U.S. patent application number 10/603129 was filed with the patent office on 2004-01-15 for rotationally molded medical articles.
Invention is credited to Schuessler, David J..
Application Number | 20040010225 10/603129 |
Document ID | / |
Family ID | 25425767 |
Filed Date | 2004-01-15 |
United States Patent
Application |
20040010225 |
Kind Code |
A1 |
Schuessler, David J. |
January 15, 2004 |
Rotationally molded medical articles
Abstract
A system and method for molding the shell of a medical device or
other molded article is disclosed. The system includes a multi-axis
rotational molding machine in which a mold is mounted. The mold has
a cavity in the shape of the article to be molded. The mold seals
to hold a vacuum. In operation, silicone or other molding material
is inserted into the mold, vacuum is applied to the mold, the mold
is rotated about at least two axes and a molding material coats the
inside walls of the mold to form the shell or other desired
article. A rotationally molded medical article is also
disclosed.
Inventors: |
Schuessler, David J.;
(Ventura, CA) |
Correspondence
Address: |
Christopher E. Chalsen
Milbank, Tweed, Hadley & McCloy, LLP
One Chase Manhattan Plaza
New York
NY
10005
US
|
Family ID: |
25425767 |
Appl. No.: |
10/603129 |
Filed: |
June 24, 2003 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10603129 |
Jun 24, 2003 |
|
|
|
09908404 |
Jul 18, 2001 |
|
|
|
Current U.S.
Class: |
604/96.01 ;
428/36.5; 623/8 |
Current CPC
Class: |
A61F 2240/004 20130101;
A61F 2/12 20130101; B29C 33/58 20130101; B29C 41/42 20130101; A61B
17/12099 20130101; Y10T 428/1376 20150115; A61B 2017/00557
20130101; B29C 41/38 20130101; A61B 17/12109 20130101; A61M 25/1029
20130101; B29C 33/0038 20130101; B29C 41/50 20130101; B29L 2031/753
20130101; Y10S 425/06 20130101; A61F 2002/3007 20130101; B29C
2791/006 20130101; B29C 41/06 20130101; B29C 41/003 20130101; B29C
33/68 20130101; A61B 17/12136 20130101; A61B 2017/00526 20130101;
B29K 2083/00 20130101; Y10S 425/812 20130101 |
Class at
Publication: |
604/96.01 ;
623/8; 428/36.5 |
International
Class: |
A61F 002/12; A61M
029/00 |
Claims
What is claimed is:
1. A rotational molding system for molding a medical article
comprising: a multi-axis rotational molding machine; and a mold
mounted to said molding machine wherein the interior of said mold
defines a cavity in the desired shape of the medical article to be
molded.
2. The system according to claim 1 wherein said mold comprises
first and second mold pieces matable to form a vacuum-tight seal
along mating surfaces between said first and second pieces.
3. The system according to claim 1 wherein said mold comprises a
sprue opening fluidly connected to said interior of said mold.
4. The system according to claim 2 wherein one piece of said mold
has a hemispherical cavity shape.
5. The system according to claim 1 wherein said interior of said
mold is sized to allow for the thickness of a liner to coat an
inside surface of said mold.
6. A method for molding a medical article comprising the steps of:
inserting a molding material into a cavity within a mold; applying
a vacuum to said mold; rotating said molding material in said mold
about at least two axes to coat the interior of said mold cavity
with said molding material.
7. The method of claim 6 further comprising the steps of: inserting
a liner material into said cavity; rotating said liner material in
said mold about at least two axes to coat the interior of said mold
cavity with said liner material.
8. The method according to claim 7 wherein said liner material
coats the interior of said mold cavity thereby masking any surface
irregularities.
9. The method according to claim 7 wherein said liner material is a
thermoplastic selected from the group consisting of polyethylene,
polypropylene, nylon and fluoropolymer.
10. The method according to claim 7 wherein said liner material is
a thermoset selected from the group consisting of polyester resin,
polyurethane and epoxy.
