U.S. patent application number 09/907475 was filed with the patent office on 2002-04-11 for magnetic tape.
This patent application is currently assigned to Quantum Corporation. Invention is credited to Hosoya, Manabu, Katashima, Mitsuhiro.
Application Number | 20020041982 09/907475 |
Document ID | / |
Family ID | 17737203 |
Filed Date | 2002-04-11 |
United States Patent
Application |
20020041982 |
Kind Code |
A1 |
Katashima, Mitsuhiro ; et
al. |
April 11, 2002 |
Magnetic tape
Abstract
Magnetic tape (1) comprising a substrate, a magnetic layer
provided on one side of the substrate and a backcoating layer (5)
provided on the other side of the substrate, wherein the
backcoating layer (5) is a layer capable of magnetic recording on
which three or more servo tracks (10a, 10b 10c) have magnetically
been formed in parallel with the longitudinal direction of the
tape, and the backcoating layer (5) has a higher coercive force
than the coercive force of the whole of all the layers on the
magnetic layer side and a lower saturation flux density than the
saturation flux density of the whole of all the layers on the
magnetic layer side.
Inventors: |
Katashima, Mitsuhiro;
(Tochigi, JP) ; Hosoya, Manabu; (Tochigi,
JP) |
Correspondence
Address: |
JOHN J. GAGEL
Fish & Richardson P.C.
225 Franklin Street
Boston
MA
02110-2804
US
|
Assignee: |
Quantum Corporation
|
Family ID: |
17737203 |
Appl. No.: |
09/907475 |
Filed: |
July 17, 2001 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
09907475 |
Jul 17, 2001 |
|
|
|
09529930 |
Sep 12, 2000 |
|
|
|
6319595 |
|
|
|
|
Current U.S.
Class: |
428/845.6 |
Current CPC
Class: |
G11B 5/584 20130101;
G11B 5/78 20130101; Y10T 428/24942 20150115; Y10T 428/256 20150115;
G11B 5/718 20130101; Y10T 428/257 20150115; G11B 5/5504
20130101 |
Class at
Publication: |
428/694.0BM |
International
Class: |
G11B 005/716 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 12, 1998 |
JP |
PCT/JP98/04766 |
Oct 21, 1997 |
JP |
9-288973 |
Claims
1. Magnetic tape comprising a substrate, a magnetic layer provided
on one side of said substrate and a backcoating layer provided on
the other side of said substrate, wherein: said backcoating layer
is a layer capable of magnetic recording on which three or more
servo tracks have magnetically been formed in parallel with the
longitudinal direction of the tape; and said backcoating layer has
a higher coercive force than the coercive force of the whole of all
the layers on the magnetic layer side and has a lower saturation
flux density than the saturation flux density of the whole of all
the layers on the magnetic layer side.
2. Magnetic tape as claimed in claim 1, wherein the coercive force
of said backcoating layer is 110% or more of the coercive force of
the whole of all the layers on the magnetic layer side, and the
saturation flux density of said backcoating layer is 90% or less of
the saturation flux density of the whole of all the layers on the
magnetic layer side.
3. Magnetic tape as claimed in claim 1, wherein the coercive force
of said backcoating layer is 90 to 400 kA/m, and the coercive force
of the whole of all the layers on the magnetic layer side is 80 to
350 kA/m.
4. Magnetic tape as claimed in claim 1, wherein the saturation flux
density of said backcoating layer is 30 to 350 mT, and the
saturation flux density of the whole of all the layers on the
magnetic layer side is 100 to 400 mT.
5. Magnetic tape as claimed in claim 1, wherein said backcoating
layer comprises magnetic powder, a binder and carbon black, said
binder is present in an amount of 10 to 50 parts by weight per 100
parts by weight of said magnetic powder, and said carbon black is
present in an amount of 2 to 50 parts by weight per 100 parts by
weight of said magnetic powder.
6. Magnetic tape as claimed in claim 5, wherein said magnetic
powder comprises tabular ferromagnetic hexagonal ferrite powder
having a tabular diameter of 20 to 100 nm.
7. Magnetic tape as claimed in claim 1, wherein one or more
magnetic or nonmagnetic intermediate layers are provided between
said substrate and said magnetic layer, and said magnetic layer
comprises acicular or spindle-shaped ferromagnetic metal powder
having a major axis length of 0.05 to 0.2 .mu.m or tabular
ferromagnetic hexagonal ferrite powder having a tabular diameter of
0.1 .mu.m or smaller.
Description
TECHNICAL FIELD
[0001] The present invention relates to magnetic tape having
magnetic servo tracks. More particularly, it relates to magnetic
tape having magnetic servo tracks on the side opposite to the
magnetic recording side.
BACKGROUND ART
[0002] The recent expanding scale of the computer network and the
importance of security for data management have been increasing the
demand for magnetic tape having an increased recording capacity for
use as a medium for data backup. Approaches to high recording
capacity are divided into improvement on recording density and
extension of the tape length.
[0003] Since the tape length that can be put in a tape cartridge as
wound is the upper limit of the recording capacity, extension of
the tape length for increasing the recording capacity cannot be
achieved but by reducing the tape thickness. Therefore, an increase
in recording capacity attained by this approach is of necessity
limited. With respect to the method of increasing a recording
density, it is known that magnetic tape has a lower recording
density than a hard disc drive. Serpentine type magnetic tape
particularly has a low recording density, which is due to the low
track density. On the other hand helical scan type magnetic tape is
known to have a higher track density than the serpentine type
magnetic tape. This is because the magnetic tape of helical scan
type uses a servo tracking system called automatic track finding
(ATF).
[0004] A servo tracking system has also been adopted to serpentine
type magnetic tape to improve the track density. Methods that have
been proposed as such a servo tracking system include an embedded
servo system, in which servo signals are written on the same track
as the data track on the magnetic recording surface, and a system
in which a track exclusive to servo signals is provided on the
magnetic recording surface. Japanese Patent Publication No.
82626/95 proposes a tracking system particularly useful where the
pitch of data tracks is as small as several tens of microns, in
which a dedicated track for servo information is provided on the
magnetic recording surface and a plurality of servo signal
reproduction heads are used to read the servo signals for tracking.
According to this technique, however, the number of servo signal
reproduction heads must be increased as the number of tracks
increases. In order to avoid this, the servo track should be
increased. Like this, conventional servo tracking systems use the
same side of magnetic tape as used for data recording, which
results in reduction of the data recording area. This problem is
conspicuous in the servo tracking system of Japanese Patent Publn.
No. 82626/95 when a track density is as high as about 30 tpmm
(tracks per mm) or even more.
DISCLOSURE OF THE INVENTION
[0005] Accordingly, an object of the present invention is to
provide magnetic tape which is capable of servo tracking without
reducing the data area.
[0006] Another object of the present invention is to provide
magnetic tape having an increased track density.
[0007] Still another object of the present invention is to provide
magnetic tape having a high recording capacity.
[0008] As a result of extensive investigation, the present
inventors found that servo tracking can be carried out without
diminishing the data area of a magnetic layer by providing a
magnetic servo track on the backcoating layer of magnetic tape,
which turned out to give rise to a new problem as to various
characteristics of the magnetic tape. As a result of further study,
they have found that the various problems associated with a
magnetic servo track formed on the backcoating layer can be solved
to provide magnetic tape accomplishing the above objects by
defining the coercive force and saturation flux density of the
backcoating layer to be above a specific value or below a specific
value, respectively, in relation to the coercive force and the
saturation flux density of the whole of all the layers on the
magnetic layer side.
[0009] Completed based on the above finding, the present invention
has accomplished the above objects by providing magnetic tape
comprising a substrate, a magnetic layer provided on one side of
the substrate and a backcoating layer provided on the other side of
the substrate, wherein the backcoating layer is a layer capable of
magnetic recording on which three or more servo tracks have
magnetically been formed in parallel with the longitudinal
direction of the tape, and the backcoating layer has a higher
coercive force than the coercive force of the whole of all the
layers on the magnetic layer side and has a lower saturation flux
density than the saturation flux density of the whole of all the
layers on the magnetic layer side.
