U.S. patent application number 09/946136 was filed with the patent office on 2002-05-23 for fuel hose.
Invention is credited to Iio, Shinji, Katayama, Kazutaka.
Application Number | 20020059960 09/946136 |
Document ID | / |
Family ID | 26599228 |
Filed Date | 2002-05-23 |
United States Patent
Application |
20020059960 |
Kind Code |
A1 |
Katayama, Kazutaka ; et
al. |
May 23, 2002 |
Fuel hose
Abstract
A fuel hose which comprises at least one layer including an
inner layer composed of a resin composition The resin composition
essentially comprises a polyester resin including at least one of
polybutylene naphthalate and polyethylene naphthalate and further
comprises a phospphate.
Inventors: |
Katayama, Kazutaka;
(Komaki-shi, JP) ; Iio, Shinji; (Komaki-shi,
JP) |
Correspondence
Address: |
ARMSTRONG,WESTERMAN & HATTORI, LLP
1725 K STREET, NW.
SUITE 1000
WASHINGTON
DC
20006
US
|
Family ID: |
26599228 |
Appl. No.: |
09/946136 |
Filed: |
September 5, 2001 |
Current U.S.
Class: |
138/137 ;
138/140; 138/141 |
Current CPC
Class: |
F16L 2011/047 20130101;
F16L 11/12 20130101; Y10S 138/07 20130101; F16L 11/06 20130101 |
Class at
Publication: |
138/137 ;
138/140; 138/141 |
International
Class: |
F16L 011/00 |
Foreign Application Data
Date |
Code |
Application Number |
Sep 5, 2000 |
JP |
JP2000-267859 |
Aug 31, 2001 |
JP |
JP2001-263947 |
Claims
What is claimed is:
1. A fuel hose comprising at least one layer including an inner
layer composed of a resin composition, the resin composition
essentially comprising a polyester resin including at least one of
polybutylene naphthalate and polyethylene naphthalate and further
comprising a phosphate.
2. A fuel hose as set forth in claim 1, wherein the phosphate is
present in the resin composition in a proportion of 0.5 to 5 parts
by weight based on 100 parts by weight of the polyester resin.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to a fuel hose and, more
particularly, to a fuel hose for automobile fuel line.
[0003] 2. Description of the Art
[0004] Fuel hoses are conventionally used for automobile fuel
lines. Typically, such a fuel hose is of a single layer structure
or of a multi-layer structure having two or more layers. An inner
layer of the fuel hose to be in contact with a fuel is composed of
a polyamide resin (nylon), a fluororesin or the like. The polyamide
resin serves as a barrier against ordinary gasoline fuel, but has
an extremely poor barrier property against so-called gasohol (a
mixture of a gasoline and an alcohol). On the other hand, the
fluororesin has an excellent barrier property against gasoline fuel
and gasohol, but is an expensive material which thereby leads to an
increase in production costs. In this connection, polyester resins
attract attention as a resin material which are less expensive than
a fluororesin and have a better barrier property against gasohol
than a polyamide resin and, it has been proposed that a fuel hose
be produced by employing polybutylene terephthalate (PBT).
[0005] PBT generally has a better barrier property against gasohol
than a conventional polyamide resin, but is still insufficient in
barrier property when evaluated on stricter criteria which requires
a further improved gasohol permeation resistance. In the future, it
will be environmentally preferred to use a gasohol containing
gasoline and an alcohol (methanol, ethanol or the like) as an
automobile fuel for cleaner automobile emissions, Therefore, these
fuel hoses are required to have a more effective barrier property
against gasohol. In the meantime, the present applicant suggested a
fuel hose comprising polybutylene naphthalate (PBN) for improvement
of gasohol permeation resistance (Japanese Patent Unexamined
Publication No. 2000-154890). However, it was found that this fuel
hose had some problems in a viewpoint of hydrolytic resistance.
[0006] In view of the foregoing, it is an object of the present
invention to provide a fuel hose which is excellent in gasohol
permeation resistance and hydrolytic resistance.
SUMMARY OF THE INVENTION
[0007] In accordance with the present invention to achieve the
aforesaid object, there is provided a fuel hose which comprises at
least one layer including an inner layer composed of a resin
composition, the resin composition essentially comprising a
polyester resin including at least one of polybutylene naphthalate
and polyethylene naphthalate and further comprising a
phosphate.