11. The method according to claim 6 wherein said molding material
is a room temperature acetoxy-cured silicone dispersion in a
solvent.
12. The method according to claim 6 wherein said molding material
is a platinum catalyzed heat-cured silicone dispersion in a
solvent.
13. The method of claim 7 further comprising the step of separating
said liner material from said molding material.
14. The method of claim 13 wherein said liner material is separated
from said molding material by dissolving said liner material.
15. The method of claim 13 wherein said liner material is separated
from said molding material by melting said liner material.
16. The method of claim 13 wherein said liner material is separated
from said molding material by burning said liner material.
17. The method of claim 13 wherein said liner material is separated
from said molding material by peeling said liner material from said
molding material.
18. The method of claim 6 further comprising the step of removing
the medical article from the mold through an opening in the mold
left by a sprue.
19. The method of claim 6 further comprising the step of inserting
a filler material into said mold cavity.
20. The method of claim 19 further comprising the step of curing
said filler material.
21. A system for rotationally molding a medical article comprising:
means for rotating a mold about at least two axes; means for
molding a material within said mold into the form of the medical
article; means for inserting a molding material into said mold; and
means for supplying vacuum to said mold.
22. The system of claim 21 further comprising means for inserting a
liner material into said mold.
23. A multi-axis rotationally molded medical article comprising: a
shell defining an interior cavity; said shell being formed of at
least one layer of a silicone selected from the group consisting of
room temperature acetoxy-cured silicone and platinum catalyzed
heat-cured silicone, and tin catalyzed silicone.
24. The medical article of claim 23 wherein said shell is
textured.
25. The medical article of claim 23 wherein said shell is
seamless.
26. The medical article of claim 23 wherein said shell is
patchless.
27. The medical article of claim 23 where said shell has a
thickness of from about 0.005 inches to about 0.06 inches.
28. The medical article of claim 23 further comprising a filler
material contained within said interior cavity.
29. The medical article of claim 28 wherein said filler material is
a silicone gel.
30. The medical article of claim 28 wherein said filler material is
a saline solution.
31. The medical article of claim 28 wherein said filler material is
a foam.
32. The medical article of claim 23 further comprising a removable
liner.
33. The medical article of claim 31 wherein said liner is a
thermoplastic selected from the group consisting of polyethylene,
polypropylene, nylon And fluoropolymer.
34. The medical article of claim 31 wherein said liner is a
thermoset selected from the group consisting of polyester resin,
polyurethane and epoxy.
35. The medical article of claim 23 wherein said article is a
medical implant.
36. The medical article of claim 35 wherein said article is a
breast implant.
37. The medical article of claim 23 wherein said article is an
elastomeric balloon.
38. The medical article of claim 23 wherein said article is a
catheter balloon.
Description
BACKGROUND OF THE INVENTION
[0001] This invention relates to producing castings of silicone
elastomers from solvent-based silicone dispersions using a hollow
mold and multi-axis rotation until the material devolatilizes to a
non-flowable state and is cured.
[0002] Rotational molding of many industrial, consumer, and medical
related parts from a variety of plastics is commonplace. The
plastic materials are typically polyolefins in pellet or powder
form, but some are flowable liquids, such as plastisols, with
sufficiently low viscosity, i.e. less than 5000 cps.
[0003] The rotational molding or casting method and system of the
present invention has utility in the manufacture of breast implants
and other medical devices and articles having a thin-walled shell,
typically formed from silicone elastomer, such as tissue expanders
and low-pressure elastomeric balloons. Low-pressure elastomeric
balloons are used, for example, in catheter fixation, occlusion of
blood flow, bracytherapy, and as intraaortic or intragastric
balloons for cardiovascular or ear-nose-and-throat procedures.
Other articles include feeding tubes, enema cuffs, catheters,
condoms, shunts, and embolic protection devices. The traditional
method of manufacturing these articles is by dipping a mandrel in a
solvent-based silicone dispersion to cast and form the shell.