BRIEF DESCRIPTION OF THE DRAWINGS
[0010] Various other objects, features and attendant advantages of
the present invention will be better understood from the following
description and the accompanying drawings, in which like reference
characters designate like parts and wherein:
[0011] FIG. 1 is a schematic view showing the structure of an
embodiment of the magnetic tape according to the present
invention.
[0012] FIG. 2 schematically shows the servo tracks formed on a
backcoating layer.
[0013] FIG. 3 is a schematic view of a drive used for recording and
reproducing the magnetic tape according to the present
invention.
[0014] FIGS. 4(a), 4(b), 4(c), 4(d), 4(e), and 4(f) schematically
illustrate a method of servo tracking on the magnetic tape
according to the present invention.
[0015] FIG. 5 schematically shows the equipment for recording servo
signals on the backcoating layer of magnetic tape.
BEST MODE FOR CARRYING OUT THE INVENTION
[0016] The magnetic tape of the present invention will be described
with reference to the preferred embodiments thereof by referring to
the accompanying drawings, in which FIG. 1 is a schematic view
showing the structure of an embodiment of the magnetic tape
according to the present invention; FIG. 2 schematically shows the
servo tracks formed on a backcoating layer; FIG. 3 is a schematic
view of a drive used for recording and reproducing the magnetic
tape according to the present invention; and FIG. 4 schematically
illustrates a method of servo tracking on the magnetic tape
according to the present invention.
[0017] A magnetic tape 1 of the embodiment shown in FIG. 1
comprises a substrate 2 having provided thereon an intermediate
layer 3 and a magnetic layer 4 as a top layer adjoining the
intermediate layer 3. The substrate 2 has on the other side a
backcoating layer 5.
[0018] The magnetic tape 1 shown in FIG. 1 is used for a serpentine
recording system. The magnetic layer 4 has a plurality of data
tracks in parallel with the running direction of the tape 1. On
use, a head unit having a predetermined number of magnetic heads is
moved across the magnetic tape 1, switching among data tracks, to
record or reproduce data on the data track corresponding to each
magnetic head. Servo tracking is carried out so that each magnetic
head may be positioned on a right data track on switching among the
tracks or during recording or reproduction.
[0019] The backcoating layer 5 is a layer formed of magnetic powder
dispersed in a binder and is capable of magnetic recording. As
shown in FIGS. 2, three servo tracks 10a, 10b, and 10c have
previously been formed magnetically on the backcoating layer 5 in
parallel with the longitudinal direction (i.e., the running
direction) of the tape. Each of these servo tracks is formed over
the whole length of the magnetic tape 1. Servo signals have
previously been recorded magnetically on these servo tracks, and
the recorded servo signals are read to carry out servo tracking on
the data tracks of the magnetic layer 4. The servo tracks, each
having a width w, have a track pitch w. As stated previously, data
tracks of the magnetic layer 4 are also formed in parallel with the
longitudinal direction of the magnetic tape 1 similarly to the
servo tracks, but the relative positional relationship between the
data tracks and the servo tracks is not particularly limited.
[0020] Servo tracking based on the reading of the servo signals
recorded on the servo tracks 10a, 10b, and 10c will be explained
with reference to FIG. 3.
[0021] FIG. 3 is a schematic view of a drive 20 which is used for
recording and reproducing the magnetic tape 1 shown in FIGS. 1 and
2. The drive 20 has a magnetic head unit 21, a pair of guide rolls
22 and 23, a forward servo signal reading head 24, and a backward
servo signal reading head 25. The magnetic head unit 21 is composed
of three magnetic heads linearly arranged side by side along the
tape running direction. A recording head 26 is in the middle, and a
forward reproduction head 27 and a backward reproduction head 28
are on each side thereof Needless to say, the drive 20 is equipped
with, while not shown, other various parts used in ordinary drives
for magnetic tape in addition to the above-mentioned parts.
[0022] In recording and reproducing the magnetic tape 1 on the
drive 20, the side of the magnetic layer 4 is brought into contact
with each head of the magnetic head unit 21, while the side of the
backcoating layer 5 is brought into contact with each servo signal
reading head. When the magnetic tape 1 runs, fore example, forward
(in the direction indicated by arrow F), the servo signals recorded
on the servo tracks of the backcoating layer 5 are first read by
the forward servo signal reading head 24. From the servo signals
are furnished the information as to the position on the magnetic
tape 1. The positional information is processed by a servo tracking
processor 29 fitted to the drive 20 to make a judgement on whether
or not the recording head 26 or the forward reproduction head 27
are on the right positions of the data tracks of the magnetic layer
4. The judgement is fed back to the respective drives (not shown)
of the magnetic head unit 21 and/or the positioning guide rolls 22
and 23 to carry out servo tracking. As a result, the recording head
26 and the forward reproduction head 27 are positioned on the right
data track of the magnetic layer 4 whereby data are recorded by the
recording head 26 or the data recorded on that data track is
reproduced by the forward reproduction head 27.
[0023] The above-described manner of servo tracking is further
explained with reference to FIG. 4. As shown in FIGS. 4(a) to 4(c),
servo signals Sa, Sb, and Sc have been recorded on the three servo
tracks 10a, 10b, and 10c, respectively, at regular intervals. It is
preferred that the servo signals Sa, Sb, and Sc have different
recording wavelengths. The recording lengths of these signals may
be substantially equal. The recording pitch of the servo signals on
each servo track is equal to the sum of the recording lengths of
the servo signals Sa, Sb, and Sc. The servo signals are recorded in
the order of Sc, Sb, and Sa in the forward direction without
overlaps.
[0024] As shown in FIGS. 4(a) to 4(c), the width of the forward
servo signal recording head 24 in its gap is greater than the track
width w of each servo track and smaller than three times the track
pitch. As a result, the forward servo signal recording head 24 can
read simultaneously the servo signals Sa, Sb, and Sc recorded on
the three servo tracks 10a, 10b and 10c, respectively.
[0025] Going into more details of servo signal reading by referring
to FIGS. 4(a) to 4(c), the magnetic tape is running in the forward
direction F, and the servo signal Sc recorded on the servo track
10c is the first to be read by the forward servo signal recording
head 24. The servo signal Sb recorded on the servo track 10b is
then read. As the tape runs further, the servo signal Sa recorded
on the servo track 10a is read. The servo signals Sa, Sb and Sc
thus read out show output wave forms as shown in FIGS. 4(d) to
4(f). FIGS. 4(d) to 4(f) correspond to the output wave forms in
case where the forward servo signal reading head 24 is at the
positions shown in FIGS. 4(a) to 4(c), respectively.
[0026] The manner of servo tracking will be further illustrated by
referring to the output wave forms shown in FIGS. 4(d) to 4(f).
FIG. 4(d) is the output wave form with the forward servo signal
reading head 24 being at the position shown in FIG. 4(a), in which
the output wave forms of the servo signals Sa and Sc are
symmetrical about the output wave form of the servo signal Sb. The
state giving such wave forms is the state where the forward servo
signal reading head 24 is positioned in the middle in the width
direction of the three servo tracks 10a, 10b and 10c, i.e., an
"on-track" state, which means the recording head 26 and the forward
reproducing head 27 are properly positioned on a prescribed data
track.
[0027] On the other hand, where the output wave form shown in FIGS.
4(e) or 4(f) is obtained, that is, where the output wave forms of
the servo signals Sa and Sc are asymmetrical about the output wave
form of the servo signal Sb, the forward servo signal reading head
24 is shifted toward either the servo track 10a or 10b as shown in
FIG. 4(b) or 4(c). This state is an "off-track" state, indicating
that the recording head 26 and the forward reproducing head 27 are
not positioned on the proper data track of the magnetic layer. As
shown in FIG. 3, the servo tracking processor 29 mounted on the
drive 20 gives instructions to the drive (not shown) of the
magnetic head unit 21 and/or the positioning guide rolls 22 and 23
so that the recording head 26 and the forward reproducing head 27
may be positioned properly. As a result, the recording head 26 and
the forward reproducing head 27 are positioned on the right track
by the drive (not shown) to achieve an "on-track" state.
[0028] The width w and the pitch p of the servo tracks 10a, 10b and
10c are described by referring to FIG. 2. These tracks are equal in
width, each preferably having a width of 10 to 500 .mu.m,
particularly 20 to 100 .mu.m. If the width w of each servo track is
less than 10 .mu.m, the system (the servo signal reading section
and the running system) tends to fail to catch the signals
accurately. If it exceeds 500 .mu.m, the system tends to fail to
achieve sufficient tracking accuracy. Therefore, it is preferred
for the width to fall within the above range.
