U.S. patent application number 10/335950 was filed with the patent office on 2003-08-14 for easily peelable laminated film.
This patent application is currently assigned to YUPO CORPORATION. Invention is credited to Koike, Hiroshi.
Application Number | 20030152735 10/335950 |
Document ID | / |
Family ID | 18700815 |
Filed Date | 2003-08-14 |
United States Patent
Application |
20030152735 |
Kind Code |
A1 |
Koike, Hiroshi |
August 14, 2003 |
Easily peelable laminated film
Abstract
An easily peelable laminated film includes a laminate of a
peelable surface layer (B) having a peeling strength of 5 to 100
g/cm with a base layer (A) containing a thermoplastic resin. The
laminated film of the invention provides an easily peelable
laminated film excellent in water resistance as a base materialfor,
for example, concealing seals and labels for preventing re-pasting.
The easily peelable laminated film of the invention requires no
specific process to start peeling.
Inventors: |
Koike, Hiroshi;
(Kashima-gun, JP) |
Correspondence
Address: |
SUGHRUE MION, PLLC
2100 Pennsylvania Avenue, NW
Washington
DC
20037-3213
US
|
Assignee: |
YUPO CORPORATION
|
Family ID: |
18700815 |
Appl. No.: |
10/335950 |
Filed: |
January 3, 2003 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10335950 |
Jan 3, 2003 |
|
|
|
PCT/JP01/05850 |
Jul 5, 2001 |
|
|
|
Current U.S.
Class: |
428/40.1 |
Current CPC
Class: |
B32B 27/32 20130101;
Y10T 428/1462 20150115; B32B 7/06 20130101; Y10T 428/1486 20150115;
C09J 7/40 20180101; Y10T 428/1452 20150115; B32B 3/26 20130101;
Y10T 428/14 20150115; Y10T 428/24372 20150115; Y10T 428/1476
20150115; Y10T 428/1471 20150115; Y10T 428/24876 20150115; B32B
27/20 20130101; Y10T 428/1405 20150115; Y10T 428/24851
20150115 |
Class at
Publication: |
428/40.1 |
International
Class: |
B32B 009/00 |
Foreign Application Data
Date |
Code |
Application Number |
Jul 5, 2000 |
JP |
P. 2000-203400 |
Claims
1. An easily peelable laminated film (i) comprising laminate of a
peelable surface layer (B) having peeling strength of from 5 to 150
g/cm, and a base layer (A) comprising a thermoplastic resin.
2. The easily peelable laminated film (i) as claimed in claim 1,
wherein the peelable surface layer (B) is a stretched film.
3. The easily peelable laminated film (i) as claimed in claim 1,
wherein the base layer (A) and the peelable surface layer (B) are
stretched at least in a monoaxial direction after being
laminated.
4. The easily peelable laminated film (i) as claimed in claim 1,
wherein the peelable surface layer (B) comprises a thermoplastic
resin.
5. The easily peelable laminated film (i) as claimed in claim 1,
wherein the peelable surface layer (B) contains from 10 to 80 wt %
of an inorganic fine powder and/or an organic fine powder, and from
90 to 20 wt % of a thermoplastic resin.
6. The easily peelable laminated film (i) as claimed in claim 1,
wherein the peelable surface layer (B) has a layer thickness of
from 0.1 to 100 .mu.m, and the base layer (A) has a layer thickness
of from 10 to 500 .mu.m.
7. The easily peelable laminated film (i) as claimed in claim 1,
wherein the easily peelable laminated film (i) has an opaqueness of
from 60 to 100%.
8. The easily peelable laminated film (i) as claimed in claim 1,
wherein the base layer (A) has a laminated structure (A1)/(A2); the
structure of a layer (A1) contiguous to the peelable surface layer
(B) in the laminated structure comprises a thermoplastic resin film
containing from 2 to 60 wt % of an inorganic fine powder and/or an
organic fine powder, and from 98 to 40 wt % of a thermoplastic
resin; the content of the inorganic fine powder and/or the organic
fine powder in the layer (A1) is less than that in the peelable
surface layer (B) by 8 wt % or more; and an outer layer (A2) on the
surface of layer (A1) opposite to the peelable surface layer (B)
comprises a thermoplastic resin film containing from 0 to 80 wt %
of an inorganic.fine powder and/or an organic fine powder, and from
100 to 20 wt % of a thermoplastic resin.
9. The easily peelable laminated film (i) as claimed in claim 1,
wherein a protective layer is provided on the outermost surface of
peelable surface layer (B).
10. The easily peelable laminated film (i) as claimed in claim 1,
wherein a coat layer is provided on at least one side of the easily
peelable laminated film (i).
11. An easily peelable laminated label (ii), wherein a
pressure-sensitive adhesive is provided on the exposed side of
peelable surface layer (B) of the easily peelable laminated film
(i) as claimed in claim 1.
12. An easily peelable laminated label (ii), wherein a
pressure-sensitive adhesive and a release paper in this order are
provided on the exposed side of peelable surface layer (B) of the
easily peelable laminated film (i) as claimed in claim 1.
13. The easily peelable laminated label (ii) as claimed in claim
11, wherein the peeling start stress is 500 g/cm or less.
14. The easily peelable laminated label (ii) as claimed in claim
11, wherein letters or graphic data are provided under the peelable
surface layer (B) or the pressure-sensitive adhesive and are
recognizable by peeling the base layer (A) off from the easily
peelable laminated label (ii).
Description
TECHNICAL FIELD
[0001] The present invention relates to an easily peelable
laminated film comprising a laminate of a base layer (A) comprising
a thermoplastic resin, and a peelable surface layer (B) weaker in
strength than the base layer (A).
[0002] An easily peelable laminated film is useful as a base
material of, for example, delivery slips, concealing seals of post
cards and passbooks, labels for preventing re-pasting, seals for
preventing alteration, application seals, and coupons free of
remaining adhesives.
BACKGROUND OF THE INVENTION
[0003] There has been conventionally such a problem in the
salesroom of foods in supermarkets and department stores that there
are persons who peel off the pressure-sensitive adhesive price
label of lowered price from the foods on sale nearing eatable limit
and replace this price label with the price label of foods of
normal price and purchase the foods at a cheaper price.
[0004] Therefore, a label for preventing re-pasting which is easily
known to be the peeled label after peeling and re-pasting the label
on other goods, or a label which cannot be re-pasted is required
and such a label has been put to practical use. However, there are
problems that these labels for preventing re-pasting are expensive,
an adhesive remains on the peeled surface and sticky to the touch,
or dusts are adhered on the surface.
[0005] For solving this problem, Japanese Patent Laid-Open No.
