U.S. patent application number 10/196845 was filed with the patent office on 2002-11-28 for removable stent for body lumens.
Invention is credited to Datta, Arindam, Huxel, Shawn Thayer, Jamiolkowski, Dennis D., Li, Yufu, Skula, E. Richard.
Application Number | 20020177904 10/196845 |
Document ID | / |
Family ID | 23868333 |
Filed Date | 2002-11-28 |
United States Patent
Application |
20020177904 |
Kind Code |
A1 |
Huxel, Shawn Thayer ; et
al. |
November 28, 2002 |
Removable stent for body lumens
Abstract
A removable stent for implantation into a lumen in a human body.
The stent is made from a soft, flexible fiber having an outer
surface. An outer bioabsorbable/degradable coating is applied to
the outer surface of the filament causing it to become rigid. The
coating softens in vivo through absorption and/or degradation such
that the stent is readily passed or removed from the lumen as a
softened filament after a pre-determined period of time through
normal flow of body fluids passing through the lumen or by manual
removal.
Inventors: |
Huxel, Shawn Thayer;
(Lawrenceville, NJ) ; Datta, Arindam;
(Hillsborough, NJ) ; Li, Yufu; (Bridgewater,
NJ) ; Jamiolkowski, Dennis D.; (Long Valley, NJ)
; Skula, E. Richard; (Wayne, NJ) |
Correspondence
Address: |
AUDLEY A. CIAMPORCERO JR.
JOHNSON & JOHNSON
ONE JOHNSON & JOHNSON PLAZA
NEW BRUNSWICK
NJ
08933-7003
US
|
Family ID: |
23868333 |
Appl. No.: |
10/196845 |
Filed: |
July 16, 2002 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10196845 |
Jul 16, 2002 |
|
|
|
09470620 |
Dec 22, 1999 |
|
|
|
Current U.S.
Class: |
623/23.75 ;
623/23.7 |
Current CPC
Class: |
A61L 31/10 20130101;
C08L 33/26 20130101; C08L 29/04 20130101; C08L 39/06 20130101; C08L
71/02 20130101; A61F 2/88 20130101; C08L 67/04 20130101; A61L 31/10
20130101; A61F 2002/072 20130101; A61L 31/10 20130101; A61L 31/10
20130101; A61L 31/10 20130101; A61F 2210/0004 20130101; A61L 31/10
20130101 |
Class at
Publication: |
623/23.75 ;
623/23.7 |
International
Class: |
A61F 002/02 |
Claims
We claim:
1. A stent, comprising: a helical structure having a plurality of
coils, said structure having a longitudinal axis and said coils
having a pitch, said structure having an internal longitudinal
passage wherein said structure is made from a filament having a
cross-section and an outer surface, said filament comprising: a
soft flexible elongated member having an outer surface; and a
bioabsorbable or biodegradable polymeric outer coating on the outer
surface of the member; wherein, the polymeric coating has
sufficient mechanical integrity to effectively maintain the
flexible member in a helical configuration, until the coating has
sufficiently been degraded or absorbed in vivo to effectively
convert the helical structure back into a soft, elongated
member.
2. The stent of claim 1 wherein the coating comprises a melt
polymer.
3. The stent of claim 1, wherein the coating comprises a solution
polymer.
4. The stent of claim 1 wherein the filament comprises a surgical
suture.
5. The stent of claim 4, wherein the suture comprises a
monofilament.
6. The stent of claim 4, wherein the suture comprises a
multifilament.
7. The stent of claim 4, wherein the suture comprises a
non-absorbable suture.
8. The stent of claim 4 wherein the suture comprises an absorbable
suture.
9. The stent of claim 1, wherein the coating comprises a polymer
made from monomers selected from the group consisting of lactide,
glycolide, para-dioxanone, caprolactone, and trimethylene
carbonate, caprolactone, blends thereof and copolymers thereof
10. The stent of claim 1, wherein the polymer of the coating has a
glass transition temperature above 55 C.
11. The stent of claim 1 wherein the polymer of the coating has a
glass transition temperature above 120 C.
12. The stent of claim 1, wherein the polymeric coating comprise a
polymer selected from the group consisting of polyacrylamides,
polyethylene glycols, polyethylene oxide, vinyl alcohols, and
poly(N-vinyl pyrrolidones.
13. The stent of claim 1, wherein the polymeric coating
additionally comprises polyamide.
