U.S. patent application number 10/089414 was filed with the patent office on 2003-05-15 for aqueous surfactant solution for developing coating film layer.
Invention is credited to Kanda, Takashi.
Application Number | 20030091732 10/089414 |
Document ID | / |
Family ID | 18729016 |
Filed Date | 2003-05-15 |
United States Patent
Application |
20030091732 |
Kind Code |
A1 |
Kanda, Takashi |
May 15, 2003 |
Aqueous surfactant solution for developing coating film layer
Abstract
The developer of the present invention is used in a method where
a water-soluble resin coating layer is applied on a resist pattern
formed by the conventional method, and the coating layer is
crosslinked by an acid supplied from the resist, and the
uncrosslinked area in the coating layer is dissolved and removed
with a developer to thicken the resist pattern. This developer
comprises an aqueous solution containing at least one surfactant
selected from an N-acylsarcosinate, an N-acyl-N-methylalaninate, an
N-acyltaurinate, an N-acyl-N-methyltaurinate- , a fatty acid
alkylol amide, and a fatty acid alkylol amide polyoxyethylene
adduct.
Inventors: |
Kanda, Takashi; (Ogasa-gun,
Shizuoka, JP) |
Correspondence
Address: |
CLARIANT CORPORATION
INTELLECTUAL PROPERTY DEPARTMENT
4000 MONROE ROAD
CHARLOTTE
NC
28205
US
|
Family ID: |
18729016 |
Appl. No.: |
10/089414 |
Filed: |
August 13, 2002 |
PCT Filed: |
July 19, 2001 |
PCT NO: |
PCT/JP01/06262 |
Current U.S.
Class: |
427/162 |
Current CPC
Class: |
G03F 7/322 20130101;
G03F 7/32 20130101 |
Class at
Publication: |
427/162 |
International
Class: |
B05D 005/06 |
Foreign Application Data
Date |
Code |
Application Number |
Aug 4, 2000 |
JP |
2000-237099 |
Claims
1. A surfactant aqueous solution for development of a coating layer
comprising a surfactant and water or a mixture of water and an
organic solvent, wherein the surfactant comprises at least one
selected from an N-acylsarcosinate, an N-acyl-N-methylalaninate, an
N-acyltaurinate, an N-acyl-N-methyltaurinate, a fatty acid alkylol
amide, and a fatty acid alkylol amide polyoxyethylene adduct.
2. The surfactant aqueous solution for development of a coating
layer according to claim 1, wherein the number of carbon atoms of
the acyl group of the surfactant is 10 to 14.
3. The surfactant aqueous solution for development of a coating
layer according to claim 1 or 2, wherein the surfactant is at least
one selected from N-lauroylsarcosinate,
N-lauroyl-N-methylalaninate, N-lauroyltaurinate, and
N-lauroyl-N-methyltaurinate.
4. The surfactant aqueous solution for development of a coating
layer according to claim 1, wherein the counter ion of the
N-acylsarcosinate, the N-acyl-N-methylalaninate, the
N-acyltaurinate, and the N-acyl-N-methyltaurinate is an organic
amine or an organic amine salt.
5. The surfactant aqueous solution for development of a coating
layer according to claim 1 or 2, wherein the number of carbon atoms
of the fatty acid of the fatty acid alkylol amide or the fatty acid
alkylol amide polyoxyethylene adduct is 6 to 22, and the number of
carbon atoms of the alkylol group thereof is 1 to 3, and the number
of repeating units of the polyoxyethylene chain of the fatty acid
alkylol amide polyoxyethylene adduct is 10 or less.
6. The surfactant aqueous solution for development of a coating
layer according to any one of claims 1 to 5, wherein the
concentration of the surfactant is 0.01 to 10.0% by weight.
7. The surfactant aqueous solution for development of a coating
layer according to any one of claims 1 to 6, wherein the organic
solvent comprises at least one selected from a saturated or
unsaturated alcohol with 1 to 8 carbon atoms, a saturated
polyvalent alcohol with 2 or 3 hydroxyl groups, a saturated or
unsaturated alkyl amine with 1 to 3 carbon atoms, and a saturated
or unsaturated alkanol amine with 1 to 3 carbon atoms.
