U.S. patent application number 09/823108 was filed with the patent office on 2001-11-15 for laminated piezoelectric transformer.
This patent application is currently assigned to Taiyo Yuden Co., Ltd.. Invention is credited to Inomata, Yasuyuki, Ishii, Shigeo, Kishi, Hiroshi, Tsujikawa, Mitsuya, Watanabe, Yoshiyuki.
Application Number | 20010040420 09/823108 |
Document ID | / |
Family ID | 18610651 |
Filed Date | 2001-11-15 |
United States Patent
Application |
20010040420 |
Kind Code |
A1 |
Watanabe, Yoshiyuki ; et
al. |
November 15, 2001 |
Laminated piezoelectric transformer
Abstract
A piezoelectric transformer includes an output part having
laminated sheets formed of a first piezoelectric material and one
or more input parts, each having laminated sheets made of a second
piezoelectric material. The piezoelectric strain constant of the
second piezoelectric material is greater than that of the first
piezoelectric material.
Inventors: |
Watanabe, Yoshiyuki; (Tokyo,
JP) ; Kishi, Hiroshi; (Tokyo, JP) ; Inomata,
Yasuyuki; (Tokyo, JP) ; Ishii, Shigeo; (Tokyo,
JP) ; Tsujikawa, Mitsuya; (Tokyo, JP) |
Correspondence
Address: |
SHAHAN ISLAM, ESQ.
ROSENMAN & COLIN LLP
575 Madison Avenue
New York
NY
10022-2585
US
|
Assignee: |
Taiyo Yuden Co., Ltd.
16-20 Ueno-6chome, Taito-ku,
Tokyo
JP
110-0005
|
Family ID: |
18610651 |
Appl. No.: |
09/823108 |
Filed: |
March 30, 2001 |
Current U.S.
Class: |
310/311 ;
310/349; 310/366 |
Current CPC
Class: |
H01L 41/107
20130101 |
Class at
Publication: |
310/311 ;
310/349; 310/366 |
International
Class: |
H01L 041/18 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 30, 2000 |
JP |
2000-095796 |
Claims
What is claimed is:
1. A piezoelectric transformer comprising: an output part having
laminated sheets of a first piezoelectric material; and one or more
input parts, each having laminated sheets of a second piezoelectric
material, wherein a piezoelectric strain constant of the second
piezoelectric material is greater than that of the first
piezoelectric material.
2. The piezoelectric transformer according to claim 1, wherein the
piezoelectric transformer is of a step-down type having an input
voltage greater than an output voltage.
3. The piezoelectric transformer according to claim 1, wherein the
piezoelectric transformer has two input parts, the output part
being disposed between the two input parts.
4. A piezoelectric transformer comprising: a laminated body having
an output part and one or more input parts; and external
electrodes, wherein the output part includes sheets formed of a
first piezoelectric material and first internal electrodes, each of
the first internal electrodes being formed between every two
neighboring sheets of the first piezoelectric material and the
first internal electrodes being alternately exposed at first two
substantially opposite sides of the laminated body and wherein each
of the input parts includes sheets formed of a second piezoelectric
material and second internal electrodes, each of the second
internal electrodes is formed between every two neighboring sheets
of the second piezoelectric material and the second internal
electrodes are alternately exposed at second two substantially
opposite sides of the laminated body, and wherein the external
electrodes are separated from each other and formed on first and
second side surfaces, and wherein a piezoelectric strain constant
of the second piezoelectric material is greater than that of the
first piezoelectric material.
5. The piezoelectric transformer according to claim 4, wherein the
piezoelectric transformer is of a step-down type having an input
voltage greater than an output voltage.
6. The piezoelectric transformer according to claim 4, wherein the
laminated body has two input parts, the output part being disposed
between the two input parts.
Description
FIELD OF THE INVENTION
[0001] The present invention relates to a piezoelectric
transformer; and, more particularly, to a laminated piezoelectric
transformer for use in a converter and an adaptor.
BACKGROUND OF THE INVENTION
[0002] Piezoelectric transformers feature smaller sizes and easily
obtainable higher efficiencies than conventional electromagnetic
transformers. For such reasons, piezoelectric transformers are
gaining popularity as step-up transformers, e.g., backlight power
sources of liquid crystal display (LCD) monitors. However,
step-down transformers are more frequently used in power supplies
than step-up transformers.
[0003] It is preferable that a piezoelectric transformer have such
characteristics as high output power, less heat generation, small
size and high efficiency. However, increasing the output power of a
conventional piezoelectric transformer gives rise to the increased
heat generation, which in turn reduces the output power thereof.
