U.S. patent application number 10/626713 was filed with the patent office on 2005-01-27 for chill blocks and methods for manufacturing chill blocks.
This patent application is currently assigned to SPX CORPORATION. Invention is credited to Malterer, Randall.
Application Number | 20050016710 10/626713 |
Document ID | / |
Family ID | 34080467 |
Filed Date | 2005-01-27 |
United States Patent
Application |
20050016710 |
Kind Code |
A1 |
Malterer, Randall |
January 27, 2005 |
Chill blocks and methods for manufacturing chill blocks
Abstract
A chill block made from copper bonded to tool steel is
disclosed. A tool steel layer of the chill block of less than about
0.5 inches thick is present on the parting surface of the chill
block or chill block face. A tool steel layer may also be present
on a portion of the sides of the chill blocks and/or the bottom of
the chill block. Chill blocks in accordance with the present
invention allow molten metal to solidify in the passageway formed
by a pair of chill blocks, and provide for efficient manufacturing
of objects by die casting methods.
Inventors: |
Malterer, Randall; (Granger,
IN) |
Correspondence
Address: |
BAKER & HOSTETLER LLP
Washington Square
Suite 1100
1050 Connecticut Avenue, N.W.
Washington
DC
20036
US
|
Assignee: |
SPX CORPORATION
|
Family ID: |
34080467 |
Appl. No.: |
10/626713 |
Filed: |
July 25, 2003 |
Current U.S.
Class: |
164/352 ;
164/100; 164/46 |
Current CPC
Class: |
B22D 15/04 20130101 |
Class at
Publication: |
164/352 ;
164/046; 164/100 |
International
Class: |
B22D 015/00; B22D
023/00 |
Claims
What is claimed is:
1. A method of manufacturing a chill block, comprising: forming a
first surface of a chill block from a first material; and bonding a
second material to the first surface.
2. The method of claim 1, wherein the first material is steel.
3. The method of claim 1, wherein the second material is a copper
metal.
4. The method of claim 1, wherein the first surface has a thickness
of the first material of less than about 0.5 inches.
5. The method of claim 1, further comprising bonding a third
material to a side of the second material that is not in contact
with the first material.
6. The method of claim 1, further comprising machining the chill
block after the step of bonding the second material to the first
material.
7. The method of claim 5, further comprising: machining the chill
block after the step of bonding the second material to the first
material; and machining the chill block after the step of bonding
the third material to the second material.
8. The method of claim 5, wherein the third material is steel.
9. The method of claim 1, wherein the first surface is formed in a
ceramic mold.
10. The method of claim 1, wherein the chill block is formed in a
ceramic mold.
11. The method of claim 2, wherein the steel is chosen from the
group consisting of ANSI H13, ANSI A2, and ANSI S7.
12. The method of claim 3, wherein the copper metal is beryllium
copper.
13. The method of claim 1, wherein a surface hardness of the first
material is at least 30 Rockwell "C" scale (Rc).
14. The method of claim 1, wherein a surface hardness of the steel
ranges from about 30 to about 70 Rc.
15. A method of manufacturing a chill block, comprising: using a
rapid solidification process to spray a first material that forms a
first layer of a chill block; using said rapid solidification
process to spray a second material onto a first surface of the
first layer, said second material comprising copper.
16. The method of claim 15, wherein the first layer has a thickness
of less than about 0.5 inches.
17. The method of claim 15, wherein the first layer has a hardness
ranging from about 30 to about 70 Rc.
18. The method of claim 15, wherein the first layer has a thickness
of less than about 0.5 inches and a hardness ranging from about 30
to about 70 Rc.
19. A chill block, comprising: a chill block base having a top
surface and a bottom surface and comprising a first material; and a
first layer of a second material bonded to the top surface of the
chill block base.
20. The chill block of claim 19, wherein the second material has a
thickness of less than about 0.5 inches.
21. The chill block of claim 19, further comprising a layer of a
third material bonded to the bottom surface of the chill block
base.
22. The chill block of claim 19, wherein the chill block base is
made from a material comprising copper.
23. A tool device for use with a die casting process for shaping
and solidifying molten metal into a shaped object, comprising:
shaping means for forming the shape of an object; and a first
chilling means for solidifying metal that exits the shaping means,
wherein the first chilling means comprises a layer of a first
material and a layer of a second material that are bonded
together.
24. The tool device of claim 23, further comprising: metal inlet
means for allowing metal to flow into the tool device.
25. The tool device of claim 23, further comprising: overflow means
between the shaping means and the first chilling means.