[0029] As for the pitch p, on the other hand, since there is no gap
between adjacent servo tracks, the pitch p is equal to the track
width w. However, to make a gap between adjacent serve tracks gives
rise to no problem. In such a case, the pitch p is preferably 11 to
600 .mu.m, still preferably 21 to 150 .mu.m.
[0030] To secure tracking accuracy, three or more servo tracks are
formed on the backcoating layer 5. It is preferred that servo
tracking be carried out using three servo tracks as one set in
accordance with the above-mentioned tracking system.
[0031] Where one or more sets each consisting of three servo tracks
are used, the sets of servo tracks may be arranged over the whole
width direction of the magnetic tape 1 at prescribed intervals, or
the sets of servo tracks may be localized in a part of the width
direction of the magnetic tape 10, for example, one or more sets
may be arranged in the central portion or either one of side
portions of the tape in the width direction at prescribed
intervals. Further, the sets spaced at prescribed intervals may be
localized in two or more portions of the magnetic tape 10 in the
width direction. For example, one or more sets can be arranged on
each side portion of the tape (the number of the sets on each
portion may be the same or different), one or more sets can be
arranged on the central portion and one of the side portions of the
tape (the number of the sets on each portion may be the same or
different), or one or more sets may be arranged on the central
portion and each side portion of the tape (the number of tracks on
each portion may be the same or different). In any case, the total
number of the sets of the servo tracks is preferably a measure of
the number of the data tracks of the magnetic layer 4.
[0032] The following problem will arise where the backcoating layer
of magnetic tape is made capable of magnetic recording and servo
tracks are magnetically formed on the backcoating layer.
[0033] Since both the magnetic layer and the backcoating layer
possess magnetism, they would interact magnetically to cause
magnetic transfer when the magnetic tape is wound. That is, the
backcoating layer will be magnetized by the magnetism of the
magnetic layer, or the magnetic layer may be magnetized by the
magnetism of the backcoating layer. It may follow that both the
data signals recorded on the magnetic layer and the servo signals
recorded on the backcoating layer have reduced outputs, failing to
furnish sufficient reproduction outputs for reliable servo
tracking.
[0034] According to the present invention, on the contrary, the
above problem can be solved by defining the coercive force and
saturation flux density of the backcoating layer to be above a
specific value or below a specific value, respectively, in relation
to the coercive force and the saturation flux density of the whole
of all the layers on the magnetic layer side, and thus there is
provided magnetic tape capable of servo tracking without suffering
from reduction in data area.
[0035] Entering into more detail, in the magnetic tape 1 of the
present invention, the coercive force of the backcoating layer S
(hereinafter referred to as Hcb) is set higher than the coercive
force of the whole of all the layers on the magnetic layer side
(hereinafter referred to as Hcm). If Hcb is equal to or less than
Hcm, the backcoating layer S would be magnetized by the magnetism
of the whole layers on the magnetic layer side when the magnetic
tape 1 is wound. As a result, the output of the servo signals
recorded on the backcoating layer 5 falls, leading to a failure of
reliable servo tracking. Hcb is preferably 110% or more, still
preferably 110 to 200%, particularly preferably 120 to 180%, of
Hcm. More specifically, Hcb preferably ranges from 90 to 400 kA/m,
particularly 120 to 300 kA/m. On the other hand, Hcm is preferably
from 80 to 350 kA/m, particularly 100 to 250 kA/m. The language
"the coercive force of the whole of all the layers on the magnetic
layer side" as used throughout the specification and claims means
that the coercive force ascribed to the whole of all the magnetic
layers provided on the magnetic layer side". Accordingly, the
magnetic tape 1 shown in FIG. 1 taken for instance, where the
intermediate layer 3 is a nonmagnetic layer, the "coercive force of
the whole of all the layers on the magnetic layer side" denotes the
coercive force of the magnetic layer 4. Where the intermediate
layer 3 is a magnetic layer, the language means the coercive force
of the whole of the magnetic layer 4 and the intermediate layer 3.
Measurement is made on magnetic tape only having the magnetic layer
4 and the intermediate layer 3 on the substrate 2 (i.e., magnetic
tape having no backcoating layer 5).
[0036] As to the saturation flux density of the backcoating layer 5
and the magnetic layer, on the other hand, the saturation flux
density of the backcoating layer (hereinafter referred to as Bsb)
is set lower than the saturation flux density of the whole of all
the layers on the magnetic layer side (hereinafter referred to as
Bsm). If Bsb is equal to or higher than Bsm, the magnetic layer 4
will be magnetized by the magnetic flux generated from the servo
signals recorded on the backcoating layer 5 when the magnetic tape
1 is wound. As a result, the data signals recorded on the magnetic
layer 4 are reduced to cause an increased error rate. It is
preferred that Bsb be 90% or less, particularly 10 to 90%,
especially 30 to 80%, of Bsm. More specifically, Bsb is preferably
30 to 350 mT, particularly 50 to 200 T, and Bsm is preferably 100
to 400 mT, particularly 120 to 300 mT. The expression "the
saturation flux density of the whole of all the layers on the
magnetic layer side" as used throughout the specification and
claims means the saturation flux density ascribed to the whole of
all the magnetic layers provided on the magnetic layer side.
Accordingly, the magnetic tape 1 shown in FIG. 1 taken for
instance, where the intermediate layer 3 is a nonmagnetic layer,
the "saturation flux density of the whole of all the layers on the
magnetic layer side" denotes the saturation flux density of the
magnetic layer 4. Where the intermediate layer 3 is a magnetic
layer, the expression means the saturation flux density of the
whole of the magnetic layer 4 and the intermediate layer 3.
Similarly to the measurement of coercive force stated above,
measurement of saturation flux density is made on magnetic tape
only having the magnetic layer 4 and the intermediate layer 3 on
the substrate 2 (i.e., magnetic tape having no backcoating layer
5).
[0037] One of the methods for providing such a backcoating layer 5
whose coercive force and saturation flux density satisfy the
above-described respective relationships to the coercive force and
the saturation flux density of the whole of all the layers on the
magnetic layer side is a method comprising adjusting the
formulation of various components constituting the backcoating
layer 5, particularly the kind and amount of magnetic powder. Each
component constituting the backcoating layer will be described
hereunder.
[0038] The backcoating layer 5 comprises magnetic powder and a
binder.
[0039] The magnetic powder which can be used include those commonly
employed in magnetic tape, such as ferromagnetic hexagonal ferrite
powder, ferromagnetic metallic powder, and ferromagnetic iron oxide
powder. In particular, it is preferred to use ferromagnetic
hexagonal ferrite powder. Having a high coercive force and a low
saturation flux density, ferromagnetic hexagonal ferrite powder
used as magnetic powder easily provides a backcoating layer 5 whose
coercive force and saturation flux density satisfy the
relationships with the coercive force and the saturation flux
density of the whole of all the layers on the magnetic layer
side.
[0040] The ferromagnetic hexagonal ferrite powder includes fine
tabular magnetic particles of barium ferrite or strontium ferrite,
part of the Fe atoms of which may be displaced with Ti Co, Ni, Zn,
V or the like atoms. The ferromagnetic hexagonal ferrite powder
preferably has a high coercive force and a low saturation
magnetization. Specifically, it preferably has a coercive force
(Hc) of 100 to 400 kA/m, particularly 150 to 350 kA/m, and a
saturation magnetization (.sigma.s) of 20 to 100 Am.sup.2/kg,
particularly 30 to 70 A.sup.2/kg.
[0041] The ferromagnetic hexagonal ferrite powder preferably has a
small particle size for the purpose of narrowing the magnetic
transition range and reducing the surface roughness. Specifically,
it preferably has a tabular diameter of 20 to 100 nm, particularly
30 to 70 nm, with an aspect ratio (diameter/thickness) of 1 to 10,
particularly 3 to 6, and a BET specific surface area of 30 to 70
m.sup.2/g.
