U.S. patent application number 09/540037 was filed with the patent office on 2002-01-03 for glass melting apparatus and method.
Invention is credited to Chenoweth, Vaughn Charles.
Application Number | 20020000101 09/540037 |
Document ID | / |
Family ID | 26992877 |
Filed Date | 2002-01-03 |
United States Patent
Application |
20020000101 |
Kind Code |
A1 |
Chenoweth, Vaughn Charles |
January 3, 2002 |
Glass melting apparatus and method
Abstract
A system for melting and delivering glass to a work area such as
spinners for making fiberglass includes a melter with heaters so
arranged that the "hot spot" in the molten glass is located away
from the walls and corrosion sensitive parts so that the various
elements of the melter wear out at substantially the same time. The
system is further provided with a dual exhaust arrangement when the
melter, conditioner and forehearth are located on the same floor of
the plant, the first exhaust being at the juncture of the melter
and conditioner, and the second being an alternating replacement
for one of the heating/cooling orifices and mechanisms in the
conditioner, so as to effectively limit the amount of corrosive
volatiles reaching the forehearth.
Inventors: |
Chenoweth, Vaughn Charles;
(Coldwater, MI) |
Correspondence
Address: |
Geoffrey R Myers Esq
Hall Priddy Myers & Vande Sande
10220 River Road
Suite 200
Potomac
MD
20854
US
|
Family ID: |
26992877 |
Appl. No.: |
09/540037 |
Filed: |
March 31, 2000 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
09540037 |
Mar 31, 2000 |
|
|
|
09342224 |
Jun 29, 1999 |
|
|
|
6044667 |
|
|
|
|
09342224 |
Jun 29, 1999 |
|
|
|
08917207 |
Aug 25, 1997 |
|
|
|
5961686 |
|
|
|
|
Current U.S.
Class: |
65/135.1 ;
65/134.1; 65/345; 65/346; 65/347 |
Current CPC
Class: |
C03B 5/0275 20130101;
Y10S 65/04 20130101; C03B 7/06 20130101; C03B 37/08 20130101; C03B
7/02 20130101; C03B 5/20 20130101; C03B 5/031 20130101 |
Class at
Publication: |
65/135.1 ;
65/134.1; 65/345; 65/346; 65/347 |
International
Class: |
C03B 005/225 |
Claims
I claim:
1. In a melter for melting glass from batch material therein in
which the batch material is floated on top of a pool of molten
glass and the batch is melted by heating means so located as to
form a finite volume of molten glass within said pool of molten
glass, which finite volume is at a temperature substantially higher
than the remainder of the molten glass within said pool, said
melter including a side wall and a bottom wall and a discharge port
located within at least one of said walls, the improvement
comprising, wherein: said heating means are so located as to create
said finite volume of substantially higher temperature at a spaced
distance from said walls and any said discharge orifice located in
said walls whereby said walls and any said discharge orifice wear
out at substantially the same time during melting of glass in the
melter.
2. The melter according to claim 1 wherein said heating means
includes a plurality of electrodes locatable within said pool of
molten glass.
3. The melter according to claim 2 wherein said heating means
further includes means for adjusting the vertical location of said
electrodes within said pool of molten glass.
4. The melter according to claim 3 wherein said heating means
further includes means for adjusting the horizontal location of
said electrodes within said pool of molten glass.
5. The melter according to claim 1 wherein said heating means
further includes means for adjusting the horizontal location of
said electrodes within said pool of molten glass.
6. The melter according to claim 1 wherein said melter is
substantially cylindrical in shape and has a vertical central axis
and further includes an open top, and wherein said heating means
includes a plurality of electrodes located so as to extend below
said batch material and into said pool of molten glass and so
arranged as to be located in an array around and proximal said
vertical central axis of said cylindrical melter.
7. The melter according to claim 6 wherein said electrodes are
arranged in a substantially horizontally circular array, with the
center of said circular array being located along the vertical
central axis of said cylindrical melter.
8. The melter according to claim 7 wherein the radius of said
cylindrical melter is about 3 times larger than the radius of said
circular array.
9. The melter according to claim 7 wherein said heating means
further includes means for adjusting the vertical and horizontal
positions of each said electrode with respect to said pool of said
molten glass.
10. The melter according to claim 1 wherein said melter includes a
water-cooled shell and a walled structure having a said side wall
joined at its base to a substantially circular said bottom wall
thereby to define a substantially cylindrical electric melter, the
walled structure having an open top so that atmosphere above the
glass batch material is not heated other than by way of heat
emitted from heated glass in said melter; wherein said at least one
discharge port is located in a said side wall of said melter, said
port permitting molten glass from within the melter to flow out of
the melter and into a conditioning area. wherein said side
discharge port includes an elongated tube comprised of a
substantially corrosion resistant metal, and having an entrance end
and an exit end thereby to define a molten glass flow communication
path between an interior of the melter and the conditioning area
and wherein said entrance end of said tube is so located as to be
spaced from said finite volume of molten glass of substantially
high temperature and proximal the remainder of said volume of
molten glass; and wherein said discharge port tube is comprised a
material which has a rate of corrosion which increases with
temperature.