99377/1996 discloses a method of manufacturing a label for
preventing re-pasting, which label satisfies the equation
c<a<b, taking the force required to peel off a first layer
from a second layer by a peeling agent as a, the adhesive force of
an adhesive layer with the material to be adhered as b, and the
force required to peel off a peelable sheet from the adhesive layer
as c, and the method comprises (a) a step of forming an adhesive
layer on a peelable sheet, (b) a step of laminating a peeling agent
layer containing a wax on one main surface of a first layer, (c) a
step of forming a second layer on the surface of the peeling agent
layer of the first layer, and (d) a step of superposing and
laminating the surface of the adhesive layer formed on the peelable
sheet and the surface of the second layer laminated on the first
layer. However, this method is not only complicated but also
inferior in water resistance when paper made of pulp is used as the
surface material of the first layer, so that the surface material
is easily broken and peeled off from the material adhered when it
is brought into contact with water. Therefore, this label is not
suited to be a label for a sealed vessel containing water, e.g.,
pickles, tofu (bean curd), konjak (devil's tongue), etc.
[0006] Further, Japanese Patent Laid-Open No. 258476/1998 discloses
a method of obtaining a film for a label to prevent re-pasting
which is excellent in water resistance comprising a
fusion-laminated base layer (A) comprising a thermoplastic resin
film having a thickness of from 10 to 500 .mu.m and a backing layer
(C) on the front surface and back surface of a peelable surface
layer (B) comprising a thermoplastic biaxially stretched film
containing from 10 to 80 wt % of an inorganic fine powder and from
90 to 20 wt % of a thermoplastic resin. The base layer (A) and the
backing layer (C) of the easily peelable laminated film obtained by
this method can be easily peeled once peeling starts, but it has
been found that a specific process, e.g., cutting a notch or a slit
only on the backing layer (C), is necessary to surely start
peeling.
[0007] Accordingly, an object of the present invention is to solve
the problems of background techniques and provide an easily
peelable laminated film having very excellent characteristics.
[0008] That is, an object of the present invention is to provide an
easily peelable laminated film which is excellent in water
resistance as a base materialfor concealing seals and labels for
preventing re-pasting and which requires no specific process to
start peeling.
Disclosure of the Invention
[0009] As a result of eager investigation for solving these
problems, the present inventors have found that an easily peelable
laminated film (i) having excellent characteristics can be obtained
by forming a thermoplastic resin film having a specific layer
constitution, thus accomplishing the present invention.
[0010] That is, the present invention provides an easily peelable
laminated film (i) which requires no specific process to start
peeling by laminating a peelable surface layer (B) having a peeling
strength of from 5 to 150 g/cm, and a base layer (A) comprising a
thermoplastic resin.
[0011] As the preferred mode of the present invention, a base layer
(A) and a peelable surface layer (B) that is a stretched film are
stretched at least in the monoaxial direction after being
laminated, the peelable surface layer (B) comprises a thermoplastic
resin, the peelable surface layer (B) contains from 10 to 80 wt %
of an inorganic fine powder and/or an organic fine powder, and from
90 to 20 wt % of a thermoplastic resin, the peelable surface layer
(B) has a layer thickness of from 0.1 to 100 .mu.m and the base
layer (A) has a layer thickness of from 10 to 500 .mu.m.
[0012] Further, the easily peelable laminated film (i) preferably
has an opaqueness of from 60 to 100%. Still further, the base layer
(A) preferably has a laminated structure. A preferred laminated
structure for the base layer (A) is constructed as follows: a layer
(A1) contiguous to the peelable surface layer (B) comprises a
thermoplastic resin film containing from 2 to 60 wt % of an
inorganic fine powder and/or an organic fine powder, and from 98 to
40 wt % of a thermoplastic resin, the content of the inorganic fine
powder and/or the organic fine powder in the layer (A1) being less
than that in the peelable surface layer (B) by 8 wt % or more, and
an outer layer (A2) next to the layer (A1) comprises a
thermoplastic resin film containing from 0 to 80 wt % of an
inorganic fine powder and/or an organic fine powder, and from 100
to 20 wt % of a thermoplastic resin.
[0013] It is preferred to provide a protective layer on the outside
of the peelable surface layer (B). Also, it is preferred to provide
a coat layer on at least one side of the easily peelable laminated
film (i).
[0014] Further, the laminated film of the present invention may be
an easily peelable laminated label (ii), wherein an adhesive is
provided on the side of the peelable surface layer (B) opposite to
the base layer (A) in the easily peelable laminated film (i), or
may be an easily peelable laminated label (ii), wherein a
pressure-sensitive adhesive and a release paper in this order are
provided on the side of the peelable surface layer (B) opposite to
the base layer (A), and it is preferred that the peeling start
stress of the easily peelable label is preferably 500 g/cm width or
less.
[0015] By peeling the base layer (A) off from the easily peelable
laminated label (ii), the letters (characters) and/or the graphic
data provided under the peelable surface layer (B) and/or the
pressure-sensitive adhesive are recognizable.
Best Mode for Carrying Out the Invention
[0016] The easily peelable laminated film according to the present
invention is described in further detail below.
[0017] As described above, the laminated film according to the
present invention is an easily peelable laminated film comprising a
base layer (A) and a peelable surface layer (B) and, if desirable,
a pressure-sensitive adhesive layer, a release paper, or other
laminated films may be provided.
[0018] [Peelable Surface Layer (B)]
[0019] The peelable (back) surface layer (B) in the present
invention is a layer which is weak in strength (i.e., both in
tensile and tear strengths) and the layer itself is easily subject
to cohesive failure so that the base layer (A) is easily peeled
with a hand (fingers) by the cohesive failure in the peelable
surface layer (B).
[0020] The peelable surface layer (B) can be formed by various
methods and it is possible to obtain more stable peelability by
adding an inorganic fine powder and/or an organic fine powder to
the peelable surface layer (B). The content of the inorganic fine
powder and/or the organic fine powder added to the peelable surface
layer (B) is from 10 to 80 wt %, and more preferably from 15 to 75
wt %. When the content of the inorganic fine powder and/or the
organic fine powder contained in the peelable surface layer (B) is
less than 10 wt %, sufficient peelability cannot be obtained, and
when the content exceeds 80 wt %, forming stability is
impaired.
[0021] Further, the peelable surface layer (B) is preferably a
stretched resin film layer. It is possible to obtain a peelable
surface layer (B) having a more uniform thickness if the resin film
is subjected to stretching.
[0022] The resin components constituting the peelable surface layer
(B) are preferably thermoplastic resins which are easily formed by
stretching.
[0023] As the thermoplastic resins, suitable resins include
polyolefin series resins, e.g., ethylene series resins such as high
density polyethylene, medium density polyethylene and low density
polyethylene, propylene series resins, polymethyl-1-pentene and
ethylene-cyclic olefin copolymers; polyamide resins, e.g., nylon-6,
nylon-6,6, nylon-6,10 and nylon-6,12; thermoplastic polyester
series resins, e.g., polyethylene terephthalate and the copolymers
thereof, polyethylene naphthalate and aliphatic polyesters;
polycarbonate; atactic polystyrene; syndiotactic polystyrene; and
polyphenylene sulfide. These resins can be used as a mixture of two
or more. Of these thermoplastic resins, it is preferred to use
polyolefin series resins. Further, of the polyolefin series resins,
propylene series resins and high density polyethylene are more
preferably used in view of production costs, water resistance and
chemical resistance.
