U.S. patent application number 10/115697 was filed with the patent office on 2002-08-15 for method and making bonded-electrode rechargeable electrochemical cells.
Invention is credited to Gozdz, Antoni S., Tarascon, Jean-Marie.
Application Number | 20020110728 10/115697 |
Document ID | / |
Family ID | 24147477 |
Filed Date | 2002-08-15 |
United States Patent
Application |
20020110728 |
Kind Code |
A1 |
Gozdz, Antoni S. ; et
al. |
August 15, 2002 |
Method and making bonded-electrode rechargeable electrochemical
cells
Abstract
A Li-ion battery cell comprising a polymeric matrix positive
electrode layer member, a polymeric matrix negative electrode layer
member, and an interposed microporous polyolefin separator layer
member is laminated into a unitary, flexible cell structure by
means of heat and pressure without necessity for applied interlayer
adhesive. A primary plasticizer for the electrode member matrix
polymer is included in the electrode layer compositions. During the
lamination operation, which may be carried out at a
moderate-temperature that does not compromise the thermal shutdown
capability of the microporous separator, the plasticizer softens
the polymer into a thermoplastic adhesive which forms an effective
bond to the untreated polyolefin surface in the region of the
electrode/separator interface. The plasticizer dissipates from the
composition along with residual lamination heat or may be extracted
with solvent or supercritical fluid, thereby enabling the electrode
polymer alone to form a strong, permanent bond to the polyolefin
separator member.
Inventors: |
Gozdz, Antoni S.; (Ocean,
NJ) ; Tarascon, Jean-Marie; (Amiens, FR) |
Correspondence
Address: |
HARNESS, DICKEY & PIERCE, P.L.C.
P.O. BOX 828
BLOOMFIELD HILLS
MI
48303
US
|
Family ID: |
24147477 |
Appl. No.: |
10/115697 |
Filed: |
April 3, 2002 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10115697 |
Apr 3, 2002 |
|
|
|
09538575 |
Mar 29, 2000 |
|
|
|
6391069 |
|
|
|
|
10115697 |
Apr 3, 2002 |
|
|
|
09538574 |
Mar 29, 2000 |
|
|
|
6413667 |
|
|
|
|
Current U.S.
Class: |
429/62 ;
29/623.1; 29/623.4 |
Current CPC
Class: |
H01M 4/622 20130101;
B29C 66/727 20130101; H01M 4/13 20130101; H01M 10/0565 20130101;
H01M 6/40 20130101; B32B 7/10 20130101; B29L 2009/00 20130101; H01M
50/46 20210101; H01M 10/0525 20130101; B29L 2031/3468 20130101;
Y02E 60/10 20130101; Y02P 70/50 20151101; B32B 37/00 20130101; Y10T
29/49112 20150115; B29C 66/72321 20130101; B29C 66/71 20130101;
H01M 10/38 20130101; H01M 50/414 20210101; B32B 2457/00 20130101;
Y10T 29/49114 20150115; B29C 65/4895 20130101; H01M 50/411
20210101; H01M 4/139 20130101; Y10T 29/49108 20150115; B29C 66/1122
20130101; B29C 66/45 20130101; H01M 10/0585 20130101; B32B 2305/026
20130101; B29C 66/723 20130101; B29C 66/71 20130101; B29K 2033/20
20130101; B29C 66/71 20130101; B29K 2033/12 20130101; B29C 66/71
20130101; B29K 2027/16 20130101; B29C 66/71 20130101; B29K 2027/08
20130101; B29C 66/71 20130101; B29K 2027/06 20130101 |
Class at
Publication: |
429/62 ;
29/623.1; 29/623.4 |
International
Class: |
H01M 010/50; H01M
010/04 |
Claims
What is claimed is:
1. A method of making a bonded-electrode rechargeable
electrochemical cell structure comprising an assemblage of positive
and negative electrode layer members having a separator layer
member interposed therebetween, each of said electrode members
comprising a polymeric matrix composition and said separator member
comprising a microporous polyolefin membrane exhibiting a property
of pore collapse at temperatures above a threshold temperature, and
each of said members being bonded at its respective interfaces to
contiguous members to form a unitary multilayer, planar,
electrochemical cell structure characterized in that a) each said
polymeric electrode member composition is prepared comprising a
primary plasticizer for the matrix polymer thereof; b) a surface of
said electrode member composition is assembled contiguous to a
porous surface of said separator membrane; c) said assemblage is
subjected to laminating pressure and temperature, said temperature
being below said threshold and sufficient to enable said
plasticizer to soften the matrix polymer of its composition and
form in said composition a thermoplastic adhesive interface with
said separator membrane surface; and d) said adhesive interface is
cooled to thereby form an adhesive interface bond between said
contiguous electrode and separator surfaces.