26. The method of claim 23, further comprising a second chilling
means arranged with the first chilling means to form a chill block
passageway.
27. The method of claim 23, wherein the first material comprises
steel, and the second material comprises copper.
Description
FIELD OF THE INVENTION
[0001] The present invention relates generally to casting devices.
More particularly, the present invention is directed to chill
blocks that are manufactured from two metals.
BACKGROUND OF THE INVENTION
[0002] In die casting, chill blocks are devices utilized in molds.
Typically, two tools are utilized to form a mold that will be
employed to manufacture a complete object. Each of the tool devices
has a cavity that defines the shape of a portion of the object to
be cast, and when arranged together define the entire shape of the
object to be cast. Each of the tools has a tool passageway leading
from the die cavity to the chill blocks.
[0003] Chill blocks are positioned in each of the tools and when
the chill blocks are arranged together, the chill blocks form a
chill block passageway. The tool passageway provided in each tool
allows gas in the die cavity to flow from the die cavity to the
chill block passageway, when molten metal is injected into a die
cavity to form an object.
[0004] The gas forced into the passageway of a die cavity enters
the chill block passageway and escapes when it reaches the end of
the chill block passageway. After a die cavity has been filled and
gas present in the mold cavity has been allowed to escape, any
metal overflow from a die cavity travels into the chill block
passageway. The molten metal may solidify in the chill block
passageway.
[0005] However, if the molten metal does not solidify while in the
chill block passageway the molten metal may escape from an end of
the chill block passageway.
[0006] Some chill blocks known in the art experience problems with
the retention of heat. For example, there are two-part chill blocks
that involve a steel part coupled to a copper part. Often, a
thermal grease is placed between the two parts to facilitate heat
exchange between the steel part and the copper part. Heat retention
is associated with the use of two-part steel and copper chill
blocks. When chill blocks retain heat, the molten metal may not
solidify at a rate to prevent it from escaping the chill
blocks.
[0007] After the molten metal has solidified in the passageway
formed between the pair of chill blocks, each of the chill blocks
may be removed from the metal that solidified between them. The
surface of a chill block that comes in contact with the overflow
metal is referred to as the parting surface of the chill block or
the chill block face. Typically, the parting surface has a jagged
surface. One conventional type of chill block is made entirely from
copper. However, users of copper chill blocks have found that
copper degrades rapidly when it comes in contact with aluminum.
Aluminum is commonly utilized in die casting to form objects. As a
result, copper chill blocks are replaced often during the
manufacturing of aluminum objects.
[0008] Accordingly, it is desirable to provide chill blocks that
avoid the retention of heat and allow molten metal to solidify
while in the passageway formed by a pair chill blocks. It is also
desirable to provide chill blocks that are durable, and allow for
efficient manufacturing of objects by die casting methods.
SUMMARY OF THE INVENTION
[0009] The foregoing needs are met, to a great extent, by the
present invention, wherein in one aspect an apparatus is provided
that in some embodiments allows molten metal to solidify in the
passageway formed by a pair of chill blocks, and that provides for
efficient manufacturing of objects by die casting methods.
[0010] In accordance with one embodiment of the present invention,
a method of manufacturing a chill block is provided, comprising
forming a first surface of a chill block from a first material and
bonding a second material to the first surface. The first material
may be steel and the second material may be copper or a copper
alloy. The first material is preferably applied at a thickness of
less than about 0.5 inches.
[0011] In accordance with another embodiment of the present
invention, a third material may be bonded to a side of the second
material that is not in contact with the first material. Any of the
surfaces may then be optionally machined. The first surface and/or
the chill block may be formed in a ceramic mold. The third material
may be steel and preferably chosen from the group consisting of
ANSI H113, ANSI A2, and ANSI S7.
[0012] In accordance with yet another embodiment of the present
invention, a method of manufacturing a chill block is provided,
comprising using a rapid solidification process to spray a first
material to form a first layer, and then using the rapid
solidification process to spray a second material onto a surface of
the first layer. The second material may be copper or a copper
alloy.
[0013] In accordance with yet another embodiment of the present
invention, chill block is provided, comprising a base having a top
surface and a bottom surface of a first material, and a first layer
of a second material bonded to the top surface of the base.
[0014] In accordance with yet another embodiment of the present
invention, a tool device for use with a die casting process for
shaping and solidifying molten metal into a shaped object is
provided, comprising a shaping means for forming the shape of an
object and a chilling means for solidifying metal that exits the
shaping means. The chilling means may comprise a layer of a first
material and a layer of a second material that are bonded together.
