U.S. patent application number 09/835292 was filed with the patent office on 2001-12-13 for compositions for three-dimensional printing of solid objects.
This patent application is currently assigned to Z Corporation. Invention is credited to Anderson, Timothy, Bredt, James F., Clark, Sarah L., DiCologero, Matthew, Tarkanian, Michael J., Uy, Evert.
Application Number | 20010050031 09/835292 |
Document ID | / |
Family ID | 27393703 |
Filed Date | 2001-12-13 |
United States Patent
Application |
20010050031 |
Kind Code |
A1 |
Bredt, James F. ; et
al. |
December 13, 2001 |
Compositions for three-dimensional printing of solid objects
Abstract
A three-dimensional printing materials system and method can
produce both appearance models and small numbers of functional
parts in an office environment. The method can include building
cross-sectional portions of a three-dimensional article, and
assembling the individual cross-sectional areas in a layer-wise
fashion to form a final article. The individual cross-sectional
areas can be built by using an ink-jet printhead to deliver an
aqueous solvent or binder to an adhesive particulate mixture,
causing the particles of the mixture to adhere together, and to
previous cross-sectional areas. The binder can include at least one
of nonaqueous organic monomeric compound, anionically ionizable
polymer, cationic polymer, polymer, waterborne colloid, or
inorganic solute.
Inventors: |
Bredt, James F.; (Watertown,
MA) ; Clark, Sarah L.; (Cambridge, MA) ; Uy,
Evert; (Marlborough, MA) ; DiCologero, Matthew;
(Medford, MA) ; Anderson, Timothy; (Cambridge,
MA) ; Tarkanian, Michael J.; (Brockton, MA) |
Correspondence
Address: |
Rodney D. Johnson, Esq.
HAMILTON, BROOK, SMITH & REYNOLDS, P.C.
Two Militia Drive
Lexington
MA
02421-4799
US
|
Assignee: |
Z Corporation
20 North Avenue
Burlington
MA
01803
|
Family ID: |
27393703 |
Appl. No.: |
09/835292 |
Filed: |
April 13, 2001 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
60197118 |
Apr 14, 2000 |
|
|
|
60197526 |
Apr 14, 2000 |
|
|
|
Current U.S.
Class: |
106/162.9 ;
106/204.01; 106/287.1 |
Current CPC
Class: |
B29C 67/24 20130101;
B33Y 80/00 20141201; C09D 11/00 20130101; B33Y 10/00 20141201; B33Y
70/00 20141201; B29K 2033/08 20130101; B29K 2105/0097 20130101;
B29C 41/003 20130101; B29C 64/165 20170801; B29C 64/112
20170801 |
Class at
Publication: |
106/162.9 ;
106/204.01; 106/287.1 |
International
Class: |
C08L 001/02; C08L
005/00; C09D 101/00; C09J 101/00; C09J 105/00; C09D 105/00 |
Claims
What is claimed is:
1. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
component comprising a nonaqueous organic monomeric compound.
2. The compositing of claim 1, wherein the compound includes at
least one of an alcohol, an ester, an ether, a silane, a vinyl
monomer, an acrylic monomer, or a methacrylate monomer.
3. The composition of claim 1, comprising a solvent and a solute,
and wherein the compound is the solvent.
4. The composition of claim 3, wherein the solvent includes an
alcohol.
5. The composition of claim 4, wherein the alcohol is methyl
alcohol, ethyl alcohol, isopropanol, or t-butanol.
6. The composition of claim 3, wherein the solvent includes an
ester.
7. The composition of claim 6, wherein the ester includes at least
one of ethyl acetate, dimethyl succinate, diethyl succinate,
dimethyl adipate, or ethylene glycol diacetate.
8. The composition of claim 2, wherein the compound includes a
mixed vinyl-silane monomer.
9. The composition of claim 8, wherein the mixed monomer includes
vinyltriisopropoxysilane.
10. The composition of claim 2, wherein the acrylic monomer
includes at least one of tri(propylene glycol) diacrylate, ethylene
glycol phenyl ether acrylate, or 1,6 hexanediol diacrylate.
11. The composition of claim 2, wherein the methacrylic monomer
includes at least one of 1,3 butylene glycol dimethacrylate,
neopentyl glycol dimethacrylate, butyl methacrylate, 1,6 hexanediol
dimethacrylate, or di(propylene glycol) allyl ether
methacrylate.
12. The composition of claim 1, wherein the compound is curable in
combination with a photoinitiator to form a solid, by ultraviolet
radiation having a wavelength between about 320-500 nm and an
energy density of about 1 joule/cm.sup.2.
13. The composition of claim 1, wherein the compound is a solvent
for a resin in the particulate material.
14. The composition of claim 13, wherein the resin includes at
least one of shellac, polyvinyl pyrrolidone, polyvinyl acetate,
polyvinyl alcohol, polystyrene, styrene-butadiene copolymer, or
acrylonitrile-butadiene-styr- ene copolymer.
15. The composition of claim 1, wherein the particulate material
includes a filler that includes an inorganic compound.
16. The composition of claim 15, wherein the filler includes at
least one of clay, aluminum oxide, silicon dioxide, aluminum
silicate, potassium aluminum silicate, calcium silicate, calcium
hydroxide, calcium aluminate, calcium carbonate, sodium silicate,
zinc oxide, titanium dioxide, or magnetite.
17. The composition of claim 15, further comprising a printing aid
dispersed throughout the filler.
18. The composition of claim 17, wherein the printing aid includes
at least one of sorbitan trioleate, sorbitan mono-oleate, sorbitan
monolaurate, polyoxyethylene sorbitan mono-oleate, polyethylene
glycol, soybean oil, mineral oil, propylene glycol, fluroaklkyl
polyoxyethylene polymers, glycerol triacetate, polypropylene
glycol, ethylene glycol octanoate, ethylene glycol decanoate,
ethoxylated derivatives of 2,4,7,9-Tetramethyl-5-decyne-4,7-diol,
oleyl alcohol, or oleic acid.
19. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder composition including an adhesive in combination with a
fluid, the adhesive comprising a nonaqueous organic monomeric
compound.
20. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
composition comprising an anionically ionizable polymer consisting
of compounds selected from the group including polymethacrylic
acid, polymethacrylic acid sodium salt, and sodium polystyrene
sulfonate.
21. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
composition including an adhesive in combination with a fluid, the
adhesive comprising an anionically ionizable polymer consisting of
compounds selected from the group including polymethacrylic acid,
polymethacrylic acid sodium salt, and sodium polystyrene
sulfonate.
22. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
composition comprising a cationic polymer.
23. The composition of claim 22, wherein the polymer includes
polyethyleneimine and polydiallyldimethylammonium chloride.
24. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder composition including an adhesive in combination with a
fluid, the adhesive comprising a cationic polymer.
25. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
composition comprising a nonionic polymer.
