N-m-tolyl-N'-p-tolyl-biphenyl-4,4'-diamine
depositing a uniform electrostatic charge on the imaging member,
exposing the imaging member to activating radiation in image
configuration to form an electrostatic latent image, and developing
the latent image with electrostatically attractable marking
particles to form a toner image in conformance to the latent image.
Description
CROSS REFERENCE TO COPENDING APPLICATION
[0001] U.S. patent application Ser. No. 10/201,874, filed in the
names of Y. Tong, et al on Jul. 23, 2002, discloses a
photoconductive imaging member which is comprised of a supporting
substrate, and thereover a layer comprised of a charge transport
layer comprising a charge transport material containing a
dendrimeric molecular structure. The entire disclosure of this
Patent Application is incorporated herein by reference.
BACKGROUND
[0002] The present invention is generally directed to layered
imaging members, imaging apparatus, and processes thereof. More
specifically, the present invention relates in general to
electrophotographic imaging members and more specifically, to
electrophotographic imaging members having a charge transport layer
comprising mixtures of at least four different symmetric and/or
unsymmetric charge transport components which are less susceptible
to crystallization in polymer binders, and to processes for forming
images on the member.
[0003] Numerous imaging members for electrostatographic imaging
systems are known including selenium, selenium alloys, such as,
arsenic selenium alloys, layered inorganic imaging and layered
organic members. Examples of layered organic imaging members
include those containing a charge transporting layer and a charge
generating layer. Thus, for example, an illustrative layered
organic imaging member can be comprised of a conductive substrate,
overcoated with a charge generator layer, which in turn is
overcoated with a charge transport layer, and an optional overcoat
layer overcoated on the charge transport layer. In a further
"inverted" variation of this device, the charge transport layer can
be overcoated with the photogenerator layer, or charge generator
layer. Examples of generator layers that can be employed in these
members include, for example, charge generator components, such as,
selenium, cadmium sulfide, vanadyl phthalocyanine, x-metal free
phthalocyanine, benzimidazole perylent (BZP), hydroxygallium
phthalocyanine (HOGaPc), chlorogallium phthalocyanine, and trigonal
selenium dispersed in binder resin, while examples of transport
layers include dispersions of various diamines, reference for
example, U.S. Pat. No. 4,265,990, the disclosure of which is
incorporated herein by reference in its entirety.
[0004] One problem encountered with photoreceptors comprising a
charge generating layer and the charge transport layer is that the
charge transport component consisting of small organic molecules
dissolved in a polymer binder can result in the small molecule
crystallizing with increasing concentrations in the polymer binder.
This crystallization can result in non-uniformity of images,
increased residual voltages, and the early development of dynamic
fatigue charge transport layer cracking during, for example,
photoreceptor belt machine function. High quality images are
essential for digital copiers, duplicators, printers, and facsimile
machines, particularly laser exposure machines that demand high
resolution images.
[0005] There continues to be a need for improved imaging members,
and improved imaging systems utilizing such members. Additionally,
there continues to be a need for imaging members with improved
lifetimes and mechanical function, and which members are economical
to prepare and retain their properties over extended periods of
time.
REFERENCES
[0006] In U.S. Pat. No. 4,410,616, to Griffiths, et al., issued
Oct. 18, 1983, there is disclosed an improved ambi-polar
photoresponsive device useful in imaging systems for the production
of positive images, from either positive or negative originals,
which device is comprised of: (a) supporting substrate, (b) a first
photogenerating layer, (c) a charge transport layer, and (d) a
second photogenerating layer, wherein the charge transport layer is
comprised of a highly insulating polymer resin having dissolved
therein components of an electrically active material of
N,N'-diphenyl-N,N'-bis("X substituted"
phenyl)-[1,1,-biphenyl]-4,4'-diami- ne wherein X is selected from
the group consisting of alkyl and halogen.
[0007] U.S. Pat. No. 4,806,443 describes a charge transport layer
including a polyether carbonate (PEC) obtained from the
condensation of
N,N'-diphenyl-N,N'bis(3-hydroxyphenyl)-[1,1'-biphenyl]-4,4'-diamine
and diethylene glycol bischloroformate. U.S. Pat. No. 4,025,341
similarly describes a photoreceptor that includes a charge
transport layer consisting of a mixture of polycarbonate and a low
molecular weight photoconductive polymer from the condensation of a
tertiary amine with an aldehyde. What is still desired is an
improved material for a charge transport layer of an imaging member
that exhibits excellent performance properties the same as or
better than existing materials discussed above.