[0008] The inventors of the present invention have conducted
studies on a material for a fuel hose inner layer to provide a fuel
hose having an excellent gasohol permeation resistance and
hydrolytic resistance. As a result, the inventors have found that
an inner layer composed of a resin composition comprising at least
one of polybutylene naphthalate (PBN) and polyethylene naphthalate
(PEN) among other polyester resins, provides a better gasohol
permeation resistance than a conventional inner layer composed of
PBT, and also have found that when the inner layer is composed of a
resin composition which includes a phosphate in addition to the
above polyester resin, the hose has an improved hydrolytic
resistance, and then attained the present invention. This better
gasohol permeation resistance is supposedly because PBN and PEN
each have a higher crystallinity and a greater molecular size than
PBT and thus provide a higher barrier effect. In general, the
terminal carboxyl groups of the polyester resin are liable to
influence the hydrolysis of the polyester resin. Since the
phosphate blended in the resin composition reacts with these
terminal carboxyl groups to prevent these carboxyl groups from
functioning as a hydrolytic catalyst, the hydrolysis of the
polyester resin is suppressed to thereby improve the hydrolytic
resistance.
[0009] When the fuel hose is constituted by a single layer, the
term "inner layer" means the single layer itself. When the fuel
hose is of a multi-layer structure having two or more layers, the
term "inner layer" means the innermost layer of the hose.
BRIEF DESCRIPTION OF THE DRAWINGS
[0010] FIG. 1 is a perspective view, partly in section,
illustrating an exemplary fuel hose according to the present
invention; and
[0011] FIG. 2 is a perspective view, partly in section,
illustrating another exemplary fuel hose according to the present
invention.
DETAILED DESCRIPTION OF THE INVENTION
[0012] The present invention will hereinafter be described in
detail by way of embodiments thereof.
[0013] A fuel hose according to the present invention may be of a
single layer structure or of a multi-layer structure having two or
more layers, but the structure thereof is not particularly limited.
For example, the fuel hose has a single layer structure, as shown
in FIG. 1, constituted by a layer of a specific resin composition
alone which therefore is the inner layer.
[0014] The resin composition essentially comprises a specific
polyester resin and further comprises a phosphate.
[0015] The polyester resin contained in the resin composition
includes at least one of polybutylene naphthalate (PBN) and
polyethylene naphthalate (PEN). The PBN or the PEN may partly be
copolymerized with an ether or an ester. Of these polymers, PBN is
preferred because of its well-balanced mechanical properties and
flexibility.
[0016] The polyester resin preferably has a melt flow rate (MFR) of
0.5 to 20 g/10 min, particularly preferably 0.5 to 10 g/10 min, as
measured at 260.degree. C. with a load of 2160 g in conformity with
ASTM D1238.
[0017] Preferred examples of the phosphate include aromatic
phosphates such as tricresyl phosphate and resorcinol
diphosphate.
[0018] The phosphate is preferably blended in the resin composition
in a proportion of 0.5 to 5 parts per hundred parts of resin
(hereinafter expressed simply as "phr"), particularly preferably 1
to 5 phr, based on 100 parts of the polyester resin. If the
proportion of the phosphate is smaller than 0.5 phr, improvement of
the hydrolytic resistance generally cannot be expected. If the
proportion of the phosphate is greater than 5 phr, the resulting
resin composition tends to have a deteriorated barrier property,
and a deteriorated processibility due to a reduction in the melt
viscosity.
[0019] The resin composition also may contain a conductive agent as
required in addition to the polyester resin and the phosphate.
[0020] Examples of suitable conductive agents include carbon black
(acetylene black or the like), graphite, carbon nano-tube,
potassium titanate, iron oxide, conductive titanium oxide,
conductive zinc oxide, conductive indium oxide, ion conductive
agents (quaternary ammonium salts, borates and surface active
agents), all of which may be used either alone or in
combination.
[0021] The conductive agent is preferably blended in the resin
composition in a proportion of 4 to 15 phr.
[0022] The resin composition may further contain one or more of a
pigment, a weatherability, a flame retardant or the like, as
required, in a proportion that does not significantly deteriorate
the properties of the resin composition.
[0023] The inventive fuel hose is produced, for example, in the
following manner. The specific polyester resin and the phosphate
are prepared, and an additive such as a conductive agent is added
thereto, as required. The resulting mixture is kneaded by means of
a kneader such as a KCK extruder (or a twin screw extruder) for
preparation of a resin composition as a material for the inner
layer of the hose. The resin composition may be pelletized by means
of a pelletizer. Then, the resin composition is extruded by means
of an extruder to produce a fuel hose of a single layer structure
having an inner layer 1 alone (see FIG. 1).