26. The composition of claim 25, wherein the polymer includes at
least one of polyvinyl pyrrolidone, polyvinyl pyrrolidone copolymer
with polyvinyl acetate, polyvinyl alcohol, polyvinyl methyl ether,
polyacrylamide, or poly-2-ethyl-2-oxazoline.
27. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder including an adhesive in combination with a fluid, the
adhesive comprising a nonionic polymer.
28. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
adhesive comprising a polymer selected from the group consisting of
polymethacrylic acid, polymethacrylic acid sodium salt, sodium
polystyrene sulfonate, and polyethyleneimine.
29. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder including an adhesive in combination with a fluid, the
adhesive comprising a polymer selected from the group consisting of
polymethacrylic acid, polymethacrylic acid sodium salt, sodium
polystyrene sulfonate, and polyethyleneimine.
30. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
adhesive comprising a waterborne colloid selected from the group
consisting of polymethyl methacrylate, polystyrene, natural rubber,
polyurethane, polyvinyl acetate, and alkyd resins.
31. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder including an adhesive in combination with a fluid, the
adhesive comprising a polymer selected from the group consisting of
polymethyl methacrylate, polystyrene, natural rubber, polyurethane,
polyvinyl acetate, and alkyd resins.
32. A chemical composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
adhesive comprising an inorganic solute selected from the group
consisting of sodium polyphosphate, sodium hydrogen phosphate,
sodium hydrogen pyrophosphate, sodium tetraborate, ammonium
hydrogen phosphate, sodium chloride, ammonium nitrate, potassium
sulfate, ammonium chloride, and calcium formate.
33. A binder composition for selectively adhering particulate
material to form a solid object in a three-dimensional printer, the
binder including an adhesive in combination with a fluid, the
adhesive comprising an inorganic solute selected from the group
consisting of sodium polyphosphate, sodium tetraborate, sodium
chloride, ammonium nitrate, potassium sulfate, ammonium chloride,
and calcium formate.
34. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition including a nonaqueous organic monomeric
compound.
35. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising an anionically ionizable polymer
consisting of compounds selected from the group including
polymethacrylic acid, polymethacrylic acid sodium salt, and sodium
polystyrene sulfonate.
36. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising a cationic polymer.
37. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising a nonionic polymer.
38. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising a polymer selected from the group
consisting of polymethacrylic acid, polymethacrylic acid sodium
salt, sodium polystyrene sulfonate, and polyethyleneimine.
39. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising a waterborne colloid selected from the
group consisting of polymethyl methacrylate, polystyrene, natural
rubber, polyurethane, polyvinyl acetate, and alkyd resins.
40. A method of forming a three-dimensional object, comprising:
forming a layer of filler that includes a particulate material; and
applying a chemical composition to the layer of filler at
particular locations to bind the filler at particular locations,
the composition comprising an inorganic solute selected from the
group consisting of sodium polyphosphate, sodium tetraborate,
sodium chloride, ammonium nitrate, potassium sulfate, ammonium
chloride, and calcium formate.
Description
RELATED APPLICATIONS
[0001] This application claims the benefit of U.S. Provisional
Application Nos. 60/197,118 and 60/197,526, both filed Apr. 14,
2000. This application is related to U.S. application Ser. No.
09/234,349, filed Jan. 20, 1999, which is a divisional application
of U.S. Pat. No. 5,902,441, issued May 11, 1999, and to U.S.
application Ser. No. 09/416,787, which is a continuation-in-part of
U.S. Pat. No. 6,007,318. The teachings of each of these references
are incorporated herein by reference in their entirety.
BACKGROUND
[0002] Rapid prototyping involves the production of prototype
articles and small quantities of functional parts, as well as
structural ceramics and ceramic shell molds for metal casting,
directly from computer-generated design data. There are a variety
of methods to form a three-dimensional article including a
selective laser-sintering process as described in U.S. Pat. No.
4,863,568, which is incorporated herein by reference.
[0003] Three-dimensional printing is a process invented by Sachs et
al. at Massachusetts Institute of Technology in the early 1980's.
In accordance with the process, an ink-jet printhead is used to
deposit a liquid ink or binder onto a print plane composed of a
powdered receiving medium. The combination of liquid binder and
solid powder solidifies to form a finished article.
[0004] U.S. Pat. No. 5,204,055, incorporated herein by reference,
describes an early three-dimensional printing technique that
involves the use of an ink-jet printing head to deliver a liquid or
colloidal binder material to layers of powdered material. The
three-dimensional ink-jet printing technique (hereafter
"liquid-binder method") involves applying a layer of a powdered
material to a surface using a counter roller. After the powdered
material is applied to the surface, the ink-jet printhead delivers
a liquid binder to the layer of powder. The binder infiltrates into
gaps in the powder material, hardening to bond the powder material
into a solidified layer. The hardened binder also bonds each layer
to the previous layer. After the first cross-sectional portion is
formed, the previous steps are repeated, building successive
cross-sectional portions until the final article is formed.
Optionally, the binder can be suspended in a carrier that
evaporates, leaving the hardened binder behind. The powdered
material can be ceramic, metal, plastic or a composite material,
and can also include fiber. The liquid-binder material can be
organic or inorganic. Typical organic binder materials used are
polymeric resins, or ceramic precursors such as polycarbosilazane.
Inorganic binders are used where the binder is incorporated into
the final articles; silica is typically used in such an
application.
[0005] In the technology of ink-jet printing, there are a number of
different types of printheads distinguished by the mechanism by
which ink is ejected onto the printing plane. The two broadest
classes of printheads are called, "continuous-jet" and
"drop-on-demand." In a continuous-jet printhead, a liquid ink or
binder is projected continuously through a nozzle. To print
segmented lines, the jet is deflected alternatively onto the print
plane or in to a collector that masks the printing plane. In a
drop-on-demand printhead, ink or binder is ejected when it is
needed by sending an impulse, most usually electrical, that causes
an actuator in the printhead to eject a droplet of ink or binder
onto the print plane.
SUMMARY
[0006] The use of liquid-binder printing techniques with a thermal
(bubble) printhead can present reliability problem associated with
the spray nozzle becoming clogged with the binder material.
Clogging can occur when binders having high levels of solids are
used. The problem with clogging requires frequent interruptions of
the build in order to clean the spray nozzle; this problem also
increases the time and labor required to build parts and to
maintain the equipment. Therefore, although the liquid-binder
printing technique represents an advance in speed and cost over the
selective laser-sintering process, it suffers from reliability
problems that slow down the build rate, increasing labor and
equipment maintenance costs. This problem interferes with the
potential speed advantage of increased printing capability
presented by the plurality of spray nozzles.
[0007] The materials for fabricating three-dimensional objects lead
to a materials system and method that produce both appearance
models and small numbers of functional parts in an office
environment. The materials system can include at least one solid
filler and a liquid binder composition. Particular binder
compositions can be effectively deposited using an
electromechanical printhead having suitable components. The
fabrication methods can be quick, reliable, safe, and
inexpensive.