[0024] As the examples of such propylene series resins,
polypropylenes which are made from propylene monomers, and show
isotactic or syndiotactic, or various stereoregularities, and
copolymers of a-olefin, e.g., ethylene, butene-1, hexene-1, or
heptene-1,4-methylpentene-1 with propylene as the main component
are exemplified. These copolymers may be binary systems, ternary
systems or quaternary systems, or may be random copolymers or block
copolymers.
[0025] As the inorganic fine powders, those generally having a
particle diameter of from 0.01 to 15 .mu.m, preferably from 0.01 to
8 .mu.m, and more preferably from 0.03 to 4 .mu.m, are suitably
employed. Specifically, calcium carbonate, calcined clay, silica,
diatomaceous earth, talc, titanium dioxide, barium sulfate and
alumina can be used.
[0026] As the organic fine powders, it is preferred to select
resins of a different kind or kinds from the thermoplastic resin or
resins employed as the main component of the film in which the
organic fine powder is incorporated. For example, when polyolefin
series resins are used as the thermoplastic resin, polyethylene
terephthalate, polybutylene terephthalate, polycarbonate, nylon-6,
nylon-6,6, cyclic olefin homopolymer, and cyclic olefin-ethylene
copolymer having a melting point of from 120 to 300.degree. C. or a
glass transition temperature of from 120 to 280.degree. C. are
suitably used as the organic fine powders.
[0027] The peelable surface layer (B) preferably has a thickness of
0.1 to 100 .mu.m, more preferably 0.2 to 80 .mu.m, still more
preferably 0.3 to 60 .mu.m. When the thickness of the peelable
surface layer (B) is less than 0.1 .mu.m, sufficient peelability
cannot be obtained, and when the thickness is more than 100 .mu.m,
there is no problem in the peeling strength but the transparency of
the peelable surface layer (B) decreases, and
information-recognizing performance decreases when the base layer
(A) described later is peeled off. In addition, the peeled surface
becomes uneven, so that a problem arises when the peeled base layer
(A) is used as a management slip by type writing a bar code,
etc.
[0028] [Base Layer (A)]
[0029] The base layer (A) itself is stronger both in tensile and
tear strengths than that of the peelable surface layer (B), and
peeling in the base layer (A) is not carried out when the base
layer (A) is peeled off by taking it.
[0030] The same thermoplastic resins as described above for the
peelable surface layer (B) can be used for the base layer (A). It
is preferred that a thermoplastic resin film (i.e., the laminate of
the base layer (A) and the peelable surface layer (B) as a whole)
obtained from the thermoplastic resin for the base layer (A) be
stretched at least in a monoaxial direction. The uniformity in
thickness of the base layer (A), and the stiffness and tensile
strength of the easily peelable laminated film (i) are improved by
stretching; as a result, the mechanical strength necessary to
processing and printing-can be improved.
[0031] The base layer (A) preferably has a thickness of from 10 to
500 .mu.m, more preferably from 20 to 300 .mu.m. When the thickness
is less than 10 .mu.m, the breaking strength of the base layer (A)
is low, and the base layer (A) may tear when the base layer (A) is
peeled off from the the peelable surface layer (B) (rather, from an
adherend by the cohesion failure of the peelable surface layer (B))
by taking the base layer (A) and the desired performances of the
invention cannot be exhibited. On the other hand, when the
thickness of the base layer (A) exceeds 500 .mu.m, the stiffness of
the easily peelable laminated film (i) becomes excessive, and the
processability and printability decrease when it is used as a
concealing seal and a label for preventing re-pasting.
[0032] The base layer (A) may or may not contain an inorganic fine
powder and/or an organic fine powder. The same inorganic fine
powders and/or organic fine powders as described above for the
peelable surface layer (B) can be used for the base layer (A). The
inorganic fine powders and/or the organic fine powders for use in
the base layer (A) and the peelable surface layer (B) may be the
same or different.
[0033] The base layer (A) may be a multilayer structure of two
layer structure, three layer structure or more. The number of
stretching of the multilayer structure may be any of
monoaxial/monoaxial, monoaxial/biaxial, biaxial/monoaxial,
monoaxial/monoaxial/biaxial, monoaxial/biaxial/monoaxial,
biaxial/monoaxial/monoaxial, monoaxial/biaxial/biaxial,
biaxial/biaxial/monoaxial, and biaxial/biaxial/biaxial. However,
the content of an inorganic fine powder and/or an organic fine
powder in layer (A1) contiguous to the peelable surface layer (B)
is preferably less than that in the peelable surface layer (B) by 8
wt % or more, more preferably by 10 wt % or more. When the
difference in contents of the inorganic fine powder and/or organic
fine powder in layer (A1) and layer (B) is less than 8 wt %, or the
content in layer (A1) is higher than that in layer (B), the
strength of layer (A1) is weaker than that of layer (B), and the
desired performances of the invention cannot be exhibited. Further,
it becomes possible to impart various performances to the easily
peelable laminated film (i) by making the base layer (A) into a
multilayer structure, e.g., writability, printability, thermal
transferability, scratch resistance, secondary processability, and
the like.
[0034] [Protective Layer]
[0035] It is also possible to provide a protective layer on the
outside of the peelable surface layer (B) of the easily peelable
laminated film (i) of the present invention. Since the peelable
surface layer (B) in the present invention is a layer which is weak
in strength, providing a protective layer may help prevent the
peelable surface layer (B) from breaking during the manufacturing
process or various processing stages.
[0036] As the thermoplastic resins which constitute the protective
layer, the thermoplastic resins exemplified in the description of
the base layer (A) can be used, and polyolefin series resins and
functional group-containing polyolefin series resins are preferably
used, as in the case of the base layer (A). Further, since it is
desired that when the base layer (A) is peeled off, the protective
layer should break easily and breaking is propagated to the
peelable surface layer (B), resins having low breaking strength are
preferably used as the protective layer. In the present invention,
the balance of cohesive forces of the base layer (A), the pressure
sensitive adhesive layer, the protective layer (if necessary), and
the peelable surface layer (B) is set as follows: (the base
layer(A))>(the pressure sensitive adhesive layer)>(the
protective layer)>(the peelable surface layer (B)). As specific
examples of such thermoplastic resins, ethylene series resins,
propylene series resins, ethylene-unsaturated carboxylic acid
copolymers, ethylene-acrylic acid copolymers, and graft-modified
products of these resins are exemplified. The protective layer may
or may not contain inorganic fine powders and/or organic fine
powders, and excellent transparency can be obtained when little or
no inorganic fine powders and/or organic fine powders are employed,
and also the recognizability of the information provided under the
protective layer is excellent when the base layer (A) is peeled
off.