SUMMARY OF THE INVENTION
[0004] A system and method for molding the shell of a medical
device or other molded article is disclosed. The system includes a
multi-axis rotational molding machine in which a mold is mounted.
The mold has a cavity in the shape of the article to be molded. The
mold seals to hold a vacuum.
[0005] In operation, silicone or other molding material is inserted
into the mold, vacuum is applied to the mold, the mold is rotated
about at least two axes and a molding material coats the inside
walls of the mold to form the shell or other desired article.
[0006] A rotationally molded medical article is also disclosed.
BRIEF DESCRIPTION OF THE DRAWINGS
[0007] FIG. 1 is a schematic illustration of an embodiment of the
rotational molding system of the present invention.
[0008] FIG. 2 is a cross-sectional schematic illustration of an
embodiment of the bottom piece of the two-piece case mold.
[0009] FIG. 3 is a top view schematic illustration of an embodiment
of the bottom piece of the two-piece case mold.
[0010] FIG. 4 is a cross-sectional schematic illustration of an
embodiment of the top piece of the two-piece case mold.
[0011] FIG. 5 is a top view schematic illustration of an embodiment
of the top piece of the two-piece case mold.
DETAILED DESCRIPTION
[0012] The present invention relates to four novel developments
using a rotational casting process that have direct application for
improving the process and products for these existing medical
devices.
[0013] The first development achieved by the rotational molding
system and process of the present invention relates to its use in
the rotational molding of silicones and other solvent-based or
gas-emitting materials. This has not been feasible heretofore with
most silicone elastomers, even LSR's (Liquid Silicone Rubbers),
because silicone elastomers with sufficient physical properties for
use with medical devices are usually high in molecular weight or
require fillers. These materials typically have too high of a
viscosity to be free-flowing as is required in a rotational molding
process. Such higher molecular weight polymers need to be combined
with a solvent to make a dispersion having a suitable viscosity.
This solvent-based, reduced viscosity dispersion allows application
of the silicone polymer onto a mandrel by spraying or dipping after
which the solvent is allowed to evaporate. Such a solvent-based
dispersion has not been practical for use in a rotational molding
process since there is no ready means to remove the significant
volume of solvent vapors that are trapped within the closed molds
heretofore used in rotational molding processes. However, by adding
a vacuum vent to the mold, e.g., one internal to the rotating arm
of the equipment, a means is provided to remove the solvent while
the arm is rotating and the dispersion material is flowing and
being deposited on the inner surface of the mold. Alternatively the
mold may be constructed of porous material, such as a porous metal
or ceramic through which the solvent can be evacuated over the
whole surface of the mold. This development of utilizing a vacuum
vent or porous mold in a rotational molding process is applicable
not only to silicones, but to any other materials which are
solvent-based or emit gaseous by-products during curing such as
polyurethanes or other polymers and the like.
[0014] A second aspect of the rotational molding system and process
of the present invention relates to providing a means for molding
seamless articles. Most articles made by rotational molding are
made using multi-part hollow molds. It is often undesirable for
medical products intended for implantation to have a seam or other
surface irregularities. Even with precision machining of the mold,
the articles produced by conventional rotational molding processes
have, at a minimum, a witness parting line in their outer surface
due to the mating surfaces of the mold. These mold parting lines
are eliminated in the process disclosed in the present invention by
first coating the inside of the assembled, multi-part mold with a
thin layer of molding material such as polyethylene, polypropylene,
polyester resin or the like to create a mold liner. After the liner
is cast, then the raw material, e.g. silicone, polyurethane, or
other polymer, for the desired article is injected into the mold
cavity and similarly rotationally cast inside the liner resulting
in a laminated construct. When the mold is disassembled and the
construct is removed from the mold, the liner material and the
desired article are physically separated resulting in the desired
article having a seamless configuration.
