U.S. patent application number 10/116276 was filed with the patent office on 2003-10-09 for batteries comprising alkali-transition metal phosphates and preferred electrolytes.
Invention is credited to Huang, Haitao, Pugh, James, Saidi, Mohammed Y..
Application Number | 20030190527 10/116276 |
Document ID | / |
Family ID | 28673938 |
Filed Date | 2003-10-09 |
United States Patent
Application |
20030190527 |
Kind Code |
A1 |
Pugh, James ; et
al. |
October 9, 2003 |
Batteries comprising alkali-transition metal phosphates and
preferred electrolytes
Abstract
Lithium batteries comprising: (a) an electrode comprising a
material of the formula A.sub.aM.sub.b(XY.sub.4).sub.cZ.sub.d,
wherein (i) A is an alkaline metal and 0<a.ltoreq.9; (ii) M
comprises a transition metal, and 1.ltoreq.b.ltoreq.3; (iii)
XY.sub.4 is X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4,
or mixtures thereof, where X' is P, As, Sb, Si, Ge, V, S, or
mixtures thereof; X" is P, As, Sb, Si, Ge, V, or mixtures thereof;
Y' is halogen, S, N, or mixtures thereof; 0.ltoreq.x<3; and
0<y.ltoreq.2; and 0<c.ltoreq.3; and (iv) Z is OH, halogen, or
mixtures thereof, and 0.ltoreq.d.ltoreq.6; and (b) a
counter-electrode; and (c) an electrolyte comprising an alkyl
and/or alkylene carbonate and a cyclic ester. Preferably, M
additionally comprises at least one non-transition metal. Preferred
embodiments include those having an olivine structure, where c=1,
and those having a NASICON structure, where c=3.
Inventors: |
Pugh, James; (Henderson,
NV) ; Saidi, Mohammed Y.; (Henderson, NV) ;
Huang, Haitao; (Henderson, NV) |
Correspondence
Address: |
VALENCE TECHNOLOGY, INC.
301 CONESTOGA WAY
HENDERSON
NV
89015
US
|
Family ID: |
28673938 |
Appl. No.: |
10/116276 |
Filed: |
April 3, 2002 |
Current U.S.
Class: |
429/231.9 ;
429/221; 429/223; 429/224; 429/231.5; 429/231.6; 429/231.95 |
Current CPC
Class: |
H01M 4/136 20130101;
H01M 4/624 20130101; H01M 4/623 20130101; H01M 4/582 20130101; H01M
10/0525 20130101; H01M 4/0471 20130101; H01M 4/5815 20130101; H01M
10/0568 20130101; H01M 10/0569 20130101; H01M 4/56 20130101; H01M
4/625 20130101; H01M 4/622 20130101; Y02E 60/10 20130101; H01M
4/5825 20130101; H01M 2004/027 20130101 |
Class at
Publication: |
429/231.9 ;
429/231.95; 429/221; 429/223; 429/231.5; 429/224; 429/231.6 |
International
Class: |
H01M 004/58 |
Claims
What is claimed is:
1. A lithium battery comprising: (a) a first electrode comprising
an active material of the formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ.sub.d, wherein (i) A is selected
from the group consisting of Li, Na, K, and mixtures thereof, and
0<a .ltoreq.9; (ii) M is one or more metals, comprising at least
one metal which is capable of undergoing oxidation to a higher
valence state, and 1.ltoreq.b.ltoreq.3; (iii) XY.sub.4 is selected
from the group consisting of X'O.sub.4-xY'.sub.x,
X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures thereof, where X' is
selected from the group consisting of P, As, Sb, Si, Ge, V, S, and
mixtures thereof; X" is selected from the group consisting of P,
As, Sb, Si, Ge, V and mixtures thereof; Y' is selected from the
group consisting of halogen, S, N, and mixtures thereof;
0.ltoreq.x.ltoreq.3; and 0<y.ltoreq.2; and 0<c.ltoreq.3; (iv)
Z is OH, halogen, or mixtures thereof, and 0.ltoreq.d.ltoreq.6; and
wherein M, XY.sub.4, Z, a, b, c, d, x and y are selected so as to
maintain electroneutrality of said compound; (b) a second electrode
which is a counter-electrode to said first electrode; and (c) an
electrolyte comprising a mixture of a cyclic ester and a carbonate
selected from the group consisting of alkyl carbonates, alkylene
carbonates, and mixtures thereof.
2. A battery according to claim 1, wherein c is about 1.
3. A battery according to claim 2, wherein A comprises Li, and
0.1.ltoreq.a.ltoreq.2, and said active material has an olivine
structure.
4. A battery according to claim 1, wherein c is about 3, and said
active material has a NASICON structure.
5. A battery according to claim 1, wherein M comprises
M'.sub.1-mM".sub.m, where M' is at least one element from Groups 4
to 11 of the Periodic Table; M" is at least one element from Groups
2, 3, and 12-16 of the Periodic Table; and 0<m<1.
6. A battery according to claim 5, wherein M' is selected from the
group consisting of Fe, Co, Ni, Mn, Cu, V, Zr, Ti, Cr, and mixtures
thereof.
7. A battery according to claim 6, wherein M' is selected from the
group consisting of Fe, Co, Mn, Ti, and mixtures thereof.
8. A battery according to claim 5, wherein M' comprises Fe and
Co.
9. A battery according to claim 8, wherein M" is selected from the
group consisting of Mg, Ca, Zn, Sr, Pb, Cd, Sn, Ba, Be, Al, and
mixtures thereof.
10. A battery according to claim 9, wherein M" is selected from the
group consisting of Mg, Ca, Al, and mixtures thereof.
11. A battery according to claim 1, wherein X' comprises Si or a
mixture of Si and P, and X" comprises Si or a mixture of Si and
P.
12. A battery according to claim 1, wherein XY.sub.4 is selected
from the group consisting Of X'O.sub.4-xY'.sub.x,
X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures thereof, where X' is
P and X" is P; and 0<x<3; and 0<y<4.
13. A battery according to claim 12, wherein XY.sub.4 is
PO.sub.4-xF.sub.x, and 0<x.ltoreq.1.
14. A battery according to claim 1, wherein Z comprises F, and
0.1<d.ltoreq.4.
15. A battery according to claim 1, wherein said carbonate
comprises an alkylene carbonate having a ring size of from 5 to 8
atoms and is unsubstituted or substituted with lower alkyl on one
or more carbon atoms.
16. A battery according to claim 1, wherein said carbonate
comprises a C.sub.1-C.sub.6 alkyl carbonate which is unsubstituted
or substituted with C.sub.1-C.sub.4 alkyl on one or more carbon
atoms.
17. A battery according to claim 1, wherein said cyclic ester has a
ring size of from 4 to 7 atoms, and is unsubstituted or substituted
on one or more carbon atoms with a lower alkyl group.
18. A battery according to claim 17, wherein said carbonate
comprises an alkylene carbonate, and the weight ratio of said
cyclic ester to said alkylene carbonate is from about 1:1 to about
5:1.
19. A battery according to claim 18, wherein said carbonate
additionally comprises an alkyl carbonate.
20. A battery according to claim 18, wherein said carbonate is
ethylene carbonate and said cyclic ester is
.gamma.-butyrolactone.
21. A battery comprising: (a) a first electrode comprising an
active material of the formula Li.sub.aM.sub.b(PO.sub.4)Z.sub.d,
wherein (i) 0.1<a.ltoreq.4; (ii) M is one or more metals,
comprising at least one metal which is capable of undergoing
oxidation to a higher valence state, and 1.ltoreq.b.ltoreq.3; and
(iii) Z is halogen, and 0.1<d.ltoreq.4; and wherein M, Z, a, b,
and d are selected so as to maintain electroneutrality of said
compound; (b) a second electrode which is a counter-electrode to
said first electrode; and (c) an electrolyte comprising a mixture
of a cyclic ester and a carbonate selected from the group
consisting of alkyl carbonates, alkylene carbonates, and mixtures
thereof.
22. A battery according to claim 21, wherein
0.2.ltoreq.a.ltoreq.1.
23. A battery according to claim 22, wherein M comprises
M'.sub.1-mM".sub.m, where M' is at least one element from Groups 4
to 11 of the Periodic Table; M" is at least one element from Groups
2, 3, and 12-16 of the Periodic Table; and 0<m<1.
24. A battery according to claim 23, wherein M' is selected from
the group consisting of Fe, Co, Mn, Cu, V, Cr, and mixtures
thereof, and M" is selected from the group consisting of Mg, Ca,
Zn, Ba, Al, and mixtures thereof.
25. A battery according to claim 21, wherein said carbonate
comprises an alkylene carbonate having a ring size of from 5 to 8
atoms and is unsubstituted or substituted with lower alkyl on one
or more carbon atoms.
26. A battery according to claim 21, wherein said carbonate
comprises a C.sub.1-C.sub.6 alkyl carbonate which is unsubstituted
or substituted with C.sub.1-C.sub.4 alkyl on one or more carbon
atoms.
27. A battery according to claim 25, wherein said cyclic ester has
a ring size of from 4 to 7 atoms, and is unsubstituted or
substituted on one or more carbon atoms with a lower alkyl
group.
28. A battery according to claim 26, wherein said alkylene
carbonate is ethylene carbonate, said cyclic ester is
.gamma.-butyrolactone, and the weight ratio of said cyclic ester to
said alkylene carbonate is from about 1:1 to about 5:1.
29. A battery comprising: (a) a first electrode comprising an
active material of the formula
Li.sub.aCo.sub.eFe.sub.fM.sup.1.sub.gM.sup.2.sub.-
hM.sup.3.sub.iXY.sub.4 wherein (i) 0<a.ltoreq.2, e>0, and
f>0; (ii) M.sup.1 is one or more transition metals, where
g.gtoreq.0; (iii) M.sup.2 is one or more +2 oxidation state
non-transition metals, where h.gtoreq.0; (iv) M.sup.3 is one or
more +3 oxidation state non-transition metals, where i.gtoreq.0;
and (v) XY.sub.4 is selected from the group consisting of
X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures
thereof, where X' is selected from the group consisting of P, As,
Sb, Si, Ge, V, S, and mixtures thereof; X" is selected from the
group consisting of P, As, Sb, Si, Ge, V and mixtures thereof; Y'
is selected from the group consisting of halogen, S, N, and
mixtures thereof; 0.ltoreq.x.ltoreq.3; and 0<y.ltoreq.2; and
wherein (e+f+g+h+i)<2, and M.sup.1, M.sup.2, M.sup.3, XY.sub.4,
a, e, f, g, h, i, x, and y are selected so as to maintain
electroneutrality of said compound; and (b) a second electrode
which is a counter-electrode to said first electrode; and (c) an
electrolyte comprising an electrolyte salt, a cyclic ester and a
carbonate selected from the group consisting of alkyl carbonates,
alkylene carbonates, and mixtures thereof.
30. A battery according to claim 29, wherein
0.8.ltoreq.(e+f+g+h+i).ltoreq- .1.2.
31. A battery according to claim 30, wherein
0.9.ltoreq.(e+f+g+h+i).ltoreq- .1.
32. A battery according to claim 30, wherein e.gtoreq.0.5.
33. A battery according to claim 32, wherein e.gtoreq.0.8.
34. A battery according to claim 31, wherein
0.01.ltoreq.f.ltoreq.0.5.
35. A battery according to claim 34, wherein
0.05.ltoreq.f.ltoreq.0.15.
36. A battery according to claim 31, wherein
0.01.ltoreq.g.ltoreq.0.5.
37. A battery according to claim 36, wherein
0.05.ltoreq.g.ltoreq.0.2.
38. A battery according to claim 36, wherein M.sup.1 is selected
from the group consisting of Ti, V, Cr, Mn, Ni, Cu and mixtures
thereof.
39. A battery according to claim 38, wherein M.sup.1 is selected
from the group consisting of Mn, Ti, and mixtures thereof.
40. A battery according to claim 31, wherein (h+i)>0.
41. A battery according to claim 40, wherein
0.01.ltoreq.(h+i).ltoreq.0.5.
42. A battery according to claim 41, wherein
0.02.ltoreq.(h+i).ltoreq.0.3.
43. A battery according to claim 41, wherein
0.01.ltoreq.h.ltoreq.0.2.
44. A battery according to claim 43, wherein
0.01.ltoreq.h.ltoreq.0.1.
45. A battery according to claim 43, wherein M.sup.2 is selected
from the group consisting of Be, Mg, Ca, Sr, Ba, and mixtures
thereof.
46. A battery according to claim 45, wherein M.sup.2 is Mg.
47. A battery according to claim 41, wherein
0.01.ltoreq.i.ltoreq.0.2.
48. A battery according to claim 47, wherein
0.01.ltoreq.i.ltoreq.0.1.
49. A battery according to claim 47, wherein M is selected from the
group consisting of B, Al, Ga, In and mixtures thereof.
50. A battery according to claim 49, wherein M.sup.3 is Al.
51. A battery according to claim 29, wherein XY.sub.4 is
PO.sub.4.
52. A battery according to claim 51, wherein e.gtoreq.0.8, and
0.05.ltoreq.f.ltoreq.0.15.
53. A battery according to claim 52, wherein
0.01.ltoreq.h.ltoreq.0.1.
54. A battery according to claim 53, wherein M.sup.2 is selected
from the group consisting of Be, Mg, Ca, Sr, Ba, and mixtures
thereof.
55. A battery according to claim 52, wherein
0.01.ltoreq.i.ltoreq.0.1.
56. A battery according to claim 55, wherein M.sup.3 is Al.
57. A battery according to claim 29, wherein XY.sub.4 is
PO.sub.4-xF.sub.x, and 0<x.ltoreq.1.
58. A battery according to claim 57, wherein
0.01.ltoreq.x.ltoreq.0.05.
59. A battery according to claim 57, wherein e.gtoreq.0.8, and
0.05.ltoreq.f.ltoreq.0.15.
60. A battery according to claim 59, wherein
0.01.ltoreq.h.ltoreq.0.1.
61. A battery according to claim 60, wherein M.sup.2 is selected
from the group consisting of Be, Mg, Ca, Sr, Ba, and mixtures
thereof.
62. A battery according to claim 59, wherein
0.01.ltoreq.i.ltoreq.0.1.
63. A battery according to claim 62, wherein M.sup.3 is Al.
64. A battery according to claim 29, wherein said carbonate
comprises an alkylene carbonate having a ring size of from 5 to 8
atoms and is unsubstituted or substituted with lower alkyl on one
or more carbon atoms.
65. A battery according to claim 64, wherein said alkylene
carbonate is selected from the group consisting of ethylene
carbonate, 1,3-propylene carbonate, 1,4-butylene carbonate,
1,5-pentylene carbonate, 1,2-propylene carbonate, 2,3-butylene
carbonate, 1,2-butylene carbonate, and mixtures thereof.
66. A battery according to claim 65, wherein said alkylene
carbonate is ethylene carbonate.
67. A battery according to claim 29, wherein said carbonate
comprises a C.sub.1-C.sub.6 alkyl carbonate which is unsubstituted
or substituted with C.sub.1-C.sub.4 alkyl on one or more carbon
atoms.
68. A battery according to claim 67, wherein said alkyl carbonate
is selected from the group consisting of diethyl carbonate, ethyl
methyl carbonate, dimethyl carbonate, and mixtures thereof.
69. A battery according to claim 66, wherein said cyclic ester has
a ring size of from 4 to 7 atoms, and is unsubstituted or
substituted on one or more carbon atoms with a lower alkyl
group.
70. A battery according to claim 69, wherein said cyclic ester is
selected from the group consisting of substituted or unsubstituted
.beta.-propiolactone; substituted or unsubstituted
.gamma.-butyrolactone, substituted or unsubstituted
.delta.-valerolactone, substituted or unsubstituted
.epsilon.-caprolactone, and mixtures thereof.
71. A battery according to claim 69, wherein said cyclic ester is
.gamma.-butyrolactone.
72. A battery according to claim 29, wherein said electrolyte salt
is a lithium salt selected from the group consisting of
LiAsF.sub.6, LiPF.sub.6, LiClO.sub.4, LiB(C.sub.6H.sub.5).sub.4,
LiAlCl.sub.4, LiBr, LiBF.sub.4, LiSO.sub.3CF.sub.3,
LiN(SO.sub.2CF.sub.3).sub.2, LiN(SO.sub.2C.sub.2F.sub.5).sub.2, and
mixtures thereof.
73. A battery according to claim 72, wherein said salt is
LiBF.sub.4.
74. A battery according to claim 29, wherein said cyclic ester
comprises at least about 60% of said electrolyte, and the weight
ratio of said cyclic ester to said alkylene carbonate is from about
1:1 to about 5:1.
75. A battery according to claim 74, wherein said weight ratio is
about 3:1.
76. A lithium battery of claim 29, wherein said first electrode is
a cathode, and said second electrode is an insertion anode.
77. A lithium battery of claim 76, wherein said second electrode
comprises a material selected from the group consisting of metal
oxides, metal chalcogenides, carbon, graphite, and mixtures
thereof.
78. A battery comprising: (a) a first electrode comprising an
active material having an olivine structure, of the formula
LiM(PO.sub.4-xY'.sub.x) wherein M is
M.sup.1.sub.gM.sup.2.sub.hM.sup.3.su- b.iM.sup.4.sub.j, and (i)
M.sup.1 is one or more transition metals; (ii) M.sup.2 is one or
more +2 oxidation state non-transition metals; (iii) M.sup.3 is one
or more +3 oxidation state non-transition metals, (iv) M.sup.4 is
one or more +1 oxidation state non-transition metals; (v) Y' is
halogen; and g>0, each of h, i, and j.gtoreq.0;
(g+h+i+j).ltoreq.1, and 0.ltoreq.x.ltoreq.0.5; and (b) a second
electrode which is a counter-electrode to said first electrode; and
(c) an electrolyte comprising an electrolyte salt, an alkylene
carbonate, and a cyclic ester and a carbonate selected from the
group consisting of alkyl carbonates, alkylene carbonates, and
mixtures thereof.
79. An electrode active material according to claim 78, wherein
g.gtoreq.0.8.
80. An electrode active material according to claim 79, wherein
g.gtoreq.0.9.
81. An electrode active material according to claim 79, wherein
M.sup.1 is a +2 oxidation state transition metal selected from the
group consisting of V, Cr, Mn, Fe, Co, Ni, and mixtures
thereof.
82. An electrode active material according to claim 81, wherein
M.sup.1 is selected from the group consisting of Fe, Co, and
mixtures thereof.
83. An electrode active material according to claim 79, wherein
(h+i)>0.
84. An electrode active material according to claim 83, wherein
0.01.ltoreq.(h+i).ltoreq.0.5.
85. An electrode active material according to claim 84, wherein
0.02.ltoreq.(h+i).ltoreq.0.3.
86. An electrode active material according to claim 83, wherein
0.01.ltoreq.h.ltoreq.0.2.
87. An electrode active material according to claim 86, wherein
0.01.ltoreq.h.ltoreq.0.1.
88. An electrode active material according to claim 86, wherein
M.sup.2 is selected from the group consisting of Be, Mg, Ca, Sr,
Ba, and mixtures thereof.
89. An electrode active material according to claim 83, wherein
0.01.ltoreq.i.ltoreq.0.2.
90. An electrode active material according to claim 89, wherein
0.01.ltoreq.i.ltoreq.0.1.
91. An electrode active material according to claim 89, wherein
M.sup.3 is Al.
92. An electrode active material according to claim 79, wherein
j=0.
93. An electrode active material according to claim 79, wherein
0.01.ltoreq.j.ltoreq.0.1.
94. An electrode active material according to claim 93, wherein
M.sup.4 is selected from the group consisting of Li, Na, and K.
95. An electrode active material according to claim 94, wherein
M.sup.4 is Li.
96. An electrode active material according to claim 79, wherein
x=0.
97. An electrode active material according to claim 96, wherein
g.gtoreq.0.8, and (g+h+i+j)=1.
98. An electrode active material according to claim 97, wherein
0.01.ltoreq.h.ltoreq.0.1 and M.sup.2 is selected from the group
consisting of Be, Mg, Ca, Sr, Ba, and mixtures thereof.
99. An electrode active material according to claim 97, wherein
0.01.ltoreq.i.ltoreq.0.1, and M.sup.3 is Al.
100. An electrode active material according to claim 97, wherein
0.01.ltoreq.j.ltoreq.0.1, and M.sup.4 is Li.
101. An electrode active material according to claim 78, wherein
0<x.ltoreq.1.
102. An electrode active material according to claim 101, wherein
0.01.ltoreq.x.ltoreq.0.05, and (g+h+i+j)<1.
103. An electrode active material according to claim 102, wherein
g.gtoreq.0.8.
104. An electrode active material according to claim 103, wherein
0.01.ltoreq.h.ltoreq.0.1, and M.sup.2 is selected from the group
consisting of Be, Mg, Ca, Sr, Ba, and mixtures thereof.
