U.S. patent application number 10/076018 was filed with the patent office on 2003-01-30 for hydrolytically degradable polymers and hydrogels made therefrom.
This patent application is currently assigned to Shearwater Corporation. Invention is credited to Bentley, Michael David, Harris, J. Milton, Shen, Xiaoming, Zhao, Xuan.
Application Number | 20030023023 10/076018 |
Document ID | / |
Family ID | 23824266 |
Filed Date | 2003-01-30 |
United States Patent
Application |
20030023023 |
Kind Code |
A1 |
Harris, J. Milton ; et
al. |
January 30, 2003 |
Hydrolytically degradable polymers and hydrogels made therefrom
Abstract
A water soluble polymer is provided having two or more oligomers
linked to each other by hydrolytically degradable carbonate
linkages. The polymer can be hydrolytically degraded into oligomers
(e.g., oligomers of ethylene oxide) under physiological conditions.
The polymer can be conjugated to biologically active agents such as
proteins or peptides to impart improved water solubility, reduced
immunogenicity, reduced rate of renal clearance, and increased
stability. The polymer is useful in making hydrolytically
degradable hydrogels which can be used in drug delivery and related
biomedical applications. On example of the polymer is a poly(ether
carbonate) of the formula X--O--[(--CH.sub.2CH.sub.2--O--).sub-
.n--CO.sub.2--].sub.n(CH.sub.2CH.sub.2)).sub.n-y where X and Y are
independently H, alkyl, alkenyl, aryl, or a reactive moiety, and at
least one of X and Y is a reactive moiety.
Inventors: |
Harris, J. Milton;
(Huntsville, AL) ; Bentley, Michael David;
(Huntsville, AL) ; Zhao, Xuan; (Huntsville,
AL) ; Shen, Xiaoming; (Madison, AL) |
Correspondence
Address: |
ALSTON & BIRD LLP
BANK OF AMERICA PLAZA
101 SOUTH TRYON STREET, SUITE 4000
CHARLOTTE
NC
28280-4000
US
|
Assignee: |
Shearwater Corporation
|
Family ID: |
23824266 |
Appl. No.: |
10/076018 |
Filed: |
February 14, 2002 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10076018 |
Feb 14, 2002 |
|
|
|
09459312 |
Dec 10, 1999 |
|
|
|
6348558 |
|
|
|
|
Current U.S.
Class: |
528/196 ;
528/198 |
Current CPC
Class: |
C08G 64/38 20130101;
C08G 64/183 20130101; C08G 64/0208 20130101 |
Class at
Publication: |
528/196 ;
528/198 |
International
Class: |
C08G 064/00 |
Claims
What is claimed is:
1. A hydrolytically degradable polymer comprising two or more
oligomers linked to each other by hydrolytically degradable
carbonate linkages, wherein said oligomers comprise two or more
alkylene oxide monomers.
2. The polymer of claim 1, wherein said oligomers are made of
ethylene oxide monomers.
3. The polymer of claim 1 wherein said oligomers are made of
monomers selected from the group consisting of ethylene oxide,
propylene oxide, and butylene oxide.
4. The polymer of claim 1 further comprising at least one reactive
terminal moiety.
5. The polymer of claim 4, wherein said reactive terminal moiety is
selected from the group consisting of N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, tresyl, 1-imidazolylcarbonyl,
vinylsulfone, acryloyl, iodoacetamide, N-succinimidylpropionate,
N-succinimidylbutyrate, N-succinimidylacetate, and
o-pyridyldithiyl.
6. The polymer of claim 1, wherein each of said oligomers is
composed of from about 10 to about 50 monomers.
7. A polymer having the formula of:
X--O--[(--CH.sub.2CH.sub.2--O--).sub.n-
--CO.sub.2].sub.m--(CH.sub.2CH.sub.2O).sub.n--Y where n is an
integer of from about 2 to about 2,000, m is an integer of from
about 2 to about 200, and where X and Y each independently is H,
alkyl, alkenyl, aryl, or a reactive moiety, and X and Y can be same
or different.
8. The polymer of claim 7, wherein X and Y are independently
selected from the group consisting of H, alkyl, alkenyl, aryl,
acryloyl, methacryloyl, tresyl, N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, 1-imidazolylcarbonyl,
vinylsulfone, iodoacetamide, and o-pyridyldithiyl.
9. The polymer of claim 7, wherein X and Y are 1-benzotriazolyloxy
carbonyl.
10. The polymer of claim 7, wherein X and Y are acryloyl or
methacryloyl.
11. The polymer of claim 7, wherein X and Y are N-succinimidyl
carbonyl.
12. The polymer of claim 7, wherein n is an integer of from about 5
to about 500.
13. The polymer of claim 7, wherein n is an integer of from about
10 to about 50.
14. The polymer of claim 7, wherein m is an integer of from about
10 to about 50.
15. A method for preparing a hydrolytically degradable polymer
comprising: providing an oligomer having a hydroxyl group at one
terminus and, at another terminus, a functional group of
--O--CO.sub.2-Z which is capable of reacting with a hydroxyl group
to form a carbonate linkage, wherein Z is a reactive leaving group,
and wherein said oligomer comprises two or more alkylene oxide
monomers; and polymerizing said oligomer at conditions sufficient
to form said hydrolytically degradable polymer, wherein the polymer
has two or more said oligomers linked to each other by
hydrolytically degradable carbonate linkages.
16. The method of claim 15, further comprising activating said
hydrolytically degradable polymer to form at least one reactive
terminal moiety on said polymer.
17. The method of claim 15, further comprising purifying said
hydrolytically degradable polymer.
18. The method of claim 15, wherein said oligomer consists of
ethylene oxide monomers.
19. The method of claim 15, wherein said polymer has the formula
of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 2 to about 2000,
m is an integer of from about 2 to about 100, and wherein said
oligomer has the formula of:
HO--(--CH.sub.2CH.sub.2--O--).sub.n--O--CO.sub.2-Z wherein n as
defined above, Z is a reactive leaving group.
20. The method of claim 19, wherein Z is N-succinimidyl,
1-benzotriazolyl, or p-nitrophenyl.
21. The method of claim 19, wherein the polymerizing step is
conducted in a solvent in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
22. The method of claim 21, wherein said solvent is selected from
the group consisting of acetonitrile, dimethylformamide,
dimethylsulfoxide, benzene, toluene, xylenes, chloroform, and
methylene chloride.
23. The method of claim 21, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
24. The method of claim 19, wherein the polymerizing step is
conducted in melt in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
25. The method of claim 24, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
26. The method of claim 19, wherein n is an integer of from about
10 to about 50.
27. The method of claim 19, wherein m is an integer of from about 5
to about 100.
28. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 5 to about 100, comprising:
polymerizing an ethylene oxide oligomer having a formula of
HO--(--CH.sub.2CH.sub.2--O--)- .sub.n--O--CO.sub.2-1-benzotriazolyl
in the presence of dimethylaminopyridine and at a temperature of
from about 45.degree. C. to about 100.degree. C., either in melt or
in anhydrous acetonitrile as solvent, thereby forming said
polymer.
29. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 5 to about 100, comprising:
polymerizing an ethylene oxide oligomer having a formula of
HO--(--CH.sub.2CH.sub.2--O--)- .sub.n--O--CO.sub.2-N-succinimidyl
in the presence of dimethylaminopyridine and at a temperature of
from about 45.degree. C. to about 100.degree. C., either in melt or
in anhydrous acetonitrile as solvent, thereby forming said
polymer.
30. A method for preparing a hydrolytically degradable polymer
comprising: providing a first oligomer having a first functional
group of --O--CO.sub.2--W at one terminus and, at another terminus,
a second functional group of --O--CO.sub.2-Z, wherein each of said
functional groups is capable of reacting with a hydroxyl group to
form a carbonate linkage, and wherein Z and W are reactive leaving
groups and can be same or different; providing a second oligomer
having two hydroxyl terminal groups; providing a polymerization
reaction mixture comprising said first and second oligomers; and
polymerizing said first and second oligomers at conditions
sufficient to form said hydrolytically degradable polymer, wherein
said polymer has two or more of said oligomers linked to each other
by a hydrolytically degradable carbonate linkage, and wherein each
of said oligomers comprises two or more alkylene oxide
monomers.
31. The method of claim 30, further comprising activating said
hydrolytically degradable polymer to form at least one reactive
terminal moiety on said polymer.
32. The method of claim 30, further comprising purifying said
hydrolytically degradable polymer.
33. The method of claim 30, wherein said first and second oligomers
consist of ethylene oxide monomers.
34. The method of claim 30, wherein the first oligomer has a
functional group of --O--CO.sub.2-Z at two termini, and the step of
providing the first oligomer comprises: providing a precursor of
the first oligomer, which has two terminal hydroxyl groups;
providing an activating molecule having the formula of
Z-O--CO.sub.2-Z; and reacting said precursor with said activating
molecule to form said first oligomer.
35. The method of claim 30, wherein said polymer has the formula
of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H said first oligomer has the formula of
HO--(--CH.sub.2CH.sub.2--O--).sub.n--OH said second oligomer has
the formula of
W--O.sub.2C--O--(--CH.sub.2CH.sub.2--O--).sub.n--O--CO.sub.2-Z
where n is an integer of from about 2 to about 2000, m is an
integer of from about 2 to about 100, W and Z are reactive leaving
groups and can be same or different.
36. The method of claim 35, wherein W and Z are N-succinimidyl,
1-benzotriazolyl, or p-nitrophenyl.
