U.S. patent application number 10/102336 was filed with the patent office on 2002-10-03 for plasma dielectric etch process using a long fluorocarbon.
Invention is credited to Ding, Jian, Tang, Betty.
Application Number | 20020142598 10/102336 |
Document ID | / |
Family ID | 22346258 |
Filed Date | 2002-10-03 |
United States Patent
Application |
20020142598 |
Kind Code |
A1 |
Tang, Betty ; et
al. |
October 3, 2002 |
Plasma dielectric etch process using a long fluorocarbon
Abstract
A process for etching a dielectric layer with an underlying stop
layer, particularly in a counterbore process for a dual-damascene
interconnect structure. The substrate is formed with a lower stop
layer, a lower dielectric layer, an upper stop layer, and an upper
dielectric layer. The initial deep via etch includes at least two
substeps. A first substep includes a non-selective etch through the
upper stop layer followed by a second substep of selectively
etching through the lower dielectric layer and stopping on the
lower stop layer. The first substep may be preceded by yet another
substep including a selective etch part ways through the upper
dielectric layer. For the oxide/nitride compositions, the selective
etch is based on a fluorocarbon and argon chemistry, preferably
with a lean etchant combined with a richer polymer former, and the
non-selective etch includes a fluorocarbon or hydrofluorocarbon,
argon and an oxygen-containing gas, such as CO.
Inventors: |
Tang, Betty; (San Jose,
CA) ; Ding, Jian; (San Jose, CA) |
Correspondence
Address: |
Applied Materials, Inc.
Patent/Legal Department
P.O. Box 450A
Santa Clara
CA
95052
US
|
Family ID: |
22346258 |
Appl. No.: |
10/102336 |
Filed: |
March 20, 2002 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10102336 |
Mar 20, 2002 |
|
|
|
09728294 |
Dec 1, 2000 |
|
|
|
6399511 |
|
|
|
|
09728294 |
Dec 1, 2000 |
|
|
|
09112864 |
Jul 9, 1998 |
|
|
|
6211092 |
|
|
|
|
Current U.S.
Class: |
438/689 ;
257/E21.252; 257/E21.579 |
Current CPC
Class: |
H01L 21/31116 20130101;
H01L 21/76807 20130101 |
Class at
Publication: |
438/689 |
International
Class: |
H01L 021/302; H01L
021/461 |
Claims
What is claimed is:
1. A multi-level dielectric etch method, comprising the steps of:
placing into a plasma reactor a substrate containing a layered
structure formed over a substrate and comprising sequentially, from
a bottom thereof, a first stop layer, a first dielectric layer, a
second stop layer, a second dielectric layer, and a first photomask
patterned with at least one first aperture; a first flowing step of
flowing a first gas mixture into said reactor and exciting it into
a first plasma, said first plasma being capable of etching both
said second dielectric layer and said second stop layer through
said at least one first aperture; continuing said first step at
least until said second stop layer is etched through; and a second
flowing step, performed without removing said substrate from said
reactor after said flowing step, of flowing a second gas mixture
into said reactor and exciting it into a second plasma, said second
plasma etching said first dielectric layer through said at least
one first aperture selectively to said first stop layer; wherein at
least one of said first and second gas mixtures comprise a
single-hydrogen fluorocarbon gas and multi-carbon fluorocarbon
gas.
2. The multi-level dielectric etch method of claim 1, wherein said
single-hydrogen gas has as F/C ratio of 3 or greater.
3. The multi-level dielectric etch method of claim 1, wherein said
multi-carbon gas has an F/C ratio of 3 or less.
4. The multi-level dielectric etch method of claim 2, wherein said
multi-carbon gas has an F/C ratio of 3 or less.
5. The multi-level dielectric etch method of claim 2, wherein said
first gas mixture further comprises CO.
6. An etching method, comprising the step of: providing a substrate
having formed on the surface a sequentially arranged structure
comprising a stop layer, a lower dielectric layer, and an upper
dielectric layer; defining a first photomask over said structure
having a plurality of first apertures extending from a top most
level a bottommost level of said photomask; placing said substrate
defined with said first photomask into a first plasma reactor
substrate and powered by RF power supply; a first step of flowing
gas mixture into said reactor and exciting it into a first plasma,
said first plasma etching said upper dielectric layer through said
first apertures; and a second step, performed without removing said
substrate from said reactor after said first flowing step, of
flowing a second gas mixture into said reactor and exciting it into
a second plasma, said second plasma etching through said lower
dielectric layer selectively to said stop layer until said stop
layer is exposed; wherein at least one of said stop first and
second gas mixtures comprise a first single-hydrogen fluorocarbon
gas and a first multi-carbon fluorocarbon gas.
7. The etching method of claim 6, wherein said single-hydrogen gas
has as F/C ratio of 3 or greater.
8. The etching method of claim 7, wherein said multi-carbon
fluorocarbon gas comprises a fluorocarbon having an F/C ratio of 3
or less.
9. The etching method of claim 6, wherein said first multi-carbon
fluorocarbon gas comprises a fluorocarbon having an F/C ratio of 3
or less.
10. The etching method of claim 9, wherein said fluorocarbon has at
least four carbon atoms.
11. The etching method of claim 6, wherein said first gas mixture
further comprises CO.
12. The etching method of claim 6, further comprising: providing a
second photomask over said substrate to define a plurality of
trenches; and performing a trench etch comprising the steps of a
first trench etch substep of flowing a first trench etch gas
mixture into said reactor and exciting it into a plasma so as to
etch said upper dielectric layer to thereby define trenches, a
first ash step of flowing ashing gas to etch said second photomask,
and a second trench etch substep of flowing a second trench etch
gas mixture into said reactor and exciting it into a plasma so as
to etch said stop layer.
13. The etching method of claim 12, wherein at least one of said
first trench etch gas mixture and second trench etch gas mixtures
comprises a second single-hydrogen fluorocarbon gas and a second
multi-carbon fluorocarbon gas.
14. The etching method of claim 16, wherein said second
multi-carbon fluorocarbon gas comprises a hydrogen-free
fluorocarbon having at least four carbon atoms.
