U.S. patent application number 10/663914 was filed with the patent office on 2004-03-25 for perpendicular magnetic recording medium and magnetic recording apparatus.
This patent application is currently assigned to KABUSHIKI KAISHA TOSHIBA. Invention is credited to Hikosaka, Takashi, Nakamura, Futoshi, Ogiwara, Hideo, Oikawa, Soichi.
Application Number | 20040058197 10/663914 |
Document ID | / |
Family ID | 26596331 |
Filed Date | 2004-03-25 |
United States Patent
Application |
20040058197 |
Kind Code |
A1 |
Nakamura, Futoshi ; et
al. |
March 25, 2004 |
Perpendicular magnetic recording medium and magnetic recording
apparatus
Abstract
A soft magnetic laminate layer is arranged between a nonmagnetic
substrate and a perpendicular magnetic recording layer so as to
provide a perpendicular magnetic recording medium low in noise and
capable of a high density recording. The soft magnetic laminate
layer comprises a soft magnetic layer having a thickness not larger
than 500 .ANG. and a nonmagnetic layer, comprises a first soft
magnetic layer and a second soft magnetic layer differing from the
first soft magnetic layer in the crystal structure, or comprises a
layer of a granular structure consisting of magnetic particles and
a nonmagnetic matrix and a soft magnetic layer.
Inventors: |
Nakamura, Futoshi;
(Yamato-shi, JP) ; Hikosaka, Takashi; (Tokyo,
JP) ; Oikawa, Soichi; (Yokohama-shi, JP) ;
Ogiwara, Hideo; (Tachikawa-shi, JP) |
Correspondence
Address: |
PILLSBURY WINTHROP, LLP
P.O. BOX 10500
MCLEAN
VA
22102
US
|
Assignee: |
KABUSHIKI KAISHA TOSHIBA
Kawasaki-shi
JP
|
Family ID: |
26596331 |
Appl. No.: |
10/663914 |
Filed: |
September 17, 2003 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10663914 |
Sep 17, 2003 |
|
|
|
09808426 |
Mar 15, 2001 |
|
|
|
Current U.S.
Class: |
428/830 ;
428/828.1; G9B/5.241 |
Current CPC
Class: |
G11B 2005/0029 20130101;
G11B 5/66 20130101; Y10S 428/90 20130101; Y10T 428/265 20150115;
Y10T 428/24942 20150115 |
Class at
Publication: |
428/694.0MM ;
428/694.00R |
International
Class: |
G11B 005/66 |
Foreign Application Data
Date |
Code |
Application Number |
Jul 19, 2000 |
JP |
2000-219447 |
Sep 12, 2000 |
JP |
2000-275890 |
Claims
What is claimed is:
1. A magnetic recording medium comprising: a nonmagnetic substrate;
a perpendicular magnetic recording layer for recording signal; and
a soft magnetic laminate layer formed between said nonmagnetic
substrate and said perpendicular magnetic recording layer for
recording signal, and including a soft magnetic layer which has a
thickness not larger than 500 .ANG. and a nonmagnetic layer.
2. The magnetic recording medium according to claim 1, wherein the
thickness of said nonmagnetic layer is not larger than 1.5 times
the thickness of said soft magnetic layer.
3. The magnetic recording medium according to claim 1, wherein the
value of the saturation magnetization per layer of said soft
magnetic layer is not larger than 90% of the saturation
magnetization value under a bulk state.
4. The magnetic recording medium according to claim 1, wherein said
soft magnetic layer contains as a main component at least one
element selected from the group consisting of Fe, Co and Ni.
5. The magnetic recording medium according to claim 1, wherein said
nonmagnetic layer is formed of at least one element selected from
the group consisting of B, C, Ti, Si, Al, Cr, Ru, Zr, Nb, and
Ta.
6. The magnetic recording medium according to claim 1, wherein said
soft magnetic layer is formed of an Fe--Al--Si alloy layer.
7. The magnetic recording medium according to claim 1, wherein said
perpendicular magnetic recording layer is formed of at least one
layer of a Co--Pt--Cr--O mainly containing magnetic thin film.
8. A magnetic recording medium comprising: a nonmagnetic substrate;
a perpendicular magnetic recording layer; a soft magnetic laminate
layer formed between the nonmagnetic substrate and the
perpendicular magnetic medium, and including a first soft magnetic
layer, and a second soft magnetic layer laminated on said first
soft magnetic layer and differing from said first soft magnetic
layer in the crystal structure.
9. The magnetic recording medium according to claim 8, wherein each
of said first and second soft magnetic layers contains as a main
component at least one element selected from the group consisting
of Fe, Co and Ni.
10. A magnetic recording medium comprising: a nonmagnetic
substrate; a perpendicular magnetic recording layer; a soft
magnetic laminate layer formed between the nonmagnetic substrate
and the perpendicular magnetic medium, and including a soft
magnetic granular layer formed of a nonmagnetic matrix and soft
magnetic metal particles dispersed in said matrix, and a soft
magnetic layer.
11. A magnetic recording medium according to claim 10, wherein said
soft magnetic granular layer is formed on said perpendicular
magnetic recording layer, and said soft magnetic layer formed on
said soft magnetic granular layer.
12. The magnetic recording medium according to claim 10, wherein
said the magnetic particles of soft magnetic layer contains as a
main component at least one element selected from the group
consisting of Fe, Co and Ni.
13. The magnetic recording medium according to claim 10, wherein
said nonmagnetic layer is formed of at least one element selected
from the group consisting of B, C, Ti, Si, Al, Cr, Ru, Zr, Nb and
Ta.
14. A magnetic recording apparatus, comprising: a magnetic
recording medium having a nonmagnetic substrate, a perpendicular
magnetic recording layer for recording signal, and a soft magnetic
laminate layer formed between said nonmagnetic substrate and said
perpendicular magnetic recording layer for recording signal, and
including a soft magnetic layer which has a thickness not larger
than 500 .ANG. and a nonmagnetic layer; driving means supporting
and rotating the perpendicular magnetic recording medium; a
magnetic head including an element for recording information in the
perpendicular magnetic recording medium and another element for
reading the recorded information; and a carriage assembly
supporting the magnetic head such that the magnetic head is movable
relative to the magnetic recording medium.
15. A magnetic recording apparatus comprising: a magnetic recording
medium having a nonmagnetic substrate, a perpendicular magnetic
recording layer, a soft magnetic laminate layer formed between the
nonmagnetic substrate and the perpendicular magnetic medium, and
including a first soft magnetic layer, and a second soft magnetic
layer laminated on said first soft magnetic layer and differing
from said first soft magnetic layer in the crystal structure;
driving means supporting and rotating the perpendicular magnetic
recording medium; a magnetic head including an element for
recording information in the perpendicular magnetic recording
medium and another element for reading the recorded information;
and a carriage assembly supporting the magnetic head and making the
magnetic head be movable relative to the magnetic recording
medium.