37. The method of claim 35, wherein the polymerizing step is
conducted in a solvent in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
38. The method of claim 37, wherein said solvent is selected from
the group consisting of acetonitrile, dimethylformamide,
dimethylsulfoxide, benzene, toluene, xylenes, chloroform, and
methylene chloride.
39. The method of claim 37, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
40. The method of claim 35, wherein wherein the polymerizing step
is conducted in melt in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
41. The method of claim 40, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
42. The method of claim 35, wherein n is from about 10 to about
50.
43. The method of claim 35, wherein m is from about 5 to about
100.
44. The method of claim 35, wherein W and Z are same, and wherein
said step of providing said second oligomer comprises: providing an
activating molecule having the formula of Z-O--CO.sub.2-Z;
providing a precursor of said second oligomer having two terminal
hydroxyl groups; and reacting Z-O--CO.sub.2-Z and said precursor to
form said second oligomer.
45. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 5 to about 100, comprising: providing
a first ethylene oxide oligomer having the formula of
HO--(--CH.sub.2CH.sub.2--O-- -).sub.n--OH; providing a second
ethylene oxide oligomer having a formula of
1-benzotriazolyl-O.sub.2C--O--(--CH.sub.2CH.sub.2--O--).sub.n--O--CO.s-
ub.2-1-benzotriazolyl; and co-polymerizing said first and second
ethylene oxide oligomer in the presence of dimethylaminopyridine
and at a temperature of from about 45.degree. C. to about
100.degree. C., either in melt or in anhydrous acetonitrile as
solvent, thereby forming said polymer.
46. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 5 to about 100, comprising: providing
a first ethylene oxide oligomer having the formula of
HO--(--CH.sub.2CH.sub.2--O-- -).sub.n--OH; providing a second
ethylene oxide oligomer having a formula of
N-succinimidyl-O.sub.2C--O--(--CH.sub.2CH.sub.2--O--).sub.n--O--CO.sub-
.2--N-succinimidyl; and co-polymerizing said first and second
ethylene oxide oligomer in the presence of dimethylaminopyridine
and at a temperature of from about 45.degree. C. to about
100.degree. C., either in melt or in anhydrous acetonitrile as
solvent, thereby forming said polymer.
47. A method for preparing a hydrolytically degradable polymer
comprising: providing an alkylene oxide oligomer having two
hydroxyl terminal groups; providing an activating molecule having
the formula of Z-O--CO.sub.2-Z, wherein Z is a reactive leaving
group; and co-polymerizing said oligomer and said activating
molecule at conditions sufficient to form said hydrolytically
degradable polymer, wherein said polymer comprises two or more of
said oligomer linked to each other by hydrolytically degradable
carbonate linkages.
48. The method of claim 47, wherein said oligomer is an ethylene
oxide oligomer.
49. The method claim 47, wherein said polymer has the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H, said oligomer has the formula of
HO--(--CH.sub.2CH.sub.2--O-- -).sub.n--OH, where n is an integer of
from about 2 to about 2000, m is an integer of from about 2 to
about 200.
50. The method of claim 49, wherein Z is N-succinimidyl,
1-benzotriazolyl, or p-nitrophenyl.
51. The method of claim 49, wherein the co-polymerizing step is
conducted in a solvent in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
52. The method of claim 51, wherein said solvent is selected from
the group consisting of acetonitrile, dimethylformamide,
dimethylsulfoxide, benzene, toluene, xylenes, chloroform, and
methylene chloride.
53. The method of claim 51, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
54. The method of claim 49, wherein said polymerizing step is
conducted in melt in the presence of an organic base, and at a
temperature of from about 37.degree. C. to about 100.degree. C.
55. The method of claim 54, wherein said organic base is selected
from the group consisting of triethylamine, pyridine, quinoline,
and 4,4-dimethylaminopyridine.
56. The method of claim 49, wherein n is from about 10 to about
50.
57. The method of claim 49, wherein m is from about 5 to about
100.
58. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 5 to about 100, comprising
co-polymerizing disuccinimidylcarbonate and
HO--(--CH.sub.2CH.sub.2--O--).sub.n--OH, in the presence of
dimethylaminopyridine and at a temperature of from about 45.degree.
C. to about 100.degree. C., either in melt or in anhydrous
acetonitrile as solvent, thereby forming said polymer.
59. A method for preparing a polymer having the formula of:
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H wherein n is an integer of from about 10 to about 50,
m is an integer of from about 2 to about 100, comprising
co-polymerizing bis(l-benzotriazolyl carbonate) and
HO--(--CH.sub.2CH.sub.2--O--).sub.n--- OH, in the presence of
dimethylaminopyridine and at a temperature of from about 45.degree.
C. to about 100.degree. C., either in melt or in anhydrous
acetonitrile as solvent, thereby forming said polymer.
60. A conjugate comprising a biologically active agent covalently
linked to a hydrolytically degradable polymer, said polymer
comprising two or more alkylene oxide oligomers linked to each
other by hydrolytically degradable carbonate linkages.
61. The conjugate of claim 60, wherein said biologically active
agent is a protein or peptide.
62. The conjugate of claim 60, wherein said biologically active
agent is covalently linked to said hydrolytically degradable
polymer by a hydrolytically degradable linkage.
63. The conjugate of claim 60, wherein said oligomers are ethylene
oxide oligomers.
64. A conjugate comprising of a biologically active agent
covalently linked to a hydrolytically degradable polymer having the
formula of:
X--O--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.su-
b.2O).sub.n--Y where n is an integer of from about 2 to about 2000,
m is an integer of from about 2 to about 100, X and Y each
independently is H, alkyl, alkenyl, aryl, or a reactive moiety
capable of reacting with an active moiety on said biologically
active agent, X and Y can be same or different, and where at least
one of X and Y is said reactive moiety.
65. The conjugate of claim 64, wherein X and Y are independently
selected from the group consisting of H, alkyl, alkenyl, aryl,
acryloyl, tresyl, N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, 1-imidazolylcarbonyl,
vinylsulfone, iodoacetamide, and o-pyridyldithiyl.
66. The conjugate of claim 64, wherein at least one of X and Y is
N-succinimidyloxycarbonyl, 1-benzotriazolyloxycarbonyl,
p-nitrophenyloxycarbonyl.
67. The conjugate of claim 64, wherein n is an integer of from
about 5 to about 500.
68. The conjugate of claim 64, wherein n is an integer of from
about 10 to about 50.
69. The conjugate of claim 64, wherein m is an integer of from
about 5 to about 100.
70. A method for preparing a conjugate having a biologically active
agent covalently linked to a hydrolytically degradable polymer,
said polymer comprising two or more alkylene oxide oligomers linked
to each other by hydrolytically degradable carbonate linkages, said
method comprising the steps of: providing said hydrolytically
degradable polymer; activating said hydrolytically degradable
polymer to form a reactive terminal moiety in said polymer;
providing a biologically active agent having an active moiety; and
reacting said reactive terminal moiety in said polymer with said
active moiety of said biologically active agent, thereby forming a
covalent linkage between said biologically active agent and said
polymer.
71. The method of claim 70, wherein said reactive terminal moiety
is selected from the group consisting of tresyl,
N-succinimidyloxycarbonyl, 1-benzotriazolyloxycarbonyl,
p-nitrophenyloxycarbonyl, N-maleimidyl, aldehydes, acetals,
1-imidazolylcarbonyl, vinylsulfone, iodoacetamide, and
o-pyridyldithiyl.
72. The method of claim 70, wherein said active moiety of said
biologically active agent is an amine or thiol group.
73. The method of claim 70, wherein the said alkylene oxide
oligomers are made of ethylene oxide monomers.
74. The method of claim 70, wherein the polymer has the formula of
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.-
2O).sub.n--H where n is an integer of from about 5 to about 500,
and m is an integer of from about 5 to about 100.
75. The method of claim 74, wherein n is an integer of from about
10 to about 50.
76. A method for delivering a biologically active agent into the
body of a mammal, comprising administering the conjugate of claim
60 into said mammal.
77. A method for delivering a biologically active agent into the
body of a mammal, comprising administering the conjugate of claim
64 into said mammal.
78. A hydrolytically degradable hydrogel comprising a backbone
bonded to a crosslinking agent, wherein said crosslinking agent is
a hydrolytically degradable polymer having at least two reactive
terminal moieties, said polymer comprising two or more alkylene
oxide oligomers linked to each other by hydrolytically degradable
carb
79. The hydrolytically degradable hydrogel of claim 78, wherein the
alkylene oxide oligomers are made of ethylene oxide monomers.
80. The hydrolytically degradable hydrogel of claim 78, wherein
said at least two reactive terminal moieties a re selected from the
group consisting of N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, tresyls, 1-imidazolylcarbonyl,
vinylsulfone, acryloyl, vinyl, iodoacetamide, and
o-pyridyldithiyl.
81. The hydrolytically degradable hydrogel of claim 78, wherein
said backbone is a biocompatible molecule having at least two
active groups available to react with said terminal reactive
moieties.
82. The hydrolytically degradable hydrogel of claim 78, wherein
said backbone is selected from the group consisting of proteins,
polyamines, polyols, amino carbohydrates, polythiols,
polycarboxylic acids, and poly(ethylene glycol) amines.
83. The hydrolytically degradable hydrogel of claim 78, wherein
said backbone is chitosan.
84. The hydrolytically degradable hydrogel of claim 78, wherein
said backbone and said crosslinking agent have the same chemical
formula having two terminal vinyl groups or terminal acryloyl or
methacryloyl groups.