15. A multi-level dielectric etch method, comprising the steps of:
placing into a plasma reactor a substrate containing a layered
structure formed over a substrate and comprising sequentially, from
a bottom thereof, a first stop layer, a first dielectric layer, a
second stop layer, a second dielectric layer, and a first photomask
patterned with at least one first aperture; a first flowing step of
flowing a first gas mixture including a first fluorocarbon into
said reactor and exciting it into a first plasma, said first plasma
being capable of etching both said second dielectric layer and said
second stop layer through said at least one first aperture;
continuing said first step at least until said second stop layer is
etched through; and a second flowing step, performed without
removing said substrate from said reactor after said flowing step,
of flowing a second gas mixture including a hydrogen-free second
fluorocarbon into said reactor and exciting it into a second
plasma, said second plasma etching said first dielectric layer
through said at least one first aperture selectively to said first
stop layer; wherein said second fluorocarbon is more heavily
polymerizing than said first fluorocarbon.
16. The method of claim 15, wherein said first fluorocarbon is a
hydrogen-containing fluorocarbon.
17. The method of claim 16, wherein said second fluorocarbon
contains at least 4 carbon atoms.
18. The method of claim 17, wherein said first fluorocarbon
comprises CHF.sub.3.
19. The method of claim 16, wherein said second fluorocarbon
contains at least 4 carbon atoms.
20. The method of claim 19, wherein said second gas mixture
additionally includes CO.
Description
RELATED APPLICATIONS
[0001] This application is a division of Ser. No. 09/728,294, filed
Dec. 1, 2000, which is a division of Ser. No. 09/112,864, filed
Jul. 9, 1998, now issued as U.S. Pat. 6,211,292. This application
is also related to Ser. No. 09/112,094, filed Jul. 9, 1998.
FIELD OF THE INVENTION
[0002] The invention relates generally to plasma etch processes. In
particular, the invention relates to the highly selective etching
of insulating materials, particularly silicon oxide, forming part
of a complex integrated-circuit structure.
BACKGROUND ART
[0003] The technology of fabricating semiconductor integrated
circuits continues to advance in the number of transistors,
capacitors, or other electronic devices which can be fabricated on
a single integrated circuit chip. This increasing level of
integration is being accomplished in large part by decreasing the
minimum feature sizes. Even as the number of layers in the
integrated circuit continues to increase, advanced processes are
being used which allow for a reduction in the number of processing
steps for a functional layer. However, these advanced processes
often make extraordinary demands upon the chemistry of the etching
process. Dielectric etching has presented some of the most
difficult demands.
[0004] In the past, the common materials for inter-level dielectric
have been based upon silicon. Such materials include silicon
dioxide, silica glass such as BPSG, and related silicon-based oxide
materials that serve as electrical insulators. Recently, interest
has developed in insulating materials with low dielectric constants
(low-k dielectrics), some of which are based upon silicon but
others are based upon carbon.
[0005] Advanced integrated circuits contain multiple wiring layers
separated from the silicon substrate and from each other by
respective dielectric layers. Particularly logic circuitry, such as
microprocessors, require several layers of metallization with
intervening inter-level dielectric layers. Small contact or via
holes need to be etched through each of the dielectric layers. The
contact or via holes are then filled with a conductor, composed
typically of aluminum in the past but more recently composed of
copper. A horizontal wiring layer is formed over one dielectric
layer and then covered by another dielectric layer. The horizontal
wiring and the underlying vias are often referred to as a single
wiring layer. The conventional process not only fills the contact
or via holes but also overfills them to form a thick planar layer
over both the filled holes and the dielectric. Conventionally, a
metal lithographic step then photographically defines a photoresist
layer over the planar metal layer and etches the exposed metal into
a network of conductive interconnects.
[0006] In contrast, a recently developed damascene process
substitutes chemical mechanical polishing for metal etching. A
dual-damascene structure, as illustrated in sectioned orthographic
view in FIG. 1, has been proposed for advanced chips which avoids
the metal etching and combines the metallization of the via and
horizontal interconnect. There are two general types of
dual-damascene processes, self-aligned and counterbore. The more
conventional self-aligned dual-damascene process will be described
first.
[0007] Over a substrate 10 is formed a thin lower stop layer 12
having a minimal thick of, for example 100 nm, a lower dielectric
layer 14, having a thickness of, for example, 1 .mu.m or somewhat
less, and a thin upper stop layer 16. The stop layers 12, 16 have
compositions relative to the dielectric material such that a
carefully chosen etch process that is selective to the material of
the stop layer etches through the overlying dielectric but stops on
the stop layer. Although copper metallization and low-k dielectric
would more fully utilize the advantage of the dual-damascene
structure, the present description will use silicon dioxide as the
principal inter-level dielectric. Silicon dioxide is preferably
grown by plasma-enhanced chemical vapor deposition (PECVD) using
tetraethylorthosilicate (TEOS) as the main precursor gas. Silicon
nitride (Si.sub.3N.sub.4) is a common material for stop layers when
the dielectric is an oxide. Silicon nitride is preferably also
grown by PECVD to reduce the thermal budget. Its general
composition is given by SiN.sub.x, where x may vary somewhat over a
range of, for example 1 to 1.5. A dielectric photolithographic step
is performed to create circular holes 18 in the upper stop layer
16. The diameters of the circular holes 18 determine the diameters
of the via holes, which usually represent the smallest dimension
defined in the dielectric etch. The smallest defined lateral
dimension in a level is often referred to as the critical dimension
(CD). The dual-damascene structure can be used both at the power
level, which is the uppermost metal layer, and at the signal
levels, for example, metal-1 and metal-2 levels for a moderately
complex logic chip. The power level typically has a larger via
size, for example, 0.6 .mu.m, while the signal levels typically
have smaller via sizes, for example, 0.3 .mu.m. This diameter is
being reduced to 0.25 .mu.m and to yet lower sizes in advanced
structures. Total dielectric thickness also varies between the
power and signal levels. The etching in this photolithographic step
is preferably selective to the principal dielectric material so
that at this point the holes 18 do not significantly extend into
the lower dielectric layer 14.
[0008] Then, in the continuation of the self-aligned dual-damascene
process, an upper dielectric layer 20 is deposited to a thickness
of, for example, 1.4 .mu.m over the partially etched structure,
including deposition into the etched depressions in the patterned
nitride layer 16. A photoresist mask is deposited and defined into
the shape of a trench 22 having a width of, for example, 1.2 .mu.m
and a much longer length. A self-aligned dual-damascene dielectric
etch is then performed both to form the trench 22 in the upper
oxide layer 20 and to extend the lower via holes 18 through the
lower oxide layer 14 and down to the lower stop layer 12. The upper
nitride stop layer 16 serves both as a stop for forming the trench
22 and as a hard mask for etching the via hole 18. The combined
etch must not significantly etch the upper stop layer 16 at the
floor 24 of the trench 22, and it must stop at the lower stop layer
12 at the bottom 26 of the via holes 18. In a further step, not
illustrated here because it is generally considered to be
non-critical, a further non-selective etch removes the portion of
the lower stop layer 12 at the bottom of the via hole 18 so as to
expose the substrate 10 to contacting when metal is filled into the
trench 22 and via hole 18.