[0015] A third aspect of the rotational molding system and process
of the present invention relates to the ability to extract the
desired article from a reusable, seamless, one-piece mold. Such a
one-piece mold may be made from rotationally molded plastic or from
a metal through an electrolytic nickel process, aluminum casting,
"lost wax" technique or the like. Using any of these mold-making
methods, a one-piece mold may be constructed having a very small
opening, e.g. approximately 1".(2.54 cm) in diameter. Into this
opening is placed a sprue for dispensing the raw material to be
used in molding the desired article and a vacuum port. Because most
medical devices made using the molding system and process of the
present invention typically have very thin walls, e.g. from about
0.005" (0.0127 cm) to about 0.060" (0.1524 cm), the desired
rotationally molded shell may be collapsed after it is cured by
applying a vacuum to the inside of the article and/or by injecting
air between the article and the wall of the one-piece mold. The
thin-walled collapsed shell may then be extracted from the
one-piece mold through the opening as the sprue is removed. This
technique results in the desired molded article having an opening
corresponding in size to the opening of the one-piece mold, which
may then be patched or otherwise utilized in much the same way as
the opening on articles produced using a mandrel.
[0016] A fourth development achieved by the rotational molding
system and process of the present invention relates to its ability
to produce a patchless molded article or shell. The primary
component of any of the above-referenced medical devices is the
shell. The current dipping technology to manufacture the shell used
in these medical devices produces a shell hole because the shell
must be cut open so that it can be removed from the mandrel on
which it was formed. Subsequent steps in the construction of these
medical devices involve patching the shell hole with a separate
piece of silicone or the like. This patching process would not be
necessary if the shell is formed under selected rotational molding
methods as the shell would be whole and not require any
cutting.
[0017] Besides the four novel developments described above, there
are many other potential benefits and extensions of the rotational
molding concept that one familiar with current manufacturing of
shells and other medical articles can appreciate. The process could
be modified to produce multi-layer, multi-material laminated
shells. Surface texturing of the shell or other molded article is
another possibility.
[0018] One benefit of the invention is its reduction in the overall
use of solvent which allows for solvent condensation and recycling,
as well as reducing and almost eliminating employee exposure to
solvents used in the molding process. Another possible application
is to fill the shell or other molded article with a filler such as
a gel and cure the combined shell and filler while still in the
mold for precise implant shaping. Soft solid fills and foamed
structures such as NuSil MED4210 elastomer or Applied Silicone
#50003 liquid foam are examples of these fill materials. Another
interesting aspect is that due to the use of a liner, the mold
surface never needs finishing. Silicone material waste is
essentially eliminated compared to a dipping process. Less clean
room space is required. The process is more automated, so should be
more repeatable and easier to validate and support. The product
produced is more uniform in thickness thereby enhancing the
performance and quality of the final product. By reducing solvent
use, the invention is environmentally friendly and generates less
waste to be disposed.
[0019] Each embodiment of the present invention requires a source
of multi-axis rotation in which a mold may be mounted. An example
of such a multi-axis rotational mold machine is the Compact
Clamshell sold by FSP Machinery. This two-axis rotational mold
machine allows for an inert gas to be injected into the mold and
controlled throughout the rotational cycle.
[0020] FIG. 1 is a schematic of an embodiment of the rotational
molding system of the present invention. A two-piece case mold 100
is fixed to a multi-axis rotational mold machine 50 by clamps
securing top mold piece 10 and bottom mold piece 20 to clamp base
52 at top locking groove 15 and bottom locking groove 25
respectively. Vacuum connection 65 runs through one arm of the mold
machine 50 to the vacuum opening 35. Additionally, material
connection tube 66, through which silicone or other molding
material(s), polyethylene, polypropylene, nylon, fluoropolymer,
polyester resin, polyurethane, epoxy or other liner materials,
and/or air are injected into the mold cavity 60, may run through or
along the same arm 55a as the vacuum connection 65 or by means of
the other arm 55b. The hub 51 of the two arms rotates about axis A
in the horizontal direction, while the arms 55 rotate about axis B,
which maybe perpendicular to axis A. This allows the liner material
and silicone material to uniformly coat the surface of the mold
cavity 60. Two-piece case mold 100 may be manufactured from copper,
aluminum, or other materials. The top mold piece 10 and bottom mold
piece 20 are fitted together at their mating surfaces, sealed with
O-ring 40, and then locked into clamp base 52 of multi-axis
rotational molding machine 50. Material reservoir 90 is fluidly
coupled to connection tube 66 for providing silicone or other
molding material, liner material and/or air to cavity 60. Vacuum
source 80 and solvent condenser 70 are fluidly coupled to vacuum
connection 65.