[0024] The inner layer 1 typically has a thickness of 0.1 to 1.5 mm
preferably 0.3 to 1.0 mm.
[0025] The structure of the inventive fuel hose is not limited to
the single layer structure shown in FIG. 1, but may be of a two
layer structure having an inner layer 1, and an outer layer 2
provided on the outer periphery of the inner layer 1 as shown in
FIG. 2. Further, the fuel hose may be of a three layer structure
having an intermediate layer provided between an inner layer 1 and
an outer layer 2 or of a multi-layer structure having four or more
layers. The respective layers may be bonded to one another with an
adhesive as required.
[0026] The outer layer 2 typically has a thickness of 0.05 to 1.0
mm, preferably 0.05 to 0.8 mm, depending on the application of the
fuel hose.
[0027] Materials for the respective layers provided on the outer
periphery of the inner layer 1 are not particularly limited, but
examples thereof include rubber materials and resin materials. For
example, the specific resin composition containing the aforesaid
specific polyester resin and the phosphate may be employed as the
material for the layer provided on the outer periphery of the inner
layer 1.
[0028] The shape of the inventive fuel hose is not particularly
limited, but the fuel hose may be a long hose, a short hose, or a
corrugated hose.
[0029] The inventive fuel hose is advantageously used as an
automobile fuel hose such as a feed hose, a return hose, a breather
hose, an evaporation hose or a filler hose.
[0030] Next, an explanation will be given to Examples and
Comparative Examples.
[0031] The following ingredients to be employed in Examples and
Comparative Examples were prepared
[0032] Polyester resins
[0033] (1) PBN having an MFR of 5 g/10 min as measured at
260.degree. C. with a load of 2160 g in conformity with ASTM
D1238.
[0034] (2) PEN having an MFR of 5 g/10 min as measured at
260.degree. C. with a load of 2160 g in conformity with ASTM
D1238.
[0035] (3) PBT having an MFR of 30 g/10 min as measured at
265.degree. C. with a load of 2160 g in conformity with ASTM
D1238.
[0036] Polyamide resin
[0037] A lower plasticity Polyamide 11 (Rilsan BESN BLACK P20TL
available from Atofina, Inc. of Paris, France)
[0038] Phosphates
[0039] (1) An aromatic condensed phosphate (PX200 available from
Daihachi Chemical Co., Ltd. of Osaka, Japan)
[0040] (2) Tricresyl phosphate (TCP available from Daihachi
Chemical Co., Ltd. of Osaka, Japan)
[0041] Conductive agents
[0042] (1) Conductive carbon black (Ketchen Black EC available from
Akzo Novel Co., Ltd. of Amergfoort, Netherland)
[0043] (2) Acetylene black (Denka Black available from Denki Kagaku
Kogyo K.K. of Tokyo, Japan)
[0044] Other additives
[0045] Polycarbodiimide (Carbodilite available from Nisshinbo
Industries, Inc. of Tokyo, Japan)
[0046] Nylon 6 (amine-modified nylon G1013 available from Ube Kosan
Co., Ltd. of Yamaguchi, Japan)
EXAMPLES 1 TO 3 AND COMPARATIVE EXAMPLES 1 TO 6
[0047] Resin compositions (inner layer materials) were each
prepared by blending the ingredients in a blend ratio as shown in
Tables 1 and 3, kneading the resulting mixture by means of a KCK
extruder (available from KCK Engineering Co., Ltd. of Osaka,
Japan), and pelletizing the mixture. When the phosphate PX200
and/or the conductive agent were employed, the resulting pellets
were blended therewith on a dry basis. When the phosphate TCP was
employed, the pellets were impregnated therewith on a wet basis.
Then, the resin compositions were each extruded by means of an
extruder. Thus, a fuel hose (inner diameter of 6 mm) was produced,
which was of a single layer structure having an inner layer
alone.
EXAMPLES 4 to 6
[0048] Pelletized resin compositions (inner layer materials) were
each prepared in substantially the same manner as in Example 1 by
blending ingredients in a blend ratio as shown in Table 1. A
pelletized resin composition (outer layer material) was prepared in
accordance with the same formulation as the resin composition in
Example 1. The inner layer materials were each coextruded with the
outer layer material by means of two extruders. Thus, a fuel hose
(inner diameter: 6 mm) was produced, which was of a two layer
structure having an inner layer and an outer layer provided on the
outer periphery of the inner layer.