14. A biodegradable filament, the filament comprising: an
elongated, flexible member having a cross-section, and an outer
surface; and, a polymeric coating on said outer surface, said
coating comprising a biodegradable or bioabsorbable polymer,
wherein, the polymeric coating has sufficient mechanical integrity
to effectively maintain the flexible member in a substantially
fixed configuration, until the coating has sufficiently been
degraded or absorbed in vivo to effectively convert the structure
back into a soft, elongated member.
15. The stent of claim 9 wherein the coating comprises a melt
polymer.
16. The stent of claim 9, wherein the coating comprises a solution
polymer.
17. The stent of claim 9 wherein the filament comprises a surgical
suture.
18. The stent of claim 12, wherein the suture comprises a
monofilament.
19. The stent of claim 12, wherein the suture comprises a
multifilament.
20. The stent of claim 12, wherein the suture comprises a
non-absorbable suture.
21. The stent of claim 12 wherein the suture comprises an
absorbable suture.
22. The stent of claim 1, wherein the coating comprises a polymer
made from monomers selected from the group consisting of lactide,
glycolide, para-dioxanone, caprolactone, and trimethylene
carbonate, caprolactone, blends thereof and copolymers thereof
23. The stent of claim 1, wherein the polymer of the coating has a
glass transition temperature above 55 C.
24. The stent of claim 1 wherein the polymer of the coating has a
glass transition temperature above 120 C.
25. The stent of claim 1, wherein the polymeric coating comprise a
polymer selected from the group consisting of polyacrylamides,
polyethylene glycols, polyethylene oxide, vinyl alochols, and
poly(N-vinyl pyrrolidones.
26. The stent of claim 1, wherein the polymeric coating
additionally comprises polyamide.
27. A method of maintaining a passageway of a body lumen
substantially open, comprising the steps of: providing a stent,
said stent comprising: a helical structure having a plurality of
coils, said structure having a longitudinal axis and a longitudinal
passage, and said coils having a pitch, wherein said structure is
made from a fiber, said fiber having a cross-section and said
filament comprising: an elongated flexible, filament member, having
an external surface and a cross-section; and, a, polymeric outer
coating on the surface of the member, wherein, the polymeric
coating has sufficient mechanical integrity to effectively maintain
the flexible member in a helical configuration; and, implanting
said stent in a body lumen and maintaining the stent in the body
lumen for a sufficient period of time to effectively maintain the
passageway of the lumen substantially open for a desired period of
time until the exterior coating softens, thereby converting the
stent structure into a soft, flexible filamentary structure.
Description
FIELD OF THE INVENTION
[0001] The field of art to which this invention relates is medical
devices, in particular, removable stent devices having
bioabsorbable or biodegradable polymer coatings.
BACKGROUND OF THE INVENTION
[0002] The use of stent medical devices, or other types of
endoluminal mechanical support devices, to keep a duct, vessel or
other body lumen open in the human body has developed into a
primary therapy for lumen stenosis or obstruction. The use of
stents in various surgical procedures has quickly become accepted
as experience with stent devices accumulates, and the number of
surgical procedures employing them increases as their advantages
become more widely recognized. For example, it is known to use
stents in body lumens in order to maintain open passageways such as
the prostatic urethra, the esophagus, the biliary tract,
intestines, and various coronary arteries and veins, as well as
more remote cardiovascular vessels such as the femoral artery, etc.
There are two types of stents that are presently utilized:
permanent stents and temporary stents. A permanent stent is
designed to be maintained in a body lumen for an indeterminate
amount of time. Temporary stents are designed to be maintained in a
body lumen for a limited period of time in order to maintain the
patency of the body lumen, for example, after trauma to a lumen
caused by a surgical procedure or an injury. Permanent stents are
typically designed to provide long term support for damaged or
traumatized wall tissues of the lumen. There are numerous
conventional applications for permanent stents including
cardiovascular, urological, gastrointestinal, and gynecological
applications.
[0003] It is known that permanent stents, over time, become
encapsulated and covered with endothelium tissues, for example, in
cardiovascular applications. Similarly, permanent stents are known
to become covered by epithelium, for example, in urethral
applications. Temporary stents, on the other hand are designed to
maintain the passageway of a lumen open for a specific, limited
period of time, and preferably do not become incorporated into the
walls of the lumen by tissue ingrowth or encapsulation. Temporary
stents may advantageously be eliminated from body lumens after a
predetermined, clinically appropriate period of time, for example,
after the traumatized tissues of the lumen have healed and a stent
is no longer needed to maintain the patency of the lumen. For
example, temporary stents can be used as substitutes for
in-dwelling catheters for applications in the treatment of
prostatic obstruction or other urethral stricture diseases. Another
indication for temporary stents in a body lumen is after energy
ablation, such as laser or thermal ablation, or irradiation of
prostatic tissue, in order to control post-operative acute urinary
retention or other body fluid retention.