16. A magnetic recording apparatus comprising: a magnetic recording
medium having a nonmagnetic substrate, a perpendicular magnetic
recording layer, a soft magnetic laminate layer formed between the
nonmagnetic substrate and the perpendicular magnetic medium, and
including a soft magnetic granular layer formed of a nonmagnetic
matrix and soft magnetic metal particles dispersed in said matrix,
and a soft magnetic layer; driving means supporting and rotating
the perpendicular magnetic recording medium; a magnetic head
including an element for recording information in the perpendicular
magnetic recording medium and another element for reading the
recorded information; and a carriage assembly supporting the
magnetic head and making the magnetic head be movable relative to
the magnetic recording medium.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is based upon and claims the benefit of
priority from the prior Japanese Patent Applications No.
2000-219447, filed Jul. 19, 2000; and No. 2000-275890, filed Sep.
12, 2000, the entire contents of both of which are incorporated
herein by reference.
BACKGROUND OF THE INVENTION
[0002] The present invention relates to a magnetic recording
apparatus and a magnetic recording medium used in the magnetic
recording apparatus.
[0003] In recent years, a magnetic recording medium come to be
required in higher recording density, particularly, the fields of
the hard disc drive (HDD) and the digital voice tape recorder
(DVTR) in accordance with progress in the performance of a
computer, and use of the digital system and progress in the quality
of the image-voice.
[0004] For example, if it is intended to achieve a high recording
density by making finer the recording bits in the ordinary
longitudinal recording, that the coercive force is made higher than
the thermal decay of the recording magnetization and a problem that
the coercive force is too high to record is generated. In order to
avoid the problem, in recent years, a perpendicular magnetic
recording system using a perpendicular magnetic recording layer
having a perpendicular anisotropy is proposed.
[0005] In the perpendicular magnetic recording system, a
perpendicular magnetic recording medium comprising a magnetic
recording layer having an easy axis of magnetization in a thickness
(perpendicular) direction of the magnetic recording medium. Signals
can be recorded by a perpendicular magnetic recording head with a
strong magnetization distribution in the thickness direction to the
magnetic recording medium so as to magnetize the perpendicular
magnetic recording medium in the thickness direction and to allow
the magnetization to remain.
[0006] A known perpendicular magnetic recording medium includes a
single layer structure in which a single perpendicular magnetic
recording layer is formed on a substrate and a double layer
structure in which a soft magnetic underlying layer of a high
permeability and a perpendicular magnetic recording layer are
formed on a substrate. As disclosed in, for example, Japanese
Patent Disclosure (Kokai) No. 52-78403, it is known to the art that
the mutual function between the magnetic head and the soft magnetic
underlying film allows the perpendicular magnetic recording medium
of the double layer structure to exhibit excellent recording
characteristics, compared with the perpendicular magnetic recording
medium of the single layer structure.
[0007] It is desirable for the soft magnetic underlying layer to
exhibit a high permeability and a high saturated magnetic flux
density. However, if the recording test is conducted by using the
perpendicular magnetic recording medium of the double layer
structure, a spike-like noise is observed. The spike-like noise is
not observed when it comes to the perpendicular magnetic recording
medium of the single layer structure consisting of the
perpendicular magnetization film alone. As disclosed in Japanese
Patent Publication (Kokoku) No. 3-53686, the noise is not uniformly
generated within the medium. It is known to the art that the
spike-like noise is generated in the portion where a domain wall is
present, and is not generated in the portion where a domain wall is
not present. The noise, which is called a Barkhausen noise, is
derived from the phenomenon that the domain wall migration takes
place irreversibly. Generation of the Barkhausen noise can be
suppressed by employing the construction that permits suppressing
the domain wall migration within the soft magnetic film, which is
positioned below the perpendicular magnetization film, or permits
completely eliminating the domain wall.
[0008] The noise generated within the magnetic recording medium
also includes a white noise derived from the film characteristics
of the magnetic recording medium in addition to the spike-like
noise described above. In order to obtain a sufficient S/Nm, it is
also necessary to improve the white noise.
BRIEF SUMMARY OF THE INVENTION
[0009] A first object of the present invention is to provide a
perpendicular magnetic recording medium low in noise and capable of
a high density recording.
[0010] A second object of the present invention is to provide a
perpendicular magnetic recording apparatus low in noise and capable
of a high density recording.
[0011] According to a first aspect of the present invention, there
is provided a magnetic recording medium comprising:
[0012] a nonmagnetic substrate;
[0013] a perpendicular magnetic recording layer for recording
signal; and
[0014] a soft magnetic laminate layer including a soft magnetic
layer which has a thickness not larger than 500 .ANG. and a
nonmagnetic layer formed between a nonmagnetic substrate and a
perpendicular magnetic recording layer for recording signal.
[0015] According to a second aspect of the present invention, there
is provided a magnetic recording medium comprising:
[0016] a nonmagnetic substrate;
[0017] a perpendicular magnetic recording layer;
[0018] a soft magnetic laminate layer formed between the
nonmagnetic substrate and the perpendicular magnetic medium,
including a first soft magnetic layer, and a second soft magnetic
layer laminated on the first soft magnetic layer and differing from
the first soft magnetic layer in the crystal structure.
[0019] According to a third aspect of the present invention, there
is provided a magnetic recording medium comprising:
[0020] a nonmagnetic substrate;
[0021] a perpendicular magnetic recording layer;
[0022] a soft magnetic laminate layer formed between the
nonmagnetic substrate and the perpendicular magnetic medium,
including a soft magnetic granular layer formed of a nonmagnetic
matrix and soft magnetic metal particles dispersed in the matrix,
and a soft magnetic layer.
[0023] According to a fourth aspect of the present invention, there
is provided a magnetic recording apparatus, comprising:
[0024] a magnetic recording medium having a nonmagnetic substrate,
a soft magnetic laminate layer formed on the nonmagnetic substrate,
and a perpendicular magnetic recording layer formed on the soft
magnetic laminate layer;
[0025] driving means supporting and rotating the perpendicular
magnetic recording medium;
[0026] a magnetic head including an element for recording
information in the perpendicular magnetic recording medium and
another element for reading the recorded information; and
[0027] a carriage assembly supporting the magnetic head such that
the magnetic head is movable relative to the magnetic recording
medium.
[0028] According to a fifth aspect of the present invention, there
is provided a magnetic recording apparatus comprising:
[0029] a magnetic recording medium having a nonmagnetic substrate,
a perpendicular magnetic recording layer, a soft magnetic laminate
layer formed between the nonmagnetic substrate and the
perpendicular magnetic medium, including a first soft magnetic
layer, and a second soft magnetic layer laminated on the first soft
magnetic layer and differing from the first soft magnetic layer in
the crystal structure;
[0030] driving means supporting and rotating the perpendicular
magnetic recording medium;
[0031] a magnetic head including an element for recording
information in the perpendicular magnetic recording medium and
another element for reading the recorded information; and
[0032] a carriage assembly supporting the magnetic head and making
the magnetic head be movable relative to the magnetic recording
medium.
