U.S. patent application number 09/755026 was filed with the patent office on 2001-07-12 for one-side welding method for steel structure.
This patent application is currently assigned to MACHIDA STEEL STRUCTURE CORPORATION. Invention is credited to Iwago, Shunji, Uchida, Masayoshi.
Application Number | 20010007331 09/755026 |
Document ID | / |
Family ID | 27342023 |
Filed Date | 2001-07-12 |
United States Patent
Application |
20010007331 |
Kind Code |
A1 |
Iwago, Shunji ; et
al. |
July 12, 2001 |
One-side welding method for steel structure
Abstract
In the present invention, by the method using a backing material
such as copper, which is not melted by a welding heat source, in an
end face of a member without using a backing metal or consumable
backing material at a joint welding time, overlay welding is
performed to increase a plate thickness and a plate width.
Thereafter, edge preparation including a member of a designed joint
weld location and an overlay weld is performed, and the groove
processed portion is placed to an opponent member to provide joint
welding in order to obtain an effective throat depth more than a
plate thickness and a plate width of the member.
Inventors: |
Iwago, Shunji; (Tosa-shi,
JP) ; Uchida, Masayoshi; (Kochi-shi, JP) |
Correspondence
Address: |
ARMSTRONG, WESTERMAN, HATTORI,
McLELAND & NAUGHTON
Suite 1000
1725 K Street, N.W.
Washington
DC
20006
US
|
Assignee: |
MACHIDA STEEL STRUCTURE
CORPORATION
Tosa-shi
JP
|
Family ID: |
27342023 |
Appl. No.: |
09/755026 |
Filed: |
January 8, 2001 |
Current U.S.
Class: |
228/163 ;
228/155; 228/159; 228/216 |
Current CPC
Class: |
B23K 33/00 20130101;
B23K 9/04 20130101; B23K 9/038 20130101; B23K 9/02 20130101; Y10T
403/479 20150115; B23K 9/035 20130101; B23K 9/235 20130101 |
Class at
Publication: |
228/163 ;
228/155; 228/159; 228/216 |
International
Class: |
B23K 031/02; B21D
039/00 |
Foreign Application Data
Date |
Code |
Application Number |
Jan 12, 2000 |
JP |
2000-3782 |
Jul 4, 2000 |
JP |
2000-202582 |
Nov 29, 2000 |
JP |
2000-363495 |
Claims
What is claimed is:
1. A one-side welding method in a steel structure, said method
comprising the steps of: placing a backing material, which is not
melted by a welding heat source, to an end face of a T-welding
joint member, or one end face of butt welding members where two
members are in substantially the same plane or both end faces;
performing overlay welding between a back face of the end of the
member and said backing material; providing edge preparation to the
end of the member including said overlay weld metal; and welding
the joint members to each other after being opposed to other as
melting a groove face consisting of the overlay weld metal and the
members from a front side of the groove, whereby ensuring a welding
throat depth in the direction of a plate thickness exceeding a
plate thickness of the end of the member of the welding joint.
2. A one-side welding method comprising the steps of: providing
overlay welding to a back face of the member at a designed edge
preparation location, serving as an end of a joint member; cutting
both a member of the designed edge preparation location and said
overlay weld metal for edge preparation; and welding the joint
members to each other after being opposed to each other as melting
a groove face consisting of the overlay weld metal and the members
from a front side of the groove, whereby ensuring a welding throat
depth in the direction of a plate thickness exceeding a plate
thickness of the end of the member of the welding joint.
3. A one-side welding method when overlay welding is performed
between a back face including side face at the end of the member of
the steel plate with a finite width and said backing material by
the method described in claim 1, said method comprising the steps
of; performing edge preparation to the end of the member including
the overlay weld metal of the steel plate back face and that of the
steel plate side face after performing the overlay welding to the
back face and side face of steel plate member; and welding the
joint members to each other after being opposed to each other as
melting a groove face of the overlay weld metal and the member from
a front side of the groove, whereby ensuring a throat depth in the
direction of a plate thickness exceeding a plate thickness at the
end of the member of the welding joint, or a throat depth in the
direction of a plate width exceeding a plate width, or a throat
depth in the directions of the plate thickness and plate width
exceeding both plate thickness and plate width.
4. A one-side welding method when overlay welding is provided to a
back face and a side face of the member at a designed edge
preparation location, serving as an end portion of a joint member
with a finite width by the method described in claim 2, said method
comprising the steps of; performing edge preparation to the member
including the overlay weld metal of the steel plate back face and
that of the steel side face after performing overlay welding to the
back face and side face of the steel plate member at the designed
location; and welding the joint members to each other after being
opposed to each other as melting a groove face of the overlay weld
metal from a front side of the groove, whereby ensuring a throat
depth in the direction of a plate thickness exceeding a plate
thickness at the end of the member of the welding joint, or a
throat depth in the direction of a plate width exceeding a plate
width, or a throat depth in the directions of the plate thickness
and plate width exceeding both plate depth and plate width.
5. A one-side welding method when overlay welding is performed
between a back face of the end of the member and said backing
material by the method described in claim 1, said method comprising
the steps of: placing a thin steel plate of the same material as
the joint member between the backing material, which is not melted
by a welding heat source and the end face of the member; performing
overlay welding as melting said thin steel plate between a back
face of the end of the member and said backing material; performing
edge preparation to the end of the member including said overlay
weld metal; and welding the joint members to each other after being
opposed to each other as melting a groove face of the overlay weld
metal and the member from a front side of the groove, whereby
ensuring a throat depth in the direction of a plate thickness
exceeding a plate thickness of the member.
6. A one-side welding method when overlay welding is performed
between a back face including side face of the member and said
backing material by the method described in claim 3, said method
comprising the steps of: placing a thin steel plate of the same
material as the joint member between the backing material, which is
not melted by a welding heat source and the end face of the member;
performing overlay welding as melting said thin steel plate;
performing edge preparation to the end of the member including said
overlay weld metal; and welding the joint members to each other
after being opposed to each other as melting a groove face of the
overlay weld metal and the member from a front side of the groove,
whereby ensuring a throat depth in the direction of a plate
thickness exceeding a plate thickness of the member, or a throat
depth in the direction of a plate width exceeding a plate width, or
a throat depth exceeding both throat depths in the directions of
the plate thickness and plate width.
7. A one-side welding method in a steel structure, said method
comprising the steps of: placing a backing material, which is not
melted by a welding heat source, to an end face of a T-welding
joint member subjected to edge preparation, or at least one end
face of butt welding members subjected to edge preparation where
two members are in substantially the same plane or both end faces;
performing overlay welding between a back face including side face,
as the case may be, of the member and said backing member; and
welding the joint members to each other after being opposed to each
other as melting a groove face of the overlay weld metal and the
member from a front side of the groove, whereby ensuring a throat
depth in the direction of a plate thickness exceeding a plate
thickness of the member, or a throat depth in the direction of a
plate width exceeding a plate width, or a throat depth exceeding
both throat depths in the directions of the plate thickness and
plate width.
8. A one-side welding method in a steel structure, said method
comprising the steps of: placing a backing material, which is not
melted by a welding heat source, to the back face or the side face
of a member whose end face of a T-welding joint member is to be
welded, or at least one end of butt welding members where two
members to be welded are in substantially the same plane or both
end faces; performing overlay welding between a back face of the
end of the member and said backing material; performing edge
preparation to the member including said overlay weld metal; and
welding the joint members to each other after being opposed to each
other as melting a groove face of the overlay weld metal and the
member from one side, whereby ensuring a throat depth in the
direction of a plate thickness exceeding a plate thickness of the
member whose end face is welded, or a throat depth in the direction
of a plate width exceeding a plate.
9. A one-side welding method in a steel structure, said method
comprising the steps of: performing a bending process to an end of
the member of a T-butt welding joint or at least one end of butt
joint members, which are in the same plane, to use an outer face of
the bend-processed end as a groove face or produce a groove face
with a groove depth more than a plate thickness of the
bend-processed material by providing a mechanical or thermal
cutting process to the bend-processed end; and welding the joint
members from a front side of the groove after being opposed to each
other, whereby ensuring a throat depth in the direction of a plate
thickness exceeding a plate thickness of the bend-processed
member.
10. A method for performing one-side welding wherein when said
one-side welding is performed with respect to a T-butt welding
joint where an end face of one member is placed on a surface of
other member to form a T shape substantially right-angled in a
steel structure, welding is performed on the member whose end face
is welded such that a position of a weld bead toe at a final
welding layer of the front side is placed to be separated from a
welding root on the back side or a tack weld toe of the backing
metal by more than 80% of the plate thickness of the member on the
front side surface and that reinforcement height of the front bead
in the area of the welding bead width on the back side is ensured
by at least more than 10% of the plate thickness so that
reinforcement height is smoothly changed from a base metal surface,
or when said one-side welding is performed with respect to a butt
welding joint where two members to be welded are in substantially
the same plane, welding of a final layer is performed on at least
thinner plate side of two members such that the position of a weld
bead toe at a final welding layer of the front side is placed to be
separated from a welding root on the back side or the weld toe of
the backing metal by more than 80% of the plate thickness of the
member on the front side and that reinforcement height of the front
bead in the area of the welding bead width on the back side is
ensured by more than 10% of the plate thickness so that
reinforcement height is smoothly changed from the base metal
surface.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention belongs to the technical field in
which a one-side welding is performed in a building structure, a
bridge structure, a general structure, and like.