[0008] An article can be made of a mixture of particles including
adhesive and at least one filler. The adhesive may be activated by
a fluid including a solvent. Optionally, the binder can also
include various processing aids or additions that modify the
working properties of the fluid and adhesive or that enhance the
mechanical properties of the finished article. The mixture of
particles can also optionally include particles of fiber and
various processing aids. The activated adhesive causes the filler
particles to adhere together, and to adhere to previously formed
adjacent layers. Adhesive can be supplied to the article by coating
it on the fiber and/or filler, by directly mixing it with the fiber
and filler before delivering the fluid and/or by dissolving or
mixing the adhesive in the fluid before the fluid is delivered to
the mixture of particles.
[0009] A particular method for producing such articles can include
applying a layer of the above-mentioned mixture onto a flat surface
that can be indexed downward. Cross-sectional portions of an
article can be defined by delivering an activating fluid, the
adhesive, to the layer of the mixture of particles in a
predetermined two-dimensional pattern. The fluid activates the
adhesive, and the activated adhesive causes the particles to adhere
together in an essentially solid layer. After the first
cross-sectional portion of the article is formed, the movable
surface can be indexed downward by an amount corresponding to the
desired layer thickness. Successive layers of the mixture of
particles are applied to previous layers in the same manner.
Application of the fluid using an electromechanical ink-jet print
head follows the application of each successive layer of the
mixture of particulate material.
[0010] Depositing a layer of the mixture of particulate material
and delivering the fluid to the layer can be repeated until the
required number of cross-sectional portions have been built,
completing formation of the article. After formation of the article
has been completed, it typically remains immersed in a bed of
unbound particulate material, where it can remain until the article
is completely dry. Delicate features of the article remain
supported by the unbound particulate material while drying. The
finished article can then be removed from the bed of unbound
particulate material and any excess unbound particulate material
clinging to the finished article can be removed by a suitable
cleaning process. For example, excess powder can be removed by
vacuuming it off the article, by blowing it off the article, and by
brushing to remove any powder left in crevices. In addition, the
finished article can be placed in an oven for more rapid
drying.
[0011] After cleaning, optional post-processing actions can include
heat-treating, resin or wax infiltration, painting and sanding.
Heat treating and infiltration can increase the strength and
durability of the finished article. Infiltration can reduce
porosity, making the article water resistant and more readily
sanded. Painting the article can provide a more aesthetically
pleasing appearance, and may also contribute to the strength and
water resistance of the final articles. Sanding improves the
surface smoothness, reducing any surface irregularities caused, for
example, by fiber penetrating through the surface. Parts can be
glued or fastened, or used as patterns for subsequent molding
operations.
[0012] Various materials systems and methods offer the advantages
of being able to fabricate relatively complex shapes reliably,
quickly, safely and inexpensively compared to the selective
laser-sintering and liquid-binder methods. Because various
materials used in the present system present little or no problems
with clogging, higher reliability can be offered relative to prior
art methods, particularly prior art methods in which high levels of
suspended solids are contained in the binder. The higher
reliability results in reduced build times compared with prior art
methods. Further, embodiments can be made and practiced more
economically than prior art methods because inexpensive equipment
and materials can be used, and the high reliability associated with
materials and methods reduces cost even further. In addition,
because non-toxic materials can be used, these methods can be
carried out safely in a typical office environment.
[0013] Additionally, the use of electromechanical ink-jet
printheads to deliver the fluid compositions allows for the
incorporation of thermally-sensitive adhesives in the fluid due to
the fact that electromechanical ink-jet printheads typically
operate at ambient-temperature. Further, fluids with a large amount
of dissolved or suspended solids subject to degradation with
temperature excursions can likewise be better accommodated by an
electromechanical printhead relative to a thermal printhead. The
use of fluids with higher solids content with an electromechanical
printhead further allows for the formation of materials that will
shrink less (due to fewer escaping components) and that have higher
strength and greater dimensional stability than materials formed
with more dilute binders. Further still, the incorporation of
adhesives in the activating fluid and the delivery of that fluid to
the particulate bed allows for an increased amount of adhesive to
be incorporated into the final part.
[0014] The composition selectively adhere particulate material to
form a solid object in a three-dimensional printer. In one
embodiment, the composition comprises a nonaqueous organic
monomeric compound. That compound can include at least one of an
alcohol, an ester, an ether, a silane, a vinyl monomer, an acrylic
monomer, or a methacrylate monomer.
[0015] The composition can include a solvent and a solute, and in
one embodiment, the compound is the solvent. The solvent can
include an alcohol such as methyl alcohol, ethyl alcohol,
isopropanol, or t-butanol. In alternative embodiments, the solvent
includes an ester that includes at least one of ethyl acetate,
dimethyl succinate, diethyl succinate, dimethyl adipate, or
ethylene glycol diacetate.
[0016] In alternative embodiments, the compound is a solvent for a
resin in the particulate material. The resin can include at least
one of shellac, polyvinyl pyrrolidone, polyvinyl acetate, polyvinyl
alcohol, polystyrene, styrene-butadiene copolymer, or
acrylonitrile-butadiene-styr- ene copolymer.
[0017] Additionally, organic acids and sugars such as sucrose,
dextrose, malic acid, and sodium citrate, and other compounds such
as urea and hydrolized amino acids can be used as solutes in water
solution. These compounds bind the particulate material together by
drying in the powder, and not have any appreciable solvent
character on their own.
[0018] The monomeric compound can include a mixed monomer
vinyl-silane and can include vinyltriisopropoxysilane.
[0019] The acrylic monomer can include at least one of
tri(propylene glycol) diacrylate, ethylene glycol phenyl ether
acrylate, or 1,6 hexanediol diacrylate. The methacrylic monomer can
include at least one of 1,3 butylene glycol dimethacrylate,
neopentyl glycol dimethacrylate, butyl methacrylate, 1,6 hexanediol
dimethacrylate, or di(propylene glycol) allyl ether
methacrylate.
[0020] The compound can be curable, in combination with a
photoinitiator in a solid, by ultraviolet radiation having a
wavelength between about 320-500 nm and an energy density of about
1 joule/cm.sup.2.
[0021] The particulate material can include a filler that includes
an inorganic compound. In one embodiment, the filler includes at
least one of clay, aluminum oxide, silicon dioxide, aluminum
silicate, potassium aluminum silicate, calcium silicate, calcium
hydroxide, calcium aluminate, calcium carbonate, sodium silicate,
zinc oxide, titanium dioxide, or magnetite. A printing aid can be
dispersed throughout the filler. The printing aid can include at
least one of sorbitan trioleate, sorbitan mono-oleate, sorbitan
monolaurate, polyoxyethylene sorbitan mono-oleate, polyethylene
glycol, soybean oil, mineral oil, propylene glycol, fluroaklkyl
polyoxyethylene polymers, glycerol triacetate, polypropylene
glycol, ethylene glycol octanoate, ethylene glycol decanoate,
ethoxylated derivatives of 2,4,7,9-Tetramethyl-5-decyne-4,7-di- ol,
oleyl alcohol, or oleic acid.