[0033] According to a sixth aspect of the present invention, there
is provided a magnetic recording apparatus comprising:
[0034] a magnetic recording medium having a nonmagnetic substrate,
a perpendicular magnetic recording layer, a soft magnetic laminate
layer formed between the nonmagnetic substrate and the
perpendicular magnetic medium, including a soft magnetic granular
layer formed of a nonmagnetic matrix and soft magnetic metal
particles dispersed in the matrix, and a soft magnetic layer;
[0035] driving means supporting and rotating the perpendicular
magnetic recording medium;
[0036] a magnetic head including an element for recording
information in the perpendicular magnetic recording medium and
another element for reading the recorded information; and
[0037] a carriage assembly supporting the magnetic head and making
the magnetic head be movable relative to the magnetic recording
medium.
[0038] According to the present invention, the soft magnetic
laminate layer is used as a magnetic layer so that generation of
the domain wall in the soft magnetic layer can be prevented so as
to suppress the noise generation from the soft magnetic layer,
thereby providing a perpendicular magnetic recording medium low in
noise and capable of a high density recording.
[0039] Also, according to the present invention, the noise
generation from the soft magnetic layer is suppressed by the use of
the particular perpendicular magnetic recording medium so as to
provide a perpendicular magnetic recording apparatus low in noise
and capable of a high density recording.
[0040] Additional objects and advantages of the present invention
will be set forth in the description which follows, and in part
will be obvious from the description, or may be learned by practice
of the present invention. The objects and advantages of the present
invention may be realized and obtained by means of the
instrumentalities and combinations particularly pointed out
hereinafter.
BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING
[0041] The accompanying drawings, which are incorporated in and
constitute a part of the specification, illustrate presently
preferred embodiments of the invention, and together with the
general description given above and the detailed description of the
preferred embodiments given below, serve to explain the principles
of the invention.
[0042] FIG. 1 is a view showing the construction of a first example
of the magnetic recording medium of the present invention;
[0043] FIG. 2 is a view showing the construction of a second
example of the magnetic recording medium of the present
invention;
[0044] FIG. 3 is a view showing the construction of a third example
of the magnetic recording medium of the present invention;
[0045] FIG. 4 is a view as observed from the side of the protective
layer shown in FIG. 3;
[0046] FIG. 5 is a view showing the construction of an example of
the magnetic recording apparatus of the present invention;
[0047] FIG. 6 is a view showing a fourth example of the magnetic
recording medium of the present invention;
[0048] FIG. 7 is a view showing a first example of a magnetic
recording medium for comparison;
[0049] FIG. 8 is a view showing a second example of a magnetic
recording medium for comparison;
[0050] FIG. 9 is a graph showing the wave form obtained by
measuring the noise of the soft magnetic layer;
[0051] FIG. 10 is a graph showing the wave form obtained by
measuring the noise of the soft magnetic layer;
[0052] FIG. 11 is a graph showing the wave form obtained by
measuring the noise of the soft magnetic layer;
[0053] FIG. 12 is a view showing a fifth example of the magnetic
recording medium of the present invention;
[0054] FIG. 13 is a view showing a sixth example of the magnetic
recording medium of the present invention;
[0055] FIG. 14 is a graph showing the relationship between the
saturation magnetization Ms and the thickness of the soft magnetic
laminate layer;
[0056] FIG. 15 is a graph showing the relationship between the DC
noise and the thickness of the soft magnetic laminate layer;
and
[0057] FIG. 16 is a graph showing the relationship between the
resolution of the perpendicular recording medium and the thickness
of the soft magnetic laminate layer.
DETAILED DESCRIPTION OF THE INVENTION
[0058] The perpendicular magnetic recording medium of the present
invention comprises in principle a nonmagnetic substrate, a
predetermined soft magnetic laminate layer formed on the
nonmagnetic substrate, and a perpendicular magnetic recording layer
formed on the soft magnetic laminate layer.
[0059] A preferred soft magnetic laminate layer comprises at least
one of the first to third soft magnetic laminate bodies described
below.
[0060] Specifically, the first soft magnetic laminate layer
comprises a nonmagnetic layer and a soft magnetic layer having a
thickness not larger than 500 .ANG.. The second soft magnetic
laminate layer comprises a first soft magnetic layer and a second
soft magnetic layer differing from the first soft magnetic layer in
the crystal structure. Further, the third soft magnetic laminate
layer comprises a granular layer composed of a nonmagnetic matrix
and soft magnetic metal particles dispersed in the nonmagnetic
matrix, and a soft magnetic layer, the granular layer is arranged
the perpendicular magnetic recording layer.
[0061] On the other hand, the perpendicular magnetic recording
apparatus of the present invention, to which the above magnetic
recording medium of the present invention is applied, comprises a
perpendicular magnetic recording medium having a nonmagnetic
substrate, a soft magnetic laminate layer formed on the nonmagnetic
substrate, and a perpendicular magnetic recording layer formed on
the soft magnetic laminate layer; driving means supporting and
rotating the perpendicular magnetic recording medium; a magnetic
head including an element to write signal in the perpendicular
magnetic recording medium and another element to read the recorded
signal; and a carriage assembly supporting the magnetic head such
that the magnetic head is movable relative to the perpendicular
magnetic recording medium.
[0062] According to the present invention, a predetermined soft
magnetic laminate layer is arranged between the nonmagnetic
substrate and the perpendicular magnetic recording layer so as to
suppress the generation of the domain wall and, thus, to suppress
the noise generated from the soft magnetic layer.
[0063] In the first soft magnetic laminate layer of the present
invention, the soft magnetic layer and the nonmagnetic layer are
laminated one upon the other a plurality of times, as required.
[0064] In the second soft magnetic laminate layer of the present
invention, the first soft magnetic layer and the second soft
magnetic layer are laminated one upon the other a plurality of
times, as required. It is also possible to use another soft
magnetic layer differing from the first and second soft magnetic
layers in the crystal structure.
[0065] Further, in the third soft magnetic laminate layer of the
present invention, the granular layer and the soft magnetic layer
are laminated one upon the other a plurality of times, as
required.
[0066] It is possible to further laminate the first to third soft
magnetic laminate bodies in combination as required, though, in the
case of using the third soft magnetic laminate layer, it is
necessary to arrange the third soft magnetic laminate layer such
that the granular layer is positioned adjacent to the magnetic
recording layer.