85. The hydrolytically degradable hydrogel of claim 78, wherein
said crosslinking agent is a hydrolytically degradable polymer
having the formula of:
X--O--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(C-
H.sub.2CH.sub.2O).sub.n--Y where n is an integer of from about 2 to
about 2000, m is an integer of from about 2 to about 100, and where
X and Y each independently is a reactive moiety, and X and Y can be
same or different.
86. The hydrolytically degradable hydrogel of claim 85, wherein X
and Y are independently selected from the group consisting of
acryloyl, tresyl, N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, 1-imidazolylcarbonyl,
vinylsulfone, iodoacetamide, and o-pyridyldithiyl.
87. The hydrolytically degradable hydrogel of claim 85, wherein X
and Y are 1-benzotriazolyl carbonyl.
88. The hydrolytically degradable hydrogel of claim 85, wherein the
backbone has the same chemical formula as the crosslinking agent,
and wherein X and Y are acrylate or methacrylate.
89. The hydrolytically degradable hydrogel of claim 85, wherein X
and Y are N-succinimidyl carbonyl.
90. The hydrolytically degradable hydrogel of claim 85, wherein n
is an integer of from about 5 to about 500.
91. The hydrolytically degradable hydrogel of claim 85, wherein n
is an integer of from about 10 to about 50.
92. The hydrolytically degradable hydrogel of claim 85, wherein m
is an integer of from about 5 to about 100.
93. A hydrolytically degradable hydrogel comprising chitosan bonded
to a hydrolytically degradable polymer having the formula of:
NS--O.sub.2C--O--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH-
.sub.2CH.sub.2O).sub.n--CO.sub.2--NS where n is an integer of from
about 10 to about 50, m is an integer of from about 5 to about 100,
and where NS is N-succinimidyl.
94. A delivery system for delivering a biologically active agent
comprising the biologically active agent carried by a
hydrolytically degradable hydrogel of claim 78.
95. The delivery system of claim 94, wherein said biologically
active agent is covalently linked to the hydrogel.
96. A delivery system for delivering a biologically active agent
comprising the biologically active agent carried by a
hydrolytically degradable hydrogel of claim 85.
Description
FIELD OF THE INVENTION
[0001] This invention generally relates to water soluble,
hydrolytically degradable, and nonpeptidic polymers, and
particularly to polymers and gels therefrom that are suitable for
medical devices, drug enhancement and in vivo delivery of
biologically active agents.
BACKGROUND OF THE INVENTION
[0002] Conjugation of agents having a known or potential
therapeutic benefit to water soluble, non-immunogenic polymers can
impart to the agent desirable characteristics including, among
others, improved solubility, greater stability, and reduced
immunogenicity. It has become increasingly important in the
pharmaceutical industry to develop conjugates having these
characteristics so as to increase the number of options for
therapeutic benefit.
[0003] An example of a polymer that can be used to develop
conjugates with therapeutic agents is poly(ethylene glycol)
("PEG"). Therapeutic agents conjugated to PEG are sometimes said to
be "PEGylated." Several PEGylated therapeutics have been developed
that exhibit enhanced water solubility, longer circulation
lifetimes, and lower immunogenicity as compared to the unconjugated
therapeutic agent. Because of the rapid motion and heavy hydration
of the polymer, PEGs usually are of much higher apparent molecular
weight than the therapeutics to which they are attached. Thus, they
tend to mask the therapeutic agent from the immune system and to
preclude excretion through kidneys.
[0004] The term PEG is commonly used to describe any of a series of
polymers having the general formula
HO--(CH.sub.2CH.sub.2--O).sub.n--H, where "n" represents the number
of ethylene oxide monomers in the polymer. However, the parent
polymer is generally unsuitable for attachment to a therapeutic
agent. Hydroxyl groups are relatively unreactive toward groups
commonly present on therapeutic agents and thus PEG normally has to
be "activated" by converting at least one end hydroxyl group into a
more reactive form. It is also usually important to activate the
PEG polymer with a terminal group that is selective in its
reactions. For example, several PEG derivatives have been developed
that are more likely to react with amine groups. Others have been
developed that preferentially react with thiol groups.
[0005] Successful PEG derivatives may have to meet a number of
requirements, depending on the specific application. For
conjugation to proteins, the PEG derivative should usually have a
desirable and suitably selective reactivity at physiologic
conditions of temperature, pressure, and pH to preserve the
activity of the unconjugated protein. In some circumstances, it is
desirable to cleave the PEG polymer from the therapeutic agent at
some point after the agent is delivered in vivo.
[0006] Some PEG derivatives have been used in combination with
other polymers to prepare insoluble gels in which drugs can be
entrapped or chemically bound. For example, Sawhney et al.,
Macromolecules, 26:581 (1993) describes the preparation of block
copolymers of PEG with polyglycolide or polylactide blocks at both
ends of the PEG chain. The copolymers are then activated by
terminal substitution with acrylate groups, as shown below.
CH.sub.2.dbd.CH--CO--(O--CH.sub.2--CO).sub.n--O-PEG-O--(CO--CH.sub.2--O).s-
ub.n--CO--CH.dbd.CH.sub.2
[0007] In the above formula, the glycolide blocks are the
--O--CH.sub.2--CO-- units. The addition of a methyl group to the
methylene gives a lactide block; n can be multiples of 2. Vinyl
polymerization of the acrylate groups produces an insoluble,
crosslinked gel with a polyethylene backbone.
[0008] The polylactide or polyglycolide segments of the polymer
backbone shown above, which are ester groups, are susceptible to
slow hydrolytic breakdown, with the result that the crosslinked gel
undergoes slow degradation and dissolution. The hydrogel degrades
in vivo and can result in non-PEG components being released into
the blood stream, which can be undesirable.
[0009] It is desirable to develop improved polymers providing
additional choices for use in drug delivery and other
applications.
SUMMARY OF THE INVENTION
[0010] This invention provides a water soluble, nonpeptidic polymer
having two or more oligomers linked together by hydrolytically
degradable carbonate linkages. The polymer can be hydrolytically
degraded into small oligomers in an aqueous environment, including
in vivo conditions. The polymer is easy to prepare and the
molecular weight of the oligomers resulting from polymer
degradation can be easily controlled, which can be desirable for
some applications. The polymer can be conjugated to a biologically
active agent such as a protein or peptide. The polymer can impart
desirable characteristics to the conjugates of improved water
solubility and reduced immunogenicity. The polymer is useful for
preparing insoluble cross linked structures, including hydrogels,
that are hydrolytically degradable into soluble polymers of
predetermined molecular weight.
[0011] The oligomers are alkylene oxide oligomers. Typically, the
oligomers are ethylene oxide oligomers, and the polymer is a
poly(ether carbonate) having the formula of:
HO--[(--CH.sub.2CH.sub.2--O).sub.n--CO.sub.2].sub.m--(--CH.sub.2CH.sub.2---
O).sub.nH
[0012] where n is from about 1 to 2,000, normally from 2 to 2,000,
and m is from about 2 to 200. Since carbonate linkages are
hydrolytically degradable under mild conditions, the polymer will
hydrolyze to produce oligomer fragments of much lower molecular
weight than the starting polymer:
HO--[(--CH.sub.2CH.sub.2--O).sub.n--CO.sub.2].sub.m--(--CH.sub.2CH.sub.2---
O).sub.nH+(m+1)H.sub.2O.fwdarw.(m+1)HO--(--CH.sub.2CH.sub.2--O--).sub.n--H-
+mCO.sub.2
[0013] In addition to providing many of the desirable features of
other polymers, including poly(ethylene glycol) as described above,
this new polymer can degrade in the body and thus facilitates
removal of the polymer from the body. The degradation products are
themselves normally nontoxic small PEGs that typically are rapidly
cleared from the body.
[0014] The polymer can be prepared in a number of ways. In one
embodiment of this invention, the poly(ether carbonate) is prepared
by polymerizing an activated oligomer having the formula of:
HO--(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2-Z
[0015] where n can be from about 2 to 2000 and Z is a reactive
leaving group such as N-succinimidyl, 1-benzotriazolyl, or
p-nitrophenyl.
[0016] The polymer can be prepared by polymerizing ethylene oxide
oligomers of the formula:
HO--(--CH.sub.2CH.sub.2--O--).sub.n--H
[0017] where n can be from about 2 to 2000 with an activating
molecule of Z-O--CO.sub.2-Z, where Z is as described.
[0018] Alternatively, the ethylene oxide oligomer
HO--(--CH.sub.2CH.sub.2--O--).sub.n--H
[0019] can be polymerized with a bifunctional ethylene oxide
oligomer:
Z-OCO.sub.2--(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2-Z
[0020] where n and Z are as described above, to form the poly(ether
carbonate).
[0021] The polymerization reactions may be conducted either in an
organic solvent or in a melt, in the presence of an organic base.
Examples of suitable solvents include acetonitrile, THF,
dimethylformamide, dimethylsulfoxide, benzene, toluene, the
xylenes, chloroform, and methylene chloride. Examples of suitable
organic bases include triethylamine, pyridine, quinoline,
4,4-dimethylaminopyridine and triethylamine. The polymerization
reactions can be conducted at a temperature of from about
37.degree. C. to 100.degree. C., typically from about 45.degree. C.
to 100.degree. C., and advantageously from about 70.degree. C. to
90.degree. C.