[0022] A binder composition is also provided, which can include an
adhesive in combination with a fluid, for selectively adhering
particulate material to form a solid object in a three-dimensional
printer. In one embodiment, the adhesive can include a nonaqueous
organic monomeric compound.
[0023] In alternative embodiments, an adhesive for selectively
adhering particulate material to form a solid object in a
three-dimensional printer includes an anionically ionizable polymer
consisting of compounds selected from the group including
polymethacrylic acid, polymethacrylic acid sodium salt, and sodium
polystyrene sulfonate.
[0024] In other embodiments, the adhesive includes a cationic
polymer such as polyethyleneimine and polydiallyldimethylammonium
chloride. In other embodiments, the adhesive includes a nonionic
polymer. The polymer can include at least one of polyvinyl
pyrrolidone, polyvinyl pyrrolidone copolymer with polyvinyl
acetate, polyvinyl alcohol, polyvinyl methyl ether, polyacrylamide,
or poly-2-ethyl-2-oxazoline. In yet other embodiments, the adhesive
includes a polymer selected from the group consisting of
polymethacrylic acid, polymethacrylic acid sodium salt, sodium
polystyrene sulfonate, and polyethyleneimine.
[0025] In further embodiments, the adhesive includes a waterborne
colloid such as polymethyl methacrylate, polystyrene, natural
rubber, polyurethane, polyvinyl acetate, and alkyd resins. In yet
other embodiments, the adhesive includes an inorganic solute
selected from the group consisting of sodium polyphosphate, sodium
tetraborate, sodium chloride, ammonium nitrate, potassium sulfate,
ammonium chloride, and calcium formate.
BRIEF DESCRIPTION OF THE DRAWINGS
[0026] FIG. 1 schematically illustrates a first layer of a mixture
of particulate material deposited onto a downwardly movable surface
on which an article is to be built, before any fluid has been
delivered;
[0027] FIG. 2 schematically illustrates an electromechanical
ink-jet nozzle delivering an activating fluid to a portion of the
layer of particulate material of FIG. 1 in a predetermined
pattern;
[0028] FIG. 3 schematically illustrates a view of a final article
made from a series of steps illustrated in FIG. 2 enclosed in the
container while it is still immersed in the loose unactivated
particles;
[0029] FIG. 4 schematically illustrates a view of the final article
from FIG. 3.
[0030] The foregoing and other objects, features and advantages
will be apparent from the following more particular description of
embodiments, as illustrated in the accompanying drawings in which
like reference characters refer to the same parts throughout the
different views. The drawings are not necessarily to scale,
emphasis instead being placed upon illustrating the principles of
the invention.
DETAILED DESCRIPTION
[0031] A materials system for three-dimensional printing comprises
a mixture of particles including a filler and possibly an adhesive.
The materials system can also include a fibrous component, a
printing aid for reducing edge curl due to uneven curing of the
adhesive and resultant distortion of a part that is
three-dimensionally printed, and an activating fluid comprising
additional adhesive and a solvent that activates the adhesive. The
activating fluid can also include such processing aids as a
humectant, a flowrate enhancer, and a dye. The fluid activates the
adhesive in the particulate mixture, adhesively bonding the
material together to form an essentially solid article.
[0032] FIG. 1 schematically illustrates a first layer of a mixture
of particulate material deposited onto a downwardly movable surface
on which an article is to be built, before any fluid has been
delivered. According to the method, a layer or film of particulate
material 20 is applied on a downwardly movable surface 22 of a
container 24. The layer or film of particulate material can be
formed in any manner; in one embodiment, the particulate material
is applied using a counter roller. The particulate material applied
to the surface includes a filler and, possibly, adhesive.
[0033] As used herein, "adhesive" is meant to define a component
that forms the primary adhesive bonds in the mixture of material
between portions of the mixture that were separate prior to
delivery of the activating fluid. The adhesive can be included both
in the particle mixture and in the activating fluid. As used
herein, a "filler" is meant to define a component that is solid
prior to application of the activating fluid, which is
substantially less soluble in the fluid than the adhesive, and
which gives structure to the final article.
[0034] According to a particular embodiment, the particulate
mixture includes a reinforcing fiber, or a reinforcing fibrous
component, added to provide structural reinforcement to the final
article. The particulate material may include a plurality of
particles of mean diameter of about 10-300 microns. As used herein,
"fiber" or "fibrous component" is meant to define a component that
is solid prior to application of the activating fluid, which can be
but is not necessarily insoluble in the fluid, that is added to
increase the final article strength. The reinforcing fiber length
is restricted to a length approximately equal to the thickness of
the layer of particulate mixture. The reinforcing fiber is
typically about 60 to about 200 microns in length, and is included
in an amount not greater than 20 percent, by weight, of the total
mixture.
[0035] Additionally, a stabilizing fiber can be added to the filler
to provide dimensional stability to the final article, as well as
to slightly increase the article strength. Spreading the
particulate mixture with the counter roller becomes increasingly
difficult as friction caused by an excess of stabilizing fiber in
the mixture increases, reducing the packing density. Restricting
both the amount and length of the stabilizing fiber increases the
packing density of the mixture resulting in finished parts of
greater strength. The stabilizing fiber may be restricted to a
length of less than half of the reinforcing fiber, in an amount not
greater than 30 percent, by weight, of the total mixture. Optimal
values can be determined with routine experimentation using, for
example, a counter roller.
[0036] According to another particular embodiment, a printing aid
in the form of an emulsifier, such as sorbitan trioleate
(commercially available as SPAN 85 from Sigma Chemical Co., St.
Louis, Mo. USA), can be added to the particulate mixture to prevent
distortions in printing. The printing aid prevents fine particles
of the mixture from becoming airborne while the fluid is dispensed
from the print head which would distort the printed article.
Lecithin, which also serves as a printing aid can be used as
well.
[0037] The composition of the particulate mixture and fluid
(binder) of a particular embodiment using a polymer solution as the
adhesive is provided in Table 1, below. The composition of the
particulate mixture and fluid (binder) of a particular embodiment
using a colloidal suspension as the adhesive is provided in Table
2, below.