[0009] In the self-aligned dual-damascene etch process, the
selectivity of the oxide etch to nitride or other stop material in
both the relatively open trench floor 24 and particularly at the
shoulders 28 of the via holes 18 is especially crucial since these
areas are exposed to the etching plasma while the via holes 18 are
being etched. Generally, the shoulders 28 etch faster than the
trench floor 24 because of their exposed geometry. The upper
nitride layer 16 and its shoulder 28 are further exposed during a
long over-etch of the lower oxide layer 14, typically greater than
100% to reliably open the via in the presence of process and other
non-uniformities. Such selectivity can be achieved by use of a
highly polymerizing chemistry which deposits a protective polymeric
coating on the non-oxide surfaces and vertical oxide surfaces but
generally not on the horizontal oxide surfaces. However, the
extensive polymerization impacts the etching of the narrow and deep
via holes 18 and may cause etch stop. Etch stop occurs when the
side walls are so heavily polymerized that the polymer closes the
hole and prevents further etching of the bottom of the hole. Of
course, etch stop in the via holes 18 must be avoided. As a result,
the process window for the self-aligned process is often limited by
the conflicting requirements of the oxide etch to maintain the
nitride shoulders 28 while continuing to open the oxide in the via
hole 18. The etch must maintain the bottom critical dimension (CD)
associated with the via hole 18 in order to maintain tight control
of the via resistance. The top critical dimension associated with
the trench 22 is less critical, but depending upon the pitch of via
holes 18, it may determine the margin for shorting between vias
associated with different trenches. The trench profile needs to be
vertical to maintain consistent line widths.
[0010] Following the etching of the dual-damascene structure by
either the self-aligned or counterbore process, a single
metallization operation fills both the via holes 18 and the trench
22. The metallization operation may require that the trench 22 and
via hole 18 be coated with barrier layers and wetting layers, as
has become well known in metallization of small features in
advanced integrated circuits. The metal deposition, usually
performed at least partially by physical vapor deposition, is
continued to the extent that the metal completely fills the via
holes 18 and trench 22 and somewhat overlies the top 30 of the
upper oxide layer 20. Chemical mechanical polishing is then
performed, and because silica is much harder than metal the
polishing stops when it encounters the upper oxide layer 20.
Thereby, the metallization is restricted on the top of the wafer to
the trench 22. The metallization may either serve both as a
horizontal interconnect between two or more locations in the
substrate through the via holes 18 and as an inter-level vertical
interconnect in the via holes 18. The dual-damascene process is
particularly useful for copper metallization because no copper
etching is required.
[0011] In the self-aligned dual-damascene process, the lower stop
layer 12 is photolithographically patterned before the upper
dielectric layer 20 is deposited, and the trench and the via are
etched in a single process step. Such a process requires balancing
nitride selectivity against etch stop margin, and achieving a wide
process window for an acceptable process poses a great challenge in
developing an oxide etch recipe.
[0012] An alternative dual-damascene process, referred to as a
counterbore dual-damascene process for reasons which will become
apparent, separates the via and trench etch steps. Thereby, the
nitride shoulder need not be exposed for such long times to the
oxide etch so that the balance between selectivity and etch stop is
eased. The counterbore process is thus advantageous for smaller via
sizes.
[0013] The counterbore process is illustrated in the flow diagram
of FIG. 2 with reference to the cross-sectional structures of FIGS.
3-8, which show the sequential development of the dual-damascene
structure. In step 40, an unpatterned planar dual-damascene
structure is grown comprising, as illustrated in the
cross-sectional view of FIG. 3, the substrate 10, the lower stop
layer 12, the lower dielectric layer 14, the upper stop layer 16,
and the upper dielectric layer 20. No photolithography is performed
between the layers 12, 14, 16, and 20, and their compositions may
be such to allow their growth by chemical vapor deposition (CVD) in
a single plasma reaction chamber by varying between the layers the
composition of the feed gas and the operating conditions.
[0014] In step 42, a first photoresist layer 44 is deposited and
photographically patterned to form mask apertures 46 corresponding
to the via or contact holes, only one of which is illustrated. It
will be assumed that the underlying substrate 10 includes a metal
surface in the area of the hole so it is properly called a via
hole. Although the metal is preferably copper, the examples of the
invention use an aluminum metallization. The composition of the
metallization has very little effect upon the dielectric etch.
[0015] In a first etch step 48, an extended via hole 50, as
illustrated in FIG. 4, is etched through the upper dielectric layer
20, the upper stop layer 16, and the lower dielectric layer 14 down
to the lower stop layer 12. The etch chemistry is chosen to be
selective to the material of the lower stop layer 12 so that the
etch stops at the top surface 52 of the bottom stop layer 12.
[0016] In an unillustrated step, the first photoresist layer 44 is
stripped. In step 54, a second photoresist layer 56, as illustrated
in FIG. 5, is deposited and photographically patterned to form a
mask aperture 58 corresponding to the trench. In a second etch step
60, a trench 62, illustrated in FIG. 6, is etched through the upper
dielectric layer 20 down to the top surface 64 of the upper stop
layer 16 without significantly eroding the top surface 52 of the
bottom stop layer 12. The depth of the extended via hole 50 is
thereby reduced to form a via hole 50'.
[0017] In a third etch step 66, the exposed portion of lower stop
layer 12 at the bottom of the via hole 50' is etched, as
illustrated in FIG. 7, through the lower stop layer 12 and down to
an upper surface 68 of the substrate 10, which is typically a metal
for a via. Depending upon the compositions of the two stop layers
12, 16, the third etch step 66 may remove portions of the upper
stop layer 16 exposed at the bottom of the trench 62 to form a
shelf 70 in the upper oxide layer 14, but this thin portion is not
critical. In another unillustrated step, performed either before or
after the third etch step 66, the second photoresist layer 56 is
stripped along with any sidewall polymer forming in the dielectric
etch.
[0018] Thereafter, as illustrated in FIG. 8, a metal 72 is filled
into the trench 62 and underlying via hole 50' to contact the upper
surface 68 of the substrate 10. Subsequent chemical mechanical
polishing (CMP) removes any metal overflowing the trench 62. The
metal 72 forms both a horizontal interconnect 74 and a via 76
contacting the underlying layer 10. As mentioned before, the metal
72 may be the conventional aluminum or the more advanced
copper.