2. A method according to claim 1 comprising the further step
wherein said plasticizer is at least partially removed from said
adhesive interface.
3. A method according to claim 2 wherein said plasticizer is
removed by means of evaporation.
4. A method according to claim 2 wherein said plasticizer is
removed by means of solvent or supercritical-fluid extraction.
5. A method according to claim 1 characterized in that a) said
matrix polymer is selected from the group consisting of polymers
and copolymers of vinyl chloride, acrylonitrile, methyl
methacrylate, ethylene oxide, vinylidene chloride, and vinylidene
fluoride; and b) said primary plasticizer is selected from the
group consisting of alkylene carbonates, dialkyl phthalates,
dialkyl succinates, dialkyl adipates, dialkyl sebacates, trialkyl
phosphates, polyalkylene glycol ethers and mixtures thereof.
6. A method according to claim 5 wherein a) said matrix polymer is
selected from the group consisting of polymers and copolymers of
vinylidene fluoride; and b) said primary plasticizer is selected
from the group consisting of alkylene carbonates and mixtures
thereof.
7. A method according to claim 6 wherein said primary plasticizer
consists essentially of propylene carbonate.
8. A method according to claim 7 wherein said propylene carbonate
plasticizer is present in said electrode composition in an amount
of between about 60% and 300% by weight of said matrix polymer.
9. A bonded-electrode rechargeable electrochemical cell structure
comprising an assemblage of positive and negative electrode layer
members having a separator layer member interposed therebetween,
each of said electrode members comprising a polymeric matrix
composition and said separator member comprising a microporous
polyolefin membrane exhibiting a property of pore collapse at
temperatures above a threshold temperature, and each of said
members being bonded at its respective interfaces to contiguous
members to form a unitary multilayer, planar, electrochemical cell
structure characterized in that the interface bond between said
separator member and an electrode member consists essentially of
matrix polymer of said electrode member.
Description
BACKGROUND OF THE INVENTION
[0001] The present invention generally relates to a method of
making bonded multilayer, flat-plate electrochemical cell devices,
such as rechargeable batteries and supercapacitors. More
specifically, the invention provides a method for establishing
persistent interfacial bonding between laminated planar electrode
and microporous polyolefin separator members utilized in such
electrochemical devices.
[0002] Widely deployed primary and secondary, rechargeable
lithium-ion electrochemical cells are typical of electrochemical
devices to which the present invention is directed. Such cells
comprise layers, or membranes, of respective positive and negative
electrode composition members assembled with a coextensive
interposed separator member comprising a layer or membrane of
electrically insulating, ion-transmissive material. This multilayer
electrochemical cell structure is normally packaged with a
mobile-ion electrolyte composition, usually in fluid state and
situated in part in the separator member, in order to ensure
essential ionic conductivity between the electrode members during
charge and discharge cycles of the electrochemical cell.
[0003] One type of separator for this purpose is a microporous
polyolefin membrane, either of single- or multilayer structure such
as described, for example, in U.S. Pat. Nos. 3,351,495; 5,565,281;
and 5,667,911. When employed as rechargeable electrochemical cell
separators, these porous membranes not only effectively retain
within their porous structure the essential liquid electrolyte
compositions, but they also provide an additional advantage in that
they possess an automatic thermal shutdown feature which prevents
uncontrolled heat buildup within the electrochemical cell, such as
might otherwise result in a dangerous explosive condition, for
instance during excessive cell recharging. This built-in safety
mechanism relies on the fact that the melting point range of the
polyolefins utilized in the fabrication of the separator membranes
is at the lower end of the danger zone of electrochemical cell heat
buildup. Thus, in the event of a runaway cell heating episode, the
porous polyolefin separator membrane becomes heated to a point of
melting and its pore structure collapses, thereby interrupting the
essential ionic conductivity within the cell and terminating the
electrochemical reaction before a dangerous condition ensues.
[0004] The packaging of electrochemical cell structures has
heretofore regularly taken the form of a metal container, whether,
for example, in elongated tubular (cylindrical) or flattened
(prismatic) shape, which has commonly been relied upon to not only
contain the liquid electrolyte component, but also to impart the
significant stack pressure required to maintain close physical
contact between the individual cell electrodes and the interposed
separator member. This intimate contact, along with the composition
of the electrolyte, is, as previously noted, essential to efficient
ion transport between electrodes during operation of the
electrochemical cell.