[0037] The protective layer is preferably a stretched resin film
layer, and it is possible to obtain a protective layer having a
thin and uniform thickness by stretching.
[0038] The thickness of the protective layer is preferably 0.1
.mu.M or more and smaller than 10 .mu.m, more preferably from 0.1
to 8 .mu.m, and still more preferably from 0.2 to 6 .mu.m. When the
layer thickness is less than 0.1 .mu.m, the protective layer cannot
cover the peelable surface layer (B) entirely, so that the function
of the protective layer is not exhibited. On the other hand, when
the layer thickness is more than 10 .mu.m, the peeling staring
property of the peelable laminated label (ii) is impaired.
[0039] [Formation of Resin Film]
[0040] The method of forming a resin film is not especially
restricted and various conventionally well-known methods can be
used, specifically cast-formation of extruding a molten resin in a
sheet-like form by using monolayer or multilayer T die(s) or I
die(s) connected with an extruder, inflation-formation of extruding
a molten resin in a tube-like form with a circular die and
expanding the resin with internal air pressure, calender-formation
of calendering kneaded material with a plurality of heat rollers
and processing in a sheet-like form, and rolling-formation are
exemplified.
[0041] [Lamination]
[0042] It is preferred that the laminate of the base layer (A) and
the peelable surface layer (B) be stretched at least in the
monoaxial direction after being laminated. Since the peelable
surface layer (B) in the present invention is low in strength and
thin in thickness, stretching of the peelable surface layer (B) as
a monolayer is very difficult. It is possible to stretch the
peelable surface layer (B) only when the base layer (A) and the
peelable surface layer (B) are laminated.
[0043] Various well-known lamination methods can be used, e.g., a
multilayer die method using feed block and multi-manifold and a
lamination method using a plurality of dies are exemplified. It is
also possible to use multilayer dies and extruding lamination in
combination.
[0044] [Stretching]
[0045] The peelable surface layer (B) in the present invention is
characterized in that the thickness is as thin as from 0.1 to 100
.mu.m, and thinning of a thickness becomes easy by performing
stretching.
[0046] Stretching can be done by any of ordinarily used various
methods.
[0047] The temperature at stretching can be selected from the
well-known range of from glass transition temperature or higher to
melting point or lower of crystal portions suitable for
thermoplastic resins. Specifically, when a propylene homopolymer
(melting point: 155 to 167.degree. C.) is used as the thermoplastic
resin, the stretching temperature is from 100 to 164.degree. C.,
and in the case of high density polyethylene (melting point: 121 to
134.degree. C.), the stretching temperature is from 70 to
133.degree. C., which are temperatures lower than melting points by
1 to 70.degree. C. When polyethylene terephthalate (melting point:
246 to 252.degree. C.) is used, the temperature at which
crystallization does not proceed abruptly is selected. The
stretching velocity is preferably from 20 to 350 m/min.
[0048] When a cast molded film is subjected to stretching,
stretching is performed by longitudinal stretching making use of
the difference between the peripheral speeds of rolls, transverse
stretching using a tenter oven, calendering, and simultaneous
biaxial stretching by combination of a tenter oven and a linear
motor. As the stretching method of an inflation film, simultaneous
biaxial stretching by a tubular method can be exemplified.
[0049] Stretching ratios are not particularly limited and are
suitably decided taking the characteristics of thermoplastic resins
into consideration. For example, when a propylene homopolymer or a
copolymer thereof is used as the thermoplastic resin and stretched
in one direction, the stretching ratio is from 1.2 to 12 times,
preferably from 2 to 10 times, and when biaxially stretched, from
1.5 to 60 times in terms of area, preferably from 4 to 50 times.
When other thermoplastic resins are used and stretched in one
direction, the stretching ratio is from 1.2 to 10 times, preferably
from 2 to 5 times, and when biaxially stretched, from 1.5 to 20
times in terms of area, preferably from 4 to 12 times.
[0050] The thus-obtained laminated film has many micro voids having
a void ratio of from 10 to 60%, preferably from 20 to 45%, which is
computed according to the following equation (1), inside the film.
By the presence of voids, the film becomes more flexible as
compared with multilayer-stretched films free of voids. Further,
there is an intimate relationship between the void ratio and the
later-described peeling strength, and it is possible to reduce the
peeling strength of the peelable surface layer (B) by heightening
the void ratio of the peelable surface layer (B).
Void ratio (%)=(.rho..sup.0-.rho..sup.1)/.rho..sup.0.times.100
equation (1)
[0051] wherein .rho..sup.0 is the density of film before
stretching, and .rho..sup.1 is the density of film after
stretching.
[0052] [Peeling Strength]
[0053] Easily peelable laminated film (i) is conditioned in a
thermostatic chamber (temperature: 20.degree. C., relative
humidity: 65%) for 12 hours, and then a pressure-sensitive adhesive
tape (trade name: Cello-Tape, manufactured by Nichiban Co., Ltd.)
is adhered on the peelable surface layer (B), which is cut out in a
size of 10 mm in width and 100 mm in length, the pressure-sensitive
adhesive tape is peeled at a tensile velocity of 300 mm/min. and an
angle of 180.degree. by a tensile tester AUTOGRAPH (manufactured by
Shimadzu Corporation), and the stress of the time when peeling of
the peelable surface layer (B) is stable is measured as the peeling
strength by a load cell. The peeling strength according to the
present invention is preferably from 5 to 150 g/cm, more preferably
from 10 to 100 g/cm, still more preferably 20 to 80 g/cm. When the
peeling strength is less than 5 g/cm, a problem arises such that
peeling easily occurs at feeding and delivery of a film in the
secondary processing, e.g. printing, type writing, cutting and the
like. When the peeling strength exceeds 150 g/cm, the peelable
surface layer (B) is not peeled off or the stress required for
peeling should be heightened, thus it is not practicable. Further,
material fracture occurs at places other than the peelable surface
layer (B) and peeled surface becomes fluffy.
[0054] [Opaqueness]
[0055] Opaqueness is the value expressing the ratio of the
reflectance of light (black plate/white plate) in percentage with
applying black and white standard plates respectively to the back
of measurement in conformity to JIS-P-8138.
[0056] The opaqueness of easily peelable laminated film (i) in the
present invention is preferably from 60 to 100%, more preferably
from 70 to 100%, and still more preferably from 85 to 100%. When
the opaqueness is less than 60%, the informations to be protected
are seen through a label when easily peelable laminated film (i) is
used as a concealing seal, and the desired effect of the invention
cannot be exhibited.