[0004] It is known in the art to make both permanent and temporary
stents from various conventional, biocompatible metals. However,
there are several disadvantages that may be associated with the use
of metal stents. For example, it is known that the metal stents may
become encrusted, encapsulated, epithelialized or ingrown with body
tissue. The stents are known to migrate on occasion from their
initial insertion location. Such stents are known to cause
irritation to the surrounding tissues in a lumen. Also, since
metals are typically much harder and stiffer than the surrounding
tissues in a lumen, this may result in an anatomical or
physiological mismatch, thereby damaging tissue or eliciting
unwanted biologic responses. Although permanent metal stents are
designed to be implanted for an indefinite period of time, it is
sometimes necessary to remove permanent metal stents. For example,
if there is a biological response requiring surgical intervention,
often the stent must be removed through a secondary procedure. If
the metal stent is a temporary stent, it will also have to be
removed after a clinically appropriate period of time. Regardless
of whether the metal stent is categorized as permanent or
temporary, if the stent has been encapsulated, epithelialized,
etc., the surgical removal of the stent will resultingly cause
undesirable pain and discomfort to the patient and possibly
additional trauma to the lumen tissue. In addition to the pain and
discomfort, the patient must be subjected to an additional time
consuming and complicated surgical procedure with the attendant
risks of surgery, in order to remove the metal stent.
[0005] Similar complications and problems, as in the case of metal
stents, may well result when using permanent stents made from
non-absorbable biocompatible polymer or polymer-composites although
these materials may offer certain benefits such as reduction in
stiffness.
[0006] It is known to use bioabsorbable and biodegradable materials
for manufacturing temporary stents. The conventional bioabsorbable
or bioresorbable materials from which such stents are made are
selected to absorb or degrade over time, thereby eliminating the
need for subsequent surgical procedures to remove the stent from
the body lumen. In addition to the advantages attendant with not
having to surgically remove such stents, it is known that
bioabsorbable and biodegradable materials tend to have excellent
biocompatibility characteristics, especially in comparison to most
conventionally used biocompatible metals in certain sensitive
patients. Another advantage of stents made from bioabsorbable and
biodegradable materials is that the mechanical properties can be
designed to substantially eliminate or reduce the stiffness and
hardness that is often associated with metal stents, which can
contribute to the propensity of a stent to damage a vessel or
lumen.
[0007] However, there are disadvantages and limitations known to be
associated with the use of bioabsorbable or biodegradable stents.
The limitations arise from the characteristics of the materials
from which such stents are made. One of the problems associated
with the current stents is that the materials break down too
quickly. This improper breakdown or degradation of a stent into
large, rigid fragments in the interior of a lumen, such as the
urethra, may cause obstruction to normal flow, such as voiding,
thereby interfering with the primary purpose of the stent in
providing lumen patency. Alternatively, they take a long time to
breakdown and stay in the target lumen for a considerable period of
time after their therapeutic use has been accomplished. There is
thus a long-term risk associated with these materials to form
stones when uretheral stents made from longer degrading
biodegradable polymers.
[0008] Accordingly, there is a need in this art for novel,
temporary stents, wherein the stents remain functional in a body
lumen for the duration of a prescribed, clinically appropriate
period of time to accomplish the appropriate therapeutical purpose,
and, then soften and are removable as an elongated string-like
member without producing fragments, which may cause irritation,
obstruction, pain or discomfort to the patient, and without the
need for a surgical procedure.
[0009] In a preferred embodiment of the present invention, the
temporary stent readily passes out of the body, or is removed as, a
limp, flexible string-like member, and irritation, obstruction,
pain or discomfort to the patient is either eliminated, or if
present, is minimal.
SUMMARY OF THE INVENTION
[0010] It is an object of the present invention to provide a stent
for insertion into a body lumen which is manufactured from a
flexible filament member, such as a suture, and then coated with a
biodegradable or bioabsorbale polymer such that the member is
formed into a relatively rigid stent, and when in the body, softens
back into a flexible filament member which is easily passed or
removed from the body lumen after a specific therapeutic period of
time.