[0022] The polymer of this invention can be modified at one termius
with alkyl or aryl groups to make one end of the polymer inert. The
polymer can be activated at one or more of its termini to form a
terminal reactive moiety. Thus, a modified or activated poly(ether
carbonate) of this invention can be represented as:
X--O--[(CH.sub.2CH.sub.2--O).sub.n--CO.sub.2].sub.m--(CH.sub.2CH.sub.2--O)-
.sub.n--Y
[0023] where m and n are as defined above, and where X and Y can
independently be H, alkyl, alkenyl, aryl, and reactive terminal
moieties, including N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl, or others.
Alternatively, X and Y can include linker groups terminating in
active groups such as aldehyde N-maleimidyl or
--S--S-ortho-pyridyl. A wide variety of activating groups and
linkers can be used.
[0024] The activated polymer of this invention can be reacted with
an active group on a biologically active agent, such as a protein
or peptide, to form a conjugate. For example, N-succinimidyloxy,
1-benzotriazolyloxy, and p-nitrophenyloxy are leaving groups
suitable for the formation of a carbamate linkage between the
polymer and a biologically active agent having an amino group. Thus
proteins, peptides, amino drugs, or amino carbohydrates can be
linked to such activated polymers. For example, when X is H, and Y
is N-succinimidyloxycarbonyl, a conjugate can be formed of the
following formula:
HO--[(CH.sub.2CH.sub.2--O).sub.n--CO.sub.2].sub.m--(CH.sub.2CH.sub.2--O).s-
ub.n--CONH-Protein
[0025] When a protein to be conjugated has an accessible thiol
group, the polymer of this invention can be activated to contain a
terminal reactive moiety that is reactive with thiol, including,
for example, iodoacetamide, vinylsulfone, maleimide, or
S--S-ortho-pyridyl, which moiety is then reacted with the thiol
group to form a thiol site-specific conjugate of the protein.
[0026] When the polymer of this invention is activated at two
termini, it can be used as a crosslinking agent to crosslink a
multifunctional molecule to form a hydrolytically degradable
hydrogel. Examples of multifunctional molecules suitable as
"backbones" in formation of hydrogels include proteins such as
collagen, aminocarbohydrates such as chitosan, polyamines such as
polylysine and poly(vinylamine), and multi-armed or branched
poly(ethylene glycol) amines. The hydrogels of this invention are
useful in many biomedical applications such as drug delivery,
surgical adhesion prevention, wound and scar healing, bioadhesives
and surgical implants.
[0027] In another embodiment, the polymer of this invention can be
activated by attachment of terminal vinyl groups. This activated
polymer can be self-polymerized in the presence of a conventional
vinyl polymerization catalyst to form a hydrolytically degradable
hydrogel.
[0028] Thus, this invention provides a versatile polymer that is
especially suited for conjugating to a biologically active agent
and for forming a hydrogel. The polymer is easy to prepare and can
be synthesized in large quantities. The polymer can be formed in a
single reaction with multiple degradable carbonate linkages in the
backbone. The conjugate and hydrogel of this invention can be
degraded under physiological conditions. The degradation generates
oligomers of predetermined molecular weight that can be easily
cleared from the body.
[0029] The foregoing and other advantages and features of the
invention, and the manner in which the same are accomplished, will
become more readily apparent upon consideration of the following
detailed description of the invention taken in conjunction with the
accompanying examples, which illustrate preferred and exemplary
embodiments.
DETAILED DESCRIPTION OF THE INVENTION
[0030] The invention will now be described more fully hereinafter
with reference to the accompanying examples, in which preferred
embodiments of the invention are shown. This invention may,
however, be embodied in many different forms and should not be
construed as limited to the embodiments set forth herein; rather,
these embodiments are provided so that this disclosure will be
thorough and complete, and will fully convey the scope of the
invention to those skilled in the art.
[0031] As used herein, the term "polymer" means a molecule, formed
by the chemical union of two or more oligomer units. The chemical
units are normally linked together by covalent linkages. The two or
more combining units in a polymer can be all the same, in which
case the polymer is referred to as a homopolymer. They can be also
be different and, thus, the polymer will be a combination of the
different units. These polymers are referred to as copolymers.
[0032] The term "oligomer" is used herein to mean a molecule,
typically an organic molecule, which in itself is formed by the
chemical union of two or more monomer units. The monomer units of
an oligomer may be different or all the same. An oligomer is
capable of reacting with another oligomer which is same or
different, in a polymerization reaction to form a polymer. As used
herein, the term oligomer by no means limits the size of the
molecule or the number of combining units or monomers in the
oligomer. Rather, "oligomer" is used to indicate a unit for forming
a polymer of the invention. The structure of an oligomer in a
polymer may be somewhat different in chemical structure from the
oligomer prior to polymerization because of the polymerization
reaction and the formation of covalent linkages.
[0033] The term "carbonate linkage" is used herein to mean a
linkage that includes the group --O--CO.sub.2--. It is to be
understood that a carbonate linkage is distinct from a carboxylate
linkage which typically has a structure of R--CO.sub.2-- (where n
is at least 1 and R=alkyl or aryl) and has different chemical and
physical properties.
[0034] The terms "group," and "moiety," are all used herein
interchangeably to refer to a distinct, definable portion or unit
of a molecule. Sometimes, the structure of a group or moiety may
include another smaller group or moiety. For example, a functional
group of --O--CO.sub.2-Z includes Z which may be a reactive group
or moiety including N-succinimidyl or 1-benzotriazolyl.
[0035] The terms "active," "reactive," and "functional" are used
herein interchangeably to mean that a molecule or a group or moiety
is reactive with other molecules or groups or moieties of
molecules.
[0036] The term "biologically active agent" when used herein means
any substance that can impact any physical or biochemical
properties of a biological organism including, but not limited to,
viruses, bacteria, fungi, plants, animals and humans. In
particular, as used herein, a biologically active agent can be any
substance intended for the diagnosis, cure, mitigation, treatment,
or prevention of a disease in humans or other animals, or to
otherwise enhance the physical or mental well being of humans or
animals. Examples of biologically active agents include, but are
not limited to, organic and inorganic compounds, proteins,
peptides, lipids, polysaccharides, nucleotides, DNAs, RNAs, other
polymers, and derivatives thereof. Examples of biologically active
agents include antibiotics, fungicides, anti-viral agents,
anti-inflammatory agents, anti-tumor agents, cardiovascular agents,
anti-anxiety agents, hormones, growth factors, steroidal agents,
and the like. Biologically active agents include microorganisms
such as bacteria and yeast cells, viral particles, plant or animal
or human cells or tissues, and the like, in their native or
modified forms.
[0037] The oligomers used in the practice of the invention should
be selected so that they and the degradation products of the
polymer of this invention are water soluble and can easily be
excreted from animal bodies under natural physiological conditions.
They should be non-toxic, or at least of acceptable low toxicity,
and should not cause a substantial adverse effect in human or
animal bodies.
[0038] Many different types of alkylene oxide oligomers are useful
in forming the polymer of this invention. In its simplest form, an
alkylene oxide "homo-oligomer" is used having the formula of
HO--(--CHRCH.sub.2--O).sub.n--H, where R is H or an alkyl,
including methyl. Suitable oligomers also include alkylene oxide
"co-oligomers," which are composed of different alkylene oxide
monomers in which R is varied independently along the chain. An
example of a co-oligomer is a structure in which two different R
groups are present in a block such as
HO--(--CHR.sub.1CH.sub.2--O--).sub.n--(--CHR.sub.2CH.sub.2--O--).sub.m--H-
, where n and m can be varied independently. An example of this
type of block structure is the case in which R.sub.1 is hydrogen
and R.sub.2 is methyl.
[0039] Block oligomers can exhibit surface activity. Degradable
surfactants are useful in drug delivery systems and can be used to
form micelles and thermally reversible gels. Random oligomers in
which R.sub.1 and R.sub.2 are randomly placed along the oligomer
chain are also useful. The oligomers can be branched, as in the
formula
R.sub.3[O--(--CHR.sub.1CH.sub.2--O--).sub.n--].sub.mH
[0040] where R.sub.3 is a core branching moiety, including glycerol
or pentaerythritol, R.sub.1 is alkyl, n can range from 2 to
hundreds, and m is at least 3.
[0041] A suitable oligomer can be formed from about 2 to 2000
monomers. However, the size of the oligomers used can vary so long
as the above requirements are met. Normally an oligomer has from
about 5 to 500 monomers. Advantageously, an oligomer has from about
10 to 50 monomers. An oligomer can be prepared by polymerizing or
co-polymerizing monomers, and the size or molecular weight of the
oligomer can be controlled by limiting the extent of this
polymerization reaction.
[0042] As noted above, the oligomers contained in the polymer of
this invention can be the same or different types of oligomers, or
oligomers of the same type but different sizes. Therefore, the
polymer of this invention can be either a homopolymer or
heteropolymer.
[0043] The polymer of this invention typically has one single
linear polymer backbone with two termini. However, branched
polymers and star polymers are also contemplated that have two or
more linear polymers, at least one of which is the linear polymer
backbone of this invention, covalently linked to a central
branching core.
[0044] The polymer of this invention can have an inert terminal
moiety, typically H, alkyl, and aryl. The alkyl and aryl groups can
be substituted or unsubstituted, and normally are methyl, ethyl,
phenyl, etc. The polymer can also have one or more reactive
moieties capable of reacting with a moiety in another molecule,
such as an amino group or a thiol group on a protein. Examples of
such reactive moieties include, but are not limited to, acryloyl,
alkenyl, tresyl, N-succinimidyloxycarbonyl,
1-benzotriazolyloxycarbonyl, p-nitrophenyloxycarbonyl,
N-maleimidyl, aldehydes, acetals, 1-imidazolylcarbonyl,
vinylsulfone, iodoacetamide, o-pyridyldithiyl, and the like.