105. An electrode active material according to claim 103, wherein
0.01.ltoreq.i.ltoreq.0.1, and M.sup.3 is Al.
106. An electrode active material according to claim 103, wherein
j=0.
107. An electrode active material according to claim 106, wherein
(g+h+i)=1-x.
108. A battery according to claim 81, wherein said active material
is selected from the group consisting of: LiFePO.sub.4;
LiFe.sub.0.9Mg.sub.0.1PO.sub.4; LiFe.sub.0.8Mg.sub.0.2PO.sub.4;
Li.sub.1.025Cu.sub.0.85Fe.sub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.80Fe.sub.0.10Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.75Fe.sub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.7(Fe.sub.0.4Mn.sub.0.6).sub.0.2Al.sub.0.025Mg.sub.0.-
05PO.sub.4,
LiCo.sub.0.8Fe.sub.0.1Al.sub.0.025Ca.sub.0.05PO.sub.3.975F.sub-
.0.025,
LiCo.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.0-
25, LiCo.sub.0.8Fe.sub.0.1Ti.sub.0.025Mg.sub.0.05PO.sub.4;
Li.sub.1.025Co.sub.0.8Fe.sub.0.1Ti.sub.0.025Al.sub.0.025PO.sub.4;
Li.sub.1.025Co.sub.0.8Fe.sub.0.1Ti.sub.0.025Mg.sub.0.025PO.sub.3.975F.sub-
.0.025; LiCu.sub.0.825Fe.sub.0.1Ti.sub.0.025Mg.sub.0.025PO.sub.4;
LiCu.sub.0.85Fe.sub.0.075Ti.sub.0.025Mg.sub.0.025PO.sub.4; and
mixtures thereof.
109. A battery according to claim 29, wherein said active material
is
LiCo.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025.
110. A battery according to claim 80, wherein said carbonate
comprises an alkylene carbonate having a ring size of from 5 to 8
atoms and is unsubstituted or substituted with lower alkyl on one
or more carbon atoms.
111. A battery according to claim 110, wherein said alkylene
carbonate is ethylene carbonate.
112. A battery according to claim 80, wherein said carbonate
comprises C.sub.1-C.sub.6 alkyl carbonate which is unsubstituted or
substituted with C.sub.1-C.sub.4 alkyl on one or more carbon
atoms.
113. A battery according to claim 112, wherein said alkyl carbonate
is diethyl carbonate.
114. A battery according to claim 80, wherein said cyclic ester has
a ring size of from 4 to 7 atoms, and is unsubstituted or
substituted on one or more carbon atoms with a lower alkyl
group.
115. A battery according to claim 114, wherein said cyclic ester is
.gamma.-butyrolactone.
116. A battery according to claim 80, wherein said salt is selected
from the group consisting of LiAsF.sub.6, LiPF.sub.6, LiClO.sub.4,
LiB(C.sub.6H.sub.5).sub.4, LiAlCl.sub.4, LiBr, LiBF.sub.4,
LiSO.sub.3CF.sub.3, LiN(SO.sub.2CF.sub.3).sub.2,
LiN(SO.sub.2C.sub.2F.sub- .5).sub.2, and mixtures thereof.
117. A battery according to claim 80, wherein the weight ratio of
said cyclic ester to said alkylene carbonate is from about 1:1 to
about 5:1.
118. A battery according to claim 117, wherein said weight ratio is
about 3:1.
119. A lithium battery of claim 80, wherein said first electrode is
a cathode, and said second electrode is an insertion anode.
120. A lithium battery of claim 119, wherein said second electrode
comprises a material selected from the group consisting of metal
oxides, metal chalcogenides, carbon, graphite, and mixtures
thereof.
121. A battery comprising: (a) a first electrode comprising an
active material of the formula
LiCo.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.05PO.s-
ub.3.975F.sub.0.025 (b) a second electrode which is a
counter-electrode to said first electrode; and (c) an electrolyte
comprising (i) an electrolyte salt; (ii) an alkylene carbonate
having a ring size of from 5 to 8 atoms and unsubstituted or
substituted with lower alkyl on one or more carbon atoms; and (iii)
a cyclic ester having a ring size of from 4 to 7 atoms, and is
unsubstituted or substituted on one or more carbon atoms with a
lower alkyl group.
122. A battery according to claim 120, wherein said first electrode
is a cathode, said second electrode is an insertion anode, said
alkylene ester is ethylene carbonate; said cyclic ester is
.gamma.-butyrolactone; the weight ratio of said cyclic ester to
said alkylene carbonate is from about 1:1 to about 5:1; and said
electrolyte salt is LiBF.sub.4.
Description
FIELD OF THE INVENTION
[0001] This invention relates to batteries. In particular, this
invention relates to batteries comprising active materials
comprising lithium or other alkali metals, transition metals, and
phosphates or similar moieties, with electrolytes comprising
alkylene carbonates and cyclic esters.
BACKGROUND OF THE INVENTION
[0002] A wide variety of electrochemical cells, or "batteries," is
known in the art. In general, batteries are devices that convert
chemical energy into electrical energy, by means of an
electrochemical oxidation-reduction reaction. Batteries are used in
a wide variety of applications, particularly as a power source for
devices that cannot practicably be powered by centralized power
generation sources (e.g., by commercial power plants using utility
transmission lines).
[0003] Batteries can be generally described as comprising three
components: an anode that contains a material that is oxidized
(yields electrons) during discharge of the battery (i.e., while it
is providing power); a cathode that contains a material that is
reduced (accepts electrons) during discharge of the battery; and an
electrolyte that provides for transfer of ions between the cathode
and anode. During discharge, the anode is the negative pole of the
battery, and the cathode is the positive pole. Batteries can be
more specifically characterized by the specific materials that make
up each of these three components. Selection of these components
can yield batteries having specific voltage and discharge
characteristics that can be optimized for particular
applications.
[0004] Batteries can also be generally categorized as being
"primary," where the electrochemical reaction is essentially
irreversible, so that the battery becomes unusable once discharged;
and "secondary," where the electrochemical reaction is, at least in
part, reversible so that the battery can be "recharged" and used
more than once. Secondary batteries are increasingly used in many
applications, because of their convenience (particularly in
applications where replacing batteries can be difficult), reduced
cost (by reducing the need for replacement), and environmental
benefits (by reducing the waste from battery disposal).
[0005] There are a variety of secondary battery systems known in
the art. Among the most common systems are lead-acid,
nickel-cadmium, nickel-zinc, nickel-iron, silver oxide, nickel
metal hydride, rechargeable zinc-manganese dioxide, zinc-bromide,
metal-air, and lithium batteries. Systems containing lithium and
sodium afford many potential benefits, because these metals are
light in weight, while possessing high standard potentials. For a
variety of reasons, lithium batteries are, in particular,
commercially attractive because of their high energy density,
higher cell voltages, and long shelf-life.
[0006] Lithium batteries are prepared from one or more lithium
electrochemical cells containing electrochemically active
(electroactive) materials. Among such batteries are those having
metallic lithium anodes and metal chalcogenide (oxide) cathodes,
typically referred to as "lithium metal" batteries. The electrolyte
typically comprises a salt of lithium dissolved in one or more
solvents, typically nonaqueous aprotic organic solvents. Other
electrolytes are solid electrolytes (typically polymeric matrixes)
that contain an ionic conductive medium (typically a lithium
containing salt dissolved in organic solvents) in combination with
a polymer that itself may be ionically conductive but electrically
insulating.
[0007] Cells having a metallic lithium anode and metal chalcogenide
cathode are charged in an initial condition. During discharge,
lithium metal yields electrons to an external electrical circuit at
the anode. Positively charged ions are created that pass through
the electrolyte to the electrochemically active (electroactive)
material of the cathode. The electrons from the anode pass through
the external circuit, powering the device, and return to the
cathode.
[0008] Another lithium battery uses an "insertion anode" rather
than lithium metal, and is typically referred to as a "lithium ion"
battery. Insertion or "intercalation" electrodes contain materials
having a lattice structure into which an ion can be inserted and
subsequently extracted. Rather than chemically altering the
intercalation material, the ions slightly expand the internal
lattice lengths of the compound without extensive bond breakage or
atomic reorganization. Insertion anodes contain, for example,
lithium metal chalcogenide, lithium metal oxide, or carbon
materials such as coke and graphite. These negative electrodes are
used with lithium-containing insertion cathodes. In their initial
condition, the cells are not charged, since the anode does not
contain a source of cations. Thus, before use, such cells must be
charged in order to transfer cations (lithium) to the anode from
the cathode. During discharge the lithium is then transferred from
the anode back to the cathode. During subsequent recharge, the
lithium is again transferred back to the anode where it reinserts.
This back-and-forth transport of lithium ions (Li+) between the
anode and cathode during charge and discharge cycles had led to
these cells as being called "rocking chair" batteries.
[0009] A variety of materials have been suggested for use as
cathode active materials in lithium batteries. Such materials
include, for example, MoS.sub.2, MnO.sub.2, TiS.sub.2, NbSe.sub.3,
LiCoO.sub.2, LiNiO.sub.2, LiMn.sub.2O.sub.4, V.sub.6O.sub.13,
V.sub.2O.sub.5, SO.sub.2, CuCl.sub.2. Transition metal oxides, such
as those of the general formula Li.sub.xM.sub.2O.sub.y, are among
those materials preferred in such batteries having intercalation
electrodes. Other materials include lithium transition metal
phosphates, such as LiFePO.sub.4, and
Li.sub.3V.sub.2(PO.sub.4).sub.3. Such materials having structures
similar to olivine or NASICON materials are among those known in
the art. Cathode active materials among those known in the art are
disclosed in S. Hossain, "Rechargeable Lithium Batteries (Ambient
Temperature)," Handbook of Batteries, 2d ed., Chapter 36, Mc-Graw
Hill (1995); U.S. Pat. No. 4,194,062, Carides, et al., issued Mar.
18, 1980; U.S. Pat. No. 4,464,447, Lazzari, et al., issued Aug. 7,
1984; U.S. Pat. No. 5,028,500, Fong et al., issued Jul. 2, 1991;
U.S. Pat. No. 5,130,211, Wilkinson, et al., issued Jul. 14, 1992;
U.S. Pat. No. 5,418,090, Koksbang et al., issued May 23, 1995; U.S.
Pat. No. 5,514,490, Chen et al., issued May 7, 1996; U.S. Pat. No.
5,538,814, Kamauchi et al., issued Jul. 23, 1996; U.S. Pat. No.
5,695,893, Arai, et al., issued Dec. 9, 1997; U.S. Pat. No.
5,804,335, Kamauchi, et al., issued Sep. 8, 1998; U.S. Pat. No.
5,871,866, Barker et al., issued Feb. 16, 1999; U.S. Pat. No.
5,910,382, Goodenough, et al., issued Jun. 8, 1999; PCT Publication
WO/00/31812, Barker, et al., published Jun. 2, 2000; PCT
Publication WO/00/57505, Barker, published Sep. 28, 2000; U.S. Pat.
No. 6,136,472, Barker et al., issued Oct. 24, 2000; U.S. Pat. No.
6,153,333, Barker, issued Nov. 28, 2000; European Patent
Publication 1,049,182, Ravet et al., published Nov. 2, 2000; PCT
Publication WO/01/13443, Barker, published Feb. 22, 2001; PCT
Publication WO/01/54212, Barker et al., published Jul. 26, 2001;
PCT Publication WO/01/84655, Barker et al., published Nov. 8,
2001.
[0010] Preferably, such a cathode material exhibits a high free
energy of reaction with lithium, is able to release and insert a
large quantity of lithium, maintains its lattice structure upon
insertion and extraction of lithium, allows rapid diffusion of
lithium, affords good electrical conductivity, is not significantly
soluble in the electrolyte system of the battery, and is readily
and economically produced. However, many of the cathode materials
known in the art lack one or more of these characteristics. As a
result, for example, many such materials are not economical to
produce, afford insufficient voltage, have insufficient charge
capacity, or lose their ability to be recharged over multiple
cycles.
SUMMARY OF THE INVENTION
[0011] The invention provides batteries comprising active materials
comprising lithium or other alkali metals, transition metals and
optionally other metals, and a phosphate, substituted phosphate or
similar moiety. In particular, the present invention provides a
lithium battery comprising
[0012] (a) a first electrode comprising an active material of the
formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ.sub.d,
[0013] wherein
[0014] (i) A is selected from the group consisting of Li, Na, K,
and mixtures thereof, and 0<a .ltoreq.9;
[0015] (ii) M is one or more metals, comprising at least one metal
which is capable of undergoing oxidation to a higher valence state,
and 1.ltoreq.b.ltoreq.3;
[0016] (iii) XY.sub.4 is selected from the group consisting of
X'O.sub.4-xY'.sub.x, X'O.sub.4-y.sub.Y'.sub.2y, X"S.sub.4, and
mixtures thereof, where X' is selected from the group consisting of
P, As, Sb, Si, Ge, V, S, and mixtures thereof; X" is selected from
the group consisting of P, As, Sb, Si, Ge, V and mixtures thereof;
Y' is selected from the group consisting of halogen, S, N, and
mixtures thereof; 0.ltoreq.x<3; and 0<y.ltoreq.2; and
0<c.ltoreq.3;
[0017] (iv) Z is OH, halogen, or mixtures thereof, and
0.ltoreq.d.ltoreq.6; and
[0018] wherein M, XY.sub.4, Z, a, b, c, d, x and y are selected so
as to maintain electroneutrality of said compound;
[0019] (b) a second electrode which is a counter-electrode to said
first electrode; and
[0020] (c) an electrolyte comprising a mixture of a cyclic ester
and a carbonate selected from the group consisting of alkyl
carbonates, alkylene carbonates, and mixtures thereof.
[0021] In a preferred embodiment, M comprises two or more
transition metals from Groups 4 to 11 of the Periodic Table. In
another preferred embodiment, M comprises M'M", where M' is at
least one transition metal from Groups 4 to 11 of the Periodic
Table; and M" is at least one element from Groups 2, 3, and 12-16
of the Periodic Table. Preferred embodiments include those where
c=1, those where c=2, and those where c=3. Preferred embodiments
include those where a.ltoreq.1 and c=1, those where a=2 and c=1,
and those where a.gtoreq.3 and c=3. Preferred embodiments also
include those having a structure similar to the mineral olivine
(herein "olivines"), and those having a structure similar to
NASICON (NA Super Ionic CONductor) materials (herein "NASICONs").
In a particularly preferred embodiment, M comprises
Co.sub.eFe.sub.fM.sup.1.sub.gM.sup.2.su- b.hM.sup.3.sub.i, where
M.sup.1 is at least one transition metal from Groups 4 to 11 of the
Periodic Table; M.sup.2 comprises one or more +2 oxidation state
non-transition metals, and M.sup.3 comprises one or more +3
oxidation state non-transition metals, and e+f+g=b. In such an
embodiment, preferably A comprises Li, 0.8.ltoreq.a.ltoreq.1.2,
0.8.ltoreq.b.ltoreq.1.5, and c=1. As used herein, unless otherwise
specified, a variable described algebraically as equal to ("="),
less than or equal to (".ltoreq."), or greater than or equal to
(".gtoreq.") a number is intended to subsume values or ranges of
values about equal or functionally equivalent to said number.
[0022] It has been found that the novel batteries of this invention
afford benefits over such materials and devices among those known
in the art. Such benefits include one or more of increased
capacity, enhanced cycling capability, enhanced reversibility, and
reduced costs. Specific benefits and embodiments of the present
invention are apparent from the detailed description set forth
herein. It should be understood, however, that the detailed
description and specific examples, while indicating embodiments
among those preferred, are intended for purposes of illustration
only and are not intended to limited the scope of the
invention.
DESCRIPTION OF THE INVENTION
[0023] The present invention provides batteries comprising certain
electrode active materials and electrolytes. As used herein,
"battery" refers to a device comprising one or more electrochemical
cells for the production of electricity. Each electrochemical cell
comprises an anode, a cathode, and an electrolyte. Two or more
electrochemical cells may be combined, or "stacked," so as to
create a multi-cell battery having a voltage that is the sum of the
voltages of the individual cells.
[0024] The electrode active materials of this invention may be used
in the anode, the cathode, or both. Preferably, the active
materials of this invention are used in the cathode. (As used
herein, the terms "anode" and "cathode" refer to the electrodes at
which oxidation and reduction occur, respectively, during battery
discharge. During charging of the battery, the sites of oxidation
and reduction are reversed. Also, as used herein, the words
"preferred" and "preferably" refer to embodiments of the invention
that afford certain benefits, under certain circumstances. However,
other embodiments may also be preferred, under the same or other
circumstances. Furthermore, the recitation of one or more preferred
embodiments does not imply that other embodiments are not useful
and is not intended to exclude other embodiments from the scope of
the invention.)
[0025] Electrode Active Materials:
[0026] The present invention provides active materials (herein
"electrode active materials") comprising lithium or other alkali
metals, a transition metal, a phosphate or similar moiety, and
(optionally) a halogen or hydroxyl moiety. Such electrode active
materials include those of the formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ.sub.d. (As used herein, the word
"include," and its variants, is intended to be non-limiting, such
that recitation of items in a list is not to the exclusion of other
like items that may also be useful in the materials, compositions,
devices, and methods of this invention.)
[0027] A is selected from the group consisting of Li (lithium), Na
(sodium), K (potassium), and mixtures thereof. In a preferred
embodiment, A is Li, a mixture of Li with Na, a mixture of Li with
K, or a mixture of Li, Na and K. In another preferred embodiment, A
is Na, or a mixture of Na with K. Preferably "a" is from about 0.1
to about 6, more preferably from about 0.2 to about 6. Where c=1, a
is preferably from about 0.1 to about 3, preferably from about 0.2
to about 2. In a preferred embodiment, where c=1, a is less than
about 1. In another preferred embodiment, where c=1, a is about 2.
Preferably "a" is from about 0.8 to about 1.2. Where c=2, a is
preferably from about 0.1 to about 6, preferably from about 1 to
about 6. Where c=3, a is preferably from about 0.1 to about 6,
preferably from about 2 to about 6, preferably from about 3 to
about 6. In another embodiment, "a" is preferably from about 0.2 to
about 1.0.
[0028] In a preferred embodiment, removal of alkali metal from the
electrode active material is accompanied by a change in oxidation
state of at least one of the metals comprising M. The amount of
said metal that is available for oxidation in the electrode active
material determines the amount of alkali metal that may be removed.
Such concepts are, in general application, well known in the art,
e.g., as disclosed in U.S. Pat. No. 4,477,541, Fraioli, issued Oct.
16, 1984; and U.S. Pat. No. 6,136,472, Barker, et al., issued Oct.
24, 2000, both of which are incorporated by reference herein.
[0029] Referring to the general formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ.su- b.d, the amount (a') of alkali
metal that can be removed, as a function of the quantity of (b')
and valence state (V.sup.M) of oxidizable metal (M), is
a'=b'(.DELTA.V.sup.M),
[0030] where .DELTA.V.sup.M is the difference between the valence
state of the metal in the active material and a valence state
readily available for the metal. (The term oxidation state and
valence state are used in the art interchangeably.) For example,
for an active material comprising iron (Fe) in the +2 oxidation
state, .DELTA.V.sup.M=1, wherein iron may be oxidized to the +3
oxidation state (although iron may also be oxidized to a +4
oxidation state in some circumstances). If b=1 (one atomic unit of
Fe per atomic unit of material), the maximum amount (a') of alkali
metal (oxidation state +1) that can be removed during cycling of
the battery is 1 (one atomic units of alkali metal). If b=1.25, the
maximum amount of (a') of alkali metal that can be removed during
cycling of the battery is 1.25.
[0031] In general, the value of "a" in the active materials can
vary over a wide range. In a preferred embodiment, active materials
are synthesized for use in preparing a lithium ion battery in a
discharged state. Such active materials are characterized by a
relatively high value of "a", with a correspondingly low oxidation
state of M of the active material. As the battery is charged from
its initial uncharged state, an amount a' of lithium is removed
from the active material as described above. The resulting
structure, containing less lithium (i.e., a-a') than in the
as-prepared state as well as the transition metal in a higher
oxidation state than in the as-prepared state, is characterized by
lower values of a, while essentially maintaining the original value
of b. The active materials of this invention include such materials
in their nascent state (i.e., as manufactured prior to inclusion in
an electrode) and materials formed during operation of the battery
(i.e., by insertion or removal of Li or other alkaline metal).