[0008] The entire disclosures of these patents are incorporated
herein by reference.
BRIEF SUMMARY
[0009] Disclosed herein is an improved electrophotographic imaging
member comprising a supporting substrate having an electrically
conductive layer,
[0010] a charge blocking layer,
[0011] an optional adhesive layer,
[0012] a charge-generating layer,
[0013] a charge transporting layer comprising a synthesized mixture
of at least four different symmetric and/or unsymmetric charge
transport molecules represented by: 1
[0014] wherein R.sub.1, R.sub.2, R.sub.3, R.sub.4 are aryl groups
with, for example, from about 6 to about 30 carbon atoms, such as
phenyl, tolyl, xylyl, butylphenyl, chlorophenyl, fluorophenyl,
naphthyl, and the like; A is a aromatic group bridge connecting two
nitrogen atoms, with, for example, from about 6 to about 30 carbon
atoms, such as phenylene, biphenyl, bitolyl, terphenyl, and the
like, and wherein in embodiments the aforementioned groups may be
substituted with, for example, halogen, and a film forming
binder.
[0015] Further disclosed herein is an improved electrophotographic
imaging member for which photoinduced discharge characteristic
(PIDC) curves do not change with time or repeated use.
[0016] By the use of the disclosed synthesized mixture of symmetric
and/or unsymmetric charge transport molecules in the charge
transport layer of the present invention, a charge transport layer
of an imaging member is achieved that has excellent hole
transporting performance and wear resistance, and that is able to
be coated onto the imaging member structure using known
conventional methods.
[0017] Aspects illustrated herein relate to;
[0018] a substrate,
[0019] a charge blocking layer,
[0020] an optional adhesive layer,
[0021] a charge generating layer,
[0022] a charge transport layer comprising: a synthesized mixture
of at least four different symmetric and/or unsymmetric charge
transport molecules.
[0023] The disclosed mixture of symmetric and/or unsymmetric charge
transport molecules can be readily synthesized by the preparative
process illustrated, for example, in Scheme I: 2
[0024] wherein R.sub.1, R.sub.2, R.sub.3, R.sub.4 are aryl groups
with, for example, from about 6 to about 30 carbon atoms, such as
phenyl, tolyl, xylyl, butylphenyl, chlorophenyl, fluorophenyl,
naphthyl, and the like; A is a aromatic group bridge connecting two
nitrogen atoms, with, for example, from about 6 to about 30 carbon
atoms, such as phenylene, biphenyl, bitolyl, terphenyl, and the
like, and wherein in embodiments the aforementioned groups may be
substituted with, for example, halogen.
[0025] As indicated in Scheme I, the mixture of symmetric and/or
unsymmetric charge transport molecules are prepared by, for
example, an Ullmann condensation of the diarylamine intermediate
with diiodide intermediate. The reaction is generally accomplished
in an inert solvent, such as dodecane, tridecane, mesitylene,
xylene, toluene, and the like, at a temperature ranging from about
100 degrees Celsius to about 280 degrees Celsius, and in
embodiments from about 110 degrees Celsius to about 250 degrees
Celsius. Any suitable catalysts for Ullmann condensation, including
copper powder, cuprous iodide, cupric sulfate,
tris(dibenzylideneacetone)dipalladium(0), and the like, may be
employed for the process of the present invention. The reaction can
be accelerated with an addition, in an effective amount, of a base
such as an alkaline metal hydroxide, or carbonate including
potassium hydroxide, potassium carbonate, sodium hydroxide, sodium
carbonate, and the like. The product is isolated by known means,
for example, by filtration, chromatography and distillation.
[0026] The imaging member may be imaged by depositing a uniform
electrostatic charge on the imaging member, exposing the imaging
member to activating radiation in image configuration to form an
electrostatic latent image, and developing the latent image with
electrostatically attractable marking particles to form a toner
image in conformance to the latent image.
