U.S. patent application number 09/488750 was filed with the patent office on 2001-11-08 for lawn colorant composition having rearing effects.
Invention is credited to Hattori, Toshio, Okura, Ken, Sakakibara, Masayoshi, Ssasaki, Shigeo.
Application Number | 20010039267 09/488750 |
Document ID | / |
Family ID | 12324471 |
Filed Date | 2001-11-08 |
United States Patent
Application |
20010039267 |
Kind Code |
A1 |
Okura, Ken ; et al. |
November 8, 2001 |
Lawn colorant composition having rearing effects
Abstract
A lawn colorant composition having rearing effects contains a
pigment and an adhesive for the pigment. The pigment comprises a
blue pigment composed as a primary component of a compound
represented by the following formula: MFe[Fe(CN).sub.6] wherein M
represents an alkali metal atom or an ammonium group, one of the
two Fe atoms is a divalent ion, and the other Fe atom is a
trivalent ion. The adhesive comprises a water-dispersed polymer and
a water-soluble polymer having compatibility with said
water-dispersed polymer.
Inventors: |
Okura, Ken; (Tokyo, JP)
; Hattori, Toshio; (Tokyo, JP) ; Sakakibara,
Masayoshi; (Tokyo, JP) ; Ssasaki, Shigeo;
(Tokyo, JP) |
Correspondence
Address: |
Oblon, Spivak, McClelland, Maier & Neustadt, P. C.
Fourth Floor
1755 Jefferson Davis Highway
Arlington
VA
22202
US
|
Family ID: |
12324471 |
Appl. No.: |
09/488750 |
Filed: |
January 21, 2000 |
Current U.S.
Class: |
514/116 |
Current CPC
Class: |
A01N 2300/00 20130101;
A01N 25/10 20130101; A01N 59/16 20130101; C05G 3/00 20130101; A01N
25/24 20130101; A01N 25/24 20130101; C05D 9/02 20130101; A01N 59/16
20130101; C05G 3/00 20130101; A01N 59/16 20130101; C05D 9/02
20130101 |
Class at
Publication: |
514/116 |
International
Class: |
A01N 057/00 |
Foreign Application Data
Date |
Code |
Application Number |
Feb 13, 1998 |
JP |
031188 |
Claims
1. A lawn colorant composition having rearing effects, said lawn
colorant composition being composed of a pigment and an adhesive
therefor, wherein said pigment comprises a blue pigment composed as
a primary component of a compound represented by the following
formula: MFe[Fe(CN).sub.6] wherein M represents an alkali metal
atom or an ammonium group, one of said two Fe atoms is a divalent
ion, and the other Fe atom is a trivalent ion; and said adhesive
comprises a water-dispersed polymer and a water-soluble polymer
having compatibility with said water-dispersed polymer.
2. A lawn colorant composition according to claim 1, wherein said
water-soluble polymer is contained in a proportion of from 1 to 30
wt. % based on said water-dispersed polymer.
Description
BACKGROUND OF THE INVENTION
[0001] a) Field of the Invention
[0002] This invention relates to a colorant composition for lawns,
and more specifically to a colorant composition which contains as a
primary component a colorant effective not only for coloring lawns
but also for promoting growth of the lawns and preventing aging of
the lawns and which, when applied to color the lawns, the color so
applied can remain for a long time and does not stain other
articles through rubbing.
[0003] b) Description of Related Art
[0004] As lawns wither into a yellow or light brown color in
winter, colorant compositions with green or blue pigments contained
therein have conventionally been sprayed to keep the lawns look
green.
[0005] In these colorant compositions, organic pigments and/or dyes
such as copper phthalocyanine blue pigments and copper
phthalocyanine green pigments have been employed for the purpose of
coloring alone.
[0006] These conventionally-employed pigments and dyes are however
intended merely to color lawns at their surfaces, and no
physiological effects for plants are observed on their coloring
components themselves.
