U.S. patent application number 09/729723 was filed with the patent office on 2001-07-26 for glow plug.
Invention is credited to Kimata, Hiroyuki, Taniguchi, Masato.
Application Number | 20010009254 09/729723 |
Document ID | / |
Family ID | 18404355 |
Filed Date | 2001-07-26 |
United States Patent
Application |
20010009254 |
Kind Code |
A1 |
Taniguchi, Masato ; et
al. |
July 26, 2001 |
Glow plug
Abstract
A glow plug and method for manufacturing the same. The glow plug
includes a metallic sleeve 1; a cylindrical metallic shell 2, which
holds the metallic sleeve 1; a terminal electrode 3, which is
attached into the cylindrical metallic shell 2 while being
insulated therefrom; a ceramic heating member 4, which is fitted
into the metallic sleeve 1; and a glass coating layer 5. In the
glow plug, a portion of an ion detection electrode 411 is exposed
at the surface of an insulator 44 of the ceramic heating member 4.
The exposed portion is coated with a glass coating layer 5, which
is formed in such a manner as to extend all around the insulator 44
of the ceramic heating member 4 and has a thickness of 10-200 .mu.m
and a softening point of not lower than 600.degree. C.
Inventors: |
Taniguchi, Masato; (Aichi,
JP) ; Kimata, Hiroyuki; (Aichi, JP) |
Correspondence
Address: |
SUGHRUE, MION, ZINN, MACPEAK & SEAS, PLLC
Suite 800
2100 Pennsylvania Avenue, N.W.
Washington
DC
20037-3213
US
|
Family ID: |
18404355 |
Appl. No.: |
09/729723 |
Filed: |
December 6, 2000 |
Current U.S.
Class: |
219/270 ;
123/145A; 219/269; 219/544 |
Current CPC
Class: |
F23Q 2007/004 20130101;
F02P 19/028 20130101; F23Q 7/001 20130101; F23Q 2007/002
20130101 |
Class at
Publication: |
219/270 ;
219/269; 219/544; 123/145.00A |
International
Class: |
F23Q 007/00 |
Foreign Application Data
Date |
Code |
Application Number |
Dec 8, 1999 |
JP |
HEI. 11-349530 |
Claims
What is claimed is:
1. A glow plug comprising a ceramic heating member which in turn
comprises an insulator, a heating resistor disposed within said
insulator, and an ion detection electrode disposed within said
insulator, characterized in that a portion of said ion detection
electrode is exposed through said insulator and the exposed portion
is coated with a glass coating layer.
2. The glow plug as claimed in claim 1, wherein the glass coating
layer covers the exposed portion and extends all around a
circumference of said insulator.
3. The glow plug as claimed in claim 1, wherein the glass coating
layer has a thickness of 10-200 .mu.m.
4. The glow plug as claimed in claim 1, wherein the glass coating
layer has a softening point of not lower than 600.degree. C.
5. The glow plug as claimed in claim 1, wherein said ion detection
electrode and said heating resistor are made of the same
material.
6. The glow plug as claimed in claim 1, wherein a portion of said
ion detection electrode is exposed through an opening in said
insulator.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to a glow plug and a method
for manufacturing the same. More particularly, the invention
relates to a glow plug exhibiting excellent durability, being
capable of preventing short circuits potentially caused by adhesion
of carbon, ensuring safety, and being capable of detecting ion
current accurately, as well as to a method for manufacturing the
same.
[0003] 2. Description of the Related Art
[0004] In recent years, in order to reduce exhaust gas or exhaust
smoke from a gasoline engine or a diesel engine, the engine
combustion control system of the engine has been required to detect
the state of combustion of the engine. The state of combustion of
the engine has been detected in terms of, for example, cylinder
pressure, light from combustion, or ion current. Particularly,
detection of ion current has been considered useful, since a
chemical reaction which accompanies combustion can be observed
directly. In order to detect ion current, a glow plug into which an
ion detection electrode is incorporated has been proposed (see, for
example, Japanese Patent Application Laid-Open (kokai) No.
10-122114).