[0057] [Formation of Pressure-Sensitive Adhesive Layer]
[0058] A pressure-sensitive adhesive layer can be provided on the
side of the peelable surface layer (B) opposite to the base layer
(A) of the easily peelable laminated film (i) of the invention
(i.e., next to the peelable surface layer or next to the protective
layer, if provided), if desired.
[0059] By providing a pressure-sensitive adhesive layer on an
easily peelable laminated film, an easily peelable laminated label
(ii) can be obtained.
[0060] As such pressure-sensitive adhesives, rubber-based
pressure-sensitive adhesives, acryl-based pressure-sensitive
adhesives and silicon-based pressure-sensitive adhesives are
representative. Specific examples of rubber-based
pressure-sensitive adhesives include polyisobutylene rubber, butyl
rubber and mixtures thereof, and pressure-sensitive adhesives
obtained by blending these rubber-based pressure-sensitive
adhesives with a tackifier, e.g., abietic acid rosin ester, a
terpene-phenol copolymer, or a terpene-indene copolymer. Specific
examples of acryl-based pressure-sensitive adhesives include those
having a glass transition temperature of -20.degree. C. or less,
e.g., a 2 thylhexyl acrylate-n-butyl acrylate copolymer and a
2-ethylhexyl acrylate-ethyl acrylate-methyl methacrylate
copolymer.
[0061] As the types of these pressure-sensitive adhesives, a
solvent-type, an emulsion-type and a hot melt-type are used. In
general, a pressure-sensitive adhesive layer is laminated by
coating a solvent-type or emulsion-type adhesive.
[0062] Coating is performed by means of a roll coater, a blade
coater, a bar coater, an air knife coater, a gravure coater, a
reverse coater, a die coater, a lip coater, a spray coater, or a
comma coater and, if necessary, smoothing is performed, and a
pressure-sensitive adhesive layer is formed through drying.
[0063] A pressure-sensitive adhesive layer is generally formed by
coating a pressure-sensitive adhesive on a release paper, which is
described later, and easily peelable laminated film (i) is
laminated thereon, but according to the case, a pressure-sensitive
adhesive may be directly coated on easily peelable laminated film
(i).
[0064] The coating amount of the pressure-sensitive adhesive is not
particularly restricted but is in general from 3 to 60 g/m.sup.2,
preferably from 10 to 40 g/m.sup.2. Further, it is preferred that
the peeling strength in the pressure-sensitive adhesive layer is
from 200 to 3,000 g/20 mm.
[0065] When the adhesive strength between easily peelable laminated
film (i) and the pressure-sensitive adhesive is small, it is
preferred to coat an anchor coating agent on the back surface of
the laminated film before coating a pressure-sensitive
adhesive.
[0066] As the anchor coating agents, polyurethane, polyisocyanate,
polyether polyol, polyisocyanate-polyester
polyol-polyethyleneimine, alkyl titanate, etc., can be used, and
these anchor coating agents are generally used by being dissolved
in an organic solvent, e.g., methanol, ethyl acetate, toluene,
hexane, etc., or water.
[0067] The coating amount of anchor coating agents is from 0.01 to
5 g/m.sup.2 in terms of solid content after coating and drying,
preferably from 0.02 to 2 g/m.sup.2.
[0068] [Release Paper]
[0069] If necessary, a release paper can also be provided on the
outer side of the adhesive layer in the easily peelable laminated
label (ii).
[0070] The side in contact with the pressure-sensitive adhesive
layer of the release paper which is provided on easily peelable
laminated film (i) with the pressure-sensitive adhesive layer is
generally subjected to silicon treatment to improve the peelability
from the pressure-sensitive adhesive layer.
[0071] Generally used release papers can be used in the invention,
e.g., wood free paper and kraft paper as they are, or subjected to
calendering process, coated with a resin, or laminated with a film,
and glassine paper, coated paper and plastic film subjected to
silicon treatment can be used.
[0072] [Coat Layer]
[0073] It is also possible to provide a coat layer on at least one
side of the surface of the easily peelable laminated film (i) of
the present invention for further improving various printing or
type writing aptitudes.
[0074] As such coat layers, as for coat layers suitable for
commercial printing, e.g., offset printing, gravure printing,
flexographic printing, screen printing and letter press printing,
the combinations of well-known pigments and binders for well-known
printing inks, as for the coat layers for heat-sensitive recording
paper, the combinations of well-known leuco dyes and developers, as
for the coat layers for ink-jet recording paper, the combinations
of water-soluble resins, emulsion binders, water absorptive
pigments and ink fixers of cationic substances, and as for the coat
layers for melting type heat transfer recording paper, the
combinations of well-known lipophilic pigments and various kinds
resin binders are exemplified.
[0075] These coat layers can be manufactured according to
well-known methods, and as the specific example, e.g., a roll
coater, a blade coater, a bar coater, an air knife coater, a
gravure coater, a reverse coater, a die coater, a lip coater, a
spray coater and a comma coater are exemplified.
[0076] The manufacture of a coat layer may be performed by
multistage of two or more stages, if necessary.
[0077] [Printing, Type Writing]
[0078] It is also possible to print or type-write a trade name, a
manufacturer, eatable limit, the drawing of a character, an entry
column, bar code, etc., on the front surface and back surface of
easily peelable laminated film (i), if necessary.
[0079] Printing or typewriting may be performed in the state of a
simple substance of an easily peelable laminated film or may be
performed after an easily peelable label structure is formed by
applying a release paper.
[0080] [Peeling Start Stress]
[0081] A test piece is cut from easily peelable laminated label
(ii) in a size of 10 mm in width and 100 mm in length. Wood free
paper having a thickness of 100 .mu.m is adhered on the end of the
test piece 30 mm in the lengthwise direction and wholly in the
widthwise direction to make a chucking allowance, and an aluminum
plate having a width of 20 mm, a length of 110 nm and a thickness
of 1 mm is adhered thereon so that the test piece is not forced
out. The prepared sample is conditioned in a thermostatic chamber
(temperature: 20.degree. C., relative humidity: 65%) for 12 hours,
and then the test piece and the aluminum plate are peeled at a
tensile velocity of 300 mm/min. and an angle of 180.degree. by a
tensile tester AUTOGRAPH (manufactured by Shimadzu Corporation),
and the stress is measured by a load cell. The maximum stress value
is taken as the peeling start stress. The peeling start stress in
the present invention is preferably 500 g/cm or less, more
preferably 1 to 400 g/cm, further preferably 20 to 350 g/cm. When
the peeling start stress is higher than 500 g/cm, surface fracture
of the object material to which the peelable laminated label (ii)
is adhered occurs, as a result, peeling is not propagated to the
peelable surface layer (B) or the easily peelable laminated film
(i) is deformed and not practicable.