[0019] However, the counterbore etch process is very demanding. The
first, via etch 48 of the extended via hole 50 is deep and narrow,
the width usually representing the critical dimension of the
process. The via etch 48 must etch through the upper stop layer 16
but stop on the lower stop layer 12. The deep via etch 48 thus
requires a vertical profile and high selectivity to the bottom stop
layer 12. Not only must the interconnect (trench) etch 60 stop on
the upper stop layer 16, it must not significantly etch the lower
stop layer 12, which is exposed during the entire interconnect
etch. The interconnect etch 60 thus requires a vertical profile and
high selectivity to the upper stop layer 16. If the lower stop
layer 12 is inadvertently etched through during the long over-etch,
an effect called punch through, the underlying metal is sputtered,
and as a result device reliability is severely impacted,
particularly if copper is used as the underlying metallization. All
etch steps, but particularly those etching through the thicker
dielectric layers, should be highly isotropic, producing nearly
vertical side walls. To achieve the vertical profile, the etching
of the stop layers should not significantly side etch the
dielectric layers located above.
[0020] The first, via etch step 48 must selectively etch the upper
stop layer 16 relative to the lower stop layer 12. This can be
accomplished in a single etch step with the choice of significantly
different materials for the two stop layer 12, 16. However, the
choice is limited and not attractive. The growth of the planar
structure of FIG. 3 is preferably performed in a single CVD
reactor, which may be difficult to accomplish for materials of
vastly different chemistries. Also, it is desired to form both stop
layers 12, 16 out of materials having fairly good insulating
properties. Use of conductive metals for either stop layer would
form a grounding plane, thus introducing electrical coupling
between interconnects on the same level. For similar reasons, the
vertical extent of the stop layers formed of only fair insulators
should be kept thin so as to reduce the lateral electrical
conductance. Silicon nitride and related compounds such as some
low-k silicon-based dielectrics have reasonably high resistivities,
can be grown in the same chamber as oxides, and nitride-selective
oxide etches are known, but it is not seen how to form two layers
of such materials with vastly different etching characteristics
while simultaneously maintaining high dielectric-to-stopper
selectivity.
[0021] It is thus desired to find a etching process satisfying
these difficult and conflicting requirements without unduly
complicating and lengthening the dielectric etch step.
SUMMARY OF THE INVENTION
[0022] The invention may be summarized as a plasma etch method,
preferably performed in a single inductively coupled high-density
plasma (HDP) reactor, of etching through a multi-layer dielectric
stack including an intermediate and lower stop layer. The etch
continues through the intermediate stop layer but stops on the
lower stop layer. The etch includes at least two substeps, a
earlier one of which is non-selective to the intermediate stop
layer, a later one being selective to the lower stop layer.
[0023] In a first preferred 2-substep sequence: a first,
non-selective etch extends to below the upper stop layer; and a
second, selective etch extends to and stops on the lower stop
layer. In a second preferred 3-substep sequence: a first, selective
etch on average does not quite reach the upper stop layer; a
second, non-selective etch punches through the upper stop layer;
and a third, selective etch extends to and stops on the lower stop
layer.
[0024] The invention may be applied to a dielectric stack structure
in which the dielectric layers are composed of silicon dioxide or
related silicon oxide materials and the stop layers are composed of
silicon nitride. With these compositions, the stack may be grown in
a single plasma reactor. For a stack of oxide and nitride, the
selective etch may be a polymerizing fluorocarbon reactive ion etch
and the non-selective etch is accomplished by adding an
oxygen-containing gas, such as CO, to the etching gas mixture.
[0025] In a multi-step etching process, preferably only the gas
components are changed between the steps. More preferably, the
principal etching gas remains substantially the same with only the
selective addition of polymer formers and oxygen-containing gases,
thus providing a smoother transition between the steps with no fear
of extinguishing the plasma. The changes in total active gas flow
can be easily kept below 30%.
[0026] The etching process is advantageously performed at a
relatively high pressure in the range of 40 to 150 milliTorr or
more advantageously in the range of 60 to 100 milliTorr in the
presence of diluent gas such as argon having a fraction at least
twice that of the etching gases.
[0027] Preferably, the selective etch uses both a lean
hydrofluorocarbon, such as trifluoromethane (CHF.sub.3), and a
polymer-forming fluorocarbon or hydrofluorocarbon. The strength of
polymerization depends upon the aspect ratio of the feature being
etched and whether the photoresist needs to be protected. The ratio
of trifluoromethane to the polymer former is preferably in the
range of 5 to 20. Preferred polymer formers are hexafluoroethane
(C.sub.2F.sub.6), cyclic octafluorobutane (C.sub.4F.sub.8), and
difluoromethane (CH.sub.2F.sub.2), dependent upon the geometry of
the feature being currently etched.
[0028] A hot silicon surface may be used to scavenge fluorine from
the selective etching gas to provide yet higher selectivity to both
nitride and photoresist.
[0029] Etching in a high-density plasma enhances polymerization to
thereby increase selectivity and cracks CO into elemental oxygen,
which provides better selectivity to photoresist than gaseous
oxygen.
[0030] The invention is particularly applicable to a counterbore
dual-damascene etch having two dielectric layers underlaid with
respective stop layer. This etch process requires an initial very
deep via etch through the upper stop layer and both dielectric
layers down to the lower stop layer.
BRIEF DESCRIPTION OF THE DRAWINGS
[0031] FIG. 1 is an orthographic view of the etched hole required
for a dual-damascene via structure for interconnecting two levels
of metallization.
[0032] FIG. 2 is a process flow diagram for the counterbore
dual-damascene etch of the invention.
[0033] FIGS. 3 through 7 are cross-sectional views of the
sequentially developed structure in the counterbore dual-damascene
etch process of FIG. 2.
[0034] FIG. 8 is a cross-sectional view of the metallization formed
in the dual-damascene etch structure of FIG. 8.
[0035] FIG. 9 is a schematic illustration, partially in
cross-sectional view, of an inductively coupled high-density plasma
reactor on which the invention may be practiced.
[0036] FIG. 10 is a process flow diagram for an inventive 2-substep
form of the via etching step of the counterbore dual-damascene etch
process of FIG. 2.
[0037] FIGS. 11 and 12 are cross-sectional views of the
sequentially developed structure in the 2-substep via etching step
of FIG. 10.
[0038] FIG. 13 is an optical emission profile for monitoring the
endpoint of the etching process of FIG. 10.
