U.S. patent application number 09/823552 was filed with the patent office on 2001-10-11 for multilayer piezoelectric transformer.
This patent application is currently assigned to Taiyo Yuden Co., Ltd. Invention is credited to Inomata, Yasuyuki, Ishii, Shigeo, Kishi, Hiroshi, Watanabe, Yoshiyuki.
Application Number | 20010028206 09/823552 |
Document ID | / |
Family ID | 18610653 |
Filed Date | 2001-10-11 |
United States Patent
Application |
20010028206 |
Kind Code |
A1 |
Watanabe, Yoshiyuki ; et
al. |
October 11, 2001 |
Multilayer piezoelectric transformer
Abstract
A piezoelectric transformer comprises one or more input parts
having first internal electrodes and input terminals and an output
part having second internal electrodes and output terminals. Each
of the second internal electrodes has an area larger than that of
each of the first internal electrodes. By such configuration,
output power is increased while heat generation is suppressed and
size thereof is not increased.
Inventors: |
Watanabe, Yoshiyuki; (Tokyo,
JP) ; Kishi, Hiroshi; (Tokyo, JP) ; Inomata,
Yasuyuki; (Tokyo, JP) ; Ishii, Shigeo; (Tokyo,
JP) |
Correspondence
Address: |
SHAHAN ISLAM, ESQ
ROSENMAN & COLIN LLP
575 Madison Avenue
New York
NY
10022-2585
US
|
Assignee: |
Taiyo Yuden Co., Ltd
16-20 Ueno 6-chome, Taito-ku,
Tokyo
JP
110-0005
|
Family ID: |
18610653 |
Appl. No.: |
09/823552 |
Filed: |
March 30, 2001 |
Current U.S.
Class: |
310/366 ;
310/359 |
Current CPC
Class: |
H01L 41/107
20130101 |
Class at
Publication: |
310/366 ;
310/359 |
International
Class: |
H01L 041/04 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 30, 2000 |
JP |
2000-095798 |
Claims
What is claimed is:
1. A piezoelectric transformer of a laminated structure,
comprising: one or more input parts having first internal
electrodes and input terminals; and an output part having second
internal electrodes and output terminals, wherein each of the
second internal electrodes has an area larger than that of each of
the first internal electrodes.
2. The piezoelectric transformer of claim 1, wherein an input
voltage is higher than an output voltage.
3. A piezoelectric transformer of a laminated structure,
comprising: a laminated body including one or more input parts and
an output part, the input parts being formed by laminating a
plurality of first piezoelectric sheets and having first internal
electrodes each of which is formed on each of the first
piezoelectric sheets and input terminals for the first internal
electrodes which are alternately exposed to opposite sides of the
laminated body, the output part being formed by laminating a
plurality of first piezoelectric sheets and having second internal
electrodes each of which is formed on each of the first
piezoelectric sheets and output terminals for the second internal
electrodes which are alternately exposed to another opposite sides
of the laminated body; and external electrodes being electrically
connected to the input terminals and the output terminals.
4. The piezoelectric transformer of claim 3, wherein an input
voltage is higher than an output voltage.
5. The piezoelectric transformer of claim 4, wherein the output
part is disposed between the input parts.
Description
FIELD OF THE INVENTION
[0001] The present invention relates to a piezoelectric
transformer; and, more particularly, to a step-down type multilayer
piezoelectric transformer.
DESCRIPTION OF THE PRIOR ART
[0002] Piezoelectric transformers feature smaller sizes and higher
efficiencies than the conventional electromagnetic transformers.
For such reasons, the piezoelectric transformers are gaining
popularity as step-up transformers employed in, e.g., backlight
power sources of liquid crystal display (LCD) monitors. However, in
power supplies, step-down piezoelectric transformers are more
frequently used than step-up transformers.
[0003] Voltage transformation by the piezoelectric transformer is
performed as follows. First, an electrical input signal is applied
to an input part of the piezoelectric transformer. Next, the
electrical input signal is transformed into the mechanical
vibration at the input part of the piezoelectric transformer and
the mechanical vibration is propagated to an output part thereof.
Then, the mechanical vibration is changed into an electrical output
signal at the output part of the piezoelectric transformer.