[0042] Any binders employable in magnetic tape can be combined with
the magnetic powder with no restriction. For example, thermoplastic
resins, thermosetting resins, reactive resins, and mixtures thereof
can be used. Specific examples of useful binders are vinyl chloride
copolymers or modified vinyl chloride copolymers, copolymers
comprising acrylic acid, methacrylic acid or esters thereof,
acrylonitrile copolymers (rubbery resins), polyester resins,
polyurethane resins, epoxy resins, cellulosic resins, and polyamide
resins. These binders preferably have a number average molecular
weight of 2,000 to 200,000. In order to improve dispersing
properties for various particles incorporated into the backcoating
layer 5, the binder resin can have a polarizing functional group
(so-called polar group), such as a hydroxyl group, a carboxyl group
or a salt thereof, a sulfo group or a salt thereof, a phosphate
group or a salt thereof, a nitro group, a nitric ester group, an
acetyl group, a sulfuric ester group or a salt thereof, an epoxy
group, a nitrile group, a carbonyl group, an amino group, an
alkylamino group, an alkylammonium salt group, a sulfobetaine
structure, a carbobetaine structure, and the like. The binder is
preferably used in an amount of 10 to 50 parts by weight,
particularly 12 to 30 parts by weight, per 100 parts by weight of
the magnetic powder.
[0043] The backcoating layer 5 can further contain abrasive grains,
carbon black, lubricants, hardeners, etc. in addition to the
above-described components.
[0044] Abrasive grains having a Mohs hardness of 7 or higher, such
as alumina, silica, ZrO.sub.2, and Cr.sub.2O.sub.3, are used for
preference. From the standpoint of reduction in frictional
coefficient during running and improvement in running durability,
the abrasive grains preferably have a primary particle size of 0.03
to 0.6 .mu.m, particularly 0.05 to 0.3 .mu.m. The abrasive grains
are preferably added in an amount of 2 to 15 parts by weight,
particularly 5 to 10 parts by weight, per 100 parts by weight of
the magnetic powder.
[0045] The carbon black functions as an antistatic agent, a solid
lubricant, and the like.
[0046] While the kind of the carbon black to be used is not
particularly limited, it is preferred to use carbon black having a
primary particle size of 15 to 80 nm, a BET specific surface area
of 10 to 80 m.sup.2/g, and a DBP oil absorption of 100 to 300
cm.sup.3/100 g because such carbon black makes the surface profile
of the backcoating layer 5 satisfactory. To assure the satisfactory
surface profile of the backcoating layer 5, the carbon black is
preferably added in an amount of 2 to 50 parts by weight,
particularly 2 to 10 parts by weight, per 100 parts by weight of
the magnetic powder.
[0047] The lubricants which can be generally used include fatty
acids and fatty acid esters. Examples of the fatty acids are
caproic acid, caprylic acid, capric acid, lauric acid, myristic
acid, palmitic acid, stearic acid, isostearic acid, linolenic acid,
oleic acid, elaidic acid, behenic acid, malonic acid, succinic
acid, maleic acid, glutaric acid, adipic acid, pimelic acid,
azelaic acid, sebacic acid, 1,12-dodecanedicarboxylic acid, and
octanedicarboxylic acid.
[0048] Examples of the fatty acid esters are alkyl esters of the
above-enumerated fatty acids, with those having 12 to 36 carbon
atoms in total being preferred.
[0049] These lubricants are preferably added in an amount of 0.5 to
20 parts by weight, particularly 1 to 10 parts by weight,
especially 2 to 8 parts by weight, per 100 parts by weight of the
magnetic powder.
[0050] The hardeners which are generally used include isocyanate
hardeners, exemplified by "Coronate L" (a trade name, produced by
Nippon Polyurethane Industry Co., Ltd.) and amine hardeners. The
hardeners are preferably added in an amount of 1 to 20 parts by
weight, particularly 3 to 10 parts by weight, per 100 parts by
weight of the magnetic powder.
[0051] The backcoating layer 5 is formed by coating the substrate 2
with a backcoating composition having the above-mentioned
components dispersed in a solvent. Examples of the solvent include
ketone solvents, ester solvents, ether solvents, aromatic
hydrocarbon solvents, and chlorinated hydrocarbon solvents. The
solvent is preferably used in an amount of 400 to 2000 parts by
weight, particularly 500 to 1500 parts by weight, per 100 parts by
weight of the binder.
[0052] The thickness of the backcoating layer 5, formed by applying
the above-described backcoating composition, is preferably 0.1 to 2
.mu.m, particularly 0.2 to 1.5 .mu.m, especially 0.2 to 1.0 .mu.m,
taking into consideration the thickness balance with the magnetic
layer 4 and the intermediate layer 3.
[0053] With regard to the surface roughness of the backcoating
layer, it is preferred for the backcoating layer to have an
arithmetic mean roughness Ra of 8 to 30 nm, particularly 10 to 20
nm, and a 10 point mean roughness Rz of 40 to 200 nm, particularly
80 to 150 nm, so as to prevent transfer of the surface profile of
the backcoating layer onto the magnetic layer while the magnetic
tape 1 is wound and to stabilize the running of the magnetic tape
1. The Ra and Rz of the backcoating layer 5 can be adjusted within
these preferred ranges by, for example, incorporating carbon black
having the aforementioned physical properties into the backcoating
layer 5 in the aforementioned amount.
[0054] The arithmetic mean roughness Ra is defined by equation (1)
shown below, and the 10 point mean roughness Rz is in accordance
with the definition of JIS-B0601-1994. Both parameters can be
measured with Laser Interferometric Microscope Maxim 3D Model 5700
manufactured by Zygo under the following conditions.
1 Filter: Fixed Remove: Cylinder Filter freg: 4.0 (1/mm) Filter
wavelength: 0.250 (mm) Trim: 0 Trim move: All Lens: Fizeau x40
[0055] In measuring the surface roughness, a sample piece is stuck
to a slide glass for microscopes which satisfies the requirements
specified in JIS-R-3502 (while, in the present invention, a slide
glass produced by Matsunami Glass K. K. was used, usable slide
glass is not limited thereto) with water or ethanol. Existence of
excessive water or ethanol will ruin the reproducibility of
measurements. Therefore, the results obtained after the water or
ethanol evaporates to some extent and while an interference fringe
can be seen from the back of the slide glass are taken as Ra and
Rz. 1 Ra = 1 l 0 I y ( x ) x ( 1 )
[0056] wherein Y represents profile data; and l represents an
assessment length.
[0057] A method of recording servo signals on the backcoating layer
will then be described by referring to FIG. 5. FIG. 5 schematically
illustrates the equipment for recording servo signals on the
backcoating layer of magnetic tape.
[0058] The equipment 30 shown in FIG. 5 has a feed reel 31, a
takeup reel 32, and a servo signal recording apparatus 33. The
servo signal recording apparatus 33 has a servo signal recording
head 34.
[0059] The feed reel 31 has a magnetic tape 1, obtained by slitting
a magnetic tape stock, wound therearound. The magnetic tape 1 is
fed at a predetermined speed. At this time, magnetic recording has
not been made on the backcoating layer of the magnetic tape 1. The
fed magnetic tape 1 is led in the servo signal recording apparatus
33, where servo signals are recorded on the backcoating layer 5 by
means of the servo signal recording head 34 set therein. While FIG.
5 shows only one servo signal recording head 34 for the sake of
simplicity, there are actually the same number of recording heads
34 as the number of the servo tracks to be formed on the
backcoating layer 5, arranged in the width direction of the
magnetic tape 1. In this way prescribed servo signals are recorded
on the portions of the backcoating layer 5 in contact with each
recording head 34, whereby servo tracks having the recorded servo
signals are formed in parallel with the longitudinal direction
(i.e., running direction) of the magnetic tape 1 over the whole
length of the magnetic tape 1. Finally, the magnetic tape 1 having
the servo signals recorded is wound around the takeup reel 32.
While not shown, it is preferable that a means for regulating
either edge of the running magnetic tape 1 is provided at any
position of the magnetic tape running system in the apparatus 33 so
that fluctuation of the running tape in the width direction may be
prevented thereby to keep the distance from that edge to each servo
track constant.
[0060] The following is the description on general particulars
concerning the magnetic tape according to the present
invention.