[0003] The present invention relates to a method for obtaining a
throat depth exceeding a thickness and a width of an end face of
the member for a welding joint. This method can be attained by
joint welding using a one-side welding process in which the member
is easily welded from the one side without using a consumable
backing metal and backing material after performing a welding
process for increasing a height and a width of a front bead or a
process in which a back face of the end of the member to be welded
is subjected to overlay welding and then the groove of the welding
member including the overlay weld is made and welded, or a process
in which the end of the member is bent to prepare the edge of the
member and the prepared edge is subjected to joint welding.
[0004] 2. Description of the Related Art
[0005] FIGS. 39 and 40 illustrate cross-sectional views showing one
example of a conventional steel structure welding method. In this
example, a member 1 and a member 2 with an edge prepared to have an
inclination of about 35.degree. are butted and welded by a T-joint.
A backing metal 3 is abutted on a back face so as to perform tack
welding 4 such that they are stably welded from one side to be
fully penetrated as shown in FIG. 39. After that, joint welding 6
is carried out as shown in FIG. 40. Namely, according to the prior
art, the joint with backing metal in which welding is performed
from one side is being the standard for the steel structure welding
for building as shown in FIGS. 39 and 40.
[0006] In the above conventional method, as shown in FIG. 39, two
recesses 1R and 2R are formed at a root of a groove 5 where the
members 1 and 2 are brought in contact with the backing metal 3,
and these portions are not easily to be melted, making it prone to
cause incomplete penetration.
[0007] Moreover, this requires the production of the backing metal
3 and the tack welding 4 for attaching the backing metal after
preparing a groove 5, and this results in an increase in the number
of man-hours needed to produce the steel structure in view of
efficiency of joint welding.
[0008] Additionally, in the following joint welding 6, since the
backing metal 3 is left, there remain a harmful notch, which
generates stress concentration due to the residual of the tack
welding 4, and harmful notches 7 and 7A, which apply stress
concentration to the portion among the backing metal 3 and the base
metals 1 and 2. This causes the joint properties such as bending
ductility, fatigue strength, earthquake resisting strength, etc.,
to be damaged. In the experiment, when the member 2 received a
upward bending load 2B in the joint form shown in FIG. 40, cracks
occurred mainly at harmful notches 7 and 7A and the joint was
broken.
[0009] In the conventional method, the production of the backing
metal 3 and the tack welding 4 for attaching the backing metal 3
are needed after performing the edge preparation of the end face to
be welded of the member, so that welding 6 of the actual joint
cannot be immediately started. This results in a disadvantage in
which the number of man-hours needed to produce the steel structure
is increased in view of the production processes and steps.
[0010] Moreover, in this conventional art, if the backing metal 3
is omitted, there must be carried out uranami welding that forms a
good shaped uranami bead with no defect from the front side of the
groove to the back face of the first layer. In the steel structure
production, however, there are difficulties in maintaining the
groove accuracy resulting from the size accuracy of material,
ensuring an amount of uranami welding, and using high current from
the first layer, and these makes it difficult to implement such
good uranami welding.
[0011] Though the use of consumable backing material is possible to
form an excellent uranami bead, this method causes problems in
which the consumable backing material is expensive and much time is
required to attach and detach the backing material.
[0012] In a case in which a space whose interior is closed as in a
connection of a building steel structure using square pipes or
circular pipes as columns as shown in FIG. 47, there is problem in
which the consumable backing material cannot be detached after
welding.
[0013] There is another method in which an overlay welding bead 13
is preset on the member 1, which is not the end face of T-joint,
the member 2 is placed thereto, and welding 14 of the first layer
is performed from the front side of the groove, thereafter joint
welding 6 is carried out as shown in FIG. 41.
[0014] Though this method is a simple and easy way in which the
backing metal can be omitted, projections and depressions are
generated by the waves of the overlay welding bead and the position
of the overlay welding bead 13 is preset, whereby making it
difficult to adjust and change the setting position of members each
having a different size accuracy. Further, this welding is
difficult to be carried out unless the welding position is
horizontal welding. The member 1 needs a constant inclination to
form the good uranami bead. Some experience is required to perform
welding 14 of the first layer from the surface and high current
cannot be used. Moreover, the above method does not lead to an
increase in a throat depth 2A.
[0015] There is another method in which an overlay welding bead 13A
is preset on the back face of the member 2 whose end face is
subjected to edge preparation in addition to the overlay welding
bead 13 preset on the surface of the member 1 of the T-joint, the
member 2 is placed thereto, the welding 14 of the first layer is
performed from the front side of the groove, thereafter the joint
welding 6 is carried out. Though this method is a simple and easy
way in which the backing metal can be omitted, the same problem as
explained in FIG. 41 exists therein. When the overlay welding bead
13A is placed to the top end of the member 2, welding is not easily
carried out. In addition, the overlay welding bead must be present
with respect to two portions of both members of the T-joint,
resulting in difficulty of welding and an increase in the number of
man-hours needed to produce the steel structure.
[0016] Unlike the peripheral welding of the square pipe and the
circular pipe in which a welding start point and a welding end
point are overlapped with other, a width of an H shape steel flange
has a finite width in welding the end portion of the flange. In
order to obtain satisfactory welding with no defect at a start
point of weld bead and an end point of weld bead, steel end tabs
are needed as shown in FIG. 43. As a result, much production cost
of end tabs and numerous attaching steps are required. The use of
ceramics end tab has been recently increased in place of the steel
end tab. In this case, high production cost and the attaching work
are also required. Moreover, the steel end tab has a notch, which
generates stress concentration between the tab and the flange, and
the ceramics end tab has a disadvantage in which weld detects are
easily generated.
[0017] "Japan Architectural Standard Specification JASS6" dated
Feb. 20, 1997 and "Recommendation for Quality Criteria and
Inspection of Steel Structures" dated Jul. 1, 1998 of The
Architectural Institute of Japan define as follows:
[0018] The reinforcement height of the member 2 at the surface
position of the opponent member 1 must not only satisfy the size
ranging from 25% of a plate thickness t to addition of 10 mm to the
value of 25% but also be smoothly changed from the base metal
surface, in the T-joint with the plate thickness of, for example,
40 mm or less, as shown FIGS. 44 and 45.
[0019] The above requirement is useful to relax the stress
concentration of a face bead, but the above reinforcement height is
allowable even if the height at the center of bead is zero and this
requirement does not refer to the effect of the height at the
center of bead on the stress concentration at weld toe. Namely, in
such a bead, as shown in FIG. 44, stress concentration at the roots
7 and 7A of the joint welding 6 is increased by bending moment 2B
and a tensile load 2C, so that cracks are easily generated at the
roots 7 and 7A. In a case where the backing metal 3 and the tack
weld 4 are placed at the face of the member 2, as shown in FIG. 45
stress concentration works on the root of the tack weld 4 and a
tack weld toe 4A in addition to the root 7 of the joint weld 6, and
a crack is easily generated particularly from the tack weld toe
4A.
[0020] Furthermore, welding with a finite length in a width
direction is performed with respect to the longitudinal end of the
H shape steel flange. Then, the end tab is often used in order to
obtain the structural integrity of the start point of weld bead and
the end point thereof, but the use of the tab needs the production
cost and the attaching cost. For this reason, an easy and low-cost
welding method in which the end tab is omitted has been
desired.
SUMMARY OF THE INVENTION
[0021] An object of the present invention is to achieve a reduction
in the number of man-hours needed to production in view of joint
welding efficiency, a reduction in the number of man-hours needed
to produce steel structure in view of production processes and
steps, improvement of easiness of positional adjustment between
joint members to be welded, improvement of weldability, an increase
in a throat depth, and elimination of inhibition factors of joint
performance resulting from the residue of harmful notches causing
stress concentration on a backing metal or between an end tab and a
base metal and harmful notches causing stress concentration on a
tack welding portion of the backing metal, by forming a groove face
larger than a groove face formed by joint members themselves and
controlling a joint welding bead shape of a final layer of the
front side in one-side welding for steel structure.
[0022] The present invention performs the following one-side
welding without using the backing metal or consumable backing
material, which is left on the joint after welding.
[0023] More specifically, as shown in FIG. 1, a metallic or
non-metallic backing material 8, which is not melted by a welding
heat source such as arc heating etc., is placed to an end face 2T
of a T-welding joint member, which is not yet subjected to edge
preparation, or one end face of butt welding members where two
members are in substantially the same plane or both end faces,
overlay welding 9 is performed between a back face of the end face
2T of the member 2 and the backing material 8 to have a
predetermined shape so as to increase a plate thickness of the end
face of the member 2. After that, as shown in FIG. 2, edge
preparation is provided to the end of the member including overlay
weld metal such that both members are flush with each other.
Thereafter, joint members 1 and 2 are opposed to each other as
shown in FIG. 3. Then, as shown in FIG. 4, the welding joint
members are welded to each other as melting a groove face 10
consisting of the overlay weld metal and the member of FIG. 3 from
a front side of the groove, whereby ensuring a throat depth 1A
exceeding a plate thickness 2A of the welding joint end face member
2.