[0004] It is preferable that a piezoelectric transformer have such
characteristics as high output power, less heat generation, small
size and high efficiency. The output power of a piezoelectric
transformer is dictated by the velocity of the mechanical
vibration. In order to generate a high vibration velocity, the
input part of the piezoelectric transformer need be driven to
effect a large strain. This can be accomplished by increasing
interface areas between the piezoelectric material and the
electrodes, e.g., by arranging the electrodes and the piezoelectric
material to form a laminated structure or increasing the areas of
the electrodes.
[0005] However, when the piezoelectric transformer is driven to
effect a large strain, heat generation is increased due to
crystallographic and electrical losses and the output power is
decreased by the generated heat. Most of the heat is generated from
the input part of the piezoelectric transformer. Therefore, when
the input part is under restricted conditions due to heat
generation, the transformation efficiency of the output part has
relatively greater effects on the electrical characteristics, e.g.,
the output power, of the piezoelectric transformer. For such
reasons, in order to produce a high output power without increasing
heat generation, the mechanical vibration generated in the input
part need be efficiently transformed into electrical signals at the
output part.
[0006] The output power P of the piezoelectric transformer is
represented as follows: 1 P k 2 1 - k 2 V v 2
[0007] where k is an electromechanical coupling coefficient of the
output part of the piezoelectric transformer, v is the velocity of
the mechanical vibration and V is the volume of the output part.
Therefore, the output power of the piezoelectric transformer can be
enhanced by increasing the volume of the output part thereof.
However, there is an upper limit for the volume of the output part
which can be activated by the given amount of the vibration energy
supplied from the input part. Further, the size of the
piezoelectric transformer becomes larger by increasing the volume
of the output part, which is not desirable.
THE SUMMARY OF THE INVENTION
[0008] It is, therefore, a primary object of the present invention
to provide a piezoelectric transformer having a laminated structure
and capable of producing a higher output power without increasing
heat generation and the device size thereof.
[0009] In accordance with a preferred embodiment of the present
invention, there is provided a piezoelectric transformer having a
laminated structure, comprising one or more input parts including
first internal electrodes and input terminals, and an output part
including second internal electrodes and output terminals, wherein
each of the second internal electrodes has an area larger than that
of each of the first internal electrodes.
[0010] In accordance with another preferred embodiment of the
present invention, there is provided a piezoelectric transformer
having a laminated structure, comprising a laminated body including
one or more input parts and an output part, the input parts being
formed by laminating a plurality of first piezoelectric sheets and
having first internal electrodes each of which is formed on each of
the first piezoelectric sheets and input terminals for the first
internal electrodes which are alternately exposed to opposite sides
of the laminated body, the output part being formed by laminating a
plurality of second piezoelectric sheets and having second internal
electrodes each of which is formed on each of the second
piezoelectric sheets and output terminals for the second internal
electrodes which are alternately exposed to another opposite sides
of the laminated body, and external electrodes which are
electrically connected to the input terminals and the output
terminals.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] The above and other objects and features of the present
invention will become apparent from the following description of
preferred embodiments given in conjunction with the accompanying
drawings, in which:
[0012] FIG. 1 shows a laminated structure of a piezoelectric
transformer in accordance with a first preferred embodiment of the
present invention;
[0013] FIG. 2A provides a comparative view depicting the
differences between the internal electrodes of the input part and
the output part of the piezoelectric transformer in accordance with
the first preferred embodiment;
[0014] FIG. 2B sets forth a perspective view of the piezoelectric
transformer in accordance with the first preferred embodiment;
[0015] FIG. 2C presents a cross-sectional view taken on line A-A of
FIG. 2B;
[0016] FIG. 3 describes a graph representing the dependency of a
temperature variation on corresponding output powers of the
piezoelectric transformer in accordance with the present invention
and a comparative piezoelectric transformer;
[0017] FIG. 4 depicts a laminated structure of a piezoelectric
transformer in accordance with a second preferred embodiment of the
present invention; and
[0018] FIGS. 5A and 5B illustrate dicing configurations of the
piezoelectric transformer in accordance with the second preferred
embodiment of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0019] A first preferred embodiment in accordance with the present
invention will now be described with reference to FIGS. 1 to 3.