[0032] The value of "b" and the total valence of M in the active
material must be such that the resulting active material is
electrically neutral (i.e., the positive charges of all cationic
species in the material balance the negative charges of all anionic
species), as further discussed below. The net valence of M
(V.sup.M) having a mixture of elements (M1, M2 . . . Mt) may be
represented by the formula
V.sup.M=V.sup.M1b.sub.1+V.sup.M2b.sub.2+ . . . V.sup.Mtb.sub.t,
[0033] where b.sub.1+b.sub.2+ . . . b.sub.t=1, and V.sup.M1 is the
oxidation state of M1, V.sup.M2 is the oxidation state of M2, etc.
(The net valence of M and other components of the electrode active
material is discussed further, below.)
[0034] M is one or more metals including at least one metal that is
capable of undergoing oxidation to a higher valence state (e.g.,
Co.sup.+2.fwdarw.Co.sup.+3), preferably a transition metal selected
from Groups 4-11 of the Periodic Table. As referred to herein,
"Group" refers to the Group numbers (i.e., columns) of the Periodic
Table as defined in the current IUPAC Periodic Table. See, e.g.,
U.S. Pat. No. 6,136,472, Barker et al., issued Oct. 24, 2000,
incorporated by reference herein. In another preferred embodiment,
M further comprises a non-transition metal selected from Groups 2,
3, and 12-16 of the Periodic Table.
[0035] In another preferred embodiment, preferably where c=1, M
comprises Co.sub.e,Fe.sub.fM.sup.1.sub.gM.sup.2.sub.hM.sup.3.sub.i,
wherein M.sup.1 is at least one transition metal from Groups 4 to
11, M.sup.2 is at least one +2 oxidation state non-transition
metal, M.sup.3 is at least one +3 oxidation state non transition
metal, e.gtoreq.0, f.gtoreq.0, g.gtoreq.0, h.gtoreq.0, i.gtoreq.0
and (e+f+g+h+i)=b. Preferably, at least one of e and f are greater
than zero, more preferably both. In a preferred embodiment
0<(e+f+g+h+i).ltoreq.2, more preferably
0.8.ltoreq.(e+f+g).ltoreq.1.2, and even more preferably
0.9.ltoreq.(e+f+g).ltoreq.1.0. Preferably, e.gtoreq.0.5, more
preferably e.gtoreq.0.8. Preferably, 0.01.ltoreq.f.ltoreq.0.5, more
preferably 0.05.ltoreq.f.ltoreq.0.15. Preferably,
0.01.ltoreq.g.ltoreq.0.5, more preferably 0.05.ltoreq.g.ltoreq.0.2.
In a preferred embodiment, (h+i)>1, preferably
0.01.ltoreq.(h+i).ltoreq.0.5, and even more preferably
0.01.ltoreq.(h+i).ltoreq.0.1. Preferably, 0.01.ltoreq.h.ltoreq.0.2,
more preferably 0.01.ltoreq.h.ltoreq.0.1. Preferably
0.01.ltoreq.i.ltoreq.0.2, more preferably
0.01.ltoreq.i.ltoreq.0.1.
[0036] Transition metals useful herein include those selected from
the group consisting of Ti (Titanium), V (Vanadium), Cr (Chromium),
Mn (Manganese), Fe (Iron), Co (Cobalt), Ni (Nickel), Cu (Copper),
Zr (Zirconium), Nb (Niobium), Mo (Molybdenum), Ru (Ruthenium), Rh
(Rhodium), Pd (Palladium), Ag (Silver), Cd (Cadmium), Hf (Hafnium),
Ta (Tantalum), W (Tungsten), Re (Rhenium), Os (Osmium), Ir
(Iridium), Pt (Platinum), Au (Gold), Hg (Mercury), and mixtures
thereof. Preferred are the first row transition series (the 4th
Period of the Periodic Table), selected from the group consisting
of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, and mixtures thereof.
Particularly preferred transition metals include those selected
from the group consisting of Fe, Co, Ti, Mn, and mixtures thereof.
In a preferred embodiment, M is Co.sub.1-mFe.sub.m, where
0<m.ltoreq.0.5. Preferably 0.01<m.ltoreq.0.2. Although, a
variety of oxidation states for such transition metals are
available, in some embodiments it is most preferable that the
transition metals have a +2 oxidation state. As used herein, the
recitation of a genus of elements, materials or other components,
from which an individual component or mixture of components can be
selected, is intended to include all possible sub-generic
combinations of the listed components, and mixtures thereof.
[0037] In a preferred embodiment, M further comprises one or more
non-transition metals. As referred to herein, "non-transition
metals" include metals and metalloids from Groups 2, 3, and 12-16
of the Periodic Table that are capable of forming stable active
materials and do not significantly impede the insertion or removal
of lithium or other alkaline metals from the active materials under
normal operating conditions. Preferably, such elements do not
include C (carbon), Si (silicon), N (nitrogen) and P (phosphorus).
Preferred non-transition metals include those not readily capable
of undergoing oxidation to a higher valence state in the electrode
active material under normal operating conditions. Among the
non-transition metals useful herein are those selected from the
group consisting of Group 2 elements, particularly Be (Beryllium),
Mg (Magnesium), Ca (Calcium), Sr (Strontium), Ba (Barium); Group 3
elements, particularly Sc (Scandium), Y (Yttrium), and the
lanthamides, particularly La (Lanthanum), Ce (Cerium), Pr
(Praseodymium), Nd (Neodymium), Sm (Samarium); Group 12 elements,
particularly Zn (zinc) and Cd (cadmium); Group 13 elements,
particularly B (Boron), Al (Aluminum), Ga (Gallium), In (Indium),
Tl (Thallium); Group 14 elements, particularly Si (Silicon), Ge
(Germanium), Sn (Tin), and Pb (Lead); Group 15 elements,
particularly As (Arsenic), Sb (Antimony), and Bi (Bismuth); Group
16 elements, particularly Te (Tellurium); and mixtures thereof.
Preferred non-transition metals include the Group 2 elements, Group
12 elements, Group 13 elements, and Group 14 elements. Particularly
preferred non-transition metals include those selected from the
group consisting of Mg, Ca, Zn, Sr, Pb, Cd, Sn, Ba, Be, Al, and
mixtures thereof. Particularly preferred are non-transition metals
selected from the group consisting of Mg, Ca, Zn, Ba, Al, and
mixtures thereof.
[0038] As further discussed herein, "b" is selected so as to
maintain electroneutrality of the electrode active material. In a
preferred embodiment, where c=1, b is from about 1 to about 2,
preferably about 1. In another preferred embodiment, where c=2, b
is from about 2 to about 3, preferably about 2.
[0039] XY.sub.4 is an anion, preferably selected from the group
consisting of X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4,
and mixtures thereof, where X' is selected from the group
consisting of P (phosphorus), As (arsenic), Sb (antimony), Si
(silicon), Ge (germanium), V (vanadium) S (sulfur), and mixtures
thereof; X" is selected from the group consisting of P, As, Sb, Si,
Ge, V, and mixtures thereof. XY.sub.4 anions useful herein include
phosphate, silicate, germanate, vanadate, arsenate, antimonate,
sulfur analogs thereof, and mixtures thereof. In a preferred
embodiment, X' and X" are each selected from the group consisting
of P, Si, and mixtures thereof. In a particularly preferred
embodiment, X' and X" are P.
[0040] Y' is selected from the group consisting of halogen, S, N,
and mixtures thereof. Preferably Y' is F (fluorine).In a preferred
embodiment 0.ltoreq.x.ltoreq.3; and 0<y.ltoreq.2, such that a
portion of the oxygen (O) in the XY.sub.4 moiety is substituted
with halogen. In another preferred embodiment, x and y are 0. In a
particularly preferred embodiment XY.sub.4 is X'O.sub.4, where X'
is preferably P or Si, more preferably P. In another particularly
preferred embodiment, XY.sub.4 is PO.sub.4-xY'.sub.x, where Y' is
halogen and 0<x.ltoreq.1. Preferably 0.01.ltoreq.x.ltoreq.0.05,
more preferably 0.02.ltoreq.x.ltoreq.0.03.
[0041] In a preferred embodiment, XY.sub.4 is PO.sub.4 (a phosphate
group) or a mixture of PO.sub.4 with another XY.sub.4 group (i.e.,
where X' is not P, Y' is not O, or both, as defined above). When
part of the phosphate group is substituted, it is preferred that
the substitute group be present in a minor amount relative to the
phosphate. In a preferred embodiment, XY.sub.4 comprises 80% or
more phosphate and up to about 20% of one or more phosphate
substitutes. Phosphate substitutes include, without limitation,
silicate, sulfate, antimonate, germanate, arsenate,
monofluoromonophosphate, difluoromonophosphate, sulfur analogs
thereof, and combinations thereof. Preferably, XY.sub.4 comprises a
maximum of about 10% of a phosphate substitute or substitutes. (The
percentages are based on mole percent.) Preferred XY.sub.4 groups
include those of the formula (PO.sub.4).sub.1-k(B).sub.k, where B
represents an XY.sub.4 group or combination of XY.sub.4 groups
other than phosphate, and k.ltoreq.0.5. Preferably, k.ltoreq.0.8,
more preferably less than about k.ltoreq.0.2, more preferably
k.ltoreq.0.1.
[0042] Z is OH, halogen, or mixtures thereof. In a preferred
embodiment, Z is selected from the group consisting of OH
(hydroxyl), F (fluorine), Cl (chlorine), Br (bromine) and mixtures
thereof. In a preferred embodiment, Z is OH. In another preferred
embodiment, Z is F, or mixtures of F with OH, Cl, or Br. In one
preferred embodiment, d=0. In another preferred embodiment, d>0,
preferably from about 0.1 to about 6, more preferably from about
0.2 to about 6. In such embodiments, where c=1, d is preferably
from about 0.1 to about 3, preferably from about 0.2 to about 2. In
a preferred embodiment, where c=1, d is about 1. Where c=2, d is
preferably from about 0.1 to about 6, preferably from about 1 to
about 6. Where c=3, d is preferably from about 0.1 to about 6,
preferably from about 2 to about 6, preferably from about 3 to
about 6.
[0043] The composition of M, XY.sub.4, Z and the values of a, b, c,
d, x, and y are selected so as to maintain electroneutrality of the
electrode active material. As referred to herein
"electroneutrality" is the state of the electrode active material
wherein the sum of the positively charged species (e.g., A and M)
in the material is equal to the sum of the negatively charged
species (e.g., XY.sub.4) in the material. Preferably, the XY.sub.4
moieties are comprised to be, as a unit moiety, an anion having a
charge of -2, -3, or -4, depending on the selection of X', X", Y',
and x and y. When XY.sub.4 is a mixture of groups such as the
preferred phosphate/phosphate substitutes discussed above, the net
charge on the XY.sub.4 anion may take on non-integer values,
depending on the charge and composition of the individual groups
XY.sub.4 in the mixture.
[0044] In general, the valence state of each component element of
the electrode active material may be determined in reference to the
composition and valence state of the other component elements of
the material. By reference to the general formula
A.sub.aM.sub.b(XY.sub.4).su- b.cZ.sub.d, the electroneutrality of
the material may be determined using the formula
(V.sup.A)a+(V.sup.M)b+(V.sup.X)c=(V.sup.Y)4c+(V.sup.Z)d
[0045] where V.sup.A is the net valence of A, V.sup.M is the net
valence of M, V.sup.Y is the net valence of Y, and V.sup.Z is the
net valence of Z. As referred to herein, the "net valence" of a
component is (a) the valence state for a component having a single
element which occurs in the active material in a single valence
state; or (b) the mole-weighted sum of the valence states of all
elements in a component comprising more than one element, or
comprising a single element having more than one valence state. The
net valence of each component is represented in the following
formulae.
(V.sup.A)b=[(V.sup.A1)a.sup.1+(Va1.sup.A2)a.sup.2+ . . .
(V.sup.An)a.sup.n]/n; a.sup.1+a.sup.2+ . . . a.sup.n=a
(V.sup.M)b=[(V.sup.M1)b.sup.1+(V.sup.M2)b.sup.2+ . . .
(V.sup.Mn)b.sup.n]/n; b.sup.1+b.sup.2+ . . . b.sup.n=b
(V.sup.X)c=[(V.sup.X1)c.sup.1+(V.sup.X2)c.sup.2+ . . .
(V.sup.Xn)c.sup.n]/n; c.sup.1+c.sup.2+ . . . c.sup.n=c
(V.sup.Y)c=[(V.sup.Y1)c.sup.1+(V.sup.Y2)c.sup.2+ . . .
(V.sup.Yn)c.sup.n]/n; c.sup.1+c.sup.2+ . . . c.sup.n=c
(V.sup.Z)d=[(V.sup.Z1)d.sup.1+(V.sup.Z2)d.sup.2+ . . .
(V.sup.Zn)d.sup.n]/n; d.sup.1+d.sup.2+ . . . d.sup.n=d
[0046] In general, the quantity and composition of M is selected
given the valency of X, the value of "c," and the amount of A, so
long as M comprises at least one metal that is capable of
oxidation. The calculation for the valence of M can be simplified,
where V.sup.A=1, V.sup.Z=1, as follows.
[0047] For compounds where c=1:
(V.sup.M)b=(V.sup.Y)4+d-a-(V.sup.X)
[0048] For compounds where c=3:
(V.sup.M)b=(V.sup.Y)12+d-a-(V.sup.X)3
[0049] The values of a, b, c, d, x, and y may result in
stoichiometric or non-stoichiometric formulas for the electrode
active materials. In a preferred embodiment, the values of a, b, c,
d, x, and y are all integer values, resulting in a stoichiometric
formula. In another preferred embodiment, one or more of a, b, c,
d, x and y may have non-integer values. It is understood, however,
in embodiments having a lattice structure comprising multiple units
of a non-stoichiometric formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ.sub.d, that the formula may be
stoichiometric when looking at a multiple of the unit. That is, for
a unit formula where one or more of a, b, c, d, x, or y is a
non-integer, the values of each variable become an integer value
with respect to a number of units that is the least common
multiplier of each of a, b, c, d, x and y. For example, the active
material Li.sub.2Fe.sub.0.5Mg.sub.0.5- PO.sub.4F is
non-stoichiometric. However, in a material comprising two of such
units in a lattice structure, the formula is
Li.sub.4FeMg(PO.sub.4).- sub.2F.sub.2.
[0050] A preferred electrode active material embodiment comprises a
compound of the formula
Li.sub.aM.sub.b(PO.sub.4)Z.sub.d,
[0051] wherein
[0052] (a) 0.1<a.ltoreq.4;
[0053] (b) M is M'.sub.1-mM".sub.m, where M' is at least one
transition metal from Groups 4 to 11 of the Periodic Table; M" is
at least one non-transition metal from Groups 2, 3, and 12-16 of
the Periodic Table, 0<m<1, and 1.ltoreq.b.ltoreq.3; and
[0054] (c) Z comprises halogen, and 0.ltoreq.d.ltoreq.4; and
[0055] wherein M, Z, a, b, and d are selected so as to maintain
electroneutrality of said compound. Preferably, M' is selected from
the group consisting of Fe, Co, Ni, Mn, Cu, V, Zr, Ti, Cr, and
mixtures thereof; more preferably M' is selected from the group
consisting of Fe, Co, Mn, Cu, V, Cr, and mixtures thereof.
Preferably, M" is selected from the group consisting of Mg, Ca, Zn,
Sr, Pb, Cd, Sn, Ba, Be, Al, and mixtures thereof; more preferably
M" is selected from the group consisting of Mg, Ca, Zn, Ba, Al, and
mixtures thereof. Preferably Z comprises F.
[0056] Another preferred embodiment comprises a compound of the
formula:
A.sub.aM.sub.b(XY.sub.4).sub.3Z.sub.d,
[0057] wherein
[0058] (a) A is selected from the group consisting of Li, Na, K,
and mixtures thereof, and 2.ltoreq.a .ltoreq.9;
[0059] (b) M comprises one or more metals, comprising at least one
metal which is capable of undergoing oxidation to a higher valence
state, and 1.ltoreq.b.ltoreq.3;
[0060] (c) XY.sub.4 is selected from the group consisting of
X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures
thereof, where X' is selected from the group consisting of P, As,
Sb, Si, Ge, V, S, and mixtures thereof; X" is selected from the
group consisting of P, As, Sb, Si, Ge, V, and mixtures thereof; Y'
is selected from the group consisting of halogen, S, N, and
mixtures thereof; 0.ltoreq.x<3; and 0<y<4; and
[0061] (d) Z is OH, halogen, or mixtures thereof, and
0.ltoreq.d.ltoreq.6; and
[0062] wherein M, XY.sub.4, Z, a, b, d, x and y are selected so as
to maintain electroneutrality of said compound. In a preferred
embodiment, A comprises Li, or mixtures of Li with Na or K. In
another preferred embodiment, A comprises Na, K, or mixtures
thereof. In a preferred embodiment, M comprises two or more
transition metals from Groups 4 to 11 of the Periodic Table,
preferably transition metals selected from the group consisting of
Fe, Co, Ni, Mn, Cu, V, Zr, Ti, Cr, and mixtures thereof. In another
preferred embodiment, M comprises M'.sub.1-mM".sub.m, where M' is
at least one transition metal from Groups 4 to 11 of the Periodic
Table; and M" is at least one element from Groups 2, 3, and 12-16
of the Periodic Table; and 0<m<1. Preferably, M' is selected
from the group consisting of Fe, Co, Ni, Mn, Cu, V, Zr, Ti, Cr, and
mixtures thereof; more preferably M' is selected from the group
consisting of Fe, Co, Mn, Cu, V, Cr, and mixtures thereof.
Preferably, M" is selected from the group consisting of Mg, Ca, Zn,
Sr, Pb, Cd, Sn, Ba, Be, Al, and mixtures thereof; more preferably,
M" is selected from the group consisting of Mg, Ca, Zn, Ba, Al, and
mixtures thereof. In a preferred embodiment, XY.sub.4 is PO.sub.4.
In another preferred embodiment, X' comprises As, Sb, Si, Ge, S,
and mixtures thereof; X" comprises As, Sb, Si, Ge and mixtures
thereof; and 0<x<3. In a preferred embodiment, Z comprises F,
or mixtures of F with Cl, Br, OH, or mixtures thereof. In another
preferred embodiment, Z comprises OH, or mixtures thereof with Cl
or Br.
[0063] Another preferred embodiment comprises a compound of the
formula
A.sub.aM.sup.1.sub.eM.sup.2.sub.fM.sup.3.sub.gXY.sub.4,
[0064] wherein
[0065] (a) A is selected from the group consisting of Li, Na, K,
and mixtures thereof, and 0<a .ltoreq.2;
[0066] (b) M.sup.1 comprises one or more transition metals, where
e>0;
[0067] (c) M.sup.2 comprises one or more +2 oxidation state non
transition metals, where f>0;
[0068] (d) M.sup.3 comprises one or more +3 oxidation state
non-transition metal, where g>0; and
[0069] (e) XY.sub.4 is selected from the group consisting of
X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures
thereof, where X' is selected from the group consisting of P, As,
Sb, Si, Ge, V, S, and mixtures thereof; X" is selected from the
group consisting of P, As, Sb, Si, Ge, V, and mixtures thereof; Y'
is selected from the group consisting of halogen, S, N, and
mixtures thereof; 0<x<3; and 0<y<2; and
[0070] wherein e+f+g<2, and M.sup.1, M.sup.2, M.sup.3, XY.sub.4,
a, e, f, g, x, and y are selected so as to maintain
electroneutrality of said compound. In embodiments where XY.sub.4
is PO.sub.4-xY'.sub.x and M.sup.1 is a +2 oxidation state
transition metal, a +2e+2f+3g=3-x.
[0071] Preferably, e+f+g=b. In a preferred embodiment
0<(e+f+g)<2, more preferably 0.8.ltoreq.(e+f+g).ltoreq.1.5,
and even more preferably 0.9.ltoreq.(e+f+g).ltoreq.1, wherein
0.01.ltoreq.(f+g).ltoreq.0.5, more preferably
0.05.ltoreq.(f+g).ltoreq.0.2, and even more preferably
0.05.ltoreq.(f+g).ltoreq.0.1.
[0072] In a preferred embodiment, A is Li. Preferably, M.sup.1 is
at least one transition metal from Groups 4 to 11 of the Periodic
Table; M.sup.2 is at least one non-transition metal from Groups 2,
3, and 12-16 of the Periodic Table, and M.sup.3 is a +3 oxidation
state metal selected from Group 13. Preferably M.sup.1 is selected
from the group consisting of Fe, Co, Ni, Mn, Cu, V, Zr, Ti, Cr, and
mixtures thereof; more preferably M.sup.1 is a +2 oxidation state
transition metal selected from the group consisting of Fe, Co, Mn,
Cu, V, Cr, and mixtures thereof. Preferably M.sup.2 is selected
from the group consisting +2 oxidation state non-transition metals
and mixtures thereof; more preferably M.sup.2 is selected from the
group consisting of Be, Mg, Ca, Sr, Ba, Ra, Zn, Cd, Hg and mixtures
thereof. Preferably, M.sup.3 is a +3 oxidation state non-transition
metal, preferably M.sup.3 is selected from Group 13, more
preferably Sc, Y, La, Ac, B, Al, Ga, In, Tl and mixtures thereof.