[0011] Therefore, an implantable stent is disclosed for use in body
lumens, wherein such lumens exist as part of the natural anatomy or
are made surgically. The stent is an elongate, hollow member having
a helical or coiled structure, and in a preferred embodiment has a
helical structure having a plurality of coils. The structure has a
longitudinal axis and a longitudinal passage. The coils have a
pitch. The structure is made from a flexible, limp filament or
fiber, such as a surgical suture, having an exterior polymeric
coating. The polymeric coating is a bioabsorbable or biodegradable
polymer, or blend thereof. At body temperature, the coating is
solid, and of sufficient thickness to effectively cause the
flexible, limp member to be maintained in a substantially rigid,
fixed state as a structure. The rate of degradation or absorption
of the coating in vivo is sufficient to effectively soften or be
removed from the outer surface of the filament within the desired
therapeutic period. This effectively provides that as the coating
degrades, softens or is absorbed in vivo, it loses its mechanical
integrity. This allows the filament to revert to its natural,
flexible limp state, causing the stent structure to effectively
collapse, and the filament may be removed or eliminated from the
lumen.
[0012] Upon in vivo exposure to body fluids, the progressively
degrading and/or absorbing coating causes the stent to soften and
collapse into a flexible filament that can readily pass out of the
body lumen, either by manipulation or through natural expulsion
with body fluids, thereby minimizing the possibility of causing
obstruction, pain or discomfort.
[0013] Yet another aspect of the present invention is the
above-described stent made from a fiber which is radio-opaque.
[0014] Yet another aspect of the present invention is a method of
using the stents of the present invention in a surgical procedure
to maintain the patency of a body lumen. A stent of the present
invention is provided. The stent is an elongate, hollow member and
in a preferred embodiment has a helical structure having a
plurality of coils. The member has a longitudinal axis. The coils
have a pitch. The structure is made from a flexible, limp filament
or a fiber, having an outer surface and an exterior polymeric
coating. The stent is inserted into a body lumen. The exposure to
in vivo body fluids causes the exterior coating to absorb and/or
degrade and soften, thereby causing the stent structure to collapse
and return to a limp, flexible filament that can then be either
eliminated by the passage of body fluids or manually removed.
[0015] These and other aspects of the present invention will become
more apparent from the following description and examples, and
accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0016] FIG. 1 is a perspective view of a preferred embodiment of a
stent device of the present invention mounted to the distal end of
an applicator instrument.
[0017] FIG. 2 is a perspective view of the stent and applicator of
FIG. 1, prior to loading the stent onto the applicator
instrument.
[0018] FIG. 3 is a side view of a stent device of the present
invention, having a helical configuration.
[0019] FIG. 4 is a cross-sectional view of the fiber used to make
the stent of FIG. 3 taken along View Line 4-4 illustrating a
circular cross-section.
[0020] FIG. 5 is a side view of the stent and applicator device of
FIG. 1, where the device is shown in the ready position, prior to
application.
[0021] FIG. 6 is a side view of the stent and applicator device of
FIG. 5, illustrating the position of the stent relative to the
applicator when the stent is partially deployed by engaging the
applicator trigger.
[0022] FIG. 7 illustrates the relative positions of the stent to
the applicator of FIG. 6 when the stent is fully deployed by fully
engaging the applicator trigger.
[0023] FIG. 8 illustrates the stent of the present invention fully
deployed in the urethra and prostate of a patient, providing for a
patent lumen.
[0024] FIG. 9 illustrates a stent of the present invention emplaced
in the urethra of a patient after the coating has degraded, been
absorbed or otherwise broken down or softened; showing the stent
being removed from the body as an elongated, soft, flexible
filament.
[0025] FIG. 10 is a schematic of a mandrel used to manufacture
stents in Example 3.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0026] Referring to FIGS. 1-9, a preferred embodiment of a stent of
the present invention is illustrated. As seen in FIG. 3, the stent
10 is seen to be a helical structure having a series of connected
coils 20. The coils are made from filament 100. The term filament
as used herein is defined to include not only filaments but fibers
as well, and is used interchangeably with the term fiber. It is
preferred that filament 100 be a continuous filament, however, it
is possible to make stent 10 from two or more sections of filament
which are subsequently connected or hinged together. As seen in
FIG. 4, the filament 100 is seen to have inner flexible member 110
and outer coating 130. The inner flexible member 110 is seen to
have outer surface 115. Covering the outer surface 115 of flexible
member 110 is the outer coating 130. Outer coating 130 is seen to
have inner surface 135 and exterior surface 140. Preferably, inner
surface 135 is in contact with, and affixed to, the outer surface
115. The stent is seen to have a longitudinal axis 70, and internal
passageway 11. The stent 10 is seen to have a first distal section
30 of coils 20 connected to a second section 50 of coils 20,
wherein the sections 30 and 50 are connected by hinged connecting
fiber 60. The distal section 30 of coils adjacent to hinged
connecting fiber 60 forms an anchoring section which is inserted
distal to the external sphincter. The proximal section 50 of the
stent 10 is maintained within the prostatic urethra. Proximal
section 50 is seen to have coils 20 having diameter 24, and also
has passageway 51. The distal section 30 of stent 10 has coils 20
having a diameter 22. Distal section 30 also has a passageway 31.