[0007] In these conventional colorant compositions, emulsions of
acrylate ester resins, vinyl acetate resins, ethylene-vinyl acetate
resins or the like or emulsions of water-dispersible polymers, such
as synthetic rubber latexes, are also used as adhesives for fixing
coloring components on turfgrass.
[0008] Incidentally, an emulsion of a polymer generally cannot form
polymer films at temperatures lower than its film-forming
temperature, so that a coloring component, especially a pigment
cannot be fixed on turfgrass. When a colorant is sprayed in winter,
the temperature is often so low that films cannot be formed with a
pigment enclosed therein unless a polymer the lowest film-forming
temperature of which is lower than the surrounding temperature, or
example, is 5.degree. C. or lower is used.
[0009] In general, a polymer the lowest film-forming temperature of
which is low is still soft and tacky even after formation into
films, and is hence accompanied by a potential problem that they
may be rubbed to stain shoes and clothing or at golf courses, to
stain equipments such as balls and clubs.
[0010] With a view to improving the film-formability of aqueous
emulsion polymers at low temperatures, film-forming aids are
therefore often used in combination. Illustrative of film-forming
aids are alkyl ethers and phenyl ethers of glycols and acetates of
such ethers, and benzene or naphthalene solvents containing
hydrocarbon groups. These film-forming aids cause no problem when
employed industrially, but they are not suited for being sprayed
over nature-oriented objects such as lawns and moreover, are also
accompanied by a problem from the standpoint of odor.
SUMMARY OF THE INVENTION
[0011] The present inventors have proceeded with an extensive
investigation with a view to overcoming the drawback that, when
lawns are colored with conventional colorant compositions at low
temperatures, the colorant compositions are rubbed to stain golf
balls and golf equipments and hence with a view to developing a
lawn colorant composition the colorant of which acts not only to
achieve coloring but also to exhibit physiological effects
(growth-promoting and anti-aging effects) for the plant. As a
result, it was found that the above object can be achieved by
using, as an adhesive, a water-dispersed resin and a water-soluble
resin in combination and also a coloring composition containing a
specific blue pigment as a coloring component. Based on this
finding, the present invention has now been completed.
[0012] To achieve the above-described object, the present invention
provides a lawn colorant composition having rearing effects, said
lawn colorant composition being composed of a pigment and an
adhesive therefor, wherein the pigment comprises a blue pigment
composed as a primary component of a compound represented by the
following formula: MFe[Fe(CN).sub.6] wherein M represents an alkali
metal atom or an ammonium group, one of the two Fe atoms is a
divalent ion, and the other Fe atom is a trivalent ion; and the
adhesive comprises a water-dispersed polymer and a water-soluble
polymer having compatibility with the water-dispersed polymer.
[0013] Even when the lawn colorant composition according to the
present invention as sprayed over a lawn is rubbed at a low
temperature as a result of its contact with an object, the lawn
colorant composition does not stain the object. Moreover, the lawn
colorant composition can achieve not only coloring of the lawn but
also promotion of growth of the lawn and prevention of aging of the
lawn.
DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS
[0014] The present invention will next be described in further
detail by preferred embodiments.
[0015] The blue pigment for use in the present invention is a
pigment which comprises, as a primary component, a compound
represented by the formula: MFe[Fe(CN).sub.6], and its preferred
average particle size ranges from 0.03 to 0.20 .mu.m, more
preferably from 0.05 to 0.10 .mu.m.
[0016] In the above formula, M represents an alkali metal atom,
such as sodium or potassium, or an ammonium group, and one of the
two Fe atoms is a divalent ion, and the other Fe atom is a
trivalent ion.
[0017] The coloring component in the colorant composition according
to the present invention may be composed solely of a pigment which
comprises as a primary component the compound represented by the
above formula. To an extent not impairing the object of the present
invention, however, another inorganic pigment or an organic pigment
or dye may also be used in combination.
[0018] The colorant composition according to the present invention
is characterized in that it comprises the above-described coloring
component and an adhesive and the adhesive is composed of a
water-dispersed polymer and a water-soluble polymer.