[0021] A preferred embodiment of a two-piece case mold 100 of the
present invention is illustrated in FIGS. 2-5. The interior of the
top mold piece 10 defines a circular cavity which is used to form
the top portion of the shell or molded article. In cross-section,
top dome cavity 11 may be hemispherical in shape. At the edge 14 of
the top dome cavity 11, near the bottom of the top mold piece 10,
there is a top mold mating surface 13. Top mold mating surface 13
joins bottom mold mating surface 23 to form the parting line of the
two-piece case mold 100. Along the outside edge of the top mold
mating surface 13, located radially outward from the center of the
top mold 10, is a lip 16 having a rectangular cross-section. Lip 16
runs around the circumference of the bottom edge of the top mold
piece 10. The mold will seal to hold a vacuum along the parting
line where the mating surfaces 13, 23 meet when the top mold piece
10 and the bottom mold piece 20 are engaged to form the two-piece
case mold 100. Top locking groove 15, rectangular in cross-section,
runs around the entire exterior of top mold piece 10 allowing top
mold piece 10 to be fixed into clamp base 52 of the multi-axis
rotational molding machine 50 during the molding process.
[0022] Bottom mold piece 20 may be composed of the same material as
top mold piece 10 and may be constructed of copper, aluminum or
other materials. Bottom mold piece 20 may be bigger than the top
mold piece 10. Bottom mold piece 20 may have the same exterior
dimensions or circumference as the exterior dimensions or
circumference of top mold piece 10. However, the internal
dimensions or circumference of bottom mold piece 20 and top mold
piece 10 should coincide. Bottom mold piece 20 has a bottom locking
groove 25, rectangular in cross-section, running around the entire
exterior of bottom mold piece 20 allowing bottom mold piece 20 to
be fixed into clamp base 52 of the multi-axis rotational molding
machine 50 during the molding process. The interior of the bottom
mold piece 20 defines a circular cavity 21 which is used to form
the bottom portion of the shell or molded article. Bottom cavity 21
of bottom mold piece 20 may be hemispherical in cross-section
similar to top dome cavity 11 but is more preferably defined by a
shallow conical wall 30 sloping down to a circular opening 29. The
circular opening 29 is connected to a circular sprue tube 24 having
an outside diameter equal to the diameter of circular opening 29.
Circular sprue tube 24 is coaxial with circular opening 29 of
bottom mold piece 20 and connects to sprue opening 26 which is also
circular. Sprue opening 26 allows for materials to enter into the
two-piece case mold 100 when the bottom mold piece 20 and the top
mold piece 10 are mated.
[0023] Also connected to the circular sprue tube 24 is an inner
vacuum tube 27 perpendicular to the circular sprue tube 24. Inner
vacuum tube 27 is connected to outer vacuum tube 28 having a
diameter greater than that of inner vacuum tube 27. Outer vacuum
tube 28 is connected to vacuum opening 35 which in turn is
connected to vacuum connection 65. The larger outer vacuum tube 28
allows the vacuum connection 65 to attach to the two-piece case
mold and not enter the circular sprue tube 24.