[0005] More recently, however, the profusion and continued
miniaturization of electronic devices powered by Li-ion batteries
and similar electrochemical energy storage cells has generated a
demand for a greater number of cell package shapes and dimensions,
e.g., relatively broad, yet thin, lightweight packages having a
significant degree of flexibility. For example, numerous end use
applications make thin, flexible tablet-style packages of polymer
film more desirable than the prior rigid-walled high-pressure metal
can containers. However, these more flexible packages are
decreasingly capable of achieving and maintaining the substantial
physical pressures required to ensure the noted essential intimate
interlayer contact throughout the electrochemical cell.
[0006] In order to minimize the deleterious effect of decreased
physical stack pressure previously relied upon to establish the
necessary contact between electrochemical cell components,
developers have progressed to the use of direct laminate bonding
between electrode and separator layers to ensure their essential
intimate contact. Typical of such innovations are electrochemical
cells utilizing polymer-based electrode and separator members, such
as described in U.S. Pat. Nos. 5,296,318; 5,456,000; 5,460,904; and
5,540,741.
[0007] In those fabrications, compositions of polymers, such as
polymers and copolymers of vinyl chloride, acrylonitrile, methyl
methacrylate, ethylene oxide, vinylidene chloride, and vinylidene
fluoride, notably of poly(vinylidene fluoride) (PVdF) copolymers
with hexafluoropropylene, which are compatible with efficient
liquid electrolyte compositions, are utilized as binders in both
the electrode and the separator members to not only support
essential ionic conductivity, but also to provide a common
composition component in those cell members which promotes strong
interfacial adhesion between them within a reasonably low
laminating temperature range. Such laminated, multilayer
rechargeable electrochemical cells operate effectively and exhibit
a stable high capacity and excellent discharge rate performance
even though packaged in flexible, lightweight polymeric film
enclosures.
[0008] Although such laminated electrochemical cells and like
energy storage devices have significantly advanced the art in
miniaturized applications, the use of substantially homogeneous
polymeric matrices and membranes in their fabrication has deprived
these devices of the desirable thermal shutdown feature achieved
when using microporous polyolefin separator membranes. However, the
low surface energy exhibited by the polyolefin membranes renders
them highly abherent in nature and thus inhibits their strong,
permanent laminate adhesion to many polymeric electrode layer
compositions, particularly within a reasonable temperature range
which does not lead to melting and, thus, thermal collapse, of the
porous structure of the polyolefin membranes.
[0009] Some attempts have been made by electrochemical cell
fabricators to overcome the adhesion-resistant property of the
otherwise desirable microporous polyolefin separator membranes by
introducing specifically formulated adhesive polymer compositions
into the region of electrode and separator member interfaces, such
as described by Abraham et al. in the Journal of Electrochemical
Society, vol. 142(3), pp. 683-687 (1995) and in U.S. Pat. Nos.
5,837,015 and 5,853,916. However, it has generally been found that
the application of such adhesive compositions, whether by
overcoating, dipping, extrusion, or the like, significantly
occludes or otherwise interferes with the porous structure of the
polyolefin membranes and causes a deleterious decrease in
electrolyte mobility and ionic conductivity. Further, the addition
of substantial amounts of such adhesive materials increases the
proportion of non-reactive components in a cell, thereby detracting
from the specific capacity of any resulting energy storage
device.
[0010] Typical of such attempts to achieve suitable interfacial
bonding between electrode and separator cell are the procedures
described in U.S. Pat. Nos. 5,681,357 and 5,716,421. There, a layer
of PVdF homopolymer is applied to the microporous separator
membrane from a solution in organic solvents when the membrane is
intended to be employed in the fabrication of an electrochemical
cell by thermal lamination with electrodes comprising binder matrix
compositions of a similar polymer. It was apparently intended that
the added polymer layer would not be of such excessive thickness as
to occlude the porosity of the membrane, but rather would provide
an intermediate transition in compatibility to the matrix polymer
binder of preferred electrode layer compositions. This approach has
proven to be insufficient in itself to enable satisfactory
interfacial bonding between cell component layers at lamination
temperatures below the critical level which results in collapse of
separator porosity and its attendant loss of effective ionic
conductivity and desirable shutdown capability. Either the added
polymer filled the pores of the membrane or the layer was too thin
to establish an interfacial bonding of any substance.