[0024] According to the present invention, in the execution of
T-joint welding and the butt welding where two members are in
substantially the same plane, a foremost end of the end face of the
joint member subjected to the edge preparation after the overlay
welding is brought in contact with a predetermined position of the
opponent's member, and then the foremost end may be directly welded
to the opponent's member. As a result, the backing metal 3 of FIG.
40 can be omitted to obtain ease of setting of the member 2, and
support to melted weld metal from the back side by the overlay weld
9 can be obtained. This makes it possible to use high current of
the first layer. Since the groove is deep and has no backing metal,
favorable penetration of member roots 1R and 2R of FIG. 39 can be
easily obtained. This makes it possible to reduce a groove gap 2G
of FIG. 3 about 50% as compared with the gap of about 7 mm in case
of a backing metal used, and to decrease a ross-sectional area of
the groove by about 30%. As a result, the amount of weld metal can
be decreased and welding time and welding distortion can be
reduced. Combination of these effects makes it possible to largely
reduce the number of man-hours needed to produce the steel
structure in view of the defect prevention in the root of the
welding joint, and to improve the reservation of size accuracy of
the steel.
[0025] According to the present invention, unlike the prior art of
FIGS. 41 and 42, welding position for performing stable uranami
welding 14 is not limited to horizontal position in view of welding
workability. Namely, stable welding can be executed at all
positions by the support from the back side of the overlay weld
similar to the normal joint welding. At the same time, if the
production of backing metal after edge preparation and the off-line
work process of attachment are omitted and overlay welding is
performed before the edge process, numerous joint welding is
continuously performed from the edge preparation. This allows a
large reduction in the number of man-hours needed to produce the
steel structure in view of the production processes and steps.
Moreover, according to the method of the present invention, even if
the notch 7 of the conventional method is eliminated but a notch
corresponding to notch 7A exists, the throat depth can be increased
and such a notch is not regarded as a harmful notch and improvement
of joint bending ductility and fatigue strength can be obtained and
earthquake strength can be easily ensured. According to the
experiment, in the case of 10% or more increase in the throat
depth, joint bending ductility was improved about twice and fatigue
strength was improved about ten times.
[0026] In the method according to the above invention, in place of
using the backing material, which is not melted by the welding heat
source such as arc heat, overlay weld 9 with a predetermined shape
is provided to the back face at the designed edge preparation
location to be served as an end of the joint member 2 as shown in
FIGS. 5 and 6. Thereafter, the member 2 at the designed edge
preparation location and the overlay weld metal 9 are cut at the
same angle as that of the face of the member as shown in FIG. 2.
After cutting, a predetermined edge preparation is performed, so
that a joint end face, which is not yet joint-welded, can be
obtained. Thereafter, the joint end face members are opposed to
each other as shown in FIG. 3, and they are welded to each other as
melting the groove face 10 of the overlay weld metal and the
members from the front side of the groove, so that one-side welding
is performed to ensure the throat depth 1A exceeding the plate
thickness of 2A of the welding joint end face member as shown in
FIG. 4.
[0027] According to the present invention, the groove shape, which
is not yet welded, and the joint shape after the welding can be
obtained similar to the method according to the above invention.
This makes it possible to obtain easiness of welding workability,
which is the same as that of the method according to the above
invention, and reduction in the number of man-hours needed to
produce the steel structure and reservation of good welding
property.
[0028] Also, when welding is performed to the H-shape steel flange
in which a welding start point and a welding end point are not
overlapped with other unlike in the peripheral welding of the
square pipe and the circular pipe, the steel plate flange becomes a
finite width. Then, when the conventional welding with the
attachment of the backing metal or the method of each invention as
mentioned above is applied, the end tab 5 and ceramics end tab for
the end tab 5 as shown in FIG. 5 are needed to obtain satisfactory
welding with no defect at a start point and an end point of the
weld. The present invention provides means for eliminating the
above need.
[0029] In other words, the present invention is the one-side
welding method as described below.
[0030] More specifically, there is a case in which overlay welding
is performed between the back face of the steel member with a
finite width and the backing material by the method of the above
invention or a case in which overlay welding is provided to the
back face of the designed edge preparation location serving as an
end of the steel member with a finite width. In either case,
overlay welding is performed to the member including the steel
plate side face 2S as shown FIGS. 7 to 12. After that, edge
preparation is provided to the member 2 including the overlay weld
metal 9 of the back face and side face of the steel plate as shown
in FIGS. 13 and 14 so as to form the groove face 10, which is
larger than the groove face formed by the members themselves.
Thereafter, the joint members are opposed to each other as shown in
FIG. 3, they are welded to each other as melting the groove face 10
including the overlay weld metal, whereby ensuring the throat depth
1A in the direction of the plate thickness exceeding the plate
thickness of 2A of the member as shown in FIG. 4, or a throat depth
2Q in the direction of the plate width exceeding a plate width 2P
of FIG. 13, or a throat depth in the directions of plate thickness
and the plate width exceeding both plate thickness and plate
width.
[0031] According to the present invention, as compared with the
conventional joint of backing system, after the joint welding,
there is no stress concentration caused by harmful notches as shown
in 7 of FIG. 40 or 25A of FIG. 43, the plate thickness and plate
width at the cross-section of joint can be increased, the tensile
strength in plane of the joint can be increased, and bending
strength, bending ductility, and fatigue strength in the direction
of the plate thickness of the joint and that of the plate width can
be increased. Also, it is possible to omit the steel end tab shown
in FIG. 43 and ceramics end tab for the steel end tab. In addition,
there is a case in which welding defect easily occurs in the
ceramics end tab. The execution method of the present invention is
effective in these cases.
[0032] Also, there is a case in which a larger overlay weld must be
formed to obtain a predetermined leg length at the side of the
non-consumable backing material, since wettability between the
non-consumable backing material and the overlay weld metal is low
in performing the overlay welding according to the method of each
invention. The present invention relates to a method for forming
overlay welding bead, which improves wettability between the
non-consumable backing material and the overlay weld metal and
which forms smooth bead shapes between both weld toes of the
overlay weld in the above case.
[0033] Namely, the present invention is the method, which is used
when overlay welding according to the method of each invention is
performed. More specifically, a thin steel plate 29 of the same
material as the overlay welding material or the welding joint
member is attached to the overlay welding side of non-consumable
backing material in advance as shown in FIG. 15. Then, overlay
welding 9 is provided to the back face of the member 2 or the side
face including the back face between the non-consumable backing
material 8 and the member 2 as shown in FIG. 16. The thin steel
plate 29 has an effect that draws the melted metal to the side of
the thin steel plate, that is, to the direction of the
non-consumable material by surface tension when being melted
partially at the overlay welding. This is effective in obtaining
the smooth overlay welding bead shape 9 from the non-consumable
backing material 8 to the member 2. By this smooth overlay welding
bead shape 9, the maximum overlay weld leg length with a minimum
amount of overlay weld can be obtained at the side of the
non-consumable backing material. Thus, the thin steel plate is
useful to form the shape of the overlay metal smoothly when being
melted. The thickness of the thin steel plate was less than 3 mm
appropriately in consideration of penetration at the welding, cost
efficiency, and edge preparation of post-process. If the overlay
weld thus obtained is subjected to edge preparation together with
the member 2 at the position indicated by 30 of FIG. 16A, a groove,
which is larger than the plate thickness of the member 2, can be
obtained as shown in FIG. 16B. If the member 2 subjected to edge
preparation as shown in FIG. 16B is brought in contact with the
plane of the opponent's material 1 and is subjected to joint
welding 6 as shown in FIG. 19, the throat depth, which is larger
than the plate thickness of the material 2 or the plate width
thereof, can be obtained.
[0034] Moreover, the above invention cannot be executed when edge
preparation is performed before the overlay welding for the reason
of production process such processing on commission. For this
reason, the present invention provides a method in which overlay
welding is provided to the member subjected to the edge preparation
previously using the non-consumable backing material so as to
increase the groove area formed by the member.
[0035] Namely, according to the present invention, in the steel
structure, the backing material 8, which is not melted by a welding
heat source such as arc heating etc., is placed to an end face of a
T-welding joint member, which is subjected to edge preparation 32
in advance as shown in FIG. 17, or one end face or both end faces
of butt welding members, and thereafter, overlay welding 9 is
performed between a back face of the end of the member or the back
face including the side face of the end of the member and the
backing material 8 as shown in FIG. 17. After that, a part 33 of
the backing material contacting surface of the overlay weld metal 9
is used as an extension of a joint groove 32 of the main member.
Thereafter, the joint members are opposed to each other as shown in
FIG. 3, they are welded to each other as melting the groove face
including the overlay weld metal, whereby ensuring the throat depth
in the direction of the plate thickness exceeding the plate
thickness of the member as shown in FIG. 4, or the throat depth in
the direction of the plate width exceeding the plate width, or the
throat depth in the directions of plate thickness and the plate
width exceeding both plate depth and plate width.