[0039] FIG. 14 is a process flow diagram for an inventive 3-substep
form of the via etching step of the counterbore dual-damascene etch
process of FIG. 2.
[0040] FIG. 15 is cross-sectional view of one intermediate
structure in the 3-substep via etch step of FIG. 14.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0041] We have found that the counterbore process can be
effectively applied to a dual-damascene structure by using a
multi-substep etch for the deep via etch step. The process window
is improved by the addition of certain gas species to control
selectivity to the stop layers. In one embodiment of the invention,
the damascene structure incorporates only silicon oxide and silicon
nitride layers, and the deep via etch can include features
associated with a conventional deep contact etch.
[0042] From the view of an integrated process, the counterbore
damascene method helps to maintain consistent via sizes. The
critical dimension at the bottom of the via hole is defined during
the deep via etch, and any misalignment of the trench mask will not
affect the via contact area with the underlying metal. This
insensitivity to misalignment is crucial for via resistance,
especially as the via size shrinks to 0.25 .mu.m and below. In
contrast, the self-aligned damascene process is susceptible to this
misalignment problem, which affects the distribution of the via
resistance.
[0043] An exemplary unpatterned structure, as illustrated in FIG.
3, is tabulated in TABLE 1. This structure was used in an example
to be described later for a 0.3 .mu.m-diameter via.
1 TABLE 1 Thickness Composition (nm) Upper Dielectric Oxide 500
Upper Stopper Nitride 150 Lower Dielectric Oxide 1000 Lower Stopper
Nitride 100
[0044] The oxide is nominally composed of silicon dioxide grown by
a standard plasma-enhanced CVD process using TEOS
(tetraethylorthosilicate) as the principal precursor. The nitride
is composed of silicon nitride, nominally of composition
Si.sub.3N.sub.4, grown by plasma-enhanced CVD. The thermal budget
is improved because plasma-enhanced CVD of nitride can be performed
around 400.degree. C. while thermal CVD requires temperatures of
greater than 700.degree. C. All depositions can thus be performed
in the same plasma reaction chamber which is adapted for the supply
of the different gases and includes hardware compatible with the
two types of deposited materials. Silicon nitride has a relatively
high dielectric constant of 7.5, compared to 3.9 for SiO.sub.2, and
has a low but still significant electrical conductivity. Therefore,
the thickness of the nitride stop layers should be kept low.
[0045] Although all the etching steps of the counterbore process
need to be consistent with the compositions of TABLE 1, the first
etching step 48 to form the extended via hole 50 is the most
demanding. We found that a process for the via etching step
involving two or three substeps performed in an inductively coupled
high-density plasma (HDP) etch reactor successfully achieves the
first, via etching step. Such a reactor provides both the
selectivity and the process flexibility required to satisfy the
conflicting requirements. Such a reactor can also be advantageously
used for the second and third etching steps as well as for the
photoresist stripping. There are other types of high-density plasma
reactors, including remote plasma source (RPS) and
electron-cyclotron resonance (ECR). A high-density plasma may be
defined as a plasma filling the entire space it is in, excluding
plasma sheaths, and having an ionization density of at least
10.sup.11 cm.sup.-3.
[0046] An example of such an inductively coupled HDP etch reactor
is the IPS (inductive plasma source) oxide etch reactor available
from Applied Materials, Inc. of Santa Clara, Calif. and described
by Collins et al. in U.S. patent application, Ser. No. 08/733,544,
filed Oct. 21, 1996. The general reactor structure and some
auxiliary equipment are illustrated in partial cross section in
FIG. 9. A wafer 80 to be processed is supported on a cathode
pedestal 82, which is supplied with RF power from a first RF power
supply 84. A silicon ring 86 surrounds the pedestal 82 and is
controllably heated by an array of heater lamps 88. A grounded
silicon wall 90 surrounds the plasma processing area. A silicon
roof 92 overlies the plasma processing area, and lamps 94 and water
cooling channels 96 control its temperature. The
temperature-controlled silicon ring 86 and to a lesser extent the
silicon roof 92 can be used to scavenge fluorine from the
fluorocarbon or other fluorine-based plasma. Processing gas is
supplied from one or more bottom gas feeds 94 through a bank of
mass flow controllers 96. Alternatively, a top gas feed may be
formed as a small showerhead in the center of the silicon roof 92.
An unillustrated vacuum pumping system connected to a pumping
channel 98 around the lower portion of the chamber maintains the
interior of the chamber at a preselected pressure. A system
controller 100 controls the operation of the reactor and its
auxiliary equipment.
[0047] In the used configuration, the silicon roof 92 is grounded,
but its semiconductor resistivity and thickness are chosen to pass
generally axial RF magnetic fields produced by an inner inductive
coil stack 106 and an outer inductive coil stack 108 powered by
respective RF power supplies 110, 112. Alternatively, a single RF
power supply may be used in conjunction with a selectable power
splitter. Other coil configurations are possible, for example, as
in the TCP reactor having a flat, spiral inductive coil overlying
the roof 92.
[0048] The system controller 100 controls the mass flow controllers
96, the heater lamps 88, 94, the supply of chilled water to the
cooling channels 96, the throttle valve to the vacuum pumps, and
the power supplies 84, 110, 112. All these regulated functions
control the etching chemistry in conformance to a process recipe of
the sort to be described in the examples below. The process recipe
is stored in the controller 100 in magnetic, optical, or
semiconductor memory, as is well known in the art, and the
controller 100 reads the recipe from a recording medium inserted
into it. It is typical for the equipment supplier to provide
recipes on magnetic media such as floppy disks or optical media
such as CDROMs, which are then read into controller 100.
[0049] A principal advantage of the inductively coupled plasma
reactor is that different amounts of power can be supplied to the
inductive coils 106, 108 and to the capacitive pedestal 82. The
inductive power creates a plasma source region located in large
part remotely from the wafer 30 while the capacitive power controls
the plasma sheath adjacent to the wafer 30 and thus determines the
DC bias across the sheath at the wafer 30. The source power can be
raised to increase the etching rate and control the number and type
of excited radicals while the bias power can be varied to cause
ions to be accelerated across the plasma sheath with either high or
low energy and which then strike the wafer 30 with the selected
energy.
[0050] A first, 2-substep embodiment of the via etching step 48 is
shown by the flow diagram of FIG. 10 with reference to the
structures of FIGS. 11 and 12. A first substep 120 is a
non-selective timed etch that, as illustrated in FIG. 11, etches a
hole 122 through the upper oxide layer 20, the upper nitride stop
layer 16, and part way into the lower oxide layer 14. A second
nitride-selective etch step 124 selectively etches through the
lower oxide layer 14 and stops on the lower nitride stop layer 12
to form the extended via hole 50 of FIG. 12.