EXAMPLE 7
[0049] A pelletized resin composition (inner layer material) was
prepared in substantially the same manner as in Example 1 by
blending ingredients in a blend ratio as shown in Table 2. A
pelletized resin composition prepared in accordance with the same
formulation as the resin composition in Example 2 was blended with
100 parts of a pelletized sheathing material on a dry basis, and
the resulting mixture was kneaded by means of a KCK extruder
(available from KCK Engineering Co., Ltd. of Osaka, Japan) for
preparation of a pelletized intermediate layer material. Further,
polyamide 12 (Rilsan AESN BLACK P40TL available from Atofina, Inc.
of Paris, France) was prepared as an outer layer material. The
inner layer material was coextruded with the intermediate layer
material and the outer layer material by means of three extruders.
Thus, a fuel hose (inner diameter of 6 mm) was produced, which was
of a three layer structure having an inner layer, an intermediate
layer provided as an adhesive layer on the outer periphery of the
inner layer, and an outer layer provided on the outer periphery of
the intermediate layer.
COMPARATIVE EXAMPLES 7 and 8
[0050] Pelletized resin compositions (inner layer materials) were
each prepared in substantially the same manner as in Example 1 by
blending the ingredients in a blend ratio as shown in Table 4.
Further, a pelletized resin composition (outer layer material) was
prepared in accordance with the same formulation as the resin
composition in Comparative Example 5. Then, the inner layer
materials were each coextruded with the outer layer material by
means of extruders. Thus, a fuel hose (inner diameter: 6 mm) was
prepared, which was of a two layer structure having an inner layer
and an outer layer provided on the outer periphery of the inner
layer.
[0051] The fuel hoses of the Examples and the Comparative Examples
thus produced were each evaluated based on the following criteria.
The results are shown in Tables 1 to 3.
[0052] Extrudability
[0053] The extrudability of the resin composition (inner layer
material) for each of the fuel hoses was evaluated. In Tables 1 to
4, a symbol "O" indicates a good extrudability, while a symbol "X"
indicates a poor extrudability manifested by a surface roughness of
the inner layer.
[0054] Surface resistivity
[0055] The surface resistivity on the inner periphery of the inner
layer of each of the fuel hoses was measured in conformity with
GM213.
[0056] Initial elongation at break (EB)
[0057] The fuel hoses were each cut into halves for preparation of
an ASTM type V dumbbell. With the use of the dumbbell, the
elongation at break (EB) of the fuel hose was measured in
conformity with ASTM D638.
[0058] Heat aging resistance
[0059] The aforesaid dumbbell was subjected to heat at 130.degree.
C. for 400 hours, and then the EB of the fuel hose was measured for
evaluation of the heat aging resistance of the fuel hose.
[0060] Hydrolytic resistance
[0061] After the aforesaid dumbbell was immersed in pure water in a
pressure vessel at 120.degree. C. for 168 hours, the EB of the fuel
hose was measured for evaluation of the hydrolytic resistance of
the fuel hose.
[0062] Gasohol permeability
[0063] A gasohol containing Fuel C (containing 50 vol % of toluene
and 50 vol % of isooctane) and methanol in a ratio of 85:15 (vol %)
was filled in each of the fuel hoses (length: 1 m), and allowed to
stand at 60.degree. C. for 7 days. Thereafter, the gasohol was
newly filled in the fuel hose, and again allowed to stand at
60.degree. C. for 7 days. A weight difference was determined for
evaluation of the gasohol permeability of the fuel hose.
[0064] Presence of cracks
[0065] The fuel hoses subjected to the gasohol permeability test
were each bent by 180 degrees, and then cut into halves. The inner
peripheral surface of the hose was visually observed for
cracks.
1 TABLE 1 (parts) Examples 1 2 3 PBN 100 100 100 PEN -- -- -- PX200
1 3 -- TCP -- -- 3 Ketchen black EC -- -- -- Thickness of inner 1 1
1 layer (mm) Thickness of outer -- -- -- layer (mm) Extrudability
.smallcircle. .smallcircle. .smallcircle. Surface resistivity 2
.times. 10.sup.13 1 .times. 10.sup.13 2 .times. 10.sup.13 (.OMEGA.)