[0036] According to the present invention, there are disadvantages
in that the part 33 of the backing material contacting surface of
the overlay weld metal 9 easily deviates from the joint groove 32
of the main member and the continuous execution from the edge
preparation to the joint welding can not be carried out. However,
this invention is effective as an alternative to the
above-mentioned invention in the joint welding of the end face
subjected to the edge preparation. The reason why a partially
vertical face 31 of the non-consumable backing material in FIG. 17
is formed is that the overlay weld metal is put in contact with a
vertical groove face of the single bevel groove of the opponent's
member to position the member 2 in right and left axial directions
as shown in FIG. 3. This invention is made by the same process as
the aforementioned invention, and has numerous advantages, which
compensate for the disadvantages of the conventional method. Unlike
the method in which the overlay welding 13 is provided to only the
diaphragm member 1 of FIG. 41 without using the backing material
and the method in which the overlay welding 13 and 13A is provided
to both members 1 and 2 of FIG. 42 without using the backing
material, the present invention is the method that can solve the
problems of the prior art as in FIGS. 41 and 42 and achieve the
part of the effects of the aforementioned invention. Furthermore,
combination of this invention and the invention shown in FIGS. 15
and 16 is effective in obtaining the smooth overlay shape.
[0037] According to the present invention, one-side welding is
performed by the following method when the present invention is
applied to the square steel pipe with a small diameter.
[0038] More specifically, in order to eliminate the corners of the
roots 1R and 2R of FIG. 39 to largely reduce stress concentration
at the roots, the backing material 8 such as copper, which is not
melted by the welding heat source, is placed to the back face of
the end of the member as shown in FIG. 18. Then, the overlay
welding 9 is performed between the back face of the joint member 2
and the backing material 8 and edge preparation is performed to the
end of the member including the overlay weld metal as shown in FIG.
2. Thereafter, the joint members are opposed to each other as shown
in FIG. 3, and they are welded to each other as melting the groove
of the overlay weld metal from the front side of the groove as
shown in FIG. 4, whereby ensuring the throat depth in the direction
of the plate thickness exceeding the plate thickness of the
member.
[0039] According to the present invention, one-side welding is
performed by the following method when the present invention is
applied to the case the one-side butt welding in which two members
such as square steel pipes with a small diameter welded to each
other are in substantially the same plane.
[0040] More specifically, the backing material 8 such as copper,
which is not melted by the welding heat source, is placed to the
back face of one end or both ends of the butt welding members as
shown in FIG. 18. Then, the overlay welding 9 is performed between
the back face of the end face 2T of the joint member and the
backing material. After that, edge preparation is performed to the
end of the member including the overlay weld metal as shown in FIG.
2. Thereafter, the joint members are opposed to each other as shown
in FIG. 3, and they are welded to each other as melting the groove
of the overlay weld metal from the front side of the groove as
shown in FIG. 4, whereby ensuring the throat depth in the direction
of the plate thickness exceeding the plate thickness of the member.
In this way, since the groove for overlay is opened to the outside
at the end face of the square steel pipe with a small diameter,
overlay welding can be easily carried out even at the end face of
the square steel pipe with a small diameter.
[0041] According to the present invention, there is a case in which
T butt joint welding or butt welding where two members are in
substantially the same plane is performed, for example, with the
backing material such as copper, which is not melted by the arc
heat, placed to the back of the end of, e.g., H-shape steel flange
in the longitudinal direction, and then overlay welding is
performed. In this case, the backing material 8 such as copper,
which is not melted by the arc heat, is placed thereto to enclose
the end of the flange as shown in FIG. 19A. Then, overlay welding
is provided to the member including the side surface of the flange
and edge preparation is performed to the member 2 including the
overlay weld as shown in FIG. 13 so as to obtain the groove depth,
which is larger than the plate thickness of the member 2, and the
groove length, which is larger than the plate width. Thereafter,
joint welding is carried out, so that the joint weld can ensure the
throat depth in the direction of the plate thickness exceeding the
plate thickness of the flange or the throat depth in the direction
of the plate width exceeding the plate width. Therefore, in this
case, the welding joint can obtain bending deformation ability,
joint tensile strength, and fatigue strength, which are larger than
the conventional welding joint of FIG. 40.
[0042] In the steel structure, butt welding with backing metal is
normally performed in the T butt welding for attaching stiffener
inserted into the H-shape steel flanges, but stress concentration
is indeed generated by attachment of the backing metal. In order to
relax this stress concentration, according to the present
invention, bending process is performed at the end of, such as the
stiffener of the T-welding joint member and the outer face of the
end of the bend-processed portion is used as a groove face. Or, the
end face of the bend-processed portion is subjected to a mechanical
or thermal cutting process to produce the groove face. Thereafter,
the joint members are opposed to each other, and they are welded to
each other from the front side of the groove, whereby ensuring the
throat depth in the direction of the plate thickness exceeding the
plate thickness of the member to which the end face is welded.
[0043] More specifically, one-side welding is performed by the
method as follows.
[0044] That is, as shown in FIG. 20, the end of the member 2 such
as stiffener is bent by a press. Then, when an upper angle portion
2K of the end face of the member 2 is lower than a bottom position
2U of the member 2 by more than about 5 mm, preferably more than 8
mm and less than 12 mm, the outer face of the end face of the
bend-processed portion is directly used as a groove face 2F, and
the joint members 1 and 2 are opposed to each other as shown in
FIG. 21, and joint welding 6 is provided these members from the
front side of the groove as shown in FIG. 22, whereby ensuring the
throat depth 1A in the direction of the plate thickness exceeding
the plate thickness t of the member 2. This makes it possible to
omit the backing metal that generates stress concentration and
reduces joint strength.
[0045] As shown in FIG. 23, the end face of the member 2 such as
stiffener is bent by a press. Then, when the upper angle portion 2K
of the end face of the member 2 is higher than the bottom position
2U of the member 2 and a lower angle portion 2L of the end face is
lower than the bottom position 2U of the member 2 by more than
about 5 mm, preferably more than 8 mm and less than 12 mm, the end
face of the member 2 is subjected to edge reparation at a process
position 2E of FIG. 24 to have a shape with a groove face 2F as
shown in FIG. 25. Then, the joint members 1 and 2 are opposed to
each other as shown in FIG. 21, and they are welded to each other
from the front side of the groove as shown in FIG. 22, whereby
ensuring the throat depth 1A in the direction of the plate
thickness exceeding the plate thickness t of the member 2 to which
the end face is welded.
[0046] Also, even in the butt welding where the members are in the
same plane, one side or both side bending process of FIG. 20 or
FIG. 23 is provided to the end face of at least one of the butt
joint welding members. Then, the outer face of the end face of the
bend-processed portion is used as a groove face in the same steps
as the above stiffener. Or, the end of the bend-processed portion
is subjected to a mechanical or thermal cutting process. The end of
the member 2 is subjected to edge reparation at the process
position 2E of FIG. 24 to produce the groove face 2F as shown in
FIG. 25. Thereafter, the joint members are opposed to each other as
shown in FIG. 21, and they are welded to each other from the front
side of the groove in the way as shown in FIG. 26 when the plate
thickness of these members are the same as each other or in the way
as shown in FIG. 27 when the plate thickness of these members are
different from each other. As a result, the throat depth 1A in the
direction of the plate thickness exceeding the plate thickness t of
at least thinner member 2 can be ensured. This eliminates the
generation of stress concentration due to the notch as in the butt
welding joint with a backing metal. This also improves bending
ductility of the joint, tensile strength, and fatigue strength.
[0047] According to the present invention, when one-side welding is
performed in the butt welding joint where T-shape members are
substantially right angles to each other, the following welding is
performed in order to strengthen the joint of the conventional
method as shown in FIG. 40 and to render the harmful notches 7 and
7A of the back face harmless.
[0048] More specifically, as shown in FIG. 28, at the side of the
member 2 to which the end face is welded, welding is performed such
that a position 6T of a welding bead weld toe of the front side is
placed to be separated from a position 7 of the welding root of the
back face by more than 80% of the plate thickness t of the member
of 2A, preferably, to be separated from the plate thickness t of
the member of 2A by 1.5 t, that is, 6B.gtoreq.=0.8 t, preferably,
t.ltoreq.6B.ltoreq.1.5 t in FIG. 28. Moreover, welding is performed
such that reinforcement height of the front bead of the final layer
in the entire area of the welding bead width of at least back face
and reinforcement height 6H of the front bead of the final layer at
the welding root of the back face are ensured by at least more than
10% of the plate thickness t, preferably more than 15% to less than
25%. Furthermore, welding is performed such that reinforcement
height of the final layer of the joint weld 6 is smoothly changed
from the base metal surface of the joint member 1 to the member
2.
[0049] By such welding, in the T-joint of FIG. 28, thickness 2H of
the notch portion of the back face is increased, stress
concentration at the notch portion is reduced, so that the T-joint
is reinforced to improve strength against tensile load 2C of the
member 2 and bending moment 2B. In this case, the reason why the
welding range is set to preferably less than 1.5 times of the base
metal is to prevent welding distortion and welding cost from being
increased.
[0050] According to the method of the present invention, when tack
welding of the backing metal exists as shown in FIG. 29, the
following welding is performed.
[0051] More specifically, welding is performed such that a distance
between the weld toe 4A, which is a stress concentration portion of
the backing metal, and the position 6T of the welding bead weld toe
of the front side becomes more than 80% of the plate thickness t of
the member of 2A, preferably, they are positioned to be separated
from the plate thickness t of the member of 2A by 1.5 t, that is,
6B.gtoreq.0.8 t, preferably, t.ltoreq.6B.ltoreq.1.5 t in FIG. 29.