11. The melter according to claim 10 wherein said melter further
includes a discharge port in said bottom wall of said melter, said
discharge port in said bottom wall is comprised of a material which
has a rate of corrosion which increases with temperature.
12. The melter according to claim 1 wherein said heating means are
so located and constructed so as to heat the molten glass within
said finite volume of highest temperature to about 3150.degree.
F.-3250.degree. F. and proximal said bottom and side walls of said
melter to about 2500.degree. F.-2700.degree. F.
13. The melter according to claims 1, 11 or 12 wherein said heating
means include a plurality of electrodes and means for adjusting
said electrodes horizontally and vertically with respect to said
walls of said melter thereby to locate said finite volume of higher
temperature molten glass at a preselected location within said
melter.
14. In the method of melting glass in a melter which includes a
bottom wall, a side wall and at least one discharge port located in
a said wall and comprised of a corrosion resistant material whose
corrosion rate increases with temperature, the steps comprising,
forming a molten pool of glass within said melter, floating batch
material on top of said molten pool, melting said batch material so
as to add further molten glass to said pool, discharging molten
glass from said melter through a said discharge port and during
said melting of said glass batch material creating within said pool
a finite volume of molten glass within said pool which is at a
significantly higher temperature than the remainder of the molten
glass within the pool, the improvement which comprises forming said
finite volume of said higher temperature molten glass at a location
sufficiently removed from said walls and said discharge port such
that said walls and discharge port wear out at substantially the
same time.
15. The method according to claim 14 which further includes the
steps of: a) operating said melter for a period of time until at
least one of said walls or discharge port requires replacement; b)
stopping said melting of said glass; c) draining said molten glass
from said melter; d) replacing said walls and said discharge port;
and, thereafter, e) melting further glass in said melter.
16. The method of claim 14 wherein the temperature of said finite
volume of said higher temperature molten glass is about
3150.degree. F.-3250.degree. F.
17. The method of claim 16 wherein the temperature at said walls
and proximal said discharge port is about 2500.degree.
F.-2700.degree. F.
18. The method of claim 14 wherein said melter further includes
electrical heating means and means for adjusting the location of
said heating means with respect to said pool of molten glass, said
method including the further step of adjusting the location of said
heating means so as to locate said finite volume of higher
temperature glass at a selected location within said pool of molten
glass.
19. The method of claim 14 wherein said melter includes at least
two discharge ports, one of said ports being located in said side
wall and the other of said ports being located in said bottom wall,
and wherein each of said ports is formed of a material which
comprises molybdenum or an alloy thereof.
20. In the combination of a walled melter, a walled conditioning
system having at least one heating element extending through an
orifice in a wall thereof and a forehearth, said melter being
connected in molten glass flow communication with said conditioning
system through a discharge port located in a wall of said melter at
a first end of said conditioning system and said opposite end of
said conditioning system being connected in molten glass flow
communication with said forehearth, the improvement comprising at
least one removable heating element extending through said orifice
in a wall thereof and exhaust means proximal said orifice for
exhausting corrosive volatiles from above said molten glass in said
conditioning system through the orifice when said removable heating
element is removed therefrom.
21. The combination of claim 20 wherein said conditioning system
has an entrance end for receiving molten glass from said melter,
and said discharge port is in flow communication with said entrance
end of said conditioning system thereby forming a juncture between
said melter and said conditioning system, the combination further
comprising a second exhaust system at said juncture for exhausting
corrosive volatiles during the glass melting and conditioning
operation.
22. The combination of claim 21 wherein said melter further
includes means for providing batch material on top of said molten
glass when in said melter so as to float on said molten glass in a
layer thereon.
23. In the method of melting, conditioning and distributing molten
glass wherein said method includes the steps of providing in serial
flow communication, a melter, a walled conditioner and a forehearth
array, melting glass in said melter, delivering molten glass from
said melter to said conditioner, providing at least one heating
means located in an orifice in a wall of said conditioner,
delivering said molten glass from said conditioner to said
forehearth and distributing said molten glass from said forehearth,
wherein the method further includes the step of removing a
substantial portion of said corrosive volatiles from the atmosphere
above the glass before they reach the forehearth, the improvement
comprising, removing at least one of said heating means from its
respective orifice, thereby to provide an open orifice in a wall of
said conditioner, providing an exhaust means in exhaust functioning
communication with respect to said open orifice, and exhausting
corrosive volatiles from said conditioner through said open
orifice.
24. The method of claim 23 wherein said method further includes the
step of providing batch material on top of the molten glass in said
melter.
25. In a system for melting glass which includes a glass melter, a
conditioner, and a forehearth wherein said glass melter is so
constructed to discharge molten glass to said conditioner, wherein
said conditioner is so constructed as to allow molten glass to flow
through said conditioner to said forehearth and enter said
forehearth at a lower temperature than the molten glass entered
said conditioner, the improvement comprising a glass flow diverting
structure so located so as to extend into said flow of molten glass
in said conditioner so as to divert molten surface glass into
molten glass beneath said molten surface glass.
