U.S. patent application number 09/754026 was filed with the patent office on 2002-09-19 for stretchable composite sheet for adding softness and texture.
Invention is credited to Baer, David J., Close, Kenneth B..
Application Number | 20020132543 09/754026 |
Document ID | / |
Family ID | 25033175 |
Filed Date | 2002-09-19 |
United States Patent
Application |
20020132543 |
Kind Code |
A1 |
Baer, David J. ; et
al. |
September 19, 2002 |
Stretchable composite sheet for adding softness and texture
Abstract
A method for increasing the thickness of a fibrous sheet
including stretching the sheet beyond its relaxed length and
returning the sheet to about the relaxed length, causing the sheet
to have a second thickness greater than the first thickness. The
sheet can be a wet-wipe. The wet-wipe includes an elastic layer and
a fibrous layer, which increases in thickness when stretched then
relaxed. The wet-wipe can be stored in a container, which causes
the wet-wipe to stretch as it is removed from the container.
Inventors: |
Baer, David J.; (Oshkosh,
WI) ; Close, Kenneth B.; (New London, WI) |
Correspondence
Address: |
SCHWEGMAN, LUNDBERG, WOESSNER & KLUTH, P.A.
P.O. Box 2938
Minneapolis
MN
55402
US
|
Family ID: |
25033175 |
Appl. No.: |
09/754026 |
Filed: |
January 3, 2001 |
Current U.S.
Class: |
442/327 ;
428/174; 428/181; 428/98; 442/328 |
Current CPC
Class: |
A47K 2010/428 20130101;
Y10T 442/2795 20150401; Y10T 428/24686 20150115; A47K 2010/3266
20130101; Y10T 442/30 20150401; A47K 10/42 20130101; Y10T 442/659
20150401; Y10T 442/601 20150401; B32B 2250/40 20130101; B32B 5/26
20130101; B32B 2250/20 20130101; B32B 5/04 20130101; B32B 2317/16
20130101; Y10T 428/24 20150115; Y10T 428/24628 20150115; B32B
2262/067 20130101; Y10T 442/232 20150401; Y10T 442/602 20150401;
Y10T 442/2943 20150401; Y10T 442/60 20150401; A47L 13/17 20130101;
Y10T 428/24479 20150115 |
Class at
Publication: |
442/327 ;
442/328; 428/98; 428/174; 428/181 |
International
Class: |
B32B 005/00; B32B
007/00; B32B 001/00; B32B 003/00; D04H 001/00; D04H 003/00; D04H
005/00 |
Claims
What is claimed is:
1. A wet-wipe dispensing system comprising a wet-wipe container and
at least one wet-wipe stored within the container, the wet-wipe
being removable from the container for use, the wet-wipe comprising
a non-woven laminate of an elastic layer and at least one gathered
layer, the gather layer being bonded to the elastic layer at at
least two points and being gathered between the at least two
points, the non-woven laminate having a first thickness within the
container and a second thickness outside the container, the second
thickness being greater than the first thickness.
2. The wet-wipe dispensing system according to claim 1, wherein the
second thickness is about 18% thicker than the first thickness.
3. The wet-wipe dispensing system according to claim 1, wherein the
second thickness is in the range of about 1.0 mm to about 1.7
mm.
4. The wet-wipe dispensing system according to claim 3, wherein the
first thickness is less than 0.90 mm.
5. The wet-wipe dispensing system according to claim 1, wherein the
at least one gathered layer includes a first gathered layer bonded
to one surface of the elastic layer and a second gathered layer
bonded to an opposite surface of the elastic layer such that the
elastic layer is sandwiched between the first gathered layer and
the second gathered layer.
6. The wet-wipe dispensing system according to claim 1, wherein the
container includes a base and a lid enclosing a n interior wherein
the a t least one wet-wipe is stored, the lid including a opening
through which the at least one wet-wipe is removed from the
interior of the container.
7. The wet-wipe dispensing system according to claim 6, wherein the
at least one wet-wipe has a first position substantially within the
interior of the container and a second position outside the
container, the at least one wet-wipe having a first thickness in
the first position and a second thickness in the second position,
the second thickness being greater than the first thickness, and
wherein the opening is formed of a yieldable and pass through
resistive material which yieldably and resistively allows the at
least one wet-wipe to move from the first position to the second
position.
8. The wet-wipe dispensing system according to claim 7, wherein the
opening yieldably resists the at least one wet-wipe transitioning
from the first position to the second position, and the elastic
layer having a relaxed state with the wet-wipe in the first and
second positions and a stretched state as the opening yieldably
resists the wet-wipe transitioning to the second position.
9. The wet-wipe dispensing system according to claim 8, wherein the
elastic layer has a stretched length of about 271 mm in the
stretched position, and relaxed length of about 190 mm in the
relaxed state.
10. The wet-wipe dispensing system according to claim 8, wherein
the elastic layer includes a plurality of parallel elastic fibers
extending in a first direction, and the at least one wet-wipe being
stretched in the first direction when transitioning between the
first and second positions.
11. The wet-wipe dispensing system according to claim 10, wherein
the first direction is the machine direction.
12. The wet-wipe dispensing system according to claim 6, wherein
the base is a rigid tub.
13. The wet-wipe dispensing system according to claim 6, wherein
the base is a flexible package.
14. The wet-wipe dispensing system according to claim 6, wherein
the lid includes a flexible, rubber-like material, and the opening
is formed in the flexible, rubber-like material.
15. The wet-wipe dispensing system according to claim 13, wherein
the opening has a length of one inch or greater.
16. The wet-wipe dispensing system according to claim 13, wherein
the opening includes a plurality of slits each of which crosses at
least one other slit.
17. The wet-wipe dispensing system according to claim 13, wherein
the flexible, rubber-like material has a Shore A hardness of about
100 or less.
18. The wet-wipe dispensing system according to claim 13, wherein
the flexible, rubber-like material has Gurley stiffness of about
10,000 mgf or less.
19. The wet-wipe dispensing system according to claim 13, wherein
the flexible, rubber-like material has a thickness of about 0.1 mm
or greater.
20. The wet-wipe dispensing system according to claim 13, wherein
the flexible, rubber-like material has an elasticity of 10 Mpa or
less.
21. The wet-wipe dispensing system according to claim 1, wherein
the at least one wet-wipe includes a plurality of wet-wipes, the
plurality of wet-wipes being interleaved in a stored position
within the container.
22. The wet-wipe according to claim 1, wherein the at least one
wet-wipe includes a plurality of wet-wipes, the plurality of
wet-wipes being non-interleaved in a stored position within the
container.
23. The wet-wipe according to claim 1, wherein the at least one
wet-wipe includes a plurality of wet-wipes, the plurality of
wet-wipes being in a roll in a stored position within the
container.
24. A method for increasing the thickness of a wet-wipe, the
wet-wipe in a first mode having a relaxed length and a first
thickness, comprising: stretching the wet-wipe in a second mode
beyond its relaxed length to an extended length; and recovering the
wet-wipe to a third mode causing the wet-wipe to have a second
thickness greater than the first thickness, the length of the
wet-wipe in the third mode being about the relaxed length.
25. The method according to claim 24, wherein stretching the
wet-wipe includes stretching the wet-wipe in a machine
direction.
26. The method according to claim 24, wherein recovering the
wet-wipe in the third mode includes increasing the thickness of the
wet-wipe by about 18%.
27. The method according to claim 24, wherein stretching the
wet-wipe in the second mode includes removing the wet-wipe from a
container through an opening which yieldably resists removal of the
wet-wipe such that the wet-wipe is stretched during removal.
28. The method according to claim 24, wherein stretching the
wet-wipe in a second mode includes stretching an elastic layer and
at least one gathered layer, and recovering the wet-wipe to the
third mode includes increasing the thickness of the at least one
gathered layer.
29. The method according to claim 24, wherein stretching the
wet-wipe includes stretching the wet-wipe to a length about 30%
greater than the length of the wet-wipe in the relaxed state.
30. A method for increasing the thickness of a non-woven composite
elastic wet-wipe including at least one non-woven elastic layer and
at least one non-woven gatherable layer, wherein the gatherable
layer is bonded to the elastic layer at at least two points and is
gathered between the at least two points, and wherein the elastic
layer is a non-woven web, the wet-wipe in a first mode having a
relaxed length and a first thickness, comprising: stretching the
wet-wipe in a second mode beyond the relaxed length to an extended
length; and releasing the wet-wipe in a third mode from the
extended length to about the relaxed length while causing the
wet-wipe to have a second thickness that is greater than the first
thickness.
31. A multi-mode wet-wipe, comprising: a first mode in which the
wet-wipe has a relaxed length and a first thickness; a second mode
in which the wet-wipe is stretched to a stretched length greater
than the relaxed length; and a third mode in which the wet-wipe
recovers to about the relaxed length and has a second thickness,
the second thickness being greater than the first thickness.
32. The multi-mode wet-wipe according to claim 31, wherein the
stretched length is less than or equal to about 30% greater than
the relaxed length.
33. The multi-mode wet-wipe according to claim 31, wherein the
second thickness is about 18% greater than the first thickness.
34. The multi-mode wet-wipe according to claim 31, wherein the
stretched length is at least about 5% greater than the relaxed
length.
35. The multi-mode wet-wipe according to claim 31, wherein the
wet-wipe in the third mode has a density less than the wet-wipe in
the first mode.
36. A non-woven composite elastic wet-wipe, comprising: at least
one non-woven elastic layer; at least one non-woven gatherable
layer, wherein the gatherable layer is bonded to the elastic layer
at at least two points and is gathered between the two points to
form a composite elastic material; a first mode in which the
wet-wipe has a relaxed length and a first thickness; a second mode
in which the wet-wipe is stretched to a stretched length greater
than the relaxed length; and a third mode in which the wet-wipe is
recovered to about the relaxed length and has a second thickness,
the second thickness being greater than the first thickness.
37. The wet-wipe according to claim 36, wherein the composite
elastic material has a density less than about 0.085 g per cubic cm
and has a CD tensile strength of greater than about 0.68
pounds.
38. The wet-wipe according to claim 36, wherein the composite
elastic material includes a liquid distributed within the
layers.
39. The wet-wipe according to claim 38, wherein the liquid
comprises at least one material selected from the group of
materials including preservatives, fragrances, emollients,
humectants, detergents and soaps.
40. The wet-wipe according to claim 36, wherein the composite
elastic material has a cup crush less than about 120 g per cm and a
CD tensile strength of greater than about 0.68 pounds.
41. The wet-wipe according to claim 36, wherein the composite
elastic material has a cup crush to density ratio of less than
about 1300 cm.sup.2 and greater than about 1100 cm.sup.2.
42. The wet-wipe according to claim 36, wherein the elastic layer
has elastic fibers arranged in a substantially parallel
configuration.
43. The wet-wipe according to claim 36, wherein the composite
elastic material has a cup crush less than about 70 g-cm.
44. The wet-wipe according to claim 36, wherein the gatherable
layer is non-elastic.
Description
BACKGROUND OF THE INVENTION
[0001] Fibrous materials and fibrous composite materials are widely
used as products, or as components of products, such as wet-wipes
because they can be manufactured inexpensively and made to have
specific characteristics. These products can be manufactured so
inexpensively that they can be viewed as disposable, as opposed to
reusable.
[0002] One approach to making fibrous composite materials for
wet-wipes the use of homogeneous mixtures of materials such as air
laid, non-woven webs of fibers mixed with cellulosic fibers or
another absorbent material. Other wet-wipes have been prepared by
joining different types of non-woven materials in a laminate or
formed as a layered structure. These products can be prepared from
plastic materials such as plastic sheets, films and non-woven webs,
prepared by extrusion processes such as, for example, slot film
extrusion, blown bubble film extrusion, meltblowing of non-woven
webs and spinbonding.
[0003] The materials that are useful for consumer products should
meet minimum product standards for strength, moisture level, size,
flexibility, thickness, softness and texture. However, if one of
these parameters is changed this can affect another of the
parameters. Thus, a goal for these laminates is to produce a
product that can mimic a soft cloth-like feel or at least get
closer to a soft cloth-like feel than has been previously possible
while still maintaining acceptable strength.
[0004] Such a soft cloth-like feel is often characterized by, among
other things, one or more of the following: thickness, bulk
density, flexibility, texture, softness, density, and durability of
the non-woven materials. These materials are suitable for
disposable products such as, for example, disposable diapers,
disposable tissues and disposable wipes, for example, disposable
wet-wipes.
[0005] Unfortunately, manufacturing and distribution processes
reduce the thickness of wet-wipes. This reduces the softness and
cloth-like feel, which is desired by the consumer. Accordingly,
there is a need to improve the softness and cloth-like texture of a
wet-wipe.