Moreover, welding is performed such that reinforcement height of
the front bead of the final layer in the entire area of the welding
bead width of at least back face and reinforcement height 6H of the
front bead at the welding root of the back face are ensured by at
least more than 10% of the plate thickness t, preferably more than
15% to less than 25%. Then, welding is performed such that
reinforcement height of the final layer of the joint weld 6 is
smoothly changed from the base metal surface of the joint welding
member 1 to the member 2.
[0052] According to the method of the present invention, when
one-side welding is performed in the butt joint where two members
to be welded to each other are in the same plane, the following
welding is performed.
[0053] More specifically, as shown in FIG. 30, at the connection
using the square steel pipe as a column and at least the thinner
member (flange 2) of two members, that is, flange 2 and diaphragm
12, welding is performed such that the position 6T of the weld bead
toe of the front side is separated from the position of the welding
bead root 7 of the back face or the weld toe where the tack welding
is provided to the backing metal 3 by more than 80% of the plate
thickness, preferably, the position 6T is separated therefrom by
more than the plate thickness t of the member 2A, that is,
6B.gtoreq.0.8 t, preferably, t.ltoreq.6B.ltoreq.1.5 t in FIG. 30.
Moreover, welding is performed such that reinforcement height of
the front bead in the area of the welding bead width of at least
back face is ensured by at least more than 10% of the plate
thickness t, preferably more than 15% to less than 25%. Then,
welding is performed such that reinforcement height is smoothly
changed from the base metal surface.
BRIEF DESCRIPTION OF THE DRAWINGS
[0054] These objects and other objects and advantages of the
present invention will become more apparent upon reading of the
following detailed description and the accompanying drawings in
which:
[0055] FIG. 1 is a cross-sectional view illustrating one example in
which a water-cooled or non-water-cooled copper is placed at an end
of a member and overlay welding is performed;
[0056] FIG. 2 is a cross-sectional view showing a state in which
overlay welding is performed to the end of the member and both the
end portion and an overlay weld are subjected to edge preparation
wherein a member 2 is shown in a state that the FIG. 1 is
illustrated upside down;
[0057] FIG. 3 is a cross-sectional view showing a state in which
the end of the member is subjected to overlay welding and edge
preparation and the resultant is placed to an opponent member;
[0058] FIG. 4 is a cross-sectional view showing a state in which
the end of the member is subjected to overlay welding and edge
preparation, the resultant is placed to an opponent member and
welded;
[0059] FIG. 5 is a cross-sectional view showing a state in which
one pass overlay welding is performed with respect to an end face
to be welded and both the end face and the overlay weld are
cut;
[0060] FIG. 6 is a cross-sectional view showing a state in which
one pass overlay welding is performed with respect to an end face
to be welded and both the end face and the overlay weld are
subjected to edge preparation;
[0061] FIG. 7 is a shop drawing showing a state in which overlay
welding is performed among a back face of an end of a steel member
with a finite width to be welded and its side face, and a
non-consumable backing metal;
[0062] FIG. 8 is a shop drawing showing a state in which overlay
welding is performed among a back face of an end of a steel member
with a finite width to be welded and its side face, and two
non-consumable backing metals 8;
[0063] FIG. 9 is an outline view showing a state after overlay
welding is performed among a back face of an end of a steel member
with a finite width to be welded and its side face, and a
non-consumable backing metal;
[0064] FIG. 10 is an outline view showing a state after overlay
welding is performed among a back face of an end of an H shape
steel member with a finite width to be welded and its side face,
and a non-consumable backing metal;
[0065] FIG. 11 is a view showing a state of overlay welding to a
steel member with a finite width to be welded;
[0066] FIG. 12 a view showing a state of overlay welding to a steel
member with a finite width to be welded using a non-consumable
backing material;
[0067] FIG. 13 is an outline view an outline view showing a state
that edge preparation is carried out after overlay welding is
performed among a back face of an end of a steel member with a
finite width to be welded and its side face, and a non-consumable
backing metal;
[0068] FIG. 14 is an outline view showing a state that edge
preparation is carried out after overlay welding is performed among
a back face of an end of an H shape steel member with a finite
width to be welded and its side face, and a non-consumable backing
metal;
[0069] FIG. 15 is a view showing a state that a thin steel plate is
placed to an overlay weld side of the non-consumable backing
material and is set with the member 2;
[0070] FIG. 16 is a view showing a state that a thin steel plate is
placed to an overlay weld side of the non-consumable backing
material and is overlay welded with the member 2;
[0071] FIG. 16A is a cross-sectional view showing a working
position for forming a groove including an overlay weld wherein a
thin steel plate is placed to an overlay weld side of the
non-consumable backing material and is overlay welded with the
member 2 and then the non-consumable backing material is
removed;
[0072] FIG. 16B is a cross-sectional view showing that a thin steel
plate is placed to an overlay weld side of the non-consumable
backing material and is overlay welded with the member 2 and the
non-consumable backing material is removed, and the resultant
including the overlay weld is subjected to edge preparation;
[0073] FIG. 17 is a cross-sectional view showing that the
non-consumable backing material is placed to an end face of a joint
member subjected to edge preparation and is overlay welded;
[0074] FIG. 18 is a cross-sectional view showing the non-consumable
backing material such as copper is placed to the back side of the
end of the member to be welded, and the back side of the end is
overlay welded by a T welding joint;
[0075] FIG. 19 is a cross-sectional view showing that a thin steel
plate is placed to an overlay weld side of the non-consumable
backing material and is overlay welded with the member 2 and the
non-consumable backing material is removed and the resultant
including the overlay weld is subjected to edge preparation and
joint welding;
[0076] FIG. 19A is an outline view showing that backing material
such as copper, which is not melted by arc heat, is placed to the
back side of an H shape steel flange in its longitudinal direction
to enclose the end of the flange;
[0077] FIG. 20 is a cross-sectional view showing a member such as a
stiffener with an end, which is largely bent by a press, and so
on;
[0078] FIG. 21 is a cross-sectional view showing a state that a
member such as a stiffener with an end, which is bent a little by a
press, etc., and which is subjected to edge preparation, is set
between H shape steel flanges;
[0079] FIG. 22 is a cross-sectional view showing a state that a
member such as a stiffener with an end, which is bent a little by a
press, etc., and which is subjected to edge preparation, is welded
between H shape steel flanges;
[0080] FIG. 23 is a cross-sectional view showing a member such as a
stiffener with an end, which is bent a little by a press, etc.;
[0081] FIG. 24 is a cross-sectional view showing a cutting position
of a member such as a stiffener with an end, which is bent a little
by a press, etc.;
[0082] FIG. 25 is a cross-sectional view showing a member such as a
stiffener with an end, which is bent a little by a press, etc., and
which is subjected to edge preparation;
[0083] FIG. 26 is a cross-sectional view showing a joint when
members, each having an end bent by a press and the same plate
thickness, are abutted and welded;
[0084] FIG. 27 is a cross-sectional view showing a joint when
members, each having an end face bent by a press and a different
plate thickness, are abutted and welded;
[0085] FIG. 28 is a cross-sectional view showing a formation of
weld reinforcement for a final layer according to the present
invention with respect to the joint of a conventional method in
which no tack welding is performed to the backing metal;
[0086] FIG. 29 is a cross-sectional view showing a formation of
weld reinforcement for a final layer according to the present
invention with respect to the joint of a conventional method in
which tack welding is performed to the backing metal;
[0087] FIG. 30 is a cross-sectional view showing an application
example of improvement of forming weld reinforcement according to
the present invention in butt welding between a beam connection
diaphragm and a beam flange;
[0088] FIG. 31 is a cross-sectional view showing steel structure
welding wherein a square pipe is welded to a diaphragm;
[0089] FIG. 32 is a cross-sectional view showing a state in which
two-pass overlay welding is performed with respect to an end to be
welded, and both the end and the overlay weld are cut;
[0090] FIG. 33 is a cross-sectional view showing a state in which
two-pass overlay welding is performed with respect to an end to be
welded, and both the end and the overlay weld are subjected to edge
preparation;
[0091] FIG. 34 is a cross-sectional view showing one example of
assembly of butt joint of square steel or circular steel columns
set up vertically according to the present invention;
[0092] FIG. 35 is a cross-sectional view showing one example of
welding process of butt joint of square steel or circular steel
columns set up vertically according to the present invention;
[0093] FIG. 36 is a view showing an example of a weld of a column
to diaphragm of a structure connection and a weld of a diaphragm to
beam with non-scallop when a back face of the end of a square steel
pipe and a back face of the end of an H shape steel are subjected
to overly welding;
[0094] FIG. 37 is a cross-sectional view showing a state in which
an end of a member is overlay welded and both the end and an
overlay weld are subjected to edge preparation with a curved
surface;
[0095] FIG. 38 is a view showing an example in which members bent
by a press are applied to the column and beam joint using an H
shape steel for column connection and welding is performed;
[0096] FIG. 39 is a cross-sectional view showing an example of a
conventional joint shape with backing metal before one-side welding
is performed;
[0097] FIG. 40 is a cross-sectional view showing an example of a
conventional joint with backing metal after one-side welding is
performed;
[0098] FIG. 41 is a cross-sectional view showing a one-side welding
method in which the surface position to be welded of a diaphragm is
subjected to overlay welding in advance, and T-joint members are
subjected to uranami welding from one side;
[0099] FIG. 42 is a cross-sectional view showing a one-side welding
method in which overlay welding is provided to both the surface of
a member to be welded such as a diaphragm and the back face of the
end of the square steel pipe subjected to edge preparation, and
T-joint members are subjected to uranami welding from one side;
[0100] FIG. 43 is an execution example in which steel end tabs are
attached to the groove end according to the conventional method of
column-beam joint;
[0101] FIG. 44 is a cross-sectional view of a formation of weld
reinforcement by the conventional method in which no tack welding
is performed to the backing metal, according to the requirement the
Japan Architectural Standard Specification;
[0102] FIG. 45 is a cross-sectional view of a formation of weld
reinforcement by the conventional method in which tack welding is
performed to the backing metal according to the requirement the
Japan Architectural Standard Specification;
[0103] FIG. 46 is a cross-sectional view showing one example of
assembly of butt joint of square steel or circular steel columns
set up vertically using backing metal according to the conventional
method;
[0104] FIG. 47 is a view showing an example of a column and a
diaphragm at a structure connection and a diaphragm and a beam at a
weld according to the conventional method;
[0105] FIG. 48 is an outline view showing an example in which the
joint of the H shape steel column and H shape steel beam using a
dog born procedure is executed by the conventional welding method
with a backing metal, and the overlay welding method or bending
procedure of the present invention in the welding of the H shape
steel column and stiffener at the connection for H shape steel is
used; and
[0106] FIG. 49 is an outline view when the overlay welding or
bending procedure of the present invention is used in the welding
of the H shape steel column and stiffener, and the welding of the H
shape steel column and H shape steel beam using a dog born
procedure at the connection for H shape steel is performed.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0107] Preferred embodiments of the present invention will be
explained with reference to the drawings accompanying herewith.