1TABLE 1 Example Example Particle Particular Composition
Composition Size Ingredient Compound Range (W/W) (W/W) Range
(.mu.m) Particulate Mixture Adhesive sucrose 10-50% 30% 10
Reinforcing cellulose 0-20% 10% 100 Fiber Filler maltodextrin 0-80%
50% <300 (dextrose equivalent = 5) Stabilizing cellulose 0-30%
10% 60 Fiber Printing lecithin 0-3% 0.27% N/A Aids sorbitan 0-3%
0.03% N/A trioleate Fluid Solvent water 20-88% 68% N/A Solvent
isopropyl 0-5% 1% N/A alcohol water-sol. sulfonated 10-50% 25% N/A
adhesive polystyrene Humectant glycerol 0-15% 5% N/A Flowrate
diethylene 0-10% 1% N/A Enhancer glycol mono- butyl ether Dye
naphthol 0-0.1% 0.1% N/A blue-black
[0038]
2TABLE 2 Example Example Particle Particular Composition
Composition Size Ingredient Compound Range (W/W) (W/W) Range
(.mu.m) Particulate Mixture Adhesive sucrose 10-50% 30% 10
Reinforcing cellulose 0-20% 10% 100 Fiber Filler maltodextrin 0-80%
50% <300 (dextrose equivalent = 5) Stabilizing cellulose 0-30%
10% 60 Fiber Printing lecithin 0-3% 0.27% N/A Aids sorbitan 0-3%
0.03% N/A trioleate Fluid Suspending water 20-88% 72% N/A Fluid
Solvent isopropyl 0-5% 1% N/A alcohol Colloid polyvinyl 10-50% 20%
50-500 nm Adhesive acetate Inorganic acetic acid 0-2% 1% N/A Buffer
Humectant glycerol 0-15% 5% N/A Flowrate diethylene 0-10% 1% N/A
Enhancer glycol mono- butyl ether Dye naphthol 0-0.1% 0.1% N/A
blue-black
[0039] FIG. 2 schematically illustrates an electromechanical
ink-jet nozzle delivering an activating fluid to a portion of the
layer of particulate material of FIG. 1 in a predetermined pattern.
The fluid 26 is delivered to the layer or film of particulate
material in any predetermined two-dimensional pattern (circular, in
the figures, for purposes of illustration only), using any
convenient mechanism, such as a drop-on-demand (hereinafter "DOD")
electromechanical printhead driven by customized software which
receives data from a computer-assisted-design (hereinafter "CAD")
system as described in greater detail in U.S. application Ser. No.
09/416,707, which is incorporated herein by reference in its
entirety. Examples of suitable piezoelectric printheads include the
Tektronix PHASOR 340 printhead by Xerox (Stanford, Conn. USA), the
PJN 320 printhead from PicoJet, Inc. (Hillsboro, Oreg. USA), and
the EPSON 900 printhead from Epson America, Inc. (Portland, Oreg.
USA). A suitable solenoid valve printhead is the 1200 Hz INKA
printhead from The Lee Co. (Westbrook, Conn. USA).
[0040] In one embodiment, where adhesive is mixed with the other
particles, the first portion 30 of the particulate mixture is
activated by the fluid, causing the activated adhesive to adhere
the particles together to form an essentially-solid circular layer
that becomes a cross-sectional portion of the final article. As
used herein, "activates" is meant to define a change in state from
essentially inert to adhesive. When the fluid initially comes into
contact with the particulate mixture, it immediately flows outward
(on the microscopic scale) from the point of impact by capillary
action, dissolving the adhesive in the particulate mixture within
the first few seconds. A typical droplet of activating fluid has a
volume of about 50 pL, and spreads to about 100 microns once it
comes into contact with the particulate mixture. As the solvent
dissolves the adhesive, the fluid viscosity increases dramatically,
arresting further migration of the fluid from the initial point of
impact.
[0041] An adhesive can be dissolved, suspended, or otherwise
included in the activating fluid before delivery, in addition to
being in the powder mixture. The adhesive that is pre-mixed with
the activating fluid will already be activated when delivered to
the powder mixture and will adhere filler and other particles to
form a solid, agglomerated structure, as described above.
[0042] Within a few minutes after the activating fluid is delivered
to the particulate mixture, the fluid (with adhesive dissolved or
suspended therein) infiltrates the less-soluble and slightly-porous
particles, forming adhesive bonds between the filler and the fiber.
The activating fluid is capable of bonding the particulate mixture
in an agglomerated mass that is several times the mass of a droplet
of the fluid. As volatile components of the fluid evaporate, the
adhesive bonds harden, joining the filler and, optionally, fiber
particulates into a rigid structure, which becomes a
cross-sectional portion of the finished article.
[0043] Any portion of the particulate mixture 32 that was not
exposed to the fluid remains loose and free-flowing on the movable
surface. The unbound particulate mixture can be left in place until
formation of the final article is complete. Leaving the unbound,
loose-particulate mixture in place ensures that the article is
supported during processing, allowing features such as overhangs,
undercuts, and cavities (not illustrated, but conventional) to be
defined without using support structures. After formation of the
first cross-sectional portion of the final article, the movable
surface is indexed downward.
[0044] Using, for example, a counter-rolling mechanism, a second
film or layer of the particulate mixture is then applied over the
first, covering both the rigid first cross-sectional portion, and
any loose particulate mixture by which it is surrounded. A second
application of fluid follows in the manner described above, forming
adhesive bonds between a portion of the previous cross-sectional
portion, the filler, and, optionally, fiber of the second layer,
and hardening to form a second rigid cross-sectional portion added
to the first rigid cross-sectional portion of the final article.
The movable surface is again indexed downward.
[0045] The previous steps of applying a layer of particulate
mixture, applying the fluid, and indexing the movable surface
downward are repeated until the final article is completed.
[0046] FIG. 3 schematically illustrates a view of a final article
made from a series of steps illustrated in FIG. 2 enclosed in the
container while it is still immersed in the loose unactivated
particles. The final article can be completely immersed in a bed 36
of unactivated particulate material. Alternatively, those skilled
in this art would know how to build an article in layers upward
from an immovable platform, by successively depositing, smoothing
and printing a series of such layers.
[0047] FIG. 4 schematically illustrates a view of the final article
from FIG. 3. The unactivated particulate material can be removed by
blown air or a vacuum. After removal of the unactivated particulate
material from the final article 38, post-processing treatment may
be performed, including cleaning, infiltration with stabilizing
materials, painting, etc.
[0048] The method of the present invention is capable of producing
features on the order of about 250 .mu.m. The accuracy achieved by
the method of the present invention is in the range of about +/-250
.mu.m. Shrinkage of the final article is about 1%, which can easily
be factored into the build to increase accuracy.
Adhesive
[0049] The adhesive is a compound selected for the characteristics
of high solubility in the activating fluid, low solution viscosity,
low hygroscopicity, and high bonding strength. The adhesive should
be highly soluble in the solvent in order to ensure that it is
incorporated rapidly and completely into the activating fluid. Low
solution viscosity can be used to ensure that activating fluid
having adhesive dissolved therein will migrate quickly to sites in
the powder bed to adhesively bond together the reinforcing
materials. If the adhesive is naturally a solid, the adhesive can
be milled as finely as possible prior to mixing with the filler
and/or activating fluid and/or prior to coating the filler
particles. The fine particle size enhances the available surface
area, enhancing dissolution in the solvent, without being so fine
as to cause "caking", an undesirable article characteristic.