Preferably M.sup.3 is Al. Preferably 0<(f+g)<1, preferably
0.01.ltoreq.(f+g).ltoreq.0.3, more preferably
0.05.ltoreq.(f+g).ltoreq.0.- 1. Preferably,
0.01.ltoreq.f.ltoreq.0.3, more preferably 0.05.ltoreq.f.ltoreq.0.1,
and even more preferably 0.01.ltoreq.f.ltoreq.0.03. Also
preferably, 0.01.ltoreq.g.ltoreq.0.3, more preferably
0.05.ltoreq.g.ltoreq.0.1, and even more preferably
0.01.ltoreq.g.ltoreq.0.03.
[0073] Another preferred embodiment comprises a compound of the
formula
Li.sub.aCO.sub.eFe.sub.fM.sup.1.sub.gM.sup.2.sub.hM.sup.3.sub.iXY.sub.4
[0074] wherein
[0075] (a) 0<a.ltoreq.2, e>0, and f>0;
[0076] (b) M.sup.1 is one or more transition metals, where
g.gtoreq.0;
[0077] (C) M.sup.2 is one or more +2 oxidation state non-transition
metals, where h.gtoreq.0;
[0078] (d) M.sup.3 is one or more +3 oxidation state non-transition
metals, where i.gtoreq.0; and
[0079] (e) XY.sub.4 is selected from the group consisting of
X'O.sub.4-xY'.sub.x, X'O.sub.4-yY'.sub.2y, X"S.sub.4, and mixtures
thereof, where X' is selected from the group consisting of P, As,
Sb, Si, Ge, V, S, and mixtures thereof; X" is selected from the
group consisting of P, As, Sb, Si, Ge, V, and mixtures thereof; Y'
is selected from the group consisting of halogen, S, N, and
mixtures thereof; 0.ltoreq.x.ltoreq.3; and 0<y.ltoreq.2;
[0080] wherein (e+f+g+h+i).ltoreq.2, and M.sup.1, M.sup.2, M.sup.3,
XY.sub.4, a, e, f, g, h, i, x, and y are selected so as to maintain
electroneutrality of said compound. Preferably,
0.8.ltoreq.(e+f+g+h+i).lt- oreq.1.2, more preferably
0.9.ltoreq.(e+f+g+h+i).ltoreq.1. Preferably, e>0.5, more
preferably, e.gtoreq.0.8. Preferably, 0.01.ltoreq.f.ltoreq.0.5,
more preferably, 0.05.ltoreq.f.ltoreq.0.15. Preferably,
0.01.ltoreq.g.ltoreq.0.5, more preferably,
0.05.ltoreq.g.ltoreq.0.2. Preferably M.sup.1 is selected from the
group consisting of Ti, V, Cr, Mn, Ni, Cu and mixtures thereof.
Preferably, M.sup.1 is selected from the group consisting of Mn,
Ti, and mixtures thereof.
[0081] Preferably, (h+i)>0, more preferably
0.01.ltoreq.(h+i).ltoreq.0.- 5, more preferably
0.02.ltoreq.(h+i).ltoreq.0.3. Preferably, 0.01.ltoreq.h.ltoreq.0.2,
more preferably, 0.01.ltoreq.h.ltoreq.0.1. Preferably, M.sup.2 is
selected from the group consisting of Be, Mg, Ca, Sr, Ba, and
mixtures thereof. More preferably, M.sup.2 is Mg. Preferably,
0.01.ltoreq.i.ltoreq.0.2, more preferably 0.01.ltoreq.i.ltoreq.0.1.
Preferably, M.sup.3 is selected from the group consisting of B, Al,
Ga, In, and mixtures thereof. More preferably, M.sup.3 is Al.
[0082] In one embodiment, XY.sub.4 is PO.sub.4. In another
embodiment, XY.sub.4 is PO.sub.4-xF.sub.x, and 0<x.ltoreq.1,
preferably, 0.01.ltoreq.x.ltoreq.0.05.
[0083] Another preferred embodiment comprises a compound having an
olivine structure. During charge and discharge of the battery,
lithium ions are added to, and removed from, the active material
preferably without substantial changes in the crystal structure of
the material. Such materials have sites for the alkali metal (e.g.,
Li), the transition metal (M), and the XY.sub.4 (e.g., phosphate)
moiety. In some embodiments, all sites of the crystal structure are
occupied. In other embodiments, some sites may be unoccupied,
depending on, for example, the oxidation states of the metal (M).
Among such preferred compounds are those of the formula
LiM(PO.sub.4-xY'.sub.x)
[0084] wherein M is
M.sup.1.sub.gM.sup.2.sub.hM.sup.3.sub.iM.sup.4.sub.j, and
[0085] (a) M.sup.1 is one or more transition metals;
[0086] (b) M.sup.2 is one or more +2 oxidation state non-transition
metals;
[0087] (c) M.sup.3 is one or more +3 oxidation state non-transition
metals,
[0088] (d) M.sup.4 is one or more +1 oxidation state non-transition
metals; and
[0089] (e) Y' is halogen; and
[0090] g,>0; h.gtoreq.0; i.gtoreq.0; j.gtoreq.0;
(g+h+i+j).ltoreq.1; and the net valence of M is 2-x. Preferably,
g.gtoreq.0.8, more preferably, g.gtoreq.0.9. Preferably, M.sup.1 is
a +2 oxidation state transition metal selected from the group
consisting of V, Cr, Mn, Fe, Co, Ni, and mixtures thereof. More
preferably, M.sup.1 is selected from the group consisting of Fe,
Co, and mixtures thereof. Preferably M.sup.1 additionally comprises
Ti.
[0091] Preferably, (h+i)>0.1, more preferably,
0.02.ltoreq.(h+i).ltoreq- .0.5, more preferably,
0.02.ltoreq.(h+i).ltoreq.0.3. Preferably, 0.01.ltoreq.h.ltoreq.0.2,
more preferably, 0.01.ltoreq.h.ltoreq.0.1. Preferably, M.sup.2 is
selected from the group consisting of Be, Mg, Ca, Sr, Ba, and
mixtures thereof. Preferably, 0.01.ltoreq.i.ltoreq.0.2, more
preferably, 0.01.ltoreq.i.ltoreq.0.1. Preferably, M.sup.3 is
Al.
[0092] In one embodiment, j=0. In another embodiment,
0.01.ltoreq.j.ltoreq.0.1. Preferably, M4 is selected from the group
consisting of Li, Na, and K. More preferably, M.sup.4 is Li.
[0093] In one embodiment, x=0. In another embodiment,
0<x.ltoreq.1. In such an embodiment, preferably,
0.01.ltoreq.x.ltoreq.0.05, and (g+h+i+j)<1. In an embodiment
where j=0, preferably, (g+h+i)=1-x.
[0094] Non-limiting examples of active materials of the invention
include the following:
Li.sub.0.95Co.sub.0.8Fe.sub.0.15Al.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.85Fe.sub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.80Fe.sub.0.10Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Cu.sub.0.45Fe.sub.0.45Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.75Fe.sub.0.15Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.7(Fe.sub.0.4Mn.sub.0.6).sub.0.2Al.sub.0.025Mg.sub.0.-
05PO.sub.4,
Li.sub.1.025Co.sub.0.75Fe.sub.0.15Al.sub.0.02Mg.sub.0.05PO.sub- .4,
Li.sub.1.025Co.sub.0.85Fe.sub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.7Fe.sub.0.08Mn.sub.0.12A.sub.0.025Mg.sub.0.05PO.sub.-
4,
LiCo.sub.0.75Fe.sub.0.15Al.sub.0.025Ca.sub.0.05PO.sub.3.975F.sub.0.025,
LiCo.sub.0.80Fe.sub.0.10Al.sub.0.025Ca.sub.0.05PO.sub.3.975F.sub.0.025,
Li.sub.1.025Co.sub.0.6Fe.sub.0.1Mn.sub.0.075Mg.sub.0.025Al.sub.0.05PO.sub-
.4,
Li.sub.1.0Na.sub.0.25Co.sub.0.6Fe.sub.0.1Cu.sub.0.075Mg.sub.0.025Al.su-
b.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.075PO- .sub.4,
Li.sub.1.025Co.sub.0.6Fe.sub.0.05Al.sub.0.12Mg.sub.0.025PO.sub.3.7-
5F.sub.0.025,
Li.sub.1.025Co.sub.0.7Fe.sub.0.1Mg.sub.0.025Al.sub.0.04PO.su-
b.3.75F.sub.0.25,
Li.sub.0.75Co.sub.0.5Fe.sub.0.025Mn.sub.0.025Ca.sub.0.01-
5Al.sub.0.04PO.sub.3F,
Li.sub.1.025Cu.sub.0.6Fe.sub.0.05B.sub.0.12Ca.sub.0-
.0325PO.sub.3.75F.sub.0.25,
Li.sub.1.025Cu.sub.0.65Fe.sub.0.05Mg.sub.0.125-
Al.sub.0.1PO.sub.3.75F.sub.0.25,
Li.sub.1.025Co.sub.0.65Fe.sub.0.05Mg.sub.-
0.065Al.sub.0.14PO.sub.3.975F.sub.0.025,
Li.sub.1.075Co.sub.0.8Fe.sub.0.05-
Mg.sub.0.025Al.sub.0.05PO.sub.3.975F.sub.0.025,
LiCo.sub.0.8Fe.sub.0.1Al.s-
ub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025,
Li.sub.0.25Fe.sub.0.7Al.sub.0.- 45PO.sub.4,
LiMnAl.sub.0.067(PO.sub.4).sub.0.8(SiO.sub.4).sub.0.2,
Li.sub.0.95Cu.sub.0.9Al.sub.0.05Mg.sub.0.05PO.sub.4,
Li.sub.0.95Fe.sub.0.8Ca.sub.0.15Al.sub.0.05PO.sub.4,
Li.sub.0.25MnBe.sub.0.425Ga.sub.0.3SiO.sub.4,
Li.sub.0.5Na.sub.0.25Mn.sub- .0.6Ca.sub.0.375Al.sub.0.1PO.sub.4,
Li.sub.0.25Al.sub.0.25Mg.sub.0.25Co.su- b.0.75PO.sub.4,
Na.sub.0.55B.sub.0.15Ni.sub.0.75Ba.sub.0.25PO.sub.4,
Li.sub.1.025Cu.sub.0.9Al.sub.0.025Mg.sub.0.05PO.sub.4,
K.sub.1.025Ni.sub.0.09Al.sub.0.025Ca.sub.0.05PO.sub.4,
Li.sub.0.95Cu.sub.0.9Al.sub.0.05Mg.sub.0.05PO.sub.4,
Li.sub.0.95Fe.sub.0.8Ca.sub.0.15Al.sub.0.05PO.sub.4,
Li.sub.0.025Co.sub.0.7(Fe.sub.0.4Mn.sub.0.6).sub.0.2Al.sub.0.025Mg.sub.0.-
05PO.sub.4,
Li.sub.1.025Co.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.05PO.sub.- 4,
Li.sub.1.025Cu.sub.0.9Al.sub.1.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.75Fe.sub.0.15Al.sub.0.025Mg.sub.0.025PO.sub.4,
LiCo.sub.0.75Fe.sub.0.15Al.sub.0.025Ca.sub.0.05PO.sub.3.975F.sub.0.025LiC-
o.sub.0.9Al.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025,
Li.sub.0.75Co.sub.0.625Al.sub.0.25PO.sub.3.75F.sub.0.25,
Li.sub.1.075Co.sub.0.8Cu.sub.0.05Mg.sub.0.025Al.sub.0.05PO.sub.3.975F.sub-
.0.025,
Li.sub.1.075Fe.sub.0.8Mg.sub.0.075Al.sub.0.05PO.sub.3.975F.sub.0.0-
25,
Li.sub.1.075Co.sub.0.8Mg.sub.0.075Al.sub.0.05PO.sub.3.975F.sub.0.025,
Li.sub.1.025Co.sub.0.8Mg.sub.0.1Al.sub.0.05PO.sub.3.975F.sub.0.025,
LiCo.sub.0.7Fe.sub.0.2Al.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025,
Li.sub.2Fe.sub.0.8Mg.sub.0.2PO.sub.4F;
Li.sub.2Fe.sub.0.5Co.sub.0.5PO.sub- .4F; Li.sub.3CoPO.sub.4F.sub.2;
KFe(PO.sub.3F)F; Li.sub.2Co(PO.sub.3F)Br.s- ub.2;
Li.sub.2Fe(PO.sub.3F.sub.2)F; Li.sub.2FePO.sub.4Cl;
Li.sub.2MnPO.sub.4OH; Li.sub.2CoPO.sub.4F;
Li.sub.2Fe.sub.0.5Co.sub.0.5PO- .sub.4F;
Li.sub.2Fe.sub.0.9Mg.sub.0.1PO.sub.4F; Li.sub.2Fe.sub.0.8Mg.sub.0-
.2PO.sub.4F; Li.sub.1.25Fe.sub.0.9Mg.sub.0.1PO.sub.4F.sub.0.25;
Li.sub.2MnPO.sub.4F; Li.sub.2CoPO.sub.4F;
K.sub.2Fe.sub.0.9Mg.sub.0.1P.su- b.0.5As.sub.0.5O.sub.4F;
Li.sub.2MnSbO.sub.4OH; Li.sub.2Fe.sub.0.6Co.sub.0- .4SbO.sub.4Br;
Na.sub.3CoAsO.sub.4F.sub.2; LiFe(AsO.sub.3F)Cl;
Li.sub.2Co(As.sub.0.5Sb.sub.0.5O.sub.3F)F.sub.2;
K.sub.2Fe(AsO.sub.3F.sub- .2)F; Li.sub.2NiSbO.sub.4F;
Li.sub.2FeAsO.sub.4OH; Li.sub.4Mn.sub.2(PO.sub- .4).sub.3F;
Na.sub.4FeMn(PO.sub.4).sub.3OH; Li.sub.4FeV(PO.sub.4).sub.3Br;
Li.sub.3VAl(PO.sub.4).sub.3F; K.sub.3VAl(PO.sub.4).sub.3Cl;
LiKNaTiFe(PO.sub.4).sub.3F; Li.sub.4Ti.sub.2(PO.sub.4).sub.3Br;
Li.sub.3V.sub.2(PO.sub.4).sub.3F.sub.2;
Li.sub.6FeMg(PO.sub.4).sub.3OH; Li.sub.4Mn.sub.2(AsO.sub.4).sub.3F;
K.sub.4FeMn(AsO.sub.4).sub.3OH;
Li.sub.4FeV(P.sub.0.5Sb.sub.0.5O.sub.4).sub.3Br;
LiNaKAlV(AsO.sub.4).sub.- 3F; K.sub.3VAl(SbO.sub.4).sub.3Cl;
Li.sub.3TiV(SbO.sub.4).sub.3F;
Li.sub.2FeMn(P.sub.0.5As.sub.0.5O.sub.3F).sub.3;
Li.sub.4Ti.sub.2(PO.sub.- 4).sub.3F;
Li.sub.3.25V.sub.2(PO.sub.4).sub.3F.sub.0.25;
Li.sub.3Na.sub.0.75Fe.sub.2(PO.sub.4).sub.3F.sub.0.75;
Na.sub.6.5Fe.sub.2(PO.sub.4).sub.3(OH)Cl.sub.0.5;
K.sub.8Ti.sub.2(PO.sub.- 4).sub.3F.sub.3Br.sub.2;
K.sub.8Ti.sub.2(PO.sub.4).sub.3F.sub.5;
Li.sub.4Ti.sub.2(PO.sub.4).sub.3F;
LiNa.sub.1.25V.sub.2(PO.sub.4).sub.3F.- sub.0.5Cl.sub.0.75;
K.sub.3.25Mn.sub.2(PO.sub.4).sub.3OH.sub.0.25;
LiNa.sub.1.25KTiV(PO.sub.4).sub.3(OH).sub.1.25Cl;
Na.sub.8Ti.sub.2(PO.sub- .4).sub.3F.sub.3Cl.sub.2;
Li.sub.7Fe.sub.2(PO.sub.4).sub.3F.sub.2;
Li.sub.8FeMg(PO.sub.4).sub.3F.sub.2.25Cl.sub.0.75;
Li.sub.5Na.sub.2.5TiMn(PO.sub.4).sub.3(OH).sub.2Cl.sub.0.5;
Na.sub.3K.sub.4.5MnCa(PO.sub.4).sub.3(OH).sub.1.5Br;
KgFeBa(PO.sub.4).sub.3F.sub.2Cl.sub.2;
Li.sub.7Ti.sub.2(SiO.sub.4).sub.2(- PO.sub.4)F.sub.2;
Na.sub.8Mn.sub.2(SiO.sub.4).sub.2(PO.sub.4)F.sub.2Cl;
Li.sub.3K.sub.2V.sub.2(SiO.sub.4).sub.2(PO.sub.4)(OH)Cl;
Li.sub.4Ti.sub.2(SiO.sub.4).sub.2(PO.sub.4)(OH);
Li.sub.2NaKV.sub.2(SiO.s- ub.4).sub.2(PO.sub.4)F;
Li.sub.5TiFe(PO.sub.4).sub.3F;
Na.sub.4K.sub.2VMg(PO.sub.4).sub.3FCl;
Li.sub.4NaAlNi(PO.sub.4).sub.3(OH)- ;
Li.sub.4K.sub.3FeMg(PO.sub.4).sub.3F.sub.2;
Li.sub.2Na.sub.2K.sub.2CrMn(- PO.sub.4).sub.3(OH)Br;
Li.sub.5TiCa(PO.sub.4).sub.3F;
Li.sub.4Ti.sub.0.75Fe.sub.1.5(PO.sub.4).sub.3F;
Li.sub.3NaSnFe(PO.sub.4).- sub.3(OH);
Li.sub.3NaGe.sub.0.5Ni.sub.2(PO.sub.4).sub.3(OH);
Na.sub.3K.sub.2VCo(PO.sub.4).sub.3(OH)Cl;
Li.sub.4Na.sub.2MnCa(PO.sub.4).- sub.3F(OH);
Li.sub.3NaKTiFe(PO.sub.4).sub.3F; Li.sub.7FeCo(SiO.sub.4).sub.-
2(PO.sub.4)F; Li.sub.3Na.sub.3TiV(SiO.sub.4).sub.2(PO.sub.4)F;
K.sub.5.5CrMn(SiO.sub.4).sub.2(PO.sub.4)Cl.sub.0.5;
Li.sub.3Na.sub.2.5V.sub.2(SiO.sub.4).sub.2(PO.sub.4)(OH).sub.0.5;
Na.sub.5.25FeMn(SiO.sub.4).sub.2(PO.sub.4)Br.sub.0.25;
Li.sub.6.5VCo(SiO.sub.4).sub.2.5(PO.sub.4).sub.0.5F;
Na.sub.7.25V.sub.2(SiO.sub.4).sub.2.25(PO.sub.4).sub.0.75F.sub.2;
Li.sub.4NaVTi(SiO.sub.4).sub.3F.sub.0.5Cl.sub.0.5;
Na.sub.2K.sub.2.5ZrV(SiO.sub.4).sub.3F.sub.0.5;
Li.sub.4K.sub.2MnV(SiO.su- b.4).sub.3(OH).sub.2;
Li.sub.3Na.sub.3KTi.sub.2(SiO.sub.4).sub.3F;
K.sub.6V.sub.2(SiO.sub.4).sub.3(OH)Br;
Li.sub.8FeMn(SiO.sub.4).sub.3F.sub- .2;
Na.sub.3K.sub.4.5MnNi(SiO.sub.4).sub.3(OH).sub.1.5;
Li.sub.3Na.sub.2K.sub.2TiV(SiO.sub.4).sub.3(OH).sub.0.5Cl.sub.0.5;
KgVCr(SiO.sub.4).sub.3F.sub.2Cl;
Li.sub.4Na.sub.4V.sub.2(SiO.sub.4).sub.3- FBr;
Li.sub.4FeMg(SO.sub.4).sub.3F.sub.2;
Na.sub.2KNiCo(SO.sub.4).sub.3(OH- );
Na.sub.5MnCa(SO.sub.4).sub.3F.sub.2Cl;
Li.sub.3NaCoBa(SO.sub.4).sub.3FB- r;
Li.sub.2.5K.sub.0.5FeZn(SO.sub.4).sub.3F;
Li.sub.3MgFe(SO.sub.4).sub.3F- .sub.2;
Li.sub.2NaCaV(SO.sub.4).sub.3FCl; Na.sub.4NiMn(SO.sub.4).sub.3(OH)-
.sub.2; Na.sub.2 KBaFe(SO.sub.4).sub.3F;
Li.sub.2KCuV(SO.sub.4).sub.3(OH)B- r;
Li.sub.1.5CoPO.sub.4F.sub.0.5; Li.sub.1.25CoPO.sub.4F.sub.0.25;
Li.sub.1.75FePO.sub.4F.sub.0.75; Li.sub.1.66MnPO.sub.4F.sub.0.66;
Li.sub.1.5Co.sub.0.75Ca.sub.0.25PO.sub.4F.sub.0.5;
Li.sub.1.75Cu.sub.0.8Mn.sub.0.2PO.sub.4F.sub.0.75;
Li.sub.1.25Fe.sub.0.75Mg.sub.0.25PO.sub.4F.sub.0.25;
Li.sub.1.66Co.sub.0.6Zn.sub.0.4PO.sub.4F.sub.0.66;
KMn.sub.2SiO.sub.4Cl; Li.sub.2VSiO.sub.4(OH).sub.2;
Li.sub.3CoGeO.sub.4F; LiMnSO.sub.4F;
NaFe.sub.0.9Mg.sub.0.1SO.sub.4Cl; LiFeSO.sub.4F; LiMnSO.sub.4OH;
KMnSO.sub.4F; Li.sub.1.75Mn.sub.0.8Mg.sub.0.2PO.sub.4F.sub.0.75;
Li.sub.3FeZn(PO.sub.4)F.sub.2;
Li.sub.0.5V.sub.0.75Mg.sub.0.5(PO.sub.4)F.- sub.0.75;
Li.sub.3V.sub.0.5Al.sub.0.5(PO.sub.4)F.sub.3.5;
Li.sub.0.75VCa(PO.sub.4)F.sub.0.75; Li.sub.4CuBa(PO.sub.4)F.sub.4;
Li.sub.0.5V.sub.0.5Ca(PO.sub.4)(H).sub.1.5;
Li.sub.1.5FeMg(PO.sub.4)(OH)C- l; LiFeCoCa(PO.sub.4)(OH).sub.3F;
Li.sub.3CoBa(PO.sub.4)(OH).sub.2Br.sub.2- ;
Li.sub.0.75Mn.sub.1.5Al(PO.sub.4)(OH).sub.3.75;
Li.sub.2Co.sub.0.75Mg.su- b.0.25(PO.sub.4)F;
LiNaCu.sub.0.8Mg.sub.0.2(PO.sub.4)F;
NaKCo.sub.0.5Mg.sub.0.5(PO.sub.4)F;
LiNa.sub.0.5K.sub.0.5Fe.sub.0.75Mg.su- b.0.25(PO.sub.4)F;
Li.sub.1.5K.sub.0.5V.sub.0.5Zn.sub.0.5(PO.sub.4)F.sub.2- ;
Na.sub.6Fe.sub.2Mg(PS.sub.4).sub.3(OH.sub.2)Cl;
Li.sub.4Mn.sub.1.5Co.sub- .0.5(PO.sub.3F).sub.3(OH).sub.3.5;
K.sub.8FeMg(PO.sub.3F).sub.3F.sub.3Cl.s- ub.3
Li.sub.5Fe.sub.2Mg(SO.sub.4).sub.3Cl.sub.5;
LiTi.sub.2(SO.sub.4).sub.- 3Cl, LiMn.sub.2(SO.sub.4).sub.3F,
Li.sub.3Ni.sub.2(SO.sub.4).sub.3Cl,
Li.sub.3Co.sub.2(SO.sub.4).sub.3F,
Li.sub.3Fe.sub.2(SO.sub.4).sub.3Br,
Li.sub.3Mn.sub.2(SO.sub.4).sub.3F, Li.sub.3MnFe(SO.sub.4).sub.3F,
Li.sub.3NiCo(SO.sub.4).sub.3Cl; LiMnSO.sub.4F; LiFeSO.sub.4Cl;
LiNiSO.sub.4F; LiCoSO.sub.4Cl; LiMn.sub.1-xFe.sub.xSO.sub.4F,
LiFe.sub.1-xMg.sub.xSO.sub.4F; Li.sub.7ZrMn(SiO.sub.4).sub.3F;
Li.sub.7MnCo(SiO.sub.4).sub.3F; Li.sub.7MnNi(SiO.sub.4).sub.3F;
Li.sub.7VAl(SiO.sub.4).sub.3F;
Li.sub.5MnCo(PO.sub.4).sub.2(SiO.sub.4)F;
Li.sub.4VAl(PO.sub.4).sub.2(SiO.sub.4)F;
Li.sub.4MnV(PO.sub.4).sub.2(SiO.- sub.4)F;
Li.sub.4VFe(PO.sub.4).sub.2(SiO.sub.4)F; Li.sub.0.6VPO.sub.4F.sub-
.0.6; Li.sub.0.8VPO.sub.4F.sub.0.8; LiVP.sub.0.4F;
Li.sub.3V.sub.2(PO.sub.- 4).sub.2F.sub.3; LiVPO.sub.4Cl;
LiVPO.sub.4OH; NaVPO.sub.4F;
Na.sub.3V.sub.2(PO.sub.4).sub.2F.sub.3;
LiV.sub.0.9Al.sub.0.1PO.sub.4F; LiFePO.sub.4F; LiTiPO.sub.4F;
LiCrPO.sub.4F; LiFePO.sub.4; LiFe.sub.0.8Mg.sub.0.1PO.sub.4;
LiFe.sub.0.8Mg.sub.0.2PO.sub.4; LiFe.sub.0.9Ca.sub.0.1PO.sub.4;