8. The surfactant aqueous solution for development of a coating
layer according to any one of claims 1 to 7, wherein water and the
organic solvent are mixed in a ratio of water to the organic
solvent of 80:20 to 99:1.
9. A method of forming a pattern comprising forming a coating layer
on a resist pattern, thickening the resist pattern by crosslinking
of the coating layer, and removing the uncrosslinked coating layer
with a developer to effectively make the pattern finer, wherein the
surfactant aqueous solution for development of a coating layer
according to any one of claims 1 to 8 is used as a developer.
Description
TECHNICAL FIELD
[0001] The present invention relates to a novel surfactant aqueous
solution for development of a coating layer, and more specifically
to a novel surfactant aqueous solution for development of a coating
layer, which is used in the method of forming resist patterns in
manufacturing semiconductor elements where a trench pattern and a
hole pattern are effectively made finer by forming a resist
pattern, forming a coating layer on the resist pattern formed, and
then thickening the resist pattern, and a method of forming fine
resist patterns using this surfactant aqueous solution.
BACKGROUND ART
[0002] In the wide field of manufacturing semiconductor elements
such as LSIs, producing liquid crystal display surfaces of LCD
panels, manufacturing circuit substrate for a thermal head, and
like use, resist patterns have been formed on substrates for
formation of fine elements or fine processing. In the formation of
resist patterns, a so-called photolithography process has been
employed which involves exposing by selectively irradiating a
photosensitive resin composition with an actinic ray such as
ultraviolet ray, deep ultraviolet ray, excimer laser, x-ray, or
electron beams and developing the resin composition. In the
photolithography process, negative or positive-working
photosensitive resin compositions are used to form resist patterns.
With the recent trend of higher integration of semiconductor
devices, wiring and separation widths required in the manufacturing
process of the semiconductor device are becoming finer, and, in
order to keep up with this trend, exposure equipment employing a
short-wavelength light source such as g-line, i-line, or excimer
laser or phase shift masks are used in the exposure. However, with
the lithography technique employing the conventional exposure, it
is difficult to form resist patterns that are finer than the limit
provided by the wavelength. On the other hand, exposure equipment
for short-wavelength and equipment employing phase shift masks are
expensive. Therefore, methods to effectively make resist patterns
finer, which use conventionally known positive or negative-working
photosensitive resin compositions and conventionally known pattern
formation equipment without using the expensive equipment, have
been intensively investigated, and are disclosed, for example,
Japanese Patent Application Laid-Open Nos.5-241348, 6-250379,
10-73927, and 11-204399. The methods described in these
publications involve following steps, that is, employing a
conventional photosensitive composition, forming a pattern by
conventional methods, forming a coating layer on the resist pattern
formed, allowing an acid generated by heating and/or exposure to
light of the resist or present in the resist to diffuse into the
coating layer, crosslinking and curing the coating layer by the
action of the acid which has diffused into the coating layer,
removing the uncrosslinked coating layer to thicken the resist
pattern, and, as a result, the intervals between the resist
patterns are narrowed, and the separation size or hole aperture
size of the resist patterns are reduced to make resist patterns
finer and to effectively form resist patterns which are fine to a
degree below the resolution limit.
[0003] In the methods of forming fine patterns mentioned above, a
water-soluble photosensitive or non-photosensitive resin
composition which can be crosslinked by an acid is used as a
composition for forming a coating layer, and water or a mixed
solvent with water and an organic solvent is used for development
and removal of uncrosslinked coating layer. When water or a mixed
solvent with water and an organic solvent is used as a developer
and the coating layer is excessively insolubilized, there arise
such problems that bridging may be formed in the resist pattern
after development, development residues such as scum may be
generated, and components containing hydrophobic groups in the
water-soluble resin composition for coating layers may adhere as
insolubles to the surface of wafer during the development, which
result in pattern defect (see FIGS. 1 and 2). Although the bridging
and scum may be prevented in some cases by applying existing
approaches such as discharging a lot of developer comprising water
or water and an organic solvent or by increasing the number of
times of paddle development, it is difficult to control the
reproducibility and uniformity of pattern dimensions made finer.