[0005] In the case of a diesel engine equipped with a glow plug
into which an ion detection electrode is incorporated, when carbon
produced in the combustion chamber adheres to the ion detection
electrode, a short circuit is formed, or a leakage current flows,
which impairs ion current detection accuracy. Accordingly, the ion
detection electrode must be exposed to a region in a temperature
zone in which carbon is burned off by a heater. Thus, the exposed
portion of the ion electrode is required to exhibit excellent heat
resistance and consumption resistance. Conventional glow plugs
which have solved the above problems include, for example, a glow
plug in which an ion detection electrode is made of a noble metal,
such as Pt, in order to ensure heat resistance and consumption
resistance thereof, or in which an exposed portion of the ion
detection electrode is metallized with a conductive layer (Japanese
Patent Application Laid-Open (kokai) No. 10-89687); and a glow plug
in which an ion detection electrode is coated with a noble metal,
such as Pt, Ir, or Rh, or an insulative porous layer, which is
formed by sintering an electrically insulative ceramic powder, such
as alumina (Japanese Patent Application Laid-Open (kokai) No.
10-110952 or 10-89226).
[0006] However, use of an ion detection electrode or a coating
layer made of a noble metal, such as Pt, results in a very
expensive glow plug. Also, use of an ion detection electrode made
of a noble metal, such as Pt, is likely to cause stress
concentration in an insulator in the vicinity of the ion detection
electrode. This is because thermal expansion differs between the
noble metal and ceramics, which the insulator is made of. As a
result, the glow plug may suffer damage, such as cracking. In the
case where an exposed portion of an ion detection electrode is
metallized with a conductive layer, there is a difficulty in
selecting a material for the coating layer. This is because the
material must exhibit corrosion resistance at an operating
temperature of a glow plug; i.e., 1000.degree. C. or higher, and
must be able to prevent separation of the coating layer which
potentially results from a difference in thermal expansion. In the
case where an exposed portion of an ion detection electrode is
coated with an insulative porous layer, the durability of the
coating layer may suffer. This is because the porous feature of the
coating layer means an increase in the surface area of the coating
layer exposed to combustion gas.
[0007] Since the tip of a glow plug assumes a high temperature,
studies have been carried out on a glow plug in which an ion
detection electrode is exposed at a side region of an insulator,
not at a tip region of the insulator, so as to ensure heat
resistance (see FIG. 1). This configuration involves difficulty in
sensing ions which have reached a side region of the insulator
opposite the ion detection electrode. Also, the orientation of the
ion detection electrode varies depending on the state of attachment
of the glow plug, resulting in variations in detection of ion
current; i.e., impaired accuracy in detection of ion current.
SUMMARY OF THE INVENTION
[0008] The present invention has been achieved in view of the
foregoing, and an object of the invention is to provide a glow plug
exhibiting excellent durability, being capable of preventing short
circuits potentially caused by adhesion of carbon, ensuring safety,
and being capable of detecting ion current accurately, as well as a
method for manufacturing the same.
[0009] The present inventors have studied a glow plug and a method
for manufacturing the same in view of the foregoing, and found that
glass, which is considered an insulating layer, exhibits sufficient
ion conductivity for detection of ion current when the temperature
thereof rises as a result of operation of an engine or a glow plug.
Based on these findings, the inventors achieved the present
invention. Specifically, they found that a glow plug including a
heating resistor and an ion detection electrode which are disposed
within an insulator exhibits excellent durability, prevents short
circuits potentially caused by adhesion of carbon, and can
accurately detect ion current, by employing the following
structural feature: a portion of the ion detection electrode is
exposed at the surface of the insulator, and the exposed portion is
coated with a glass coating layer.
[0010] A glow plug according to the invention comprises a ceramic
heating member which in turn comprises an insulator, a heating
resistor disposed within the insulator, and an ion detection
electrode disposed within the insulator. The glow plug is
characterized in that a portion of the ion detection electrode is
exposed through the insulator of the ceramic heating member and the
exposed portion is coated with a glass coating layer.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1 is a longitudinal sectional view of a glow plug
according to an embodiment of the present invention;
[0012] FIG. 2(a) is an enlarged longitudinal sectional view of a
main portion of the glow plug of FIG. 1; and
[0013] FIG. 2(b) is a sectional view taken along line B-B' of FIG.
2 (a);
[0014] FIG. 3 is a view illustrating an integrated assembly of a
heating resistor and lead wires;
[0015] FIG. 4 is a view illustrating injection molding for
manufacturing an integrated assembly of a heating resistor and lead
wires;
[0016] FIG. 5 is a view illustrating a step of forming a compact
assembly by pressing;
[0017] FIG. 6 is an enlarged longitudinal sectional view of a main
portion of a glow plug according to another embodiment of the
present invention;
[0018] FIG. 7 is a view illustrating a state in which the glow plug
of FIG. 1 is mounted on an engine while being connected to a glow
plug operation circuit; and
[0019] FIG. 8 is a side view showing a main portion of the glow
plug according to the embodiment as viewed facing an ion detection
electrode.