The output power P of the piezoelectric transformer is represented
as follows: 1 P k 2 1 - k 2 V v 2
[0004] where k is an electromechanical coupling coefficient of a
secondary part of the piezoelectric transformer, .nu. is a
propagation velocity of a mechanical vibration and V is the volume
of the secondary part. If the temperature of the secondary part is
increased due to the increased heat generation, the
electromechanical coupling coefficient k of the secondary part
decreases and the output power P also decreases accordingly.
SUMMARY OF THE INVENTION
[0005] It is, therefore, a primary object of the present invention
to provide a piezoelectric transformer capable of generating a high
output power by suppressing heat generation therefrom.
[0006] In accordance with a preferred embodiment of the present
invention, there is provided a piezoelectric transformer
including:
[0007] an output part having laminated sheets of a first
piezoelectric material; and
[0008] one or more input parts, each having laminated sheets of a
second piezoelectric material, wherein a piezoelectric strain
constant of the second piezoelectric material is greater than that
of the first piezoelectric material.
[0009] In accordance with another preferred embodiment of the
present invention, there is provided a piezoelectric transformer
including:
[0010] a laminated body having an output part and one or more input
parts; and
[0011] external electrodes,
[0012] wherein the output part includes sheets formed of a first
piezoelectric material and first internal electrodes, each of the
first internal electrodes being formed between every two
neighboring sheets of the first piezoelectric material and the
first internal electrodes being alternately exposed at first two
substantially opposite sides of the laminated body and
[0013] wherein each of the input parts includes sheets formed of a
second piezoelectric material and second internal electrodes, each
of the second internal electrodes is formed between every two
neighboring sheets of the second piezoelectric material and the
second internal electrodes are alternately exposed at second two
substantially opposite sides of the laminated body, and
[0014] wherein the external electrodes are separated from each
other and formed on first and second side surfaces, and
[0015] wherein a piezoelectric strain constant of the second
piezoelectric material is greater than that of the first
piezoelectric material.
BRIEF DESCRIPTION OF THE DRAWINGS
[0016] The above and other objects and features of the present
invention will become apparent from the following description of
preferred embodiments given in conjunction with the accompanying
drawings, in which:
[0017] FIG. 1 shows a laminated structure of a piezoelectric
transformer in accordance with a first preferred embodiment of the
present invention;
[0018] FIG. 2 offers a perspective view of the piezoelectric
transformer in accordance with the first preferred embodiment of
the present invention;
[0019] FIGS. 3A-3C depict laminated structures of the piezoelectric
transformer of the present invention and exemplary conventional
piezoelectric transformers;
[0020] FIG. 4 provides a graph expressing the dependency of output
powers on corresponding load resistances for the piezoelectric
transformer of the present invention and exemplary conventional
piezoelectric transformers;
[0021] FIG. 5 presents a laminated structure of a piezoelectric
transformer in accordance with a second preferred embodiment of the
present invention;
[0022] FIGS. 6A and 6B illustrate cut configurations of the
piezoelectric transformer in accordance with the second preferred
embodiment of the present invention; and
[0023] FIGS. 7A and 7B represent schematic diagrams of a
piezoelectric transformer in accordance with a third preferred
embodiment of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0024] An output power of a piezoelectric transformer is basically
dictated by a mechanical vibration velocity thereof. Therefore, it
is preferable that large strain material having a large
piezoelectric strain constant be used as the piezoelectric material
in order to obtain a high vibration velocity which gives rise to a
high output power. In fact, however, the widely used piezoelectric
material is the one having a large mechanical quality factor (Qm)
capable of generating a large output power with a relatively small
strain. The use of such piezoelectric material satisfies the
requirements for obtaining a high output power with mild vibrations
in the piezoelectric transformer.
[0025] Many conventional piezoelectric transformers, such as Rosen
type piezoelectric transformers, operate using a longitudinal
vibration mode. Therefore, it is difficult to form the input and
output parts of a piezoelectric transformer by using different
materials. In a piezoelectric transformer, however, an electrical
signal is converted into a mechanical vibration at the input part
thereof and a mechanical vibration is converted into an electrical
signal at the output part thereof. Accordingly, it may be
preferable to choose a soft piezoelectric material at the input
part thereof since a soft piezoelectric material is more efficient
to convert the electrical signal into the mechanical vibration than
a hard piezoelectric material. At the output part thereof, it may
be preferable to adopt a hard piezoelectric material since the hard
piezoelectric hard material is more efficient in converting a
mechanical vibration into an electrical signal than a soft
piezoelectric material.