[0027] Any suitable substrate may be employed in the imaging member
of this invention. The substrate may be opaque or substantially
transparent, and may comprise any suitable material having the
requisite mechanical properties. Thus, for example, the substrate
may comprise a layer of insulating material including inorganic or
organic polymeric materials, such as, MYLAR.RTM. a commercially
available polymer, MYLAR.RTM. coated titanium, a layer of an
organic or inorganic material having a semiconductive surface
layer, such as, indium, tin, oxide, aluminum, titanium and the
like, or exclusively be made up of a conductive material, such as,
aluminum, chromium, nickel, brass and the like. The substrate may
be flexible, seamless or rigid and may have a number of many
different configurations, such as, for example, a plate, a drum, a
scroll, an endless flexible belt, and the like. In one embodiment,
the substrate is in the form of a seamless flexible belt. The back
of the substrate, particularly when the substrate is a flexible
organic polymeric material, may optionally be coated with a
conventional anticurl layer.
[0028] The thickness of the substrate layer depends on numerous
factors, including mechanical performance and economic
considerations. The thickness of this layer may range from about 65
micrometers to about 3,000 micrometers, and in embodiments from
about 75 micrometers to about 1,000 micrometers for optimum
flexibility and minimum induced surface bending stress when cycled
around small diameter rollers, for example, 19 millimeter diameter
rollers. The surface of the substrate layer is preferably cleaned
prior to coating to promote greater adhesion of the deposited
coating composition. Cleaning may be effected by, for example,
exposing the surface of the substrate layer to plasma discharge,
ion bombardment, and the like methods.
[0029] Electron blocking layers for positively charged
photoreceptors allow holes from the imaging surface of the
photoreceptor to migrate toward the conductive layer. For
negatively charged photoreceptors, any suitable charge blocking
layer capable of forming a barrier to prevent hole injection from
the conductive layer to the opposite photoconductive layer may be
utilized. The charge blocking layer may include polymers such as
polyvinylbutyral, epoxy resins, polyesters, polysiloxanes,
polyamides, polyurethanes, and the like, or may be nitrogen
containing siloxanes or nitrogen containing titanium compounds such
as trimethoxysilyl propylene diamine, hydrolyzed trimethoxysilyl
propyl ethylene diamine, N-beta-(aminoethyl) gamma-amino-propyl
trimethoxy silane, isopropyl 4-aminobenzene sulfonyl,
di(dodecylbenzene sulfonyl) titanate, isopropyl
di(4-aminobenzoyl)isostearoyl titanate, isopropyl
tri(N-ethylamino-ethylamino)titanate, isopropyl trianthranil
titanate, isopropyl tri(N,N-dimethyl-ethylamino)titanate,
titanium-4-amino benzene sulfonate oxyacetate, titanium
4-aminobenzoate isostearate oxyacetate,
[H.sub.2N(CH.sub.2).sub.4]CH.sub.3Si(OCH.sub.3).sub.2,
gamma-aminobutyl) methyl diethoxysilane, and
[H.sub.2N(CH.sub.2).sub.3]CH.sub.3Si(OCH.sub.3- ).sub.2,
(gamma-aminopropyl)-methyl diethoxysilane, as disclosed in U.S.
Pat. Nos. 4,338,387, 4,286,033 and 4,291,110. Other suitable charge
blocking layer polymer compositions are also described in U.S. Pat.
No. 5,244,762. These include vinyl hydroxyl ester and vinyl hydroxy
amide polymers, wherein the hydroxyl groups have been partially
modified to benzoate and acetate esters which modified polymers are
then blended with other unmodified vinyl hydroxy ester and amide
unmodified polymers. An example of such a blend is a 30 mole
percent benzoate ester of poly (2-hydroxyethyl methacrylate)
blended with the parent polymer poly (2-hydroxyethyl methacrylate).
Still, other suitable charge blocking layer polymer compositions
are described in U.S. Pat. No. 4,988,597. These include polymers
containing an alkyl acrylamidoglycolate alkyl ether repeat unit. An
example of such an alkyl acrylamidoglycolate alkyl ether containing
polymer is the copolymer poly(methyl acrylamidoglycolate methyl
ether-co-2-hydroxyethyl methacrylate). The disclosures of the U.S.