EXAMPLE 1
[0051] The 2-substep via etching step 48 has been performed upon
the structure presented above in TABLE 1 using the process recipe
of following TABLE 2. The mask for the via hole etch had a diameter
of 0.3 .mu.m.
2 TABLE 2 First Second Substep Substep CHF.sub.3 Flow (sccm) 80 80
C.sub.2F.sub.6 Flow (sccm) 10 10 CO Flow (sccm) 15 0 Ar Flow (sccm)
425 425 Inner Source Power (W) 710 710 Outer Source Power (W) 2310
2310 Bias Power (W) 1400 1400 Pressure (mT) 75 75 Roof Temp.
(.degree. C.) 145 145 Ring Temp. (.degree. C.) 350 350 Cathode
Temp. (.degree. C.) -10 -10 Backside He Pressure (T) 15 15 Time (s)
60 80
[0052] In the experimentally tested example, the oxide etch rate
was about 850 nm/min, and the via profile was very close to
90.degree.. The nitride loss for the bottom stop layer was minimal
even with a 20% overetch. In FIG. 13 is illustrated the output of
the end point detector which monitors the optical emission
associated with the CN radical during the via etching. The signal
strength indicates the amount of nitride being etched. A first peak
124 during the first substep is associated with the punch through
of the upper nitride stop layer. A second, broader peak 126 is
associated with the selective etch stopping on the lower nitride
stop layer.
[0053] The etch recipe was determined based on the following
considerations. The deep via etch resembles a typical contact
structure with an aspect ratio of about 5.5:1. In the example of
TABLE 2, trifluoromethane (CHF.sub.3) is used as the main etchant
gas with argon (Ar) as the chemically inactive diluent to
constitute a relative lean chemistry for high oxide etch rate and
vertical profile. Other diluent gases such as neon (Ne) are
available. It is believed that CHF.sub.3 primarily forms neutral
CF.sub.2* radicals in the plasma which react with SO.sub.2 to form
volatile SiF.sub.x and CO. By a lean chemistry is meant that the
F/C ratio of CHF.sub.3 is a relatively high value of 3 or greater
resulting in strong etching of SiO.sub.2 and low polymerization.
Another single-hydrogen fluorocarbon that can be used as the lean
principal etching gas is pentafluoroethane (C.sub.2HF.sub.5).
Carbon tetrafluoride (CF.sub.4) is also known as a lean etching
gas. A high flow rate of the principal etching gas CHF.sub.3 is
used to increase the oxide etch rate by the use of appropriate
power settings.
[0054] Argon ions activate the surface etching chemistry when they
strike the surface with a relatively high energy but less than that
associated with sputter etching.
[0055] The addition of hexafluoroethane (C.sub.2F.sub.6) supplies a
polymerizing gas to provide selectivity to the bottom nitride stop
layer. It is believed that multi-carbon fluorocarbons such as
C.sub.2F.sub.6 provide C.sub.2* radicals required for effective
polymerization during plasma etch, thus increasing etch selectivity
to base layers as SiN.sub.x and Si. The C.sub.2F.sub.6 also
provides sidewall passivation by forming a carbon-rich polymer on
the oxide sidewalls, thereby reducing bowing of the via hole. The
combination of the single-carbon hydrofluoromethane CHF.sub.3 and
the higher-carbon fluorocarbon C.sub.2F.sub.6 provides selectivity
to SiN.sub.x and a vertical via profile with good etch depth
margin. A minimum selectivity of 5:1 of etching oxide to nitride is
required. Even higher values are desired, e.g. 10:1. Unless stated
otherwise, a fluorocarbon is understood to include a
hydrofluorocarbon. In contrast, typical etch processes with high
nitride selectivity often result in tapered profiles, which impact
the via resistance. The ratio of the principal etching gas to the
lesser amount of polymer former is 8:1 in the example. A most
preferred range is 4:1 to 16:1
[0056] In order to punch through the upper nitride stop layer, an
oxygen-containing gas providing a source of oxygen consumes any
polymer building up on the silicon nitride since SiN.sub.x unlike
SiO.sub.2 does not contain oxygen. In the example of TABLE 2, the
oxygen-containing gas is carbon monoxide (CO). The interaction of
the oxygen in the plasma and carbon in the polymer produces
volatile carbon monoxide, thereby reducing the selectivity to the
oxygen-free nitride. Molecular oxygen (O.sub.2) can be used for
this purpose, but an O.sub.2 plasma also efficiently etches
photoresist. The selectivity to photoresist should be kept as high
as possible to maintain the photomasking with a minimum initial
thickness. In the high-density plasma achievable in the inductively
coupled IPS chamber of FIG. 9, CO dissociates into C* and O*
radicals, thereby providing a source of oxygen for nitride polymer
removal without excessive photoresist removal. It is noted that the
use of CO for decreasing selectivity to nitride or silicon is
contrary to the teachings of Tahara in U.S. Pat. No. 5,356,515,
according to which increasing the flow of CO in a fluorocarbon
plasma etch process increases the selectivity to nitride.
[0057] The relatively high pressure of 75 milliTorr used in the
recipe of TABLE 2 increases the selectivity to photoresist and at
the same time increases the oxide etch rate. A preferred range of
pressures is 40 to 150 milliTorr. A more preferred range is 60 to
100 milliTorr. Also a good profile is achieved with the combination
of high flow and high pressure achieved by flowing the diluent gas
at at least twice the rate of the etching gases.
[0058] The total source power of 3020W with a power ratio of 3.25
between outer and inner coils provides good uniformity of etch
across the wafer.
[0059] The lower silicon roof temperature of 145.degree. C. is used
to increase the etch rate and etch depth margin since the silicon
roof acts as a fluorine-scavenging surface providing selectivity to
photoresist. Similarly, a hot silicon ring at 350.degree. C. is
used to scavenge free fluorine F* in the plasma. The elevated
silicon temperatures, particularly keeping the silicon ring above
200.degree. C. and the silicon roof above 130.degree. C., keeping
the roof free of polymer, thus reducing particulates and providing
a clean process. The wafer temperature is kept low by means of high
helium backside pressure and low chiller temperature to promote
polymerization and reduce the photoresist etch rate.