Therefore, there has been required a improvement for higher yield,
easier operation, and more stable process.
[0004] When a water-soluble resin composition which crosslinks by
an acid to form an insolubilized layer is used as a material to
form a coating layer, the acid concentration generated in the base
resist pattern varies depending on the locations in cases where
several patterns with different pattern dimensions are present in
the base resist pattern, or patterns are configured sparsely and
densely, or a certain arrangement of the pattern is present. This
unevenness produces a variation in the crosslinking density in the
coating layer, which lowers the dimensional controllability of the
resultant pattern. Furthermore, when a solution such as a mixed
solution of water and an organic solvent which shows a high
solubility toward the coating layer is used as a developer, the
dissolution rate varies in the different pattern arrangements,
which results in reduced dimensional controllability of the
resultant pattern. Since attempts to substantially avoid this
problem requires slight changes in the design of the exposure
pattern such as the pattern dimension and pattern arrangement of
the base resist, this situation is in need of improvement in terms
of the cost and easiness of manufacturing semiconductor
devices.
[0005] Examples of the method of forming fine resist patterns
mentioned above include use of water or aqueous TMAH
(tetramethylammonium hydroxide) solution for development of a
coating layer comprising a water-soluble resin composition as
disclosed in Japanese Patent Application Laid-Open No.10-73927 and
development of a coating layer comprising a water-soluble resin
composition with a solution comprising water and an organic
solvent, which has a high solubility to the composition, and
rinsing the coating layer with a solution having a low solubility
to the composition such as water as disclosed in Japanese Patent
Application Laid-Open No.11-204399. Although the latter patent
application describes the solution with a high solubility contains
a surfactant, neither specific examples of the surfactant nor the
effect of the surfactant are described. These conventional methods
may result in development defect and pattern defect without enough
dimensional controllability of the resultant fine resist pattern.
Under the present circumstances, coating layers cannot be formed
independent on the dimension and arrangement of the base resist
pattern and without influencing the base resist pattern and the
shrunk resist pattern, and the dimensional controllability of the
resultant resist pattern cannot be significantly improved.
[0006] Furthermore, Japanese Patent Application Laid-Open
No.11-204399 describes that the developer contains a surfactant,
but there are problems in such a case that air bubbles are formed
when a developer is discharged onto a wafer in development, and all
of the generated air bubbles do not disappear in the developer,
which makes the development uneven and produces a pattern with low
dimensional controllability. Therefore, a low-frothing surfactant
or a surfactant which highly defoams even if it once froths up is
required as a surfactant for use in a developer.
[0007] It is an object of the present invention to provide an
surfactant aqueous solution for development of a coating layer
which is free from the above-mentioned problems and a method of
forming fine resist patterns which employs this surfactant aqueous
solution.
[0008] Accordingly, the object of the present invention is to
provide an surfactant aqueous solution for development of a coating
layer, which can prevent formation of bridging caused by excessive
crosslinking, generation of development residues such as scum, and
reattachment of insolubles, and which does not influence the base
resist pattern or the resist pattern made finer (or shrunk), and
which works independent of the dimension and pattern arrangement of
the base resist pattern, and which cannot cause uneven development
attributable to froths of the developer, and which can improve the
dimensional controllability of the pattern, in the method of
forming a pattern where a trench pattern and a hole pattern can be
effectively made finer to a degree below the resolution limit by
forming a coating layer on a resist pattern and thickening the
resist pattern, and a method of forming fine resist patterns which
employs this surfactant aqueous solution.
DISCLOSURE OF THE INVENTION
[0009] As a result of intensive investigation, the inventor has
found that, when an aqueous solution containing a surfactant with a
specific structure is used as a developer in the method of forming
a pattern where a resist pattern is made finer by forming a coating
layer on a resist pattern formed by the conventional method and
then thickening the resist pattern, generation of development
defect and pattern defect such as bridging and scum is suppressed
and the dimensional controllability in the miniaturization of
patterns is improved, thus having achieved the present invention
based on the finding.