EXAMPLE
[0082] The present invention is further specifically described with
reference to the following examples, comparative example and test
example, but the present invention should not be construed as being
limited thereto. The materials, use amounts, ratios and operations
can be modified so long as they do not depart from the spirit of
the present invention. Accordingly, the scope of the present
invention is not limited to the specific examples shown below.
[0083] In the following, the thermoplastic resin composition for
use in the present invention are shown collectively in Table 1
below.
1TABLE 1 Name of Material Content Thermoplastic A thermoplastic
resin composition obtained by kneading in resin composition a an
extruder set at 230.degree. C. a composition obtained by blending a
mixture comprising 70 wt % of a propylene homopolymer (Novatec
PP:FY4, manufactured by Japan Polychem Corporation) having MFR of 5
g/10 min (230.degree. C., load: 2.16 kg) and 20 wt % of high
density polyethylene (Novatec HD:HJ360, manufactured by Japan
Polychem Corporation) having MFR of 5.5 g/min (190.degree. C.,
load: 2.16 kg) with 10 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m Thermoplastic A thermoplastic resin
composition obtained by kneading in resin composition b an extruder
set at 230.degree. C. a composition obtained by blending a mixture
comprising 70 wt % of a propylene homopolymer (Novatec PP:FY4,
manufactured by Japan Polychem Corporation) having MFR of 5 g/10
min (230.degree. C., load: 2.16 kg) and 10 wt % of high density
polyethylene (Novatec HD:HJ360, manufactured by Japan Polychem
Corporation) with 20 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m Thermoplastic A thermoplastic resin
composition obtained by kneading in resin composition c an extruder
set at 230.degree. C. a composition obtained by blending a mixture
comprising 60 wt % of a propylene homopolymer (Novatec PP:FY4,
manufactured by Japan Polychem Corporation) having MFR of 5 g/10
min (230.degree. C., load: 2.16 kg) and 10 wt % of high density
polyethylene (Novatec HD:HJ360, manufactured by Japan Polychem
Corporation) with 30 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m Thermoplastic A thermoplastic resin
composition obtained by kneading in resin composition d an extruder
set at 230.degree. C. a composition obtained by blending 60 wt % of
a propylene homopolymer (Novatec PP:MA3, manufactured by Japan
Polychem Corporation) having MFR of 11 g/10 min (230.degree. C.,
load: 2.16 kg) with 40 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m Thermoplastic A thermoplastic resin
composition obtained by kneading in resin composition e an extruder
set at 230.degree. C. a composition obtained by blending 50 wt % of
a propylene homopolymer (Novatec PP:MA3, manufactured by Japan
Polychem Corporation) having MFR of 11 g/10 min (230.degree. C.,
load: 2.16 kg) with 50 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m Thermoplastic A thermoplastic resin
composition obtained by kneading in resin composition f an extruder
set at 230.degree. C. a composition obtained by blending 40 wt % of
a propylene homopolymer (Novatec PP:MA3, manufactured by Japan
Polychem Corporation) having MFR of 11 g/10 min (230.degree. C.,
load: 2.16 kg) with 60 wt % of calcium carbonate (Softon 1800,
manufactured by Shiraishi Calcium Kaisha Ltd.) having an average
particle size of 1.2 .mu.m
Example 1
[0084] After each of thermoplastic resin composition d as layer
(B), thermoplastic resin composition b as layer (A1), and
thermoplastic resin composition c as layer (A2) was kneaded in each
extruder set at 230.degree. C., they were supplied to a
co-extrusion die set at 250.degree. C., laminated in the die and
extruded in a sheet. The laminate was cooled by a cooler, thereby a
three-layer unstretched sheet was obtained. The unstretched sheet
was heated at 130.degree. C. and stretched 5 times in the machine
direction.
[0085] The above sheet was cooled to a temperature of 60.degree.
C., again heated to a temperature of 150.degree. C. and stretched
8.0 times in the transverse direction in a tenter oven, subjected
to annealing treatment at a temperature of 162.degree. C., cooling
at 60.degree. C., and corona discharge treatment, and then
trimming, thereby a laminated film of a three-layer structure
[(B)/(A1)/(A2): 1/49/10 .mu.m in thickness, stretched layer
constitution: biaxial/biaxial/biaxial] having a thickness of 60
.mu.m, a peeling strength of 25 g/cm, and an opaqueness of 91% was
obtained.
Example 2
[0086] After each of thermoplastic resin composition d as layer (B)
and thermoplastic resin composition b as layer (A1) was kneaded in
each extruder set at 230.degree. C., they were supplied to a
co-extrusion die set at 250.degree. C., laminated in the die and
extruded in a sheet. The laminate was cooled by a cooler, thereby a
two-layer unstretched sheet was obtained. The unstretched sheet was
heated at 130.degree. C. and stretched 4 times in the machine
direction.
[0087] Thermoplastic resin composition b as layer (A2) was kneaded
in an extruder set at 250.degree. C. and extruded in a sheet, and
this sheet was laminated on the above-prepared 4 time-stretched
film (A1), thereby a three-layer structure laminated film was
obtained. The three-layer structure laminated film was cooled to a
temperature of 60.degree. C., again heated to about 160.degree. C.
by a tenter oven and stretched 7.5 times in the transverse
direction, subjected to annealing treatment in a heat-set zone
adjusted to 165.degree. C., cooling at 60.degree. C., and then
trimming, thereby a laminated film of a three-layer structure
[(B)/(A1)/(A2): 1/49/30 .mu.m in thickness, stretched layer
constitution: biaxial/biaxial/monoaxial] having a thickness of 80
.mu.m, a peeling strength of 40 g/cm, and an opaqueness of 88% was
obtained.
Example 3
[0088] After each of thermoplastic resin composition f as layer
(B), thermoplastic resin composition b as layer (A1), and
thermoplastic resin composition c as layer (A2) was kneaded in each
extruder set at 240.degree. C., they were supplied to a
co-extrusion die set at 270.degree. C., laminated in the die and
extruded in a sheet. The laminate was cooled by a cooler, thereby a
three-layer unstretched sheet was obtained. The unstretched sheet
was heated at 120.degree. C. and stretched 5 times in the machine
direction, subjected to annealing treatment at 160.degree. C.,
corona discharge treatment, and then trimming, thereby a laminated
film of a three-layer structure [(B)/(A1)/(A2): 4/46/10 .mu.m in
thickness, stretched layer constitution:
monoaxial/monoaxial/monoaxial] having a thickness of 60 .mu.m, a
peeling strength of 90 g/cm, and an opaqueness of 87% was
obtained.
Example 4
[0089] After each of thermoplastic resin composition c as layer (B)
and thermoplastic resin composition b as layer (A1) was kneaded in
each extruder set at 220.degree. C., they were supplied to a
co-extrusion die set at 240.degree. C., laminated in the die and
extruded in a sheet. The laminate was cooled by a cooler, thereby a
two-layer unstretched sheet was obtained. The unstretched sheet was
heated at 140.degree. C. and stretched 4 times in the machine
direction.