[0020] FIG. 1 shows a laminated structure of a piezoelectric
transformer in accordance with the first preferred embodiment of
the present invention having an output part (secondary side) 20
located between two input parts 10 (primary sides). Each of the
input parts 10 is formed by laminating two sheets, i.e., an upper
sheet 14 and a lower sheet 16, made of a piezoelectric material.
Each sheet has a round-shaped internal electrode 12 in a
substantially center portion thereof. As shown in FIG. 1, there is
formed at the internal electrode 12 of the upper sheet 14 a
terminal portion 14A extended to a rear edge of the sheet 14.
Further, at the internal electrode 12 of the lower sheet 16, a
terminal portion 16A is extended to a front edge of the sheet 16.
Namely, the internal electrode 12 for each input part 10 is
extended in either front or rear direction through the terminal
portion 14A or 16A.
[0021] The output part 20 is provided by laminating first sheets 24
and second sheets 26 alternately. Each sheet is made of a
piezoelectric material and has a rectangular-shaped internal
electrode 22 in a center portion thereof. For instance, six pairs
of the first and the second sheets, i.e., twelve sheets in total,
may be laminated to form the output part. As shown in FIG. 1, there
is formed at the internal electrode 22 of the first sheet 24 a
terminal portion 24A extended to a right edge of the sheet 24.
Further, at the internal electrode 22 of the second sheet 26, a
terminal portion 26A is extended to a left edge of the sheet 26.
That is, the internal electrode 22 of the output part 20 is
extended in either right or left direction through the terminal
portion 24A or 26A.
[0022] Insulating sheets 30 are provided between each input part 10
and the output part 20 in order to separate the former from the
latter as shown in FIG. 1. Further, protective sheets 32 are
provided as an uppermost layer and a lowermost layer of the
piezoelectric transformer.
[0023] Comparing the configuration of the internal electrode 12 of
the input part 10 with that of the internal electrode 22 of the
output part 20, the former has a smaller area than the latter, as
shown in FIG. 2A.
[0024] All the sheets are compressed after being stacked as shown
in FIG. 1, thereby forming a laminated body. Thereafter, a binder
removing process and a sintering process are performed and then
external electrodes are formed on the laminated body as shown in
FIG. 2B. In the present embodiment, the terminal portions 14A of
the input parts 10 are connected to an external electrode 40A and
the terminal portions 16A thereof are connected to an external
electrode 40B. Further, the terminal portions 24A of the output
part 20 are connected to an external electrode 42A and the terminal
portions 26A thereof are connected to an external electrode 42B.
The external electrodes 40A, 40B, 42A and 42B are made of a
conductive material such as silver (Ag). Next, a poling process for
the piezoelectric material included in the laminated body is
performed through the use of the external electrodes. For example,
the poling process may be performed by applying an electric field
of 2 kV/mm between the external electrodes 40A and 40B and between
the external electrodes 42A and 42B at 150.degree. C. for 10
minutes. As a result, the piezoelectric transformer is
obtained.
[0025] The characteristics of the piezoelectric transformer in
accordance with the present embodiment are compared with those of a
comparative piezoelectric transformer which has an identical
configuration with the present embodiment except that each internal
electrode of the output part has a same shape and a same area as
those of each internal electrode of the input part.
[0026] FIG. 3 is a graph illustrating the relationship between
temperature variations and output powers of the piezoelectric
transformer, wherein the piezoelectric transformer in accordance
with the present embodiment is represented by a curve GA and the
comparative piezoelectric transformer is represented by a curve GB.
The horizontal and the vertical axes of the graph indicate the
output power (W) and the temperature variation (.degree. C.),
respectively. The output power is adjusted by, e.g., changing the
input power and the temperature variations are measured from the
surfaces of the piezoelectric transformers. As shown in FIG. 3,
when the temperature variations of both piezoelectric transformers
are the same, the piezoelectric transformer in accordance with the
present embodiment has a larger output power than the comparative
piezoelectric transformer. For example, at the temperature
variation of 25.degree. C., the output power of the former is 35 W
and that of the latter is 30 W.