The tool may also include a metal inlet means for allowing metal to
flow into the tool, an overflow means between the shaping means and
the chilling means, and/or a second chilling means arranged with
the first chilling means to form a chill block passageway.
[0015] There has thus been outlined, rather broadly, certain
embodiments of the invention in order that the detailed description
thereof herein may be better understood, and in order that the
present contribution to the art may be better appreciated. There
are, of course, additional embodiments of the invention that will
be described below and which will form the subject matter of the
claims appended hereto.
[0016] In this respect, before explaining at least one embodiment
of the invention in detail, it is to be understood that the
invention is not limited in its application to the details of
construction and to the arrangements of the components set forth in
the following description or illustrated in the drawings. The
invention is capable of embodiments in addition to those described
and of being practiced and carried out in various ways. Also, it is
to be understood that the phraseology and terminology employed
herein, as well as the abstract, are for the purpose of description
and should not be regarded as limiting.
[0017] As such, those skilled in the art will appreciate that the
conception upon which this disclosure is based may readily be
utilized as a basis for the designing of other structures, methods
and systems for carrying out the several purposes of the present
invention. It is important, therefore, that the claims be regarded
as including such equivalent constructions insofar as they do not
depart from the spirit and scope of the present invention.
BRIEF DESCRIPTION OF THE DRAWINGS
[0018] FIG. 1 is a top view of a tool incorporating a chill block
in accordance with an embodiment of the present invention.
[0019] FIG. 2 is perspective view of a chill block in accordance
with an embodiment of the present invention.
[0020] FIG. 3 is a flow chart illustrating a method of
manufacturing chill blocks in accordance with the present
invention.
[0021] FIG. 4 illustrates a pair of chill blocks in accordance with
the present invention.
DETAILED DESCRIPTION
[0022] The invention will now be described with reference to the
drawing figures, in which like reference numerals refer to like
parts throughout. An embodiment, in accordance with the present
invention, provides a chill block made from copper metal that is
bonded to a layer of tool steel.
[0023] The tool steel layer can have a thickness of less then about
0.5 inches. In some embodiments, preferably, the tool steel layer
has a thickness ranging from about 0.060 to about 0.090 inches and
is present on the parting surface of the chill block or chill block
face. A tool steel layer may also be bonded on a portion of the
sides of the chill blocks and/or the bottom of the chill block.
Chill blocks in accordance with the present invention allow molten
metal to solidify in the passageway formed by a pair of chill
blocks, and provide for efficient manufacturing of objects by die
casting methods.
[0024] A tool 10 incorporating chill blocks 12, 14 in accordance
with the present invention is illustrated in FIG. 1. The tool 10
includes chill blocks 12, 14 positioned within a tool. Although
only one tool 10 is shown in FIG. 1, typically two tools 10 are
utilized to form a complete mold for forming an object via die
casting. Die cavities 16, 18, 20, 22, corresponding to the shape of
objects to be cast are formed in the tool 10. The die cavities 16,
18, 20, 22 shown in FIG. 1 correspond to one portion of the mold
that will form the resulting object. The other portion of the mold
will be present in die cavities of a tool similar to tool 10, and
when tool 10 and a corresponding tool are placed adjacent one
another, a complete mold for the objects to be cast is formed.
[0025] A tool inlet port 24 is provided in the tool 10 that allows
the injection of a molten metal into the tool 10. A channel 26 is
coupled to the tool inlet port 24 that allows molten metal injected
into the tool 10 to flow into the die cavities 16, 18, 20, 22 via
die cavity inlet ports 28, 30, 32, 34, 36, 38, 40, 42.
[0026] Die cavity outlet ports 44, 46, 48, 50, 52, 54, 56, 58 are
provided in the tool 10 that allow molten metal to exit the die
cavities 16, 18, 20, 22. Overflow passageways 60, 61, 62, 64, 66,
68, 70, 72, 74, 76, 78, 80, 82 are coupled to the die cavity outlet
ports 44, 46, 48, 50, 52, 54, 56, 58 and allow any overflow metal
exiting the die cavities 16, 18, 20, 22 to reach the chill blocks
12, 14. Each of the chill blocks includes a parting surface/chill
face 84, 86 that has a ribbed or jagged surface. Chill outlet ports
83, 85 are provided that allow a gas, for example, air, to exit the
tool 10.
[0027] Shown in FIG. 2 is a preferred embodiment of a chill block
12 in accordance with the present invention. Molten metal enters
chill block 12 from an overflow passageway 60, 61, 62, 64, 66, 68,
70, 72, 74, 76, 78, 80, 82 via a chill block inlet port 100. That
is, the chill block inlet port 100 receives overflow metal from a
die cavity 16, 18, 20, 22. The base of the chill block 88 (chill
block base) is made from a material, for example, copper, or a
metallic composition that includes copper, for example, beryllium
copper, and is the foundation to which the tool steel is layered
upon.