[0067] In such first and second soft magnetic laminate bodies, a
nonmagnetic layer is interposed between adjacent soft magnetic
layers so as to break the continuity of the crystal structure
between the soft magnetic layers. Also, the soft magnetic laminate
layer is interposed between the nonmagnetic substrate and the
perpendicular magnetic recording layer. The particular construction
permits weakening the co-relation in the perpendicular direction of
the soft magnetic layers of the magnetic recording medium, permits
maintaining the characteristics of each soft magnetic layer, and
permits suppressing the generation of domain wall so as to suppress
the noise generation from the soft magnetic layers.
[0068] In the third soft magnetic laminate layer, the granular
layer is formed for suppressing the domain wall generation. As a
result, the correlation between magnetic particles in the
longitudinal direction of the soft magnetic layers of the magnetic
recording medium is weakened. It is considered reasonable to use
ferromagnetic particles of Co, CoPt, etc. having a high Hk value,
which particle diameter is decreased close to a superparamagnetism
particle, as the magnetic material contained in the granular layer.
These ferromagnetic particles do not form domain walls, but greatly
affect the recording process of the magnetic recording layer,
resulting in failure to form a bit pattern. Such being the
situation, magnetic particles having a relatively small Hk value
are used in the present invention. Further, in the present
invention, these magnetic particles covered with a nonmagnetic
matrix is effective to achieve a good smoothness of the surface of
a magnetic recording layer. However, in the magnetic recording
layer of this type, density of the magnetic particles is diluted by
the presence of the nonmagnetic matrix, with the result that the
average saturation magnetic flux density Bs of the magnetic layer
is lowered, compared with the continuous magnetic recording layer.
Therefore, in the present invention, a soft magnetic continuous
layer is further laminated on the granular layer so as to increase
the saturation magnetic flux density Bs.
[0069] Because of the particular construction, the magnetic flux
coming from the main pole of the head is concentrated on the
magnetic particle portion of the granular layer having a high
permeability and passes through the lower continuous magnetic film
without passing through the nonmagnetic matrix between adjacent
particles so as to return to the return pole of the head. It
follows that it is possible to obtain highly concentrate magnetic
flux in the magnetic particle in the soft magnetic layer.
[0070] Further, the second soft magnetic laminate layer produces
the merit that the Mst value is rendered higher than that of the
first soft magnetic laminate layer in which the same number of soft
magnetic layers and nonmagnetic layers are laminated one upon the
other.
[0071] If the thickness of the soft magnetic layer in the first
soft magnetic laminate layer exceeds 500 .ANG., fail to suppress
the noise sufficiently result in a bad S/Nm of perpendicular
recording medium. It is desirable for the thickness of the soft
magnetic layer to fall within a range of between 50 .ANG. and 200
.ANG..
[0072] The thickness of the nonmagnetic layer in the first soft
magnetic laminate layer should preferably be not larger than 1.5
times the thickness of the soft magnetic layer, more preferably 0.2
to 1.0 times the thickness of the soft magnetic layer. If the
thickness of the nonmagnetic layer exceeds 1.5 times the thickness
of the soft magnetic layer, it is difficult to obtain the effect of
preventing the domain wall generation.
[0073] If the soft magnetic layer has a thickness not larger than
500 .ANG., the domain wall is converted into a Neel wall. If the
thickness of the nonmagnetic layer is not larger than 1.5 times the
thickness of the soft magnetic layer, the distance between adjacent
soft magnetic layers is not rendered unduly large particularly
where a plurality of nonmagnetic layers and soft magnetic layers
are alternately laminated one upon the other. If the thickness of
each of the soft magnetic layer and the nonmagnetic layer falls
within the range specified in the present invention, the reel wall
coupling is generated between the adjacent soft magnetic layers so
as to decrease the internal energy and, thus, to cause the domain
wall not to be sharp. As a result, it is possible to suppress the
noise when the R/W characteristics are measured.
[0074] The Neel wall coupling between adjacent soft magnetic layers
also takes place in the second soft magnetic laminate layer so as
to decrease the internal energy and, thus, to cause the domain wall
not to be sharp, thereby suppressing the noise generation.
[0075] The entire thickness of the first or second soft magnetic
laminate layer should preferably fall within a range of between 500
.ANG. and 4,000 .ANG., more preferably should be about 2,000
.ANG..
[0076] The saturation magnetization per layer of the soft magnetic
layers used in the first or second soft magnetic laminate layer
should preferably be not higher than 90% of the saturation
magnetization of the soft magnetic layer under the state of bulk.
In this case, each soft magnetic layer is in the state close to the
structure in which the magnetic particles are separated from each
other. Since the magnetic particles are separated from each other,
the coercive force is diminished and, thus, the domain wall is
unlikely to be generated.
[0077] The nonmagnetic substrate can be made from, for example,
glass, aluminum, silicon, plastic materials, and synthetic resins.
The substrate can be in any shape of a disc, a tape or a drum.
[0078] Each of the soft magnetic layer and the perpendicular
magnetic recording layer can be formed by a physical vapor
deposition method such as a sputtering method, a vacuum evaporation
method.
[0079] The perpendicular magnetic recording layer is formed of a
ferromagnetic material containing at least one element selected
from Co, Fe and Ni. For example, the perpendicular magnetic
recording layer contains combination of CoPtCr, CoCrTa, CoTaPt,
CoNiTa, CoPt or oxide thereof.
[0080] It is desirable for the soft magnetic layer used in the
first or second soft magnetic laminate layer to contain as a main
component at least one element selected from Fe, Co and Ni. On the
other hand, it is desirable for the nonmagnetic layer used in the
first soft magnetic laminate layer to contain at least one element
selected from the group consisting of B, C, Ti, Si, Al, Cr, Ru, Zr,
Nb, and Ta.
[0081] The soft magnetic layer used in the third soft magnetic
laminate layer is formed of a soft magnetic material containing at
least one element selected from Co, Fe and Ni. For example, the
particular soft magnetic layer is formed of CoFe, NiFe or
CoZnNb.
[0082] The nonmagnetic matrix of the granular layer is formed of a
nonmagnetic metal such as Ag, Ti, Ru or C or its compound as well
as an oxide, a nitride, a fluoride or a carbide such as SiO.sub.2,
SiO, Si.sub.3N.sub.4, Al.sub.2O.sub.3, AlN, TiN, BN, CaF, or
TiC.
[0083] Particularly, in the case of the nonmagnetic matrix or the
surface layer or the soft magnetic laminate layer is formed of a
material which can play the roles of controlling the crystallinity
and the orientation of the perpendicular magnetic recording medium
such as Ti or TiN, it is possible to diminish the underlayer of the
perpendicular magnetic recording layer in order to improve the
efficiency of the soft magnetic laminate layer as an underlying
film and to permit a high density recording. It is also possible to
arrange an intermediate layer of Ti, a nonmagnetic CoCr, etc. which
control the crystallinity and the orientation of the perpendicular
magnetic recording layer between the soft magnetic laminate layer
and the perpendicular magnetic recording layer.