[0108] FIGS. 1 to 4 show one embodiment of the present invention,
and is an example in which the present invention is applied to a
normal T-joint.
[0109] According to this embodiment, as shown in FIG. 1,
non-metallic backing material 8 or water-cooled or non-water-cooled
copper backing material 8 suffering no melting damage due to
welding heat source, is placed to an end 2T of a member 2, and
overlay wielding 9 is provided between the back face of the end 2T
of the joint member and the backing material 8. Then, as shown in
FIG. 2, the end of the member including an overlay weld is
subjected to edge preparation. After that, the resultant is placed
to an opponent's member face as shown in FIG. 3, and joint welding
is performed thereto as shown in FIG. 4.
[0110] This eliminates the need for providing various work
associated with the attachment of the backing metal unlike the
conventional case shown in FIGS. 39 and 40, and makes it possible
to carry out continuous work from edge preparation to joint
welding. Namely, since this makes it possible to omit the backing
metal, simplify the setting of members, use high welding current at
the first layer and ensure the size accuracy of steel structure, a
large reduction in the number of man-hours needed to produce the
steel structure can be attained. At the same time, the production
of backing metal after edge preparation and the off-line work
process of attachment are omitted so that numerous joint welding is
continuously performed. This allows a large reduction in the number
of man-hours needed to produce the steel in view of the production
processes and steps. Moreover, since the removal of harmful
notches, the increase in the throat depth, and the ensuring of size
accuracy of the steel structure can be attained, bending ductility,
fatigue strength, and earthquake resisting strength can be easily
ensured.
[0111] In this way, the number of man-hours needed to produce the
steel structure is largely reduced by improvement in view of
efficiency of the joint welding and that of the production
processes and steps. This makes it possible to reduce the number of
man-hours needed to production by about 30% in the joint of average
plate thickness of 25 mm even if the number of man-hours needed to
execute overlay welding is included.
[0112] In FIG. 4, the throat depth of joint is 2A in the case that
the overlay welding 9 is not provided. However, if throat depth 1A
of the joint obtained at the groove portion, which includes the
overlay weld combined with the base metal, by the actual welding is
referred to as a throat depth of the present invention, the throat
depth of the joint is increased to 1A from 2A in the welding
according to the present invention. According to the experiment,
the cracks were generated at the root when a bending angle of the
member 2 was 15 to 25.degree.in the conventional joint shown in
FIG. 40. By contrast, in the execution of work according to the
present invention, it is assumed that the increase in the throat of
the welding joint obtained by use of the same welding material as
that of the member 1 is more than 10% of the member 2. In this
case, even if the upward bending load 2B is applied on the member
2, generation of crack is little recognized and the member 2 is
only bent since an angle at which the crack of member 2 is
generated is 50 degrees or more. In other words, since the joint
according to the present invention has the increase in the throat,
the presence of a few unwelded portions at the root 9B of the joint
weld 6 of FIG. 4 does not work as an adverse effect factor of
stress concentration.
[0113] If stiffness is low such as a case in which the thickness of
the member 1 is smaller than that of the member 2, uranami welding
is provided to the root 9B of the joint weld of the present
invention by horizontal welding. Moreover, if a weld of the member
is exposed outside as in the H shape flange, welding is
additionally provided to the root 9B or a grinder finish is given
to the root 9B. This eliminates the stress concentration portion,
so that fatigue strength of the joint can be further improved.
[0114] FIG. 31 is a view showing an example in which the one-side
welding method according to this embodiment is applied to the joint
between the square steel pipe column and the diaphragm at the steel
structure connection.
[0115] In the conventional method, since the backing metal 3 is
attached to the inner periphery of the square steel pipe to perform
joint welding as shown in FIG. 47, the removal of a reinforcement
of the longitudinal joint by producing the square steel pipe is
needed to attach the backing metal. This requires much time and
effort in attaching the backing metal for column, positioning the
members, and tack welding, and a great number of man-hours needed
to production are needed.
[0116] In the method according to the present invention, however,
since overlay welding 9 is performed to the back face of the end of
the square steel pipe beforehand as shown in FIG. 31, the square
steel pipe 11 only has to be placed to the diaphragm 12. Whereby,
the positional adjustment of the square steel pipe 11 to the
diaphragm 12 can be easily carried out and the gap adjustment
between the square steel pipe 11 and the diaphragm 12 and the tack
welding become unnecessary. This allows joint welding 6 to be
performed immediately without depending on the welding position.
Though FIG. 31 shows the application to the square steel pipe, this
can be applied to the circular steel pipe in the same way.
[0117] FIG. 32 is a view showing another embodiment of the present
invention.
[0118] In this embodiment, the overlay welding 9 with a
predetermined shape is provided to the back face of the member at a
designed edge preparation location 15A, serving as an end of the
joint member 2, in one to three passes. In this example, overlay
welding is performed in two passes so as to obtain reinforcement
larger than reinforcement obtained in one pass. Thereafter, both
the member of the designed edge preparation location and the
reinforcement weld metal are cut at the same angle as that of the
face of the opponent's member. After cutting as in this example,
edge preparation is provided to the member 2 including the overlay
weld metal as shown in FIG. 2.
[0119] FIG. 33 is a view showing a modification of FIG. 32.
[0120] In this example, similar to FIG. 32, the overlay welding 9
is provided to the back face of the member at the designed edge
preparation location 15A, serving as an end of the joint member 2,
in two passes, which obtains reinforcement larger than
reinforcement obtained in one pass. Thereafter, the resultant is
cut at the same angle as the groove angle of the designed edge
preparation location, and a cut face 15 obtained is used as a
groove face as it is. In this way, a groove, which is larger than
the case of one pass, can be obtained by performing overlay welding
9 in two passes. Thereafter, in a case where this is applied to the
T-welding joint, the joint welding as shown in FIG. 4 is
executed.
[0121] In addition, the size of the designed edge preparation
location 15A in FIGS. 32 and 33 is normally 0 to 500 mm.
[0122] FIG. 46 is a cross-sectional view showing one example of
assembly of butt joint of square steel or circular steel columns
set up vertically according to the conventional method. At a joint
welding preparation, since assembly and adjustment of inner side of
pipes 16 and 17 and adjustment of a groove gap 16G are difficult to
be carried out, a backing metal 18 and a stopper 19 are used at one
joint in this example, and the backing metal 18 welded to the upper
member 16 by tack welding 20 is inserted to the lower member 17 in
a spigot-joint manner to welded the members to each other. Then,
the groove gap is adjusted by the upper and lower positions of the
backing metal 18, the long and short length thereof, and the upper
and lower positions of the stopper 19. This conventional method
needs a great number of man-hours needed to produce the backing
plate and stopper and to perform correct attachment, has difficulty
in adjustment because of variations in the product size accuracy of
pipe.
[0123] FIG. 34 is a cross-sectional view showing one example of
assembly of butt joint of square steel or circular steel columns
set up vertically according to the method of the present invention.
As is obvious from FIG. 34, even if there is a little misalignment
between the members 16 and 17, the distance between the members 16
and 7 and the gap 16G can be maintained constant by only abutting
both members against each other due to overlay 22 and 23. As shown
in FIG. 35, full penetration and a throat depth 16B exceeding a
plate thickness 16A of the member are easily ensured by the joint
welding. In this case, if the throat depth that is comparable to
the plate thickness 16A of the member is needed to be stably
ensured, the overlay welding 22 of FIGS. 34 and 35 can be reduced
or omitted.