Passage ways 31 and 51 are in communication to form passageway 11
of stent 10. As seen in FIG. 4, one preferred embodiment of the
stent 10 of the present invention has a filament 100 having a
circular cross-sectional configuration. The filament 100 may have
various configurations depending upon the application including
round, square, polygonal, curved, oval, and combinations thereof
and equivalents thereof. Those skilled in the art will appreciate
that certain cross-sectional configurations will provide different
advantages in the stent. For example, the advantages of fiber of
the present invention having a round cross-section include ease of
the stent manufacturing process due to a possible on-line, one-step
transition from the fiber to the stent in future manufacturing
processes, flexibility during the stent deployment by being able to
tailor the length of the stent during a surgical procedure to fit a
particular patient's anatomy, and the use of commercially available
filaments such as sutures.
[0027] The stent 10 is preferably manufactured from a flexible,
polymeric filament 100 having a desired cross-sectional
configuration. The length and overall diameter of the stent 10 will
depend upon a number of factors including the anatomy of the
patient, the size of the anatomy and the type of surgical procedure
which has effected the urethral lumen. For example, the overall
length of a stent 10 useful in the practice of the present
invention will be sufficient to effectively maintain the lumen
passage open. Typically the length for urethral applications in and
adult male, the length will be about 10 mm to about 200 mm, more
typically about 20 mm to about 100 mm, and preferably about 40 mm
to about 80 mm. The diameter of a stent 10 of the present invention
will be sufficient to effectively maintain patency of the lumen.
For prostatic urethral applications, where the stent has two
sections having different diameters, typically the diameter in the
prostatic urethra will typically be about 2 mm to about 25 mm, more
typically about 4 mm to about 15 mm, and preferably about 6 mm to
about 10 mm. The diameter of the section used to anchor distal to
the external sphincter will be about 2 mm to about 25 mm, more
typically about 4 mm to about 15 mm, and preferably about 6 mm to
about 10 mm. The major cross-sectional dimension of a fiber used to
manufacture a stent of the present invention will be sufficient to
provide effective support and flexibility. Typically, when
utilizing a circular cross-section, the diameter for urethral
applications will be about 0.1 mm to about 4 mm, more typically
about 0.5 mm to about 3 mm, and preferably about 1 mm to about 2
mm. The pitch, length, diameter and fiber diameter of the stents of
the present invention will be sufficient to effectively provide
sufficient support in response to radial stress of the urethral
vessel walls, while providing for ease of insertion and stability
while inserted in the urethral lumen, as well as desired
flexibility and lumen patency. The pitch of the stent is defined to
be the number of coils per unit length. In this patent application
specification, for this example, pitch is defined as the number of
coils per centimeter of stent length. Typically, for urethral
applications, the pitch will be about 2.5 to about 100, more
typically about 3 to about 20, and preferably about 5 to about 10.
Although it is preferred for urethral applications that there be no
space between adjacent coils, the stents of the present invention
may have spaces between adjacent coils.
[0028] The flexible members 110 coated with coatings 130 to form
filaments 100 of the present invention will preferably be selected
to have sufficient flexibility and softness and limpness to
effectively provide for a stent that will collapse and be easily
removed from a body lumen. The materials useful for the flexible
member include flexible, limp monofilament and braided string-like
members. It is particularly preferred to use conventional
nonabsorbable sutures, such as monofilament or braided
polypropylene, silk, polyester, nylon and the like and equivalents
thereof. The flexible members may also be conventional absorbable
sutures, monofilament or braided, including 95/5 lactide/glycolide,
and polydioxanone, and the like. The flexible member 110 may also
be made from yarn type materials made from biocompatible fibers
that are "spun" together to form the yarn.