Definitions
[0006] For the purposes of the present application, the following
terms shall have the following meanings:
[0007] The term "elastic", as used herein, means any material
which, upon application of a biasing force, is stretchable, that
is, elongatable at least about 5 to about 30 percent (i.e., to a
stretched, biased length which is at least about 105 to about 130
percent of its relaxed unbiased length), and which, will recover at
least 55 percent of its elongation upon release of the stretching,
elongating force. A hypothetical example would be a one (1) cm
sample of a material which is elongatable to at least 1.30 cm and
which, upon being elongated to 1.30 cm and released, will recover
to a length of not more than 1.135 cm. Many elastic materials can
be elongated by much more than 30 percent (i.e., much more than 130
percent of their relaxed length), for example, elongated 60
percent, 100 percent or more, and many of these will recover to
substantially their initial relaxed length, for example, to within
105 percent of their original relaxed length, upon release of the
stretching force.
[0008] As used herein, the term "non-elastic" means any material
which does not fall within the definition of "elastic," above.
[0009] As used herein, the term "non-woven web" means a structure
or a web of material which has been formed without use of weaving
processes to produce a structure of individual fibers or threads
which are intermeshed or interlaid, but not in an identifiable,
repeating manner. Non-woven webs have been, in the past, formed by
a variety of conventional processes such as, for example,
meltblowing processes, spinbonding processes, film aperturing
processes and staple fiber carding processes.
[0010] The terms "recover" and "recovery", as used herein, mean a
contraction of a stretched material upon termination of a biasing
force following stretching of the material by application of the
biasing force. For example, if a material having a relaxed,
unbiased length of one (1) cm is elongated 50 percent by stretching
to a length of one and one half (1.5) cm the material would be
elongated 50 percent (0.5 cm) and would have a stretched length
that is 150 percent of its relaxed length. If this exemplary
stretched material contracted, that is, recovered to a length of
one and one tenth (1.1) cm after release of the biasing and
stretching force, the material would have recovered 80 percent (0.4
cm) of its one-half (0.5) cm elongation. Recovery can be expressed
as [(maximum stretch length--final sample length)/(maximum stretch
length--initial sample length)] times 100.
[0011] As used herein, the term "meltblown fibers" means fibers
formed by extruding a molten thermoplastic material through a
plurality of fine, usually circular, die capillaries as molten
threads or filaments into a high velocity gas (e.g. air) stream
which attenuates the filaments of molten thermoplastic material to
reduce their diameter, which can be to microfiber diameter.
Thereafter, the meltblown fibers are carried by the high velocity
gas stream and are deposited on a collecting surface to form a web
of randomly disbursed meltblown fibers. Such a process is
disclosed, for example, in U.S. Pat. No. 3,849,241 to Butin.
[0012] As used herein, the term "spunbonded fibers" means small
diameter fibers which are formed by extruding a molten
thermoplastic material as filaments from a plurality of fine,
usually circular, capillaries of a spinnerette with the diameter of
the extruded filaments then being rapidly reduced as by, for
example, eductive drawing or other well-known spun-bonding
mechanisms. The production of spun-bonded non-woven webs is
illustrated in patents such as, for example, in U.S. Pat. No.
4,340,563 to Appel et al., and U.S. Pat. No. 3,692,618 to Dorschner
et al.
[0013] As used herein, the term "coform" means a non-woven
composite material of air-formed matrix material including
thermoplastic polymer microfibers having an average fiber diameter
of less than about 10 microns, and a multiplicity of individualized
absorbent fibers such as, for example, wood pulp fibers disposed
throughout the matrix of polymer microfibers and engaging at least
some of the microfibers to space the microfibers apart from each
other. The absorbent fibers are interconnected by and held captive
within the matrix of microfibers by mechanical entanglement of the
microfibers with the absorbent fibers, the mechanical entanglement
and interconnection of the microfibers and absorbent fibers alone
forming a coherent integrated fibrous structure. These materials
are prepared according to the descriptions in U.S. Pat. No.
4,100,324 to Anderson et al. U.S. Pat. No. 5,508,102 to Georger et
al. and U.S. Pat. No. 5,385,775 to Wright.
[0014] As used herein, the term "microfibers" means small diameter
fibers having an average diameter not greater than about 100
microns, for example, having an average diameter of from about 0.5
microns to about 50 microns, or more particularly, microfibers may
have an average diameter of from about 4 microns to about 40
microns.
[0015] As used herein, the term "autogenous bonding" means bonding
provided by fusion and/or self-adhesion of fibers and/or filaments
without an applied external adhesive or bonding agent. Autogenous
bonding can be provided by contact between fibers and/or filaments
while at least a portion of the fibers and/or filaments are
semi-molten or tacky. Autogenous bonding may also be provided by
blending a tackifying resin with the thermoplastic polymers used to
form the fibers and/or filaments. Fibers and/or filaments formed
from such a blend can be adapted to self-bond with or without the
application of pressure and/or heat. Solvents may also be used to
cause fusion of fibers and filaments which remains after the
solvent is removed.
[0016] As used herein, the term "machine direction (MD)" is the
direction of travel of the forming surface onto which fibers are
deposited during formation of a non-woven fibrous web.
[0017] As used herein, the term "cross-machine direction (CD)" is
the direction that is essentially perpendicular to the machine
direction defined above.
[0018] As used herein, the term "tensile strength" is the maximum
load or force (i.e., peak load) encountered while elongating the
sample to break. Measurements of peak load are made in the machine
and cross-machine directions using wet samples.
[0019] As used herein, the term "wet-wipe" means a fibrous sheet
which, during its manufacture, has a liquid applied thereto so that
the liquid will be retained on or within the fibrous sheet until
its utilization by a consumer. The liquid may include a fragrance
and/or an emollient and may serve to aid the sheet in retention of
materials which are to be wiped up during its utilization.
[0020] As used herein, the terms "stretch-bonded laminate" or
"composite elastic material" means a non-woven fabric material
having at least one of the layer of material being elastic and at
least one layer of the material being non-elastic, e.g., a
gatherable layer. The elastic web layer(s) are joined or bonded to
at least at least two locations to the non-elastic web layer(s).
Preferably, the bonding is at intermittent bonding points or areas
while the non-woven web layer(s) are in juxtaposed configuration
and while the elastic non-woven web layer(s) have a tensioning
force applied thereto in order to bring the elastic non-woven web
to a stretched state. Upon removal of the tensioning force after
joining of the web layers, an elastic non-woven web layer will
attempt to recover to its unstretched condition and will thereby
gather the non-elastic non-woven web layer between the points or
areas of joining of the two layers. The composite material is
elastic in the direction of stretching of the elastic layer during
joining of the layers and can be stretched until the gathers of the
non-elastic layer have been removed. A stretch-bonded laminate may
include more than two layers. For example, the elastic layer may
have a non-elastic web layer joined to both of its sides while it
is in a stretched condition so that a three layer non-woven web
composite is formed having the structure of gathered non-elastic
(non-woven web or film) /elastic (non-woven web or film)/gathered
non-elastic (non-woven web or film). Yet other combinations of
elastic and non-elastic layers can also be utilized. Such composite
elastic materials are disclosed, for example, by U.S. Pat. No.
4,720,415 to Vander Wielen et al., and U.S. Pat. No. 5,385,775 to
Wright.
[0021] As used herein, "thermal point bonding" involves passing a
material such as two or more webs of fibers to be bonded between a
heated calendar roll and an anvil roll. The calender roll is
usually, though not always, patterned in some way so that the
entire fabric is not bonded across its entire surface, and the
anvil roll is usually flat. As a result, various patterns for
calender rolls have been developed for functional as well as
aesthetic reasons. In one embodiment of this invention the bond
pattern allows void spaces in the machine direction to allow a
gatherable layer to gather when the stretched elastic web
retracts.
[0022] As used herein, the term "superabsorbent" refers to a water
swellable, substantially insoluble organic or inorganic material
capable of absorbing at least 10 times its weight of an aqueous
solution containing 0.9 wt % of sodium chloride.
[0023] As used herein, the term "palindromic" means a multilayer
laminate, for example a stretch-bonded laminate, which is
substantially symmetrical. Examples of palindromic laminates could
have layer configurations of A/B/A, A/B/B/A, A/A/B/B/A/A,
A/B/C/B/A, and the like. Examples of non-palindromic layer
configurations would include A/B/C, A/B/CIA, A/B/C/D, etc.
[0024] As used herein, the term "polymer" generally includes, but
is not limited to, homopolymers, copolymers, such as, for example,
block, graft, random and alternating copolymers, terpolymers, etc.
and blends and modifications thereof. Furthermore, unless otherwise
specifically limited, the term "polymer" shall include all possible
geometrical configurations of the material. These configurations
include, but are not limited to, isotactic, syndiotactic and random
symmetries.
SUMMARY OF THE INVENTION
[0025] The problem of lack of softness or cloth-like feel
associated with previous composite elastic materials has been
addressed by the composite elastic material of the present
invention, which is adapted to provide a more cloth-like feel than
otherwise available. This can be accomplished by providing a
non-woven composite material having a first thickness and a second
thickness. The second thickness is greater than the first thickness
and, thus, provides a softer, more cloth-like feeling composite
elastic material.
[0026] The composite elastic material of one embodiment contains at
least one elastic layer including an elastic layer having embedded
elastic fibers and at least one gatherable layer joined at spaced
apart locations to the elastic layer so that the gatherable layer
is gathered between the spaced-apart locations.
[0027] The gatherable layer can be a non-woven web of fibers, such
as, for example, a web of spunbonded fibers, a web of meltblown
fibers, a bonded carded web of fibers, a multilayer material
including at least one of the webs of spunbonded fibers, meltblown
fibers, or a bonded carded web of fibers. The gatherable layer may
also be a mixture of fibers and one or more other materials such
as, for example, wood pulp, staple-length fibers, particulates and
super-absorbent materials. Such mixtures may be formed by adding
fibers and/or particulates to the gas stream in which meltblown
fibers are carried so that an intimate entangled commingling of
meltblown fibers and other materials, e.g., wood pulp, staple
fibers and particulates such as, for example, hydrocolloid
(hydrogel) particulates commonly referred to as superabsorbent
materials, occurs prior to collection of the meltblown fibers upon
a collecting device to form a coherent web of randomly dispersed
meltblown fibers and other materials such as disclosed in U.S. Pat.
No. 4,100,324, to Anderson et al.
[0028] In another aspect of the invention, the elastic composite is
formed into a wet-wipe, which is removably stored in a container.
The wet-wipe has a non-woven laminate of an elastic layer and at
least one gathered layer, the gathered layer being bonded to the
elastic layer at at least two points and being gathered between the
at least two points, the non-woven laminate having a first
thickness within the container and a second thickness outside the
container, the second thickness being greater than the first
thickness. The second thickness provides the user of the wet-wipe
with a softer feeling wet-wipe than the thinner wet-wipe having the
first thickness.
[0029] Another aspect of the invention is a method for increasing
the thickness of a wet-wipe, the wet-wipe in a first mode having a
relaxed length and a first thickness, including stretching the
wet-wipe in a second mode beyond its relaxed length to an extended
length, and recovering the wet-wipe in a third mode to about the
relaxed length, causing the wet-wipe to have a second thickness
greater than the first thickness. The thicker, second mode wet-wipe
provides a softer wet-wipe, which is desired by consumers.
BRIEF DESCRIPTION OF THE FIGURES
[0030] FIG. 1 is a schematic drawing of an exemplary process for
forming a composite elastic material of the present invention.
[0031] FIG. 2 is a schematic drawing of an exemplary process for
forming an elastic fibrous web, which is a component of the
composite elastic material of the present invention.
[0032] FIG. 3 is a schematic drawing of an exemplary process for
preparing a gatherable layer.
[0033] FIG. 3A is an enlarged view of the pulp generator of FIG.
3.
[0034] FIG. 4 is a schematic drawing of an exemplary process for
the heat treatment of the composite elastic material of the present
invention activated by treatment in a heat activator.
[0035] FIG. 5 is a flowchart of a process for the preparation of
the composite elastic material of the present invention.
[0036] FIG. 6 is a chart of wet density of several commercially
available wet-wipes and the wet density of the wet-wipes of the
present invention.
[0037] FIG. 7 is a chart of cup crush of several commercially
available wet-wipes and the cup crush of the wet-wipes of the
present invention.
[0038] FIG. 8 is a chart of cup crush to density ratio of several
commercially available wet-wipes and the cup crush of the wet-wipes
of the present invention.
[0039] FIG. 9 is a chart of CD tensile strength of several
commercially available wet-wipes and the CD tensile strength
wet-wipes of the present invention.
[0040] FIG. 10 is a representative plan view of a bonding pattern
suitable for bonding the layers of the composite elastic
material.
[0041] FIG. 11 is a view of a load testing apparatus for testing a
composite according to the present invention.