[0084] A Fe--Al--Si alloy soft magnetic laminate layer prepared by
laminating a Fe--Al--Si alloy magnetic layer having a thickness not
larger than 500 .ANG. on a nonmagnetic substrate with a nonmagnetic
layer interposed between constitutes a further preferred example of
the first soft magnetic laminate layer. The Fe--Al--Si alloy
magnetic layer has a good stability again applied magnetic field
and, thus, is stable in its output. Also, since the domain wall is
not formed in the Fe--Al--Si alloy magnetic layer, the spike noise
is not generated. However big domain walls are not generated, the
Fe--Al--Si alloy magnetic layer shows the noise derived from the
fine domain walls in size of about 1 to 10 .mu.m is generated as a
white noise, and so not suitable for the underlayer of the
perpendicular magnetic recording media in the practical use. In the
present invention, however, the Fe--Al--Si alloy magnetic thin
films are laminated to erase the fine domain walls, and succeeded
in suppressing the noise generation. It follows that the present
invention provides a soft magnetic layer exhibiting the
characteristics of the Fe--Al--Si alloy magnetic thin film and
capable of further suppressing the noise generation.
[0085] The present invention also provides a further improved
perpendicular magnetic recording medium prepared by laminating at
least one Co--Pt--Cr--O series perpendicular magnetic recording
layer on a Fe--Al--Si alloy soft magnetic laminate layer prepared
by laminating a Fe--Al--Si alloy magnetic thin film thinner than
500 .ANG. and a nonmagnetic thin film alternately on a nonmagnetic
substrate. The Co--Pt--Cr--O series perpendicular magnetic
recording layer is a recording medium with small demagnetization
and excellent thermal stability, as described in "The 2000 IEEE
International Magnetic Conference DP-05". When the Co--Pt--Cr--O
series perpendicular magnetic recording layer is combined with the
Fe--Al--Si alloy soft magnetic laminate layer, the magnetic flux
distribution from recording head is improved and it becomes
possible to derive more effectively the characteristics of the high
Ku Co--Pt--Cr--O alloy. It should also be noted that, where the
Fe--Al--Si alloy magnetic thin film is laminated, the surface of
the thin film is made smoother. Therefore, where the Fe--Al--Si
alloy magnetic laminate layer is used as a soft magnetic lining
layer, the surface of the Co--Pt--Cr--O perpendicular magnetic
recording layer is also made smoother. It should also be noted that
a heat treatment is not necessary for the Co--Pt--Cr--O series
perpendicular magnetic recording layer and the Fe--Al--Si alloy
magnetic laminate layer to obtain excellent characteristics. By
using the soft magnetic laminate layer as an underlayer of a double
layered perpendicular magnetic recording medium GH (Glide Height)
is suppressed in a low level easily. It should also be noted that,
since a heat treatment is not applied, it is possible to form the
magnetic laminate layer and the perpendicular magnetic recording
layer on a nonmagnetic resin substrate, which is cheap and low in
its heat resistance.
[0086] The present invention will now be described more in detail
with reference to the accompanying drawings.
[0087] FIG. 1 shows an example of the magnetic recording medium 40
of the present invention using the first soft magnetic laminate
layer. As shown in the drawing, the magnetic recording medium 40
comprises a nonmagnetic substrate 41, a soft magnetic laminate
layer 45 consisting of a soft magnetic layer 42 formed on the
nonmagnetic substrate 41 and having a thickness not larger than 500
.ANG. and a nonmagnetic layer 43 formed on the soft magnetic layer
42, and a perpendicular recording layer 44 formed on the soft
magnetic laminate layer 45. Each of the soft magnetic layer 42, the
nonmagnetic layer 43 and the perpendicular recording layer 44 can
be formed by a sputtering method.
[0088] FIG. 2 shows an example of the magnetic recording medium 50
of the present invention using the soft magnetic laminate layer. As
shown in the drawing, the magnetic recording medium 50 comprises a
nonmagnetic substrate 51, a soft magnetic laminate layer 55
consisting of a first soft magnetic layer 52 formed on the
nonmagnetic substrate 51 and a second soft magnetic layer 53 formed
on the first soft magnetic layer 52, and a perpendicular recording
layer 54 formed on the soft magnetic laminate layer 55. Each of the
soft magnetic layer 52, the nonmagnetic layer 53 and the
perpendicular recording layer 54 can be formed by a sputtering
method.
[0089] FIG. 3 shows as a model an example of a magnetic recording
medium 60 of the present invention using the third soft magnetic
laminate layer. As shown in the drawing, the magnetic recording
medium 60 comprises: a nonmagnetic substrate 61, a third soft
magnetic laminate layer including a soft magnetic layer 62 formed
on the nonmagnetic substrate 61, and a granular layer 65 formed on
the soft magnetic layer 62, which consists of magnetic particles 63
and a nonmagnetic matrix 64 surrounding the magnetic particles 63,
a perpendicular magnetic recording layer 66 formed on the granular
layer 65, and a protective layer 67 formed on the perpendicular
magnetic recording layer 66.
[0090] FIG. 4 shows the model drawing of FIG. 3 as viewed from the
side of the protective layer. The circles of broken lines 68 in
FIG. 4 denote the positions where the magnetic particles 63 are
present below the protective layer 67. FIG. 4 clearly shows that
the magnetic particles 63 are surrounded by the nonmagnetic matrix
64 in the granular layer 65.
[0091] FIG. 5 shows an example of the magnetic recording apparatus
of the present invention. As shown in the drawing, a magnetic disc
121 of a hard structure for recording information is mounted to a
spindle 122 and is rotated at a predetermined speed by a spindle
motor (not shown). A slider 123 has a magnetic head is provided on
the tip of a suspension 124 formed in a thin plate-like leaf spring
which access to the magnetic disc 121 to read and write signals.
The suspension 124 is connected to one end portion of an arm 125
having a bobbin etc. for holding a driving coil (not shown).
[0092] A voice coil motor 126, which is a kind of a linear motor,
is mounted on the other end portion of the arm 125. The voice coil
motor 126 comprises a driving coil (not shown) wound up to the
bobbin portion of the arm 125 and a magnetic circuit consisting of
a permanent magnet arranged to have the driving coil held therein
and a yoke positioned to face the permanent magnet.
[0093] The arm 125 is held by ball bearings mounted in the upper
and lower portions of a stationary shaft 127 so as to be rotated
and swung by the voice coil motor 126. In other words, the position
of the slider 123 on the magnetic disc 121 is controlled by the
voice coil motor 126. Incidentally, a reference numeral 128 in FIG.
5 denotes a lid.
[0094] The present invention will now be described in detail with
reference to Examples.
EXAMPLE 1
[0095] FIG. 6 shows sample 1 prepared by applying the first soft
magnetic laminate layer.