26. The improvement according to claim 25 wherein said conditioner
includes a top wall and glass flow diverting structure includes a
walled structure extending downwardly from said top wall and of
sufficient length so as to extend into said molten glass a
sufficient distance to substantially equalize the depthwise
temperature of the glass at any given location of the conditioner
thereby to reduce crystallization of said glass in said
conditioner.
27. The improvement according to claim 26 wherein said glass
diverting structure includes means for cooling said structure.
Description
RELATED APPLICATION
[0001] This application is a continuation-in-part of Application
Ser. No. 08/917,207 filed Aug. 25, 1997, now U.S. Pat. No.
______.
BACKGROUND OF THE INVENTION
[0002] This invention relates to certain improvements in apparatus
and methods for melting glass. More particularly, this invention
relates to apparatus and methods which control the location of the
"hot spot," i.e. area of highest temperature in the liquid pool of
melting or molten glass in a glass melter so as to control the wear
out of various melter and discharge elements thereby reducing the
number of shutdowns needed for replacement or rebuild purposes.
Still further, this invention relates to unique methods and
apparatus for venting corrosive volatiles from the system.
[0003] Melters of various shapes and sizes which present glass
batch (usually in powdered ingredient form, with or without cullet)
often by floating the batch material as a relatively thick layer on
top of a molten pool of glass being heated and melted beneath the
batch, and thereafter distributing the molten glass from the pool
through a discharge port in a side wall of the melter to a
conditioning zone (conditioner), and thereafter to a forehearth
array or other working area, are well known in the art. Exemplary
of such systems are conventional, in line combinations of a melter,
conditioner, and forehearth used to distribute molten glass to an
array of spinners for making fiberglass batts of insulation. Other
uses for such combinations are, of course, known, and the art, as a
whole, is generally represented by the following prior art
references:
1 U.S. Pat. No. 3,498,779 4,365,987 3,897,234 4,812,372 4,001,001
4,994,099 4,017,294 5,194,081 4,023,950 5,616,994
[0004] Generally speaking, and prior to my invention in the
aforesaid application Ser. No. 08/917,207, now U.S. Pat. No.
______, the art of glass making accepted the problem of multiple
shutdowns due to the fact that the various elements in conventional
melters, except in very unusual and unpredictable situations, wore
out at different times. In this respect, it is characteristic in
the prior art construction of melters to employ a cylindrical or
rectangular tank-like configuration in which the side and bottom
walls are formed of refractory material such as Cr, Al--Zr--Si, or
Al/Cr based compositions whose corrosion rate usually increases
with increased temperatures. Adding to this problem is the fact
that in such configurations one or more discharge ports are either
required or desired at different locations within the tank, e.g. in
the bottom wall and in at least one location in the side wall of
the tank. Because the temperature of the glass can, and often does,
differ markedly between a "hot spot" volume in the molten glass,
usually in the center of the tank near the bottom wall, and the
remaining molten glass volume, e.g. at the side walls, melter parts
in the cooler areas wear out less rapidly than parts located in or
proximal the "hot spot."
[0005] In a typical example of this problem, the melting tank is
provided in its bottom wall with a discharge port for draining the
tank and a side discharge port for distributing the molten glass to
a conditioning zone. Such discharge ports, whether in the bottom or
side walls, are normally formed of molybdenum or an alloy thereof
which is relatively corrosion resistant and thus is reasonably able
to withstand the high temperatures experienced in the melter over a
given period of time. Unfortunately, like the refractory wall
material, these molybdenum based ports have a corrosion rate which
increases with temperature.
[0006] In many melters it has also been conventional to cool the
walls by various techniques such as with a water-cooled shell
surrounding the melter. Such cooling of the bottom and side walls,
despite inherent currents of flow in the molten glass, tend to
isolate the "hot spot" and set up the temperature differentials as
discussed above, which then lead to the differences in wear out
rates of the various parts and the need for expensive, time
consuming, multiple shutdowns otherwise unnecessary if all the
parts were to wear out at substantially the same time.
[0007] In a typical prior art melter, for example, usually of a
circular, cylindrical bottom, side wall configuration, the furnace
is open topped, side and bottom wall cooled, and is provided with
electrodes to melt the batch material. These electrodes are usually
located in the melter either above the batch or in the molten pool
of glass itself, often near the bottom or inserted through the
batch. Powdered batch material is then "floated" on top of the
melting glass beneath it, usually by a conventional, metered batch
delivery system located above the melt area and fed by gravity
continuously to the batch layer as its underneath surface melts
into the molten volume of glass beneath it. It is, of course,
within this molten glass volume beneath the batch layer that the
aforesaid "hot spot" forms.
