U.S. patent application number 09/745291 was filed with the patent office on 2001-09-20 for infrared reflective color pigment.
Invention is credited to Blonski, Robert P., Pipoly, Richard A., Sliwinski, Terrence R..
Application Number | 20010022151 09/745291 |
Document ID | / |
Family ID | 22654614 |
Filed Date | 2001-09-20 |
United States Patent
Application |
20010022151 |
Kind Code |
A1 |
Sliwinski, Terrence R. ; et
al. |
September 20, 2001 |
Infrared reflective color pigment
Abstract
The present invention provides new solid solutions having a
corundum-hematite crystalline structure which are useful as
inorganic color pigments. Solid solutions according to the present
invention include a host component having a corundum-hematite
crystalline structure which contains as guest components one or
more elements from the group consisting of aluminum, antimony,
bismuth, boron, chrome, cobalt, gallium, indium, iron, lanthanum,
lithium, magnesium, manganese, molybdenum, neodymium, nickel,
niobium, silicon, tin, titanium, vanadium, and zinc. Solid
solutions according to the present invention are formed by
thoroughly mixing compounds, usually metal oxides or precursors
thereof, which contain the host and guest components and then
calcining the compounds to form the solid solutions having the
corundum-hematite crystalline structure. Some of the new solid
solutions according to the present invention exhibit relatively low
Y CIE tri-stimulus values and relatively high near infrared
reflectance.
Inventors: |
Sliwinski, Terrence R.;
(Brookpark, OH) ; Pipoly, Richard A.; (Garfield
Heights, OH) ; Blonski, Robert P.; (North Royalton,
OH) |
Correspondence
Address: |
RANKIN, HILL, PORTER & CLARK, LLP
700 HUNTINGTON BUILDING
925 EUCLID AVENUE
CLEVELAND
OH
44115-1405
US
|
Family ID: |
22654614 |
Appl. No.: |
09/745291 |
Filed: |
December 20, 2000 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
09745291 |
Dec 20, 2000 |
|
|
|
09178957 |
Oct 26, 1998 |
|
|
|
6174360 |
|
|
|
|
Current U.S.
Class: |
106/453 ;
106/404; 106/459 |
Current CPC
Class: |
C01P 2002/50 20130101;
C09C 3/06 20130101; C01P 2004/62 20130101; C01P 2006/60 20130101;
C09C 1/34 20130101; C01P 2004/61 20130101; C09D 7/62 20180101; C08K
9/02 20130101; C08K 3/22 20130101; C01P 2002/82 20130101 |
Class at
Publication: |
106/453 ;
106/404; 106/459 |
International
Class: |
C09C 001/28 |
Claims
What is claimed:
1. A solid solution comprising a host component having the
corundum-hematite crystalline structure, said host component
comprising iron oxide, and a guest component, said guest component
being incorporated into the crystalline lattice structure of said
host component, said guest component comprising metal oxides or
precursors thereof having as cations the elements aluminum, chrome,
and titanium, said solid solution having a Y CIE tri-stimulus value
below about 10 as measured on a neat pressed cup powder sample
using a Diano Matchscan II Spectrophotometer using a 1931 CIE 2
degree observer with a C Illuminant in accordance with the
procedures set forth in ASTM Standard E308 (1996), Standard
Practice for Computing the Colors of Objects by Using the CIE
System, and a reflectance above about 60% as measured on a neat
pressed cup powder sample using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory at a wavelength of 2.5 .mu.m.
2. The solid solution as in claim 1 wherein cations of the element
iron comprise from about 45% to about 98% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 0.1% to about 43% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 15% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 10% of the weight of all cations
in the crystalline lattice.
3. The solid solution as in claim 1 wherein cations of the element
iron comprise from about 60% to about 95% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 2% to about 37% of the weight of all cations in
the crystalline lattice, cations of the element aluminum comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice, and cations of the element titanium comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice.
4. The solid solution as in claim 1 wherein cations of the element
iron comprise from about 70% to about 82% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 17% to about 29% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 0.5% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 0.5% of the weight of all cations
in the crystalline lattice.
5. The solid solution as in claim 1 having a reflectance above
about 70% as measured on a neat pressed cup powder sample using a
Perkin Lambda 19 Spectrophotometer equipped with a Labsphere
RSA-PE-19 reflectance spectroscopy accessory at a wavelength of 2.5
.mu.m.
6. The solid solution as in claim 1 wherein said guest component
further comprises a metal oxide or precursor thereof having as a
cation the element molybdenum.
7. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 45% to about 98% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 0.1% to about 43% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 15% of the weight of all cations
in the crystalline lattice, cations of the element molybdenum
comprise from about 0.1% to about 10% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 10% of the weight of all cations
in the crystalline lattice.
8. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 60% to about 95% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 2% to about 37% of the weight of all cations in
the crystalline lattice, cations of the element aluminum comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice, cations of the element molybdenum comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice, and cations of the element titanium comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice.
9. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 55% to about 69% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 30% to about 42% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 2% of the weight of all cations
in the crystalline lattice, cations of the element molybdenum
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice.
10. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 58% to about 72% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 26% to about 38% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 2% of the weight of all cations
in the crystalline lattice, cations of the element molybdenum
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice.
11. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 72% to about 86% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 13% to about 25% of the weight of all cations
in the crystalline lattice, cations of the element aluminum
comprise from about 0.1% to about 2% of the weight of all cations
in the crystalline lattice, cations of the element molybdenum
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice, and cations of the element titanium
comprise from about 0.1% to about 1% of the weight of all cations
in the crystalline lattice.
12. The solid solution as in claim 6 wherein cations of the element
iron comprise from about 87% to about 98% of the weight of all
cations in the crystalline lattice, cations of the element chrome
comprise from about 2% to about 10% of the weight of all cations in
the crystalline lattice, cations of the element aluminum comprise
from about 0.1% to about 2% of the weight of all cations in the
crystalline lattice, cations of the element molybdenum comprise
from about 0.1% to about 1% of the weight of all cations in the
crystalline lattice, and cations of the element titanium comprise
from about 0.1% to about 1% of the weight of all cations in the
crystalline lattice.
13. The solid solution as in claim 6 having a reflectance above
about 70% as measured on a neat pressed cup powder sample using a
Perkin Lambda 19 Spectrophotometer equipped with a Labsphere
RSA-PE-19 reflectance spectroscopy accessory at a wavelength of 2.5
.mu.m.
14. A pigment comprising a solid solution having the
corundum-hematite crystalline structure, said pigment having a Y
CIE tri-stimulus value below about 10 as measured on a neat pressed
cup powder sample using a Diano Matchscan II Spectrophotometer
using a 1931 CIE 2 degree observer with a C Illuminant in
accordance with the procedures set forth in ASTM Standard E308
(1996), Standard Practice for Computing the Colors of Objects by
Using the CIE System, and a reflectance above about 60% as measured
on a neat pressed cup powder sample using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory at a wavelength of 2.5 .mu.m.
15. The pigment as in claim 14 having a reflectance above about 70%
as measured on a neat pressed cup powder sample using a Perkin
Lambda 19 Spectrophotometer equipped with a Labsphere RSA-PE-19
reflectance spectroscopy accessory at a wavelength of 2.5
.mu.m.
16. The pigment as in claim 14 wherein said solid solution
comprises a host component and at least one guest component
incorporated into the crystalline lattice structure of said host
component, said host component comprising iron oxide.
17. The pigment as in claim 16 wherein said guest component
comprises one or more metal oxides or precursors thereof having as
cations elements selected from the group consisting of aluminum,
antimony, bismuth, boron, chrome, cobalt, gallium, indium,
lanthanum, lithium, magnesium, manganese, molybdenum, neodymium,
nickel, niobium, silicon, tin, titanium, vanadium, and zinc.
18. A building material that contains a pigment having a Y CIE
tri-stimulus value below about 10 as measured on a neat pressed cup
powder sample using a Diano Matchscan II Spectrophotometer using a
1931 CIE 2 degree observer with a C Illuminant in accordance with
the procedures set forth in ASTM Standard E308 (1996), Standard
Practice for Computing the Colors of Objects by Using the CIE
System, and a reflectance above about 60% as measured on a neat
pressed cup powder sample using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory at a wavelength of 2.5 .mu.m.
19. The building material as in claim 18 comprising stucco.
20. The building material as in claim 18 comprising roofing
tile.
21. The building material as in claim 18 comprising roofing
granules.
22. The building material as in claim 18 comprising roofing
shingles.
23. The building material as in claim 18 comprising brick.
Description
REFERENCE TO PRIOR APPLICATION
[0001] This is a continuation-in-part of application Ser. No.
09/178,957, filed Oct. 26, 1998.
FIELD OF INVENTION
[0002] The present invention concerns new solid solutions which are
useful as inorganic color pigments. More particularly, the present
invention concerns new solid solutions having a corundum-hematite
crystalline structure which are useful as inorganic color pigments,
some of which exhibit low Y CIE tri-stimulus values and high
reflectivity in the near infrared portion of the electromagnetic
spectrum.
BACKGROUND OF THE INVENTION
[0003] Chromium green-black hematite (basic chemical formula:
Cr.sub.2O.sub.3) is an inorganic color pigment, C.I. Pigment Green
17, having a corundum-hematite crystalline structure. It is
commonly used to impart a green color to ceramics, paints,
polymers, and other materials. The DCMA Classification and Chemical
Description of the Complex Inorganic Color Pigments, Third Addition
(1991), published by the Dry Color Manufacturer's Association,
states that its composition may include any one or a combination of
the modifiers Al.sub.2O.sub.3 (alumina), Fe.sub.2O.sub.3 (iron
oxide), or Mn.sub.2O.sub.3 (manganese oxide).