[0090] After each of thermoplastic resin composition d as layer
(A2) and thermoplastic resin composition e as layer (A3) was
kneaded in each extruder set at 250.degree. C., they were supplied
to a co-extrusion die set at 250.degree. C., laminated in the die
and extruded in a sheet, and this sheet was laminated on the
above-prepared 4 time-stretched film (A1), thereby a four-layer
structure laminated film was obtained. The four-layer structure
laminated film was cooled to a temperature of 60.degree. C., again
heated to about 160.degree. C. by a tenter oven and stretched 7.5
times in the transverse direction, subjected to annealing treatment
in a heat-set zone adjusted to 170.degree. C., cooling at
60.degree. C., and then trimming, thereby a laminated film of a
four-layer structure [(B)/(A1)/(A2)/(A3): 1/39/100/10 .mu.m in
thickness, stretched layer constitution:
biaxial/biaxial/monoaxial/monoaxial] having a thickness of 150
.mu.m, a peeling strength of 130 g/cm, and an opaqueness of 66% was
obtained.
Example 5
[0091] Thermoplastic resin composition b as layer (A2) was kneaded
in an extruder set at 250.degree. C., supplied to a die set at
250.degree. C., extruded in a sheet, and the sheet was cooled by a
cooler, thereby a monolayer unstretched sheet was obtained. The
unstretched sheet was heated at 135.degree. C. and stretched 4
times in the machine direction.
[0092] After each of thermoplastic resin composition f as layer (B)
and thermoplastic resin composition b as layer (A1) was kneaded in
each extruder set at 230.degree. C., they were supplied to a
co-extrusion die set at 240.degree. C., laminated in the die and
extruded in a sheet, and this sheet was laminated on the
above-prepared 4 time-stretched film (A2), further, thermoplastic
resin composition d as layer (A3) was kneaded in an extruder set at
240.degree. C., and extruded in a sheet, and this sheet was
laminated on the opposite side of the above-prepared 4
time-stretched film (A2), thereby a four-layer structure laminated
film was obtained. The four-layer structure laminated film was
cooled to 60.degree. C., again heated to about 120.degree. C. by a
tenter oven and stretched 8.0 times in the transverse direction,
subjected to annealing treatment in a heat-set zone adjusted to
160.degree. C., cooling at 60.degree. C., and then trimming,
thereby a laminated film of a four-layer structure
[(B)/(A1)/(A2)/(A3): 3/70/57/70 .mu.m in thickness, stretched layer
constitution: monoaxial/monoaxial/biaxial/monoaxial] having a
thickness of 200 .mu.m a peeling strength of 140 g/cm, and an
opaqueness of 95% was obtained.
Example 6
[0093] Thermoplastic resin composition a as layer (A1) was kneaded
in an extruder set at 230.degree. C., supplied to a die set at
250.degree. C., extruded in a sheet, and the sheet was cooled by a
cooler, thereby an unstretched sheet was obtained.
[0094] Thermoplastic resin composition e as layer (B) was kneaded
in an extruder set at 240.degree. C., and extruded from a die set
at 270 degrees C., and laminated on the above-prepared unstretched
sheet, thereby a two-layer structure laminated sheet was obtained.
The two-layer structure laminated unstretched sheet was heated at a
temperature of 120.degree. C. and stretched 5 times in the machine
direction, subjected to annealing treatment at 140.degree. C.,
corona discharge treatment, and then trimming, thereby a laminated
film of a two-layer structure [(B)/(A1): 7/93 .mu.m in thickness,
stretched layer constitution: monoaxial/monoaxial] having a
thickness of 100 .mu.m, a peeling strength of 110 g/cm, and an
opaqueness of 85% was obtained.
Example 7
[0095] After each of thermoplastic resin composition a as a
protective layer, thermoplastic resin composition c as layer (B),
thermoplastic resin composition a as the layer (A1), and
thermoplastic resin composition b as the layer (A2) was kneaded in
each extruder set at 230.degree. C., they were supplied to a
co-extrusion die set at 250.degree. C., and laminated in the die
and extruded in a sheet. The laminated sheet was cooled by a
cooler, thereby a four-layer unstretched sheet was obtained. The
unstretched sheet was heated at 120.degree. C. and stretched 5
times in the machine direction, and then cooled to 60.degree. C.
The sheet was again heated to about 140.degree. C. by a tenter oven
and stretched 8 times in the transverse direction, and subjected to
annealing treatment in a heat-set zone adjusted to 160.degree. C.,
cooling at 60.degree. C., corona discharge treatment, and then
trimming, thereby a laminated film of a four-layer structure
[protective layer/(B)/(A1)/(A2): 1/39/90/10 .mu.m in thickness,
stretched layer constitution: biaxial/biaxial/biaxial/biaxial]
having a thickness of 140 .mu.m, a peeling strength of 25g/cm, and
an opaqueness of 95% was obtained.
Comparative Example 1
[0096] After each of thermoplastic resin composition d as layer
(B), thermoplastic resin composition b as layer (A1), and
thermoplastic resin composition c as layer (A2) was kneaded in each
extruder set at 240.degree. C., they were supplied to a
co-extrusion die set at 260.degree. C., laminated in the die and
extruded in a sheet The laminate was cooled by a cooler, thereby a
three-layer unstretched sheet was obtained. The unstretched sheet
was heated at 140.degree. C. and stretched 4 times in the machine
direction, subjected to annealing treatment at 160.degree. C.,
corona discharge treatment, and then trimming, thereby a laminated
film of a three-layer structure [(B)/(A1)/(A2): 4/46/10 .mu.m in
thickness, stretched layer constitution:
monoaxial/monoaxial/monoaxial] having a thickness of 60 .mu.m, a
peeling strength of 200 g/cm, and an opaqueness of 67% was
obtained.
Comparative Example 2
[0097] The easily peelable resin-stretched film disclosed in
Example 1 in Japanese Patent Laid-Open No. 258476/1998 was
used.
Test Example
[0098] A release paper comprising wood free paper having a
thickness of 173 .mu.m and density of 0.9 g/m.sup.3 both surfaces
of which were laminated with a polyethylene film and one surface of
which was treated with silicon was prepared. A pressure-sensitive
adhesive "Oribain" BPS-1109 (trade name, manufactured by TOYO INK
MFG CO., LTD.) was coated on the silicon-treated surface of the
release paper in a solid content of 25 g/m.sup.2 by means of a
comma coater and dried, thereby a pressure-sensitive adhesive layer
was obtained. The pressure-sensitive adhesive layer was laminated
on each of the easily peelable laminated films (i) prepared in the
above Examples and Comparative Examples so that the
pressure-sensitive adhesive layer was in contact with the peelable
surface layer (B) (or the protective layer, in the case of Example
7), thereby easily peelable label (ii) of laminated structure
comprising an easily peelable laminated film/a pressure-sensitive
adhesive layer/a release paper was obtained. The peeling start
stress of each easily peelable label (ii) was measured according to
the above method.