[0010] Accordingly, the present inventions are surfactant aqueous
solution s for development of a coating layer and a method of
forming a pattern comprising the following constitutions.
[0011] (1) An surfactant aqueous solution for development of a
coating layer comprising a surfactant and water or a mixture of
water and an organic solvent, wherein the surfactant comprises at
least one selected from an N-acylsarcosinate, an
N-acyl-N-methylalaninate, an N-acyltaurinate, an
N-acyl-N-methyltaurinate, a fatty acid alkylol amide, and a fatty
acid alkylol amide polyoxyethylene adduct.
[0012] (2) The surfactant aqueous solution for development of a
coating layer according to above-mentioned (1), wherein the number
of carbon atoms of the acyl group of the surfactant is 10 to
14.
[0013] (3) The surfactant aqueous solution for development of a
coating layer according to above-mentioned (1) or (2), wherein the
surfactant is at least one selected from an N-lauroylsarcosinate,
an N-lauroyl-N-methylalaninate, an N-lauroyltaurinate, and an
N-lauroyl-N-methyltaurinate.
[0014] (4) The surfactant aqueous solution for development of a
coating layer according to above-mentioned (1), wherein the counter
ion of the N-acylsarcosinate, the N-acyl-N-methylalaninate, the
N-acyltaurinate, and the N-acyl-N-methyltaurinate is an organic
amine or an organic amine salt.
[0015] (5) The surfactant aqueous solution for development of a
coating layer according to above-mentioned (1) or (2), wherein the
number of carbon atoms of the fatty acid of the fatty acid alkylol
amide or the fatty acid alkylol amide polyoxyethylene adduct is 6
to 22, and the number of carbon atoms of the alkylol group thereof
is 1 to 3, and the number of repeating units of the polyoxyethylene
chain of the fatty acid alkylol amide polyoxyethylene adduct is 10
or less.
[0016] (6) The surfactant aqueous solution for development of a
coating layer according to any one of above-mentioned (1) to (5),
wherein the concentration of the surfactant is 0.01 to 10.0% by
weight.
[0017] (7) The surfactant aqueous solution for development of a
coating layer according to any one of above-mentioned (1) to (6),
wherein the organic solvent comprises at least one selected from a
saturated or unsaturated alcohol with 1 to 8 carbon atoms, a
saturated polyvalent alcohol with 2 or 3 hydroxyl groups, a
saturated or unsaturated alkyl amine with 1 to 3 carbon atoms, and
a saturated or unsaturated alkanol amine with 1 to 3 carbon
atoms.
[0018] (8) The surfactant aqueous solution for development of a
coating layer according to any one of above-mentioned (1) to (7),
wherein water and the organic solvent are mixed in a ratio of water
to the organic solvent of 80:20 to 99:1.
[0019] (9) A method of forming a pattern comprising forming a
coating layer on a resist pattern, thickening the resist pattern by
crosslinking of the coating layer, and removing the uncrosslinked
coating layer with a developer to effectively make the pattern
finer, wherein the surfactant aqueous solution for development of a
coating layer according to any one of above-mentioned (1) to (8) is
used as a developer.
[0020] The present invention will be described hereinafter.
[0021] In the surfactant aqueous solution of the present invention,
an N-acylsarcosinate, an N-acyl-N-methylalaninate, an
N-acyltaurinate, an N-acyl-N-methyltaurinate, a fatty acid alkylol
amide, or a fatty acid alkylol amide polyoxyethylene adduct is used
as a surfactant. The acyl group in the surfactant preferably has 10
to 14 carbon atoms.