[0020] Reference numerals are used to identify elements shown in
the drawings as follows: A: glow plug; 1: metallic sleeve; 2:
cylindrical metallic shell; 3: terminal electrode; 4: ceramic
heating member; 41: heating resistor; 411: ion detection electrode;
42, 43: lead wires; 44: insulator; 5: glass coating layer; 61, 62,
63: external connection wires; 64, 65: external lead wires; 7:
terminal lead conduit; 8: glass seal; 9: cylinder head; 91: swirl
chamber; 92: main combustion chamber; 93: piston; 94: fuel
injection nozzle; 10, 11: glow relay; 12: battery; 13:
direct-current power source; 14: ion current detection resistor;
141: potentiometer; 15: brazing material
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0021] FIGS. 1 and 2 show an example of a glow plug of the first
embodiment of the invention.
[0022] As shown in FIG. 1, a glow plug A includes a metallic sleeve
1; a cylindrical metallic shell 2, which holds the metallic sleeve
1; a terminal electrode 3, which is attached into the cylindrical
metallic shell 2 while being insulated therefrom; a ceramic heating
member 4, which is fitted into the metallic sleeve 1; and a glass
coating layer 5.
[0023] A rear portion of the metallic sleeve 1 is fixedly attached
to the inner wall of the cylindrical metallic shell 2 by means of a
glass seal. The terminal electrode 3 is fixedly attached to the
cylindrical metallic shell 2 and a terminal lead conduit 7 while
being insulated therefrom, by means of a glass seal 8. The ceramic
heating member 4 assumes a substantially circular cross section.
The glass coating layer 5 is formed on the ceramic heating member 4
so as to cover the exposed portion of the ion detection electrode
and to extend along the substantially circular circumference of the
ceramic heating member 4.
[0024] As shown in FIG. 2, the ceramic heating member 4 is
configured such that a U-shaped heating resistor 41 and lead wires
42 and 43 are embedded in an insulator 44. The U-shaped heating
resistor 41 includes an ion detection electrode 411, which projects
from a side portion thereof. The ion detection electrode 411 is
exposed at a side portion of the ceramic heating member 4.
[0025] As shown in FIG. 2, one end 42A of the lead wire 42 and one
end 43A of the lead wire 43 are connected to the corresponding end
portions of the heating resistor 41. The other end 42B of the lead
wire 42 is exposed at the surface of an intermediate portion of the
insulator 44, whereas the other end 43B of the lead wire 43 is
exposed at the surface of a rear portion of the insulator 44. The
other end 42B of the lead wire 42 is electrically connected to the
terminal lead conduit 7 via a helical external connection wire 61
and a coated Ni lead. The other end 43B of the lead wire 43 is
electrically connected to the terminal electrode 3 via helical
external connection lines 62 and 63.
[0026] The "glass coating layer" 5 in the first embodiment of the
invention is made of glass which contains SiO.sub.2 as a main
component, and is formed on the surface of the ceramic heating
member 4 so as to cover the exposed portion of the ion detection
electrode 411. Trace components other than SiO.sub.2 of the glass
forming the "glass coating layer" 5 are not particularly limited.
However, alkali metals, such as Na and K, are preferably contained,
since such alkali metals, if present, improve the ion conductivity
of the glass coating layer 5 to thereby enable accurate detection
of ion current. The "glass coating layer" 5 must cover at least a
portion of the ion detection electrode 411 which is exposed from
the insulator 44 of the ceramic heating member 4. In this regard,
the glass coating layer 5 may be formed so as to cover a wider
region in order to detect not only ions which have reached a region
located above the ion detection electrode 411, but also ions which
have reached any portion of the glass coating layer 5. In a further
preferred embodiment of the invention, the glass coating layer may
be formed so as to cover the exposed portion and to extend all
around the insulator of the ceramic heating member as shown in FIG.
2(b), which is sectional view taken along line B-B'.
[0027] Since such glass penetrates into grain boundaries of ceramic
forming the insulator 44, the formed glass coating layer 5 is
completely integrated with the insulator 44, thereby avoiding
potential separation thereof from the ceramic heating member 4.