Initial elongation at 300 280 290 break (%) Heat aging resistance:
-20 -10 -17 reduction in extensibility (%) Hydrolytic resistance:
-10 -5 -10 reduction in extensibility (%) Gasohol permeability 0.2
0.2 0.3 (g/m/day) Cracks No No No
[0066]
2 TABLE 2 (parts) Examples 4 5 6 7 PBN 100 100 100 100 PX200 3 --
-- 3 TCP -- 5 5 -- Ketchen black EC 5 5 -- 5 Denka black -- -- 15
-- Thickness of inner 0.1 0.1 0.1 0.1 layer (mm) Thickness of
inter- -- -- -- 0.1 mediate layer (mm) Thickness of outer 0.9 0.9
0.9 0.6 layer (mm) Extrudability .smallcircle. .smallcircle.
.smallcircle. .smallcircle. Surface resistivity 2 .times. 10.sup.4
1 .times. 10.sup.4 1 .times. 10.sup.4 2 .times. 10.sup.4 (.OMEGA.)
Initial elongation at 210 230 220 250 break (%) Heat aging
resistance: -25 -20 -30 -25 reduction in extensibility (%)
Hydrolytic resistance: -5 -10 -15 -10 reduction in extensibility
(%) Gasohol permeability 0.2 0.3 0.3 0.4 (g/m/day) Cracks No No No
No
[0067]
3TABLE 3 (parts) Comparative Examples 1 2 3 4 5 6 PBN 100 -- -- --
-- -- PEN -- 100 -- -- -- -- PBT -- -- 100 -- 100 100 Polyamide 11
-- -- -- 100 -- -- Carbodilite -- -- -- -- 3 -- Nylon 6 -- -- -- --
-- 10 Ketchen black EC -- -- -- -- -- -- Thickness of inner 1 0.5 1
1 1 1 layer (mm) Extrudability .largecircle. .largecircle.
.largecircle. .largecircle. .largecircle. .largecircle. Surface
resistivity 5 .times. 10.sup.13 3 .times. 10.sup.13 4 .times.
10.sup.13 7 .times. 10.sup.13 1 .times. 10.sup.13 3 .times.
10.sup.13 (.OMEGA.) Initial elongation at 240 200 260 280 250 230
break (%) Heat aging resistance: -25 -48 -90 -8 -70 -90 reduction
in extensibility (%) Hydrolytic resistance: -30 -65 -95 -10 -40 -95
reduction in extensibility (%) Gasohol permeability 0.1> 0.1 0.7
5.5 1.0 4.3 (g/m/day) Cracks No No No No Yes No
[0068]
4 TABLE 4 (parts) Comparative Examples 7 8 PBT 100 100 Polyamide 11
-- -- Carbodilite -- -- Nylon 6 -- -- Ketchen black EC 2 20
Thickness of inner 0.1 0.1 layer (mm) Thickness of outer 0.9 0.9
layer (mm) Extrudability .smallcircle. x Surface resistivity 5
.times. 10.sup.12 5 .times. 10.sup.2 (.OMEGA.) Initial elongation
at 250 180 break (%) Heat aging resistance: -95 -98 reduction in
extensibility (%) Hydrolytic resistance: -95 -98 reduction in
extensibility (%) Gasohol permeability 1.0 1.2 (g/m/day) Cracks No
No
[0069] As can be understood from the above results, the fuel hoses
of Examples 1 to 7 were each excellent in gasohol permeation
resistance with a low gasohol permeability and also were each
excellent in hydrolytic resistance.
[0070] On the other hand, the fuel hoses of Comparative Examples 1
and 2 were each inferior in hydrolytic resistance because the resin
compositions did not contain the phosphates. The fuel hose of
Comparative Example 3 produced by employing the PBT-based resin
composition was poor in gasohol permeation resistance by having a
greater gasohol permeability than the fuel hoses of the Examples.
The fuel hose of Comparative Example 4 produced by employing the
Polyamide 11-based resin composition had an extremely poor gasohol
permeation resistance. The fuel hoses of Comparative Examples 5 to
8 produced by employing the PBT-based resin compositions each had a
poor gasohol permeation resistance by having a greater gasohol
permeability than the fuel hoses of the Examples. The fuel hose of
Comparative Example 5 had an improved hydrolytic resistance because
polycarbodiimide contained in the resin composition reacted with
terminal carboxyl groups of PBT, but the hose was embrittled during
use. This is because polycarbodiimide was highly reactive with
hydroxyl groups of the alcohol (methanol) contained in the gasohol.
Further, the fuel hose of Comparative Example 3 suffered from
cracks when the hose was bent after the gasohol permeation
test.
[0071] As described above, the inventive fuel hose, which comprises
at least one layer including an inner layer composed of the resin
composition essentially containing the specific polyester resin and
further containing the phosphate, is excellent in gasohol
permeation resistance.
* * * * *