[0029] The outer coatings useful for the stents and filaments of
the present invention will be conventional biodegradable or
bioabsorbable polymers, and blends thereof, including polymers made
from monomers selected from the group consisting of lactide,
glycolide, para-dioxanone, caprolactone, and trimethylene
carbonate, caprolactone, blends thereof and copolymers thereof. The
effect of the degradation or absorption of the polymeric coating is
to convert the filament back into a soft, flexible member after a
predetermined time period, such that the stent effectively
collapses, and the flexible member can then be easily removed or
passed from the lumen. In a flow environment, the progressively
degrading stent can readily pass through the body or be removed
from the lumen without causing obstruction. The types of polymeric
coatings that can advantageously provide stiffness to form a
filament 100 include polymers with glass transition temperatures
above room temperature and preferably above 55.degree. C., and most
preferably above about 120.degree. C. These materials may be
amorphous, that is, not display crystallinity. Polymers that have
glass transition temperatures that are low, especially below room
temperature, will generally require some crystallinity to provide
the dimensional stability and stiffness to function in the present
application. These can be described as semicrystalline. Regarding
water soluble polymers for the coating, there are two general
classes of water soluble polymers: ionic and non-ionic. In general
of use are polyacrylamides, polyacrylic acid polymers, polyethers
(especially the polyethylene glycols or polyethylene oxides), vinyl
polymers such as some polyvinyl alcohols and some poly(N-vinyl
pyrrolidone)s. Certain polysaccharide gums may also be useful;
certain hydroxy celluloses, such as hydroxy methyl cellulose or
certain hydroxy isopropyl cellulose are also useful.
[0030] One can control the dissolution process by material
selection. Altering molecular weight of the water soluble resin
also provides a means of control.
[0031] One can control the dissolution process by material
selection. Altering molecular weight of the water soluble resin
also provides a means of control.
[0032] Utilization of polymer blending is particularly advantageous
to achieve the necessary rates of dissolution. Polyamide (nylon)
may be used as a component to advantage because it can provide
mechanical strength, absorbs some water, etc.
[0033] A possible preferred blend component is polyethylene glycol
(PEG or polyethylene oxide, PEO), especially those higher molecular
weight resins that are semicrystalline. The melting point of PEG is
about 60.degree. C., which is high enough to meet requirements of a
coating useful in the present invention. Optionally, the PEO may be
blended with nylon. In addition, biodegradable polymers made from
poly glycolide/lactide copolymers, polycaprolactone, and the like
may be used for the outer coating of the filament 100. In addition,
polyoxaesters can be utilized which are water soluble and degrade
by hydrolysis. Other suitable polymers are found in U.S. Pat. No.
5,980,551, which is incorporated by reference.
[0034] A stent must be designed to withstand radial stresses in
order to perform its function of maintaining a passage through a
lumen open. The mechanical capability of the stents of the present
invention to withstand radial stresses when the stent is emplaced
in the body lumen is provided primarily by the
biodegradable/bioabsorbable material in the outer coating. The
strength and stiffness and thickness of this material in the outer
coating is sufficient to be effectively withstand the loads
necessary to keep the stent functional. As the coating degrades and
breaks down, it will have a sufficient thickness of properly
selected biodegradable material to effectively be able to withstand
the load necessary for the time period required to keep the lumen
patent. In essence then, the coating can be designed to fulfill the
mechanical requirements of keeping the body lumen patent or open
for the specific therapeutic time period.
[0035] After the coating has degraded/absorbed and effectively been
removed from the stent structure by body fluids, the remaining
filament returns to its soft, pliable, fibrillar state as a
flexible member. The remaining soft filament is readily excreted or
removed from the lumen.
[0036] The coated filaments of the present invention may be made by
conventional processes including co-extrusion, melt coating,
solution coating or powder coating followed by spreading the
coating by melting, etc., and the like. For example, when using a
coating process, the inner flexible member can be a mono-filament
extruded material or can be made from a multi-filament braid. The
outer coating can be added on top of the flexible member either by
melt coating or solution coating by passing the inner core through
a bath, through coating rollers, brushes, spraying and/or a
die.
[0037] In another embodiment of the present invention, the polymers
and blends that are used to form the coating can be used as a drug
delivery matrix. To form this matrix, the coating material would be
mixed with a therapeutic agent. The variety of different
therapeutic agents that can be used in conjunction with the
polymers of the present invention is vast. In general, therapeutic
agents which may be administered via the pharmaceutical
compositions of the invention include, without limitation:
anti-infectives such as antibiotics and anti-viral agents;
analgesics and analgesic combinations; anti-inflammatory agents;
hormones such as steroids; bone regenerating growth factors; and
naturally derived or genetically engineered proteins,
polysaccharides, glycoproteins, or lipoproteins.