[0019] Preferred examples of the water-dispersed polymer for use in
the present invention can include polymer emulsions (or latexes)
the lowest film-forming temperatures of which are in a range of
from 0 to 100.degree. C., for example, vinyl acetate emulsion,
vinyl acetate copolymer emulsions, acrylate ester polymer
emulsions, acrylate ester copolymer emulsions, methacrylate ester
polymer emulsions, methacrylate ester copolymer emulsions, and
styrene copolymer emulsions. More preferred are synthetic resin
emulsions the lowest film-forming temperatures of which are in a
range of from 0 to 50.degree. C.
[0020] Examples of the water-soluble polymer for use in the present
invention can include those having compatibility with the
water-dispersed polymer, such as polyvinyl alcohol, acrylic acid
polymers, acrylic acid copolymers, maleic acid resins, cellulose
resins, starch, and chitosan.
[0021] The preferred proportion of the water-soluble polymer is in
a range of from 1 to 30%, with a range of from 1 to 10 wt. % being
more preferred, both based on the water-dispersed polymer (solid
content).
[0022] When the colorant composition according to the present
invention is stored over a long time, it is effective to use one or
more of various surfactants as a dispersant for the pigment. From
anionic surfactants, cationic surfactants and non-ionic
surfactants, one or more surfactants can be selected for use in the
present invention in view of the dispersibility of the pigment and
also their compatibility with the water-dispersed polymer and
water-soluble polymer. Non-ionic surfactants can be mentioned as
particularly preferred surfactants, although the present invention
is not limited to the use of such non-ionic surfactant or
surfactants. Further, defoaming agents, antiseptics, fungicides and
the like can also be added as needed.
[0023] Next, the present invention will be specifically described
by Examples and Comparative Examples. It shall however be borne in
mind that the present invention is not limited by the Examples. All
designations of "part" or "parts" and "%" in the Examples are by
weight.
EXAMPLE 1
[0024] Ten (10) parts of a Prussian blue ("Milori Blue 671", trade
name; product of Dainichiseika Color & Chemicals Mfg. Co.,
Ltd.), 10 parts of a disazo yellow AAOA ("Seika Fast Yellow 2400",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 0.5 part of an anionic surfactant ("Demol EP", trade
name; product of Kao Corporation), 4.0 parts of a non-ionic
surfactant ("Emulgen A-90", trade name; product of Kao
Corporation), and 75.5 parts of water were dispersed in a beads
mill. To the resultant dispersion, 10 parts of a water-soluble
polymer ("Jullimer AT-210", trade name; product of Nihon Junyaku
Co., Ltd.) were evenly mixed, followed by the addition of 120 parts
of a water-dispersed polymer ("Boncoat 2310", trade name; product
of Dainippon Ink & Chemicals, Incorporated), whereby a lawn
colorant composition according to the present invention was
obtained.
[0025] On October 30 Korai turfgrass lots were sprayed at 300
ml/m.sup.2 with 50-fold and 100-fold dilute solutions of the
thus-obtained colorant composition, respectively, and their
subsequent conditions were observed. The results will be shown in
comparison with those of Comparative Example 1 to be described
below.
Comparative Example 1
[0026] Five (5) parts of a cyanine green ("Cyanine Green 2GN",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 10 parts of a disazo yellow AAOA ("Seika Fast Yellow
2400", trade name; product of Dainichiseika Color & Chemicals
Mfg. Co., Ltd.), 5 parts of an anionic surfactant ("Demol EP",
trade name; product of Kao Corporation), and 80 parts of water were
dispersed in a beads mill. To the resultant dispersion, 120 parts
of a water-dispersed polymer ("Boncoat 2310", trade name; product
of Dainippon Ink & Chemicals, Incorporated) were added, whereby
a lawn colorant composition of a comparative example was obtained.
On October 30 Korai turfgrass lots were sprayed at 300 ml/m.sup.2
with 50-fold and 100-fold dilute solutions of the thus-obtained
colorant composition, respectively, and their subsequent conditions
were observed.