[0061] The magnetic layer 4 of the magnetic tape 1 shown in FIG. 1
is formed by applying a magnetic coating composition comprising
ferromagnetic powder and a binder. Namely, the magnetic tape 1 is
particulate magnetic tape.
[0062] The ferromagnetic powder which can be used include acicular
or spindle-shaped ferromagnetic powder and tabular ferromagnetic
powder. Acicular or spindle-shaped ferromagnetic powder includes
ferromagnetic metal powder mainly comprising iron and ferromagnetic
iron oxide powder, and tabular ferromagnetic powder includes
ferromagnetic hexagonal ferrite powder. Where, in particular, the
backcoating layer 5 contains the above-described ferromagnetic
hexagonal ferrite powder, it is preferable to use ferromagnetic
powder having a high saturation magnetization in the magnetic
layer. Specifically, it is preferred to use acicular or
spindle-shaped ferromagnetic metal powder or ferromagnetic iron
oxide powder.
[0063] The ferromagnetic metal powder includes powder having a
metal content of 50% by weight or more, 60% by weight or more of
the metal content being Fe. Specific examples of such ferromagnetic
metal powders include Fe--Co, Fe--Ni, Fe--Al, Fe--Ni--Al,
Fe--Co--Ni, Fe--Ni--Al--Zn, and Fe--Al--Si. The ferromagnetic iron
oxide powder includes .gamma.-Fe.sub.2O.sub.3, Co-doped
.gamma.-Fe.sub.2O.sub.3, and Co-doped FeO.sub.x
(4/3.ltoreq.x<1.5). The acicular or spindle-shaped ferromagnetic
powder preferably has a major axis length of 0.05 to 0.2 .mu.m,
particularly 0.05 to 0.16 .mu.m, with an acicular ratio (major axis
length/minor axis length) of 3 to 15, particularly 3 to 10. In
using the tabular ferromagnetic hexagonal ferrite powder, the
tabular diameter is preferably 0.1 .mu.m or smaller. In order that
the above-mentioned relationships between the backcoating layer 5
and the whole of all the layers on the magnetic layer side in terms
of coercive force and saturation flux density are easily satisfied,
it is preferred for the acicular or spindle-shaped ferromagnetic
powder to have such a coercive force and a saturation magnetization
as fall within the following respective ranges. That is, the
acicular or spindle-shaped ferromagnetic powder preferably has a
coercive force (Hc) of 100 to 400 kA/m, particularly 150 to 350
kA/m, and a saturation magnetization (as) of 100 to 200
Am.sup.2/kg, particularly 120 to 170 Am.sup.2/kg. Further, the BET
specific surface area of the acicular or spindle-shaped
ferromagnetic powder is preferably 30 to 70 m.sup.2/g, particularly
40 to 70 m.sup.2/g.
[0064] If desired, the ferromagnetic powder can contain rare earth
elements or transition metal elements. The ferromagnetic powder can
be subjected to a surface treatment to improve dispersibility and
the like. The surface treatment can be performed by a method
similar to the method described in T. J. Wiseman et al.,
Characterization of Powder Surfaces, Academic Press (1976), for
example, a method comprising coating the surface of the
ferromagnetic particles with an inorganic oxide. Inorganic oxides
which can be used in this surface treatment include
Al.sub.2O.sub.3, SiO.sub.2, TiO.sub.2, ZrO.sub.2, SnO.sub.2,
Sb.sub.2O.sub.3, and ZnO. These inorganic oxides can be used either
individually or as a mixture of two or more thereof. The surface
treatment can also be carried out by an organic treatment, such as
a silane coupling treatment, a titanium coupling treatment or an
aluminum coupling treatment.
[0065] The binder to be used can be of those illustrated for the
formation of the backcoating layer 5. While the details of the
binder are not described here, the explanations given in relation
to the backcoating layer 5 apply appropriately. The binder is
preferably used in an amount of 10 to 40 parts by weight,
particularly 15 to 25 parts by weight, per 100 parts by weight of
the ferromagnetic powder.
[0066] The magnetic layer 4 can further contain abrasive grains,
carbon black, lubricants, hardeners, etc. in addition to the
aforementioned components. These components can be of those which
can be used in the backcoating layer 5. While the details of these
components are not described here, the explanations given with
respect to the backcoating layer 5 apply appropriately. Preferred
amounts of these components to be added are shown below, given in
terms of parts by weight per 100 parts by weight of the
ferromagnetic powder.
2 Abrasive grains: 2 to 20 parts by weight, particularly 5 to 15
parts by weight Carbon black: 0.1 to 10 parts by weight,
particularly 0.1 to 5 parts by weight Lubricant: 0.5 to 10 parts by
weight, particularly 0.5 to 5 parts by weight Hardener: 1 to 6
parts by weight, particularly 2 to 5 parts by weight
[0067] If desired, the magnetic layer 4 can contain various
additives customarily used in magnetic tape, such as dispersants,
rust inhibitors, and antifungals, in addition to the
above-described components.
[0068] The magnetic layer 4 is formed by applying a magnetic
coating composition having the aforesaid components dispersed in a
solvent on an intermediate layer 3. The solvent can be of those
useful in the backcoating composition. The solvent is preferably
used in an amount of 80 to 500 parts by weight, particularly 100 to
350 parts by weight, per 100 parts by weight of the ferromagnetic
powder present in the magnetic coating composition.
[0069] The magnetic coating composition is prepared by, for
example, preliminarily mixing the ferromagnetic powder and the
binder together with a portion of the solvent in a Naughter mixer,
etc., kneading the premixture in a continuous pressure kneader, a
twin-screw kneading machine, etc., diluting the mixture with
another portion of the solvent, followed by dispersing in a sand
mill, etc., adding to the dispersion additives, such as a
lubricant, filtering the dispersion, and adding thereto the
remainder of the solvent and a hardener.
[0070] For obtaining an improved S/N ratio and for preventing
self-demagnetization, the thickness of the magnetic layer 4 is
preferably 0.1 to 3 .mu.m, still preferably 0.1 to 2 .mu.m.
[0071] In order that the above-mentioned relationships between the
backcoating layer 5 and the whole of all the layers on the magnetic
layer side in terms of coercive force and saturation flux density
be easily satisfied, it is preferred for the magnetic layer 4 to
have such a coercive force and a saturation flux density as fall
within the following respective ranges. That is, the magnetic layer
4 preferably has a coercive force (Hc) of 80 to 350 kA/m,
particularly 100 to 250 kA/m, and a saturation flux density (Bs) of
100 to 400 mT, particularly 120 to 300 mT.
[0072] The intermediate layer 3 is explained below.
[0073] The intermediate layer 3 may be either a layer having
magnetism or a nonmagnetic layer. Where the intermediate layer 3 is
a layer having magnetism, it is a magnetic layer containing
magnetic powder, which is formed by using a magnetic coating
composition mainly comprising magnetic powder, nonmagnetic powder,
a binder, and a solvent. Where, on the other hand, the intermediate
layer 3 is a nonmagnetic layer, the intermediate layer 5 is formed
by using a nonmagnetic coating composition mainly comprising
nonmagnetic powder, a binder, and a solvent. These coating
compositions will be inclusively referred to as an intermediate
layer coating composition.
[0074] The magnetic powder to be used is preferably ferromagnetic
powder. Either of hard magnetic powder and soft magnetic powder can
be used preferably.
[0075] The hard magnetic powder includes the ferromagnetic
hexagonal ferrite powder, ferromagnetic metal powder and
ferromagnetic iron oxide powder which can be used in the magnetic
layer 4. Of these powders, ferromagnetic hexagonal ferrite powder,
particularly ferromagnetic hexagonal ferrite powder having a
tabular diameter of 0.1 .mu.m or smaller, is especially preferred.
The details of these ferromagnetic powders, while not described
here, are the same as the ferromagnetic powders used in the
magnetic layer 4, and the explanations given thereto apply
appropriately.
[0076] While the soft magnetic powder to be used is not
particularly limited, magnetic powder generally used in what we
call low-current devices, such as a magnetic head and an electron
circuit, are preferred. For example, the soft magnetic materials
described in Chikazumi Toshinobu, "Kyojiseitai no Buturi (2nd Vol.)
Jikitokusei to Ohyo", pp. 368-376, Shokabo (1984) can be used.