[0008] While convection currents created in the melting glass serve
to equalize, somewhat, the temperature of the molten glass pool, it
is very often an inherent characteristic of such melters,
particularly where bottom entry electrodes are employed, that the
bottom center of the melter is where the "hot spot" forms. For
example, a typical "hot spot" may be from about
3150.degree.-3250.degree. F. By contrast, the side walls will only
then be, particularly if water-cooled, at a significantly lower
temperature, e.g. about 2500.degree.-2700.degree. F. Even if
water-cooled, in certain instances, the bottom wall will be so
close to the "hot spot" that its temperature in a localized area
will, for all intents and purposes, be that of the "hot spot," thus
differing from other areas of the bottom wall, as well as the side
wall and discharge port in the side wall. Since the drainage port
is conventionally located in the center of the bottom wall, and
thus at or proximal the usual "hot spot" location, its corrosion
rate differs markedly from that of the side discharge port and side
walls.
[0009] As exemplified by the above typical melter arrangement,
multiple melter shutdowns may thus become necessary. For example,
the discharge drain port and/or bottom wall may have to be
replaced, while the side walls and side discharge port remain in
acceptable operating condition, only to have to replace one or more
of these two latter parts at a later time in a second shutdown,
while the replaced bottom wall and/or drain discharge port are not
yet worn sufficiently to economically justify their
replacement.
[0010] In short, it would constitute a considerable advance in the
art of glass melting if a technique were developed which could
control the location of the aforesaid "hot spot" in a glass melter
so as to displace it (locate it) away from the refractory walls and
metallic discharge port tubes (side and bottom) such that all of
the elements in the melter subject to corrosion and wear out
therefrom were to wear out at substantially the same time.
[0011] The term "at substantially the same time," as used herein,
means that the elements which are the subject of corrosive wear out
are in such a condition at the time that one element is in the most
advanced condition of wear out, that it is economically justifiable
to replace all the elements, rather than to go through another
shutdown to replace a less worn out element when it completely
wears out later in time.
[0012] In my aforesaid co-pending Application Ser. No. 08/917,207,
now U.S. Pat. No. ______, the disclosure of which is incorporated
herein by reference, a significant advance toward reaching this
goal and solving this prior art problem was achieved, based upon
the acceptance of the inherent location of the "hot spot" in the
melter. By the use of a unique discharge port concept located in
the side wall of the melter, a sufficient distance away from the
"hot spot," coupled optionally with side and bottom wall cooling
means, the side discharge ports and side walls could justifiably be
replaced at the same time. In addition, in certain embodiments, by
relying on convection currents and sufficient bottom wall cooling,
the bottom wall and bottom discharge drain theoretically could, at
times, be controlled to wear out at substantially the same time as
the side wall and side discharge port. Despite this significant
advance in the art, it has now been found that the "hot spot" (i.e.
volume of highest temperature) often exists, in certain furnaces,
inherently too close to the bottom and/or side walls of the melter
tank and that circulation currents, even with wall cooling, are
insufficient to keep the wear out rate of the bottom wall and
bottom discharge orifice truly substantially equal to that of the
side walls and side discharge orifice. Thus there continues to be a
need in the art for a still further improvement which creates an
even more equalized wear out rate among the essential parts in the
melter (e.g. the refractory melter lining which makes up the melter
walls, side and bottom, and the various discharge ports in these
walls.
[0013] There is yet another problem which the art of glass melting
has had to face. In many glass melting operations, such as in
melting glass ultimately used to make fiberglass insulation, it is
necessary to employ batch ingredients which create highly corrosive
volatiles during the melting and/or conditioning operation. These
volatiles often end up in the atmosphere above the glass and can
thus rapidly corrode walls, orifices and heater elements if not
effectively exhausted from the system. Such volatiles are. well
known and include, for example, various sodium and borate
compounds.
[0014] In melting systems which do not employ, or need not employ,
the highly advantageous technique during glass melting of floating
batch material in a relatively thick layer (e.g. about 3"-4", or at
times as high as 10") on top of the molten glass, the corrosive
volatiles can usually be exhausted during melting by exhausting
them from the melter itself. However, when the more desirable batch
technique of floating the batch on top of a molten pool of glass is
employed, the volatiles do not readily escape through the batch,
but rather are only released in the conditioner when the molten
glass is then freed from the batch material being on top of it.
This, then, gives rise to the need for a new technique for
effectively eliminating corrosive volatiles from the glass in the
conditioner, particularly before they reach the forehearth.
[0015] It is a purpose of this invention to fulfill the above needs
in the art, as well as other needs which will become apparent to
the skilled artisan once given the following disclosure.
SUMMARY OF THE INVENTION
[0016] Generally speaking, this invention fulfills at least one of
the above-described needs in the art by providing both a method and
an apparatus for melting glass which controls the location of the
"hot spot" so as to locate it within the melt at a sufficient
distance from the side and bottom walls, as well as any discharge
orifice therein, so that the discharge orifices and walls (bottom
and side) may be replaced at substantially the same time.
[0017] In one embodiment of this invention this is accomplished by
providing in a melter for melting glass from batch material therein
in which the batch material is floated on top of a pool of molten
glass and the batch is melted by heating means so located as to
form a finite volume of molten glass within the pool of molten
glass, which finite volume is at a temperature substantially higher
than the remainder of the molten glass within said pool, the melter
including a side wall and a bottom wall and a discharge port
located within at least one of the walls, the improvement
comprising wherein:
[0018] the heating means are so located as to create this finite
volume of substantially higher temperature at a spaced distance
from the walls and any side discharge orifice located in the walls
whereby the walls and any side discharge orifice wear out at
substantially the same time during melting of glass in the
melter.