[0026] More specifically, since an electrical signal is converted
into a mechanical vibration at the input part of the piezoelectric
transformer, it is preferable to employ a material capable of
generating a large strain with the application of a low voltage at
the input part. Since a large strain material used in a
piezoelectric actuator or a piezoelectric acoustic device has a
large piezoelectric strain constant "d" and a large mechanical
quality factor Qm, it is called a soft piezoelectric material and
is preferably used for the input part of a piezoelectric
transformer.
[0027] Since the output part of a piezoelectric transformer serves
to generate an output power by converting a mechanical vibration
into an electrical signal, it is preferable to use a material
capable of generating a large electrical signal from a small input
strain. A high output power generation material having a large
mechanical quality factor Qm is preferably used for the output
part.
[0028] Requirements for preferable piezoelectric materials for the
input and the output parts of a transformer are summarized in Table
1 below.
1 TABLE 1 Dielectric constant (.epsilon.) Input part > Output
part Piezoelectric strain constant (d) Input part > Output part
Mechanical quality factor (Qm) Input part .ltoreq. Output part
[0029] As discussed above, in order to realize a piezoelectric
transformer capable of generating a large output power, different
material characteristics are required at the input and the output
parts of a piezoelectric transformer. In accordance with the
present invention, a high strain material and a high output power
generation material are used at the input and the output parts of a
piezoelectric transformer, respectively, thereby enhancing the
vibration velocity thereof and increasing the output power
thereof.
[0030] Referring to FIGS. 1 to 4, a first preferred embodiment of
the present invention will now be described. FIG. 1 shows a
laminated structure of a piezoelectric transformer in accordance
with the first preferred embodiment having an output part (power
generation part) 20 thereof located between two input parts 10
(vibrator part). At each of the lower and the upper input parts, a
first sheet 14 and a second sheet 16 are laminated, each sheet
having at substantially the center portion thereof an electrode 12
of, e.g., a circular shape. The number of sheets in each input
portion 10 can be more than two. There is formed at the internal
electrode 12 on the first sheet 14 a terminal portion 14A extended
to a rear edge of the sheet 14. Also formed at the internal
electrode 12 on the second sheet 16 is a terminal portion 16A
extended to a front edge of the sheet 16. Namely, the internal
electrodes 12 for each input part extend along the forward and
backward directions by the terminal portions 16A and 14A,
respectively.
[0031] At the output part 20, upper sheets 24 and lower sheets 26
are alternately laminated, wherein an internal electrode 22 having,
e.g., a circular shape is formed around a center portion on each of
the sheets 24 and 26. For example, six pairs of upper and lower
sheets (i.e., twelve sheets in total) are laminated.
[0032] At the internal electrode 22 on each upper sheet 24, there
is formed a terminal portion 24A extended to a right edge of the
sheet 24. Also formed at the internal electrode 22 on the lower
sheet 26 is a terminal portion 26A extended to a left edge of the
sheet 26. That is, the internal electrodes 22 are extended along
the right and the left directions by the terminal portions 24A and
26A, respectively.
[0033] Insulation sheets 30 for separating the input parts 10 from
the output part 20 are disposed therebetween as shown in FIG. 1.
Protection sheets 32 are provided on an uppermost sheet 14 and a
lowermost sheet 16, respectively.
[0034] High strain piezoelectric (PZT), e.g., green sheets having a
large dielectric constant ".epsilon.", a large piezoelectric strain
constant "d" and a small mechanical quality factor Qm are used for
the sheets 14 and 16 of the input parts 10. On the other hand, high
output power piezoelectric, e.g., green sheets having a small
dielectric constant ".epsilon.", a small piezoelectric strain
constant "d" and a large mechanical quality factor Qm are used for
the sheets 24 and 26 of the output part 20. An Ag or Pd alloy is
used as the internal electrodes 12, 22 and terminal portions 14A,
16A, 24A and 26A.
[0035] All the sheets constituting the piezoelectric transformer
are compressed after being stacked as shown in FIG. 1. Thereafter,
a binder removing and a sintering processes are performed and then
external electrodes are formed on the sintered body as shown in
FIG. 2. In this embodiment, the terminal portions 14A of the input
parts 10 are connected to an external electrode 40A and the
terminal portions 16A thereof are connected to an external
electrode 40B as illustrated in FIG. 2. The terminal portions 24A
of the output part 20 are connected to an external electrode 42A
and the terminal portions 26A thereof are connected to an external
electrode 42B.