Specifically, soft magnetic oxide powder and soft magnetic metal
powder can be used.
[0077] Spinel type ferrite powder is preferably used as the soft
magnetic oxide powder. The spinel type ferrite powder includes
MnFe.sub.2O.sub.4, Fe.sub.3O.sub.4, CoFe.sub.2O.sub.4,
NiFe.sub.2O.sub.4, MgFe.sub.2O.sub.4, Li.sub.0.5Fe.sub.0.4, Mn--Zn
type ferrite, Ni--Zn type ferrite, Ni--Cu type ferrite, Cu--Zn type
ferrite, Mg--Zn type ferrite, Li--Zn type ferrite, Zn type ferrite,
and Mn type ferrite. These soft magnetic oxide powders may be used
either individually or as a combination of two or more thereof.
[0078] The soft magnetic metal powder includes Fe--Si alloys,
Fe--Al alloys (e.g., Alperm, Alfenol and Alfer), Permalloy (e.g.,
Ni--Fe binary alloys or multinary alloys composed of the Ni--Fe
binary system and Mo, Cu, Cr, etc.), Sendust (Fe--Si(9.6 wt
%)-Al(5.4 wt %), and Fe--Co alloys. These soft magnetic metal
powders may be used either individually or as a combination of two
or more thereof.
[0079] The soft magnetic oxide powder usually has a coercive force
of 8 to 12000 A/m and a saturation magnetization of 30 to 90
Am.sup.2/kg. The soft magnetic metal powder usually has a coercive
force of 1.6 to 8000 A/m and a saturation magnetization of 5 to 500
Am.sup.2/kg.
[0080] While not limiting, the shape of the soft magnetic powders
include a spherical shape, a tabular shape, and an acicular shape.
The size of the particles is preferably 5 to 800 nm.
[0081] If desired, the above-described magnetic powder can contain
rare earth elements or transition metal elements similarly to the
ferromagnetic powder contained in the magnetic layer 4. Further,
the same surface treatment as could be given to the ferromagnetic
metal powder may be effected.
[0082] The aforementioned nonmagnetic powder is explained. The
nonmagnetic powder includes particles of nonmagnetic iron oxide
(red oxide), barium sulfate, zinc sulfide, magnesium carbonate,
calcium carbonate, calcium oxide, zinc oxide, magnesium oxide,
magnesium dioxide, tungsten disulfide, molybdenum disulfide, boron
nitride, tin dioxide, silicon carbide, cerium oxide, corundum,
artificial diamond, garnet, siliceous stone, silicon nitride,
molybdenum carbide, boron carbide, tungsten carbide, titanium
carbide, diatomaceous earth, dolomite, and resins. Preferred of
them are nonmagnetic iron oxide (red oxide), titanium oxide, and
boron nitride. These nonmagnetic powders can be used either
individually or as a combination of two or more thereof. The
nonmagnetic particles may have any of a spherical shape, a tabular
shape, and an acicular shape or may be amorphous. Spherical,
tabular, and amorphous particles preferably have a particle size of
5 to 200 nm, and acicular particles preferably have a major axis
length of 20 to 300 nm with an acicular ratio of 3 to 20. Where the
nonmagnetic powder is used in combination with the magnetic powder
(i.e., where the intermediate layer 3 is a magnetic layer), the
nonmagnetic powder is preferably used in an amount of 30 to 70
parts by weight, particularly 40 to 60 parts by weight, per 100
parts by weight of the magnetic powder. Where, on the other hand,
the magnetic powder is not used (i.e., where the intermediate layer
3 is a nonmagnetic layer), the amounts of the other components are
decided based on 100 parts by weight of the nonmagnetic powder. If
necessary, the above-mentioned various nonmagnetic powders can be
subjected to the same surface treatment as could be done for the
magnetic powder.
[0083] The intermediate layer 3, either magnetic or nonmagnetic,
can contain a binder in addition to the above-mentioned components
and may further contain abrasive grains, lubricants, carbon black,
hardeners, and the like. While not described specifically, these
components are the same as those described with reference to the
backcoating layer 5 and magnetic layer 4. Preferred amounts of
these components are shown below, given in terms of parts by weight
per 100 parts by weight of the total amount of the magnetic powder
and the nonmagnetic powder (where the intermediate layer 3 is a
magnetic layer) or 100 parts by weight of the nonmagnetic powder
(where the intermediate layer 3 is a nonmagnetic layer).
3 Binder: 16 to 40 parts by weight, particularly 20 to 28 parts by
weight Abrasive grains: 6 to 30 parts by weight, particularly 8 to
12 parts by weight Lubricant: 2 to 20 parts by weight, particularly
5 to 7 parts by weight Carbon black: 5 to 30 parts by weight,
particularly 12 to 20 parts by weight Hardener: 2 to 12 parts,
particularly 4 to 8 parts by weight
[0084] If desired, the intermediate layer 3 can contain various
additives as could be added to the magnetic layer 4.
[0085] The intermediate layer 3 is formed by coating the substrate
2 with an intermediate layer coating composition containing the
aforementioned various components and a solvent. The solvent may be
of those used in the backcoating composition and the magnetic
coating composition. The amount of the solvent to be used is
preferably 100 to 700 parts by weight, particularly 300 to 500
parts by weight, per 100 parts by weight of the total of the
magnetic powder and the nonmagnetic powder (where the intermediate
layer 3 is a magnetic layer) or 100 parts by weight of the
nonmagnetic powder (where the intermediate layer 3 is a nonmagnetic
layer).
[0086] The intermediate layer 3 should have some thickness to
control the capacity of holding lubricants which is influential on
the durability of the magnetic tape 1, but too large a thickness is
liable to cause crack initiation when deflected. Accordingly, a
suitable thickness is 0.5 to 10 .mu.m, particularly 0.1 to 3
.mu.m.
[0087] Where the intermediate layer 3 is a layer having magnetism,
its coercive force and saturation flux density preferably fall
within the following respective ranges so that the above-mentioned
relationships between the backcoating layer 5 and all the layers on
the magnetic layer side in terms of coercive force and saturation
flux density may be fulfilled with ease. That is, it is preferred
for the intermediate layer 3 to have a coercive force (Hc) of 90 to
400 kA/m, particularly 120 to 300 kA/m, and a saturation flux
density (Bs) of 30 to 350 mT, particularly 50 to 200 mT.
[0088] Materials constituting the substrate 2 are nonmagnetic
materials including polymers, such as polyesters, such as
polyethylene terephthalate, polybutylene terephthalate,
polyethylene naphthalate, polycyclohexylene dimethylene
terephthalate, and polyethylene bisphenoxycarboxylate; polyolefins,
such as polyethylene and polypropylene; cellulose derivatives, such
as cellulose acetate butyrate and cellulose acetate propionate;
vinyl resins, such as polyvinyl chloride and polyvinylidene
chloride; polyamide; polyimide; polycarbonate; polysulfone;
polyether ether ketone; and polyurethane. These materials can be
used individually or in combination of two or more thereof. If
necessary, the substrate made of these materials can be subjected
to uniaxial or biaxial stretching, a corona discharge treatment, a
treatment for improving adhesion, and the like.
[0089] The thickness of the substrate 2 is not particularly
limited. It is preferably 2 to 100 .mu.m, still preferably 2 to 76
.mu.m.
[0090] The outline of a preferred process for producing the
magnetic tape 1 shown in FIG. 1 is described below.
[0091] A magnetic coating composition for forming the magnetic
layer 4 and an intermediate layer coating composition for forming
the intermediate layer 3 are applied simultaneously to the
substrate 2 in a wet-on-wet coating system to form coating layers
corresponding to the magnetic layer 4 and the intermediate layer 3.
That is, the magnetic layer 4 is preferably provided while the
intermediate layer 3 is wet.
[0092] The coating layers are then subjected to magnetic field
orientation, dried, and wound. Thereafter, the coated material is
calendered, and a backcoating layer is formed. Alternatively,
formation of the intermediate layer 3 and the magnetic layer 4 may
be preceded by formation of the backcoating layer 5. The coated
material is aged at 40 to 80.degree. C. for 6 to 100 hours and then
slit to a prescribed width. Servo signals are magnetically recorded
on the backcoating layer 5 in accordance with the aforementioned
method to obtain the magnetic tape 1.