[0042] FIG. 12 is an exploded view of the load testing apparatus of
FIG. 11.
[0043] FIG. 13 is a perspective view of one embodiment of a
wet-wipe container with the lid open, illustrating the placement of
the dispenser within a removable inner cover.
[0044] FIG. 14 is a perspective view of another embodiment of a
wet-wipe container, with the lid open, wherein a wet-wipe dispenser
is recessed within a rigid top of the container.
[0045] FIG. 15 is a perspective view of another embodiment of a
wet-wipe container, wherein a wet-wipe dispenser is attached to a
flexible container package.
[0046] FIGS. 16A and 16B are schematic views of non-interleaved
stacks of the composite elastic material.
[0047] FIGS. 17A and 17B are schematic views of interleaved stacks
of the composite elastic material.
[0048] FIG. 18 is a schematic view of a roll of wet-wipes according
to the present invention.
[0049] FIG. 19 is a graph of the effect of dispensing wet-wipes
according to the present invention.
DETAILED DESCRIPTION
[0050] The present invention provides a composite elastic material
such as, for example, a stretch-bonded laminate, which is adapted
to provide improved softness and cloth-like feel. This can be
accomplished by providing, a non-woven composite material having a
low cup crush and a low density, while maintaining a desired level
of strength and tear resistance. This composite elastic material
can include an elastic fibrous web that can be a composite of
elastomeric fiber and elastomeric meltblown fibers.
[0051] The softness and cloth-like texture (feel) is further
enhanced by stretching the stretch-bonded laminate prior to use,
and allowing the laminate to return (recover) to about its relaxed
state or mode. The stretching and recovery causes the thickness of
the laminate to increase; thereby, increasing the softness and
cloth-like texture of the laminate. One use of the laminate is a
disposable wet-wipe.
[0052] The wet-wipes of the present invention provide improved
softness and cloth-like feel because they have a combination of
properties, such as low cup crush (i.e., increased flexibility) and
a low density (i.e., maximum bulk per unit mass), while maintaining
a desired level of strength and tear resistance (i.e., sufficient
tensile strength in both MD and CD) that were not previously
available in wet-wipes. The wet-wipes of the invention include a
non-woven composite elastic material having at least one elastic
layer and at least one gatherable layer. The gatherable layer is
bonded to the elastic layer at at least two points; and is gathered
between the bonded points. The elastic layer includes a non-woven
web having embedded elastic fibers, arranged in a substantially
parallel configuration. Moreover, softness and cloth-like texture
are further enhanced by stretching and relaxing the wet-wipe;
thereby, causing the at least one non-woven gatherable layer to
increase in thickness. An increase in thickness lowers the density
and increases the softness of the wet-wipe.
[0053] The feel of a wet-wipe is often characterized by one or more
of the following attributes of the materials that comprise them:
thickness, bulk density, flexibility, texture, softness, and
durability. In preparing a wet-wipe having a soft cloth-like feel,
it is important to balance the properties of the composite elastic
material, e.g., cup crush, density, and tensile strength. However,
this is a difficult task because these properties can be
interdependent, i.e., changing one property can adversely affect
another property of the wet-wipe (and the overall feel of the
wet-wipe). Typically, when the basis weight is decreased, the
cup-crush is decreased, and tensile strength is decreased. When the
basis weight is decreased then the reverse changes occur. Thus,
when a property is varied, to enhance the softness, careful
attention should be paid to the results obtained to avoid a
resultant product having less desirable overall properties.
[0054] The composite elastic material has a density less than about
0.085 g per cubic cm, in its initial (non-stretched and recovered)
state and a CD tensile strength of greater than about 0.68 pounds
per inch. The composite material can have a cup crush less than
about 120 g per cm and can have a cup crush to density ratio of
less than about 1579 cm.sup.2 and greater than about 950 cm.sup.2.
Preferably, the cup crush to density ratio can be less than about
1500 cm and greater than about 1000 cm.sup.2. More preferably, the
cup crush to density ratio can be less than about 1400 cm.sup.2 and
greater than about 1100 cm.sup.2. Most preferably, the cup crush to
density ratio can be less than about 1300 cm.sup.2 and greater than
about 1100 cm.sup.2.
[0055] The composite elastic material can have a CD tensile
strength of greater than about 308.4 gm (0.68 lbs.). A preferred CD
tensile strength is of greater than about 317.5 gm (0.70 lbs.). A
more preferred CD tensile strength is of greater than about 340.2
gm (0.75 lbs.) A slightly more preferred CD tensile strength is of
greater than about 3 62.9 gm (0.80 lbs.) A yet more preferred CD
tensile strength is of greater than about 385.6 gm (0.85 lbs.). A
much more preferred CD tensile strength is of greater than about
408.2 gm (0.90 lbs.) A very much more preferred CD tensile strength
is of greater than about 430.9 gm (0.95 lbs.). The most preferred
CD tensile strength is of greater than about 453.6 gm (1.0 lbs.).
Accordingly, it is desired to have the highest tensile strength
without adversely effecting the other properties of the composite
to such an extent that the composite becomes undesirable in the
marketplace due to a lack of softness and cloth-like feel,
[0056] The basis weight (in grams per square meter, g/m.sup.2 or
gsm) is calculated by dividing the dry weight by the area (in
square meters). The density of the wet-wipe, as used herein, is a
"wet density" and is calculated as the basis weight (in grams per
square meter, g/m2 or gsm) divided by the thickness of the wet-wipe
after wetting with the solution.
[0057] The wet-wipes of the present invention include a basesheet
of the composite elastic material and a liquid. The liquid can be
any solution that can be absorbed into the wet-wipe basesheet and
may include any suitable components that provide the desired wiping
properties. For example, the components may include water,
emollients, surfactants, fragrances, preservatives, chelating
agents, pH buffers or combinations thereof as are known to those
skilled in the art. The liquid may also contain lotions and/or
medicaments.
[0058] The amount of liquid contained within each wet-wipe may vary
depending upon the type of material being used to provide the
wet-wipe, the type of liquid being used, the type of container
being used to store the wet-wipes, and the desired end use of the
wet-wipe. Generally, each wet-wipe can contain from about 150 to
about 600 weight percent and preferably from about 250 to about 450
weight percent liquid based on the dry weight of the wipe for
improved wiping. In a more preferred embodiment, the amount of
liquid contained within the wet-wipe is from about 300 to about 400
weight percent and desirably about 330 weight percent based on the
dry weight of the wet-wipe. If the amount of liquid is less than
the above-identified ranges, the wet-wipe can be too dry and may
not adequately perform. If the amount of liquid is greater than the
above-identified ranges, the wet-wipe can be oversaturated and
soggy and the liquid may undesirably pool in the bottom of the
container.
[0059] Each wet-wipe is generally rectangular in shape and may have
any suitable unfolded width and length. For example, the wet-wipe
may have an unfolded length of from about 2.0 to about 80.0
centimeters and desirably from about 10.0 to about 27.0
centimeters, and an unfolded width of from about 2.0 to about 80.0
centimeters and desirably from about 10.0 to about 25.0
centimeters. Preferably, each individual wet-wipe is arranged in an
interfolded configuration and stacked one on top of the other to
provide a stack of wet-wipes suitable for pop-up type dispensing.
Such folded configurations are known to those skilled in the art
and include c-folded, z-folded, quarter-folded configurations and
the like. The stack of folded wet-wipes are typically placed in an
interior of a container, such as a plastic tub or flexible bag, to
provide a package of wet-wipes for eventual sale to the consumer.
Alternatively, the wet-wipes may include a continuous strip of
material, which has perforations separating individual wet-wipes
and which may be arranged in a stack or wound into a roll for
individual dispensing.
[0060] The layered basesheet of the wet-wipes of the present
invention includes at least two layers of material having different
physical properties. The different physical properties which a
layer may be configured to provide by selecting the appropriate
materials include softness, resiliency, strength, flexibility,
integrity, toughness, absorbency, liquid retention, thickness, tear
resistance, surface texture, drapability, hand, wettability,
wicking ability and the like, and combinations thereof. Preferably,
the materials used for the layered basesheet are configured to
provide softness and flexibility while maintaining adequate
strength, integrity and resiliency, particularly when wetted. For
example, the wet-wipes may include at least one layer of material
which is configured to provide strength and resilience to the
wet-wipe and at least one other layer which is configured to
provide a soft, gentle wiping surface to the wet-wipe. Preferably,
the wet-wipes include a soft layer on each side of a strong and
resilient layer such that both exposed surfaces of the wipe provide
a soft, gentle surface for contact with the skin.
[0061] Elements in the drawings which are the same or similar in
more than one view may be designated by the same reference number
for clarity of description.
[0062] FIG. 1 illustrates a process, 10, for forming a
stretch-bonded laminate that includes an elastic fibrous web 12.
The elastic fibrous web 12 is prepared in a web forming machine 100
(illustrated in detail in FIG. 2) and travels in the direction
indicated by the arrows associated therewith. The elastic fibrous
web layer 12 passes through an S-roller arrangement 16 before
entering the horizontal calender having a patterned calender roller
20 and an anvil roller 22. Calender roller 20 can have from 1 to
about 30% embossing pin bond area with the preferred area being
from about 12 to about 14%. Both the anvil and pattern rollers can
be heated to provide thermal point bonding as described above. The
temperature and nip forces required to achieve adequate bonding are
dependent on the material being laminated. It should be noted that
the positions of the calender roller 20 and an anvil roller 22 in
FIG. 1 are illustrative only and can be reversed.
[0063] A first gatherable layer 24 and a second gatherable layer 28
are prepared in the coform banks 2 and 4 (illustrated in detail in
FIG. 3) and are guided and.backslash.or tensioned by rollers 9.
FIG. 1 shows numerous rollers for guiding and.backslash.or
tensioning the gatherable layers 24 or 28. For clarity of
illustration not all rollers are labeled with reference number 9.
It will be understood that all schematic depictions of rollers 9,
e.g. circles in contact with a layer 24 or 28, as well as composite
40, in FIG. 1 are guiding and.backslash.or tensioning rollers. The
gatherable layers 24 and 28 further pass through the horizontal
calender arrangement 20, 22 with elastic layer 12. The layers are
bonded by the calender roller 20 and the anvil roller 22 to form
composite 40. The gatherable layers can be formed using one or more
sets of extruders for providing the microfibers. The microfibers
can be formed by extrusion processes such as, for example,
meltblowing processes or spunbonding.
[0064] The coherent integrated fibrous structure of layers 24 and
28 may be formed by the microfibers and wood pulp fibers without
any adhesive, molecular or hydrogen bonds between the two different
types of fibers. The absorbent fibers are preferably distributed
uniformly throughout the matrix of microfibers to provide a
homogeneous material. The material is formed by initially forming a
primary air stream containing the melt blown microfibers, forming a
secondary air stream containing the wood pulp fibers, merging the
primary and secondary streams under turbulent conditions to form an
integrated air stream containing a thorough mixture of the
microfibers and wood pulp fibers, and then directing the integrated
air stream onto a forming surface to air form the fabric-like
material. The microfibers are in a soft nascent condition at an
elevated temperature when they are turbulently mixed with the wood
pulp fibers in air.
[0065] The coform layer(s), layers 24 and 28 in the illustrated
embodiment, can have from 20-50 wt. % of polymer fibers and 80-50
wt. % of pulp fibers. The preferred ratio of polymer fibers to pulp
fibers can be from 25-40 wt. % of polymer fibers and 75-60 wt. % of
pulp fibers. A more preferred ratio of polymer fibers to pulp
fibers can be from 30-40 wt. % of polymer fibers and 70-60 wt. % of
pulp fibers. The most preferred ratio of polymer fibers to pulp
fibers can be from 35 wt. % of polymer fibers and 65 wt. % of pulp
fibers.
[0066] Non-limiting examples of the polymers suitable for
practicing the invention are polyolefin materials such as, for
example, polyethylene, polypropylene and polybutylene, including
ethylene copolymers, propylene copolymers and butylene copolymers
thereof. A particularly useful polypropylene is Basel PF-105.
Additional polymers are disclosed in U.S. Pat. No. 5,385,775.
[0067] Fibers of diverse natural origin are applicable to the
invention. Digested cellulose fibers from softwood (derived from
coniferous trees), hardwood (derived from deciduous trees) or
cotton linters may be utilized. Fibers from Esparto grass, bagasse,
kemp, flax, and other lignaceous and cellulose fiber sources may
also be utilized as raw material in the invention. For reasons of
cost, ease of manufacture and disposability, preferred fibers are
those derived from wood pulp (i.e., cellulose fibers). A commercial
example of such a wood pulp material is available from Weyerhaeuser
as CF-405. Generally wood pulps will be utilized. Applicable wood
pulps include chemical pulps, such as Kraft (i.e., sulfate) and
sulfite pulps, as well as mechanical pulps including, for example,
ground wood pulp, thermomechanical pulp (i.e., TMP) and
chemithermomechanical pulp (i.e., CTMP). Completely bleached,
partially bleached and unbleached fibers are useful herein. It may
frequently be desired to utilize bleached pulp for its superior
brightness and consumer appeal.