[0038] Matrix formulations may be formulated by mixing one or more
therapeutic agents with the polymer. The therapeutic agent, may be
present as a liquid, a finely divided solid, or any other
appropriate physical form. Typically, but optionally, the matrix
will include one or more additives, such as diluents, carriers,
excipients, stabilizers or the like.
[0039] The amount of therapeutic agent will depend on the
particular drug being employed and medical condition being treated.
Typically, the amount of drug represents about 0.001 percent to
about 70 percent, more typically about 0.001 percent to about 50
percent, most typically about 0.001 percent to about 20 percent by
weight of the matrix. The quantity and type of polymer incorporated
into the drug delivery matrix will vary depending on the release
profile desired and the amount of drug employed.
[0040] Upon contact with body fluids, the polymer coating undergoes
gradual degradation (mainly through hydrolysis) or absorption with
concomitant release of the dispersed drug for a sustained or
extended period. This can result in prolonged delivery (over, say 1
to 5,000 hours, preferably 2 to 800 hours) of effective amounts
(say, 0.0001 mg/kg/hour to 10 mg/kg/hour) of the drug. This dosage
form can be administered as is necessary depending on the subject
being treated, the severity of the affliction, the judgment of the
prescribing physician, and the like. Following this or similar
procedures, those skilled in the art will be able to prepare a
variety of formulations.
[0041] The stents 10 of the present invention when made from the
coated filament 100 may be manufactured in the following manner
using a winding process. A filament 100 is wound about a mandrel by
heating the filament 100 and then coiling it around the mandrel.
The assembly of the mandrel and the coil are annealed under
constraint and then the mandrel is removed. The pitch and diameter
of the coils are selected to provide the desired size and shape of
stent. If desired, the filament 100 may be wound about the mandrel
without heat, for example immediately upon entering a coating bath
or melt bath, or the uncoated flexible member 110 can be wound
about a mandrel, and then the coating can be applied in a
conventional manner, and cured as necessary.
[0042] The stents of the present invention may be utilized in the
following manner in urethral stent placement procedures as
illustrated in FIGS. 1, 2, 5, 6, 7 and 8. Initially a stent 10 is
placed upon the distal end of an applicator instrument 200.
Instrument 200 is seen to have handle 250 having grip 255. At the
top 257 of the handle 250 is mounted the shaft retention member
290. Retention member 290 is seen to have longitudinal passageway
292, front 295 and back 296. The mounting tube 240 is seen to have
distal end 242 and proximal end 244. Mounting tube 240 is seen to
have passage 248. The proximal end 244 of tube 240 is seen to be
mounted in passage way 292 such that the inner passageway 248 is in
communication with passageway 292. Slidably mounted in passageway
248 is the applicator tube 220. Tube 220 has distal end 222,
proximal end 224, and passageway 226. Mounted to the proximal end
224 of tube 220 is the mounting block 300, which is affixed to end
224 by pin 309. Mounted to the bottom of block 300 is rack gear
member 330 having gear teeth 335. Contained in handle 250 is the
cavity 350 for receiving pinion gear member 270, having teeth 275.
Pinion gear member 270 is pivotally mounted in cavity 350 by pivot
pins 265. Teeth 275 mesh with and are engaged by teeth 335.
Extending out from pinion gear member 270 on the opposite side of
pins 265 is the actuation trigger 280. Actuation of trigger 280
will move tube 220 proximally and distally with respect to tube
240. Actuating the trigger 280 will allow the stent 10 to be
released from the tubes 220 and 240.
[0043] The stent and distal end of the instrument 200 are inserted
into the urethra 410 through the meatus 400 of the patient's penis
as seen in FIGS. 8 and 9. The distal end of the instrument 200 and
the stent 10 are manipulated through the urethra 410 such that the
prostatic section of the stent is located within the prostatic
urethra 411 and the distal end of the stent is distal to the
external sphincter 430, thereby providing an open passage for urine
from bladder 450 through the lumen of the urethra. Then, the
application instrument 200 is withdrawn from the urethra 410 by
engaging trigger 260 and pulling distally on the instrument,
thereby completing the procedure and providing for an implanted
stent 10 which allows for patency of the urethral lumen 410. As
seen in FIG. 9, the stent 10 after having been in place for the
appropriate period of time has been converted into a state wherein
it is substantially a soft, flexible filament, and is readily
passed from the urethra 410 out of the patient's body with the
urine flow, or is manually pulled out of the lumen. It will be
appreciated by those skilled in the art that placement for other
types of body lumens could be done in a similar manner, with
modification as required by the unique characteristics of the lumen
or of the surgical emplacement procedure.