[0019] In certain preferred embodiments of this invention the
heating means comprises a plurality of electrodes in a generally
circular array located within the molten pool beneath the batch
material floating thereon, and including a retaining structure for
each electrode extending above the batch, which retaining structure
includes an adjustment mechanism for adjusting the depth to which
the electrode is inserted into the molten pool, and also,
preferably, for adjusting the horizontal location of each electrode
within the pool, as well. By adjustment of the electrode array both
horizontally and vertically within the pool, the optimal location
for the inevitable "hot spot" can be achieved for any particular
size and/or configuration of melter tank (furnace) extant to
optimize the goal of achieving substantially the same wear out time
of the various melter parts.
[0020] In certain preferred embodiments, in this respect, the
melter may be one of an open top type, with a water-cooled jacket
or shell, whose batch feed, optionally, may be a simple tube
located above and in the center of the electrode array. In still
further preferred embodiments, the melter is a cylindrical tank
with a side discharge port of the type disclosed in my aforesaid
pending Application Ser. No. 08/917,207, now U.S. Pat. No. ______.
A particularly advantageous electrode array, in this respect,
consists essentially of six electrodes equally spaced in a circular
pattern about the center of the cylindrical tank, the radius of the
circle being about one-third the radius of the inside diameter of
the tank.
[0021] This invention further includes within its scope certain
unique methods for melting glass. Generally speaking, in this
respect, this invention includes in the method of melting glass in
a melter which includes a bottom wall, a side wall and at least one
discharge port located in a said wall and comprised of a corrosion
resistant material whose corrosion rate increases with temperature,
the steps comprising, forming a molten pool of glass within the
melter, floating batch material on top of the molten pool, melting
the batch material so as to add further molten glass to the pool,
discharging molten glass from the melter through a discharge port,
and during the melting of the glass batch material, creating within
the pool a finite volume of molten glass which is at a
significantly higher temperature than the remainder of the molten
glass within the pool, the improvement which comprises forming the
finite volume of the higher temperature molten glass at a location
sufficiently removed from the walls and the discharge port such
that the walls and discharge port wear out at substantially the
same time.
[0022] This invention further includes within its scope certain
unique apparatus and methods for exhausting corrosion causing
volatiles from the overall system before they reach the forehearth,
thus fulfilling yet other needs in the art.
[0023] Generally speaking, the unique apparatus as contemplated
herein for exhausting volatiles during glass melting and
distribution includes, in the combination of a walled melter, a
walled conditioning system having at least one heating element
extending through an orifice in a wall thereof and a forehearth,
said melter being connected in molten glass flow communication with
said conditioning system through a discharge port located in a wall
of the melter at a first end of the conditioning system and the
opposite end of the conditioning system being connected in molten
glass flow communication with the forehearth, the improvement
comprising at least one removable heating element extending through
the orifice in a wall of the conditioning system and exhaust means
proximal the orifice for exhausting corrosive volatiles from above
the molten glass in the conditioning system through the orifice
when the removable heating element is removed therefrom.
[0024] In certain preferred embodiments of this invention the
melter, conditioning system and forehearth are all located in
substantially the same horizontal plane. In certain other preferred
embodiments, of course, this invention employs as its melter the
aforesaid unique melter which controls the "hot spot" so that its
various elements wear out at substantially the same time.
[0025] Still further, and generally speaking, the unique methods
associated with this novel exhaust technique include in the method
of melting, conditioning and distributing molten glass wherein the
method includes the steps of providing in serial flow
communication, a melter, a walled conditioner and a forehearth
array, melting glass in the melter, delivering molten glass from
the melter to the conditioner, providing at least one heating means
located in an orifice in a wall of the conditioner, delivering the
molten glass from the conditioner to the forehearth and
distributing the molten glass from the forehearth, wherein the
method further includes the step of removing a substantial portion
of the corrosive volatiles from the atmosphere above the glass
before they reach the forehearth, the improvement comprising,
removing at least one of the heating means from its respective
orifice thereby providing an open orifice in a wall of the
conditioner, providing an exhaust means in exhaust functioning
communication with respect to the open orifice, and exhausting
corrosive volatiles from the conditioner through the open
orifice.
[0026] In certain preferred embodiments the method as above set
forth further includes the step of providing batch material on top
of the molten glass in the melter.
[0027] This invention will now be described with respect to certain
embodiments thereof accompanied by various illustrations
wherein:
IN THE DRAWINGS
[0028] FIG. 1 is a partial side sectional view of one embodiment of
this invention.
[0029] FIG. 1A is a partial top view of the embodiment of FIG. 1,
with the molten glass and batch only partially shown so as to
illustrate the inside bottom wall of the melter.
[0030] FIG. 2 is a partial side sectional view of the embodiment of
FIG. 1.
[0031] FIG. 3 is a schematic outline of the current pattern among
the electrodes in the embodiment of FIG. 1.