[0045] In one embodiment of this invention, the hydrolytically
degradable polymer is a poly(ether carbonate) composed of two or
more alkylene oxide oligomers and/or alkylene oxide monomers
covalently linked together by carbonate linkages. For example, the
poly(ether carbonate) can have the formula of
X--O--{[(R.sub.1--O).sub.a--CO.sub.2--].sub.h--[(R.sub.2--O).sub.b--CO.sub-
.2--].sub.i}.sub.m--{[(R.sub.3--O).sub.c--CO.sub.2--].sub.j--[(R.sub.4--O)-
.sub.d--CO.sub.2--].sub.k}--(R.sub.5--O).sub.e--Y
[0046] wherein
[0047] R.sub.1, R.sub.2, R.sub.3, R.sub.4, and R.sub.5 are alkyl
groups which may be linear, branched, substituted or unsubstituted,
and they can be same or different; typically R.sub.1, R.sub.2,
R.sub.3, R.sub.4, and R.sub.5 are ethyl;
[0048] a, b, c, d, e each is an integer of from 1 to about 2000,
normally from about 5 to 500, and advantageously from about 10 to
50;
[0049] h, i, j, and k each is an integer of from 0 to about 100,
and the sum of h, i, j, and k is from about 2 to 200, normally from
about 5 to 100, and advantageously from about 10 to 50; and
[0050] each of X and Y is hydrogen, alkyl, alkenyl, aryl, or
reactive moieties as described above, and X and Y can be same or
different.
[0051] In a preferred embodiment, the poly(ether carbonate) of this
invention has the formula of:
X--O--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub-
.2O).sub.n--Y
[0052] wherein n is an integer of from about 2 to 2000, normally
from about 5 to 500, and advantageously from about 10 to 50; m is
an integer of from about 2 to 100, typically from about 5 to 100,
and advantageously from about 10 to 50, and wherein X and Y can be
same or different and each independently is H, alkyl, alkenyl,
aryl, or a reactive moiety, acryloyl, tresyl,
N-succinimidyloxycarbonyl, 1-benzotriazolyloxycarbonyl,
p-nitrophenyloxycarbonyl, N-maleimidyl, aldehydes, acetals,
1-imidazolylcarbonyl, vinylsulfone, iodoacetamide, and
o-pyridyldithiyl.
[0053] This specific form of poly(ether carbonate) contains
repeating ethylene oxide oligomers linked by carbonate linkages
that can be hydrolytically cleaved. Such hydrolytic cleavage leads
to ethylene oxide oligomers and carbon dioxide. Therefore, the
poly(ether carbonate) differs substantially from poly(ethylene
glycol) or PEG in having multiple degradable backbone carbonate
linkages that allow the polymer to be broken down into many smaller
oligomers. Since the rate of degradation of the polymer is
proportional to the number of degradable carbonate linkages
present, and since the size and number of the oligomers can be
predetermined, substantial control over both degradation rate and
the size of the degradation products is thus possible.
[0054] To prepare polymers of the invention, in one example, one or
more oligomers as described above are provided each having a
hydroxyl group at one terminus and a functional group of
--O--CO.sub.2-Z at another terminus. The oligomers are then
polymerized or co-polymerized in a condensation polymerization
reaction under conditions sufficient to form a hydrolytically
degradable polymer.
[0055] The functional group --O--CO.sub.2-Z is capable of reacting
with a hydroxyl group to form a carbonate linkage. Typically, Z can
be any reactive leaving groups so long as the functional group can
react with a hydroxyl group to form a carbonate linkage. Examples
of suitable leaving groups include N-succinimidyl,
1-benzotriazolyl, and p-nitrophenyl. Methods for preparing an
oligomer having a functional group --O--CO.sub.2-Z as described
above are well known in the art, and are disclosed in U.S. Pat.
Nos. 5,650,234, 5,281,698 and 5,468,478; Veronese, et al., Appl.
Biochem. Biotech., 11:141 (1985); and Sartore et al., Appl.
Biochem. Biotech., 27:45 (1991), all of which are incorporated
herein by reference.
[0056] As discussed above, one or more types of oligomers can be
polymerized together. In addition, if desired, monomers having a
hydroxyl terminus and a functional group --O--CO.sub.2-Z at another
terminus, can also be included in the polymerization mixture.
[0057] Thus, to give an example, the poly(ether carbonate)
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.2-
O).sub.n--H
[0058] as described above can be prepared in accordance with this
method by the following steps. First, an ethylene oxide oligomer is
provided having a formula of
HO--(--CH.sub.2CH.sub.2--O--).sub.n--O--CO.sub.2-Z, where Z is a
reactive leaving group such as N-succinimidyl, 1-benzotriazolyl,
and p-nitrophenyl. This oligomer is then polymerized under
controlled conditions to provide the above poly(ether
carbonate).
[0059] In another example of this invention, a first oligomer is
provided, which is a bifunctional oligomer having a first
functional group of --O--CO.sub.2--W at one terminus and, at
another terminus, a second functional group of --O--CO.sub.2-Z.
Both functional groups are capable of reacting with a hydroxyl
group to form a carbonate linkage. Z and W are reactive leaving
groups, and can be any leaving groups known in the art so long as
the functional groups containing them, as stated above, are capable
of reacting with a hydroxyl group to form a carbonate linkage. Z
and W can be same or different. The preferred Z and W are
N-succinimidyl, 1-benzotriazolyl, and p-nitrophenyl. Two or more
different bifunctional oligomers can also be used in the same
polymerization reaction.
[0060] Methods for preparing such bifunctional oligomers are
similar to those for making the monofunctional oligomers described
above. Preferably, Z and W are the same, and the bifunctional
molecule Z-oligomer-Z can be provided by activating an oligomer
having two hydroxyl terminal groups, with an activating molecule
having the formula of Z-O--CO.sub.2-Z. Suitable examples of the
activating molecule include, disuccinimidylcarbonate,
bis(1-benzotriazolyl) carbonate and bis(p-nitrophenyl) carbonate.
See, e.g., U.S. Pat. Nos. 5,281,698; 5,650,234; Veronese, et al.,
Appl. Biochem. Biotech., 11:141 (1985); and Sartore et al., Appl.
Biochem. Biotech., 27:45 (1991), all of which are incorporated
herein by reference.
[0061] In addition to the first oligomer that is bifunctional, a
second oligomer is also provided having two terminal hydroxyl
groups. This second oligomer is then polymerized with the first
oligomer to form the polymer of this invention.
[0062] Two or more types of bifunctional oligomers can be used in
the same polymerization reaction. In addition, two or more types of
oligomers having two terminal hydroxyl groups can also be used in a
polymerization reaction. As will be apparent to a skilled artisan,
when only one type of bifunctional oligomer and one type of
dihydroxyl oligomer are used, and when the two oligomers are the
same except for the terminal groups, the polymer formed therefrom
will be a homopolymer having a single type of repeating unit or
oligomer linked with hydrolytically degradable linkages. Otherwise,
a heteropolymer or block polymer or terpolymer will be made
containing different types of oligomers in the polymer
backbone.
[0063] To give an example of the method of this embodiment, the
poly(ether carbonate)
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.2-
O).sub.n--H
[0064] can be prepared by co-polymerizing a first ethylene oxide
oligomer having a formula of
Z-O.sub.2C--O--(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2-Z
[0065] and a second ethylene oxide oligomer
HO--(--CH.sub.2CH.sub.2--O--).- sub.n--OH, under suitable
polymerization conditions. Z is preferably N-succinimidyl,
1-benzotriazolyl, or p-nitrophenyl. The oligomer
Z-O.sub.2C--O--(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2-Z
[0066] can be prepared by reacting Z-O--CO.sub.2-Z with
HO--(--CH.sub.2CH.sub.2--O--).sub.n--OH, under the conditions
disclosed in U.S. Pat. No. 5,281,698.
[0067] In yet another method, one or more oligomers having two
hydroxyl terminal groups are polymerized directly with an
activating molecule having the formula of Z-O--CO.sub.2-Z to form
the hydrolytically degradable polymer. Thus, for example, the
poly(ether carbonate)
HO--[(--CH.sub.2CH.sub.2--O--).sub.n--CO.sub.2--].sub.m--(CH.sub.2CH.sub.2-
O).sub.n--H
[0068] can also be prepared by co-polymerizing an activating
molecule Z-O--CO.sub.2-Z and the oligomer
HO--(--CH.sub.2CH.sub.2--O--).sub.n--OH, under conditions
sufficient to form the poly(ether carbonate).
[0069] Again, in this method, either one oligomer is used to
generate a homopolymer, or two or more different oligomers can be
used in the same polymerization reaction to produce a
heteropolymer, or block polymer or terpolymer.
[0070] The polymerization reactions are conducted under conditions
sufficient to form the hydrolytically degradable polymer of this
invention. The polymerization reaction in each of the
above-described methods is a condensation reaction. Many different
known reaction conditions can be used. Typically, a catalyst is
included in the polymerization reaction mixture. Examples of
suitable catalysts are organic bases, including triethylamine,
pyridine, quinoline, and 4,4-dimethylaminopyridine. Amine bases
such as 4,4-dimethylaminopyridine and triethylamine are
preferred.