[0096] Sample 1 was prepared as follows. In the first step, each
target of Fe(11 atm %)-Al(17 atm %)-Si, C, Ti, Ru, and Co(20 atm
%)-Pt(16 atm %)-Cr was put in a vacuum chamber evacuated to a
vacuum of 2.times.10.sup.-1 Pa. Each vacuum chamber was constructed
to permit the medium to move from one chamber to another without
being brought into the air atmosphere.
[0097] Then, a nonmagnetic glass substrate 1 was arranged to face
the FeAlSi target, and sputtering was performed under the discharge
of DC 1500W while allowing an Ar gas to flow into the vacuum
chamber to set up a pressure of 0.5 Pa so as to form an FeAlSi soft
magnetic film 2-1 having a thickness of 100 .ANG. in one second.
Further, the nonmagnetic glass substrate 1 was moved into another
vacuum chamber while maintaining the vacuum condition and arranged
to face a C target. Under this condition, sputtering was performed
under the discharge of DC 1000W while allowing an Ar gas to flow
into the vacuum chamber to set up a pressure of 0.5 Pa, thereby
forming a C nonmagnetic layer 3-1 having a thickness of 40 .ANG. in
5 minutes.
[0098] Similarly, FeAlSi soft magnetic layers 2-2 to 2-20 and C
nonmagnetic films 3-2 to 3-20 were formed alternately so as to form
an example of the first soft magnetic laminate layer consisting of
FeAlSi films 2-1 to 2-20 and C films 3-1 to 3-20.
[0099] After formation of the laminate structure, the nonmagnetic
glass substrate 1 was moved into another vacuum chamber while
maintaining the vacuum condition and arranged to face a Ti target.
Under this condition, sputtering was performed under the discharge
of DC 1000W while allowing an Ar gas to flow into the vacuum
chamber to set up a pressure of 0.5 Pa so as to form a Ti seed
layer 4 having a thickness of 120 .ANG..
[0100] Further, the nonmagnetic glass substrate 1 was moved into
another vacuum chamber while maintaining the vacuum condition and
arranged to face a Ru target. Under this condition, sputtering was
performed under the discharge of DC 1000W while allowing an Ar gas
to flow into the vacuum chamber to set up a pressure of 0.5 Pa so
as to form a Ru underlying layer 5 having a thickness of 500
.ANG..
[0101] Further, the nonmagnetic glass substrate 1 was moved into
another vacuum chamber while maintaining the vacuum condition and
arranged to face a CoPtCr target. Under this condition, sputtering
was performed under the discharge of DC 250W while allowing an Ar
gas containing 0.05% of O.sub.2 to flow into the vacuum chamber to
set up a pressure of 20 Pa so as to form a lower CoPtCrO
perpendicular magnetic recording layer 6a having a thickness of 120
.ANG..
[0102] Then, the nonmagnetic glass substrate 1 was moved again into
the vacuum chamber having the Ru target arranged therein while
maintaining the vacuum condition and arranged to face the Ru
target. Under this condition, sputtering was performed under the
discharge of DC 250W this time while allowing an Ar gas to flow
into the vacuum chamber to set up a pressure of 0.5 Pa so as to
form a Ru nonmagnetic layer 7 having a thickness of 40 .ANG..
Further, an upper CoPtCrO perpendicular magnetic recording layer 6b
was formed on the Ru nonmagnetic layer 7 as in the formation of the
lower CoPtCrO perpendicular recording layer 6a.
[0103] Finally, the nonmagnetic glass substrate 1 was arranged to
face the C target, and the sputtering was performed under the
discharge of DC 1000W while allowing an Ar gas to flow into the
vacuum chamber to set up a pressure of 0.5 Pa so as to form a C
protective layer 8 having a thickness of 70 .ANG.. After completion
of the film formation, the C protective layer 8 was coated with a
PFPE lubricant in a thickness of 10 .ANG. by a dipping method so as
to obtain sample 1.
Comparative Example 1
[0104] FIG. 7 shows a medium according to Comparative Example 1
[0105] A FeAlSi film 10a was formed on a nonmagnetic glass
substrate 9 as in sample 1, except that the FeAlSi film 10a was
formed in a thickness of 1,000 .ANG.. Then, a C nonmagnetic layer
11a was formed on the FeAlSi film 10a as in Example 1. Further, an
FeAlSi film 10b and a C nonmagnetic layer 11b were alternately
formed on the C nonmagnetic layer 11a. Still further, a Ti seed
layer 12, a Ru underlying layer 13, a lower CoPtCrO perpendicular
magnetic recording layer 14a, a Ru nonmagnetic layer 15, an upper
CoPtCrO perpendicular magnetic recording layer 14b, and a C
protective layer 16 were formed as in Example 1, followed by
coating the C protective layer 16 with a PFPE lubricant so as to
obtain a conventional sample 2.
Comparative Example 2
[0106] FIG. 8 shows a medium according to Comparative Example
2.
[0107] Sputtering was performed as in Example 1, except that a
CoZrNb film 18 was formed in a thickness of 2,000 .ANG. by
arranging a nonmagnetic glass substrate 17 to face a Co(6 atm
%)-Zr(10 atm %)-Nb target in place of the Fe (11 atm %)-Al (17 atm
%)-Si target used in Example 1.
[0108] Further, a Ti seed layer 19, a Ru underlying layer 20, a
lower CoPtCrO perpendicular magnetic recording layer 21a, a Ru
nonmagnetic layer 22, an upper CoPtCrO perpendicular magnetic
recording layer 21b, and a C protective layer 23 were formed as in
Example 1, followed by coating the C protective layer 23 with a
PFPE lubricant so as to obtain a conventional sample 3.
[0109] An R/W test was applied to each of these samples 1, 2 and 3
by using the method of writing signals by using a single magnetic
pole head and reading the signals by using an MR head so as to
measure S/Nm and D50. The measurement was performed at a constant
radial position of 20 mm from the center while rotating the disc at
4,200 rpm. Thus measured values of S/Nm and D50 are shown in Table
1.
[0110] Sample 1 for Example 1 was found to be superior to
conventional samples 2 and 3 in each of S/Nm and D50. Particularly,
fine noises covering the entire signal wave form were generated as
a white noise in sample 2. Also, abrupt spike noises were found to
have been generated in sample 3. On the other hand, a noise was not
generated in sample 1 for Example 1.
[0111] Since samples 1, 2 and 3 were equal to each other in the
recording layer, the noise is considered to have been generated
from the soft magnetic layer positioned below the recording layer.
Such being the situation, the soft magnetic layers alone were
formed for comparison of the noise generation after the DC
erasing.
[0112] FIGS. 9 to 11 show wave forms of the noises for samples 1, 2
and 3, respectively. As shown in FIG. 9, a noise is not observed in
the case where the FeAlSi thin films 2 and the nonmagnetic layers 3
alone were alternately laminated one upon the other as in sample 1.