[0004] Iron brown hematite (basic chemical formula:
Fe.sub.2O.sub.3), is an inorganic pigment, C.I. Pigment Red 101
& 102, having a dark brown to black color and a
corundum-hematite crystalline structure. See DCMA Classification
and Chemical Description of the Complex Inorganic Color Pigments,
Third Addition (1991). It is commonly used to impart dark brown to
black color to ceramics, paints, plastics, and other material. Its
composition may include any one or a combination of the modifiers
Cr.sub.2O.sub.3 (chrome oxide),, Fe.sub.2O.sub.3 (iron oxide),
Mn.sub.2O.sub.3 (manganese oxide), or NiO (nickel oxide).
[0005] Chromium green-black hematite is one of the principle
pigments used in the manufacture of green shade military camouflage
paint and netting. In such applications, chromium green-black
hematite is combined with cobalt bearing mixed metal oxides, such
as cobalt containing spinel pigment V12600 available from Ferro
Corporation of Cleveland, Ohio. This combination of pigments is
effective in simulating the reflectivity of chlorophyl in the
visible portion of the electromagnetic spectrum, being that portion
of the spectrum which is viewable by the naked eye with wavelengths
ranging from approximately 0.40 .mu.m to 0.70 .mu.m.
[0006] Chlorophyl, which is an organic pigment, generally exhibits
a relatively uniform high degree of reflectivity in the near
infrared, being that portion of the electromagnetic spectrum with
wavelengths ranging from approximately 0.7 .mu.m, to 2.5 .mu.m.
Cobalt, however, exhibits a strong absorption band (i.e., low
reflectivity) in a portion of the near infrared with wavelengths
ranging from approximately 1.2 .mu.m to 1.6 .mu.m. In recent years,
advancements in imaging technology have made it possible to
contrast known military green shade camouflage painted or covered
objects from the background foliage in that portion of the near
infrared. A substitute military green shade camouflage pigment
which contains no cobalt and which closely matches the reflectivity
of chlorophyl in the visible and near infrared is therefore highly
desired.
[0007] In order to satisfy military specifications, a substitute
green shade camouflage pigment would have to exhibit a dark drab
green appearance in the visible portion of the spectrum and would
also have to simulate the reflectance curve for chlorophyl in the
near infrared. Generally speaking, known inorganic pigments which
exhibit a low degree of reflectivity in the visible portion of the
light spectrum (i.e., dark drab colored pigments) also tend to
exhibit a correspondingly low degree of reflectivity (i.e., high
absorption) in other portions of the light spectrum, including the
near infrared. A chromium green-black hematite pigment manufactured
by Bayer Corporation of Germany, product number AC 5303, was
observed to exhibit a higher near infrared reflectance than other
chromium green-black hematite sources (this pigment, however, does
not have the desired dark drab appearance in the visible spectrum
required for military green shade camouflage paint applications).
It was found by chemical analysis that this pigment contained both
alumina and titania (basic chemical formula: TiO.sub.2) as minor
additives. A search failed to disclose any references teaching the
use of alumina and titania to improve the near infrared reflectance
of chromium green-black hematite pigments.
SUMMARY OF INVENTION
[0008] The present invention provides new solid solutions having a
corundum-hematite crystalline structure which are useful as
inorganic color pigments. Solid solutions according to the present
invention are comprised of a host component having a
corundum-hematite crystalline structure which contains as a guest
component one or more elements from the group consisting of
aluminum, antimony, bismuth, boron, chrome, cobalt, gallium,
indium, iron, lanthanum, lithium, magnesium, manganese, molybdenum,
neodymium, nickel, niobium, silicon, tin, titanium, vanadium, and
zinc. Solid solutions according to the present invention are formed
by thoroughly mixing compounds, usually metal oxides or precursors
thereof, which contain the host and guest components and then
calcining the compounds to form the solid solutions having the
corundum-hematite crystalline structure.
[0009] Some of the new solid solutions according to the present
invention, such as for example chrome oxide as a host component
containing the elements iron, boron, and titanium as guest
components, exhibit dark drab colors in the visible and high
reflectivity in the near infrared portions of the electromagnetic
spectrum. One of the primary uses for new solid solutions having
these properties would be as inorganic color pigments in military
camouflage paint or netting applications, which would permit the
radiation signature of a painted or covered object to be tailored
to match the reflectance curve of the background foliage in the
visible and near infrared portions of the electromagnetic spectrum.
Because many of these new solid solutions exhibit relatively high
near infrared reflectance, they would also be suitable for use in
the general paint and polymer markets, most specifically for
architectural applications where increased near infrared
reflectance would result in lower heat build-up and thus lower
energy costs.