[0068] Also useful in the present invention are fibers derived from
recycled paper, which can contain any or all of the above
categories as well as other non-fibrous materials such as fillers
and adhesives used to facilitate the original paper making
process.
[0069] The elastic fibrous web 12 passes through S-rollers 16 in a
reverse-S path as viewed in FIG. 1. From the S-roll arrangement,
the elastic fibrous web 12 passes through pressure nip 32 formed in
the horizontal calender 20, 22 by a bonding roller arrangement.
Additional S-roll arrangements (not shown) can be introduced
between the illustrated S-roller arrangement and the calender
roller arrangement to stabilize the stretched material and to
control the amount of stretching. Because the peripheral linear
speed of the rollers of the S-roll arrangement is controlled to be
less than the peripheral linear speed of the rollers of the
calender roller arrangement, the elastic fibrous web 12 is
tensioned between the S-roll arrangement and the pressure nip 32
formed in the horizontal calender roller arrangement. The filaments
of the elastic fibrous web 12 typically run along the direction
that the web is stretched so that they can provide the desired
stretch properties in the finished composite material. By adjusting
the difference in the speeds of the rollers, the elastic fibrous
web is tensioned so that it stretches a desired amount and is
maintained in a stretched condition while the gatherable layers 24
and 28 are joined to the elastic fibrous web 12 during their pass
through the calender roller arrangement to form a composite elastic
material 40. The elastic fibrous web can be stretched in the range
from about 25% (i.e., a 1 cm length can be stretched to 1.25 cm) to
about 300% (i.e., a 1 cm length can be stretched to 4 cm) of its
relaxed length. Preferably, the web can be stretched to from about
30% to about 150% of its relaxed length. More preferably, the web
can be stretched to from about 75% to about 100% of its relaxed
length.
[0070] The composite elastic material, 40, can be relaxed upon
release of the tensioning force provided by the S-roll arrangement
and the calender rollers. The gatherable layers are gathered in the
composite elastic material 40. The composite elastic material 40 is
then wound up on a winder roll 42. Optionally, composite elastic
material 40 is activated by heat treatment in a heat activation
unit 44. Processes of making composite elastic materials of this
type are described in, for example, U.S. Pat. No. 4,720,415 to
Vander Wielen et al. and U.S. Pat. No. 5,385,775 to Wright.
[0071] In an alternative embodiment the gatherable layer(s) can be
supplied from a supply roll(s) (not shown) in place of the coform
banks 2 and 4. When a second gatherable layer 28 is employed, this
would be supplied from a supply roll separate from the supply roll
for layer 24.
[0072] Gatherable layers 24 and 28 can be non-woven materials such
as, for example, spunbonded webs, meltblown webs, air laid layer
webs, bonded carded webs, hydroentangled webs, wet-formed webs or
any combination thereof. In one embodiment of the present
invention, one or both of gatherable layers 24 and 28 is a
multilayer material having, for example, at least one layer of
spunbonded web joined to at least one layer of meltblown web,
bonded carded web or other suitable material.
[0073] One or both of the gatherable layers 24 and 28 can be a
composite material made of a mixture of two or more different
fibers or a mixture of fibers and particulates. Such mixtures can
be formed by adding fibers and/or particulates to the gas stream in
which meltblown fibers are carried so that an intimate entangled
commingling of meltblown fibers and other materials, e.g., wood
pulp, staple fibers and particulates such as, for example,
hydrocolloid (hydrogel) particulates commonly referred to as
superabsorbent materials, occurs prior to collection of the
meltblown fibers upon a collecting device to form a coherent web of
randomly dispersed meltblown fibers and other materials such as
disclosed in U.S. Pat. No. 4,100,324, to Anderson et al.
[0074] A coherent integrated fibrous structure can be formed by the
microfibers and absorbent fibers without any adhesive, molecular or
hydrogen bonds between the two different types of fibers. The
absorbent fibers are preferably distributed uniformly throughout
the matrix of microfibers to provide a homogeneous material. The
material is formed by initially forming a primary air stream
containing the melt blown microfibers, forming a secondary air
stream containing the wood pulp fibers, merging the primary and
secondary streams under turbulent conditions to form an integrated
air stream containing a thorough mixture of the microfibers and
wood pulp fibers, and then directing the integrated air stream onto
a forming surface to air form the fabric-like material. The
microfibers are in a soft nascent condition at an elevated
temperature when they are turbulently mixed with the wood pulp
fibers in air.
[0075] In one embodiment, gatherable layers 24 and 28 are coform
layers having from 20-50 wt. % of polymer fibers and 80-50 wt. % of
pulp fibers. The preferred ratio of polymer fibers to pulp fibers
can be from 25-40 wt. % of polymer fibers and 75-60 wt. % of pulp
fibers. A more preferred ratio of polymer fibers to pulp fibers can
be from 30-40 wt. % of polymer fibers and 70-60 wt. % of pulp
fibers. The most preferred ratio of polymer fibers to pulp fibers
can be from 35 wt. % of polymer fibers and 65 wt. % of pulp
fibers.
[0076] One or both of the gatherable layers 24 and 28 can be made
of pulp fibers, including wood pulp fibers, to form a material such
as, for example, a tissue layer. Additionally, the gatherable
layers can be layers of hydraulically entangled fibers such as, for
example, hydraulically entangled mixtures of wood pulp and staple
fibers such as disclosed in U.S. Pat. No. 4,781,966, to Taylor.
[0077] The gatherable layers 24 and 28 can be joined to the elastic
fibrous web 12 at least at two places by any suitable means such
as, for example, thermal bonding or ultrasonic welding which
softens at least portions of at least one of the materials, usually
the elastic fibrous web because the elastomeric materials used for
forming the elastic fibrous web 12 have a lower softening point
than the components of the gatherable layers 24 and 28. Joining can
be produced by applying heat and/or pressure to the overlaid
elastic fibrous web 12 and the gatherable layers 24 and 28 by
heating these portions (or the overlaid layer) to at least the
softening temperature of the material with the lowest softening
temperature to form a reasonably strong and permanent bond between
the re-solidified softened portions of elastic fibrous web 12 and
gatherable layers 24 and 28.
[0078] The calender (bonding) roller arrangement includes a smooth
anvil roller 22 and a patterned calendar roller 20, such as, for
example, a pin embossing roller arranged with a smooth anvil
roller. One or both of the smooth anvil roller and the calendar
roller can be heated and the pressure between these two rollers can
be adjusted by well-known structures to provide the desired
temperature, if any, and bonding pressure to join the gatherable
layers to the elastic fibrous web. As can be appreciated, the
bonding between the gatherable layers and the elastic sheet is a
point bonding. Various bonding patterns can be used, depending upon
the desired tactile properties of the final composite laminate
material. The bonding points are preferably evenly distributed over
the bonding area of the composite material. One embodiment of the
bonding of the gatherable layer(s) and the elastic layer is
explained below in conjunction with FIG. 10.
[0079] With regard to thermal bonding, one skilled in the art will
appreciate that the temperature to which the materials, or at least
the bond sites thereof, are heated for heat-bonding will depend not
only on the temperature of the heated roller(s) or other heat
sources but on the residence time of the materials on the heated
surfaces, the compositions of the materials, the basis weights of
the materials and their specific heats and thermal conductivities.
Typically, the bonding can be conducted at a temperature of from
about 40.degree. to about 80.degree. C. Preferably, the bonding can
be conducted at a temperature of from about 55.degree. to about
75.degree. C. More preferably, the bonding can be conducted at a
temperature of from about 60.degree. to about 70.degree. C. The
typical pressure range, on the rollers, can be from about 18 to
about 56.8 Kg per linear cm (KLC). The preferred pressure range, on
the rollers, can be from about 18 to about 24 Kg per linear cm
(KLC) However, for a given combination of materials, and in view of
the herein contained disclosure, the processing conditions
necessary to achieve satisfactory bonding can be readily determined
by one of skill in the art.
[0080] The elastic fibrous web 12 can also be preformed and unwound
from a supply roll (not shown) and passed directly through the
S-roll arrangement 16 before being bonded to at least one
gatherable layer 24 or 28 at nip 32. Gatherable layers 24 and 28
can be preformed and unwound from supply rolls (not shown) and
passed directly through the horizontal calender arrangement 20,
22.
[0081] Conventional drive means, e.g. electric motors, and other
conventional devices which can be utilized in conjunction with the
apparatus of FIG. 1 are well known and, for purposes of clarity,
have not been illustrated.
[0082] One component of the composite elastic material 40 is the
elastic fibrous web 12. The elastic web can be a web including
meltblown fibers or the web can contain two or more layers of
materials; where at least one layer can be a layer of elastomeric
meltblown fibers and at least one layer can contain substantially
parallel rows of elastomeric fibers autogenously bonded to at least
a portion of the elastomeric meltblown fibers. The elastomeric
fibers can have an average diameter ranging from about 40 to about
750 microns and extend along length (i.e. machine direction) of the
fibrous web. The elastomeric fibers can have an average diameter in
the range from about 50 to about 500 microns, for example, from
about 100 to about 200 microns.
[0083] The elastic fibers extending along the length (i.e., MD) of
the fibrous web increases the tensile modulus about 10% more than
the increase in the tensile modulus of the fibrous web in the width
(i.e. CD). For example, the tensile modulus of an elastic fibrous
web can be about 20% to about 90% greater in the MD than the
tensile modulus of a substantially isotropic non-woven web having
about the same basis weight containing only elastomeric meltblown
fibers. This increased MD tensile modulus increases the amount of
retraction that can be obtained for a given basis weight of the
composite elastic material.
[0084] The elastic fibrous web can contain at least about 20
percent, by weight, of elastomeric fibers. For example, the elastic
fibrous web can contain from about 20 percent to about 100 percent,
by weight, of the elastomeric fibers. Preferably, the elastomeric
fibers can constitute from about 20 to about 60 percent, by weight,
of the elastic fibrous web. More preferably, the elastomeric fibers
can constitute from about 20 to about 40 percent, by weight, of the
elastic fibrous web.
[0085] FIG. 2 is a schematic view of system 100 for forming an
elastic fibrous web, which can be used as a component of the
composite elastic material of the present invention. In forming the
fibers which are used in the elastic fibrous web, pellets or chips,
etc. (not shown) of an extrudable elastomeric polymer are
introduced into pellet hoppers 102 and 104 of extruders 106 and
108.
[0086] Each extruder has an extrusion screw (not shown) which is
driven by a conventional drive motor (not shown). As the polymer
advances through the extruder, due to rotation of the extrusion
screw by the drive motor, it is progressively heated to a molten
state. Heating the polymer to the molten state can be accomplished
in a plurality of discrete steps with its temperature being
gradually elevated as it advances through discrete heating zones of
the extruder 106 toward a meltblowing die 110 and extruder 108
toward a continuous filament forming unit 112. The meltblowing die
110 and the continuous filament forming unit 112 can be yet another
heating zone where the temperature of the thermoplastic resin is
maintained at an elevated level for extrusion. Heating of the
various zones of the extruders 106 and 108 and the meltblowing die
110 and the continuous filament forming unit 112 can be achieved by
any of a variety of conventional heating arrangements (not
shown).
[0087] The elastomeric filament component of the elastic fibrous
web can be formed utilizing a variety of extrusion techniques. For
example, the elastic fibers can be formed utilizing one or more
conventional meltblowing die units which have been modified to
remove the heated gas stream (i.e., the primary air stream) which
flows generally in the same direction as that of the extruded
threads to attenuate the extruded threads. This modified
meltblowing die unit 112 usually extends across a foraminous
collecting surface 114 in a direction which is substantially
transverse to the direction of movement of the collecting surface
114. The modified die unit 112 includes a linear array 116 of small
diameter capillaries aligned along the transverse extent of the die
with the transverse extent of the die being approximately as long
as the desired width of the parallel rows of elastomeric fibers
which is to be produced. That is, the transverse dimension of the
die is the dimension which is defined by the linear array of die
capillaries. Typically, the diameter of the capillaries can be on
the order of from about 0.025 cm (0.01 in) to about 0.076 cm (0.03
in). Preferably, the diameter of the capillaries can be from about
0.0368 cm (0.0145 in) to about 0.0711 cm (0.028 in). More
preferably, the diameter of the capillaries can be from about 0.06
cm (0.023 in) to about 0.07 cm (0.028 in). From about 5 to about 50
such capillaries can be provided per linear inch of die face.