[0032] FIG. 4 is a partial side sectional view of the side
discharge port and vent chamber of the embodiment of FIG. 1.
[0033] FIG. 5 is an end sectional view of the cooling means and
side discharge tube of FIG. 1.
[0034] FIG. 6 is a side sectional view of a conditioner cooling
means used in the practice of an embodiment of this invention.
DETAILED DESCRIPTION OF CERTAIN EMBODIMENTS
[0035] With reference initially to FIG. 1, there is illustrated
therein an apparatus for melting glass according to this invention.
The apparatus as illustrated includes a melter 1, a conditioner 3,
and, as partially shown, a forehearth 5. Forehearth 5 is
conventional and, for example, may be of the type provided with
multiple orifices along its elongated bottom wall (not shown for
convenience) for distributing molten, conditioned glass at an
appropriate temperature to a conventional spinner array for making
fiberglass insulation batts (also not shown for convenience).
Orifice 7, as illustrated, is an air-cooled drain orifice in this
embodiment used to drain the system during shutdown, the
distribution orifices leading to fiberglass spinners being further
downstream.
[0036] In the embodiment of FIG. 1 the three zones of operation,
i.e. melter 1, conditioner 3, and forehearth 5 are preferably all
located in substantially the same horizontal plane. This eliminates
a known use of the location of the forehearth on a level (e.g. on a
separate floor of the plant) below the conditioner, called the
"drop area", which heretofore was advantageously used to exhaust
volatiles from the system. In this way, the need to build into the
plant facility a separate level or floor is eliminated and its
considerable cost saved. However, this eliminates the aforesaid
advantageous drop area between the exit end of conditioner 3 and
entrance end 6 of forehearth 5 which was used to vent (exhaust)
corrosive volatiles. This, in turn, gives rise to the unique
venting system of this invention discussed above and described more
fully below.
[0037] Turning now to a more detailed description of melter 1,
attention is directed, in addition to FIG. 1, to FIGS. 1A, 2 and 3.
The mechanism illustrated is one embodiment of a mechanism as
contemplated by this invention for selecting the location of, and
controlling the size of, "hot spot" 9 created in molten glass pool
11 during the melting operation. As illustrated schematically in
FIGS. 1, 1A, and 3 in dotted lines, by using an array of heating
electrodes 13, and here preferably six, arranged in a substantially
circular fashion below the layer of batch material 15 floating on
pool 11, "hot spot" 9 is generally confined to a finite, generally
hexagonal or circular cylindrically shaped volume of glass below
batch 15, whose central vertical axis "C" corresponds with the
central vertical axis of cylindrical melter tank 1. FIG. 3 is a
schematic whose full lines illustrate the theoretical paths of
heating current extending among the electrodes and whose dotted
lines illustrate a top view of "hot spot" 9.
[0038] Melter 1 is of a conventional tank-like, cylindrical
construction having conventional side wall 19, and bottom wall 23,
each lined with refractory linings 21 and 25, respectively. Such
refractory linings 21 and 25 may be formed of conventionally used
refractory material such as a chromium based material which is
known for its corrosion resistance, but whose corrosion rate
increases with temperature. In a typical example, lining 21 may be
90% or more by weight Cr, while linings 19, 23, and 25 may have
less Cr, e.g. about 30-50% by weight. Melter 1 further includes in
conventional fashion drain discharge port 31 located centrally of
melter 1. Discharge port 31 is conventionally formed of a corrosion
resistant metallic tube 33 inserted through an orifice in shell 29,
bed material 35, wall 23 and liner 25. Port 31 is principally used
for draining glass from melter 1 preparatory to shutdown.
[0039] As further illustrated in FIG. 1, but better shown in FIG.
2, batch material 15 is floated on pool 11 of molten glass such
that the underside surface of batch material 15 is constantly being
melted while the batch layer is being added to as it is consumed by
a conventional metered batch system whose exit end tube is shown at
37. As best illustrated in FIGS. 1, 1A, powdered batch 15 is fed by
gravity to the substantial center of the circle having a radius R,
whose circumference is subscribed by the location of the six
electrodes 13 as points on the circle and whose center is
contiguous vertical axis "C".
[0040] As best illustrated in FIG. 2, the depth "D" of molten pool
11 is the distance from the inner surface of lining 25 to the under
surface of batch material layer 15. Distance "D" varies, of course,
given the drainage slope in the bottom wall structure of melter
tank 1. As shown in FIG. 1A, in one embodiment of such a melter 1,
radius R.sub.2 may be about 7-8 feet, radius R.sub.1, about 1/4-1/3
of R.sub.2, e.g. about 2-3 feet, while depth "D" at the side wall
19 may be about 13-15inches and the thickness "T" of the powdered
to semi-molten batch layer may be about 3-5 inches or more (e.g. up
to 101").