[0010] The foregoing and other features of the invention are
hereinafter more fully described and particularly pointed out in
the claims, the following description setting forth in detail
certain illustrative embodiments of the invention, these being
indicative, however, of but a few of the various ways in which the
principles of the present invention may be employed.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for the infrared reflective
color pigments embodied in Examples 1, 6, and 7 herein as compared
to a standard chromium green-black hematite pigment.
[0012] FIG. 2 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for the infrared reflective
color pigments embodied in Examples 3, 4, and 5 herein as compared
to a standard chromium green-black hematite pigment.
[0013] FIG. 3 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for the infrared reflective
color pigments embodied in Examples 8, 10, and 11 herein as
compared to a standard chromium green-black hematite pigment.
[0014] FIG. 4 is a graph showing Y CIE tri-stimulus values and
percent reflectance as measured at a wavelength of 2.5 .mu.m for
the infrared reflective color pigments embodied in Examples 1
through 16 herein as compared to a standard chromium green-black
hematite pigment.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
[0015] In accordance with the present invention, solid solutions
having a corundum-hematite crystalline structure can be obtained by
using metal oxides, or precursors thereof, which form
corundum-hematite lattices as host components and incorporating
into them as guest components such metal oxides, or precursors
thereof, the cations of which possess radii which are comparable
with the radii of the metal ions, or the statistical mean of the
radii of the metal ions of the host components. The guest
components are incorporated in such proportions relative to one
another that the ratio of the sum of the added cations to the sum
of the added anions, while preserving statistical
electro-neutrality in the lattice, is substantially 2:3. The total
proportion of the guest components may be of any value, but the
amount is preferably not greater than approximately the total
amount of the host components. Conceptually, these additions can be
considered in a manner similar to the Hund crystalline solid
solution patents, U.S. Pat. Nos. 3,022,186, 3,091,544, and
4,285,726, the specifications of which are hereby incorporated by
reference. Essentially, guest components or dopants can be added to
the host component or crystalline lattice as long as the
crystalline structure, charge, and cation sites of the host
component are substantially conserved.
[0016] Table 1 below sets forth some of the various compounds which
have a corundum-hematite crystalline structure and comparable
lattice constant ranges so as to be capable of forming solid
solutions according to the present invention:
1TABLE 1 Representative Corundum-Hematite Crystalline Lattice
Constants Formula A C JCPDS Card Number Cr.sub.2O.sub.3 4.958.ANG.
13.593.ANG. 38-1479 Al.sub.2O.sub.3 4.758.ANG. 12.991.ANG. 10-173
V.sub.2O.sub.3 4.920.ANG. 13.883.ANG. 34-187 Ga.sub.2O.sub.3
4.979.ANG. 13.429.ANG. 6-503 Fe.sub.2O.sub.3 5.036.ANG. 13.749.ANG.
33-664 Mn.sub.2O.sub.3 5.04.ANG. 14.12.ANG. 33-900 Ti.sub.2O.sub.3
5.139.ANG. 13.659.ANG. 10-63 In.sub.2O.sub.3 5.49.ANG. 14.52.ANG.
22-336 TiBO.sub.3 4.67.ANG. 14.90.ANG. 17-310 NiTiO.sub.3
5.032.ANG. 13.791.ANG. 33-961 MgTiO.sub.3 5.054.ANG. 13.898.ANG.
6-494 CoTiO.sub.3 5.068.ANG. 13.922.ANG. 15-866 ZnTiO.sub.3
5.078.ANG. 13.927.ANG. 25-1500 FeTiO.sub.3 5.088.ANG. 14.093.ANG.
29-733 MnTiO.sub.3 5.140.ANG. 14.290.ANG. 29-902 CrBO.sub.3
4.578.ANG. 14.260.ANG. 15-663 NiCrO.sub.3 4.925.ANG. 13.504.ANG.
22-748 FeBO.sub.3 4.613.ANG. 14.470.ANG. 21-423 FeMoO.sub.3
4.67.ANG. 15.03.ANG. 19-611 FeSn(BO.sub.3).sub.2 4.733.ANG.
15.08.ANG. 18-657 BiFeO.sub.3 5.57.ANG. 13.84.ANG. 20-169
AlBO.sub.3 4.463.ANG. 13.746.ANG. 32-4
Mg.sub.3Al.sub.2Si.sub.3O.sub.12 4.755.ANG. 13.360.ANG. 30-788
NdAlO.sub.3 5.326.ANG. 12.920.ANG. 29-57 LaAlO.sub.3 5.344.ANG.
13.110.ANG. 31-22 MnSnO.sub.3 5.358.ANG. 14.505.ANG. 33-913
LiNbO.sub.3 5.149.ANG. 13.862.ANG. 20-631 LaCoO.sub.3 5.441.ANG.