[0060] The only significant change between the two substeps is the
supply of CO, which affects nitride etching. The oxide etch rate
should be about the same. The transition between the two substeps
can be quickly made. Although it is not necessary, advantageously
the plasma should be maintained through the sequence of substeps
with the gas flows changing only in fairly minor extent to affect
the selectivity. In the two-substep process of TABLE 2, the active
gas flow changes less than 30% between the substeps, the other
process parameters being maintained constant with no interruption
of the plasma. The chemically inactive diluent gas, Ar, has a flow
of four times that of the active gases. Similar effects are
expected with a factor of two or greater. The process can be
readily modified for different dielectric stack structures by
changing the etching times for the respective substeps.
[0061] An alternative 3-substep via etching step 48' is shown by
the flow diagram of FIG. 14 with reference to the cross-sectional
views of FIGS. 15, 11, and 12. In the first substep 130, a
nitride-selective etch forms a first hole 132, as illustrated in
FIG. 15, that only partially extends through the upper oxide layer
20, leaving a thin portion 134 of the oxide layer 20 under the hole
132. Preferably, the first substep 130 involves an etching
chemistry that includes no carbon monoxide and is selective to
nitride. Such a chemistry is relatively selective to the
photoresist so as to protect the hard mask as long as possible. The
selectivity provides a vertical profile and also provides process
margin since the etch cannot significantly extend into the upper
nitride layer 16. Such an etch that selectively etches oxide over
nitride is well known and is not particularly difficult since the
hole 132 at that point has a relatively low aspect ratio and the
selectivity to nitride need not be high for the small fraction of
holes in which the upper nitride layer 16 is exposed. The first
substep 130 is a timed step and does not critically rely upon the
selectivity of the etch. It is possible to extend the time of the
first substep 130 so that the etch would reliably extend to but
stop on the upper nitride layer 16. That is, in this variant the
thin oxide portion 134 underlying the hole 132 disappears during
the first substep 130.
[0062] The second and third substeps 136, 138 are functionally
similar to the substeps 120, 124 of the two-substep process 48 of
FIG. 10. The second substep 136 etches through the upper nitride
layer 16, as illustrated in FIG. 11. It may be a timed etching step
that is relatively unselective between oxide and nitride. The
timing is chosen so that the hole 132 is deepened to the hole 122
which reliably extends through the upper nitride layer 16 and may
extend part way into the lower oxide layer 14. Verticality is
desired but is not critical in view of the relative shallowness of
the second etching substep 124.
[0063] The third etching substep 138 completes the formation of the
extended via hole 50, as illustrated in FIG. 12. The time of the
third substep 138 is chosen to be sufficiently long that the etch
reaches and stops on the lower nitride layer 12. This etching
substep is difficult because of the high aspect ratio of the hole
50, which promotes etch stop. Good verticality and moderately high
selectivity to nitride is also required. Generally, stronger
polymer formation is required in the final substep 138, but etch
stop should be prevented by the continued use of a lean chemistry.
One example of the etching gases used in this substep 126 includes
the principal etchant trifluoromethane (CHF.sub.3), a lesser amount
of the polymer former octafluorocyclobutane (C.sub.4F.sub.8), and a
large amount of the diluent argon. Trifluoromethane is lean
relative to C.sub.4F.sub.8 in forming polymer, thereby reducing the
risk of etch stop. Selectivity to nitride is enhanced by
maintaining the silicon ring at a relatively high temperature to
scavenge fluorine from the plasma.
EXAMPLE 2
[0064] The 3-substep via etch was tested using a dielectric stack
having a structure summarized in TABLE 3. The via mask aperture had
a diameter of 0.6 .mu.m and the total oxide thickness was much
thicker, so this dual-damascene structure is more appropriate for a
power level.
3 TABLE 3 Thickness Composition (nm) Upper Dielectric Oxide 1400
Upper Stopper Nitride 50 Lower Dielectric Oxide 1000 Lower Stopper
Nitride 50
[0065] The 3-substep process recipe that was developed for the
broader trench geometry is summarized in TABLE 4.
4 TABLE 4 First Second Third Substep Substep Substep CHF.sub.3 Flow
(sccm) 90 90 80 CH.sub.2F.sub.2 Flow (sccm) 10 10 0 CO Flow (sccm)
0 15 0 C.sub.4F.sub.8 Flow (sccm) 0 0 10 Ar Flow (sccm) 425 425 425
Inner Source Power (W) 610 610 610 Outer Source Power (W) 2100 2310
2310 Bias Power (W) 1400 1400 1400 Pressure (mT) 75 75 75 Roof
Temp. (.degree. C.) 145 145 145 Ring Temp. (.degree. C.) 350 350
350 Cathode Temp. (.degree. C.) -10 -10 -10 Backside He Pressure
(T) 15 15 15 Time(s) 70 50 60
[0066] The example yielded an oxide etch rate of 930 nm/min. The
via profile was vertical at close to 90.degree.. The nitride loss
at the bottom stop layer was less than 10 nm after a 16%
overetch.
[0067] The recipe is similar to that for the 0.3 .mu.m process.
However, the oxide is thicker and the nitride stop layers are
thinner so that the total etch time is much longer for the same
photoresist thickness of 900 nm.
[0068] In order to reduce photoresist etch rate, difluoromethane
(CH.sub.2F.sub.2) is added for the first and second substeps.
Difluoromethane is a dihydrofluorocarbon providing a source of
hydrogen, which is believed to scavenge free fluorine in the plasma
and promotes polymerization on the photoresist to improve
selectivity to photoresist.
[0069] Carbon monoxide (CO) is added in the second substep to
reduce selectivity to nitride when punching through the upper
nitride layer. Carbon monoxide is useful in this step since it
affords reasonably good selectivity to the photoresist. Carbon
dioxide (CO.sub.2) has the potential of providing the same
selectivity to nitride in a high-density plasma, but experiments
have shown a degradation in selectivity to photoresist relative to
CO, probably because of a different degree of dissociation in the
plasma. Gaseous oxygen (O.sub.2) would be expected to be
non-selective.
[0070] Octafluorocyclobutane (C.sub.4F.sub.8) is added in the
critical third substep to increase selectivity to the lower nitride
layer. It, like C.sub.2F.sub.6, provides C.sub.2 species for
effective polymerization and resultant nitride selectivity. Since
the nitride layer is thinner in this structure, C.sub.4F.sub.8 is
chosen over C.sub.2F.sub.6 because of its greater polymerizing
power over either the C.sub.2F.sub.6 or CH.sub.2F.sub.2 used in the
first two substeps. It is generally easier to form polymer on small
exposed nitride surfaces as compared to the larger exposed surfaces
experienced here. For small features size, C.sub.2F.sub.6 is more
desirable since it provides adequate nitride selectivity without
sacrificing etch depth in the via, that is, without etch stop. For
larger feature sizes, C.sub.4F.sub.8 can be used to provide high
nitride selectivity without too much concern about etch depth
margin.