[0036] The external electrodes 40A, 40B, 42A and 42B are formed of
a conductive material, e.g., Ag. Next, a poling of the sintered
body is performed through the use of external electrodes formed
thereon. For instance, the poling of the sintered body is achieved
by applying an electric field of 2 kV/mm between the external
electrodes 40A and 40B and between 42A and 42B at 100.degree. C.
for 10 min. As a result, a piezoelectric transformer 44 is
obtained.
[0037] Thereafter, the piezoelectric transformer 44 so obtained is
compared with conventional piezoelectric transformers. FIGS. 3A-3C
depict laminated structures of the piezoelectric transformer of the
present invention and two prior art transformers. FIG. 3A depicts a
laminated structure of the piezoelectric transformer of the present
invention, wherein the high strain material (S) is used at the
input parts 10 thereof and the high output power generation
material (H) is used at the output part 20. FIG. 3B illustrates a
laminated structure of a first comparative sample, wherein a high
strain material (S) is used as the output part 20 where a high
output power generation material (H) is used for the input parts 10
thereof. FIG. 3C presents a laminated structure of a second
comparative sample, wherein a high output power generation material
(H) is used both at the output part 20 and the input parts 10
thereof.
[0038] Referring to FIG. 4, there are illustrated test results of
the piezoelectric transformers shown in FIGS. 3A-3C, showing output
powers as a function of load resistance. In FIG. 4, a horizontal
axis and a vertical axis represent a load resistance (.OMEGA.) and
an output power (W), respectively. Graphs GA, GB and GC of FIG. 4
correspond to the samples of FIGS. 3A to 3C, respectively. As is
apparent from FIG. 4, the piezoelectric transformer of the present
invention generates a higher output power than the first and the
second comparative samples.
[0039] Since the material constituting the input parts has a higher
piezoelectric strain constant (d) than that for the output part in
accordance with the invention as described above, an efficient
mechanical vibration can be obtained at the input parts and the
mechanical vibration is efficiently converted into a corresponding
electric signal at the output part. Accordingly, a piezoelectric
transformer having less power loss, which gives rise to less heat
generation and greater output power, can be obtained.
[0040] Referring to FIGS. 5 to 6B, a second preferred embodiment of
the present invention will now be described. Like reference
numerals used in the first and the second preferred embodiments
represent like parts. FIG. 5 presents a laminated structure of a
piezoelectric transformer in accordance with the second preferred
embodiment of the present invention.
[0041] As shown in FIG. 5, disjointed internal electrodes 54A to
54D, each having, e.g., a rectangular shape, are formed on a sheet
54 in each input part 10, wherein the electrodes 54A and 54B are
exposed at a front edge of the sheet 54 and the electrodes 54C and
54D are exposed at a rear edge of the sheet 54. On a sheet 56 of
each of the input parts 10, there is formed an internal electrode
56A such that the internal electrode 56A overlaps with portions of
the internal electrodes 54A and 54D when viewed from top. Further,
a rectangular internal electrode 56B is also formed on the sheet 56
such that the internal electrode 56B overlaps with portions of the
internal electrodes 54B and 54C when viewed from the top. The
internal electrodes 56A and 56B are separated from each other and
are not exposed at any edges of the sheet 56.
[0042] Meanwhile, rectangular-shaped internal electrodes 64A to 64D
are formed separately on every sheet 64 of the output part 20 such
that two electrodes 64B and 64C are exposed at a right edge of the
sheet 64 and the remaining electrodes 64A and 64D are exposed at a
left edge of the sheet 64. Further, a rectangular-shaped internal
electrode 66A is formed on every sheet 66 of the output part 20
such that the internal electrode 66A overlaps with the internal
electrodes 64A and 64B when viewed from top. A rectangular-shaped
internal electrode 66B is also formed on every sheet 66 such that
the internal electrode 66B overlaps with the internal electrodes
64C and 64D. The internal electrodes 66A and 66B are separated from
each other and are not exposed at the edges of the sheet 66.
[0043] Insulation sheets 30 for separating the input parts 10 from
the output part 20 are laminated therebetween as shown in FIG. 5.
Protection sheets 32 are also laminated at top and bottom of the
laminated structure.