Typical adhesive particle grain sizes are about 5-50 .mu.m. Low
hygroscopicity of an adhesive used in the particulate mixture
avoids absorption of excessive moisture from the air, which causes
"caking", in which unactivated powder spuriously adheres to the
outside surface of the part, resulting in poor surface
definition.
[0050] Various types of adhesives that can be used with this
invention are further and more specifically described under the
section entitled, "Activating Fluid," below.
Filler
[0051] The filler of the present invention is a compound selected
for the characteristics of insolubility in the activating fluid, or
extremely low solubility in the activating fluid, rapid wetting,
low hygroscopicity, and high bonding strength. The filler provides
mechanical structure to the hardened composition. Sparingly soluble
filler material is used in particular, although insoluble filler
material can also be used. The filler particles become adhesively
bonded together when the adhesive dries/hardens after the
activating fluid has been applied. The filler can include a
distribution of particle grain sizes, ranging from the practical
maximum of about 200 .mu.m downward, to the practical minimum of
about 5 .mu.m. Large grain sizes appear to improve the final
article quality by forming large pores in the powder through which
the fluid can migrate rapidly, permitting production of a more
homogeneous material. Smaller grain sizes serve to reinforce
article strength.
[0052] Compounds suitable for use as the filler of the present
invention can be selected from the same general groups from which
the adhesive is selected, provided that the solubility,
hygroscopicity, bonding strength and solution viscosity criteria
described above are met. Examples of such fillers, which can be
used alone or in combination, include starches such as
maltodextrin, clay, cellulose fiber, glass, limestone, gypsum,
aluminum oxide, aluminum silicate, potassium aluminum silicate,
calcium silicate, calcium hydroxide, calcium aluminate, and sodium
silicate; metals; metal oxides such as zinc oxide, titanium
dioxide, and magnetite (Fe.sub.3O.sub.4); carbides such as silicon
carbide; and borides such as titanium diboride. In other
embodiments, the filler is limestone, which can be used alone or in
combination with other inorganic fillers. For example, the filler
can be a combination of plaster (0-20%), limestone (calcium
carbonate) (40-95%) and glass beads (0-80%). Generally the filler
materials are selected on the basis of their ability to bond with
the adhesive components, combined with the spreading
characteristics of the dry powder. The selection of the solvent
also typically determines which filler can be used.
Reinforcing Fiber
[0053] The reinforcing fiber can be insoluble or can dissolve
substantially slower in the fluid than the adhesive dissolves. The
reinforcing fiber is a stiff material chosen to increase the
mechanical reinforcement and dimensional control of the final
article without making the powder too difficult to spread. In order
to promote wetting of the reinforcing fibers, the chosen fibers
have a high affinity for the solvent. A particular embodiment
includes a fiber length approximately equal to the layer thickness,
which provides the greatest degree of mechanical reinforcement.
Using longer fibers adversely affects the surface finish, and using
too much fiber of any length can make spreading of the powder
increasingly difficult. Fibrous material suitable for reinforcing
the present invention includes, but is not limited to polymeric
fiber, ceramic fiber, graphite fiber and fiberglass. The polymeric
fiber may be cellulose and cellulose derivatives or substituted or
unsubstituted, straight or branched, alkyl or alkene, including
monomers up to eight carbon atoms in length. Specific useable
fibrous materials include, but are not limited to cellulose fiber,
silicon carbide fiber, graphite fiber, aluminosilicate fiber,
polypropylene fiber, fiberglass, nylon, and rayon.
[0054] As indicated in Table 1, both the reinforcing fiber and the
stabilizing fiber are can be cellulose. Some of the useful
properties of cellulose making it particularly suitable for use in
connection with the invention are low toxicity, biodegradability,
low cost and availability in a wide variety of lengths.
[0055] Further considerations when selecting the adhesive, filler
and fiber depend on the desired properties of the final article.
The final strength of the finished article depends largely on the
quality of the adhesive contacts between the particles of the
mixture, and the size of the empty pores that persist in the
material after the adhesive has hardened; both of these factors
vary with the grain size of the particulate material. In general,
the mean size of the grains of particulate material should not be
larger than the layer thickness. A distribution of grain sizes
increases the packing density of the particulate material, which in
turn increases both article strength and dimensional control.
Printing Aid
[0056] As indicated in Table 1, sorbitan trioleate (SPAN 85) is
used as a printing aid in the exemplary particulate mixture.
Sorbitan trioleate is a liquid which is only slightly soluble in
water. By adding a small amount to the powder, the sorbitan
trioleate provides a light adhesion between powder grains before
printing, thereby reducing dust formation. After printing, the
sorbitan trioleate continues to adhere insoluble grains together
for a short time until it dissolves. This effect tends to reduce
distortion in printed layers in the brief time that is required for
the adhesive to dissolve and redistribute in the powder.
Hydrophillic grades of lecithin are particularly suitable. A wide
variety of other liquid compounds work for the same purpose.
Polypropylene glycol (PPG), especially with a molecular weight of
about 400, and citronellol are two examples. Other suitable
printing aides include ethylene glycol octanoate, ethylene glycol
decanoate, and ethoxylated derivatives of
2,4,7,9-Tetramethyl-5-decyne-4,7-diol. Sorbitan trioleate can be
used in combination with lethicin, which also functions as a
printing aid. Other liquid compounds that can be used as printing
aids include sorbitan mono-oleate, sorbitan monolaurate,
polyoxyethylene sorbitan mono-oleate, polyethylene glycol, soybean
oil, mineral oil, propylene glycol, fluroalkyl polyoxyethylene
polymers, glycerol triacetate, oleyl alcohol, and oleic acid.
Activating Fluid
[0057] The fluid of the present invention is selected to comport
with the degree of solubility required for the various particulate
components of the mixture, as described above. The fluid includes a
solvent in which the adhesive is active, particularly soluble, and
can include processing aids such as a humectant, a flowrate
enhancer, and a dye. An ideal solvent is one in which the adhesive
component of the powder is highly soluble, and in which both the
filler and fiber are substantially less soluble. The solvent can be
aqueous or non-aqueous, although aqueous solvents offer some
advantages. Suitable solvents can be selected from the following
non-limiting list: water, methyl alcohol, ethyl alcohol,
isopropanol, t-butanol, ethyl acetate, dimethyl succinate, diethyl
succinate, dimethyl adipate, and ethylene glycol diacetate.
[0058] The activating fluid, which can have adhesive pre-mixed, is
also referred to as the "binder." The function of the binder is to
infiltrate the insoluble or semi-soluble particle mixture and to
bond the grains together. The activating fluid, with adhesive
included, can belong to any one of the following classes: (1)
polymer solutions, (2) colloidal suspensions, (3) inorganic (salt)
solutions, (4) organic monomeric solutions, (5) non aqueous
liquids. Classes 1-4 can be aqueous. The following description of
particular fluids and adhesives are not meant to be limiting, other
suitable compounds may be used in place of or in combination with
the listed compounds.