Typically, the length of the capillaries can be from about 0.127 cm
(0.05 in) to about 0.508 cm (0.20 in). Typically, the length of the
capillaries can be about 0.287 cm (0.113 in) to about 0.356 cm
(0.14 in) long. A meltblowing die can extend from about 51 cm (20
in) to about 185 or more cm (about 72 in) in length in the
transverse direction. One familiar with the art would realize that
the capillaries could be a shape other than circular, such as, for
example, triangular, rectangular, and the like; and that the
spacing or density of the capillaries can vary across the length of
the die.
[0088] Since the heated gas stream (i.e., the primary air stream)
which flows past the die tip is greatly reduced or absent, it is
desirable to insulate the die tip or provide heating elements to
ensure that the extruded polymer remains molten and flowable while
in the die tip. Polymer is extruded from the array 116 of
capillaries in the modified die unit 112 to create extruded
elastomeric fibers 118.
[0089] The extruded elastomeric fibers 118 have an initial velocity
as they leave the array 116 of capillaries in the modified die unit
112. These fibers 118 are deposited upon a foraminous surface 114,
which should be moving at least at the same velocity as the initial
velocity of the elastic fibers 118. This foraminous surface 114 is
an endless belt conventionally driven by rollers 120. The fibers
118 are deposited in substantially parallel alignment on the
surface of the endless belt 114 which is rotating as indicated by
the arrow 122 in FIG. 2. Vacuum boxes (not shown) can be used to
assist in retention of the matrix on the surface of the belt 114.
The tip of the die unit 112 is positioned as close as practical to
the surface of the foraminous belt 114 upon which the continuous
elastic fibers 118 are collected. For example, this forming
distance can be from about 2 inches to about 10 inches. Desirably,
this distance is from about 2 inches to about 8 inches.
[0090] It may be desirable to have the foraminous surface 114
moving at a speed that is much greater than the initial velocity of
the elastic fibers 118 in order to enhance the alignment of the
fibers 118 into substantially parallel rows and/or elongate the
fibers 118 so they achieve a desired diameter. For example,
alignment of the elastomeric fibers 118 can be enhanced by having
the foraminous surface 114 move at a velocity from about 2 to about
10 times greater than the initial velocity of the elastomeric
fibers 118. Even greater speed differentials can be used if
desired. While different factors will affect the particular choice
of velocity for the foraminous surface 114, it will typically be
from about four to about eight times faster than the initial
velocity of the elastomeric fibers 118.
[0091] Desirably, the continuous elastomeric fibers are formed at a
density per inch of width of material which corresponds generally
to the density of capillaries on the die face. For example, the
filament density per inch of width of material may range from about
10 to about 120 such fibers per inch width of material. Typically,
lower densities of fibers (e.g., 10-35 fibers per inch of width)
can be achieved with only one filament forming die. Higher
densities (e.g., 35-120 fibers per inch of width) can be achieved
with multiple banks of filament forming equipment.
[0092] The meltblown fiber component of the elastic fibrous web is
formed utilizing a conventional meltblowing device 124. Meltblowing
devices 124 generally extrude a thermoplastic polymer resin through
a plurality of small diameter capillaries of a meltblowing die as
molten threads into a heated gas stream (the primary air stream)
which is flowing generally in the same direction as that of the
extruded threads so that the extruded threads are attenuated, i.e.,
drawn or extended, to reduce their diameter. Such meltblowing
techniques, and apparatus therefor, are discussed fully in U.S.
Pat. No. 4,663,220 to Wisneski et al.
[0093] In the meltblown die arrangement 110, the position of air
plates which, in conjunction with a die portion define chambers and
gaps, can be adjusted relative to the die portion to increase or
decrease the width of the attenuating gas passageways so that the
volume of attenuating gas passing through the air passageways
during a given time period can be varied without varying the
velocity of the attenuating gas. Generally speaking, lower
attenuating gas velocities and wider air passageway gaps are
generally preferred if substantially continuous meltblown fibers or
microfibers are to be produced.
[0094] The two streams of attenuating gas converge to form a stream
of gas which entrains and attenuates the molten threads, as they
exit the orifices, into fibers depending upon the degree of
attenuation, microfibers, of a small diameter which is usually less
than the diameter of the orifices. The gas-borne fibers or
microfibers 126 are blown, by the action of the attenuating gas,
onto a collecting arrangement which, in the embodiment illustrated
in FIG. 2, is the foraminous endless belt 114 which carries the
elastomeric filaments in substantially parallel alignment. The
fibers or microfibers 126 are collected as a coherent matrix of
fibers on the surface of the elastomeric fibers 118 and foraminous
endless belt 114 which is rotating as indicated by the arrow 122 in
FIG. 2. If desired, the meltblown fibers or microfibers 126 can be
collected on the foraminous endless belt 114 at numerous
impingement angles. Vacuum boxes (not shown) can be used to assist
in retention of the matrix on the surface of the belt 114.
Typically the tip 128 of the die 110 is from about 6 inches to
about 14 inches from the surface of the foraminous belt 114 upon
which the fibers are collected. The entangled fibers or microfibers
124 autogenously bond to at least a portion of the elastic
continuous fibers 118 because the fibers or microfibers 124 are
still somewhat tacky or molten while they are deposited on the
elastic continuous fibers 118, thereby forming the elastic fibrous
web 130. The fibers are quenched by allowing the fibers to cool to
a temperature below about 38.degree. C.
[0095] As discussed above, the elastomeric fibers and elastomeric
meltblown fibers can be deposited upon a moving foraminous surface.
In one embodiment of the invention, meltblown fibers can be formed
directly on top of the extruded elastomeric fibers. This is
achieved by passing the fibers and the foraminous surface under
equipment which produces meltblown fibers. Alternatively, a layer
of elastomeric meltblown fibers can be deposited on a foraminous
surface and substantially parallel rows of elastomeric fibers can
be formed directly upon the elastomeric meltblown fibers. Various
combinations of filament forming and fiber forming equipment can be
set up to produce different types of elastic fibrous webs. For
example, the elastic fibrous web may contain alternating layers of
elastomeric fibers and elastomeric meltblown fibers. Several dies
for forming meltblown fibers or creating elastomeric fibers may
also be arranged in series to provide superposed layers of
fibers.
[0096] The elastomeric meltblown fibers and elastomeric fibers can
be made from any material that can be manufactured into such fibers
such as natural polymers or synthetic polymers. Generally, any
suitable elastomeric fiber forming resins or blends containing the
same can be utilized for the elastomeric meltblown fibers and any
suitable elastomeric filament forming resins or blends containing
the same can be utilized for the elastomeric fibers. The fibers can
be formed from the same or different elastomeric resin.
[0097] For example, the elastomeric meltblown fibers and/or the
elastomeric fibers can be made from block copolymers having the
general formula A-B-A' where A and A' are each a thermoplastic
polymer endblock which can contain a styrenic moiety such as a poly
(vinyl arene) and where B is an elastomeric polymer midblock such
as a conjugated diene or a lower alkene polymer. The block
copolymers can be, for example,
(polystyrene/poly(ethylene-butylene)/polystyrene) block copolymers
available from the Shell Chemical Company under the trademark
KRATON. One such block copolymer can be, for example, KRATON.TM.
G-1657.
[0098] Other exemplary elastomeric materials which can be used
include polyurethane elastomeric materials such as, for example,
those available under the trademark ESTANE from B.F. Goodrich &
Co., polyamide elastomeric materials such as, for example, those
available under the trademark PEBAX from the Rilsan Company, and
polyester elastomeric materials such as, for example, those
available under the trade designation Hytrel from E.I. DuPont De
Nemours & Company. Formation of elastomeric meltblown fibers
from polyester elastic materials is disclosed in, for example, U.S.
Pat. No. 4,741,949.
[0099] Useful elastomeric polymers also include, for example,
elastic copolymers of ethylene and at least one vinyl monomer such
as, for example, vinyl acetates, unsaturated aliphatic
monocarboxylic acids, and esters of such monocarboxylic acids. The
elastic copolymers and formation of elastomeric meltblown fibers
from those elastic copolymers are disclosed in, for example, U.S.
Pat. No. 4,803,117 to Daponte. Also, suitable elastomeric polymers
are those prepared using metallocene catalysts such as those
disclosed in International Application WO 00/48834.
[0100] Processing aids can be added to the elastomeric polymer. For
example, a polyolefin can be blended with the elastomeric polymer
(e.g., the A-B-A elastomeric block copolymer) to improve the
processability of the composition. The polyolefin must be one
which, when so blended and subjected to an appropriate combination
elevated pressure and elevated temperature conditions, extrudable,
in blended form, with the elastomeric polymer. Useful blending
polyolefin materials include, for example, polyethylene,
polypropylene and polybutylene, including ethylene copolymers,
propylene copolymers and butylene copolymers. A particularly useful
polyethylene can be obtained from the U.S.I. Chemical Company under
the trade designation Betrothing NA 601 (also referred to herein as
PE NA 601 or polyethylene NA 601). Two or more of the polyolefins
can be utilized. Extrudable blends of elastomeric polymers and
polyolefins are disclosed in, for example, previously referenced
U.S. Pat. No. 4,663,220.
[0101] The elastomeric meltblown fibers and/or the elastomeric
fibers can have some tackiness adhesiveness to enhance autogenous
bonding. For example, the elastomeric polymer itself can be tacky
when formed into fibers and, optionally, a compatible tackifying
resin can be added to the extrudable elastomeric compositions
described above to provide tackified elastomeric fibers and/or
fibers that autogenously bond. In regard to the tackifying resins
and tackified extrudable elastomeric compositions, note the resins
and compositions as disclosed in U.S. Pat. No. 4,787,699, to
Moulin.
[0102] Any tackifier resin can be used which is compatible with the
elastomeric polymer and can withstand the high processing (e.g.,
extrusion) temperatures. If the elastomeric polymer (e.g., A-B-A
elastomeric block copolymer) is blended with processing aids such
as, for example, polyolefins or extending oils, the tackifier resin
should also be compatible with those processing aids. Generally,
hydrogenated hydrocarbon resins are preferred tackifying resins,
because of their better temperature stability. REGALREZ.TM. and
ARKON.TM. series tackifiers are examples of hydrogenated
hydrocarbon resins. ZONATAK.TM. 501 lite is an example of a terpene
hydrocarbon. REGALREZ.TM. hydrocarbon resins are available from
Hercules incorporated. ARKON.TM. series resins are available from
Arakawa Chemical (U.S.A.) Inc. The present invention is not limited
to use of these tackifying resins, and other tackifying resins
which are compatible with the other components of the composition
and can withstand the high processing temperatures, can also be
used.
[0103] Typically, the blend used to form the elastomeric fibers
include, for example, from about 40 to about 95 percent by weight
elastomeric polymer, from about 5 to about 40 percent polyolefin
and from about 5 to about 40 percent resin tackifier. For example,
a particularly useful composition included, by weight, about 61 to
about 65 percent KRATON.TM. G-1657, about 17 to about 23 percent
polyethylene polymer, and about 15 to about 20 percent REGALREZ.TM.
1126. The preferred polymers are metallocene catalyzed polyethylene
polymers, such as, for example Affinity.RTM. polymers, available
from Dow.RTM. Chemical Company as Affinity XUS59400.03L.
[0104] The elastomeric meltblown fiber component of the present
invention can be a mixture of elastic and nonelastic fibers or
particulates. For example, such a mixture, is disclosed in U.S.
Pat. No. 4,209,563 to Sisson, where elastomeric and non-elastomeric
fibers are commingled to form a single coherent web of randomly
dispersed fibers. Another example of such an elastic composite web
could be made by a technique disclosed in previously cited U.S.
Pat. No. 4,741,949 to Morman et al. This patent discloses an
elastic non-woven material which includes a mixture of meltblown
thermoplastic fibers and other materials. The fibers and other
materials are combined in the gas stream in which the meltblown
fibers are borne so that an intimate entangled commingling of
meltblown fibers and other materials, e.g., wood pulp, staple
fibers or particulates such as, for example, activated charcoal,
clays, starches, or hydrocolloid (hydrogel) particulates commonly
referred to as super-absorbents occurs prior to collection of the
fibers upon a collecting device to form a coherent web of randomly
dispersed fibers.
[0105] FIG. 3 is a schematic view of an exemplary process for
forming a gatherable web or layer 24 and 28 such as coform, which
can be used as a component of the composite elastic material of the
invention. The matrix material comprising thermoplastic polymer
microfibers from the extruder banks 201 and 201A (201A is an
optional additional extruder bank) of the meltblowing extruders
202, are blended with the individualized absorbent fibers from the
pulp generator 206. The non-woven web 208 is carried along the
forming wire 210 to the calender or wound on a roll.
[0106] If desired, the composite elastic material of the invention
can be heat activated. Heat activation can provide dimensional
stability in the web by increasing the retraction that occurs in
the manufacturing process. Elevating the temperature of the web and
imparting energy to the elastomer can cause it to retract beyond
the range achievable at ambient conditions. There are numerous heat
activation methods including, but not limited to, through-air
heating, surface heating, infrared, microwave, and liquid transfer.