[0044] As in the first preferred embodiment of the invention, PZT
green sheets having a large dielectric constant ".epsilon.", a
large piezoelectric strain constant "d" and a small mechanical
quality factor Qm are used for the sheets 54 and 56 of the input
parts 10. Meanwhile, PZT green sheets having a small piezoelectric
strain constant "d", a small dielectric constant ".epsilon." and a
large mechanical quality factor Qm are used for the sheets 64 and
66 of the output part 20 as in the first embodiment.
[0045] All the sheets constituting the laminated structure are
compressed after being stacked and diced into four parts along the
lines LA and LB as illustrated in FIGS. 6A and 6B. Since the input
parts 10 are diced along lines LA and LB as shown in FIG. 6A, the
internal electrodes 56A and 56B are exposed at diced edges thereof.
Further, since the output part 20 is diced along the lines LA and
LB as shown in FIG. 6B, the internal electrodes 66A and 66B are
exposed at the diced edges thereof. After dicing, a binder removing
process and a sintering process are performed on the diced
laminated structure and then external electrodes are formed thereon
in a similar fashion as illustrated in FIG. 2.
[0046] The piezoelectric transformers obtained by the first and the
second preferred embodiments are identical each other excepting the
shapes of the internal electrodes.
[0047] Referring FIGS. 7A and 7B, there are presented laminated
structures of piezoelectric transformers 710 and 720 in accordance
with a third preferred embodiment of the present invention. As
shown in FIG. 7A, an input part 110 of the piezoelectric
transformer 710 has internal electrodes 114 which are vertically
laminated in a piezoelectric member 112. The internal electrodes
114 are alternately connected to an upper external electrode 116
and a lower external electrode 118.
[0048] Meanwhile, an output part 120 of the piezoelectric
transformer 710 has internal electrodes 124 which are horizontally
laminated in a piezoelectric member 122. The internal electrodes
124 are alternately connected to an upper external electrode 126
and a lower external electrode 128. The external electrodes may be
formed on front and rear surfaces of the piezoelectric members. The
input part 110 and the output part 120 are coupled by an insulating
binder member 130.
[0049] A material having a large piezoelectric strain constant "d",
a large dielectric constant ".epsilon." and a small mechanical
quality factor Qm is used for the piezoelectric member 112 of the
input part 110; and a material having a small piezoelectric strain
constant "d", a small dielectric constant ".epsilon." and a large
mechanical quality factor Qm is used for the piezoelectric member
122 of the output part 120 as in the first and second preferred
embodiments of the present invention.
[0050] In the third preferred embodiment of the present invention,
the input part 110 may be formed to have a structure of
horizontally laminated internal electrodes and the output part 120
may be constructed to have vertically laminated internal
electrodes.
[0051] In FIG. 7B, an input part 210 of the piezoelectric
transformer 720 has internal electrodes 214 horizontally laminated
in a piezoelectric member 212. The internal electrodes 214 are
alternately connected to an upper external electrode 216 and a
lower external electrode 218. The output part 120 and the
insulating binder member 130 of the transformer 720 are identical
to those of the transformer 710.
[0052] The piezoelectric transformer 720 shown in FIG. 7B can be
considered as a variation of the piezoelectric transformers of the
first and second preferred embodiments of the present invention. It
is to be appreciated that shapes of the piezoelectric sheets or the
electrodes, locations of external electrodes and the number of
piezoelectric sheets may be varied appropriately if necessary.
Further, various known materials may be used as the piezoelectric
or the electrode material.
[0053] The present invention may be preferably employed in
fabricating step-down piezoelectric transformers in order to obtain
a large output power. However, the present invention may also be
applied in fabricating step-up piezoelectric transformers as well.
A step-up piezoelectric transformer can be obtained by decreasing
the impedance of an input part and increasing the impedance of an
output part. Conversely, a step-down piezoelectric transformer can
be obtained by increasing the impedance of an input part and
decreasing the impedance of an output part. This can be achieved by
changing the laminated structure of the piezoelectric
transformer.
[0054] As described above, a high strain material and a high output
power generation material are used as the input part and the output
part of the piezoelectric transformer of the present invention,
respectively. Accordingly, efficient mechanical vibration can be
achieved at the input part thereof and at the output part thereof,
the mechanical vibration can be efficiently converted into an
electrical signal, thereby obtaining a piezoelectric transformer
having reduced heat generation and increased output power
generation characteristics.
[0055] While the present invention has been described with respect
to certain preferred embodiments only, other modifications and
variations may be made without departing from the sprit and scope
of the present invention as set forth in the following claims.
* * * * *