[0071] The polymerization can be conducted in either melt or
solvent. Suitable solvents include, but are not limited to,
acetonitrile, THF, dimethylformamide, dimethylsulfoxide, benzene,
toluene, xylenes, chloroform, and methylene chloride. The
polymerization reaction rate and the extent of polymerization,
which determines the average molecule weight of the final
hydrolytically degradable polymer product can be partly controlled
by the reaction temperature and the reaction time. Suitable
reaction temperature can vary from about 0.degree. C. to
100.degree. C. Higher reaction temperatures lead to greater
reaction speed. Preferably, the polymerization reaction is
conducted at a temperature of from about 37.degree. C. to
100.degree. C., typically from about 45.degree. C. to 100.degree.
C. and advantageously from about 70.degree. C. to 90.degree. C.
When the reaction is conducted in a melt, the temperature needs be
maintained at a certain minimum temperature in order to keep the
reaction mixture at a melt state.
[0072] In the above described three embodiments of the method of
this invention, the polymerization reactions would be predicted to
lead to polymers with an activated carbonate terminal group. In
practice, however, NMR analysis of the polymer products indicates
that the terminal groups of the hydrolytically degradable polymer
prepared therefrom often are hydroxyl groups. While not wishing to
be bound by any theory, it is believed that this is caused by
reaction with a small amount of water present as an impurity in the
reaction. Any small amount of remaining terminally activated
carbonate may be removed by hydrolyis in water for a short period
or near a neutral pH. The terminal activating groups are much more
sensitive to water than are the degradable carbonate linkages.
[0073] The polymer of this invention can optionally be activated at
one or all termini, thus providing an activated polymer capable of
being covalently linked to another molecule, including, for
example, a protein, to form a conjugate. The polymer can also be
capped at one terminus by an inert group and at another terminus by
a reactive moiety.
[0074] The polymer of this invention can be activated at its
terminus to form a terminal reactive moiety by methods well known
to those familiar with the art of organic or polymer chemistry. The
well established methods in the broad field of poly(ethylene
glycol) chemistry are generally useful, and such methods should be
apparent to a skilled artisan. The polymer can be activated at one
terminus, or all termini, in which case, the reactive moieties at
different termini can be same or different.
[0075] For example, the polymer may be activated to form a terminal
moiety of N-succinimidyl carbonate (see e.g., U.S. Pat. Nos.
5,281,698, 5,468,478), amine (see, e.g., Buckmann et al. Makromol.
Chem. 182:1379 (1981), Zaplipsky et al. Eur. Polym. J. 19:1177
(1983)), hydrazide (See, e.g., Andresz et al. Makromol. Chem.
179:301 (1978)), succinimidyl propionate and succinimidyl butanoate
(see, e.g., Olson et al. in Poly(ethylene glycol) Chemistry &
Biological Applications, pp 170-181, Harris & Zaplipsky Eds.,
ACS, Washington, D.C., 1997; see also U.S. Pat. No. 5,672,662),
succinimidyl succinate (See, e.g., Abuchowski et al. Cancer
Biochem. Biophys. 7:175 (1984) and Joppich et al. Macrolol. Chem.
180:1381 (1979), succinimidyl ester (see, e.g., U.S. Pat. No.
4,670,417), benzotriazole carbonate (see, e.g., U.S. Pat. No.
5,650,234), glycidyl ether (see, e.g., Pitha et al. Eur. J.
Biochem. 94:11 (1979), Elling et al., Biotech. Appl. Biochem.
13:354 (1991), oxycarbonylimidazole (see, e.g., Beauchamp, et al.,
Anal. Biochem. 131:25 (1983), Tondelli et al. J. Controlled Release
1:251 (1985)), p-nitrophenyl carbonate (see, e.g., Veronese, et
al., Appl. Biochem. Biotech., 11:141 (1985); and Sartore et al.,
Appl. Biochem. Biotech., 27:45 (1991)), aldehyde (see, e.g., Harris
et al. J. Polym. Sci. Chem. Ed. 22:341 (1984), U.S. Pat. Nos.
5,824,784, 5,252,714), maleimide (see, e.g., Goodson et al.
Bio/Technology 8:343 (1990), Romani et al. in Chemistry of Peptides
and Proteins 2:29 (1984)), and Kogan, Synthetic Comm. 22:2417
(1992)), orthopyridyl-disulfide (see, e.g., Woghiren, et al.
Bioconj. Chem. 4:314 (1993)), acrylol (see, e.g., Sawhney et al.,
Macromolecules, 26:581 (1993)), vinylsulfone (see, e.g., U.S. Pat.
No. 5,900,461). In addition, two molecules of the polymer of this
invention can also be linked to the amino acid lysine to form a
di-substituted lysine, which can then be further activated with
N-hydroxysuccinimide to form an active of N-succinimidyl moiety
(see, e.g., U.S. Pat. No. 5,932,462). All of the above references
are incorporated herein by reference.
[0076] To give an example, the polymer of this invention may be
activated to form a terminal reactive moiety of N-succinimidyl
carbonate or 1-benzotriazolyl carbonate by reacting the polymer
with di-N-succinimidyl carbonate or di-1-benzotriazolyl carbonate
respectively. To give another example, terminal reactive moieties
such as N-maleimidyl and o-pyridyldithiyl may be prepared by
reacting the polymer with activated carbonates connected to
N-maleimidyl or o-pyridyldithiyl by linker groups. Terminal
aldehyde and acetal moieties can be attached by linking groups.
Terminal acid groups can be attached by reaction of the above
active carbonates with amino acids or other acid linkers. These
acids can then be activated by formation of active esters such as
succinimidyl active esters.
[0077] The polymer of this invention, activated or not, as prepared
by the above methods, can be easily purified from the reaction
mixture. Many methods known in the art can be used. A preferred
method for purifying the polymer and its derivatives is by
precipitation from a solvent in which they are essentially
insoluble while the reactants are soluble. Suitable solvents
include ethyl ether or isopropanol. As is apparent to a skilled
artisan, other methods such as ion exchange, size exclusion, silica
gel, and reverse phase chromatography can also be useful.
[0078] In accordance with another aspect of this invention, the
activated polymer is used to form a conjugate with a biologically
active agent. The conjugate comprises the polymer of this invention
covalently linked to a biologically active agent. Because the
polymer of this invention is hydrolytically degradable in vivo and
can be cleaved at the carbonate linkages, thus forming smaller
oligomers, the conjugate is especially useful for controlled
delivery of the bound agent into animal bodies. Since the polymer
in the conjugate is susceptible to breakdown into smaller
oligomers, the polymer typically is excreted from animal bodies
faster than a polymer of similar size that is not degradable. Thus,
potential adverse effects that may be caused by a large polymer's
long period of stay in the body is avoided. Therefore, conjugation
of the polymer of this invention to a biologically active agent can
provide for a sufficient circulation period for the agent while
minimizing any adverse effects of the polymer.
[0079] In the conjugates of this invention, the linkage between the
biologically active agent and the polymer of this invention can be
stable or hydrolytically degradable. When it is degradable,
substantially all of the polymer can be cleaved off the
biologically active agent under physiological conditions, releasing
the agent substantially in its native form inside the body. Methods
for forming a hydrolytically degradable linkage between a
biologically active agent and a water soluble polymer are well
known in the art and should be apparent to a skilled artisan. For
example, ester linkages formed by the reaction of PEG carboxylic
acids or activated PEG carboxylic acids with alcohol groups on a
biologically active agent generally hydrolyze under physiological
conditions to release the agent. Other hydrolytically degradable
linkages include carbonate linkages; imine linkages resulted from
reaction of an amine and an aldehyde (see, e.g., Ouchi et al.,
Polymer Preprints, 38(1):582-3 (1997), which is incorporated herein
by reference.); phosphate ester linkages formed by reacting an
alcohol with a phosphate group; hydrozone linkages which are
reaction product of a hydrazide and an aldehyde; acetal linkages
that are the reaction product of an aldehyde and an alcohol;
orthoester linkages that are the reaction product of a formate and
an alcohol; peptide linkages formed by an amine group, e.g., at an
end of a polymer such as PEG, and a carboxyl group of a peptide;
and oligonucleotide linkages formed by a phosphoramidite group,
e.g., at the end of a polymer, and a 5' hydroxyl group an
oligonucleotide.
[0080] Methods for conjugating the polymer of this invention to a
biologically active agent should be apparent based on the above
discussion. Typically, the polymer of this invention must be
activated to form the activated polymer of this invention as
described above, having at least one terminal reactive moiety. The
terminal reactive moiety may vary depending on the reactivity of a
target moiety on the biologically active agent to be conjugated.
Examples of reactive groups on proteins are thiols and amines,
while on small molecule drugs, amines, alcohols, thiols, and
carboxylic acids are common reactive gorups. The conjugate is then
formed by reacting the terminal reactive moiety of the activated
polymer with the target moiety on the biologically active agent.
Such methods are well known in the art, and are discussed in the
patents and publications referred to above in the context of
forming terminal reactive moieties.
[0081] In a preferred embodiment, the polymer of this invention
used for forming a conjugate is a poly(ether carbonate) composed of
alkylene oxide oligomers, more preferably ethylene oxide oligomers,
linked together by carbonate linkages. Ethylene oxide oligomers are
poly(ethylene glycol)s with a predetermined molecular weight,
typically from about 88 to about 8000, preferably from about 88 to
about 2000. Thus, in this embodiment of the invention, the polymer
behaves in a similar manner as polyethylene glycol. However, when
delivered in vivo, the polymer in the conjugate will break down
into a number of smaller oligomer fragments. If the linkage between
the polymer and the biologically active agent is stable, then,
after degradation, one oligomer is linked to the agent.