Patents are incorporated herein by reference in their entirety.
[0030] The blocking layer is continuous and may have a thickness of
less than about 10 micrometers because greater thicknesses may lead
to undesirably high residual voltage. In embodiments, a blocking
layer of from about 0.005 micrometers to about 1.5 micrometers
facilitates charge neutralization after the exposure step and
optimum electrical performance is achieved. The blocking layer may
be applied by any suitable conventional technique such as spraying,
dip coating, draw bar coating, gravure coating, silk screening, air
knife coating, reverse roll coating, vacuum deposition, chemical
treatment, and the like. For convenience in obtaining thin layers,
the blocking layer is in embodiments applied in the form of a
dilute solution, with the solvent being removed after deposition of
the coating by conventional techniques, such as, by vacuum,
heating, and the like. Generally, a weight ratio of blocking layer
material and solvent of from about 0.05:100 to about 5:100 is
satisfactory for spray coating.
[0031] If desired an optional adhesive layer may be formed on the
substrate. Typical materials employed in an undercoat layer
include, for example, polyesters, polyamides, poly(vinyl butyral),
poly(vinyl alcohol), polyurethane and polyacrylonitrile, and the
like. Typical polyesters include, for example, VITEL.RTM. PE100 and
PE200 available from Goodyear Chemicals, and MOR-ESTER 49,000.RTM.
available from Norton International. The undercoat layer may have
any suitable thickness, for example, of from about 0.001
micrometers to about 30 micrometers. A thickness of from about 0.1
micrometers to about 3 micrometers is used in a specific
embodiment. Optionally, the undercoat layer may contain suitable
amounts of additives, for example, of from about 1 weight percent
to about 10 weight percent, of conductive or nonconductive
particles, such as, zinc oxide, titanium dioxide, silicon nitride,
carbon black, and the like, to enhance, for example, electrical and
optical properties. The undercoat layer can be coated onto a
supporting substrate from a suitable solvent. Typical solvents
include, for example, tetrahydrofuran, dichloromethane, xylene,
ethanol, methyl ethyl ketone, and mixtures thereof.
[0032] The components of the photogenerating layer comprise
photogenerating particles, for example, of Type V hydroxygallium
phthalocyanine, x-polymorph metal free phthalocyanine, or
chlorogallium phthalocyanine photogenerating pigments dispersed in
a matrix comprising an arylamine hole transport molecules and
certain selected electron transport molecules. Type V
hydroxygallium phthalocyanine is well known and has X-ray powder
diffraction (XRPD) peaks at, for example, Bragg angles (2
theta+/-0.2.degree.) of 7.4, 9.8, 12.4, 16.2, 17.6, 18.4, 21.9,
23.9, 25.0, 28.1, with the highest peak at 7.4 degrees. The X-ray
powder diffraction traces (XRPDs) were generated on a Philips X-Ray
Powder Diffractometer Model 1710 using X-radiation of CuK-alpha
wavelength (0.1542 nanometer). The Diffractometer was equipped with
a graphite monochrometer and pulse-height discrimination system.
Two-theta is the Bragg angle commonly referred to in x-ray
crystallographic measurements. I (counts) represents the intensity
of the diffraction as a function of Bragg angle as measured with a
proportional counter. Type V hydroxygallium phthalocyanine may be
prepared by hydrolyzing a gallium phthalocyanine precursor
including dissolving the hydroxygallium phthalocyanine in a strong
acid and then reprecipitating the resulting dissolved precursor in
a basic aqueous media; removing any ionic species formed by washing
with water; concentrating the resulting aqueous slurry comprising
water and hydroxygallium phthalocyanine as a wet cake; removing
water from the wet cake by drying; and subjecting the resulting dry
pigment to mixing with a second solvent to form the Type V
hydroxygallium phthalocyanine. These pigment particles in
embodiments have an average particle size of less than about 5
micrometers.
[0033] The photogenerating layer containing photoconductive
compositions and/or pigments and the resinous binder material
generally ranges in thickness of from about 0.1 micrometer to about
5.0 micrometers, and in embodiments have a thickness of from about
0.3 micrometers to about 3 micrometers. The photogenerating layer
thickness is generally related to binder content. Thus, for
example, higher binder content of 30 compositions generally require
thicker layers for photogeneration. Of course, thickness outside
these ranges can be selected providing the objectives of the
present invention are achieved.