[0124] This execution example can be easily applied to not only the
building but also the stable welding from the exterior or interior
of a pipeline or a water piping for electric generation, and is
effective in ensuring strength and quality of the joint and
reducing the number of man-hours needed to production.
[0125] FIG. 47 is a view showing an example of a joint between a
diaphragm 12 and a square steel pipe column 11 at a steel structure
connection and a joint between the diaphragm 12 and a H shape steel
flange 26 according to the conventional method. In either of these
joints, many backing metals 3 and tack welds 4 are used.
[0126] FIG. 36 shows a case in which the joint welding 6 is applied
to the same joint as that of FIG. 47 in the method according to the
present invention. FIG. 36 shows a state in which the present
invention is applied to the welding of the diagram 12 to the square
steel pipe 11, neither the backing metal nor the tack welding is
provided, and penetration deeper than the plate thickness of the
member 11 is obtained, and no harmful notch 7 of the conventional
joint shown in FIG. 40 is formed. FIG. 47 shows a scallop what is
called weld access hole 28, which is a large opening, the backing
plate, and the tack welding 4 at the joint between the diaphragm 12
and the H shape steel flange 26. However, FIG. 36 shows a state,
which is just before the joint welding 6 is executed after
performing the overlay welding 9 at the joint between the diaphragm
12 and the H shape steel flange 26 by the method according to the
present invention. A dotted line shows the joint welding 6 at the
connection and a designed weld location 27A for a web without
scallop. In this case, FIG. 36 illustrates a state in which neither
the backing metal nor the tack welding for attaching the backing
metal is provided, and penetration deeper than the plate thickness
of the member 26 is obtained, no harmful notch 7 of the
conventional joint shown in FIG. 40 is formed, and no scallop 28
shown in FIG. 47 is formed. Namely, in this embodiment according to
the present invention, the welding portion of an H shape steel beam
at a steel structure connection can be easily executed by a
non-scallop procedure. In the example of the conventional method of
FIG. 47, if the scallop 28 is eliminated, there are needed special
contrivances, for example, two backing metals 3 are used at both
sides of a web 27 separately. However, in this embodiment according
to the present invention, neither the backing metal nor the scallop
is needed, and this is excellent in the safety of joint and the
reduction in the number of man-hours needed to production.
[0127] In the method of the present invention, as welding material
to be used in the overlay welding 9 executed between the
non-consumable backing material 8 and the joint end of the member
2, welding material with strength lower than that of the joint end
face of the member 2 can be used. The use of such welding material
ensures tensile strength and brings about relaxation of stress
concentration by dispersion of plastic distortion so as to further
help to improve bending ductility and fatigue strength as a welding
joint.
[0128] In the method of the present invention, there is a case in
which the welding joint members 1 and 2 are welded to each other as
melting a groove surface 10 of the overlay weld metal of FIG. 3
from the front side of the groove as shown in FIG. 4. In this case,
the use of welding material with strength lower than that of the
welding joint members 1 and 2 can relax sensitivity of the crack
generation at the root. Also, the use of welding material with
strength higher than that of the welding joint members improves
strength of the root. Either case is effective in more improving
bending ductility and fatigue strength.
[0129] In the method of the present invention, at the time of
performing edge preparation with the welding member 2 and the
overlay welding 9 as shown in FIG. 37, edge preparation is provided
to the groove surface 10 to form not a flat surface but a curved
surface with a radius of curvature of 1 to 5 mm at a groove bottom
34. This expands the groove bottom 34 and is effective in obtaining
deep penetration at the root of the joint welding 6 shown in FIG. 4
more easily.
[0130] In a case where the present invention is applied to the
square steel pipes each having a small diameter in the steel
structure such as a building, as shown in FIG. 18, the backing
material 8 such as copper, which is not melted by the welding heat
source, is placed to the back face of the end of the member 2 to
which the end face of the T-butt welding is welded, that is, placed
to the inner side of the steel pipe. Then, the overlay welding 9 is
carried out between the back face of the joint member 2 and the
backing material. Thereafter, one-side welding is performed by the
method for ensuring the throat depth 1A in the direction of plate
thickness exceeding the plate thickness 2A of the member 2 to which
end face is welded through the same steps as those of FIGS. 2 to 4.
In this case, ceramics with high melting point, tungsten, carbon,
graphite, and the like can be used in place of the backing material
8 such as copper shown in FIG. 18, which is not melted. In order to
easily take out these backing metals from the interior of the
square steel pipe as a divided form or miniaturize these backing
metals, a method in which water cooling is performed to improve
cooling efficiency may be possible. Moreover, there is a case in
which a thin plate with the same metal as that of the member 2 is
attached to the overlay welding side of the backing material 8 such
as copper, which is not melted, as shown in FIG. 15 and the overlay
welding 9 shown in FIG. 16 is carried out. Damage of the backing
material 8 is reduced and wettability of the overlay weld metal and
the thin plate is increased, making it possible to perform the
overlay welding smoothly.
[0131] In a case where the present invention is applied to one-side
butt welding of such as square steel pipes each having a small
diameter, as shown in FIG. 18, the backing material 8 such as
copper, which is not melted by the welding heat source, is placed
to the back face of one or both ends of the butt joint member.
Then, the overlay welding 9 is carried out between the back face of
the end face 2T of the welding joint member and the backing
material. Thereafter, one-side welding is performed by the method
for ensuring the throat depth 1A in the direction of plate
thickness exceeding the plate thickness 2A of the member 2 to which
end face is welded through the same steps as those of FIGS. 2 to 4.
As a result, since the groove for overlaying is opened outside at
the end of the square steel pipe with a small diameter, the
execution of overlay welding can be easily performed even at the
end of the square pipe with a small diameter. The execution method
of the present invention can be applied to the circular steel pipe
as well as the square steel pipe, and a case in which the butt
joint members have different plate thickness or a large
misalignment. In the case that the butt joint members have
different plate thickness, overlay welding is provided to only the
member with a thinner plate thickness from the inner face by the
method according to the present invention, the end of the member
with a thicker plate thickness is subjected to welding at a single
bevel groove as being finished at the right angle. This makes it
possible to carry out the execution method having joint strength
and cost efficiency.
[0132] The backing material 8 such as copper, which is not melted
by the arc heat, is placed to the back face of the longitudinal end
of the member of the H shape steel flange to enclose the end of the
flange as shown in FIG. 19A. Then, overlay welding is provided to
the resultant including the side surface of the flange and edge
preparation is performed to the member 2 including the overlay weld
as shown in FIG. 13. Thereafter, joint welding is carried out, so
that the joint weld can ensure the throat depth in the direction of
the plate thickness exceeding the plate thickness of the flange 2
or the throat depth in the direction of the plate width exceeding
the plate width. In a case where overlay welding is performed to
the member 2 in a state of FIG. 19A, flat position welding is
normally carried out, but horizontal position welding may be easily
carried out. In this case, the backing material such as copper is
further placed to the upper side of FIG. 19 and overlay wielding is
executed, whereby facilitating the execution of the side face of
the flange. The execution method according to the present invention
allows concurrent use of the non-scallop procedure with no scallop
28 of FIG. 47 as shown in FIG. 36.
[0133] According to the present invention, as shown in FIG. 18, the
backing material 8 such as copper, which is not melted by the
welding heat source, is placed to the back face of the end of the
member 2 to which the end of the T-welding joint is welded and the
overlay welding 9 is carried out between the back face of the
welding joint member 2 and the backing material. Particularly, this
is extremely effective in the case in which the overlay welding is
provided to the inner side of the narrow end of the square or
circular steel pipe with a small diameter of less than 250 mm, as
compared with the method in which the backing material 8 such as
copper, which is not melted by the welding heat source, is placed
to the end face of the larger member 2 to which the end of the
T-welding joint is welded and the overlay welding 9 is carried out
between the back face of the joint member 2 and the backing
material as shown in FIG. 1.
[0134] In the present invention, after performing the overlay
welding 9 shown in FIG. 18 or FIG. 19A, edge preparation of FIG. 2
including the overlay portion is performed to have a J groove in
which a curved surface is formed on the groove bottom as shown in
FIG. 37. This is effective in ensuring penetration of the first
layer welding.
[0135] Though the press work shown in FIGS. 20 and 23 is carried
out by cold work or hot work depending on the plate thickness or
material, it is possible to use a method of molding the groove up
to a predetermined groove shape by a forging process in place of a
simple bending process. Also, this can be used as an inner
diaphragm at the steel structure connection using the square steel
pipes and circular steel pipes. In this case, if the end face of
the diaphragm produced by the press is hit by a hammer and the
like, the end face can be easily fit to the inner shape of the
square steel pipe or the circular steel pipe.
[0136] FIG. 22 shows an example in which the groove is formed by
the press and the stiffener 2 is butted and welded to the H shape
steel flange 1. In such a joint, the back face is opened in most
cases. The back face of the member 2 is gouged to be finished to a
sound portion as required, the back face is simply finished to the
sound portion by a grinder, or additional welding is provided to
the back face by CO.sub.2 gas shielded arc welding process,
shielded metal arc welding process, or tungsten insert gas (TIG)
gas welding process so that the back face can be smoothly
finished.