The heat activation step can also be executed in multiple locations
such as the in-line manufacturing process, after material winding,
or during converting. In-line through-air heat activation is the
method illustrated because it provides good heat transfer.
[0107] In the embodiment of this invention illustrated in FIG. 4,
the composite elastic web 40 is allowed to retract as much as
possible at ambient temperatures and fed into the heat activation
unit 44. Web 40 is stretched, heated to about 57.degree. C. and
allowed to retract. This retraction occurs after the web travels
from a vacuum drum in the heating section to a vacuum drum in the
quenching section. After this additional retraction has occurred
the web is cooled on the quench vacuum roll(s) to preserve this
retracted state as the web is processed further. More particularly,
a transfer roller 402 feeds web into heat activation unit 44. The
vacuum rolls 403 (two shown) provide the necessary residence time
for heat activation to occur. Heated air is supplied to the chamber
405 containing the vacuum rolls and evacuated through the center of
the vacuum rolls. If multiple rollers are employed they can be
operated at the same speed or at different speeds. One or more
vacuum rollers 404 is provided to allow residence time in the
quenching/cooling chamber 406 to reduce the fabric temperature to
ambient conditions. If multiple rollers are employed they can be
operated at the same speed or at different speeds. The quenching
vacuum roller(s) can be run at a slower speed than the vacuum
roller(s) in the heating section to allow retraction to occur prior
to cooling the web. The quenching roll/rolls can run from about 6%
to about 10% slower than the rolls in the heating section.
[0108] FIG. 5 shows a flowchart representing steps for producing a
composite or laminate according to the present invention. It is
believed that these steps are described herein and further
description in not necessary.
[0109] Various properties of the composite of the present invention
were determined during laboratory tests. The laboratory conditions
under which testing was performed generally adhere to ASTM E 171,
"Standard Atmospheres for Conditioning and Testing Materials", as
well as 21 CFR 58.61-63, "Good laboratory practices for nonclinical
laboratory studies" and CFR 211.160(b)(4), "Current Good
Manufacturing Practices for Finished Pharmaceuticals".
[0110] FIGS. 11 and 12 show a cup-crush testing system 1100, which
includes a cup forming assembly 1102 and force testing unit 1103.
The force testing unit 1103 includes a force sensor 1104 to which
is cantilevered a rigid rod 1105. A hemispherical foot 1108 is
positioned at the free end of rod 1105. Force sensor 1104 includes
electronics and mechanics for measuring the force experienced at
foot 1108 and transferred through rigid rod 1105. The assembly 1102
includes mating, top-hat shaped former cups 1110 and 1112, which
grip a sheet 1202 (such as wet-wipe 1000, see FIG. 10), at at least
four points. The four corners 1106 of sheet 1202 extend outside of
the assembly 1102. The cup 1112 is removed after forming sheet 1202
into a cup. A gripping ring 1114 holds the formed sheet 1202 in cup
1110 during testing.
[0111] One measure of the softness of a non-woven fabric sheet 1202
is determined according to the "cup crush" test by system 1100. The
cup crush test evaluates fabric stiffness by measuring the peak
load (also called the "cup crush load" or just "cup crush")
required for a 4.5 cm diameter hemispherically shaped foot 1108 to
crush a 17.8 cm by 17.8 cm piece of fabric 1202 shaped into an
approximately 6.5 cm diameter by 6.5 cm tall cup shape, while the
now cup shaped fabric is surrounded by an approximately 6.5 cm
diameter cylinder cup 1110 to maintain a uniform deformation of the
cup shaped fabric 1102. There can be gaps between the ring 1114 and
forming cup 1110, but at least four comers 1106 must be fixedly
pinched therebetween. The foot 1108 and cylinder cup 1110 are
aligned to avoid contract between the cup walls and the foot that
could affect the readings. The load is measured in grams, and
recorded a minimum of twenty times per second while the foot is
descending at a rate of about 406 mm per minute. The cup crush test
provides a value for the total energy required to crush a sample
(the "cup crush energy") which is the energy over a 4.5 cm range
beginning 0.5 cm below the top of the fabric cup, i.e., the area
under the curve formed by the load in grams on one axis and the
distance the foot travels in millimeters on the other. Cup crush
energy is reported in gm-mm (or inch-pounds). A lower cup crush
value indicates a softer material. A suitable device for measuring
cup crush is a model FTD-G-500 load cell (500 gram range) available
from the Schaevitz Company, Pennsauken, N.J.
[0112] The peak load tensile test is a measure of breaking strength
and elongation or strain of a fabric when subjected to
unidirectional stress. This test is known in the art and is similar
to ASTM-1117-80, section seven, which uses a 12-inch per minute
strain rate. The results are expressed in grams to break and
percent stretch before breakage. Higher numbers indicate a
stronger, more stretchable fabric. The term "load" means the
maximum load or force, expressed in units of weight, required to
break or rupture the specimen in a tensile test. The term "strain"
or "total energy" means the total energy under a load versus
elongation curve as expressed in weight-length units. The term
"elongation" means the increase in length of a specimen during a
tensile test and is given in percent. Values for tensile strength
and elongation are obtained using a specified width of fabric, in
this case 1 inch (25.4 mm), clamp width and a constant rate of
extension. The test is conducted using wet product as would be
representative of consumer use. Fabric testing can be conducted in
both the machine direction (MD) and cross-machine direction (CD)
which can be determined by one familiar with non-woven materials by
the orientation of the fibers. It is important that the samples be
either parallel or perpendicular to the machine direction to insure
accuracy. The test is conducted using a 2 inch (50.8 mm) wide clamp
with one smooth face and one 0.25 inch round horizontal rod
comprising each clamp mechanism. The specimen is clamped in, for
example, an Instron Model.TM., available from the Instron
Corporation, 2500 Washington St., Canton, Mass. 02021, or a
Thwing-Albert Model INTELLECT II available from the Thwing-Albert
Instrument Co., 10960 Dutton Rd., Phil., Pa. 19154, which have 3
inch (76 mm) long parallel clamps. This closely simulates fabric
stress conditions in actual use.
[0113] The caliper of the composite elastic materials of the
invention is a measure of thickness. The thickness is measured at
0.05 psi with a Starret-type bulk tester, in units of millimeters
using a 7.62 cm (3 in) diameter platen. This test is conducted on
the finished wet-wipe product and care must be taken to insure the
platen does not fall on a fold or wrinkle that has resulted from
packaging.
[0114] The density of the wet-wipe, as used herein, is a
wet-density calculated as the basis weight divided by the caliper
(measured wet). The wet thickness is employed so as to represent
the product as obtained by a consumer. The commercially available
wet-wipes that were used for comparison testing are usually only
available in the form of a wet finished product. Dry basis weight
is used to accurately assess the wet-density by elimination of
variability caused by the amount of solution on the various brands
of wet-wipes.
[0115] The wet-wipes are removed from their container and randomly
selected. Each wipe is unfolded, numbered and measured (length and
width). The wipes are stacked and compressed to about 15-20 metric
tons in a press for about 10 seconds. This step is repeated until a
steady stream of solution is no longer observed. The wipes are
draped over a rod and placed in a drying oven at 105.+-.2 degrees
C. for about 2 hours. The dry wipes are allowed to cool for about
14-15 minutes and weighed to .+-.0.01 g.
[0116] The invention will now be illustrated by the following
non-limiting examples.
EXAMPLE 1
[0117] Wet wipes were made as described in the present application.
Each wet wipe contained a three-layer laminate composite elastic
material, which included two gatherable outer coform layers and an
inner elastomeric core.
Elastomeric Core
[0118] The elastomeric layer in this example is produced using a
two bank meltblown process and a single continuous speed foraminous
belt. The first bank of the meltblown process was setup to extrude
elastomeric filaments/fibers directly onto the foraminous belt in a
substantially parallel configuration without the use of heated
primary air to draw the filaments. A metallocene-catalyzed
polyethylene resin available from DOW Chemical Company, under the
trade designation of Dow Affinity.TM. XUS59400.03L, were used to
produce the fibers at a nominal melt temperature of 220 degrees C.
The substantially parallel fibers were extruded through a spin beam
with a nominal hole size of 0.07 cm and a density of 7 holes per
cm. The velocity of the polymer through the spin beam and speed of
the foraminous belt were adjusted to produce a web of fibers with a
basis weight of 21 grams per square meter. The fiber web basis
weight, the density of the capillaries in the spin beam, and the
capillary size dictates the drawing ratio of the elastomeric
filaments.
[0119] The second bank in the meltblown process/system operates as
a conventional meltblown head. The molten thermoplastic is extruded
through fine die capillaries converging into a hot air stream,
which attenuates the filaments of molten material reducing their
diameter. The high velocity air stream carries these meltblown
fibers to the constant speed foraminous surface. Such a process is
disclosed for example in U.S. Pat. No. 3,849,241 to Butin. The
meltblown head used here utilizes 0.0368 cm diameter capillaries at
a density of 12 capillaries per cm, and operates at a melt
temperature of 250 degrees C. The elastomeric polymer used to
produce the meltblown fibers is a dry blended resin in the
following proportions: 80% Dow Affinity XUS59400.03L, 15% Regalrez
1126, and 5% Dow 6806. As the meltblown fibers are deposited on the
foraminous surface carrying the previously formed, substantially
parallel, filament autogeneous bonding occurs and discrete points
where the still molten fibers cross over the filaments. The basis
weight of the web prepared is about 9 grams per square meter.
[0120] The web is then cooled to a temperature less than about 35
degrees C. by drawing ambient air through the foraminous belt as
the web travels over a vacuum box. This cooling is required prior
to removing the web from the foraminous surface.
Stretching
[0121] The web is transported to an S-wrap roll arrangement by a
series of idler rollers. The S-wrap rollers are driven to control
their speed, and this combined with the large surface contact serve
as a nip. The speed of the foraminous meltblown forming belt and
S-wrap rollers travel at about the same speed and this speed is 50%
of the speed of the calender rolls. This speed difference results
in a 100% elongation of the elastic web between the S-wrap rolls
and the calender roll. This stretching effect reduces the basis
weight by about 50% and imparts significant stored energy to the
elastomeric web as it is presented to be joined with the gatherable
layers.
Gatherable Coform Layers
[0122] The gatherable coform layers were comprised of intermingled
polypropylene meltblown fibers and fiberized softwood pulp. The
polypropylene comprised 35 weight percent of the gatherable layer
with the softwood pulp comprising the remaining 65 weight percent.
Each coform layer is an air formed matrix produced utilizing a
coform process with two forming stations. At each forming station
an air stream containing fiberized softwood pulp (available under
the trade designation CF-405 from Weyerhaeuser Corporation) is
merged with two heated primary air streams containing polypropylene
(available from BASELL under the trade designation PF-105)
meltblown fibers. The two polypropylene meltblown streams oppose
each other at an angle of 90 degrees and the pulp air stream is
contained between these streams at an angle of 45 degrees to each.
The air streams merge under turbulent conditions at a distance of
approximately 20 cm above a constant speed foraminous surface. This
first coform layer then travels on the foraminous surface under a
second forming station producing a second layer of equal portions
and basis weight. The second coform layer is bonded through
mechanical entanglement to the first layer by virtue of the high
velocity forming air common to coform processes. The second
gatherable layer is formed in a similar fashion to the first.
[0123] The first and second gatherable layers are formed
simultaneously by different forming stations on separate foraminous
belting surfaces, which rotate in opposite directions conveying the
coform layers toward each other. The coform layers are then removed
from the foraminous surfaces and conveyed by conventional means to
the vertical calender.
Combining
[0124] After leaving the foraminous surfaces the first and second
gatherable layers enter the vertical embossing calender from
opposite directions as shown in FIG. 1. (Alternatively, the
gatherable layers could be traveling from a foraminous surface in
the same direction into a calender, and in yet in another
embodiment these gatherable layers may be transferred from a wound
roll rather than foraminous surface.)
[0125] The elastomeric web enters the calender between the two
gatherable layers in an elongated state (about twice the formed
length, or 100% elongation), and could come from a separate
foraminous surface as it does in the example, or from a wound roll.
The smooth anvil roll and patterned calender roll bond the layers
together at a plurality of discrete points in the configuration
shown in FIG. 10. The heated bond rolls and high pressure cause
additional mechanical entanglement and thermal bonding of the
polymers in the fabric. A temperature of 65 degrees C. and an
embossing pressure of 21 kg per linear centimeter are used
here.