[0024] Bottom mold mating surface 23 is different than the top mold
mating surface 13 of top mold piece 10. As seen in the
cross-section of FIG. 2, the outer edge of conical wall surface 30
transitions upward in a curve to form arc 31 such that when top
mold piece 10 and bottom mold piece 20 are engaged at their
respective mating surfaces, the edge of arc 31 is aligned with edge
14 of the mating surface 13 of top mold piece 10. Arc 31 allows the
mold 100 to have a smooth transition surface from top mold piece 10
to the bottom mold piece 20 and further allows for the top mold
piece 10 and the bottom mold piece 20 to form a tight seal when a
vacuum is applied to the mold. Radially spaced away from the center
of the bottom mold piece 20 and outside the perimeter of arc 31,
O-ring groove 34 runs around the circumference of the top edge of
the mating surface 23 of bottom mold piece 20. A typical
elastomeric O-ring 40, e.g. a Viton.RTM. O-ring, is inserted into
the O-ring groove 34 to maintain the integrity of the seal between
top mold piece 10 and bottom mold piece 20. A locking ledge 32 is
formed around the outside edge of bottom mold piece 20 into which a
corresponding lip 16 of top mold piece 10 fits to maintain the
orientation of the two mold pieces 10, 20 and form a seal when they
are mated together and locked into the clamp base 52 of the
multi-axis rotational molding machine 50 using locking grooves 15,
25. When top mold piece 10 and bottom mold piece 20 are mated
together, the two-piece case mold 100 formed thereby defines the
inside cavity 60 of the mold.
[0025] The first step in manufacturing a shell or other article
utilizing the multi-axis rotational molding system of the present
invention is to make a liner which coats the internal mold surface
of the two-piece case mold 100. The liner should cover the interior
surfaces of top dome cavity 11 and the bottom cavity 21. Covering
the internal mold surface thus masks any interruptions in the
surface, such as the mold parting lines, machining marks located on
the internal mold surface, or minor damage to the internal mold
surface. The liner may be any suitable material but should meet
several requirements. First, the liner should have a low
extractability level so it is biocompatible with the implant shell
or other molded article. The liner should also be resistant to any
solvent or solvents being used in the silicone or other materials
used in making the implant shell or other molded article. The liner
material should be able to completely and uniformly coat the
internal mold surface during the rotation of the mold by the
multi-axis rotational molding machine. If heat is used to cure the
silicone during the molding process, the liner should have a high
level of heat resistance. The liner should be easily removable or
releaseable from the mold surface and from the cured shell or other
molded article. Lastly, the liner may be used to impart a desired
surface finish to the silicone elastomer or other material, e.g.
glossy, matte, textured, etc. Suitable liner materials include:
polyethylene (Equistar.TM. # MP658-662), polypropylene (A.
Schulman.TM. #PD 8020), nylon (Capron.RTM. #8280); fluoropolymers
(DuPont.RTM. Teflon.RTM. PFA), polyester resin (Hypol.TM. #
320300-10), polyurethane (Smooth-On Smooth Cast #305) and epoxy
(Polytek.RTM. Development Corp. Polypoxy.RTM. 1010), all of which
can be found on the open market. A skilled artisan in the field
will recognize that other similar materials can replace these
listed liner materials.
[0026] A predetermined volume or weight of the chosen liner
material is dispensed into the mold so as to produce a lining of
the desired thickness. The liner material is either in the form of
a fine powder or a liquid depending on the selection of the liner
material as long as the selected material is free flowing. The
liner material is inserted into the two-piece case mold 100 through
sprue opening 26 and circular sprue tube 24. Circular sprue tube 24
extends approximately halfway into the interior cavity 60 of case
mold 100 and remains in this position during the entire process of
forming a liner and shell or other article. The liner material can
be inserted into the case mold prior to the case mold being locked
into the rotational arms of the multi-axis rotational molding
machine or after the case mold has been locked into the rotational
arms. The closed mold 100 is rotated about two or more axes
allowing the liner material inside to form a consistent coating
along the internal surface of cavity 60. The rotation of the mold
about the axes forms a liner of uniform thickness. If the liner
material is composed of thermoplastics, heat is applied so as to
cause the liner material to melt and coat the inside mold surface
as per conventional rotational molding techniques. In the case a
chemical set is used for the liner material system, such as a
polyester resin, no heat needs to be applied. In addition, air
pressure, vacuum, inert gas such as nitrogen or other vapors or
solid particles may be applied to the interior of the mold to
minimize bubbles or to affect the surface finish of the liner in
the desired manner.