[0022] Specific examples of the surfactant which can be preferably
used in the surfactant aqueous solution of the present invention
include N-acylsarcosinates such as, for example, coconut oil fatty
acid sarcosinate, lauroylsarcosinate, myristoylsarcosinate, and
oleoylsarcosinate; N-acyl-N-methylalaninates such as, for example,
coconut oil fatty acid methylalaninate, lauroylmethylalaninate,
myristoylmethylalaninate, and oleoylmethylalaninate;
N-acyltaurinates such as, for example, N-lauroyltaurinate,
N-myristoyltaurinate, and N-oleoyltaurinate;
N-acyl-N-methyltaurinates such as, for example,
N-lauroyl-N-methyltaurinate, N-myristoyl-N-methyltaurinate, and
N-oleoyl-N-methyltaurinate; fatty acid alkylol amides and fatty
acid alkylol amide polyoxyethylene adducts such as, for example,
coconut oil fatty acid monoethanol amide, coconut oil fatty acid
diethanol amide, lauric acid monoethanol amide, lauric acid
diethanol amide, myristic acid monoethanol amide, myristic acid
diethanol amide, stearic acid monoethanol amide, stearic acid
diethanol amide, palmitic acid monoethanol amide, palmitic acid
diethanol amide, oleic acid monoethanol amide, oleic acid diethanol
amide, palm kernel oil monoethanol amide, palm kernel oil fatty
acid diethanol amide, lauric acid monoisopropanol amide, myristic
acid monoisopropanol amide, stearic acid monoisopropanol amide,
palmitic acid monoisopropanol amide, oleic acid monoisopropanol
amide, palm kernel oil fatty acid monoisopropanol amide, and
polyoxyethylene adducts thereof.
[0023] Among these surfactants, an N-acylsarcosinate, an
N-acyl-N-methylalaninate, an N-acyltaurinate, or an
N-acyl-N-methyltaurinate with its acyl group being a lauroyl group
is preferable, and a fatty acid alkylol amide or a fatty acid
alkylol amide polyoxyethylene adduct with its acyl group of the
fatty acid being a lauroyl group is preferable, and specifically,
N-lauroylsarcosinate, N-lauroyl-N-methylalaninate,
N-lauroyltaurinate, or N-lauroyl-N-methyltaurinate, lauric acid
monoethanol amide, or lauric acid diethanol amide is more
preferable.
[0024] Among these surfactants, any counter ion can be used,
provided it is a basic ion, for an N-acylsarcosinate, an
N-acyl-N-methylalaninate, an N-acyltaurinate, or an
N-acyl-N-methyltaurinate, but an organic amine or an organic amine
salt is preferable. Specific examples of the organic amine used as
a counter ion of the surfactant in the present invention include,
for example, alkanol amines such as monoethanol amine, diethanol
amine, triethanol amine, N-methylethanol amine, or N-ethylethanol
amine, and alkyl amines such as monoethyl amine, diethyl amine, or
triethyl amine. Examples of the organic amine salt include, for
example, tetramethylammonium hydroxide and tetraethylammonium
hydroxide.
[0025] These surfactants may be used singly or in combination with
one or more of them, and may be blended in any amount provided it
forms a uniform aqueous solution. The surfactant is blended at 0.01
to 10.0% by weight in view of the effect, and more preferably 0.1
to 5.0% by weight based on the total amount of the surfactant
aqueous solution of the present invention.
[0026] The surfactant used in the present invention is preferably
freed of organic impurities, metal ions, chlorine ion and so on by
means of distillation, salting out, recrystallization, ion exchange
treatment, desalting by ultrafiltration, filtering treatment, and
various adsorption treatments. However, preservatives such as
paraben may be used in order to improve rot proof properties.