[0059] There also exists a collection of water-based compounds that
have been found to work particularly well in electromechanical
printheads. In the first category, a water-soluble polymer can be
dissolved in the binder to form a relatively low viscosity
solution. Of these, there are a few particularly suitable polymers.
These are anionically ionizable polymers, cationic polymers and
nonionic polymers. The anionically ionizable polymers include
polymethacrylic acid, polymethacrylic acid sodium salt, and sodium
polystyrene sulfonate. The cationic polymers include
polyethyleneimine and polydiallyldimethyl ammonium chloride. As a
class, polyethyleneimine comes in two forms, linear and branched,
both of which are useful. The nonionic soluble polymers that are
particularly useful as binders are polyvinyl pyrrolidone, polyvinyl
pyrrolidone copolymer with polyvinyl acetate, polyvinyl alcohol,
polyvinyl methyl ether, polyacrylamide, and
poly-2-ethyl-2-oxazoline.
[0060] In a typical embodiment, a low molecular weight polymer such
as sodium polystyrene sulfonate is dissolved in water to form a
solution containing approximately 20% solids by weight. A cosolvent
such as isopropyl alcohol, at approximately 1% to 5% by weight, can
modify the viscosity of the solution by controlling the
conformation of the polymer chains in solution. A humectant such as
glycerol used at approximately 5% to 10% will reduce the tendency
of the binder to dry in the printhead. Other solution parameters
such as pH and salt concentration may be used to modify flow
properties. Added salts tend to lower the viscosity of binders that
include a polyelectrolyte, such as sodium chloride, sodium
phosphate, sodium sulfate, and potassium sulfate.
[0061] In the second category, colloidal suspensions of materials
can be used as binders in three-dimensional printing. Organic
latexes such as polymethyl methacrylate, polystyrene, styrenated
polyacrylic acid, natural rubber, polyurethane latex, polyvinyl
acetate latex, and alkyd resin latex are materials that can be
applied to the process. Additionally, inorganic suspensions such as
colloidal alumina, clay, and colloidal graphite could all be used
to for solid articles containing substantial amounts of these
technologically important materials. The advantage of using a
colloid over a solution is that a very large content of solid
materials can be suspended without greatly increasing the viscosity
of the fluid.
[0062] The first two classes do not necessarily exclude one
another. Very often, a soluble polyelectrolyte will be used to
stabilize a suspension of solid particles. The polyelectrolyte will
contribute to the structure of the finished article in addition to
the dispersed particles.
[0063] A typical embodiment of a colloid-based binder comprises a
polyvinyl acetate including approximately 30% solids. Additional
additives such as triethanolamine at 2% to 5% by weight are used to
control the pH of the suspension. Additionally, a humectant such as
glycerol at 5% to 10% is used to reduce the tendency of the latex
to dry in the printhead during idle periods.
[0064] In the third category, inorganic solutes can be dissolved in
an aqueous solvent and printed as a binder. Glass-forming solutes
such as sodium silicate, sodium polyphosphate and sodium
tetraborate can be used to deposit a ceramic binder in a finished
article. This ceramic binder could be fused in a subsequent heat
treatment into a glass-bonded ceramic. Other inorganic solutes that
could be printed include sodium chloride, ammonium nitrate, and
potassium sulfate, ammonium chloride, and calcium formate.
[0065] Inorganic solutes participate in acid-base reactions. For
example, sodium hydrogen phosphate solution could be printed onto
powdered calcium carbonate. The acid binder etches the alkaline
powder and forms calcium phosphate that recrystallizes and cements
together the grains of powder. Another example is sodium silicate,
which can be printed in a binder solution and can react with, for
example, gypsum plaster to form calcium silicate.
[0066] In the fourth category, a solution of monomeric organic
compounds can be printed through an electromechanical
drop-on-demand printhead for three-dimensionally printed articles.
These monomeric organic compounds generally fall into several broad
classes: alcohols, esters, ethers, silanes, vinyl monomers, acrylic
monomers, and methacrylate monomers.
[0067] Alcohols and esters that have been found to function well as
the solvent phase, in addition to functioning as a solute in
another solvent (usually water) are: methyl alcohol, ethyl alcohol,
isopropanol, t-butanol, ethyl acetate, dimethyl succinate, diethyl
succinate, dimethyl adipate, and ethylene glycol diacetate. These
materials act as solvents for resins in the powder bed.
[0068] Resins that have been found to work in a 3-D printer are:
shellac, polyvinyl pyrrolidone, polyvinyl acetate, polyvinyl
alcohol, polystyrene, styrene-butadiene copolymer, and
acrylonitrile-butadiene-styrene copolymer. These resins can be used
in combination with any filler, or they can be used by themselves.
A particularly suitable combination is 100% dimethyl succinate
binder printed over a powder of 100%
acrylonitrile-butadiene-styrene copolymer.
[0069] The other monomers contain active sites for polymerization,
and possess mixed characteristics. The classes of polymerizable
monomers are the vinyl monomers, acrylic monomers, and methacrylate
monomers. A exemplary mixed vinyl-silane monomer is
vinyltriisopropoxysilane. Acrylic monomers include tri(propylene
glycol) diacrylate, ethylene glycol phenyl ether acrylate, and 1,6
hexanediol diacrylate. Methacrylates include 1,3 butylene glycol
dimethacrylate, neopentyl glycol dimethacrylate, butyl
methacrylate, 1,6 hexanediol dimethacrylate, and di(propylene
glycol) allyl ether methacrylate.
[0070] In addition, there are some proprietary monomers of unknown
character that have been found to print well. These are
manufactured by Sartomer Co. of Exton, Pa., with designations SR
521, SR 516, and CN 131. These materials are reactive, and when
mixed with a photoinitiator, they can be solidified by applying
ultraviolet radiation. A particularly suitable binder formula for
this polymerizable class is 99% neopentyl glycol dimethacrylate
mixed with 1% of Sartomer product # KT046 as a photoinitiator. Any
of the above-listed monomers can be made to work, but this formula
yields a suitable flow through the printhead and suitable
reactivity. The radiation necessary to cure these materials is
ultraviolet light with a wavelength of 363-378 nm and an energy
density of 1 joule/cm.sup.2. A particularly suitable powder formula
for this mixture is given in Table 1, above.
[0071] Additionally, there are organic acids and sugars: sucrose,
dextrose, malic acid, and sodium citrate, and other compounds such
as urea and the hydrolyzed amino acids that can be used as solutes
in water solution. These compounds would bind by drying in the
powder, and not have any appreciable solvent character on their
own. In addition, reactive monomers, such as melamine-formaldehyde,
can be printed in a liquid solution and later polymerized by heat,
by an initiator, or by actinic radiation such as ultra-violet
radiation.