LiFe.sub.0.8Ca.sub.0.2PO.sub.4; LiFe.sub.0.8Zn.sub.0.2PO.sub.4;
Li.sub.3V.sub.2(PO.sub.4).sub.3; Li.sub.3Fe.sub.2(PO.sub.4).sub.3;
Li.sub.3Mn.sub.2(PO.sub.4).sub.3; Li.sub.3FeTi(PO.sub.4).sub.3;
Li.sub.3CoMn(PO.sub.4).sub.3; Li.sub.3FeV(PO.sub.4).sub.3;
Li.sub.3VTi(PO.sub.4).sub.3; Li.sub.3FeCr(PO.sub.4).sub.3;
Li.sub.3FeMo(PO.sub.4).sub.3; Li.sub.3FeNi(PO.sub.4).sub.3;
Li.sub.3FeMn(PO.sub.4).sub.3; Li.sub.3FeAl(PO.sub.4).sub.3;
Li.sub.3FeCo(PO.sub.4).sub.3; Li.sub.3Ti.sub.2(PO.sub.4).sub.3;
Li.sub.3TiCr(PO.sub.4).sub.3; Li.sub.3TiMn(PO.sub.4).sub.3;
Li.sub.3TiMo(PO.sub.4).sub.3; Li.sub.3TiCo(PO.sub.4).sub.3;
Li.sub.3TiAl(PO.sub.4).sub.3; Li.sub.3TiNi(PO.sub.4).sub.3;
Li.sub.3ZrMnSiP.sub.2O.sub.12; Li.sub.3V.sub.2SiP.sub.2O.sub.12;
Li.sub.3MnVSiP.sub.2O.sub.12; Li.sub.3TiVSiP.sub.2O.sub.12;
Li.sub.3TiCrSiP.sub.2O.sub.12;
Li.sub.3.5AlVSi.sub.0.5P.sub.2.5O.sub.12;
Li.sub.3.5V.sub.2Si.sub.0.5P.su- b.2.5O.sub.12;
Li.sub.2.5AlCrSi.sub.0.5P.sub.2.5O.sub.12;
Li.sub.2.5V.sub.2P.sub.3O.sub.11.5F.sub.0.5;
Li.sub.2V.sub.2P.sub.3O.sub.- 11F;
Li.sub.2.5VMnP.sub.3O.sub.11.5F.sub.0.5;
Li.sub.2V.sub.0.5Fe.sub.1.5P- .sub.3O.sub.11F;
Li.sub.3V.sub.0.05V.sub.0.5P.sub.3O.sub.11.5F.sub.0.5;
Li.sub.3V.sub.2P.sub.3O.sub.11F;
Li.sub.3Mn.sub.0.5V.sub.1.5P.sub.3O.sub.- 11F.sub.0.5;
LiCo.sub.0.05Fe.sub.0.1Ti.sub.0.025Mg.sub.0.05PO.sub.4;
Li.sub.1.025Co.sub.0.8Fe.sub.0.1Ti.sub.0.025Al.sub.0.025PO.sub.4;
Li.sub.1.025Cu.sub.0.8Fe.sub.0.1Ti.sub.0.025Mg.sub.0.025PO.sub.3.975F.sub-
.0.025; LiCu.sub.0.825Fe.sub.0.1Tio.sub.0.025Mg.sub.0.025PO.sub.4;
LiCu.sub.0.85Fe.sub.0.075Ti.sub.0.025Mg.sub.0.025PO.sub.4;
LiCu.sub.0.8Fe.sub.0.1Ti.sub.0.025Al.sub.0.025Mg.sub.0.025PO.sub.4,
Li.sub.1.025Cu.sub.0.8Fe.sub.0.1Ti.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Cu.sub.0.8Fe.sub.0.1Ti.sub.0.025Al.sub.0.025Mg.sub.0.025PO.su-
b.4, LiCu.sub.0.8Fe.sub.0.1Ti.sub.0.05Mg.sub.0.05PO.sub.4, and
mixtures thereof. Preferred active materials include LiFePO.sub.4;
LiFe.sub.0.9Mg.sub.0.1PO.sub.4; LiFe.sub.0.9Mg.sub.0.2PO.sub.4;
Li.sub.1.025Co.sub.0.85Fe.sub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Cu.sub.0.80Fe.sub.0.10Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Cu.sub.0.75Fe.sub.0.15Al.sub.0.025Mg.sub.0.05PO.sub.4,
Li.sub.1.025Co.sub.0.7(Fe.sub.0.4Mn.sub.0.6).sub.0.2Al.sub.0.025Mg.sub.0.-
05PO.sub.4,
LiCo.sub.0.08Fe.sub.0.10Al.sub.0.025Ca.sub.0.05PO.sub.3.975F.s-
ub.0.025,
LiCo.sub.0.8Fe.sub.0.1Al.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0-
.025, LiCo.sub.0.08Fe.sub.0.1Ti.sub.0.025Mg.sub.0.05PO.sub.4;
Li.sub.1.025Co.sub.0.08Fe.sub.0.1Ti.sub.0.025Al.sub.0.025PO.sub.4;
Li.sub.1.025Cu.sub.0.8Fe.sub.0.1Ti.sub.0.025Mg.sub.0.025PO.sub.3.975F.sub-
.0.025; LiCo.sub.0.825Fe.sub.0.1Ti.sub.0.025Mg.sub.0.025PO.sub.4;
LiCo.sub.0.85Fe.sub.0.075Ti.sub.0.025Mg.sub.0.025PO.sub.4; and
mixtures thereof. A particularly preferred active material is
LiCo.sub.0.8Fe.sub.0.1Al0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025.
[0095] Methods of Manufacture:
[0096] Active materials of general formula
A.sub.aM.sub.b(XY.sub.4).sub.cZ- .sub.d are readily synthesized by
reacting starting materials in a solid state reaction, with or
without simultaneous oxidation or reduction of the metal species
involved. According to the desired values of a, b, c, and d in the
product, starting materials are chosen that contain "a" moles of
alkali metal A from all sources, "b" moles of metals M from all
sources, "c" moles of phosphate (or other XY.sub.4 species) from
all sources, and "d" moles of halide or hydroxide Z, again taking
into account all sources. As discussed below, a particular starting
material may be the source of more than one of the components A, M,
XY.sub.4, or Z. Alternatively it is possible to run the reaction
with an excess of one or more of the starting materials. In such a
case, the stoichiometry of the product will be determined by the
limiting reagent among the components A, M, XY.sub.4, and Z.
Because in such a case at least some of the starting materials will
be present in the reaction product mixture, it is usually desirable
to provide exact molar amounts of all the starting materials.
[0097] In one aspect, the moiety XY.sub.4 of the active material
comprises a substituted group represented by X'O.sub.4-xY'.sub.x
where x is less than or equal to 1, and preferably less than or
equal to about 0.1. Such groups may be synthesized by providing
starting materials containing, in addition to the alkali metal and
other metals, phosphate or other X'O.sub.4 material in a molar
amount equivalent to the amount necessary to produce a reaction
product containing X'O.sub.4. Where Y' is F, the starting materials
further comprise a source of fluoride in a molar amount sufficient
to substitute F in the product as shown in the formula. This is
generally accomplished by including at least "x" moles of F in the
starting materials. For embodiments where d>0, the fluoride
source is used in a molar limiting quantity such that the fluorine
is incorporated as a Z-moiety. Sources of F include ionic compounds
containing fluoride ion (F.sup.-) or hydrogen difluoride ion
(HF.sub.2.sup.-). The cation may be any cation that forms a stable
compound with the fluoride or hydrogen difluoride anion. Examples
include +1, +2, and +3 metal cations, as well as ammonium and other
nitrogen-containing cations. Ammonium is a preferred cation because
it tends to form volatile by-products that are readily removed from
the reaction mixture.
[0098] Similarly, to make X'O.sub.4-xN.sub.x, starting materials
are provided that contain "x" moles of a source of nitride ion.
Sources of nitride are among those known in the art including
nitride salts such as Li.sub.3N and (NH.sub.4).sub.3N.
[0099] It is preferred to synthesize the active materials of the
invention using stoichiometric amounts of the starting materials,
based on the desired composition of the reaction product expressed
by the subscripts a, b, c, and d above. Alternatively it is
possible to run the reaction with a stoichiometric excess of one or
more of the starting materials. In such a case, the stoichiometry
of the product will be determined by the limiting reagent among the
components. There will also be at least some unreacted starting
material in the reaction product mixture. Because such impurities
in the active materials are generally undesirable (with the
exception of reducing carbon, discussed below), it is generally
preferred to provide relatively exact molar amounts of all the
starting materials.
[0100] The sources of components A, M, phosphate (or other XY.sub.4
moiety) and optional sources of F or N discussed above, and
optional sources of Z may be reacted together in the solid state
while heating for a time and at a temperature sufficient to make a
reaction product. The starting materials are provided in powder or
particulate form. The powders are mixed together with any of a
variety of procedures, such as by ball milling, blending in a
mortar and pestle, and the like. Thereafter the mixture of powdered
starting materials may be compressed into a pellet and/or held
together with a binder material to form a closely cohering reaction
mixture. The reaction mixture is heated in an oven, generally at a
temperature of about 400.degree. C. or greater until a reaction
product forms.
[0101] Another means for carrying out the reaction at a lower
temperature is a hydothermal method. In a hydrothermal reaction,
the starting materials are mixed with a small amount of a liquid
such as water, and placed in a pressurized bomb. The reaction
temperature is limited to that which can be achieved by heating the
liquid water under pressure, and the particular reaction vessel
used.
[0102] The reaction may be carried out without redox, or if
desired, under reducing or oxidizing conditions. When the reaction
is carried out under reducing conditions, at least some of the
transition metals in the starting materials are reduced in
oxidation state. When the reaction is done without redox, the
oxidation state of the metal or mixed metals in the reaction
product is the same as in the starting materials. Oxidizing
conditions may be provided by running the reaction in air. Thus,
oxygen from the air is used to oxidize the starting material
containing the transition metal.
[0103] The reaction may also be carried out with reduction. For
example, the reaction may be carried out in a reducing atmosphere
such as hydrogen, ammonia, methane, or a mixture of reducing gases.
Alternatively, the reduction may be carried out in situ by
including in the reaction mixture a reductant that will participate
in the reaction to reduce a metal M, but that will produce
by-products that will not interfere with the active material when
used later in an electrode or an electrochemical cell. The
reductant is described in greater detail below.
[0104] Sources of alkali metal include any of a number of salts or
ionic compounds of lithium, sodium, potassium, rubidium or cesium.
Lithium, sodium, and potassium compounds are preferred, with
lithium being particularly preferred. Preferably, the alkali metal
source is provided in powder or particulate form. A wide range of
such materials is well known in the field of inorganic chemistry.
Examples include the lithium, sodium, and/or potassium fluorides,
chlorides, bromides, iodides, nitrates, nitrites, sulfates,
hydrogen sulfates, sulfites, bisulfites, carbonates, bicarbonates,
borates, phosphates, hydrogen ammonium phosphates, dihydrogen
ammonium phosphates, silicates, antimonates, arsenates, germinates,
oxides, acetates, oxalates, and the like. Hydrates of the above
compounds may also be used, as well as mixtures. In particular, the
mixtures may contain more than one alkali metal so that a mixed
alkali metal active material will be produced in the reaction.
[0105] Sources of metals M, M.sup.1, M.sup.2, M.sup.3, and M.sup.4
include salts or compounds of any of the transition metals,
alkaline earth metals, or lanthamide metals, as well as of
non-transition elements such as boron, aluminum, gallium, indium,
thallium, germanium, tin, lead, antimony, and bismuth. The metal
salts or compounds include fluorides, chlorides, bromides, iodides,
nitrates, nitrites, sulfates, hydrogen sulfates, sulfites,
bisulfites, carbonates, bicarbonates, borates, phosphates, hydrogen
ammonium phosphates, dihydrogen ammonium phosphates, silicates,
antimonates, arsenates, germanates, oxides, hydroxides, acetates,
oxalates, and the like. Hydrates may also be used. The metal M in
the starting material may have any oxidation state, depending on
the oxidation state required in the desired product and the
oxidizing or reducing conditions contemplated, as discussed below.
In particular, the cobalt and iron of the active materials may be
provided by starting materials with Co.sup.+2, Co.sup.+3,
Fe.sup.+2, or Fe.sup.+3. The metal sources are chosen so that at
least one metal in the final reaction product is capable of being
in an oxidation state higher than it is in the reaction product. In
a preferred embodiment, the metal sources also include a +2
non-transition metal. Also preferably, at least one metal source is
a source of a +3 non-transition metal. In embodiments comprising
Ti, a source of Ti is provided in the starting materials and the
compounds are made using reducing or non-reducing conditions
depending on the other components of the product and the desired
oxidation state of Ti and other metals in the final product.
Suitable Ti-containing precursors include TiO.sub.2,
Ti.sub.2O.sub.3, and TiO.
[0106] Sources of the desired starting material anions, such as
phosphates, halides and hydroxides, are provided by a number of
salts or compounds containing positively charged cations in
addition to a source of phosphate (or other XY.sub.4 species),
halide, or hydroxide. Such cations include metal ions such as the
alkali metals, alkaline metals, transition metals, or other
non-transition elements, as well as complex cations such as
ammonium or quaternary ammonium. The phosphate anion in such
compounds may be phosphate, hydrogen ammonium phosphate, or
dihydrogen ammonium phosphate. As with the alkali metal source and
metal source discussed above, the phosphate or other XY.sub.4
species, halide and hydroxide starting materials are preferably
provided in particulate or powder form. Hydrates of any of the
above may be used, as can mixtures of the above.
[0107] As noted above, the active materials
A.sub.aM.sub.b(XY.sub.4).sub.c- Z.sub.d of the invention can
contain a mixture of alkali metals A, a mixture of metals M, a
phosphate group representative of the XY.sub.4 group in the formula
and, optionally, a halide or hydroxide Z. In another aspect of the
invention, the phosphate group can be completely or partially
substituted by a number of other XY.sub.4 moieties, which will also
be referred to as "phosphate replacements" or "modified
phosphates." Thus, active materials are provided according to the
invention wherein the XY.sub.4 moiety is a phosphate group that is
completely or partially replaced by such moieties as sulfate
(SO.sub.4).sup.2-, monofluoromonophosphate, (PO.sub.3F).sup.2-,
difluoromonophosphate (PO.sub.2F).sup.2-, silicate
(SiO.sub.4).sup.4-, arsenate, antimonate, and germanate. Analogues
of the above oxygenate anions where some or all of the oxygen is
replaced by sulfur are also useful in the active materials of the
invention, with the exception that the sulfate group may not be
completely substituted with sulfur. For example thiomonophosphates
may also be used as a complete or partial replacement for phosphate
in the active materials of the invention. Such thiomonophosphates
include the anions (PO.sub.3S).sup.3-, (PO.sub.2S.sub.2).sup.3-,
(POS.sub.3).sup.3-, and (PS.sub.4).sup.3-. They are most
conveniently available as the sodium, lithium, or potassium
derivative.
[0108] To synthesize the active materials containing the modified
phosphate moieties, it is usually possible to substitute all or
preferably only part of the phosphate compounds discussed above
with a source of the replacement anion. The replacement is
considered on a stoichiometric basis. Starting materials providing
the source of the replacement anions are provided along with the
other starting materials as discussed above. Synthesis of the
active materials containing the modified phosphate groups proceeds
as discussed above, either without redox or under oxidizing or
reducing conditions. As was the case with the phosphate compounds,
the compound containing the modified or replacement phosphate group
or groups may also be a source of other components of the active
materials. For example, the alkali metal and/or any of the other
metals may be a part of the modified phosphate compound.