When glass is softened at high temperature, the apparent Young's
modulus thereof drops. Thus, stress concentration does not occur,
thereby preventing the occurrence of cracking, with a resultant
improvement in durability of the glass coating layer 5.
[0028] The thickness of the "glass coating layer" 5 is not
particularly limited. The thickness is preferably 10-200 .mu.m, and
is more preferably 20-100 .mu.m, even more preferably 30-60 .mu.m.
When the thickness of the glass coating layer 5 is less than 10
.mu.m, the durability of the glass coating layer 5 is impaired.
When the thickness is in excess of 200 .mu.m, the strength of the
glass coating layer 5 is impaired due to increased thermal stress,
and again the durability of the glass coating layer 5 is
impaired.
[0029] The softening point of the "glass coating layer" 5 is not
particularly limited. However, the softening point is preferably
not lower than 600.degree. C., and is preferably not lower than
700.degree. C., more preferably not lower than 800.degree. C. When
the softening point of the glass coating layer 5 is lower than
600.degree. C., glass which forms the glass coating layer 5 may run
while the vehicle is traveling, potentially resulting in exposure
of the ion detection electrode 411 to combustion gas. Notably, the
above-mentioned softening point is also called the Littleton point
and indicates temperature as measured at a viscosity of
4.5.times.10.sup.7 poise. The softening point may be measured by
using a differential thermal analyzer.
[0030] In the first embodiment of the invention, a position where
the "ion detection electrode" 411 is exposed is not particularly
limited. Usually, as shown in FIGS. 1 and 2, the ion detection
electrode 411 is exposed at a side surface of the ceramic heating
member 4, but may be exposed at a tip portion of the ceramic
heating member 4. When the ion detection electrode 411 is exposed
at a side surface of the ceramic heating member 4, the distance
between the ion detection electrode 411 and the metallic sleeve 1
can be made 2 mm or less. In this case, since the ion detection
electrode 411 can be located at a position which is advantageous in
terms of temperature, the durability of the glow plug is improved,
resulting in extended life of the glow plug. Since the glass
coating layer 5 is electrically nonconductive at near room
temperature, shortening the distance between the ion detection
electrode 411 and the metallic sleeve 1 does not result in a short
circuit potentially caused by adhesion of carbon.
[0031] Materials for the "ion detection electrode" 411 and the
"heating resistor" 41 in the first embodiment of the invention are
not particularly limited. Usually, the ion detection electrode 411
and the heating resistor 41 are formed by sintering a ceramic
compact (Si.sub.3N.sub.4, SiO.sub.2, WC, rare earth oxide, or the
like). Also, W, Ir, Ta, and Pt, for example, are usable materials.
As shown in FIG. 6, the "ion detection electrode" 411 and the
"heating resistor" 41 may be made of different materials.
Preferably, the ion detection electrode 411 and the heating
resistor 41 are made of the same material so that they can be
integrally formed; i.e., they can be manufactured efficiently (see
FIGS. 3 and 4). In the first embodiment of the invention the "ion
detection electrode" 411 and the "heating resistor" 41 are
integrated into a single unit, but they may be formed as different
elements.
[0032] Material for the "insulator" 44 in the first embodiment of
the invention is not particularly limited so long as the material
has insulating properties. The insulator 44 may be made of
Al.sub.2O.sub.3, but is preferably formed by sintering a ceramic
compact which contains Si.sub.3N.sub.4 as a main component. This is
because properties such as strength and toughness of the
thus-formed insulator 44 are balanced.
[0033] A method for manufacturing a glow plug embodying the
invention is characterized by coating with a glass coating layer a
portion of an ion detection electrode disposed within the insulator
of the ceramic heating member, the portion being exposed from the
insulator. The coating method is not particularly limited so long
as the portion of the ion detection electrode which is exposed from
the insulator of the ceramic heating member can be coated.
[0034] Use of a glow plug A of the present invention will next be
described with reference to FIG. 7. When the engine is started,
glow relays 10 and 11 are turned on to thereby close the circuit
between a battery 12 and the heating resistor 41 of the glow plug
A. As a result, current flows through the heating resistor 41, to
generate heat. Thus, the glow plug A is heated to firing
temperature. Each time fuel is injected from a fuel injection
nozzle 94, the injected fuel is ignited, causing a piston 93 to
operate. Thus the engine is driven.