[0082] In accordance with another aspect of this invention, a
hydrolytically degradable hydrogel and method of making thereof are
also provided. As is known in the art, a hydrogel typically is a
polymeric network formed by crosslinking one or more
multifunctional backbone molecules or polymers. The resulting
polymeric network is hydrophilic and swells in an aqueous
environment thus forming a gel-like material, i.e., hydrogel.
Hydrogels are useful for drug delivery as they can be implanted or
injected into animal bodies. Typically a hydrogel comprises a
backbone bonded to a crosslinking agent.
[0083] In accordance with this invention, the polymer of this
invention is used as the crosslinking agent in the hydrogel. The
polymer must be activated so that it has at least two terminal
reactive moieties that are capable of reacting with multiple
moieties on the backbone to form covalent linkages.
[0084] Alternatively, two or more types of activated polymer are
used as crosslinking agents. Each activated polymer has one
terminal reactive moiety capable of reacting with a moiety on the
backbone, and another terminal reactive moiety capable of reacting
with the corresponding terminal reactive moiety on the other type
of activated polymer. An example of this other moiety is, for
example, a vinyl-containing group such as an acrylate group that
can participate in chain polymerization among the different types
of activated polymers. When the polymer of this invention is
activated so that it has two terminal vinyl groups, the polymer
itself may act as both crosslinking agent and backbone, and
self-polymerize into a hydrolytically degradable hydrogel through a
chain polymerization reaction.
[0085] The backbone of the hydrogel is a nontoxic biocompatible
macromolecule or small molecule, having at least two or preferably
more active groups available to react with the terminal reactive
moieties of the crosslinking agent to form covalent linkages. By
"biocompatible" it is intended that the molecule used as backbone
would not substantially adversely affect the body and tissue of the
living subject into which the hydrogel is to be implanted or
injected. More particularly, the material does not substantially
adversely affect the growth and any other desired characteristics
of the tissue cells surrounding the implanted hydrogel. It is also
intended that the material used does not cause any substantially
medically undesirable effect in any other parts of the living
subject. In addition, if the molecule is degradable inside the
body, the degradation products should also be substantially
biocompatible as defined above. Generally, the methods for testing
the biocompatibility of a material well known in the art.
[0086] Examples of suitable backbones include, but are not limited
to, proteins, modified proteins such as glycoproteins,
phosphorylated proteins, acylated proteins, and chemically modified
proteins, peptides, aminocarbohydrates, glycosaminoglycans,
aminolipids, polyols, polythiols, polycarboxylic acids, polyamines
such as dilysine, poly(vinylamine) and polylysine, poly(ethylene
glycol) amines, pharmaceutical agents having at least two active
groups, etc. Specific examples of the backbone include, but are not
limited to, branched PEG amines, fibrin, fibrinogen, thrombin,
albumins, globulins, collagens, fibronectin, chitosan, and the
like. In addition, the backbone may also be microorganisms such as
viral particles, bacterial or yeast cells, animal or human cells or
tissues.
[0087] The activated polymer of this invention used as a
crosslinking agent can be in a linear, branched or star form. In
branched or star forms, three or more linear polymers are
covalently linked, at one terminus, to a central, branched core
moiety. The central branch core moiety can be derived from the
amino acid lysine, or polyols such as glycerol, pentaerythritol and
sorbitol. Branched PEGs are known in the art. These branched PEGs
can be incorporated as components of the poly(ether carbonate)s of
this invention.
[0088] As will be apparent, because of the carbonate linkages
incorporated in the crosslinking agent, the hydrogel of this
invention is hydrolytically degradable. In addition, the linkages
between the backbones and the crosslinking agents formed from the
crosslinking reactions can also be made hydrolyzable, by methods
described in the context of the conjugate of this invention. Thus,
the hydrogel of this invention can gradually break down or degrade
in the body as a result of the hydrolysis of the hydrolytically
degradable linkages.
[0089] Therefore, the hydrogel of this invention is suitable as a
biomedical material and a carrier for the delivery of biologically
active agents. For example, the hydrogel can carry therapeutic
drugs and can be implanted or injected in the target area of the
body. The hydrogel may also carry other agents such as nutrients or
labeling agents for imaging analysis. A hydrogel containing a
biologically active agent is termed herein as "a delivery
system".
[0090] In the various applications of the hydrogel of this
invention, the biologically active agents to be delivered can be
used as the backbone, or part of the backbone of the hydrogel.
Alternatively, biologically active agents can be "hinged" to the
hydrogel through a polymer of this invention or a linker molecule
with one terminus of the polymer or the linker linked to the
biologically active agent, and the other being connected through a
covalent linkage to the hydrogel. In addition, biologically active
agents or other substances to be delivered can also be loaded into
the hydrogel during the formation of the hydrogel, or afterwards
by, for example, diffusion into the matrix of the hydrogel without
being covalently bonded to the hydrogel structure.
[0091] Because the crosslinking agents (i.e., the polymers of this
invention) in the hydrogel are water soluble, the hydrogel can be
substantially water swellable. The degradation or breakdown of the
hydrogel in the body is gradual in nature and subject to control
because of the hydrolytically degradable carbonate linkages in the
crosslinking agents. Thus, the hydrogels of the invention are
particularly useful for sustained release of a biologically active
agent or other substance in the body. The hydrogels have potential
utility for adhesion prevention, bioadhesives, surgical sealants,
and related surgical applications.
[0092] The present invention is further illustrated in the
following examples which are given to illustrate the invention, but
should not be considered in limitation of the invention.
EXAMPLE 1
[0093] Synthesis of HO-PEC.sub.14 KDa-OH from
HO--(--CH.sub.2CH.sub.2--O--- ).sub.nCO.sub.2Bt
(Bt=1-benzotriazolyl) (n.sub.ave=23)
[0094] HO--(--CH.sub.2CH.sub.2--O--).sub.nCO.sub.2Bt (n.sub.ave=23)
(5 g) and 1.2 g of dimethylaminopyridine were dissolved in 10 ml of
anhydrous acetonitrile . The reaction was stirred at 70.degree. C.
for 22 hours. The product was precipitated with 200 ml of
isopropanol, stirred for one-half hour, then collected by vacuum
filtration. The product was washed with isopropanol (100
ml.times.2), and dried in vacuo overnight. Yield: 4.1 g (82%). The
resulting polymer was 99% pure by gpc analysis and had a molecular
weight of 13,800 Da with a polydispersity of 1.47.
EXAMPLE 2
[0095] Synthesis of HO-PEC.sub.7K-OH from
Bt-O.sub.2C--(--O--CH.sub.2CH.su- b.2--).sub.n--OCO.sub.2-Bt and
HO--(--CH.sub.2CH.sub.2--O--).sub.n--H (n.sub.ave=23)
[0096] 1. Preparation of
Bt-O.sub.2C--(O--CH.sub.2CH.sub.2--).sub.n--OCO.s- ub.2-Bt
(n.sub.ave=23)
[0097] HO--(--CH.sub.2CH.sub.2--O--).sub.n--H (n.sub.ave=23) (15 g,
Aldrich) was dissolved in 100 ml of anhydrous acetonitrile, and
solvent was removed by distillation. The residue was dissolved in
100 ml of anhydrous acetonitrile, and 13.3 g (1.5 equivalent) of
di(1-benzotriazolyl carbonate) and 3.1 ml (1.3 equiv) of anhydrous
pyridine were added. The reaction was stirred at room temperature
under Ar overnight. The solvent was evaporated to dryness under
reduced pressure. The product was precipitated by addition of 300
ml of cold diethyl ether. The precipitate was stirred under Ar for
30 min., collected by vacuum filtration and dried in vacuo
overnight. There was 100% substitution by nmr analysis.
[0098] 2. Preparation of HO-PEC.sub.7K-OH
[0099] HO--(--CH.sub.2CH.sub.2--O--).sub.n--H (n.sub.ave=23)
(Aldrich, 10 g) was dissolved in 50 ml of anhydrous acetonitrile
and the solvent removed by distillation. The residue was dissolved
in 20 ml of anhydrous acetonitrile and 10 g (1.0 equiv) of
Bt-O.sub.2C--(--O--CH.sub.2CH.sub.2-- -).sub.nOCO.sub.2-Bt
(n.sub.ave=23)- and 2.5 g of dimethyaminopyridine were added. The
reaction was stirred at 70.degree. C. for about 22 hours. The
product was precipitated with 500 ml of isopropanol, stirred for
half hour, then collected by vacuum filtration. The collected
product was washed with isopropanol 200 ml.times.2), and dried in
vacuo overnight. The resulting polymer was about 97% pure by gpc
and nmr and had a molecular weight of 7000 Da.
EXAMPLE 3
[0100] Synthesis of bis-benzotriazolyl Carbonate of HO-PEC.sub.7
KDa-OH
[0101] 15.0 g of HO-PEC.sub.7 KDa-OH (prepared in Example 2) was
dissolved in 50 ml of anhydrous acetonitrile, and solvent was
distilled off. This process was repeated once. The residue was
dissolved in 50 ml of anhydrous acetonitrile, and 1.8 g of
bis(1-benzotriazolyl carbonate) and 0.5 ml of anhydrous pyridine
were added. The reaction was stirred at room temperature under Ar
overnight. The solvent was evaporated to dryness at reduced
pressure and the product was precipitated by addition of 500 ml of
isopropanol. The precipitate was stirred under Ar for 30 min.,
collected by vacuum filtration, and dried in vacuo overnight.
Substitution was greater than 95% by nmr. Yield: 14.3 g.