[0044] The following examples are illustrative of the principles
and practice of the present invention, although not limited
thereto.
EXAMPLE 1
[0045] Manufacture of Filament Having Absorbable Coating by
Extrusion Coating Process.
[0046] A polydioxanone homopolymer was added to a nitrogen purged
hopper of a 3/4" vertical single screw extruder with a 24:1 L:D
standard screw. The temperature profile of the extruder was
250.degree., 260.degree., 270.degree. and 275.degree. F. from rear
zone to die. The screw speed was 6.5 RPM and the adapt pressure was
1345 psi. A B&H 25 cross head was employed with a 20 mil
diameter guider (pressure tip) and a 48 mil diameter die. A spool
of Vicryl brand suture, available from Ethicon, Inc., Somerville,
N.J., with 18 mil diameter on a pay-off was guided through the
guider inside the cross head, then coated by polydioxanone molt,
chilled in a water trough, dried by a air wiper, took off and
spooled sequentially. The temperature of the water trough was
8.degree. C. The take-off speed was 2.1 M/min. The fiber with the
O.D. of 44 mil was made and stored in nitrogen environment.
EXAMPLE 2
[0047] Manufacture of Stent Using the Coated Filament
[0048] The coated suture of Example 1 was tied so that it created a
small loop through the first hole C of the mandrel (see FIG. 10).
Two metal posts (.phi.2.times.15 mm length) are inserted into the
holes A and B.
[0049] A post was located at hole A and B. Clamp the C-side end of
the mandrel to a winding motor. The 5-foot long fiber was cut from
the spool and passed through the loop. The two free ends were held
together and the folded fiber was stretched loosely so that the
loop was positioned to be in the approximate center of the fiber.
The fiber was loosely hold by two figures as a guide to make sure
that the coils are packed closely together. A winder was run
between 20-30 RPM for the length of the Prostatic Section.
[0050] The coiling start from point C. Once the first post (B) was
reached, the fiber was then bent over the post at an angle toward
the distal section. Winding 180.degree. more to form the connector,
the fiber reached toward the second post (A), and then past it. The
fiber is pulled back to a perpendicular position to the mandrel and
the distal loop is then coiled. A wire tie was used to secure the
fiber onto the mandrel. The assembly was stored under vacuum for 48
hours to allow it to dry prior to annealing.
[0051] Prior to annealing, the posts were removed from the mandrel.
The entire assembly was hanged in annealing over and annealed at
80.degree. C. for 10 hours. The stent was removed from the mandrel
and stored in nitrogen box.
EXAMPLE 3
[0052] A male patient is appropriately anesthetized and undergoes a
prostrate thermal ablation procedure using conventional laser
treatment devices. After successful completion of the surgical
procedure, a stent 10 of the present invention is inserted into the
patient's urethra and bladder in the following manner using an
applicator 200. The surgeon trims the stent to size. The stent is
placed at the end of the applicator. A conventional scope is
inserted into the lumen of the applicator. The stent and applicator
are lubricated with a water soluble medical grade lubricant. A
fluid reservoir is attached to the applier as in any standard
cystoscopy procedure. The stent is placed in the prostatic urethra
under direct visualization using a scope. Once positioned
correctly, the applier is removed, leaving behind the stent in the
prostatic urethra. In approximately 28 days after implantation, the
outer coating absorbs and or degrades, thereby converting the stent
into a soft, flexible filamentary structure that is removed from
the urinary tract by grasping the end of the filament and pulling
it from the lumen.
[0053] The stents of the present invention provide many advantages
over the stents of the prior art. The advantages include: rigidity
(lumen patency) for a prescribed time; a degradation/absorption
softening mechanism, whereby the stent softens into a readily
passable/removable filament; biocompatibility; means to prevent
migration; means to non-invasively monitor the stent and its
position by X-ray. etc.
[0054] Although this invention has been shown and described with
respect to detailed embodiments thereof, it will be understood by
those skilled in the art that various changes in form and detail
may be made without departing from the spirit and scope of the
claimed invention.
* * * * *