[0035] During the above operation, a large amount of positive and
negative ions are generated in the combustion-flame region. Since a
direct-current power source 13 applies voltage between a cylinder
head 9 and the ion detection electrode 411 of the glow plug A, the
ion detection electrode 411 and the cylinder head 9 capture ions.
Thus, an ion current flows through a current circuit including an
ion current detection resistor 14. A potentiometer 141 detects the
ion current in the form of potential difference across the ion
current detection resistor 14.
[0036] Near room temperature, the resistivity of glass is very
high, and thus glass is electrically nonconductive. Adhesion of
carbon, if any, does not cause a short circuit. As the temperature
rises, movement of alkali metal ions contained in glass becomes
intensive. At the softening point of glass or higher temperature,
glass becomes electrically conductive. Accordingly, by coating with
a glass coating layer as specified in the present invention, not
only ions which have reached a region located above the ion
detection electrode, but also ions which have reached any portion
of the glass coating layer can be detected. Thus, ion current can
be detected accurately, whereby the state of ionization during
operation is accurately determined.
[0037] The present invention will next be described specifically by
reference to the following Examples and comparative Examples.
However, the present invention should not be construed as being
limited thereto.
[0038] (1) Configuration of Glow Plug of the Present Embodiment
[0039] A glow plug of the present embodiment is shown in FIGS. 1 to
5.
[0040] In the glow plug of the present embodiment, the metallic
sleeve 1 has a wall thickness of 0.6 mm and is made of a
heat-resistant metal, and the cylindrical metallic shell 2 is made
of carbon steel. The heating resistor 41 excluding the exposed
portion of the ion detection electrode 411 is embedded in the
insulator 4 such that the distance between the surface of the
heating resistor 41 and the surface of the insulator 4 is not less
than 0.3 mm. Thus, even when the heating resistor 41 assumes a high
temperature (800.degree. C. to 1500.degree. C.) when the glow plug
is in use, the heating resistor 41 can be protected from oxidation
and can maintain a high mechanical strength. The lead wires 42 and
43 are each manufactured in the following manner: a W wire having a
diameter of 0.3 mm to 0.4 mm is electroplated with silver such that
the plating thickness becomes 3 .mu.m.
[0041] (2) Fabrication of Glow Plug of the Present Embodiment
[0042] First, a material for the heating resistor 41 is prepared.
The material contains 60.0 wt % WC and 40 wt % insulative ceramic
(Si.sub.3N.sub.4: 85 parts by weight; rare earth oxide: 10 parts by
weight; SiO.sub.2: 5 parts by weight). A dispersant and a solvent
are added to the material, followed by pulverizing and drying. An
organic binder is added to the pulverized substance, to thereby
obtain a granular substance.
[0043] Next, the W wire is cut to pieces, each having a
predetermined length. The cut pieces are formed into predetermined
shapes. The thus-formed W wire pieces are electroplated with silver
such that the plating thickness becomes 3 .mu.m, to thereby obtain
the lead wires 42 and 43.
[0044] As shown in FIG. 4, the above granular substance is
injection molded so as to connect to the ends 42A and 43A of the
lead wires 42 and 43, thereby forming a U-shaped green heating
resistor 41A and the lead wires 42 and 43 integral with each other
as shown in FIG. 3. In this molding step, a protrusion which will
become the ion detection electrode 411 is formed on the green
heating resistor 41A so as to become a protruding portion of the
heating resistor 41. In a later step, the protruding portion can be
exposed at the surface of the insulator by polishing. Notably, when
a W electrode or Ir electrode is used as the ion detection
electrode, the W electrode or Ir electrode is disposed at a
position corresponding to the protrusion before the granular
substance is injection molded, so as to integrate the W electrode
or Ir electrode with the green heating resistor 41A.
[0045] Next, a ceramic powder which the insulator 44 is made of is
prepared. Si.sub.3N.sub.4 (85 parts by weight), rare earth oxide
(10 parts by weight), and SiO.sub.2 (5 parts by weight) are mixed
to obtain the ceramic powder. An organic binder is added to the
ceramic powder to thereby obtain a granular substance. As shown in
FIG. 5, a pair of compact halves 44A and 44B are formed from the
granular substance. The integrated unit shown in FIG. 3 is placed
on the compact half 44A, and then the compact half 44B is placed on
the compact half 44A. The resulting assembly is pressed to thereby
obtain a compact 44C.