[0093] The simultaneous coating technique in a wet-on-wet coating
system is described in Japanese Patent Laid-Open No. 73883/93,
column 42, line 31 to column 43, line 31. This is a technique in
which a magnetic coating composition is applied before an
intermediate layer coating composition dries. This technique being
followed, there is obtained magnetic tape which causes few dropouts
and can cope with high-density recording, and the coating layers of
the resulting magnetic tape have excellent durability.
[0094] The magnetic field orientation treatment is carried out
before each coating composition dries. The treatment can be
performed by applying a magnetic field of about 40 kA/m or higher,
preferably about 80 to 800 kA/m, in parallel with the side coated
with the magnetic coating composition or passing the coated
material through a solenoid type magnet of about 80 to 800 kA/m
while the magnetic coating composition is wet. By the magnetic
field orientation treatment under such conditions, the
ferromagnetic powder in the magnetic layer 4 are orientated in the
longitudinal direction of the magnetic tape 1. For the purpose of
inhibiting the thus orientated ferromagnetic powder from changing
its orientation during the subsequent drying step, it is a
preferred manipulation to apply warm air of 30 to 50.degree. C.
from above the magnetic layer 4 immediately before the magnetic
field orientation treatment, whereby the coated material is dried
preliminarily to have a controlled residual solvent content in each
layer.
[0095] The drying of the coating layers is carried out by, for
example, supplying gas heated to 30 to 120.degree. C. The degree of
drying can be controlled by adjusting the temperature and the feed
rate of the gas.
[0096] The calendering is carried out by, for example,
supercalendering comprising passing the coated film between two
rolls, such as a combination of a metal roll and a cotton roll or a
synthetic resin roll, or a pair of metal rolls. The calendering
conditions are preferably, for example, 60 to 140.degree. C. in
temperature and 100 to 500 kg/cm in linear pressure.
[0097] In the production of the magnetic tape 1, the surface of the
magnetic layer 4 can be subjected to a finishing step, such as
burnishing or cleaning, according to necessity. It is possible to
apply the magnetic coating composition and the intermediate layer
coating composition by a generally known successive coating
technique.
[0098] While the magnetic tape of the present invention has been
described based on the preferred embodiments thereof, it should be
understood that the present invention is not deemed to be limited
thereto, and various changes and modifications can be made therein
without departing from the spirit and scope of the present
invention.
[0099] For example, the signals shown in FIG. 4 may be replaced
with other servo signals to be recorded on the servo tracks.
[0100] Further, the magnetic tape 1 shown in FIG. 1 may have a
primer layer between the substrate 2 and the intermediate layer 3
or the backcoating layer 5.
[0101] Furthermore, while the aforementioned embodiments are
particulate magnetic tapes, the same effects would be exerted on
magnetic tapes of metallizing.
[0102] The present invention has been described and will be better
understood from the following Examples. However, the Examples are
given for illustrative purposes only, and the present invention is
not deemed to be limited thereto unless otherwise noted. Unless
otherwise specified, all the parts and percents are by weight.
EXAMPLE 1
[0103] The following components except the hardener were kneaded in
a kneader, dispersed in a stirrer, and further finely dispersed in
a sand mill. The dispersion was filtered through a 1 .mu.m filter,
and finally, the hardener was added thereto to prepare a
backcoating composition, a magnetic coating composition, and an
intermediate layer coating composition having the respective
formulations described below.
4 Formulation of Backcoating Composition: Magnetic powder A (see
Tables 1 and 2 as to kind and amount) Sulfoxyl-containing vinyl
chloride copolymer (binder) 20 parts Sulfoxyl-containing
polyurethane resin (binder) 20 parts Alumina (abrasive; primary
particle size: 0.18 .mu.m) 10 parts Carbon black 5 parts (primary
particle size: 54 nm; BET specific surface area: 32 m.sup.2/g; DBP
oil absorption: 180 cm.sup.3/100 g) Stearic acid (lubricant) 1 part
Butylstearate (lubricant) 3 parts Methyl ethyl ketone (solvent) 100
parts Toluene (solvent) 100 parts Cyclohexanone (solvent) 100
parts
[0104]
5 Formulation of Magnetic Coating Composition: Ferromagnetic powder
a (see Tables 1 and 2 as to kind and amount) Alumina (abrasive;
primary particle size: 0.15 .mu.m) 8 parts Carbon black
(antistatic; primary particle size: 0.018 .mu.m) 0.5 part Vinyl
chloride copolymer 10 parts (binder; average degree of
polymerization: 280; epoxy group content: 1.2 wt %; sulfoxyl group
content: 8 .times. 10.sup.-5 equiv./g) Polyurethane resin 7 parts
(binder; number average molecular weight: 25000; sulfoxyl group
content: 1.2 .times. 10.sup.-4 equiv./g; glass transition point:
45.degree. C.) Stearic acid (lubricant) 1.5 parts 2-Ethylhexyl
oleate (lubricant) 2 parts Polyisocyanate (hardener) 5 parts
(Coronate L (trade name, produced by Nippon Polyurethane Industry
Co., Ltd.)) Methyl ethyl ketone 120 parts Toluene 80 parts
Cyclohexanone 40 parts
[0105]
6 Formulation of Intermediate Layer Coating Composition:
Nonmagnetic powder i (see Tables 1 and 2 as for kind and amount)
Magnetic powder I (see Tables 1 and 2 as for kind and amount)
Alumina (abrasive; primary particle size: 0.15 .mu.m) 3 parts Vinyl
chloride copolymer 12 parts (binder; average degree of
polymerization: 280; epoxy group content: 1.2 wt %; sulfoxyl group
content: 8 .times. 10.sup.-5 equiv./g) Polyurethane resin 8 parts
(binder; number average molecular weight: 25000; sulfoxyl group
content: 1.2 .times. 10.sup.-4 equiv./g; glass transition point:
45.degree. C.) Stearic acid (lubricant) 1 part 2-Ethylhexyl oleate
(lubricant) 4 parts Polyisocyanate (hardener) 4 parts (Coronate L
(trade name, produced by Nippon Polyurethane Industry Co., Ltd.))
Methyl ethyl ketone 90 parts Toluene 60 parts Cyclohexanone 30
parts
[0106] The intermediate layer coating composition and the magnetic
coating composition were applied simultaneously onto a 4.5 .mu.m
thick polyethylene naphthalate film by means of a die coater to
form the respective coating layers having a dry thickness of 1.5
.mu.m and 0.2 .mu.m, respectively. The coated film was passed
through a solenoid type magnet of 400 kA/m while wet and dried in a
drying oven by applying hot air of 80.degree. C. at a rate of 10
m/min. After the drying, the coated film was calendered to form an
intermediate layer and a magnetic layer. Subsequently, the reverse
side of the substrate was coated with the backcoating composition
and dried at 90.degree. C. to form a backcoating layer having a
thickness of 0.5 .mu.m. The resulting magnetic tape stock was slit
into 12.7 mm wide tape.
[0107] Servo signals were recorded on the backcoating layer of the
magnetic tape over the whole length by use of the equipment shown
in FIG. 5. The number of tracks was 30. The width of each track was
30 .mu.m. There was thus obtained a magnetic tape having servo
signals recorded on its backcoating layer.
EXAMPLES 2 TO 5 AND COMPARATIVE EXAMPLES 1 TO 3
[0108] A magnetic tape having servo signals recorded on its
backcoating layer was obtained in the same manner as in Example 1,
except for changing the kinds and amounts of the magnetic powder
used in the backcoating composition, the ferromagnetic powder in
the magnetic coating composition, and the magnetic powder and the
nonmagnetic powder in the intermediate layer coating composition as
shown in Tables 1 and 2.
[0109] The coercive force and saturation flux density of the
backcoating layer, the magnetic layer, and the intermediate layer
of the magnetic tapes obtained in Examples and Comparative Examples
were measured. The coercive force and saturation flux density of
the whole of the magnetic layer and the intermediate layer were
also measured. The results obtained are shown in Table 2.
Measurement of the coercive force and saturation flux density of
each of the backcoating layer, magnetic layer and intermediate
layer was carried out on each layer separated by adhesive tape.