13.088.ANG. 25-1060 MgSiO.sub.3 4.725.ANG. 13.563.ANG. 39-300
ZnSiO.sub.3 4.746.ANG. 13.755.ANG. 34-575 Mn(Sb,Fe)O.sub.3
5.226.ANG. 14.325.ANG. 20-699
[0017] It should be noted that Table 1 does not contain all of the
possible compounds that can form solid solutions according to the
present invention. For example, molybdenum can be incorporated as a
guest component into a chrome oxide host according to the present
invention. One would reasonably expect that since iron and chrome
have lattice constants which are very close, and both form
extensive solid solutions, CrMoO.sub.3 would exist and be similar
in crystal structure to FeMoO.sub.3, although CrMoO.sub.3 is not
shown in Table 1. Solid solutions according to the present
invention, irrespective of whether shown on Table 1, are comprised
of a host component having a corundum-hematite crystalline
structure which contain as a guest component one or more elements
from the group consisting of aluminum, antimony, bismuth, boron,
chrome, cobalt, gallium, indium, iron, lanthanum, lithium,
magnesium, manganese, molybdenum, neodymium, nickel, niobium,
silicon, tin, titanium, vanadium, and zinc.
[0018] Solid solutions according to the present invention are
prepared by thoroughly dry or wet mixing compounds containing the
host and guest components and then calcining the components to form
a solid solution. Generally, the host and guest components will
both comprise metal oxides. However, precursors thereof, meaning
compounds which at the calcining temperature are converted in the
presence of an oxidizing atmosphere into metal oxides can also be
used. Such precursors include, for example: aluminum hydrate (basic
chemical formula: Al(OH).sub.3)) which can be used as a precursor
for aluminum oxide; manganese carbonate (basic chemical formula:
MnCO.sub.3) which can be used as a precursor for manganese
sesquioxide (basic chemical formula: Mn.sub.2O.sub.3); and indium
hydroxide (basic chemical formula: In(OH).sub.3) which can be used
as a precursor for indium oxide (basic chemical formula:
In.sub.2O.sub.3). It will be appreciated that a wide variety of
precursors can be used to practice the invention, and that the
selection of precursors is not per se critical.
[0019] The host and guest components are preferably milled to a
fine powder and then thoroughly mixed in the appropriate
proportions. Milling fineness is not critical, but average particle
size diameters from approximately 0.2 .mu.m to about 5 .mu.m are
preferred. Standard pigment grade metal oxide powders and
precursors currently available on the market can generally be used
without additional milling prior to mixing. Mixing can occur in a
dry state, or the powders can be mixed in solution, dried, and then
milled again if necessary to break up any particle agglomerations.
The mixture is then calcined to form crystalline solid solutions.
Calcination can be achieved in a standard refractory sagger, kiln,
or other suitable device to form the solid solutions. Calcination
can also be achieved through the use of a rotary calciner.
Calcination sufficient to form solid solutions generally occurs at
a temperature of from about 1,750.degree. F. to about 2,250.degree.
F. for about 0.5 to about 24 hours. However, it will be understood
to those practicing the invention that a wide range of calcination
temperatures and times can be used, and that so long as the
temperature and length of time used is sufficient to form the solid
solutions according to the present invention, the temperature and
length of time of calcination is not per se critical.
[0020] In most instances, it is unnecessary to mill or grind solid
solutions formed according to the present invention after
calcination. However, when a smaller average particle size is
desired or when a particular application requires a strict
avoidance of minor particle agglomerations, additional milling or
grinding of the solid solutions can be performed.
[0021] It should be apparent to those skilled in the art that the
method of the present invention can be practiced to manufacture a
wide variety of solid solutions having utility as inorganic
pigments for use in ceramics, polymers, paints, and other
materials. The selection of guest and host components used to form
solid solutions can readily be made within the total specification
disclosure. In similar fashion, it is to be appreciated that the
process steps of the method, including mixing, calcination, and
product recovery, are generally conventional and thus can be
readily determined by those skilled in the art.
[0022] The following examples are intended to illustrate the
invention without limiting it in any way. All raw materials
referenced in the examples are standard pigment grade powders
unless otherwise indicated.
EXAMPLE 1
[0023] 93.46 grams chrome oxide, 0.94 grams iron oxide, 2.38 grams
aluminum oxide from aluminum hydrate and 1.88 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 2
[0024] 93.02 grams chrome oxide, 0.93 grams iron oxide, 3.35 grams
aluminum oxide from aluminum hydrate and 0.83 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 3
[0025] 93.23 grams chrome oxide, 0.92 grams iron oxide, 0.43 grams
molybdenum trioxide (basic chemical formula: MoO.sub.3), 3.11 grams
aluminum oxide from aluminum hydrate and 0.57 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 4
[0026] 95.49 grams chrome oxide, 0.96 grams iron oxide, 1.63 grams
boron oxide (basic chemical formula: B.sub.2O.sub.3) and 1.92 grams
titanium dioxide were thoroughly mixed in a Waring blender and
calcined in a crucible at 2,000.degree. F. for three hours.