However, a white noise is observed in the case where the FeAlSi
thin films 10 and the C nonmagnetic layers 11 alone were
alternately laminated one upon the other as in sample 2. Further,
spike noises were observed in the case where the CoZrNb films 18
alone was laminated as in sample 3.
[0113] The state of magnetization was observed with an MFM in
respect of the laminate structure of these soft magnetic layers.
The domain wall was not observed in sample 1. However, domain walls
forming domains of 0.31 .mu.m were observed in sample 2. Further,
domain walls forming domains of the size that cannot be observed
were observed in sample 3.
[0114] Also, the noise after the DC erasing was compared in respect
of the soft magnetic layer prepared by laminating a single FeAlSi
thin film 2 and a single nonmagnetic layer 3 for sample 1. It has
been found that the noise has a wave form similar to that shown in
FIG. 9, supporting that the effect of preventing the noise
generation can be produced by only a single layer. Further, the
state of magnetization was similarly observed with an MFM in
respect of the soft magnetic layer prepared by laminating a single
FeAlSi thin film 2 and a single nonmagnetic layer 3 for sample 1.
It has been found that a domain wall was not formed in this case.
In other words, it has been found that the noise can be suppressed
to a low level even in the case where the soft magnetic laminate
layer consists of a single FeAlSi thin film 2 and a single
nonmagnetic layer 3, making it possible to laminate 20 thin films 2
and 20 nonmagnetic layers 3 without amplifying the noise.
[0115] Further, the domain wall was observed over the entire medium
surface by the principle of Kerr effect by using an OSA (Optical
Surface Analyzer) apparatus for observing the reflection of the
laser light onto the entire surface of the medium. A domain wall
was not observed in sample 1 in this case, too. However, domain
walls dividing the medium surface into several regions were
observed in sample 3. These domain walls are considered to cause
the white noise and the spike noise.
[0116] Also, the values of Ms of these three soft magnetic film
portions alone were measured by using a VSM (Vibrating Sample
Magnetometer) without taking the volume of the nonmagnetic
intermediate layer into consideration. It has been found that the
value of Ms for sample 1 was 580 emu/cc, which was about 80% of the
theoretical bulk value of FeAlSi. Also, the value of Ms for sample
2 was found to be 720 emu/cc, which was substantially equal to the
theoretical value of FeAlSi. Further, the value of Ms for sample 3
was found to be 1070 emu/cc, which was substantially equal to the
theoretical value of CoZrNb.
[0117] As described above, the magnetic recording medium prepared
in Example 1 included the soft magnetic thin film that does not
generate noise.
EXAMPLE 2
[0118] FIG. 12 shows a sample 4 comprising the second soft magnetic
laminate layer.
[0119] In preparing the magnetic recording medium of sample 4, a
soft magnetic laminate layer was formed as in Example 1, except
that a CoZrNb target for forming a soft magnetic layer was used in
place of the C target used in Example 1 for forming a nonmagnetic
layer, and that FeAlSi thin films 25-1 to 25-10 each having a
thickness of 4 nm and CoZrNb thin films 26-1 to 26-10 each having a
thickness of 4 nm were alternately laminated to form an example of
the second soft magnetic laminate layer instead of the first
magnetic laminate layer. Further, a Ti seed layer 27, a Ru
underlying layer 28, a lower CoPtCrO perpendicular recording layer
29a, a Ru nonmagnetic layer 30, an upper CoPtCrO perpendicular
recording layer 29b, and a C protective layer 31 were formed,
followed by coating the C protective layer 31 with a PFPE lubricant
so as to obtain sample 4.
[0120] Sample 4 thus prepared widely differs from sample 1 in that
the FeAlSi thin films 25-1 to 25-10 and the CoZrNb thin films 26-1
to 26-10 are soft magnetic layers differing from each other in
crystal structure.
[0121] These two layers were independently formed and the XRD
(X-ray diffraction) patterns of these films were examined under the
conditions of Cu-K.alpha. and 2.theta.=30 to 70.degree.. A peak
that is considered to be the (220) plane of a cubic lattice
appeared about 45.degree. in the FeAlSi thin film. However, only a
broad peak appeared on the order of 40.degree. in the CoZrNb
intermediate layer, indicating that the CoZrNb intermediate layer
was amorphous.
[0122] A R/W test was applied as in Example 1 to sample 4 thus
prepared. Table 1 shows the results.
[0123] Noise was not observed in the actual R/W wave form and in
the noise measurement of the soft magnetic laminate film as in
Example 1.
EXAMPLE 3
[0124] FIG. 13 shows sample 5 prepared by using another example of
the first soft magnetic laminate layer. Sample 5 was prepared as
follows. Specifically, CoZrNb soft magnetic layer 33-1 to 33-20
each having a thickness of 20 nm and Ti nonmagnetic layers 34-1 to
34-19 each having a thickness of 7 nm were alternately laminated
alternately to form another example of the first soft magnetic
laminated layer on a nonmagnetic substrate 32. Then, a Ti seed
layer 35, which was the uppermost Ti nonmagnetic layer, was formed
on the uppermost CoZrNb thin film 33-20, followed by forming a
CoCrTa perpendicular magnetic recording layer 36 on the Ti seed
layer 35. Further, a C protective layer 37 was formed on the CoCrTa
perpendicular magnetic recording layer 36 so as to prepare sample 5
of the magnetic recording medium.
[0125] A R/W test was applied to sample 5 as in Example 1. The
results are shown in Table 1.
1 TABLE 1 S/Nm (dB) D50 (kFCI) Example 1 Sample 1 30.2 361
Comparative Example 1 Sample 2 18.6 253 Comparative Sample 3 21.4
248 Example 2 Example 2 Sample 4 31.0 370 Example 3 Sample 5 29.7
348
[0126] Table 1 clearly shows that the perpendicular magnetic
recording medium prepared in, for example, Example 1, exhibits
large values of S/Nm and D50.
[0127] The perpendicular magnetic recording medium prepared in
Example 2, i.e., sample 4, was found to be somewhat superior to
sample 1 in each of S/Nm and D50. Further, where the magnetic thin
films and magnetic intermediate layers differing from the magnetic
thin film in the crystallinity were used for forming the laminated
soft magnetic layer, the resultant perpendicular magnetic recording
medium was found to exhibit S/Nm and D50 fully comparable with
those of the perpendicular magnetic recording medium prepared by
using a laminate layer consisting of magnetic thin films and
nonmagnetic thin films, though the number of laminated layers or
films in the case of using the magnetic intermediate layers is
smaller than that in the case of using nonmagnetic thin films.
[0128] However, the perpendicular magnetic recording medium
prepared in each of Comparative Examples 1 and 2 was found to be
insufficient in each of the S/Nm value and the D50 value.
EXAMPLES 4 TO 10 AND COMPARATIVE EXAMPLE 3 TO 8
[0129] Samples 6 to 11 comprising the third soft magnetic laminate
layer will now be described with reference to FIG. 3.