Retracting
[0126] As the composite web leaves the calender the stored energy
in the elastomer is released as the web is conveyed at a decreasing
linear speed through the process and the elastomeric core gathers
the exterior layers. With the components described the retraction
occurs over a period of about 4 seconds and dictates an appropriate
free web span for the given calender roll speed. For example if the
calender roll has a linear speed of 5 meters per second then the
web must be free to retract and decelerate over a distance of 20
meters. The exemplary composite web described herein retracts about
25% during this gathering step. This results in an increase in the
basis weight of the web, corresponding to about 25%.
Heat Activation
[0127] In order to obtain further retraction and increase the
dimensional stability of the composite, same is transferred to a
foraminous drum where it is held at a fixed dimension by vacuum.
While held on the rotating, foraminous drum, or similar surface,
the temperature of the web is elevated near the glass transition
temperature of the elastomeric center layer by drawing a heated air
stream through the web. Monitoring the temperature of the
elastomeric portion of the composite is not possible as it is
located between the gatherable layers and therefore the temperature
of the external gatherable layers is used to monitor the process
and is measured as it exits transitions off the foraminous drum.
This is a reasonable approximation as the heat transfer with the
through-air process. The external web temperature required for this
example is about 55 degrees C. Once heated the web is transferred
to another vacuum drum, or similar surface, through space. This
second drum is traveling slower than the heated drum (approximately
5% for this example) and additional retraction occurs between the
two surfaces. Again an increase in basis weight of the web occurs.
The second drum draws ambient air through the web reducing the
temperature back to ambient following this retraction step.
[0128] The fabric can then be converted into individual wet wipes
using numerous cutting, folding, wetting, and stacking methods
known in the art. The wet wipes included a solution similar to that
currently being used with Kleenex.TM. Huggies.TM. Supreme Care
Scented baby wipes, which were commercially available from
Kimberly-Clark Corporation, a business having offices located in
Neenah, Wis. The wet wipes included about 330 weight percent of the
solution based on the dry weight of the wipe.
EXAMPLE 2
[0129] Following the procedure of Example 1, a composite elastic
material is prepared using an elastomeric web containing 100%
elastomeric meltblown fibers at a basis weight of 25 grams per
square meter.
EXAMPLE 3
[0130] A particularly suitable solution for the wet wipes of the
present invention was prepared according to the following
formulation:
1 Ingredient CTFA Designation wt. % Water 98.52 Potassium Laureth
mono alkyl phosphate 0.6 Glycerin 0.29 Polysorbate-20 0.30 Sodium
hydroxymethylglycinate 0.20 Propylparaben 0.1 Fragrance 0.05
[0131] The potassium laureth mono alkyl phosphate was commercially
available from Rhone-Poulenc under the trade designation RHODAFAC.
The Polysorbate-20 was commercially available from Rhone Poulenc
under the trade designation ALKAMULS PSML-20. The sodium
hydroxymethylglycinate was commercially available from Sutton Labs,
a business having offices located in Catham, N.J., under the trade
designation SUTTOCIDE A. Malic acid was then added to the solution
to bring the pH level to 5.5. The solution exhibited a silky,
lubricious feel and was relatively nonirritating to the skin.
EXAMPLE 4
[0132] A suitable solution for the wet wipes of the present
invention was prepared according to the following formulation:
2 Ingredient CTFA Designation wt. % Water 97.02 Potassium Coco mono
alkyl phosphate 0.4 Propylene Glycol 0.5 Polysorbate-20 0.30 Sodium
hydroxymethylglycinate 0.15 Fragrance 0.03
[0133] The potassium coco mono alkyl phosphate was commercially
available from Rhone-Poulenc under the trade designation RHODAFAC.
The Polysorbate-20 was commercially available from Rhone-Poulenc
under the trade designation ALKAMULS PSML-20. The sodium
hydroxymethylglycinate was commercially available from Sutton Labs,
a business having offices located in Chatham, N.J., under the trade
designation SUTTOCIDE A. Malic acid was then added to the solution
to bring the pH level to 5.5. The solution was cloudy, exhibited a
slight silky after feel and precipitated.
EXAMPLE 5
[0134] Composite elastic materials, prepared according to Example
1, is formed into sheets and moistened, using a solution prepared
according to Example 3, to provide wet-wipes. These wet-wipes were
compared to commercially available wet-wipes obtained from about
September 1996 through about January 2000 as recited in Table
I.
[0135] The cup crush, density, thickness, tensile strength, bulk
and basis weight for the wet-wipes were determined. The results are
summarized in Table II. The wet density of several commercially
available wet-wipes and the wet density of the wet-wipes of the
present invention are compared in FIG. 6. The cup crush of several
commercially available wet-wipes and the cup crush of the wet-wipes
of the present invention are compared in FIG. 7. The cup crush to
density ratio of several commercially available wet-wipes and the
cup crush to density ratio of the wet-wipes of the present
invention are compared in FIG. 8. The CD tensile strength of
several commercially available wet-wipes and the CD tensile
strength of the wet-wipes of the present invention are compared in
FIG. 9.
3 TABLE 1 Product Obtained Product from retail stores Sample 1
Nov-97 Sample 2 Nov-97 Sample 3 Nov-99 Huggies Sensitive Skin
Sep-96 Sample 4 Jan-00 Luvs 1QTR'99 Huggies Supreme Care Jan-00
Pure N' Gentle Premium Dec-99 Huggies Supreme Care Nov-99 Huggies
Natural Care 1QTR'99 Pamper Rash Care 1QTR'99 Equate 1QTR'99
Huggies Supreme Care 1QTR'99 Pampers Baby Fresh Natural Aloe
1QTR'99 Huggies Original 1QTR'99 Pampers Baby Fresh-Moisture
Pillows 1QTR'99 Pampers Premium 1QTR'99 European Pampers Sep-96
Chubs 1QTR'99
[0136]
4TABLE 2 Title: Wipe With Improved Clothlike Properties Cup Crush/
Basis Wet Cup Absorption Density Density Wt Bulk Crush Capacity CD
Peak CD TEA MD Peak MD TEA Density Cup Attribute Product
g/m{circumflex over ( )}2 mm g * cm gram/gram gram N *
m/cm{circumflex over ( )}2 gram/cm N * m/cm{circumflex over ( )}2
(g/cm{circumflex over ( )}3) Crush/Density Sample 1 82 1.14 69.2
6.88 335.66 *** 233.94 *** 0.072 965 Sample 2 82 1.07 87.5 5.87
358.34 *** 364.30 *** 0.077 1138 Sample 3 86 1.15 92 6.12 350.99
30.448 320.83 71.201 0.075 1227 Sensitive Skin 84 0.75 106.2 8.99
263.08 *** 196.44 *** 0.112 950 Sample 4 85 1.35 115 5.74 389.09
34.813 388.94 77.323 0.063 1828 Luvs 57 0.76 122.4 8.99 232.51
7.860 167.11 6.702 0.076 1609 82229 Supreme Care 78 1.08 139 8.88
553.38 40.411 487.52 53.269 0.072 1923 Pure N' Gentle Premium 66
0.70 150.1 7.18 1987.22 56.876 788.05 22.839 0.095 1579 7366
Supreme Care 77 1.30 163.7 7.77 581.87 44.352 487.77 59.042 0.059
2753 Natural Care-prince 75 0.83 165.7 10.38 363.51 25.142 309.69
28.127 0.090 1831 Pamper Rash Care 62 0.73 168.7 7.51 242.31 6.922
180.36 7.316 0.085 1977 Equate 62 0.57 174.6 6.53 408.19 12.141
322.35 15.027 0.110 1594 Supreme Care 80 1.25 180.9 8.41 613.21
43.747 426.89 47.978 0.064 2815 Baby Fresh Natural Aloe 64 0.71
188.6 6.97 301.00 8.037 193.58 7.881 0.091 2068 Original 79 0.78
198.6 8.57 315.61 21.353 331.80 22.357 0.101 1961 Baby
Fresh-Moisture 64 0.73 199 7.03 294.83 *** 205.37 *** 0.088 2265
Pillows Pampers Premium 69 0.72 226.2 7.49 346.59 9.172 247.69
9.588 0.096 2354 Euro Pampers 82 0.84 255.7 9.24 403.70 *** 405.37
*** 0.097 2632 Chubs 65 0.51 256.3 3.41 374.03 8.492462 486.6270
16.87733 0.129 1981 ***Not Measured
[0137] FIG. 10 shows a plan view of a wet-wipe 1000 created
according to the processes described herein. As discussed above,
elastic fibers 1010, schematically depicted in FIG. 10 as dashed
lines, extend in the machine direction (MD). Wet-wipe 1000 includes
a plurality of bonding points 1020 arranged in non-linear waves
which are not orthogonal to the either the machine direction (MD)
indicated by arrow 1005 or the cross direction (CD) indicated by
arrow 1006. For clarity of illustration, only a few bonding points
1020 are labeled with reference numerals. The bonding points 1020
are created by the bonding roller arrangement 20, 22 as the elastic
layer 12 and gatherable layer(s) 24 and.backslash.or 28 pass
through the bonding roller arrangement. The wet-wipe 1000 further
has decorative outlines, here shown as various forms of teddy
bears, forming additional bonding areas 1030 joining at least one
gatherable layer 24 or 28 to elastic layer 12. The calender roller
20, in one embodiment, includes a plurality of pins corresponding
to each bonding point 1020 and bosses corresponding to outlines
forming bonding areas 1030. While the illustrated embodiment has
numerous bonding points 1020 and bonding areas 1030, it is
understood that one embodiment requires fewer bonding points than
illustrated in FIG. 10, such as only two bonding points 1020 or
bonding areas 1030. Further, wet-wipe 1000 does not require both
bonding points 1020 and bonding areas 1030. For example, only a
plurality bonding points 1020 join the gatherable layer 24 to
elastic layer 12. That is, the wet-wipe does not have bonding areas
1030. In another embodiment, only a plurality of bonding areas 1030
are provided.
[0138] FIG. 13 shows a rigid plastic wet-wipe container having a
lid 1301 hingedly attached to a base 1302 and a removable inner
cover 1303. The removable inner cover contains a pop-up style
wet-wipe dispenser including a rigid port 1305 which surrounds a
flexible, rubber-like material or sheet 1306 having a dispensing
opening 1307. The dispensing opening 1307 is illustrated as several
slits through which individual wet wipes are removed from the
container. It will be understood that the opening can have other
configurations, such as a polygon, oval, circle, etc., which
provide the yieldable resistance required to stretch the wet-wipe
to increase its thickness as it is removed from the container. The
removable inner cover shown is somewhat dome-shaped with a slight
pitch toward the front of the container. The cover is removably
secured to the sidewalls of the base by a small lip around the
periphery of the inner cover that engages with notches within
several protruding ribs on the inner surface of the sidewalls (not
shown). It also rests on a small support surface in each of the
four comers of the base, which is outwardly visible by
discontinuities 1308 in the rounded comers of the base. The lid is
secured in a closed position by a suitable latching mechanism, in
which a protrusion 1309 in the front lip of the base is engaged by
an opening 1311 in the front lip of the lid.
[0139] The shape of the rigid port in the embodiment shown in FIG.
13 is oval, but can be any shape and size large enough to enable
the user to reach into the container with their fingers to grasp
the next available wet wipe in the event of a dispensing failure.
Other suitable shapes include, without limitation, polygons, such
as square, rectangular, and triangular; circular and irregular. The
area of the oval illustrated in the container of FIG. 13 is about 6
square inches.
[0140] Dispensing opening 1307 includes slits in the flexible,
rubber-like sheet, which, as shown, are star-shaped and cross
essentially at one point on the sheet. The longest slit is about
1.75 inches and the smaller slits are about 0.25 inch. However,
many other slit configurations are also suitable including, without
limitation, X-shaped slits, straight slits and curvilinear slits.
The length of the individual slits can be about 0.25 inch to about
3 inches, more specifically from about 0.25 inch to about 2 inches.
The length of the slits will in part depend upon the slit
configuration and the number of slits. The sum total length for all
of the slits in the sheet or material can be about 2.5 inches or
greater. It is preferred to have at least one slit with a length of
about 1 inch which, in combination with the elasticity of the
rubber-like sheet or material, will allow the user to reach into
the container with at least two fingers as necessary. For very tall
containers, it may be necessary to lengthen at least one of the
slits so that the user can still reach the bottom of the container.
For such a container, at least one of the slits may need to be
between 2 and 6 inches in length, more specifically between 3 and 4
inches in length. This will allow the user to insert one or more
fingers as well as part of the hand into the container to retrieve
a wipe.
[0141] FIG. 14 is a perspective view of another rigid plastic
container in accordance with this invention, in which the pop-up
style dispenser is recessed within the lid of the container.
Elements which are similar to those described above are designated
by the same reference numbers. Shown is a removable lid 1301, a
base 1302, a rigid port 1305 which surrounds a flexible,
rubber-like sheet 1306 having a dispensing opening 1307 through
which the wet wipes are dispensed. This container also has a pop-up
lid 1420, which can be closed to seal the container when not in
use.