EXAMPLE 5
[0027] 86.79 grams chrome oxide, 0.96 grams iron oxide, 10.59 grams
bismuth trioxide (basic chemical formula: Bi.sub.2O.sub.3) and 1.75
grams titanium dioxide were thoroughly mixed in a Waring blender
and calcined in a crucible at 2,000.degree. F. for three hours.
EXAMPLE 6
[0028] 91.86 grams chrome oxide, 0.92 grams iron oxide, 2.42 grams
aluminum oxide from aluminum hydrate and 3.56 grams tin oxide
(basic chemical formula: SnO) were thoroughly mixed in a Waring
blender and calcined in a crucible at 2,000.degree. F. for three
hours.
EXAMPLE 7
[0029] 93.87 grams chrome oxide, 0.94 grams iron oxide, 2.39 grams
aluminum oxide from aluminum hydrate and 1.45 grams silicon dioxide
(basic chemical formula: SiO.sub.2) were thoroughly mixed in a
Waring blender and calcined in a crucible at 2,000.degree. F. for
three hours.
EXAMPLE 8
[0030] 93.05 grams chrome oxide, 0.93 grams manganese sesquioxide
from manganese carbonate, 2.68 grams aluminum oxide from aluminum
hydrate and 1.39 grams titanium dioxide were thoroughly mixed in a
Waring blender and calcined in a crucible at 2,000.degree. F. for
three hours.
EXAMPLE 9
[0031] 89.96 grams chrome oxide, 0.90 grams iron oxide, 6.13 grams
indium oxide from indium hydroxide and 1.81 grams titanium dioxide
were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 10
[0032] 90.06 grams chrome oxide, 0.91 grams iron oxide, 7.22 grams
lanthanum oxide (basic chemical formula: La.sub.2O.sub.3) and 1.81
grams titanium dioxide were thoroughly mixed in a Waring blender
and calcined in a crucible at 2,000.degree. F. for three hours.
EXAMPLE 11
[0033] 89.85 grams chrome oxide, 0.90 grams iron oxide, 7.44 grams
neodymium oxide (basic chemical formula: Nd.sub.2(SO.sub.4).sub.3)
and 1.81 grams titanium dioxide were thoroughly mixed in a Waring
blender and calcined in a crucible at 2,000.degree. F. for three
hours.
EXAMPLE 12
[0034] 95.08 grams chrome oxide, 0.96 grams iron oxide, 2.50 grams
aluminum oxide from aluminum hydrate and 0.06 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 13
[0035] 79.36 grams chrome oxide, 0.80 grams iron oxide, 9.98 grams
aluminum oxide from aluminum hydrate and 4.27 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 2,000.degree. F. for three hours.
EXAMPLE 14
[0036] 99.06 grams chrome oxide and 0.94 grams iron oxide were
thoroughly mixed in a Waring blender and calcined in a crucible at
2,000.degree. F. for three hours.
EXAMPLE 15
[0037] 93.15 grams chrome oxide, 0.88 grams iron oxide, 3.06 grams
aluminum oxide from aluminum hydrate and 1.19 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 1,850.degree. F. for three hours.
EXAMPLE 16
[0038] 48.46 grams chrome oxide, 48.46 grams iron oxide, 1.58 grams
aluminum oxide from aluminum hydrate and 0.61 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined in a
crucible at 1,850.degree. F. for three hours.
[0039] FIG. 1 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for infrared reflective color
pigments prepared as described in Examples 1, 6, and 7 above as
compared to a standard chromium green-black hematite pigment
available as G-4099 from Elementis Pigments, Inc. of Fairview
Heights, Ill. Percent reflectance measurements were made on neat
pressed cup powder samples using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory. FIG. 1 shows that some of the infrared
reflective color pigments according to the present invention
exhibit significantly higher near infrared reflectance than known
chromium green-black hematite pigments. FIG. 1 also shows that
elements such as silicon and tin can be substituted for titanium in
the crystal lattice structure of pigments according to the present
invention.
[0040] FIG. 2 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for infrared reflective color
pigments prepared as described in Examples 3, 4, and 5 above as
compared a standard chromium green-black hematite pigment available
as G-4099 from Elementis Pigments, Inc. of Fairview Heights, Ill.
Percent reflectance measurements were made on neat pressed cup
powder samples using a Perkin Lambda 19 Spectrophotometer equipped
with a Labsphere RSA-PE-19 reflectance spectroscopy accessory. FIG.
2 shows that elements such as bismuth, boron, and molybdenum can be
substituted for the aluminum cation in the crystal lattice
structure of pigments according to the present invention, allowing
for adjustments of the visible color while retaining the preferable
high near infrared reflectance.