[0011] In an attempt to overcome this difficulty, a bonding process
was devised which involved heating the assembled individual
components of a multilayer structure under pressure within a
package also enclosing a lithium salt-containing organic
electrolyte solution which was to act as a mutual adhesive-forming
solvent for the added polymer and the polymer of the electrode
compositions. However, this method suffers several problems with
respect to assembly and cell performance. First, it is extremely
difficult to achieve within an enclosing package a sufficiently
controlled and uniform pressure on a multi-ply folded or wound
electrode/separator assembly to obtain an adequately strong bond
between the respective layers, particularly in the fold region.
Second, very thin electrode layers and current collectors have to
be used to prevent the electrodes and the current collectors from
cracking and delamination. Third, heating a liquid electrolyte
activated electrochemical cell to a temperature sufficiently high
to effect such bonding is deleterious to the cell's long-term
electrochemical performance and often causes permanent physical and
chemical damage to the multilayer foil packaging material and the
foil feed-through tabs typically employed in the fabrication of
such flat electrochemical cells.
[0012] Other methods directed at achieving some measure of bond
strength between microporous polyolefin separator and polymeric
composite electrode members while preserving the open-pore
structure of the separator member have been tried. U.S. Pat. No.
5,981,107 suggests a method in which numerous small dots comprising
a fluid adhesive mastic of PVdF in N-methyl-pyrrolidinone (NMP) are
applied to both sides of a microporous polyolefin separator. The
separator is then sandwiched between two PVdF polymer composition
electrodes under pressure followed by drying of the applied
adhesive. It was apparently intended that the dispersed adhesive
pattern would maintain an open-pored field within which electrolyte
could freely reside; however, since NMP is a powerful solvent for
PVdF and its copolymers, it significantly dissolves the binder
polymer of the electrode and causes local filling of the micropores
of the separator with such polymer, thus decreasing the effective
ionic conductivity of the separator. In addition, the applied
adhesive polymer composition unproductively increases the cell
mass, thus lowering its effective energy storage capacity.
[0013] U.S. Pat. No. 6,024,773 discloses a similar method which
involves uniformly coating both sides of a separator member with a
fluid solution of PVdF in NMP or other strong solvent, sandwiching
the separator between electrode members, pressing the three layers
together, and drying the assembly at elevated temperature to form a
laminate. The problems mentioned above are even more pronounced in
this method.
[0014] Therefore, there remains a need in the art for an improved
and economical method of fabricating high-capacity, thermal
shutdown-protected, electrochemical cells incorporating microporous
polyolefin separator membranes. There also remains a need for a
simple, economical, and easily controlled method of effectively
bonding microporous polyolefin separator membranes into
high-capacity, high-discharge rate, shutdown-protected,
bonded-electrode rechargeable electrochemical cells.
SUMMARY OF THE INVENTION
[0015] The present invention provides a simplified method of
fabricating flat, high-capacity, high-discharge-rate,
thermal-shutdown-protected electrochemical cells through the use of
polymer matrix electrodes and economical, commercially available
microporous polyolefin separator membranes. More particularly, the
present invention comprises a method for facilitating the
lamination of electrochemical cell members without resort to
additional polymeric adhesive compositions and at laminating
temperatures and pressures which effect firm interfacial bonding
between polymer matrix electrode members and an unmodified
microporous separator membrane, yet are sufficiently low to avoid
thermal and mechanical collapse or other occlusion of the porous
membrane structure of the cell separator member.
[0016] In the method of the present invention, positive and
negative electrode members are provided which respectively comprise
layers of plasticized polymeric matrix compositions of active
electrode materials, such as Li-ion-intercalatable carbons and
transition metal oxides, e.g., LiCoO.sub.2 and LiMn.sub.2O.sub.4.
Such electrode compositions, preferably comprising poly (vinylidene
fluoride) polymers or copolymers, are typically highly compacted or
densified layers, such as formed under calendering or laminating
pressure, and may additionally be coated upon or laminated into
sub-assemblies with solid or reticulated metal foil current
collector members.
[0017] Electrochemical cell electrode members of this type are
described in a number of U.S. patent specifications, e.g., U.S.
Pat. Nos. 5,456,000 and 5,587,253, the disclosures of which are
incorporated herein by reference. These polymeric electrode
composition cell members have been used primarily with cell
separator members comprising a matrix of similar polymer to form
thermally laminated cell structures which rely in great measure on
the compatibility of the matrix polymers of the electrode and
separator compositions to provide strong interfacial laminate
bonding.