[0041] With further reference to FIG. 1 and FIG. 4 more
particularly, melter 1 is provided with a side discharge port
generally at 39 for distributing molten glass from pool 11 to
conditioner 3. In preferred embodiments of this invention side
discharge port 39 is constructed according to my aforesaid
Application Ser. No. 08/917,207, now U.S. Pat. No. ______. As
disclosed therein and as illustrated here, discharge port 39
includes a corrosion resistant metallic tube 41 (e.g. of molybdenum
or an alloy thereof and usually of the same metal which makes up
drain tube 33) extending through the side wall structure of tank 1
in flow communication with the entrance end of conditioner 3. As
shown in FIGS. 1 and 5, tube 41 is thicker at its top than bottom
circumference, and is cooled by circulating water or other fluid
through surrounding shell 43 in the direction of the arrows (FIG.
5).
[0042] The purpose of making the top of tube 41 thicker is because,
for some reason not fully understood, and despite the fact that
tube 41 is fully submerged in molten glass theoretically protecting
it throughout its circumference from oxidation, the top of tube 41
wears out more rapidly than its bottom portion. Thus it has been
found in practice to be advantageous for longer wear life to, for
example, with a discharge tube of about 6 inches (O.D.), use a 4
inch (ID) orifice created by a 1/2 inch offset from center. While
not fully understood, this uneven wear pattern may be explainable
by the phenomenon known as "upward drilling" in a refractory
material as it is corroded by corrosive materials in the glass.
[0043] Conditioner 3 is principally used to lower the glass exiting
melter 1 to an appropriate temperature for distribution to the
forehearth. For example, in a typical operation, glass "G" may exit
side discharge tube 41 at a temperature of about 2560.degree. F.,
and be lowered to about 2230.degree. (e.g. a drop of greater than
200.degree. F.) as it enters forehearth 5 beneath submerged block
(dam) 45 which functions along with dam 47 to isolate molten glass
in conditioner 3 from glass in forehearth 5 during shutdown. Dam 45
further serves to isolate the relatively volatile free atmosphere
of forehearth 5 from the atmosphere of conditioner 3. In a similar
manner, of course, dam 49 isolates molten glass in conditioner 3
from melter 1 and exhaust area "E" (described below) during a
shutdown. Drain port 51 is provided in bottom wall 53 (which may be
water-cooled) to drain glass from conditioner 3 prior to shutdown
or when otherwise needed.
[0044] Provided in top wall 55 of conditioner 3 is a cooling baffle
structure 57 (more than one can be optionally added, if desired)
for circulating cooling water or air therethrough. Baffle 57 is a
unique concept to this invention. Without baffle(s) 57, there would
be formed a stream of higher temperature glass on the surface of
flow, potentially causing lower glass to crystallize. Baffle(s) 57
divert hot glass downwardly, thereby preventing this problem from
occurring and creating better homogeniety of temperature in the
glass and a lack of stagnant glass in the bottom of conditioner
3.
[0045] In addition, top wall 55 is provided with removable burners
59a-e located in their respective orifices extending through wall
55. During start-up of the system, in conventional fashion, burners
59a-e are employed to heat the refractory walls so that molten
glass flowing from melter 1 and exiting tube 41 will remain molten,
and continue to flow through conditioner 3, rather than solidify
when it contacts the refractory walls.
[0046] After start-up and filling conditioner 3 to the depth
desired with molten glass (not shown for convenience), the molten
glass must then be cooled to the required exit temperature as
aforesaid. For this purpose, one or more of the removable burners
59a-e are removed (thus vacating their respective orifice 60a, b,
c, d, or e) and replaced by water-cooled tubes such as a cooling
tube 61 shown in FIG. 6, which is inserted into a vacated orifice
made open by removal of a burner 59 therefrom. As shown in FIG. 6,
cooling tube 61 is a simple rectangular or circular shell 63
(depending on the conforming shape of the vacated orifice it is
inserted in). Shell 63 has located in its wall, water outlet port
65. Within shell 63 there is located an internal tube 67 for
providing cooling water (or other fluid) to shell 63 in the
direction of the arrows. Cooling tubes 61 are metallic and may be
made of a corrosion resistant metal such as molybdenum, if desired.
Tubes 61 can be provided with a simple mechanism for controlling
their depth of emersion into the molten glass. This, in turn, can
be used to ultimately control the outlet temperature of the glass
at the entrance 6 of forehearth 5. In this respect, orifice 64 is
used for a thermocouple (not shown) to sense the temperature of the
glass that is entering forehearth 5.
[0047] To cool the glass, cooling air may be used instead of, or
alternatively with, cooling tubes 61. For example, in a typical
operation which cools the molten glass from about 2560.degree. F.
to 2230.degree. F. in conditioner 3, orifice 59a may have cooling
air blown through it, as may orifice 59e. This also forces an
atmosphere changeover to continuously rid the atmosphere of
volatiles. Then, cooling tubes 61 may be inserted into orifices 59b
and c. This leaves orifice 59d open for use in a unique exhaust
system as contemplated by this invention and as described below. It
is understood, of course, that orifices 59a-e may have other
combinations of air flow and/or cooling tubes employed, including
all cooling tubes 61 or all cooling air flow if desired. It is,
however, an important feature of a preferred embodiment of this
invention that at least one of these vacated orifices, preferably
either orifice 59d or 59e, and most preferably 59d, be employed to
exhaust corrosive volatiles from the atmosphere above the molten
glass in conditioner 3.