[0041] FIG. 3 is a graph showing percent reflectance at wavelengths
ranging from 0.6 .mu.m to 2.5 .mu.m for infrared reflective color
pigments prepared as described in Examples 8, 10, and 11 above as
compared to a standard chromium green-black hematite pigment
available as G-4099 from Elementis Pigments, Inc. of Fairview
Heights, Ill. Percent reflectance measurements were made on neat
pressed cup powder samples using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory. FIG. 3 shows that elements such as
manganese, lanthanum, and neodymium can be substituted for the iron
or aluminum cations in the crystal lattice structure of pigments
according to the present invention, allowing for adjustments of the
visible color while retaining the preferable high near infrared
reflectance. By adjusting the quantity and identity of the
combinations of cations in crystalline lattice structure in
pigments according to the present invention, a wide range of colors
can be produced.
[0042] FIG. 4 is a graph showing Y CIE tri-stimulus values versus
percent reflectance measured at a wavelength of 2.5 .mu.m for the
infrared reflective color pigments prepared as described in
Examples 1 through 16 above as compared to a standard chromium
green-black hematite pigment available as G-4099 from Elementis
Pigments, Inc. of Fairview Heights, Ill. Y CIE tri-stimulus values
were measured on neat pressed cup powder samples using a Diano
Matchscan II Spectrophotometer using a 1931 CIE 2 degree observer
with a C Illuminant in accordance with the procedures set forth in
ASTM Standard E308 (1996), Standard Practice for Computing the
Colors of Objects by Using the CIE System, the text of which can be
purchased from the American Society for Testing and Materials of
West Conshohocken, Pa. Percent reflectance measurements were made
on neat pressed cup powder samples using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory. FIG. 4 shows that some of the new solid
solutions according to the present invention, such as those
embodied in Examples 1, 3, 4, 8, 10, 11, 13, and 16, exhibit
relatively low Y CIE tri-stimulus values (13.53 or less) and
relatively high near infrared reflectance at 2.5 .mu.m (71.7% or
higher). Generally speaking, the Y CIE tri-stimulus value refers to
the lightness or darkness of a color, with a lower Y CIE
tri-stimulus value correlating with a darker color.
[0043] Table 2 below lists the Y CIE tri-stimulus values, x and y
CIE chromaticity coordinates, and percent reflectance at various
wavelengths in the near infrared spectrum for the solid solutions
embodied in Examples 1 through 16 as compared to a standard
chromium green-black hematite pigment available as G-4099 from
Elementis Pigments, Inc. of Fairview Heights, Ill. Y CIE
tri-stimulus values and x and y CIE chromaticity coordinates were
measured on neat pressed cup powder samples using a Diano Matchscan
II Spectrophotometer using a 1931 CIE 2 degree observer with a C
Illuminant in accordance with the procedures set forth in ASTM
Standard E308 (1996), Standard Practice for Computing the Colors of
Objects by Using the CIE System, the text of which can be purchased
from the American Society for Testing and Materials of West
Conshohocken, Pa. Percent reflectance measurements were made on
neat pressed cup powder samples using a Perkin Lambda 19
Spectrophotometer equipped with a Labsphere RSA-PE-19 reflectance
spectroscopy accessory.
2TABLE 2 Color and % IR Reflectance (Pressed Cups) Example Y x y
0.72 .mu.m 0.80 .mu.m 0.90 .mu.m 1.0 .mu.m 1.5 .mu.m 2.5 .mu.m
Standard 20.33 .315 .409 35.0 59.6 58.9 57.4 55.0 56.0 1 11.91 .328
.378 25.0 57.0 67.8 66.2 72.0 78.0 2 15.99 .331 .406 24.2 59.6 71.3
69.0 73.9 76.3 3 12.61 .333 .391 28.6 66.5 79.1 76.2 84.2 88.5 4
10.77 .323 .372 23.8 62.2 74.8 73.0 77.4 87.3 5 12.64 .332 .386
27.0 59.3 66.2 64.3 64.3 74.8 6 16.53 .326 .399 33.3 63.1 67.2 66.0
67.7 71.9 7 16.81 .326 .402 32.8 59.0 61.9 60.6 59.4 61.5 8 10.71
.321 .374 21.5 50.5 68.3 74.8 76.0 81.0 9 12.04 .331 .379 25.5 57.2
63.8 61.1 60.9 75.0 10 11.50 .330 .376 25.2 60.0 68.0 66.2 70.0
81.4 11 11.10 .326 .368 24.0 58.1 70.0 69.2 75.2 80.0 12 14.28 .330
.405 29.7 56.1 59.5 58.1 57.0 58.0 13 13.53 .334 .398 31.6 64.1
72.7 70.0 71.2 83.2 14 15.35 .334 .408 27.4 59.2 62.1 61.0 60.0
65.0 15 14.82 .330 .403 30.6 60.1 67.2 65.5 69.9 75.4 16 6.43 .328
.325 11.6 22.1 34.5 37.0 63.6 71.7
EXAMPLE 17
[0044] 36.14 grams chrome oxide, 60.32 grams iron oxide, 1.61 grams
of aluminum oxide from aluminum hydrate, 0.62 grams titanium
dioxide and 0.40 grams molybdic oxide were thoroughly mixed in a
Waring blender and calcined at 1750.degree. F. for seven hours.