[0027] Comparison in the Effects of Spraying
[0028] Shortly after the spraying, no substantial difference was
observed on coloring ability between Example 1 and Comparative
Example 1. The turfgrass lots presented external appearances which
were commensurate with the colorant concentrations.
[0029] Thirty days after the spraying, that is, on November 29, the
aboveground leaves of the unsprayed turfgrass mostly withered into
a brown color. The turfgrass sprayed with the colorant composition
of Example 1 retained a green color, whereas the turfgrass sprayed
with the colorant composition of Comparative Example 1 faded and
presented a color close to a withered lawn color. As a result of
detailed observation of their conditions, the aboveground parts of
the turfgrass in the unsprayed lot and the lots sprayed with the
lawn colorant composition of Comparative Example 1 were observed to
be in a resting period and to have withered mostly, while in the
lots sprayed with the lawn colorant composition of Example 1, the
aboveground parts of the turfgrass presented a green color as if
they were still active, and adhesion of the colorant on the
surfaces of the turfgrass was observed. On the second day after the
spraying, the turfgrass in each lot was rubbed with a sheet of
white paper to determine a degree of stain. Substantial stain was
observed in the case of the lawn colorant composition of
Comparative Example 1, but practically no stain was observed in the
case of the lawn colorant composition of Example 1.
EXAMPLE 2
[0030] Ten (10) parts of a Prussian blue ("N650 Prussian Blue",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 10 parts of a disazo yellow AAOA ("Seika Fast Yellow
2400", trade name; product of Dainichiseika Color & Chemicals
Mfg. Co., Ltd.), 1 part of an anionic surfactant ("Demol N", trade
name; product of Kao Corporation), 5 parts of a non-ionic
surfactant ("Emulgen A-90", trade name; product of Kao
Corporation), 0.2 part of a defoaming agent ("Nopco NXZ", trade
name; product of San Nopco Limited), and 73 parts of water were
dispersed in a beads mill. To the resultant dispersion, 20 parts of
a water-soluble polymer ("Water Sol S-701", trade name; product of
Dainippon Ink & Chemicals, Incorporated) and 100 parts of a
water-dispersed polymer ("Movinyl 123E", trade name; product of
Hoechst Synthesis) were added, whereby a lawn colorant composition
according to the present invention was obtained.
[0031] Korai turfgrass planted on May 30 in planters were sprayed
at 250 ml/m.sup.2 with 50-fold and 100-fold dilute solutions of the
thus-obtained colorant composition, respectively, and the
subsequent growth conditions of the turfgrass planted in the
rearing planters were observed. The results will be shown in
comparison with those of Comparative Example 2 to be described
below.
Comparative Example 2
[0032] Five (5) parts of a cyanine blue ("Cyanine Blue 4920", trade
name; product of Dainichiseika Color & Chemicals Mfg. Co.,
Ltd.), 10 parts of a disazo yellow AAOA ("Seika Fast Yellow 2400",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 5 parts of an anionic surfactant ("Demol N", trade
name; product of Kao Corporation), 1 part of a non-ionic surfactant
("Emulgen A-90", trade name; product of Kao Corporation), 1 part of
a defoaming agent ("Nopco NXZ", trade name; product of San Nopco
Limited), and 78 parts of water were dispersed in a beads mill. To
the resultant dispersion, 100 parts of a water-dispersed polymer
("Movinyl 123E", trade name; product of Hoechst Synthesis) were
added, whereby a green colorant composition of a comparative
example was obtained.
[0033] Korai turfgrass planted on May 30 in planters were sprayed
at 250 ml/m.sup.2 with 50-fold and 100-fold dilute solutions of the
thus-obtained colorant composition, respectively, and their
subsequent conditions were observed.
[0034] Comparison in the Effects of Spraying
[0035] Shortly after the spraying, no substantial difference was
observed on coloring ability between Example 2 and Comparative
Example 2. The turfgrass presented external appearances which were
commensurate with the colorant concentrations.