[0142] FIG. 15 shows another container, in which the container is a
flexible package 1505, such as a plastic film-wrapped package,
having a flip-top style dispensing opening structure. The flexible
plastic film package 1505 contains a stack of wet-wipes. A
dispenser 1510 is provided on the top of the package, which
dispenser includes a rigid port 1511 surrounding a flexible,
rubber-like sheet 1306 having dispensing opening 1307, for example
formed of one or more slits, through which the wet wipes are
removed from the package 1505. The flip-top lid 1516 can be closed
over the rigid port to seal off the container when not being used.
Any suitable closure design can be used to effect a proper
seal.
[0143] While the dispenser useful for purposes of this invention
has been specifically illustrated in three different styles of
container, those skilled in the art will appreciate that many
different container designs are possible, including canister style
containers, without departing from the scope of the invention.
[0144] The flexible, rubber-like sheet 1306 forms dispensing
opening 1307, wherein the dispensing opening has a Penetration
Index of from about 50 to about 600 grams. More specifically, the
Shore A hardness (as measured by ASTM D2240) of the flexible,
rubber-like sheet or material 1306 is about 100 or less, more
specifically from about 20 to about 70, and still more specifically
from about 30 to about 60. The Gurley stiffness of the flexible,
rubber-like sheet or material (as measured by ASTM D 6125-97
"Standard Test Method for Bending Resistance of Paper and
Paperboard") is about 10,000 milligrams of force (mgf) or less,
more specifically from about 100 to about 8000 mgf, more
specifically from about 200 to about 6500 mgf, and still more
specifically from about 300 to about 1500 mgf. The thickness of the
flexible, rubber-like sheet 1306 is about 0.1 millimeter or
greater, more specifically from about 0.1 to about 2 millimeters,
and still more specifically from about 0.8 to about 1.5
millimeters.
[0145] The elasticity of the flexible rubber-like material or sheet
1306, as characterized by the tensile stress at 100 percent
elongation and measured in accordance with ASTM D412 "Standard Test
Methods for Vulcanized Rubber and Thermoplastic Elastomers", is
about 10 megapascals (Mpa) or less, more specifically from about
0.1 to about 7 Mpa, and still more specifically from about 0.5 to
about 2.5 Mpa.
[0146] Alternatively, the performance of the dispensing opening can
be measured more directly by using a tensile testing machine to
insert a ball-shaped probe into the dispensing opening under
controlled conditions and measuring the force required to overcome
the resistance of the opening. This simulates the use of a person's
finger to reach into the container to retrieve a wipe. In general,
the measurement involves placing a container to be tested
underneath a specially-designed probe which is mounted to a tensile
tester. The tensile tester lowers the probe into the center of the
container's dispensing opening at a predetermined speed and
measures the peak load, in grams, required to penetrate the
opening. This test, as more specifically described below, results
in a value referred to herein as the "Penetration Index". The
containers of this invention have a Penetration Index of from about
50 to about 600 grams, more specifically from about 100 to about
500 grams, and still more specifically from about 200 to about 400
grams.
[0147] On example of the tensile tester is a MTS Sintech 1/G with a
MTS 10 pound load cell. The software is Testworks for Windows 3.10.
The load cell contains a 0.5 inch grip adapter for receiving the
metal ball probe. The ball probe used is approximately 4.5 inches
long. The bottom portion of the probe, which contacts the sample to
be tested, is ball-shaped and has a ball diameter of 0.75 inch. The
middle portion of the probe consists of a connecting "neck" which
is approximately 0.375 inches in diameter and 1.375 inches long.
The upper section of the probe is approximately 0.5 inch in
diameter and 2.4 inches long. The end of the upper section contains
a flat area to allow the probe to fit into the grip adapter of the
tensile tester. The flat area is 0.125 inch off of the center of
the probe. When conducting the test, the container to be tested is
securely placed on a suitable surface such that the center of the
dispensing opening is placed directly underneath the ball probe.
The probe is initially positioned such that it is approximately one
inch above the dispensing opening. Upon the start of the test, the
probe moves downward at a rate of 80 inches per minute for a
distance of 2 inches. The probe is held for one second at this
bottom position and then is moved upward to its initial position at
the same rate. The test is repeated two additional times. The peak
load readings from the tensile tester, expressed as grams of force,
are averaged and the result is the Penetration Index for the
sample.
[0148] FIGS. 16A and 16B schematically show stacks of wet-wipes
1610 as may be stored in the containers illustrated in FIGS. 13-15.
The stacks 1610 include a plurality of individual wet-wipes 1615
stacked one on top of each other in a non-interleaved
configuration. Each wipe is folded onto itself with no portion of
another wipe being positioned between the folds of the adjacent
wipe(s).
[0149] FIGS. 17A and 17B schematically show stacks of wet-wipes
1710 as may be stored in the containers illustrated in FIGS. 13-15.
The stacks 1710 include a plurality of individual wet-wipes 1715,
which are stacked one on top of each other in an interleaved
configuration. Each wipe 1715 includes a portion 1717 positioned
between, in a sandwich-like configuration, portions of adjacent
wipe(s).
[0150] FIG. 18 shows a plurality of wet-wipes 1815 held in a roll
1810. Individual wet-wipes 1815 are separated from the adjacent
wet-wipe(s) by perforation(s) 1818, which allows the wet-wipe 1815
(show on the right in FIG. 18) to be removed from the roll 1810 by
tearing along the perforation between wet-wipe 1815 and the
adjacent wet-wipe. A roll 1810 of wet-wipes may be stored in a
container adapted to support the roll and allow removal on the
wet-wipes. It is within the scope of the present invention to
provide such a container with a dispenser 1307 as discussed above
so that the wet-wipe removed from the container is suitably
stretched and relaxed to increase the thickness of the wipe. While
FIG. 18 shows the wipe being removed from the outer diameter of
roll 1810, it is further understood that it is within the scope of
the present invention to remove wipes from the inner diameter of
the roll.
[0151] While one of ordinary skill would understand how to operate
the wet-wipe, with or without the container, in order to increase
its thickness and, hence, improve its cloth-like feel and softness,
a description of its operation is provided. Wet-wipes lose some of
their thickness during manufacturing, packaging, and distribution.
It is desired to recapture the thickness prior to wet-wipe use. In
one embodiment, wet-wipe 1000 is held by the top and bottom as
shown in FIG. 10, and stretched in the machine direction. In the
case of a wet-wipe 1000 having a machine direction length of about
190 mm in a relaxed state or mode, it is stretched to a length of
about 271 mm in a stretched state or mode. The wet-wipe is released
and recovers to about its relaxed state. During the stretching and
recovering functions, the gathered layers 24 and 28 are stretched
and then pulled back to about their original state by elastic layer
12 through bonding points. This causes the gathered layers 24 and
28 to increase in thickness, and hence, softness is improved. The
increasing of the thickness of gathered layers 24 and 28 decreases
the density of the wet-wipe and adds to the increased "softness" of
the wet-wipe.
[0152] In another embodiment, the wet-wipe is stretched as it is
pulled through dispensing opening 1307 (FIGS. 13-15). A user
reaches through opening 1307 and grips and end of the wet-wipe 1000
stored within the interior of container 1302 or 1505.
Alternatively, a portion of wet-wipe 1000 extends a small extent
outside of the container to aid in its removal. The wet-wipes 1000
are arranged in the container such that the act of removal is in
the machine direction. The wet-wipes may be stored in stacks,
interleaved or non-interleaved, or in rolls. As the wet-wipe 1000
is removed, the opening 1307 yieldably resists the removal of the
wet-wipe. This causes the wet-wipe to stretch when it passes
through opening 1307, i.e. the wet-wipe is in its stretched mode.
When the wet-wipe snaps free of dispensing opening 1307, the
wet-wipe returns to about its relaxed length by action of the
elastic layer. However, the mode is now different because the
gatherable layers 24 and/or 28 have an increased thickness.
[0153] It is believed that the stretching of the wet-wipe should be
in a range of about 5% to about 50% of its relaxed state. For
example, if the wet-wipe has a length of 200 mm, then its stretched
length should be in the range of about 210 mm to about 300 mm. In
another embodiment, the stretching range is in the range of about
5% to 30%. In yet another embodiment the stretching range is about
10% to about 20%. Using the same example wet-wipe having a length
of 200 mm, then the wet-wipe of this embodiment has a stretched
length of about 220 mm to about 240 mm. It will be understood that
it is undesirable to stretch the wet-wipe to a point where it
begins to tear. It is believed that the wet-wipe can be stretched
to about 50% of its relaxed length, but it is preferable to only
stretch the wet-wipe to a maximum of about 30% of its length to
reduce the risk of tearing.
[0154] After the wet-wipe is stretched, it recovers to about its
relaxed length. Ideally, the elastic layer acts as a perfect
elastomer and returns to the relaxed length after it is stretched
and released. It will be understood that the wet-wipe according to
the present invention may not return to exactly the same length and
may be about 5% longer after recovery.
[0155] The present wet-wipe dispensing system provides a wet-wipe
for use having improved texture and softness. The system includes
wet-wipe container 1302 or 1505 and at least one wet-wipe 1000
stored within the container. The wet-wipe is removed from the
container for use. The wet-wipe 1000 has a non-woven laminate 40 of
an elastic layer 12 and at least one gathered layer 24 or 28. The
gathered layer 24 or 28 is bonded to elastic layer 12 at at least
two points and is gathered between the at least two points. As the
wet-wipe is removed from the container 1302 or 1505, it stretches.
After its release from the container's dispensing opening 1307, the
wet-wipe recovers to about its relaxed length. The non-woven
laminate 40 has a first thickness within the container and a second
thickness outside the container, the second thickness being greater
than the first thickness, which helps improve the softness and
cloth-like texture.
[0156] FIG. 19 is a graph of test data comparing wet-wipes 1000
which were removed from the container 1302 or 1505 though an open
lid ("reach-in dispensing") with wet-wipes 1000 which were removed
though a dispensing opening 1307 ("dispensed through orifice"). The
wet-wipes used in this comparison were formed according to a
stretch bonded laminate manufacturing process, and have an inner
elastic layer and two non-elastic layers bonded to the elastic
layer. Prior to bonding the non-elastic layers to the elastic
layer, the elastic layer is stretched. After bonding the
non-elastic layers to the elastic layer, the tensioning force is
removed from the elastic layer, which now attempts to recover its
unstretched or relaxed state. When the elastic layer recovers
(unstretches), the non-elastic layers are gathered. Resulting in a
wet-wipe which is textured, soft, and has a high z-directional
thickness. The z-directional thickness being measured generally
perpendicular to the x-y plane illustrated in FIG. 10; that is, the
z-direction is generally perpendicular to the MD and CD. Subsequent
processing, packaging, and distribution reduces the z-directional
thickness and adversely effects the softness and texture.
[0157] In this comparison, the wet-wipes dispensed through the
orifice were stretched and relaxed (recovered) as described herein.
The wet-wipes removed by reach-in dispensing were not subject to
the stretching and relaxing. The X-axis of FIG. 19 is the sample
number for each removal method and the Y-axis is the thickness of
the removed wipe. As the graph shows, the dispensed through orifice
(stretched and recovered) wet-wipes have a greater thickness.
Additional data with regard to this comparison test is found in
Table 3.
5 TABLE 3 Dispensed through Orifice Dispensed by Reach-In Samples N
= 64 N = 64 Mean Thickness 1.0459 mm 0.8509 mm Standard Deviation
0.0729 mm 0.0509 mm Maximum Thickness 1.24 mm 0.95 mm Minimum
Thickness 0.90 mm 0.76 mm
[0158] The each wet-wipe removal type includes 64 samples of
wet-wipes. The mean thickness of the wet-wipes that were stretched
is 0.195 mm (about 18%) greater than the wet-wipes which were not
stretched. The maximum thickness of the stretched wet-wipes is 0.29
mm (about 23%) greater than the non-stretched wet-wipes. The
minimum thickness of the stretched wet-wipes is 0.14 mm (about 15%)
greater than non-stretched wet-wipes. Moreover, the thickest
non-stretched wet-wipe (0.90 mm) is less than the thinnest
stretched wet-wipe (0.95 mm). The greater thickness of the
stretched and recovered wet-wipes provides a softer feeling
wet-wipe, which is desired by the consumers of wet-wipes.
[0159] All publications, patents, and patent documents cited in the
specification are incorporated by reference herein, as though
individually incorporated by reference. In the case of any
inconsistencies, the present disclosure, including any definitions
herein will prevail.
[0160] The invention has been described with reference to various
specific and preferred embodiments and techniques. However, it
should be understood that many variations and modifications may be
made while remaining within the spirit and scope of the invention
which is defined according to the claims appended hereto.
* * * * *