[0109] Non-limiting examples of sources of monofluoromonophosphates
include Na.sub.2PO.sub.3F, K.sub.2PO.sub.3F,
(NH.sub.4).sub.2PO.sub.3F.H.- sub.2O, LiNaPO.sub.3F.H.sub.2O,
LiKPO.sub.3F, LiNH.sub.4PO.sub.3F, NaNH.sub.4PO.sub.3F,
NaK.sub.3(PO.sub.3F).sub.2 and CaPO.sub.3F.2H.sub.2O.
Representative examples of sources of difluoromonophosphate
compounds include, without limitation, NH.sub.4PO.sub.2F.sub.2,
NaPO.sub.2F.sub.2, KPO.sub.2F.sub.2, Al(PO.sub.2F.sub.2).sub.3, and
Fe(PO.sub.2F.sub.2).sub.3.
[0110] When it is desired to partially or completely replace
phosphorous in the active materials with silicon, it is possible to
use a wide variety of silicates and other silicon containing
compounds. Thus, useful sources of silicon in the active materials
of the invention include orthosilicates, pyrosilicates, cyclic
silicate anions such as (Si.sub.3O.sub.9).sup.6-,
(Si.sub.6O.sub.18).sup.12- and the like, and pyrocenes represented
by the formula [(SiO.sub.3).sup.2-].sub.n, for example
LiAl(SiO.sub.3).sub.2. Silica or SiO.sub.2 may also be used.
Partial substitution of silicate for phosphate is illustrated in
Example 4.
[0111] Representative arsenate compounds that may be used to
prepare the active materials of the invention include
H.sub.3AsO.sub.4 and salts of the anions [H.sub.2AsO.sub.4].sup.-
and [HAsO.sub.4].sup.2-. Sources of antimonate in the active
materials can be provided by antimony-containing materials such as
Sb.sub.2O.sub.5, M.sup.ISbO.sub.3 where M.sup.I is a metal having
oxidation state +1, M.sup.IIISbO.sub.4 where M.sup.III is a metal
having an oxidation state of +3, and M.sup.IISb.sub.2O.sub.7 where
M.sup.II is a metal having an oxidation state of +2. Additional
sources of antimonate include compounds such as Li.sub.3SbO.sub.4,
NH.sub.4H.sub.2SbO.sub.4, and other alkali metal and/or ammonium
mixed salts of the [SbO.sub.4].sup.3- anion.
[0112] Sources of sulfate compounds that can be used to partially
or completely replace phosphorous in the active materials with
sulfur include alkali metal and transition metal sulfates and
bisulfates as well as mixed metal sulfates such as
(NH.sub.4).sub.2Fe(SO.sub.4).sub.2, NH.sub.4Fe(SO.sub.4).sub.2 and
the like. Finally, when it is desired to replace part or all of the
phosphorous in the active materials with germanium, a germanium
containing compound such as GeO.sub.2 may be used.
[0113] To prepare the active materials containing the modified
phosphate groups, it generally suffices to choose the stoichiometry
of the starting materials based on the desired stoichiometry of the
modified phosphate groups in the final product and react the
starting materials together according to the procedures described
above with respect to the phosphate materials. Naturally, partial
or complete substitution of the phosphate group with any of the
above modified or replacement phosphate groups will entail a
recalculation of the stoichiometry of the required starting
materials.
[0114] A starting material may provide more than one of the
components A, M, XY.sub.4, and Z, as is evident in the list above.
In various embodiments of the invention, starting materials are
provided that combine, for example, the metal and the phosphate,
thus requiring only the alkali metal to be added. In one
embodiment, a starting material is provided that contains alkali
metal, metal, and phosphate. As a general rule, there is
flexibility to select starting materials containing any of the
components of alkali metal A, metal M, and phosphate (or other
XY.sub.4 moiety), as well as halide or hydroxide Z, depending on
availability. Combinations of starting materials providing each of
the components may also be used.
[0115] In general, any anion may be combined with the alkali metal
cation to provide the alkali metal source starting material, or
with a metal M cation to provide a metal starting material.
Likewise, any cation may be combined with the halide or hydroxide
anion to provide the source of Z component starting material, and
any cation may be used as counterion to the phosphate or similar
XY.sub.4 component. It is preferred, however, to select starting
materials with counterions that give rise to the formation of
volatile by-products during the solid state reaction. Thus, it is
desirable to choose ammonium salts, carbonates, bicarbonates,
oxides, hydroxides, and the like where possible. Starting materials
with these counterions tend to form volatile by-products such as
water, ammonia, and carbon dioxide, which can be readily removed
from the reaction mixture. Similarly, sulfur-containing anions such
as sulfate, bisulfate, sulfite, bisulfite and the like tend to
result in volatile sulfur oxide by-products. Nitrogen-containing
anions such as nitrate and nitrite also tend to give volatile
NO.sub.x by-products.
[0116] As noted above, the reactions may be carried out without
reduction, or in the presence of a reductant. In one aspect, the
reductant, which provides reducing power for the reactions, may be
provided in the form of a reducing carbon by including a source of
elemental carbon along with the other particulate starting
materials. In this case, the reducing power is provided by
simultaneous oxidation of carbon to either carbon monoxide or
carbon dioxide.
[0117] The starting materials containing transition metal compounds
are mixed together with carbon, which is included in an amount
sufficient to reduce the metal ion of one or more of the
metal-containing starting materials without full reduction to an
elemental metal state. (Excess quantities of the reducing carbon
may be used to enhance product quality.) An excess of carbon,
remaining after the reaction, functions as a conductive constituent
in the ultimate electrode formulation. This is an advantage since
such remaining carbon is very intimately mixed with the product
active material. Accordingly, large quantities of excess carbon, on
the order of 100% excess carbon or greater are useable in the
process. In a preferred embodiment, the carbon present during
compound formation is intimately dispersed throughout the precursor
and product. This provides many advantages, including the enhanced
conductivity of the product. In a preferred embodiment, the
presence of carbon particles in the starting materials also
provides nucleation sites for the production of the product
crystals.
[0118] Alternatively or in addition, the source of reducing carbon
may be provided by an organic material. The organic material is
characterized as containing carbon and at least one other element,
preferably hydrogen. The organic material generally forms a
decomposition product, referred to herein as a carbonaceous
material, upon heating under the conditions of the reaction.
Without being bound by theory, representative decomposition
processes that can lead to the formation of the carbonaceous
material include pyrolization, carbonization, coking, destructive
distillation, and the like. These process names, as well as the
term thermal decomposition, are used interchangeably in this
application to refer to the process by which a decomposition
product capable of acting as a reductant is formed upon heating of
a reaction mixture containing an organic material.
[0119] A typical decomposition product contains carbonaceous
material. During reaction in a preferred embodiment, at least a
portion of the carbonaceous material formed participates as a
reductant. That portion that participates as reductant may form a
volatile by-product such as discussed below. Any volatile
by-product formed tends to escape from the reaction mixture so that
it is not incorporated into the reaction product.
[0120] Although the invention is understood not to be limited as to
the mechanism of action of the organic precursor material, it
believed that the carbonaceous material formed from decomposition
of the organic material provides reducing power similar to that
provided by elemental carbon discussed above. For example, the
carbonaceous material may produce carbon monoxide or carbon
dioxide, depending on the temperature of the reaction.
[0121] In a preferred embodiment, some of the organic material
providing reducing power is oxidized to a non-volatile component,
such as for example, oxygen-containing carbon materials such as
alcohols, ketones, aldehydes, esters, and carboxylic acids and
anhydrides. Such non-volatile by-products, as well as any
carbonaceous material that does not participate as reductant (for
example, any present in stoichiometric excess or any that does not
otherwise react) will tend to remain in the reaction mixture along
with the other reaction products, but will not be significantly
covalently incorporated.
[0122] The carbonaceous material prepared by heating the organic
precursor material will preferably be enriched in carbon relative
to the mole percent carbon present in the organic material. The
carbonaceous material preferably contains from about 50 up to about
100 mole percent carbon.
[0123] While in some embodiments the organic precursor material
forms a carbonaceous decomposition product that acts as a reductant
as discussed above with respect to elemental carbon, in other
embodiments a portion of the organic material may participate as
reductant without first undergoing a decomposition. The invention
is not limited by the exact mechanism or mechanisms of the
underlying reduction processes.
[0124] As with elemental carbon, reactions with the organic
precursor material are conveniently carried out by combining
starting materials and heating. The starting materials include at
least one transition metal compound as noted above. For
convenience, it is preferred to carry out the decomposition of the
organic material and the reduction of a transition metal in one
step. In this embodiment, the organic material decomposes in the
presence of the transition metal compound to form a decomposition
product capable of acting as a reductant, which reacts with the
transition metal compound to form a reduced transition metal
compound. In another embodiment, the organic material may be
decomposed in a separate step to form a decomposition product. The
decomposition product may then be combined with a transition metal
compound to form a mixture. The mixture may then be heated for a
time and at a temperature sufficient to form a reaction product
comprising a reduced transition metal compound.
[0125] The organic precursor material may be any organic material
capable of undergoing pyrolysis or carbonization, or any other
decomposition process that leads to a carbonaceous material rich in
carbon. Such precursors include in general any organic material,
i.e., compounds characterized by containing carbon and at least one
other element. Although the organic material may be a perhalo
compound containing essentially no carbon-hydrogen bonds, typically
the organic materials contain carbon and hydrogen. Other elements,
such as halogens, oxygen, nitrogen, phosphorus, and sulfur, may be
present in the organic material, as long as they do not
significantly interfere with the decomposition process or otherwise
prevent the reductions from being carried out. Precursors include
organic hydrocarbons, alcohols, esters, ketones, aldehydes,
carboxylic acids, sulfonates, and ethers. Preferred precursors
include the above species containing aromatic rings, especially the
aromatic hydrocarbons such as tars, pitches, and other petroleum
products or fractions. As used here, hydrocarbon refers to an
organic compound made up of carbon and hydrogen, and containing no
significant amounts of other elements. Hydrocarbons may contain
impurities having some heteroatoms. Such impurities might result,
for example, from partial oxidation of a hydrocarbon or incomplete
separation of a hydrocarbon from a reaction mixture or natural
source such as petroleum.
[0126] Other organic precursor materials include sugars and other
carbohydrates, including derivatives and polymers. Examples of
polymers include starch, cellulose, and their ether or ester
derivatives. Other derivatives include the partially reduced and
partially oxidized carbohydrates discussed below. On heating,
carbohydrates readily decompose to form carbon and water. The term
carbohydrates as used here encompasses the D-, L-, and DL-forms, as
well as mixtures, and includes material from natural or synthetic
sources.
[0127] In one sense as used in the invention, carbohydrates are
organic materials that can be written with molecular formula
(C).sub.m (H.sup.20).sub.n, where m and n are integers. For simple
hexose or pentose sugars, m and n are equal to each other. Examples
of hexoses of formula C.sub.6H.sub.12O.sub.6 include allose,
altose, glucose, mannose, gulose, inose, galactose, talose,
sorbose, tagatose, and fructose. Pentoses of formula
C.sub.5H.sub.10O.sub.5 include ribose, arabinose, and xylose.
Tetroses include erythrose and threose, while glyceric aldehyde is
a triose. Other carbohydrates include the two-ring sugars
(di-saccharides) of general formula C.sub.12H.sub.22O.sub.11.
Examples include sucrose, maltose, lactose, trehalose, gentiobiose,
cellobiose, and melibiose. Three-ring (trisaccharides such as
raffinose) and higher oligomeric and polymer carbohydrates may also
be used. Examples include starch and cellulose. As noted above, the
carbohydrates readily decompose to carbon and water when heated to
a sufficiently high temperature. The water of decomposition tends
to turn to steam under the reaction conditions and volatilize.
[0128] It will be appreciated that other materials will also tend
to readily decompose to H.sub.2O and a material very rich in
carbon. Such materials are also intended to be included in the term
"carbohydrate" as used in the invention. Such materials include
slightly reduced carbohydrates such as glycerol, sorbitol,
mannitol, iditol, dulcitol, talitol, arabitol, xylitol, and
adonitol, as well as "slightly oxidized" carbohydrates such as
gluconic, mannonic, glucuronic, galacturonic, mannuronic,
saccharic, manosaccharic, ido-saccharic, mucic, talo-mucic, and
allo-mucic acids. The formula of the slightly oxidized and the
slightly reduced carbohydrates is similar to that of the
carbohydrates.
[0129] A preferred carbohydrate is sucrose. Under the reaction
conditions, sucrose melts at about 150-180.degree. C. Preferably,
the liquid melt tends to distribute itself among the starting
materials. At temperatures above about 450.degree. C., sucrose and
other carbohydrates decompose to form carbon and water. The
as-decomposed carbon powder is in the form of fresh amorphous fine
particles with high surface area and high reactivity.
[0130] The organic precursor material may also be an organic
polymer. Organic polymers include polyolefins such as polyethylene
and polypropylene, butadiene polymers, isoprene polymers, vinyl
alcohol polymers, furfuryl alcohol polymers, styrene polymers
including polystyrene, polystyrene-polybutadiene and the like,
divinylbenzene polymers, naphthalene polymers, phenol condensation
products including those obtained by reaction with aldehyde,
polyacrylonitrile, polyvinyl acetate, as well as cellulose starch
and esters and ethers thereof described above.
[0131] In some embodiments, the organic precursor material is a
solid available in particulate form. Particulate materials may be
combined with the other particulate starting materials and reacted
by heating according to the methods described above.
[0132] In other embodiments, the organic precursor material may be
a liquid. In such cases, the liquid precursor material is combined
with the other particulate starting materials to form a mixture.
The mixture is heated, whereupon the organic material forms a
carbonaceous material in situ. The reaction proceeds with
carbothermal reduction. The liquid precursor materials may also
advantageously serve or function as a binder in the starting
material mixture as noted above.
[0133] Reducing carbon is preferably used in the reactions in
stoichiometric excess. To calculate relative molar amounts of
reducing carbon, it is convenient to use an "equivalent" weight of
the reducing carbon, defined as the weight per gram-mole of carbon
atom. For elemental carbons such as carbon black, graphite, and the
like, the equivalent weight is about 12 g/equivalent. For other
organic materials, the equivalent weight per gram-mole of carbon
atoms is higher. For example, hydrocarbons have an equivalent
weight of about 14 g/equivalent. Examples of hydrocarbons include
aliphatic, alicyclic, and aromatic hydrocarbons, as well as
polymers containing predominantly or entirely carbon and hydrogen
in the polymer chain. Such polymers include polyolefins and
aromatic polymers and copolymers, including polyethylenes,
polypropylenes, polystyrenes, polybutadienes, and the like.
Depending on the degree of unsaturation, the equivalent weight may
be slightly above or below 14.
[0134] For organic materials having elements other than carbon and
hydrogen, the equivalent weight for the purpose of calculating a
stoichiometric quantity to be used in the reactions is generally
higher than 14. For example, in carbohydrates it is about 30
g/equivalent. Examples of carbohydrates include sugars such as
glucose, fructose, and sucrose, as well as polymers such as
cellulose and starch.
[0135] Although the reactions may be carried out in oxygen or air,
the heating is preferably conducted under an essentially
non-oxidizing atmosphere. The atmosphere is essentially
non-oxidizing so as not to interfere with the reduction reactions
taking place. An essentially non-oxidizing atmosphere can be
achieved through the use of vacuum, or through the use of inert
gases such as argon, nitrogen, and the like. Although oxidizing gas
(such as oxygen or air), may be present, it should not be at so
great a concentration that it interferes with the carbothermal
reduction or lowers the quality of the reaction product. It is
believed that any oxidizing gas present will tend to react with the
reducing carbon and lower the availability of the carbon for
participation in the reaction. To some extent, such a contingency
can be anticipated and accommodated by providing an appropriate
excess of reducing carbon as a starting material. Nevertheless, it
is generally preferred to carry out the carbothermal reduction in
an atmosphere containing as little oxidizing gas as practical.
[0136] In a preferred embodiment, reduction is carried out in a
reducing atmosphere in the presence of a reductant as discussed
above. The term "reducing atmosphere" as used herein means a gas or
mixture of gases that is capable of providing reducing power for a
reaction that is carried out in the atmosphere. Reducing
atmospheres preferably contain one or more so-called reducing
gases. Examples of reducing gases include hydrogen, carbon
monoxide, methane, and ammonia, as well as mixtures thereof.
Reducing atmospheres also preferably have little or no oxidizing
gases such as air or oxygen. If any oxidizing gas is present in the
reducing atmosphere, it is preferably present at a level low enough
that it does not significantly interfere with any reduction
processes taking place.
[0137] The stoichiometry of the reduction can be selected along
with the relative stoichiometric amounts of the starting components
A, M, PO.sub.4 (or other XY.sub.4 moiety), and Z. It is usually
easier to provide the reducing agent in stoichiometric excess and
remove the excess, if desired, after the reaction. In the case of
the reducing gases and the use of reducing carbon such as elemental
carbon or an organic material, any excess reducing agent does not
present a problem. In the former case, the gas is volatile and is
easily separated from the reaction mixture, while in the latter,
the excess carbon in the reaction product does not harm the
properties of the active material, particularly in embodiments
where carbon is added to the active material to form an electrode
material for use in the electrochemical cells and batteries of the
invention. Conveniently also, the by-products carbon monoxide or
carbon dioxide (in the case of carbon) or water (in the case of
hydrogen) are readily removed from the reaction mixture.
[0138] When using a reducing atmosphere, it is difficult to provide
less than an excess of reducing gas such as hydrogen. Under such as
a situation, it is preferred to control the stoichiometry of the
reaction by the other limiting reagents. Alternatively the
reduction may be carried out in the presence of reducing carbon
such as elemental carbon. Experimentally, it would be possible to
use precise amounts of reductant carbon to make products of a
chosen stoichiometry. However, it is preferred to carry out the
carbothermal reduction in a molar excess of carbon. As with the
reducing atmosphere, this is easier to do experimentally, and it
leads to a product with excess carbon dispersed into the reaction
product, which as noted above provides a useful active electrode
material.
[0139] Before reacting the mixture of starting materials, the
particles of the starting materials are intermingled. Preferably,
the starting materials are in particulate form, and the
intermingling results in an essentially homogeneous powder mixture
of the precursors. In one embodiment, the precursor powders are
dry-mixed using, for example, a ball mill. Then the mixed powders
are pressed into pellets. In another embodiment, the precursor
powders are mixed with a binder. The binder is preferably selected
so as not to inhibit reaction between particles of the powders.
Preferred binders decompose or evaporate at a temperature less than
the reaction temperature. Examples include mineral oils, glycerol,
and polymers that decompose or carbonize to form a carbon residue
before the reaction starts, or that evaporate before the reaction
starts. In one embodiment, the binders used to hold the solid
particles also function as sources of reducing carbon, as described
above. In still another embodiment, intermingling is accomplished
by forming a wet mixture using a volatile solvent and then the
intermingled particles are pressed together in pellet form to
provide good grain-to-grain contact.
[0140] The mixture of starting materials is heated for a time and
at a temperature sufficient to form an inorganic transition metal
compound reaction product. If the starting materials include a
reducing agent, the reaction product is a transition metal compound
having at least one transition metal in a lower oxidation state
relative to its oxidation state in the starting materials.
[0141] Preferably, the particulate starting materials are heated to
a temperature below the melting point of the starting materials.
Preferably, at least a portion of the starting material remains in
the solid state during the reaction.
[0142] The temperature should preferably be about 400.degree. C. or
greater, and desirably about 450.degree. C. or greater, and
preferably about 500.degree. C. or greater, and generally will
proceed at a faster rate at higher temperatures. The various
reactions involve production of CO or CO.sub.2 as an effluent gas.
The equilibrium at higher temperature favors CO formation. Some of
the reactions are more desirably conducted at temperatures greater
than about 600.degree. C.; most desirably greater than about
650.degree. C.; preferably about 700.degree. C. or greater; more
preferably about 750.degree. C. or greater. Suitable ranges for
many reactions are from about 700 to about 950.degree. C., or from
about 700 to about 800.degree. C.
[0143] Generally, the higher temperature reactions produce CO
effluent and the stoichiometry requires more carbon be used than
the case where CO.sub.2 effluent is produced at lower temperature.
This is because the reducing effect of the C to CO.sub.2 reaction
is greater than the C to CO reaction. The C to CO.sub.2 reaction
involves an increase in carbon oxidation state of +4 (from 0 to 4)
and the C to CO reaction involves an increase in carbon oxidation
state of +2 (from ground state zero to 2). Here, higher temperature
generally refers to a range of about 650.degree. C. to about
1000.degree. C. and lower temperature refers to up to about
650.degree. C. Temperatures higher than about 1200.degree. C. are
not thought to be needed.