[0027] Although the solvent of the surfactant aqueous solution of
the present invention is desirably water, a water-soluble organic
solvent may be mixed when the solubility of the surfactant is low,
or the surfactant aqueous solution is highly frothy, or resists
spreading over a pattern. Although any water-soluble organic
solvent may be used, saturated or unsaturated alcohols with 1 to 8
carbon atoms such as methanol, ethanol, propanol, or isopropanol,
saturated polyvalent alcohols with 2 or 3 hydroxyl groups such as
ethylene glycol, diethylene glycol, or glycerol, saturated or
unsaturated alkyl amines with 1 to 3 carbon atoms such as
monomethyl amine, dimethyl amine, trimethyl amine, monoethyl amine,
ethanol amine, or diethanol amine, alkyl amine salts such as
tetramethylammonium salts, and mixture of two or more thereof are
used in view of the effect. The organic solvent may be blended at
any concentration provided it is miscible with water, but the
organic solvent is preferably blended at 1.0 to 20.0% by weight,
and more preferably 1.0 to 5.0% by weight based on the total amount
of the surfactant aqueous solution of the present invention.
[0028] No specific limitation is set on the quality of water to
dissolve the surfactant and the organic solvent in the present
invention, but water is preferably freed of organic impurities,
metal ions, and chlorine ion by means of distillation, ion exchange
treatment, filtering treatment, various adsorption treatments etc.
Furthermore, the surfactant aqueous solution of the present
invention is preferably subjected to a treatment to remove
impurities as described above, and is desirably free from solid
matter of quarter micron size or larger.
[0029] For the development of the coating layer with the surfactant
aqueous solution of the present invention, the same methods as the
conventionally known development methods of the resists can be
employed, and development equipment conventionally used for the
development of resists can be used. Generally, development is
conducted with a development nozzle such as a soft impact nozzle by
paddle development or shower development, and subsequently the
surfactant left on the surface and inside of the resist pattern is
rinsed away with pure water. A mixture of water and an alcohol such
as ethanol or isopropanol, an organic amine such as triethylamine,
or an organic amine salt such as tetramethylammonium salt may be
used instead of pure water for rinsing. Furthermore, the resist may
be baked to remove water in the pattern after the development
step.
[0030] Furthermore, in order to use the surfactant aqueous solution
of the present invention more effectively, it is desirable to
control the solution temperature, the discharging pressure and time
from the nozzle, and the humidity and temperature of the
development container in the appropriate range.
[0031] No specific limitation is set on the resin composition for
coating layer on which the surfactant aqueous solution for
development of a coating layer of the present invention works
effectively provided it is a resin composition for coating layer
which has been ever reported, and commercially available examples
thereof include AZ R200 (`AZ` is a registered trademark, and this
applies to the following part) manufactured by Clariant (Japan)
K.K. and it is easily obtainable.
BRIEF DESCRIPTION OF THE DRAWINGS
[0032] FIG. 1 shows a contact hole pattern observed under
microscope, on which development residues are present.
[0033] FIG. 2 shows a line and space pattern observed under
microscope, on which development residues are present.
BEST MODE FOR CARRYING OUT THE INVENTION
[0034] The present invention will be described in more detail with
reference to examples and comparative examples hereinafter, but
embodiments of the present invention are not limited to these
examples.
[0035] Preparation of Surfactant Aqueous Solution s
[0036] Components were mixed in the following ratio (weight ratio),
stirred thoroughly to dissolve, and the resultant solution was
filtered with a 0.1 .mu.m filter to prepare surfactant aqueous
solution s A and B.
1 [Surfactant aqueous solution A] N-lauroylsarcosine
triethanolamine 5.0 Water 95.0 [Surfactant aqueous solution B]
N-lauroyl-N-methylalanine triethanolamine 5.0 Water 95.0
[0037] Comparative Developer
[0038] As a comparative developer to compare with the
above-mentioned surfactant aqueous solution s A and B, AZ R2
Developer (an organic solvent aqueous solution which does not
contain a surfactant) commercially available from Clariant (Japan)
K.K. was used. As other comparative developers, AZ 600MIF and AZ
AQUATAR manufactured by Clariant (Japan) K. K. which are aqueous
solutions containing surfactants other than the surfactant used in
the present invention were used.