EXAMPLE 18
[0045] 32.32 grams chrome oxide, 64.48 grams iron oxide, 1.44 grams
of aluminum oxide from aluminum hydrate, 0.56 grams titanium
dioxide and 0.40 grams molybdic oxide were thoroughly mixed in a
Waring blender and calcined at 1750.degree. F. for seven hours.
EXAMPLE 19
[0046] 19.48 grams chrome oxide, 77.94 grams iron oxide, 1.12 grams
of aluminum oxide from aluminum hydrate, 0.44 grams titanium
dioxide and 0.40 grams molybdic oxide were thoroughly mixed in a
Waring blender and calcined at 1900.degree. F. for seven hours.
EXAMPLE 20
[0047] 4.95 grams chrome oxide, 94.10 grams iron oxide, 0.28 grams
of aluminum oxide from aluminum hydrate, 0.11 grams titanium
dioxide and 0.40 grams molybdic oxide were thoroughly mixed in a
Waring blender and calcined at 1900.degree. F. for seven hours.
EXAMPLE 21
[0048] 23.38 grams chrome oxide, 76.05 grams iron oxide, 0.24 grams
of aluminum oxide from aluminum hydrate and 0.20 grams titanium
dioxide were thoroughly mixed in a Waring blender and calcined at
1700 EF for four hours.
[0049] Table 3 below lists the Y CIE tri-stimulus values, x and y
CIE chromaticity coordinates, and percent reflectance at various
wavelengths in the near infrared spectrum for the solid solutions
embodied in Examples 17 through 21 as compared to a standard red
hematite pigment available as R03097 from Harcross Pigments, Inc.
of Easton, Pa. Y CIE tri-stimulus values and x and y CIE
chromaticity coordinates were measured on neat pressed cup powder
samples using a Diano Matchscan II Spectrophotometer using a 1931
CIE 2 degree observer with a C Illuminant accordance with the
procedures set forth in ASTM Standard E308 (1996), Standard
Practice for Computing the Colors of Objects by Using the CIE
System, the test of which can be purchased from the American
Society for Testing and Materials of West Conshohocken, Pa. Percent
reflectance measurements were made on neat pressed cup powder
samples using a Perkin Lambda 19 Spectrophotometer equipped with a
Labsphere RSA-PE-19 reflectance spectroscopy accessory.
3TABLE 3 Color and % IR Reflectance (Pressed Cups) Example Y x y
0.72 .mu.m 0.80 .mu.m 0.90 .mu.m 1.0 .mu.m 1.5 .mu.m 2.5 .mu.m
Standard 11.64 .450 .342 36.3 27.0 28.4 43.1 44.5 28.6 17 8.31 .319
.320 15.3 17.8 26.2 27.2 56.8 64.3 18 6.66 .329 .316 12.1 19.9 26.9
32.4 73.1 71.6 19 9.27 .308 .312 11.4 16.2 21.1 29.8 59.0 68.8 20
10.03 .310 .308 16.5 18.9 20.2 34.0 54.3 61.4 21 7.01 .329 .315
16.8 28.5 32.1 44.7 76.5 79.0
[0050] One of the primary uses for new solid solutions according to
the present invention which exhibit relatively low Y CIE
tri-stimulus values and relatively high near infrared reflectance
would be as inorganic pigments in military camouflage paint or
netting applications. By using these pigments in place of known
pigments which contain cobalt, the radiation signature of a
camouflage painted or covered object can be tailored to match the
background in the visible and near infrared portions of the
electromagnetic spectrum. Moreover, because many of these new solid
solutions exhibit relatively high near infrared reflectance in a
range of colors, they would also be suitable for use in the general
paint and polymer markets, most specifically for architectural
applications, such as vinyl siding, where increased near infrared
reflectance would result in lower heat build-up and thus lower
energy costs. Due to their high IR reflectivity, pigments according
to the present invention are particularly useful in building
material applications where heat reduction is desirable such as,
for example, stucco, paint, vinyl siding, roofing tiles, roofing
granules, roofing shingles, and brick.
[0051] Additional advantages and modifications will readily occur
to those skilled in the art. Therefore, the invention in its
broader aspects is not limited to the specific details and
illustrative examples shown and described herein. Accordingly,
various modifications may be made without departing from the spirit
or scope of the general inventive concept as defined by the
appended claims and their equivalents.
* * * * *