[0137] FIG. 38 shows an example when the present invention is
applied to the column and beam joint using the H shape steel for
column connection. The member 1 is a column using the H shape
steel, and a member 36 is a stiffener, which is fitted to the H
shape steel column and welded thereto. Either of the welds 6, that
is; one is between the column 1 and the stiffener 36 and the other
is between the column and the beam, shows an example in which the
end of the member 36 is bent and subjected to edge preparation to
complete the joint welding. As shown in FIG. 38, in either weld 6,
no backing metal is provided and the throat depth A1 in the
direction of the plate thickness exceeding the plate thickness t of
the member 36 is ensured, and harmful stress concentration
resulting from the presence of backing metal is not generated. In
addition, the same effect as mentioned above can be obtained even
if the following process is performed in place of the bending
process of the end of the member 36 in the execution example of
FIG. 38. More specifically, overlay welding is provided to the back
face of the end of the member 36 and the member 36 including the
overlay weld is subjected to edge preparation as shown in FIG. 2 to
carry out the joint weld 6.
[0138] Moreover, even in the butt welding of the members which are
in the same plane, the end of the member 2 is subjected to bending
process or cutting process in some instances to produce a groove
face 2F by the procedure of FIG. 20 or the procedures of FIGS. 23,
24, and 25 with respect to the end of at least one member of the
butt welding members. Thereafter, the joint members are opposed to
each other and the welding joint members are butted and welded from
the front side of the groove as shown in FIG. 26 or FIG. 27,
whereby obtaining the throat depth 1A in the direction of the plate
thickness exceeding the plate thickness t of thinner member 2. Even
in such a joint, the back face is opened in most cases. The back
faces of the members 1 and 2 are gouged to be finished to a sound
portion as required, the back face is simply finished to the sound
portion by a grinder, or additional welding is provided to the back
face by CO.sub.2 gas shielded arc welding process, shielded metal
arc welding process, or tungsten insert gas (TIG) gas welding
process so that the back face can be smoothly finished.
[0139] Additionally, in the present invention, the method, in which
the overlay welding is provided to the back face of the end of the
member and the back face including the overlay weld is subjected to
edge preparation so as to carry out joint welding, can be widely
applied to many joints in the wide range of the steel structure
welding joint. The press process of the present invention shown in
FIGS. 20 to 27 is effective in attaching the stiffener with a small
size, a light weight and simple handling to the H shape steel in
view of ease of press process.
[0140] Furthermore, in the present invention, edge preparation,
which is performed to have a J groove as shown in FIG. 37, is
effective in ensuring penetration of the first layer welding.
[0141] FIG. 28 is a view showing further another embodiment of the
present invention.
[0142] The method of this embodiment is the same as the
conventional method in that the welding is sequentially performed
from the first layer to the upper layer. The difference
therebetween lies in that the width and height of the final layer
of the joint weld 6 at the side of the member 2 to which the end is
welded are larger than those of the conventional method. Namely, in
the present invention, at the side of the member 2 to which the end
is welded, welding is performed such that a position 6T of a weld
bead toe of the front side is placed to be separated from a
position 7 of the welding root of the back face by more than 80% of
the plate thickness t of the member of 2A, preferably, to be
separated from the plate thickness t of the member of 2A by 1.5 t,
that is, 6B.gtoreq.0.8 t, preferably, t.ltoreq.6B.ltoreq.1.5 t in
FIG. 28. Moreover, welding is performed such that reinforcement
height of the front bead in the entire area of the welding bead
width of at least back face and reinforcement height 6H of the
front bead at the welding root of the back face are ensured by at
least more than 10% of the plate thickness t, preferably more than
15% to less than 25%. Furthermore, welding is performed such that
reinforcement height of the final layer of the joint weld 6 is
smoothly changed from the base metal surface of the joint welding
member 1 to the member 2. In this way, the wide and high final
layer can be attained by weaving the welding bead of the final
layer or increasing the number of passes.
[0143] According to the experiment, regarding the 400 MPa and 500
MPa class steel materials having thickness of 20 mm and 30 mm, the
crack was normally generated at the root when the member 2 was bent
at the bending angle of 10 to 30.degree. by bending moment 2B in
the conventional joint shown in FIG. 44. In the joint of FIG. 28
according to the present invention, no crack was generated even if
the member 2 was bent at the angle of more than 60.degree.. Also,
when the method according to the present invention was applied to
the joint using the back face overlaying method of FIG. 4
similarly, the crack was little generated even if the member 2 was
bent at the angle of more than 90.degree. by bending moment 2B in
most cases. In any of these bending tests, the bending portion was
the base material. Furthermore, when the tensile test was executed
using the same steel material, the crack or rupture occurred at the
notch 7 of the root in most cases in the joint of the conventional
method shown in FIG. 44. However, when the tensile load 2C was
given by the method according to the present invention shown in
FIG. 28, not the weld but the base metal was ruptured and original
strength of the base metal was ensured. When the method according
to the present invention as shown in FIG. 29 was applied to the
conventional joint shown in FIG. 45, improvement of bending
ductility and the rapture of the base metal against the tensile
load were similarly obtained.
[0144] There is a case in which one-side welding is carried out by
the method of the present invention in the butt welding joint of
the diaphragm 12 and the flange 2 wherein two members to be welded
are in the same plane according to the conventional method using
the backing metal. As shown in FIG. 28, the final layer is widely
welded, making it possible to improve joint strength and ductility.
Namely, as shown in FIG. 31, the connecting using the square steel
pipe 11 and the diaphragm 12 is produced by the process based on
the back face overlay welding method of FIGS. 2 to 4. Then, as
shown in FIG. 30, in the butt welding joint of the diaphragm 12 and
the flange 2 according to the conventional method using the backing
metal, the final layer is finished by 1-pass weaving weld or
multi-pass weld. At that time, welding is preferably performed such
that the final layer of the joint welding is set to
t.ltoreq.6B.ltoreq.1.5 t and such that reinforcement height of the
front bead in the entire area of the welding bead width of at least
front face is ensured by more than 15% to less than 25%. Moreover,
in case that one-side welding is performed in the butt welding
joint wherein the connection is produced by the overlay welding
method of the present invention as shown in FIG. 31 and two members
are in substantially the same plane, as shown in FIG. 18 or FIG.
19A, the backing material such as copper, which is not melted by
arc heat, is placed to the back face of the H shape steel flange
and the overlay welding is provided thereto in advance, and edge
preparation including the overlay portion is performed. Thereafter,
the joint welding between members 12 and 16 is performed as shown
in FIG. 36. Moreover, by the method of the present invention,
welding is performed such that the final layer of the joint welding
6 is set to t.ltoreq.6B.ltoreq.1.5 t and such that reinforcement
height of the front bead in the entire area of the welding bead
width of at least front face is ensured by more than 15% to less
than 25%. Then, as shown in FIG. 36, non-scallop welding 27A can be
executed.
[0145] In addition, the execution method of the present invention
reduces stress concentration and brings about improvement of
bending ductility and joint property with respect to the
conventional T-joint with the backing metal that causes stress
concentration. This is helpful to improve bending ductility and
joint strength in the application to the known steel structure.
[0146] Still moreover, in a case where the various methods
according to the present invention are used in the welding portion
between the building connection and the H shape steel beam, the
connecting portion is strengthened and buckling is generated at the
beam without breaking the connecting portion when the bending load
is added to the beam with respect to the earthquake force.
[0147] Namely, FIG. 48 is an outline view showing an example in
which the joint of the H shape steel column and H shape steel beam
using a dog born procedure 35 is executed by the conventional
welding execution method with a backing metal by use of the overlay
welding method and bending procedure of the present invention in
the welding of the H shape steel column stiffener 36 at the
connection for H shape steel. In the dog born joint 35 in which the
H shape steel beam flange 26 as shown in FIG. 48 is partially cut
and notched, when the bending load is applied to the H shape steel
beam, the buckling occurs at the notched beam instead of the fact
that the column and beam joint is not broken. Therefore, this may
be safe in view of the building as compared with the conventional
welding joint wherein the backing metal 3 and scallop 28 exist and
no dog born joint 35 is provided. However, since the joint of the
present invention has high strength, the method of the present
invention has a feature in which the joint with no notch in the
flange 26 has higher strength. Moreover, from the viewpoint of
cost, the method of the present invention has a feature in which no
notch process is provided in the flange 26 and production cost is
low as compared with the dog born procedure.
[0148] FIG. 49 is an outline view when the overlay welding method
and bending procedure of the present invention are used in the
welding of the H shape steel column stiffener and the welding of
the H shape steel column and H shape steel beam using a dog born
procedure at the connection for H shape steel. The execution method
of the present invention can be applied to the joint without being
contradictory to the dog born procedure. However, the use of the
method of the present invention eliminates the need for using the
dog born procedure 35 that reduces strength and increases
production cost since buckling occurs at the beam flange 26, if no
dog born 35 is provided.
[0149] Various embodiments and changes may be made there unto
without departing from the broad spirit and scope of the invention.
The above-described embodiments are intended to illustrate the
present invention, not to limit the scope of the present invention.
The scope of the present invention is shown by the attached claims
rather than the embodiments. Various modifications made within the
meaning of an equivalent of the claims of the invention and within
the claims are to be regarded to be in the scope of the present
invention.
* * * * *