[0144] In one embodiment, the methods of this invention utilize the
reducing capabilities of carbon in a unique and controlled manner
to produce desired products having structure and alkali metal
content suitable for use as electrode active materials. The
advantages are at least in part achieved by the reductant, carbon,
having an oxide whose free energy of formation becomes more
negative as temperature increases. Such oxide of carbon is more
stable at high temperature than at low temperature. This feature is
used to produce products having one or more metal ions in a reduced
oxidation state relative to the precursor metal ion oxidation
state.
[0145] Referring back to the discussion of temperature, at about
700.degree. C. both the carbon to carbon monoxide and the carbon to
carbon dioxide reactions are occurring. At closer to about
600.degree. C. the C to CO.sub.2 reaction is the dominant reaction.
At closer to about 800.degree. C. the C to CO reaction is dominant.
Since the reducing effect of the C to CO.sub.2 reaction is greater,
the result is that less carbon is needed per atomic unit of metal
to be reduced. In the case of carbon to carbon monoxide, each
atomic unit of carbon is oxidized from ground state zero to plus 2.
Thus, for each atomic unit of metal ion (M) which is being reduced
by one oxidation state, one half atomic unit of carbon is required.
In the case of the carbon to carbon dioxide reaction, one quarter
atomic unit of carbon is stoichiometrically required for each
atomic unit of metal ion (M) which is reduced by one oxidation
state, because carbon goes from ground state zero to a plus 4
oxidation state. These same relationships apply for each such metal
ion being reduced and for each unit reduction in oxidation state
desired.
[0146] The starting materials may be heated at ramp rates from a
fraction of a degree up to about 10.degree. C. per minute. Higher
or lower ramp rates may be chosen depending on the available
equipment, desired turnaround, and other factors. It is also
possible to place the starting materials directly into a pre-heated
oven. Once the desired reaction temperature is attained, the
reactants (starting materials) are held at the reaction temperature
for a time sufficient for reaction to occur. Typically the reaction
is carried out for several hours at the final reaction temperature.
The heating is preferably conducted under non-oxidizing or inert
gas such as argon or vacuum, or in the presence of a reducing
atmosphere.
[0147] After reaction, the products are preferably cooled from the
elevated temperature to ambient (room) temperature (i.e., about
10.degree. C. to about 40.degree. C.). The rate of cooling may vary
according to a number of factors including those discussed above
for heating rates. For example, the cooling may be conducted at a
rate similar to the earlier ramp rate. Such a cooling rate has been
found to be adequate to achieve the desired structure of the final
product. It is also possible to quench the products to achieve a
higher cooling rate, for example on the order of about 100.degree.
C./minute.
[0148] The general aspects of the above synthesis routes are
applicable to a variety of starting materials. The metal compounds
may be reduced in the presence of a reducing agent, such as
hydrogen or carbon. The same considerations apply to other metal
and phosphate containing starting materials. The thermodynamic
considerations such as ease of reduction of the selected starting
materials, the reaction kinetics, and the melting point of the
salts will cause adjustment in the general procedure, such as the
amount of reducing agent, the temperature of the reaction, and the
dwell time.
[0149] Electrodes:
[0150] The present invention also provides electrodes comprising an
electrode active material of the present invention. In a preferred
embodiment, the electrodes of the present invention comprise an
electrode active material of this invention, a binder; and an
electrically conductive carbonaceous material.
[0151] In a preferred embodiment, the electrodes of this invention
comprise:
[0152] (a) from about 25% to about 95%, more preferably from about
50% to about 90%, active material;
[0153] (b) from about 2% to about 95% electrically conductive
material (e.g., carbon black); and
[0154] (c) from about 3% to about 20% binder chosen to hold all
particulate materials in contact with one another without degrading
ionic conductivity.
[0155] (Unless stated otherwise, all percentages herein are by
weight.) Cathodes of this invention preferably comprise from about
50% to about 90% of active material, about 5% to about 30% of the
electrically conductive material, and the balance comprising
binder. Anodes of this invention preferably comprise from about 50%
to about 95% by weight of the electrically conductive material
(e.g., a preferred graphite), with the balance comprising
binder.
[0156] Electrically conductive materials among those useful herein
include carbon black, graphite, powdered nickel, metal particles,
conductive polymers (e.g., characterized by a conjugated network of
double bonds like polypyrrole and polyacetylene), and mixtures
thereof. Binders useful herein preferably comprise a polymeric
material and extractable plasticizer suitable for forming a bound
porous composite. Preferred binders include halogenated hydrocarbon
polymers (such as poly(vinylidene chloride) and
poly((dichloro-1,4-phenylene)ethylene), fluorinated urethanes,
fluorinated epoxides, fluorinated acrylics, copolymers of
halogenated hydrocarbon polymers, epoxides, ethylene propylene
diamine termonomer (EPDM), ethylene propylene diamine termonomer
(EPDM), polyvinylidene difluoride (PVDF), hexafluoropropylene
(HFP), ethylene acrylic acid copolymer (EAA), ethylene vinyl
acetate copolymer (EVA), EAA/EVA copolymers, PVDF/HFP copolymers,
and mixtures thereof.
[0157] In a preferred process for making an electrode, the
electrode active material is mixed into a slurry with a polymeric
binder compound, a solvent, a plasticizer, and optionally the
electroconductive material. The active material slurry is
appropriately agitated, and then thinly applied to a substrate via
a doctor blade. The substrate can be a removable substrate or a
functional substrate, such as a current collector (for example, a
metallic grid or mesh layer) attached to one side of the electrode
film. In one embodiment, heat or radiation is applied to evaporate
the solvent from the electrode film, leaving a solid residue. The
electrode film is further consolidated, where heat and pressure are
applied to the film to sinter and calendar it. In another
embodiment, the film may be air-dried at moderate temperature to
yield self-supporting films of copolymer composition. If the
substrate is of a removable type it is removed from the electrode
film, and further laminated to a current collector. With either
type of substrate it may be necessary to extract the remaining
plasticizer prior to incorporation into the battery cell.
[0158] Batteries:
[0159] The batteries of the present invention comprise:
[0160] (a) a first electrode comprising an active material of the
present invention;
[0161] (b) a second electrode which is a counter-electrode to said
first electrode; and
[0162] (c) an electrolyte between said electrodes.
[0163] The electrode active material of this invention may comprise
the anode, the cathode, or both. Preferably, the electrode active
material comprises the cathode.
[0164] The active material of the second, counter-electrode is any
material compatible with the electrode active material of this
invention. In embodiments where the electrode active material
comprises the cathode, the anode may comprise any of a variety of
compatible anodic materials well known in the art, including
lithium, lithium alloys, such as alloys of lithium with aluminum,
mercury, manganese, iron, zinc, and intercalation based anodes such
as those employing carbon, tungsten oxides, and mixtures thereof.
In a preferred embodiment, the anode comprises:
[0165] (a) from about 0% to about 95%, preferably from about 25% to
about 95%, more preferably from about 50% to about 90%, of an
insertion material;
[0166] (b) from about 2% to about 95% electrically conductive
material (e.g., carbon black); and
[0167] (c) from about 3% to about 20% binder chosen to hold all
particulate materials in contact with one another without degrading
ionic conductivity.
[0168] In a particularly preferred embodiment, the anode comprises
from about 50% to about 90% of an insertion material selected from
the group active material from the group consisting of metal oxides
(particularly transition metal oxides), metal chalcogenides, and
mixtures thereof. In another preferred embodiment, the anode does
not contain an insertion active, but the electrically conductive
material comprises an insertion matrix comprising carbon, graphite,
cokes, mesocarbons and mixtures thereof. One preferred anode
intercalation material is carbon, such as coke or graphite, which
is capable of forming the compound LixC. Insertion anodes among
those useful herein are described in U.S. Pat. No. 5,700,298, Shi
et al., issued Dec. 23, 1997; U.S. Pat. No. 5,712,059, Barker et
al., issued Jan. 27, 1998; U.S. Pat. No. 5,830,602, Barker et al.,
issued Nov. 3, 1998; and U.S. Pat. No. 6,103,419, Saidi et al.,
issued Aug. 15, 2000; all of which are incorporated by reference
herein.
[0169] In embodiments where the electrode active material comprises
the anode, the cathode preferably comprises:
[0170] (a) from about 25% to about 95%, more preferably from about
50% to about 90%, active material;
[0171] (b) from about 2% to about 95% electrically conductive
material (e.g., carbon black); and
[0172] (c) from about 3% to about 20% binder chosen to hold all
particulate materials in contact with one another without degrading
ionic conductivity.
[0173] Active materials useful in such cathodes include electrode
active materials of this invention, as well as metal oxides
(particularly transition metal oxides), metal chalcogenides, and
mixtures thereof. Other active materials include lithiated
transition metal oxides such as LiCoO.sub.2, LiNiO.sub.2, and mixed
transition metal oxides such as LiCo.sub.1-mNi.sub.mO.sub.2, where
0<m<1. Another preferred active material includes lithiated
spinel active materials exemplified by compositions having a
structure of LiMn.sub.2O.sub.4, as well as surface treated spinels
such as disclosed in U.S. Pat. No. 6,183,718, Barker et al., issued
Feb. 6, 2001, incorporated by reference herein. Blends of two or
more of any of the above active materials may also be used. The
cathode may alternatively further comprise a basic compound to
protect against electrode degradation as described in U.S. Pat. No.
5,869,207, issued Feb. 9, 1999, incorporated by reference
herein.
[0174] The batteries of this invention also comprise a suitable
electrolyte that provides a physical separation but allows transfer
of ions between the cathode and anode. The electrolyte is
preferably a material that exhibits high ionic conductivity, as
well as having insular properties to prevent self-discharging
during storage. The electrolyte can be either a liquid or a solid.
A liquid electrolyte comprises a solvent and an alkali metal salt
that together form an ionically conducting liquid. So called "solid
electrolytes" contain in addition a matrix material that is used to
separate the electrodes.
[0175] One preferred embodiment is a solid polymeric electrolyte,
made up of a solid polymeric matrix and a salt homogeneously
dispersed via a solvent in the matrix. Suitable solid polymeric
matrices include those well known in the art and include solid
matrices formed from organic polymers, inorganic polymers or a
solid matrix-forming monomer and from partial polymers of a solid
matrix forming monomer.
[0176] In another variation, the polymer, solvent and salt together
form a gel which maintains the electrodes spaced apart and provides
the ionic conductivity between electrodes. In still another
variation, the separation between electrodes is provided by a glass
fiber mat or other matrix material and the solvent and salt
penetrate voids in the matrix.
[0177] The electrolytes of the present invention comprise a salt
dissolved in a mixture of an alkylene carbonate and a cyclic ester.
Preferably, the salt of the electrolyte is a lithium or sodium
salt. Such salts among those useful herein include LiAsF.sub.6,
LiPF.sub.6, LiClO.sub.4, LiB(C.sub.6H.sub.5).sub.4, LiAlCl.sub.4,
LiBr, LiBF.sub.4, LiSO.sub.3CF.sub.3, LiN(SO.sub.2CF.sub.3).sub.2,
LiN(SO.sub.2C.sub.2F.sub- .5).sub.2, and mixtures thereof, as well
as sodium analogs, with the less toxic salts being preferable. The
salt content is preferably from about 5% to about 65%, preferably
from about 8% to about 35% (by weight of electrolyte). A preferred
salt is LiBF.sub.4. In a preferred embodiment, the LiBF.sub.4 is
present at a molar concentration of from 0.5M to 3M, preferably
1.0M to 2.0M, and most preferably about 1.5M. Electrolyte
compositions comprising salts among those useful herein are
described in U.S. Pat. No. 5,418,091, Gozdz et al., issued May 23,
1995; U.S. Pat. No. 5,508,130, Golovin, issued Apr. 16, 1996; U.S.
Pat. No. 5,541,020, Golovin et al., issued Jul. 30, 1996; U.S. Pat.
No. 5,620,810, Golovin et al., issued Apr. 15, 1997; U.S. Pat. No.
5,643,695, Barker et al., issued Jul. 1, 1997; U.S. Pat. No.
5,712,059, Barker et al., issued Jan. 27, 1997; U.S. Pat. No.
5,851,504, Barker et al., issued Dec. 22, 1998; U.S. Pat. No.
6,020,087, Gao, issued Feb. 1, 2001; U.S. Pat. No. 6,103,419, Saidi
et al., issued Aug. 15, 2000; and PCT Application WO 01/24305,
Barker et al., published Apr. 5, 2001; all of which are
incorporated by reference herein.
[0178] The electrolyte solvent contains a blend of a cyclic ester
with an alkylene carbonate, an alkyl carbonate, or mixtures
thereof. The alkylene carbonates (cyclic carbonates) have a
preferred ring size of from 5 to 8. The carbon atoms of the ring
may be optionally substituted with alkyl groups, preferably lower
alkyl (C.sub.1-C.sub.6) chains. Examples of unsubstituted cyclic
carbonates are ethylene carbonate (5-membered ring), 1,3-propylene
carbonate (6-membered ring), 1,4butylene carbonate (7-membered
ring), and 1,5-pentylene carbonate (8-membered ring). Optionally
the rings may be substituted with lower alkyl groups, preferably
methyl, ethyl, propyl, or isopropyl groups. Such structures are
well known; examples include a methyl substituted 5-membered ring
(also known as 1,2-propylene carbonate, or simply propylene
carbonate (PC)), and a dimethyl substituted 5-membered ring
carbonate (also known as 2,3-butylene carbonate) and an ethyl
substituted 5-membered ring (also known as 1,2-butylene carbonate
or simply butylene carbonate (BC). Other examples include a wide
range of methylated, ethylated, and propylated 5-8 membered ring
carbonates. In a preferred embodiment, the first component is a 5-
or 6-membered ring carbonate. More preferably, the cyclic carbonate
has a 5-membered ring. In a particular preferred embodiment, the
alkylene carbonate comprises ethylene carbonate.
[0179] The alkyl carbonates are preferably C.sub.1-C.sub.6 alkyl,
which may be unsubstituted or substituted on one or more carbon
atoms with C.sub.1-C.sub.4 alkyl. Alkyl carbonates among those
useful herein include diethyl carbonate (DEC), dimethyl carbonate
(DMC), dipropyl carbonate (DPC), ethyl methyl carbonate (EMC), and
mixtures. DEC is a preferred alkyl carbonate.
[0180] The carbonate component of the electrolyte solvent may
comprise an alkylene carbonate, an alkyl carbonate or mixtures
thereof. Preferably, the carbonate is an alkylene carbonate.
[0181] The electrolyte solvent also comprises a cyclic ester,
preferably a lactone. Preferred cyclic esters include those with
ring sizes of 4 to 7. The carbon atoms in the ring may be
optionally substituted with alkyl groups, preferably lower alkyl
(C.sub.1-C.sub.6) chains. Examples of unsubstituted cyclic esters
include the 4-membered .beta.-propiolactone (or simply
propiolactone); .gamma.-butyrolactone (5-membered ring),
.delta.-valerolactone (6-membered ring) and .epsilon.-caprolactone
(7-membered ring). Any of the positions of the cyclic esters may be
optionally substituted, preferably by methyl, ethyl, propyl, or
isopropyl groups. Thus, preferred second components include one or
more solvents selected from the group of unsubstituted, methylated,
ethylated, or propylated lactones selected from the group
consisting of propiolacone, butyrolactone, valerolactone, and
caprolactone. (It will be appreciated that some of the alkylated
derivatives of one lactone may be named as a different alkylated
derivative of a different core lactone. To illustrate,
.gamma.-butyrolactone methylated on the .gamma.-carbon may be named
as .gamma.-valerolactone.)
[0182] In a preferred embodiment, the cyclic ester of the second
component has a 5- or a 6-membered ring. Thus, preferred second
component solvents include one or more compounds selected from
.gamma.-butyrolactone (gamma-butyrolactone), and
.delta.-valerolactone, as well as methylated, ethylated, and
propylated derivatives. Preferably, the cyclic ester has a
5-membered ring. In a particular preferred embodiment, the second
component cyclic ester comprises .gamma.-butyrolactone.
[0183] The preferred two component solvent system contains the two
components in a weight ratio of from about 1:20 to a ratio of about
20:1. More preferably, the ratios range from about 1:10 to about
10:1 and more preferably from about 1:5 to about 5:1. In a
preferred embodiment the cyclic ester is present in a higher amount
than the cyclic carbonate. Preferably, at least about 60% (by
weight) of the two component system is made up of the cyclic ester,
and preferably about 70% or more. In a particularly preferred
embodiment, the ratio of cyclic ester to cyclic carbonate is about
3 to 1. In one embodiment, the solvent system is made up
essentially of .gamma.-butyrolactone and ethylene carbonate. A
preferred solvent system thus contains about 3 parts by weight
.gamma.-butyrolactone and about 1 part by weight ethylene
carbonate. The preferred salt and solvent are used together in a
preferred mixture comprising about 1.5 molar LiBF.sub.4 in a
solvent comprising about 3 parts .gamma.-butyrolactone and about 1
part ethylene carbonate by weight.
[0184] The solvent optionally comprises additional solvents. Such
solvents include low molecular weight organic solvents. The
optional solvent is preferably a compatible, relatively
non-volatile, aprotic, polar solvent. Examples of such optional
solvents among those useful herein include ethers such as diglyme,
triglyme, and tetraglyme; dimethylsulfoxide, dioxolane, sulfolane,
and mixtures thereof.
[0185] A separator allows the migration of ions while still
providing a physical separation of the electric charge between the
electrodes, to prevent short-circuiting. The polymeric matrix
itself may function as a separator, providing the physical
isolation needed between the anode and cathode. Alternatively, the
electrolyte can contain a second or additional polymeric material
to further function as a separator. In a preferred embodiment, the
separator prevents damage from elevated temperatures within the
battery that can occur due to uncontrolled reactions preferably by
degrading upon high temperatures to provide infinite resistance to
prevent further uncontrolled reactions.
[0186] A separator membrane element is generally polymeric and
prepared from a composition comprising a copolymer. A preferred
composition contains a copolymer of about 75% to about 92%
vinylidene fluoride with about 8% to about 25% hexafluoropropylene
copolymer (available commercially from Atochem North America as
Kynar FLEX) and an organic solvent plasticizer. Such a copolymer
composition is also preferred for the preparation of the electrode
membrane elements, since subsequent laminate interface
compatibility is ensured. The plasticizing solvent may be one of
the various organic compounds commonly used as solvents for
electrolyte salts, e.g., propylene carbonate or ethylene carbonate,
as well as mixtures of these compounds. Higher-boiling plasticizer
compounds such as dibutyl phthalate, dimethyl phthalate, diethyl
phthalate, and tris butoxyethyl phosphate are preferred. Inorganic
filler adjuncts, such as fumed alumina or silanized fumed silica,
may be used to enhance the physical strength and melt viscosity of
a separator membrane and, in some compositions, to increase the
subsequent level of electrolyte solution absorption. In a
non-limiting example, a preferred electrolyte separator contains
about two parts polymer per one part of fumed silica.
[0187] A preferred battery comprises a laminated cell structure,
comprising an anode layer, a cathode layer, and
electrolyte/separator between the anode and cathode layers. The
anode and cathode layers comprise a current collector. A preferred
current collector is a copper collector foil, preferably in the
form of an open mesh grid. The current collector is connected to an
external current collector tab. Such structures are disclosed in,
for example, U.S. Pat. No. 4,925,752, Fauteux et al, issued May 15,
1990; U.S. Pat. No. 5,011,501, Shackle et al., issued Apr. 30,
1991; and U.S. Pat. No. 5,326,653, Chang, issued Jul. 5, 1994; all
of which are incorporated by reference herein. In a battery
embodiment comprising multiple electrochemical cells, the anode
tabs are preferably welded together and connected to a nickel lead.
The cathode tabs are similarly welded and connected to a welded
lead, whereby each lead forms the polarized access points for the
external load.
[0188] A preferred battery comprises a laminated cell structure,
comprising an anode layer, a cathode layer, and
electrolyte/separator between the anode and cathode layers. The
anode and cathode layers comprise a current collector. A preferred
current collector is a copper collector foil, preferably in the
form of an open mesh grid. The current collector is connected to an
external current collector tab, for a description of tabs and
collectors. Such structures are disclosed in, for example, U.S.
Pat. No. 4,925,752, Fauteux et al, issued May 15, 1990; U.S. Pat.
No. 5,011,501, Shackle et al., issued Apr. 30, 1991; and U.S. Pat.