[0046] The compact 44C is hot pressed in a nitrogen gas atmosphere
at a temperature of 1750.degree. C. by applying a pressure of 200
kg/cm.sup.2, thereby forming a sintered ceramic body assuming the
form of a substantially round bar and having a hemispherical tip
portion. The surface of the sintered ceramic body is polished into
the form of a column having predetermined dimensions and so as to
expose the other ends 42B and 43B of the lead wires 42 and 43 at
the surface of the sintered ceramic body. The ceramic heating
member 4 is thus completed.
[0047] A glass layer is formed on the ceramic heating member 4 by
baking in such a manner as to extend all around the insulator 44
and to cover the exposed portion of the ion detection electrode and
a portion of the insulator 44 which is to be held by the metallic
sleeve 1. For example, a glass paste is first prepared by mixing a
glass powder (product of Asahi Glass Co., 103) with a binder and a
solvent. The glass paste is then coated on the ceramic heating
member 4 and dried at a temperature of 120.degree. C. for 10-20
minutes and baked for 5 minutes in a hydrogen-nitrogen atmosphere
at a temperature of 1300.degree. C. The glass layer is composed,
e.g., of SiO.sub.2.B.sub.2O.sub.3.R.sub.2O (R: alkali metal, e.g.,
Li, Na, K) high-melting-point glass (softening point: 820.degree.
C.).
[0048] The ceramic heating member 4 and the metallic sleeve 1, and
the ceramic heating member 4 and the external connection wires 61
and 62 are electrically connected by brazing. The external
connection wires 61 and 62 are electrically connected to the
terminal lead conduit 7 and the terminal electrode 3, respectively.
Subsequently, the resulting assembly of the ceramic heating member
4 is inserted into the cylindrical metallic shell 2. A rear portion
of the metallic sleeve 1 is silver brazed to the inner wall of a
holder portion of the cylindrical metallic shell 2. Finally, an end
of the cylindrical metallic shell 2 is caulked, thereby completing
a dual insulation type glow plug A.
[0049] (2) Evaluation of Performance of Glow Plug
[0050] {circle over (1)} Durability-to-Energization Test
[0051] Glow plugs of Examples 1 to 6 and comparative Examples 1 to
5 were manufactured according to the above-described method while
employing the materials for the ion detection electrode and the
coating layer and the thickness of the coating layer as specified
in Table 1. The glow plugs were subjected to a
durability-to-energization test, of 10,000 cycles, to thereby
evaluate their durability to energization. Each cycle is composed
of 1-minute energization (temperature of tip portion of insulator:
1400.degree. C.) and 1-minute de-energization (cooled to room
temperature). The test results are shown in Table 1. In Table 1,
the term "heating element" appearing in the "Electrode Material"
column means that the ion detection electrode 411 and the heating
resistor 41 are made of the same material.
1TABLE 1 Electrode Electrode Coating Material Coating Thickness
Results Example 1 Heating Glass 5 .mu.m Swelling of heating Element
element due to oxidation after 2000 cycles Example 2 Heating Glass
10 .mu.m No anomaly after Element 10000 cycles Example 3 Heating
Glass 50 .mu.m No anomaly after Element 10000 cycles Example 4
Heating Glass 100 .mu.m No anomaly after Element 10000 cycles
Example 5 Heating Glass 200 .mu.m No anomaly after Element 10000
cycles Example 6 W Glass 20 .mu.m No anomaly after 10000 cycles
Comparative Heating Not 0 Swelling of electrode Example 1 Element
coated due to oxidation after 100 cycles Comparative W Not 0
Swelling of electrode Example 2 coated due to oxidation after 50
cycles Comparative Ir Not 0 Cracking of insulator Example 3 coated
after 1200 cycles Comparative W Au 2 .mu.m Swelling of electrode
Example 4 deposition due to oxidation after 250 cycles Comparative
W Au--Ni 15 .mu.m Separation of coating Example 5 applied by layer
after 400 cycles baking
[0052] A durability-on-engine test was conducted using a 4-cylinder
diesel engine (2400 cc).
[0053] Each of the glow plugs of Examples 7 to 11 and comparative
Examples 6 to 9 was mounted on the engine such that an externally
threaded portion of the cylindrical metallic shell 2 was screwed
into the cylinder head 9 of the engine as shown in FIG. 7. The glow
plug A is mounted such that a tip portion thereof projects into a
swirl chamber 91, which is a portion of a combustion chamber of the
cylinder head 9.