[0130] In the first step, a 2.5 inch glass substrate 61 was
prepared as nonmagnetic substrate. Also Co.sub.80Fe.sub.20 target
was prepared for the soft magnetic layer 62. Further a
Co.sub.80Fe.sub.20TiN composite target was prepared, adjusted such
that the volume ratio after the film formation of
Co.sub.80Fe.sub.20 for forming the magnetic particles 63 to the TiN
for forming the nonmagnetic matrix 64 would be 60:40.
[0131] Then, a continuous soft magnetic layer 62 having a thickness
of 50 nm was formed on each glass substrate 61 by an opposed
stationary magnetron sputtering method under an Ar gas atmosphere,
DC power 1000W, by using the Co.sub.80Fe.sub.20 target. Further,
granular layers having a variety of thickness such as 10, 50, 100,
200, 400, and 600 nm were formed, respectively, as shown in a
granular layer 65 by an opposed stationary magnetron sputtering
method by using the Co.sub.80Fe.sub.20--TiN composite target. Each
CoPt.sub.20Cr film having a thickness of 50 nm is formed as the
perpendicular magnetic recording layer 66 by an opposed stationary
magnetron sputtering method under a mixed gas prepared by adding
traces of oxygen to an Ar gas using the CoPt.sub.20Cr.sub.16 alloy
target. Finally, the C protective film 67 was formed in a thickness
of 8 nm on each perpendicular magnetic recording layer 66. Samples
6 to 11 of the perpendicular magnetic recording media were
obtained.
[0132] Samples 12 to 17 corresponding to Comparative Examples 3 to
8 were prepared by forming the granular layers in a thickness of 10
nm, 50 nm, 100 nm, 200 nm, 400 nm and 600 nm, respectively, as in
Examples 4 to 10, except that the continuous soft magnetic layer
was not formed on the substrate.
[0133] The relationship between the magnetic characteristics and
the film structure of the resultant perpendicular magnetic
recording medium was studied. Specifically, the magnetic
characteristics of the film formed were examined by a VSM
(Vibrating Sample Magnetometer), and the film structure was
examined by using a TEM (Transmission Electron Spectroscopy). The
value of S.sub.0/NmRMS when the recording was performed at a
recording density of 250 Kfci was measured by using a GMR head
having a read gap length of 0.5 .mu.m and a read track width of 0.8
.mu.m, a single magnetic pole head having a main magnetic pole film
thickness of 0.4 .mu.m and a write track width of 2 .mu.m, using a
spin stand having the spacing between a medium and a head is 40
nm.
[0134] FIG. 14 is a graph showing the relationship between the
saturation magnetization Ms granular+bulk of the entire recording
layer and the thickness of the soft magnetic laminate layer and a
single granular layer of the perpendicular magnetic recording
medium thus prepared a line 101 including six dots on the line
according to Examples 4 to 10, and a line 102 including six dots on
line according to Comparative Examples 3 to 8.
[0135] Also, the noise was measured.
[0136] FIG. 15 is a graph showing the relationship between the DC
noise after DC erasing and the thickness of the soft magnetic
laminate layer with and without continuous soft magnetic layer. A
line 103 relates to Examples, and a line 104 relates to Comparative
Examples.
[0137] As apparent from FIG. 15, the noise of the perpendicular
magnetic recording medium using the granular layer alone has been
found to increase simply with increase in the film thickness. On
the other hand, in the perpendicular magnetic recording medium in
which the continuous soft magnetic layer was formed below the
granular layer, the noise of media, in which the thickness of the
granular layer was 10 nm, was found to be about two times as high
as the noise of sample using the granular layer alone.
[0138] The experimental data suggest that the influence of noise
derived from the continuous soft magnetic layer formed below the
granular layer appears greatly. It is considered reasonable to
understand that, in the case of the thinner granular layer, the
noise from the continuous soft magnetic layer formed below the
granular layer effects on the noise of media. It is also considered
reasonable to understand that, where the granular layer is thicker,
the noise of the granular layer would be predominant.
[0139] It is considered reasonable to understand that the desirable
film thickness is determined by the value of Bs, the permeability,
the thickness of the soft magnetic laminate layer, and the content
of volume of the magnetic particles within the granular layer,
etc.
[0140] Then, the differential PW.sub.50 was obtained for each of
the perpendicular recording media described above when the media
was recorded at 250 kfci of a recording density. FIG. 16 is a graph
showing the relationship between PW.sub.50 thus obtained and the
thickness of the soft magnetic laminate layer. A line 105 relates
to Comparative Examples, and a line 106 relates to Examples.
[0141] The differential value of PW.sub.50 of the soft magnetic
laminate layer was significantly increased at the thickness of not
larger than 100 nm. It is considered that this results from
significant appearance of an influence of the continuous soft
magnetic layer. The differential value of PW.sub.50 of the soft
magnetic laminate layer having a thickness except for the above
range was smaller in comparison with the differential value of
PW.sub.50 of the single granular layer. It is considered because of
a desired magnetization conversion that is caused by laminating of
the continuous soft magnetic layer, a mirror image effect and an
effect of controlling magnetic flux would be taken when
recording.
[0142] A soft magnetic granular layer was formed by the same way as
the steps of forming above perpendicular magnetic recording medium
except for using RF magnetron spattering method with a composite
target containing SiO.sub.2 as a nonmagnetic matrix and CoFe as a
magnetic particles to obtain a soft magnetic laminate layer.
[0143] The DC noise is measured for the media without magnetic
recording layer. The differential PW.sub.50 is measured for a
perpendicular magnetic recording medium comprising the obtained
soft magnetic laminate layer and further comprising a magnetic
layer similar to the above magnetic layer on the laminate layer.
The result was similar to that of the perpendicular magnetic
recording medium having the granular layer including TiN as a
nonmagnetic matrix.
[0144] However when the recording density is increased to 500 kfci,
the value of the DC noise and the differential PW.sub.50 become a
somewhat larger than the value of the media having the granular
layer including TiN as a nonmagnetic matrix. And when a frequency
is higher, it was found that the noise of media with the granular
longer became larger.
[0145] The experimental data suggest that, in the case of the
perpendicular magnetic recording medium using TiN having a low
resistivity for forming the nonmagnetic matrix, an eddy current
generated under a high frequency makes the recording insufficient,
and that, in the case of the perpendicular magnetic recording
medium using SiO.sub.2 having a high resistivity for forming the
nonmagnetic matrix, the generation of the eddy current is
suppressed so as to achieve a sufficient recording.
[0146] Additional advantages and modifications will readily occur
to those skilled in the art. Therefore, the invention in its
broader aspects is not limited to the specific details and
representative embodiments shown and described herein. Accordingly,
various modifications may be made without departing from the spirit
or scope of the general inventive concept as defined by the
appended claims and their equivalents.
* * * * *