[0018] Now, in the present invention, it has been surprisingly
discovered that the plasticized polymeric cell electrode members
which had previously been laminated solely with separator members
comprising similar or compatible matrix polymer are also able to
form substantial interfacial laminate bonds with
thermal-shutdown-capable microporous polyolefin cell separator
membrane materials. This bonding may be effected by means of direct
thermal lamination without resort to additional adhesive polymer
compositions or treatments and at temperatures sufficiently low to
avoid compromise of either the electrolyte retention or shutdown
properties of the off-the-shelf microporous membrane. So effective,
in fact, is this newly discovered property of these prior electrode
compositions that there is no requirement to make significant
changes in available fabrication equipment or procedures. Heated
roller laminators or platen presses and post-lamination cell
activation with electrolyte solutions continue to be effective in
preparing the final rechargeable battery cell.
[0019] Also useful with the battery cell structure obtained by use
of the present invention is the intermediate treatment of the
laminate with liquid solvent or supercritical fluid to extract the
plasticizer from the electrode composition. In addition to the
previously acknowledged purpose of conditioning the laminate
structure polymer electrode compositions to absorb subsequently
applied electrolyte solution, such extraction, or the alternative
treatment of the compositions to effect evaporation of the
plasticizer, leads to a toughening of the electrode matrix polymer
with a resulting increase in strength of the interfacial
electrode/separator laminate bond. Packaging the resulting
multilayer bonded cell in a flexible pouch or envelope with a
measure of a lithium salt-containing electrolyte solution in order
to activate the cell in the manner of previously described
practices continues to be a preferred final step in the preparation
of a working battery cell.
[0020] Plasticizers useful in the invention are moderately volatile
primary plasticizers for the electrode composition matrix polymer
and include alkylene carbonates, dialkyl phthalates, dialkyl
succinates, dialkyl adipates, dialkyl sebacates, trialkyl
phosphates, polyalkylene glycol ethers and mixtures thereof.
Selection of an appropriate such plasticizer depends upon the
specific matrix polymer employed in the electrode member
composition and may be accomplished by the skilled artisan without
excessive experimentation. The amount of composition plasticizer
may likewise be routinely determined to achieve, in addition to the
desired flexibility in fabrication, e.g., suitable current
collector lamination and prismatic folding, a suitable degree of
adhesive flow in the electrode/separator interfacial region at
temperatures below shutdown threshold without noticeable
plasticizer exudation at ambient conditions.
[0021] A preferred plasticizer for use with widely employed poly
(vinylidene fluoride) (PVdF) polymer or poly(vinylidene
fluoride-hexafluoropropylene) (PVdF-HFP) copolymer electrode member
compositions is propylene carbonate (PC). The effective proportion
of this plasticizer, as with any other selected on the basis of
matrix polymer, depends not only on the matrix polymer itself, but
is heavily influenced by the amounts and properties of other
components of the composition, such as the volume and particle size
of the active electrode material. For example, an effective amount
of PC in a positive electrode formulation with PVdF-HFP may vary
from about 60% to 300% by weight of the electrode matrix polymer
component. Thus, in view of the numerous composition variables that
are within the purview of the cell fabricator alone, the amount of
plasticizer in any formulation is preferably to be determined
empirically by the fabricator.
[0022] Electrode members prepared for use according to the present
invention are prepared in any previously employed manner by solvent
casting, extrusion, or the like, and are preferably used in the
form of highly densified polymeric composition layers deposited on
or laminated to metal-foil current collectors, such as those
employed in liquid-electrolyte Li-ion cells, or as densified and
non-extracted or extracted plastic Li-ion electrodes, such as those
described in the earlier-noted U.S. patents. In order to facilitate
subsequent fluid processing, at least one electrode preferably has
a reticulated metal current collector in the form of an expanded
metal grid, mesh, metallic non-woven material, or etched or
perforated foil.
[0023] Lamination of plasticized polymer matrix electrode cell
members with an untreated separator member according to the present
invention is preferably carried out between heated pressure rollers
at a temperature and pressure level which does not significantly
affect the porous structure, i.e., a temperature below the shutdown
temperature of the separator membrane. Effective lamination may be
carried out between 70.degree. C. and 130.degree. C., preferably
between 100.degree. C. and 125.degree. C., and more preferably at
about 110.degree. C., and under a linear pressure load between
about 20 and 180 kilograms per centimetre (kg/cm), preferably
between about 55 and 125 kg/cm, although it should be apparent to
the skilled artisan that the optimum temperature and pressure
conditions will depend on the particular laminator construction and
mode of its use.