[0054] As shown in FIG. 7, the glow plug is connected to a glow
plug operation circuit. Specifically, glow relays 10 and 11 and a
12 V battery 12 in the glow plug operation circuit are electrically
connected to the lead wires 42 and 43 by means of external lead
wires 64 and 65 and via the terminal lead conduit 7 and the
terminal electrode 3, thereby forming a heating circuit for the
heating resistor 41. An ion detection circuit is connected to the
ion current detection resistor 14 via the direct-current power
source 13. The potentiometer 141 is connected to the ion current
detection resistor 14 in order to detect ion current.
[0055] The durability-on-engine test was conducted for 1000 cycles
in a mode operation. Each cycle included the following steps (4
minutes per cycle).
[0056] {circle over (1)} Engine speed 0 rpm (engine in halt)
[0057] The heating member is energized for 1 minute, and the ion
detection electrode is de-energized.
[0058] {circle over (2)} Engine speed 700 rpm, no load (idling)
[0059] The heating member is de-energized, and the ion detection
electrode is energized for 1 minute.
[0060] {circle over (3)} Engine speed 3600 rpm, full load
[0061] The heating member is de-energized, and the ion detection
electrode is energized for 2 minutes.
[0062] The test results are shown in Table 2. In Table 2, the term
"short" appearing in the "Results" column means that adhesion of
carbon to the ion detection electrode caused a short circuit during
energization, with a resultant fuse blowout. The term "1000 cycles
durable" means "passing the 1000 cycle Durability-on-Engine Test"
or no material change after the 1000 cycle Durability-on-Engine
Test. Also, the term "heating element" appearing in the "Electrode
Material" column means that the ion detection electrode 411 and the
heating resistor 41 are made of the same material.
2TABLE 2 Electrode Electrode Coating Material Coating Thickness
Results Example 7 Heating Glass 5 .mu.m 1000 cycles element durable
Example 8 Heating Glass 10 .mu.m 1000 cycles element durable
Example 9 Heating Glass 100 .mu.m 1000 cycles element durable
Example 10 Heating Glass 200 .mu.m 1000 cycles element durable
Example 11 Heating Glass 300 .mu.m 1000 cycles element durable
Comparative Heating Not coated 0 Short after 70 Example 6 element
cycles Comparative W Not coated 0 Short after 60 Example 7 cycles
Comparative Ir Not coated 0 Short after 100 Example 8 cycles
Comparative W Au 2 .mu.m Short after 40 Example 9 deposition
cycles
[0063] Glow plugs of Examples 12 and 13 and comparative Example 10
were manufactured according to the above-described method while
employing the length of the glass coating region (X) of FIG. 8 as
specified in Table 3. Using the glow plugs, voltage was measured
which was detected when the ion detection electrode 411 was
oriented toward a fuel injection nozzle and when the ion detection
electrode 411 was oriented opposite the fuel injection nozzle.
Measurement was conducted in the following manner. In the glow plug
operation circuit shown in FIG. 7, the direct-current power source
13 supplies a direct-current voltage of 300 V, and the ion current
detection resistor 14 assumes a resistance of 10 k.OMEGA.. Ion
current was detected for 1 minute in the idling state. The average
value of detected voltages measured by means of the potentiometer
141 was taken as a measured value.
[0064] The test results are shown in Table 3. In FIG. 8, the cross
section of the insulator 44 has a diameter of 3.5 mm; the ion
detection electrode 411 has a diameter of 0.8 mm; the distance X
between the ion detection electrode 411 and the metallic sleeve 1
is 1.5 mm; and the distance between the tip of the insulator 44 and
the metallic sleeve 1 is 10 mm.
3TABLE 3 Glass Coating Detected Region X Electrode Orientation
Voltage Example 12 2 mm Toward injection nozzle 2.0 V Opposite
injection nozzle 1.9 V Example 13 5 mm Toward injection nozzle 2.4
V Opposite injection nozzle 2.3 V Comparative 0 mm Toward injection
nozzle 0.8 V Example 10 Opposite injection nozzle 0.3 V
[0065] (3) As shown in Table 1, the glow plugs of comparative
Examples 1 to 3, which did not employ the glass coating layer,
suffered swelling of the heating element or ion detection electrode
with resultant cracking of the insulator after 50-1200 cycles of
the durability-to-energization test. The glow plug of comparative
Example 4, which employed Au deposition as a coating layer instead
of a glass coating layer, suffered cracking of the insulator due to
oxidation of W after 250 cycles of the durability-to-energization
test. The glow plug of comparative Example 5, which employed an
Au--Ni layer applied by baking as a coating layer, suffered
separation of the coating layer after 400 cycles of the
durability-to-energization test. These test results indicate that
the durability to energization of the glow plug is impaired
significantly unless the glass coating layer is employed.