[0028] A layer, preferably having a thickness of less then about
0.5 inches and more preferably ranging from about 0.06 to about
0.09 inches, of a tool steel is applied, for example, by a spraying
technique, such as a rapid solidification process developed at the
Idaho National Engineering and Environmental Laboratory, to the
parting line surface 90 of the chill block 12, and to a portion 92,
94 or to all of the sides 96, 98 of the chill block 12. The rapid
solidification process is a spraying technique to harden the tool
steel. The rapid solidification process is described in U.S. Pat.
Nos. 5,718,863 and 6,074,194, which are incorporated by reference.
The tool steel utilized is steel that is stronger than the material
forming the chill block base 88.
[0029] In a preferred embodiment of the present invention, the tool
steel utilized may be any ANSI (American National Standards
Institute) or International Standards Organization(s) defined tool
steel. Examples of these tool steels include, but are not limited
to, ANSI H13, ANSI A2, and ANSI S7. According to other preferred
embodiments, other materials having, for example, materials having
a surface hardness of at least 30 Rockwell "C" scale (Rc) may be
utilized, and preferably materials having a surface hardness
ranging from about 30 to about 70 Rc may be utilized. More
preferably, materials having a surface hardness ranging from 30 to
about 65 Rc are utilized. According to some embodiments, however,
steel having a surface hardness greater than 65 Rc may also be
utilized.
[0030] An exemplary composition of ANSI H13 tool steel includes, by
percentage weight, about 0.4 carbon (C), about 0.4 manganese (Mn),
about 1.00 Silicon (Si), about 5.25 chromium (Cr), about 1.35
molybdenum (Mo), and about 1.00 vanadium (V). The remainder of the
exemplary composition of ANSI H13 is iron or primarily iron. The
ANSI H13 tool steel is characterized by its toughness and ability
to resist thermal fatigue cracking that may occur as a result of
cyclic heating and cooling cycles that result from the repeated use
of a tool to form an object from die casting methods.
[0031] An exemplary composition of ANSI A2 tool steel, includes, by
percentage weight, 1.00 carbon (C), 0.75 manganese (Mn), 0.30
Silicon (Si), 5.00 chromium (Cr), 1.00 molybdenum (Mo), and 0.25
vanadium (V). The remainder of the exemplary composition of A2 is
iron or primarily iron. The ANSI A2 tool steel is characterized by
its toughness and strength.
[0032] An exemplary composition of ANSI S7 tool steel, includes, by
percentage weight 0.50 carbon (C), 0.75 manganese (Mn), 0.25
Silicon (Si), 3.25 chromium (Cr), and 1.40 molybdenum (Mo). The
remainder of the exemplary composition of S7 is iron or primarily
iron. The ANSI A2 tool steel is characterized by its toughness and
wear resistance properties.
[0033] In a second embodiment of the present invention, the chill
block base 88 is made from a material, for example, copper or a
metallic mixture including copper, for example, beryllium copper. A
layer having a thickness, of less than about 0.5 inches and
preferably ranging from about 0.060 to about 0.090 inches, of a
tool steel is applied, for example, by a spraying technique, such
as the rapid solidification process developed at the Idaho National
Engineering and Environmental Laboratory, to the parting line
surface/chill face 90 of the chill block base 88 and around a
portion 92, 94 of the sides 96, 98 of the chill block 12. In
addition, a layer of tool steel is present on the bottom of the
chill block base 88.
[0034] In a third embodiment of the present invention, a layer of
tool steel is not present on any portion of the sides 96, 98 of the
chill block 12.
[0035] FIG. 3 is a flow chart illustrating a preferred embodiment
of a new method 102 for manufacturing a chill block. The process of
manufacturing a chill block in accordance with the preferred
embodiment of the present invention involves applying a layer of a
first material, for example tool steel, having a thickness of less
than about 0.5 inches and preferably ranging from about 0.060 to
about 0.090 inches, on an inside surface of a mold that is a
negative of the chill block being formed 104.
[0036] Preferably, a rapid solidification process is utilized to
apply the tool steel. A second material, for example, copper or
beryllium copper is added on top of the first material, preferably,
by the rapid solidification process 106. The tool steel is porous.
When the copper metal is added on top of the tool steel, the copper
metal fills the pores formed in the tool steel. Thus, in accordance
with the present invention, when the copper metal solidifies, the
copper metal bonds, for example, mechanically and/or chemically, to
the tool steel. The chill block 12 is then machined to the size
required for installation in the desired tool 108.