[0034] The active charge transport layer may comprise any suitable
transparent organic polymer or non-polymeric material capable of
supporting the injection of photo-generated holes and electrons
from the charge generating layer and allowing the transport of
these holes or electrons through the organic layer to selectively
discharge the surface charge. The active charge transport layer not
only serves to transport holes or electrons, but also protects the
photoconductive layer from abrasion or chemical attack and
therefore extends the operating life of the photoreceptor imaging
member. The charge transport layer should exhibit negligible, if
any, discharge when exposed to a wavelength of light useful in
xerography, for example, 4,000 Angstroms to 8,000 Angstroms.
Therefore, the charge transport layer is substantially transparent
to radiation in a region in which the photoconductor is to be used.
Thus, the active charge transport layer is a substantially
non-photoconductive material which supports the injection of
photogenerated holes or electrons from the generating layer. The
active transport layer is normally transparent when exposure is
effected through the active layer to ensure that most of the
incident radiation is utilized by the underlying charge generating
layer for efficient photogeneration. The charge transport layer in
conjunction with the generating layer is a material which is an
insulator to the extent that an electrostatic charge placed on the
transport layer is not conductive in the absence of illumination,
that is, does not discharge at a rate sufficient to prevent the
formation and retention of an electrostatic latent image
thereon.
[0035] In embodiments, a transport layer employed in the
electrically operative layer in the photoconductor embodiment of
this invention comprises from about 25 to about 75 percent by
weight of at least one charge transporting aromatic amine compound,
and about 75 to about 25 percent by weight of a polymeric film
forming resin in which the aromatic amine is soluble. In a specific
embodiment, the charge transport layer comprises a synthesized
mixture of at least four different symmetric and/or unsymmetric
charge transport molecules Examples of charge transporting aromatic
amines for charge transport layer(s) capable of supporting the
injection of photogenerated holes of a charge generating layer and
transporting the holes through the charge transport layer include
N,N'-diphenyl-N,N'-di(3-methylphenyl)-1,1-biphenyl-4,4'-diamine,
(m-TBD).
[0036] Any suitable arylamine hole transporter molecules may be
utilized in this invention. In embodiments an arylamine hole charge
transport molecule may be represented by: 3
[0037] wherein X is selected from the group consisting of alkyl and
halogen. The alkyl, for example, may contain from about 1 to about
10 carbon atoms, and in embodiments from about 1 to about 5 carbon
atoms. Typical aryl amines include, for example,
N,N'-diphenyl-N,N'-bis(alkylphe- nyl)-1,1-biphenyl-4,4'-diamine
wherein alkyl is selected from the group consisting of methyl,
ethyl, propyl, butyl, propyl, hexyl, and the like; and
N,N'-diphenyl-N,N'-bis(halophenyl)-1,1'-biphenyl-4,4'-diamine,
wherein the halo substituent is, in embodiments, a chloro
substituent. Other specific examples of aryl amines include,
2,7-bis(phenyl-3-methylph- enyl amino)fluorene, tritolylamine,
N,N'-bis(3,4 dimethylphenyl)-N"(1-biph- enyl) amine, 2-bis
((4'-methylphenyl) amino-p-phenyl) 1,1-diphenyl ethylene,
1-bisphenyl-diphenylamino-1-propene, and the like.
[0038] Any suitable inactive thermoplastic resin binder soluble in
methylene chloride or other suitable solvent may be employed in the
process of this invention to form the thermoplastic polymer matrix
of the imaging member. Typical inactive resin binders soluble in
methylene chloride include polycarbonate resin, polyvinylcarbazole,
polyester, polyarylate, polyacrylate, polyether, polysulfone,
polystyrene, polyamide, and the like. Molecular weights can vary
from about 20,000 to about 150,000.
[0039] Any suitable and conventional technique may be utilized to
mix and thereafter apply the charge transport layer coating mixture
to the charge generating layer. Typical application techniques
include spraying, dip coating, roll coating, wire wound rod
coating, and the like. Drying of the deposited coating may be
effected by any suitable conventional technique such as oven
drying, infra red radiation drying, air drying and the like.