EXAMPLE 4
[0102] Preparation of
HO--[--(CH.sub.2CH.sub.2O--).sub.nCO.sub.2].sub.m(---
CH.sub.2CH.sub.2O).sub.n--H (n.sub.ave=45; m.sub.ave=18 from
HO(--CH.sub.2CH.sub.2O--).sub.nCO.sub.2NS (n.sub.ave=45)
(NS=N-succinimidyl) in Solution
[0103] HO(--CH.sub.2CH.sub.2O--).sub.nCO.sub.2NS (n.sub.ave=45) (5
g) was dissolved in acetonitrile (10 ml), dimethylaminopyridine
(0.6 g) was added, and the resulting mixture was stirred at
70-80.degree. C. overnight. Methylene chloride (20 ml) was added
and the resulting mixture added to 600 ml of isopropyl alcohol. The
resulting precipitate was collected by vacuum filtration and dried
under vacuum overnight at room temperature. Nmr and gpc analysis
indicated the polymer to have a molecular weight of 38,000 Da.
EXAMPLE 5
[0104] Preparation of HO-PEC.sub.35 Kda-OH from
HO(--CH.sub.2CH.sub.2O--) .sub.nCO.sub.2NS (n.sub.ave=45)
(NS=N-succinimidyl) in a Melt.
[0105] HO(--CH.sub.2CH.sub.2O--).sub.nCO.sub.2NS (n.sub.ave=45) (5
g) and dimethylaminopyridine (0.6 g) were mixed and the resulting
mixture was stirred at 80-90.degree. C. overnight. Methylene
chloride (20 ml) was added and the resulting mixture added to 600
ml of isopropyl alcohol. The resulting precipitate was collected by
vacuum filtration and dried under vacuum overnight at room
temperature. Nmr and gpc analysis indicated the polymer to have a
molecular weight of 35,000 Da.
EXAMPLE 6
[0106] Preparation of HO-PEC.sub.9.4 KDa-OH from
HO--(--CH.sub.2CH.sub.2--- O--).sub.n--H(n.sub.ave=14) and
di(N-succinimidyl) carbonate
[0107] HO--(--CH.sub.2CH.sub.2--O--).sub.n--H (n.sub.ave=14) (10.0
g) was dissolved in 100 ml of acetonitrile and the solution was
dried by azeotropic distillation. After removal of acetonitrile, 80
ml of methylene chloride and 20 ml of acetonitrile, 2.7 ml of
pyridine, and 4.3 g of di-(N-succinimidyl) carbonate were added.
After stirring overnight, the solvent was removed under reduced
pressure and 10 ml of acetonitrile and 4 g of DMAP were added. The
mixture was stirred at 80-90.degree. C. for 5 h and the product
precipitated by addition of isopropanol. The product was collected
by vacuum filtration and dried under vacuum at room temperature to
obtain the product as a white powder (4.5 g). NMR and GPC analysis
indicated that the polymer has a molecular weight of 9400 Da.
EXAMPLE 7
[0108] Preparation of Hydrogels from Bt-O.sub.2C--O-PEC.sub.7
KDa-O--CO.sub.2-Bt and 8-arm-PEG amine (10 kDa)
[0109] In a test tube, 110 mg of Bt-O.sub.2C--O-PEC.sub.7
KDa-O--CO.sub.2-Bt was dissolved in 1 ml of phosphate buffer (0.1
M, pH 7.0). To it was added 0.36 ml of 8-arm-PEG-amine (110 mg/ml
in the buffer). After rapid shaking, it was allowed to sit. A
hydrogel formed within 2 hours.
EXAMPLE 8
[0110] Degradation of the Hydrogel (Example 7) Prepared from PEC
and 8-arm-PEG amine (10 kDa).
[0111] The hydrogel (0.5 g) was placed in 3 ml of PBS buffer or rat
serum at 37.degree. C. Rat serum was replaced with fresh serum
every 10 to 12 hours. Gel disappearance was monitored visually. The
gel prepared from PEC.sub.7 KDa disappeared in PBS buffer within
3.5 days but in 1.5 days in rat serum, while the similar gel
prepared from PEC3 Kda disappeared in PBS buffer in approximately
10 days.
EXAMPLE 9
[0112] Preparation of PEC.sub.7 KDa Diacrylate
[0113] HO-PEC.sub.7 KDa-OH (10 g) (prepared in Example 2) in
toluene (200 ml) was dried by azeotropic distillation and
triethylamine (1.75 ml) in CH.sub.2Cl.sub.2 was added. The
resulting solution was cooled to 0.degree. C. and acryloyl chloride
(2.5 ml) was added under argon. After the addition was complete,
the mixture was stirred overnight at room temperature. The
resulting solution was concentrated, filtered, and the product
precipitated from the filtrate by addition of ethyl ether (300 ml).
The precipitate was collected by filtration, dissolved in 100 ml of
methylene chloride, and the resulting solution stirred with 10 g of
sodium carbonate overnight. The mixture was filtered and the
product was precipitated with 500 ml of ethyl ether. The product
was collected by filtration and dried under vacuum. NMR comparison
of acrylate and backbone absorptions indicated approximately 100%
of the terminal groups were acryloylated.
EXAMPLE 10
[0114] Preparation of Hydrogel from PEC.sub.7 KDa Diacrylate
[0115] PEC.sub.7 KDa diacrylate (100 mg) was dissolved in 1 ml of
pH 7 buffer and 30 ul of potassium persulfate was added. To the
resulting solution was added 30 .mu.l of 100 mM iron(II) sulfate
solution. The solution was shaken and a hydrogel formed in several
minutes.
EXAMPLE 11
[0116] Preparation of Degradable Hydrogel from
NS--O.sub.2C--O-PEC.sub.7 KDa-O--CO.sub.2--NS and Chitosan
[0117] NS--O.sub.2C--O-PEC.sub.7 KDa-O--CO.sub.2--NS (300 mg) was
mixed with 3 ml of a 1 wt. % solution of chitosan at pH 4. The
resulting solution formed a clear, firm hydrogel within 2
hours.
EXAMPLE 12
[0118] Preparation of
HO--[--(CH.sub.2CH.sub.2O--).sub.nCO.sub.2].sub.m(---
CH.sub.2CH.sub.2O).sub.n--H(N.sub.ave=22; m=2 from
benzyl-O--(CH.sub.2CH.s- ub.2O).sub.n--H(n.sub.ave=22) and
Bt-O.sub.2C--O--(CH.sub.2CH.sub.2O).sub.-
n--CO.sub.2Bt(n.sub.ave=22)
[0119] Azeotropically dried benzyl-PEG.sub.1 KDa-OH (40.6 g, 40.6
mmoles), Bt-O.sub.2C--O-PEG.sub.1 KDa-O--CO.sub.2-Bt (25 g, 20.3
mmoles) and dimethylaminopyridine (5 g, 81.2 mmoles) was mixed in
300 ml of acetonitrile. The reaction was stirred at 75-80.degree.
C. overnight. The solvent was removed by rotary evaporation and the
product was precipitated using diethyl ether/isopropyl alcohol (500
ml, 50/50) in an ice bath. The product was collected by filtration
and dried under vacuum. The dry product was placed in a 500 ml Parr
bottle and dissolved in 100 ml of anhydrous 1,4-dioxane. 11.0 g of
Pd/C (10% pd by wt.) was added and the bottle pressurized with 45
psi of hydrogen and shaken for 20.5 hours. The mixture was filtered
to remove the Pd/C and the solvent removed by rotary evaporation.
The crude solid was precipitated by adding 500 ml of isopropyl
alcohol. The product was collected by filtration and dried under
vacuum. The product was demonstrated to be greater than 98% pure
with a polydispersity of 1.034 by GPC.
[0120] Preparation of NS--O.sub.2C--O-PEC.sub.3
KDa-O--CO.sub.2--NS(NS=N-s- uccinimidyl) from HO-PEC.sub.3
KDa-OH
[0121] The dried HO-PEC.sub.3 KDa-OH was dissolved in anhydrous
CH.sub.3CN (150 ml) and stirred at room temperature under argon.
Di-N-succinimidyl carbonate (2.6 g, 10 mmoles) was added and
allowed to dissolve before pyridine (0.81 ml, 10 mmoles) was added.
The reaction mixture was stirred overnight (15 hrs.) The CH.sub.3CN
was removed under vacuum. The crude solid was dissolved in
CH.sub.2Cl.sub.2 (100 ml) and washed once with buffer solution (100
ml). The aqueous layer was extracted with an additional 50 ml of
CH.sub.2Cl.sub.2 and the combined organic layers were dried using
Na.sub.2SO.sub.4. The solvent was removed under vacuum until a
viscous residue remained. To this was added IPA (500 ml) to
precipitate the product. The product was collected by filtration
and dried under vacuum. The product was demonstrated by .sup.1H nmr
to have greater than 95% purity.
EXAMPLE 13
[0122] Hydrolysis Kinetics of a Single Carbonate Linkage in a PEC
Polymer
[0123]
CH.sub.3O--(CH.sub.2CH.sub.2O).sub.n--CO.sub.2(CH.sub.2CH.sub.2O).s-
ub.n--OCH.sub.3(n.sub.ave=113) (1 wt. % in buffer, pH 7.4) was
thermostated at 37.degree. C. and the hydrolysis rate of the
carbonate linkage was measured by analysis of the product using
GPC. The half-life for hydrolysis under these conditions was found
to be 44 days.
[0124] The foregoing description is to be considered illustrative
rather than descriptive of the invention. Therefore, it should be
understood that the specific embodiments described herein are
illustrative of how the invention may be practiced and that
modifications and other embodiments are intended to be included
within the scope of the appended claims.
* * * * *