Measurement on the whole of the magnetic layer and the intermediate
layer was made on the magnetic tape from which only the backcoating
layer had been removed by using magnetic tape.
[0110] To evaluate the performance of the magnetic tapes obtained
in Examples and Comparative Examples, the reproduction output of
the magnetic tape and the arithmetic mean roughness Ra, 10 point
mean roughness Rz, coefficient of dynamic friction, and surface
resistivity of the backcoating layer were measured. Further, a
tracking test was conducted after the magnetic tape was stored for
3 months in a wound state. The results obtained are shown in Table
2. Of these measurements, the measurements of the arithmetic mean
roughness Ra and 10 point mean roughness Rz of the backcoating
layer were made in accordance with the above-described methods, and
the other measurements were made as follows.
[0111] Reproduction Output:
[0112] Signals having a recording wavelength of 0.6 .mu.m were
recorded in accordance with a head tester method. The reproduction
output was measured and expressed relatively taking Comparative
Example 1 as a standard (0 dB).
[0113] Coefficient of Dynamic Friction:
[0114] A tension (T2) required for making a magnetic tape run at a
speed of 14.3 mm/sec in contact with a stainless pole under a
tension of 10 g (T1) was measured. The coefficient of dynamic
friction (.mu.) of the magnetic tape was calculated from the
measured value according to the following formula:
.mu.=(1/.pi.)1n(T2/T1)
[0115] Surface Resistivity:
[0116] Two electrodes having a radius of 10 mm, plated with 24 K
gold, and finished to have a roughness of N4 (ISO 1302), were
horizontally placed in parallel on the magnetic layer at a
center-to-center distance d of 12.7 mm. A direct current voltage of
100.+-.10 V was applied to the electrodes while imposing a force of
0.25 N to both ends of the magnetic tape. The current between the
electrodes was measured, from which the surface resistivity was
obtained.
[0117] Tracking Test:
[0118] Tracking was actually conducted by utilizing the servo
signals recorded on the backcoating layer. Variations in output of
the signals recorded on the magnetic layer and positional
variations of the tape in its width direction were measured to
evaluate the tracking performance.
7TABLE 1 Backcoating Layer Magnetic Layer Intermediate Layer
Magnetic Powder Ferromagnetic Powder Nonmagnetic Powder Magnetic
Powder A Tabular hexagonal barium ferrite a Acicular ferromagnetic
metal i .alpha.-Fe.sub.2O.sub.3 I Tabular hexagonal barium ferrite
Tabular diameter: 0.05 .mu.m powder mainly comprising iron Major
axis: 0.12 .mu.m Tabular diameter: 0.05 .mu.m Aspect ratio: 5 Major
axis: 0.07 .mu.m Acicular ratio: 10 Aspect ratio: 5 Coercive force:
200 kA/m Acicular ratio: 6 BET specific surface area: Coercive
force: 200 kA/m Saturation magnetization: Coercive force: 160 kA/m
48 m.sup.2/g Saturation magnetization: 50 Am.sup.2/kg Saturation
magnetization: 50 Am.sup.2/kg BET specific surface area: 142
Am.sup.2/kg BET specific surface area: 50 m.sup.2/g BET specific
surface area: 50 m.sup.2/g 56 m.sup.2/g B Acicular ferromagnetic
metal b Tabular hexagonal barium ferrite ii TiO.sub.2 (acicular) II
Acicular ferromagnetic metal powder mainly comprising iron Tabular
diameter: 0.05 .mu.m Major axis: 0.25 .mu.m powder mainly
comprising iron Major axis: 0.07 .mu.m Aspect ratio: 5 Acicular
ratio: 5 Major axis: 0.07 .mu.m Acicular ratio: 6 Coercive force:
200 kA/m BET specific surface area: Acicular ratio: 6 Coercive
force: 160 kA/m Saturation magnetization: 30 m.sup.2/g Coercive
force: 160 kA/m Saturation magnetization: 50 Am.sup.2/kg Saturation
magnetization: 142 Am.sup.2/kg BET specific surface area: 142
Am.sup.2/kg BET specific surface area: 50 m.sup.2/g BET specific
surface area: 56 m.sup.2/g 56 m.sup.2/g C Co-.gamma.-iron oxide c
Co-.gamma.-iron oxide iii TiO.sub.2 (spherical) III Co-y-iron oxide
Major axis: 0.15 .mu.m Major axis: 0.15 .mu.m Particle size: 0.05
.mu.m Major axis: 0.15 .mu.m Acicular ratio: 8 Acicular ratio: 8
BET specific surface area: Acicular ratio: 8 Coercive force: 120
kA/m Coercive force: 120 kA/m 40 m.sup.2/g Coercive force: 120 kA/m
Saturation magnetization: Saturation magnetization: Saturation
magnetization: 100 Am.sup.2/kg 100 Am.sup.2/kg 100 Am.sup.2/kg BET
specific surface area: BET specific surface area: BET specific
surface area: 30 m.sup.2/g 30 m.sup.2/g 30 m.sup.2/g
[0119]
8 TABLE 2 Backcoating Layer Magnetic Layer Reproduction Coercive
Saturation Dynamic Surface Magnetic Coercive Saturation
Ferro-magnetic Output Force Flux Density Ra Rz Friction Resistivity
Powder Force Flux Density Powder (dB)* (kA/m) (mT) (nm) (nm)
Coefficient (.OMEGA./.quadrature.) Kind part (kA/m) (mT) Kind Part
Ex. 1 +1.1 135 50 15 89 0.23 3.5 .times. 10.sup.9 A 100 120 250 a
100 Ex. 2 +0.8 150 80 13 93 0.21 4.3 .times. 10.sup.10 B 100 138
233 b 100 Ex. 3 +1.2 148 75 16 100 0.18 7.8 .times. 10.sup.10 C 100
128 195 c 100 Ex. 4 +0.9 115 45 12 108 0.22 4.0 .times. 10.sup.8 A
75 105 210 a 100 Ex. 5 +1.4 149 60 15 98 0.25 9.3 .times. 10.sup.9
A 120 128 180 a 100 Comp. 0 85 75 18 93 0.23 4.0 .times. 10.sup.9 A
50 120 250 a 100 Ex. 1 Comp. -3.1 150 280 16 108 0.18 3.8 .times.
10.sup.10 B 120 120 250 a 100 Ex. 2 Comp. -3.5 85 275 13 110 0.20
9.8 .times. 10.sup.10 A 150 120 250 a 100 Ex. 3 Whole on Magnetic
Intermediate Layer Layer Side Coercive Saturation Magnetic
Non-Magnetic Coercive Saturation Force Flux Density Powder Powder
Force Flux Density Tracking (kA/m) (mT) Kind Part Kind Part (kA/m)
(mT) Test Ex. 1 105 105 I 50 i 100 120 250 OK Ex. 2 120 75 II 50 ii
100 140 180 OK Ex. 3 133 50 III 50 iii 100 110 200 OK Ex. 4 105 45
I 50 i 100 100 195 OK Ex. 5 112 68 I 50 i 100 120 173 OK Comp. 105
105 I 50 i 100 120 230 NG Ex. 1 Comp. 105 105 I 50 ii 100 120 230
NG Ex. 2 Comp. 105 105 I 50 iii 100 120 230 NG Ex. 3 *Comparative
Example 1 was taken as a standard (0 dB)
[0120] As is apparent from Table 1 and the results shown in Table
2, it is seen that the magnetic tapes of Examples (samples
according to the present invention) enable reliable servo tracking
without suffering from impairment of the function essential to the
backcoating layer. To the contrary, because the comparative
magnetic tapes suffered magnetic transfer, they had reduced
reproduction outputs and failed in servo tracking.
[0121] Industrial Applicability:
[0122] As described in detail, the present invention provides
magnetic tape which is capable of servo tracking without reducing
the data area.
[0123] The present invention provides magnetic tape which is
capable of servo tracking without suffering impairment of the
function essential to the backcoating layer.
[0124] The present invention provides magnetic tape having an
improved track density.
[0125] The present invention provides magnetic tape having a high
recording capacity.
[0126] It is apparent from the above teachings that various
modifications can be made in the present. Accordingly, it should be
understood that the invention can be practiced otherwise than as
specifically described within the scope of what is claimed attached
hereto.
* * * * *