[0040] Generally, the thickness of the charge transport layer is
between from about 10 to about 50 micrometers, but thicknesses
outside this range can also be used. The hole transport layer
should be an insulator to the extent that the electrostatic charge
placed on the hole transport layer is not conducted in the absence
of illumination at a rate sufficient to prevent formation and
retention of an electrostatic latent image thereon. In general, the
ratio of the thickness of the hole transport layer to the charge
generator layer is, in embodiments, maintained from about 2:1 to
about 200:1 and in some instances as great as about 400:1.
[0041] In embodiments, the electrically inactive resin materials
are polycarbonate resins, which have a molecular weight from about
20,000 to about 150,000, more specifically from about 50,000 to
about 120,000. Most specifically, as the electrically inactive
resin material is poly(4,4'-dipropylidene-diphenylene carbonate)
with a molecular weight of from about 35,000 to about 40,000,
available as LEXAN 145 from General Electric Company;
poly(4,4'-isopropylidene-diphenylene carbonate) with a molecular
weight of from about 40,000 to about 45,000, available as LEXAN 141
from the General Electric Company; a polycarbonate resin having a
molecular weight of from about 50,000 to about 120,000, available
as MAKROLON from Farbenfabricken Bayer A.G. and a polycarbonate
resin having a molecular weight of from about 20,000 to about
50,000 available as MERLON from Mobay Chemical Company. Methylene
chloride solvent is a desirable component of the charge transport
layer coating mixture for adequate dissolving of all the components
and for its low boiling point.
[0042] The charge transport layer material may also include
additional additives used for their known conventional functions as
recognized by practitioners in the art. Such as, for example,
antioxidants, leveling agents, surfactants, wear resistant
additives, such as, polytetrafluoroethylene (PTFE) particles, light
shock resisting or reducing agents, and the like.
[0043] The solvent system can be included as a further component of
the charge transport layer material. Conventional binder resins for
charge transport layers have utilized the use of methylene chloride
as a solvent to form a coating solution, for example, that renders
the coating suitable for application via dip coating. However,
methylene chloride has environmental concerns that usually require
this solvent to have special handling and results in the need for
more expensive coating and clean-up procedures. Currently, however,
binder resins can be dissolved in a solvent system that is more
environmentally friendly than methylene chloride, thereby enabling
the charge transport layer to be formed less expensively than with
some conventional polycarbonate binder resins. In embodiments, a
solvent system for use with the charge transport layer material of
the present invention comprises tetrahydrofuran, toluene, and the
like.
[0044] The total solid to total solvents of the coating material
may, for example, be around from about 10:90 weight percent to
about 30:70 weight percent, and in embodiments from about 15:85
weight percent to about 25:75 weight percent.
[0045] The components may be added together in any suitable order,
although the solvent system is in embodiments added to the vessel
first. The transport molecule binder polymer may be dissolved
together, although each is in embodiments dissolved separately and
then combined with the solution in the vessel. Once all of the
components of the charge transport layer material have been added
to the vessel, the solution may be mixed to form a uniform coating
composition.
[0046] The charge transport layer solution is applied to the
photoreceptor structure. More in particular, the charge transport
layer is formed upon a previously formed layer of the photoreceptor
structure. In embodiments, the charge transport layer may be formed
upon a charge generating layer. Any suitable and conventional
techniques may be utilized to apply the charge transport layer
coating solution to the photoreceptor structure. Typical
application techniques include, for example, spraying, dip coating,
extrusion coating, roll coating, wire wound rod coating, draw bar
coating, and the like.
[0047] Any suitable multilayer photoreceptor may be employed in the
imaging member of this invention. The charge generating layer and
charge transport layer as well as the other layers may be applied
in any suitable order to produce either positive or negative
charging photoreceptors. For example, the charge generating layer
may be applied prior to the charge transport layer, as illustrated
in U.S. Pat. No. 4,265,990, or the charge transport layer may be
applied prior to the charge generating layer, as illustrated in
U.S. Pat. No. 4,346,158, the entire disclosures of these patents
being incorporated herein by reference. In embodiments, however,
the charge transport layer is employed upon a charge generating
layer, and the charge transport layer may optionally be overcoated
with an overcoat and/or protective layer.