[0039] Formation of Line and Space Pattern and Contact Hole
Pattern
[0040] An HMDS-treated 6-inch silicon wafer was coated with a
positive-working photosensitive resin composition, AZ DX5400P
manufactured by Clariant (Japan) K.K., by using a spin coater
(MK-V) manufactured by Tokyo Electron Ltd. and pre-baked on a hot
plate at 90.degree. C. for 60 seconds to form a resist layer of
about 0.54 .mu.m in thickness. The wafer was then exposed through
line and space patterns with various space widths by using exposure
equipment having an exposure wavelength of KrF laser (248 nm)
(FPA-3000EX5 manufactured by Canon Inc., NA=0.63), subjected to
post-exposure baking (PEB) on a hot plate at 110.degree. C. for 90
seconds, and subjected to spray paddle development with an alkaline
developer (AZ 300MIF developer, an aqueous solution containing
2.38% by weight of tetramethylammonium hydroxide) manufactured by
Clariant (Japan) K.K. at 23.degree. C. for one minute to obtain a
positive resist pattern.
[0041] Formation of Contact Hole Pattern
[0042] An HMDS-treated 6-inch silicon wafer was coated with a
positive-working photosensitive resin composition, AZ DX3200SC
manufactured by Clariant (Japan) K.K., by using a spin coater
(MK-V) manufactured by Tokyo Electron Ltd. and pre-baked on a hot
plate at 80.degree. C. for 90 seconds to form a resist layer of
about 0.76 .mu.m in thickness. The wafer was then exposed through
hole patterns with various hole diameters by using exposure
equipment (FPA-3000EX5 manufactured by Canon Inc., NA=0.63) having
an exposure wavelength of KrF laser (248 nm), subjected to
post-exposure baking (PEB) on a hot plate at 110.degree. C. for 60
seconds, and subjected to spray paddle development with an alkaline
developer (AZ 300MIF developer, an aqueous solution containing
2.38% by weight of tetramethylammonium hydroxide) manufactured by
Clariant (Japan) K.K. at 23.degree. C. for one minute to obtain a
positive resist pattern.
EXAMPLES 1 AND 2, COMPARATIVE EXAMPLE 1
[0043] The line and space pattern and the contact hole pattern were
coated with AZ R200 manufactured by Clariant (Japan) K.K. by using
a spin coater (MK-V) manufactured by Tokyo Electron Ltd. and baked
on a hot plate at 85.degree. C. for 70 seconds to form a
water-soluble resin film of about 0.4 .mu.m in thickness. The
patterns were then subjected to mixing bake on a hot plate at
115.degree. C. for 70 seconds to promote the crosslinking reaction
of the water-soluble resin film, and then subjected to paddle
development with the above-mentioned surfactant aqueous solution A
or B, and AZ R2 Developer at 23.degree. C. for one minute to remove
the uncrosslinked layer to form a crosslinked, insolubilized layer
on the line and space pattern and the contact hole pattern. The
patterns were baked on a hot plate at 110.degree. C. for 70 seconds
to dry them. The resultant shrunk patterns were evaluated for
dimensional shrinkage and generation of development residues. The
results are shown in Table 1.
[0044] [Dimensional Shrinkage Evaluation]
[0045] The space width in the line and space pattern and the hole
diameter in the hole pattern were measured by using S-9200 Advanced
CD-measurement SEM manufactured by Hitachi Ltd., before and after
formation of the insolubilized layer, and the shrinkage rates were
calculated according to the following formula and used for the
evaluation of dimensional shrinkage.
Shrinkage rate (%)=[{(dimension before formation of insolubilized
layer)-(dimension after formation of insolubilized
layer)}/(dimension before formation of insolubilized
layer)].times.100
[0046] [Evaluation of Generation of Development Residues]
[0047] A hundred points on the whole surface of the silicon wafer
were observed by using S-9200 Advanced CD-measurement SEM
manufactured by Hitachi Ltd. before and after formation of the
insolubilized layer, and the number of the points where development
residues such as bridging and scum were present was counted and
used for the evaluation of generation of development residues.
[0048] Incidentally, examples of a contact hole pattern and line
and space pattern where development residues are present are shown
in FIGS. 1 and 2. In the above-mentioned evaluation of generation
of development residues, even a point where a slight residue was
found was counted as one point regardless of the degree of
generation.