No. 5,326,653, Chang, issued Jul. 5, 1994; all of which are
incorporated by reference herein. In a battery embodiment
comprising multiple electrochemical cells, the anode tabs are
preferably welded together and connected to a nickel lead. The
cathode tabs are similarly welded and connected to a welded lead,
whereby each lead forms the polarized access points for the
external load.
[0189] Lamination of assembled cell structures is accomplished by
conventional means by pressing between metal plates at a
temperature of about 120-160.degree. C. Subsequent to lamination,
the battery cell material may be stored either with the retained
plasticizer or as a dry sheet after extraction of the plasticizer
with a selective low-boiling point solvent. The plasticizer
extraction solvent is not critical, and methanol or ether are often
used.
[0190] In a preferred embodiment, an electrode membrane comprising
the electrode active material (e.g., an insertion material such as
carbon or graphite or a insertion compound) is dispersed in a
polymeric binder matrix. The electrolyte/separator film membrane is
preferably a plasticized copolymer, comprising a polymeric
separator and a suitable electrolyte for ion transport. The
electrolyte/separator is positioned upon the electrode element and
is covered with a positive electrode membrane comprising a
composition of a finely divided lithium insertion compound in a
polymeric binder matrix. An aluminum collector foil or grid
completes the assembly. A protective bagging material covers the
cell and prevents infiltration of air and moisture.
[0191] In another embodiment, a multi-cell battery configuration
may be prepared with copper current collector, a negative
electrode, an electrolyte/separator, a positive electrode, and an
aluminum current collector. Tabs of the current collector elements
form respective terminals for the battery structure.
[0192] In a preferred embodiment of a lithium-ion battery, a
current collector layer of aluminum foil or grid is overlaid with a
positive electrode film, or membrane, separately prepared as a
coated layer of a dispersion of insertion electrode composition.
This is preferably an insertion compound such as the active
material of the present invention in powder form in a copolymer
matrix solution, which is dried to form the positive electrode. An
electrolyte/separator membrane is formed as a dried coating of a
composition comprising a solution containing VdF:HFP copolymer and
a plasticizer solvent is then overlaid on the positive electrode
film. A negative electrode membrane formed as a dried coating of a
powdered carbon or other negative electrode material dispersion in
a VdF:HFP copolymer matrix solution is similarly overlaid on the
separator membrane layer. A copper current collector foil or grid
is laid upon the negative electrode layer to complete the cell
assembly. Therefore, the VdF:HFP copolymer composition is used as a
binder in all of the major cell components, positive electrode
film, negative electrode film, and electrolyte/separator membrane.
The assembled components are then heated under pressure to achieve
heat-fusion bonding between the plasticized copolymer matrix
electrode and electrolyte components, and to the collector grids,
to thereby form an effective laminate of cell elements. This
produces an essentially unitary and flexible battery cell
structure.
[0193] Cells comprising electrodes, electrolytes and other
materials among those useful herein are described in the following
documents, all of which are incorporated by reference herein: U.S.
Pat. No. 4,668,595, Yoshino et al., issued May 26, 1987; U.S. Pat.
No. 4,792,504, Schwab et al., issued Dec. 20, 1988; U.S. Pat. No.
4,830,939, Lee et al., issued May 16, 1989; U.S. Pat. No.
4,935,317, Fauteaux et al., issued Jun. 19, 1980; U.S. Pat. No.
4,990,413, Lee et al., issued Feb. 5, 1991; U.S. Pat. No.
5,037,712, Shackle et al., issued Aug. 6, 1991; U.S. Pat. No.
5,262,253, Golovin, issued Nov. 16, 1993; U.S. Pat. No. 5,300,373,
Shackle, issued Apr. 5, 1994; U.S. Pat. No. 5,399,447,
Chaloner-Gill, et al., issued Mar. 21, 1995; U.S. Pat. No.
5,411,820, Chaloner-Gill, issued May 2, 1995; U.S. Pat. No.
5,435,054, Tonder et al., issued Jul. 25, 1995; U.S. Pat. No.
5,463,179, Chaloner-Gill et al., issued Oct. 31, 1995; U.S. Pat.
No. 5,482,795, Chaloner-Gill., issued Jan. 9, 1996; U.S. Pat. No.
5,660,948, Barker, issued Sep. 16, 1995; and U.S. Pat. No.
6,306,215, Larkin, issued Oct. 23, 2001. A preferred electrolyte
matrix comprises organic polymers, including VdF:HFP. Examples of
casting, lamination and formation of cells using VdF:HFP are as
described in U.S. Pat. Nos. 5,418,091, Gozdz et al., issued May 23,
1995; U.S. Pat. No. 5,460,904, Gozdz et al., issued Oct. 24, 1995;
U.S. Pat. No. 5,456,000, Gozdz et al., issued Oct. 10, 1995; and
U.S. Pat. No. 5,540,741, Gozdz et al., issued Jul. 30, 1996; all of
which are incorporated by reference herein.
[0194] The electrochemical cell architecture is typically governed
by the electrolyte phase. A liquid electrolyte battery generally
has a cylindrical shape, with a thick protective cover to prevent
leakage of the internal liquid. Liquid electrolyte batteries tend
to be bulkier relative to solid electrolyte batteries due to the
liquid phase and extensive sealed cover. A solid electrolyte
battery, is capable of miniaturization, and can be shaped into a
thin film. This capability allows for a much greater flexibility
when shaping the battery and configuring the receiving apparatus.
The solid state polymer electrolyte cells can form flat sheets or
prismatic (rectangular) packages, which can be modified to fit into
the existing void spaces remaining in electronic devices during the
design phase.
[0195] The following non-limiting examples illustrate the
compositions and methods of the present invention.
EXAMPLE 1
[0196] An electrode active material of formula
Li.sub.0.025Cu.sub.0.9Al.su- b.0.025Mg.sub.0.05PO.sub.4, is made as
follows. The following sources of Li, Co, Al, Mg, and phosphate are
provided containing the respective elements in a molar ratio of
1.025:0.9:0.025:0.05:1.
1 0.05125 moles Li.sub.2CO.sub.3 (mol. wt. 73.88 g/mol) 3.8 g 0.03
moles Co.sub.3O.sub.4 (240.8 g/mol) 7.2 g 0.0025 moles Al(OH).sub.3
(78 g/mol) 0.195 g 0.005 moles Mg(OH).sub.2 (58 g/mol) 0.29 g 0.1
moles (NH.sub.4).sub.2HPO.sub.4 (132 g/mol) 13.2 g 0.2 moles
elemental carbon (12 g/mol) (>100% excess) 2.4 g
[0197] The above starting materials are combined and ball milled to
mix the particles. Thereafter, the particle mixture is pelletized.
The pelletized mixture is heated for 4-20 hours at 750.degree. C.
in an oven in an argon atmosphere. The sample is removed from the
oven and cooled. An x-ray diffraction pattern shows that the
material has an olivine type crystal structure. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% poly vinylidene difluoride. A cell with that
electrode as cathode and lithium metal as anode is constructed with
an electrolyte comprising 1 M LiBF.sub.4 dissolved in a 3:1 by
weight mixture of .gamma.-butyrolactone:ethylene carbonate. The
active material exhibits a reversible capacity over 140 mAhg-1.
EXAMPLE 2
[0198] An electrode active material of formula
Li.sub.1.025Co.sub.0.85Fe.s- ub.0.05Al.sub.0.025Mg.sub.0.05PO.sub.4
(LiCo.sub.0.85Fe.sub.0.05Al.sub.0.0-
25Mg.sub.0.05Li.sub.0.025PO.sub.4) is made as follows. The
following sources of Li, Co, Fe, Al, Mg, and phosphate are provided
containing the respective elements in a molar ratio of
1.025:0.85:0.05:0.025:0.05:1.
2 0.05125 moles Li.sub.2CO.sub.3 (mol. wt. 73.88 g/mol) 3.8 g
0.02833 moles Co.sub.3O.sub.4 (240.8 g/mol) 6.82 g 0.0025 moles
Fe.sub.2O.sub.3 (159.7 g/mol) 0.4 g 0.0025 moles Al(OH).sub.3 (78
g/mol) 0.195 g 0.005 moles Mg(OH).sub.2 (58 g/mol) 0.29 g 0.1 moles
(NH.sub.4).sub.2HPO.sub.4 (132 g/mol) 13.2 g 0.2 moles elemental
carbon (12 g/mol) (>100% excess) 2.4 g
[0199] The above starting materials are combined and ball milled to
mix the particles. Thereafter, the particle mixture is pelletized.
The pelletized mixture is heated for 4-20 hours at 750.degree. C.
in an oven in an argon atmosphere. The sample is removed from the
oven and cooled. An x-ray diffraction pattern shows that the
material has an olivine type crystal structure. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% poly vinylidene difluoride. A cell with that
electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1 M LiPF.sub.6 dissolved
in a 2:1:1 by weight mixture of .gamma.-butyrolactone:ethylene
carbonate:dimethyl carbonate.
EXAMPLE 3
[0200] An electrode active material of the formula
Li.sub.1.025Cu.sub.0.8F- e.sub.0.1Al.sub.0.025Mg.sub.0.05PO.sub.4
(LiCu.sub.0.8Fe.sub.0.1Al.sub.0.0-
25Mg.sub.0.05Li.sub.0.025PO.sub.4) is made as follows. The
following sources of Li, Co, Fe, Al, Mg, and phosphate are provided
containing the respective elements in a molar ratio of
1.025:0.8:0.1:0.025:0.05:1.
3 0.05125 moles Li.sub.2CO.sub.3 (mol. wt. 73.88 g/mol) 3.8 g
0.02667 moles Co.sub.3O.sub.4 (240.8 g/mol) 6.42 g 0.005 moles
Fe.sub.2O.sub.3 (159.7 g/mol) 0.8 g 0.0025 moles Al(OH).sub.3 (78
g/mol) 0.195 g 0.005 moles Mg(OH).sub.2 (58 g/mol) 0.29 g 0.1 moles
(NH.sub.4).sub.2HPO.sub.4 (132 g/mol) 13.2 g 0.2 moles elemental
carbon (12 g/mol) (>100% excess) 2.4 g
[0201] The above starting materials are combined and ball milled to
mix the particles. Thereafter, the particle mixture is pelletized.
The pelletized mixture is heated for 4-20 hours at 750.degree. C.
in an oven in an argon atmosphere. The sample is removed from the
oven and cooled. An x-ray diffraction pattern shows that the
material has an olivine type crystal structure. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% poly vinylidene difluoride. A cell with that
electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1 M LiPF.sub.6 dissolved
in a 3:1 by weight mixture of .gamma.-butyrolactone:ethylene
carbonate.
EXAMPLE 4
[0202] An electrode active material of the formula
LiCo.sub.0.8Fe.sub.0.05-
Al.sub.0.1Mg.sub.0.05(PO.sub.4).sub.0.9(SiO.sub.4).sub.0.1 is made
as follows. The following sources of Li, Co, Fe, Al, Mg, phosphate,
and silicate are provided containing the respective elements in a
molar ratio of 1:0.8:0.05:0.1:0.05:0.9:0.1.
4 0.05 moles Li.sub.2CO.sub.3 (mol. wt. 73.88 g/mol) 3.7 g 0.08
moles CoCO.sub.3 (118.9 g/mol) 9.5 g 0.0025 moles Fe.sub.2O.sub.3
(159.7 g/mol) 0.4 g 0.0025 moles Al(OH).sub.3 (78 g/mol) 0.195 g
0.005 moles Mg(OH).sub.2 (58 g/mol) 0.29 g 0.09 moles
(NH.sub.4).sub.2HPO.sub.4 (132 g/mol) 11.9 g 0.01 moles SiO.sub.2
(60.1 g/mol) 0.6 g 0.2 moles elemental carbon (12 g/mol) (excess)
2.4 g
[0203] The above amounts of starting materials are combined and
ball milled to mix the particles. Note that the reducing carbon is
present in approximately a 40-fold excess, relative to the 0.05
moles of iron in the iron III oxide to be reduced. Thereafter, the
particle mixture is pelletized. The pelletized mixture is heated
for 4-20 hours at 750.degree. C. in an oven in an argon atmosphere.
The sample is removed from the oven and cooled. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% polyvinylidene difluoride. A cell with that
electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1 M LiBF.sub.4 dissolved
in 3:1 by weight mixture of .gamma.-butyrolactone:et- hylene
carbonate.
EXAMPLE 5
[0204] An electrode active material of the formula
LiCo.sub.0.8Fe.sub.0.1A-
l.sub.0.025Mg.sub.0.05PO.sub.3.975F.sub.0.025 is made as follows.
The following sources containing Li, Co, Fe, Al, Mg, phosphate, and
fluoride are provided containing the respective elements in a molar
ratio of 1.0:0.8:0.1:0.025:0.05:1.0:0.025.
5 0.05 moles Li.sub.2CO.sub.3 (mol. wt. 73.88 g/mol), 0.1 mol Li
3.7 g 0.02667 moles Co.sub.3O.sub.4 (240.8 g/mol), 0.08 mol Co 6.42
g 0.005 moles Fe.sub.2O.sub.3 (159.7 g/mol), 0.01 mol Fe 0.8 g
0.0025 moles Al(OH).sub.3 (78 g/mol), 0.0025 mol Al 0.195 g 0.005
moles Mg(OH).sub.2 (58 g/mol), 0.005 mol Mg 0.29 g 0.1 moles
(NH.sub.4).sub.2HPO.sub.4 (132 g/mol), 0.1 mol phosphate 13.2 g
0.00125 moles NH.sub.4HF.sub.2 (57 g/mol), 0.0025 mol F 0.071 g 0.2
moles elemental carbon (12 g/mol) (>100% excess) 2.4 g
[0205] The above starting materials are combined and ball milled to
mix the particles. Thereafter, the particle mixture is pelletized.
The pelletized mixture is heated for 4-20 hours at 750.degree. C.
in an oven in an argon atmosphere. The sample is removed from the
oven and cooled. An x-ray diffraction pattern shows that the
material has an olivine type crystal structure. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% polyvinylidene difluoride. A cell with that
electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1M LiBF.sub.4 dissolved
in a 3:1 mixture by weight of .gamma.-butyrolactone:propylene
carbonate.
EXAMPLE 6
[0206] An electrode active material of the formula
LiFe.sub.0.9Mg.sub.0.1P- O.sub.4 is made according to the following
reaction scheme.
0.50Li.sub.2CO.sub.3+0.45Fe.sub.2O.sub.3+0.10Mg(OH).sub.2+(NH.sub.4).sub.2-
HPO.sub.4+0.45C.fwdarw.LiFe.sub.0.9Mg.sub.0.1PO.sub.4+0.50CO.sub.2+0.45CO+-
2.0NH.sub.3+1.6H.sub.2O
[0207] A mixture of 36.95 g (0.50 mol) of Li.sub.2CO.sub.3, 71.86 g
(0.45 mol) of Fe.sub.2O.sub.3, 5.83 g (0.10 mol) of 0.10
Mg(OH).sub.2, 132.06 g (1.0 mol) of (NH.sub.4).sub.2HPO.sub.4, and
10.8 g (0.90 g-mol, 100% excess) of carbon is made, using a mortar
and pestle. The mixture is pelletized, and transferred to a
temperature-controlled tube furnace equipped with an argon gas
flow. The mixture is heated at a ramp rate of about 2.degree.
C./minute to an ultimate temperature of about 750.degree. C. in the
inert atmosphere and maintained at this temperature for about 8
hours. The product is then cooled to ambient temperature (about
22.degree. C.). An electrode is made with 80% of the active
material, 10% of Super P conductive carbon, and 10% polyvinylidene
difluoride. A cell with that electrode as cathode and a carbon
intercalation anode is constructed with an electrolyte comprising
1M LiBF.sub.4 dissolved in a 4:1 mixture by weight of
6-valerolactone:ethylene carbonate.
EXAMPLE 7
[0208] An electrode active material comprising
Li.sub.1.25Fe.sub.0.9Mg.sub- .0.1PO.sub.4F.sub.0.25 is made
according to the following reaction scheme.
1.0LiFe.sub.0.9Mg.sub.0.1PO.sub.4+dLiF.fwdarw.Li.sub.1+dFe.sub.0.9Mg.sub.0-
.1PO.sub.4F.sub.d
[0209] For d equal to 0.25, 1.082 grams of
LiFe.sub.0.9Mg.sub.0.1PO.sub.4 (made as in Example 6) and 0.044
grams of LiF are premixed and pelletized, transferred to an oven
and heated to an ultimate temperature of 700.degree. C. and
maintained for 15 minutes at this temperature. The sample is cooled
and removed from the oven. Almost no weight loss is recorded for
the reaction, consistent with full incorporation of the lithium
fluoride into the phosphate structure to make an active material of
formula Li.sub.1.25Fe.sub.0.9Mg.sub.0.1PO.sub.4F.sub.0.25. An
electrode is made with 80% of the active material, 10% of Super P
conductive carbon, and 10% polyvinylidene difluoride. A cell with
that electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1M LiBF.sub.4 dissolved
in a 3:1 mixture by weight of .gamma.-butyrolactone:ethylene
carbonate.
EXAMPLE 8
[0210] An electrode active material comprising NaVPO.sub.4F is made
according to the following reaction scheme.
0.5Na.sub.2CO.sub.3+NH.sub.4F+VPO.sub.4.fwdarw.NaVPO.sub.4F+NH.sub.3+0.5CO-
.sub.2+0.5H.sub.2O
[0211] 1.23 grams Of VPO.sub.4, 0.31 grams of NH.sub.4F, and 0.45
grams Na.sub.2CO.sub.3 are premixed with approximately 20
milliliters of deionized water and transferred and sealed in a Parr
Model 4744 acid digestion bomb, which is a Teflon lined stainless
steel reaction vessel. The bomb is placed in an oven and heated to
an ultimate temperature of 250.degree. C. and maintained at this
temperature for forty-eight hours. The sample is cooled to room
temperature and removed for analysis. The sample is washed
repeatedly with the deionized water to remove unreacted impurities
and thereafter is dried in an argon atmosphere at 250.degree. C.
for an hour.
EXAMPLE 9
[0212] An electrode active material comprising
Li.sub.2.025Co.sub.0.9Al.su- b.0.025Mg.sub.0.05PO.sub.4F is made as
follows. (This Example shows the synthesis of a mixed metal active
material containing lithium and three different metals, with two
metals in a +2 and one metal in a +3 oxidation state). For A=Li,
a=2.025, M.sup.1=Co, M.sup.2=Al, and M.sup.3=Mg, the reaction
proceeds according to the following scheme. 1 0.5125 Li 2 CO 3 +
0.3 Co 3 ( Po 4 ) 2 8 H 2 O + 0.0125 A1 2 O 3 + 0.05 Mg ( OH ) 2 +
LiF + 0.4 NH 4 H 2 PO 4 Li 2.025 Co 0.9 A1 0.025 Mg 0.05 PO 4 F +
0.5125 CO 2 + 0.4 NH 3 + 8.9 H 2 O .
[0213] Powdered starting materials are provided in the molar ratios
indicated, mixed, pelletized, and heated in an oven at 750.degree.
C. for four hours to produce a reaction product. An electrode is
made with 80% of the active material, 10% of Super P conductive
carbon, and 10% polyvinylidene difluoride. A cell with that
electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1M LiBF.sub.4 dissolved
in a 3:2 mixture by weight of .beta.-propiolactone:ethylene
carbonate.
EXAMPLE 10
[0214] An electrode active material comprising
Li.sub.6V.sub.2(PO.sub.4).s- ub.3F is synthesized according to the
equation
3C+2.5Li.sub.2CO.sub.3+V.sub.2O.sub.5+LiF+3NH.sub.4H.sub.2PO.sub.4.fwdarw.-
Li.sub.6V.sub.2(PO.sub.4).sub.3F+2.5CO.sub.2+3NH.sub.3+4.5H.sub.2O+3CO.
[0215] The equation presupposes that the carbothermal reaction
proceeds with production of carbon monoxide. The carbon is provided
in excess, in this case to reduce the vanadium +5 species all the
way down to its lowest oxidation of +2. It is appreciated in the
reaction scheme that such a reduction is possible because there is
enough lithium in the reaction scheme that lithium is incorporated
into the reaction product in an amount sufficient to neutralize the
[(PO.sub.4).sub.3F].sup.10- group of the active material. An
electrode is made with 80% of the active material, 10% of Super P
conductive carbon, and 10% polyvinylidene difluoride. A cell with
that electrode as cathode and a carbon intercalation anode is
constructed with an electrolyte comprising 1M LiBF.sub.4 dissolved
in a 3:1 mixture by weight of .gamma.-butyrolactone:ethylene
carbonate.
[0216] The examples and other embodiments described herein are
exemplary and not intended to be limiting in describing the full
scope of compositions and methods of this invention. Equivalent
changes, modifications and variations of specific embodiments,
materials, compositions and methods may be made within the scope of
the present invention, with substantially similar results.
* * * * *