[0048] The following examples are provided to further define
various species of the present invention, it being noted that these
examples are intended to illustrate and not limit the scope of the
present invention
EXAMPLE I
[0049] A charge transport component mixture was prepared by
combining. 0.25 mole of di-4-tolylamine, 0.25 mole of
N-3-methylphenyl,N'-phenylamin- e, 0.25 mole of
N-n-butylphenyl,N'-4-methylphenylamine, 0.25 mole of
N-n-butylphenyl,N'-3-methylphenylamine and 0.5 mole of
1,4-diiodobiphenyl. The components were heated to 240 degrees
Celsius for 18 hours under argon gas flow, using copper and
potassium carbonate as catalysts. The reaction mixture was then
cooled to room temperature. Toluene was used to extract the
product. The product was purified by Filtrol and then carbon black.
The final product was a kind of white powder with very good
solubility in THF, methylene chloride, toluene. This product
consists of 10 different charge transport molecules. The synthesis
route is shown in Scheme 1. 456
EXAMPLE II
[0050] Three photoreceptors were prepared by forming coatings using
conventional techniques on a substrate comprising vacuum deposited
titanium layer on a polyethylene terephthalate film. The first
coating was a siloxane barrier layer formed from hydrolyzed
gamma-aminopropyltriethoxysilane having a thickness of 0.005
micrometers (50 Angstroms). The barrier layer coating composition
was prepared by mixing 3-aminopropyltriethoxysilane (available from
PCR Research Center Chemicals of Florida) with ethanol in a 1:50
volume ratio. The coating composition was applied by a multiple
clearance film applicator to form a coating having a wet thickness
of 0.5 millimeter. The coating was then allowed to dry for 5
minutes at room temperature, followed by curing for 10 minutes at
110 degrees Centigrade in a forced air oven. The second coating was
an adhesive layer of polyester resin (49,000, available from E.I.
duPont de Nemours & Co.) having a thickness of 0.005
micrometers (50 Angstroms). The second coating composition was
applied using a 0.5 millimeter bar and the resulting coating was
cured in a forced air oven for 10 minutes. This adhesive interface
layer was thereafter coated with a photogenerating layer containing
40 percent by volume hydroxygallium phthalocyanine and 60 percent
by volume of a block copolymer of styrene (82 percent)/4-vinyl
pyridine (18 percent) having a weight average molecular weight of
11,000. This photogenerating coating composition was prepared by
dissolving 1.5 grams of the block copolymer of styrene/4-vinyl
pyridine in 42 milliliters of toluene. To this solution was added
1.33 grams of hydroxygallium phthalocyanine and 300 grams of 1/8
inch diameter stainless steel shot. This mixture was then placed on
a ball mill for 20 hours. The resulting slurry was thereafter
applied to the adhesive interface with a Bird applicator to form a
layer having a wet thickness of 0.25 millimeter. This layer was
dried at 135 degrees Celsius for 5 minutes in a forced air oven to
form a photogenerating layer having a dry thickness 0.4
micrometers. The next applied layer was a transport layer which was
formed by using a Bird coating applicator to apply a solution
containing 50 weight percent poly(4,4'-diphenyl-1,1'-cyc- lohexane
carbonate)-400, with a weight average molecular weight of 40,000
and 50 weight percent of the new charge transport layer material
mixture dissolved in THF/toluene mixture. The devices were oven
dried at 100 degrees Celsius for 30 minutes.
[0051] The devices containing the newly mixed charge transport
layer materials were scanned in a drum scanner. The charge
transport was good and there was no cycle up in 10 k scanning
cycles. With the above imaging members, it is believed that there
can be generated images of excellent resolution with minimal or no
background deposits. These imaging members are reusable for
extended time periods.
[0052] Although the invention has been described with reference to
specific preferred embodiments, it is not intended to be limited
thereto, rather those having ordinary skill in the art will
recognize that variations and modifications including equivalents,
substantial equivalents, similar equivalents, and the like may be
made therein which are within the spirit of the invention and
within the scope of the claims.
* * * * *