[0066] By contrast, the glow plugs of Examples 1 to 6, in which the
exposed portion of the ion detection electrode was coated with the
glass coating layer, endured 2000 cycles or more of the
durability-to-energizat- ion test, thereby proving to be excellent
in durability to energization. Particularly, the glow plugs of
Examples 2 to 6, in which the glass coating layer had a thickness
of not less than 10 .mu.m, were free of anomaly even after 10,000
cycles of the durability-to-energization test, thereby proving to
be particularly excellent in durability to energization.
[0067] As shown in Table 2, the glow plugs of comparative Examples
6 to 8, which did not employ the glass coating layer, suffered a
short circuit with a resultant fuse blowout due to adhesion of
carbon after 60-100 cycles of the durability-on-engine test, which
was carried out by use of an actual diesel engine. The glow plug of
comparative Example 9, which employed Au deposition as a coating
layer, suffered a short circuit with a resultant fuse blowout after
40 test cycles.
[0068] By contrast, the glow plugs of Examples 7 to 11, which
employed the glass coating layer, did not suffer a short circuit
potentially caused by adhesion of carbon even after 1000 test
cycles, thereby proving to be favorably usable with an actual
diesel engine while being free of anomaly caused by adhesion of
carbon.
[0069] As shown in Table 3, the glow plug of comparative Example
10, which did not employ the glass coating layer, exhibited a
detected voltage of 0.8 V, which is less than half the values
exhibited by the glow plugs of Examples 12 and 13. The detected
voltage as measured when the electrode is oriented toward the fuel
injection nozzle was 0.8 V, whereas the detected voltage as
measured when the electrode is oriented opposite the fuel injection
nozzle was 0.3 V, which is about 60% less than 0.8 V.
[0070] By contrast, the glow plugs of Examples 12 and 13, which
employed the glass coating layer, exhibited a detected voltage of
about 2.0 V, indicating capability to detect ion current more
accurately as compared with comparative Example 10. The difference
between the detected voltage as measured when the electrode is
oriented toward the fuel injection nozzle and the detected voltage
as measured when the electrode is oriented opposite the fuel
injection nozzle is within about 10%, indicating that ion current
can be detected accurately regardless of electrode orientation.
When a glow plug is mounted on an engine by screw engagement, the
orientation of the glow plug is unknown. Thus, it is desirable that
a glow plug be able to detect ion current accurately regardless of
electrode orientation. Therefore, the glow plugs of Examples 12 and
13 are more favorable than the glow plug of comparative Example 10.
Furthermore, the glow plug of Example 13, which has a wider glass
coating region than that of the glow plug of Example 12, exhibited
a detected voltage greater than that exhibited by the glow plug of
Example 12, indicating that the wider the glass coating region, the
more accurately ion current can be detected.
[0071] The present invention is not limited to the above-described
embodiments, but may be modified according to purpose and
application without departing from the scope of the present
invention. For example, the material and diameter of the lead wires
42 and 43 are not particularly limited. The diameter is usually
0.1-1.0 mm, preferably 0.2-0.8 mm. The lead wires 42 and 43 are
usually coated with silver. However, the coating material is not
particularly limited. Also, the thickness of the coating layer is
not particularly limited. In view of cost and a reduction in a
reaction layer, the thickness is usually 1-10 .mu.m, preferably 3-8
.mu.m.
[0072] The glow plugs embodying the invention employ a glass
coating layer which covers an exposed portion of an ion detection
electrode, thereby detecting ion current accurately, improving
durability, and preventing short circuits potentially caused by
adhesion of carbon. The method of manufacturing a glow plug
according to the invention can provide a glow plug having the
above-mentioned advantages at low cost and in an easy manner.
[0073] This application is based on Japanese Patent Application No.
Hei. 11-349530 filed Dec. 8, 1999, which is incorporated herein by
reference in its entirety.
* * * * *