2 TABLE 1 Examples or Kind of Pattern size Comparative surfactant
(.mu.m) Ratio of Numbers of development Kind of Examples aqueous
Before After shrinkage residues generated patterns No. solution s
shrinkage shrinkage (%) (points/100 points basis) Contact Example 1
A 0.219 0.137 37.4 0 hall Example 2 B 0.221 0.142 35.7 2 pattern
Comparative R2 Developer 0.219 0.151 31.1 48 Example 1 Line and
Example 1 A 0.221 0.126 43.0 1 Space Example 2 B 0.220 0.132 40.0 0
Pattern Comparative R2 Developer 0.220 0.142 35.5 100 Example 1
[0049] Table 1 above shows the surfactant aqueous solution for
development of a coating layer of the present invention can prevent
the generation of pattern defect and has superior dimensional
shrinkage controllability.
EXAMPLES 3 AND 4, COMPARATIVE EXAMPLES 2, 3, AND 4
(Evaluation of Frothing Properties 1)
[0050] The line and space pattern and contact hole pattern obtained
in the above-mentioned manner were coated with an water-soluble
resin by using a spin coater (MK-V) manufactured by Tokyo Electron
Ltd. and baked on a hot plate at 85.degree. C. for 70 seconds to
form a water-soluble resin film of about 0.4 .mu.m in thickness.
The patterns were then subjected to mixing baking on a hot plate at
115.degree. C. for 70 seconds to promote the crosslinking reaction
of the water-soluble resin film, and the above-mentioned surfactant
aqueous solution A or B, R2 Developer, AZ 600MIF, and AZ AQUATAR
were spread on the patterns at 23.degree. C., and air bubbles
formed in the step were inspected by eyes. The results are shown in
Table 2, "Frothing properties on wafer" column.
[0051] The evaluation of frothing property 1 was made according to
the following criteria.
[0052] The frothing properties were rated as "high" when fine air
bubbles were seen all over the wafer, "medium" when fine air
bubbles were present at the edge of the water (when the air bubbles
covered less than 10% of the whole surface area of the wafer), and
"low" when few fine air bubbles were present.
EXAMPLES 5 AND 6, COMPARATIVE EXAMPLES 5, 6, AND 7
(Evaluation of Frothing Properties 2)
[0053] The frothing properties of the surfactant aqueous solution s
were evaluated by a different method from the above-mentioned
evaluation of frothing properties 1.
[0054] Approximately 12 g of the above-mentioned surfactant aqueous
solution A or B, R2 Developer, AZ 600MIF, and AZ AQUATQR were
respectively placed into a 50 ml transparent glass container, and
the container was agitated by using a touch mixer for 30 seconds,
and the air bubbles were inspected by eyes to measure the time
taken till all the air bubbles disappeared. The results are shown
in Table 2, "Deforming properties after shaking" column.
3TABLE 2 Kind of surfactant aqueous Frothing properties on
Deforming properties after solution s the wafer shaking (hour) A
Low (Example 3) 0.5 (example 5) B Low (Example 4) 1.0 (example 6)
R2 Developer Nil 0 (Comparative Example 2) (Comparative Example 5)
AZ 600MIF Low 0.5 (Comparative Example 3) (Comparative Example 6)
AZ High 24.0 AQUATAR (Comparative Example 4) (Comparative Example
7)
[0055] Table 2 shows the surfactant aqueous solution of the present
invention shows frothing properties and deforming properties, which
are equal to or lower than the conventional developers.
[0056] Effect of the Invention
[0057] As described above in detail, use of the surfactant aqueous
solution of the present invention as a developer can prevent
formation of development residues and pattern defects, and can form
a coating layer with excellent dimensional controllability in the
step of pattern miniaturization, in the pattern formation method
where a trench pattern and a hole pattern can be effectively made
finer by forming a coating layer on a resist pattern formed by the
conventional method and thickening the resist pattern. Furthermore,
fine processing can be effected with a high yield without the need
of larger facilities in the recent manufacture of highly integrated
semiconductor elements.
* * * * *