[0024] The adhesive bond formed at the electrode and separator
member interfaces as a result of the present invention was found to
be surprisingly durable despite the fact that the normally abherent
polyolefin surfaces of the microporous separator had not been
previously subjected to expensive pre-coatings or polymeric
adhesive compositions. Particularly noteworthy is the fact that the
interfacial bonds of these cell members are able to survive
extended exposure to solvent-based cell electrolyte compositions
even at battery storage temperatures in the range of about
80.degree. C. The surprising efficacy of plasticized polymeric
electrode compositions alone in establishing strong interfacial
bonds with untreated microporous polyolefin separator membranes
provides a novel and simplified means for making long-sought-after
flat, permanently bonded, rechargeable electrochemical battery
cells with thermal shutdown capability as well as excellent
performance characteristics and long operating life.
BRIEF DESCRIPTION OF THE DRAWING
[0025] The present invention will be described with reference to
the accompanying drawing of which:
[0026] FIG. 1 is a representation in cross-sectional elevation of
electrochemical cell electrode and separator members in a process
of lamination which makes effective use of the method of the
present invention;
[0027] FIG. 2 is a representation in cross-sectional elevation of
magnified sections of microporous separator membrane and contacting
plasticized electrode member layer which provides an adhesive
interface bond at laminating conditions in the method of the
invention;
[0028] FIG. 3 is a graphic representation of the highly regular
voltage profile during cycling of a rechargeable battery cell
prepared according to the method of the invention;
[0029] FIG. 4 is a graphic representation of the stability in cell
capacity of the cycling rechargeable battery of FIG. 3;
[0030] FIG. 5 is a graphic representation of the thermal protection
response provided by a rechargeable battery cell prepared according
to the method of the invention; and
[0031] FIG. 6 is a graphic representation of capacity utilization
at varying cycling rates of a rechargeable battery cell prepared
according to the method of the invention.
DESCRIPTION OF THE INVENTION
[0032] As seen in FIG. 1, a preferred method of preparing a
rechargeable Li-ion battery cell comprises assembling a positive
cell electrode member 12 comprising a polymeric composition layer
13 and an associated current collector 11 which may be previously
laminated with layer 13 into an electrode subassembly, an
interposed electron-insulative, ion-transmissive separator member
16, and a negative cell electrode member 18 comprising a polymeric
composition layer 17 and an associated current collector 19. The
assembly is then laminated under heat and pressure, such as by
means of heated rollers (not shown) opposedly biased in the
direction of the arrows.
[0033] A preferred separator member, and one to which the present
invention is directed, comprises a microporous polyolefin membrane
16 which may be seen represented at a region of surface in
magnified cross-section (FIG. 2) as comprising a polyolefin body 22
throughout which are dispersed interconnected pores 24. Such a
separator in an electrochemical cell not only entrains within the
pores electrolyte solution which provides an efficient medium for
Li-ion mobility, but the porous structure also provides protection
against runaway cell heat buildup in that the polyolefin softens
with increasing temperature leading to collapse of the porous
structure at a prescribed pre-danger threshold. Such collapse
occludes the pores and prevents ion transmission with resulting
shut-down of electrochemical activity in the cell.
[0034] Also represented in magnified cross-section in FIG. 2 in
contact with separator 16 at the interface region 25 is a section
of positive electrode member 13 in which, assisted by the heat of
the lamination operation, the incorporated primary plasticizer
softens the matrix polymer to form an adhesive composition 27 which
establishes a fluid adhesive interface with polyolefin 22 of
separator 16. Due to the effect of the plasticizer in the electrode
composition 27, the temperature of lamination may remain below the
shutdown threshold of separator member 16, as is apparent from the
well-defined pores 24 represented in the polyolefin body 22 of the
microporous membrane. Although only a section of positive electrode
member 13 is depicted in the interest of clarity, it should be
understood that the same activity simultaneously occurs at negative
electrode member 17.
[0035] Prior to ultimate cooling of the completed laminate cell
structure, the plasticizer in the interfacial adhesive composition
27 is able to dissipate from the structure, thereby effecting a
firming and strengthening of the laminate bond, as well as a
reduction in the bulk weight of the cell. Additionally, or as an
alternative, the laminate may be immersed in an extracting solvent
selected to have little effect on the electrode matrix polymer,
e.g., diethyl ether or methanol, to remove the plasticizer resident
in the electrode member layer. The completed laminate cell is then
sealed in an encompassing package or envelope of impermeable film
or the like with a measure of electrolyte salt solution to activate
the laminate structure into an operable rechargeable battery
cell.