[0037] According to a second preferred method for forming a chill
block according to the present invention, after the second
material, for example, copper or beryllium copper is added on top
of the first material 106, the chill block is machined such that is
smaller than a predetermined final size for the chill block 108a. A
third layer of a material, for example, a tool steel, is added on
top of the second layer of material that is not in contact with the
inside surface of the mold 110, and the chill block may be larger
than the desired size for the chill block. In accordance with the
present invention, the copper or beryllium copper bonds, for
example, mechanically and/or chemically, to the tool steel. The
chill block is then machined, a second time, to the size required
for installation into a tool 112.
[0038] In an exemplary embodiment, a chill block resulting from the
second method of forming a chill block has a first layer and a
third layer that are formed from tool steel, and the second layer
is copper or copper beryllium. Accordingly, the external surfaces,
top, bottom and sides, of the chill block are tool steel, and the
external surfaces encapsulate the copper layer or layers.
Accordingly, the copper layer or layers of the chill block is
protected when being handled, installed, and/or removed from a
tool.
[0039] Shown in FIG. 4 is a side view of two chill blocks 12, 14
placed in a mold 114. In a preferred embodiment of the present
invention, a chill block 12 is placed in the tool 116 that forms,
for example the top portion of the mold (top tool device). The
chill block 12 placed in the top tool device 116 is referred to as
the cover chill block. In a preferred embodiment of the present
invention, chill block 144 is placed in the in the tool 118 that
forms, for example the bottom portion of mold (bottom tool device).
The chill block 14 placed in the bottom tool device 118 is referred
to as the ejector chill block.
[0040] As shown in FIG. 4, the chill blocks 12, 14 are assembled,
such that a chill block passageway 120 is formed between the pair
of chill blocks 12, 14. In an exemplary embodiment of the present
invention, a vacuum 122 is coupled to the chill block outlet port
124 via a conduit 126 to remove gas that enters the chill block
passageway 120.
[0041] During die casting, molten metal is injected into the tool
inlet port 24. The molten metal flows into the channel 26, and into
the die cavity inlet ports 28, 30, 40, 42 that are open to the
channel 24. As the molten metal flows into the die cavities 16, 18,
20, 22 gas, for example, air, that is present in a die cavity 16,
18, 20, 22 flows out of a die cavity 16, 18, 20, 22 via the die
cavity outlet ports 44, 46, 48, 50, 52, 54, 56, 58 and into
overflow passageways 60, 61 and 62, 64, 66, 68, 70, 72, 74, 76, 78,
80, 82. From the overflow passageways, the gas moves into one or
more chill block passageways 118 via the chill block inlet port 100
and out from chill block passageway 118 via a chill block outlet
port 83, 85, 124.
[0042] The application of, for example, copper or beryllium copper
to the chill block base, provides for a heat transfer rate that
allows molten metal that flows into a chill block passageway 118 to
solidify in the chill block passageway 116. Accordingly, molten
metal may be prevented from exiting the tool via the chill block
outlet port 83, 85, 124.
[0043] After any overflow molten metal has solidified in the chill
block passageway 118, the top and bottom tool devices 114, 116,
including the cover and ejector chill blocks 12, 14, are separated
and the objects formed in the die cavities are removed.
[0044] Aluminum is a common metal utilized in die casting to form
objects. The application of a hardened tool steel to the chill
block parting surface toughens and strengthens chill block parting
surfaces, and allows the chill blocks, in accordance with the
present invention, to resist the degrading properties of molten
aluminum for a period of time.
[0045] Further, the chill blocks, in accordance with the present
invention, involve a steel layer that is bonded to a copper metal
layer. Accordingly, the need mechanically couple the a steel part
to a copper part, as required when utilizing the prior art two-part
steel and copper chill blocks is eliminated. Also, the need for a
thermal grease to facilitate the transfer of heat between the steel
part and the copper part is obviated. Moreover, the thickness of
the steel layer is thinner than a steel layer of a conventional
two-part steel and copper chill block of the prior art.
[0046] The many features and advantages of the invention are
apparent from the detailed specification, and thus, it is intended
by the appended claims to cover all such features and advantages of
the invention which fall within the true spirit and scope of the
invention. Further, since numerous modifications and variations
will readily occur to those skilled in the art, it is not desired
to limit the invention to the exact construction and operation
illustrated and described, and accordingly, all suitable
modifications and equivalents may be resorted to, falling within
the scope of the invention.
* * * * *