[0072] The fifth class includes members that can be used with
electromechanical printheads that are designed for printing molten
wax, such as the Tektronix Phasor 340 printhead (which includes a
temperature control). In this category, a room temperature solid
such as wax can be used by itself or to replace water as a medium
to convey the primary adhesives discussed in categories 1-4. The
wax itself would serve as an adhesive to cement together powder
particles. Binders formulated from these materials would be
appropriate for electromechanical printheads that work at elevated
temperatures. At these operating temperatures, the binder would
become fluid and could then be used in the three-dimensional
printing process.
[0073] Typical wax-based binder formulations would include waxes
with a low melt viscosity (less than 100 centipoise) such as
different grades of natural mineral, or refined waxes. Examples
include but are not limited to carnauba wax beeswax, ceresine,
ozokerite, montan, orlcury wax, paraffin, and microcrystalline wax.
The waxes can be chemically modified to include reactive groups
such as alcohols, organic acids, alcohol oxazolates, and urethane
derivatives. To modify binder material properties such as melting
point, melt viscosity, toughness and hardening rate, as well as to
increase compatibility with added components, the waxes can be
blended or compounded with resins, oils, and other polymers.
Additional components include rosin, fatty acids, fatty acid salts,
mono and diglycerides, mineral oils, and turpentines. Resins
include polyethylene, polypropylene, polybutadiene, polyethylene
oxide, polyethylene glycol, polymethyl methacrylate,
poly-2-ethyl-oxazoline, polyvinylpyrrollidone, polyacrylamide, and
polyvinyl alcohol.
[0074] Adhesives in members of the first class (polymer solutions)
and the second class (inorganic solutions) will often adsorb water
if left exposed to ambient atmosphere. However, these adhesives
will generally perform with greater reliability and efficacy if
maintained in either a completely dry or wet state. By
incorporating the adhesives in the liquid binder, they can thereby
be maintained in a wet state and therefore exhibit the desired
reliability and efficacy.
Humectant
[0075] A humectant can be included in the inventive mixture to
retard evaporation of the solvent from the printed material, and to
prevent drying/clogging of the printhead delivery system. Glycerol
is a particularly suitable humectant when the solvent is aqueous.
Other polyhydric alcohols, including but not limited to ethylene
glycol, diethylene glycol, and propylene glycol, are also known in
the art to retard evaporation. Additional humectants include
thiodiethanol, n-methyl pyrrolidinone, and dimethyl hydantoin.
Flowrate Enhancer
[0076] A flowrate enhancer can be included that has some humectant
properties, but serves mainly to alter the hydrodynamic properties
or wetting characteristics of the fluid to maximize the volume of
fluid delivered by the printhead. Flowrate enhancement is thought
to be a viscoelastic phenomena increasing the flow rate of the
fluid, allowing thicker layers to be printed, thus allowing the
final article to be built more quickly. Specific compounds that
increase the flowrate of the fluid, either by reducing friction
between the fluid and the walls of the jet, or by reducing the
viscosity of the fluid, include ethylene glycol diacetate and
potassium aluminum sulfate. Other suitable compounds for use as the
flowrate enhancer can be selected from the following non-limiting
list: tetraethylene glycol dimethylether, isopropyl alcohol,
ethylene glycol monobutyl ether, diethylene glycol monobutyl ether,
dodecyl dimethylammoniopropane sulfonate, glycerol triacetate,
ethyl acetoacetate, and water-soluble polymers including polyvinyl
pyrrolidone with a molecular weight of about 30,000 units,
polyethylene glycol, polyacrylic acid, and sodium polyacrylate. For
the ionic polymers, such as sodium polyacrylate, the increase in
flow rate varies with pH. Salts that can be used to enhance
flowrate include potassium sulfate, potassium aluminum sulfate,
sodium hydrogen phosphate and sodium polyphosphate.
Dye
[0077] The fluid of the present invention can include a dye to
provide a visual aid to the operator while building the article.
The dye provides contrast between activated and unactivated powder
which allows the operator to monitor the printed layers while
building the article. The dye can be selected from the group
including, but not limited to, naphthol blue-black and direct red.
Other dyes that are compatible with the fluid can likewise be
used.
Additional Ingredients in the Activating Fluid
[0078] Cosolvents can be added to an aqueous solution to alter the
viscosity of a solution by altering the solvency of the liquid for
the solute. Long-chain molecules in solution conform themselves
either into extended chains or into coiled structures. If the
solvent has a high affinity for the solute, long molecules will
spread out causing the viscosity of the solution to be high. By
adding a cosolvent to the solution, the polymer can be come less
strongly attracted to other dissolved polymer molecules, and begin
to coil into compact balls. This tends to reduce the viscosity of a
polymer solution and allows more polymer to be dissolved.
Cosolvents include isopropanol, ethyl alcohol, ethylene glycol
monobutyl ether, butyrolactone and acetone.
[0079] Additives that control the pH of the binder, generally
called buffers, can impart increased stability to the adhesive
solutions and suspensions. Such materials include, but are not
limited to, potassium hydroxide, ammonia, ammonium chloride,
triethanolamine, sodium acetate, sodium gluconate, potassium
sulfate, potassium hydrogen sulfate, sodium aluminum sulfate, and
sodium tetraborate.
[0080] Wetting agents are substances that control the surface
tension of a liquid. These can be used to modify the spreading of
the liquid adhesive on the surfaces of the printhead mechanism.
These include, but are not limited to, sodium dodecyl sulfate,
sodium di-octyl sulfosuccinate, ethyl butyrate, diethylene glycol
monobutyl ether, polyethylene glycol alkyl ether, and sodium
p-toluene sulfonate.
[0081] Lubricants can be used to increase the rate at which liquid
binder passes through the nozzles of a printhead. Depending on the
materials of construction, substances such as glycerol triacetate,
polyethylene oxide, polypropylene glycol, ethyl acetoacetate,
diethyl succinate, and sodium polyacrylate can be used.
[0082] Additional substances can be used to promote the stability
of suspensions. Stabilizers include emulsifiers such as sorbitan
trioleate, polyoxyethylene mono-dodecyl ether, polyoxyethylene
sorbitan mono-oleate, and protective colloids such as
polyoxyethylene-co-polyoxypropylene, polyvinyl pyrrolidone,
polyacrylic acid, gelatin, and acacia gum.
[0083] The equipment used in the method of the present invention is
reliable, inexpensive, and easy to maintain, making it ideal for
use in an office environment. The materials used in the present
invention are capable of achieving much better performance in 3D
Printing than those presently used in the liquid binder method.
Thus, less equipment maintenance is required, and the reliability
of the equipment is increased. Therefore, methods of the present
invention can involve shorter build times and less labor than prior
art methods.
[0084] Those skilled in the art will readily appreciate that all
parameters listed herein are meant to be exemplary and actual
parameters depend upon the specific application for which the
methods and materials of the present invention are used. It is,
therefore, to be understood that the foregoing embodiments are
presented by way of example only and that, within the scope of the
appended claims and equivalents thereto, the invention can be
practiced otherwise than as specifically described.
* * * * *