[0071] Generally, the longer the carbon molecule, the better it
performs as a polymer former. Some carbon in the fluorocarbon also
indicates stronger polymer formation.
[0072] The critical etching steps are preferably performed in a
high-density plasma. First, it affords a higher etch rate.
Secondly, the separate biasing of the pedestal allows control of
the ion energy without sacrificing etching rate. Thirdly, it has
been experimentally observed that a polymer formed in a
high-density plasma has a higher carbon-to-fluorine ratio. A
low-fluorine polymer provide better selectivity to underlying
layers not containing oxygen.
[0073] Each of the two-substep and three-substep processes
summarized in TABLES 2 and 3 is preferably performed in a single
high-density plasma reactor in an essentially continuous process.
The RF powers and more importantly the various temperatures are
maintained the same so no reequilibration is required. The gas flow
of the principal etchant CHF.sub.3 is maintained constant to within
15% with only the selective additions of the polymer formers and
the oxygen-containing CO, to an extent of no more than 30% of the
active gas flow. The oxygen-containing CO has a flow rate of less
than 25% of the active etching gases and less than 20% of the
primary etchant CHF.sub.3. Additionally, the high diluent flow,
greater than twice that of the active gases, allows the gas
pressure to remain essentially constant with no adjustment of the
throttle valve. Thereby, the substeps smoothly transition with no
interruption of the plasma.
[0074] Although the via etch is the critical step for the
counterbore dual-damascene etch, the trench etch, its photomasking,
and the lower stop removal must be performed consistent with the
entire process. These further steps are part of an integrated
process disclosed by Hung et al. in U.S. patent application Ser.
No. 09/112,094, filed Jul. 9, 1994 and incorporated herein in its
entirety. The details of the other parts of the integrated process
are not essential to this invention. An unexpected feature of the
integrated process is that it is preferred to strip the photoresist
in the post-etch treatment (PET) or ashing step before the lower
nitride stop layer is removed. Exemplary process recipes for these
steps are summarized in TABLE 5. These steps can be sequentially
performed also in the IPS chamber of FIG. 9 after the formation of
the trench photomask. The IPS chamber may be the same chamber or
another one. Alternatively, since the trench etch and other steps
associated with it are not so critical, it is possible to perform
them in a less sophisticated plasma etch reactor, for example, one
relying solely upon RF capacitive coupling between the pedestal and
the grounded chamber walls.
5 TABLE 5 Trench Nitride Etch Ash Etch C.sub.4F.sub.8 Flow (sccm)
14 0 0 CH.sub.2F.sub.2 Flow (sccm) 0 0 40 O.sub.2 Flow (sccm) 0 400
60 Ar Flow (sccm) 100 0 100 Inner Source Power (W) 260 800 420
Outer Source Power (W) 1040 2400 1320 Bias Power (W) 1400 150 150
Pressure (mT) 7 60 9 Roof Temp. (.degree. C.) 180 180 180 Ring
Temp. (.degree. C.) 270 270 270 Cathode Temp. (.degree. C.) +10 +10
+10 Backside He Pressure (T) 15 15 15 Time(s) 100 60 100
[0075] The trench etch when performed with the 0.3 .mu.m
counterbore via with the above recipe produced an oxide etch rate
of 600 nm/min. The trench profile was slightly V-shaped at between
85.degree. and 90.degree.. The nitride loss of the upper stop layer
was less than 20 nm with a 20% over etch. The bottom stop layer
lost significant thickness, but there was no punch through.
[0076] The chemistry used in the exemplary trench etch uses
C.sub.4F.sub.8/Ar at low source power. Since the trench etch is
performed with a low aspect ratio with a large area of exposed
SiN.sub.x at the upper stop layer and an unprotected bottom
SiN.sub.x layer, it is desirable to use a highly polymerizing
process with a low ion density to minimize sputtering of SiN.sub.x.
The highly polymerizing nature of C.sub.4F.sub.8 provides good
selectivity to the top nitride layer. The lower source power
reduces the ion density, which in turn reduces the sputtering of
the SiN.sub.x corner of the upper stop layer, to thereby maintain
the critical dimension of the via. A relatively high silicon roof
temperature of 200.degree. C. is used as an additional control to
increase selectivity to nitride. The relatively low chamber
pressure of 7 mT is used in this case to minimize micro-loading
between different sizes of the trenches, which can range between
0.3 .mu.m to greater than 1 .mu.m. Micro-loading produces
differential etching rates for different geometries, which results
in SiN.sub.x erosion in one of the geometries. The lower pressure
also produces a more vertical profile, especially for the highly
polymerizing chemistry being used in the trench etch.
[0077] The photoresist and polymer are stripped in a typical ashing
step summarized in TABLE 5 using only O.sub.2 at high source power
and low bias power. The stripping is performed prior to the nitride
removal step to avoid residue originating form the polymer coming
from the roof and wafer.
[0078] The third and final etch step 66 removing the exposed lower
stop layer 12 is typically a soft plasma etch to avoid copper
sputtering and the formation of a residue.
[0079] The various temperature settings for all three steps in
TABLE 5 are the same allowing a quick transition between the
steps.
[0080] Although the examples of the invention have relied upon the
inductively coupled IPS chamber, other etch reactor and
particularly other types of high-density plasma reactors may be
used advantageously with the invention.
[0081] Although the examples of the invention have used layers of
PECVD SiO.sub.2 and Si.sub.3N.sub.4 for the oxide and nitride
layers, the invention is not so limited. There are other forms of
silicon oxide, such as borophosphosilicate glass (BPSG),
fluorinated silica glass (FSG), and spin-on glass (SOG) and other
forms of oxygen-free silicides. Indeed, the broader aspects of the
invention are not limited to only silicon-based dielectrics and
stop layers but may be extended to carbon-based materials for one
or both of these types of layers.
[0082] It is thus seen that the deep via etch through multiple
layers can be efficiently and quickly performed in a single etch
reactor while providing a highly desirable structure, particularly
in conjunction the counterbore dual-damascene structure. However,
the invention is not limited to a dual-damascene structure but may
be applied to other multi-layer dielectric structures.
[0083] Although the recipes of the examples are presented for the
combination of silicon oxide and silicon nitride, many aspects of
the invention can be applied to other dielectric structures,
including those using carbon-based low-k dielectrics.
* * * * *