[0099] (Peelability)
[0100] A sample of each easily peelable label (ii) was cut out in a
square of 5 cm.times.5 cm, the release paper was peeled off from
the label, and the easily peelable label was stuck on a Japanese
official post card, and the peelability was evaluated.
[0101] (1) Peeling starting property
[0102] One side of the four sides of the easily peelable label
(easily peelable laminated film/pressure-sensitive adhesive layer)
was taken with fingers and peeled off from the postcard. The state
until peeling of the peelable surface layer (B) started was
observed and evaluated according to the following four grades, when
the base layer (A) was peeled off from the post card.
[0103] Good (.circleincircle.): Peeling started immediately.
[0104] A little good (.smallcircle.): 2 mm or more was required to
start peeling.
[0105] A little bad (.DELTA.): Peeling started partially (i.e., 2
mm or more and less than 10 mm was required to start peeling, and
the peeling start portion has an uneven surface).
[0106] Bad (X): 10 mm or more was required to start peeling.
[0107] (2) Propagation of peeling
[0108] A pressure-sensitive adhesive tape (trade name: Cello-Tape,
manufactured by Nichiban Co., Ltd.) was adhered on one side of the
four sides of the base layer (A) in the easily peelable label to
make it easy to start peeling of the peelable surface layer (B),
when the base layer (A) was peeled off from the post card. The base
layer (A) was peeled off from the post card and the state of
propagation of the peelable surface layer (B) and the peeling force
were evaluated according to the following four grades.
[0109] Good (.circleincircle.): Peeling force was light and peeling
was propagated to the surface throughout.
[0110] A little good (.smallcircle.): Peeling force was a little
heavy but peeling was propagated to the surface throughout.
[0111] A little bad (.DELTA.): Peeling force was very heavy but
peeling was propagated to the surface throughout.
[0112] Bad (X): Peeling could not be propagated to the surface at
all and the base layer (A) tore on the way.
[0113] (Information-Concealing Property)
[0114] Twenty six letters of the alphabet of the letter size of 10
points were typed on a Japanese official post card. After peeling
off the release paper from a sample of each of the easily peelable
labels, the easily peelable label was stuck on the typed alphabet
letters. The information-concealing property of the easily peelable
label was visually judged from the letters seen through the easily
peelable label and evaluated according to four grades of good
(.circleincircle.), a little good (.smallcircle.), a little bad
(.DELTA.), and Bad (X).
[0115] Good (.circleincircle.): It was impossible to recognize the
letters (characters).
[0116] A little good (.smallcircle.): It was possible to see the
presence of the letters through the easily peelable label very
slightly, but it was impossible to recognize them as letters.
[0117] A little bad (.DELTA.): It was possible to see the presence
of the letters through the easily peelable label while they were
not so clear, and it was possible to recognize part of the
letters.
[0118] Bad (X): It was possible to clearly recognize all of the
letters.
[0119] (Information-Recognizing Property)
[0120] Bar code (CODE39) was printed on a synthetic paper (trade
name: "VES85", manufactured by Yupo Corporation) by means of a bar
code printer (trade name: "B30", manufactured by TEC) to thereby
prepare an exact sample for bar code-reading.
[0121] The release paper was peeled off from a sample of each of
the easily peelable labels, the easily peelable label was stuck on
the bar code on the synthetic paper, and ten samples whose bar
codes were concealed were prepared. Each of the bar codes after
peeling off the base layer (A) of the easily peelable label was
read with a bar code reader (LASERCHEK II, manufactured by Fuji
Denki Reiki Co., Ltd.), and the number of times which succeeded in
recognizing bar code was evaluated according to the following four
grades.
[0122] Good (.circleincircle.): Succeeded 10 times.
[0123] A little good (.smallcircle.): Succeeded from 8 to 9
times.
[0124] A little bad (.DELTA.): Succeeded from 2 to 7 times.
[0125] Bad (X): Succeeded 1 time or less.
[0126] The results obtained are shown in Table 2 below.
2 TABLE 2 Easily Peelable Laminated Film Peeling Stretched Layer
Amount of Strength Thickness (.mu.m) Constitution Fine Powder (%)
(layer (B) Opaque- Example Layer Layer (A) Layer Layer (A) Layer
Layer (A) surface) ness No. Entire (B) (A1/A2/A3) (B) (A1/A2/A3)
(B) (A1/A2/A3) (g/cm) (%) Ex. 1 60 1 49/10 biaxial biaxial/biaxial
40 20/30 25 91 Ex. 2 80 1 49/30 biaxial biaxial/monoaxial 40 20/20
40 88 Ex. 3 60 4 46/10 monoaxial monoaxial/monoaxial 60 20/30 90 87
Ex. 4 150 1 39/100/10 biaxial biaxial/monoaxial/ 30 20/40/50 130 66
monoaxial Ex. 5 200 3 70/57/70 monoaxial monoaxial/biaxial/ 60
20/20/40 140 95 monoaxial Ex. 6 100 7 93 monoaxial monoaxial 50 10
110 85 Ex. 7 140 39 90/10 biaxial biaxial/biaxial 30 10/20 25 95
Comp. 60 4 46/10 monoaxial monoaxial/monoaxial 40 20/30 200 67 Ex.
1 Comp. -- -- -- -- -- -- -- -- 91 Ex. 2 Peeling Item of Evaluation
Start Peelability Example Stress Starting Information- Information-
No. (g/cm) property Propagation Concealing Property recognizing
property Ex. 1 70 .circleincircle. .circleincircle.
.circleincircle. .circleincircle. Ex. 2 90 .circleincircle.
.circleincircle. .circleincircle. .circleincircle. Ex. 3 210
.circleincircle. .circleincircle. .circleincircle. .circleincircle.
Ex. 4 250 .largecircle. .smallcircle. .smallcircle.
.circleincircle. Ex. 5 310 .largecircle. .smallcircle.
.circleincircle. .circleincircle. Ex. 6 280 .largecircle.
.smallcircle. .circleincircle. .circleincircle. Ex. 7 190
.circleincircle. .circleincircle. .circleincircle. .smallcircle.
Comp. 530 X x .smallcircle. .circleincircle. Ex. 1 Comp. -- X
.circleincircle. .circleincircle. .circleincircle. Ex. 2
Industrial Applicability
[0127] The easily peelable laminated film according to the present
invention requires no specific processing to start peeling, and the
peelable surface layer (B) can be peeled off with light force.
Therefore, the easily peelable laminated film in the invention can
be used for various uses, such as delivery slips, concealing seals,
labels for preventing re-pasting, seals for preventing alteration,
application seals, coupons, etc.
* * * * *