[0036] A useful separator member material employed in the present
invention is a commercially available, unmodified microporous
polyolefin membrane, such as the Celgard 2300 product marketed by
Celgard, Inc., which comprises two coextensive microporous
polypropylene membranes with an interposed polyethylene membrane
fashioned into a moderately adhering laminate. Similarly useful
microporous products available commercially are Teklon membranes
(Entek International, Lebanon, Oreg.) and Setela membranes (Tonen
Corp., Japan). In each of these separator materials, the body of
polyolefin structure having interconnected pores dispersed
throughout readily takes in and contains electrolyte solutions to
establish the essential ionic conductivity within the
electrochemical cell, while also providing the heat-collapsible
shutdown safety feature of the cell.
[0037] In the light of the foregoing discussion of variant
invention embodiments, the following examples will provide the
skilled artisan with further guidance toward selection of useful
combinations of ingredients, compositions, and operations for
effective practice of the present invention.
EXAMPLE I
Preparation of Polymeric Matrix Positive Electrode
[0038] A composition of 79 g of finely divided, commercial-grade
LiCoO.sub.2, 6.5 g of PVdF-hexafluoropropylene (PVdF-HFP) copolymer
(Kynar PowerFLEX LBG, Elf Atochem NA), 3.5 g of Super P conductive
carbon (MMM Carbon, Belgium), 11 g of propylene carbonate (PC)
plasticizer (Aldrich), and 90 g acetone (J. T. Baker) was mixed in
an hermetically sealed vessel for 1 hour at about 45.degree. C.
After additional homogenization in a laboratory blender, the
resulting paste was cast on a polyester carrier film using a
doctor-blade apparatus gapped at about 0.3 mm. The acetone was
evaporated in a stream of warm air and the resulting
self-supporting plasticized polymer electrode composition layer was
removed from the carrier. A section of the layer was laminated with
a similarly sized section of expanded aluminum foil grid
(MicroGrid, Delker Corp.), which had been pretreated as disclosed
in U.S. Pat. No. 5,840,087, using a heated double-roll laminator at
a temperature of about 145.degree. C. In the lamination operation,
the polymeric electrode composition layer was compacted, or
densified, to ensure contiguity of active material particles. As an
alternative means of fabricating the electrode sub-assembly, two
electrode composition layers formed by the above process may be
jointly laminated on opposite surfaces of the aluminum grid to
create a positive electrode member structure having an embedded
aluminum current collector member.
EXAMPLE II
Preparation of Polymeric Matrix Negative Electrode
[0039] A mixture of 72 g of MCMB 25-28 microbead mesophase
artificial graphite (Osaka Gas Co., Japan), 7.5 g of PVdF-HFP
copolymer (Kynar PowerFLEX LBG), 2.5 g of Super P conductive
carbon, 18 g of PC plasticizer, and 70 g of acetone was processed
as set forth in Example I. A section of the formed electrode
membrane was laminated with a similarly sized section of expanded
copper foil grid (MicroGrid, Delker Corp.) using the heated
double-roll laminator at a temperature of about 135.degree. C. As
alternative embodiments, the copper grid may be embedded between
two electrode membranes in the manner described in Example I or a
copper foil may be coated with electrode composition paste.
EXAMPLE III
Assembly of Bonded-Electrode Electrochemical Cell
[0040] A functional laminated rechargeable Li-ion electrochemical
battery cell was prepared by assembling the cell electrode members
12, 18 of Examples I and II with a Celgard 2300 microporous
separator member 16 as depicted in FIG. 1, and laminating the
assemblage in a commercial heated double-roll laminator device at
about 110.degree. C. and 10 kg/cm roll pressure. After cooling, the
laminate cell structure was immersed for several minutes in diethyl
ether to extract electrode composition plasticizer, air dried,
placed in a circulating-air oven at about 70.degree. C. for 1 hour
to remove moisture and any residual plasticizer. The well-bonded
unitary cell structure was then packaged in an hermetically sealed
multilayer foil/polymer envelope in a helium atmosphere with a
measure of an activating solution of 1 M LiPF.sub.6 in a mixture of
cyclic and acyclic carbonate ester solvents.
[0041] The cell was then connected by means of extending conductor
leads to a computerized battery cycler and tested under various
conditions of common usage employing a CC-CV (constant current
followed by constant voltage) charging protocol, i.e., charge at a
0.7C rate, where 1C denotes current equivalent to a full cell
capacity at a 5-hour discharge rate, to an upper cutoff voltage of
4.2 V followed by a 1-hour CV holding period at 4.2 V. As shown in
FIGS. 3 and 4, the electrochemical cell exhibited highly responsive
performance and a remarkably stable capacity over extended
cycles.