[0036] Sixty days after the spraying, that is, on July 31, however,
the unsprayed turfgrass did not sufficiently take root, and one
third of the entire ground surface was exposed. The turfgrass
sprayed with the lawn colorant composition of Example 2 took root
completely, and the growth of their aboveground parts was also
vigorous.
EXAMPLE 3
[0037] Ten (10) parts of a Prussian blue ("N650 Prussian Blue",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 10 parts of a disazo yellow AAOA ("Seika Fast Yellow
2400", trade name; product of Dainichiseika Color & Chemicals
Mfg. Co., Ltd.), 1 part of an anionic surfactant ("Demol N", trade
name; product of Kao Corporation), 5 parts of a non-ionic
surfactant ("Emulgen A-90", trade name; product of Kao
Corporation), 0.2 part of a defoaming agent ("Nopco NXZ", trade
name; product of San Nopco Limited), and 73 parts of water were
dispersed in a beads mill. To the resultant dispersion, 5 parts of
a water-soluble polymer ("Water Sol S-753", trade name; product of
Dainippon Ink & Chemicals, Incorporated), 80 parts of a
water-dispersed polymer ("Polysol EVA AD-6", trade name; product of
Showa Highpolymer Co., Ltd.) and 50 parts of an aqueous solution of
chitosan ("Daichitosan W-100", product of Dainichiseika Color &
Chemicals Mfg. Co., Ltd.) were added, whereby a lawn colorant
composition according to the present invention was obtained.
Comparative Example 3
[0038] Three (3) parts of a cyanine blue ("Cyanine Blue 4920",
trade name; product of Dainichiseika Color & Chemicals Mfg.
Co., Ltd.), 2 parts of a cyanine green ("Cyanine Green 2GN",
product of Dainichiseika Color & Chemicals Mfg. Co., Ltd.), 10
parts of a disazo yellow AAMX ("Seika Fast Yellow 2600", trade
name; product of Dainichiseika Color & Chemicals Mfg. Co.,
Ltd.), 5 parts of an anionic surfactant ("Demol N", trade name;
product of Kao Corporation), 1 part of a non-ionic surfactant
("Emulgen A-90", trade name; product of Kao Corporation), 1 part of
a defoaming agent ("Nopco NXZ", trade name; product of San Nopco
Limited), and 78 parts of water were dispersed in a beads mill. To
the resultant dispersion, 100 parts of a water-dispersed polymer
("Polysol EVA AD-6" trade name; product of Showa Highpolymer Co.,
Ltd.) were added, whereby a green colorant composition of a
comparative example was obtained.
[0039] On October 30 Korai turfgrass lots were sprayed at 300
ml/m.sup.2 with 50-fold and 100-fold dilute solutions of the
thus-obtained colorant compositions of Example 3 and Comparative
Example 3, respectively, and their subsequent conditions were
observed.
[0040] Comparison in the Effects of Spraying
[0041] Shortly after the spraying, no substantial difference was
observed on coloring ability between Example 3 and Comparative
Example 3. The turfgrass lots presented external appearances which
were commensurate with the colorant concentrations.
[0042] Thirty days after the spraying, that is, on November 29, the
aboveground leaves of the unsprayed turfgrass mostly withered into
a brown color. The turfgrass sprayed with the colorant composition
of Example 3 retained a green color, whereas the turfgrass sprayed
with the colorant composition of Comparative Example 3 faded and
presented a color close to a withered lawn color. As a result of
detailed observation of their conditions, the aboveground parts of
the turfgrass in the unsprayed lot and the lots sprayed with the
lawn colorant composition of Comparative Example 3 were observed to
be in a resting period and to have withered mostly, while in the
lots sprayed with the lawn colorant composition of Example 3, the
aboveground parts of the turfgrass presented a green color as if
they were still active, and adhesion of the colorant on the
surfaces of the turfgrass was observed. On the second day after the
spraying, the turfgrass in each lot was rubbed with a sheet of
white paper to determine a degree of stain. Substantial stain was
observed in the case of the lawn colorant composition of
Comparative Example 3, but practically no stain was observed in the
case of the lawn colorant composition of Example 3.
* * * * *