[0048] As illustrated in FIG. 1 in phantom dotted lines, an exhaust
system 69 is provided at orifice 59d which may be turned on after
burner 59d is removed, thus exhausting volatiles from conditioner 3
before they reach forehearth 5. As a further part of a preferred
exhaust system, a further permanent exhaust port 71 is provided at
the initial entrance end of area "E" in conditioner 3 where an
initial portion of the volatiles may first be removed from the
atmosphere above the molten glass immediately as it exits side
discharge tube 41.
[0049] Turning now, more particularly, to the electrode melting
apparatus illustrated in FIGS. 1-3, there is presented a unique
apparatus and method for controlling the size and location of "hot
spot" 9 which can otherwise be so detrimental to wear out, and
which, if not controlled, can cause unnecessary multiple shutdowns
of the system as described above.
[0050] In the melting configuration as illustrated there are
provided six conventional electrode melters 13 which are
conventionally water-cooled by entrance line 73 and exit line 75.
Other configurations using lesser numbers of, or more, electrodes
may be used. Electrode 13, including its current-carrying shaft 79,
may be formed of molybdenum as is the actual electrode melter
portion 81. Water-cooled shell 77 may be formed of stainless steel.
As illustrated schematically in FIG. 2 and more realistically in
FIG. 1, electrode portion 81 is immersed in the molten glass 11 to
the depth required, while molybdenum shaft 79 is protectively
cooled by cooling shell 77.
[0051] Electrode 13 is supported by horizontal shaft 83 which
carries electric current and the cooling water to and from the
electrode. In turn, shaft 83 is connected to an adjusting mechanism
85 which includes a central shaft 87 which retains, in vertical
position, outer shaft 89. Rotating mechanism 91 allows shafts 89,
and thus shaft 83 attached thereto, to be angularly adjusted in the
horizontal plane by rotating the shaft on ball bearing 93 and
securing the shaft at the desired angle by a conventional locking
mechanism 95 when the desired angle is reached.
[0052] In addition to this horizontal adjustment, the vertical
position of electrode 13 within molten pool 11 is accomplished by
gear rachet mechanism 97 which, via screw threaded rod 99 attached
to shaft (sleeve) 89, slidable in retaining tube 101, may be
activated to vertically adjust the height of shaft 83 above melter
1 and thus that of electrode 13 with respect to pool 11. Protective
bellows 103 extends between slidable shaft 89 and upper nonslidable
shaft 105 to which rachet mechanism 97 is attached, to protect that
portion of shaft 87 on which shaft 89 slides during vertical
adjustment, from dust and other contamination.
[0053] As can be seen, the adjusting mechanism 85 provides an
effective mechanism for adjusting both the horizontal and vertical
positions of each electrode 13 with respect to the molten bath.
Since it is the electrode array which ultimately defines and limits
the finite volume of "hot spot" 9 (e.g. typically at 3150.degree.
F.-3250.degree. F.), the unique apparatus illustrated here
presents, by its precise adjustability, the ability to control the
location, size and, indeed, in certain instances, the general shape
of the "hot spot" 9. Thus, by proper adjustment, the "hot spot" may
be controlled at a preselected location within melter 1 (i.e.
within pool 11) sufficiently removed from the sensitive refractory
and metallic parts, so that these elements wear out at
substantially the same time, thus minimizing the number of
shutdowns needed for repair.
[0054] In a typical operation of the above-described system,
electrodes 13 are adjusted so as to be equally spaced (as
illustrated in FIG. 1A) about vertical axis "C" of tank 1.
Electrode melter portion 81 of each electrode 13 may be
approximately 6 inches in diameter and about 61/2 inches in height
and may be operated at about 4000 amps. Given a side height "D"
within the aforesaid range, and a radius R.sub.2 of about 8 feet
and a radius R.sub.1 of about 3 feet, with an adjusted depth of
about 9-12 inches between the bottom of electrodes 13 and the top
surface of bottom wall liner 25 for each of the six electrodes
employed in the array as shown, a "hot spot" 9 as illustrated in
FIGS. 1, 1A is sufficiently controlled and confined to a finite
volume within the electrode array such that the "hot spot", usually
at about 3150.degree. F.-3250.degree. F. is substantially removed
from the refractory walls and discharge ports, while such walls and
ports are located nearest the coolest glass as cooled by the
cooling water in cooling shell 29 and as affected by glass flow
currents shown by the circulating arrows in FIG. 1. In this way,
and by proper adjustment of the electrode array for any given
configuration of melting tank, arrived at by routine
experimentation well within the skill of the artisan once given
this disclosure, a unique technique for substantially equalizing
wear out of the melting tank parts may be accomplished, thus
minimizing the number of shutdowns required for replacement of
parts.
[0055] Once given the above disclosure, many other features,
modifications and improvements will become apparent to the skilled
artisan. Such features, modifications and improvements are,
therefore, considered a part of this invention, the scope of which
is to be determined by the following claims:
* * * * *