[0042] At the conclusion of the period of cycle testing, the
packaged electrochemical cell was contacted with a heated platen to
raise its temperature to about 140.degree. C., a temperature in
excess of the designed shutdown temperature of the polyolefin
separator membrane, while continuously recording its ohmic
resistance at an AC current frequency of 1 kHz. As shown in FIG. 5,
the resistance of the laminated cell rapidly increased from an
operating level of about 0.1 ohm to about 100 ohm at a cell
temperature of about 132-135.degree. C., indicating that the
microporous structure of the separator was maintained during the
laminating operation and that the laminated microporous separator
was capable of functioning as an effective thermal shutdown element
of a battery cell.
[0043] A series of duplicate cells was tested under similar
protocol employing a variety of CC (C/5, C/2, 1C, 2C and 3C)
discharges. Particularly effective capacity utilization in the
cells was exhibited as shown in FIG. 6.
EXAMPLE IV
Cell Member Interfacial Bond Strength
[0044] Test samples of battery cell structures were prepared
according to the present invention by laminating sections of
untreated Celgard 2300 microporous membrane between densified,
plasticized electrode/current collector assemblies of Examples I
and II using a double-roll laminator at several pressure values
(5.5-18 kg/cm) and temperatures (110-125.degree. C.). After
extraction of plasticizer in diethyl ether, the laminated samples
were dried for 1 hour at 70.degree. C. in an air oven, and cut into
75.times.25 mm test strips.
[0045] Peel strength at the separator-electrode interface of the
samples was tested using an Instron Model 5542 tensile tester at a
strain rate of 200%/min. The results showed that the interface
couples of the samples prepared according to the present invention
registered substantial peel bond strength, which, depending upon
the composition and type of electrode and the specific lamination
conditions, was of the order of 24 to 88 gf/cm. Importantly, this
value markedly exceeds the peel strength between the three
component layers of the Celgard 2300 membrane, which was separately
determined to be between about 6 and 12 gf/cm. These data were
inconclusive in determining the actual electrode/separator
interfacial bond strength, however, since in most instances bond
failure occurred not at that interface, but mostly within the body
of the respective electrode composition layers. It was thus
apparent that the electrode/separator interfacial bond effected by
the present invention indeed exceeds the strength of the individual
electrode composition layers.
[0046] Additional peel test samples were similarly prepared and
placed in sealed plastic laminate envelopes filled with a 1 M
LiPF.sub.6 electrolyte solution in a mixture of cyclic and acyclic
carbonate esters in the manner of an operational battery cell. The
samples were held overnight in an air oven at 80.degree. C.,
simulating an extreme of high-temperature battery storage condition
under which most prior art bonding expedients failed. The same
exceptional interfacial bonds were exhibited by these samples as
were registered by the samples held at moderate ambient
conditions.
EXAMPLE V
Cell Member Lamination Counter-Example
[0047] A positive electrode member typical of such members
comprising many presently available commercial electrochemical
cells was prepared in the manner of Example I from a composition of
90 g of LiCoO.sub.2, 5 g of PVdF homopolymer (Kynar 741, Elf
Atochem), 5 g of Super P carbon, and 60 ml of NMP. The resulting
paste was coated on 0.03 mm aluminum foil at about 0.3 mm and dried
in circulating warm air. The coated foil was then calendered to
about 0.1 mm thickness to form a positive electrode member. A
negative electrode member was similarly prepared in the manner of
Example II from a mixture of 90 g of MCMB 25-28 microbead graphite,
7 g of PVdF polymer, and 3 g of Super P carbon.
[0048] Samples of these unplasticized cell electrode members were
assembled with untreated Celgard 2300 microporous membrane
separator members and processed in the lamination operation of
Example III at roller pressures up to about 18 kg/cm and at several
temperatures up to a micropore collapse, shutdown temperature of
about 135.degree. C. The interfacial bond between these sample
electrode and separator member combinations was marginal, at best,
with none of the electrode/separator sets providing sufficient
interfacial bonding to yield meaningful peel strength data. The
efficacy of the method of utilizing plasticized matrix polymer
electrode members to effect lamination with untreated microporous
separator members in the fabrication of rechargeable battery cells
according to the present invention is exceptionally apparent in
these results.
[0049] It is anticipated that other embodiments and variations of
the present invention will become readily apparent to the skilled
artisan in the light of the foregoing description and examples, and
such embodiments and variations are intended to likewise be
included within the scope of the invention as set out in the
appended claims.
* * * * *