[0027] As shown above, since the input part of the piezoelectric
transformer in accordance with the present embodiment includes the
input parts which have the same configurations as those of the
comparative piezoelectric transformer, the amount of heat
generation in the former is substantially identical with that of
the latter. Further, the sizes of the piezoelectric sheets and the
numbers of the layers included in the former are same as those
included in the latter and, therefore, the device size of the
former is substantially identical with that of the latter. However,
the output part of the former includes the internal electrodes
having a larger area than those of the input parts and, therefore,
the volume of the output part increases effectively. Accordingly,
the mechanical vibration may be efficiently converted into the
electric power and the output power may be increased without
generating heat and increasing the device size.
[0028] A second preferred embodiment in accordance with the present
invention will now be described with reference to FIGS. 4 and 5.
Like reference numerals used in the first and the second preferred
embodiments refer to the like elements.
[0029] FIG. 4 presents a laminated structure of a piezoelectric
transformer in accordance with the second preferred embodiment of
the present invention.
[0030] As shown in FIG. 4, disjointed internal electrodes 54A to
54D, each having a round shape, are formed on an upper sheet 54 of
each input part 10. The electrodes 54A and 54B are exposed at a
front edge of the upper sheet 54 and the electrodes 54C and 54D are
exposed at a rear edge of the upper sheet 54. Further, an internal
electrode 56A is formed on a lower sheet 56 such that the internal
electrode 56A overlaps with the areas of the internal electrodes
54A and 54D on the upper sheet when viewed from top. On the lower
sheet 56 of each input part 10, there is also formed an internal
electrode 56B such that the internal electrode 56B overlaps with
the areas of the internal electrodes 54B and 54C on the upper sheet
when viewed from top.
[0031] Meanwhile, rectangular-shaped internal electrodes 64A to 64D
are formed separately on a first sheet 64 in the output part 20
such that two electrodes 64B and 64C are exposed at the right edge
of the first sheet 64 and the remaining electrodes are exposed at
the left edge of the first sheet 64. Further, a rectangular-shaped
internal electrode 66A is formed on a second sheet 66 such that the
internal electrode 66A overlaps with portions of the areas of the
internal electrodes 64A and 64B when viewed from top. A
rectangular-shaped internal electrode 66B is also formed on the
second sheet 66 such that the internal electrode 66B overlaps with
portions of the areas of the internal electrodes 64C and 64D.
[0032] Insulating sheets 30 are provided between the input part 10
and the output part 20 to separate the former from the latter as
shown in FIG. 1. Further, protective sheets 32 are provided as an
uppermost layer and a lowermost layer of the piezoelectric
transformer as shown in FIG. 4.
[0033] All the sheets are stacked as shown in FIG. 4 and compressed
to thereby form a stacked body. The stacked body is diced into four
parts as illustrated in FIGS. 5A and 5B, thereby forming four
laminated bodies. The input part 10 is diced along lines LA and LB
as shown in FIG. 5A and the internal electrodes 56A and 56B are
thereby exposed at diced edges thereof. Further, the output part 20
is diced along lines LA and LB as shown in FIG. 5B and the internal
electrodes 66A and 66B are thereby exposed at diced edges thereof.
After dicing, a binder removing process and a sintering process are
performed and then external electrodes are formed on the laminated
body in a similar way as illustrated in FIG. 2, thereby obtaining
the piezoelectric transformer.
[0034] The piezoelectric transformer in accordance with the second
preferred embodiment brings about the same effects as that of the
first preferred embodiment although the shape of the internal
electrodes and extending directions from the internal electrodes
thereof are different from those of the piezoelectric transformer
of the first embodiment.
[0035] Since the output part of the piezoelectric transformer in
accordance with the present invention includes the internal
electrodes having larger areas than those of the input part, the
output power can be increased while heat generation is suppressed
and the size thereof is not increased.
[0036] It is to be appreciated that the shapes of piezoelectric
sheets or the electrodes, the locations of external electrodes on a
laminated body and the number of piezoelectric sheets may be varied
appropriately if necessary. Further, various known materials may be
used as the piezoelectric material or electrode material.
[0037] Since the piezoelectric transformer in accordance with the
present invention can produce a large output power, the
piezoelectric transformer of the present invention may be
preferably used as a step-up transformer. However, the present
invention may also be applied in fabricating step-down transformers
as well.
[0038] While the present invention has been described with respect
to the particular embodiments, it will be apparent to those skilled
in the art that various changes and modifications may be made
without departing from the spirit and scope of the invention as
defined in the following claims.
* * * * *