[0027] Once the liner has been formed, the next step is to form the
shell or other desired article. Circular sprue tube 24 remains in
the sprue opening 26 during the entire process of curing the liner
and the molding material. To keep the sprue tube 24 clean and to
maintain a vacuum during the casting step, the exterior end of the
sprue has a removable cap. Silicone or other molding material is
injected into the interior of the mold. A predetermined amount of
molding material is inserted based on the desired size and
thickness of the finished shell or article. For breast implants,
the desired materials are usually silicones dispersed in a solvent.
NuSil MED 10-6605 is a good selection for a room temperature
acetoxy-curing (RTV) silicone dispersion. NuSil MED 10-6400 may be
used as platinum catalyzed heat-cured (HTV) silicone dispersion.
Tin catalyzed silicones or polyurethanes may also be used, as well
as other silicone elastomers or solvent systems.
[0028] After the silicone or other molding material has been
dispensed into the mold cavity 60 with the liner via the, sprue
tube 24 and sprue opening 26, the mold is rotated around at least
two axes while a vacuum is applied to its interior. The vacuum may
be applied in different fashions. The vacuum can be applied to the
sprue of a sealed mold by way of the vacuum opening 35. The vacuum
may also be applied to the interior cavity or chamber in which an
open sprue mold is rotating. Alternatively, the mold may be
constructed of a porous material and a vacuum applied to the
exterior of such porous mold. In addition, positive pressure using
either, or in combination, air, nitrogen, or other gases may be
applied intermittently to aid in bubble removal within the silicone
elastomer or other molding material. Bubbles need to be removed to
allow for a uniform smooth surface of the liner, and ultimately the
shell or other molded article. In the case of RTV silicones, which
require the presence of some water molecules in the mold cavity to
carry out the condensation reaction, the applied positive pressure
gas could include water vapor.
[0029] The silicone or other molding material is rotated and
allowed to cure as the arms of the rotational molding machine
rotate around their axes, thereby forming the desired shape.
Rotating the mold at a higher speed can compensate for a lower
viscosity level of the inserted materials. Heat is applied if
necessary or to accelerate the curing process. The silicone or
other material "sets up" and stops flowing as it is rotated and
cures in place along with the liner material. If a laminated part
is desired, the above steps may be repeated. If additional wall
thickness is desired for the shell or other molded article, the
steps may also repeated.
[0030] After the cure cycle has been completed and the silicone or
other molding material has been cured to the desired thickness, the
mold is opened at the parting line, i.e. where the mating surfaces
of the top mold piece and the bottom mold piece converge. The
formed shell or article surrounded by the liner is removed from the
mold. The shell or other molded article is separated from the liner
by one of the following methods appropriate to the liner system:
dissolving the liner in a suitable solvent; melting or burning the
liner away from the more temperature resistant shell or molded
article; tearing or breaking the liner away from the shell; or
peeling the flexible formed shell away from the liner and removing
it through the opening in the liner created by the sprue opening.
The liner may be discarded, or if the liner has not been damaged or
dissolved depending on the separation process of the liner from the
shell or molded article, the liner may be reused in the process
again.
[0031] The mold is cleaned, if necessary, of any particles that
might have remained from the previous manufacturing of the liner
and shell or other article. After cleaning, the mold is ready for
the next cycle. If the previously used liner is in satisfactory
condition, the liner can be reused in the next molding process with
or without a two-piece case mold.
[0032] If the shell is being used for breast implants, the formed
shell is ready for further assembly or processing consistent with
the usual manner in creating a final breast implant product. For
example, the implant shell may be filled with a filler material of
silicone gel, saline solution or other biocompatible filler
material well known to those of skill in the art.
[0033] It will be understood that the above-described embodiments
are merely illustrative of the principles of the invention and that
other arrangements may be devised by those skilled in the art
without departing from the spirit and scope of the invention.
* * * * *